JP2019157527A

JP2019157527A - Floor sheet

Info

Publication number: JP2019157527A
Application number: JP2018046554A
Authority: JP
Inventors: 石田　尚也; Hisaya Ishida; 尚也石田; 寛充林; Hiromitsu Hayashi
Original assignee: Fukuvi Chemical Industry Co Ltd
Current assignee: Fukuvi Chemical Industry Co Ltd
Priority date: 2018-03-14
Filing date: 2018-03-14
Publication date: 2019-09-19
Anticipated expiration: 2038-03-14
Also published as: JP7143095B2

Abstract

To provide a floor sheet having high design properties while being able to impart shock absorption and heat insulation to a floor of a building.SOLUTION: The bathroom floor 3 is composed of a base layer 9 and a floor sheet 35 affixed thereon. The floor sheet 35 is formed by laminating a cushion layer 30, a print layer 31, and a surface layer 32 in order from the base layer 9 side. The cushion layer 30 is made of a soft foamed resin, and the surface layer 32 is made of a resin material and has light transmittance. The print layer 31 has a print surface formed in a surface direction extending in a direction perpendicular to the Z axis. The surface layer 32 has a plurality of crests 32a protruding to the opposite side to the base layer 9 in the Z direction, and a groove 32b formed between the crests 32a. The groove portion 32b is formed so as to communicate from end to end in a plane direction orthogonal to the Z direction.SELECTED DRAWING: Figure 3

Description

本発明は、床用シートに関する。 The present invention relates to a floor sheet.

家屋の床には、衝撃吸収性や断熱性などが求められる。例えば、浴室の床においては、高齢者、子供、障碍者などが利用する際に、転倒などの場合にも怪我をし難いように衝撃吸収性を備えることが求められる。 The floor of a house is required to have shock absorption and heat insulation. For example, a bathroom floor is required to have shock absorption so that an elderly person, a child, a handicapped person, or the like uses it to prevent injury even if it falls.

また、玄関土間や浴室などの床では、冬場などにおいて足が冷え難いように断熱性を備えることも求められる。 In addition, it is also required that the floors of the entrance soil and the bathroom have heat insulating properties so that the feet do not get cold in winter.

このような衝撃吸収性や断熱性を備える床用のシートが、特許文献１で提案されている。特許文献１で提案されている床用シート材は、クッション層と補強層と表面層とが順に積層された構成となっている。クッション層は、軟質発泡樹脂から構成されており、表面層は、熱可塑性樹脂から構成されている。 Patent Document 1 proposes a floor sheet having such shock absorption and heat insulation properties. The floor sheet material proposed in Patent Document 1 has a configuration in which a cushion layer, a reinforcing layer, and a surface layer are sequentially laminated. The cushion layer is made of a soft foam resin, and the surface layer is made of a thermoplastic resin.

特許文献１で提案されている床用シートでは、軟質発泡樹脂から構成されたクッション層を備える。このため、当該床用シートを浴室などの床に貼り付けることにより、衝撃吸収性および断熱性を有する床とすることができる。 The floor sheet proposed in Patent Document 1 includes a cushion layer made of a soft foam resin. For this reason, it can be set as the floor which has shock absorption property and heat insulation by sticking the said sheet | seat for floors on floors, such as a bathroom.

特開２０１４−２０６０２６号公報JP 2014-206026 A

しかしながら、上記特許文献１で提案されている床用シートでは、表面層に印刷や塗装を施す構造となっているので、高い意匠性を実現する上で改善の余地がある。上記特許文献１で提案の構成では、深みのある（立体感のある）意匠性を備えた床用シートを実現しようとすることは困難であると考えられる。 However, since the floor sheet proposed in Patent Document 1 has a structure in which printing or coating is applied to the surface layer, there is room for improvement in realizing high designability. In the configuration proposed in Patent Document 1, it is considered difficult to achieve a floor sheet having a deep (three-dimensional) design.

本発明は、上記のような問題の解決を図ろうとなされたものであって、建築物の床に衝撃吸収性および断熱性を付与することができるとともに、高い意匠性を備えた床用シートを提供することを目的とする。 The present invention has been made to solve the above-described problems, and can provide a floor sheet having high design properties while being able to impart shock absorption and heat insulation to a floor of a building. The purpose is to provide.

本発明の一態様に係る床用シートは、建築物の床下地に貼付または載置される床用シートであって、前記床下地の上に配置され、軟質発泡樹脂からなるクッション層と、前記クッション層の上に配置され、模様が印刷されてなる印刷層と、前記印刷層の上に配置され、樹脂材料からなるとともに、光透過性を有する表面層と、が積層されてなる。 A floor sheet according to an aspect of the present invention is a floor sheet that is attached to or placed on a floor foundation of a building, and is disposed on the floor foundation, and includes a cushion layer made of a soft foam resin, A print layer disposed on the cushion layer and printed with a pattern, and a surface layer disposed on the print layer and made of a resin material and having light transmittance are laminated.

上記態様に係る床用シートでは、軟質発泡樹脂からなるクッション層を含んでいるので、衝撃吸収性および断熱性に優れる。よって、床用シートを貼付または載置した床では、その上を歩く人が転倒したり、物を落としたりしたような場合でも床用シートで衝撃を吸収することができる。 Since the floor sheet according to the above aspect includes a cushion layer made of a soft foamed resin, it is excellent in impact absorption and heat insulation. Therefore, on the floor on which the floor sheet is stuck or placed, even if a person walking on the floor falls or drops an object, the floor sheet can absorb the impact.

また、床下地に床用シートを貼付または載置した場合には、仮に床下地が冷えているような場合にも、その上に居る人が冷たく感じるのを緩和することができる。 In addition, when a floor sheet is affixed or placed on the floor foundation, even if the floor foundation is cold, it is possible to alleviate the feeling of a person on the floor feeling cold.

また、上記態様に係る床用シートでは、印刷層を表面層の下に配設しているので、上に居る人が表面層を通して印刷層で構成された模様を見た場合に、立体感のある高い意匠性を感じることができる。 Further, in the floor sheet according to the above aspect, since the printed layer is disposed under the surface layer, when a person on the top sees a pattern composed of the printed layer through the surface layer, the three-dimensional effect is obtained. A certain high design property can be felt.

従って、上記態様に係る床用シートでは、建築物の床に衝撃吸収性および断熱性を付与することができるとともに、高い意匠性を備える。 Therefore, the floor sheet according to the above aspect can impart impact absorbability and heat insulation to the floor of the building, and has high design properties.

本発明の別態様に係る床用シートは、上記態様において、前記印刷層は、光透過性を有する基材と、当該基材の上面に形成され、前記模様を構成するインク膜と、前記基材の下面に形成され、前記クッション層と前記表面層との間の光の透過を抑制する隠蔽膜と、を有する。 The floor sheet according to another aspect of the present invention is the above-described aspect, wherein the printed layer includes a base material having light permeability, an ink film formed on an upper surface of the base material, and constituting the pattern, and the base. And a concealing film that is formed on a lower surface of the material and suppresses light transmission between the cushion layer and the surface layer.

上記態様に係る床用シートは、印刷層が基材とインク膜と隠蔽膜とからなる構成となっている。そして、隠蔽膜がクッション層と表面層との間の光の透過を抑制する機能を有する膜であるので、クッション層の色（例えば、黄色）が表面層の上からは見えないようになっている。よって、上記態様に係る床用シートでは、より優れた意匠性を実現することができる。 The floor sheet according to the above aspect has a configuration in which the printing layer includes a base material, an ink film, and a concealing film. And since the masking film is a film having a function of suppressing the transmission of light between the cushion layer and the surface layer, the color (for example, yellow) of the cushion layer cannot be seen from above the surface layer. Yes. Therefore, in the floor sheet according to the above aspect, more excellent design properties can be realized.

また、上記態様に係る床用シートでは、インク膜が基材の上面に形成されているので、インク膜がともに光透過性を有する基材と表面層とで上下を挟まれた構成となっている。これより、上記態様に係る床用シートでは、インク膜で構成された模様が浮いたように見え、より立体的な印象を与えることができる。よって、上記態様に係る床用シートでは、より高い意匠性を実現することができる。 Further, in the floor sheet according to the above aspect, since the ink film is formed on the upper surface of the base material, the ink film has a structure in which the upper and lower sides are sandwiched between the light-transmitting base material and the surface layer. Yes. As a result, in the floor sheet according to the above aspect, the pattern composed of the ink film appears to float, and a three-dimensional impression can be given. Therefore, in the floor sheet according to the above aspect, higher designability can be realized.

