JP2021107687A - Flooring material - Google Patents

Flooring material Download PDF

Info

Publication number
JP2021107687A
JP2021107687A JP2021075181A JP2021075181A JP2021107687A JP 2021107687 A JP2021107687 A JP 2021107687A JP 2021075181 A JP2021075181 A JP 2021075181A JP 2021075181 A JP2021075181 A JP 2021075181A JP 2021107687 A JP2021107687 A JP 2021107687A
Authority
JP
Japan
Prior art keywords
denim
layer
resin
fabric
laminated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2021075181A
Other languages
Japanese (ja)
Inventor
弘幸 三好
Hiroyuki Miyoshi
弘幸 三好
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tajima Roofing Inc
Original Assignee
Tajima Roofing Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tajima Roofing Inc filed Critical Tajima Roofing Inc
Priority to JP2021075181A priority Critical patent/JP2021107687A/en
Publication of JP2021107687A publication Critical patent/JP2021107687A/en
Pending legal-status Critical Current

Abstract

To provide a flooring material that prevents the generation of frays and tears of fiber and in which denim textures are laminated.SOLUTION: A flooring material 1 comprises: a denim layer 10 that includes a denim texture 11, a first resin coating layer 12 laminated at a top surface of the denim texture, and a second resin coating layer 13 laminated at an undersurface of the denim texture; and a base material 20 laminated under the denim layer.SELECTED DRAWING: Figure 2

Description

本発明は、デニム生地を積層した床材及びその製造方法に関する。 The present invention relates to a flooring material in which denim fabrics are laminated and a method for producing the same.

デニム生地は強度及び耐久性があることから、主にジーンズや作業衣に使われているが、近年では、衣料用の他に靴、鞄や室内装飾用にも使用されている。例えば特許文献１には、デニム生地を表層に使用した床材が開示されている。 Denim fabric is mainly used for jeans and work clothes because of its strength and durability, but in recent years, it has also been used for shoes, bags and interior decoration in addition to clothing. For example, Patent Document 1 discloses a flooring material using a denim fabric as a surface layer.

特開２００１−３３６２７７号公報Japanese Unexamined Patent Publication No. 2001-336277

しかしながら、デニム生地をそのまま床材の表層として使用すると、歩行による繊維のほつれや破れが発生し、汚れが付着する等の不具合が生じる場合があった。また、デニム生地を塩化ビニル樹脂等に接着剤等を用いて接着する場合、接着剤が硬化するまで時間がかかるため非効率で生産性が低い。 However, when the denim fabric is used as it is as the surface layer of the flooring material, the fibers may be frayed or torn due to walking, and problems such as dirt adhering may occur. Further, when the denim cloth is adhered to a vinyl chloride resin or the like using an adhesive or the like, it takes time for the adhesive to cure, which is inefficient and low in productivity.

１つの側面では、本発明は繊維のほつれや破れが発生するのを防止された、デニム生地を積層した床材を提供することを目的とする。また、別の側面では効率的にデニム生地が積層された床材を製造する製造方法を提供することを目的とする。 On one side, it is an object of the present invention to provide a flooring material laminated with denim fabric, which is prevented from causing fraying and tearing of fibers. Another aspect is to provide a manufacturing method for efficiently manufacturing a flooring material in which denim fabrics are laminated.

上記課題を解決するために、１つの形態によれば、デニム生地と、デニム生地の上面に積層される第１樹脂コーティング層と、デニム生地の下面に積層される第２樹脂コーティング層と、を有するデニム層と、デニム層の下方に積層される基材と、を備える、デニム生地を積層した床材を提供する。 In order to solve the above problems, according to one form, the denim fabric, the first resin coating layer laminated on the upper surface of the denim fabric, and the second resin coating layer laminated on the lower surface of the denim fabric are provided. Provided is a floor material in which a denim fabric is laminated, which comprises a denim layer having a denim layer and a base material laminated below the denim layer.

