JP2020111663A - Aqueous solid coating and stick coating - Google Patents
Aqueous solid coating and stick coating Download PDFInfo
- Publication number
- JP2020111663A JP2020111663A JP2019003052A JP2019003052A JP2020111663A JP 2020111663 A JP2020111663 A JP 2020111663A JP 2019003052 A JP2019003052 A JP 2019003052A JP 2019003052 A JP2019003052 A JP 2019003052A JP 2020111663 A JP2020111663 A JP 2020111663A
- Authority
- JP
- Japan
- Prior art keywords
- water
- case
- based solid
- paint
- coating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、水性固形塗料及び水性固形塗料を備えるスティック型塗料に関する。 The present invention relates to a water-based solid paint and a stick-type paint including the water-based solid paint.
例えば建材などの木材の表面には、表面の保護や意匠性の向上を目的として、塗装が施されている。
例えば特許文献１には、建材の切断面や欠損面などに現れる未塗装面の塗装を行うための液状の水性塗料が開示されている。同文献１に記載の水性塗料によれば、含有される樹脂によって、未塗装面に耐水性の塗膜が形成される。
For example, the surface of wood such as building materials is coated for the purpose of protecting the surface and improving the design.
For example, Patent Document 1 discloses a liquid water-based coating material for coating an unpainted surface that appears on a cut surface or a defective surface of a building material. According to the water-based paint described in the document 1, the resin contained forms a water-resistant coating film on the unpainted surface.
ところで、特許文献１に記載の水性塗料を用いて塗装作業を行う場合には、作業者は容器内の水性塗料に刷毛やローラなどの塗装具を浸し、塗装具に水性塗料を予め染み込ませておく必要があることから、塗布作業が煩雑となる。 By the way, when performing a painting operation using the water-based paint described in Patent Document 1, an operator dips a paint tool such as a brush or a roller into the water-based paint in the container and pre-immerses the water-based paint in the paint tool. Since it is necessary to keep it, the coating work becomes complicated.
特に、垂直な未塗装面の塗装を行う場合や厚みのある塗装を行う場合には、液状の水性塗料が垂れ易い。このため、塗装具に少しずつ水性塗料を染み込ませてから塗る作業を繰り返す必要があるため、作業時間が増大するという問題がある。 In particular, when a vertical unpainted surface is applied or when a thick coating is applied, the liquid water-based paint is likely to drip. For this reason, it is necessary to gradually soak the coating material with the water-based paint and then to apply the water-based coating material.
本発明は、このような実情に鑑みてなされたものであって、その目的は、液垂れを抑制しつつ塗装作業を容易に行うことができる水性固形塗料及びスティック型塗料を提供することにある。 The present invention has been made in view of such circumstances, and an object thereof is to provide a water-based solid paint and a stick-type paint that can easily perform painting work while suppressing dripping. ..
上記目的を達成するための、水性固形塗料は、主成分として、水、常温反応硬化型の樹脂、及び凝固剤を含有し、スティック状に成形されてなる。
同構成によれば、水性固形塗料がスティック状をなしているため、作業者は、水性固形塗料をペンのように把持しながら塗装を行うことができる。そして、塗り延ばされた水性固形塗料から水分が蒸発することにより、樹脂を含む塗膜が形成される。特に、水性固形塗料が水及び常温反応硬化型の樹脂を含有していることにより、水性固形塗料を滑らかに塗り延ばすことができる。また、塗料が固形であるため、液垂れを抑制することができる。したがって、液垂れを抑制しつつ塗装作業を容易に行うことができる。
The water-based solid coating material for achieving the above object contains water, a room temperature reaction-curable resin, and a coagulant as main components, and is formed into a stick shape.
According to this configuration, since the water-based solid coating material has a stick shape, the worker can perform coating while gripping the water-based solid coating material like a pen. Then, by evaporating the water from the spread aqueous solid paint, a coating film containing a resin is formed. In particular, since the water-based solid paint contains water and a room temperature reaction-curable resin, the water-based solid paint can be spread smoothly. Moreover, since the coating material is solid, it is possible to suppress liquid dripping. Therefore, the coating work can be easily performed while suppressing the liquid dripping.
