JP2021009813A - Electrochemical reaction cell stack - Google Patents

Abstract

To suppress a decrease in strength due to the pressing force from a first protruding portion included in a first current collecting member.SOLUTION: An electrochemical reaction cell stack includes a plurality of electrochemical reaction units each including a single cell having an electrolyte layer and an air electrode and a fuel electrode facing each other in the first direction across the electrolyte layer, and a first current collecting member arranged on one electrode side of the air electrode and the fuel electrode of the single cell. The first current collecting member includes a plurality of first protrusions periodically arranged at a fixed reference distance in a second direction perpendicular to the first direction. In at least one of the plurality of electrochemical reaction units, the surface of one electrode has a curvature of less than 0.0036 (1/mm) based on any three points aligned at reference distance intervals in the first directional view, and the curvature satisfies a first requirement that it is the reciprocal of the radius of a virtual circle passing through any three points in the third directional view perpendicular to both the first direction and the second direction.SELECTED DRAWING: Figure 6

Description

The techniques disclosed herein relate to electrochemical reaction cell stacks.

A solid oxide fuel cell (hereinafter referred to as "SOFC") having an electrolyte layer containing a solid oxide is known as one of the types of fuel cells that generate electricity by utilizing an electrochemical reaction between hydrogen and oxygen. Has been done. SOFCs are generally used in the form of fuel cell stacks comprising a plurality of power generation units arranged in a predetermined direction (hereinafter referred to as "first direction"). The power generation unit is arranged on one electrode side of a single cell including an air electrode and a fuel electrode facing each other in the first direction across the electrolyte layer and the air electrode and the fuel electrode of the single cell. A current collecting member that is electrically connected to the electrodes of the above. The current collecting member has a plurality of protrusions, each of which protrudes toward the surface of one electrode and is electrically connected to the surface of one electrode. Further, the plurality of protrusions are periodically arranged at predetermined distances in the second direction perpendicular to the first direction.

Here, for example, the single cell may have a warp in the first direction due to shrinkage during firing of the single cell or the like. If there is a warp in a single cell, for example, when stacking a plurality of single cells in the manufacturing stage of a fuel cell stack, the stacking load is concentrated on a specific location of the warped single cell, so that the single cell is cracked or cracked (hereinafter referred to as , "Cracks, etc.") are more likely to occur. Further, since the thermal stress is concentrated on a specific portion of the warped single cell due to the repetition of power generation and stop of the fuel cell stack, there is a high possibility that the single cell is cracked or the like.

Therefore, conventionally, various techniques have been proposed in which the overall amount of warpage (deflection amount) of a single cell is within a predetermined numerical range (Patent Documents 1 to 4).

Japanese Unexamined Patent Publication No. 2013-89496 Japanese Unexamined Patent Publication No. 2014-71935 Japanese Unexamined Patent Publication No. 2001-247373 Japanese Unexamined Patent Publication No. 2006-104058

The single cell is not limited to the overall warp of the single cell described above, but is simply due to, for example, variations in the thickness of the cell precursor and variations in the density of constituent components, which are the states before firing of the single cell. There may be local irregularities on the surface of the cell. Even if there are local irregularities on the surface of the single cell, there is a high possibility that cracks or the like will occur due to the pressing force from the protruding portion of the current collecting member at the irregularities. However, even if the above-mentioned conventional technique can suppress cracks and the like caused by the overall warpage of a single cell, it cannot suppress cracks and the like caused by local unevenness. Such problems become more prominent as the area and thinning of single cells are increased.

It should be noted that such a problem is also a problem common to solid oxide fuel cell (hereinafter referred to as "SOEC") that generates hydrogen by utilizing the electrolysis reaction of water. In the present specification, the fuel cell single cell and the electrolytic single cell are collectively referred to as an electrochemical reaction single cell.

This specification discloses a technique capable of solving at least a part of the above-mentioned problems.

The technique disclosed in the present specification can be realized in the following forms.

(1) The electrochemical reaction cell stack disclosed in the present specification includes a single cell containing an electrolyte layer containing a solid oxide and an air electrode and a fuel electrode facing each other in the first direction across the electrolyte layer. In an electrochemical reaction cell stack comprising a plurality of electrochemical reaction units, the first current collecting member arranged on one electrode side of the air electrode and the fuel electrode of the single cell. The current collecting member is a plurality of first projecting portions projecting toward the surface of the one electrode and electrically connected to the surface of the one electrode, and is a first projecting portion perpendicular to the first direction. It has a plurality of first protrusions periodically arranged in two directions at fixed reference distances, and in at least one of the plurality of electrochemical reaction units, the surface of the one electrode is formed. In the first directional view, the curvature based on any three points arranged at the interval of the reference distance is less than 0.0036 (1 / mm), and the curvature is the first direction and the second direction. In the third directional view perpendicular to both directions, the first requirement is satisfied that it is the inverse of the radius of the virtual circle passing through the arbitrary three points.

In the present electrochemical reaction cell stack, the surface of one electrode in at least one of a plurality of electrochemical reaction units is a reference which is the distance between the first protrusions periodically arranged in the first current collector. It satisfies the first requirement that the curvature based on any three points arranged at distance intervals is less than 0.0036 (1 / mm). As a result, according to the present electrochemical reaction cell stack, the local portion on the surface of one electrode is compared with the configuration in which a portion having the same curvature of 0.0036 (1 / mm) or more exists on the surface of one electrode. It is possible to suppress a decrease in strength due to vertical warpage. Further, the surface of one electrode has a curvature of less than 0.0036 (1 / mm) based on any three points arranged at intervals different from the reference distance. Since the variation in the pressing force received from each of the plurality of first protrusions of the first current collecting member is suppressed, the strength of the first current collecting member is reduced due to the pressing force from the first protrusion. It can be suppressed.

(2) In the electrochemical reaction cell stack, the surface of the one electrode may further satisfy the second requirement that the warpage rate of the surface is 0.18% or less. According to the present electrochemical reaction cell stack, the surface of one electrode of a single cell further satisfies the second requirement that the surface warpage rate is 0.18% or less. As a result, the strength of the single cell can be improved as compared with the configuration in which the surface warpage rate is higher than 0.18%.

(3) In the electrochemical reaction cell stack, the electrochemical reaction unit further comprises a second current collecting member arranged on the other electrode side of the single cell, which is located on the opposite side of the one electrode. The second current collecting member is a plurality of second projecting portions that project toward the surface of the other electrode and are electrically connected to the surface of the other electrode. It has a plurality of second protrusions arranged in the direction of the above, and in the first directional view, each of the second protrusions has the first protrusion of the first current collecting member. It may be configured to be located between the parts. In the present electrochemical reaction cell stack, each second protrusion of the second current collecting member is viewed in the first direction (opposite direction between the first current collecting member and the second current collecting member). It is located between the first protruding portions of the first current collecting member. Therefore, the single cell receives a large shear stress due to the pressing force from each of the first current collecting member and the second current collecting member. However, according to the present electrochemical reaction cell stack, the surface of one of the electrodes satisfies the first requirement, so that the shearing force due to the pressing force from the first current collecting member and the second current collecting member is obtained. It is possible to suppress the decrease in strength caused by.

