JP2022179501A - 口腔ケア用および医療用のデバイスおよび構成要素の固体自由形状製作のための熱可塑性ポリウレタン組成物 - Google Patents
口腔ケア用および医療用のデバイスおよび構成要素の固体自由形状製作のための熱可塑性ポリウレタン組成物 Download PDFInfo
- Publication number
- JP2022179501A JP2022179501A JP2022144608A JP2022144608A JP2022179501A JP 2022179501 A JP2022179501 A JP 2022179501A JP 2022144608 A JP2022144608 A JP 2022144608A JP 2022144608 A JP2022144608 A JP 2022144608A JP 2022179501 A JP2022179501 A JP 2022179501A
- Authority
- JP
- Japan
- Prior art keywords
- component
- tpu
- oral care
- polyol
- thermoplastic polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】 口腔ケア用および医療用のデバイスおよび構成要素の固体自由形状製作のための熱可塑性ポリウレタン組成物を提供すること【解決手段】 本発明は、口腔ケア用または医療用のデバイス、構成要素、および応用例の固体自由形状製作のための組成物および方法であって、この組成物が、そのような加工に特に適切な熱可塑性ポリウレタンを含んでいる、上記組成物および方法に関する。有用な熱可塑性ポリウレタンは、(a)芳香族ジイソシアネート成分、(b)鎖延長剤成分、および任意選択のポリオール成分から誘導される。【選択図】 なし
Description
発明の分野
本発明は、口腔ケア用および医療用のデバイス、構成要素、および応用例の直接固体自由形状製作のための、組成物および方法に関する。口腔ケア用および医療用のデバイスは、そのような加工に適切な、生体適合性熱可塑性ポリウレタンから形成することができる。有用な熱可塑性ポリウレタンは、(a)芳香族ジイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリオール成分から誘導される。
本発明は、口腔ケア用および医療用のデバイス、構成要素、および応用例の直接固体自由形状製作のための、組成物および方法に関する。口腔ケア用および医療用のデバイスは、そのような加工に適切な、生体適合性熱可塑性ポリウレタンから形成することができる。有用な熱可塑性ポリウレタンは、(a)芳香族ジイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリオール成分から誘導される。
背景
固体自由形状製作(SFF)は、付加製造とも呼ばれ、加算形成ステップ(additive formation steps)によって、コンピューターデータから直接的に、任意形状の構造物の製作を可能にする技術である。任意のSFFシステムの基本操作は、三次元コンピューターモデルをスライスして薄い横断面にするステップと、その結果を二次元位置データに翻訳するステップと、そのデータを、層ごとの様式(layerwise manner)で三次元構造を製作する制御装置に供給するステップからなる。
固体自由形状製作(SFF)は、付加製造とも呼ばれ、加算形成ステップ(additive formation steps)によって、コンピューターデータから直接的に、任意形状の構造物の製作を可能にする技術である。任意のSFFシステムの基本操作は、三次元コンピューターモデルをスライスして薄い横断面にするステップと、その結果を二次元位置データに翻訳するステップと、そのデータを、層ごとの様式(layerwise manner)で三次元構造を製作する制御装置に供給するステップからなる。
固体自由形状製作は、三次元印刷、電子ビーム積層造形(electron beam
melting)、ステレオリソグラフィー、選択的レーザー焼結、薄板積層(laminated object manufacturing)、熱溶解積層などを含む、多くの異なるアプローチを伴う。
melting)、ステレオリソグラフィー、選択的レーザー焼結、薄板積層(laminated object manufacturing)、熱溶解積層などを含む、多くの異なるアプローチを伴う。
これらのプロセス間の相違は、部品が創出されるように層が配置される手法、ならびに利用される材料にある。選択的レーザー焼結(SLS)、熱溶解積層(FDM)、または溶融フィラメント製作(FFF)などのいくつかの方法は、層が生成されるように材料を融解しまたは軟化させる。立体リソグラフィ(SLA)などのその他の方法は、液体材料を硬化する。
典型的には、熱可塑性物質に関する付加製造は、2つのタイプの印刷方法を利用する。押出しタイプとして公知の第1の方法では、対象材料のフィラメントおよび/または樹脂(「ペレット印刷」と呼ぶ)を軟化させまたは融解させ、次いで機械により層状に堆積させて、所望の物体を形成する。押出しタイプの方法は、熱溶解積層(FDM)または溶融フィラメント製作(FFF)として公知である。押出し方法では、熱可塑性樹脂、または熱可塑性フィラメントのストランドを、ノズルヘッドに供給し、このノズルヘッドで熱可塑性物質を加熱し、流れをオンおよびオフに切り換える。部品は、材料の小さいビーズを押し出し、これを硬化して層を形成することにより構築される。
第2の方法は、粉末を粒状床に堆積させ、次いで選択的溶融または融解によって、先に得られた層と溶融する、粉末または粒状タイプである。技法は、典型的には高出力レーザーを使用して層の部分を溶融する。各断面を加工した後、粉末床を低下させる。次いで粉末化材料の新しい層を付着させ、部品が完全に構築されるまでステップを繰り返す。しばしば機械は、バルク粉末床材料をその融点よりも僅かに低くなるまで予熱する能力を備えたものが、設計される。この機械によれば、選択された領域の温度を融点まで上昇させるレーザーの、エネルギーの量および時間の長さが削減される。
押出し方法とは異なり、粒状または粉末方法は、生成される部品の突起または梁および
薄壁を支持するのに、非溶融媒体を使用する。このようにすることで、小片が構築されるときに一時的な支持を行う必要が低減されまたはなくなる。特定の方法には、選択的レーザー焼結(SLS)、選択的熱焼結(SHS)、および選択的レーザー融解(SLM)が含まれる。SLMでは、レーザーが粉末を完全に融解する。このため、層ごとに形成する方法で、従来製造されてきた部品の性質に類似した、機械的性質を有する部品が形成される。別の粉末または粒状方法は、インクジェット印刷システムを利用する。この技術では、小片は、粉末の層の上部に、インクジェット様プロセスを使用して部品の断面に結合剤を印刷することにより、層ごとに創出される。粉末の追加の層を付加し、各層が印刷されるまでプロセスを繰り返す。
薄壁を支持するのに、非溶融媒体を使用する。このようにすることで、小片が構築されるときに一時的な支持を行う必要が低減されまたはなくなる。特定の方法には、選択的レーザー焼結(SLS)、選択的熱焼結(SHS)、および選択的レーザー融解(SLM)が含まれる。SLMでは、レーザーが粉末を完全に融解する。このため、層ごとに形成する方法で、従来製造されてきた部品の性質に類似した、機械的性質を有する部品が形成される。別の粉末または粒状方法は、インクジェット印刷システムを利用する。この技術では、小片は、粉末の層の上部に、インクジェット様プロセスを使用して部品の断面に結合剤を印刷することにより、層ごとに創出される。粉末の追加の層を付加し、各層が印刷されるまでプロセスを繰り返す。
口腔ケア用のデバイスおよび応用例に用いられる現行の固体自由形状製作は、間接的な製作、例えば引き続き材料で満たされる型の印刷、または後に表面に熱形成されたデバイスが成型される形状の印刷に、焦点を当てており;あるいは医療応用例では、視覚化、デモンストレーション、および機械的プロトタイピングが行われ、例えば予測される結果をモデル化し、その後に、3D印刷プロトタイプをベースにした手順を行う。したがって、SFFは、ツーリングおよび労働力において最少の投資で、機能的なプロトタイプの迅速な製作を容易にする。そうしたラピッドプロトタイピングは、設計者への迅速で効果的なフィードバックを提供することによって、製品開発サイクルを短縮し、設計プロセスを改善する。SFFは、例えば美的感覚、フィット、アセンブリーなどの設計の様々な側面を評価する目的で、非機能的部分の迅速な製作のために使用することもできる。
