JP2019130920A - Photo-curable composition for three-dimensional modeling - Google Patents

Abstract

To relate a photo-curable composition for three-dimensional modeling having a capability of easily adjusting a viscosity, and providing a three-dimensional article that has an excellent mechanical strength even at high temperatures, a method for producing an optically shaped article using the composition, and an optically shaped article obtained by the production method.SOLUTION: There is provided a photo-curable composition for three-dimensional modeling, comprising: A) a photo-curable resin precursor; B) fine cellulose fibers in which a number average fiber diameter is 0.5 nm or more and 200 nm or less, and a carboxy group content is 0.1 mmol/g or more; and/or a modified product thereof.SELECTED DRAWING: None

Description

The present invention relates to a photocurable composition for three-dimensional modeling. In more detail, precision equipment, electricity,
Photocurable composition suitable as a material for three-dimensional modeling of electronic products, products such as automobiles, or parts or cases thereof, a method of manufacturing an optically shaped article using the composition, and light obtained by the manufacturing method It relates to a model.

In recent years, various three-dimensional optical modeling methods have been studied because a three-dimensional model can be manufactured with good dimensional accuracy without using a mold.

For example, in Patent Document 1, a cationically polymerizable organic compound, a radical polymerizable organic compound, an active energy ray sensitive cationic polymerization initiator, and an optical energy three-dimensional resin composition containing an active energy ray sensitive radical polymerization initiator As a cationically polymerizable organic compound, when a specific aromatic triepoxy compound is contained in a predetermined ratio, the three-dimensional object obtained from the optical three-dimensional resin composition has a high heat distortion temperature and is heat resistant. Excellent, mechanical strength such as tensile strength and bending strength is large and has an appropriate elongation, excellent toughness, excellent transparency, small discoloration such as yellowing and excellent hue, excellent transparency It has been reported that sex and hue are maintained even after exposure to high temperatures.

Further, in Patent Document 2, a monofunctional monomer having a low glass transition temperature of the cured product has a slower increase in viscosity during the curing reaction than a monofunctional monomer having a high glass transition temperature of the homopolymer. By curing an ink composition containing a specific amount of a monofunctional monomer having a low glass transition temperature of the polymer, it is possible to secure time for alleviating the curing shrinkage of the ink composition, thereby achieving both rubber elasticity and dimensional stability. It is disclosed that a cured product is obtained.

JP 2010-265408 A JP2015-78255A

However, the application of the technology for three-dimensional optical modeling has been expanded, and further improvements are required. That is, since the surrounding conditions when modeling are diverse, a composition before curing having a handleability (viscosity) according to each situation is necessary, but on the other hand, the composition is cured. There is a demand for the development of a photocurable composition for three-dimensional modeling in which the obtained three-dimensional model has a higher strength and maintains its strength even in a high temperature range.

The present invention relates to a photocurable composition for three-dimensional modeling that can easily adjust the viscosity and can provide a three-dimensional modeled object that is excellent in mechanical strength even at high temperatures, and optical modeling using the composition The present invention relates to an object manufacturing method and an optically shaped object obtained by the manufacturing method.

The present invention relates to the following [1] to [3].
[1] A) Photocurable resin precursor, and B) Number average fiber diameter of 0.5 nm or more and 200 nm
A photocurable composition for three-dimensional modeling, comprising: a fine cellulose fiber having a carboxy group content of 0.1 mmol / g or more and / or a modified product thereof.
[2] A method for producing an optically shaped article, wherein the photocurable composition according to [1] is used in an optical shaping apparatus.
[3] An optically shaped article obtained by the production method according to [2].

The photocurable composition of the present invention has an excellent effect that the three-dimensional structure obtained by curing the composition is excellent in mechanical strength even at high temperatures, while the viscosity can be easily adjusted.

The photocurable composition of the present invention comprises A) a photocurable resin precursor, and B) a number average fiber diameter of 0.00.
It is characterized by containing fine cellulose fibers having a carboxy group content of 0.1 mmol / g or more and / or a modified product thereof. In addition, in this specification, this composition may be described as the resin composition of this invention.

