JP2024045125A - 表面摩擦と粘着性が低減された弾性繊維 - Google Patents
表面摩擦と粘着性が低減された弾性繊維 Download PDFInfo
- Publication number
- JP2024045125A JP2024045125A JP2023218856A JP2023218856A JP2024045125A JP 2024045125 A JP2024045125 A JP 2024045125A JP 2023218856 A JP2023218856 A JP 2023218856A JP 2023218856 A JP2023218856 A JP 2023218856A JP 2024045125 A JP2024045125 A JP 2024045125A
- Authority
- JP
- Japan
- Prior art keywords
- wax
- elastic fiber
- fibers
- laminate
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】クリープ性能に悪影響を与えることなく表面摩擦とオーバーエンドテイクオフ粘着性を低減するワックス組成物を含む弾性繊維、これらの繊維を含む布地、衣服および積層体、ならびにそれらの調製方法を提供する。【解決手段】ポリウレタンまたはポリウレタン尿素および約0.5重量%~4重量%のワックス組成物を含む弾性繊維である。前記ワックス組成物はポリオレフィンワックスを含み、前記ワックス組成物は、無水マレイン酸を含むC24~C36ポリマーを含む変性ポリマーワックスを含む。【選択図】図1
Description
スパンデックスエラストマー糸は、横糸ニット、縦糸ニット、織物、および他のテキス
タイルなど、高い伸縮性、伸びからの良好な回復、およびそれらから作製される物品への
良好な適合性を提供することができる。しかし、スパンデックス基材は、従来の非弾性繊
維と比較して高い粘着性と摩擦に悩まされており、これは、商業用途を制限する可能性が
ある。粘着性が増加するため、スパンデックスフィラメントは互いに凝集したり、あるい
はさまざまな表面に接着したりする場合がある。高い粘着性は、スパンデックスフィラメ
ントがコアの周りに巻かれているパッケージングで特に問題になる。繊維が近接している
ため、特にコアの近くで繊維に圧力が加わると、隣接するフィラメントが互いに接着させ
得、巻かれているパッケージから破損することなく繊維を取り除くことが困難になり得る
ため、影響を受けたフィラメントを使用不可能なままにする場合がある。繊維が破損しな
い場合でも、粘着性ポイントおよび関連する張力スパイクにより、依然として、非常に可
変性の伸びが発生する可能性がある。使用不可能なフィラメントは一般に、コアで発生し
、「コア廃棄物」と称される。パッケージング後、時間と温度に応じて保管中にフィラメ
ントの粘着性が増加する場合がある。より長い保管時間とより高い温度は、新たに紡績さ
れパッケージされたスパンデックスよりも粘着性が増加し、コア廃棄物が多くなることに
等しい。したがって、スパンデックスの粘着性を減らすと、コア廃棄物が減り、巻き戻し
性能が向上し、費用対効果が向上する。
タイルなど、高い伸縮性、伸びからの良好な回復、およびそれらから作製される物品への
良好な適合性を提供することができる。しかし、スパンデックス基材は、従来の非弾性繊
維と比較して高い粘着性と摩擦に悩まされており、これは、商業用途を制限する可能性が
ある。粘着性が増加するため、スパンデックスフィラメントは互いに凝集したり、あるい
はさまざまな表面に接着したりする場合がある。高い粘着性は、スパンデックスフィラメ
ントがコアの周りに巻かれているパッケージングで特に問題になる。繊維が近接している
ため、特にコアの近くで繊維に圧力が加わると、隣接するフィラメントが互いに接着させ
得、巻かれているパッケージから破損することなく繊維を取り除くことが困難になり得る
ため、影響を受けたフィラメントを使用不可能なままにする場合がある。繊維が破損しな
い場合でも、粘着性ポイントおよび関連する張力スパイクにより、依然として、非常に可
変性の伸びが発生する可能性がある。使用不可能なフィラメントは一般に、コアで発生し
、「コア廃棄物」と称される。パッケージング後、時間と温度に応じて保管中にフィラメ
ントの粘着性が増加する場合がある。より長い保管時間とより高い温度は、新たに紡績さ
れパッケージされたスパンデックスよりも粘着性が増加し、コア廃棄物が多くなることに
等しい。したがって、スパンデックスの粘着性を減らすと、コア廃棄物が減り、巻き戻し
性能が向上し、費用対効果が向上する。
簡単に説明すると、本開示の実施形態としては、クリープ性能に悪影響を与えることな
く表面摩擦およびオーバーエンドテイクオフ粘着性を低減するために繊維に組み込まれた
ワックスを含む弾性繊維、繊維の調製方法、この繊維の使用方法、繊維、繊維を含む布地
、衣服、繊維を含むテキスタイルなどを含む積層体が挙げられる。
く表面摩擦およびオーバーエンドテイクオフ粘着性を低減するために繊維に組み込まれた
ワックスを含む弾性繊維、繊維の調製方法、この繊維の使用方法、繊維、繊維を含む布地
、衣服、繊維を含むテキスタイルなどを含む積層体が挙げられる。
1つの非限定的な例示的弾性繊維は、とりわけ、ポリウレタンもしくはポリウレタン尿
素またはそれらの混合物および約0.25重量%~約4重量%のワックス組成物を含む。
非限定的な一実施形態では、ワックス組成物は、ポリオレフィンワックスを含む。非限定
的な一実施形態では、弾性繊維は、ステアリン酸カルシウム、ステアリン酸マグネシウム
、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択され
る少なくとも1つの添加剤をさらに含む。さらに、本開示の非限定的な実施形態は、本明
細書に記載される弾性繊維を含む布地を含む。さらに、本開示の非限定的な実施形態は、
本明細書に記載される弾性繊維を含む積層体を含む。さらに、本開示の非限定的な実施形
態は、本明細書に記載される弾性繊維を含む衣服を含む。
素またはそれらの混合物および約0.25重量%~約4重量%のワックス組成物を含む。
非限定的な一実施形態では、ワックス組成物は、ポリオレフィンワックスを含む。非限定
的な一実施形態では、弾性繊維は、ステアリン酸カルシウム、ステアリン酸マグネシウム
、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択され
る少なくとも1つの添加剤をさらに含む。さらに、本開示の非限定的な実施形態は、本明
細書に記載される弾性繊維を含む布地を含む。さらに、本開示の非限定的な実施形態は、
本明細書に記載される弾性繊維を含む積層体を含む。さらに、本開示の非限定的な実施形
態は、本明細書に記載される弾性繊維を含む衣服を含む。
とりわけ、弾性繊維を調製するための非限定的な例示的なプロセスは、a)少なくとも
1つのポリウレタン、ポリウレタン尿素、またはそれらの混合物を含む組成物を調製する
ことと、(b)組成物に約0.25重量%~4重量%のワックス組成物を添加することと
、(c)任意選択的に、組成物に、ステアリン酸カルシウム、ステアリン酸マグネシウム
、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択され
る少なくとも1つの添加剤を添加することと、(d)湿式紡糸、乾式紡糸および溶融紡糸
からなる群から選択される紡糸プロセスにより組成物から繊維を調製することと、を含む
。
1つのポリウレタン、ポリウレタン尿素、またはそれらの混合物を含む組成物を調製する
ことと、(b)組成物に約0.25重量%~4重量%のワックス組成物を添加することと
、(c)任意選択的に、組成物に、ステアリン酸カルシウム、ステアリン酸マグネシウム
、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択され
る少なくとも1つの添加剤を添加することと、(d)湿式紡糸、乾式紡糸および溶融紡糸
からなる群から選択される紡糸プロセスにより組成物から繊維を調製することと、を含む
。
本開示をより詳細に説明する前に、本開示は説明した特定の実施形態に限定されず、し
たがって当然ながら変化する可能性があることを理解されたい。また、本開示の範囲は添
付の特許請求の範囲によってのみ限定されるため、本明細書で使用される用語は特定の実
施形態を説明することのみを目的としており、限定することを意図しないことも理解され
たい。
