JP2021031744A - Smelting process of high nitrogen stainless steel - Google Patents
Smelting process of high nitrogen stainless steel Download PDFInfo
- Publication number
- JP2021031744A JP2021031744A JP2019154661A JP2019154661A JP2021031744A JP 2021031744 A JP2021031744 A JP 2021031744A JP 2019154661 A JP2019154661 A JP 2019154661A JP 2019154661 A JP2019154661 A JP 2019154661A JP 2021031744 A JP2021031744 A JP 2021031744A
- Authority
- JP
- Japan
- Prior art keywords
- molten steel
- nitrogen
- amount
- nitrogen gas
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、高窒素ステンレス溶鋼の溶製方法に関する。 The present invention relates to a method for melting high nitrogen stainless molten steel.
耐摩耗性や耐食性の向上を目的として窒素濃度の高いステンレス溶鋼を溶製する際、溶鋼に窒素を添加する手段として、窒素ガスを溶鋼に吹き込むことが多く行われている。しかし、溶鋼に含有される窒素成分がばらつく傾向にあり、窒素成分の安定化に課題がある。窒素添加時に吹込み窒素ガス総流量を制御するが、溶鋼中に溶解するのはその一部である。そのため、窒素溶解度が低く、加えて処理単位ごとに窒素溶解度がばらつくという課題がある。
また、溶鋼中の炭素濃度及び酸素濃度を低減しなければならない場合、真空脱ガス処理を行う必要があるが、溶鋼中の窒素が真空雰囲気下で脱離することにより窒素濃度が低下し、窒素低下量を安定化できない(窒素低下量がばらつく)ことも窒素成分ばらつきの要因となっている。
When melting stainless molten steel having a high nitrogen concentration for the purpose of improving wear resistance and corrosion resistance, nitrogen gas is often blown into the molten steel as a means for adding nitrogen to the molten steel. However, the nitrogen component contained in the molten steel tends to vary, and there is a problem in stabilizing the nitrogen component. The total flow rate of blown nitrogen gas is controlled when nitrogen is added, but only a part of it dissolves in molten steel. Therefore, there is a problem that the nitrogen solubility is low and the nitrogen solubility varies depending on the treatment unit.
In addition, when it is necessary to reduce the carbon concentration and oxygen concentration in the molten steel, it is necessary to perform vacuum degassing treatment, but the nitrogen concentration in the molten steel decreases due to desorption in a vacuum atmosphere, and nitrogen The inability to stabilize the amount of decrease (the amount of decrease in nitrogen varies) is also a factor in the variation in nitrogen components.
真空脱ガス処理中に窒素が脱離する課題に対して、特許文献1には、脱ガス時の真空度及び真空処理時間を制御することで必要な脱酸量を確保しながら、窒素の脱離量を低減する方法が記載されている。
また、特許文献2には、従来の窒素含有合金の添加では真空脱ガス処理後でしか窒素が添加できず処理時間が増大するため、真空脱ガス処理と窒素ガス吹込みを同時に行う方法が記載されている。この方法では、還元剤の投入による脱酸と窒素添加を同時に行うことで窒素溶解量を高めている(特許文献2の段落[0011])。
In response to the problem of degassing nitrogen during vacuum degassing,
Further,
特許文献1には、窒素ガス吹込みによる窒素添加後の溶鋼窒素濃度のばらつき解消について記載されていない。特許文献1記載の方法の場合、真空脱ガス処理時に溶鋼窒素濃度のばらつきが増大することがある。特に、真空脱ガス処理前の溶鋼窒素濃度にばらつきがある場合、真空脱ガス処理によって溶鋼窒素濃度のばらつきがさらに増大することがある。
特許文献2記載の方法は、溶鋼窒素濃度の増大に成功しているが、依然として溶鋼窒素濃度のばらつきが存在し、窒素成分の安定化は実現されていない。
このように従来の技術は、溶鋼に含有される窒素成分のばらつきを課題としていない。
Although the method described in
As described above, the conventional technique does not have a problem of variation in the nitrogen component contained in the molten steel.
本発明はかかる事情に鑑みてなされたもので、ステンレス溶鋼への窒素添加において、窒素ガス供給量に対して溶鋼に含有される窒素濃度が安定しない課題、即ち、溶鋼窒素濃度がばらつく課題を解決することを目的とする。 The present invention has been made in view of such circumstances, and solves a problem that the nitrogen concentration contained in the molten steel is not stable with respect to the amount of nitrogen gas supplied, that is, a problem that the nitrogen concentration of the molten steel varies when nitrogen is added to the molten stainless steel. The purpose is to do.
