JP2020035608A - Manufacturing method of positive electrode layer - Google Patents
Manufacturing method of positive electrode layer Download PDFInfo
- Publication number
- JP2020035608A JP2020035608A JP2018160434A JP2018160434A JP2020035608A JP 2020035608 A JP2020035608 A JP 2020035608A JP 2018160434 A JP2018160434 A JP 2018160434A JP 2018160434 A JP2018160434 A JP 2018160434A JP 2020035608 A JP2020035608 A JP 2020035608A
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- active material
- material particles
- electrode active
- lithium niobate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本開示は、正極層の製造方法に関する。 The present disclosure relates to a method for manufacturing a positive electrode layer.
近年におけるパソコン、ビデオカメラおよび携帯電話等の情報関連機器や通信機器等の急速な普及に伴い、その電源として利用される電池の開発が重要視されている。また、自動車産業界等においても、電気自動車用あるいはハイブリッド自動車用の高出力かつ高容量の電池の開発が進められている。
全固体電池の中でも全固体リチウムイオン電池は、リチウムイオンの移動を伴う電池反応を利用するためエネルギー密度が高いという点、また、正極と負極の間に介在する電解質として、有機溶媒を含む電解液に替えて固体電解質を用いるという点で注目されている。
With the rapid spread of information-related devices such as personal computers, video cameras, and mobile phones, and communication devices in recent years, the development of batteries used as power sources for them has been regarded as important. Also, in the automobile industry and the like, development of a high-output and high-capacity battery for an electric vehicle or a hybrid vehicle is being promoted.
Among all-solid-state batteries, all-solid-state lithium-ion batteries have a high energy density because they use a battery reaction involving the movement of lithium ions.In addition, an electrolyte containing an organic solvent as an electrolyte interposed between the positive electrode and the negative electrode Has attracted attention in that a solid electrolyte is used instead.
特許文献１には、活物質の表面に噴霧したニオブのペルオキソ錯体及びリチウムを含有する溶液を１２３℃〜３５０℃の温度で５時間加熱することにより、活物質とその表面の少なくとも一部に付着させたニオブ酸リチウムとを有する活物質複合粉体を得る技術が開示されている。 Patent Document 1 discloses that a solution containing a peroxo complex of niobium and lithium sprayed on the surface of an active material is heated at a temperature of 123 ° C. to 350 ° C. for 5 hours to adhere to the active material and at least a part of the surface thereof. There is disclosed a technique for obtaining an active material composite powder having lithium niobate.
特許文献２には、活物質の表面に付着させたリチウムイオン及びニオブイオンを含有するアルコキシド溶液を大気雰囲気中で１２０℃以上２００℃以下の温度で５時間加熱することにより、活物質粒子とその表面に付着させたニオブ酸リチウムを含む被覆層とを有する活物質粉体を得る技術が開示されている。 Patent Document 2 discloses that an alkoxide solution containing lithium ions and niobium ions attached to the surface of an active material is heated in an air atmosphere at a temperature of 120 ° C. or more and 200 ° C. or less for 5 hours to form active material particles and A technique for obtaining an active material powder having a coating layer containing lithium niobate attached to the surface is disclosed.
特許文献１〜２に開示の技術では、ニオブ酸リチウムの前駆体の加熱時間が５時間と長いことから、前駆体の加熱により生成した非晶質のニオブ酸リチウムの結晶化が進行し、当該ニオブ酸リチウムの結晶相が形成され、当該ニオブ酸リチウムのリチウムイオン伝導度が低くなってしまうという問題がある。
また、非晶質のニオブ酸リチウムの結晶化を抑制するために、ニオブ酸リチウムの前駆体の加熱温度を低くし過ぎると、ニオブ酸リチウムの水分含有量が増加し、当該ニオブ酸リチウムを全固体電池の材料に用いた場合、ニオブ酸リチウムに含まれる水分が硫化物系固体電解質と反応し、硫化物系固体電解質が変質し、電池の出力が低下するという問題がある。
本開示は、上記実情に鑑み、電池に用いたときに当該電池の出力を向上させることができる正極層の製造方法を提供することを目的とする。
In the techniques disclosed in Patent Literatures 1 and 2, since the heating time of the precursor of lithium niobate is as long as 5 hours, the crystallization of amorphous lithium niobate generated by heating the precursor progresses. There is a problem that a crystal phase of lithium niobate is formed and the lithium ion conductivity of the lithium niobate is lowered.
Further, if the heating temperature of the precursor of lithium niobate is too low in order to suppress the crystallization of amorphous lithium niobate, the water content of lithium niobate increases, and the lithium niobate is completely removed. When used as a material for a solid-state battery, there is a problem that moisture contained in lithium niobate reacts with the sulfide-based solid electrolyte, the sulfide-based solid electrolyte is altered, and the output of the battery is reduced.
In view of the above circumstances, an object of the present disclosure is to provide a method for manufacturing a positive electrode layer that can improve the output of a battery when used in the battery.
本開示は、正極活物質粒子と、当該正極活物質粒子の表面の少なくとも一部を被覆するニオブ酸リチウムを含む被覆層と、を有する複合活物質粒子を含有する正極層の製造方法であって、
前記正極活物質粒子に、ニオブイオンとリチウムイオンとを含有する溶液を噴霧し、当該正極活物質粒子の表面に当該溶液を付着させる工程と、
前記溶液を乾燥させ、前記正極活物質粒子の表面に前記ニオブ酸リチウムの前駆体を形成させる工程と、
前記前駆体を表面に付着させた前記正極活物質粒子を２００℃〜３００℃の温度で、１分以上６０分以下の時間、加熱することにより前記複合活物質粒子を得る工程を有することを特徴とする正極層の製造方法を提供する。
The present disclosure is a method for producing a positive electrode layer containing composite active material particles comprising: positive electrode active material particles; and a coating layer containing lithium niobate that covers at least a part of the surface of the positive electrode active material particles. ,
A step of spraying a solution containing niobium ions and lithium ions on the positive electrode active material particles, and attaching the solution to the surface of the positive electrode active material particles,
Drying the solution, forming a precursor of the lithium niobate on the surface of the positive electrode active material particles,
A step of heating the positive electrode active material particles having the precursor adhered to the surface thereof at a temperature of 200 ° C. to 300 ° C. for 1 minute to 60 minutes to obtain the composite active material particles. And a method for producing a positive electrode layer.
本開示は、電池に用いたときに当該電池の出力を向上させることができる正極層の製造方法を提供することができる。 The present disclosure can provide a method for manufacturing a positive electrode layer that can improve the output of a battery when used in the battery.
本開示は、正極活物質粒子と、当該正極活物質粒子の表面の少なくとも一部を被覆するニオブ酸リチウムを含む被覆層と、を有する複合活物質粒子を含有する正極層の製造方法であって、
前記正極活物質粒子に、ニオブイオンとリチウムイオンとを含有する溶液を噴霧し、当該正極活物質粒子の表面に当該溶液を付着させる工程と、
前記溶液を乾燥させ、前記正極活物質粒子の表面に前記ニオブ酸リチウムの前駆体を形成させる工程と、
前記前駆体を表面に付着させた前記正極活物質粒子を２００℃〜３００℃の温度で、１分以上６０分以下の時間、加熱することにより前記複合活物質粒子を得る工程を有することを特徴とする正極層の製造方法を提供する。
The present disclosure is a method for producing a positive electrode layer containing composite active material particles comprising: positive electrode active material particles; and a coating layer containing lithium niobate that covers at least a part of the surface of the positive electrode active material particles. ,
A step of spraying a solution containing niobium ions and lithium ions on the positive electrode active material particles, and attaching the solution to the surface of the positive electrode active material particles,
Drying the solution, forming a precursor of the lithium niobate on the surface of the positive electrode active material particles,
A step of heating the positive electrode active material particles having the precursor adhered to the surface thereof at a temperature of 200 ° C. to 300 ° C. for 1 minute to 60 minutes to obtain the composite active material particles. And a method for producing a positive electrode layer.
本研究者らは、所定の溶液を乾燥させて得たニオブ酸リチウムの前駆体を２００℃〜３００℃の温度で、１〜６０分、加熱することにより含有水分量の低いニオブ酸リチウムが得られることを見出した。そして、当該ニオブ酸リチウムを正極活物質粒子の表面に被覆して得た複合活物質粒子を正極層の材料として用いることにより、当該正極層を備える全固体電池の電池出力を向上させることができることを見出した。
本開示によれば、ニオブ酸リチウムの前駆体を６０分以下の時間加熱することにより、生成した非晶質のニオブ酸リチウムの結晶化の進行を抑制できる。結晶化したニオブ酸リチウムは、非晶質のニオブ酸リチウムと比較してリチウムイオン伝導度が低いことが知られている。そのため、本開示で用いるニオブ酸リチウムは、従来のニオブ酸リチウムと比較して、含有水分量が低く、且つ、リチウムイオン伝導度が高いと考えられる。そして、本開示で用いるニオブ酸リチウムを全固体電池の正極層の材料として用いることにより、電池の出力を向上することができると考えられる。
また、本開示によれば、ニオブ酸リチウムが、従来の５時間よりも短時間（１０分以下）のニオブ酸リチウムの前駆体の加熱により得られるため、製造コストを低減することができる。
The present researchers have obtained a lithium niobate precursor obtained by drying a predetermined solution at a temperature of 200 ° C to 300 ° C for 1 to 60 minutes to obtain lithium niobate having a low water content. Was found to be. Then, by using the composite active material particles obtained by coating the surface of the positive electrode active material particles with the lithium niobate as the material of the positive electrode layer, it is possible to improve the battery output of an all-solid battery including the positive electrode layer. Was found.
