JP2023065146A - Production method of cobalt sulfate - Google Patents

Abstract

To provide a production method of a highly pure cobalt sulfate from a cobalt chloride solution containing impurities without using an electrolysis process.SOLUTION: A production method of obtaining cobalt sulfate by removing impurities from a cobalt chloride solution containing one or more kinds of impurities of copper, zinc, manganese, calcium, and magnesium includes: (1) a prestage step including a copper removal step S1 of adding a sulfating agent to a cobalt chloride solution to generate, separate and remove a precipitation of a sulfide of copper, and a first solvent extraction step S2 of bringing a cobalt chloride solution into contact with an organic solvent containing alkylphosphoric acid-based extractant to extract into the organic solvent, thereby, separating and removing zinc, manganese, and calcium; and (2) a poststage step including a second solvent extraction step S3 of bringing the cobalt chloride solution after the prestage step into contact with an organic solvent containing strait-chain carboxylic acid, and thereafter subjecting to back-extraction with sulfuric acid to obtain a cobalt sulfate solution.SELECTED DRAWING: Figure 1

Description

The present invention relates to a method for producing cobalt sulfate. More particularly, it relates to a production method for obtaining high-purity cobalt sulfate by removing impurity elements contained in a cobalt chloride solution.

Cobalt is a valuable metal that is widely used in industrial applications as a raw material for magnetic materials and lithium-ion secondary batteries, in addition to being used as an additive element in special alloys. In particular, recently, lithium ion secondary batteries have been widely used as batteries for mobile devices and electric vehicles, and along with this, the demand for cobalt is rapidly expanding. However, most of cobalt is produced as a by-product of nickel smelting and copper smelting, so separation from impurities such as nickel and copper is an important elemental technology in cobalt production. .

For example, when recovering cobalt as a by-product in nickel hydrometallurgy, first, in order to obtain a solution containing nickel and cobalt, the raw material is leached or extracted into a solution using a mineral acid or an oxidizing agent, or is subjected to a dissolution treatment. attached. Furthermore, nickel and cobalt contained in the obtained acidic solution are often separated and recovered by a conventionally known method by solvent extraction using various organic extractants.
However, the obtained cobalt solution often contains various impurities derived from the processing raw material.

Therefore, it is necessary to further remove impurity elements such as manganese, copper, zinc, calcium and magnesium from the cobalt solution after nickel has been separated and recovered by the solvent extraction method.
Moreover, in order to produce a high-purity cobalt product with a low impurity content, it is necessary to remove the impurity elements from the cobalt solution that has been separated and recovered from the cobalt-containing nickel solution in advance, and then remove the cobalt by electrolysis or crystallization. It had to be produced.

Patent Documents 1 and 2 disclose conventional techniques for removing impurity elements in a cobalt solution.
Patent Document 1 describes (1) adding a sulfiding agent to a cobalt solution, adjusting the oxidation-reduction potential (ORP) (based on Ag/AgCl electrode) to 50 mV or less and pH to 0.3 to 2.4, and sulfiding (2) adding an oxidizing agent and a neutralizing agent to the copper-removing purification solution, and increasing the oxidation-reduction potential (based on Ag/AgCl electrode) to 950 to 1050 mV and the pH; 2.4 to 3.0 to obtain a manganese precipitate and a demanganized purified liquid; A method for purifying a cobalt solution is disclosed that includes a solvent extraction step to extract zinc, calcium and trace impurities.
In Patent Document 2, a cobalt chloride solution with a hydrochloric acid concentration of 2 to 6 mol/L is brought into contact with an anion exchange resin, and iron and zinc that form a complex having a partition coefficient with respect to the anion exchange resin greater than that of the cobalt chloride complex. , a technique of adsorbing and separating metal impurities such as tin.

The solvent extraction method using alkyl phosphoric acid as an extractant described in Patent Document 1 has high separation performance for zinc and calcium. However, in the case of a cobalt chloride solution with a hydrochloric acid concentration of 2 to 6 mol/L, the ion exchange method using an anion exchange resin and the solvent extraction method using an amine-based extractant are better than the solvent extraction method using the above-mentioned alkyl phosphoric acid. It has higher zinc and cobalt separation performance.
Further, when removing a very small amount of zinc in a cobalt chloride solution, the ion exchange method is more efficient and economical because the steps and operations are simpler.

From this point of view, as a method for removing these impurity elements from a cobalt chloride solution containing manganese, copper, and zinc, a method combining the purification method of Patent Document 1 and the separation technology of Patent Document 2 has been proposed. (For example, Patent Document 3).
The method for producing high-purity cobalt chloride described in paragraph 0022 of Patent Document 3 includes a solvent extraction step for separating nickel and cobalt, a demanganization step for removing manganese, a decoppering step for removing copper, and a dezincing step for removing zinc. and electrolysis steps.
In the dezincification step, the cobalt chloride aqueous solution obtained in the decopperization step is brought into contact with an anion exchange resin to adsorb and remove zinc. In the electrolysis step, the high-purity cobalt chloride aqueous solution obtained in the dezincification step is used as an electrolysis supply liquid to produce metallic cobalt (also called electrolytic cobalt).