上記目的を達成するため、本発明に係る高窒素ステンレス溶鋼の溶製方法は、
一次精錬工程において、吹酸脱炭処理を行ったステンレス溶鋼に還元剤を投入した後に、該溶鋼中の溶存酸素濃度が100ppm以下となるまで脱酸処理し、その後、該溶鋼に窒素ガスを吹き込む処理を実施して出鋼し、
前記一次精錬工程後の真空脱ガス工程において、圧力が0.03MPa以下である真空雰囲気に前記溶鋼を暴露する時間を40分以下とし、
前記真空脱ガス工程後の取鍋精錬工程において、前記溶鋼中の溶存窒素量を基に該溶鋼に供給する窒素ガス量を決定し、該溶鋼に窒素ガスを供給することを特徴としている。
In order to achieve the above object, the method for melting high nitrogen stainless molten steel according to the present invention is:
In the primary refining step, after adding a reducing agent to the stainless molten steel that has been decarburized by blowing acid, the molten steel is deoxidized until the dissolved oxygen concentration in the molten steel becomes 100 ppm or less, and then nitrogen gas is blown into the molten steel. Processed and steeled,
In the vacuum degassing step after the primary refining step, the time for exposing the molten steel to a vacuum atmosphere having a pressure of 0.03 MPa or less is set to 40 minutes or less.
In the ladle refining step after the vacuum degassing step, the amount of nitrogen gas to be supplied to the molten steel is determined based on the amount of dissolved nitrogen in the molten steel, and the nitrogen gas is supplied to the molten steel.
本発明が対象とする「高窒素ステンレス溶鋼」は、窒素濃度が250ppm以上のステンレス溶鋼を想定しており、特に窒素濃度が500ppm以上のステンレス溶鋼に対して有効な溶製方法である。
また、「還元剤」は、ステンレス溶鋼中の酸素と反応して酸化物を形成することによって溶鋼を還元する役割を果たす副原料である。
The "high nitrogen stainless molten steel" targeted by the present invention is assumed to be a stainless molten steel having a nitrogen concentration of 250 ppm or more, and is a particularly effective melting method for a stainless molten steel having a nitrogen concentration of 500 ppm or more.
Further, the "reducing agent" is an auxiliary raw material that plays a role of reducing the molten steel by reacting with oxygen in the molten stainless steel to form an oxide.
還元反応によって溶鋼の溶存酸素濃度を下げることにより、窒素が溶鋼に溶けやすくなる。しかし、還元反応過渡期は脱炭炉内の溶鋼に酸素濃度のばらつきがあるため、窒素ガスを溶鋼に吹き込むと、窒素溶解量にばらつきが生じる。また、低圧下では溶鋼から窒素が脱離するが、脱離速度の制御は難しい。 By lowering the dissolved oxygen concentration of the molten steel by the reduction reaction, nitrogen becomes more easily dissolved in the molten steel. However, since the molten steel in the decarburization furnace has variations in oxygen concentration during the transitional period of the reduction reaction, when nitrogen gas is blown into the molten steel, the amount of nitrogen dissolved varies. In addition, nitrogen is desorbed from the molten steel under low pressure, but it is difficult to control the desorption rate.
そこで、本発明では、一次精錬工程において、吹酸脱炭処理を行った溶鋼の溶存酸素濃度が100ppm以下となるまで脱酸処理した後、該溶鋼に窒素ガスを吹込み、真空脱ガス工程において、真空雰囲気に溶鋼を暴露する時間を40分以下とする。さらに、取鍋精錬工程までに生じた溶鋼窒素濃度のばらつきを低減するため、取鍋精錬工程において、溶鋼中の溶存窒素量を基に該溶鋼に供給する窒素ガス量を決定して該溶鋼に窒素ガスを供給する。 Therefore, in the present invention, in the primary refining step, after deoxidizing the molten steel subjected to the blow acid decarburization treatment until the dissolved oxygen concentration becomes 100 ppm or less, nitrogen gas is blown into the molten steel and the vacuum degassing step is performed. The time for exposing the molten steel to the vacuum atmosphere is 40 minutes or less. Further, in order to reduce the variation in the nitrogen concentration of molten steel generated up to the ladle refining step, in the ladle refining step, the amount of nitrogen gas supplied to the molten steel is determined based on the amount of dissolved nitrogen in the molten steel, and the molten steel is used. Supply nitrogen gas.
