JP2021087616A - Fabric for skin adhesive tape, skin adhesive tape, and medical supply - Google Patents
Fabric for skin adhesive tape, skin adhesive tape, and medical supply Download PDFInfo
- Publication number
- JP2021087616A JP2021087616A JP2019219593A JP2019219593A JP2021087616A JP 2021087616 A JP2021087616 A JP 2021087616A JP 2019219593 A JP2019219593 A JP 2019219593A JP 2019219593 A JP2019219593 A JP 2019219593A JP 2021087616 A JP2021087616 A JP 2021087616A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive tape
- skin adhesive
- woven fabric
- fabric
- skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、皮膚粘着テープ用織物、皮膚粘着テープ、及び医療用品に関する。 The present invention relates to woven fabrics for skin adhesive tapes, skin adhesive tapes, and medical supplies.
従来、指などの小さな傷や、ひじ、ひざなどのすり傷の保護材として絆創膏が医療機関はもとより、一般家庭の必需品として広く普及している。例えば、以下の特許文献１に記載されるように、かかる絆創膏は、適当な大きさ、形の粘着剤層を有する基材の中央にガーゼなどのパッド材を粘着したものがほとんどである。 Conventionally, adhesive plasters have been widely used as a necessary item for general households as well as medical institutions as a protective material for small scratches such as fingers and scratches such as elbows and knees. For example, as described in Patent Document 1 below, most of such adhesive plasters have a pad material such as gauze adhered to the center of a base material having an adhesive layer having an appropriate size and shape.
絆創膏の基材としては、塩化ビニル等のフィルム材が用いられているが、塩化ビニル等のフィルム材は通気性や透湿性に劣り、患部が蒸れたりかぶれたりすることがある。このため、基材に多数の小孔を設けて通気性を確保することが行われている。 A film material such as vinyl chloride is used as the base material of the adhesive plaster, but the film material such as vinyl chloride is inferior in breathability and moisture permeability, and the affected area may get stuffy or rash. Therefore, a large number of small holes are provided in the base material to ensure air permeability.
しかしながら、炊事や洗面等で水がかかったり、風呂で湯につかったりした際に、この小孔を通じて、基材と皮膚との間に水が浸入してしまうことがあった。 However, when water is splashed in cooking or washing, or when it is soaked in hot water in a bath, water may infiltrate between the base material and the skin through these small holes.
本発明は、このような従来の実情に鑑みて提案されたものであり、本発明の目的は、小孔を設けなくても通気性や透湿性を有し、薄くても耐摩耗性に優れた皮膚粘着テープ用織物、皮膚粘着テープ、及び医療用品を提供することにある。 The present invention has been proposed in view of such conventional circumstances, and an object of the present invention is to have breathability and moisture permeability without providing small holes, and to have excellent wear resistance even if it is thin. The purpose of the present invention is to provide woven fabrics for skin adhesive tapes, skin adhesive tapes, and medical supplies.
本発明者らは、皮膚粘着テープ用の基材として、フィルム材や編物に代えて、織物を採用するとともに、該織物について皮膚粘着テープ用の基材としての要求特性を鋭意研究し実験を重ねることにより、特定し、もって、上記目的を達成できることを予想外に見出し、本発明を完成させるに至ったものである。
すなわち、本発明は以下のとおりのものである。
［１］合成長繊維とポリウレタン弾性繊維の複合糸から構成される、皮膚粘着テープ用織物であって、伸長率が経緯ともに２０％〜５０％であり、伸長回復率が経緯ともに８０％以上であり、そして目付が５０ｇ／ｍ２〜１２０ｇ／ｍ２であることを特徴とする、皮膚粘着テープ用織物。
［２］撥水度が初期４級以上である、前記［１］に記載の皮膚粘着テープ用織物。
［３］前記合成長繊維がポリエステル系繊維又はポリアミド系繊維である、［１］又は［２］に記載の皮膚粘着テープ用織物。
［４］前記合成長繊維の繊度が、２０ｄｔｅｘ〜６０ｄｔｅｘである、前記［１］〜［３］のいずれかに記載の皮膚粘着テープ用織物。
［５］スナッグが３級以上である、前記［１］〜［４］のいずれかに記載の皮膚粘着テープ用織物。
［６］
前記織物の厚みが１５μｍ〜４０μｍである、［１］〜［５］のいずれかに記載の皮膚粘着テープ用織物。
［７］前記［１］〜［６］のいずれかに記載の皮膚粘着テープ用織物を用いた皮膚粘着テープ。
［８］前記［７］に記載の皮膚粘着テープを用いた医療用品。
The present inventors adopt a woven fabric instead of a film material or a knitted fabric as a base material for a skin adhesive tape, and diligently research and experiment with the required characteristics of the woven fabric as a base material for a skin adhesive tape. As a result, the present invention has been completed by identifying and unexpectedly finding that the above object can be achieved.
That is, the present invention is as follows.
[1] A woven fabric for skin adhesive tape composed of a composite yarn of synthetic long fibers and polyurethane elastic fibers, which has an elongation rate of 20% to 50% in both warp and weft and a stretch recovery rate of 80% or more in both warp and weft. There, and basis weight is characterized by a 50g / m 2 ~120g / m 2 , textile skin adhesive tape.
[2] The woven fabric for skin adhesive tape according to the above [1], which has a water repellency of 4th grade or higher at the initial stage.
[3] The woven fabric for skin adhesive tape according to [1] or [2], wherein the synthetic long fibers are polyester fibers or polyamide fibers.
[4] The woven fabric for skin adhesive tape according to any one of [1] to [3], wherein the synthetic long fibers have a fineness of 20 dtex to 60 dtex.