Generally, when the composition of the resin precursor is changed in the curable resin composition, not only the composition before curing but also the physical properties of the molded article itself after curing are likely to fluctuate. It is not easy to adjust the type and amount of the resin precursor in order to impart desired physical properties.
On the other hand, a polymer material has conventionally been used to adjust the viscosity and dispersion stability of the composition. However, the curable resin composition containing the conventional polymer material has not been sufficient in mechanical strength under high temperature of the molded article after curing. Therefore, in the present invention, by adding a specific fine cellulose fiber and / or a modified product thereof to a system containing a photocurable resin precursor, it is easy to adjust the viscosity of the composition before curing, while curing. It has been found that the later modeled object can improve the mechanical strength at high temperatures. Although the detailed reason is unknown, the dispersion of cellulose fibers having a finer fiber diameter than the conventional nanofibers improves the dispersibility in the resin and makes it easy to adjust the viscosity. In addition, since the fine cellulose fibers are relatively resistant to heat, the fibers are entangled and express strength, so it is estimated that the strength in a high temperature region can be improved. In this specification, “mechanical strength” means a property evaluated by “storage modulus” described later.

(Photocurable composition)
[Photocurable resin precursor]
The photocurable resin precursor in the present invention is not particularly limited as long as the polymerization reaction proceeds by irradiation with active energy rays such as ultraviolet rays and electron beams, if necessary, using a photopolymerization initiator. For example, a monomer (monofunctional monomer or polyfunctional monomer), an oligomer having a reactive unsaturated group, a resin, or the like can be used.

Examples of the monofunctional monomer include (meth) acrylic monomers such as (meth) acrylic acid esters, vinyl monomers such as vinylpyrrolidone, isobornyl (meth) acrylate, adamantyl (meth) acrylate, and the like. And (meth) acrylate having a bridged cyclic hydrocarbon group. The polyfunctional monomer includes a polyfunctional monomer having about 2 to 8 polymerizable groups. Examples of the bifunctional monomer include ethylene glycol di (meth) acrylate and propylene glycol di (meth) And di (meth) acrylate having a bridged cyclic hydrocarbon group such as acrylate. Examples of the 3-8 functional monomer include glycerin tri (meth) acrylate. In the present invention, (meth) acrylate includes a methacrylic acid compound and an acrylic acid compound.

Examples of oligomers or resins having reactive unsaturated groups include (meth) acrylates and epoxy (meth) acrylates of bisphenol A-alkylene oxide adducts (bisphenol A type epoxy (meth) acrylates, novolak type epoxy (meth) acrylates, etc.) Polyester (meth) acrylate (for example, aliphatic polyester type (meth) acrylate, aromatic polyester type (meth) acrylate, etc.), urethane (meth) acrylate (polyester type urethane (meth) acrylate, polyether type urethane (meth)) Acrylate),
Silicone (meth) acrylates can be exemplified, and among them, one or more selected from the group consisting of acrylic resins, (meth) acrylic resins, and epoxy resins are preferable.
These oligomers or resins may be used together with the monomers.

These can be used alone or in combination of two or more.
The composition can be adjusted as appropriate.

Moreover, these may use what was prepared according to the well-known method, and may use a commercial item. In the present invention, suitable commercial products include, for example, OBJET FULLURE.
720 (manufactured by Stratasys, acrylic acid resin), SCR774, SCR11120, SC
R780 and SCR780C (both manufactured by DEMEC, epoxy resin) can be used.

[Fine cellulose fiber or modified product thereof]
Examples of the fine cellulose fiber or modified product thereof used in the present invention include a known fine cellulose fiber and a fine cellulose fiber modified product in which a modifying group is introduced into the fine cellulose fiber. In the present specification, the fact that the modifying group is introduced into the fine cellulose fiber means
This means that the modifying group is bonded to the carboxy group on the surface of the fine cellulose fiber by an ionic bond and / or an amide bond. More specifically, when the carboxy group of the fine cellulose fiber is deprotonated, the amine having the modifying group is ionically bonded, or the carbon atom of the amide group is covalently bonded to the cellulose skeleton of the fine cellulose fiber, and the nitrogen atom The modification group is covalently bonded directly or via a linking group.