また、本発明に係る高窒素ステンレス溶鋼の溶製方法において、前記取鍋精錬工程では、前記溶鋼の溶存酸素濃度が50ppm以下となるまで脱酸処理した後、前記溶鋼に窒素ガスを供給するようにしてもよい。 Further, in the method for melting high nitrogen stainless steel molten steel according to the present invention, in the ladle refining step, nitrogen gas is supplied to the molten steel after deoxidizing treatment until the dissolved oxygen concentration of the molten steel becomes 50 ppm or less. It may be.
当該構成では、取鍋精錬工程において、溶鋼の溶存酸素濃度が50ppm以下となるまでさらに脱酸処理を行うことにより、最終的な窒素成分値のばらつきを抑制する。 In this configuration, in the ladle refining step, further deoxidation treatment is performed until the dissolved oxygen concentration of the molten steel becomes 50 ppm or less, thereby suppressing the variation in the final nitrogen component value.
本発明に係る高窒素ステンレス溶鋼の溶製方法では、一次精錬工程、真空脱ガス工程、及び取鍋精錬工程の各工程において溶鋼窒素濃度のばらつきを抑制するので、目標とする窒素成分値を有するステンレス溶鋼を効率的に溶製することができる。
また、上記波及効果として、精錬処理時間のばらつきが抑制可能となるので、精錬処理時間が長くなることを見込んで用いていた昇熱材の使用量を削減することができる。
The method for melting high nitrogen stainless steel molten steel according to the present invention has a target nitrogen component value because it suppresses variation in molten steel nitrogen concentration in each step of the primary refining step, the vacuum degassing step, and the ladle refining step. It is possible to efficiently melt stainless molten steel.
Further, as the above-mentioned spillover effect, the variation in the refining treatment time can be suppressed, so that the amount of the heating material used in anticipation of a long refining treatment time can be reduced.
続いて、添付した図面を参照しつつ、本発明を具体化した実施の形態について説明し、本発明の理解に供する。 Subsequently, an embodiment embodying the present invention will be described with reference to the attached drawings, and the present invention will be understood.
[溶鋼窒素濃度がばらつく要因]
鋼片中の窒素濃度により硬度等の特性が変化する。そのため、製品の品質向上のためには鋳造時の溶鋼窒素濃度をばらつきなく制御することが必要となる。
溶鋼中に窒素を溶解させる方法には、窒素ガスの吹込みと窒素合金の投入がある。しかし、いずれの方法も溶鋼温度の低下を招くため、昇温機構を備えていない設備では、窒素添加可能量に上限が存在する。従って、鋳造前の最終工程である取鍋精錬工程において溶鋼窒素濃度の調整を行うとしても限界があり、鋳片中の窒素濃度を精度よく制御するためには、取鍋精錬を行う前に窒素濃度のばらつきをできるだけ抑制しておくことが重要となる。
[Factors of fluctuation in molten steel nitrogen concentration]
Properties such as hardness change depending on the nitrogen concentration in the steel piece. Therefore, in order to improve the quality of the product, it is necessary to control the molten steel nitrogen concentration at the time of casting without variation.
Methods for dissolving nitrogen in molten steel include blowing nitrogen gas and inputting a nitrogen alloy. However, since both methods cause a decrease in the molten steel temperature, there is an upper limit to the amount of nitrogen that can be added in equipment that does not have a temperature raising mechanism. Therefore, even if the molten steel nitrogen concentration is adjusted in the ladle refining process, which is the final step before casting, there is a limit. In order to accurately control the nitrogen concentration in the slab, nitrogen is used before the ladle refining. It is important to suppress the variation in concentration as much as possible.
ステンレス溶鋼(以下では、単に「溶鋼」と呼ぶことがある。)の精錬工程は、一次精錬工程と真空脱ガス工程を経由する必要がある。窒素添加ステンレス鋼を製造する場合、一次精錬工程の処理中あるいは処理後に窒素添加を行い、その後、真空脱ガス工程において真空処理を行う。その後、必要であれば取鍋精錬を行うことが一般的である。 The refining process of stainless molten steel (hereinafter, may be simply referred to as "molten steel") needs to go through a primary refining process and a vacuum degassing process. When producing nitrogen-added stainless steel, nitrogen is added during or after the treatment in the primary refining step, and then vacuum treatment is performed in the vacuum degassing step. After that, it is common to perform ladle refining if necessary.