The technique disclosed in the present specification can be realized in various forms, for example, a fuel cell power generation unit, a fuel cell stack including a plurality of fuel cell power generation units, and a power generation module including a fuel cell stack. , Fuel cell system with power generation module, electrolytic cell unit, electrolytic cell stack with multiple electrolytic cell units, hydrogen generation module with electrolytic cell stack, hydrogen generation system with hydrogen generation module, etc. Is.

It is a perspective view which shows the appearance structure of the fuel cell stack 100 in this embodiment. It is explanatory drawing which shows the XZ cross-sectional structure of the fuel cell stack 100 at the position of II-II of FIG. It is explanatory drawing which shows the YZ cross-sectional structure of the fuel cell stack 100 at the position of III-III of FIG. It is explanatory drawing which shows the XZ cross section configuration of two power generation units 102 adjacent to each other at the same position as the cross section shown in FIG. It is explanatory drawing which shows the YZ cross section configuration of two power generation units 102 adjacent to each other at the same position as the cross section shown in FIG. It is explanatory drawing which shows typically the XY plane (top surface) structure of a single cell 110. It is explanatory drawing which shows the cross-sectional structure of the single cell 110 at the position of VII-VII of FIG. It is explanatory drawing which shows the performance evaluation result.

A. Embodiment:
A-1. Constitution:
(Structure of fuel cell stack 100)
FIG. 1 is a perspective view showing an external configuration of the fuel cell stack 100 in the present embodiment, and FIG. 2 is an explanatory view showing an XZ cross-sectional configuration of the fuel cell stack 100 at the position II-II of FIG. FIG. 3 is an explanatory view showing a YZ cross-sectional configuration of the fuel cell stack 100 at the position III-III of FIG. Each figure shows XYZ axes that are orthogonal to each other to identify the direction. In the present specification, for convenience, the Z-axis positive direction is referred to as an upward direction, and the Z-axis negative direction is referred to as a downward direction, but the fuel cell stack 100 is actually installed in a direction different from such an orientation. May be done. The same applies to FIGS. 4 and later.

The fuel cell stack 100 includes a plurality of power generation units 102 (seven in this embodiment) and a pair of end plates 104 and 106. The seven power generation units 102 are arranged side by side in a predetermined arrangement direction (vertical direction in the present embodiment). The pair of end plates 104 and 106 are arranged so as to sandwich an aggregate composed of seven power generation units 102 from above and below. The arrangement direction (vertical direction) corresponds to the first direction in the claims.

A plurality of holes (eight in this embodiment) penetrating in the vertical direction are formed on the peripheral edge of each layer (power generation unit 102, end plates 104, 106) constituting the fuel cell stack 100 in the vertical direction. , The holes formed in each layer and corresponding to each other communicate with each other in the vertical direction to form a communication hole 108 extending in the vertical direction from one end plate 104 to the other end plate 106. In the following description, the holes formed in each layer of the fuel cell stack 100 to form the communication holes 108 may also be referred to as communication holes 108.

A bolt 22 extending in the vertical direction is inserted into each communication hole 108, and the fuel cell stack 100 is fastened by the bolt 22 and the nuts 24 fitted on both sides of the bolt 22. As shown in FIGS. 2 and 3, between the nut 24 fitted on one side (upper side) of the bolt 22 and the upper surface of the end plate 104 forming the upper end of the fuel cell stack 100, and the bolt. An insulating sheet 26 is interposed between the nut 24 fitted on the other side (lower side) of the 22 and the lower surface of the end plate 106 forming the lower end of the fuel cell stack 100. However, in the place where the gas passage member 27 described later is provided, the insulating sheets arranged on the upper side and the lower side of the gas passage member 27 and the gas passage member 27 between the nut 24 and the surface of the end plate 106, respectively. 26 is intervening. The insulating sheet 26 is made of, for example, a mica sheet, a ceramic fiber sheet, a ceramic dust sheet, a glass sheet, a glass-ceramic composite agent, or the like.

The outer diameter of the shaft portion of each bolt 22 is smaller than the inner diameter of each communication hole 108. Therefore, a space is secured between the outer peripheral surface of the shaft portion of each bolt 22 and the inner peripheral surface of each communication hole 108. As shown in FIGS. 1 and 2, the position is located near the midpoint of one side (the side on the positive side of the X axis among the two sides parallel to the Y axis) on the outer circumference of the fuel cell stack 100 around the Z direction. In the space formed by the bolt 22 (bolt 22A) and the communication hole 108 into which the bolt 22A is inserted, the oxidant gas OG is introduced from the outside of the fuel cell stack 100, and the oxidant gas OG is generated for each power generation. It functions as an oxidizer gas introduction manifold 161 that is a gas flow path supplied to the unit 102, and is the midpoint of the side opposite to the side (the side on the negative direction of the X axis of the two sides parallel to the Y axis). The space formed by the bolt 22 (bolt 22B) located in the vicinity and the communication hole 108 into which the bolt 22B is inserted provides the oxidizer off-gas OOG, which is the gas discharged from the air chamber 166 of each power generation unit 102. It functions as an oxidant gas discharge manifold 162 that discharges to the outside of the fuel cell stack 100. In this embodiment, for example, air is used as the oxidant gas OG.

Further, as shown in FIGS. 1 and 3, the vicinity of the midpoint of one side (the side on the positive side of the Y axis among the two sides parallel to the X axis) on the outer circumference of the fuel cell stack 100 around the Z direction. A fuel gas FG is introduced from the outside of the fuel cell stack 100 into the space formed by the bolt 22 (bolt 22D) located in the above and the communication hole 108 into which the bolt 22D is inserted, and the fuel gas FG is generated by each power generation. A bolt 22 that functions as a fuel gas introduction manifold 171 to be supplied to the unit 102 and is located near the midpoint of the side opposite to the side (the side on the negative side of the Y axis of the two sides parallel to the X axis). The space formed by (bolt 22E) and the communication hole 108 into which the bolt 22E is inserted sends the fuel off-gas FOG, which is the gas discharged from the fuel chamber 176 of each power generation unit 102, to the outside of the fuel cell stack 100. It functions as a fuel gas discharge manifold 172 to be discharged. In the present embodiment, for example, a hydrogen-rich gas obtained by reforming city gas is used as the fuel gas FG.