<Fine cellulose fiber>
(Number average fiber diameter)
The fine cellulose fibers in the present invention have a number average fiber diameter of 0.5 nm or more and 200 nm or less, but from the viewpoint of dispersing fine cellulose fibers having a uniform fiber diameter in a molded article, preferably 0.8 nm or more, and more Preferably it is 1.0 nm or more. In addition, from the viewpoint of handleability and strength expression of a shaped article, it is preferably 100 nm or less, more preferably 50 nm or less,
More preferably, it is 20 nm or less, More preferably, it is 10 nm or less, More preferably, it is 5 nm
It is as follows. In addition, in this specification, the number average fiber diameter of a cellulose fiber can be measured using an atomic force microscope (AFM), and is specifically measured by the method as described in the below-mentioned Example. Generally, the minimum unit of cellulose nanofibers prepared from higher plants is 6
Since the molecular chains of × 6 are packed in a substantially square shape, the height analyzed by the AFM image can be regarded as the fiber width.

(Carboxy group content)
The fine cellulose fiber in the present invention has a carboxy group content of 0.1 mmol / g or more, but preferably 0.4 mmol from the viewpoint of dispersibility in the resin composition and introduction of the modifying group.
/ G or more, more preferably 0.6 mmol / g or more, still more preferably 0.8 mmol / g
That's it. Moreover, from a viewpoint of handleability and cost, Preferably it is 3 mmol / g or less, More preferably, it is 2 mmol / g or less, More preferably, it is 1.8 mmol / g or less. In the fine cellulose fiber used in the present invention, a fine cellulose fiber having a carboxy group content outside this range may be unintentionally contained as an impurity. The “carboxy group content” means the total amount of carboxy groups in the cellulose constituting the fine cellulose fiber, and is specifically measured by the method described in Examples described later.

(Average aspect ratio)
In addition, the fine cellulose fibers in the present invention have an average aspect ratio (fiber length / fiber diameter) of preferably 10 or more, more preferably 20 or more, and still more preferably 30 or more, from the viewpoint of expressing the strength of the molded article. Moreover, from a viewpoint of handleability, Preferably it is 1000 or less, More preferably, it is 800 or less, More preferably, it is 600 or less, More preferably, it is 400 or less. Fine cellulose fibers having an average aspect ratio in the above range are excellent in dispersibility in a composition when blended with a resin precursor, have a high mechanical strength, and are difficult to brittle. In the present specification, in this specification, the average aspect ratio is the aspect ratio of the cellulose fiber according to the following formula (1) from the relationship between the cellulose fiber concentration in the dispersion and the specific viscosity of the dispersion with respect to water. Is calculated in reverse. In addition, following formula (1) is The Theory of
Polymer Dynamics, M.M. DOI and D.D. F. EDWARDS, CL
ARENDON PRESS · OXFORD, 1986, P312 viscosity equation of rigid-rod molecules according to the (8.138), the relationship wherein the _{^{Lb 2 × ρ = M / N}} A, L is the fiber length, b is the fiber width (cellulose The cross section of the fiber is square), ρ is the concentration of cellulose fiber (kg / m ³ ),
M is the molecular weight, the N _A are those derived from the representative of Avogadro's number]. Moreover, in said viscosity formula (8.138), let a rigid rod-shaped molecule | numerator be a cellulose fiber. In the following formula (1),
η _SP is the specific viscosity, π is the circularity, ln is the natural logarithm, P is the aspect ratio (L / b), γ = 0.
8, ρ _S is the density of the dispersion medium (kg / m ³ ), ρ ₀ is the density of the cellulose crystal (kg / m ³ ),
C represents the mass concentration of cellulose (C = ρ / ρ _S ).