本発明の別態様に係る床用シートは、上記態様において、前記隠蔽膜は、白色または銀色の膜であって、前記基材における下面の全面に形成されている。 In the floor sheet according to another aspect of the present invention, in the above aspect, the masking film is a white or silver film, and is formed on the entire lower surface of the base material.

上記態様に係る床用シートでは、隠蔽膜を白色または銀色の膜で構成することとしているので、クッション層の色味が表面層側から見えるのを確実に抑制することができ、基材の上面に形成されたインク膜の模様がより高い意匠性を以って表面層の上に居る人に見せることが可能である。 In the floor sheet according to the above aspect, since the concealing film is composed of a white or silver film, the color of the cushion layer can be reliably suppressed from being seen from the surface layer side, and the upper surface of the base material The pattern of the ink film formed on the surface layer can be shown to a person on the surface layer with a higher design.

本発明の別態様に係る床用シートは、上記態様において、前記表面層は、その上面に、上方に向けて突出した複数の山部と、当該複数の山部同士の間に設けられた溝部と、を有しており、前記複数の山部のぞれぞれは、中央部分に頂を有し、当該頂部から前記溝部に向けて突出高さが低くなるように形成されている。 The floor sheet according to another aspect of the present invention is the above-described aspect, wherein the surface layer has a plurality of ridges protruding upward on the upper surface and a groove provided between the ridges. And each of the plurality of peak portions has a top at a central portion, and is formed so that the protruding height decreases from the top toward the groove portion.

上記態様に係る床用シートでは、表面層が複数の山部と溝部とを有する構成としているので、表面層における山部の上に水分や埃が残り難い。よって、上記態様に係る床用シートは、上に居る人が触れる山部に水分や埃が残るのを少なくすることができる。 In the floor sheet according to the above aspect, since the surface layer has a plurality of ridges and grooves, moisture and dust hardly remain on the ridges in the surface layer. Therefore, the floor sheet according to the aspect described above can reduce moisture and dust from remaining on the mountain portion touched by the person on the floor.

本発明の別態様に係る床用シートは、上記態様において、前記表面層を平面視するとき、前記溝部は、前記表面層の外縁辺まで繋がる状態で形成されている。 In the above aspect, the floor sheet according to another aspect of the present invention is formed in a state where the groove portion is connected to the outer edge of the surface layer when the surface layer is viewed in plan.

上記態様に係る床用シートでは、溝部が表面層の外縁辺まで繋がる状態で形成されているので、溝部に入った水分や埃を溝部を通して床用シートから排出することができる。よって、上記態様に係る床用シートは、溝部に入った水分や埃を清掃し易い。 In the floor sheet according to the above aspect, since the groove portion is formed in a state of being connected to the outer edge of the surface layer, moisture and dust that have entered the groove portion can be discharged from the floor sheet through the groove portion. Therefore, the floor sheet according to the above aspect is easy to clean the moisture and dust that have entered the groove.

本発明の別態様に係る床用シートは、上記態様において、前記溝部は、前記平面視で格子状に形成されている。 In the floor sheet according to another aspect of the present invention, the groove is formed in a lattice shape in the plan view.

上記態様に係る床用シートでは、格子状に形成された溝部を有するので、山部の面上に水分や埃が付着しても、周囲の溝部に排除することが容易となる。 Since the floor sheet according to the above aspect has the grooves formed in a lattice shape, even if moisture or dust adheres to the surface of the ridges, it is easy to exclude the surrounding grooves.

本発明の別態様に係る床用シートは、上記態様において、前記印刷層における前記模様は、御影石調の模様、グリッドタイル調の模様、ガラスモザイク調の模様、ファブリック調の模様、グリッド調の模様の何れかの模様であって、前記溝部に沿う線部を有する。 The floor sheet according to another aspect of the present invention is the above aspect, wherein the pattern in the printed layer is a granite pattern, a grid tile pattern, a glass mosaic pattern, a fabric pattern, a grid pattern And has a line portion along the groove.

上記態様に係る床用シートでは、印刷層における模様が、溝部に沿う線部を有しているので、当該床用シートの上に居る人に対して表面層に設けられた溝部を目立ちにくくすることができる。よって、上記態様に係る床用シートでは、さらに優れた意匠性を実現するのに優位である。 In the floor sheet according to the above aspect, since the pattern in the printed layer has a line part along the groove part, the groove part provided in the surface layer is less noticeable to a person who is on the floor sheet. be able to. Therefore, the floor sheet according to the above aspect is superior in realizing further excellent design properties.

なお、本発明の上記態様に係る床用シートでは、前記基材は、前記表面層を構成する前記樹脂材料と同種の樹脂材料からなる、とすることができる。これは、印刷層で構成される模様によっては、間にインク膜を介さず、基材と表面層とが接する領域が存在する場合が生じ得る場合がある。このような場合において、基材と表面層とを同種の樹脂材料から構成することとすれば、上記のような基材と表面層とが直接接しているような領域において、光の屈折や反射を抑制することができる。よって、上記態様に係る床用シートでは、さらに高い意匠性を実現することができる。 In the floor sheet according to the above aspect of the present invention, the base material can be made of the same kind of resin material as the resin material constituting the surface layer. This may occur depending on the pattern composed of the print layer, where there is a region where the substrate and the surface layer are in contact with each other without an ink film interposed therebetween. In such a case, if the base material and the surface layer are made of the same kind of resin material, the light is refracted and reflected in the region where the base material and the surface layer are in direct contact with each other. Can be suppressed. Therefore, in the floor sheet according to the above aspect, higher designability can be realized.

上記の各態様に係る床用シートは、建築物の床に衝撃吸収性および断熱性を付与することができるとともに、高い意匠性を備える。 The floor sheet according to each aspect described above can impart impact absorbability and heat insulation to the floor of a building, and has high design properties.

実施形態１に係る床用シートを採用した浴室の構成を示す模式斜視図である。It is a model perspective view which shows the structure of the bathroom which employ | adopted the sheet | seat for floors concerning Embodiment 1. FIG. 図１のＡ部を拡大して示す模式平面図である。It is a schematic plan view which expands and shows the A section of FIG. 図２のＩＩＩ−ＩＩＩ断面を示す模式断面図である。It is a schematic cross section which shows the III-III cross section of FIG. 床用シートにおける表面層の構成を示す模式平面図である。It is a schematic plan view which shows the structure of the surface layer in a sheet | seat for floors. 床用シートにおける印刷層の構成を示す模式断面図である。It is a schematic cross section which shows the structure of the printing layer in a sheet | seat for floors. 床用シートに対して光が入射した場合の光路を示す模式図である。It is a schematic diagram which shows the optical path when light injects with respect to the sheet | seat for floors. 実施形態２に係る床用シートの構成の内、表面層の構成を示す模式断面図である。It is a schematic cross section which shows the structure of a surface layer among the structures of the floor sheet which concerns on Embodiment 2. FIG. 実施形態３に係る床用シートの構成を示す模式断面図である。It is a schematic cross section which shows the structure of the sheet | seat for floors concerning Embodiment 3. FIG.

以下では、本発明の実施形態について、図面を参酌しながら説明する。なお、以下で説明の形態は、本発明の一態様であって、本発明は、その本質的な構成を除き何ら以下の形態に限定を受けるものではない。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. The form described below is one embodiment of the present invention, and the present invention is not limited to the following form except for the essential configuration.

以下の説明で用いる図面においては、Ｚ方向が鉛直上下方向であり、Ｘ方向およびＹ方向が水平方向である。 In the drawings used in the following description, the Z direction is the vertical vertical direction, and the X direction and the Y direction are horizontal directions.

［実施形態１］
１．浴室１の構成
本実施形態に係る浴室１の構成について、図１を用いて説明する。 [Embodiment 1]
1. Configuration of Bathroom 1 The configuration of the bathroom 1 according to the present embodiment will be described with reference to FIG.