The fuel cell stack 100 is provided with four gas passage members 27. Each gas passage member 27 has a hollow tubular main body 28 and a hollow tubular branch 29 branched from the side surface of the main body 28. The hole of the branch portion 29 communicates with the hole of the main body portion 28. A gas pipe (not shown) is connected to the branch portion 29 of each gas passage member 27. Further, as shown in FIG. 2, the hole of the main body 28 of the gas passage member 27 arranged at the position of the bolt 22A forming the oxidant gas introduction manifold 161 communicates with the oxidant gas introduction manifold 161. The hole of the main body 28 of the gas passage member 27 arranged at the position of the bolt 22B forming the oxidant gas discharge manifold 162 communicates with the oxidant gas discharge manifold 162. Further, as shown in FIG. 3, the hole of the main body 28 of the gas passage member 27 arranged at the position of the bolt 22D forming the fuel gas introduction manifold 171 communicates with the fuel gas introduction manifold 171 and fuel gas. The hole of the main body 28 of the gas passage member 27 arranged at the position of the bolt 22E forming the discharge manifold 172 communicates with the fuel gas discharge manifold 172.

(Structure of end plates 104 and 106)
The pair of end plates 104 and 106 are substantially rectangular flat plate-shaped conductive members, and are made of, for example, stainless steel. One end plate 104 is arranged above the power generation unit 102 located at the top, and the other end plate 106 is arranged below the power generation unit 102 located at the bottom. A plurality of power generation units 102 are held in a pressed state by a pair of end plates 104 and 106. The upper end plate 104 functions as a positive output terminal of the fuel cell stack 100, and the lower end plate 106 functions as a negative output terminal of the fuel cell stack 100.

(Structure of power generation unit 102)
FIG. 4 is an explanatory view showing an XZ cross-sectional configuration of two power generation units 102 adjacent to each other at the same position as the cross section shown in FIG. 2, and FIG. 5 is an explanatory view showing an XZ cross-sectional configuration at the same position as the cross section shown in FIG. It is explanatory drawing which shows the YZ cross-sectional structure of two power generation units 102.

As shown in FIGS. 4 and 5, the power generation unit 102, which is the minimum unit of power generation, includes a single cell 110, a separator 120, an air pole side frame 130, an air pole side current collector 134, and a fuel pole side frame. It includes 140, a fuel electrode side current collector 144, and a pair of interconnectors 150 that form the uppermost layer and the lowermost layer of the power generation unit 102. Holes corresponding to the communication holes 108 into which the bolts 22 described above are inserted are formed in the peripheral edges of the separator 120, the air pole side frame 130, the fuel pole side frame 140, and the interconnector 150 in the Z direction.

The interconnector 150 is a substantially rectangular flat plate-shaped conductive member, and is made of, for example, ferritic stainless steel. The interconnector 150 ensures electrical continuity between the power generation units 102 and prevents mixing of reaction gases between the power generation units 102. In the present embodiment, when two power generation units 102 are arranged adjacent to each other, one interconnector 150 is shared by two adjacent power generation units 102. That is, the upper interconnector 150 in a certain power generation unit 102 is the same member as the lower interconnector 150 in another power generation unit 102 adjacent to the upper side of the power generation unit 102. Further, since the fuel cell stack 100 includes a pair of end plates 104 and 106, the power generation unit 102 located at the top of the fuel cell stack 100 does not have the upper interconnector 150 and is located at the bottom. The power generation unit 102 does not include the lower interconnector 150 (see FIGS. 2 and 3).

The single cell 110 includes an electrolyte layer 112, an air electrode (cathode) 114 and a fuel electrode (anode) 116 facing each other in the vertical direction (arrangement direction in which the power generation units 102 are arranged) with the electrolyte layer 112 in between. The single cell 110 of the present embodiment is a fuel pole support type single cell in which the fuel pole 116 supports the electrolyte layer 112 and the air pole 114.

The electrolyte layer 112 is a substantially rectangular flat plate-shaped member and contains at least Zr, and solid oxides such as YSZ (yttria-stabilized zirconia), ScSZ (scandia-stabilized zirconia), and CaSZ (calcia-stabilized zirconia). It is formed by objects. The air electrode 114 is a substantially rectangular flat plate-shaped member, and is formed of, for example, a perovskite-type oxide (for example, LSCF (lanternstrontium cobalt iron oxide), LSM (lanternstrontium manganese oxide), LNF (lantern nickel iron)). Has been done. The fuel electrode 116 is a substantially rectangular flat plate-shaped member, and is formed of, for example, Ni (nickel), a cermet composed of Ni and ceramic particles, a Ni-based alloy, or the like. As described above, the single cell 110 (power generation unit 102) of the present embodiment is a solid oxide fuel cell (SOFC) that uses a solid oxide as an electrolyte.

The separator 120 is a frame-shaped member in which a substantially rectangular hole 121 penetrating in the vertical direction is formed near the center, and is made of metal, for example. The peripheral portion of the hole 121 in the separator 120 faces the peripheral edge of the surface of the electrolyte layer 112 on the side of the air electrode 114. The separator 120 is bonded to the electrolyte layer 112 (single cell 110) by a bonding portion 124 formed of a brazing material arranged at the opposite portion thereof. The separator 120 partitions the air chamber 166 facing the air electrode 114 and the fuel chamber 176 facing the fuel electrode 116, and a gas leak from one electrode side to the other electrode side at the peripheral edge of the single cell 110. It is suppressed. The single cell 110 to which the separator 120 is joined is also referred to as a single cell with a separator.

The air electrode side frame 130 is a frame-shaped member in which a substantially rectangular hole 131 penetrating in the vertical direction is formed near the center, and is formed of, for example, an insulator such as mica. The hole 131 of the air electrode side frame 130 constitutes an air chamber 166 facing the air electrode 114. The air electrode side frame 130 is in contact with the peripheral edge of the surface of the separator 120 opposite to the side facing the electrolyte layer 112 and the peripheral edge of the surface of the interconnector 150 facing the air electrode 114. .. Further, the air electrode side frame 130 electrically insulates between the pair of interconnectors 150 included in the power generation unit 102. Further, in the air electrode side frame 130, the oxidant gas supply communication hole 132 that communicates the oxidant gas introduction manifold 161 and the air chamber 166, and the oxidant gas that communicates the air chamber 166 and the oxidant gas discharge manifold 162. A discharge communication hole 133 is formed.

The fuel electrode side frame 140 is a frame-shaped member in which a substantially rectangular hole 141 penetrating in the vertical direction is formed near the center, and is formed of, for example, metal. Hole 141 of the fuel electrode side frame 140 constitutes a fuel chamber 176 facing the fuel electrode 116. The fuel electrode side frame 140 is in contact with the peripheral edge of the surface of the separator 120 facing the electrolyte layer 112 and the peripheral edge of the surface of the interconnector 150 facing the fuel electrode 116. Further, in the fuel electrode side frame 140, a fuel gas supply communication hole 142 that communicates the fuel gas introduction manifold 171 and the fuel chamber 176, and a fuel gas discharge communication hole 143 that communicates the fuel chamber 176 and the fuel gas discharge manifold 172. And are formed.