上記水性固形塗料において、前記水の含有割合は３０〜５０質量％である。
水性固形塗料に含有される水の割合が３０質量％よりも低い場合には、水性固形塗料を塗り延ばす際の円滑性が確保されにくい。一方、水性固形塗料に含有される水の割合が５０質量％よりも高い場合には、水性固形塗料の形状保持性が確保されにくい。
In the above water-based solid coating material, the water content is 30 to 50 mass %.
When the proportion of water contained in the water-based solid paint is lower than 30% by mass, it is difficult to secure smoothness when the water-based solid paint is spread. On the other hand, when the proportion of water contained in the water-based solid paint is higher than 50% by mass, it is difficult to secure the shape retention of the water-based solid paint.
この点、上記構成によれば、水の含有割合が３０〜５０質量％であるため、水性固形塗料を塗り延ばす際の円滑性の確保及び水性固形塗料の形状保持性の確保の両立を図ることができる。 In this respect, according to the above configuration, since the content ratio of water is 30 to 50% by mass, it is possible to secure both smoothness in spreading the aqueous solid paint and shape retention of the aqueous solid paint. You can
上記目的を達成するための、スティック型塗料は、上記水性固形塗料と、一端に開口を有し、前記水性固形塗料を収容する筒状のケースと、前記ケースに対して着脱可能に設けられ、前記ケースの前記開口を塞ぐキャップと、前記ケースに設けられ、前記ケースの前記開口を通じて前記水性固形塗料を進退させる進退機構と、を備える。 In order to achieve the above object, the stick-type paint, the water-based solid paint, having an opening at one end, a cylindrical case for accommodating the water-based solid paint, is provided detachably to the case, A cap is provided for closing the opening of the case, and an advancing/retreating mechanism provided in the case for advancing/retreating the aqueous solid paint through the opening of the case.
同構成によれば、作業者は塗装作業を行う際に、ケースからキャップを取り外し、進退機構を操作することでケースの開口から水性固形塗料を外部に進出させる。また、塗装作業を完了した後には、進退機構を操作することでケース内に水性固形塗料を退避させ、ケースにキャップを装着する。こうしたスティック型塗料によれば、作業者は、水性固形塗料を直接把持しなくて済む。また、水性固形塗料全体がケース及びキャップによって覆われることにより、水性固形塗料の乾燥を抑制できる。 According to this configuration, when performing the painting work, the worker removes the cap from the case and operates the advancing/retreating mechanism to allow the water-based solid paint to advance to the outside through the opening of the case. After the painting work is completed, the advancing/retreating mechanism is operated to retract the water-based solid paint in the case, and the cap is attached to the case. With such a stick-type paint, an operator does not have to directly grip the water-based solid paint. Further, since the entire water-based solid paint is covered with the case and the cap, it is possible to suppress the drying of the water-based solid paint.
本発明によれば、塗装作業を容易に行うことができる。 According to the present invention, the painting work can be easily performed.
以下、図１及び図２を参照して、スティック型塗料の一実施形態について説明する。
図１（ａ）及び図１（ｂ）に示すように、スティック型塗料１０は、スティック状の水性固形塗料２０と、一端に開口３２を有し、水性固形塗料２０を収容する筒状のケース３０と、ケース３０に対して着脱可能に設けられ、ケース３０の開口３２を塞ぐキャップ４０とを備えている。
An embodiment of a stick-type paint will be described below with reference to FIGS. 1 and 2.
As shown in FIGS. 1A and 1B, the stick-type paint 10 includes a stick-shaped water-based solid paint 20 and a cylindrical case having an opening 32 at one end and containing the water-based solid paint 20. 30 and a cap 40 that is detachably attached to the case 30 and closes the opening 32 of the case 30.