[5] The woven fabric for skin adhesive tape according to any one of [1] to [4] above, wherein the snag is grade 3 or higher.
[6]
The woven fabric for skin adhesive tape according to any one of [1] to [5], wherein the woven fabric has a thickness of 15 μm to 40 μm.
[7] A skin adhesive tape using the woven fabric for skin adhesive tape according to any one of the above [1] to [6].
[8] A medical product using the skin adhesive tape according to the above [7].
本発明によれば、織物の繊維材料を限定するともに、織物についての特性を上記のように規定することにより、小孔を設けなくても通気性や透湿性を有し、薄くても耐摩耗性に優れた皮膚粘着テープ用織物、皮膚粘着テープ、及び医療用品を実現することができる。 According to the present invention, by limiting the fiber material of the woven fabric and defining the characteristics of the woven fabric as described above, it has breathability and moisture permeability without providing small holes, and is wear resistant even if it is thin. It is possible to realize a woven fabric for skin adhesive tape, a skin adhesive tape, and a medical product having excellent properties.
以下、本発明を実施するための実施の形態について詳細に説明する。
なお、以下の説明において、「〜」で表されている数値範囲は、上限と下限の数値を含むものとする。
Hereinafter, embodiments for carrying out the present invention will be described in detail.
In the following description, the numerical range represented by "~" shall include the numerical values of the upper limit and the lower limit.
本実施形態の皮膚粘着テープ用織物は、合成長繊維とポリウレタン弾性繊維の複合糸から構成される織物であって、伸長率が経緯ともに２０〜５０％であり、伸長回復率が経緯ともに８０％以上であり、そして目付が５０〜１２０ｇ／ｍ２であることを特徴とする。 The woven fabric for skin adhesive tape of the present embodiment is a woven fabric composed of a composite yarn of synthetic long fibers and polyurethane elastic fibers, and has an elongation rate of 20 to 50% in both warp and weft and an elongation recovery rate of 80% in both warp and weft. The above, and the texture is 50 to 120 g / m 2 .
本実施形態では、合成長繊維とポリウレタン弾性繊維を用いた織物について、各種特性を上記のように規定することにより、薄くても耐摩耗性に優れた皮膚粘着テープ用織物を実現することができる。 In the present embodiment, by defining various characteristics of the woven fabric using synthetic long fibers and polyurethane elastic fibers as described above, it is possible to realize a woven fabric for skin adhesive tape having excellent abrasion resistance even if it is thin. ..
本実施形態の皮膚粘着テープ用織物に用いられる合成長繊維は、特に限定されるものではないが、ポリエステル系繊維又はポリアミド系繊維であることが好ましい。 The synthetic long fibers used in the woven fabric for skin adhesive tape of the present embodiment are not particularly limited, but are preferably polyester fibers or polyamide fibers.
ポリエステル系繊維としては、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリトリメチレンテレフタレートなどからなる繊維が挙げられる。このようなポリエステル系繊維は、医療用具に使用される電子滅菌に対し耐性が高く、好ましく用いられる。特に、ポリエチレンテレフタレートが強度や寸法安定性が高い点でより好ましく使用される。 Examples of polyester fibers include fibers made of polyethylene terephthalate, polybutylene terephthalate, polytrimethylene terephthalate and the like. Such polyester fibers have high resistance to electronic sterilization used in medical devices and are preferably used. In particular, polyethylene terephthalate is more preferably used because of its high strength and dimensional stability.
ポリアミド系繊維としては、ナイロン６、ナイロン６６、ナイロン６１０、ナイロン６１２などのナイロン系繊維が挙げられる。 Examples of the polyamide fiber include nylon fibers such as nylon 6, nylon 66, nylon 610, and nylon 612.
本発明の皮膚粘着テープ用織物において、合成長繊維とポリウレタン弾性繊維の複合糸を構成する合成長繊維は、モノフィラメント又はマルチフィラメントのいずれでもよいが、総繊度が２０ｄｔｅｘ〜６０ｄｔｅｘ（デシテックス）であることが好ましい。更に好ましくは３０ｄｔｅｘ〜５０ｄｔｅｘである。
２０ｄｔｅｘ未満であると引裂が低下し使用に耐えられない。また、６０ｄｔｅｘ以上であると厚く（重く）なる。
In the woven fabric for skin adhesive tape of the present invention, the synthetic long fibers constituting the composite yarn of the synthetic long fibers and the polyurethane elastic fibers may be either monofilaments or multifilaments, but the total fineness shall be 20 dtex to 60 dtex (decitex). Is preferable. More preferably, it is 30 dtex to 50 dtex.
If it is less than 20 dtex, tearing is reduced and it cannot be used. Further, when it is 60 dtex or more, it becomes thick (heavy).
合成長繊維とポリウレタン弾性繊維の複合糸を構成するポリウレタン弾性繊維は、ポリウレタンやポリウレタンウレアを主な構成単位とする重合体からなる伸縮性を持つ繊維である。 The polyurethane elastic fiber constituting the composite yarn of the combined growth fiber and the polyurethane elastic fiber is a fiber having elasticity composed of a polymer having polyurethane or polyurethane urea as a main constituent unit.
ポリウレタン弾性繊維は、ポリエーテルジオール及び有機ジイソシアネートから成るソフトセグメント部分と、有機ジイソシアネート及びジアミン又はジオールから成るハードセグメント部分とから構成される。 The polyurethane elastic fiber is composed of a soft segment portion composed of a polyether diol and an organic diisocyanate and a hard segment portion composed of an organic diisocyanate and a diamine or a diol.