図１に示すように、浴室１には、浴槽２が設置されており、その外側に浴室床３が広がっている。浴室１の壁側には、カラン４およびシャワーヘッド５が設けられている。 As shown in FIG. 1, a bathtub 1 is installed in the bathroom 1, and a bathroom floor 3 spreads outside thereof. On the wall side of the bathroom 1, a currant 4 and a shower head 5 are provided.

また、浴室床３の隅部分には、排水孔６が配設されている。そして、浴室床３には、排水孔６に繋がる排水溝６ａ，６ｂが設けられている。排水孔６は、蓋７で塞がれている。浴室１において、浴室床３の湯水は、排水溝６ａ，６ｂを通り、排水孔６から排水管へと排出される。 In addition, drain holes 6 are provided at the corners of the bathroom floor 3. The bathroom floor 3 is provided with drain grooves 6a and 6b connected to the drain holes 6. The drain hole 6 is closed with a lid 7. In the bathroom 1, hot water from the bathroom floor 3 passes through the drain grooves 6a and 6b and is discharged from the drain hole 6 to the drain pipe.

２．浴室床３の構成
浴室床３の構成について、図２および図３を用いて説明する。図２は、図１のＡ部を拡大した模式平面図であり、図３は、図２のＩＩＩ−ＩＩＩ断面を示す模式断面図である。 2. Configuration of Bathroom Floor 3 The configuration of the bathroom floor 3 will be described with reference to FIGS. 2 and 3. FIG. 2 is an enlarged schematic plan view of a portion A in FIG. 1, and FIG. 3 is a schematic sectional view showing a III-III section in FIG.

図２に示すように、浴槽床３を平面視するとき（図１における上側から平面視するとき）、浴室床３には、Ｘ方向およびＹ方向の各方向に複数の濃色模様部３ａと複数の淡色模様部３ｂとが互いに重なり合う状態で設けられている。本実施形態に係る浴槽床３に描かれている模様は、全体として御影石調の模様となっている。 As shown in FIG. 2, when the bathtub floor 3 is viewed in plan (when viewed from the top in FIG. 1), the bathroom floor 3 has a plurality of dark pattern portions 3 a in each direction of the X direction and the Y direction. The plurality of light color pattern portions 3b are provided so as to overlap each other. The pattern drawn on the bathtub floor 3 according to the present embodiment is a granite-like pattern as a whole.

図２に示すように、本実施形態では、一例として、濃色模様部３ａおよび淡色模様部３ｂがともに矩形状をしている。そして、濃色模様部３ａの外縁辺３ｃおよび淡色模様部３ｂの外縁辺３ｅは、ともにＸ方向に延びている。また、濃色模様部３ａの外縁辺３ｄおよび淡色模様部３ｂの外縁辺３ｆは、ともにＹ方向に延びている。 As shown in FIG. 2, in the present embodiment, as an example, both the dark color pattern portion 3a and the light color pattern portion 3b are rectangular. The outer edge side 3c of the dark color pattern portion 3a and the outer edge side 3e of the light color pattern portion 3b both extend in the X direction. Further, the outer edge side 3d of the dark color pattern portion 3a and the outer edge side 3f of the light color pattern portion 3b both extend in the Y direction.

なお、複数の濃色模様部３ａおよび複数の淡色模様部３ｂとで構成される模様は、後述する印刷層３１に形成された模様であり、両模様部３ａ，３ｂが存在しない領域も、より淡色の色彩が施されている。 The pattern composed of the plurality of dark color pattern portions 3a and the plurality of light color pattern portions 3b is a pattern formed on the print layer 31 described later, and an area where both the pattern portions 3a and 3b do not exist is more Light color is given.

次に、図３に示すように、浴室床３は、床下地９とその上に貼付された床用シート３５とから構成されている。床下地９に対する床用シート３５の貼付には、接着剤が用いられている。図１に示したように、床用シート３５は、蓋７の上にあたる部分が切り欠かれている（切欠き部３５ａ）。 Next, as shown in FIG. 3, the bathroom floor 3 is composed of a floor base 9 and a floor sheet 35 affixed thereon. An adhesive is used to attach the floor sheet 35 to the floor base 9. As shown in FIG. 1, the floor sheet 35 is cut out at a portion corresponding to the lid 7 (cutout portion 35 a).

床用シート３５は、Ｚ方向の下側（床下地９の側）から順に、クッション層３０と印刷層３１と表面層３２とが積層されてなる。床用シート３５のＺ方向の厚み寸法は、一例として、４．０ｍｍである。 The floor sheet 35 is formed by laminating a cushion layer 30, a print layer 31, and a surface layer 32 in order from the lower side in the Z direction (the floor base 9 side). The thickness dimension in the Z direction of the floor sheet 35 is 4.0 mm as an example.

クッション層３０は、軟質発泡樹脂から形成されている。表面層３２は、光透過性を有し、熱可塑性樹脂（例えば、ポリ塩化ビニル）から構成されている。 The cushion layer 30 is formed from a soft foamed resin. The surface layer 32 has optical transparency and is made of a thermoplastic resin (for example, polyvinyl chloride).

なお、本実施形態では、表面層３２の可視光透過率を、一例として６０％以上の範囲、より望ましくは６５％以上の範囲としている。 In the present embodiment, the visible light transmittance of the surface layer 32 is, for example, in the range of 60% or more, and more preferably in the range of 65% or more.

３．表面層３２の構成
次に、表面層３２の構成について、図３および図４を用いて説明する。図４は、表面層３２の一部をＺ方向上側から平面視した模式平面図である。 3. Configuration of Surface Layer 32 Next, the configuration of the surface layer 32 will be described with reference to FIGS. 3 and 4. FIG. 4 is a schematic plan view of a part of the surface layer 32 as viewed from above in the Z direction.

図３に示すように、表面層３２の上面は、上向きに突出した複数の山部３２ａと、複数の山部３２ａ同士の間に設けられた溝部３２ｂと、を有する。図４に示すように、複数の山部３２ａは、Ｘ方向およびＹ方向の双方向において、溝部３２ｂを間に挟んで配列されており、平面視でマトリクス状に配置されている。 As shown in FIG. 3, the upper surface of the surface layer 32 has a plurality of peak portions 32a protruding upward, and a groove portion 32b provided between the plurality of peak portions 32a. As shown in FIG. 4, the plurality of peak portions 32a are arranged with the groove portions 32b interposed therebetween in both directions of the X direction and the Y direction, and are arranged in a matrix in a plan view.

溝部３２ｂは、表面層３２のＺ方向上側の部分において、Ｘ方向およびＹ方向の双方向において、表面層３２の外縁辺まで繋がった状態で形成されている。即ち、溝部３２ｂは、図１の排水溝６ａ，６ｂに繋がるように線状に形成されている。また、本実施形態に係る溝部３２ｂは、平面視において、全体として格子状をなすよう形成されている。 The groove part 32b is formed in a state of being connected to the outer edge of the surface layer 32 in both the X direction and the Y direction at the upper part of the surface layer 32 in the Z direction. That is, the groove 32b is formed in a linear shape so as to be connected to the drain grooves 6a and 6b in FIG. Moreover, the groove part 32b which concerns on this embodiment is formed so that a grid | lattice form may be made as a whole in planar view.

なお、各山部３２ａにおけるＹ方向の長さ寸法Ｌ_１およびＸ方向の長さ寸法Ｌ_３は、一例として３０ｍｍである。また、溝部３２ｂにおけるＹ方向の幅寸法Ｌ_２およびＸ方向の幅寸法Ｌ_４は、一例として５ｍｍである。 Note that the length dimension _{L 1} and X direction length _{L 3} in the Y direction at each peak portion 32a is 30mm as an example. Also, the width _{L 4} of the width dimension in the Y direction in the groove 32 b _{L 2} and X direction is 5mm as an example.

図３および図４に示すように、山部３２ａは、中央部分の山部頂部３２ｄからＸ方向およびＹ方向の周辺部分に向けて形成された斜面部３２ｃとで構成されている。 As shown in FIGS. 3 and 4, the peak portion 32 a is configured by a slope portion 32 c formed from the peak portion 32 d of the central portion toward the peripheral portion in the X direction and the Y direction.