On the other hand, as described above, the demand for cobalt as a raw material for lithium ion secondary batteries has increased recently, and cobalt sulfate solutions or cobalt sulfate crystals are desired.
In order to obtain cobalt sulfate crystals from metallic cobalt obtained by the prior art of Patent Document 3, the metallic cobalt is dissolved in sulfuric acid to obtain a cobalt sulfate solution, and this solution is further crystallized to obtain cobalt sulfate crystals. Obtainable. However, when this manufacturing method is used, manufacturing costs increase due to an increase in the number of steps and an increase in the cost of chemicals. In addition, plate-like metallic cobalt has a slow dissolution rate in sulfuric acid as it is used in corrosion-resistant alloys, and in order to dissolve it in a short time, it is necessary to powderize the plate-like metallic cobalt by atomizing treatment or the like. .
Therefore, there has been a demand for a method of directly obtaining a cobalt sulfate solution from a cobalt chloride solution without going through metallic cobalt.

JP-A-2004-285368 Japanese Patent Application Laid-Open No. 2001-020021 JP 2020-19664 A

The present invention has been proposed in view of the above circumstances, and provides a method for producing cobalt sulfate of high purity by separating impurities and cobalt from a cobalt chloride solution containing impurities without using an electrolysis step. With the goal.

A method for producing cobalt sulfate according to a first aspect of the present invention is a method for producing cobalt sulfate by removing impurities from a cobalt chloride solution containing one or more impurities of copper, zinc, manganese, calcium and magnesium, comprising: is a decoppering step in which a sulfiding agent is added to the cobalt chloride solution to form a precipitate of copper sulfide to be separated and removed; It includes a first solvent extraction step in which zinc, manganese and calcium are extracted into an organic solvent and separated and removed. It is characterized by comprising a second solvent extraction step of contacting a solvent to extract cobalt with the organic solvent, and then back-extracting the cobalt with sulfuric acid to obtain a cobalt sulfate solution.
A method for producing cobalt sulfate according to a second aspect of the invention is characterized in that, in the first aspect of the invention, the preceding step is performed in the order of the decoppering step and the first solvent extraction step.
A method for producing cobalt sulfate according to a third aspect of the invention is characterized in that, in the first aspect of the invention, the first stage step is performed in the order of the first solvent extraction step and the copper removal step.
A fourth aspect of the invention is a method for producing cobalt sulfate, which is characterized in that, in the first aspect, the cobalt sulfate solution obtained through the second solvent extraction step is subjected to a crystallization step to obtain crystals of cobalt sulfate.
A method for producing cobalt sulfate according to a fifth aspect of the invention is characterized in that, in the first, second or third aspect of the invention, in the decoppering step, an oxidizing agent and a neutralizing agent are added to a cobalt chloride solution to which a sulfiding agent has been added to obtain an oxidation-reduction potential. is adjusted to −100 to 200 mV (Ag/AgCl electrode reference), and the pH is adjusted to 1.3 to 3.0.
A sixth aspect of the invention is a method for producing cobalt sulfate, wherein the alkyl phosphate-based extractant in the first solvent extraction step is bis(2-ethylhexyl) hydrogen phosphate in the first, second, or third aspect of the invention; The pH of the cobalt solution is adjusted to 1.5 to 3.0 and subjected to solvent extraction using the extractant to extract the impurity elements into the organic solvent.
A method for producing cobalt sulfate according to a seventh invention is the method according to the first, second or third invention, wherein in the second solvent extraction step, an alkaline solution is added to the cobalt chloride solution from which copper, zinc, manganese and calcium have been removed. Then, the pH is adjusted to 4.0 to 7.0, and an extraction step is performed in which cobalt is extracted into an organic solvent using a carboxylic acid-based extractant.
A method for producing cobalt sulfate according to an eighth aspect of the invention is the method according to the seventh aspect, wherein following the extraction step in the second solvent extraction step, the organic solvent from which cobalt has been extracted is brought into contact with a sulfuric acid solution to adjust the pH to 2.0 to 2.0. 4.5 and performing a back-extraction step of back-extracting the cobalt into a sulfuric acid solution.

According to the first invention, copper, zinc, manganese, and calcium can be removed from the cobalt chloride solution containing impurities by the decoppering step and the first solvent extraction step included in the former step, and the second solvent extraction included in the latter step. Magnesium can be removed by the process. Therefore, high-purity cobalt sulfate can be produced without using an electrolytic process.
According to the second invention, copper, zinc, manganese, and calcium can be separated and removed from the cobalt chloride solution containing impurities by performing the decoppering step and the first solvent extraction step in that order, so that the second solvent extraction can be performed. A high-purity cobalt sulfate solution from which impurities are removed can be obtained by separating and removing magnesium in the process.
According to the third invention, copper, zinc, manganese, and calcium can be separated and removed from the cobalt chloride solution containing impurities by performing the first solvent extraction step and the copper removal step in that order, so that the second solvent extraction can be performed. A high-purity cobalt sulfate solution from which impurities are removed can be obtained by separating and removing magnesium in the process.
According to the fourth invention, high-purity cobalt sulfate crystals can be obtained from the cobalt sulfate solution by further performing the crystallization step.
According to the fifth invention, by adjusting the oxidation-reduction potential and pH to appropriate ranges, copper sulfide can be precipitated and sufficiently removed from the cobalt chloride solution, and co-precipitation of cobalt can be suppressed.
According to the sixth invention, by adjusting the pH to 1.5 to 3.0, zinc, manganese and calcium can be extracted and separated from cobalt while cobalt remains in the aqueous phase.
According to the seventh invention, even if the pH is adjusted to the low pH side of 4.0 to 7.0, cobalt can be extracted by bringing it into contact with an organic solvent containing a carboxylic acid-based extractant. In addition, since extraction can be performed at a low pH, precipitates such as hydroxides are less likely to occur, and as a result, crud is less likely to form, resulting in stable operation.
According to the eighth invention, the cobalt extracted in the organic phase is brought into contact with the sulfuric acid solution to adjust the pH to 2.0 to 4.5, whereby the cobalt can be back-extracted into the sulfuric acid solution. A high-purity cobalt sulfate solution is thus obtained.