The fuel electrode side current collector 144 is arranged in the fuel chamber 176. The fuel electrode side current collector 144 includes an interconnector facing portion 146, an electrode facing portion 145, and a connecting portion 147 connecting the electrode facing portion 145 and the interconnector facing portion 146. For example, nickel or nickel alloy. , Stainless steel, etc. The electrode facing portion 145 is in contact with the surface of the fuel pole 116 opposite to the side facing the electrolyte layer 112 (hereinafter, referred to as “lower surface 116D of the fuel pole 116”), and the interconnector facing portion 146 is an interconnector. It is in contact with the surface of the connector 150 on the side facing the fuel electrode 116. However, as described above, since the power generation unit 102 located at the bottom of the fuel cell stack 100 does not have the lower interconnector 150, the interconnector facing portion 146 in the power generation unit 102 is the lower end plate. It is in contact with 106. Since the fuel pole side current collector 144 has such a configuration, the fuel pole 116 and the interconnector 150 (or the end plate 106) are electrically connected to each other. A spacer 149 formed of, for example, mica is arranged between the electrode facing portion 145 and the interconnector facing portion 146. Therefore, the fuel electrode side current collector 144 follows the deformation of the power generation unit 102 due to the temperature cycle and the reaction gas pressure fluctuation, and the fuel electrode 116 and the interconnector 150 (or the end plate 106) via the fuel electrode side current collector 144 follow. Good electrical connection with is maintained.

The air pole side current collector 134 is arranged in the air chamber 166. The air electrode side current collector 134 is composed of a plurality of substantially square columnar current collector elements 135, and is formed of, for example, ferritic stainless steel. The air electrode side current collector 134 faces the surface of the air electrode 114 opposite to the side facing the electrolyte layer 112 (hereinafter, referred to as "the upper surface 114U of the air electrode 114") and the air electrode 114 of the interconnector 150. It is in contact with the surface on the side of the air. Specifically, the air electrode side current collector 134 is in a state of being pressed by the air electrode 114. However, as described above, since the power generation unit 102 located at the top of the fuel cell stack 100 does not have the upper interconnector 150, the air electrode side current collector 134 in the power generation unit 102 has an upper end plate. It is in contact with 104. Since the air electrode side current collector 134 has such a configuration, the air electrode 114 and the interconnector 150 (or the end plate 104) are electrically connected. The air electrode side current collector 134 and the interconnector 150 may be formed as an integral member.

A-2. Operation of fuel cell stack 100:
As shown in FIGS. 2 and 4, the oxidant gas OG is supplied via a gas pipe (not shown) connected to the branch portion 29 of the gas passage member 27 provided at the position of the oxidant gas introduction manifold 161. Then, the oxidant gas OG is supplied to the oxidant gas introduction manifold 161 through the holes of the branch portion 29 and the main body portion 28 of the gas passage member 27, and the oxidizer gas introduction manifold 161 oxidizes each power generation unit 102. It is supplied to the air chamber 166 through the agent gas supply communication hole 132. Further, as shown in FIGS. 3 and 5, the fuel gas FG is supplied via a gas pipe (not shown) connected to the branch portion 29 of the gas passage member 27 provided at the position of the fuel gas introduction manifold 171. Then, the fuel gas FG is supplied to the fuel gas introduction manifold 171 through the holes of the branch portion 29 and the main body portion 28 of the gas passage member 27, and the fuel gas supply communication of each power generation unit 102 is performed from the fuel gas introduction manifold 171. It is supplied to the fuel chamber 176 through the hole 142.

When the oxidant gas OG is supplied to the air chamber 166 of each power generation unit 102 and the fuel gas FG is supplied to the fuel chamber 176, power is generated by the electrochemical reaction of the oxidant gas OG and the fuel gas FG in the single cell 110. Will be. This power generation reaction is an exothermic reaction. In each power generation unit 102, the air pole 114 of the single cell 110 is electrically connected to one of the interconnectors 150 via the air pole side current collector 134, and the fuel pole 116 is via the fuel pole side current collector 144. It is electrically connected to the other interconnector 150. Further, the plurality of power generation units 102 included in the fuel cell stack 100 are electrically connected in series. Therefore, the electric energy generated in each power generation unit 102 is taken out from the end plates 104 and 106 that function as the output terminals of the fuel cell stack 100. Since the SOFC generates electricity at a relatively high temperature (for example, 700 ° C. to 1000 ° C.), the fuel cell stack 100 is a heater (for example, until the high temperature can be maintained by the heat generated by the power generation after the start-up. (Not shown) may be heated.

As shown in FIGS. 2 and 4, the oxidant off-gas OOG discharged from the air chamber 166 of each power generation unit 102 is discharged to the oxidant gas discharge manifold 162 through the oxidant gas discharge communication hole 133, and further oxidized. The fuel cell stack 100 is passed through the holes of the main body 28 and the branch 29 of the gas passage member 27 provided at the position of the agent gas discharge manifold 162, and the gas pipe (not shown) connected to the branch 29. It is discharged to the outside of. Further, as shown in FIGS. 3 and 5, the fuel off-gas FOG discharged from the fuel chamber 176 of each power generation unit 102 is discharged to the fuel gas discharge manifold 172 through the fuel gas discharge communication hole 143, and further, the fuel gas. To the outside of the fuel cell stack 100 via the holes of the main body 28 and the branch 29 of the gas passage member 27 provided at the position of the discharge manifold 172, and via a gas pipe (not shown) connected to the branch 29. It is discharged.

A-3. Arrangement relationship between the air pole side current collector 134 and the fuel pole side current collector 144:
As shown in FIG. 5, each current collector element 135 constituting the air electrode side current collector 134 protrudes toward the upper surface 114U of the air electrode 114 and is electrically connected to the upper surface 114U of the air electrode 114. There is. Further, the plurality of current collector elements 135 are constant while being spaced apart from each other in one direction (Y direction or less, also referred to as "arrangement direction of current collector elements 135") perpendicular to the vertical direction (Z direction). It is arranged periodically for each reference distance ΔD1. The reference distance ΔD1 is the distance between the center position of one current collector element 135 adjacent to each other in the same arrangement direction and the center position of the other current collector element 135 (arrangement period of the current collector element 135). .. In the present embodiment, for example, the reference distance ΔD1 is 2.5 mm, the width ΔD2 of each current collector element 135 in the array direction is 1.0 mm, and the two current collector elements 135 adjacent to each other. The separation distance ΔD3 between them is 1.5 mm. In the present embodiment, the shape of each current collector element 135 in the vertical direction is a rectangular shape that is long in the direction perpendicular to the arrangement direction (X direction) (see FIGS. 2 and 4). Further, the air electrode 114 corresponds to one electrode in the claims, the air electrode side current collector 134 corresponds to the first current collector member in the claims, and the current collector element 135 It corresponds to the first protrusion in the claims. Further, the arrangement direction of the current collector elements 135 corresponds to the second direction in the claims.