一方、溝部３２ｂは、Ｘ方向およびＹ方向の双方向に平坦な溝部底面部３２ｅと、溝部底面部３２ｅと山部３２ａの斜面部３２ｃとの間に設けられた溝部斜面部３２ｆとが連続するように設けられている。 On the other hand, the groove 32b has a groove bottom surface 32e that is flat in both the X and Y directions, and a groove slope 32f provided between the groove bottom 32e and the slope 32c of the peak 32a. It is provided as follows.

ここで、図３のＢ部に拡大して示すように、斜面部３２ｃと溝部斜面部３２ｆとの境界部分である角部３２ｇは、曲面を以って構成されている。同じように、図３のＣ部に拡大して示すように、溝部底面部３２ｅと溝部斜面部３２ｆとの境界部分である角部３２ｈも、曲面を以って構成されている。 Here, as shown in an enlarged view in part B of FIG. 3, the corner part 32g, which is a boundary part between the slope part 32c and the groove part slope part 32f, is configured with a curved surface. Similarly, as shown in an enlarged view in part C of FIG. 3, the corner part 32h, which is a boundary part between the groove bottom surface part 32e and the groove sloped surface part 32f, is also configured with a curved surface.

なお、本実施形態では、角部３２ｇおよび角部３２ｈの曲率半径を、一例としてＲ０．５ｍｍとしている。 In the present embodiment, the radius of curvature of the corner portion 32g and the corner portion 32h is set to R 0.5 mm as an example.

また、図３に示すように、本実施形態では、Ｚ方向における山部頂部３２ｄから角部３２ｇまでの高さ寸法Ｔ_１を、一例として０．５ｍｍとしている。同様に、Ｚ方向における角部３２ｇから溝部底面部３２ｅまでの高さ寸法Ｔ_２を、一例として０．５ｍｍとしている。 Further, as shown in FIG. 3, in this embodiment, the height T ₁ of the the crest apex 32d in the Z-direction to the corner portion 32g, is set to 0.5mm as one example. Similarly, the height _{T 2} of the from the corner portion 32g in the Z direction to the groove bottom portion 32e, is set to 0.5mm as one example.

図４に示すように、山部３２ａの外縁辺３２ｉ（図３の角部３２ｇに相当）は、上述のように、Ｘ方向およびＹ方向の長さ寸法Ｌ_１，Ｌ_３がともに３０ｍｍの正方形の山部３２ａを規定している。そして、詳しい図示を省略しているが、本実施形態では、平面視における山部３２ａの角部３２ｊについても、曲面を以って構成されている。角部３２ｊの曲率半径も、一例としてＲ０．５ｍｍとしている。 As shown in FIG. 4, the outer edge 32i of the peak portion 32a (corresponding to the corner portion 32g in FIG. 3) is a square whose length dimensions L ₁ and L ₃ in the X and Y directions are both 30 mm as described above. Is defined. And although detailed illustration is abbreviate | omitted, in this embodiment, also about the corner | angular part 32j of the peak part 32a in planar view, it is comprised with the curved surface. As an example, the radius of curvature of the corner 32j is set to R 0.5 mm.

なお、図４では、印刷層３１の模様を表していないが、本実施形態では、濃色模様部３ａの外縁辺３ｃ，３ｄおよび淡色模様部３ｂの外縁辺３ｅ，３ｆが、山部３２ａの外縁辺３２ｉ（溝部３２ｂの幅方向縁辺）に沿うように形成されている。即ち、床用シート３５では、平面視における模様の各模様部３ａ，３ｂの外縁辺３ｃ，３ｅがＸ方向に延び、外縁辺３ｄ，３ｆが、Ｙ方向に延びるように模様が形成されているので、Ｘ方向およびＹ方向に延びる各山部３２ａの外縁辺３２ｉに沿うようになっている。 In FIG. 4, the pattern of the print layer 31 is not shown. However, in the present embodiment, the outer edge sides 3c and 3d of the dark color pattern portion 3a and the outer edge sides 3e and 3f of the light color pattern portion 3b are the peaks 32a. It is formed along the outer edge 32i (the edge in the width direction of the groove 32b). That is, in the floor sheet 35, the pattern is formed so that the outer edge sides 3c and 3e of the pattern portions 3a and 3b in the plan view extend in the X direction and the outer edge sides 3d and 3f extend in the Y direction. Therefore, it comes to follow the outer edge 32i of each peak part 32a extended in a X direction and a Y direction.

４．印刷層３１の構成
印刷層３１の構成について、図５を用いて説明する。図５は、印刷層３１の構成を示す模式断面図である。 4). Configuration of Print Layer 31 The configuration of the print layer 31 will be described with reference to FIG. FIG. 5 is a schematic cross-sectional view showing the configuration of the print layer 31.

図５に示すように、印刷層３１は、光透過性を有し、熱可塑性樹脂（例えば、ポリ塩化ビニル）からなる基材３１０と、基材３１０のＺ方向上側に形成されたインク膜３１１と、基材３１０のＺ方向下側に形成された隠蔽膜３１２と、からなる。 As shown in FIG. 5, the printing layer 31 has a light-transmitting property, a base material 310 made of a thermoplastic resin (for example, polyvinyl chloride), and an ink film 311 formed on the upper side of the base material 310 in the Z direction. And a masking film 312 formed on the lower side of the base material 310 in the Z direction.

基材３１０におけるＺ方向の厚み寸法Ｔ_３は、一例として０．１ｍｍである。インク膜３１１の厚み寸法Ｔ_４および隠蔽膜３１２の厚み寸法Ｔ_５は、ともに１０μｍ以下、望ましくは１μｍ以下である。 Thickness _{T 3} in the Z direction in the substrate 310 is 0.1mm, for example. Thickness _{T 5} of the thickness _{T 4} and hiding film 312 of the ink film 311 are both 10μm or less, preferably is 1μm or less.

ここで、本実施形態では、基材３１０の可視光透過率を、一例として８５％以上、望ましくは８８％以上としている。 Here, in this embodiment, the visible light transmittance of the base material 310 is 85% or more, desirably 88% or more, as an example.

本実施形態では、一例として、基材３１０に対して白色塗料をベタ塗りして隠蔽膜３１２を形成している。このため、隠蔽膜３１２が形成された基材３１０の可視光透過率を、一例として５５％以下、望ましくは５０％以下となる。 In the present embodiment, as an example, a solid paint is applied to the base material 310 to form the concealment film 312. For this reason, the visible light transmittance of the base material 310 on which the concealing film 312 is formed is 55% or less, desirably 50% or less, as an example.

５．床用シート３５に入射した可視光Ｒ_１，Ｒ_２の光路
上記のような構成を有する床用シート３５に対して、Ｚ方向上側から入射した可視光Ｒ_１，Ｒ_２の光路について、図６を用いて説明する。図６は、床用シート３５に入射した可視光Ｒ_１，Ｒ_２の光路を示す模式図である。 5). Optical Paths of Visible Light R ₁ and R ₂ Incident to Floor Sheet 35 Regarding the optical paths of visible lights R ₁ and R ₂ incident on the floor sheet 35 having the above-described configuration from above in the Z direction, FIG. Will be described. FIG. 6 is a schematic diagram showing optical paths of visible light R ₁ and R ₂ that have entered the floor sheet 35.

図６に示すように、浴室１において、可視光Ｒ_１，Ｒ_２は、Ｚ方向上側から入射する。入射した可視光Ｒ_１，Ｒ_２のうちの可視光Ｒ_１は、表面層３２を厚み方向（Ｚ方向）に進み、インク膜３１１の上側面３１１ａで反射して表面層３２をＺ方向上側に抜けて行く。これにより、浴室１に居る人は、印刷層３１に形成された模様（本実施形態では、一例として御影石調の模様）を見ることができる。 As shown in FIG. 6, in the bathroom 1, visible light R ₁ and R ₂ are incident from the upper side in the Z direction. Visible light _{R 1} of the incident visible light _R 1, _{R 2} proceeds the surface layer 32 in the thickness direction (Z-direction), the surface layer 32 is reflected by the upper surface 311a of the ink film 311 in the Z direction upward Go through. Thereby, the person who is in the bathroom 1 can see the pattern (in this embodiment, a granite tone pattern as an example) formed in the printing layer 31.