According to the present disclosure, the progress of crystallization of the generated amorphous lithium niobate can be suppressed by heating the precursor of lithium niobate for 60 minutes or less. It is known that crystallized lithium niobate has a lower lithium ion conductivity than amorphous lithium niobate. Therefore, lithium niobate used in the present disclosure is considered to have a lower water content and a higher lithium ion conductivity than conventional lithium niobate. And it is considered that the output of the battery can be improved by using lithium niobate used in the present disclosure as a material of the positive electrode layer of the all-solid battery.
Further, according to the present disclosure, lithium niobate can be obtained by heating a precursor of lithium niobate in a shorter time (10 minutes or less) than in the conventional 5 hours, so that the production cost can be reduced.
本開示の正極層の製造方法は、少なくとも（ａ）溶液の噴霧工程と、（ｂ）溶液の乾燥工程と、（ｃ）加熱工程を有する。
以下、各工程について順に説明する。
The method for producing a positive electrode layer according to the present disclosure includes at least (a) a solution spraying step, (b) a solution drying step, and (c) a heating step.
Hereinafter, each step will be described in order.
（ａ）溶液の噴霧工程
噴霧工程は、前記正極活物質粒子に、ニオブイオンとリチウムイオンとを含有する溶液を噴霧し、当該正極活物質粒子の表面に当該溶液を付着させる工程である。
ニオブイオンとリチウムイオンとを含有する溶液としては、ニオブのペルオキソ錯体とリチウムイオンとを含有する錯体溶液（以下、錯体溶液と称する場合がある）、ニオブイオンとリチウムイオンとを含有するアルコキシド溶液（以下、アルコキシド溶液と称する場合がある）等が挙げられ、製造コストを低減する観点から、錯体溶液が好ましい。なお、本開示においてニオブイオンは、錯イオンの状態であってもよい。
図１に、ニオブのペルオキソ錯体（［Ｎｂ（Ｏ２）４］３−）の構造式を示す。
錯体溶液は、例えば、過酸化水素水、ニオブ酸、及び、アンモニア水を用いることにより透明溶液を作製した後、作製した透明溶液にリチウム化合物を添加することによって得られる水溶液等を挙げることができる。錯体溶液中のニオブ酸の含水率が変わっても、ニオブのペルオキソ錯体は合成可能なため、ニオブ酸の含水率は特に限定されない。ニオブのペルオキソ錯体を合成可能であれば、ニオブ酸及びアンモニア水の混合比率は特に限定されない。また、リチウム化合物としては、ＬｉＯＨ、ＬｉＮＯ３、Ｌｉ２ＳＯ４等を例示することができる。
アルコキシド溶液は、例えば、エトキシリチウム粉末を脱水エタノールに溶解させた後、これを攪拌しながら、モル比でリチウム：ニオブ＝１：１となる量のペンタエトキシニオブを加えることにより作製することができる。アルコキシド溶液に用いる溶媒としては、脱水エタノール、脱水プロパノール、脱水ブタノール等を例示することができる。アルコキシド溶液に含まれているリチウムイオンとニオブイオンとのモル比は、特に限定されないが、例えば、１：１であってもよい。
(A) Spraying Step of Solution The spraying step is a step of spraying a solution containing niobium ions and lithium ions on the positive electrode active material particles, and attaching the solution to the surfaces of the positive electrode active material particles.
Examples of the solution containing niobium ions and lithium ions include a complex solution containing a peroxo complex of niobium and lithium ions (hereinafter sometimes referred to as a complex solution) and an alkoxide solution containing niobium ions and lithium ions ( Hereinafter, the complex solution may be referred to as an alkoxide solution). From the viewpoint of reducing the production cost, a complex solution is preferable. In the present disclosure, niobium ions may be in a complex ion state.
FIG. 1 shows a structural formula of a peroxo complex of niobium ([Nb (O 2 ) 4 ] 3− ).
The complex solution includes, for example, an aqueous solution obtained by preparing a transparent solution by using aqueous hydrogen peroxide, niobic acid, and aqueous ammonia, and then adding a lithium compound to the prepared transparent solution. . Even if the water content of niobic acid in the complex solution changes, the water content of niobic acid is not particularly limited because a peroxo complex of niobium can be synthesized. The mixing ratio of niobic acid and aqueous ammonia is not particularly limited as long as a peroxo complex of niobium can be synthesized. Examples of the lithium compound include LiOH, LiNO 3 , and Li 2 SO 4 .
The alkoxide solution can be produced, for example, by dissolving ethoxylithium powder in dehydrated ethanol, and then adding pentaethoxyniobium in a molar ratio of lithium: niobium = 1: 1 with stirring. . Examples of the solvent used for the alkoxide solution include dehydrated ethanol, dehydrated propanol, and dehydrated butanol. The molar ratio between lithium ions and niobium ions contained in the alkoxide solution is not particularly limited, but may be, for example, 1: 1.
正極活物質としては、特に制限はなく、例えば、ＬｉＣｏＯ２、ＬｉＮｉｘＣｏ１−ｘＯ２（０＜ｘ＜１）、ＬｉＮｉ１／３Ｃｏ１／３Ｍｎ１／３Ｏ２、ＬｉＭｎＯ２、異種元素置換Ｌｉ−Ｍｎスピネル（ＬｉＭｎ１．５Ｎｉ０．５Ｏ４、ＬｉＭｎ１．５Ａｌ０．５Ｏ４、ＬｉＭｎ１．５Ｍｇ０．５Ｏ４、ＬｉＭｎ１．５Ｃｏ０．５Ｏ４、ＬｉＭｎ１．５Ｆｅ０．５Ｏ４、ＬｉＭｎ１．５Ｚｎ０．５Ｏ４）、チタン酸リチウム（例えばＬｉ４Ｔｉ５Ｏ１２）、リン酸金属リチウム（ＬｉＦｅＰＯ４、ＬｉＭｎＰＯ４、ＬｉＣｏＰＯ４、ＬｉＮｉＰＯ４）、遷移金属酸化物（Ｖ２Ｏ５、ＭｏＯ３）、ＴｉＳ２、ＬｉＣｏＮ、Ｓｉ、ＳｉＯ２、Ｌｉ２ＳｉＯ３、Ｌｉ４ＳｉＯ４、リチウム貯蔵性金属間化合物（例えばＭｇ２Ｓｎ、Ｍｇ２Ｇｅ、Ｍｇ２Ｓｂ、Ｃｕ３Ｓｂ）等を挙げることができる。
正極活物質の粒子の平均粒径（Ｄ５０）は、例えば１ｎｍ以上１００μｍ以下であることが好ましく、１０ｎｍ以上３０μｍ以下であることがより好ましい。
There is no particular limitation on the positive electrode active material. For example, LiCoO 2 , LiNi x Co 1-x O 2 (0 <x <1), LiNi 1/3 Co 1/3 Mn 1/3 O 2 , LiMnO 2 , Li-Mn spinel (LiMn 1.5 Ni 0.5 O 4 , LiMn 1.5 Al 0.5 O 4 , LiMn 1.5 Mg 0.5 O 4 , LiMn 1.5 Co 0.5 O 4, LiMn 1.5 Fe 0.5 O 4 , LiMn 1.5 Zn 0.5 O 4), lithium titanate (for example, Li 4 Ti 5 O 12), phosphoric acid metal lithium (LiFePO 4, LiMnPO 4, LiCoPO 4, LiNiPO 4), transition metal oxide (V 2 O 5, MoO 3 ), TiS 2, LiCoN, Si, SiO 2, Li 2
The average particle diameter (D 50 ) of the particles of the positive electrode active material is, for example, preferably from 1 nm to 100 μm, and more preferably from 10 nm to 30 μm.
（ｂ）溶液の乾燥工程
乾燥工程は、前記溶液を乾燥させ、前記正極活物質粒子の表面に前記ニオブ酸リチウムの前駆体を形成させる工程である。
乾燥工程により、正極活物質粒子の表面に付着させた溶液に含まれている、溶媒や水和水等の揮発成分を除去する。溶液は、乾燥後、ニオブ酸リチウムの前駆体となる。ニオブ酸リチウムの前駆体は、ニオブ酸リチウムの原料の混合物であってもよい。
ここで、溶液として、上記錯体溶液を用いた場合、錯体溶液に含まれている過酸化水素は、強力な酸化作用を有している。それゆえ、長時間に亘って錯体溶液を正極活物質粒子に接触させると、過酸化水素によって正極活物質粒子が浸食される虞があり、浸食された正極活物質粒子は劣化する。そこで、正極活物質粒子の劣化を抑制するため、正極活物質粒子に錯体溶液を噴霧することにより錯体溶液を正極活物質粒子の表面に付着させた直後に、正極活物質粒子の表面に存在している錯体溶液を乾燥してもよい。このような形態にすることにより、電池の反応抵抗を低減することが可能な複合活物質粒子を製造することが可能になる。
噴霧工程の直後に乾燥工程を行う方法としては、例えば、転動流動コーティング装置やスプレードライヤー等を用いる方法等が挙げられる。転動流動コーティング装置としては、パウレック社製のマルチプレックスや、フロイント産業株式会社製のフローコーター等を例示することができる。転動流動コーティング装置を用いる場合、１つの正極活物質粒子に着目すると、正極活物質粒子に錯体溶液が噴霧された直後に錯体溶液が乾燥され、その後、正極活物質粒子の表面に付着しているニオブ酸リチウムの前駆体の層の厚さが目的の厚さになるまで、正極活物質粒子へ向けた錯体溶液の噴霧、及び、正極活物質粒子に噴霧された錯体溶液の乾燥が繰り返される。
(B) Step of Drying Solution The drying step is a step of drying the solution to form the precursor of lithium niobate on the surface of the positive electrode active material particles.