また、別の形態によれば、デニム生地を積層した床材の製造方法であって、デニム生地の上面に第１樹脂コーティングを積層し、デニム生地の下面に第２樹脂コーティングを積層して、デニム層を形成する工程と、熱ラミネートにより、デニム層の下面に基材を積層する工程と、を備える、床材の製造方法を提供する。 Further, according to another form, it is a method of manufacturing a floor material in which denim cloth is laminated, in which a first resin coating is laminated on the upper surface of the denim cloth and a second resin coating is laminated on the lower surface of the denim cloth. Provided is a method for manufacturing a floor material, comprising a step of forming a denim layer and a step of laminating a base material on the lower surface of the denim layer by thermal laminating.

開示の床材により繊維のほつれや破れの発生が防止される。また、デニム生地を積層した床材を効率的に製造する製造方法が提供される。 The disclosed flooring material prevents the occurrence of fraying and tearing of fibers. Further, a manufacturing method for efficiently manufacturing a flooring material in which denim fabrics are laminated is provided.

第一実施形態のデニム生地を積層した床タイルを示す断面図である。It is sectional drawing which shows the floor tile which laminated the denim cloth of 1st Embodiment. 第一実施形態のデニム生地を積層した床タイルの作製方法を示す図であり、（ａ）はデニム生地を含むデニム層を形成する工程を示す図、（ｂ）はデニム層を基材に積層する工程を示す図である。It is a figure which shows the manufacturing method of the floor tile which laminated the denim cloth of 1st Embodiment, (a) is a figure which shows the process of forming the denim layer containing the denim cloth, (b) is laminated with the denim layer on the base material. It is a figure which shows the process to perform. 第二実施形態のデニム生地を積層した床タイルを示す断面図である。It is sectional drawing which shows the floor tile which laminated the denim cloth of the 2nd Embodiment. 第二実施形態のデニム生地を積層した床タイルの作製方法を示す図であり、（ａ）はデニム層を形成する工程を示す図、（ｂ）はガラス不織布を含む中間積層体を形成する工程を示す図、（ｃ）はデニム層を中間積層体に積層して床タイルを形成する工程を示す図である。It is a figure which shows the manufacturing method of the floor tile which laminated the denim cloth of the 2nd Embodiment, (a) is the figure which shows the step of forming a denim layer, (b) is the step of forming an intermediate laminate containing a glass non-woven fabric. (C) is a diagram showing a step of laminating a denim layer on an intermediate laminate to form a floor tile.

以下、添付図面を用いて本出願の実施の形態を、具体的な実施例に基づいて詳細に説明する。また、以下の実施の形態において同一又は類似の要素には共通の参照符号を付けて示し、理解を容易にするために、これらの図面は縮尺を適宜変更している。 Hereinafter, embodiments of the present application will be described in detail with reference to the accompanying drawings, based on specific examples. Further, in the following embodiments, the same or similar elements are indicated by a common reference reference numeral, and the scales of these drawings are appropriately changed in order to facilitate understanding.

図１は、第一実施形態の床タイル１を示す断面図である。床タイル１は床材の一例である。床タイル１は、樹脂製の基材２０と、樹脂製の基材２０の上面に積層されたデニム層１０を備える。デニム層１０は、デニム生地１１と、デニム生地１１の上面に積層される第１樹脂コーティング層１２と、デニム生地１１の下面に積層される第２樹脂コーティング層１３とを有する。基材２０は、塩化ビニル樹脂による板状の部材である。 FIG. 1 is a cross-sectional view showing the floor tile 1 of the first embodiment. The floor tile 1 is an example of a flooring material. The floor tile 1 includes a resin base material 20 and a denim layer 10 laminated on the upper surface of the resin base material 20. The denim layer 10 has a denim fabric 11, a first resin coating layer 12 laminated on the upper surface of the denim fabric 11, and a second resin coating layer 13 laminated on the lower surface of the denim fabric 11. The base material 20 is a plate-shaped member made of vinyl chloride resin.