The electrode facing portion 145 and the connecting portion 147 (hereinafter, referred to as “electrode facing portion 145, etc.”) of the fuel pole side current collector 144 project toward the lower surface 116D of the fuel pole 116, and electricity is applied to the lower surface 116D of the fuel pole 116. Is connected. Further, the plurality of electrode facing portions 145 and the like are periodically arranged for each constant reference distance ΔD1 in the arrangement direction (Y direction) of the current collector element 135, similarly to the current collector element 135. Further, in the vertical view, each electrode facing portion 145 and the like are located between two current collector elements 135 adjacent to each other. In short, in the vertical view, the current collector element 135 and the electrode facing portion 145 and the like are arranged so as to be alternately arranged along the arrangement direction. However, at least one of the pair of electrode facing portions 145 and the like located at both ends in the same arrangement direction is located outside the current collector elements 135 located at both ends in the same arrangement direction. The fuel electrode 116 corresponds to the other electrode in the claims, the fuel electrode side current collector 144 corresponds to the second current collector member in the claims, and the electrode facing portion 145 and the like correspond to the electrode facing portion 145 and the like. It corresponds to the second protrusion in the claims.

A-4. Requirements for the surface of the air electrode 114 of the single cell 110:
FIG. 6 is an explanatory view schematically showing the XY plane (upper surface) configuration of the single cell 110, and FIG. 7 is parallel to the vertical direction (Z direction) of the single cell 110 at the position of VII-VII in FIG. It is explanatory drawing which shows the cross-sectional structure.

The single cell 110 meets at least the following first requirement with respect to the upper surface 114U of the air electrode 114. The upper surface 114U of the air electrode 114 is a surface extending in a plane direction substantially perpendicular to the vertical direction.
<First requirement>
"The upper surface 114U of the air electrode 114 has a curvature of less than 0.0036 (1 / mm) based on any three points arranged at intervals of the above-mentioned reference distance ΔD1 in the vertical view."
The "curvature" here is the reciprocal of the radius of the virtual circle passing through any three points in the direction (X direction) perpendicular to both the vertical direction and the arrangement direction.

The method for determining whether or not the first requirement is satisfied is as follows.
(1) A part of the surface of the upper surface 114U of the air electrode 114, not the entire surface, is defined as the target area E. The target area E is an area defined by a rectangle located inside by a predetermined width ΔH from the outer line of the air electrode 114. The predetermined width ΔH is 2.5% of the maximum width Q of the outer shape of the target area E in the vertical direction. The maximum width Q is the diagonal width of the rectangular air pole 114 in the example of FIG. The region from the outer line of the air electrode 114 to the predetermined width ΔH has a low contribution to the power generation reaction, and even if cracks or the like occur, the influence on the power generation characteristics of the single cell 110 is relatively small. Like the form, it is preferable not to include it in the target area E.
(2) A plurality of first virtual straight lines L1 arranged at intervals of a reference distance ΔD1 in the arrangement direction (Y direction) of the current collector elements 135 on the target region E, and a reference distance ΔD1 in a direction perpendicular to the arrangement direction. The second virtual straight line L2 arranged at the interval of is arranged, and among the plurality of intersections of the first virtual straight line L1 and the second virtual straight line L2, the intersection of one row arranged along the outermost circumference of the target area E. Other than the above, let the measurement point P for measuring the curvature. It is assumed that one intersection of the first virtual straight line L1 and the second virtual straight line L2 substantially coincides with the center point O of the air pole 114 in the vertical view. In FIG. 6, for convenience, the reference distance ΔD1 with respect to the size of the air electrode 114 is shown to be larger than the actual one.
(3) For each measurement point P, three intersections (measurement point P and its) arranged on a straight line centered on the measurement point P and parallel to the arrangement direction (second virtual straight line L2) in the vertical direction. Measure the curvature based on (two intersections located in the front and back). For example, the curvature centered on the measurement point P2 is calculated based on the measurement points P2 and the two intersections (measurement points P1 and P3) arranged along the second virtual straight line L2 with the measurement point P2 as the center. Specifically, as shown in the X1 portion enlarged in FIG. 6, when viewed in a direction (X direction) orthogonal to both the vertical direction (Z direction) and the arrangement direction (Y direction) of the current collector elements 135. The reciprocal of the radius of the virtual circle passing through the three measurement points P1 to P3 is defined as the curvature with respect to the measurement point P2. Information on the height difference in the vertical direction of the intersections of the three points can be obtained by a known device or method such as an optical 3D measuring device.
(4) When the curvature is less than 0.0036 (1 / mm) for all the measurement points P, it is determined that the first requirement is satisfied.

It is preferable that the single cell 110 further satisfies the following second requirement with respect to the upper surface 114U of the air electrode 114.
<Second requirement>
"The upper surface 114U of the air electrode 114 has a warp rate of 0.18% or less of the upper surface 114U of the air electrode 114."
The "warp rate (%)" referred to here is expressed by the following equation.
Warpage rate (%) = (“Maximum height difference ΔZ in target area E” / “Maximum width Q of outer shape of target area E”) × 100
The maximum height difference ΔZ in the target area E is the maximum height difference ΔZ of the target area E in the air pole 114 when the single cell 110 is arranged on the horizontal plane M with the fuel pole 116 facing down, as illustrated in FIG. It's a difference. Information on the vertical height difference of the upper surface 114U of the air electrode 114 can be obtained by a known device or method such as an optical 3D measuring device.

A-5. Manufacturing method of fuel cell stack 100:
First, a single cell 110 is produced. Specifically, it is as follows.
(Preparation of green sheet for fuel electrode substrate layer)
With respect to the mixed powder (100 parts by weight) of NiO powder (50 parts by weight) and YSZ powder (50 parts by weight), organic beads (15% by weight with respect to the mixed powder) which are pore-forming materials, and butyral resin , DOP which is a plasticizer, a dispersant, and a mixed solvent of toluene + ethanol are added and mixed with a ball mill to prepare a slurry. Organic beads are, for example, spherical particles formed of a polymer such as polymethyl methacrylate or polystyrene. The obtained slurry is thinned by the doctor blade method and dried to prepare a green sheet for a fuel electrode substrate layer having a thickness of 200 μm or more and 300 μm or less. Specifically, the obtained slurry is defoamed and stirred, thinned by a doctor blade method, and coated on a carrier (not shown). The coated slurry is conveyed from the carry-in port of the drying chamber (not shown) toward the carry-out port by the carrier. Drying air flowing from the carry-in port to the carry-out port is supplied to the drying chamber.