ポリウレタン弾性繊維はモノフィラメント及びマルチフィラメントのいずれでもよいが、１５ｄｔｅｘ以上４４ｄｔｅｘ未満が好ましく、１７ｄｔｅｘ以上３０ｄｔｅｘ以下がより好ましい。１５ｄｔｅｘ未満であるとストレッチ性が不足する、糸の拘束力が弱くなるなどのおそれがある。また、４４ｄｔｅｘ以上であるとストレッチ性が高いものが得られるが、ゴム感が強く、風合いが硬い生地となってしまう。 The polyurethane elastic fiber may be either monofilament or multifilament, but is preferably 15 dtex or more and less than 44 dtex, and more preferably 17 dtex or more and 30 dtex or less. If it is less than 15 dtex, there is a risk that the stretchability will be insufficient and the binding force of the thread will be weakened. Further, when it is 44 dtex or more, a material having high stretchability can be obtained, but the fabric has a strong rubber feeling and a hard texture.
本実施形態の皮膚粘着テープ用織物は、合成長繊維とポリウレタン弾性繊維の複合糸を用いたものであれば、特に限定されるものではなく、合成長繊維を鞘糸とし、ポリウレタン弾性繊維を芯糸としてシングルカバーリングした複合糸条を、経糸及び／又は緯糸として用いて製織されたものであることができる。具体的には、例えば、ポリアミド繊維糸条を鞘糸とし、ポリウレタン弾性糸を芯糸とするシングルカバーリング繊維糸条が好ましく用いられる。 The woven fabric for skin adhesive tape of the present embodiment is not particularly limited as long as it uses a composite yarn of synthetic long fibers and polyurethane elastic fibers, and the synthetic long fibers are used as sheath yarns and polyurethane elastic fibers are used as the core. A composite yarn that is single-covered as a yarn can be woven by using it as a warp and / or a weft. Specifically, for example, a single covering fiber yarn having a polyamide fiber yarn as a sheath yarn and a polyurethane elastic yarn as a core yarn is preferably used.
本実施形態の皮膚粘着テープ用織物の組織としては、平織、ツイル織、サテン織、経二重織、緯二重織、ドビー織等の組織を使用できるが、これに限定されるものではないが、厚みを薄くするためには平織であることが好ましい。 As the structure of the woven fabric for skin adhesive tape of the present embodiment, a structure such as plain weave, twill weave, satin weave, warp double weave, weft double weave, and dobby weave can be used, but is not limited thereto. However, in order to reduce the thickness, a plain weave is preferable.
本実施形態の皮膚粘着テープ用織物の織密度としては、経方向で１００〜２５０本／２．５４ｃｍ、緯方向で１００〜２５０本／２．５４ｃｍが好ましい。 The weaving density of the woven fabric for skin adhesive tape of the present embodiment is preferably 100 to 250 pieces / 2.54 cm in the warp direction and 100 to 250 pieces / 2.54 cm in the weft direction.
織密度が前記下限値よりも小さいと、生地の十分な強度が得られない。一方、織密度が前記上限値よりも大きいと、通気性が十分に得られない。織密度を前記範囲とすることで、十分な強度と通気性とを得ることができる。 If the weaving density is smaller than the lower limit, sufficient strength of the fabric cannot be obtained. On the other hand, if the weaving density is larger than the upper limit value, sufficient air permeability cannot be obtained. By setting the weaving density within the above range, sufficient strength and breathability can be obtained.
本実施形態の皮膚粘着テープ用織物の伸長率は、経緯ともに２０〜５０％であり、伸長回復率が経緯ともに８０％以上である。 The elongation rate of the woven fabric for skin adhesive tape of the present embodiment is 20 to 50% in both the warp and weft, and the stretch recovery rate is 80% or more in both the warp and weft.
本明細書において、伸長率は、ＪＩＳ−Ｌ−１０９６「織物及び編物の生地試験方法」に規定の方法に従い、Ａ法にて繊維方向の織物の伸長率を測定した値である。具体的な測定条件については後述する。 In the present specification, the elongation rate is a value obtained by measuring the elongation rate of the woven fabric in the fiber direction by the method A according to the method specified in JIS-L-1096 "Fabric test method for woven fabrics and knitted fabrics". Specific measurement conditions will be described later.
伸長率が２０％未満では、ストレッチ性が不足する。また、伸長率が５０％を超えると伸長回復率が低く、反発性に劣る。伸長率が前記範囲であることにより、良好なストレッチ性と反発性を有するものとなる。 If the elongation rate is less than 20%, the stretchability is insufficient. Further, when the elongation rate exceeds 50%, the elongation recovery rate is low and the resilience is inferior. When the elongation rate is within the above range, it has good stretchability and resilience.
また、伸長回復率は、ＪＩＳ−Ｌ−１０９６「織物及び編物の生地試験方法」に規定の方法に従い、Ａ法にて伸長回復率を測定した値である。尚、伸長回復率は交織物の反発性の指標となる。具体的な測定条件については後述する。 The elongation recovery rate is a value obtained by measuring the elongation recovery rate by the method A according to the method specified in JIS-L-1096 "Fabric test method for woven fabrics and knitted fabrics". The elongation recovery rate is an index of the resilience of the mixed fabric. Specific measurement conditions will be described later.
伸長回復率が８０％未満であると、反発性に劣る。例えば、このような織物を基材として用いた絆創膏を指の関節部分に貼り、指を曲げ戻した際に、絆創膏と皮膚の間に隙間ができてしまう。伸長回復率が前記範囲であることにより、良好な反発性を有するものとなり、皮膚粘着テープを貼った指を曲げ伸ばししても隙間ができず、隙間からの水の浸入なども防止される。 If the elongation recovery rate is less than 80%, the resilience is inferior. For example, when an adhesive plaster using such a woven fabric as a base material is attached to a joint portion of a finger and the finger is bent back, a gap is formed between the adhesive plaster and the skin. When the stretch recovery rate is within the above range, it has good resilience, and even if the finger to which the skin adhesive tape is attached is bent and stretched, no gap is formed, and water intrusion from the gap is prevented.