一方、入射した可視光Ｒ_１，Ｒ_２のうちの可視光Ｒ_２は、インク膜３１１をＺ方向下側に透過し、隠蔽膜３１２の上側面３１２ａで反射される。そして、上側面３１２ａで反射された可視光Ｒ_２は、インク膜３１１および表面層３２を透過してＺ方向上側に抜けて行く。これによっても、浴室１に居る人は、印刷層３１に形成された模様を見ることができる。 On the other hand, visible light _{R 2} of the visible light _R 1, _{R 2} The incident ink film 311 passes through the Z direction downward, is reflected by the upper surface 312a of the concealing layer 312. Then, the visible light R ₂ reflected by the upper side surface 312 a passes through the ink film 311 and the surface layer 32 and escapes upward in the Z direction. Also by this, the person in the bathroom 1 can see the pattern formed on the printed layer 31.

さらに、本実施形態に係る床用シート３５では、基材３１０のＺ方向下側、即ち、クッション層３０の上に隠蔽膜３１２を形成しているので、例えばクッション層３０が黄色みを帯びているような場合にも、可視光Ｒ２がクッション層３０まで到達し反射してくることが抑制されるので、クッション層３０の色が可視光Ｒ_１，Ｒ_２の色度や印刷層３１の模様などに影響を与え難い。 Further, in the floor sheet 35 according to the present embodiment, since the concealment film 312 is formed on the lower side in the Z direction of the base material 310, that is, on the cushion layer 30, for example, the cushion layer 30 is yellowish. Even in such a case, since the visible light R2 reaches the cushion layer 30 and is reflected, the color of the cushion layer 30 is changed to the chromaticity of the visible lights R ₁ and R ₂ and the pattern of the printing layer 31. It is hard to affect.

６．各部位に用いる材料の例
床用シート３５を構成する各部位に用いる材料としては、例えば、次のような材料をあげることができる。 6). Examples of materials used for each part Examples of materials used for each part constituting the floor sheet 35 include the following materials.

（１）クッション層３０
塩化ビニル樹脂、可塑剤および化学発泡剤を含有する塩化ビニル発泡シートを採用することができる。 (1) Cushion layer 30
A vinyl chloride foam sheet containing a vinyl chloride resin, a plasticizer and a chemical foaming agent can be employed.

なお、塩化ビニル樹脂としては、ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体樹脂、塩化ビニル−エチレン共重合体樹脂、ポリエチレン樹脂、ポリプロピレン樹脂、ＥＶＡ樹脂などを採用することができる。 As the vinyl chloride resin, polyvinyl chloride, vinyl chloride-vinyl acetate copolymer resin, vinyl chloride-ethylene copolymer resin, polyethylene resin, polypropylene resin, EVA resin, or the like can be used.

また、可塑剤としては、フタル酸ジ−ｎ−オクチル、フタル酸−２−エチルヘキシル、アジピン酸ジイソノニル、アジピン酸ジイソデシルのようなニ塩基酸エステル系可塑剤、トリ−２−エチルヘキシルホスファイト、イソデシルジフェニルホスファイト、トリクレジルホスファイトのようなリン酸エステル系可塑剤、塩素化パラフィン、ポリエステル系可塑剤をあげることができる。これらは単独で、あるいは２種類以上を組み合わせて用いることができる。 Plasticizers include di-n-octyl phthalate, 2-ethylhexyl phthalate, diisononyl adipate, and dibasic acid ester plasticizers such as diisodecyl adipate, tri-2-ethylhexyl phosphite, isodecyl. Examples thereof include phosphate plasticizers such as diphenyl phosphite and tricresyl phosphite, chlorinated paraffins, and polyester plasticizers. These can be used alone or in combination of two or more.

また、化学発泡剤としては、熱分解型有機発泡剤が使用される。具体的には、例えば、アゾジカルボンアミド、アゾビスイソブチロニトリル、ベンゼンスルホニルホドラジド、ｐ−トルエンスルホニルヒドラジド、ジニトロソペンタメチレンテトラミン等を挙げることができる。 As the chemical foaming agent, a pyrolytic organic foaming agent is used. Specific examples include azodicarbonamide, azobisisobutyronitrile, benzenesulfonyl hydrazide, p-toluenesulfonyl hydrazide, dinitrosopentamethylenetetramine, and the like.

さらに、本実施形態の塩化ビニル発泡シートには、上記以外に、カルボン酸亜鉛塩およびカルボン酸縮合物の部分エステル化合物のうち少なくとも１つが含まれていることが好ましい。好ましくは、カルボン酸亜鉛塩およびカルボン酸縮合物の部分エステル化合物の両方が含有される。 Furthermore, in addition to the above, the vinyl chloride foam sheet of this embodiment preferably contains at least one of a carboxylic acid zinc salt and a partial ester compound of a carboxylic acid condensate. Preferably, both the carboxylic acid zinc salt and the partial ester compound of the carboxylic acid condensate are contained.

塩化ビニル発泡シートに用いることができるカルボン酸亜鉛塩としては、例えば、カルボン酸亜鉛正塩、塩基性カルボン酸亜鉛塩、並びにカルボン酸亜鉛正塩及び過塩基性カルボン酸亜鉛塩の混合物挙げることができる。なかでも好ましいカルボン酸亜鉛塩は、カルボン酸２モルに対し酸化亜鉛１モルを反応して得られるカルボン酸正塩と、カルボン酸に対し過剰の酸化亜鉛を反応させることで得られる塩基性カルボン酸亜塩の混合物からなるものである。 Examples of the zinc carboxylate salt that can be used for the vinyl chloride foam sheet include a zinc carboxylate normal salt, a basic carboxylate zinc salt, and a mixture of a zinc carboxylate normal salt and an overbased zinc carboxylate salt. it can. Of these, preferred carboxylic acid zinc salts are basic carboxylic acids obtained by reacting 2 mol of carboxylic acid with 1 mol of zinc oxide and reacting 1 mol of zinc oxide with excess zinc oxide with respect to carboxylic acid. It consists of a mixture of subsalts.

（２）表面層３２
表面層３２は、上述のように、床用シート３５における化粧層として機能する層であり、熱可塑性樹脂で構成される。 (2) Surface layer 32
As described above, the surface layer 32 is a layer that functions as a decorative layer in the floor sheet 35 and is made of a thermoplastic resin.

熱可塑性樹脂としては、特に限定はされないが、例えば、塩化ビニル樹脂、アクリル樹脂、ポリエチレン樹脂、ポリプロピレン樹脂、ＥＶＡ樹脂などのポリオレフィン樹脂、ポリエチレンテレフタレート樹脂などのポリエステル系樹脂等を使用することができる。なかでも、塩化ビニル樹脂は、加工性、作業性という観点から好ましく用いられる。 Although it does not specifically limit as a thermoplastic resin, For example, polyester resins, such as polyolefin resin, such as a vinyl chloride resin, an acrylic resin, a polyethylene resin, a polypropylene resin, EVA resin, a polyethylene terephthalate resin, etc. can be used. Among these, vinyl chloride resin is preferably used from the viewpoint of processability and workability.

塩化ビニル樹脂としては、ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体樹脂、塩化ビニル−エチレン共重合体樹脂等が挙げられる。 Examples of the vinyl chloride resin include polyvinyl chloride, vinyl chloride-vinyl acetate copolymer resin, vinyl chloride-ethylene copolymer resin, and the like.

また、前記熱可塑性樹脂には可塑剤や充填剤等の添加剤を加えてもよい。 Moreover, you may add additives, such as a plasticizer and a filler, to the said thermoplastic resin.