Here, by controlling the air flow velocity at the inlet of the drying chamber, the inhomogeneity of the green sheet for the fuel electrode substrate layer after drying (for example, the variation in the thickness of the green sheet and the density of the constituent components of the green sheet). (Variation, etc.) is suppressed, and as a result, not only the overall warp of the fuel electrode substrate layer formed by the firing step described later but also the occurrence of local unevenness can be suppressed. That is, it is difficult to supply air from the carry-in port to the drying chamber at a uniform flow velocity (flow rate) over the width direction orthogonal to the transport direction, and there is a difference in air flow velocity in the width direction in the transport chamber. For example, on the outside in the width direction of the drying chamber, the flow velocity of air is slower than that on the center side in the width direction due to the resistance of the inner side wall of the drying chamber. If there is a difference in air flow velocity in this width direction, the drying variation becomes large especially in the portion of the slurry to be conveyed, which is located near the carry-in port and still contains a large amount of solvent, and as a result, the fuel electrode after drying becomes large. The green sheet for the substrate layer becomes inhomogeneous. On the other hand, by slowing the flow velocity of the air at the carry-in port, the difference in the flow velocity of the air in the width direction can be reduced. Therefore, the inhomogeneity of the green sheet for the fuel electrode substrate layer can be suppressed by appropriately adjusting the air flow velocity at the carry-in port. The ratio of NiO powder and YSZ powder in the green sheet for the fuel electrode substrate layer can be appropriately changed as long as the performance is satisfied. For example, even if the NiO powder: YSZ powder is 60:40 or 40:60. I do not care. That is, the NiO powder can be appropriately changed between 40 and 60 parts by weight so that the mixed powder of the NiO powder and the YSZ powder is 100 parts by weight, and the rest can be the YSZ powder.

(Preparation of green sheet for fuel polar active layer)
A butyral resin, a plasticizer DOP, a dispersant, and a toluene + ethanol mixed solvent are added to a mixed powder (100 parts by weight) of NiO powder (60 parts by weight) and YSZ powder (40 parts by weight). In addition, mix with a ball mill to prepare the slurry. The obtained slurry is thinned by a doctor blade method to prepare a green sheet for a fuel polar active layer having a thickness of 10 μm or more and 30 μm or less. The ratio of NiO powder and YSZ powder in the green sheet for the fuel polar active layer can be appropriately changed as long as the performance is satisfied. For example, even if the NiO powder: YSZ powder is 50:50 or 40:60. I do not care. That is, the NiO powder can be appropriately changed between 40 and 60 parts by weight so that the mixed powder of the NiO powder and the YSZ powder is 100 parts by weight, and the rest can be the YSZ powder.

(Preparation of green sheet for electrolyte layer)
Butyral resin, plasticizer DOP, dispersant, and toluene + ethanol mixed solvent are added to YSZ powder (100 parts by weight) and mixed with a ball mill to prepare a slurry. The obtained slurry is thinned by the doctor blade method to prepare a green sheet for an electrolyte layer having a thickness of 5 μm or more and 15 μm or less.

(Lamination of electrolyte layer 112 and fuel electrode 116)
The green sheet for the fuel electrode substrate layer, the green sheet for the fuel electrode active layer, and the green sheet for the electrolyte layer are attached and degreased at about 280 ° C. Further, firing is performed at about 1350 ° C. to obtain a laminate of the electrolyte layer 112 and the fuel electrode 116. Here, as described above, the single cell 110 of the present embodiment is a fuel electrode support type single cell, and has the thickness of the fuel electrode active layer (green sheet for the fuel electrode active layer) and the electrolyte layer 112 (for the electrolyte layer). The thickness of the green sheet) is extremely thin compared to the thickness of the fuel electrode substrate layer (green sheet for the fuel electrode substrate layer). Therefore, the cause of the warp and local unevenness of the laminate (so-called half cell) of the electrolyte layer 112 and the fuel electrode 116 is mainly the heterogeneity of the green sheet for the fuel electrode substrate layer. That is, in the laminate of the electrolyte layer 112 and the fuel electrode 116, the electrolyte layer 112 and the fuel electrode active layer are thinner and more easily deformed than the fuel electrode substrate layer, so that the fuel electrode substrate layer is warped or locally uneven. As a result, the shape of the surface (upper surface) of the electrolyte layer 112 opposite to that of the fuel electrode active layer also becomes a shape corresponding to the warp and local unevenness of the fuel electrode substrate layer. Therefore, in the present embodiment, the flow velocity of the air for drying is not particularly controlled at the stage of producing the green sheet for the electrolyte layer and the green sheet for the fuel polar active layer. Of course, even at the stage of producing the green sheet for the electrolyte layer and the green sheet for the fuel polar active layer, the heterogeneity of the green sheet for the electrolyte layer and the green sheet for the fuel polar active layer can be improved by controlling the flow velocity of the air for drying. It is preferable to suppress it.

(Formation of air pole 114)
A mixed solution consisting of La _0.6 Sr _0.4 Co _0.2 Fe _0.8 O ₃ powder and isopropyl alcohol is prepared. The prepared mixed solution can be screen-printed on the surface of the electrolyte layer 112 in the above-mentioned laminate and fired at 1100 ° C. to form an air electrode 114 to obtain a fired body (single cell 110 before reduction). it can. The thickness of the air electrode 114 is also extremely thin as compared with the thickness of the fuel electrode substrate layer (green sheet for the fuel electrode substrate layer), as is the thickness of the fuel electrode active layer and the like. Therefore, the influence of the inhomogeneity of the air electrode 114 on the warp of the single cell 110 is small.

After that, the remaining assembly steps (for example, joining the air electrode 114 and the air electrode side current collector 134 and fastening the fuel cell stack 100 with bolts 22) are performed, and the assembly of the fuel cell stack 100 is completed.

A-6. Effect of this embodiment:
As described above, in the fuel cell stack 100 of the present embodiment, the plurality of current collector elements 135 included in the air electrode side current collector 134 are constant in the arrangement direction (Y direction) of the current collector elements 135. It is periodically arranged for each reference distance ΔD1 (see FIGS. 3, 5 and 6). The upper surface 114U of the air electrode 114 in the single cell 110 has a curvature of less than 0.0036 (1 / mm) based on any three points arranged at intervals of the reference distance ΔD1 in the vertical view (first). Requirements). As a result, according to the present embodiment, there is a local portion on the upper surface 114U of the air electrode 114 as compared with a configuration in which a portion having the same curvature of 0.0036 (1 / mm) or more exists on the upper surface 114U of the air electrode 114. It is possible to suppress a decrease in strength due to warpage (for example, occurrence of cracks in the single cell 110). Further, according to the present embodiment, poor contact between the air electrode 114 and the current collector element 135 occurs due to the local unevenness of the upper surface 114U of the air electrode 114, and the air electrode 114 and the current collector element 135 ( It is possible to suppress a decrease in electrical conductivity with the air electrode side current collector 134).