口腔ケア用および医療用の応用例での付加製造で利用される現行の材料は、典型的にはABS、ナイロン、ポリカーボネート、ポリカプロラクトン、ポリ乳酸(PLA)、ポリ-L-乳酸(PLLA)、およびフォトポリマー/硬化液体材料を含む。これらの材料のいくつかは、それらの生体適合性または長期生体耐久性の欠如により、プロトタイプ、型、外科計画、および解剖模型などの体外での応用例に限定される。
熱可塑性ポリウレタンが提供する魅力的な特性の組合せ、およびより慣用的な製作手段を用いて作製される広範な物品を前提として、口腔ケア用および医療用のデバイス、構成要素、および応用例の直接固体自由形状製作に非常に良く適した熱可塑性ポリウレタンを特定し、および/または開発することが望ましい。
要旨
本開示の技術は、(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物を含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術は、(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物を含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、鎖延長剤成分が、1,6-ヘキサンジオール(HDO)、1,4-シクロヘキサンジメタノール(CHDM)、またはその組合せを含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、芳香族ジイソシアネートが、MDIを含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、付加製造が熱溶解積層または選択的レーザー焼結を含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、熱可塑性ポリウレタンが生体適合性である、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、ポリオール成分をさらに含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、ポリオール成分に対する鎖延長剤のモル比が25.0より大きい、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、ポリオール成分が少なくとも650の数平均分子量を有する、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、ポリオール成分が、PTMEG、エチレンオキシドキャップされたプロピレンオキシド、またはその組合せの1つまたは1つより多くを含むポリエーテルポリオールを含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、ポリオール成分が、ポリカプロラクトンを含むポリエステルポリオールを含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、鎖延長剤成分が組成物の総重量の25重量%~35重量%である、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、ポリイソシアネート成分が、TDI、IPDI、LDI、BDI、PDI、CHDI、TODI、NDI、HXDIまたはその任意の組合せをさらに含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、鎖延長剤成分がHDO/CHDMを含み、ポリオール成分がポリ(テトラメチレンエーテルグリコール)を含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、熱可塑性ポリウレタンが、着色剤、酸化防止剤(フェノール類(phenolics)、ホスファイト、チオエステルおよび/またはアミンを含む)、放射線不透化剤、安定剤、潤滑剤(lubricatn)、抑制剤(inhibitor)、加水分解安定剤、ヒンダードアミン系光安定剤、ベンゾトリアゾールUV吸収剤、熱安定剤、変色を防止するための安定剤、染料、顔料、補強剤またはその任意の組合せの1つまたは1つより多くをさらに含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、口腔ケア用のデバイスまたは構成要素が、歯科用アライナー、歯科用維持装置、または矯正デバイスの1つまたは1つより多くを含む、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、口腔ケア用のデバイスまたは構成要素が、患者に個人化されている、口腔ケア用のデバイスまたは構成要素を提供する。
本開示の技術はさらに、(I)物体の固体自由形状製作のためのシステムを動作させるステップを含む、三次元の口腔ケア用のデバイスまたは構成要素を製作する方法であって、前記システムが、(a)芳香族ジイソシアネート成分を含むポリイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリオール成分から誘導された熱可塑性ポリウレタンを含む構築材料から三次元の口腔ケア用のデバイスまたは構成要素を形成するように動作する、固体自由形状製作装置を含む、方法を提供する。
本開示の技術はさらに、(a)芳香族ジイソシアネート、(b)鎖延長剤成分、および(c)任意選択のポリオール成分から誘導された、選択的に堆積された熱可塑性ポリウレタン組成物を含む、直接的形成された口腔ケア用のデバイスまたは構成要素をさらに提供する。
本開示の技術はさらに、(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物を含む、医療用のデバイスまたは構成要素をさらに提供する。
本開示の技術はさらに、医療用のデバイスまたは構成要素が、副子、外部支持装具、または矯正デバイスの1つまたは1つより多くを含む、医療用のデバイスまたは構成要素をさらに提供する。
詳細な説明
様々な好ましい特徴および実施形態を、非限定的な例示によって、以下で説明することとする。
様々な好ましい特徴および実施形態を、非限定的な例示によって、以下で説明することとする。
本開示の技術は、口腔ケア用および医療用のデバイスおよび構成要素の直接固体自由形状製作に有用な、熱可塑性ポリウレタン組成物を提供する。本記載の熱可塑性ポリウレタンは、生体適合性および生体耐久性があり、それと共に、口腔ケア用のデバイスおよび構成要素の固体自由形状製作方法で使用される従来の材料で必要とされた加工助剤を含まない。
熱可塑性ポリウレタン
熱可塑性ポリウレタン
本記載の技術に有用な熱可塑性ポリウレタンは、(a)芳香族ジイソシアネート成分、(b)ポリオール成分、および(c)鎖延長剤成分から誘導され、(b)に対する(c)のモル比が25より大きい。本明細書に記載されるTPU組成物は、(a)ポリイソシアネート成分を使用して作製される。前記ポリイソシアネートおよび/またはポリイソシアネート成分は、1つまたは1つより多くのポリイソシアネートを含む。いくつかの実施形態では、ポリイソシアネート成分は、1つまたは1つより多くのジイソシアネートを含む。
いくつかの実施形態では、ポリイソシアネートおよび/またはポリイソシアネート成分は、5~20個の炭素原子を有するα,ω-アルキレンジイソシアネートを含む。
いくつかの実施形態では、ポリイソシアネート成分は、1つまたは1つより多くの芳香族ジイソシアネートを含む。いくつかの実施形態では、ポリイソシアネート成分は、脂肪族ジイソシアネートを本質的には含まない、またはさらにはそれを完全に含まない。
有用なポリイソシアネートの例には、芳香族ジイソシアネート、例えば4,4’-メチレンビス(フェニルイソシアネート)(MDI)、m-キシレンジイソシアネート(XDI)、フェニレン-1,4-ジイソシアネート、ナフタレン-1,5-ジイソシアネートおよびトルエンジイソシアネート(TDI);ならびに脂肪族ジイソシアネート、例えばイソホロンジイソシアネート(IPDI)、1,4-シクロヘキシルジイソシアネート(CHDI)、デカン-1,10-ジイソシアネート、リシンジイソシアネート(LDI)、1,4-ブタンジイソシアネート(BDI)、イソホロンジイソシアネート(PDI)、3,3’-ジメチル-4,4’-ビフェニレンジイソシアネート(TODI)、1,5
-ナフタレンジイソシアネート(NDI)およびジシクロヘキシルメタン-4,4’-ジイソシアネート(H12MDI)が含まれる。2つまたは2つより多くのポリイソシアネートの混合物を使用することができる。いくつかの実施形態では、ポリイソシアネートはMDIである。
-ナフタレンジイソシアネート(NDI)およびジシクロヘキシルメタン-4,4’-ジイソシアネート(H12MDI)が含まれる。2つまたは2つより多くのポリイソシアネートの混合物を使用することができる。いくつかの実施形態では、ポリイソシアネートはMDIである。