デニム生地１１は、１０番手以上のタテ糸をインディゴによって染色し、ヨコ糸を未晒し糸（染色加工をしていない糸）で綾織りにした、素材が綿の厚地織布である。第１樹脂コーティング層１２は、例えば透明なアクリル樹脂である。第１樹脂コーティング層１２は、ウレタン樹脂、塩化ビニル樹脂であってもよい。第２樹脂コーティング層は、塩化ビニル樹脂である。第２コーティング層は、アクリル樹脂、ウレタン樹脂であってもよい。第１樹脂コーティング層１２及び第２樹脂コーティング層１３を、デニム生地１１にコーティングするには、図２（ａ）に示すように、例えばロールコータ４４を用いて行われる。従来のデニム生地を有する床タイルは、デニム生地がそのまま露出した状態で使用されるため、歩行により力が加わると繊維のほつれ等が生じる場合があった。本実施形態のデニム生地１１が積層された床タイル１は、露出する表面部分に、アクリル樹脂による第１樹脂コーティング層１２がコーティングされ、第１樹脂コーティング層１２により、歩行者による力が加わっても繊維のほつれが生じることが防止される。 The denim fabric 11 is a thick cotton woven fabric in which 10-count or higher warp yarns are dyed with indigo, and weft yarns are twill-woven with unbleached yarns (undyed yarns). The first resin coating layer 12 is, for example, a transparent acrylic resin. The first resin coating layer 12 may be a urethane resin or a vinyl chloride resin. The second resin coating layer is a vinyl chloride resin. The second coating layer may be an acrylic resin or a urethane resin. To coat the first resin coating layer 12 and the second resin coating layer 13 on the denim fabric 11, for example, a roll coater 44 is used as shown in FIG. 2A. Since the floor tiles having the conventional denim fabric are used in a state where the denim fabric is exposed as it is, the fibers may be frayed when a force is applied by walking. In the floor tile 1 on which the denim fabric 11 of the present embodiment is laminated, the exposed surface portion is coated with the first resin coating layer 12 made of acrylic resin, and the force of a pedestrian is applied by the first resin coating layer 12. Also prevents the fibers from fraying.

図２（ａ）及び図２（ｂ）を用いて、図１に示すデニム生地１１が積層された床タイル１の製造方法を説明する。先ず、図２（ａ）に示すように、デニム生地１１の片面に第１樹脂コーティング層１２として透明なアクリル樹脂を、矢印Ａ方向に移動させロールコータ４４を用いて塗布することでコーティングする。その後、第１樹脂コーティング層１２が塗布されたデニム生地１１を、乾燥オーブン４５に通して乾燥させ、巻取機４７により巻き取る。次にデニム生地１１の反対の面に第２樹脂コーティング層１３としての塩化ビニル樹脂を、ロールコータ４４を用いて塗布する。ロールコータ４４により塩化ビニル樹脂を塗布した後、デニム層１０を乾燥オーブン４５により加熱乾燥させる。乾燥したデニム層１０は巻取機４７により巻き取られる（ステップ１）。 A method of manufacturing the floor tile 1 on which the denim fabric 11 shown in FIG. 1 is laminated will be described with reference to FIGS. 2 (a) and 2 (b). First, as shown in FIG. 2A, a transparent acrylic resin as the first resin coating layer 12 is coated on one side of the denim fabric 11 by moving it in the direction of arrow A and applying it using a roll coater 44. Then, the denim cloth 11 coated with the first resin coating layer 12 is passed through a drying oven 45 to be dried, and the denim cloth 11 is wound by a winder 47. Next, the vinyl chloride resin as the second resin coating layer 13 is applied to the opposite surface of the denim fabric 11 using the roll coater 44. After applying the vinyl chloride resin with the roll coater 44, the denim layer 10 is heated and dried in the drying oven 45. The dried denim layer 10 is wound by the winder 47 (step 1).