In the drying step, volatile components such as a solvent and water of hydration contained in the solution attached to the surfaces of the positive electrode active material particles are removed. After drying, the solution becomes a precursor of lithium niobate. The precursor of lithium niobate may be a mixture of raw materials of lithium niobate.
Here, when the above-mentioned complex solution is used as the solution, hydrogen peroxide contained in the complex solution has a strong oxidizing action. Therefore, when the complex solution is brought into contact with the positive electrode active material particles for a long time, the positive electrode active material particles may be eroded by hydrogen peroxide, and the eroded positive electrode active material particles are deteriorated. Therefore, in order to suppress the deterioration of the positive electrode active material particles, the complex solution is present on the surface of the positive electrode active material particles immediately after the complex solution is attached to the surface of the positive electrode active material particles by spraying the complex solution onto the positive electrode active material particles. The complex solution may be dried. By adopting such a form, it becomes possible to manufacture composite active material particles capable of reducing the reaction resistance of the battery.
As a method of performing the drying step immediately after the spraying step, for example, a method using a tumbling fluidized coating apparatus, a spray dryer, or the like can be mentioned. Examples of the tumbling fluidized coating apparatus include a multiplex manufactured by Powrex and a flow coater manufactured by Freund Corporation. When using a tumbling fluidized coating apparatus, focusing on one positive electrode active material particle, the complex solution is dried immediately after the complex solution is sprayed on the positive electrode active material particle, and then adheres to the surface of the positive electrode active material particle. The spraying of the complex solution toward the positive electrode active material particles and the drying of the complex solution sprayed on the positive electrode active material particles are repeated until the thickness of the lithium niobate precursor layer becomes the desired thickness. .
（ｃ）加熱工程
加熱工程は、前記前駆体を表面に付着させた前記正極活物質粒子を２００℃〜３００℃の温度で、１分以上６０分以下の時間、加熱することにより前記複合活物質粒子を得る工程である。
加熱工程により、正極活物質粒子と、当該正極活物質粒子の表面を被覆するニオブ酸リチウムを含む被覆層とを有する複合活物質粒子を得ることができる。
前駆体を所定の温度で所定の時間加熱することにより、非晶質のニオブ酸リチウムが生成される。そして、前駆体を所定の温度を超えて加熱すること、及び、所定の時間を超えて加熱することの少なくともいずれか一方により、生成した非晶質のニオブ酸リチウムの結晶化が進行すると考えられる。
加熱方法は特に限定されず、ホットプレートを用いる方法等が挙げられる。
加熱工程における加熱時の雰囲気は特に限定されないが、大気雰囲気であってもよいが、複合活物質粒子を、硫化物系固体電解質を含む全固体電池に用いた場合に当該硫化物系固体電解質が複合活物質粒子に含まれる水分と反応し変質することを抑制する観点から、真空雰囲気、乾燥空気雰囲気、窒素ガス雰囲気、アルゴンガス雰囲気等が好ましい。
(C) Heating step In the heating step, the composite active material is heated by heating the positive electrode active material particles having the precursor attached to the surface thereof at a temperature of 200 ° C to 300 ° C for 1 minute to 60 minutes. This is the step of obtaining particles.
By the heating step, composite active material particles having positive electrode active material particles and a coating layer containing lithium niobate that covers the surface of the positive electrode active material particles can be obtained.
By heating the precursor at a predetermined temperature for a predetermined time, amorphous lithium niobate is generated. Then, it is considered that crystallization of the generated amorphous lithium niobate proceeds by heating the precursor beyond a predetermined temperature, and / or heating the precursor over a predetermined time. .
The heating method is not particularly limited, and examples thereof include a method using a hot plate.
The atmosphere at the time of heating in the heating step is not particularly limited, but may be an air atmosphere.However, when the composite active material particles are used in an all-solid battery including a sulfide-based solid electrolyte, the sulfide-based solid electrolyte is A vacuum atmosphere, a dry air atmosphere, a nitrogen gas atmosphere, an argon gas atmosphere, or the like is preferable from the viewpoint of suppressing the reaction with water contained in the composite active material particles to alter the quality.
加熱工程では、加熱温度を２００℃以上にすることにより、溶液中の溶媒や水和水等の不純物（揮発成分）の残存量を低減することができる。
また、加熱工程では、加熱時間を１分以上とすることにより、溶液中の溶媒や水和水等の不純物（揮発成分）の残存量を低減することができる。
水和水はリチウムイオン伝導の妨げとなるため、この残存量を低減することにより、複合活物質粒子のリチウムイオン伝導度を向上させることが可能になる。
In the heating step, by setting the heating temperature to 200 ° C. or higher, the residual amount of impurities (volatile components) such as a solvent and water of hydration in the solution can be reduced.
In the heating step, by setting the heating time to 1 minute or more, the amount of impurities (volatile components) such as a solvent and water of hydration in the solution can be reduced.
Since the hydration water hinders lithium ion conduction, it is possible to improve the lithium ion conductivity of the composite active material particles by reducing the residual amount.
加熱工程では、加熱温度を３００℃以下にすることにより、前駆体の加熱により生成した非晶質のニオブ酸リチウムの結晶化を抑制することができる。
また、加熱工程では、加熱時間を６０分以下にすることにより、前駆体の加熱により生成した非晶質のニオブ酸リチウムの結晶化を抑制することができる。
結晶化したニオブ酸リチウムは非晶質のニオブ酸リチウムよりもリチウムイオン伝導度が低いため、電池の反応抵抗増加の一因になる。
In the heating step, by setting the heating temperature to 300 ° C. or lower, the crystallization of amorphous lithium niobate generated by heating the precursor can be suppressed.
In the heating step, by setting the heating time to 60 minutes or less, crystallization of amorphous lithium niobate generated by heating the precursor can be suppressed.
Crystallized lithium niobate has a lower lithium ion conductivity than amorphous lithium niobate, which contributes to an increase in the reaction resistance of the battery.
［複合活物質粒子］
上記（ａ）〜（ｃ）の工程を経て正極活物質粒子と、当該正極活物質粒子の表面の少なくとも一部を被覆するニオブ酸リチウムを含む被覆層と、を有する複合活物質粒子が得られる。
図２は、本開示の複合活物質粒子を説明する図である。図２では、１粒の複合活物質粒子を抽出し、且つ、この複合活物質粒子を簡略化して示している。便宜上、図２には、１つの正極活物質粒子の表面にニオブ酸リチウムを付着（被覆）させている形態を図示したが、本開示の複合活物質粒子は、当該形態に限定されない。本開示の複合活物質粒子は、複数の正極活物質粒子が集合した二次粒子の形態である正極活物質粒子の表面にニオブ酸リチウムを付着（被覆）させた形態であっても良い。
図２に示すように、複合活物質粒子２０は、正極活物質粒子２１と、当該正極活物質粒子２１の表面を被覆するニオブ酸リチウムからなる被覆層２２と、を有している。
[Composite active material particles]
Through the steps (a) to (c), composite active material particles including the positive electrode active material particles and the coating layer containing lithium niobate that covers at least a part of the surface of the positive electrode active material particles are obtained. .
FIG. 2 is a diagram illustrating the composite active material particles of the present disclosure. In FIG. 2, one composite active material particle is extracted and the composite active material particle is shown in a simplified manner. For convenience, FIG. 2 illustrates a form in which lithium niobate is attached (coated) to the surface of one positive electrode active material particle, but the composite active material particle of the present disclosure is not limited to this form. The composite active material particles of the present disclosure may have a form in which lithium niobate is attached (coated) to the surface of positive electrode active material particles that are in the form of secondary particles in which a plurality of positive electrode active material particles are aggregated.
As shown in FIG. 2, the composite active material particles 20 include positive electrode
正極活物質粒子の表面に、ニオブ酸リチウムを含有する被覆層を有する複合活物質粒子は、当該複合活物質粒子を含む正極層を備える全固体電池において、正極活物質粒子と、固体電解質との反応を抑制することができる。
被覆層の厚さは、下限が例えば、０．１ｎｍ以上であり、１ｎｍ以上であっても良い。一方、被覆層の厚さは、上限が例えば、１００ｎｍ以下であり、２０ｎｍ以下であっても良い。被覆層が正極活物質粒子の表面を被覆する面方向の被覆率は、例えば、７０％以上であり、９０％以上であっても良い。被覆率は、粒子の断面の走査型電子顕微鏡（ＳＥＭ）画像等を観測することにより算出してもよい。
On the surface of the positive electrode active material particles, a composite active material particle having a coating layer containing lithium niobate is used in an all-solid battery including a positive electrode layer including the composite active material particle. The reaction can be suppressed.
The lower limit of the thickness of the coating layer is, for example, 0.1 nm or more, and may be 1 nm or more. On the other hand, the upper limit of the thickness of the coating layer is, for example, 100 nm or less, and may be 20 nm or less. The coverage in the surface direction in which the coating layer covers the surface of the positive electrode active material particles is, for example, 70% or more, and may be 90% or more. The coverage may be calculated by observing a scanning electron microscope (SEM) image or the like of the cross section of the particle.