本明細書に記載されるTPU組成物は、(b)ポリオール成分を使用して作製される。
ポリオールには、ポリエーテルポリオール、ポリエステルポリオール、ポリカーボネートポリオール、ポリシロキサンポリオールおよびその組合せが含まれる。
存在する場合、ヒドロキシル末端中間体とも記載される適切なポリオールは、1つもしくは1つより多くのヒドロキシル末端ポリエステル、1つもしくは1つより多くのヒドロキシル末端ポリエーテル、1つもしくは1つより多くのヒドロキシル末端ポリカーボネート、1つもしくは1つより多くのヒドロキシル末端ポリシロキサンまたはその混合物を含むことができる。
適切なヒドロキシル末端ポリエステル中間体は、約500~約10,000、約700~約5,000または約700~約4,000の数平均分子量(Mn)を有する線状ポリエステルを含み、一般に1.3未満または0.5未満の酸価を有する。その分子量は、末端官能基のアッセイによって決定され、それは数平均分子量と関連付けられる。ポリエステル中間体は、(1)1つもしくは1つより多くのグリコールと1つもしくは1つより多くのジカルボン酸または無水物とのエステル化反応によって、あるいは、(2)エステル交換反応、すなわち1つもしくは1つより多くのグリコールとジカルボン酸のエステルとの反応によって作製することができる。末端ヒドロキシル基を優勢に有する直鎖が得られるように、酸に対して1モル超の過剰のグリコールのモル比が好ましい。適切なポリエステル中間体には、一般にε-カプロラクトンとジエチレングリコールなどの二官能性開始剤とによって作製されるポリカプロラクトンなどの種々のラクトンも含まれる。所望のポリエステルのジカルボン酸は、脂肪族、脂環式、芳香族またはその組合せであってよい。単独かまたは混合物で使用できる適切なジカルボン酸は、一般に、合計4~15個の炭素原子を有し、それらには:コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、ドデカン二酸、イソフタル酸、テレフタル酸、シクロヘキサンジカルボン酸などが含まれる。無水フタル酸、無水テトラヒドロフタル酸などの上記ジカルボン酸の無水物を使用することもできる。アジピン酸が好ましい酸である。望ましいポリエステル中間体を生成させるために反応させるグリコールは、鎖延長剤部分中に上記グリコールのいずれかを含む脂肪族、芳香族またはその組合せであってよく、それは合計で2~20個または2~12個の炭素原子を有する。適切な例には、エチレングリコール、1,2-プロパンジオール、1,3-プロパンジオール、1,3-ブタンジオール、1,4-ブタンジオール、1,5-ペンタンジオール、1,6-ヘキサンジオール、2,2-ジメチル-1,3-プロパンジオール、1,4-シクロヘキサンジメタノール、デカメチレングリコール、ドデカメチレングリコールおよびその混合物が含まれる。
ポリオール成分は、1つまたは1つより多くのポリカプロラクトンポリエステルポリオールを含むこともできる。本明細書に記載される技術において有用なポリカプロラクトンポリエステルポリオールには、カプロラクトンモノマーから誘導されるポリエステルジオールが含まれる。ポリカプロラクトンポリエステルポリオールは、第一級ヒドロキシル基によって末端化される。適切なポリカプロラクトンポリエステルポリオールは、ε-カプロラクトンと、二官能性開始剤、例えばジエチレングリコール、1,4-ブタンジオールまたは本明細書で挙げる他のグリコールおよび/もしくはジオールのいずれかとから作製することができる。いくつかの実施形態では、ポリカプロラクトンポリエステルポリオールは、カプロラクトンモノマーから誘導される線状ポリエステルジオールである。
有用な例には、そのどちらもPerstorp Polyols Incから市販されているCAPA(商標)2202A(2000の数平均分子量(Mn)の線状ポリエステルジオール)およびCAPA(商標)2302A(3000のMnの線状ポリエステルジオール)が含まれる。これらの材料は、2-オキセパノンと1,4-ブタンジオールとのポリマーと記載することもできる。
ポリカプロラクトンポリエステルポリオールは2-オキセパノンおよびジオールから調製することができ、そのジオールは1,4-ブタンジオール、ジエチレングリコール、モノエチレングリコール、1,6-ヘキサンジオール、2,2-ジメチル-1,3-プロパンジオールまたはその任意の組合せであってよい。いくつかの実施形態では、ポリカプロラクトンポリエステルポリオールを調製するために使用されるジオールは直鎖状である。いくつかの実施形態では、ポリカプロラクトンポリエステルポリオールは、1,4-ブタンジオールから調製される。いくつかの実施形態では、ポリカプロラクトンポリエステルポリオールは、500~10,000、または500~5,000、または1,000もしくはさらには2,000、または2,000~4,000もしくはさらには3000の数平均分子量を有する。
適切なヒドロキシル末端ポリエーテル中間体には、合計2~15個の炭素原子を有するジオールまたはポリオール、いくつかの実施形態では、2~6個の炭素原子を有するアルキレンオキシド、一般にエチレンオキシドもしくはプロピレンオキシドまたはその混合物を含むエーテルと反応されたアルキルジオールまたはグリコールから誘導されるポリエーテルポリオールが含まれる。例えば、ヒドロキシル官能性ポリエーテルは、最初にプロピレングリコールをプロピレンオキシドと反応し、続いてエチレンオキシドと反応することによって生成させることができる。エチレンオキシドから得られる第一級ヒドロキシル基は第二級ヒドロキシル基より反応性であり、したがって好ましい。有用な市販のポリエーテルポリオールには、エチレングリコールと反応させたエチレンオキシドを含むポリ(エチレングリコール)、プロピレングリコールと反応させたプロピレンオキシドを含むポリ(プロピレングリコール)、重合したテトラヒドロフランと称することもでき、および一般にPTMEGと称されるテトラヒドロフランと反応させた水を含むポリ(テトラメチレンエーテルグリコール)が含まれる。いくつかの実施形態では、ポリエーテル中間体にはPTMEGが含まれる。適切なポリエーテルポリオールは、アルキレンオキシドのポリアミド付加体も含み、それらは、例えば、エチレンジアミンとプロピレンオキシドとの反応生成物を含むエチレンジアミン付加体、ジエチレントリアミンとプロピレンオキシドとの反応生成物を含むジエチレントリアミン付加体、および類似のポリアミド型ポリエーテルポリオールを含むことができる。コポリエーテルを、本記載の組成物において使用することもできる。典型的なコポリエーテルには、THFとエチレンオキシドまたはTHFとプロピレンオキシドの反応生成物が含まれる。これらは、BASFから、PolyTHF(登録商標)B、ブロックコポリマー、およびpoly THF(登録商標)R、ランダムコポリマーとして入手することができる。種々のポリエーテル中間体は一般に、約1,000超、例えば約1,000~約10,000、約1,000~約5,000または約1,000~約2,500の平均分子量である、末端官能基のアッセイによって決定された数平均分子量(Mn)を有する。いくつかの実施形態では、ポリエーテル中間体には、2,000MnのPTMEGと1000MnのPTMEGのブレンドなどの2つまたは2つより多くの異なる分子量のポリエーテルのブレンドが含まれる。
適切なヒドロキシル末端ポリカーボネートには、グリコールをカーボネートと反応させることによって調製されるものが含まれる。米国特許第4,131,731号を、ヒドロキシル末端ポリカーボネートおよびそれらの調製のその開示について参照により本明細書に組み込む。そうしたポリカーボネートは線状であり、他の末端基を本質的に排除して末