デニム層１０を形成した後、図２（ｂ）に示すように、デニム層１０と基材２０を熱ラミネートロール４０に通し、基材２０の上面にデニム層１０を接着する。その後、積層体５０をタイル打ち抜き機４６に通し、タイル状にカットして床タイル１が完成する（ステップ２）。本実施形態の床タイル１は、デニム生地１１の下面に、第２樹脂コーティング層１３として塩化ビニル樹脂がコーティングされているため、塩化ビニル樹脂と基材２０とを熱ラミネートロール４０により連続的に積層させて接着することができる。そのため、デニム生地１１を有する床タイル１を効率よく製造することができる。 After forming the denim layer 10, as shown in FIG. 2B, the denim layer 10 and the base material 20 are passed through a thermal laminate roll 40, and the denim layer 10 is adhered to the upper surface of the base material 20. After that, the laminated body 50 is passed through a tile punching machine 46 and cut into tiles to complete the floor tile 1 (step 2). In the floor tile 1 of the present embodiment, since the lower surface of the denim fabric 11 is coated with vinyl chloride resin as the second resin coating layer 13, the vinyl chloride resin and the base material 20 are continuously coated with the heat laminating roll 40. It can be laminated and bonded. Therefore, the floor tile 1 having the denim fabric 11 can be efficiently manufactured.

図３は、第二実施形態である床タイル２を示す断面図である。床タイル２は床材の一例である。図３に示すように、床タイル２は、図１に示す床タイル１と同様、デニム層１０と基材２０とを備える。床タイル２は、デニム層１０と基材２０との間に強化層３０を更に備える。強化層３０は、ガラス不織布３１と、ガラス不織布３１の上面に積層される第１樹脂層３２と、ガラス不織布３１の下面に積層される第２樹脂層３３を備える。第１樹脂層３２及び第２樹脂層３３は塩化ビニル樹脂により作製されるが、アクリル樹脂、ウレタン樹脂により作製されてもよい。 FIG. 3 is a cross-sectional view showing the floor tile 2 according to the second embodiment. The floor tile 2 is an example of a flooring material. As shown in FIG. 3, the floor tile 2 includes a denim layer 10 and a base material 20 like the floor tile 1 shown in FIG. The floor tile 2 further includes a reinforcing layer 30 between the denim layer 10 and the base material 20. The reinforcing layer 30 includes a glass nonwoven fabric 31, a first resin layer 32 laminated on the upper surface of the glass nonwoven fabric 31, and a second resin layer 33 laminated on the lower surface of the glass nonwoven fabric 31. The first resin layer 32 and the second resin layer 33 are made of vinyl chloride resin, but may be made of acrylic resin or urethane resin.

デニム層１０と樹脂製の基材２０とは線膨張率に差があるため反りが発生する場合がある。床タイル２では、ガラス不織布３１を含む強化層３０を、デニム層１０と基材２０との間に設けることにより、床タイル２の反りを防止している。 Since there is a difference in linear expansion coefficient between the denim layer 10 and the resin base material 20, warpage may occur. In the floor tile 2, the reinforcing layer 30 including the glass non-woven fabric 31 is provided between the denim layer 10 and the base material 20 to prevent the floor tile 2 from warping.