本発明者らは、取鍋精錬前の溶鋼窒素濃度のばらつきが生じる主要因は、後述するように、一次精錬工程における窒素溶解量のばらつきと、真空脱ガス工程における窒素脱離量のばらつきであることを見出した。 As will be described later, the main factors that cause the variation in the nitrogen concentration of molten steel before the pot refining are the variation in the amount of nitrogen dissolved in the primary refining step and the variation in the amount of nitrogen desorbed in the vacuum degassing step. I found that there is.
a)一次精錬工程における窒素溶解量のばらつき
上述したように、溶鋼中に窒素を溶解させる方法には、窒素ガスの吹込みと窒素合金の投入があるが、窒素添加量に対する窒素溶解量の比率が、窒素ガス吹込みのほうが窒素合金の投入に比べて高いことから、一次精錬工程における窒素添加は、窒素ガスの吹込みによって行われてきた。しかし、窒素ガスの吹込み量に対して窒素の溶解量は一定ではなく、添加後の溶鋼中窒素濃度にばらつきが存在していた。
a) Variation in the amount of nitrogen dissolved in the primary refining process As described above, the methods for dissolving nitrogen in molten steel include blowing nitrogen gas and inputting a nitrogen alloy. The ratio of the amount of dissolved nitrogen to the amount of nitrogen added However, since the injection of nitrogen gas is higher than the injection of nitrogen alloy, the addition of nitrogen in the primary refining step has been performed by blowing nitrogen gas. However, the amount of nitrogen dissolved was not constant with respect to the amount of nitrogen gas blown in, and the nitrogen concentration in the molten steel after the addition varied.
窒素ガスの溶解は、微視的にはガスの気相と溶鋼の液相の界面で進行するが、界面において溶解反応を阻害する元素(酸素、硫黄等)が存在すると、溶解反応の進行速度が低下すると考えられる。そこで、本発明者らは、溶鋼中の溶存酸素濃度を一定に制御した状態で窒素添加を行ったが、窒素溶解量のばらつきは解消されなかった。 The dissolution of nitrogen gas progresses microscopically at the interface between the gas phase of the gas and the liquid phase of the molten steel, but if there are elements (oxygen, sulfur, etc.) that inhibit the dissolution reaction at the interface, the progress rate of the dissolution reaction Is thought to decrease. Therefore, the present inventors added nitrogen in a state where the dissolved oxygen concentration in the molten steel was controlled to be constant, but the variation in the amount of dissolved nitrogen was not eliminated.
脱炭炉内の溶鋼に窒素ガスを吹込むと、炉内の各所で窒素の溶解反応が同時並行的に進行する。ここで、当該反応進行中における各所の溶存酸素量を検討すると、溶鋼中に溶存酸素量が高い領域と低い領域が併存することが判明した。溶鋼中の溶存酸素量にばらつきがある状態で窒素ガスの吹込みを行うと、窒素の溶解速度にばらつきが生じ、溶解する窒素の総量がばらつくことを本発明者らは発見した。因って、炉内で溶鋼中の溶存酸素濃度にばらつきがないように制御できれば窒素の溶解量のばらつきを抑制できることに本発明者らは想到した。 When nitrogen gas is blown into the molten steel in the decarburization furnace, the nitrogen dissolution reaction proceeds in parallel at various points in the furnace. Here, when the amount of dissolved oxygen in each part during the reaction was examined, it was found that a region having a high dissolved oxygen amount and a region having a low dissolved oxygen amount coexisted in the molten steel. The present inventors have found that when nitrogen gas is blown in a state where the amount of dissolved oxygen in the molten steel varies, the dissolution rate of nitrogen varies, and the total amount of dissolved nitrogen varies. Therefore, the present inventors have conceived that if the dissolved oxygen concentration in the molten steel can be controlled so as not to vary in the furnace, the variation in the dissolved amount of nitrogen can be suppressed.
b)真空脱ガス工程における窒素脱離量のばらつき
溶鋼の極低炭素化及び高純化のためには、真空脱ガス工程は必須である。しかし、高窒素ステンレス溶鋼の処理を行う場合、真空雰囲気下では溶鋼表面において窒素の脱離反応が進行する。
窒素の脱離反応の速度は、真空排気槽中の窒素分圧に依存する。しかし、窒素分圧は真空度のみならずCOガスやCO2ガスの濃度によっても変化する。このため、脱離反応速度の制御は困難であるため、真空脱ガス処理において窒素脱離量のばらつきは不可避的に生じ、真空処理時間が長いほど窒素脱離量のばらつきは大きくなる。
b) Variation in the amount of nitrogen degassed in the vacuum degassing step The vacuum degassing step is indispensable for ultra-low carbonization and high purification of molten steel. However, when the high nitrogen stainless molten steel is treated, the nitrogen desorption reaction proceeds on the surface of the molten steel in a vacuum atmosphere.