端ヒドロキシル基を有する。本質的な反応物はグリコールおよびカーボネートである。適切なグリコールは、4~40個、およびまたはさらには4~12個の炭素原子を含む脂環式および脂肪族のジオール、ならびに、分子当たり2~20のアルコキシ基を有し、各アルコキシ基が2~4個の炭素原子を含むポリオキシアルキレングリコールから選択される。適切なジオールには、4~12個の炭素原子を含む脂肪族ジオール、例えば1,4-ブタンジオール、1,5-ペンタンジオール、ネオペンチルグリコール、1,6-ヘキサンジオール、2,2,4-トリメチル-1,6-ヘキサンジオール、1,10-デカンジオール、水素化ジリノレイルグリコール、水素化ジオレイルグリコール、3-メチル-1,5-ペンタンジオール;および脂環式ジオール、例えば1,3-シクロヘキサンジオール、1,4-ジメチロールシクロヘキサン、1,4-シクロヘキサンジオール-、1,3-ジメチロールシクロヘキサン-、1,4-エンドメチレン-2-ヒドロキシ-5-ヒドロキシメチルシクロヘキサンおよびポリアルキレングリコールが含まれる。反応で使用されるジオールは、最終生成物において望ましい特性に応じて、単一のジオールであってもジオールの混合物であってもよい。ヒドロキシル末端化されているポリカーボネート中間体は、当技術分野および文献で一般に公知のものである。適切なカーボネートは、5~7員環から構成されるアルキレンカーボネートから選択される。本明細書で使用するのに適切なカーボネートには、エチレンカーボネート、トリメチレンカーボネート、テトラメチレンカーボネート、1,2-プロピレンカーボネート、1,2-ブチレンカーボネート、2,3-ブチレンカーボネート、1,2-エチレンカーボネート、1,3-ペンチレンカーボネート、1,4-ペンチレンカーボネート、2,3-ペンチレンカーボネートおよび2,4-ペンチレンカーボネートが含まれる。ジアルキルカーボネート、脂環式カーボネートおよびジアリールカーボネートもやはり本明細書で適している。ジアルキルカーボネートは、各アルキル基中に2~5個の炭素原子を含むことができ、その具体的な例は、ジエチルカーボネートおよびジプロピルカーボネートである。脂環式カーボネート、特に二脂環式(dicycloaliphatic)カーボネートは、各環状構造中に4~7個の炭素原子を含むことができ、そうした構造の1つまたは2つであってよい。一方の基が脂環式である場合、他方の基は、アルキルかまたはアリールであってよい。他方、一方の基がアリールである場合、他方の基は、アルキルかまたは脂環式であってよい。各アリール基中に6~20個の炭素原子を含むことができる適切なジアリールカーボネートの例は、ジフェニルカーボネート、ジトリルカーボネートおよびジナフチルカーボネートである。
端ヒドロキシル基を有する。本質的な反応物はグリコールおよびカーボネートである。適切なグリコールは、4~40個、およびまたはさらには4~12個の炭素原子を含む脂環式および脂肪族のジオール、ならびに、分子当たり2~20のアルコキシ基を有し、各アルコキシ基が2~4個の炭素原子を含むポリオキシアルキレングリコールから選択される。適切なジオールには、4~12個の炭素原子を含む脂肪族ジオール、例えば1,4-ブタンジオール、1,5-ペンタンジオール、ネオペンチルグリコール、1,6-ヘキサンジオール、2,2,4-トリメチル-1,6-ヘキサンジオール、1,10-デカンジオール、水素化ジリノレイルグリコール、水素化ジオレイルグリコール、3-メチル-1,5-ペンタンジオール;および脂環式ジオール、例えば1,3-シクロヘキサンジオール、1,4-ジメチロールシクロヘキサン、1,4-シクロヘキサンジオール-、1,3-ジメチロールシクロヘキサン-、1,4-エンドメチレン-2-ヒドロキシ-5-ヒドロキシメチルシクロヘキサンおよびポリアルキレングリコールが含まれる。反応で使用されるジオールは、最終生成物において望ましい特性に応じて、単一のジオールであってもジオールの混合物であってもよい。ヒドロキシル末端化されているポリカーボネート中間体は、当技術分野および文献で一般に公知のものである。適切なカーボネートは、5~7員環から構成されるアルキレンカーボネートから選択される。本明細書で使用するのに適切なカーボネートには、エチレンカーボネート、トリメチレンカーボネート、テトラメチレンカーボネート、1,2-プロピレンカーボネート、1,2-ブチレンカーボネート、2,3-ブチレンカーボネート、1,2-エチレンカーボネート、1,3-ペンチレンカーボネート、1,4-ペンチレンカーボネート、2,3-ペンチレンカーボネートおよび2,4-ペンチレンカーボネートが含まれる。ジアルキルカーボネート、脂環式カーボネートおよびジアリールカーボネートもやはり本明細書で適している。ジアルキルカーボネートは、各アルキル基中に2~5個の炭素原子を含むことができ、その具体的な例は、ジエチルカーボネートおよびジプロピルカーボネートである。脂環式カーボネート、特に二脂環式(dicycloaliphatic)カーボネートは、各環状構造中に4~7個の炭素原子を含むことができ、そうした構造の1つまたは2つであってよい。一方の基が脂環式である場合、他方の基は、アルキルかまたはアリールであってよい。他方、一方の基がアリールである場合、他方の基は、アルキルかまたは脂環式であってよい。各アリール基中に6~20個の炭素原子を含むことができる適切なジアリールカーボネートの例は、ジフェニルカーボネート、ジトリルカーボネートおよびジナフチルカーボネートである。
適切なポリシロキサンポリオールには、α-ω-ヒドロキシルまたはアミンまたはカルボン酸またはチオールまたはエポキシ末端化ポリシロキサンが含まれる。例には、ヒドロキシルまたはアミンまたはカルボン酸またはチオールまたはエポキシ基で末端化されたポリ(ジメチルシロキサン)(poly(dimethysiloxane))が含まれる。いくつかの実施形態では、ポリシロキサンポリオールはヒドロキシル末端ポリシロキサンである。いくつかの実施形態では、ポリシロキサンポリオールは、300~5,000または400~3,000の範囲の数平均分子量を有する。
ポリシロキサンポリオールは、ポリシロキサンヒドリドと脂肪族多価アルコールまたはポリオキシアルキレンアルコールを脱水素反応して、アルコール性ヒドロキシ基をポリシロキサン主鎖上に導入することによって得ることができる。
いくつかの実施形態では、ポリシロキサンは以下の式:
(式中、各R1およびR2は独立に、1~4個の炭素原子のアルキル基、ベンジルまたはフェニル基であり;各EはOHまたはNHR3であり、R3は水素、1~6個の炭素原子のアルキル基または5~8個の炭素原子のシクロアルキル基であり;aおよびbはそれぞれ独立に2~8の整数であり;cは3~50の整数である)
を有する1つまたは1つより多くの化合物で表すことができる。アミノ含有ポリシロキサンにおいて、E基の少なくとも1つはNHR3である。ヒドロキシル含有ポリシロキサンにおいて、E基の少なくとも1つはOHである。いくつかの実施形態では、R1とR2はどちらもメチル基である。
を有する1つまたは1つより多くの化合物で表すことができる。アミノ含有ポリシロキサンにおいて、E基の少なくとも1つはNHR3である。ヒドロキシル含有ポリシロキサンにおいて、E基の少なくとも1つはOHである。いくつかの実施形態では、R1とR2はどちらもメチル基である。
適切な例には、α-ω-ヒドロキシプロピル末端化ポリ(ジメチルシロキサン)およびα-ω-アミノプロピル末端化ポリ(ジメチルシロキサン)が含まれる。これはどちらも市販されている材料である。他の例には、ポリ(ジメチルシロキサン)材料とポリ(アルキレンオキシド)のコポリマーが含まれる。
ポリオール成分は、ポリ(エチレングリコール)、ポリ(テトラメチレンエーテルグリコール)、ポリ(トリメチレンオキシド)、エチレンオキシドキャップされたポリ(プロピレングリコール)、ポリ(ブチレンアジペート)、ポリ(エチレンアジペート)、ポリ(ヘキサメチレンアジペート)、ポリ(テトラメチレン-co-ヘキサメチレンアジペート)、ポリ(3-メチル-1,5-ペンタメチレンアジペート)、ポリカプロラクトンジオール、ポリ(ヘキサメチレンカーボネート)グリコール、ポリ(ペンタメチレンカーボネート)グリコール、ポリ(トリメチレンカーボネート)グリコール、ダイマー脂肪酸ベースのポリエステルポリオール、植物油ベースのポリオールまたはその任意の組合せを含むことができる。
適切なポリエステルポリオールを調製するために使用できるダイマー脂肪酸の例には、Crodaから市販されているPriplast(商標)ポリエステルグリコール/ポリオールおよびOleonから市販されているRadia(登録商標)ポリエステルグリコールが含まれる。
いくつかの実施形態では、ポリオール成分には、ポリエーテルポリオール、ポリカーボネートポリオール、ポリカプロラクトンポリオールまたはその任意の組合せが含まれる。
いくつかの実施形態では、ポリオール成分には、ポリエーテルポリオールが含まれる。いくつかの実施形態では、ポリオール成分は、ポリエーテルポリオールを本質的に含まないか、またはさらにはそれを完全に含まない。いくつかの実施形態では、TPUを調製するために使用されるポリオール成分は、ポリシロキサンを実質的に含まないか、またはさらにはそれを完全に含まない。
いくつかの実施形態では、ポリオール成分には、ポリカプロラクトン、ポリ(テトラメチレンエーテルグリコール)、または末端がキャップされたポリプロピレンオキシドのような三官能性エーテルなど、またはその組合せが含まれる。いくつかの実施形態では、ポ
リオール成分には、ポリカプロラクトンが含まれる。いくつかの実施形態では、ポリオール成分には、末端がキャップされたポリプロピレンオキシドが含まれる。いくつかの実施形態では、ポリオール成分には、ポリ(テトラメチレンエーテルグリコール)が含まれる。
リオール成分には、ポリカプロラクトンが含まれる。いくつかの実施形態では、ポリオール成分には、末端がキャップされたポリプロピレンオキシドが含まれる。いくつかの実施形態では、ポリオール成分には、ポリ(テトラメチレンエーテルグリコール)が含まれる。