また、本実施形態の床タイル２では、ガラス不織布３１の位置が、床タイル２全体の厚みＴ１の中心Ｃより上方になるよう設定される。例えば、床タイル２の厚みＴ１を５ｍｍとする場合は、デニム層１０、第１樹脂層３２、ガラス不織布３１、第２樹脂層３３、基材２０の厚みを夫々、０．７０、０．６８、０．４０、０．８５、２．３７ｍｍとすることで、ガラス不織布３１を床タイル２全体の厚みＴ１の中心Ｃより上方に配置することができる。デニム層１０と基材２０である塩化ビニル樹脂との線膨張率の差により、床タイル２では反りが生じやすくなるが、ガラス不織布３１の位置が、床タイル全体の厚みＴ１の中心Ｃより上方に配置されることで、床タイル２の反りを防止することができる。 Further, in the floor tile 2 of the present embodiment, the position of the glass nonwoven fabric 31 is set to be above the center C of the thickness T1 of the entire floor tile 2. For example, when the thickness T1 of the floor tile 2 is 5 mm, the thicknesses of the denim layer 10, the first resin layer 32, the glass non-woven fabric 31, the second resin layer 33, and the base material 20 are 0.70 and 0.68, respectively. , 0.40, 0.85, 2.37 mm, the glass non-woven fabric 31 can be arranged above the center C of the thickness T1 of the entire floor tile 2. Due to the difference in linear expansion coefficient between the denim layer 10 and the vinyl chloride resin which is the base material 20, warpage is likely to occur in the floor tile 2, but the position of the glass non-woven fabric 31 is above the center C of the thickness T1 of the entire floor tile. By arranging the tiles in, it is possible to prevent the floor tile 2 from warping.

図４（ａ）〜図４（ｃ）を用いて、第二実施形態の床タイル２の製造方法について説明する。第一実施形態の床タイル１と同様に、デニム生地１１を準備し、ロールコータ４４を用いてデニム生地１１の片面に第１樹脂コーティング層１２としてのアクリル樹脂を塗布する。アクリル樹脂が塗布されたデニム生地１１を乾燥オーブン４５により加熱乾燥させる。そして、デニム生地１１の反対面に、第２樹脂コーティング層１３として塩化ビニル樹脂を、ロールコータ４４を用いて塗布する。塩化ビニル樹脂が塗布されたデニム生地１１を乾燥オーブン４５により加熱乾燥させ、デニム層１０を巻取機４７により巻き取る（ステップ１）。 The method for manufacturing the floor tile 2 of the second embodiment will be described with reference to FIGS. 4 (a) to 4 (c). Similar to the floor tile 1 of the first embodiment, the denim fabric 11 is prepared, and an acrylic resin as the first resin coating layer 12 is applied to one side of the denim fabric 11 using a roll coater 44. The denim cloth 11 coated with the acrylic resin is heated and dried in a drying oven 45. Then, a vinyl chloride resin as the second resin coating layer 13 is applied to the opposite surface of the denim fabric 11 using a roll coater 44. The denim fabric 11 coated with the vinyl chloride resin is heated and dried in a drying oven 45, and the denim layer 10 is wound up by a winder 47 (step 1).

次に、図４（ｂ）に示すように、基材２０と、第２樹脂層３３としての塩化ビニル樹脂シートと、ガラス不織布３１とを第１熱ラミネートロール４１に通して、中間積層体３４を形成する（ステップ２）。 Next, as shown in FIG. 4B, the base material 20, the vinyl chloride resin sheet as the second resin layer 33, and the glass non-woven fabric 31 are passed through the first thermal laminate roll 41, and the intermediate laminate 34 is passed. (Step 2).

次に、図４（ｃ）に示すように、中間積層体３４を加熱装置４３により温めたのち、中間積層体３４と、第１樹脂層３２としての塩化ビニル樹脂シートと、ステップ１で作製したデニム層１０とを、第２熱ラミネートロール４２に通してラミネートし、積層体３５を作製する。そして、積層体３５をタイル打ち抜き機４６に通し、タイル状にカットして床タイル２が完成する（ステップ３）。第２熱ラミネートロール４２により連続的に、デニム層１０、第１樹脂層３２及び第２樹脂層３３を基材２０に積層させることができるため、デニム生地の風合いを活かした床タイル２を効率よく製造することができる。 Next, as shown in FIG. 4C, the intermediate laminate 34 was heated by the heating device 43, and then the intermediate laminate 34 and the vinyl chloride resin sheet as the first resin layer 32 were prepared in step 1. The denim layer 10 and the denim layer 10 are passed through a second heat laminating roll 42 and laminated to prepare a laminated body 35. Then, the laminated body 35 is passed through a tile punching machine 46 and cut into tiles to complete the floor tile 2 (step 3). Since the denim layer 10, the first resin layer 32, and the second resin layer 33 can be continuously laminated on the base material 20 by the second heat laminating roll 42, the floor tile 2 utilizing the texture of the denim fabric can be efficiently laminated. Can be manufactured well.