The rate of nitrogen desorption reaction depends on the partial pressure of nitrogen in the vacuum exhaust tank. However, the partial pressure of nitrogen changes not only with the degree of vacuum but also with the concentration of CO gas and CO 2 gas. Therefore, since it is difficult to control the desorption reaction rate, the amount of nitrogen desorption inevitably varies in the vacuum degassing treatment, and the longer the vacuum treatment time, the larger the variation in the amount of nitrogen desorption.
[本発明の一実施の形態に係る高窒素ステンレス溶鋼の溶製方法]
本発明の一実施の形態に係る高窒素ステンレス溶鋼の溶製方法では、一次精錬工程において窒素ガス吹込みにおける窒素溶解量のばらつきを低減し、さらに真空脱ガス工程において窒素脱離量のばらつきを低減する。そして、取鍋精錬工程の前までに生じた溶鋼窒素濃度のばらつきを取鍋精錬工程において低減する。
[Method for melting high nitrogen stainless molten steel according to an embodiment of the present invention]
In the method for melting high nitrogen stainless steel molten steel according to the embodiment of the present invention, the variation in the amount of nitrogen dissolved in the nitrogen gas blowing in the primary refining step is reduced, and the variation in the amount of nitrogen desorption in the vacuum degassing step is reduced. Reduce. Then, the variation in the nitrogen concentration of molten steel that has occurred before the ladle refining step is reduced in the ladle refining step.
(STEP−1:一次精錬工程)
転炉10(脱炭炉の一例)内に挿入したランス13及び転炉10底部に設けられた羽口12から転炉10内のステンレス溶鋼20に酸素22を吹込み、吹酸脱炭処理を行う(図1(A)参照)。
なお、1チャージ当たりの溶鋼量は、50ton〜350ton程度である。
(STEP-1: Primary refining process)
The amount of molten steel per charge is about 50 ton to 350 ton.
(STEP−2:一次精錬工程)
副原料投入口15から転炉10内の溶鋼20に還元剤21を投入した後、溶存酸素濃度が100ppm以下となるまで溶鋼20を撹拌し脱酸処理を行う(図1(A)参照)。これにより、転炉10内で溶存酸素濃度が均等になる。
上記脱酸処理では、溶鋼20単位量当たりの撹拌動力密度を10(kW/ton)以上とし、5分以上撹拌すれば、溶存酸素濃度を100ppm以下とすることが可能となる。撹拌には、例えばArガスの吹込みやArガスの吹付け等の公知の方法が利用できる。
(STEP-2: Primary refining process)
After the reducing
In the above deoxidizing treatment, the stirring power density per 20 units of molten steel is set to 10 (kW / ton) or more, and if stirring is performed for 5 minutes or more, the dissolved oxygen concentration can be set to 100 ppm or less. For stirring, a known method such as blowing Ar gas or blowing Ar gas can be used.
還元剤21には、反応性及び運搬性の高さの観点から、フェロシリコン合金、その他のSi−Mn合金のようなシリコン合金、金属アルミニウム、及び炭素のいずれか一つ又はその組み合わせが主として使用されるが、鉄及びクロムよりも酸素との反応性が高い金属を主成分とするものであれば上記合金に限らない。
The reducing
撹拌動力密度の上限は特に定めず、使用する設備で可能な範囲とすればよい。例えば、1000(kW/ton)の設備が知られているが、100(kW/ton)以下が可能となる設備が一般的である。 The upper limit of the stirring power density is not particularly set, and may be within the range possible by the equipment to be used. For example, equipment of 1000 (kW / ton) is known, but equipment capable of 100 (kW / ton) or less is common.