Further, even if the curvature based on any three points on the upper surface 114U of the air electrode 114 is less than 0.0036 (1 / mm), the distance between the arbitrary three points is different from the reference distance ΔD1. In the configuration (hereinafter referred to as "comparative configuration"), the following problems occur. That is, in the comparative configuration, the appearance cycle of the unevenness on the upper surface 114U of the air electrode 114 and the arrangement period of the plurality of current collector elements 135 included in the current collector 134 on the air electrode side are different. Therefore, each of the plurality of portions having different uneven heights on the upper surface 114U of the air electrode 114 is pressed by each current collector element 135. As a result, on the upper surface 114U of the air electrode 114, for example, the single cell 110 is likely to be cracked due to the variation in the pressing force received from the plurality of current collector elements 135. On the other hand, in the present embodiment, the appearance cycle of the unevenness on the upper surface 114U of the air electrode 114 and the arrangement cycle of the plurality of current collector elements 135 are the same. Therefore, since the variation of the pressing force received by the upper surface 114U of the air electrode 114 from each of the plurality of current collector elements 135 is suppressed, the decrease in strength of the single cell 110 due to the pressing force from the current collector element 135 is suppressed. can do.

Further, in the fuel cell stack 100 of the present embodiment, the upper surface 114U of the air electrode 114 in the single cell 110 further has a warpage rate of 0.18% or less on the entire surface (second requirement). As a result, the strength of the single cell 110 can be improved as compared with the configuration in which the warpage rate of the entire surface is higher than 0.18%.

In the fuel cell stack 100 of the present embodiment, the electrode facing portion of the fuel pole side current collector 144 is viewed in the vertical direction (the direction opposite to the Z direction air pole side current collector 134 and the fuel pole side current collector 144). 145 and the like are located between the current collector elements 135 of the air electrode side current collector 134. Therefore, the single cell 110 receives a large shear stress due to the pressing force from each of the current collector element 135 and the electrode facing portion 145 and the like. However, according to the present embodiment, the upper surface 114U of the air electrode 114 satisfies the first requirement, and is caused by the shearing force due to the pressing force from the first current collecting member and the second current collecting member. It is possible to suppress a decrease in strength.

A-7. Performance evaluation:
A plurality of single-cell samples were prepared, and performance evaluation was performed using the prepared multiple single-cell samples. FIG. 8 is an explanatory diagram showing the performance evaluation result. The ratio of the curvature C in FIG. 8 indicates the degree of local unevenness on the outer surface (upper surface 114U) of the air electrode 114 of the single cell. Specifically, the curvature C at each measurement point P in the target region E is measured by the method of determining whether or not the above-mentioned first requirement is satisfied. Next, based on the measurement result, a measurement point P having a curvature C of less than 0.0010 (1 / mm) and a curvature C of 0.0010 (1 / mm) or more and less than 0.0020 (1 / mm). The measurement point P and the measurement point P having a curvature C of 0.0020 (1 / mm) or more and less than 0.0030 (1 / mm) and a curvature C of 0.0030 (1 / mm) or more and 0.0036 ( It is classified into a measurement point P having a curvature C of less than 1 / mm) and a measurement point P having a curvature C of 0.0036 (1 / mm) or more. The ratio of the curvature for each classification means the ratio of the number of measurement points P belonging to the classification to the total number of measurement points P in the target region E. Further, the warp rate in FIG. 8 means the overall warp rate of the upper surface 114U of the air electrode 114 in the second requirement described above. The presence or absence of cell cracks means the presence or absence of cracks or cracks (hereinafter referred to as "cracks, etc.") in a single cell when each sample is incorporated into the fuel cell stack 100. In particular, the pressing of the air electrode side current collector 134 (current collector element 135) against the air electrode 114 causes cracks or the like in the single cell. In this evaluation, the single cell is sandwiched between the air electrode side current collector 134 and the fuel electrode side current collector 144 in the vertical direction, and the current collector element 135 and the electrode facing portion 145 and the like are described in the vertical direction. Arrange the current collector elements 135 alternately along the arrangement direction (see FIGS. 3 and 5), pressurize them in the vertical direction with a press device (not shown), and then check for cracks in the single cell. Judged. The presence or absence of cracks in a single cell can be determined based on, for example, visual recognition or the sound of hitting the single cell.

A-7-1. For each sample:
As shown in FIG. 8, the performance evaluation was performed on Comparative Examples and Examples 1 to 6. Comparative Examples and Examples 1 to 6 are single cells including an electrolyte layer 112, an air electrode 114, and a fuel electrode 116, and have at least one of a degree of local unevenness and an overall warpage rate. Different from each other. In the comparative example, there is a measurement point P having a curvature C of 0.0036 (1 / mm) or more, and in Examples 1 to 6, there is no measurement point P having a curvature C of 0.0036 (1 / mm) or more. .. In Comparative Examples and Examples 1 and 3, the warp rate is 0.18% or more, and in Examples 2 and 4 to 6, the warp rate is less than 0.18%.

A-7-2. Evaluation result:
As shown in FIG. 8, in the comparative example, there was a measurement point P having a curvature C of 0.0036 (1 / mm) or more, and cracks or the like occurred in the single cell. On the other hand, in Examples 1 to 6, there is no measurement point P having a curvature C of 0.0036 (1 / mm) or more, and no cracks or the like occur in the single cell. From this evaluation result, the single cell is the first requirement (the upper surface 114U of the air electrode 114 has a curvature based on any three points arranged at intervals of the reference distance ΔD1 which is the arrangement period of the current collector element 135 in the vertical view. Is less than 0.0036 (1 / mm)), it can be seen that the occurrence of cracks and the like in a single cell can be suppressed. Further, although the warpage rates of Comparative Examples and Examples 1 and 3 were almost the same, cracks and the like occurred in a single cell only in Comparative Examples. This means that even if the overall warpage rate in a single cell is the same, cracks and the like are likely to occur due to the presence of local irregularities. Conversely, even if the warpage rate is 0.18% or more, it means that the occurrence of cracks or the like in a single cell can be suppressed by satisfying the first requirement. That is, satisfying the first requirement for a single cell is effective in suppressing the occurrence of cracks and the like.

B. Modification example:
The technique disclosed in the present specification is not limited to the above-described embodiment, and can be transformed into various forms without departing from the gist thereof. For example, the following modifications are also possible. For example, in the above embodiment, the fuel pole support type single cell 110 is exemplified as the single cell, but the composite may be an electrolyte support type single cell or an air pole support type single cell. For example, in an electrolyte-supported single cell, it is preferable that at least the first requirement is satisfied for the outer surface of either the fuel electrode or the air electrode opposite to the electrolyte layer. Further, the single cell 110 may be configured to include an intermediate layer (reaction prevention layer) at least between the electrolyte layer 112 and the air electrode 114 and between the electrolyte layer 112 and the fuel electrode 116. .. Further, in the above embodiment, all the power generation units 102 satisfy the first requirement, but at least one power generation unit 102 may satisfy the first requirement. Of the total power generation units 102 included in the fuel cell stack 100, 50% of the power generation units 102 preferably satisfy the first requirement, and 80% of the power generation units 102 more preferably satisfy the first requirement.