本実施形態の皮膚粘着テープ用織物の引裂き強度は、経緯ともに１２Ｎ以上であることが好ましい、これにより十分な強度を有するものとなる。 The tear strength of the woven fabric for skin adhesive tape of the present embodiment is preferably 12 N or more in both the warp and weft, whereby the woven fabric for skin adhesive tape has sufficient strength.
本明細書において、引裂き強度は、ＪＩＳ−Ｌ−１０９６「織物及び編物の生地試験方法」に規定の方法に従い、Ｄ法（ペンジュラム法）により試験を行い評価したものである。具体的な測定条件については後述する。 In the present specification, the tear strength is evaluated by testing by the D method (pendulum method) according to the method specified in JIS-L-1096 "Fabric test method for woven fabrics and knitted fabrics". Specific measurement conditions will be described later.
皮膚粘着テープ用織物において、撥水度が初期４級以上であることが好ましい。これにより、皮膚粘着テープ用織物は、十分な撥水性を有するものとなる。 In the woven fabric for skin adhesive tape, the water repellency is preferably 4th grade or higher at the initial stage. As a result, the fabric for skin adhesive tape has sufficient water repellency.
本明細書において、撥水度は、ＪＩＳ−Ｌ−１０９２「繊維製品の防水性試験方法」 ７．２ はっ水度試験（スプレー試験）に規定の方法に従い、試験を行い評価したものである。具体的な測定条件については後述する。 In the present specification, the water repellency is evaluated by conducting a test according to the method specified in JIS-L-1092 "Waterproof test method for textile products" 7.2 Water repellency test (spray test). .. Specific measurement conditions will be described later.
本実施形態の皮膚粘着テープ用織物の目付は、５０〜１２０ｇ／ｍ２である。 The basis weight of the woven fabric for skin adhesive tape of this embodiment is 50 to 120 g / m 2 .
本明細書において、目付は、ＪＩＳ−Ｌ−１９０６「織物及び編物の生地試験方法」に規定の方法に従い、測定されたものであり、縦２０ｃｍ×横２５ｃｍの試験片を試料の幅１ｍあたり３箇所採取して質量を測定し、その平均値を単位面積あたりの質量に換算して求める。 In the present specification, the grain size is measured according to the method specified in JIS-L-1906 "Fabric test method for woven fabrics and knitted fabrics", and a test piece having a length of 20 cm and a width of 25 cm is 3 per 1 m of a sample width. The mass is measured by collecting the samples at each location, and the average value is converted into the mass per unit area.
目付けが５０ｇ／ｍ２未満では、繊維量が少なくなり、肌触り性などが低下する。一方、１２０ｇ／ｍ２を超えると、繊維量が多く剛性が高くなり、また生地も重いため皮膚に貼った際の快適性が低下する。さらに、後述するスナッグ性も低下する。 If the basis weight is less than 50 g / m 2 , the amount of fibers is reduced and the feel to the touch is lowered. On the other hand, if it exceeds 120 g / m 2 , the amount of fibers is large and the rigidity is high, and the fabric is heavy, so that the comfort when applied to the skin is lowered. Furthermore, the snag property described later is also reduced.
本実施形態の皮膚粘着テープ用織物において、スナッグが３級以上であることが好ましい。
スナッグとは、椅子の傷、金属のバリ、爪などが布帛表面に引っ掛かり、布帛を構成している糸の一部が布帛表面から引き出され、外観を損なう欠点をいう。
In the woven fabric for skin adhesive tape of the present embodiment, it is preferable that the snag is grade 3 or higher.
Snag refers to a defect that scratches on a chair, metal burrs, nails, etc. are caught on the surface of the fabric, and a part of the threads constituting the fabric is pulled out from the surface of the fabric, which impairs the appearance.
本明細書において、織物のスナッグ性は、ＪＩＳ−Ｌ１０５８「織物及び編物のスナッグ試験方法」に規定の方法に従い、Ｄ−１法（ダメージ棒を回転箱に取り付ける方法）による試験を行い、評価したものである。具体的な測定条件については後述する。 In the present specification, the snag property of a woven fabric is evaluated by conducting a test by the D-1 method (a method of attaching a damage rod to a rotating box) according to the method specified in JIS-L1058 "Snag test method of woven fabric and knitted fabric". It is a thing. Specific measurement conditions will be described later.
ＪＩＳ−Ｌ１０５８（Ｄ−１法）に準ずる試験で３級を下回ると、実着用時のスナッグによる外観悪化が顕著になることがある。 If the test is based on JIS-L1058 (D-1 method) and the level is lower than the third grade, the appearance may be significantly deteriorated due to the snag when actually worn.
このスナッグを抑制する方法として、一般的には織物の組織や密度を工夫する。具体的には、織物を、凹凸の少ない組織や高密度に仕上げることである。このように、凹凸のような引っ掛かる表面状態をなくすことで、スナッグは抑制される。 As a method of suppressing this snag, generally, the structure and density of the woven fabric are devised. Specifically, the woven fabric is finished with a structure having few irregularities and a high density. In this way, snags are suppressed by eliminating the catching surface condition such as unevenness.
本実施形態の皮膚粘着テープ用織物の厚みは、１５μｍ〜４０μｍ以下であることが好ましい。 The thickness of the woven fabric for skin adhesive tape of the present embodiment is preferably 15 μm to 40 μm or less.