1 is a principle diagram of a method for producing cobalt sulfate according to the present invention; FIG. BRIEF DESCRIPTION OF THE DRAWINGS It is process drawing which shows the manufacturing method of cobalt sulfate which concerns on 1st Embodiment of this invention. 3 is a detailed process diagram showing a method for producing cobalt sulfate shown in FIG. 2. FIG. FIG. 4 is a detailed process diagram of a first solvent extraction step S2 shown in FIG. 3; FIG. 4 is a detailed process diagram of a second solvent extraction step S3 shown in FIG. 3; It is process drawing which shows the manufacturing method of the cobalt sulfate which concerns on 2nd Embodiment of this invention. 7 is a detailed process diagram showing a method for producing cobalt sulfate shown in FIG. 6. FIG. FIG. 8 is a detailed process diagram of a first solvent extraction step S2 shown in FIG. 7; FIG. 8 is a detailed process diagram of a second solvent extraction step S3 shown in FIG. 7;

Specific embodiments of the present invention will be described in detail below. In addition, the present invention is not limited to the following embodiments, and various modifications are possible without changing the gist of the present invention.

(Basic principle of the present invention)
The basic principle of the method for producing cobalt sulfate according to the present invention will be described with reference to FIG.
The present invention provides a production method for obtaining cobalt sulfate by removing impurities from a cobalt chloride solution containing one or more impurities of copper, zinc, manganese, calcium and magnesium, comprising:
(1) The former step includes a decoppering step S1 in which a sulfiding agent is added to the cobalt chloride solution to form a precipitate of copper sulfide to separate and remove it, and an organic A first solvent extraction step S2 of contacting a solvent and extracting zinc, manganese and calcium into the organic solvent to separate and remove them,
(2) In the latter step, the cobalt chloride solution that has undergone the preceding step is brought into contact with an organic solvent containing a carboxylic acid-based extractant having a linear structure to extract cobalt with the organic solvent, and then the cobalt is back-extracted with sulfuric acid. and a second solvent extraction step S3 for obtaining a cobalt sulfate solution.
The preceding step may be performed in the order of the copper removal step S1 and the first solvent extraction step S2, or may be performed in the order of the first solvent extraction step S2 and the copper removal step S1. . The second solvent extraction step S3 included in the latter step is performed after the former step.

In the present invention, a crystallization step S4 of precipitating crystals from a cobalt sulfate solution is carried out as necessary after each of the steps S1 to S3. By performing the crystallization step S4, crystals can be precipitated from the solution to obtain cobalt sulfate crystals.

In the present invention, after the first solvent extraction step S2 and/or after the second solvent extraction step S3, the step of subjecting the liquid to an oil-water separator such as an activated carbon column in order to separate and remove organic components mixed in the liquid. may be added.

The cobalt chloride solution used as a starting material in the present invention contains one or more of copper, zinc, manganese, calcium and magnesium as impurity elements. The application of the present invention is not limited at all as long as the cobalt chloride solution contains such impurities. It is preferably applied to a cobalt chloride solution after nickel has been separated and recovered by an amine-based extractant.

According to the present invention, copper is removed from the cobalt chloride solution by producing copper sulfide precipitates in the decoppering step S1, zinc, manganese and calcium are separated and removed in the first solvent extraction step S2, and the second solvent is A high-purity cobalt sulfate solution can be obtained by separating and removing magnesium in the extraction step S3. Therefore, a high-purity cobalt sulfate solution can be directly produced by separating impurities and cobalt without using an electrolytic process.

(First embodiment)
A first embodiment of a method for producing cobalt sulfate will be described with reference to FIGS. 2 to 5. FIG. FIG. 2 is a diagram showing all the steps in the first embodiment, and FIG. 3 shows details of each step S1 to S3 shown in FIG.
In the first embodiment, as shown in FIG. 2, the copper removal step S1 and then the first solvent extraction step S2 are performed in the order of the former steps.

(Decopper step S1)
The copper removal step S1 will be explained based on FIG.
The copper removal step S1 is performed by adding a sulfiding agent to a cobalt chloride solution containing one or more impurities of copper, zinc, manganese, calcium and magnesium, which are starting materials. Also, an oxidizing agent and a neutralizing agent are added to adjust the oxidation-reduction potential of the cobalt chloride solution to −100 to 200 mV (based on Ag/AgCl electrode) and the pH to 1.3 to 3.0.
By this step, a precipitate of copper sulfide is generated and separated from the cobalt chloride solution, and a cobalt chloride solution from which copper has been removed can be obtained.