Further, in the above embodiment, the reference distance ΔD1 may be less than 2.5 mm or longer than 2.5 mm. In short, the reference distance ΔD1 may be an arrangement period of the current collector elements 135 in the air electrode side current collector 134. Further, in the above embodiment, the shape of each current collector element 135 in the vertical direction is a rectangular shape extending over substantially the entire length of the single cell 110 in the X direction. For example, each current collector element 135 has a rectangular shape. It may be composed of a plurality of rectangular protrusions arranged at intervals in the X direction of the single cell 110. Further, the shape of the protruding portion in the vertical direction may be circular, square, elliptical or the like. Here, when the shape of the protruding portion in the vertical direction is long in one direction (for example, the X direction in FIG. 6), the reference distance is the direction perpendicular to the longitudinal direction of the long shape in one direction. It is preferable to set the arrangement period of the protruding portions in (for example, the Y direction in FIG. 6) and satisfy the first requirement in the vertical direction. Further, the shape of the protruding portion in the vertical direction is a symmetrical shape such as a circle or a square, and the plurality of protruding portions are orthogonal to each other in two directions (for example, the X direction and the Y direction in FIG. 6). In a configuration arranged with the same arrangement period, it is preferable to measure the curvature in each of the two directions and the average value of the curvatures satisfies the first requirement. When a plurality of protrusions are arranged in a direction along a diagonal line in a rectangular single cell, it is preferable that the first requirement is satisfied in the direction along the diagonal line.

Further, in the above embodiment, the upper surface 114U of the air electrode 114 does not have to satisfy the second requirement. Further, in the above embodiment, the electrode facing portion 145 or the like of the fuel pole side current collector 144 is not located between the current collector elements 135 of the air pole side current collector 134 in the vertical view. It may be a configuration.

Further, the material forming each member in the above embodiment is merely an example, and each member may be formed of another material.

For example, the techniques disclosed herein can also be applied to known structures of fuel cells such as cylindrical and cylindrical flat plates. In the case of these fuel cells, the above-mentioned maximum width Q in the first requirement is the maximum outer diameter of the circular cell.

Further, in the above embodiment, the SOFC that generates power by utilizing the electrochemical reaction between hydrogen contained in the fuel gas and oxygen contained in the oxidizing agent gas is targeted, but the present invention comprises an electrolysis reaction of water. It is also applicable to an electrolytic cell unit, which is the smallest unit of a solid oxide fuel cell (SOEC) that uses it to generate hydrogen, and an electrolytic cell stack having a plurality of electrolytic cell units. The configuration of the electrolytic cell stack is not described in detail here because it is known as described in, for example, Japanese Patent Application Laid-Open No. 2014-207120, but is generally the same as the fuel cell stack 100 in the above-described embodiment. It is a configuration. That is, the fuel cell stack 100 in the above-described embodiment may be read as an electrolytic cell stack, and the power generation unit 102 may be read as an electrolytic cell unit. However, during the operation of the electrolytic cell stack, a voltage is applied between both electrodes so that the air electrode 114 is positive (anode) and the fuel electrode 116 is negative (cathode), and the voltage is applied through the communication hole 108. Water vapor as a raw material gas is supplied. As a result, an electrolysis reaction of water occurs in each electrolytic cell unit, hydrogen gas is generated in the fuel chamber 176, and hydrogen is taken out to the outside of the electrolytic cell stack through the communication hole 108. Even in the electrolytic cell unit and the electrolytic cell stack having such a configuration, if the configuration in which the electrolytic cell satisfies the first requirement is adopted as in the above embodiment, the strength is lowered due to the local warpage on the surface of the electrolytic cell. It has the effect of suppressing.

22: Bolt 24: Nut 26: Insulation sheet 27: Gas passage member 28: Main body 29: Branch 100: Fuel cell stack 102: Power generation unit 104, 106: End plate 108: Communication hole 110: Single cell 112: Electrolyte layer 114: Air pole 114U: Top surface 116: Fuel pole 120: Separator 121: Hole 124: Joint 130: Air pole side frame 131: Hole 132: Oxidizing agent gas supply communication hole 133: Oxidizing agent gas discharge communication hole 134: Air pole Side current collector 135: Current collector element 140: Fuel pole side frame 141: Hole 142: Fuel gas supply communication hole 143: Fuel gas discharge communication hole 144: Fuel pole side current collector 145: Electrode facing part 146: Interconnector Opposing part 147: Connecting part 149: Spacer 150: Interconnector 161: Oxidizing gas introduction manifold 162: Oxidizing gas discharge manifold 166: Air chamber 171: Fuel gas introduction manifold 172: Fuel gas discharge manifold 176: Fuel chamber ΔD1: Reference Distance E: Target area H: Predetermined width Δ L1: First virtual straight line L2: Second virtual straight line M: Plane O: Center point Q: Maximum width ΔZ: Maximum height difference

Claims (3)

A single cell containing an electrolyte layer containing a solid oxide and an air electrode and a fuel electrode facing each other in a first direction across the electrolyte layer, and one electrode side of the air electrode and the fuel electrode of the single cell. In an electrochemical reaction cell stack comprising a plurality of electrochemical reaction units comprising a first current collector arranged in
The first current collecting member is a plurality of first projecting portions projecting toward the surface of the one electrode and electrically connected to the surface of the one electrode, and is the first direction. It has a plurality of first protrusions periodically arranged at regular reference distances in a second direction perpendicular to.
In at least one of the plurality of electrochemical reaction units, the surface of the one electrode is
In the first directional view, the curvature based on any three points arranged at the reference distance interval is less than 0.0036 (1 / mm).
Moreover, the curvature is the reciprocal of the radius of the virtual circle passing through the arbitrary three points in the third directional view perpendicular to both the first direction and the second direction.
Meet the first requirement,
It is characterized by an electrochemical reaction cell stack. In the electrochemical reaction cell stack according to claim 1,
The surface of the one electrode further
The second requirement that the warpage rate of the surface is 0.18% or less is satisfied.
It is characterized by an electrochemical reaction cell stack. In the electrochemical reaction cell stack according to claim 1 or 2.
The electrochemical reaction unit further comprises a second current collecting member arranged on the other electrode side of the single cell, which is located on the opposite side of the one electrode.
The second current collecting member is a plurality of second projecting portions that project toward the surface of the other electrode and are electrically connected to the surface of the other electrode, and are in the second direction. It has multiple second protrusions arranged in
In the first directional view, each of the second protrusions is located between the first protrusions of the first current collector.
It is characterized by an electrochemical reaction cell stack.