本開示の正極層は、上記（ａ）〜（ｃ）の工程を経て得られた複合活物質粒子を正極材料として用いて、従来公知の方法で形成することができる。
例えば、複合活物質粒子と、後述する導電材及びバインダーを溶媒中に投入し、撹拌することにより、正極用スラリーを作製し、当該スラリーを正極集電体等の基板の一面上に塗布して乾燥させることにより、正極層が得られる。
溶媒は、例えば酢酸ブチル、ヘプタン、Ｎ−メチル−２−ピロリドン等が挙げられる。
正極集電体としては、電池の集電体として使用可能な公知の金属を用いることができる。そのような金属としては、Ｃｕ、Ｎｉ、Ａｌ、Ｖ、Ａｕ、Ｐｔ、Ｍｇ、Ｆｅ、Ｔｉ、Ｃｏ、Ｃｒ、Ｚｎ、Ｇｅ、Ｉｎからなる群から選択される一又は二以上の元素を含む金属材料を例示することができる。
正極集電体の形態は特に限定されるものではないが、箔状が好ましい。
正極集電体等の基板の一面上に正極用スラリーを塗布する方法は、特に限定されず、ドクターブレード法、メタルマスク印刷法、静電塗布法、ディップコート法、スプレーコート法、ロールコート法、グラビアコート法、スクリーン印刷法等が挙げられる。
また、正極層の形成方法の別の方法として、複合活物質粒子及び必要に応じ他の成分を含む正極合剤の粉末を加圧成形することにより正極層を形成してもよい。
The positive electrode layer of the present disclosure can be formed by a conventionally known method using the composite active material particles obtained through the above steps (a) to (c) as a positive electrode material.
For example, composite active material particles, a conductive material and a binder described below are charged into a solvent and stirred to prepare a positive electrode slurry, and the slurry is applied to one surface of a substrate such as a positive electrode current collector. By drying, a positive electrode layer is obtained.
Examples of the solvent include butyl acetate, heptane, N-methyl-2-pyrrolidone and the like.
As the positive electrode current collector, a known metal that can be used as a current collector of a battery can be used. As such a metal, a metal containing one or more elements selected from the group consisting of Cu, Ni, Al, V, Au, Pt, Mg, Fe, Ti, Co, Cr, Zn, Ge, and In Materials can be exemplified.
The form of the positive electrode current collector is not particularly limited, but a foil shape is preferable.
The method for applying the slurry for the positive electrode on one surface of the substrate such as the positive electrode current collector is not particularly limited, and a doctor blade method, a metal mask printing method, an electrostatic coating method, a dip coating method, a spray coating method, a roll coating method , Gravure coating, screen printing, and the like.
Further, as another method of forming the positive electrode layer, the positive electrode layer may be formed by press-molding a powder of a positive electrode mixture containing composite active material particles and other components as necessary.
［全固体電池］
本開示の正極層は、種々の電池の正極層として用いることができるが、電池の反応抵抗低減効果を顕著に発現するために、全固体電池に用いられることが好ましく、硫化物系固体電解質を含む全固体電池に用いられることがより好ましい。
本開示に用いられる全固体電池は、本開示の複合活物質粒子を含有する正極層を含む正極と、負極層を含む負極と、当該正極層及び当該負極層の間に配置される固体電解質層と、を備える。
本開示の全固体電池は、本開示の複合活物質粒子を含有した正極層を含む正極を備えていることにより、電池の反応抵抗を低減することができる。
[All solid state battery]
The positive electrode layer of the present disclosure can be used as a positive electrode layer of various batteries, but is preferably used for an all-solid battery in order to remarkably exhibit a reaction resistance reduction effect of the battery. More preferably, it is used for an all-solid-state battery.
The all solid state battery used in the present disclosure includes a positive electrode including a positive electrode layer containing the composite active material particles of the present disclosure, a negative electrode including a negative electrode layer, and a solid electrolyte layer disposed between the positive electrode layer and the negative electrode layer. And.
The all-solid-state battery according to the present disclosure includes the positive electrode including the positive electrode layer containing the composite active material particles according to the present disclosure, so that the reaction resistance of the battery can be reduced.
図３は、本開示に用いられる全固体電池の一例を示す断面模式図である。
図３に示すように、全固体電池１００は、正極層１２及び正極集電体１４を含む正極１６と、負極層１３及び負極集電体１５を含む負極１７と、正極１６と負極１７の間に配置される固体電解質層１１を備える。
FIG. 3 is a schematic cross-sectional view illustrating an example of the all solid state battery used in the present disclosure.
As shown in FIG. 3, the all-solid-
［正極］
正極は、少なくとも正極層と、正極集電体を有する。
正極層は、本開示の複合活物質粒子を含み、任意成分として、固体電解質、導電材、バインダーが含まれていてもよい。
[Positive electrode]
The positive electrode has at least a positive electrode layer and a positive electrode current collector.
The positive electrode layer includes the composite active material particles of the present disclosure, and may include a solid electrolyte, a conductive material, and a binder as optional components.
正極層における固体電解質は、後述する固体電解質層に用いられる固体電解質と同様の材料が挙げられる。
正極層における固体電解質の含有量は特に限定されるものではない。
Examples of the solid electrolyte in the positive electrode layer include the same materials as the solid electrolyte used for the solid electrolyte layer described below.
The content of the solid electrolyte in the positive electrode layer is not particularly limited.
導電材としては、例えば、炭素材料、金属材料が挙げられる。炭素材料としては、例えば、アセチレンブラック（ＡＢ）やケッチェンブラック（ＫＢ）等のカーボンブラック、カーボンナノチューブ（ＣＮＴ）、及び、カーボンナノファイバー（ＣＮＦ）からなる群より選ばれる少なくとも一種を挙げることができる。カーボンナノチューブ、及び、カーボンナノファイバーは気相法炭素繊維（ＶＧＣＦ）であってもよい。
正極層における導電材の含有量は特に限定されるものではない。
Examples of the conductive material include a carbon material and a metal material. Examples of the carbon material include at least one selected from the group consisting of carbon black such as acetylene black (AB) and Ketjen black (KB), carbon nanotube (CNT), and carbon nanofiber (CNF). it can. Carbon nanotubes and carbon nanofibers may be vapor grown carbon fibers (VGCF).
The content of the conductive material in the positive electrode layer is not particularly limited.
バインダーとしては、アクリロニトリルブタジエンゴム（ＡＢＲ）、ブタジエンゴム（ＢＲ）、ポリフッ化ビニリデン（ＰＶｄＦ）、スチレンブタジエンゴム（ＳＢＲ）等を例示することができる。正極層におけるバインダーの含有量は特に限定されるものではない。 Examples of the binder include acrylonitrile butadiene rubber (ABR), butadiene rubber (BR), polyvinylidene fluoride (PVdF), and styrene butadiene rubber (SBR). The content of the binder in the positive electrode layer is not particularly limited.
正極層の厚みについては特に限定されるものではない。
正極の全体としての形状は特に限定されるものではないが、シート状が好ましい。この場合、正極の全体としての厚みは特に限定されるものではなく、目的とする性能に応じて、適宜決定すればよい。
The thickness of the positive electrode layer is not particularly limited.
Although the overall shape of the positive electrode is not particularly limited, a sheet shape is preferable. In this case, the overall thickness of the positive electrode is not particularly limited, and may be appropriately determined according to the intended performance.
［固体電解質層］
固体電解質層は、少なくとも固体電解質を有する。
固体電解質は、酸化物系固体電解質、硫化物系固体電解質等が挙げられ、電池の出力を向上させる観点から、硫化物系固体電解質が好ましい。
硫化物系固体電解質としては、例えば、Ｌｉ２Ｓ−Ｐ２Ｓ５、Ｌｉ２Ｓ−ＳｉＳ２、ＬｉＸ−Ｌｉ２Ｓ−ＳｉＳ２、ＬｉＸ−Ｌｉ２Ｓ−Ｐ２Ｓ５、ＬｉＸ−Ｌｉ２Ｏ−Ｌｉ２Ｓ−Ｐ２Ｓ５、ＬｉＸ−Ｌｉ２Ｓ−Ｐ２Ｏ５、ＬｉＸ−Ｌｉ３ＰＯ４−Ｐ２Ｓ５、Ｌｉ３ＰＳ４等が挙げられる。なお、上記「Ｌｉ２Ｓ−Ｐ２Ｓ５」の記載は、Ｌｉ２ＳおよびＰ２Ｓ５を含む原料組成物を用いてなる材料を意味し、他の記載についても同様である。また、上記ＬｉＸの「Ｘ」は、ハロゲン元素を示す。さらに、原料組成物中にＬｉＸは、１種含まれていてもよく、２種以上含まれていてもよい。硫化物系固体電解質の具体例としては、１０ＬｉＩ−１５ＬｉＢｒ−３７．５Ｌｉ３ＰＳ４、２０ＬｉＩ−８０（７５Ｌｉ２Ｓ−２５Ｐ２Ｓ５）等が挙げられる。なお、例示した硫化物系固体電解質の原料組成比はモル比である。
硫化物系固体電解質は、ガラスであってもよく、結晶材料であってもよく、ガラスセラミックスであってもよい。ガラスは、原料組成物（例えばＬｉ２ＳおよびＰ２Ｓ５の混合物）を非晶質処理することにより得ることができる。非晶質処理としては、例えば、メカニカルミリングが挙げられる。メカニカルミリングは、乾式メカニカルミリングであっても良く、湿式メカニカルミリングであっても良いが、後者が好ましい。容器等の壁面に原料組成物が固着することを防止できるからである。また、ガラスセラミックスは、ガラスを熱処理することにより得ることができる。また、結晶材料は、例えば、原料組成物に対して固相反応処理することにより得ることができる。
酸化物系固体電解質としては、例えばＬｉ６．２５Ｌａ３Ｚｒ２Ａｌ０．２５Ｏ１２、Ｌｉ３ＰＯ４、Ｌｉ３＋ｘＰＯ４−ｘＮｘ（ＬｉＰＯＮ）等が挙げられる。
[Solid electrolyte layer]
The solid electrolyte layer has at least a solid electrolyte.
