JP2021000872A - Pneumatic tire - Google Patents
Pneumatic tire Download PDFInfo
- Publication number
- JP2021000872A JP2021000872A JP2019114579A JP2019114579A JP2021000872A JP 2021000872 A JP2021000872 A JP 2021000872A JP 2019114579 A JP2019114579 A JP 2019114579A JP 2019114579 A JP2019114579 A JP 2019114579A JP 2021000872 A JP2021000872 A JP 2021000872A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- tread rubber
- mass
- cap
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、空気入りタイヤに関するものであり、詳しくは、ロードノイズの低減、操縦安定性および耐久性の向上を同時に満たす空気入りタイヤに関するものである。 The present invention relates to a pneumatic tire, and more particularly to a pneumatic tire that simultaneously satisfies the reduction of road noise, the improvement of steering stability and the durability.
空気入りタイヤは左右一対のビード部およびサイドウォール部と、両サイドウォール部に連なるとともにキャップトレッドとアンダートレッドとからなるトレッド部から主に構成されている。タイヤの内側にはカーカス層が設けられ、カーカス層の両端部はビードコアをタイヤ内側から外側へ包みこむように折り返されている。 Pneumatic tires are mainly composed of a pair of left and right bead parts and sidewall parts, and a tread part that is connected to both sidewall parts and is composed of a cap tread and an under tread. A carcass layer is provided on the inside of the tire, and both ends of the carcass layer are folded back so as to wrap the bead core from the inside to the outside of the tire.
ところで、モータを動力源として走行する電気自動車は、内燃機関を動力源として走行する自動車と比較して、車両由来の騒音が大きく低減されている一方で、車両走行におけるタイヤ由来の騒音（ロードノイズ）については両自動車共に差異がみられない。そのため、タイヤ由来のロードノイズをさらに低減させる技術が求められている。 By the way, an electric vehicle that runs on a motor as a power source has significantly reduced vehicle-derived noise as compared to a vehicle that runs on an internal combustion engine, while tire-derived noise (road noise) during vehicle running. ), There is no difference between the two cars. Therefore, there is a demand for a technique for further reducing road noise derived from tires.
ロードノイズを低減するには、例えばキャップトレッドゴム等のタイヤを構成する部材を柔らかくすることによって、タイヤのバネ特性を低下させる手法が知られている。しかし、例えばキャップトレッドゴムを柔らかくすると操縦安定性および耐久性が低下するという問題点があり、ロードノイズの低減と、操縦安定性および耐久性の向上とは、二律背反の関係にある。 In order to reduce road noise, there is known a method of reducing the spring characteristics of a tire by softening a member constituting the tire such as a cap tread rubber. However, for example, softening the cap tread rubber has a problem that steering stability and durability are lowered, and reduction of road noise and improvement of steering stability and durability are in a trade-off relationship.
なお、ロードノイズの低減と操縦安定性の向上を図る技術としては、例えば特許文献１〜３に開示がある。 Patent Documents 1 to 3 disclose, for example, as a technique for reducing road noise and improving steering stability.
したがって本発明の目的は、ロードノイズの低減、操縦安定性および耐久性の向上を同時に満たす空気入りタイヤを提供することにある。 Therefore, an object of the present invention is to provide a pneumatic tire that simultaneously satisfies the reduction of road noise, the improvement of steering stability and the durability.
本発明者は鋭意研究を重ねた結果、アンダートレッドゴムの厚み、アンダートレッドゴムの組成、およびキャップトレッドゴムの硬度とアンダートレッドゴムの貯蔵弾性率の比を特定化することにより、前記課題を解決できることを見出し、本発明を完成することができた。
すなわち本発明は以下の通りである。
As a result of intensive studies, the present inventor has solved the above problems by specifying the thickness of the undertread rubber, the composition of the undertread rubber, and the ratio of the hardness of the cap tread rubber to the storage elastic modulus of the undertread rubber. We found what we could do and were able to complete the present invention.
That is, the present invention is as follows.