(Crystallinity)
The degree of crystallinity of the fine cellulose fiber is preferably 30% or more, more preferably 35% or more, still more preferably 40% or more, and still more preferably 45%, from the viewpoint of expressing the strength of the molded article.
That's it. Moreover, from a viewpoint of cost, Preferably it is 95% or less, More preferably, it is 90% or less, More preferably, it is 85% or less, More preferably, it is 80% or less. In the present specification, the crystallinity of cellulose is the cellulose I-type crystallinity calculated by the Segal method from the diffraction intensity value by the X-ray diffraction method, and is defined by the following calculation formula (A).
Cellulose type I crystallinity (%) = [(I22.6-I18.5) /I22.6] × 1
00 (A)
[Wherein I22.6 is a lattice plane (002 plane) in X-ray diffraction (diffraction angle 2θ = 22.6 °
), I18.5 indicates the diffraction intensity of the amorphous part (diffraction angle 2θ = 18.5 °)]
Cellulose type I is a crystalline form of natural cellulose, and cellulose type I crystallinity means the proportion of the total amount of crystal region in the whole cellulose.

<Modified product of fine cellulose fiber (fine cellulose fiber composite)>
The modified product of fine cellulose fiber used in the present invention is one in which a modifying group is bonded to the surface of the fine cellulose fiber, which is selected from, for example, carboxy groups already present on the surface of the fine cellulose fiber. Thus, it can be obtained by ion-bonding and / or amide-bonding an amine having a modifying group. In addition, in this specification, the modified product of a fine cellulose fiber may be described as a fine cellulose fiber composite.

(Amine having a modifying group)
As the amine having a modifying group, any amine having a modifying group described later may be used, and in the case of ionic bonding, any of a primary amine, secondary amine, tertiary amine, and quaternary ammonium cation may be used. However, from the viewpoint of reactivity, a primary amine, a secondary amine, or a quaternary ammonium cation is preferable, a primary amine or a quaternary ammonium cation is more preferable, and a primary amine is more preferable. In the case of an amide bond, either a primary amine or a secondary amine may be used, but a primary amine is preferable from the viewpoint of reactivity.

As the modifying group in the present invention, a hydrocarbon group, an ethylene oxide / propylene oxide (EO / PO) copolymerized portion, or the like can be used from the viewpoint of improving the strength of the shaped article. These may be introduced into the fine cellulose fiber alone or in combination of two or more.

Examples of the hydrocarbon group include a chain saturated hydrocarbon group, a chain unsaturated hydrocarbon group, a cyclic saturated hydrocarbon group, and an aromatic hydrocarbon group. From the viewpoint, a chain saturated hydrocarbon group, a cyclic saturated hydrocarbon group, and an aromatic hydrocarbon group are preferable.

The chain saturated hydrocarbon group may be linear or branched. The number of carbons of the chain saturated hydrocarbon group is preferably 1 or more, more preferably 2 or more, from the viewpoint of improving the strength of the shaped article.
Three or more are more preferable. Moreover, from the same viewpoint, 30 or less is preferable and 18 or less is more preferable.

Specific examples of the chain saturated hydrocarbon group include, for example, methyl group, ethyl group, propyl group, isopropyl group, butyl group, sec-butyl group, tert-butyl group, isobutyl group, pentyl group, tert-pentyl group, Isopentyl group, hexyl group, isohexyl group, heptyl group, octyl group, 2-ethylhexyl group, nonyl group, decyl group, dodecyl group, tridecyl group, tetradecyl group, octadecyl group, docosyl group, octacosanyl group, etc.
From the viewpoint of improving the strength of the molded article, preferably propyl group, isopropyl group, butyl group, sec-butyl group, tert-butyl group, isobutyl group, pentyl group, tert-pentyl group, isopentyl group, hexyl group, isohexyl group , Heptyl group, octyl group, 2-ethylhexyl group, nonyl group, decyl group, dodecyl group, tridecyl group, tetradecyl group, octadecyl group, docosyl group, octacosanyl group, more preferably propyl group, isopropyl group, butyl group, sec-butyl group, tert-butyl group, isobutyl group, pentyl group, tert-pentyl group, isopentyl group, hexyl group, isohexyl group, heptyl group, octyl group, 2-ethylhexyl group, nonyl group, decyl group, dodecyl group, Tridecyl group, tetradecyl group, octadecyl group Group. These may be introduced alone or two or more of them may be introduced in an arbitrary ratio.