Examples of the solid electrolyte include an oxide solid electrolyte and a sulfide solid electrolyte. From the viewpoint of improving the output of the battery, a sulfide solid electrolyte is preferable.
The sulfide-based solid electrolyte, for example, Li 2 S-P 2 S 5, Li 2 S-SiS 2, LiX-Li 2 S-SiS 2, LiX-Li 2 S-P 2 S 5, LiX-Li 2 O-Li 2 S-P 2 S 5, LiX-Li 2 S-P 2 O 5, LiX-
The sulfide-based solid electrolyte may be glass, a crystalline material, or a glass ceramic. Glass can be obtained by subjecting a raw material composition (for example, a mixture of Li 2 S and P 2 S 5 ) to amorphous treatment. Examples of the amorphous treatment include mechanical milling. The mechanical milling may be dry mechanical milling or wet mechanical milling, but the latter is preferred. This is because the raw material composition can be prevented from sticking to the wall surface of the container or the like. Glass ceramics can be obtained by heat-treating glass. The crystalline material can be obtained, for example, by subjecting the raw material composition to a solid phase reaction treatment.
Examples of the oxide-based solid electrolyte include Li 6.25 La 3 Zr 2 Al 0.25 O 12 , Li 3 PO 4 , and Li 3 + x PO 4-x N x (LiPON).
固体電解質の形状は、粒子状であることが好ましい。
また、固体電解質の粒子の平均粒径（Ｄ５０）は、特に限定されないが、下限が０．５μｍ以上であることが好ましく、上限が２μｍ以下であることが好ましい。
The shape of the solid electrolyte is preferably particulate.
The average particle size (D50) of the solid electrolyte particles is not particularly limited, but the lower limit is preferably 0.5 μm or more, and the upper limit is preferably 2 μm or less.
固体電解質は、１種単独で、又は２種以上のものを用いることができる。また、２種以上の固体電解質を用いる場合、２種以上の固体電解質を混合してもよく、又は２層以上の固体電解質それぞれの層を形成して多層構造としてもよい。 As the solid electrolyte, one kind can be used alone, or two or more kinds can be used. When two or more solid electrolytes are used, two or more solid electrolytes may be mixed, or two or more solid electrolyte layers may be formed to form a multilayer structure.
固体電解質層には、可塑性を発現させる等の観点から、固体電解質同士を結着させるバインダーを含有させることもできる。そのようなバインダーとしては、上述した正極に含有させることが可能なバインダー等を例示することができる。ただし、高出力化を図り易くするために、固体電解質の過度の凝集を防止し且つ均一に分散された固体電解質を有する固体電解質層を形成可能にする等の観点から、固体電解質層に含有させるバインダーは５質量％以下とすることが好ましい。 The solid electrolyte layer may also contain a binder that binds the solid electrolytes from the viewpoint of developing plasticity and the like. Examples of such a binder include the above-mentioned binders that can be contained in the positive electrode. However, in order to easily achieve high output, the solid electrolyte layer is contained in the solid electrolyte layer from the viewpoint of preventing excessive aggregation of the solid electrolyte and enabling formation of a solid electrolyte layer having a uniformly dispersed solid electrolyte. The content of the binder is preferably 5% by mass or less.
固体電解質層の厚みは特に限定されるものではなく、通常０．１μｍ以上１ｍｍ以下である。 The thickness of the solid electrolyte layer is not particularly limited, and is usually 0.1 μm or more and 1 mm or less.
本開示において、粒子の平均粒径は、特記しない限り、レーザー回折・散乱式粒子径分布測定により測定される体積基準のメディアン径（Ｄ５０）の値である。また、本開示においてメディアン径（Ｄ５０）とは、粒子の粒径を小さい順に並べた場合に、粒子の累積体積が全体の体積の半分（５０％）となる径（体積平均径）である。 In the present disclosure, the average particle diameter of the particles is a value of a volume-based median diameter (D 50 ) measured by a laser diffraction / scattering particle diameter distribution measurement unless otherwise specified. In the present disclosure, the median diameter (D 50 ) is a diameter (volume average diameter) at which the cumulative volume of particles becomes half (50%) of the total volume when the particle diameters of the particles are arranged in ascending order. .
［負極］
負極は、負極層と負極集電体を有する。
負極層は、負極活物質を含む。
[Negative electrode]
The negative electrode has a negative electrode layer and a negative electrode current collector.
The negative electrode layer contains a negative electrode active material.
負極活物質としては、従来公知の材料を用いることができ、例えば、金属リチウム（Ｌｉ）、リチウム合金、炭素、Ｓｉ、Ｓｉ合金、Ｌｉ４Ｔｉ５Ｏ１２（ＬＴＯ）等が挙げられる。
リチウム合金としては、ＬｉＳｎ、ＬｉＳｉ、ＬｉＡｌ、ＬｉＧｅ、ＬｉＳｂ、ＬｉＰ、及びＬｉＩｎ等が挙げられる。
Ｓｉ合金としては、Ｌｉ等の金属との合金等が挙げられ、その他、Ｓｎ、Ｇｅ、Ａｌからなる群より選ばれる少なくとも一種の金属との合金であってもよい。
なお、Ｓｉは、全固体電池を組み立てた後に行われる初期充電によって、Ｌｉ等の金属と反応してアモルファス合金を形成する。そして、合金となった部分は、放電によってリチウムイオン等の金属イオンが放出された後にもアモルファス化されたままとなる。したがって、本開示においてＳｉを用いた負極層は、Ｓｉがアモルファス合金化された状態を含む。
負極活物質の形状については、特に限定されるものではないが、例えば粒子状、薄膜状とすることができる。
負極活物質が粒子である場合の当該粒子の平均粒径（Ｄ５０）は、例えば１ｎｍ以上１００μｍ以下であることが好ましく、１０ｎｍ以上３０μｍ以下であることがより好ましい。
As the negative electrode active material, conventionally known materials can be used, and examples thereof include lithium metal (Li), a lithium alloy, carbon, Si, a Si alloy, and Li 4 Ti 5 O 12 (LTO).
Examples of the lithium alloy include LiSn, LiSi, LiAl, LiGe, LiSb, LiP, and LiIn.
Examples of the Si alloy include an alloy with a metal such as Li and the like, and may be an alloy with at least one metal selected from the group consisting of Sn, Ge, and Al.
Note that Si reacts with a metal such as Li to form an amorphous alloy by initial charging performed after assembling the all-solid-state battery. Then, the alloyed portion remains amorphous even after metal ions such as lithium ions are released by discharge. Therefore, the negative electrode layer using Si in the present disclosure includes a state in which Si is alloyed.
The shape of the negative electrode active material is not particularly limited, but may be, for example, a particle shape or a thin film shape.
When the negative electrode active material is a particle, the average particle diameter (D50) of the particle is, for example, preferably from 1 nm to 100 μm, more preferably from 10 nm to 30 μm.
負極層を形成する方法としては、特に限定されないが、負極活物質及び必要に応じ他の成分を含む負極合剤の粉末を加圧成形する方法等が挙げられる。また、負極層を形成する方法の別の例としては、負極活物質、溶媒及び必要に応じ他の成分を含む負極用スラリーを用意し、当該負極用スラリーを負極集電体又は固体電解質層の一面上に塗布し、当該負極用スラリーを乾燥する方法等が挙げられる。負極用スラリーに用いられる溶媒は、正極用スラリーに用いられるものと同様のものが挙げられる。負極集電体又は固体電解質層の一面上に負極用スラリーを塗布する方法は、正極用スラリーを塗布する方法と同様の方法が挙げられる。 A method for forming the negative electrode layer is not particularly limited, and examples thereof include a method of pressure-forming a powder of a negative electrode mixture containing a negative electrode active material and other components as necessary. Further, as another example of a method of forming the negative electrode layer, a negative electrode slurry containing a negative electrode active material, a solvent and other components as necessary is prepared, and the negative electrode slurry is used as a negative electrode current collector or a solid electrolyte layer. A method of applying the composition on one surface and drying the slurry for the negative electrode may be used. Examples of the solvent used for the negative electrode slurry include the same solvents as those used for the positive electrode slurry. The method for applying the slurry for the negative electrode on one surface of the negative electrode current collector or the solid electrolyte layer includes the same method as the method for applying the slurry for the positive electrode.
負極集電体は、全固体電池の集電体として使用可能な公知の金属を用いることができる。そのような金属としては、Ｃｕ、Ｎｉ、Ａｌ、Ｖ、Ａｕ、Ｐｔ、Ｍｇ、Ｆｅ、Ｔｉ、Ｃｏ、Ｃｒ、Ｚｎ、Ｇｅ、Ｉｎからなる群から選択される一又は二以上の元素を含む金属材料を例示することができる。
負極集電体の形態は特に限定されるものではなく、箔状、メッシュ状等、種々の形態とすることができる。
As the negative electrode current collector, a known metal that can be used as a current collector for an all solid state battery can be used. As such a metal, a metal containing one or more elements selected from the group consisting of Cu, Ni, Al, V, Au, Pt, Mg, Fe, Ti, Co, Cr, Zn, Ge, and In Materials can be exemplified.