１．キャップトレッドゴムと、前記キャップトレッドゴムのタイヤ径方向内側に配置されるアンダートレッドゴムと、を備える空気入りタイヤにおいて、
前記アンダートレッドゴムの厚みが前記キャップトレッドゴムの厚みの５％以上であり、
前記アンダートレッドゴムは、ジエン系ゴム１００質量部に対し、天然ゴムを４０質量部以上、カーボンブラックを４０質量部以上、およびシリカを２０質量部以下配合してなり、かつ
前記キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）と、前記アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）とが、下記式を満たす
ことを特徴とする空気入りタイヤ。
３．５≦（Ｈｓ cap）／（Ｅ’ut）≦１８．０
２．前記カーボンブラックの窒素吸着比表面積（Ｎ２ＳＡ）が、２５〜１２０ｍ２／ｇであることを特徴とする前記１に記載の空気入りタイヤ。
３．前記ジエン系ゴム１００質量部に対し、前記カーボンブラックの配合割合が４０〜８０質量部であることを特徴とする前記１または２に記載の空気入りタイヤ。
1. 1. In a pneumatic tire including a cap tread rubber and an under tread rubber arranged inside the cap tread rubber in the tire radial direction.
The thickness of the under tread rubber is 5% or more of the thickness of the cap tread rubber.
The undertread rubber is made by blending 40 parts by mass or more of natural rubber, 40 parts by mass or more of carbon black, and 20 parts by mass or less of silica with 100 parts by mass of diene rubber, and 20 parts by mass of the cap tread rubber. A pneumatic tire characterized in that the hardness (Hs cap) at ° C. and the storage elastic modulus (E'ut) of the undertread rubber at 20 ° C. satisfy the following formula.
3.5 ≤ (Hs cap) / (E'ut) ≤ 18.0
2. 2. The pneumatic tire according to 1 above, wherein the carbon black has a nitrogen adsorption specific surface area (N 2 SA) of 25 to 120 m 2 / g.
3. 3. The pneumatic tire according to 1 or 2, wherein the blending ratio of the carbon black is 40 to 80 parts by mass with respect to 100 parts by mass of the diene rubber.
本発明の空気入りタイヤは、キャップトレッドゴムと、前記キャップトレッドゴムのタイヤ径方向内側に配置されるアンダートレッドゴムと、を備え、前記アンダートレッドゴムの厚みが前記キャップトレッドゴムの厚みの５％以上であり、前記アンダートレッドゴムは、ジエン系ゴム１００質量部に対し、天然ゴムを４０質量部以上、カーボンブラックを４０質量部以上、およびシリカを２０質量部以下配合してなり、かつ前記キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）と、前記アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）とが、３．５０≦（Ｈｓ cap）／（Ｅ’ut）≦１８．０を満たすことを特徴としているので、ロードノイズの低減、操縦安定性および耐久性の向上を同時に満たす空気入りタイヤを提供することができる。 The pneumatic tire of the present invention includes a cap tread rubber and an under tread rubber arranged inside the cap tread rubber in the tire radial direction, and the thickness of the under tread rubber is 5% of the thickness of the cap tread rubber. As described above, the undertread rubber is made by blending 40 parts by mass or more of natural rubber, 40 parts by mass or more of carbon black, and 20 parts by mass or less of silica with respect to 100 parts by mass of diene rubber, and the cap. The hardness (Hs cap) of the tread rubber at 20 ° C. and the storage elastic coefficient (E'ut) of the under tread rubber at 20 ° C. are 3.50 ≦ (Hs cap) / (E'ut) ≦ 18.0. Since it is characterized by satisfying, it is possible to provide a pneumatic tire that simultaneously satisfies the reduction of road noise, the improvement of steering stability and the durability.
上述のように、ロードノイズを低減するには、キャップトレッドゴムを柔らかくすることが有効であるが、その反面、操縦安定性および耐久性が低下してしまう。本発明では、アンダートレッドゴムの厚み、アンダートレッドゴムの組成、およびキャップトレッドゴムの硬度とアンダートレッドゴムの貯蔵弾性率の比を特定化することにより、キャップトレッドゴムがロードノイズの改善を担い操縦安定性および耐久性を減じた場合でも、アンダートレッドゴムが操縦安定性および耐久性を補完する役割を果たし、結果として二律背反の関係にあるロードノイズの低減と操縦安定性および耐久性の向上とを同時に達成することが可能となった。 As described above, in order to reduce road noise, it is effective to soften the cap tread rubber, but on the other hand, steering stability and durability are lowered. In the present invention, the cap tread rubber is responsible for improving the road noise and maneuvering by specifying the thickness of the under tread rubber, the composition of the under tread rubber, and the ratio of the hardness of the cap tread rubber to the storage elastic modulus of the under tread rubber. Even when stability and durability are reduced, the undertread rubber plays a role of complementing steering stability and durability, resulting in reduction of road noise and improvement of steering stability and durability, which are in a trade-off relationship. It became possible to achieve at the same time.