(STEP−3:一次精錬工程)
転炉10底部の羽口12から転炉10内の溶鋼20に窒素ガス23を吹き込む処理を実施して出鋼する(図1(B)参照)。
(STEP-3: Primary refining process)
(STEP−4:真空脱ガス工程)
転炉10から排出された溶鋼20を取鍋11内に装入した後、取鍋11上に真空排気槽16をセットし(図1(C)参照)、真空排気槽16内の真空雰囲気圧力を0.03MPa以下とする。そして、取鍋11底部に設けられた羽口(図示省略)から取鍋11内の溶鋼20にArガス24を吹込むと共に、真空排気槽16内に挿入したランス14から取鍋11内の溶鋼20に酸素22を吹込み、真空脱ガス処理を行う。真空雰囲気に溶鋼20を暴露する時間は40分以下とする。
(STEP-4: Vacuum degassing process)
After charging the
真空雰囲気に溶鋼20を暴露する時間は短ければ短いほど、溶鋼窒素濃度のばらつき増大を抑制することができる。しかし、本発明が対象とする高窒素ステンレス溶鋼の場合、一次精錬のみで含有炭素量を目標値まで低減することができない。そのため、10分以上(0.03MPa以下の暴露時間)の真空脱ガス処理を必要とする場合が多い。
真空雰囲気圧力は、真空脱ガス装置の排気能力に依存し、例えば、0.0013MPa(10Torr)程度まで圧力を低減することができる装置が実用化されている。本発明者らの知見によれば、0.03MPa以下の暴露時間が40分以下であれば、溶鋼窒素濃度に関して顕著なばらつき増大は認められないことを確認している。
The shorter the exposure time of the
The vacuum atmospheric pressure depends on the exhaust capacity of the vacuum degassing device, and for example, a device capable of reducing the pressure to about 0.0013 MPa (10 Torr) has been put into practical use. According to the findings of the present inventors, it has been confirmed that when the exposure time of 0.03 MPa or less is 40 minutes or less, no significant increase in variation in the molten steel nitrogen concentration is observed.
(STEP−5:取鍋精錬工程)
溶鋼20中の溶存窒素量を基に溶鋼20に供給する窒素ガス量を決定し、取鍋11底部の羽口から取鍋11内の溶鋼20に窒素ガス23を吹込む(図1(D)参照)。
本発明における一次精錬要件及び真空脱ガス要件が満足されると、取鍋精錬工程前における溶鋼20の溶存窒素量は安定する。従って、溶鋼20中の溶存窒素量には、溶鋼サンプルを採取した実測値、過去の実績データに基づいた推定値や計算値、吸窒脱窒のモデル式に基づく計算値等、いずれも使用することができる。
(STEP-5: Ladle refining process)
The amount of nitrogen gas supplied to the
When the primary refining requirement and the vacuum degassing requirement in the present invention are satisfied, the amount of dissolved nitrogen in the
本工程では、溶鋼20の溶存酸素濃度が50ppm以下となるまで脱酸処理した後、溶鋼20に窒素ガス23を供給するようにしてもよい。溶鋼20中の溶存酸素濃度が高いと、取鍋11内で酸素濃度分布にばらつきが生じ、窒素ガス23吹込みによる窒素溶解量ばらつきの要因となりうる。そこで、溶存酸素濃度が50ppm以下になるまでさらに脱酸処理を行うことにより、最終成分値における溶鋼窒素濃度のばらつきを抑制することができる。
In this step,
上記脱酸処理において、溶鋼単位量当たりの撹拌動力密度を1(kW/ton)以上とし、5分以上撹拌すれば、溶存酸素濃度が50ppm以下の到達が可能となる。撹拌には、例えばArガスの吹込みやArガスの吹付け等の公知の方法が利用できる。
予め、溶鋼20に還元剤21を投入してもよい。
In the above deoxidizing treatment, if the stirring power density per unit amount of molten steel is set to 1 (kW / ton) or more and stirring is performed for 5 minutes or more, the dissolved oxygen concentration can reach 50 ppm or less. For stirring, a known method such as blowing Ar gas or blowing Ar gas can be used.
The reducing
撹拌動力密度の上限は特に定めない。使用する設備で可能な範囲とすればよく、例えば、10(kW/ton)以下の設備が知られている。 The upper limit of the stirring power density is not specified. The range may be within the range possible with the equipment to be used, and for example, equipment of 10 (kW / ton) or less is known.