たがって当然ながら変化する可能性があることを理解されたい。また、本開示の範囲は添
付の特許請求の範囲によってのみ限定されるため、本明細書で使用される用語は特定の実
施形態を説明することのみを目的としており、限定することを意図しないことも理解され
たい。
別に定義されない限り、本明細書で使用されるすべての技術用語および科学用語は、本
開示が属する技術分野の当業者によって一般に理解されるのと同じ意味を有する。本明細
書に記載のものと類似または同等の任意の方法および材料も本開示の実施または試験に使
用することができるが、好ましい方法および材料をここで説明する。
開示が属する技術分野の当業者によって一般に理解されるのと同じ意味を有する。本明細
書に記載のものと類似または同等の任意の方法および材料も本開示の実施または試験に使
用することができるが、好ましい方法および材料をここで説明する。
本明細書で引用されるすべての出版物および特許は、各出版物または特許が具体的かつ
個別に参照により組み込まれることが示されているように参照により本明細書に組み込ま
れ、出版物が引用された関連する方法および/または材料を開示および説明するために参
照により本明細書に組み込まれる。いかなる出版物の引用も、出願日前のその開示に関す
るものであり、本開示が事前の開示によりそのような出版物に先行する権利がないことの
承認として解釈されるべきではない。さらに、提供される出版日は、実際の出版日とは異
なる可能性があり、個別に確認する必要がある場合がある。
個別に参照により組み込まれることが示されているように参照により本明細書に組み込ま
れ、出版物が引用された関連する方法および/または材料を開示および説明するために参
照により本明細書に組み込まれる。いかなる出版物の引用も、出願日前のその開示に関す
るものであり、本開示が事前の開示によりそのような出版物に先行する権利がないことの
承認として解釈されるべきではない。さらに、提供される出版日は、実際の出版日とは異
なる可能性があり、個別に確認する必要がある場合がある。
本開示を読むと当業者には明らかなように、本明細書で説明および図示する個々の実施
形態のそれぞれは、本開示の範囲または趣旨から逸脱することなく、他のいくつかの実施
形態のいずれかの特徴から容易に分離または組み合わせることができる個別の構成要素お
よび特徴を有する。列挙された方法は、列挙されたイベントの順序、または論理的に可能
な任意の他の順序で実行することができる。
形態のそれぞれは、本開示の範囲または趣旨から逸脱することなく、他のいくつかの実施
形態のいずれかの特徴から容易に分離または組み合わせることができる個別の構成要素お
よび特徴を有する。列挙された方法は、列挙されたイベントの順序、または論理的に可能
な任意の他の順序で実行することができる。
本開示の実施形態は、別に示されない限り、化学、布地、テキスタイルなどの技術を使
用し、これらは当該技術分野の技術の範囲内である。そのような技術は、文献で十分に説
明されている。
用し、これらは当該技術分野の技術の範囲内である。そのような技術は、文献で十分に説
明されている。
以下の実施例は、本明細書に開示および特許請求される方法の実施方法ならびに組成物
および化合物の使用方法の完全な開示および説明を当業者に提供するために提示される。
数字(例えば、量、温度など)に関して正確性を確保するための努力がなされてきたが、
いくつかの誤差と偏差は考慮されるべきである。特に指定のない限り、部は重量部であり
、温度は℃であり、圧力は大気圧である。標準の温度および圧力は、25℃および1気圧
として定義されている。
および化合物の使用方法の完全な開示および説明を当業者に提供するために提示される。
数字(例えば、量、温度など)に関して正確性を確保するための努力がなされてきたが、
いくつかの誤差と偏差は考慮されるべきである。特に指定のない限り、部は重量部であり
、温度は℃であり、圧力は大気圧である。標準の温度および圧力は、25℃および1気圧
として定義されている。
本開示の実施形態を詳細に説明する前に、特に指定のない限り、本開示は、特定の材料
、試薬、反応材料、製造プロセスなどに限定されず、したがって変化し得ることを理解さ
れたい。また、本明細書で使用される用語は、特定の実施形態を説明することのみを目的
としており、限定することを意図していないことも理解されたい。本開示では、論理的に
可能な場合、ステップを異なる順序で実行することも可能である。
、試薬、反応材料、製造プロセスなどに限定されず、したがって変化し得ることを理解さ
れたい。また、本明細書で使用される用語は、特定の実施形態を説明することのみを目的
としており、限定することを意図していないことも理解されたい。本開示では、論理的に
可能な場合、ステップを異なる順序で実行することも可能である。
明細書および添付の特許請求の範囲で使用されているように、単数形「a」、「an」
、および「the」は、文脈が明らかにそうでないことを示す場合を除き、複数の指示対
象を含むことに注意しなければならない。したがって、例えば、「支持体」への言及は、
複数の支持体を含む。本明細書および後続の特許請求の範囲では、反対の意図が明らかで
ない限り、以下の意味を有すると定義されるいくつかの用語を参照する。
定義
、および「the」は、文脈が明らかにそうでないことを示す場合を除き、複数の指示対
象を含むことに注意しなければならない。したがって、例えば、「支持体」への言及は、
複数の支持体を含む。本明細書および後続の特許請求の範囲では、反対の意図が明らかで
ない限り、以下の意味を有すると定義されるいくつかの用語を参照する。
定義
本明細書で使用されるとき、「繊維」という用語は、布地および糸ならびにテキスタイ
ル製造で使用することができるフィラメント状材料を指す。1本以上の繊維を使用して、
布地または糸を製造することができる。糸は、当該技術分野で知られている方法に従って
完全に延伸またはテクスチャー加工することができる。
ル製造で使用することができるフィラメント状材料を指す。1本以上の繊維を使用して、
布地または糸を製造することができる。糸は、当該技術分野で知られている方法に従って
完全に延伸またはテクスチャー加工することができる。
本明細書で使用されるとき、「スパンデックス」とは、繊維形成物質が約85重量%以
上のセグメント化ポリウレタンで構成される長鎖合成エラストマーである合成繊維を指し
、ポリウレタン尿素はそのようなポリウレタンのサブクラスとみなされる。このような合
成繊維は、供給パッケージを形成するために円筒状のコアに巻き付けられてもよい。スパ
ンデックス組成物は、湿式紡糸プロセスまたは乾式紡糸プロセスによって調製することが
でき、円形断面または平坦な「テープ状」断面などのさまざまな断面のいずれかを有する
ことができる。あるいは、ポリウレタン溶液を注型し、乾燥させて「テープ」構成を形成
することができる。
上のセグメント化ポリウレタンで構成される長鎖合成エラストマーである合成繊維を指し
、ポリウレタン尿素はそのようなポリウレタンのサブクラスとみなされる。このような合
成繊維は、供給パッケージを形成するために円筒状のコアに巻き付けられてもよい。スパ
ンデックス組成物は、湿式紡糸プロセスまたは乾式紡糸プロセスによって調製することが
でき、円形断面または平坦な「テープ状」断面などのさまざまな断面のいずれかを有する
ことができる。あるいは、ポリウレタン溶液を注型し、乾燥させて「テープ」構成を形成
することができる。
本明細書で使用されるとき、「ワックス組成物」という句は、弾性繊維に添加された場
合、表面摩擦および/またはオーバーエンドテイクオフ粘着性もしくは張力を、ワックス
含有添加剤を含まない弾性繊維の場合と比較して減少させるワックス含有添加剤を包含す
ることを意図する。
考察
合、表面摩擦および/またはオーバーエンドテイクオフ粘着性もしくは張力を、ワックス
含有添加剤を含まない弾性繊維の場合と比較して減少させるワックス含有添加剤を包含す
ることを意図する。
考察
本開示の実施形態は、繊維に組み込まれたワックス組成物を含む弾性繊維、繊維の調製
方法、この繊維の使用方法、繊維を含む積層体、繊維を含む布地、繊維を含む衣服、繊維
を含むテキスタイルなどを提供する。本開示の実施形態は、パッケージまたはコアからの
繊維の良好な送達を提供する弾性繊維を提供する。本開示の実施形態は、繊維の不規則な
送達を引き起こす他の弾性繊維とは対照的に、繊維の挟み込み、破損、および/または他
の損傷を低減し得る、弾性繊維の滑らかで均一な送達を提供する。
方法、この繊維の使用方法、繊維を含む積層体、繊維を含む布地、繊維を含む衣服、繊維