可塑剤としては、例えば、フタル酸ジ−ｎ−オクチル、フタル酸ジ−２−エチルヘキシル、フタル酸ジイソオクチル、フタル酸イソヘプチル、フタル酸ジイソノニル、フタル酸ジイソデシルのようなフタル酸エステル系可塑剤、トリ−２−エチルヘキシルトリメリット酸のようなトリメリット酸エステル系可塑剤、アジピン酸ジ−２−エチルヘキシル、アジピン酸ジイソノニル、アジピン酸ジイソデシルのようなニ塩基酸エステル系可塑剤、トリ−２−エチルヘキシルホスファイト、イソデシルジフェニルホスファイト、トリクレジルホスファイトのようなリン酸エステル系可塑剤、塩素化パラフィン、ポリエステル系可塑剤をあげることができる。これらは単独で、あるいは２種類以上を組み合わせて用いることができる。 Examples of the plasticizer include phthalate plasticizers such as di-n-octyl phthalate, di-2-ethylhexyl phthalate, diisooctyl phthalate, isoheptyl phthalate, diisononyl phthalate, diisodecyl phthalate, tri- Trimellitic acid ester plasticizers such as 2-ethylhexyl trimellitic acid, dibasic acid ester plasticizers such as di-2-ethylhexyl adipate, diisononyl adipate, diisodecyl adipate, tri-2-ethylhexyl phosphite And phosphoric ester plasticizers such as isodecyl diphenyl phosphite and tricresyl phosphite, chlorinated paraffins, and polyester plasticizers. These can be used alone or in combination of two or more.

充填剤は強度を付与するために光透過性を阻害しない範囲で必要に応じて添加されるが、その具体例としては、炭酸カルシウム、炭酸マグネシウム、硫酸カルシウム、酸化カルシウム、酸化チタン、水酸化アルミ、クレー、シリカ等挙げることができる。 Fillers are added as necessary within a range that does not impair the light transmission to give strength. Specific examples thereof include calcium carbonate, magnesium carbonate, calcium sulfate, calcium oxide, titanium oxide, and aluminum hydroxide. , Clay, silica and the like.

（３）基材３１０
基材３１０には、表面層３２を構成する材料と同種の材料（樹脂材料）を用いることができる。ただし、必ずしも同種の樹脂材料を用いなくてもよい。 (3) Base material 310
For the base material 310, the same kind of material (resin material) as the material constituting the surface layer 32 can be used. However, the same kind of resin material is not necessarily used.

７．効果
本実施形態に係る床用シート３５では、軟質発泡樹脂からなるクッション層３０を含んでいるので、衝撃吸収性および断熱性に優れる。よって、床下地９に床用シート３５を貼付した床３では、その上を歩く人が転倒したり、物を落としたりしたような場合でも床用シート３５で衝撃を吸収することができる。また、床下地９に床用シート３５を貼付した場合には、仮に床下地９が冷えているような場合にも、その上に居る人が冷たく感じるのを緩和することができる。 7). Effect Since the floor sheet 35 according to the present embodiment includes the cushion layer 30 made of a soft foamed resin, the floor sheet 35 is excellent in shock absorption and heat insulation. Therefore, in the floor 3 in which the floor sheet 35 is pasted on the floor base 9, the floor sheet 35 can absorb the impact even when a person walking on the floor 3 falls or drops an object. In addition, when the floor sheet 35 is pasted on the floor base 9, even if the floor base 9 is cold, it is possible to alleviate the feeling of a person on the floor 9 feeling cold.

また、本実施形態に係る床用シート３５では、印刷層３１を表面層３２の下層（Ｚ方向下側）に配設しているので、当該床用シート３５の上に居る人は、表面層３２を通して印刷層３１で構成された模様（本実施形態では、一例として御影石調の模様）を見た場合に、立体感のある高い意匠性を感じることができる。 Further, in the floor sheet 35 according to the present embodiment, the printed layer 31 is disposed below the surface layer 32 (the lower side in the Z direction). When a pattern composed of the print layer 31 through 32 (in this embodiment, a granite-like pattern is taken as an example), a high design with a three-dimensional effect can be felt.

また、本実施形態に係る床用シート３５は、印刷層３１が基材３１０とインク膜３１１と隠蔽膜３１２とからなる構成となっている。そして、隠蔽膜３１２が白色のベタ塗りにより構成され、クッション層３０と表面層３２との間の可視光Ｒ_２の透過を抑制する機能を有する膜であるので、クッション層３０が黄色みを帯びていた場合にも、当該クッション層３０の色が表面層３２の上からは見えないようになっている。よって、本実施形態に係る床用シート３５では、より優れた意匠性を実現することができる。 Further, in the floor sheet 35 according to the present embodiment, the print layer 31 includes a base material 310, an ink film 311, and a concealing film 312. The concealment film 312 is constituted by a white solid fill, since a film having a function of suppressing the transmission of visible light R ₂ between the cushion layer 30 and the surface layer 32, the cushion layer 30 is yellowish Even in such a case, the color of the cushion layer 30 is not visible from the surface layer 32. Therefore, in the floor sheet 35 according to the present embodiment, a more excellent design can be realized.

また、本実施形態に係る床用シート３５では、インク膜３１１が基材３１０の上面に形成されているので、インク膜３１１がともに光透過性を有する基材３１０と表面層３２とで上下を挟まれた構成となっている。これより、床用シート３５では、インク膜３１１で形成された模様が浮いたように見え、より立体的な印象を与えることができる。よって、本実施形態に係る床用シート３５では、より高い意匠性を実現することができる。 In the floor sheet 35 according to this embodiment, since the ink film 311 is formed on the upper surface of the base material 310, the ink film 311 is moved up and down by the base material 310 and the surface layer 32 both having light transmittance. It has a sandwiched configuration. Thus, in the floor sheet 35, the pattern formed by the ink film 311 appears to float, and a three-dimensional impression can be given. Therefore, in the floor sheet 35 according to the present embodiment, higher designability can be realized.

また、本実施形態に係る床用シート３５では、隠蔽膜３１２を白色のベタ塗り膜（基材３１０の下面全体に形成した膜）としているので、クッション層３０の色み（例えば、黄色み）が上側から見えるのを確実に抑制することができ、基材３１０における表面層３２側に形成されたインク膜３１１の模様がより高い意匠性を以って表面層の上に居る人に見せることが可能である。 Further, in the floor sheet 35 according to the present embodiment, the concealment film 312 is a white solid coating film (a film formed on the entire lower surface of the base material 310), and thus the color of the cushion layer 30 (for example, yellow) Can be reliably suppressed from being seen from above, and the pattern of the ink film 311 formed on the surface layer 32 side of the substrate 310 is shown to a person on the surface layer with a higher design. Is possible.

なお、隠蔽膜３１２については、白色のベタ塗り膜以外にも、銀色のベタ塗り膜などの光反射膜とすることもできる。 In addition to the white solid coating film, the concealing film 312 may be a light reflection film such as a silver solid coating film.

また、本実施形態に係る床用シート３５では、表面層３２が複数の山部３２ａと溝部３２ｂとを有する構成としているので、表面層３２における山部３２ａの上（斜面部３２ｃ）に水分や埃が残り難い。そして、床用シート３５では、溝部３２ｂが表面層３２の外縁辺まで繋がる状態で形成されているので、溝部３２ｂに入った水分や埃を溝部３２ｂを通して床用シート３５から排出することができる。よって、床用シート３５は、上に居る人が触れる山部３２ａに水分や埃が残るのを少なくすることができるとともに、溝部３２ｂに入った水分や埃を清掃し易い。 Further, in the floor sheet 35 according to the present embodiment, the surface layer 32 has a plurality of peak portions 32a and groove portions 32b, and therefore moisture or moisture is formed on the peak portion 32a (slope portion 32c) in the surface layer 32. Dust hardly remains. And in the floor sheet 35, since the groove part 32b is formed in the state connected to the outer edge of the surface layer 32, the water | moisture content and dust which entered the groove part 32b can be discharged | emitted from the floor sheet 35 through the groove part 32b. Therefore, the floor sheet 35 can reduce moisture and dust from remaining on the mountain portion 32a touched by a person on the floor, and can easily clean the moisture and dust contained in the groove portion 32b.

また、本実施形態に係る床用シート３５では、表面層３２の角部３２ｇ，３２ｈ，３２ｊが曲面を以って構成されているので、上を歩いたり立ったりしている人が足裏に刺激を受け難く、また、水分や埃を溝部に落ちやすくすることができる。 Further, in the floor sheet 35 according to the present embodiment, the corners 32g, 32h, 32j of the surface layer 32 are configured with curved surfaces, so that a person who is walking or standing on the sole is on the sole. It is difficult to receive stimulation, and moisture and dust can be easily dropped into the groove.