The chain unsaturated hydrocarbon group may be linear or branched. From the viewpoint of handleability, the number of carbon atoms of the chain unsaturated hydrocarbon group is preferably 1 or more, more preferably 2 or more, and still more preferably 3 or more. Further, from the viewpoint of availability, 30 or less is preferable, and 18 or less is more preferable.

Specific examples of the chain unsaturated hydrocarbon group include, for example, ethylene group, propylene group, butene group, isobutene group, isoprene group, pentene group, hexene group, heptene group, octene group,
Nonene group, decene group, dodecene group, tridecene group, tetradecene group, octadecene group can be mentioned. From the viewpoint of affinity with the precursor, ethylene group, propylene group, butene group, isobutene group, isoprene group, pentene group are preferable. Hexene group, heptene group, octene group, nonene group, decene group and dodecene group, more preferably hexene group, heptene group, octene group, nonene group, decene group and dodecene group. These may be introduced alone or two or more of them may be introduced in an arbitrary ratio.

From the viewpoint of handleability, the number of carbon atoms of the cyclic saturated hydrocarbon group is preferably 3 or more, more preferably 4 or more, and still more preferably 5 or more. Moreover, from a viewpoint of availability, 20 or less is preferable and 16 or less is more preferable.

Specific examples of the cyclic saturated hydrocarbon group include, for example, a cyclopropane group, a cyclobutyl group,
Examples include cyclopentane group, cyclohexyl group, cycloheptyl group, cyclooctyl group, cyclononyl group, cyclodecyl group, cyclododecyl group, cyclotridecyl group, cyclotetradecyl group, cyclooctadecyl group, etc. From the viewpoint, it is preferably a cyclopropane group, a cyclobutyl group, a cyclopentane group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclononyl group, a cyclodecyl group, or a cyclododecyl group, and more preferably a cyclohexyl group, a cycloheptyl group, a cyclo An octyl group, a cyclononyl group, a cyclodecyl group, and a cyclododecyl group; These may be introduced alone or two or more of them may be introduced in an arbitrary ratio.

The aromatic hydrocarbon group is selected from the group consisting of an aryl group and an aralkyl group, for example. The aryl group and aralkyl group may be substituted or unsubstituted on the aromatic ring itself.

The total number of carbon atoms of the aryl group may be 6 or more. From the viewpoint of affinity with the precursor, it is preferably 24 or less, more preferably 20 or less, still more preferably 14 or less, and still more preferably 1
2 or less, more preferably 10 or less.

The total number of carbon atoms of the aralkyl group is 7 or more, preferably 8 or more from the viewpoint of affinity with the precursor, and from the same viewpoint, preferably 24 or less, more preferably 20 or less, still more preferably. Is 14 or less, more preferably 13 or less, and still more preferably 11 or less.

Examples of the aryl group include a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, a biphenyl group, a triphenyl group, a terphenyl group, and a group in which these groups are substituted with a substituent described later. One kind alone or two or more kinds may be introduced in an arbitrary ratio. Especially, a phenyl group, a biphenyl group, and a terphenyl group are preferable from a viewpoint of affinity with a precursor, and a phenyl group is more preferable.

As an aralkyl group, for example, a benzyl group, a phenethyl group, a phenylpropyl group, a phenylpentyl group, a phenylhexyl group, a phenylheptyl group, a phenyloctyl group, and an aromatic group of these groups are substituted with a substituent described later. Group etc. are mentioned, These may be introduce | transduced individually by 1 type or 2 types or more, respectively. Among them, from the viewpoint of affinity with the precursor, benzyl group, phenethyl group, phenylpropyl group, phenylpentyl group, phenylhexyl group, phenylheptyl group are preferable, benzyl group, phenethyl group, phenylpropyl group, phenylpentyl group. A phenylhexyl group is more preferable, and a benzyl group, a phenethyl group, a phenylpropyl group, and a phenylpentyl group are more preferable.