本明細書において、織物の厚みは、ＪＩＳ−Ｌ−１９０６に規定の方法に従い測定した値であり、接圧荷重１００ｇ／ｃｍ２にて幅方向に１０箇所測定し、その平均値を厚みとする。 In the present specification, the thickness of the woven fabric is a value measured according to the method specified in JIS-L-1906, measured at 10 points in the width direction with a contact pressure load of 100 g / cm 2 , and the average value is taken as the thickness. ..
生地の厚みが前記下限値よりも薄いと、十分な強度を確保するのが困難である。また、厚みが前記上限値よりも厚いと、剛性が高くなり、ごわつき感が生じる。また、生地が重くなり皮膚に貼った際の快適性が低下する。織物生地の厚みを前記範囲とすることで、十分な強度を確保し肌触りがよいものとすることができる。 If the thickness of the dough is thinner than the lower limit, it is difficult to secure sufficient strength. Further, when the thickness is thicker than the upper limit value, the rigidity becomes high and a feeling of stiffness occurs. In addition, the fabric becomes heavy and the comfort when applied to the skin is reduced. By setting the thickness of the woven fabric within the above range, sufficient strength can be ensured and the fabric can be soft to the touch.
このような皮膚粘着テープ用織物を基材として用いた皮膚粘着テープは、薄く良好なストレッチ性を有し、皮膚に貼った際に快適に用いられる。小孔を設けなくても十分な通気性を有するため、蒸れたりかぶれたりすることが防止される。さらに、指の関節部分などに貼った場合に、指の曲げ伸ばし等をしてもテープと皮膚との間に隙間ができないため、隙間からテープと皮膚との間に水が入り込むようなこともなく、快適に使用することができる。 The skin adhesive tape using such a woven fabric for skin adhesive tape as a base material has thin and good stretchability, and is comfortably used when applied to the skin. Since it has sufficient air permeability without providing small holes, it prevents stuffiness and rashes. Furthermore, when it is attached to the joints of fingers, there is no gap between the tape and the skin even if the finger is bent and stretched, so water may enter between the tape and the skin through the gap. It can be used comfortably.
以下では、本発明の皮膚粘着テープ用織物を用いた医療用品として、絆創膏を例に挙げて説明する。
絆創膏は、支持体としての前記織物の片面にパッド材を含む接着剤層を有する。
Hereinafter, as a medical product using the woven fabric for skin adhesive tape of the present invention, an adhesive plaster will be described as an example.
The adhesive plaster has an adhesive layer containing a pad material on one side of the woven fabric as a support.
粘着剤層は、織物の片面に粘着剤が全面−様、又は不存部が点在する様、あるいは線状にうすく塗布された層である。粘着剤としては、例えば、ゴム系、アクリル系、ビニルエーテル系、ウレタン系やゴム系の接着剤、その他皮膚に刺激を与えないものであればよい。 The pressure-sensitive adhesive layer is a layer in which the pressure-sensitive adhesive is thinly applied to one side of the woven fabric so that the entire surface-like, absent parts are scattered, or linearly. The adhesive may be, for example, a rubber-based, acrylic-based, vinyl ether-based, urethane-based or rubber-based adhesive, or any other adhesive that does not irritate the skin.
パッド材は、傷口からの血液などの液体を吸収し、傷口を保護する役目を果たすものである。 The pad material absorbs a liquid such as blood from the wound and plays a role of protecting the wound.
パッド材としては、通常の絆創膏に使用されているものを用いることができ、例えば、ガーゼやネット、不織布、軟質発泡体等の多孔質体や多孔質体の外側をポリエステル等のフィラメントで形成したネットや粗目布等で被覆したもの等が挙げられる。その中でも、ガーゼ、脱脂綿などが、肌触りがよく好ましい。傷口への通気性をもたすため、特殊ネットを積層してもよい。必要に応じて、殺菌剤や止血剤、鎮痛剤、消毒剤、その他の薬剤を含ませることができる。
本発明の織物の一方の面にパッド材を積層一体化させる方法としては、不織布又はパッド材のどちらかにホットメルト樹脂を点在させ、加熱接着させる方法、不織布又はパッド材のどちらかに接着剤を、不在部を有して塗布し、加圧接着させる方法など通気性を損なわないようにすればいずれの方法でもよい。
As the pad material, those used for ordinary adhesive plasters can be used. For example, a porous body such as gauze, a net, a non-woven fabric, or a soft foam, or the outside of the porous body is formed of a filament such as polyester. Examples thereof include those covered with a net or a coarse cloth. Among them, gauze, cotton wool and the like are preferable because they are soft to the touch. A special net may be laminated to provide breathability to the wound. If desired, bactericides, hemostats, analgesics, disinfectants and other agents can be included.
As a method of laminating and integrating the pad material on one surface of the woven fabric of the present invention, hot melt resin is scattered on either the non-woven fabric or the pad material and heat-bonded, or adhered to either the non-woven fabric or the pad material. Any method may be used as long as the air permeability is not impaired, such as a method in which the agent is applied with an absent portion and pressure-bonded.
傷口パッドを含む接着剤層の表面は、非使用時には離型シート等のカバーフィルムで覆われているのが一般的であり、使用に際してはカバーフィルムを剥して利用される。 The surface of the adhesive layer including the wound pad is generally covered with a cover film such as a release sheet when not in use, and the cover film is peeled off before use.
このような絆創膏（医療用品）では、上述したような薄くても耐摩耗性に優れた織物を用いているので、通気性や透湿性を有し使用時の快適性に優れたものとなる。 Since such a plaster (medical product) uses a woven fabric that is thin but has excellent abrasion resistance as described above, it has breathability and moisture permeability and is excellent in comfort during use.