また、本実施形態に係る床用シート３５では、表面層３２が、平面視で格子状に形成された溝部３２ｂを有するので、山部３２ａの斜面部３２ｃ上に水分や埃が付着しても、周囲の溝部３２ｂに排除することが容易となる。 Further, in the floor sheet 35 according to the present embodiment, the surface layer 32 includes the groove portions 32b formed in a lattice shape in a plan view, so that moisture or dust adheres to the slope portion 32c of the mountain portion 32a. It is easy to eliminate the peripheral groove 32b.

また、本実施形態に係る床用シート３５では、印刷層３１で形成された模様部３ａ，３ｂの外縁辺（線部）が、山部３２ａの外縁辺３２ｉ（溝部３２ｂの幅方向縁辺）に合致または沿うように構成されているので、当該床用シート３５の上に居る人に対して表面層３２の山部３２ａおよび溝部３２ｂを目立ちにくくすることができる。よって、床用シート３５では、さらに優れた意匠性を実現するのに優位である。 Further, in the floor sheet 35 according to the present embodiment, the outer edge sides (line portions) of the pattern portions 3a and 3b formed by the printing layer 31 are the outer edge sides 32i of the peak portions 32a (the width direction edges of the groove portions 32b). Since it is configured to match or follow, the peak portion 32a and the groove portion 32b of the surface layer 32 can be made inconspicuous for a person who is on the floor sheet 35. Therefore, the floor sheet 35 is superior in realizing further excellent design properties.

以上のように、本実施形態に係る床用シート３５は、建築物の床３に衝撃吸収性および断熱性を付与することができるとともに、高い意匠性を備える。 As described above, the floor sheet 35 according to the present embodiment can impart shock absorption and heat insulation to the floor 3 of the building, and has high design properties.

なお、本実施形態に係る床用シート３５では、基材３１０と表面層３３とを同種の樹脂材料である熱可塑性樹脂（例えば、ポリ塩化ビニル）を用いて形成することとしている。このため、本実施形態では、印刷層３１で構成される模様によっては、間にインク膜３１１を介さず、基材３１０と表面層３３とが接する領域が存在する場合が生じ得る場合であっても、当該領域において、光の屈折や反射を抑制することができ、さらに高い意匠性を実現することができる。 In the floor sheet 35 according to the present embodiment, the base material 310 and the surface layer 33 are formed using a thermoplastic resin (for example, polyvinyl chloride) that is the same kind of resin material. For this reason, in the present embodiment, depending on the pattern formed by the printing layer 31, there may be a case where there is a region where the substrate 310 and the surface layer 33 are in contact without the ink film 311 interposed therebetween. However, in this region, light refraction and reflection can be suppressed, and higher design properties can be realized.

［実施形態２］
実施形態２に係る床用シートの構成について、図７を用いて説明する。図７は、本実施形態に係る床用シートの構成の内、表面層３３の構成を示す模式断面図である。 [Embodiment 2]
The configuration of the floor sheet according to the second embodiment will be described with reference to FIG. FIG. 7 is a schematic cross-sectional view showing the configuration of the surface layer 33 in the configuration of the floor sheet according to the present embodiment.

なお、本実施形態に係る床用シートは、以下で説明する表面層３３の構成を除き、上記実施形態１に係る床用シート３５と同じ構成を有する。 The floor sheet according to the present embodiment has the same configuration as the floor sheet 35 according to the first embodiment except for the configuration of the surface layer 33 described below.

図７に示すように、本実施形態に係る床用シートの表面層３３も複数の山部３３ａと溝部３３ｂとをＺ方向上側部分に有する。そして、本実施形態に係る表面層３３が上記実施形態１に係る表面層３２と異なる点は、山部３３ａの形状にある。 As shown in FIG. 7, the surface layer 33 of the floor sheet according to the present embodiment also has a plurality of peak portions 33a and groove portions 33b in the upper part in the Z direction. Then, the surface layer 33 according to the present embodiment is different from the surface layer 32 according to the first embodiment in the shape of the mountain portion 33a.

具体的には、本実施形態に係る表面層３３では、山部３３ａが扁平直方体形状のブロック部３３ｃ，３３ｄ，３３ｅの積層構造を有している。ブロック部３３ｄはブロック部３３ｃよりもＸ方向およびＹ方向にサイズが大きく、ブロック部３３ｅはブロック部３３ｄよりもＸ方向およびＹ方向にサイズが大きい。 Specifically, in the surface layer 33 according to the present embodiment, the mountain portion 33a has a laminated structure of block portions 33c, 33d, and 33e having a flat rectangular parallelepiped shape. The block part 33d is larger in size in the X and Y directions than the block part 33c, and the block part 33e is larger in the X and Y directions than the block part 33d.

表面層３３の山部３３ａは、上記のような積層構造を採用することにより、中央部分からＸ方向およびＹ方向の周辺部分に向けて高さが段階的に低くなってゆくようになっている。 The peak portion 33a of the surface layer 33 adopts the laminated structure as described above, so that the height gradually decreases from the central portion toward the peripheral portion in the X direction and the Y direction. .

上記構成を有する表面層３３を備える床用シートにおいても、上記実施形態１に係る床用シート３５と同じ効果を得ることができる。 Also in the floor sheet provided with the surface layer 33 having the above configuration, the same effect as the floor sheet 35 according to the first embodiment can be obtained.

［実施形態３］
実施形態３に係る床用シート８５の構成について、図８を用いて説明する。図８は、本実施形態に係る床用シート８５の構成を示す模式断面図である。 [Embodiment 3]
The configuration of the floor sheet 85 according to the third embodiment will be described with reference to FIG. FIG. 8 is a schematic cross-sectional view showing the configuration of the floor sheet 85 according to the present embodiment.

なお、本実施形態に係る床用シート８５は、以下で説明する補強層８３を有する点を除き、上記実施形態１に係る床用シート３５と同じ構成を有する。 The floor sheet 85 according to the present embodiment has the same configuration as the floor sheet 35 according to the first embodiment, except that the floor sheet 85 includes a reinforcing layer 83 described below.

図８に示すように、床用シート８は、Ｚ方向下側から順に、クッション層３０、補強層８３、印刷層３１、および表面層３２が積層されてなる。この内、クッション層３０、印刷層３１、および表面層３２については、上記実施形態１に係る床用シート３５の各部位と同じ構成を有する。 As shown in FIG. 8, the floor sheet 8 is formed by laminating a cushion layer 30, a reinforcing layer 83, a printing layer 31, and a surface layer 32 in order from the lower side in the Z direction. Among these, the cushion layer 30, the print layer 31, and the surface layer 32 have the same configuration as each part of the floor sheet 35 according to the first embodiment.

補強層８３は、一例として、ガラス繊維を含む不織布から形成されてなる層である。Ｚ方向における補強層８３の厚み寸法は、例えば、０．３ｍｍ〜１．０ｍｍの範囲である。なお、補強層８３の厚み寸法を０．３ｍｍ未満とした場合には、必要な剛性を確保することができなくなるとともに、寸法の安定性も低下してしまう。 For example, the reinforcing layer 83 is a layer formed of a nonwoven fabric containing glass fibers. The thickness dimension of the reinforcing layer 83 in the Z direction is, for example, in the range of 0.3 mm to 1.0 mm. If the thickness dimension of the reinforcing layer 83 is less than 0.3 mm, the required rigidity cannot be ensured and the dimensional stability is also reduced.

一方、補強層８３の厚み寸法を１．０ｍｍよりも厚くした場合には、印刷層３１との接着性が低下し、耐久性を得られなくなる。 On the other hand, when the thickness dimension of the reinforcing layer 83 is thicker than 1.0 mm, the adhesiveness with the printing layer 31 is lowered, and durability cannot be obtained.

ここで、補強層８３に用いられる不織布としては、上述したようなガラス繊維を含む不織布が用いられるが、ガラス繊維だけでは引張り強度が十分でない場合があるため、ガラス繊維にポリエチレンテレフタレート（ＰＥＴ）繊維またはパルプ等を混合させた不織布を用いることが好ましい。 Here, as the nonwoven fabric used for the reinforcing layer 83, a nonwoven fabric containing glass fibers as described above is used. However, since the tensile strength may not be sufficient only with glass fibers, polyethylene terephthalate (PET) fibers are used for the glass fibers. Alternatively, it is preferable to use a nonwoven fabric mixed with pulp or the like.