以下、本発明をさらに詳細に説明する。 Hereinafter, the present invention will be described in more detail.
（アンダートレッドゴム）
本発明の空気入りタイヤに用いられるアンダートレッドゴムは、タイヤ接地面を構成するキャップトレッドゴムのタイヤ径方向内側に配置される部材である。なおタイヤ径方向内側とはタイヤ径方向（空気入りタイヤの回転軸と直交する方向）において回転軸に近い側をいう。
(Under tread rubber)
The undertread rubber used in the pneumatic tire of the present invention is a member arranged inside the cap tread rubber constituting the tire contact patch in the tire radial direction. The inside in the tire radial direction means the side close to the rotation axis in the tire radial direction (direction orthogonal to the rotation axis of the pneumatic tire).
本発明において、アンダートレッドゴムの厚みは、キャップトレッドゴムの厚み（最大厚み；アンダートレッドとの接触面からタイヤ径方向におけるタイヤ表面までの最大長さ）の５％以上であることが必要である。アンダートレッドゴムの前記厚みが５％未満であると、ロードノイズの低減と操縦安定性および耐久性の向上とを同時に達成することができない。
キャップトレッドゴムの厚みに対するアンダートレッドゴムの厚みは、７〜２０％が好ましく、１０〜１５％がさらに好ましい。
In the present invention, the thickness of the under tread rubber needs to be 5% or more of the thickness of the cap tread rubber (maximum thickness; maximum length from the contact surface with the under tread to the tire surface in the tire radial direction). .. If the thickness of the undertread rubber is less than 5%, reduction of road noise and improvement of steering stability and durability cannot be achieved at the same time.
The thickness of the under tread rubber with respect to the thickness of the cap tread rubber is preferably 7 to 20%, more preferably 10 to 15%.
アンダートレッドゴムの厚みは、０.５ｍｍ〜５ｍｍであることが好ましい。
キャップトレッドゴムの厚みは、５ｍｍ〜１５ｍｍが好ましい。
The thickness of the under tread rubber is preferably 0.5 mm to 5 mm.
The thickness of the cap tread rubber is preferably 5 mm to 15 mm.
本発明では、アンダートレッドゴムの組成が特定される。すなわち、アンダートレッドゴムは、ジエン系ゴム１００質量部に対し、天然ゴム（ＮＲ）を４０質量部以上、カーボンブラックを４０質量部以上、およびシリカを２０質量部以下配合してなる。 In the present invention, the composition of the under tread rubber is specified. That is, the undertread rubber is made by blending 40 parts by mass or more of natural rubber (NR), 40 parts by mass or more of carbon black, and 20 parts by mass or less of silica with respect to 100 parts by mass of diene rubber.
前記ＮＲの配合割合が４０質量部未満である場合、前記カーボンブラックの配合割合が４０質量部未満である場合、および／または、シリカの配合割合が２０質量部を超える場合は、ロードノイズの低減と操縦安定性および耐久性の向上を同時に達成することができない。 Reduction of road noise when the blending ratio of the NR is less than 40 parts by mass, when the blending ratio of the carbon black is less than 40 parts by mass, and / or when the blending ratio of silica exceeds 20 parts by mass. And the improvement of steering stability and durability cannot be achieved at the same time.