The amine having a hydrocarbon group can be prepared according to a known method. Also,
Commercially available products may be used. Examples of amines having a chain saturated hydrocarbon group include propylamine, isopropylamine, butylamine, sec-butylamine, tert-butylamine, isobutylamine, pentylamine, tert-pentylamine, Pentylamine, hexylamine, isohexylamine, heptylamine, octylamine, 2-
Ethylhexylamine, nonylamine, decylamine, dodecylamine, tridecylamine, tetradecylamine, octadecylamine, docosylamine, and octacosanylamine can be used. Examples of the amine having a chain unsaturated hydrocarbon group include ethyleneamine, propyleneamine, buteneamine, isobuteneamine, isopreneamine, penteneamine, hexeneamine, hepteneamine, octeneamine, nonenamine, deceneamine, and dodecenamine. As an amine having a cyclic saturated hydrocarbon group,
Cyclopropanamine, cyclobutylamine, cyclopentaneamine, cyclohexylamine, cycloheptylamine, cyclooctylamine, cyclononylamine, cyclodecylamine, and cyclododecylamine can be used. Examples of the amine having an aromatic hydrocarbon group include aniline, 4-biphenylylamine, diphenylamine, 2-aminonaphthalene, p-terphenylamine, 2-aminoanthracene, 2-aminoanthraquinone, benzylamine, phenethylamine, 3 -Phenylpropylamine, 5-phenylpentylamine, 6-phenylhexylamine, 7-phenylheptylamine, 8-phenyloctylamine can be used. Examples of the quaternary alkylammonium cation include tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetraethylammonium chloride, tetrabutylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium chloride, lauryltrimethylammonium chloride, Dilauryldimethylammonium chloride, stearyltrimethylammonium chloride, distearyldimethylammonium chloride, cetyltrimethylammonium chloride, and alkylbenzyldimethylammonium chloride can be used.

The average bond amount (mmol / g) of hydrocarbon groups in the fine cellulose fiber composite is the same as that of the fine cellulose fibers for chain saturated hydrocarbon groups, chain unsaturated hydrocarbon groups, and cyclic saturated hydrocarbon groups. On the other hand, since the control of the bonding amount of the hydrocarbon group is easy, it is preferably 0.001 mmol / g or more, more preferably 0.005 mmol / g or more, and still more preferably 0.01 mmol / g or more. From the viewpoint of reactivity, preferably 3 mmol
/ G or less, more preferably 2 mmol / g or less. In addition, for the aromatic hydrocarbon group, the average bond amount of the hydrocarbon group is preferably 0.1 mmol /
g or more, more preferably 0.2 mmol / g or more, still more preferably 0.5 mmol / g or more. From the viewpoint of reactivity, it is preferably 3 mmol / g or less, more preferably 2
mmol / g or less, more preferably 1.5 mmol / g or less. Here, a hydrocarbon group selected from a chain saturated hydrocarbon group, a chain unsaturated hydrocarbon group, and a cyclic saturated hydrocarbon group;
Even in the case where the aromatic hydrocarbon group is introduced at the same time, the average amount of individual bonds is preferably within the above range.

The average bond amount (parts by mass) of the hydrocarbon groups in the fine cellulose fiber composite is the fine cellulose fiber for the chain saturated hydrocarbon group, the chain unsaturated hydrocarbon group, and the cyclic saturated hydrocarbon group. It is preferably 10 parts by mass or more, more preferably 15 parts by mass or more, and still more preferably 20 parts by mass or more because the amount of bonded hydrocarbon groups is easily controlled with respect to 100 parts by mass. From the viewpoint of reactivity, it is preferably 50 parts by mass or less, more preferably 4
5 parts by mass or less, more preferably 40 parts by mass or less. Moreover, about an aromatic hydrocarbon group, from the viewpoint of the intensity | strength of a molded article, the average bond amount of a hydrocarbon group becomes like this. Preferably it is 5 mass parts or more, More preferably, it is 10 mass parts or more. Moreover, from a reactive viewpoint, Preferably it is 40 mass parts or less, More preferably, it is 35 mass parts or less, More preferably, it is 30 mass parts or less. Here, even when a hydrocarbon group selected from a chain saturated hydrocarbon group, a chain unsaturated hydrocarbon group, and a cyclic saturated hydrocarbon group and an aromatic hydrocarbon group are simultaneously introduced. The average bond amount is preferably within the above range.