いくつかの実施形態では、ポリオールは、少なくとも650の数平均分子量を有する。他の実施形態では、ポリオールは、少なくとも2000、2,500、3,000の数平均分子量、および/または最大で2,500、3,000、4,000、またはさらには6,000の数平均分子量を有する。
本明細書に記載されるTPU組成物はc)鎖延長剤成分を使用して作製される。鎖延長剤には、芳香族グリコール、ジオール、ジアミンおよびその組合せが含まれる。
適切な鎖延長剤には、比較的小さいポリヒドロキシ化合物、例えば、2~20個または2~12個または2~10個の炭素原子を有する低級脂肪族または短鎖グリコールが含まれる。適切な例には、エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール(DPG)、1,4-ブタンジオール(BDO)、1,6-ヘキサンジオール(HDO)、1,3-ブタンジオール、1,5-ペンタンジオール、ネオペンチルグリコール、1,4-シクロヘキサンジメタノール(CHDM)、2,2-ビス[4-(2-ヒドロキシエトキシ)フェニル]プロパン(HEPP)、ヘキサメチレンジオール、ヘプタンジオール、ノナンジオール、ドデカンジオール、3-メチル-1,5-ペンタンジオール、エチレンジアミン、ブタンジアミン、ヘキサメチレンジアミンおよびヒドロキシエチルレゾルシノール(HER)などならびにその混合物が含まれる。いくつかの実施形態では、鎖延長剤には、HDOが含まれる。いくつかの実施形態では、鎖延長剤にはHDOおよびCHDMが含まれる。
いくつかの実施形態では、ポリオールに対する鎖延長剤のモル比は25より大きい。他の実施形態では、熱可塑性ポリウレタンは、ポリオール成分を含まず、ポリオールに対する鎖延長剤のモル比は無限である。
本明細書に記載される熱可塑性ポリウレタンは、熱可塑性ポリウレタン(TPU)組成物であると考えることもできる。そうした実施形態では、その組成物は、1つまたは1つより多くのTPUを含むことができる。これらのTPUは、:a)上記のポリイソシアネート成分;b)上記のポリオール成分;およびc)上記の鎖延長剤成分を反応させることによって調製され、この反応は、触媒の存在下で実施することができる。組成物中のTPUの少なくとも1つは、それを固体自由形状製作、特に熱溶解積層に適したものにする上記パラメーターを満たさなければならない。
反応を実施する手段は、過度に限定されず、回分処理と連続処理の両方を含む。いくつかの実施形態では、本技術は芳香族TPUの回分処理で対処する。いくつかの実施形態では、本技術は芳香族TPUの連続処理で対処する。
本記載の組成物は、上記のTPU材料を含み、また、そうしたTPU材料および1つまたは1つより多くの追加の成分を含むTPU組成物も含む。これらの追加の成分は、本明細書に記載されるTPUとブレンドできる他のポリマー材料を含む。これらの追加の成分は、その組成物の特性に影響を及ぼすための、TPUまたはTPUを含むブレンドに添加できる1つまたは1つより多くの添加剤を含む。
本明細書に記載されるTPUは、1つまたは1つより多くの他のポリマーとブレンドすることもできる。本明細書に記載されるTPUをブレンドできるポリマーは、過度に限定
されない。いくつかの実施形態では、本記載の組成物は、本記載のTPU材料の2つまたは2つより多くを含む。いくつかの実施形態では、その組成物は、本記載のTPU材料の少なくとも1つ、および本記載のTPU材料の1つではない少なくとも1つの他のポリマーを含む。
されない。いくつかの実施形態では、本記載の組成物は、本記載のTPU材料の2つまたは2つより多くを含む。いくつかの実施形態では、その組成物は、本記載のTPU材料の少なくとも1つ、および本記載のTPU材料の1つではない少なくとも1つの他のポリマーを含む。
本明細書に記載されるTPU材料と一緒に使用できるポリマーには、非カプロラクトンポリエステルベースのTPU、ポリエーテルベースのTPUまたは非カプロラクトンポリエステル基とポリエーテル基の両方を含むTPUなどのより慣用的なTPU材料も含まれる。本明細書に記載されるTPU材料とブレンドできる他の適切な材料には、ポリカーボネート、ポリオレフィン、スチレンポリマー、アクリルポリマー、ポリオキシメチレンポリマー、ポリアミド、ポリフェニレンオキシド、ポリフェニレンスルフィド、ポリ塩化ビニル、塩素化ポリ塩化ビニル、ポリ乳酸またはその組合せが含まれる。
本明細書に記載されるブレンドにおいて使用するためのポリマーには、ホモポリマーおよびコポリマーが含まれる。適切な例には:(i)ポリオレフィン(PO)、例えばポリエチレン(PE)、ポリプロピレン(PP)、ポリブテン、エチレンプロピレンゴム(EPR)、ポリオキシエチレン(POE)、環状オレフィンコポリマー(COC)またはその組合せ;(ii)スチレン系、例えばポリスチレン(PS)、アクリロニトリルブタジエンスチレン(ABS)、スチレンアクリロニトリル(SAN)、スチレンブタジエンゴム(SBRまたはHIPS)、ポリアルファメチルスチレン、スチレン無水マレイン酸(SMA)、スチレン-ブタジエンコポリマー(SBC)(スチレン-ブタジエン-スチレンコポリマー(SBS)およびスチレン-エチレン/ブタジエン-スチレンコポリマー(SEBS)など)、スチレン-エチレン/プロピレン-スチレンコポリマー(SEPS)、スチレンブタジエンラテックス(SBL)、エチレンプロピレンジエンモノマー(EPDM)および/またはアクリルエラストマーで改質されたSAN(例えば、PS-SBRコポリマー)またはその組合せ;(iii)上記のもの以外の熱可塑性ポリウレタン(TPU);(iv)ポリアミド6,6(PA66)、ポリアミド1,1(PA11)、ポリアミド1,2(PA12)、コポリアミド(COPA)またはその組合せを含むポリアミド、例えばNylon(商標);(v)アクリルポリマー、例えばポリメチルアクリレート、ポリメチルメタクリレート、メチルメタクリレートスチレン(MS)コポリマーまたはその組合せ;(vi)ポリ塩化ビニル(PVC)、塩素化ポリ塩化ビニル(CPVC)またはその組合せ;(vii)ポリオキシメチレン(polyoxyemethylene)、例えばポリアセタール;(viii)ポリエステル、例えばポリエチレンテレフタレート(PET)、ポリブチレンテレフタレート(PBT)、グリコール変性ポリエチレンテレフタレート(PETG)などのポリエーテル-エステルブロックコポリマーを含むコポリエステルおよび/またはポリエステルエラストマー(COPE)、ポリ乳酸(PLA)、ポリグリコール酸(PGA)、PLAとPGAのコポリマーまたはその組合せ;(ix)ポリカーボネート(PC)、ポリフェニレンスルフィド(PPS)、ポリフェニレンオキシド(PPO)またはその組合せ;あるいはその組合せが含まれる。
いくつかの実施形態では、これらのブレンドには、(i)、(iii)、(vii)、(viii)またはそのいくつかの組合せの群から選択される1つもしくは1つより多くの追加のポリマー材料が含まれる。いくつかの実施形態では、これらのブレンドには、(i)の群から選択される1つまたは1つより多くの追加のポリマー材料が含まれる。いくつかの実施形態では、これらのブレンドには、(iii)の群から選択される1つまたは1つより多くの追加のポリマー材料が含まれる。いくつかの実施形態では、これらのブレンドには、(vii)の群から選択される1つまたは1つより多くの追加のポリマー材料が含まれる。いくつかの実施形態では、これらのブレンドには、(viii)の群から選択される1つまたは1つより多くの追加のポリマー材料が含まれる。
本明細書に記載されるTPU組成物において使用するのに適した追加の任意選択の添加剤は、過度に限定されない。適切な添加剤には、顔料、UV安定剤、UV吸収剤、酸化防止剤、潤滑剤、熱安定剤、加水分解安定剤、架橋結合活性剤、生体適合性難燃剤、層状シリケート、着色剤、補強剤、接着媒介剤(adhesion mediators)、衝撃強度改質剤、抗菌剤、放射線不透化剤(radio opacifier)、フィラーおよびその任意の組合せが含まれる。本明細書に開示される本発明のTPU組成物は、無機充填剤、有機充填剤、または不活性な充填剤(例えば、タルク、炭酸カルシウム、TiO2、理論に拘泥するものではないがTPU組成物の印刷可能性を支援し得ると考えられる粉末)の使用を必要としないことに留意されたい。このように、一部の実施形態では、本開示の技術は充填剤を含んでいてもよく、一部の実施形態では、本開示の技術は充填剤を含んでいなくてもよい。
本明細書に記載されるTPU組成物は、安定剤と称することができる追加の添加剤も含むことができる。安定剤は、酸化防止剤、例えばフェノール類、ホスファイト、チオエステルおよびアミン、光安定剤、例えばヒンダードアミン系光安定剤およびベンゾチアゾールUV吸収剤、および他のプロセス安定剤およびその組合せを含むことができる。一実施形態では好ましい安定剤は、BASFからのIrganox 1010およびChemturaからのNaugard 445である。安定剤は、TPU組成物の約0.1重量%~約5重量%、別の実施形態では約0.1重量%~約3重量%、別の実施形態では約0.5重量%~約1.5重量%の量で使用される。