を含むテキスタイルなどを提供する。本開示の実施形態は、パッケージまたはコアからの
繊維の良好な送達を提供する弾性繊維を提供する。本開示の実施形態は、繊維の不規則な
送達を引き起こす他の弾性繊維とは対照的に、繊維の挟み込み、破損、および/または他
の損傷を低減し得る、弾性繊維の滑らかで均一な送達を提供する。
本開示の実施形態は、ワックス組成物を含む弾性繊維またはスパンデックス繊維を含む
。ワックス組成物は、繊維に局所仕上げを加えることなく繊維を使用することができるよ
うに、粘着防止効果および/またはスパンデックス繊維の表面摩擦の減少をもたらす任意
のワックスを含むことができる。さらに、ほとんどの粘着防止組成物とは異なり、弾性繊
維のワックス組成物の含有は、繊維または糸の接着性に有害な影響を与えず、ホットメル
ト弾性貼り付け接着剤を使用して布地への糸の接着性を高めることさえできる。非限定的
な一実施形態では、ワックス組成物はポリオレフィンワックスを含む。非限定的な例とし
ては、ポリプロピレンもしくはポリエチレンワックス、または無水マレイン酸、モンタン
ワックス酸のエステルを含むC24~C36ポリマーを含む他の高度に修飾されたポリマ
ーワックスが挙げられる。商業的な例としては、CLARIANTが製造するCerid
ust5551、Ceridust8020、およびCeridust6050が挙げら
れる。非限定的な一実施形態では、ワックス組成物は、ステアリン酸カルシウム、ステア
リン酸マグネシウム、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物など
の追加の添加剤をさらに含む。繊維の紡糸前に、ワックス組成物および任意選択的に添加
剤(複数可)をポリウレタンまたはポリウレタン尿素ポリマーに添加する。
。ワックス組成物は、繊維に局所仕上げを加えることなく繊維を使用することができるよ
うに、粘着防止効果および/またはスパンデックス繊維の表面摩擦の減少をもたらす任意
のワックスを含むことができる。さらに、ほとんどの粘着防止組成物とは異なり、弾性繊
維のワックス組成物の含有は、繊維または糸の接着性に有害な影響を与えず、ホットメル
ト弾性貼り付け接着剤を使用して布地への糸の接着性を高めることさえできる。非限定的
な一実施形態では、ワックス組成物はポリオレフィンワックスを含む。非限定的な例とし
ては、ポリプロピレンもしくはポリエチレンワックス、または無水マレイン酸、モンタン
ワックス酸のエステルを含むC24~C36ポリマーを含む他の高度に修飾されたポリマ
ーワックスが挙げられる。商業的な例としては、CLARIANTが製造するCerid
ust5551、Ceridust8020、およびCeridust6050が挙げら
れる。非限定的な一実施形態では、ワックス組成物は、ステアリン酸カルシウム、ステア
リン酸マグネシウム、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物など
の追加の添加剤をさらに含む。繊維の紡糸前に、ワックス組成物および任意選択的に添加
剤(複数可)をポリウレタンまたはポリウレタン尿素ポリマーに添加する。
非限定的な一実施形態では、本開示の弾性繊維は、ポリウレタンまたはポリウレタン尿
素およびワックス組成物、ならびに任意選択的に1つ以上の添加剤を含む。好適な添加剤
としては、有機ステアリン酸(例えば、ステアリン酸カルシウムまたはステアリン酸マグ
ネシウム)、鉱油、シリコン油、およびそれらの混合物が挙げられるが、これらに限定さ
れない。特定の実施形態では、弾性繊維またはワックス組成物は、本明細書に記載のワッ
クス組成物に加えて、少なくとも1つの追加の粒子状粘着防止剤を含むことができる。
素およびワックス組成物、ならびに任意選択的に1つ以上の添加剤を含む。好適な添加剤
としては、有機ステアリン酸(例えば、ステアリン酸カルシウムまたはステアリン酸マグ
ネシウム)、鉱油、シリコン油、およびそれらの混合物が挙げられるが、これらに限定さ
れない。特定の実施形態では、弾性繊維またはワックス組成物は、本明細書に記載のワッ
クス組成物に加えて、少なくとも1つの追加の粒子状粘着防止剤を含むことができる。
非限定的な一実施形態では、本開示の弾性繊維は、例えば、繊維の約0.25重量%~
4重量%のワックス組成物を含む。
4重量%のワックス組成物を含む。
非限定的な一実施形態では、本開示のワックス組成物は、微粉化されたメタロセンベー
スのポリプロピレンワックスである。
スのポリプロピレンワックスである。
非限定的な一実施形態では、本開示のワックス組成物は、微粉化されたポリエチレンワ
ックスである。
ックスである。
非限定的な一実施形態では、本開示の弾性繊維は、添加剤を含む。非限定的な一実施形
態では、弾性繊維は、約0.1%~1.0%、約0.1%~2.0%、約0.1%~3.
0%、約0.1%~4.0%、約0.1%~5.0%、約0.1%~6.0%、約0.1
%~7.0%、約0.1%~8.0%、約0.1%~9.0%、または約0.1%~10
.0%の添加剤(例えば、ステアリン酸、シリコン油または鉱油)を含み得る。
態では、弾性繊維は、約0.1%~1.0%、約0.1%~2.0%、約0.1%~3.
0%、約0.1%~4.0%、約0.1%~5.0%、約0.1%~6.0%、約0.1
%~7.0%、約0.1%~8.0%、約0.1%~9.0%、または約0.1%~10
.0%の添加剤(例えば、ステアリン酸、シリコン油または鉱油)を含み得る。
本開示の実施形態は、本明細書に記載される弾性繊維のいずれか1つを調製するための
プロセスを含む。本プロセスは、少なくともポリウレタン、ポリウレタン尿素、またはそ
れらの混合物を含む組成物を調製することを含む。その後、本プロセスは、ワックス組成
物を組成物に添加することを含む。次に、本プロセスは任意選択的に、組成物に添加物(
例えば、ステアリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリ
コン油、鉱油、またはそれらの混合物)を添加することを含む。次に、本プロセスは、紡
糸プロセス(例えば、湿式紡糸、乾式紡糸、および溶融紡糸)によって組成物から繊維を
調製することを含む。
プロセスを含む。本プロセスは、少なくともポリウレタン、ポリウレタン尿素、またはそ
れらの混合物を含む組成物を調製することを含む。その後、本プロセスは、ワックス組成
物を組成物に添加することを含む。次に、本プロセスは任意選択的に、組成物に添加物(
例えば、ステアリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリ
コン油、鉱油、またはそれらの混合物)を添加することを含む。次に、本プロセスは、紡
糸プロセス(例えば、湿式紡糸、乾式紡糸、および溶融紡糸)によって組成物から繊維を
調製することを含む。
非限定的な一実施形態では、繊維の生産のための紡糸プロセスは、乾式紡糸である。乾
式紡糸とは、ポリマー溶液を紡糸口金のオリフィスからシャフトに押し込んでフィラメン
トを形成するプロセスを指す。加熱された不活性ガスがチャンバーを通過し、フィラメン
トがシャフトを通過するときに、フィラメントから溶媒を蒸発させる。次いで、得られた
弾性繊維を円筒形コアに巻き付けて、スパンデックス供給パッケージを形成することがで
きる。湿式紡糸プロセスも、ポリマー溶液のキャスティングおよび乾燥と同様に使用され
てもよい。
式紡糸とは、ポリマー溶液を紡糸口金のオリフィスからシャフトに押し込んでフィラメン
トを形成するプロセスを指す。加熱された不活性ガスがチャンバーを通過し、フィラメン
トがシャフトを通過するときに、フィラメントから溶媒を蒸発させる。次いで、得られた
弾性繊維を円筒形コアに巻き付けて、スパンデックス供給パッケージを形成することがで
きる。湿式紡糸プロセスも、ポリマー溶液のキャスティングおよび乾燥と同様に使用され
てもよい。
非限定的な一実施形態では、本プロセスは、少なくとも1つのポリウレタンもしくはポ
リウレタン尿素、またはそれらの混合物を含む組成物を調製することと、ステアリン酸カ
ルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリコン油、鉱油、およびそ
れらの混合物から選択される組成物に添加剤を添加することと、約0.25%~4%のワ
ックス組成物を組成物に添加することと、ならびに得られた組成物から、湿式紡糸、乾式
紡糸、および溶融紡糸から選択される紡糸プロセスにより繊維を調製することと、を含む
。
リウレタン尿素、またはそれらの混合物を含む組成物を調製することと、ステアリン酸カ
ルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリコン油、鉱油、およびそ
れらの混合物から選択される組成物に添加剤を添加することと、約0.25%~4%のワ
ックス組成物を組成物に添加することと、ならびに得られた組成物から、湿式紡糸、乾式
紡糸、および溶融紡糸から選択される紡糸プロセスにより繊維を調製することと、を含む
。
一実施形態では、本開示の弾性繊維を作製するために使用されるポリマーは、高分子グ
リコールを、例えば、ジイソシアネートでキャッピングし、次いで、得られたキャッピン
グされたグリコールを好適な溶媒(例えば、ジメチルアセトアミド(DMAc)、N-メ
チルピロリドン、ジメチルホルムアミドなど)に溶解し、キャッピングされたグリコール
を、ジオールなどの連鎖延長剤で鎖延長してポリウレタンを形成するか、またはジアミン
を使用してポリウレタン尿素を形成することによって調製される。
リコールを、例えば、ジイソシアネートでキャッピングし、次いで、得られたキャッピン
グされたグリコールを好適な溶媒(例えば、ジメチルアセトアミド(DMAc)、N-メ
チルピロリドン、ジメチルホルムアミドなど)に溶解し、キャッピングされたグリコール
を、ジオールなどの連鎖延長剤で鎖延長してポリウレタンを形成するか、またはジアミン
を使用してポリウレタン尿素を形成することによって調製される。
少なくとも85重量%のセグメント化されたポリウレタンを含む繊維または長鎖合成ポ
リマーの調製に有用なポリウレタン尿素組成物。通常、これらには、ジイソシアネートと
反応してNCO末端プレポリマー(「キャッピングされたグリコール」)を形成する高分
子グリコールが含まれ、次いで、これを、ジメチルアセトアミド、ジメチルホルムアミド
、またはN-メチルピロリドンなどの好適な溶媒に溶解し、二次的に二官能性連鎖延長剤
と反応させる。
リマーの調製に有用なポリウレタン尿素組成物。通常、これらには、ジイソシアネートと
反応してNCO末端プレポリマー(「キャッピングされたグリコール」)を形成する高分
子グリコールが含まれ、次いで、これを、ジメチルアセトアミド、ジメチルホルムアミド
、またはN-メチルピロリドンなどの好適な溶媒に溶解し、二次的に二官能性連鎖延長剤
と反応させる。
ポリウレタンは、連鎖延長剤がジオールである場合の第2ステップで形成される(およ
び溶媒なしで調製することもできる)。ポリウレタンのサブクラスであるポリウレタン尿
素は、連鎖延長剤がジアミンの場合に形成される。スパンデックスに紡糸することができ
るポリウレタン尿素ポリマーの調製において、グリコールは、ヒドロキシ末端基とジイソ
シアネートおよび1つ以上のジアミンとの連続的な反応によって延長される。いずれの場
合も、粘度を含む必要な特性を備えたポリマーを提供するために、グリコールは、鎖延長
を受けなければならない。所望される場合、ジブチルスズジラウレート、オクタン酸第一
スズ、鉱酸、トリエチルアミンなどの第三級アミン、N,N’-ジメチルピペラジンなど
、および他の既知の触媒を使用して、キャッピングステップを支援することができる。
び溶媒なしで調製することもできる)。ポリウレタンのサブクラスであるポリウレタン尿
素は、連鎖延長剤がジアミンの場合に形成される。スパンデックスに紡糸することができ
るポリウレタン尿素ポリマーの調製において、グリコールは、ヒドロキシ末端基とジイソ
シアネートおよび1つ以上のジアミンとの連続的な反応によって延長される。いずれの場
合も、粘度を含む必要な特性を備えたポリマーを提供するために、グリコールは、鎖延長
を受けなければならない。所望される場合、ジブチルスズジラウレート、オクタン酸第一
スズ、鉱酸、トリエチルアミンなどの第三級アミン、N,N’-ジメチルピペラジンなど
、および他の既知の触媒を使用して、キャッピングステップを支援することができる。
好適な高分子グリコール成分の例としては、ポリエーテルグリコール、ポリカーボネー
トグリコール、および数平均分子量が約600~3,500のポリエステルグリコールが
挙げられるが、これらに限定されない。2つ以上のポリマーグリコールまたはコポリマー
の混合物を含めることができる。
トグリコール、および数平均分子量が約600~3,500のポリエステルグリコールが
挙げられるが、これらに限定されない。2つ以上のポリマーグリコールまたはコポリマー
の混合物を含めることができる。
使用することができるポリエーテルグリコールの例としては、エチレンオキシド、プロ
ピレンオキシド、トリメチレンオキシド、テトラヒドロフラン、および3-メチルテトラ
ヒドロフランの開環重合および/もしくは共重合からの、またはエチレングリコール、1
,3-プロパンジオール、1,4-ブタンジオール、1,5-ペンタンジオール、1,6
-ヘキサンジオール、2,2-ジメチル-1,3プロパンジオール、3-メチル-1,5
-ペンタンジオール、1,7-ヘプタンジオール、1,8-オクタンジオール、1,9-
ノナンジオール、1,10-デカンジオールおよび1,12-ドデカンジオールなどの各
分子に12個未満の炭素原子を含む、ジオールもしくはジオール混合物などの多価アルコ
ールの縮合重合からの、2つのヒドロキシル基を有するグリコールが挙げられるが、これ
らに限定されない。分子量が約1,700~約2,100のポリ(テトラメチレンエーテ
ル)グリコール、例えば2の官能基を有するTerathane(登録商標)1800(
カンザス州ウィチタのINVISTA)が、具体的な好適なグリコールの例である。コポ
リマーには、ポリ(テトラメチレン-コ-エチレンエーテル)グリコールが含まれ得る。
ピレンオキシド、トリメチレンオキシド、テトラヒドロフラン、および3-メチルテトラ
ヒドロフランの開環重合および/もしくは共重合からの、またはエチレングリコール、1
,3-プロパンジオール、1,4-ブタンジオール、1,5-ペンタンジオール、1,6
-ヘキサンジオール、2,2-ジメチル-1,3プロパンジオール、3-メチル-1,5
-ペンタンジオール、1,7-ヘプタンジオール、1,8-オクタンジオール、1,9-
ノナンジオール、1,10-デカンジオールおよび1,12-ドデカンジオールなどの各
分子に12個未満の炭素原子を含む、ジオールもしくはジオール混合物などの多価アルコ
ールの縮合重合からの、2つのヒドロキシル基を有するグリコールが挙げられるが、これ
らに限定されない。分子量が約1,700~約2,100のポリ(テトラメチレンエーテ
ル)グリコール、例えば2の官能基を有するTerathane(登録商標)1800(
カンザス州ウィチタのINVISTA)が、具体的な好適なグリコールの例である。コポ
リマーには、ポリ(テトラメチレン-コ-エチレンエーテル)グリコールが含まれ得る。
使用することができるポリエステルポリオールの例としては、各分子に12個以下の炭
素原子を含む低分子量の脂肪族ポリカルボン酸およびポリオールまたはそれらの混合物の
縮合重合によって生成される2つのヒドロキシル基を有するエステルグリコールが挙げら
れるが、これらに限定されない。好適なポリカルボン酸の例としては、マロン酸、コハク
酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ウ
ンデカンジカルボン酸、およびドデカンジカルボン酸が挙げられるが、これらに限定され
ない。ポリエステルポリオールを調製するための好適なポリオールの例としては、エチレ
ングリコール、1,3-プロパンジオール、1,4-ブタンジオール、1,5-ペンタン
ジオール1,6-ヘキサンジオール、ネオペンチルグリコール、3-メチル-1,5-ペ
ンタンジオール、1,7-ヘプタンジオール、1,8-オクタンジオール、1,9-ノナ
ンジオール、1,10-デカンジオールおよび1,12-ドデカンジオールが挙げられる
が、これらに限定されない。約5℃~50℃の融解温度を有する線状二官能性ポリエステ
ルポリオールが、具体的なポリエステルポリオールの例である。
素原子を含む低分子量の脂肪族ポリカルボン酸およびポリオールまたはそれらの混合物の
縮合重合によって生成される2つのヒドロキシル基を有するエステルグリコールが挙げら
れるが、これらに限定されない。好適なポリカルボン酸の例としては、マロン酸、コハク
酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ウ
ンデカンジカルボン酸、およびドデカンジカルボン酸が挙げられるが、これらに限定され
ない。ポリエステルポリオールを調製するための好適なポリオールの例としては、エチレ
ングリコール、1,3-プロパンジオール、1,4-ブタンジオール、1,5-ペンタン