水性固形塗料２０は、主成分として、水、常温反応硬化型の樹脂、及び凝固剤を含有しており、スティック状（本実施形態では、円柱状）に成形されている。
ケース３０は、円筒状のケース本体３１を有している。ケース本体３１は、軸線方向の両端に開口３２，３３を有している。
The water-based solid coating material 20 contains water, a room temperature reaction-curable resin, and a coagulant as main components, and is formed in a stick shape (a cylindrical shape in the present embodiment).
The case 30 has a cylindrical case body 31. The case body 31 has openings 32 and 33 at both ends in the axial direction.
ケース本体３１の一方の端部外周面は、ケース本体３１の他の部分よりも縮径されている。この端部外周面には、上記キャップ４０の内周面に係止される円環状の係止突部３４が設けられている。 The outer peripheral surface of one end of the case body 31 has a smaller diameter than the other part of the case body 31. On the outer peripheral surface of the end portion, an annular locking protrusion 34 that is locked to the inner peripheral surface of the cap 40 is provided.
ケース本体３１の内周面には、複数（本実施形態では３つ）の案内突条３５が軸線方向に沿って延設されている。
ケース本体３１の他方の開口３３には、同開口３３を塞ぐとともに、ケース本体３１に対して回動可能な略円板状の回動体３６が設けられている。回動体３６には、同回動体３６の中心からケース本体３１内の軸線方向に沿って延在するとともに外周面に雄ねじが形成された螺軸３７が固定されている。螺軸３７には、略円板状の内皿３８が螺合されている。内皿３８の外径は、ケース本体３１の内径よりも僅かに小さい。内皿３８の外周面には、軸線方向に沿って延在するとともにケース本体３１の複数の案内突条３５にそれぞれ係合する複数（本実施形態では３つ）の案内溝３９が形成されている。
On the inner peripheral surface of the case body 31, a plurality of (three in the present embodiment) guide ridges 35 extend along the axial direction.
The other opening 33 of the case body 31 is provided with a substantially disk-shaped rotating body 36 that closes the opening 33 and is rotatable with respect to the case body 31. A screw shaft 37, which extends from the center of the rotating body 36 along the axial direction in the case body 31 and has a male screw formed on the outer peripheral surface, is fixed to the rotating body 36. A substantially disc-shaped inner plate 38 is screwed onto the screw shaft 37. The outer diameter of the inner tray 38 is slightly smaller than the inner diameter of the case body 31. On the outer peripheral surface of the inner tray 38, a plurality of (three in the present embodiment) guide grooves 39 that extend along the axial direction and engage with the plurality of guide protrusions 35 of the case body 31 are formed. There is.
上記水性固形塗料２０の中心には、螺軸３７が螺入されている。また、水性固形塗料２０の基端は、内皿３８に支持されている。
ケース本体３１、回動体３６、螺軸３７、及び内皿３８は、いずれも硬質樹脂材料により形成されている。
A screw shaft 37 is screwed into the center of the water-based solid paint 20. The base end of the water-based solid paint 20 is supported by the inner dish 38.
The case body 31, the rotating body 36, the screw shaft 37, and the inner tray 38 are all made of a hard resin material.
キャップ４０は、片側有底円筒状をなしており、ケース本体３１などと同様の硬質樹脂材料により形成されている。
こうした構成を有するスティック型塗料１０によれば、内皿３８の各案内溝３９とケース本体３１の各案内突条３５とが係合しており、螺軸３７と内皿３８とが螺合している。このため、回動体３６によって螺軸３７を一方向（回動体３６からケース本体３１を見たときの時計回り方向）に回転させると、内皿３８及び内皿３８に支持された水性固形塗料２０が回転することなくケース３０の開口３２に向かって移動する。
The cap 40 has a cylindrical shape with a bottom on one side, and is made of the same hard resin material as the case body 31 and the like.
According to the stick-type paint 10 having such a configuration, the guide grooves 39 of the inner tray 38 and the guide protrusions 35 of the case body 31 are engaged with each other, and the screw shaft 37 and the inner tray 38 are screwed together. ing. Therefore, when the screw shaft 37 is rotated in one direction (clockwise direction when the case body 31 is viewed from the rotating body 36) by the rotating body 36, the inner dish 38 and the water-based solid paint 20 supported by the inner dish 38 are rotated. Moves toward the opening 32 of the case 30 without rotating.