ここで、本発明の効果向上の観点から、下記の形態が好ましい。
（１）前記ジエン系ゴム１００質量部に対し、前記ＮＲの配合割合は４０〜６０質量部が好ましい。
（２）前記ジエン系ゴム１００質量部に対し、前記カーボンブラックの配合割合は４０〜８０質量部が好ましい。
（３）前記カーボンブラックの窒素吸着比表面積（Ｎ２ＳＡ）は２５〜１２０ｍ２／ｇが好ましく、５０〜１２０ｍ２／ｇがさらに好ましい。
（４）前記ジエン系ゴム１００質量部に対し、前記シリカの配合割合は０〜１５質量部が好ましい。すなわち、本発明におけるアンダートレッドゴムは、シリカを含まなくてもよい。
なお本発明でいうＮＲは、合成イソプレンゴム（ＩＲ）を含むものとする。また窒素吸着比表面積（Ｎ２ＳＡ）は、ＪＩＳ Ｋ ６２１７−２：２００１「第２部：比表面積の求め方−窒素吸着法−単点法」にしたがって測定した値である。
Here, from the viewpoint of improving the effect of the present invention, the following form is preferable.
(1) The blending ratio of the NR is preferably 40 to 60 parts by mass with respect to 100 parts by mass of the diene rubber.
(2) The blending ratio of the carbon black is preferably 40 to 80 parts by mass with respect to 100 parts by mass of the diene rubber.
(3) said carbon black nitrogen adsorption specific surface area (N 2 SA) is preferably 25~120m 2 / g, more preferably 50~120m 2 / g.
(4) The blending ratio of the silica is preferably 0 to 15 parts by mass with respect to 100 parts by mass of the diene rubber. That is, the under tread rubber in the present invention does not have to contain silica.
The NR referred to in the present invention includes synthetic isoprene rubber (IR). The nitrogen adsorption specific surface area (N 2 SA) is a value measured according to JIS K 6217-2: 2001 "Part 2: Method for obtaining specific surface area-Nitrogen adsorption method-Single point method".
本発明で使用されるジエン系ゴムは、ＮＲ以外のジエン系ゴムを必要に応じて併用することもできる。例えば、ブタジエンゴム（ＢＲ）、スチレン−ブタジエン共重合体ゴム（ＳＢＲ）、アクリロニトリル−ブタジエン共重合体ゴム（ＮＢＲ）、エチレン−プロピレン−ジエンターポリマー（ＥＰＤＭ）等を配合してもよい。本発明で使用されるジエン系ゴムは、その分子量やミクロ構造はとくに制限されず、アミン、アミド、シリル、アルコキシシリル、カルボキシル、ヒドロキシル基等で末端変性されていても、エポキシ化されていてもよい。 As the diene rubber used in the present invention, a diene rubber other than NR can be used in combination as needed. For example, butadiene rubber (BR), styrene-butadiene copolymer rubber (SBR), acrylonitrile-butadiene copolymer rubber (NBR), ethylene-propylene-dienter polymer (EPDM) and the like may be blended. The diene-based rubber used in the present invention is not particularly limited in its molecular weight and microstructure, and may be terminal-modified with amines, amides, silyls, alkoxysilyls, carboxyls, hydroxyl groups, etc., or epoxidized. Good.
本発明で使用するシリカは特に限定されず、例えばタイヤ用途でゴム組成物に配合されている従来公知の任意のシリカを用いることができる。
シリカの具体例としては、湿式シリカ、乾式シリカ、ヒュームドシリカ等が挙げられる。シリカは、１種のシリカを単独で用いても、２種以上のシリカを併用してもよい。
The silica used in the present invention is not particularly limited, and for example, any conventionally known silica blended in a rubber composition for tire applications can be used.
Specific examples of silica include wet silica, dry silica, fumed silica and the like. As the silica, one type of silica may be used alone, or two or more types of silica may be used in combination.
また、前記アンダートレッドゴムには、前記した成分に加えて、各種充填剤、カップリング剤、各種オイル、老化防止剤、可塑剤、酸化亜鉛などのアンダートレッドゴムに一般的に配合されている各種添加剤を配合することができる。また加硫の際は、公知の加硫又は架橋剤、加硫又は架橋促進剤を制限なく使用できる。これらの添加剤の配合量も、本発明の目的に反しない限り、従来の一般的な配合量とすることができる。 Further, in the undertread rubber, in addition to the above-mentioned components, various fillers, coupling agents, various oils, antiaging agents, plasticizers, zinc oxide and other undertread rubbers are generally blended. Additives can be added. In the case of vulcanization, known vulcanization or cross-linking agents, vulcanization or cross-linking accelerators can be used without limitation. The blending amount of these additives can also be a conventional general blending amount as long as it does not contradict the object of the present invention.