尚、本実施形態の皮膚粘着テープ用織物は、絆創膏以外にも、固定用テープ、テープ包帯、テーピング用テープ、磁石付きパッチ、湿布等、皮膚に粘着して用いられる医療用品の基材として、広く適用することができることは言うまでもない。 In addition to adhesive plasters, the woven skin adhesive tape of the present embodiment can be used as a base material for medical products such as fixing tapes, tape bandages, taping tapes, patches with magnets, and compresses, which are used by adhering to the skin. It goes without saying that it can be widely applied.
以下、実施例及び比較例を挙げて本実施の形態をより具体的に説明する。しかしながら、本実施の形態は、その要旨から逸脱しない限り、以下の実施例に限定されるものではない。実施例中の物性は以下の方法により測定した。 Hereinafter, the present embodiment will be described in more detail with reference to Examples and Comparative Examples. However, the present embodiment is not limited to the following examples as long as it does not deviate from the gist thereof. The physical properties in the examples were measured by the following methods.
（１）目付（ｇ／ｍ２）
ＪＩＳ−Ｌ−１９０６に規定の方法にしたがい、縦２０ｃｍ×横２５ｃｍの試験片を、試料の幅１ｍ当たり３箇採取して質量を測定し、その平均値を単位面積当たりの質量に換算して求めた。
(1) Metsuke (g / m 2 )
According to the method specified in JIS-L-1906, 3 test pieces of 20 cm in length × 25 cm in width were collected per 1 m of sample width, the mass was measured, and the average value was converted into the mass per unit area. I asked.
（２）厚み（μｍ）
ＪＩＳ−Ｌ−１９０６に規定の方法に従い、接圧荷重１００ｇ／ｃｍ２にて幅方向に１０箇所測定し、その平均値を厚みとした。厚み計は、ＰＥＡＣＯＣＫ社製ＮＯ．２０７を用いた。測定値はｍｍにて得られるが、小数点第３位まで読み取り平均した後、有効数字を２桁としてμｍに換算した。
(2) Thickness (μm)
According to the method specified in JIS-L-1906, measurements were taken at 10 points in the width direction with a contact pressure load of 100 g / cm 2 , and the average value was taken as the thickness. The thickness gauge is NO. 207 was used. The measured value was obtained in mm, but after reading and averaging to the third decimal place, it was converted to μm with two significant figures.
（３）伸長率（％）
ＪＩＳ−Ｌ−１０９６「織物及び編物の生地試験方法」に規定の方法に従い、Ａ法にて繊維方向の織物の伸長率を測定した。
伸長率ＬＡ（％）＝［（Ｌ１−Ｌ）／Ｌ］×１００
Ｌ１：１４．７Ｎの荷重を加え１分間保持後の印間の長さ（ｍｍ）
Ｌ：元の印間の長さ（２００ｍｍまたは５００ｍｍ）
(3) Elongation rate (%)
The elongation rate of the woven fabric in the fiber direction was measured by the method A according to the method specified in JIS-L-1096 "Fabric test method for woven fabrics and knitted fabrics".
Elongation rate LA (%) = [(L1-L) / L] × 100
Length between marks (mm) after applying a load of L1: 14.7N and holding for 1 minute
L: Length between original marks (200 mm or 500 mm)
（４）伸長回復率（％）
ＪＩＳ−Ｌ−１０９６「織物及び編物の生地試験方法」に規定の方法に従い、Ａ法にて伸長回復率を測定した。
伸長回復率ＬＢ（％）＝［（Ａ１−Ａ２）／（Ａ１−Ａ）］×１００
Ａ２：荷重を取り除いた後１時間後に初荷重を加えたときの印間の長さ（ｍｍ）
Ａ１：１４．７Ｎの荷重を１時間加えた後の印間の長さ（ｍｍ）
Ａ：初荷重を加えたときの印間の長さ（２００ｍｍまたは５００ｍｍ）
(4) Growth recovery rate (%)
The elongation recovery rate was measured by the A method according to the method specified in JIS-L-1096 "Fabric test method for woven fabrics and knitted fabrics".
Elongation recovery rate LB (%) = [(A1-A2) / (A1-A)] × 100
A2: Length between marks (mm) when the initial load is applied 1 hour after the load is removed.
A1: Length between marks (mm) after applying a load of 14.7N for 1 hour
A: Length between marks when initial load is applied (200 mm or 500 mm)
（５）引裂き強度（Ｎ）
ＪＩＳ−Ｌ−１０９６「織物及び編物の生地試験方法」に規定の方法に従い、Ｄ法（ペンジュラム法）にて試験を行い測定した。本明細書においては、経方向と緯方向の引裂き強度を３点以上測定し、平均値を計算した当該数値をパラメータとした。
(5) Tear strength (N)
The test was carried out by the D method (Pendulum method) according to the method specified in JIS-L-1096 "Fabric test method for woven fabrics and knitted fabrics" and measured. In the present specification, the tear strength in the warp direction and the weft direction is measured at three or more points, and the value obtained by calculating the average value is used as a parameter.
（６）撥水度
ＪＩＳ−Ｌ−１０９２「繊維製品の防水性試験方法」７．２はっ水度試験（スプレー試験）に規定の方法に従い試験を行い評価した。
試験片を保持具に取り付け、水２５０ｍｌを２５〜３０秒間散布する。保持具を外し試験片の表側を下向きにして固い物に軽く当てて水滴を落とした後、比較見本を基準にはっ水度を判定した。
比較見本を基準に１級〜５級の５段階ではっ水度を評価した。
１級：表面全体に湿潤を示すもの
２級：表面の半分に湿潤を示し、小さな個々の湿潤が布を浸透する状態を示
すもの
３級：表面に小さな個々の水滴状の湿潤を示すもの
４級：表面に湿潤しないが、小さな水滴の付着を示すもの
５級：表面に湿潤及び水滴の付着がないもの
(6) Water repellency JIS-L-1092 "Waterproof test method for textile products" 7.2 The water repellency test (spray test) was conducted and evaluated according to the specified method.