一方、回動体３６によって螺軸３７を上記一方向とは逆方向（回動体３６からケース本体３１を見たときの反時計回り方向）に回転させると、内皿３８及び内皿３８に支持された水性固形塗料２０が回転することなくケース３０の底部である回動体３６に向かって移動する。このようにして内皿３８を昇降させることによって、ケース３０の開口３２を通じて水性固形塗料２０が進退される。したがって、案内突条３５を有するケース本体３１、回動体３６、螺軸３７、及び案内溝３９を有する内皿３８によって、本発明に係る進退機構が構成されている。 On the other hand, when the screw shaft 37 is rotated by the rotating body 36 in a direction opposite to the one direction (counterclockwise direction when the case body 31 is viewed from the rotating body 36), the screw shaft 37 is supported by the inner plate 38 and the inner plate 38. The water-based solid paint 20 moves toward the rotating body 36 which is the bottom of the case 30 without rotating. By raising and lowering the inner tray 38 in this manner, the water-based solid paint 20 is advanced and retracted through the opening 32 of the case 30. Therefore, the case main body 31 having the guide ridge 35, the rotating body 36, the screw shaft 37, and the inner tray 38 having the guide groove 39 configure the advancing/retreating mechanism according to the present invention.
次に、水性固形塗料２０の製造方法について説明する。
まず、常温反応硬化型の樹脂を３０〜４０質量％含有する樹脂水溶液Ａに対して着色剤Ｂを投入し、これを攪拌する。この攪拌されたものに対して凝固剤Ｃを投入し、これを攪拌する。続いて、加温を行った後、冷却固化するとともにスティック状に成形することにより、水性固形塗料２０が製造される。
Next, a method for manufacturing the water-based solid coating material 20 will be described.
First, the colorant B is added to the resin aqueous solution A containing 30 to 40% by mass of a room temperature reaction-curable resin, and this is stirred. The coagulant C is added to this agitated material, and this is agitated. Subsequently, after heating, the water-based solid coating material 20 is manufactured by cooling and solidifying and molding into a stick shape.
ここで、樹脂水溶液Ａは、水性固形塗料２０全体に対して６０〜９５質量％の割合で配合されている。この樹脂水溶液Ａには、架橋剤としてカルボジイミドが含有されている。樹脂水溶液Ａに含有される常温反応硬化型の樹脂は、塗り延ばされた水性固形塗料２０に含まれる水分が蒸発して架橋剤との硬化反応（架橋反応）が進行することにより、上記樹脂を含む塗膜を形成する。本実施形態では、こうした常温反応硬化型の樹脂として、アクリルシリコン樹脂及びポリビニル系樹脂の混合物を用いている。 Here, the resin aqueous solution A is blended in a proportion of 60 to 95 mass% with respect to the entire aqueous solid coating material 20. The resin aqueous solution A contains carbodiimide as a crosslinking agent. The room-temperature reaction-curable resin contained in the resin aqueous solution A has the above-mentioned resin as the water contained in the spread aqueous solid coating material 20 evaporates and the curing reaction (crosslinking reaction) with the crosslinking agent proceeds. To form a coating film containing. In this embodiment, a mixture of acrylic silicone resin and polyvinyl resin is used as such a room temperature reaction-curable resin.
着色剤Ｂは、水性固形塗料２０全体に対して０〜２０質量％の割合で配合されている。すなわち、水性固形塗料２０において、着色剤Ｂは必須の構成ではなく、着色剤Ｂが含有されていないものであってもよい。本実施形態では、酸化チタンや、カーボンブラック、酸化鉄、シリカなどの周知の顔料を含有する着色剤Ｂを用いている。こうした顔料は、目的の色（白色、黄土色、ベージュ、または茶色）を着けるために適宜配合されている。 The colorant B is blended in a proportion of 0 to 20 mass% with respect to the entire aqueous solid coating material 20. That is, in the water-based solid coating material 20, the colorant B is not an essential component and may not contain the colorant B. In the present embodiment, the colorant B containing well-known pigments such as titanium oxide, carbon black, iron oxide and silica is used. Such pigments are appropriately blended in order to give a desired color (white, ocher, beige, or brown).