本発明において、キャップトレッドゴムの組成は、下記で説明する（Ｈｓ cap）／（Ｅ’ut）の関係を満たすことができれば、とくに制限されず、適宜選択することができる。
例えば、ジエン系ゴム、各種充填剤、カップリング剤、各種オイル、老化防止剤、可塑剤、酸化亜鉛などのキャップトレッドゴムに一般的に配合されている各種成分を配合することができる。また加硫の際は、公知の加硫又は架橋剤、加硫又は架橋促進剤を制限なく使用できる。これらの添加剤の配合量も、本発明の目的に反しない限り、従来の一般的な配合量とすることができる。
In the present invention, the composition of the cap tread rubber is not particularly limited and can be appropriately selected as long as the relationship of (Hs cap) / (E'ut) described below can be satisfied.
For example, various components generally blended in cap tread rubber such as diene rubber, various fillers, coupling agents, various oils, antiaging agents, plasticizers, and zinc oxide can be blended. In the case of vulcanization, known vulcanization or cross-linking agents, vulcanization or cross-linking accelerators can be used without limitation. The blending amount of these additives can also be a conventional general blending amount as long as it does not contradict the object of the present invention.
また、本発明の空気入りタイヤにおけるその他の部材、例えばカーカス、ビード部やサイドウォール部等を構成する部材についても、各成分の配合割合はとくに制限されず、適宜選択することができる。
例えばその他の部材のゴム組成物として、ジエン系ゴム、各種充填剤、各種オイル、老化防止剤、可塑剤、酸化亜鉛等の一般的に配合されている各種成分を配合することができる。また加硫の際は、公知の加硫又は架橋剤、加硫又は架橋促進剤を制限なく使用できる。これらの添加剤の配合量も、本発明の目的に反しない限り、従来の一般的な配合量とすることができる。
Further, with respect to other members in the pneumatic tire of the present invention, for example, members constituting a carcass, a bead portion, a sidewall portion, etc., the blending ratio of each component is not particularly limited and can be appropriately selected.
For example, as the rubber composition of other members, various commonly blended components such as diene-based rubber, various fillers, various oils, antioxidants, plasticizers, and zinc oxide can be blended. In the case of vulcanization, known vulcanization or cross-linking agents, vulcanization or cross-linking accelerators can be used without limitation. The blending amount of these additives can also be a conventional general blending amount as long as it does not contradict the object of the present invention.
本発明の空気入りタイヤは、前記キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）と、前記アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）とが、下記式を満たすことが必要である。 In the pneumatic tire of the present invention, the hardness (Hs cap) of the cap tread rubber at 20 ° C. and the storage elastic modulus (E'ut) of the under tread rubber at 20 ° C. must satisfy the following equations. is there.
３．５≦（Ｈｓ cap）／（Ｅ’ut）≦１８．０ 3.5 ≤ (Hs cap) / (E'ut) ≤ 18.0
すなわち、（Ｈｓ cap）／（Ｅ’ut）が３．５〜１８．０の範囲であることにより、上述のように、キャップトレッドゴムがロードノイズの改善を担い操縦安定性および耐久性を減じた場合でも、アンダートレッドゴムが操縦安定性および耐久性を補完する役割を果たし、結果として二律背反の関係にあるロードノイズの低減と操縦安定性および耐久性の向上とを同時に達成することが可能となる。 That is, since (Hs cap) / (E'ut) is in the range of 3.5 to 18.0, as described above, the cap tread rubber is responsible for improving road noise and reducing steering stability and durability. Even in this case, the undertread rubber plays a role of complementing the steering stability and durability, and as a result, it is possible to simultaneously achieve the reduction of road noise and the improvement of steering stability and durability, which are in a trade-off relationship. Become.
本発明で言う前記キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）は、ＪＩＳ Ｋ６２５３に準拠し、デュロメータのタイプＡにより温度２０℃で測定されたゴム硬度である。
また本発明で言う前記アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）は、ＪＩＳ Ｋ６３９４に準拠し、初期歪１０％、振幅±２％、周波数２０Ｈｚの条件下で、東洋精機製作所製粘弾性スペクトロメータにより２０℃で測定された貯蔵弾性率である。
The hardness (Hs cap) of the cap tread rubber in the present invention at 20 ° C. is the rubber hardness measured at a temperature of 20 ° C. by a durometer type A in accordance with JIS K6253.