The form of the negative electrode current collector is not particularly limited, and may be various forms such as a foil shape and a mesh shape.
負極の全体としての形状は特に限定されるものではないが、シート状が好ましい。この場合、負極の全体としての厚みは特に限定されるものではなく、目的とする性能に応じて、適宜決定すればよい。 Although the shape of the negative electrode as a whole is not particularly limited, a sheet shape is preferable. In this case, the overall thickness of the negative electrode is not particularly limited, and may be appropriately determined according to the intended performance.
全固体電池は、必要に応じ、正極、負極、及び、固体電解質層を収容する外装体を備える。
外装体の形状としては、特に限定されないが、ラミネート型等を挙げることができる。
外装体の材質は、電解質に安定なものであれば特に限定されないが、ポリプロピレン、ポリエチレン、及び、アクリル樹脂等の樹脂等が挙げられる。
The all-solid-state battery includes, as necessary, a positive electrode, a negative electrode, and an exterior body that accommodates the solid electrolyte layer.
The shape of the exterior body is not particularly limited, and examples thereof include a laminate type.
The material of the exterior body is not particularly limited as long as it is stable to the electrolyte, and examples thereof include resins such as polypropylene, polyethylene, and acrylic resin.
全固体電池としては、負極の反応として金属リチウムの析出−溶解反応を利用したリチウム電池、正負極間をリチウムイオンが移動することによって充放電を行うリチウムイオン電池、ナトリウム電池、マグネシウム電池及びカルシウム電池等を挙げることができ、好ましくはリチウムイオン電池であってもよい。また、全固体電池は、一次電池であってもよく二次電池であってもよい。
全固体電池の形状としては、例えば、コイン型、ラミネート型、円筒型、及び角型等を挙げることができる。
Examples of the all-solid-state battery include a lithium battery using a precipitation-dissolution reaction of metallic lithium as a reaction of a negative electrode, a lithium ion battery that performs charge and discharge by moving lithium ions between a positive electrode and a negative electrode, a sodium battery, a magnesium battery, and a calcium battery. And the like, and preferably a lithium ion battery. Further, the all-solid-state battery may be a primary battery or a secondary battery.
Examples of the shape of the all solid state battery include a coin type, a laminate type, a cylindrical type, and a square type.
本開示の全固体電池の製造方法は、例えば、まず、固体電解質材料の粉末を加圧成形することにより固体電解質層を形成する。そして、固体電解質層の一面上で正極合剤の粉末を加圧成形することにより正極層を得る。その後、固体電解質層の正極層を形成した面とは反対側の面上で負極合剤の粉末を加圧成形することにより負極層を得る。そして、得られた正極層−固体電解質層−負極層接合体を全固体電池とすることができる。
この場合、固体電解質材料の粉末、正極合剤の粉末、及び負極合剤の粉末を加圧成形する際のプレス圧は、通常１ＭＰａ以上６００ＭＰａ以下程度である。
加圧方法としては、特に制限されないが、例えば、平板プレス、ロールプレス等を用いて圧力を付加する方法等が挙げられる。
本開示の全固体電池の製造方法の別の例としては、例えば、まず、固体電解質材料の粉末を加圧成形することにより固体電解質層を形成する。そして、正極集電体の一面上に正極用スラリーを塗布し、当該正極用スラリーを乾燥させることにより正極層を含む正極を得る。その後、負極集電体の一面上に負極用スラリーを塗布し、当該負極用スラリーを乾燥させることにより負極層を含む負極を得る。そして、正極集電体、正極層、固体電解質層、負極層、負極集電体の順となるように固体電解質層を正極層と負極層の間に配置することにより全固体電池を得ることができる。
全固体電池の製造は、系内の水分をできるだけ除去した状態で行うとよい。例えば、各製造工程において、系内を減圧すること、系内を不活性ガス等の水分を実質的に含まないガスで置換すること等が有効と考えられる。
In the method for manufacturing an all-solid battery of the present disclosure, for example, first, a solid electrolyte layer is formed by pressure-forming a solid electrolyte material powder. Then, a positive electrode layer is obtained by pressing the powder of the positive electrode mixture on one surface of the solid electrolyte layer. Thereafter, the negative electrode layer is obtained by pressing and molding the powder of the negative electrode mixture on the surface of the solid electrolyte layer opposite to the surface on which the positive electrode layer is formed. Then, the obtained positive electrode layer-solid electrolyte layer-negative electrode layer assembly can be used as an all-solid battery.
In this case, the press pressure at the time of press-molding the solid electrolyte material powder, the positive electrode mixture powder, and the negative electrode mixture powder is usually about 1 MPa or more and about 600 MPa or less.
The pressing method is not particularly limited, and examples thereof include a method of applying pressure using a flat plate press, a roll press, or the like.
As another example of the method for manufacturing an all-solid battery according to the present disclosure, for example, first, a solid electrolyte layer is formed by pressing a solid electrolyte material powder under pressure. Then, a positive electrode slurry is applied on one surface of the positive electrode current collector, and the positive electrode slurry is dried to obtain a positive electrode including a positive electrode layer. Thereafter, a negative electrode slurry is applied on one surface of the negative electrode current collector, and the negative electrode slurry is dried to obtain a negative electrode including a negative electrode layer. Then, by arranging the solid electrolyte layer between the positive electrode layer and the negative electrode layer in the order of the positive electrode current collector, the positive electrode layer, the solid electrolyte layer, the negative electrode layer, and the negative electrode current collector, an all-solid battery can be obtained. it can.
The production of an all-solid-state battery is preferably performed in a state where water in the system is removed as much as possible. For example, in each manufacturing process, it is considered effective to reduce the pressure in the system or to replace the inside of the system with a gas substantially free of moisture such as an inert gas.
（比較例１）
［正極活物質粒子の準備］
正極活物質粒子としてＬｉＮｉ１／３Ｍｎ１／３Ｃｏ１／３Ｏ２（日亜化学工業株式会社製）の粒子を準備した。
(Comparative Example 1)
[Preparation of positive electrode active material particles]
Particles of LiNi 1/3 Mn 1/3 Co 1/3 O 2 (produced by Nichia Corporation) were prepared as positive electrode active material particles.
［錯体溶液の準備］
濃度３０質量％の過酸化水素水８７０．４ｇを入れた容器へ、イオン交換水９８７．４ｇ、及び、ニオブ酸（Ｎｂ２Ｏ５・３Ｈ２Ｏ（Ｎｂ２Ｏ５含水率７２％））４４．２ｇを添加した。次に、上記容器へ、濃度２８質量％のアンモニア水８７．９ｇを添加した。そして、アンモニア水を添加した後に容器内の内容物を十分に攪拌することにより、透明溶液を得た。さらに、得られた透明溶液に、水酸化リチウム・１水和物（ＬｉＯＨ・Ｈ２Ｏ）１０．１ｇを加えることにより、ニオブのペルオキソ錯体及びリチウムイオンを含有する錯体溶液を得た。得られた錯体溶液における、Ｌｉ及びＮｂのモル濃度は、何れも０．１２ｍｏｌ／ｋｇであった。
[Preparation of complex solution]
To a vessel containing hydrogen peroxide 870.4g of concentration 30% by weight, ion-exchanged water 987.4G, and niobate (Nb 2 O 5 · 3H 2 O (Nb 2 O 5 water content 72%)) 44 .2 g were added. Next, 87.9 g of aqueous ammonia having a concentration of 28% by mass was added to the container. Then, after adding the ammonia water, the contents in the container were sufficiently stirred to obtain a transparent solution. Further, by adding 10.1 g of lithium hydroxide monohydrate (LiOH.H 2 O) to the obtained transparent solution, a complex solution containing a peroxo complex of niobium and a lithium ion was obtained. The molar concentrations of Li and Nb in the obtained complex solution were both 0.12 mol / kg.
［錯体溶液の噴霧及び乾燥］
得られた錯体溶液２８４０ｇ、及び、１０００ｇの正極活物質粒子と、転動流動コーティング装置（ＭＰ−０１、パウレック社製）とを用いて、正極活物質粒子に錯体溶液を噴霧し、且つ、これと並行して錯体溶液を乾燥することにより、ニオブ酸リチウムの前駆体を含む層を正極活物質粒子の表面に被覆した。なお、転動流動コーティング装置の運転条件は、吸気ガス：窒素、吸気温度：１２０℃、吸気風量：０．４ｍ３／ｍｉｎ、ロータ回転数：毎分４００回転、噴霧速度：４．５ｇ／ｍｉｎとした。
[Spray and drying of complex solution]
The complex solution was sprayed on the positive electrode active material particles using 2840 g of the obtained complex solution and 1000 g of the positive electrode active material particles, and a tumbling fluidized coating apparatus (MP-01, manufactured by Powrex), and The layer containing the precursor of lithium niobate was coated on the surface of the positive electrode active material particles by drying the complex solution in parallel with the above. The operating conditions of the rolling fluidized coating apparatus were as follows: intake gas: nitrogen, intake temperature: 120 ° C., intake air volume: 0.4 m 3 / min, rotor rotation speed: 400 revolutions per minute, spray speed: 4.5 g / min. And
［加熱工程］
噴霧及び乾燥により得られた、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末について、ホットプレートを用いて１５０℃で１分間加熱することにより、ＬｉＮｉ１／３Ｍｎ１／３Ｃｏ１／３Ｏ２と、その表面に付着させたニオブ酸リチウムとを有する複合活物質粒子（比較例１の複合活物質粒子）を得た。
[Heating process]
About the powder obtained by spraying and drying and having a layer containing a precursor of lithium niobate formed on the surface of the positive electrode active material particles and the positive electrode active material particles, using a hot plate at 150 ° C. for 1 minute By heating, composite active material particles having LiNi 1/3 Mn 1/3 Co 1/3 O 2 and lithium niobate adhered to the surface thereof (composite active material particles of Comparative Example 1) were obtained. .