Similarly, the average bond amount (% by mass) of hydrocarbon groups in the fine cellulose fiber composite is hydrocarbon for chain saturated hydrocarbon groups, chain unsaturated hydrocarbon groups, and cyclic saturated hydrocarbon groups. From the viewpoint of easy control of the bonding amount of the group, it is preferably 10% by mass or more, more preferably 15% by mass or more, and still more preferably 20% by mass or more. From the viewpoint of reactivity,
Preferably it is 50 mass% or less, More preferably, it is 45 mass% or less, More preferably, it is 40 mass%
It is as follows. Moreover, about an aromatic hydrocarbon group, the average bond amount of a hydrocarbon group becomes like this from a viewpoint of the intensity | strength of a molded article, Preferably it is 5 mass% or more, More preferably, it is 10 mass% or more. Moreover, from a reactive viewpoint, Preferably it is 40 mass% or less, More preferably, it is 35 mass% or less, More preferably, it is 30 mass% or less. Here, even when a hydrocarbon group selected from a chain saturated hydrocarbon group, a chain unsaturated hydrocarbon group, and a cyclic saturated hydrocarbon group and an aromatic hydrocarbon group are simultaneously introduced. The average bond amount is preferably within the above range.

The introduction rate of the hydrocarbon group is preferably 10% or more for the chain saturated hydrocarbon group, the chain unsaturated hydrocarbon group, and the cyclic saturated hydrocarbon group from the viewpoint of the strength of the resulting molded article. ,
More preferably, it is 30% or more, more preferably 50% or more, further preferably 60% or more, further preferably 70% or more. From the viewpoint of reactivity, it is preferably 99% or less, more preferably 97% or less, Preferably it is 95% or less, More preferably, it is 90% or less. Also,
With respect to the aromatic hydrocarbon group, the introduction rate of the hydrocarbon group is preferably 10% or more, more preferably 30% or more, still more preferably 50% or more, and still more preferably, from the viewpoint of obtaining a molded article having excellent mechanical strength. Is 60% or more, more preferably 70% or more, more preferably 80% or more. From the viewpoint of reactivity, it is preferably 99% or less, more preferably 97% or less, still more preferably 95% or less, and still more preferably. 90% or less. Where a chain saturated hydrocarbon group,
When a hydrocarbon group selected from a chain unsaturated hydrocarbon group and a cyclic saturated hydrocarbon group and an aromatic hydrocarbon group are introduced simultaneously, the total introduction rate exceeds 100% of the upper limit. It is preferable to be within the above range in a range that is not present.

The EO / PO copolymer part is ethylene oxide (EO) and propylene oxide (PO).
) Means a structure polymerized in a random or block form. For example, when an amine having an EO / PO copolymer part is represented by the formula (i) described later, ethylene oxide (EO) and propylene oxide (PO) have a random or block chain structure. Is an amine having a structure represented by formula (ii) described below, (EO) a (PO) b,
(EO) c (PO) d and (EO) e (PO) f need not be linked.

The PO content (mol%) in the EO / PO copolymerization part is preferably 1 mol% or more, more preferably 5 mol% or more, still more preferably 7 mol% or more, from the viewpoint of the strength of the molded article. From the same viewpoint, it is preferably 100 mol% or less, more preferably 90 mol% or less, still more preferably 85 mol% or less, still more preferably 75 mol% or less, still more preferably 60 mol. % Or less, more preferably 50 mol% or less, more preferably 4
It is 0 mol% or less, More preferably, it is 30 mol% or less. The PO content of 100 mol% means that the EO / PO copolymer part is composed only of PO, and in the present invention, the PO polymer part may be introduced.