図2は、高窒素ステンレス溶鋼の溶製過程における溶鋼窒素濃度のばらつきを表したイメージ図であり、(A)は従来方法、(B)は本実施の形態に係る高窒素ステンレス溶鋼の溶製方法を示している。
従来方法では、一次精錬工程から真空脱ガス工程、取鍋精錬工程へと処理が進むにつれて溶鋼窒素濃度のばらつきが拡大していき、取鍋精錬終了時に、目標とする溶鋼窒素濃度に達しない場合があることがわかる。
FIG. 2 is an image diagram showing variations in molten steel nitrogen concentration in the melting process of high nitrogen stainless molten steel. FIG. 2A is a conventional method, and FIG. 2B is a method for melting high nitrogen stainless molten steel according to the present embodiment. Is shown.
In the conventional method, when the processing progresses from the primary refining process to the vacuum degassing process and the ladle refining process, the variation in the molten steel nitrogen concentration increases and the target molten steel nitrogen concentration is not reached at the end of the ladle refining. It turns out that there is.
一方、本実施形態では、一次精錬工程において窒素溶解量のばらつきを低減し、さらに真空脱ガス工程において窒素脱離量のばらつきを低減するので、取鍋精錬工程前の段階で、溶鋼窒素濃度のばらつきが大幅に抑制されていることがわかる。また、取鍋精錬工程において、さらに脱酸処理をして溶鋼に窒素ガスを吹込むことにより、溶鋼窒素濃度のばらつきが取鍋精錬工程において発生していないことがわかる。総処理時間も従来方法に比べて大幅に短縮されている。 On the other hand, in the present embodiment, the variation in the amount of nitrogen dissolved in the primary refining step is reduced, and the variation in the amount of nitrogen desorbed in the vacuum degassing step is reduced. It can be seen that the variation is greatly suppressed. Further, it can be seen that the variation in the nitrogen concentration of the molten steel does not occur in the ladle refining step by further deoxidizing the molten steel in the ladle refining step and blowing nitrogen gas into the molten steel. The total processing time is also significantly reduced compared to the conventional method.
以上、本発明の一実施の形態について説明してきたが、本発明は何ら上記した実施の形態に記載の構成に限定されるものではなく、特許請求の範囲に記載されている事項の範囲内で考えられるその他の実施の形態や変形例も含むものである。 Although one embodiment of the present invention has been described above, the present invention is not limited to the configuration described in the above-described embodiment, but is within the scope of the claims. It also includes other possible embodiments and variations.
本発明の効果について検証するために実施した検証試験について説明する。
一次精錬工程には転炉を使用した。一次精錬工程では、還元剤(例えば、金属Siを含むFeSi合金、金属Al)投入後に窒素ガスを溶鋼に吹込んだ。一次精錬工程終了後、真空脱ガス工程で真空処理し、取鍋精錬工程において窒素ガスを溶鋼に吹込み窒素添加ステンレス溶鋼の溶製を行った。その際、溶鋼窒素濃度のばらつきを検証するため、還元条件及び脱ガス条件を変化させ、表1に示す成分値の窒素添加ステンレス溶鋼の溶製を行った。各溶鋼の成分値はタンディッシュで測定した。
The verification test carried out for verifying the effect of the present invention will be described.
A converter was used in the primary refining process. In the primary refining step, nitrogen gas was blown into the molten steel after the reducing agent (for example, FeSi alloy containing metallic Si, metallic Al) was added. After the completion of the primary refining step, vacuum treatment was performed in the vacuum degassing step, and nitrogen gas was blown into the molten steel in the ladle refining step to melt the nitrogen-added stainless molten steel. At that time, in order to verify the variation in the nitrogen concentration of the molten steel, the reduction conditions and the degassing conditions were changed, and the nitrogen-added stainless molten steel having the component values shown in Table 1 was melted. The component values of each molten steel were measured with a tundish.
なお、実施例2は、真空脱ガス処理後の取鍋精錬において、還元剤(例えば、金属Siを含むFeSi合金、金属Al)添加とArガス撹拌による脱酸処理を行って溶存酸素濃度を50ppm以下とした後、窒素ガスを溶鋼へ吹込んだ。 In Example 2, in the ladle refining after the vacuum degassing treatment, a reducing agent (for example, FeSi alloy containing metal Si, metal Al) was added and deoxidized treatment was performed by stirring Ar gas to reduce the dissolved oxygen concentration to 50 ppm. After the following, nitrogen gas was blown into the molten steel.