ジオール1,6-ヘキサンジオール、ネオペンチルグリコール、3-メチル-1,5-ペ
ンタンジオール、1,7-ヘプタンジオール、1,8-オクタンジオール、1,9-ノナ
ンジオール、1,10-デカンジオールおよび1,12-ドデカンジオールが挙げられる
が、これらに限定されない。約5℃~50℃の融解温度を有する線状二官能性ポリエステ
ルポリオールが、具体的なポリエステルポリオールの例である。
使用することができるポリカーボネートポリオールの例としては、各分子に12個以下
の炭素原子を含む低分子量のホスゲン、クロロギ酸エステル、ジアルキルカーボネートま
たはジアリルカーボネートおよび脂肪族ポリオール、またはそれらの混合物の縮合重合に
よって生成される2つ以上のヒドロキシ基を有するカーボネートグリコールが挙げられる
が、これらに限定されない。ポリカーボネートポリオールを調製するための好適なポリオ
ールの例としては、ジエチレングリコール、1,3-プロパンジオール、1,4-ブタン
ジオール、1,5-ペンタンジオール、1,6-ヘキサンジオール、ネオペンチルグリコ
ール、3-メチル-1,5-ペンタンジオール、1,7-ヘプタンジオール、1,8-オ
クタンジオール、1,9-ノナンジオール、1,10-デカンジオールおよび1,12-
ドデカンジオールが挙げられるが、これらに限定されない。約5℃~約50℃の融解温度
を有する線状二官能性ポリカーボネートポリオールが、具体的なポリカーボネートポリオ
ールの例である。
の炭素原子を含む低分子量のホスゲン、クロロギ酸エステル、ジアルキルカーボネートま
たはジアリルカーボネートおよび脂肪族ポリオール、またはそれらの混合物の縮合重合に
よって生成される2つ以上のヒドロキシ基を有するカーボネートグリコールが挙げられる
が、これらに限定されない。ポリカーボネートポリオールを調製するための好適なポリオ
ールの例としては、ジエチレングリコール、1,3-プロパンジオール、1,4-ブタン
ジオール、1,5-ペンタンジオール、1,6-ヘキサンジオール、ネオペンチルグリコ
ール、3-メチル-1,5-ペンタンジオール、1,7-ヘプタンジオール、1,8-オ
クタンジオール、1,9-ノナンジオール、1,10-デカンジオールおよび1,12-
ドデカンジオールが挙げられるが、これらに限定されない。約5℃~約50℃の融解温度
を有する線状二官能性ポリカーボネートポリオールが、具体的なポリカーボネートポリオ
ールの例である。
非限定的な一実施形態では、ジイソシアネート成分はまた、4,4’-メチレンビス(
フェニルイソシアネート)および2,4’-メチレンビス(フェニルイソシアネート)を
含有するジフェニルメタンジイソシアネート(MDI)の異性体混合物を含む単一のジイ
ソシアネートまたは異なるジイソシアネートの混合物を含む。任意の好適な芳香族または
脂肪族ジイソシアネートを含めることができる。使用することができるジイソシアネート
の例としては、4,4’-メチレンビス(フェニルイソシアネート)、2,4’-メチレ
ンビス(フェニルイソシアネート)、4,4’-メチレンビス(シクロヘキシルイソシア
ネート)、1,3-ジイソシアナト-4-メチル-ベンゼン、2,2’-トルエンジイソ
シアネート、2,4’-トルエンジイソシアネート、およびそれらの混合物が挙げられる
が、これらに限定されない。
フェニルイソシアネート)および2,4’-メチレンビス(フェニルイソシアネート)を
含有するジフェニルメタンジイソシアネート(MDI)の異性体混合物を含む単一のジイ
ソシアネートまたは異なるジイソシアネートの混合物を含む。任意の好適な芳香族または
脂肪族ジイソシアネートを含めることができる。使用することができるジイソシアネート
の例としては、4,4’-メチレンビス(フェニルイソシアネート)、2,4’-メチレ
ンビス(フェニルイソシアネート)、4,4’-メチレンビス(シクロヘキシルイソシア
ネート)、1,3-ジイソシアナト-4-メチル-ベンゼン、2,2’-トルエンジイソ
シアネート、2,4’-トルエンジイソシアネート、およびそれらの混合物が挙げられる
が、これらに限定されない。
いくつかの非限定的な実施形態で使用され得る連鎖延長剤は、水またはポリウレタン尿
素用のジアミン連鎖延長剤のいずれかであり得る。ポリウレタン尿素および得られる繊維
の所望の特性に応じて、異なる連鎖延長剤の組み合わせを含めることができる。好適なジ
アミン連鎖延長剤の例としては、ヒドラジン、1,2-エチレンジアミン、1,4-ブタ
ンジアミン、1,2-ブタンジアミン、1,3-ブタンジアミン、1,3-ジアミノ-2
,2-ジメチルブタン、1,6-ヘキサメチレンジアミン、1,12-ドデカンジアミン
、1,2-プロパンジアミン、1,3-プロパンジアミン、2-メチル-1,5-ペンタ
ンジアミン、1-アミノ-3,3,5-トリメチル-5-アミノメチルシクロヘキサン、
2,4-ジアミノ-1-メチルシクロヘキサン、N-メチルアミノ-ビス(3-プロピル
アミン)、1,2-シクロヘキサンジアミン、1,4-シクロヘキサンジアミン、4,4
’-メチレン-ビス(シクロヘキシルアミン)、イソホロンジアミン、2,2-ジメチル
-1,3-プロパンジアミン、メタテトラメチルキシレンジアミン、1,3-ジアミノ-
4-メチルシクロヘキサン、1,3-シクロヘキサンジアミン、1,1-メチレン-ビス
(4,4’-ジアミノヘキサン)、3-アミノメチル-3,5,5-トリメチルシクロヘ
キサン、1,3-ペンタンジアミン(1,3-ジアミノペンタン)、m-キシリレンジア
ミン、およびJeffamine(登録商標)(Texaco)が挙げられるが、これら
に限定されない。
素用のジアミン連鎖延長剤のいずれかであり得る。ポリウレタン尿素および得られる繊維
の所望の特性に応じて、異なる連鎖延長剤の組み合わせを含めることができる。好適なジ
アミン連鎖延長剤の例としては、ヒドラジン、1,2-エチレンジアミン、1,4-ブタ
ンジアミン、1,2-ブタンジアミン、1,3-ブタンジアミン、1,3-ジアミノ-2
,2-ジメチルブタン、1,6-ヘキサメチレンジアミン、1,12-ドデカンジアミン
、1,2-プロパンジアミン、1,3-プロパンジアミン、2-メチル-1,5-ペンタ
ンジアミン、1-アミノ-3,3,5-トリメチル-5-アミノメチルシクロヘキサン、
2,4-ジアミノ-1-メチルシクロヘキサン、N-メチルアミノ-ビス(3-プロピル
アミン)、1,2-シクロヘキサンジアミン、1,4-シクロヘキサンジアミン、4,4
’-メチレン-ビス(シクロヘキシルアミン)、イソホロンジアミン、2,2-ジメチル
-1,3-プロパンジアミン、メタテトラメチルキシレンジアミン、1,3-ジアミノ-
4-メチルシクロヘキサン、1,3-シクロヘキサンジアミン、1,1-メチレン-ビス
(4,4’-ジアミノヘキサン)、3-アミノメチル-3,5,5-トリメチルシクロヘ
キサン、1,3-ペンタンジアミン(1,3-ジアミノペンタン)、m-キシリレンジア
ミン、およびJeffamine(登録商標)(Texaco)が挙げられるが、これら
に限定されない。
ポリウレタンが所望される場合、連鎖延長剤はジオールである。使用することができる
そのようなジオールの例としては、エチレングリコール、1,3-プロパンジオール、1
,2-プロピレングリコール、3-メチル-1,5-ペンタンジオール、2,2-ジメチ
ル-1,3-プロパンジオール、2,2,4-トリメチル-1,5-ペンタンジオール、
2-メチル-2-エチル-1,3-プロパンジオール、1,4-ビス(ヒドロキシエトキ
シ)ベンゼン、および1,4-ブタンジオール、ヘキサンジオールおよびその混合物が挙
げられるが、これらに限定されない。
そのようなジオールの例としては、エチレングリコール、1,3-プロパンジオール、1
,2-プロピレングリコール、3-メチル-1,5-ペンタンジオール、2,2-ジメチ
ル-1,3-プロパンジオール、2,2,4-トリメチル-1,5-ペンタンジオール、
2-メチル-2-エチル-1,3-プロパンジオール、1,4-ビス(ヒドロキシエトキ
シ)ベンゼン、および1,4-ブタンジオール、ヘキサンジオールおよびその混合物が挙
げられるが、これらに限定されない。
非限定的な一実施形態では、ポリマーの分子量を制御するために、単官能性アルコール
または第一級/第二級単官能性アミンを任意選択的に含めることができる。1つ以上の単
官能性アルコールと1つ以上の単官能性アミンとのブレンドも含めることができる。本開
示で有用な単官能性アルコールの例としては、フルフリルアルコール、テトラヒドロフル
フリルアルコール、N-(2-ヒドロキシエチル)スクシンイミド、4-(2-ヒドロキ