さらに他の任意選択の添加剤を、本明細書に記載されるTPU組成物において使用することができる。その添加剤には、着色剤、酸化防止剤(フェノール類、ホスファイト、チオエステルおよび/またはアミンを含む)、安定剤、潤滑剤、抑制剤、加水分解安定剤、光安定剤、ヒンダードアミン系光安定剤、ベンゾトリアゾールUV吸収剤、熱安定剤、変色を防止するための安定剤、染料、顔料、補強剤ならびにその組合せが含まれる。
上記の添加剤のすべては、これらの物質についての慣用的な有効量で使用することができる。非難燃剤添加剤は、TPU組成物の全量の約0~約30重量%、一実施形態では約0.1~約25重量%、別の実施形態では約0.1~約20重量%の量で使用することができる。
これらの追加の添加剤は、TPU樹脂の調製のための成分中または反応混合物中に、あるいはTPU樹脂の作製後に混ぜ込むことができる。別のプロセスでは、すべての材料をTPU樹脂と混合し次いで溶融させるか、または、それらをTPU樹脂の溶融物中に直接混ぜ込むことができる。
上記TPU材料は、(I):a)上記芳香族ジイソシアネート成分;b)上記ポリオール成分;およびc)上記鎖延長剤成分を反応させるステップを含むプロセスによって調製することができ、その反応は、熱可塑性ポリウレタン組成物をもたらす触媒の存在下で実施することができる。
本プロセスは:(II)ステップ(I)のTPU組成物を、上記のもののいずれかを含む1つまたは1つより多くの追加のTPU材料および/またはポリマーを含む1つまたは1つより多くのブレンド成分と混合するステップをさらに含むことができる。
本プロセスは:(II)ステップ(I)のTPU組成物を、上記の追加の添加剤の1つまたは1つより多くと混合するステップをさらに含むことができる。
本プロセスは:(II)ステップ(I)のTPU組成物を、上記のもののいずれかを含
む1つまたは1つより多くの追加のTPU材料および/またはポリマーを含む1つまたは1つより多くのブレンド成分と混合するステップ、および/または:(III)ステップ(I)のTPU組成物を、上記の追加の添加剤の1つまたは1つより多くと混合するステップをさらに含むことができる。
システムおよび方法。
む1つまたは1つより多くの追加のTPU材料および/またはポリマーを含む1つまたは1つより多くのブレンド成分と混合するステップ、および/または:(III)ステップ(I)のTPU組成物を、上記の追加の添加剤の1つまたは1つより多くと混合するステップをさらに含むことができる。
システムおよび方法。
固体自由形状製作システム、および本記載の技術において有用なその使用方法は、過度に限定されない。本記載の技術は、現行の材料および他の熱可塑性ポリウレタンより、医療用のデバイスおよび構成要素の固体自由形状製作に良く適した特定の熱可塑性ポリウレタンを提供することに留意されたい。いくつかの熱溶解積層システムを含むいくつかの固体自由形状製作システムは、それらの装置構成、加工パラメーター等のため、熱可塑性ポリウレタンを含む特定の材料を加工するのにより良く適し得ることに留意されたい。しかし、本記載の技術は、いくつかの熱溶解積層システムを含む固体自由形状製作システムの詳細に焦点を合わせるのではなく、むしろ、本記載の技術は、医療用のデバイスおよび構成要素の固体自由形状製作により良く適した特定の熱可塑性ポリウレタンを提供することに焦点を合わせる。
本発明において有用な押出しタイプ付加製造システムおよびプロセスは、その構築材料を半液体状態まで加熱し、コンピューター制御された経路にしたがってそれを押し出すことによって、その部分を層ごと構築するシステムおよびプロセスを含む。材料は、ストランドまたは樹脂として供給され、分配器からの半連続流および/またはフィラメントとして分配するか、あるいは、個々の液滴として分配することができる。FDMでは、構築物を完成するためにしばしば2つの材料が使用される。モデリング材料を、完成品を構築するために使用する。モデリング材料のための足場として機能するように、支持材料を使用することもできる。構築材料(例えば、TPU)を、そのシステム材料貯蔵部から、一般に二次元平面で動くそのプリントヘッドへ供給し、材料を堆積させて各層を完成させ、続いてそのベースを第3の軸に沿って新たなレベルおよび/または平面へ移動させて次の層が開始される。そのシステムが構築をし終わったら、使用者は、支持材料を取り外すか、またはさらにはそれを溶解させて、すぐに使える部分を残すことができる。一部の実施形態では、付加製造システムおよびプロセスは、本明細書に開示される本発明のTPUとは異なるTPUを含む支持材料を、含む。一部の実施形態では、システムおよびプロセスは、支持材料を含まない。
本発明のSLSに有用な付加製造システムおよびプロセスの粉末または粒状タイプは、材料、例えばTPUの小粒子を溶融して所望の三次元形状を有する塊にするのに、高出力レーザー(例えば、二酸化炭素レーザー)の使用を含む。層の、選択的溶融による生成は、粉末形態の材料の層を堆積し、層の一部分または領域を選択的に融解し、粉末の新しい層を堆積し、再び前記層の一部分を融解し、かつこの手法を、所望の物体が得られるまで継続することからなる、物品を生成するための方法である。融解される層の部分の選択性は、例えば、吸収剤、阻害剤、マスクを使用することによって、または例えばレーザーもしくは電磁ビームなどの集束エネルギーの入力を介して得られる。層の付加による焼結が好ましく、特にレーザーを使用した焼結によるラピッドプロトタイピングが好ましい。ラピッドプロトタイピングは、レーザーを使用して重ねられた粉末層を焼結することにより、生成されることになる物品の三次元画像から器具なしでかつ機械加工なしで、複雑な形状の部品を得るのに使用される方法である。レーザー焼結によるラピッドプロトタイピングに関する一般的情報は、米国特許第6,136,948号と出願WO96/06881および米国特許出願公開第20040138363号とで提供されている。
これらの方法を実施するための機械は、粉末を供給する2つのピストンにより左右で取り囲まれている、生成ピストン上の構築チャンバーと、レーザーと、ローラーなどの粉末
を放散させるための手段とを含んでいてもよい。チャンバーは一般に、変形が回避されるよう一定温度で維持される。
を放散させるための手段とを含んでいてもよい。チャンバーは一般に、変形が回避されるよう一定温度で維持される。
WO01/38061およびEP1015214に記載されたものなどのレーザー印加によるその他の生成方法も、適切である。これら2つの方法は、粉末を融解するのに赤外線加熱を使用する。融解部分の選択性は、第1の方法の場合には阻害剤の使用によって、第2の方法の場合にはマスクの使用によって得られる。別の方法は、DE10311438に記載されている。この方法において、ポリマーを融解するためのエネルギーはマイクロ波発生器によって供給され、選択性は、サセプターを使用することによって得られる。
本開示の技術は、本記載のシステムおよび方法における本記載の熱可塑性ポリウレタンの使用、およびそれから作製された医療用のデバイスおよび構成要素をさらに提供する。
医療用のデバイス、構成要素、および応用例
医療用のデバイス、構成要素、および応用例
本明細書で記載されるプロセスは、様々な医療用のデバイスおよび構成要素を生成するのに、本明細書に記載される熱可塑性ポリウレタンを利用してもよい。
すべての付加製造と同様に、ラピッドプロトタイピングおよび新製品開発の一部として、慣用的部分および/または一度きりの部分の作製の一部として、あるいは、物品の多数の大量生産が保証されていない、および/または実際的でない同様の応用例での、物品の作製におけるそうした技術のために特に価値がある。
本発明の組成物から付加製造され得る有用な口腔ケア用のデバイスおよび構成成分は、歯科用アライナー、維持装置、矯正デバイスなどを含む。本発明の組成物から付加製造され得る有用な医療用のデバイスおよび構成成分は、副子、外部支持装具、矯正デバイスなどを含む。
記載される各化学成分の量は、別段の指定のない限り、市販の材料中に慣用的に存在し得る任意の溶媒または希釈油を除いて、すなわち、活性化学物質ベースで提示される。しかし、別段の指定のない限り、本明細書で参照する各化学物質または組成物は、異性体、副生成物、誘導体および、商用グレード中に存在すると通常理解される他のそうした材料を含み得る商用グレード材料であると解釈すべきである。