Attach the test piece to the holder and spray 250 ml of water for 25-30 seconds. After removing the holder and lightly applying the test piece to a hard object with the front side facing down to drop water droplets, the water repellency was determined based on a comparative sample.
The water repellency was evaluated on a scale of 1 to 5 based on a comparative sample.
Grade 1: Wetness on the entire surface Grade 2: Wetness on half of the surface, showing the state in which small individual wetts penetrate the cloth
Grade 3: Small individual water droplets on the surface Grade 4: Not wet on the surface but showing adhesion of small water droplets Grade 5: No wetness and water droplets on the surface
（７）スナッグ性
ＪＩＳ−Ｌ１０５８「織物及び編物のスナッグ試験方法」に規定の方法に従い、Ｄ−１法（ダメージ棒を回転箱に取り付ける方法）による試験を行い、評価した。
たて１２０ｍｍ×よこ１００ｍｍ、たて１００ｍｍ×よこ１２０ｍｍをそれぞれ２枚採取し、特殊ゴム管に巻き付け、特殊ゴム管に巻き付けられた試料を、ピリング試験箱に入れ、更にダメージ棒を箱の中にセットし、試験箱を回転させた。
ダメージ棒に研磨布を用いた場合は１時間試験箱を回転し試験後、スナッグ判定標準写真と比較し級数を付けた。
(7) Snag property According to the method specified in JIS-L1058 "Snag test method for woven fabrics and knitted fabrics", a test was conducted by the D-1 method (a method of attaching a damage rod to a rotating box) and evaluated.
Take two pieces each of 120 mm long x 100 mm wide and 100 mm wide x 120 mm wide, wrap them around a special rubber tube, put the sample wrapped around the special rubber tube in a pilling test box, and put the damage rod inside the box. It was set and the test box was rotated.
When a polishing cloth was used for the damage rod, the test box was rotated for 1 hour, and after the test, a series was given by comparing with the standard photograph for snag judgment.
［実施例１］
ポリアミド繊維（合成長繊維）とポリウレタン弾性繊維とを用いた織物を製織した。
経糸に、３３デシテックス／１０フィラメントのポリアミド繊維糸条を鞘糸とし、２２デシテックスのポリウレタン弾性糸を芯糸とするシングルカバーリング繊維糸条を用いた。
緯糸に、３３デシテックス／１０フィラメントのポリアミド繊維糸条を鞘糸とし、１７デシテックスのポリウレタン弾性糸を芯糸とするシングルカバーリング繊維糸条を用いた。
織物の経密度は１４５本／２．５４ｃｍであり、緯密度は１１０本／２．５４ｃｍであった。
[Example 1]
A woven fabric using polyamide fibers (synthetic long fibers) and polyurethane elastic fibers was woven.
As the warp, a single covering fiber yarn having 33 decitex / 10 filament polyamide fiber yarn as a sheath yarn and 22 decitex polyurethane elastic yarn as a core yarn was used.
As the weft, a single covering fiber yarn having 33 decitex / 10 filament polyamide fiber yarn as a sheath yarn and 17 decitex polyurethane elastic yarn as a core yarn was used.
The warp density of the woven fabric was 145 pieces / 2.54 cm, and the weft density was 110 pieces / 2.54 cm.
次に、常法に従い精練、乾燥、及び中間セットした後、常法に従い染色、乾燥、撥水、及び仕上げセットを行い、加工布としての織物を得た。 Next, after refining, drying, and intermediate setting according to a conventional method, dyeing, drying, water repellency, and finishing set were performed according to a conventional method to obtain a woven fabric as a processed cloth.
このようにして得られた織物は、経密度が１８９本／２．５４ｃｍであり、緯密度が１５６本／２．５４ｃｍであり、目付が８４．８ｇ／ｍ２であり、引裂強度が経１３．８Ｎ、緯１２．７Ｎであり、伸長率が経４３％、緯３５％であり、伸長回復率が経９２％、緯９０％であり、撥水度が初期５級であり、そしてスナッグが３級であった。 The woven fabric thus obtained has a warp density of 189 / 2.54 cm, a weft density of 156 / 2.54 cm, a basis weight of 84.8 g / m 2 , and a tear strength of 13 warp. It is .8N, weft 12.7N, elongation 43%, weft 35%, elongation recovery rate 92%, weft 90%, water repellency is early 5th grade, and snag It was the third grade.
［比較例１］
ポリウレタン弾性糸を用いなかった以外は、実施例１と同様にして織物（加工布）を得た。
このようにして得られた織物は、経密度が２００本／２．５４ｃｍであり、緯密度が１５５本／２．５４ｃｍであり、目付が８０ｇ／ｍ２であり、引裂強度が経１３．８Ｎ、緯１２．７Ｎであり、伸長率が経５．２％、緯７．０％であり、伸長回復率が経５５．５％、緯５３．５％であり、撥水度が初期４級であり、そしてスナッグが３級であった。
[Comparative Example 1]
A woven fabric (processed cloth) was obtained in the same manner as in Example 1 except that the polyurethane elastic yarn was not used.