Copper in the cobalt chloride solution is removed from the solution by forming a precipitate of copper sulfide according to Equation 1, Equation 2 or Equation 3 below.
CuCl ₂ +H ₂ S→CuS↓+2HCl (Formula 1)
CuCl ₂ +Na ₂ S→CuS↓+2NaCl (Formula 2)
CuCl ₂ +NaHS→CuS↓+NaCl+HCl (Formula 3)

In the decoppering step S1, the oxidation-reduction potential of the cobalt chloride solution is adjusted to −100 to 200 mV (based on Ag/AgCl electrode) and the pH is adjusted to 1.3 to 3.0. It can be sufficiently removed and, moreover, the co-precipitation of cobalt can be suppressed.
If the oxidation-reduction potential exceeds 200 mV, the removal of copper in the solution becomes insufficient, and if the oxidation-reduction potential is less than -100 mV, the amount of co-precipitation of cobalt increases, which is not preferable. On the other hand, if the pH is less than 1.3, the removal of copper in the solution becomes insufficient, and the filterability of the sulfide precipitate that forms deteriorates. If the pH exceeds 3.0, the amount of cobalt co-precipitation increases due to the removal of copper, which is not preferable.

The oxidation-reduction potential can be adjusted by adjusting the amount of the sulfiding agent added. The sulfiding agent is not particularly limited, but hydrogen sulfide gas, crystals or aqueous solutions of sodium sulfide or sodium hydrosulfide can be used.
When hydrogen sulfide or sodium hydrosulfide is used as the sulfiding agent, the pH is adjusted by adjusting the addition amount of the sulfiding agent and adding a neutralizing agent. The neutralizing agent is not particularly limited, and alkali salts such as sodium hydroxide, calcium hydroxide, sodium carbonate and cobalt carbonate can be used. Moreover, when the oxidation-reduction potential becomes lower than the desired value due to the introduction of the sulfurizing agent, it can be adjusted by adding the oxidizing agent. For example, it can be adjusted by introducing air into the solution and stirring it, or by adding a hydrogen peroxide solution.

(First solvent extraction step S2)
1st solvent extraction process S2 is demonstrated based on FIG.3 and FIG.4.
In the first solvent extraction step S2, the cobalt chloride solution that has undergone the copper removal step S1 is brought into contact with an organic solvent containing an alkyl phosphate-based extractant, and zinc, manganese, and calcium are extracted from the organic solvent and separated and removed. is.

As the organic solvent, an alkyl phosphate-based extractant diluted with a diluent is used. As alkyl phosphate-based extractants, bis(2-ethylhexyl) hydrogen phosphate (trade name D2EHPA), (2-ethylhexyl) 2-ethylhexyl phosphonate (trade name PC-88A), di(2,4,4-trimethyl) pentyl)phosphinic acid (trade name CYANEX272). Among these, bis(2-ethylhexyl) hydrogen phosphate is preferably used as an extractant because it is highly separable from cobalt when zinc, manganese and calcium are separated from a cobalt chloride solution from which copper has been removed.

The diluent is not particularly limited as long as it can dissolve the extractant. As a diluent, for example, a naphthenic solvent or an aromatic solvent can be used. The concentration of the extractant is preferably adjusted to 10-60% by volume, more preferably 20-50% by volume. When the concentration of the extracting agent is within this range, both high-concentration impurity elements and low distribution ratios (concentration of element in organic substance/concentration of element in solution) can be sufficiently extracted. On the other hand, if the concentration of the extracting agent is less than 10%, impurity elements with high concentrations and impurity elements with low distribution ratios cannot be sufficiently extracted and tend to remain in the cobalt chloride solution. On the other hand, when the concentration of the extractant exceeds 60%, the viscosity of the organic solvent increases, and the phase separation between the organic solvent (organic phase) and the cobalt chloride solution (aqueous phase) deteriorates after the extraction operation.

An acidic extractant such as an alkyl phosphate-based extractant extracts metal ions by replacing the -H of the extractant with cations in the aqueous phase to form a metal salt, as shown in Equation 4. It is an extractant that In general, the higher the pH, the easier it is for metal ions to be extracted into the organic phase, and the lower the pH, the more the reaction of formula 4 proceeds in the opposite direction, and the more likely it is that the metal ions extracted into the organic phase will be back-extracted into the aqueous phase. .
Since the extracted pH differs depending on the type of metal ion, the target element and the impurity element are separated by controlling the pH in the solvent extraction step using an acidic extractant.
nRH _org + M ^{n +} _aq → MR _norg + nH ⁺ _aq (equation 4)
In the formula, RH is an acidic extractant, Mn ⁺ is an n-valent metal ion, org is an organic phase, and aq is an aqueous phase.