上記材料の一部は最終処方物中で相互作用する可能性があり、その結果、最終処方物の成分が、当初添加されたものと異なっている可能性があることは公知である。例えば、金属イオン(例えば、難燃剤の金属イオン)は、他の分子の他の酸性またはアニオン性部位に移動し得る。その目的とする使用において本明細書に記載される技術の組成物を使用して形成される生成物を含む、それによって形成される生成物は、容易に記載することができない可能性がある。それにもかかわらず、すべてのそうした改変物および反応生成物は本明細書に記載される技術の範囲に含まれ;本明細書に記載される技術は、上記の成分を混合することによって調製される組成物を包含する。
以下の非限定的な実施例を参照すれば、本明細書に記載される技術をより良く理解することができる。
実施例1
実施例1
材料
いくつかの熱可塑性ポリウレタン(TPU)を調製し、口腔ケア用のデバイスの直接固体自由形状製作におけるそれらの使用の適切性について評価する。本発明のTPU-Aは
、ポリオールに対する鎖延長剤のモル比が約31.3である、ポリエーテルポリオールを含有するTPUである。本発明のTPU-Bは、ポリオールに対する鎖延長剤のモル比が約178である、エチレンオキシドでキャップされたプロピレンオキシドポリオールを含有するTPUである。本発明のTPU-Cは、ポリオールに対する鎖延長剤のモル比が約29.7である、ポリエステルポリオールを含有するTPUである。本発明のTPU-Dは、ポリオールを含有しない、したがって鎖延長剤に対するポリオールの無限のモル比を有する、TPUである。
いくつかの熱可塑性ポリウレタン(TPU)を調製し、口腔ケア用のデバイスの直接固体自由形状製作におけるそれらの使用の適切性について評価する。本発明のTPU-Aは
、ポリオールに対する鎖延長剤のモル比が約31.3である、ポリエーテルポリオールを含有するTPUである。本発明のTPU-Bは、ポリオールに対する鎖延長剤のモル比が約178である、エチレンオキシドでキャップされたプロピレンオキシドポリオールを含有するTPUである。本発明のTPU-Cは、ポリオールに対する鎖延長剤のモル比が約29.7である、ポリエステルポリオールを含有するTPUである。本発明のTPU-Dは、ポリオールを含有しない、したがって鎖延長剤に対するポリオールの無限のモル比を有する、TPUである。
各TPU材料を試験して、選択された自由形状製作プロセスで使用するためのそれらの適切性を決定する。各TPU材料を、一軸スクリュー押出し機を使用して樹脂から約1.8mmの直径のロッドに押し出す。引張りバーを、熱溶解積層プロセスを利用して、MakerBot 2Xデスクトップ3Dプリンター上に印刷するが、このプリンターは、MakerBot Desktop Software Version 3.7を下記の試験パラメーターで実行するものである:
押出し温度 200℃~230℃
構築プラットフォーム温度 40℃~150℃
印刷速度 30mm/秒~120mm/秒
押出し温度 200℃~230℃
構築プラットフォーム温度 40℃~150℃
印刷速度 30mm/秒~120mm/秒
結果により示されるように、本発明のTPU組成物は、固体自由形状製作に適切な組成物を提供する。
実施例2
実施例2
本発明のTPU組成物Dの三次元印刷サンプルを、同じ組成の標準的な射出成形TPU材料と比較して、ASTM D412に従って、「x」、「y」および「z」軸(ASTM 52921によって特定される)における引張強度および伸びについて評価した。結果を、以下の表2に示す。
表2に見られ得るように、本発明の三次元印刷TPU材料の最終的な引張強度は、xz軸方向を使用して印刷された場合、射出成形材料のものと同等である。
分子量分布は、Watersモデル515ポンプ、Watersモデル717オートサンプラーおよび40℃で保持されたWatersモデル2414屈折率検出器を備えたWatersゲル浸透クロマトグラフ(GPC)で測定することができる。GPC条件は、40℃の温度、Phenogel Guard+2×混合D(5u)、300×7.5mmのカラムセット、250ppmのブチル化ヒドロキシトルエンで安定化したテトラヒドロフラン(THF)の移動相、1.0ml/minの流量、50μlの注入量、試料濃度約0.12%、およびWaters Empower Pro Softwareを使用したデータ取得であってよい。一般に少量、一般に約0.05gのポリマーを、20mlの安定化HPLCグレードTHFに溶解し、0.45ミクロンのポリテトラフルオロエチレンの使い捨て型フィルター(Whatman)でろ過し、GPCに注入する。分子量校正曲線は、Polymer LaboratoriesからのEasiCal(登録商標)ポリスチレン標準品で確立することができる。
上記に具体的に挙げられているかどうかに関係なく、優先権の主張がなされる任意の先の出願を含む上記に参照した文献のそれぞれを参照により本明細書に組み込む。任意の文献への言及は、そうした文献が、従来技術としての資格を有する、または任意の権限において当業者の一般的知見を構成すると認めるものではない。実施例を除いて、または別段の明らかな指定のない限り、材料の量、反応条件、分子量、炭素原子数などを指定する本記載におけるすべての数量は、「約」という用語で修飾されているものと理解されたい。本明細書で示される量、範囲および比の上限および下限は、独立に組み合わせることができることを理解されたい。同様に、本明細書に記載される技術の各要素についての範囲および量は、他の要素のいずれかについての範囲および量と一緒に使用することができる。
「含む(including)」、「含む(containing)」または「~を特徴とする(characterized by)」と同意語である、本明細書で使用する
移行用語「含む(comprising)」は、包括的またはオープンエンド(open-ended)であり、言及されていない追加的な要素または方法ステップを排除するものではない。しかし、本明細書での「含むこと(comprising)」の各言及において、この用語は、代替の実施形態として、「~から本質的になる(consisting essentially of)」および「~からなる(consisting of)」という語句も包含するものとする。ここで、「~からなる」は、指定されていない任意の要素またはステップを排除し、「~から本質的になる」は、考慮下にある組成物または方法の基本的および新規な特徴に実質的に影響を及ぼすことのない、言及されていない追加的な要素またはステップの包含を許容する。すなわち、「~から本質的になる」は、考慮下にある組成物の基本的および新規な特徴に実質的に影響を及ぼすことのない物質の包含を許容する。
移行用語「含む(comprising)」は、包括的またはオープンエンド(open-ended)であり、言及されていない追加的な要素または方法ステップを排除するものではない。しかし、本明細書での「含むこと(comprising)」の各言及において、この用語は、代替の実施形態として、「~から本質的になる(consisting essentially of)」および「~からなる(consisting of)」という語句も包含するものとする。ここで、「~からなる」は、指定されていない任意の要素またはステップを排除し、「~から本質的になる」は、考慮下にある組成物または方法の基本的および新規な特徴に実質的に影響を及ぼすことのない、言及されていない追加的な要素またはステップの包含を許容する。すなわち、「~から本質的になる」は、考慮下にある組成物の基本的および新規な特徴に実質的に影響を及ぼすことのない物質の包含を許容する。
本明細書に記載される本技術を例示する目的で、特定の代表的実施形態および詳細を示してきたが、本発明の範囲を逸脱することなく、様々な変更および改変をそこで行うことができることは当業者に明らかである。これに関して、本明細書に記載される技術の範囲は、添付の特許請求の範囲によってのみ限定されるものとする。
本発明の好ましい実施形態によれば、例えば、以下が提供される。
(項1)
(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物
を含む、口腔ケア用のデバイスまたは構成要素。
(項2)
前記鎖延長剤成分が、1,6-ヘキサンジオール(HDO)、1,4-シクロヘキサンジメタノール(CHDM)、またはその組合せを含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項3)
前記芳香族ジイソシアネートが、MDIを含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項4)
前記付加製造が、熱溶解積層または選択的レーザー焼結を含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項5)
前記熱可塑性ポリウレタンが生体適合性である、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項6)