凝固剤Ｃは、水性固形塗料２０全体に対して５〜１０質量％の割合で配合することが好ましい。水性固形塗料２０に含有される凝固剤Ｃの割合が５％よりも低い場合には、水性固形塗料２０が柔らかくなって形状保持性が確保されにくくなるため、ケース３０からの出し入れが困難となる。一方、水性固形塗料２０に含有される凝固剤Ｃの割合が１０％よりも高い場合には、水性固形塗料２０が硬くなって水性固形塗料２０を塗り延ばす際の円滑性が確保されにくくなる。本実施形態では、主成分としてステアリン酸ナトリウムを含有する凝固剤Ｃを用いている。 The coagulant C is preferably blended in a proportion of 5 to 10 mass% with respect to the entire aqueous solid coating material 20. If the proportion of the coagulant C contained in the water-based solid coating material 20 is lower than 5%, the water-based solid coating material 20 becomes soft and it becomes difficult to secure the shape retention, so that it is difficult to take it in and out of the case 30. .. On the other hand, when the proportion of the coagulant C contained in the water-based solid coating material 20 is higher than 10%, the water-based solid coating material 20 becomes hard and it becomes difficult to secure smoothness when the water-based solid coating material 20 is spread. In this embodiment, the coagulant C containing sodium stearate as the main component is used.
水性固形塗料２０に含有される水の割合が３０質量％よりも低い場合には、水性固形塗料２０を塗り延ばす際の円滑性が確保されにくい。一方、水性固形塗料２０に含有される水の割合が５０質量％よりも高い場合には、水性固形塗料２０の形状保持性が確保されにくい。したがって、水性固形塗料２０における水の含有割合は、３０〜５０質量％であることが好ましい。 When the proportion of water contained in the aqueous solid coating material 20 is lower than 30% by mass, it is difficult to secure smoothness when the aqueous solid coating material 20 is spread. On the other hand, when the proportion of water contained in the aqueous solid coating material 20 is higher than 50% by mass, it is difficult to secure the shape retention of the aqueous solid coating material 20. Therefore, the content ratio of water in the water-based solid coating material 20 is preferably 30 to 50 mass %.
次に、本実施形態におけるスティック型塗料１０の作用について説明する。
図１（ａ）に示すように、作業者は塗装作業を行う際に、ケース３０からキャップ４０を取り外す。そして、回動体３６を一方向に回転させることで、図１（ｂ）に示すように、ケース３０の開口３２を通じて水性固形塗料２０が外部に進出する。
Next, the operation of the stick-type paint 10 in this embodiment will be described.
As shown in FIG. 1A, the worker removes the cap 40 from the case 30 when performing the painting work. Then, by rotating the rotating body 36 in one direction, as shown in FIG. 1B, the water-based solid coating material 20 advances to the outside through the opening 32 of the case 30.
水性固形塗料２０の使用時においては、図２に示すように、作業者は、ケース３０を介して水性固形塗料２０をペンのように把持しながら塗装作業を行う。
また、塗装作業を完了した後には、回動体３６を上記一方向とは逆方向に回転させることで、ケース３０内に水性固形塗料２０を退避させ、ケース３０にキャップ４０を装着する。
When the water-based solid paint 20 is used, as shown in FIG. 2, an operator performs the painting work while holding the water-based solid paint 20 like a pen through the case 30.
Further, after the painting work is completed, the rotary body 36 is rotated in the direction opposite to the one direction to evacuate the water-based solid paint 20 into the case 30, and the cap 40 is attached to the case 30.