なお、ガラス繊維・ＰＥＴ繊維混合不織布を用いる場合、ガラス繊維に対するＰＥＴ繊維の混合割合が４０〜７０％程度のものを用いることが好ましい。一方、ガラス繊維・パルプ混合不織布を用いる場合、ガラス繊維に対するパルプの混合割合が４０〜７０％程度のものを用いることが好ましい。 In addition, when using a glass fiber / PET fiber mixed nonwoven fabric, it is preferable to use a glass fiber / PET fiber mixing ratio of about 40 to 70%. On the other hand, when using a glass fiber / pulp mixed non-woven fabric, it is preferable to use one having a mixing ratio of pulp to glass fiber of about 40 to 70%.

さらに、補強層８３におけるＺ方向下側（クッション層３０の側）に、塩化ビニル樹脂またはアクリル樹脂を含浸させてもよい。 Further, a vinyl chloride resin or an acrylic resin may be impregnated on the lower side in the Z direction (the cushion layer 30 side) of the reinforcing layer 83.

塩化ビニル樹脂またはアクリル樹脂は、補強層８３の厚み全体に対し、３０〜７０％程度の厚みまで、前記熱可塑性樹脂を含浸させることが好ましい。３０％未満となると、充分な接着性が得られず、層間剥離が起こる可能性があり、７０％を超えると、補強層８３としての剛性が低く寸法安定性が得られなくなるため、好ましくない。 The vinyl chloride resin or acrylic resin is preferably impregnated with the thermoplastic resin to a thickness of about 30 to 70% with respect to the entire thickness of the reinforcing layer 83. If it is less than 30%, sufficient adhesion cannot be obtained and delamination may occur, and if it exceeds 70%, rigidity as the reinforcing layer 83 is low and dimensional stability cannot be obtained, which is not preferable.

塩化ビニル樹脂またはアクリル樹脂の含浸量は、塩化ビニル樹脂またはアクリル樹脂の塗工量によって調節することができる。 The impregnation amount of the vinyl chloride resin or the acrylic resin can be adjusted by the coating amount of the vinyl chloride resin or the acrylic resin.

上記構成を有する補強層８３を備える床用シート８５においても、上記実施形態１に係る床用シート３５と同じ効果を得ることができる。 Also in the floor sheet 85 including the reinforcing layer 83 having the above configuration, the same effect as the floor sheet 35 according to the first embodiment can be obtained.

［変形例］
上記実施形態１〜３では、浴室１の浴室床３に用いる床用シート３５，８５を一例に構成の説明をしたが、床用シートの用途はこれに限定を受けるものものではない。例えば、玄関土間に対して床用シートを用いることとしてもよい。なお、玄関土間に床用シートを用いる場合には、清掃時などに床用シートを外すことができるように、粘着剤などで床用シートを貼付するようにしてもよい。また、床用シートを単に載置だけにすることともできる。 [Modification]
In the first to third embodiments, the configuration of the floor sheets 35 and 85 used for the bathroom floor 3 of the bathroom 1 has been described as an example, but the use of the floor sheet is not limited thereto. For example, a floor sheet may be used between the entrance soils. In addition, when using a floor sheet between entrance soils, you may make it stick a floor sheet with an adhesive etc. so that a floor sheet can be removed at the time of cleaning. Further, the floor sheet can be simply placed.

また、上記実施形態１〜３では、インク膜３１１の形成方法については、特に言及しなかったが、種々の印刷方法を採用することができる。例えば、グラビア印刷、オフセット印刷、転写シートを用いた転写印刷、あるいはインクジェット装置を用いた印刷などを採用することができる。 In the first to third embodiments, a method for forming the ink film 311 is not particularly mentioned, but various printing methods can be employed. For example, gravure printing, offset printing, transfer printing using a transfer sheet, or printing using an inkjet device can be employed.

また、上記実施形態１〜３では、表面層３２の表面側（Ｚ方向上側）に複数の山部３２ａと溝部３２ｂとを設けることとしたが、本発明では、必ずしも山部および溝部を設けなくてもよい。 In the first to third embodiments, the plurality of peak portions 32a and the groove portions 32b are provided on the surface side (upper Z direction) of the surface layer 32. However, in the present invention, the peak portions and the groove portions are not necessarily provided. May be.

また、上記実施形態１では、表面層３２の複数の山部３２ａのそれぞれを、山部頂部３２ｄを頂点とした三角形の断面形状を有する構成としたが、本発明は、これに限定を受けるものではない。例えば、ドーム形（球面の一部を切り取ったような形状）の山部を設けることとしてもよい。 In the first embodiment, each of the plurality of peak portions 32a of the surface layer 32 has a triangular cross-sectional shape with the peak portion 32d as a vertex. However, the present invention is limited to this. is not. For example, it is good also as providing the peak part of a dome shape (shape which cut off a part of spherical surface).

また、上記実施形態１では、印刷層３１で形成される模様の一例として、御影石調の模様を採用することとしたが、本発明は、これに限定を受けるものではない。例えば、グリッドタイル調、ガラスモザイク調の模様、ファブリック調の模様、グリッド調の模様、御影石調の模様などを採用することも可能である。 In Embodiment 1 described above, a granite-like pattern is adopted as an example of the pattern formed by the printing layer 31, but the present invention is not limited to this. For example, it is also possible to adopt a grid tile pattern, a glass mosaic pattern, a fabric pattern, a grid pattern, a granite pattern, and the like.

ここで、印刷層３１で形成する模様については、上記実施形態１のように、表面層３２の山部３２ａの外縁辺３２ｉに沿う外縁辺を有する模様とすることが、表面層３２の溝部３２ｂを目立ち難くするとの観点から望ましい。 Here, the pattern formed by the printing layer 31 may be a pattern having an outer edge along the outer edge 32 i of the peak 32 a of the surface layer 32 as in the first embodiment, so that the groove 32 b of the surface layer 32 is formed. It is desirable from the viewpoint of making it difficult to stand out.

１浴室
３浴室床（床）
９床下地
３０クッション層
３１印刷層
３２，３３表面層
３２ａ，３３ａ山部
３２ｂ，３３ｂ溝部
３２ｇ，３２ｈ角部
３５，８５床用シート
８１補強層
３１０基材
３１１インク膜
３１２隠蔽膜 1 bathroom 3 bathroom floor (floor)
9 Floor base 30 Cushion layer 31 Print layer 32, 33 Surface layer 32a, 33a Mountain part 32b, 33b Groove part 32g, 32h Corner part 35,85 Floor sheet 81 Reinforcement layer 310 Base material 311 Ink film 312 Concealment film

Claims

A floor sheet affixed or placed on the floor of a building,
A cushion layer disposed on the floor base and made of a soft foam resin;
A printed layer disposed on the cushion layer and printed with a pattern;
A surface layer disposed on the printing layer and made of a resin material, and having light transmittance;
Layered,
Floor sheet.

The floor sheet according to claim 1,
The printed layer is formed on a light-transmitting base material, an upper surface of the base material, an ink film constituting the pattern, a lower surface of the base material, and the cushion layer and the surface layer. A concealing film that suppresses light transmission between
Floor sheet.

In the floor sheet according to claim 2,
The concealing film is a white or silver film, and is formed on the entire lower surface of the substrate.
Floor sheet.

In the floor sheet according to any one of claims 1 to 3,
The surface layer has, on its upper surface, a plurality of peak portions protruding upward, and a groove portion provided between the plurality of peak portions,
Each of the plurality of peak portions has a top at the center portion, and is formed so that the protruding height decreases from the top portion toward the groove portion.
Floor sheet.

The floor sheet according to claim 4, wherein
When the surface layer is viewed in plan, the groove is formed in a state of being connected to the outer edge of the surface layer.
Floor sheet.

In the floor sheet according to claim 4 or 5,
The groove is formed in a lattice shape in the plan view.
Floor sheet.

The floor sheet according to any one of claims 4 to 6,
The pattern in the printed layer is any one of a granite-like pattern, a grid tile-like pattern, a glass mosaic-like pattern, a fabric-like pattern, and a grid-like pattern, and a line portion along the groove portion. Have
Floor sheet.