真空脱ガス工程において真空排気槽内の圧力を0.03MPaから最低圧力(0.01MPa)へ減圧するパターンは各ケース同じとし、最低圧力(0.01MPa)の保持時間を調整して、真空曝露時間(雰囲気圧力が0.03MPa以下の真空に暴露する時間)を決定した。 In the vacuum degassing step, the pattern of reducing the pressure in the vacuum exhaust tank from 0.03 MPa to the minimum pressure (0.01 MPa) is the same in each case, and the holding time of the minimum pressure (0.01 MPa) is adjusted to vacuum exposure. The time (time to expose to vacuum with atmospheric pressure of 0.03 MPa or less) was determined.
各ケースそれぞれ同じ条件で3回ずつ溶製を行って、窒素目標値に対する実測成分値の差の絶対値の平均値を算出し、算出した平均値を基に各ケースのばらつきを評価した。具体的には、平均値が3%以下の場合は◎(優)、3%超〜5%以下の場合は○(良)、5%超の場合には×(不可)とした。
検証試験結果を表2に示す。
Melting was performed three times under the same conditions in each case, the average value of the absolute values of the differences between the measured component values and the nitrogen target values was calculated, and the variation in each case was evaluated based on the calculated average values. Specifically, when the average value was 3% or less, it was evaluated as ⊚ (excellent), when it was more than 3% to 5% or less, it was evaluated as ○ (good), and when it was more than 5%, it was evaluated as × (impossible).
The verification test results are shown in Table 2.
表2より以下のことがわかる。
実施例1は溶鋼窒素濃度判定が○、実施例2は、取鍋精錬工程における窒素ガス吹込み時の溶存酸素濃度が50ppm以下であったため、溶鋼窒素濃度判定は◎であった。
一方、比較例1及び2は、還元剤投入直後の溶存酸素濃度が100ppm超であったため、溶鋼窒素濃度判定は×であった。比較例3は、真空暴露時間が40分を超えていたため、溶鋼窒素濃度判定は×であった。
The following can be seen from Table 2.
In Example 1, the molten steel nitrogen concentration determination was ◯, and in Example 2, the dissolved oxygen concentration at the time of blowing nitrogen gas in the ladle refining step was 50 ppm or less, so the molten steel nitrogen concentration determination was ⊚.
On the other hand, in Comparative Examples 1 and 2, since the dissolved oxygen concentration immediately after the addition of the reducing agent was more than 100 ppm, the molten steel nitrogen concentration determination was x. In Comparative Example 3, since the vacuum exposure time exceeded 40 minutes, the molten steel nitrogen concentration determination was x.
なお、実施例1と同じ処理条件で、異なるCr濃度、異なる窒素濃度のステンレス溶鋼の溶製を行ったところ、窒素濃度のばらつきは、上記実施例と同様、5%以内のばらつきで制御可能であった。 When molten stainless steels having different Cr concentrations and different nitrogen concentrations were melted under the same treatment conditions as in Example 1, the variation in nitrogen concentration could be controlled within 5% as in the above example. there were.
10:転炉(脱炭炉の一例)、11:取鍋、12:羽口、13、14:ランス、15:副原料投入口、16:真空排気槽、20:溶鋼(ステンレス溶鋼)、21:還元剤、22:酸素、23:窒素ガス、24:Arガス 10: converter (an example of decarburization furnace), 11: ladle, 12: tuyere, 13, 14: lance, 15: auxiliary material inlet, 16: vacuum exhaust tank, 20: molten steel (stainless molten steel), 21 : Reducing agent, 22: Oxygen, 23: Nitrogen gas, 24: Ar gas
Claims (2)
前記一次精錬工程後の真空脱ガス工程において、圧力が0.03MPa以下である真空雰囲気に前記溶鋼を暴露する時間を40分以下とし、
前記真空脱ガス工程後の取鍋精錬工程において、前記溶鋼中の溶存窒素量を基に該溶鋼に供給する窒素ガス量を決定し、該溶鋼に窒素ガスを供給することを特徴とする高窒素ステンレス溶鋼の溶製方法。 In the primary refining step, after adding a reducing agent to the stainless molten steel that has been decarburized by blowing acid, the molten steel is deoxidized until the dissolved oxygen concentration in the molten steel becomes 100 ppm or less, and then nitrogen gas is blown into the molten steel. Processed and steeled,
In the vacuum degassing step after the primary refining step, the time for exposing the molten steel to a vacuum atmosphere having a pressure of 0.03 MPa or less is set to 40 minutes or less.
In the pan refining step after the vacuum degassing step, the amount of nitrogen gas to be supplied to the molten steel is determined based on the amount of dissolved nitrogen in the molten steel, and the nitrogen gas is supplied to the molten steel. Melting method of molten stainless steel.