（実施例１）
発明者らは実際に床タイル２を製造して、本発明に係る床タイル２の有効性を実験により確認した。デニム生地１１としては、カイハラ産業株式会社製の布帛２００７−ＡＣＴを用意した。デニム生地１１の片面に水系アクリル樹脂５００ｇ／ｍ２をロールコータ４４で塗布し加熱乾燥させ、水系アクリル樹脂により第１樹脂コーティング層１２を設けた。また、デニム生地の反対面に塩化ビニル樹脂６００ｇ／ｍ２を同様の方法で塗布し乾燥させて、塩化ビニル樹脂により第２樹脂コーティング層１３を設けデニム層１０を作製した。デニム層１０のアクリル樹脂の厚みは１２〜１５μｍ、塩化ビニル樹脂の厚みは６０〜９０μｍになるよう調整した。また、熱ラミネートロールによりガラス不織布３１を積層した。また、ガラス不織布３１の位置は、床タイルの全厚Ｔ１の半分以上に位置するよう基材２０の厚さを調整した。
（実施例２）
デニム生地１１の表面に第１樹脂コーティング層１２として水系アクリル樹脂とは異なるウレタン樹脂を塗布して作製し、それ以外の条件は実施例１と同一の条件で床タイル２を作製した。 (Example 1)
The inventors actually manufactured the floor tile 2 and confirmed the effectiveness of the floor tile 2 according to the present invention by experiments. As the denim fabric 11, a fabric 2007-ACT manufactured by Kaihara Sangyo Co., Ltd. was prepared. A water-based acrylic resin 500 g / m 2 was applied to one side of the denim fabric 11 with a roll coater 44, dried by heating, and the first resin coating layer 12 was provided by the water-based acrylic resin. Further, 600 g / m 2 of vinyl chloride resin was applied to the opposite surface of the denim cloth in the same manner and dried to provide a second resin coating layer 13 with vinyl chloride resin to prepare a denim layer 10. The thickness of the acrylic resin of the denim layer 10 was adjusted to 12 to 15 μm, and the thickness of the vinyl chloride resin was adjusted to 60 to 90 μm. Further, the glass non-woven fabric 31 was laminated by a heat laminating roll. Further, the thickness of the base material 20 was adjusted so that the position of the glass non-woven fabric 31 was located at half or more of the total thickness T1 of the floor tile.
(Example 2)
The surface of the denim fabric 11 was prepared by applying a urethane resin different from the water-based acrylic resin as the first resin coating layer 12, and the floor tile 2 was prepared under the same conditions as in Example 1 except for the conditions.

（比較例１）
比較例１として、デニム生地１１に、第１樹脂コーティング層１２としての水系アクリル樹脂またはウレタン樹脂を塗布せず、他の条件は全て実施例１及び２と同一の条件で床タイルを作製した。 (Comparative Example 1)
As Comparative Example 1, the floor tile was prepared under the same conditions as in Examples 1 and 2 without applying the water-based acrylic resin or urethane resin as the first resin coating layer 12 to the denim fabric 11.

（比較例２）
ガラス不織布３１の位置をタイル全厚Ｔ１の中心Ｃより、下方に配置した場合であって、それ以外は実施例１と同一の条件で床タイルを作製した。 (Comparative Example 2)
A floor tile was produced under the same conditions as in Example 1 except that the position of the glass nonwoven fabric 31 was arranged below the center C of the tile total thickness T1.