Therefore, in the first solvent extraction step S2, it is desirable to adjust the pH of the cobalt chloride solution from which copper has been removed to 1.5 to 3.0. In this pH range, the extractability of zinc, manganese and calcium tends to be higher than that of cobalt, leaving cobalt in the aqueous phase and extracting these impurity elements into the organic phase to separate them from cobalt. It is possible.
If the pH is less than 1.5, the extraction rate of these impurities is low, making it difficult to separate them from cobalt. . When the pH is adjusted to 1.5 to 3.0, some of the cobalt may be extracted, but the organic phase after the extraction is brought into contact with a hydrochloric acid solution having a pH lower than that of the extraction to back-extract the cobalt. Cobalt loss can also be reduced.
Furthermore, when this organic phase is brought into contact with an acidic solution having a pH of 1 or less, most of the extracted metal ions can be back-extracted into the aqueous phase, and the organic phase after back-extraction can be reused.

(Second solvent extraction step S3)
The second solvent extraction step S3 will be described based on FIGS. 3 and 5. FIG.
In the second solvent extraction step S3, the cobalt chloride solution that has undergone the first solvent extraction step is brought into contact with an organic solvent containing a carboxylic acid-based extractant having a linear structure to extract cobalt with the organic solvent, followed by sulfuric acid. It is a step of back-extracting cobalt to obtain a cobalt sulfate solution.

As the organic solvent, a straight-chain carboxylic acid-based extractant diluted with a diluent is used. Carboxylic acid-based extractants include versatic acid, naphthenic acid, and the like, which have branched structures. In the present invention, linear structures ("linear ”) is used as an extractant.
Carboxylic acids with a straight chain structure can be extracted with cobalt at a lower pH than versatic acids with a branched structure. It is possible to avoid unfavorable situations in operation such as crud formation. Therefore, there is an advantage that the operation is stable.

In general, when extracting metal ions, a carboxylic acid-based extractant releases protons corresponding to the valence of the metal into the aqueous phase, and the metal ions are coordinated to carbonyl oxygen. Many carboxylic acids form dimers and trimers with each other through hydrogen bonding in nonpolar solvents. In addition, when extracting metal ions, carboxylic acids that are not acid-dissociated may be coordinated so as to remove water of hydration that is coordinated to the metal ions. For example, a reaction in which a hexacoordinated divalent metal ion M ²⁺ is extracted by a dimeric carboxylic acid-based extractant R ₂ H ₂ is represented by Equation 5.
_[ M( _H2O ) ₆ ] ²⁺ _aq +3( _R2H2 ) _org
→ (MR ₂ ·4RH) _org +2H ⁺ _aq +6H ₂ O _aq (Formula 5)
Here, org in the formula indicates an organic phase and aq indicates an aqueous phase.

(Extraction process)
In the second solvent extraction step S3, an alkaline solution is added as a neutralizing agent to the cobalt chloride solution from which copper, zinc, manganese and calcium have been removed to adjust the pH to 4.0 to 7.0.
In the case of the extractant of the present invention, as described above, there is an advantage that extraction can be performed at a pH lower than that of the conventional one. On the other hand, since the solubility is slightly high, there is also a demerit that the concentration of TOC (total organic carbon) in the aqueous phase obtained by solvent extraction increases. Specifically, when octanoic acid is 1%, TOC increases by 5 mg/L, and when 30%, the TOC increases by 150 mg/L, so the load on COD (Chemical Oxygen Demand) treatment in wastewater treatment increases accordingly. However, even with the above disadvantages, extraction at a low pH has the great advantage of avoiding crud formation and stabilizing the operation.

In the present invention, since the pH is adjusted to the above range, the cobalt can be extracted into the organic phase by bringing it into contact with an organic solvent containing a straight-chain carboxylic acid-based extractant. At this time, magnesium is not extracted and remains in the aqueous phase. If the pH is less than 4, extraction of cobalt is difficult, while if the pH exceeds 7, the solubility of cobalt decreases and precipitation may occur.

As the alkaline solution, specifically, a solution of sodium hydroxide or potassium hydroxide can be used.
In order to prevent oxidation during extraction, bubbling may be performed using an inert gas such as nitrogen gas, argon gas, or carbon dioxide gas.

(Reverse extraction process)
After the extraction step, the extracted cobalt and sulfuric acid solution are brought into contact with the organic phase to adjust the pH to 2.0-4.5. This allows the cobalt to be back-extracted into the sulfuric acid solution. A high-purity cobalt sulfate solution is thus obtained.
Back-extraction is possible even if the pH is less than 2, but this is not preferable because the amount of back-extraction of trace impurities extracted at a pH lower than that of cobalt increases. On the other hand, if the pH exceeds 4.5, the reverse extraction rate of cobalt decreases, and the recovery amount of cobalt decreases, which is not preferable.

Since fine water phases are mixed in the organic phase after extraction even after phase separation, a washing step may be added to remove the water phases before back extraction. For example, a cobalt sulfate solution can be used for the aqueous phase of the washing step. In addition, the organic phase after back extraction can be reused as the organic phase in the extraction process.
A high-purity cobalt sulfate solution containing few impurities can be produced by the above method.

(Crystallization step S4)
The crystallization step S4 will be explained based on FIG.
In the crystallization step S4, crystals of cobalt sulfate are precipitated from the cobalt sulfate solution obtained in the second solvent extraction step S3. A crystallization method is not particularly limited, and a general crystallization method can be used.