The woven fabric thus obtained has a warp density of 200 pieces / 2.54 cm, a weft density of 155 pieces / 2.54 cm, a basis weight of 80 g / m 2 , and a tear strength of 13.8 N pieces. , Weft 12.7N, elongation rate is 5.2%, weft 7.0%, elongation recovery rate is 55.5%, weft 53.5%, and water repellency is initial 4th grade. And the snag was grade 3.
［比較例２］
目付が１２０ｇ／ｍ２より大きくなるようにした以外は、実施例１と同様にして織物（加工布）を得た。
このようにして得られた織物は、経密度が２７０本／２．５４ｃｍであり、緯密度が２３０本／２．５４ｃｍであり、目付が１２８ｇ／ｍ２であり、引裂強度が経１１．５Ｎ、緯１０．８Ｎであり、伸長率が経３０％、緯２７％であり、伸長回復率が経９０％、緯８７％であり、撥水度が初期４級であり、そしてスナッグが３級であった。
[Comparative Example 2]
A woven fabric (processed cloth) was obtained in the same manner as in Example 1 except that the basis weight was made larger than 120 g / m 2.
The woven fabric thus obtained has a warp density of 270 lines / 2.54 cm, a weft density of 230 lines / 2.54 cm, a basis weight of 128 g / m 2 , and a tear strength of 11.5 N. , Weft 10.8N, Elongation rate 30%, Weft 27%, Elongation recovery rate 90%, Weft 87%, Water repellency is initial 4th grade, and Snag is 3rd grade. Met.
［比較例３］
合成長繊維としてのポリアミド繊維の代わりに、吸湿性繊維（綿、Ｔ／Ｃ等）を用いたこと以外は、実施例１と同様にして織物（加工布）を得た。
このようにして得られた織物は、経密度が１１０本／２．５４ｃｍであり、緯密度が９１本／２．５４ｃｍであり、目付が１１２ｇ／ｍ２であり、引裂強度が経１８．８Ｎ、緯１６．０Ｎであり、伸長率が経４０％、緯３８％であり、伸長回復率が経８５％、緯８３％であり、撥水度が初期３級であり、そしてスナッグが２級であった。
[Comparative Example 3]
A woven fabric (processed cloth) was obtained in the same manner as in Example 1 except that hygroscopic fibers (cotton, T / C, etc.) were used instead of the polyamide fibers as the combined growth fibers.
The woven fabric thus obtained has a warp density of 110 pieces / 2.54 cm, a weft density of 91 pieces / 2.54 cm, a basis weight of 112 g / m 2 , and a tear strength of 18.8 N pieces. , Weft 16.0N, elongation 40%, weft 38%, elongation recovery rate 85%, weft 83%, water repellency is early 3rd grade, and snag is 2nd grade Met.
以上のようにして製織された実施例、及び比較例の織物を支持体（基材）として絆創膏を作製した。その絆創膏を皮膚に貼り、そのときの快適性について評価した。 Adhesive plasters were prepared using the woven fabrics of Examples and Comparative Examples woven as described above as a support (base material). The bandage was applied to the skin and the comfort at that time was evaluated.
実施例１では、薄くて軽い絆創膏とすることができた。また、小孔を設けなくても通気性や透湿性を有するため、皮膚に貼った際にも蒸れたりすることなく快適であった。また、伸長回復率も十分に高いため、絆創膏を指の関節部分に貼り、指を曲げ戻した際にも、皮膚と絆創膏との間に隙間ができることはなかった。 In Example 1, a thin and light bandage could be obtained. In addition, since it has breathability and moisture permeability without providing small holes, it was comfortable even when it was applied to the skin without getting stuffy. In addition, since the elongation recovery rate was sufficiently high, no gap was formed between the skin and the adhesive plaster even when the adhesive plaster was applied to the joint portion of the finger and the finger was bent back.
ポリウレタンを使用しなかった比較例１では、生地の伸長率が１０％以下であり、伸長回復率は８０％未満であった。このように伸長回復率が悪いため、絆創膏を指の関節部分に貼り、指を曲げ戻した際に、皮膚と絆創膏との間に隙間ができてしまった。 In Comparative Example 1 in which polyurethane was not used, the elongation rate of the dough was 10% or less, and the elongation recovery rate was less than 80%. Due to the poor elongation recovery rate, when the adhesive plaster was applied to the joints of the fingers and the fingers were bent back, a gap was created between the skin and the adhesive plaster.
目付が１２０ｇ／ｍ２より大きい比較例２では、生地が重くなり、皮膚に貼った際に快適ではなかった。 In Comparative Example 2 in which the basis weight was larger than 120 g / m 2 , the dough became heavy and was not comfortable when applied to the skin.
合成長繊維に代えて吸湿性繊維を用いた比較例では、生地が吸湿するため、皮膚に貼った際にふやけ易くなり快適ではなかった。 In the comparative example in which hygroscopic fibers were used instead of the combined growth fibers, the fabric absorbs moisture, so that it is easy to swell when applied to the skin, which is not comfortable.
以上、本発明の実施の形態について説明してきたが、本発明はこれに限定されるものではなく、発明の趣旨を逸脱しない範囲で適宜変更可能である。 Although the embodiments of the present invention have been described above, the present invention is not limited to this, and can be appropriately changed without departing from the spirit of the invention.
本発明による膚粘着テープ用織物を用いることで、小孔を設けなくても通気性や透湿性を有し、薄くても耐摩耗性に優れたものとなり、絆創膏等の医療用品として広く利用することができる。 By using the woven fabric for skin adhesive tape according to the present invention, it has breathability and moisture permeability without providing small holes, and even if it is thin, it has excellent abrasion resistance, and is widely used as a medical product such as an adhesive plaster. be able to.
Claims (8)