The storage elastic modulus (E'ut) of the undertread rubber in the present invention at 20 ° C. is based on JIS K6394, and is manufactured by Toyo Seiki Seisakusho under the conditions of initial strain of 10%, amplitude of ± 2%, and frequency of 20 Hz. It is a storage elastic modulus measured at 20 ° C. by a viscoelastic spectrometer.
前記キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）の調整は、例えば可塑剤、充填剤、加硫剤または架橋剤の増減により可能である。
また、前記アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）の調整は、例えば可塑剤、充填剤、加硫剤または架橋剤の増減により可能である。
The hardness (Hs cap) of the cap tread rubber at 20 ° C. can be adjusted, for example, by increasing or decreasing the amount of plasticizer, filler, vulcanizing agent or cross-linking agent.
Further, the storage elastic modulus (E'ut) of the undertread rubber at 20 ° C. can be adjusted by, for example, increasing or decreasing a plasticizer, a filler, a vulcanizing agent or a cross-linking agent.
なお本発明の効果が一層向上するという観点から、前記（Ｈｓ cap）／（Ｅ’ut）は、５〜１８であることが好ましく、８〜１８であることがさらに好ましい。 From the viewpoint of further improving the effect of the present invention, the (Hs cap) / (E'ut) is preferably 5 to 18, and more preferably 8 to 18.
また本発明の空気入りタイヤは、従来の空気入りタイヤの製造方法に従って製造が可能であり、例えば乗用車用途が好ましい。 Further, the pneumatic tire of the present invention can be manufactured according to a conventional method for manufacturing a pneumatic tire, and is preferably used for passenger cars, for example.
以下、本発明を実施例および比較例によりさらに説明するが、本発明は下記例に制限されるものではない。 Hereinafter, the present invention will be further described with reference to Examples and Comparative Examples, but the present invention is not limited to the following examples.
標準例、実施例１〜３および比較例１〜２
表１に示す配合（質量部）において、加硫促進剤と硫黄を除く成分を１．７リットルの密閉式バンバリーミキサーで５分間混練し、ゴムをミキサー外に放出して室温冷却した。次いで、該ゴムを同ミキサーに再度入れ、加硫促進剤および硫黄を加えてさらに混練し、各種アンダートレッドゴム組成物を得た。
Standard Examples, Examples 1-3 and Comparative Examples 1-2
In the formulation (parts by mass) shown in Table 1, the vulcanization accelerator and the components excluding sulfur were kneaded with a 1.7 liter sealed Banbury mixer for 5 minutes, and the rubber was discharged to the outside of the mixer and cooled to room temperature. Then, the rubber was put into the same mixer again, a vulcanization accelerator and sulfur were added, and the mixture was further kneaded to obtain various undertread rubber compositions.
次に、キャップトレッドゴムを常法にしたがい調製し、可塑剤の量を増減することにより、表１に示す各種硬度を有するキャップトレッドゴムを得た。 Next, the cap tread rubber was prepared according to a conventional method, and the amount of the plasticizer was increased or decreased to obtain a cap tread rubber having various hardnesses shown in Table 1.
キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）は、ＪＩＳ Ｋ６２５３に準拠し、デュロメータのタイプＡにより温度２０℃で測定した。
アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）は、ＪＩＳ Ｋ６３９４に準拠し、初期歪１０％、振幅±２％、周波数２０Ｈｚの条件下で、東洋精機製作所製粘弾性スペクトロメータにより２０℃で測定した。結果を表１に示す。
The hardness (Hs cap) of the cap tread rubber at 20 ° C. was measured at a temperature of 20 ° C. by a durometer type A in accordance with JIS K6253.
The storage elastic modulus (E'ut) of the undertread rubber at 20 ° C. is based on JIS K6394, and is 20 by a viscoelastic spectrometer manufactured by Toyo Seiki Seisakusho under the conditions of initial strain of 10%, amplitude of ± 2%, and frequency of 20 Hz. Measured at ° C. The results are shown in Table 1.