For example, a method of obtaining crystals by placing a cobalt sulfate solution in a crystallizer and crystallizing in the crystallizer can be used. The crystallizer deposits crystals by evaporating water in the cobalt sulfate solution under a predetermined pressure. For example, a rotary evaporator or a double propeller type crystallizer is used. The internal pressure is reduced by a vacuum pump or the like, and crystallization proceeds while rotating the flask with a rotary evaporator and stirring with a double propeller. In the crystallizer, the cobalt sulfate solution is mixed with cobalt sulfate crystals to form a slurry.

The slurry discharged from the crystallizer is subjected to solid-liquid separation into cobalt sulfate crystals and a mother liquor by a filter, a centrifugal separator, or the like. After that, the cobalt sulfate crystals are dried in a dryer to remove water.
Cobalt sulfate crystals can be produced from a cobalt sulfate solution in the manner described above. Of course, since the cobalt sulfate solution contains few impurities and is of high purity, the obtained cobalt sulfate crystals are also of high purity with few impurities.

(Second embodiment)
A second embodiment of the method for producing cobalt sulfate will be described with reference to FIGS. 6 to 9. FIG.
FIG. 6 is a diagram showing all the steps in the second embodiment, and FIG. 7 shows details of each step S2, S1, and S3 shown in FIG.
In the second embodiment, as shown in FIG. 6, the first solvent extraction step S2 and then the copper removal step S1 are performed in the order of the former steps.

(First solvent extraction step S2)
1st solvent extraction process S2 is demonstrated based on FIG.7 and FIG.8.
In the first solvent extraction step S2, a cobalt chloride solution containing one or more impurities of copper, zinc, manganese, calcium and magnesium, which is a starting material, is brought into contact with an organic solvent containing an alkyl phosphate-based extractant, and the organic solvent is This is the process of extracting and separating and removing zinc, manganese and calcium. Note that part of the copper can also be extracted and separated and removed.

The alkyl phosphate-based extractant as the organic solvent may be the same as that used in the first embodiment, and the diluent may also be the same as in the first embodiment. In addition, including the adjustment range of pH, the execution of this step S2 is performed in the same manner as in the first embodiment.

In this first solvent extraction step S2, when the pH of the cobalt chloride solution is adjusted to 1.5 to 3.0, the extraction rates of zinc, manganese and calcium tend to be higher than the extraction rates of cobalt, and cobalt is extracted from the aqueous phase. These impurity elements can be separated from cobalt by leaving them in the organic phase and extracting them into the organic phase. When the pH is adjusted to 1.5 to 3.0, some of the cobalt may be extracted, but the organic phase after the extraction is brought into contact with a hydrochloric acid solution having a pH lower than that of the extraction to back-extract the cobalt. Cobalt loss can also be reduced.

(Decopper step S1)
The copper removal step S1 will be described with reference to FIG.
The copper removal step S1 is performed by adding a sulfiding agent to the cobalt chloride solution that has passed through the first solvent extraction step S2. Also, an oxidizing agent and a neutralizing agent are added to adjust the oxidation-reduction potential of the cobalt chloride solution to −100 to 200 mV (based on Ag/AgCl electrode) and the pH to 1.3 to 3.0.
By this step S1, a precipitate of copper sulfide is generated and separated from the cobalt chloride solution, and a cobalt chloride solution from which copper has been removed can be obtained.

The method for adjusting the oxidation-reduction potential and the method for adjusting the pH may be the same as in the first embodiment, and the sulfiding agent used in the first embodiment may be used.
By carrying out this step, copper sulfide precipitates can be obtained according to formula (1), formula (2) or formula (3) shown in the first embodiment, and copper can be removed from the solution.

(Second solvent extraction step S3)
The second solvent extraction step S3 will be explained based on FIGS. 7 and 9. FIG.
In the second solvent extraction step S3, the cobalt chloride solution that has undergone the first solvent extraction step S2 and the copper removal step S1 is brought into contact with an organic solvent containing a linear carboxylic acid extractant, and cobalt is extracted into the organic solvent. Then, the cobalt is back-extracted with sulfuric acid to obtain a cobalt sulfate solution.

For the carboxylic acid-based extractant as the organic solvent, a straight-chain carboxylic acid is used as in the first embodiment. Therefore, carboxylic acids such as heptanoic acid, octanoic acid, decanoic acid and dodecanoic acid are used as extractants.
By using a carboxylic acid having this linear structure, the effect of suppressing the generation of hydroxide crud and stabilizing the operation is achieved, as in the first embodiment.

The addition of the alkaline solution in the extraction step in the second solvent extraction step S3 and the adjustment range of the pH may be the same as in the first embodiment.
In addition, the contact with the sulfuric acid solution in the back extraction step and the operation procedure such as the adjustment range of pH may be the same as in the first embodiment.
By carrying out the above steps, it is possible to leave magnesium in the aqueous phase and obtain a high-purity cobalt sulfate solution with reduced impurities. Then, in the second solvent extraction step S3, it is possible to avoid situations unfavorable to the operation such as the generation of hydroxide due to the increase in pH during operation and the accompanying crud generation, so that the operation is stable. can be played.