作製した床タイル上を一定期間、被験者に歩行させ、実施例１及び２、比較例１及び２のデニム生地のほつれや反りについて調査した。その結果を以下に示す。

Figure 2021107687
The subjects were allowed to walk on the prepared floor tiles for a certain period of time, and the fraying and warping of the denim fabrics of Examples 1 and 2 and Comparative Examples 1 and 2 were investigated. The results are shown below.
Figure 2021107687

比較実験の結果により、本発明に係るデニム生地１１を積層した床タイル２（実施例１及び２）は、生地繊維のほつれ、破れがなく、反りも発生しないことが分かる。比較例１は、タイルの反りは確認されなかったが、生地繊維のほつれが発生していた。また、比較例２は生地繊維のほつれはないものの反りが発生する場合があった。本実施形態に係る床タイル２を用いれば、デニム生地１１の風合いが損なわれることなく、生地繊維のほつれ、破れが生じるのを防止すると共に、反りを防止し、汚れ付着の少ないデニム生地を積層した床タイル２を提供することができる。
なお、本発明の実施形態の参考例として、下記のものも含まれる。
[参考例]
デニム生地と、前記デニム生地の上面に積層される第１樹脂コーティング層と、
前記デニム生地の下面に積層される第２樹脂コーティング層と、を有するデニム層と、
前記デニム層の下方に積層される樹脂製の基材と、
ガラス不織布と、前記ガラス不織布の上面に積層される第１樹脂層と、前記ガラス不織布の下面に積層される第２樹脂層とを有する補強層であって、前記デニム層と前記基材との間に積層される補強層と、を備える、床材であって、
前記ガラス不織布の位置が前記床材の全体の厚みの中心よりも上方になるよう設定され、前記第１樹脂コーティング層および前記第２樹脂コーティング層は、それぞれ、アクリル樹脂、ウレタン樹脂、塩化ビニル樹脂のうちから選択された樹脂からなる、床材。 From the results of the comparative experiment, it can be seen that the floor tiles 2 (Examples 1 and 2) in which the denim fabric 11 according to the present invention is laminated do not fray or tear the fabric fibers and do not warp. In Comparative Example 1, no warpage of the tile was confirmed, but fraying of the fabric fibers occurred. Further, in Comparative Example 2, although the fabric fibers were not frayed, warpage may occur. By using the floor tile 2 according to the present embodiment, the texture of the denim fabric 11 is not impaired, the fabric fibers are prevented from fraying and tearing, the warp is prevented, and the denim fabric with less dirt adhesion is laminated. The floor tile 2 can be provided.
The following are also included as reference examples of the embodiments of the present invention.
[Reference example]
The denim fabric, the first resin coating layer laminated on the upper surface of the denim fabric, and
A denim layer having a second resin coating layer laminated on the lower surface of the denim fabric, and
A resin base material laminated below the denim layer and
A reinforcing layer having a glass nonwoven fabric, a first resin layer laminated on the upper surface of the glass nonwoven fabric, and a second resin layer laminated on the lower surface of the glass nonwoven fabric, the denim layer and the base material. A flooring material comprising a reinforcing layer laminated between them.
The position of the glass non-woven fabric is set to be above the center of the total thickness of the floor material, and the first resin coating layer and the second resin coating layer are made of an acrylic resin, a urethane resin, and a vinyl chloride resin, respectively. A flooring material made of a resin selected from the above.

１、２ 床タイル
１０ デニム層
１１ デニム生地
１２ 第１樹脂コーティング層
１３ 第２樹脂コーティング層
２０ 基材
３０ 強化層
３１ ガラス不織布
３２ 第１樹脂層
３３ 第２樹脂層
３４ 中間積層体
４０ 熱ラミネートロール
４１ 第１熱ラミネートロール
４２ 第２熱ラミネートロール
４３ 加熱装置
４４ ロールコータ
４５ 乾燥オーブン
４６ タイル打ち抜き機
４７ 巻取機 1, 2 Floor tiles 10 Denim layer 11 Denim fabric 12 1st resin coating layer 13 2nd resin coating layer 20 Base material 30 Reinforcement layer 31 Glass non-woven fabric 32 1st resin layer 33 2nd resin layer 34 Intermediate laminate 40 Thermal laminate roll 41 1st heat laminating roll 42 2nd heat laminating roll 43 Heating device 44 Roll coater 45 Drying oven 46 Tile punching machine 47 Winding machine