前記アンダートレッドゴムと、前記キャップトレッドゴムとを組み込み、タイヤサイズ２４５／４０Ｒ１８の各種空気入りタイヤを製造した。またアンダートレッドゴムおよびキャップトレッドゴム以外の各部材の条件は、各種空気入りタイヤ間で同一とした。なお各例におけるキャップトレッドゴムの厚みは８．５ｍｍ、アンダートレッドゴムの厚みは１ｍｍである。（ただし、比較例１におけるキャップトレッドゴムの厚みは２０ｍｍ、アンダートレッドゴムの厚みは０．８ｍｍである。） By incorporating the under tread rubber and the cap tread rubber, various pneumatic tires having a tire size of 245 / 40R18 were manufactured. The conditions for each member other than the under tread rubber and the cap tread rubber were the same among the various pneumatic tires. The thickness of the cap tread rubber in each example is 8.5 mm, and the thickness of the under tread rubber is 1 mm. (However, the thickness of the cap tread rubber in Comparative Example 1 is 20 mm, and the thickness of the under tread rubber is 0.8 mm.)
得られた各種空気入りタイヤについて、下記の評価を行った。結果を表１に示す。 The following evaluations were performed on the obtained various pneumatic tires. The results are shown in Table 1.
ロードノイズ：各試験タイヤをリムサイズ１８×８．５Ｊのホイールに組み付けて試験車両に装着し、空気圧２４０ｋＰａの条件にて、走行時のロードノイズについてテストドライバーによる官能評価を行った。評点は、３．０を満点（明確な改善を確認できる）とする相対評価とし、標準例を１．０点（改善を確認できない）とした。評点が高くなるほど、ロードノイズが小さいことを意味する。 Road noise: Each test tire was assembled on a wheel having a rim size of 18 × 8.5J and mounted on a test vehicle, and a sensory evaluation was performed by a test driver for road noise during running under the condition of an air pressure of 240 kPa. The score was a relative evaluation with a perfect score of 3.0 (a clear improvement could be confirmed) and a standard example of 1.0 (improvement could not be confirmed). The higher the score, the smaller the road noise.
操縦安定性：各試験タイヤをリムサイズ１８×８．５Ｊのホイールに組み付けて試験車両に装着し、空気圧２４０ｋＰａの条件にて、舗装路からなるテストコースにおいてテストドライバーによる官能評価を実施した。評点は、３．０を満点（明確な性能の改善を確認できる）とする相対評価とし、標準例を２．０点（性能変化なし）とした。評点が高くなるほど、操縦安定性に優れる。 Steering stability: Each test tire was assembled on a wheel having a rim size of 18 × 8.5J and mounted on a test vehicle, and a sensory evaluation was carried out by a test driver on a test course consisting of a paved road under the condition of an air pressure of 240 kPa. The score was a relative evaluation with a perfect score of 3.0 (a clear improvement in performance can be confirmed), and a standard example of 2.0 points (no change in performance). The higher the score, the better the steering stability.
耐久性：タイヤをリムサイズ１８×８．５のリムにリム組みし、空気圧２４０ｋＰａを充填し、荷重４５ｋＮを負荷し、速度４５ｋｍ／ｈで、直径１７０７ｍｍの回転ドラム上で走行させ、タイヤが故障するまでの走行距離を測定した。標準例の走行距離を１００として指数で示した。指数値が大きいほどタイヤ耐久性能が優れている。 Durability: The tire is assembled on a rim with a rim size of 18 x 8.5, filled with an air pressure of 240 kPa, loaded with a load of 45 kN, run on a rotating drum with a diameter of 1707 mm at a speed of 45 km / h, and the tire breaks down. The mileage to was measured. The mileage of the standard example is set as 100 and shown as an index. The larger the index value, the better the tire durability.