次に、本実施形態の作用効果について説明する。
（１）水性固形塗料２０は、主成分として、水、常温反応硬化型の樹脂、及び凝固剤を含有し、スティック状に成形されてなる。
Next, the function and effect of this embodiment will be described.
(1) The water-based solid coating material 20 contains water, a room temperature reaction-curable resin, and a coagulant as main components, and is formed into a stick shape.
こうした構成によれば、水性固形塗料２０がスティック状をなしているため、作業者は、水性固形塗料２０をペンのように把持しながら塗装を行うことができる。そして、塗り延ばされた水性固形塗料２０から水分が蒸発することにより、樹脂を含む塗膜が形成される。特に、水性固形塗料２０が常温反応硬化型の樹脂を含有していることにより、水性固形塗料２０を滑らかに塗り延ばすことができる。また、塗料が固形であるため、液垂れを抑制することができる。したがって、液垂れを抑制しつつ塗装作業を容易に行うことができる。 With this configuration, since the water-based solid paint 20 is in the form of a stick, an operator can perform painting while gripping the water-based solid paint 20 like a pen. Then, the coating film containing the resin is formed by evaporating the water from the spread aqueous solid coating material 20. In particular, since the water-based solid coating material 20 contains a room temperature reaction curable resin, the water-based solid coating material 20 can be smoothly spread. Moreover, since the coating material is solid, it is possible to suppress liquid dripping. Therefore, the coating work can be easily performed while suppressing the liquid dripping.
（２）水性固形塗料２０の水の含有割合は３０〜５０質量％である。
水性固形塗料２０に含有される水の割合が３０質量％よりも低い場合には、水性固形塗料２０を塗り延ばす際の円滑性が確保されにくい。一方、水性固形塗料２０に含有される水の割合が５０質量％よりも高い場合には、水性固形塗料２０の形状保持性が確保されにくい。
(2) The water content of the water-based solid coating material 20 is 30 to 50 mass %.
When the proportion of water contained in the aqueous solid coating material 20 is lower than 30% by mass, it is difficult to secure smoothness when the aqueous solid coating material 20 is spread. On the other hand, when the proportion of water contained in the aqueous solid coating material 20 is higher than 50% by mass, it is difficult to secure the shape retention of the aqueous solid coating material 20.
この点、上記構成によれば、水の含有割合が３０〜５０質量％であるため、水性固形塗料２０を塗り延ばす際の円滑性の確保及び水性固形塗料２０の形状保持性の確保の両立を図ることができる。 In this respect, according to the above configuration, since the content ratio of water is 30 to 50% by mass, it is possible to ensure both smoothness in spreading the aqueous solid coating material 20 and securing the shape retention of the aqueous solid coating material 20. Can be planned.
（３）スティック型塗料１０は、水性固形塗料２０と、一端に開口３２を有し、水性固形塗料２０を収容する筒状のケース３０と、ケース３０に対して着脱可能に設けられ、ケース３０の開口３２を塞ぐキャップ４０と、ケース３０に設けられ、ケース３０の開口３２を通じて水性固形塗料２０を進退させる進退機構とを備える。 (3) The stick-type paint 10 is provided with the water-based solid paint 20, a cylindrical case 30 having an opening 32 at one end and housing the water-based solid paint 20, and detachably attached to the case 30. A cap 40 that closes the opening 32 of the above, and an advance/retreat mechanism that is provided in the case 30 and that advances and retracts the aqueous solid paint 20 through the opening 32 of the case 30.
こうした構成によれば、上記作用を奏することから、作業者は、水性固形塗料２０を直接把持しなくて済む。また、水性固形塗料２０全体がケース３０及びキャップ４０によって覆われることにより、水性固形塗料２０の乾燥を抑制できる。 According to such a configuration, since the above-described operation is achieved, the operator does not have to directly grip the water-based solid coating material 20. Further, since the entire water-based solid paint 20 is covered with the case 30 and the cap 40, it is possible to suppress the drying of the water-based solid paint 20.