(Crystallization step S4)
The crystallization step S4 will be explained based on FIG.
In the crystallization step S4, crystals of cobalt sulfate are precipitated from the cobalt sulfate solution obtained in the second solvent extraction step S3. A crystallization method is not particularly limited, and a general crystallization method can be used. Therefore, a crystallization method using a crystallization can can be used as in the first embodiment.

Cobalt sulfate crystals can be produced from a cobalt sulfate solution in the manner described above. Of course, since the cobalt sulfate solution contains few impurities and is of high purity, the obtained cobalt sulfate crystals are also of high purity with few impurities.

EXAMPLES The present invention will be described in more detail below with reference to examples, but the present invention is not limited to the following examples. Examples 1 to 4 below are included in the manufacturing method of the first embodiment.

(Comparative example 1)
First, a method for producing a cobalt chloride solution using a branched carboxylic acid-based extractant in the second solvent extraction step S3 will be described as Comparative Example 1. FIG.
(Decopper step S1)
A sodium hydrosulfide solution was added as a sulfiding agent to 2 L of the cobalt chloride solution having the composition shown in the original solution A in Table 1 adjusted to pH 2.5 to adjust the oxidation-reduction potential to −50 mV (based on Ag/AgCl electrode). to form copper sulfide precipitates. The precipitate was separated and removed with a filter to obtain a filtrate having the composition shown in B after sulfurization in Table 1. The copper concentration was less than 0.001 g/L, and the copper could be separated and removed.

(First solvent extraction step S2)
Organic diluted with a diluent (trade name Teclean N20, JX Nikko Nisseki Energy Co., Ltd.) so that the concentration of alkyl phosphate-based extractant (trade name D2EHPA, manufactured by Daihachi Chemical Co., Ltd.) is 40% by volume Prepare the phases. 0.9 L of the aqueous phase consisting of the cobalt chloride solution obtained in the copper removal step S1 and 1.8 L of the organic phase are mixed, and a sodium hydroxide solution is added to adjust the pH to 1.7, and impurities are removed. Extracted. The same extraction operation was repeated with 0.9 L of the aqueous phase after extraction and 1.8 L of the new organic phase, and a total of three extraction operations were carried out. As a result, a cobalt chloride solution having the composition shown in Table 1 after the first SX was obtained. The concentrations of zinc, manganese and calcium were all less than 0.001 g/L, and these impurities could be separated and removed.

(Second solvent extraction step S3)
A branched carboxylic acid-based extractant (trade name Versatic Acid 10, manufactured by Oxalis Chemicals) having a structure different from that of the present invention was used, and diluted with a diluent (Techleen N20) so that its concentration was 30% by volume. An organic phase was prepared. 0.44 L of the aqueous phase consisting of the cobalt chloride solution obtained in the first solvent extraction step S2 and 1 L of the organic phase are mixed, the pH is adjusted by adding a sodium hydroxide solution to 6.5, and cobalt is removed. Extract into the organic phase.
0.6 L of the extracted organic phase and 0.6 L of a cobalt chloride solution having a cobalt concentration of 10 g/L were mixed to wash the aqueous phase mixed in the extracted organic phase. Subsequently, this organic phase was mixed with 0.09 L of pure water, sulfuric acid was added to adjust the pH to 5, and cobalt was back-extracted. The magnesium concentration was less than 0.001 g/L, and magnesium could be separated and removed.

By carrying out the above production method, a cobalt sulfate solution having the composition shown in Table 1, Second SX D, was obtained.
In Table 1, "after sulfurization" means "after copper removal step S1", "after 1SX" means "after first solvent extraction step S2", and "after 2SX" means "after second solvent extraction step S3". means The same applies to Tables 3, 5, 7 and 9.

As described above, in the second solvent extraction step S3, the concentration of each of copper, zinc, manganese, calcium, and magnesium is less than 0.001 g/L even by the production method using a branched carboxylic acid-based extractant. A high-purity cobalt sulfate solution was obtained.
In Comparative Example 1, at pH 5, hydroxide may be generated during back extraction, so the pH was lowered to around 4, but the extraction rate decreased, and extraction was repeated to ensure the extraction amount.

(Crystallization step S4)
The cobalt sulfate solution was put into a rotary evaporator, the pressure inside was reduced by a vacuum pump, and the temperature was maintained at 40° C., and water was evaporated while rotating the flask portion to precipitate crystals of cobalt sulfate. After the solid-liquid separation, the cobalt sulfate crystals obtained were dried with a dryer. As a result, high-purity cobalt sulfate crystals as shown in Table 2 were obtained.

(Example 1)
A cobalt sulfate solution was obtained in the same manner as in Comparative Example 1, except that in the second solvent extraction step S3, the carboxylic acid-based extractant was changed to linear heptanoic acid.
A reagent manufactured by FUJIFILM Wako Pure Chemical Industries, Ltd. (trade name: heptanoic acid) was used as the extractant. As for the manufacturer and product name of the extracting agent, the chemical name is the same as the product name in each of the following examples.
Table 3 shows the composition after impurity separation in Example 1. As shown in D after 2nd SX in Table 3, a high-purity cobalt sulfate solution having copper, zinc, manganese, calcium and magnesium concentrations of less than 0.001 g/L was obtained.