シエチル)モルホリン、メタノール、エタノール、ブタノール、ネオペンチルアルコール
、ヘキサノール、シクロヘキサノール、シクロヘキサンメタノール、ベンジルアルコール
、オクタノール、オクタデカノール、N、N-ジエチルヒドロキシルアミン、2-(ジエ
チルアミノ)エタノール、2-ジメチルアミノエタノール、および4-ピペリジンエタノ
ール、およびそれらの組み合わせを含む、1~18個の炭素を有する脂肪族および脂環式
第一級および第二級アルコール、フェノール、置換フェノール、分子量500未満を含む
分子量750未満のエトキシ化アルキルフェノールおよびエトキシ化脂肪族アルコール、
ヒドロキシアミン、ヒドロキシメチルおよびヒドロキシエチル置換第三級アミン、ヒドロ
キシメチルおよびヒドロキシエチル置換複素環式化合物、およびそれらの組み合わせから
なる群から選択される少なくとも1つのメンバーが挙げられるが、これらに限定されない
。好適な単官能性ジアルキルアミン遮断剤の例としては、N,N-ジエチルアミン、N-
エチル-N-プロピルアミン、N,N-ジイソプロピルアミン、N-tert-ブチル-
N-メチルアミン、N-tert-ブチル-N-ベンジルアミン、N,N-ジシクロヘキ
シルアミン、N-エチル-N-イソプロピルアミン、N-tert-ブチル-N-イソプ
ロピルアミン、N-イソプロピル-N-シクロヘキシルアミン、N-エチル-N-シクロ
ヘキシルアミン、N,N-ジエタノールアミン、および2,2,6,6-テトラメチルピ
ペリジンが挙げられるが、これらに限定されない。
または第一級/第二級単官能性アミンを任意選択的に含めることができる。1つ以上の単
官能性アルコールと1つ以上の単官能性アミンとのブレンドも含めることができる。本開
示で有用な単官能性アルコールの例としては、フルフリルアルコール、テトラヒドロフル
フリルアルコール、N-(2-ヒドロキシエチル)スクシンイミド、4-(2-ヒドロキ
シエチル)モルホリン、メタノール、エタノール、ブタノール、ネオペンチルアルコール
、ヘキサノール、シクロヘキサノール、シクロヘキサンメタノール、ベンジルアルコール
、オクタノール、オクタデカノール、N、N-ジエチルヒドロキシルアミン、2-(ジエ
チルアミノ)エタノール、2-ジメチルアミノエタノール、および4-ピペリジンエタノ
ール、およびそれらの組み合わせを含む、1~18個の炭素を有する脂肪族および脂環式
第一級および第二級アルコール、フェノール、置換フェノール、分子量500未満を含む
分子量750未満のエトキシ化アルキルフェノールおよびエトキシ化脂肪族アルコール、
ヒドロキシアミン、ヒドロキシメチルおよびヒドロキシエチル置換第三級アミン、ヒドロ
キシメチルおよびヒドロキシエチル置換複素環式化合物、およびそれらの組み合わせから
なる群から選択される少なくとも1つのメンバーが挙げられるが、これらに限定されない
。好適な単官能性ジアルキルアミン遮断剤の例としては、N,N-ジエチルアミン、N-
エチル-N-プロピルアミン、N,N-ジイソプロピルアミン、N-tert-ブチル-
N-メチルアミン、N-tert-ブチル-N-ベンジルアミン、N,N-ジシクロヘキ
シルアミン、N-エチル-N-イソプロピルアミン、N-tert-ブチル-N-イソプ
ロピルアミン、N-イソプロピル-N-シクロヘキシルアミン、N-エチル-N-シクロ
ヘキシルアミン、N,N-ジエタノールアミン、および2,2,6,6-テトラメチルピ
ペリジンが挙げられるが、これらに限定されない。
非限定的な一実施形態では、本開示のポリマー溶液を合成した後、粘着防止添加剤が溶
液に組み込まれる。中に粘着防止添加剤を分散させた溶液を乾式紡糸して、本開示の弾性
繊維を形成することができる。乾式紡糸とは、ポリマー溶液を紡糸口金のオリフィスから
シャフトに押し込んでフィラメントを形成するプロセスを指す。加熱された不活性ガスが
チャンバーを通過し、フィラメントがシャフトを通過するときにフィラメントから溶媒を
蒸発させる。次いで、得られた弾性繊維を円筒形コアに巻き付けて、スパンデックス供給
パッケージを形成することができる。湿式紡糸プロセスも、ポリマー溶液のキャスティン
グおよび乾燥と同様に使用されてもよい。
液に組み込まれる。中に粘着防止添加剤を分散させた溶液を乾式紡糸して、本開示の弾性
繊維を形成することができる。乾式紡糸とは、ポリマー溶液を紡糸口金のオリフィスから
シャフトに押し込んでフィラメントを形成するプロセスを指す。加熱された不活性ガスが
チャンバーを通過し、フィラメントがシャフトを通過するときにフィラメントから溶媒を
蒸発させる。次いで、得られた弾性繊維を円筒形コアに巻き付けて、スパンデックス供給
パッケージを形成することができる。湿式紡糸プロセスも、ポリマー溶液のキャスティン
グおよび乾燥と同様に使用されてもよい。
非限定的な一実施形態では、本開示の弾性繊維は、特定の目的のために添加される追加
の従来の添加剤(複数可)をさらに含んでもよい。例としては、そのような添加剤が本開
示のスパンデックスエラストマーまたはワックス組成物と拮抗効果を生じない限り、酸化
防止剤、熱安定剤、UV安定剤、顔料および艶消し剤(例えば、二酸化チタン)、染料お
よび染料エンハンサー、潤滑剤(例えば、シリコーン油)、塩素分解に対する耐性を高め
る添加剤(例えば、酸化亜鉛、酸化マグネシウム、およびハンタイトとハイドロマグネサ
イトの混合物)などが挙げられるが、これらに限定されない。二酸化チタンなどの従来の
添加剤の中には、弾性繊維の粘着性を判断するために使用されるパラメータであるオーバ
ーエンドテイクオフ張力(OETOT)測定にわずかな効果を示すものがあるが(以下の
実施例で説明されるように)、そのいずれも、OETOT測定に目に見えるほどの効果は
なく、粘着性を減らすような量でスパンデックスに添加されることはない。
の従来の添加剤(複数可)をさらに含んでもよい。例としては、そのような添加剤が本開
示のスパンデックスエラストマーまたはワックス組成物と拮抗効果を生じない限り、酸化
防止剤、熱安定剤、UV安定剤、顔料および艶消し剤(例えば、二酸化チタン)、染料お
よび染料エンハンサー、潤滑剤(例えば、シリコーン油)、塩素分解に対する耐性を高め
る添加剤(例えば、酸化亜鉛、酸化マグネシウム、およびハンタイトとハイドロマグネサ
イトの混合物)などが挙げられるが、これらに限定されない。二酸化チタンなどの従来の
添加剤の中には、弾性繊維の粘着性を判断するために使用されるパラメータであるオーバ
ーエンドテイクオフ張力(OETOT)測定にわずかな効果を示すものがあるが(以下の
実施例で説明されるように)、そのいずれも、OETOT測定に目に見えるほどの効果は
なく、粘着性を減らすような量でスパンデックスに添加されることはない。
本開示の実施形態は、本開示の弾性繊維を含む製品を含む。これらの製品としては、布
地、衣服、および積層構造が挙げられるが、これらに限定されない。
地、衣服、および積層構造が挙げられるが、これらに限定されない。
非限定的な一実施形態では、本開示は、ポリウレタンまたはポリウレタン尿素および約
0.25重量%~4重量%のワックス組成物を含む弾性繊維を含む布地を提供する。ステ
アリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリコン油、鉱油
、およびそれらの混合物などの追加の添加剤を含めることができる。本発明の布地として
は、編物、織物、または不織布の構造を有するものが挙げられるが、これらに限定されな
い。
0.25重量%~4重量%のワックス組成物を含む弾性繊維を含む布地を提供する。ステ
アリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリコン油、鉱油
、およびそれらの混合物などの追加の添加剤を含めることができる。本発明の布地として
は、編物、織物、または不織布の構造を有するものが挙げられるが、これらに限定されな
い。
非限定的な一実施形態では、積層構造は、ポリウレタンまたはポリウレタン尿素、約0
.25重量%~4重量%のワックス組成物、およびステアリン酸カルシウム、ステアリン
酸マグネシウム、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物などの少
なくとも1つの追加の添加剤を有する本開示の弾性繊維を含む。特定の実施形態では、繊
維は、布地、不織布、フィルム、およびそれらの組み合わせなどの基材の1つ以上の層に
接着される。積層構造は、接着剤、超音波接着、熱接着、機械的接着、またはそれらの組
み合わせによって接着されてもよい。本発明の弾性繊維で形成された積層構造は、おむつ