Claims (2)

デニム生地と、前記デニム生地の上面に積層される第１樹脂コーティング層と、
前記デニム生地の下面に積層される第２樹脂コーティング層と、を有するデニム層と、
前記デニム層の下方に積層される樹脂製の基材と、
ガラス不織布と、前記ガラス不織布の上面に積層される第１樹脂層と、前記ガラス不織布の下面に積層される第２樹脂層とを有する補強層であって、前記デニム層と前記基材との間に積層される補強層と、を備える、床材であって、
前記ガラス不織布の位置が前記床材の全体の厚みの中心よりも上方になるよう設定され、前記第１樹脂コーティング層および前記第２樹脂コーティング層は、それぞれ、アクリル樹脂、ウレタン樹脂、塩化ビニル樹脂のうちから選択された樹脂からなる、床材。 The denim fabric, the first resin coating layer laminated on the upper surface of the denim fabric, and
A denim layer having a second resin coating layer laminated on the lower surface of the denim fabric, and
A resin base material laminated below the denim layer and
A reinforcing layer having a glass nonwoven fabric, a first resin layer laminated on the upper surface of the glass nonwoven fabric, and a second resin layer laminated on the lower surface of the glass nonwoven fabric, the denim layer and the base material. A flooring material comprising a reinforcing layer laminated between them.
The position of the glass non-woven fabric is set to be above the center of the total thickness of the floor material, and the first resin coating layer and the second resin coating layer are made of an acrylic resin, a urethane resin, and a vinyl chloride resin, respectively. A flooring material made of a resin selected from the above. デニム生地を積層した床材の製造方法であって、
前記デニム生地の上面に第１樹脂コーティング層を積層し、前記デニム生地の下面に第２樹脂コーティング層を積層して、デニム層を形成する工程と、
熱ラミネートにより、ガラス不織布の下面に第２樹脂層を積層し、前記第２樹脂層の下面に基材を積層して、中間積層体を形成する工程と、
熱ラミネートにより、前記デニム層と前記中間積層体との間に第１樹脂層を積層して、前記ガラス不織布と、前記第１樹脂層と、前記第２樹脂層とからなる補強層を形成する工程と、
熱ラミネートにより、前記デニム層の下面に樹脂製の基材を積層する工程と、
を備え、
前記ガラス不織布の位置が前記床材の全体の厚みの中心よりも上方になるよう設定され、前記第１樹脂コーティング層および前記第２樹脂コーティング層は、それぞれ、アクリル樹脂、ウレタン樹脂、塩化ビニル樹脂のうちから選択された樹脂からなる、床材の製造方法。 It is a method of manufacturing flooring made by laminating denim fabric.
A step of laminating a first resin coating layer on the upper surface of the denim fabric and laminating a second resin coating layer on the lower surface of the denim fabric to form a denim layer.
A step of laminating a second resin layer on the lower surface of the glass nonwoven fabric by thermal laminating and laminating a base material on the lower surface of the second resin layer to form an intermediate laminate.
By thermal lamination, the first resin layer is laminated between the denim layer and the intermediate laminate to form a reinforcing layer composed of the glass non-woven fabric, the first resin layer, and the second resin layer. Process and
A step of laminating a resin base material on the lower surface of the denim layer by heat laminating, and
With
The position of the glass non-woven fabric is set to be above the center of the total thickness of the flooring material, and the first resin coating layer and the second resin coating layer are made of an acrylic resin, a urethane resin, and a vinyl chloride resin, respectively. A method for manufacturing a flooring material, which is made of a resin selected from the above.
JP2021075181A 2018-04-25 2021-04-27 Flooring material Pending JP2021107687A (en)