［水分量測定］
カールフィッシャー滴定法を用いて、複合活物質粒子の水分量を測定した。２００℃に設定された加熱部で複合活物質粒子から放出される水分を、窒素ガスをキャリアとして、測定部にフローし計測した。測定時間は４０分とした。結果を、表１に示す。
[Water content measurement]
The water content of the composite active material particles was measured by Karl Fischer titration. Moisture released from the composite active material particles in the heating unit set at 200 ° C. was measured by flowing to the measurement unit using nitrogen gas as a carrier. The measurement time was 40 minutes. Table 1 shows the results.
［正極］
得られた比較例１の複合活物質粒子と硫化物系固体電解質（１０ＬｉＩ−１５ＬｉＢｒ−３７．５Ｌｉ３ＰＳ４）とを、体積比で複合活物質粒子：硫化物系固体電解質＝６：４となるように秤量し、これを、ヘプタンを入れた容器へと投入した。さらに、３質量％となる量の導電材（気相法炭素繊維、昭和電工株式会社製）及び、０．７質量％となる量のバインダー（ブチレンラバー、ＪＳＲ株式会社製）を、ヘプタン等を入れた容器へと投入することにより、正極用混合物を作製した。
次いで、作製した正極用混合物を超音波ホモジナイザー（ＵＨ−５０、株式会社エスエムテー製。以下において同じ。）で分散させることにより得た正極用スラリーを、正極集電体としてのアルミニウム箔の上面に塗工し、引き続き、１００℃で３０分間乾燥させることにより、アルミニウム箔の上面に正極層を形成した。次に、上面に正極層が形成されている状態のアルミニウム箔を１ｃｍ２の大きさに打ち抜くことにより、アルミニウム箔上に正極層を有する正極を得た。
[Positive electrode]
Composite active material particles and the sulfide-based solid electrolyte obtained in Comparative Example 1 and (10LiI-15LiBr-37.5Li 3 PS 4), the composite active material particles by volume: sulfide-based solid electrolyte = 6: 4 and And weighed into a container containing heptane. Further, a conductive material (vapor-grown carbon fiber, manufactured by Showa Denko KK) in an amount of 3% by mass and a binder (butylene rubber, manufactured by JSR Corporation) in an amount of 0.7% by mass were added to heptane and the like. The mixture for the positive electrode was prepared by charging the mixture into the container.
Next, the positive electrode slurry obtained by dispersing the prepared positive electrode mixture with an ultrasonic homogenizer (UH-50, manufactured by SMT Co., Ltd .; the same applies hereinafter) is applied to the upper surface of an aluminum foil as a positive electrode current collector. Then, by drying at 100 ° C. for 30 minutes, a positive electrode layer was formed on the upper surface of the aluminum foil. Next, a positive electrode having the positive electrode layer on the aluminum foil was obtained by punching out the aluminum foil having the positive electrode layer formed on the upper surface into a size of 1 cm 2 .
［負極］
一方、負極活物質（層状炭素）と硫化物系固体電解質（１０ＬｉＩ−１５ＬｉＢｒ−３７．５Ｌｉ３ＰＳ４）とを、体積比で負極活物質：硫化物系固体電解質＝６：４となるように秤量し、これを、ヘプタンを入れた容器へと投入した。さらに、１．２質量％となる量のバインダー（ブチレンラバー、ＪＳＲ株式会社製）をヘプタンや負極活物質等を入れた容器へと投入することにより、負極用混合物を作製した。
次いで、作製した負極用混合物を超音波ホモジナイザーで分散させることにより得た負極用スラリーを、負極集電体としての銅箔の上面に塗工し、引き続き、１００℃で３０分間乾燥させることにより、銅箔の上面に負極層を形成した。
次に、上面に負極層が形成されている状態の銅箔を１ｃｍ２の大きさに打ち抜くことにより、銅箔上に負極層を有する負極を得た。
[Negative electrode]
On the other hand, the negative electrode active material (layered carbon) and sulfide-based solid electrolyte and (10LiI-15LiBr-37.5Li 3 PS 4), the negative electrode active material in a volume ratio: sulfide-based solid electrolyte = 6: so that 4 It was weighed and poured into a container containing heptane. Furthermore, a binder (butylene rubber, manufactured by JSR Corporation) in an amount of 1.2% by mass was charged into a container containing heptane, a negative electrode active material, and the like, to prepare a negative electrode mixture.
Next, the negative electrode slurry obtained by dispersing the prepared negative electrode mixture with an ultrasonic homogenizer is applied to the upper surface of a copper foil as a negative electrode current collector, and subsequently dried at 100 ° C. for 30 minutes, A negative electrode layer was formed on the upper surface of the copper foil.
Next, a negative electrode having a negative electrode layer on the copper foil was obtained by punching a copper foil having a negative electrode layer formed on the upper surface into a size of 1 cm 2 .
［固体電解質層］
次に、内径断面積１ｃｍ２の筒状セラミックスに、硫化物系固体電解質（１０ＬｉＩ−１５ＬｉＢｒ−３７．５Ｌｉ３ＰＳ４）６４．８ｍｇを入れ、表面を平滑にしてから９８ＭＰａでプレスすることにより、固体電解質層を形成した。
[Solid electrolyte layer]
Next, the cylindrical ceramic inner diameter cross-sectional area 1 cm 2, by pressing putting sulfide-based solid electrolyte (10LiI-15LiBr-37.5Li 3 PS 4) 64.8mg, the surface after the smoothing at 98 MPa, A solid electrolyte layer was formed.
［全固体電池の作製］
その後、この固体電解質層が正極層と負極層との間に配置されるように、正極及び負極を筒状セラミックスに入れ、４２１．４ＭＰａでプレスした後、正極側、及び、負極側にステンレス棒を入れ、これを９８ＭＰａで拘束することにより、比較例１の全固体電池を作製した。
[Preparation of all solid state battery]
Thereafter, the positive electrode and the negative electrode were placed in cylindrical ceramics and pressed at 421.4 MPa so that the solid electrolyte layer was disposed between the positive electrode layer and the negative electrode layer, and then a stainless steel rod was placed on the positive electrode side and the negative electrode side. , And constrained at 98 MPa to produce an all-solid-state battery of Comparative Example 1.
（比較例２）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱時間を１０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Comparative Example 2)
In the above [heating step], except that the heating time of the powder having the positive electrode active material particles and the layer containing the lithium niobate precursor formed on the surface of the positive electrode active material particles was set to 10 minutes, Composite active material particles were produced in the same manner as in Example 1, and the water content of the composite active material particles was measured. Thereafter, as in Comparative Example 1, an all solid state battery was produced.
（比較例３）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱時間を３０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Comparative Example 3)
In the above [heating step], except that the heating time of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles was set to 30 minutes, Composite active material particles were produced in the same manner as in Example 1, and the water content of the composite active material particles was measured. Thereafter, as in Comparative Example 1, an all solid state battery was produced.
（実施例１）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を２００℃としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 1)
In the above [heating step], except that the heating temperature of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles was set to 200 ° C. Composite active material particles were produced in the same manner as in Example 1, and the water content of the composite active material particles was measured. Thereafter, as in Comparative Example 1, an all solid state battery was produced.
（実施例２）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を２００℃、加熱時間を１０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 2)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the lithium niobate precursor formed on the surface of the positive electrode active material particles is 200 ° C., and the heating time is 10 minutes. Except for this, composite active material particles were produced in the same manner as in Comparative Example 1, the water content of the composite active material particles was measured, and then, in the same manner as in Comparative Example 1, an all solid state battery was produced.
（実施例３）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を２００℃、加熱時間を３０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 3)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the lithium niobate precursor formed on the surface of the positive electrode active material particles is 200 ° C., and the heating time is 30 minutes. Except for this, composite active material particles were produced in the same manner as in Comparative Example 1, the water content of the composite active material particles was measured, and then, in the same manner as in Comparative Example 1, an all solid state battery was produced.
（実施例４）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を２００℃、加熱時間を６０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 4)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles is 200 ° C., and the heating time is 60 minutes. Except for this, composite active material particles were produced in the same manner as in Comparative Example 1, the water content of the composite active material particles was measured, and then, in the same manner as in Comparative Example 1, an all solid state battery was produced.
（実施例５）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を３００℃としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 5)
In the above [heating step], except that the heating temperature of the powder having the cathode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the cathode active material particles was set to 300 ° C, Composite active material particles were produced in the same manner as in Example 1, and the water content of the composite active material particles was measured. Thereafter, as in Comparative Example 1, an all solid state battery was produced.
（実施例６）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を３００℃、加熱時間を１０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 6)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles is 300 ° C., and the heating time is 10 minutes. Except for this, composite active material particles were produced in the same manner as in Comparative Example 1, the water content of the composite active material particles was measured, and then, in the same manner as in Comparative Example 1, an all solid state battery was produced.