＜変更例＞
上記実施形態は、例えば以下のように変更することもできる。上記実施形態及び以下の変更例は、技術的に矛盾しない範囲で互いに組み合わせて実施することができる。
<Example of change>
The above embodiment may be modified as follows, for example. The above-described embodiment and the following modified examples can be implemented in combination with each other within a technically consistent range.
・上記実施形態では、常温反応硬化型の樹脂の一例としてアクリルシリコン樹脂及びポリビニル系樹脂の混合物について例示したが、アクリルシリコン樹脂のみ、またはポリビニル系樹脂のみを用いるようにしてもよい。 In the above embodiment, a mixture of an acrylic silicone resin and a polyvinyl resin was illustrated as an example of the room temperature reaction-curable resin, but an acrylic silicone resin alone or a polyvinyl resin alone may be used.
・上記実施形態では、回動体３６の回動操作に伴って水性固形塗料２０を昇降させる進退機構について例示したが、進退機構の構成はこれに限定されない。例えば、ケースの側壁に軸線方向に沿って延在する操作孔を形成し、同操作孔を通じてケースの内外に挿通されたレバーの操作によって水性固形塗料を昇降させる構成であってもよい。 -In the said embodiment, although the advancing/retreating mechanism which raises/lowers the aqueous solid coating material 20 with rotation operation of the rotating body 36 was illustrated, the structure of an advancing/retreating mechanism is not limited to this. For example, a configuration may be adopted in which an operation hole extending in the axial direction is formed on the side wall of the case, and the water-based solid paint is moved up and down by operating a lever inserted through the operation hole into and out of the case.
・水性固形塗料の形状を四角柱状に変更することもできる。この場合、水性固形塗料の形状に合わせてケース及びキャップの形状を変更すればよい。
・水性固形塗料は、筒状のケースに収容されるスティック型のものに限定されず、水性固形塗料の外周面にテープが巻かれているものであってもよい。この場合、テープを適宜剥がしながら水性固形塗料を使用すればよい。また、水性固形塗料単体で使用することもできる。この場合であっても、上記実施形態の作用効果（１）に準じた作用効果を奏することができる。
-The shape of the water-based solid paint can also be changed to a square column. In this case, the shapes of the case and the cap may be changed according to the shape of the water-based solid paint.
The water-based solid paint is not limited to the stick type housed in a cylindrical case, and may be a tape wound around the outer peripheral surface of the water-based solid paint. In this case, the water-based solid paint may be used while the tape is peeled off as appropriate. It is also possible to use the aqueous solid paint alone. Even in this case, it is possible to achieve the operational effect according to the operational effect (1) of the above-described embodiment.
１０…スティック型塗料、２０…水性固形塗料、３０…ケース、３１…ケース本体、３２，３３…開口、３４…係止突部、３５…案内突条、３６…回動体、３７…螺軸、３８…内皿、３９…案内溝、４０…キャップ。 10... Stick type paint, 20... Water-based solid paint, 30... Case, 31... Case body, 32, 33... Opening, 34... Locking projection, 35... Guide ridge, 36... Rotating body, 37... Screw shaft, 38... inner plate, 39... guide groove, 40... cap.
Claims (3)
水性固形塗料。 As a main component, it contains water, a room temperature reaction curable resin, and a coagulant, and is molded into a stick shape,
Aqueous solid paint.
請求項１に記載の水性固形塗料。 The content ratio of the water is 30 to 50% by mass,
The water-based solid coating material according to claim 1.
一端に開口を有し、前記水性固形塗料を収容する筒状のケースと、
前記ケースに対して着脱可能に設けられ、前記ケースの前記開口を塞ぐキャップと、
前記ケースに設けられ、前記ケースの前記開口を通じて前記水性固形塗料を進退させる進退機構と、を備える、
スティック型塗料。 A water-based solid coating material according to claim 1 or 2,
A cylindrical case having an opening at one end and containing the water-based solid paint,
A cap that is detachably attached to the case and closes the opening of the case;
An advancing/retreating mechanism that is provided in the case and moves the water-based solid paint through the opening of the case.
Stick type paint.