、トレーニングパンツ、成人用失禁用品、または女性用衛生用品などの使い捨て衛生用品
に使用することができるが、これらに限定されない。
実施例
.25重量%~4重量%のワックス組成物、およびステアリン酸カルシウム、ステアリン
酸マグネシウム、有機ステアリン酸、シリコン油、鉱油、およびそれらの混合物などの少
なくとも1つの追加の添加剤を有する本開示の弾性繊維を含む。特定の実施形態では、繊
維は、布地、不織布、フィルム、およびそれらの組み合わせなどの基材の1つ以上の層に
接着される。積層構造は、接着剤、超音波接着、熱接着、機械的接着、またはそれらの組
み合わせによって接着されてもよい。本発明の弾性繊維で形成された積層構造は、おむつ
、トレーニングパンツ、成人用失禁用品、または女性用衛生用品などの使い捨て衛生用品
に使用することができるが、これらに限定されない。
実施例
本開示の実施形態を説明したが、一般に、以下の実施例は本開示のいくつかの追加の実
施形態を説明する。本開示の実施形態は以下の実施例および対応する本文および図に関連
して説明されるが、本開示の実施形態をこの説明に限定する意図はない。それどころか、
その意図は、本開示の実施形態の趣旨および範囲内に含まれるすべての代替物、修正形、
および等価物を網羅することである。
実施例1
施形態を説明する。本開示の実施形態は以下の実施例および対応する本文および図に関連
して説明されるが、本開示の実施形態をこの説明に限定する意図はない。それどころか、
その意図は、本開示の実施形態の趣旨および範囲内に含まれるすべての代替物、修正形、
および等価物を網羅することである。
実施例1
表面摩擦係数は、参照により本明細書に組み込まれる米国特許第9,487,889号
、11列57~68行および12列1~14行に記載されているとおりに決定した。46
m/分の速度と最初のロールから最後のロールまでの2.78倍のドラフトを使用して、
長さ100mにわたって5cmごとに読み取り値を収集して測定を行う。
、11列57~68行および12列1~14行に記載されているとおりに決定した。46
m/分の速度と最初のロールから最後のロールまでの2.78倍のドラフトを使用して、
長さ100mにわたって5cmごとに読み取り値を収集して測定を行う。
ワックス組成物を有する弾性繊維を、以下の合成方法に従って調製した。Ceridu
st5551、Ceridust8020、およびCeridust6050を、乾燥紡
績機で仕上げることなく、約486デニール(540デシテックス)のポリウレタン尿素
繊維に紡糸した。図1に示すように、ワックス組成物は糸の表面摩擦係数を大幅に低下さ
せた。
st5551、Ceridust8020、およびCeridust6050を、乾燥紡
績機で仕上げることなく、約486デニール(540デシテックス)のポリウレタン尿素
繊維に紡糸した。図1に示すように、ワックス組成物は糸の表面摩擦係数を大幅に低下さ
せた。
この実施例で使用されるポリマーを、分子量1800のポリテトラメチレンエーテルグ
リコールを1.69のモル比でMDIでキャッピングすることにより作製した。得られた
キャッピングされたグリコールを、エチレンジアミンと2-メチル-1,5-ペンタンジ
アミンの混合物((90/10モル比)でDMAc溶媒中で連鎖延長し、ジエチルアミン
で終端した。ワックス組成物に加えて、ポリマーには、1.4重量%のCibaから入手
可能なIrgonox酸化防止剤、0.5重量%のE.I.du Pont de Ne
mours,Incから入手可能なMethacrol 2462B UV安定剤、3.
9%のMicrofine Minerals,Ltd.から入手可能なハンチッテ/ハ
イドロマグネサイト鉱物混合物Ultracarb、96%のポリジメチルシロキサンと
4重量%ポリジアミルシロキサンからなる0.42重量%のシリコン油、0.3重量%の
E.I.du Pont de Nemours,Inc.から入手可能な二酸化チタン
艶消し剤も含まれていた。
実施例2
リコールを1.69のモル比でMDIでキャッピングすることにより作製した。得られた
キャッピングされたグリコールを、エチレンジアミンと2-メチル-1,5-ペンタンジ
アミンの混合物((90/10モル比)でDMAc溶媒中で連鎖延長し、ジエチルアミン
で終端した。ワックス組成物に加えて、ポリマーには、1.4重量%のCibaから入手
可能なIrgonox酸化防止剤、0.5重量%のE.I.du Pont de Ne
mours,Incから入手可能なMethacrol 2462B UV安定剤、3.
9%のMicrofine Minerals,Ltd.から入手可能なハンチッテ/ハ
イドロマグネサイト鉱物混合物Ultracarb、96%のポリジメチルシロキサンと
4重量%ポリジアミルシロキサンからなる0.42重量%のシリコン油、0.3重量%の
E.I.du Pont de Nemours,Inc.から入手可能な二酸化チタン
艶消し剤も含まれていた。
実施例2
オーバーエンドテイクオフ張力(OETOT)を、参照により本明細書に組み込まれる
米国特許第4,296,174号、4列20~45行、および図6に記載されているとお
りに決定した。測定は、糸の管状供給パッケージから183mの長さのスパンデックス糸
のサンプルを45.7m/分の送り速度で取り除くのに必要な平均引張荷重で行われる。
以下の実施例では、パッケージの表面とコアで測定を行った。例えば、数グラムの繊維を
取り除いて意図した巻き付けパターン(すなわち「表面」)を確立した後に測定を行い、
また、約100gを除くすべての繊維がパッケージから取り除かれた後に測定を行う(す
なわち「コア」)。
米国特許第4,296,174号、4列20~45行、および図6に記載されているとお
りに決定した。測定は、糸の管状供給パッケージから183mの長さのスパンデックス糸
のサンプルを45.7m/分の送り速度で取り除くのに必要な平均引張荷重で行われる。
以下の実施例では、パッケージの表面とコアで測定を行った。例えば、数グラムの繊維を
取り除いて意図した巻き付けパターン(すなわち「表面」)を確立した後に測定を行い、
また、約100gを除くすべての繊維がパッケージから取り除かれた後に測定を行う(す
なわち「コア」)。
ワックス組成物を有する弾性繊維を、以下の合成方法に従って調製した。Ceridu
st5551、Ceridust8020、およびCeridust6050を、乾燥紡
績機で仕上げることなく、約486デニール(540デシテックス)のポリウレタン尿素
繊維に紡糸した。図2のOETOTによって定量化されるように、ワックス組成物は糸の
粘着性を著しく減少させた。
st5551、Ceridust8020、およびCeridust6050を、乾燥紡
績機で仕上げることなく、約486デニール(540デシテックス)のポリウレタン尿素
繊維に紡糸した。図2のOETOTによって定量化されるように、ワックス組成物は糸の
粘着性を著しく減少させた。
この実施例で使用されるポリマーを、分子量1800のポリテトラメチレンエーテルグ
リコールを1.69のモル比でMDIでキャッピングすることにより作製した。得られた
キャッピングされたグリコールを、エチレンジアミンと2-メチル-1,5-ペンタンジ
アミンの混合物((90/10モル比)でDMAc溶媒中で連鎖延長し、ジエチルアミン
で終端した。ワックス組成物に加えて、ポリマーには、1.4重量%のCibaから入手
可能なIrgonox酸化防止剤、0.5重量%のE.I.du Pont de Ne
mours,Incから入手可能なMethacrol 2462B UV安定剤、3.
9%のMicrofine Minerals,Ltd.から入手可能なハンチッテ/ハ
イドロマグネサイト鉱物混合物Ultracarb、96%のポリジメチルシロキサンと
4重量%ポリジアミルシロキサンからなる0.42重量%のシリコン油、0.3重量%の
E.I.du Pont de Nemours,Inc.から入手可能な二酸化チタン
艶消し剤も含まれていた。
実施例3
リコールを1.69のモル比でMDIでキャッピングすることにより作製した。得られた
キャッピングされたグリコールを、エチレンジアミンと2-メチル-1,5-ペンタンジ
アミンの混合物((90/10モル比)でDMAc溶媒中で連鎖延長し、ジエチルアミン
で終端した。ワックス組成物に加えて、ポリマーには、1.4重量%のCibaから入手
可能なIrgonox酸化防止剤、0.5重量%のE.I.du Pont de Ne
mours,Incから入手可能なMethacrol 2462B UV安定剤、3.