（実施例７）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を３００℃、加熱時間を３０分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、当該複合活物質粒子の水分量を測定し、その後、比較例１と同様に、全固体電池を作製した。
(Example 7)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles is 300 ° C., and the heating time is 30 minutes. Except for this, composite active material particles were produced in the same manner as in Comparative Example 1, the water content of the composite active material particles was measured, and then, in the same manner as in Comparative Example 1, an all solid state battery was produced.
（比較例４）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を２００℃、加熱時間を３００分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、その後、比較例１と同様に、全固体電池を作製した。比較例４の複合活物質粒子については水分量を測定しなかった。
(Comparative Example 4)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles is 200 ° C., and the heating time is 300 minutes. Except for this, composite active material particles were produced in the same manner as in Comparative Example 1, and thereafter, an all-solid battery was produced in the same manner as in Comparative Example 1. The water content of the composite active material particles of Comparative Example 4 was not measured.
（比較例５）
上記［加熱工程］において、正極活物質粒子と、該正極活物質粒子の表面に形成されたニオブ酸リチウムの前駆体を含む層とを有する粉末の加熱温度を２００℃、加熱時間を３００分としたこと以外は、比較例１と同様に、複合活物質粒子を作製し、その後、正極、負極、及び固体電解質層に用いた硫化物系固体電解質を２０ＬｉＩ−８０（７５Ｌｉ２Ｓ−２５Ｐ２Ｓ５）に変更したこと以外は、比較例１と同様に、全固体電池を作製した。比較例５の複合活物質粒子については水分量を測定しなかった。
(Comparative Example 5)
In the above-mentioned [heating step], the heating temperature of the powder having the positive electrode active material particles and the layer containing the precursor of lithium niobate formed on the surface of the positive electrode active material particles is 200 ° C., and the heating time is 300 minutes. was except that, in the same manner as in Comparative example 1, to prepare a composite active material particles, then the positive electrode, negative electrode and a sulfide-based solid electrolyte used in the solid electrolyte layer 20LiI-80 (75Li 2 S- 25P 2 S An all-solid-state battery was produced in the same manner as in Comparative Example 1, except that the above method was changed to 5 ). The water content of the composite active material particles of Comparative Example 5 was not measured.
［全固体電池の反応抵抗測定］
上述の方法で作製した実施例５の全固体電池、及び、比較例４〜５の全固体電池のそれぞれを、電圧４．５５Ｖまで充電し、次いで２．５Ｖまで放電した後に、３．６Ｖまで充電し、３．６Ｖにおいて交流インピーダンス測定を行った。そして、ナイキストプロット（Ｎｙｑｕｉｓｔプロット）により得られた円弧から、各全固体電池の反応抵抗［Ω・ｃｍ２］を特定した。小数第３位を四捨五入することによって得られる反応抵抗の値を、表１に示す。
[Reaction resistance measurement of all solid state battery]
The all-solid-state battery of Example 5 and the all-solid-state batteries of Comparative Examples 4 to 5 were charged to a voltage of 4.55 V, then discharged to 2.5 V, and then discharged to 3.6 V. The battery was charged and the AC impedance was measured at 3.6 V. Then, the reaction resistance [Ω · cm 2 ] of each all-solid-state battery was specified from the arc obtained by the Nyquist plot (Nyquist plot). Table 1 shows the values of the reaction resistance obtained by rounding off the third decimal place.
［全固体電池の電池出力測定］
上述の方法で作製した実施例１〜７の全固体電池、及び、比較例１〜４の全固体電池のそれぞれを、開回路電圧（ＯＣＶ）３．６６Ｖ、カットオフ電圧２．５Ｖの条件で、各全固体電池を上記開回路電圧に調整後、定電力放電法で、５秒間で放電可能な最大の電力値を測定し、当該電力値を各全固体電池の電池出力とした。結果を、表１に示す。
[Battery output measurement of all solid state batteries]
Each of the all-solid-state batteries of Examples 1 to 7 and the all-solid-state batteries of Comparative Examples 1 to 4 manufactured by the above-described method was subjected to an open circuit voltage (OCV) of 3.66 V and a cutoff voltage of 2.5 V. After adjusting each of the all-solid-state batteries to the above-mentioned open-circuit voltage, the maximum power value that can be discharged in 5 seconds was measured by a constant power discharge method, and the power value was used as the battery output of each all-solid-state battery. Table 1 shows the results.
表１に示すように、実施例１〜７の全固体電池は比較例１〜３の全固体電池と比較して、電池出力が高い。これは、３００℃以下の温度でニオブ酸リチウムの前駆体を表面に付着させた正極活物質粒子を加熱することにより、非晶質のニオブ酸リチウムの結晶化を抑制し、リチウムイオン伝導度の高いニオブ酸リチウムが得られ、且つ、２００℃以上の温度でニオブ酸リチウムの前駆体を表面に付着させた正極活物質粒子を加熱することにより、得られる複合活物質粒子に含まれる水分量を低減することができ、当該複合活物質粒子を全固体電池に用いることで、全固体電池の反応抵抗を抑制できたためであると考えられる。
また、比較例４の全固体電池は、実施例１〜４の全固体電池と比較して、電池出力が低い。また、比較例４の全固体電池は、実施例５の全固体電池と比較して反応抵抗が高い。これは、ニオブ酸リチウムの前駆体を表面に付着させた正極活物質粒子を長時間加熱したことにより、非晶質のニオブ酸リチウムの結晶化が促進され、リチウムイオン伝導度の低いニオブ酸リチウムが得られたためである。
また、実施例５の全固体電池は、比較例５の全固体電池と比較して反応抵抗が顕著に低い。そのため、本開示の製造方法により得られる正極層を備える全固体電池は、従来の正極層を備える全固体電池と比較して、全固体電池の反応抵抗を低減することができることが実証された。
なお、表１に示すように、実施例７の複合活物質粒子は実施例４の複合活物質粒子よりも水分量が少ない。そのため、３００℃で６０分間、ニオブ酸リチウムの前駆体を表面に付着させた正極活物質粒子を加熱して得られた複合活物質粒子を正極層に用いた全固体電池は、実施例４の全固体電池と同等の電池出力が得られると推定される。
As shown in Table 1, the all solid state batteries of Examples 1 to 7 have higher battery outputs than the all solid state batteries of Comparative Examples 1 to 3. This is because the crystallization of amorphous lithium niobate is suppressed by heating the positive electrode active material particles having a precursor of lithium niobate adhered to the surface thereof at a temperature of 300 ° C. or less, and the lithium ion conductivity is reduced. A high lithium niobate is obtained, and by heating the positive electrode active material particles having a lithium niobate precursor adhered to the surface thereof at a temperature of 200 ° C. or more, the amount of water contained in the obtained composite active material particles is reduced. It is considered that the reaction resistance of the all-solid-state battery could be suppressed by using the composite active material particles for the all-solid-state battery.
Further, the all-solid-state battery of Comparative Example 4 has a lower battery output than the all-solid-state batteries of Examples 1 to 4. Further, the all-solid-state battery of Comparative Example 4 has a higher reaction resistance than the all-solid-state battery of Example 5. This is because the crystallization of amorphous lithium niobate is promoted by heating the positive electrode active material particles having a precursor of lithium niobate adhered to the surface for a long time, and lithium niobate having low lithium ion conductivity. Is obtained.
Further, the all-solid-state battery of Example 5 has a significantly lower reaction resistance than the all-solid-state battery of Comparative Example 5. Therefore, it was demonstrated that the all-solid-state battery provided with the positive electrode layer obtained by the manufacturing method of the present disclosure can reduce the reaction resistance of the all-solid-state battery as compared with the all-solid battery provided with the conventional positive electrode layer.
In addition, as shown in Table 1, the composite active material particles of Example 7 have a smaller moisture content than the composite active material particles of Example 4. Therefore, the all-solid-state battery using the composite active material particles obtained by heating the positive electrode active material particles having the lithium niobate precursor adhered to the surface thereof at 300 ° C. for 60 minutes for the positive electrode layer is described in Example 4. It is estimated that a battery output equivalent to that of an all solid state battery is obtained.
１１ 固体電解質層
１２ 正極層
１３ 負極層
１４ 正極集電体
１５ 負極集電体
１６ 正極
１７ 負極
２０ 複合活物質粒子
２１ 正極活物質粒子
２２ 被覆層
１００ 全固体電池
REFERENCE SIGNS LIST 11
Claims (1)
前記正極活物質粒子に、ニオブイオンとリチウムイオンとを含有する溶液を噴霧し、当該正極活物質粒子の表面に当該溶液を付着させる工程と、
前記溶液を乾燥させ、前記正極活物質粒子の表面に前記ニオブ酸リチウムの前駆体を形成させる工程と、
前記前駆体を表面に付着させた前記正極活物質粒子を２００℃〜３００℃の温度で、１分以上６０分以下の時間、加熱することにより前記複合活物質粒子を得る工程を有することを特徴とする正極層の製造方法。 A method for producing a positive electrode layer containing composite active material particles, comprising: a positive electrode active material particle; and a coating layer containing lithium niobate that covers at least a part of the surface of the positive electrode active material particle,
A step of spraying a solution containing niobium ions and lithium ions on the positive electrode active material particles, and attaching the solution to the surface of the positive electrode active material particles,
Drying the solution, forming a precursor of the lithium niobate on the surface of the positive electrode active material particles,
A step of heating the positive electrode active material particles having the precursor adhered to the surface thereof at a temperature of 200 ° C. to 300 ° C. for 1 minute to 60 minutes to obtain the composite active material particles. A method for producing a positive electrode layer.