ポリオール成分をさらに含む、上記項1のいずれかに記載の口腔ケア用のデバイスまたは構成要素。
(項7)
ポリオール成分に対する鎖延長剤のモル比が25.0より大きい、上記項6に記載の口腔ケア用のデバイスまたは構成要素。
(項8)
前記ポリオール成分が少なくとも650の数平均分子量を有する、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項9)
前記ポリオール成分が、PTMEG、エチレンオキシドキャップされたプロピレンオキシド、またはその組合せの1つまたは1つより多くを含むポリエーテルポリオールを含む、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項10)
前記ポリオール成分が、ポリカプロラクトンを含むポリエステルポリオールを含む、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項11)
前記鎖延長剤成分が前記組成物の総重量の25重量%~35重量%である、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項12)
前記ポリイソシアネート成分が、TDI、IPDI、LDI、BDI、PDI、CHDI、TODI、NDI、HXDIまたはその任意の組合せをさらに含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項13)
前記鎖延長剤成分がHDO/CHDMを含み、前記ポリオール成分がポリ(テトラメチレンエーテルグリコール)を含む、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項14)
前記熱可塑性ポリウレタンが、1つまたは1つより多くの着色剤、酸化防止剤(フェノール類、ホスファイト、チオエステルおよび/またはアミンを含む)、放射線不透化剤、安定剤、潤滑剤、抑制剤、加水分解安定剤、光安定剤、ヒンダードアミン系光安定剤、ベン
ゾトリアゾールUV吸収剤、熱安定剤、変色を防止するための安定剤、染料、顔料、補強剤またはその任意の組合せをさらに含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項15)
前記口腔ケア用のデバイスまたは構成要素が、歯科用アライナー、歯科用維持装置、または矯正デバイスの1つまたは1つより多くを含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項16)
前記口腔ケア用のデバイスまたは構成要素が、患者に個人化されている、上記項15に記載の口腔ケア用のデバイスまたは構成要素。
(項17)
(I)物体の固体自由形状製作のためのシステムを動作させるステップを含む、三次元の口腔ケア用のデバイスまたは構成要素を直接製作する方法であって、
前記システムが、(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリオール成分から誘導された熱可塑性ポリウレタンを含む構築材料から三次元のまたは口腔ケア用または医療用のデバイスまたは構成要素を形成するように動作する、固体自由形状製作装置を含む、方法。
(項18)
(a)芳香族ジイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリエーテルまたはポリエステルポリオール成分から誘導された、選択的に堆積された熱可塑性ポリウレタン組成物
を含む、直接形成された口腔ケア用のデバイスまたは構成要素。
(項19)
(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物
を含む、医療用のデバイスまたは構成要素。
(項20)
前記医療用のデバイスまたは構成要素が、副子、外部支持装具、または矯正デバイスのうちの1つまたは1つより多くを含む、上記項19に記載の医療用のデバイスまたは構成要素。
(項1)
(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物
を含む、口腔ケア用のデバイスまたは構成要素。
(項2)
前記鎖延長剤成分が、1,6-ヘキサンジオール(HDO)、1,4-シクロヘキサンジメタノール(CHDM)、またはその組合せを含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項3)
前記芳香族ジイソシアネートが、MDIを含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項4)
前記付加製造が、熱溶解積層または選択的レーザー焼結を含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項5)
前記熱可塑性ポリウレタンが生体適合性である、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項6)
ポリオール成分をさらに含む、上記項1のいずれかに記載の口腔ケア用のデバイスまたは構成要素。
(項7)
ポリオール成分に対する鎖延長剤のモル比が25.0より大きい、上記項6に記載の口腔ケア用のデバイスまたは構成要素。
(項8)
前記ポリオール成分が少なくとも650の数平均分子量を有する、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項9)
前記ポリオール成分が、PTMEG、エチレンオキシドキャップされたプロピレンオキシド、またはその組合せの1つまたは1つより多くを含むポリエーテルポリオールを含む、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項10)
前記ポリオール成分が、ポリカプロラクトンを含むポリエステルポリオールを含む、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項11)
前記鎖延長剤成分が前記組成物の総重量の25重量%~35重量%である、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項12)
前記ポリイソシアネート成分が、TDI、IPDI、LDI、BDI、PDI、CHDI、TODI、NDI、HXDIまたはその任意の組合せをさらに含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項13)
前記鎖延長剤成分がHDO/CHDMを含み、前記ポリオール成分がポリ(テトラメチレンエーテルグリコール)を含む、上記項7に記載の口腔ケア用のデバイスまたは構成要素。
(項14)
前記熱可塑性ポリウレタンが、1つまたは1つより多くの着色剤、酸化防止剤(フェノール類、ホスファイト、チオエステルおよび/またはアミンを含む)、放射線不透化剤、安定剤、潤滑剤、抑制剤、加水分解安定剤、光安定剤、ヒンダードアミン系光安定剤、ベン
ゾトリアゾールUV吸収剤、熱安定剤、変色を防止するための安定剤、染料、顔料、補強剤またはその任意の組合せをさらに含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項15)
前記口腔ケア用のデバイスまたは構成要素が、歯科用アライナー、歯科用維持装置、または矯正デバイスの1つまたは1つより多くを含む、上記項1に記載の口腔ケア用のデバイスまたは構成要素。
(項16)
前記口腔ケア用のデバイスまたは構成要素が、患者に個人化されている、上記項15に記載の口腔ケア用のデバイスまたは構成要素。
(項17)
(I)物体の固体自由形状製作のためのシステムを動作させるステップを含む、三次元の口腔ケア用のデバイスまたは構成要素を直接製作する方法であって、
前記システムが、(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリオール成分から誘導された熱可塑性ポリウレタンを含む構築材料から三次元のまたは口腔ケア用または医療用のデバイスまたは構成要素を形成するように動作する、固体自由形状製作装置を含む、方法。
(項18)
(a)芳香族ジイソシアネート成分、(b)鎖延長剤成分、および(c)任意選択のポリエーテルまたはポリエステルポリオール成分から誘導された、選択的に堆積された熱可塑性ポリウレタン組成物
を含む、直接形成された口腔ケア用のデバイスまたは構成要素。
(項19)
(a)芳香族ジイソシアネートを含むポリイソシアネート成分、(b)鎖延長剤成分、および任意選択で(c)ポリオール成分から誘導された、付加製造された熱可塑性ポリウレタン組成物
を含む、医療用のデバイスまたは構成要素。
(項20)
前記医療用のデバイスまたは構成要素が、副子、外部支持装具、または矯正デバイスのうちの1つまたは1つより多くを含む、上記項19に記載の医療用のデバイスまたは構成要素。
Claims (1)
- 明細書に記載の発明。