9%のMicrofine Minerals,Ltd.から入手可能なハンチッテ/ハ
イドロマグネサイト鉱物混合物Ultracarb、96%のポリジメチルシロキサンと
4重量%ポリジアミルシロキサンからなる0.42重量%のシリコン油、0.3重量%の
E.I.du Pont de Nemours,Inc.から入手可能な二酸化チタン
艶消し剤も含まれていた。
実施例3
糸のクリープを、2層の不織布(通常はポリプロピレン)の間に弾性貼り付け接着剤を
使用して伸びて接着されたスパンデックス繊維からなる積層体を作製した後に決定する。
積層体を緩めて収縮させる。積層体を、不織布層が滑らかになるように引き伸ばし、次い
で端部で支持フレームに取り付ける。支持フレーム内の所定の長さのスパンデックス繊維
を測定し、マークする。個々のスパンデックス繊維の端部をマークで切断する。積層体と
支持フレームを40℃で4時間保管する。スパンデックス繊維の長さを保管後に測定する
。切断されたスパンデックスの収縮長さと所定の長さとのパーセント差を、糸のクリープ
率として報告する。
使用して伸びて接着されたスパンデックス繊維からなる積層体を作製した後に決定する。
積層体を緩めて収縮させる。積層体を、不織布層が滑らかになるように引き伸ばし、次い
で端部で支持フレームに取り付ける。支持フレーム内の所定の長さのスパンデックス繊維
を測定し、マークする。個々のスパンデックス繊維の端部をマークで切断する。積層体と
支持フレームを40℃で4時間保管する。スパンデックス繊維の長さを保管後に測定する
。切断されたスパンデックスの収縮長さと所定の長さとのパーセント差を、糸のクリープ
率として報告する。
図3は、糸のクリープ率がすべてのサンプルと対照繊維で非常に似ているため、繊維に
ワックスを添加してもスパンデックス繊維の接着性が低下しないことを示している。
ワックスを添加してもスパンデックス繊維の接着性が低下しないことを示している。
本明細書では、比率、濃度、量、および他の数値データは、範囲形式で表現され得るこ
とに留意されたい。そのような範囲形式は、便宜のためおよび簡潔さのために使用されて
おり、したがって範囲の限界として明示的に列挙された数値だけでなく、あたかも各数値
とサブ範囲が明示的に列挙されているかのように、その範囲内に包含されるすべての個々
の数値またはサブ範囲も含むように柔軟に解釈されるべきであることを理解されたい。例
示すると、「約0.1%~約5%」の濃度範囲は、明示的に列挙された約0.1重量%~
約5重量%の濃度だけでなく、個々の濃度(例えば、1%、2%、3%、および4%)な
らびに示された範囲内のサブ範囲(例えば、0.5%、1.1%、2.2%、3.3%、
および4.4%)も含むように解釈されるべきである。「約」という用語は、修正される
数値(複数)の±1%、±2%、±3%、±4%、±5%、±8%、または±10%を含
むことができる。さらに、「約「x」~「y」」という句は、「約「x」~約「y」」を
含む。
とに留意されたい。そのような範囲形式は、便宜のためおよび簡潔さのために使用されて
おり、したがって範囲の限界として明示的に列挙された数値だけでなく、あたかも各数値
とサブ範囲が明示的に列挙されているかのように、その範囲内に包含されるすべての個々
の数値またはサブ範囲も含むように柔軟に解釈されるべきであることを理解されたい。例
示すると、「約0.1%~約5%」の濃度範囲は、明示的に列挙された約0.1重量%~
約5重量%の濃度だけでなく、個々の濃度(例えば、1%、2%、3%、および4%)な
らびに示された範囲内のサブ範囲(例えば、0.5%、1.1%、2.2%、3.3%、
および4.4%)も含むように解釈されるべきである。「約」という用語は、修正される
数値(複数)の±1%、±2%、±3%、±4%、±5%、±8%、または±10%を含
むことができる。さらに、「約「x」~「y」」という句は、「約「x」~約「y」」を
含む。
上記の実施形態に対して多くの変形および修正を行うことができる。そのような修正お
よび変形はすべて、本明細書において本開示の範囲内に含まれ、添付の特許請求の範囲に
よって保護されることを意図している。
よび変形はすべて、本明細書において本開示の範囲内に含まれ、添付の特許請求の範囲に
よって保護されることを意図している。
Claims (33)
- ポリウレタンまたはポリウレタン尿素および約0.5重量%~4重量%のワックス組成
物を含む弾性繊維。 - 前記ワックス組成物はポリオレフィンワックスを含む、請求項1に記載の弾性繊維。
- 前記ワックス組成物は、無水マレイン酸を含むC24~C36ポリマーを含む変性ポリ
マーワックスを含む、請求項1に記載の弾性繊維。 - 前記ワックス組成物は、モンタンワックス酸のエステルを含む、請求項1に記載の弾性
繊維。 - ステアリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリン酸、シリコン油
、鉱油、およびそれらの混合物からなる群から選択される少なくとも1つの追加の添加剤
をさらに含む、請求項1または2に記載の弾性繊維。 - 前記ポリオレフィンワックスは、微粉化されたメタロセンベースのポリプロピレンワッ
クスである、請求項2に記載の弾性繊維。 - 前記ポリオレフィンワックスは、微粉化されたポリエチレンワックスである、請求項2
に記載の弾性繊維。 - 少なくとも1つの粒子状粘着防止剤をさらに含む、請求項1に記載の弾性繊維。
- 前記繊維は、紡績仕上げ剤を除外する、請求項1に記載の弾性繊維。
- 局所適用された鉱油もしくはシリコン油、または適用後の最終繊維の約0.5重量%~
2.0重量%の量の紡糸仕上げ剤としての鉱油もしくはシリコン油を含むブレンドをさら
に含む、請求項1に記載の弾性繊維。 - 弾性繊維を調製するためのプロセスであって、
(a)少なくとも1つのポリウレタン、ポリウレタン尿素、またはそれらの混合物を含
む組成物を調製することと、
(b)前記組成物に約0.25重量%~4重量%のワックス組成物を添加することと、
(c)前記組成物に、ステアリン酸カルシウム、ステアリン酸マグネシウム、有機ステ
アリン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択される少なくと
も1つの添加物を添加することと、
(d)湿式紡糸、乾式紡糸、および溶融紡糸からなる群から選択される紡糸プロセスに
よって前記組成物から繊維を調製することと、を含む、プロセス。 - 前記ワックス組成物は、ポリオレフィンワックスを含む、請求項11に記載のプロセス
。 - 前記ポリオレフィンワックスは、微粉化されたメタロセンベースのポリプロピレンワッ
クスである、請求項11に記載のプロセス。 - 前記ポリオレフィンワックスは、微粉化されたポリエチレンワックスである、請求項1
1に記載のプロセス。 - 前記ワックス組成物は、無水マレイン酸を含むC24~C36ポリマーを含む変性ポリ
マーワックスを含む、請求項11に記載のプロセス。 - 前記ワックス組成物は、モンタンワックス酸のエステルを含む、請求項11に記載のプ
ロセス。 - ポリウレタンまたはポリウレタン尿素および約0.25重量%~4重量%のワックス組
成物を含む弾性繊維を含む、布地。 - 前記ワックス組成物は、ポリオレフィンワックスを含む、請求項17に記載の布地。
- 前記ポリオレフィンワックスは、微粉化されたメタロセンベースのポリプロピレンワッ
クスである、請求項17に記載の布地。 - 前記ポリオレフィンワックスは、微粉化されたポリエチレンワックスである、請求項1
7に記載の布地。 - 前記弾性繊維は、ステアリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリ
ン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択される少なくとも1
つの追加の添加剤をさらに含む、請求項17に記載の布地。 - 前記布地は、編物、織物、または不織布の構造を含む、請求項17~21のいずれか一
項に記載の布地。 - 請求項17~21のいずれか一項に記載の布地を含む、衣服。
- 積層体構造であって、
ポリウレタンまたはポリウレタン尿素と、約0.25重量%~4重量%のワックス組成
物と、を含む、弾性繊維を含み、
前記繊維は、布地、不織布、フィルム、およびそれらの組み合わせからなる群から選択
される基材の1つ以上の層に接着されている、積層体構造。 - 前記ワックス組成物は、ポリオレフィンワックスを含む、請求項24に記載の積層体。
- 前記ポリオレフィンワックスは、微粉化されたメタロセンベースのポリプロピレンワッ
クスである、請求項24に記載の積層体。 - 前記ワックス組成物は、無水マレイン酸を含むC24~C36ポリマーを含む変性ポリ
マーワックスを含む、請求項24に記載の積層体。 - 前記ワックス組成物は、モンタンワックス酸のエステルを含む、請求項24に記載の積
層体。 - 前記ポリオレフィンワックスは、微粉化されたポリエチレンワックスである、請求項2
4に記載の積層体。 - 前記弾性繊維は、ステアリン酸カルシウム、ステアリン酸マグネシウム、有機ステアリ
ン酸、シリコン油、鉱油、およびそれらの混合物からなる群から選択される少なくとも1
つの追加の添加剤をさらに含む、請求項24~29のいずれか一項に記載の積層体。 - 前記積層体は、接着剤、超音波接着、熱接着、機械的接着、またはそれらの組み合わ
せにより接着される、請求項24~29のいずれか一項に記載の積層体。 - 使い捨て衛生用品を含む、請求項24~31のいずれか一項に記載の積層体を含む使い
捨て衛生用品。 - おむつ、トレーニングパンツ、成人用失禁用品、および女性用衛生用品からなる群から
選択される、請求項32に記載の使い捨て衛生用品。