Subsequently, crystallization was carried out in the same manner as in Comparative Example 1, and high-purity cobalt sulfate crystals as shown in Table 4 were obtained.

(Example 2)
A cobalt sulfate solution was obtained in the same manner as in Example 1, except that in the second solvent extraction step S3, the carboxylic acid-based extractant was changed to linear octanoic acid.
Table 5 shows the composition in this case. As shown in D after 2nd SX in Table 5, a high-purity cobalt sulfate solution having copper, zinc, manganese, calcium and magnesium concentrations of less than 0.001 g/L was obtained.

Subsequently, crystallization was carried out in the same manner as in Example 1, and high-purity cobalt sulfate crystals as shown in Table 6 were obtained.

(Example 3)
A cobalt sulfate solution was obtained in the same manner as in Example 1, except that linear decanoic acid was used as the carboxylic acid-based extractant in the second solvent extraction step S3.
Table 7 shows the composition in this case. As shown in D after 2nd SX in Table 7, a high-purity cobalt sulfate solution having copper, zinc, manganese, calcium and magnesium concentrations of less than 0.001 g/L was obtained.

Subsequently, crystallization was carried out in the same manner as in Example 1, and high-purity cobalt sulfate crystals as shown in Table 8 were obtained.

(Example 4)
A cobalt sulfate solution was obtained in the same manner as in Example 1, except that in the second solvent extraction step S3, the carboxylic acid-based extractant was changed to linear dodecanoic acid.
Table 9 shows the composition in this case. As shown in D after 2nd SX in Table 9, a high-purity cobalt sulfate solution having copper, zinc, manganese, calcium and magnesium concentrations of less than 0.001 g/L was obtained.

Subsequently, crystallization was carried out in the same manner as in Example 1, and high-purity cobalt sulfate crystals as shown in Table 10 were obtained.

According to the results of Examples 1 to 4 belonging to the method for producing cobalt sulfate according to the first embodiment, it was possible to obtain cobalt sulfate of high purity in which impurities were sufficiently removed. In addition, stable operation was possible without generation of crud. Although no experiments were conducted on the method for producing cobalt sulfate according to the second embodiment, the second embodiment differs from the first embodiment only in the order of the copper removal step S1 and the first solvent extraction step S2. Since there is no essential difference between the

The high-purity cobalt sulfate crystals obtained by the present invention can be used as raw materials for lithium-ion secondary batteries, as well as for various other purposes.

S1 Copper removal step S2 First solvent extraction step S3 Second solvent extraction step S4 Crystallization step

Claims (8)

A manufacturing method for obtaining cobalt sulfate by removing impurities from a cobalt chloride solution containing one or more impurities of copper, zinc, manganese, calcium and magnesium, comprising:
The former step includes a decoppering step of adding a sulfiding agent to the cobalt chloride solution to form a precipitate of copper sulfide to separate and remove the copper sulfide, and bringing the cobalt chloride solution into contact with an organic solvent containing an alkyl phosphate-based extractant. , a first solvent extraction step of extracting zinc, manganese and calcium into the organic solvent to separate and remove;
In the second step, the cobalt chloride solution that has passed through the first step is brought into contact with an organic solvent containing a linear carboxylic acid-based extractant to extract cobalt with the organic solvent. A method for producing cobalt sulfate, comprising a second solvent extraction step to obtain a cobalt solution. 2. The method for producing cobalt sulfate according to claim 1, wherein the first stage step is performed in the order of the copper removal step and the first solvent extraction step. 2. The method for producing cobalt sulfate according to claim 1, wherein the first step is performed in the order of the first solvent extraction step and the copper removal step. 2. The method for producing cobalt sulfate according to claim 1, wherein the cobalt sulfate solution obtained through the second solvent extraction step is subjected to a crystallization step to obtain cobalt sulfate crystals. In the decoppering step, an oxidizing agent and a neutralizing agent are added to a cobalt chloride solution containing a sulfiding agent to adjust the redox potential to −100 to 200 mV (based on Ag/AgCl electrode) and pH to 1.3 to 3. 4. The method for producing cobalt sulfate according to claim 1, 2 or 3, wherein the ratio is adjusted to 0.0. The alkyl phosphate-based extractant in the first solvent extraction step is bis(2-ethylhexyl) hydrogen phosphate,
Claim 1, 2 or 3, wherein the pH of the cobalt chloride solution is adjusted to 1.5 to 3.0 and subjected to solvent extraction using the extractant to extract the impurity elements into the organic solvent. A method for producing cobalt sulfate as described. In the second solvent extraction step, an alkaline solution is added to the cobalt chloride solution from which copper, zinc, manganese and calcium have been removed, the pH is adjusted to 4.0 to 7.0, and cobalt is removed as a carboxylic acid-based extractant. 4. The method for producing cobalt sulfate according to claim 1, 2 or 3, wherein an extraction step of extracting into an organic solvent using is carried out. Following the extraction step in the second solvent extraction step, a sulfuric acid solution is brought into contact with the organic solvent from which cobalt has been extracted, the pH is adjusted to 2.0 to 4.5, and the cobalt is back extracted into the sulfuric acid solution. 8. The method for producing cobalt sulfate according to claim 7, wherein an extraction step is performed.