＊１：ＮＲ（ＴＳＲ２０）
＊２：ＢＲ（日本ゼオン（株）製Ｎｉｐｏｌ ＢＲ１２２０）
＊３：カーボンブラックＨＡＦ（新日化カーボン社製商品名ニテロン＃G、Ｎ２ＳＡ＝35ｍ２／ｇ）
＊４：カーボンブラックＩＳＡＦ（新日化カーボン社製商品名ニテロン＃１０N、Ｎ２ＳＡ＝40ｍ２／ｇ）
＊５：シリカ（EVONIK社製商品名Ultrasil VN3GR）
＊６：酸化亜鉛（正同化学工業（株）製酸化亜鉛３種）
＊７：老化防止剤（FLEXSYS社製SANTOFLEX 6PPD）
＊８：加硫促進剤（FLEXSYS社製SANTOCURE CBS）
＊９：硫黄（四国化成工業（株）製ミュークロンＯＴ−２０）
* 1: NR (TSR20)
* 2: BR (Nippon Zeon Corporation Nipol BR1220)
* 3: Carbon black HAF (trade name Niteron # G, N 2 SA = 35m 2 / g manufactured by Shin Nikka Carbon Co., Ltd.)
* 4: Carbon black ISAF (trade name Niteron # 10N, N 2 SA = 40m 2 / g manufactured by Shin Nikka Carbon Co., Ltd.)
* 5: Silica (trade name Ultrasil VN3GR manufactured by EVONIK)
* 6: Zinc oxide (3 types of zinc oxide manufactured by Shodo Chemical Industry Co., Ltd.)
* 7: Anti-aging agent (SANTOFLEX 6PPD manufactured by FLEXSYS)
* 8: Vulcanization accelerator (SANTOCURE CBS manufactured by FLEXSYS)
* 9: Sulfur (Muclon OT-20 manufactured by Shikoku Chemicals Corporation)
上記の表１から明らかなように、実施例１〜３で調製された空気入りタイヤは、アンダートレッドゴムの厚み、アンダートレッドゴムの組成、およびキャップトレッドゴムの硬度とアンダートレッドゴムの貯蔵弾性率の比を特定化したので、標準例に比べ、ロードノイズの低減、操縦安定性および耐久性の向上が認められた。
比較例１は、アンダートレッドゴムの厚みが本発明で規定する下限未満であるので、標準例に比べ、操縦安定性および耐久性が悪化した。
比較例２は、（Ｈｓ cap）／（Ｅ’ut）が本発明で規定する下限未満であるので、耐久性が悪化した。
As is clear from Table 1 above, the pneumatic tires prepared in Examples 1 to 3 have the thickness of the undertread rubber, the composition of the undertread rubber, and the hardness of the cap tread rubber and the storage elastic modulus of the undertread rubber. Since the ratio of tire tread was specified, reduction of road noise, improvement of steering stability and durability were recognized as compared with the standard example.
In Comparative Example 1, since the thickness of the undertread rubber was less than the lower limit specified in the present invention, steering stability and durability were deteriorated as compared with the standard example.
In Comparative Example 2, since (Hs cap) / (E'ut) was less than the lower limit specified in the present invention, the durability was deteriorated.
Claims (3)
前記アンダートレッドゴムの厚みが前記キャップトレッドゴムの厚みの５％以上であり、
前記アンダートレッドゴムは、ジエン系ゴム１００質量部に対し、天然ゴムを４０質量部以上、カーボンブラックを４０質量部以上、およびシリカを２０質量部以下配合してなり、かつ
前記キャップトレッドゴムの２０℃における硬度（Ｈｓ cap）と、前記アンダートレッドゴムの２０℃における貯蔵弾性率（Ｅ’ut）とが、下記式を満たす
ことを特徴とする空気入りタイヤ。
３．５≦（Ｈｓ cap）／（Ｅ’ut）≦１８．０ In a pneumatic tire including a cap tread rubber and an under tread rubber arranged inside the cap tread rubber in the tire radial direction.
The thickness of the under tread rubber is 5% or more of the thickness of the cap tread rubber.
The undertread rubber is made by blending 40 parts by mass or more of natural rubber, 40 parts by mass or more of carbon black, and 20 parts by mass or less of silica with 100 parts by mass of diene rubber, and 20 parts by mass of the cap tread rubber. A pneumatic tire characterized in that the hardness (Hs cap) at ° C. and the storage elastic modulus (E'ut) of the undertread rubber at 20 ° C. satisfy the following formula.
3.5 ≤ (Hs cap) / (E'ut) ≤ 18.0