The molecular weight of the EO / PO copolymerization part is preferably 700 or more, more preferably 1,000 or more, still more preferably 1,500 or more, from the viewpoints of dispersibility in the precursor and the strength of the model. From the viewpoint of the strength, preferably 10,000 or less, more preferably 7,000
Hereinafter, it is more preferably 5,000 or less, further preferably 4,000 or less, more preferably 3,500 or less, and further preferably 2,500 or less. For example, in the case of an amine having a structure represented by formula (ii) described later, (EO) a (PO) b + (EO) c (PO)
The total molecular weight of d + (EO) e (PO) f is defined as the molecular weight of the EO / PO copolymer part. EO
The PO content (mol%) in the / PO copolymerization part and the molecular weight of the EO / PO copolymerization part can be calculated from the average number of moles added when the amine is produced.

The EO / PO copolymer part and the amine are preferably bonded directly or via a linking group. As the linking group, a hydrocarbon group is preferable, and an alkylene group having 1 to 6 carbon atoms, more preferably 1 to 3 carbon atoms is used. For example, an ethylene group and a propylene group are preferable.

  Examples of the amine having such an EO / PO copolymer part include the following formula (i):

[Wherein, R ₁ represents a hydrogen atom, a linear or branched alkyl group having 1 to 6 carbon atoms, —CH ₂ C
H (CH ₃ ) NH ₂ group or a group represented by the following formula (ii), EO and PO are present in a random or block form, a is a positive number indicating the average added mole number of EO, b Is a positive number indicating the average number of moles of PO added.]
The compound represented by these is mentioned.

Formula (ii):

[In the formula, n is 0 or 1, R ₂ represents a phenyl group, a hydrogen atom, or a linear or branched alkyl group having 1 to 3 carbon atoms, and EO and PO are present in a random or block form. , C
And e represent the average number of moles of EO added and are independently a number from 0 to 50; d and f are PO
The average number of moles added is independently a number from 1 to 50]

In the formula (i), a represents the average added mole number of EO, and from the viewpoint of the strength of the molded article, it is preferably 11 or more, more preferably 15 or more, still more preferably 20 or more, and still more preferably 25.
From the same viewpoint, it is preferably 100 or less, more preferably 70 or less, still more preferably 60 or less, still more preferably 50 or less, and even more preferably 40 or less.

In formula (i), b represents the average number of moles of PO added, and is preferably 1 or more, more preferably 2 or more, still more preferably 3 or more from the viewpoint of the strength of the molded article, and from the same viewpoint, preferably 50 or less, more preferably 40 or less, still more preferably 30 or less, still more preferably 25 or less, still more preferably 20 or less, still more preferably 15 or less.

The PO content (mol%) in the EO / PO copolymer part is calculated from the above a and b when the amine is represented by the formula (i). When the amine is represented by the formula (i) and the formula (ii), the formula: (b + d + f) × 100 / (a + b + c + d +
e + f). A preferred range is as described above.

R ₁ in formula (i) is a hydrogen atom, a linear or branched alkyl group having 1 to 6 carbon atoms,
A —CH ₂ CH (CH ₃ ) NH ₂ group or a group represented by the formula (ii) is shown, and a hydrogen atom is preferable from the viewpoint of the strength of the shaped article. The linear or branched alkyl group having 1 to 6 carbon atoms is preferably a methyl group, an ethyl group, an iso or normal propyl group.

In addition, when R ₁ in formula (i) is a group represented by formula (ii), the linear or branched alkyl group having 1 to 3 carbon atoms of R ₂ in formula (ii) is preferably A methyl group and an ethyl group. When R ₂ is a methyl group or an ethyl group, n is preferably 1, and when R ₂ is a hydrogen atom, n is preferably 0. Moreover, as c and e in Formula (ii), 10-30 are preferable independently, and d and f are independently,
5-25 are preferable.

The amine having an EO / PO copolymer moiety represented by the formula (i) can be prepared according to a known method. For example, a desired amount of ethylene oxide or propylene oxide may be added to propylene glycol alkyl ether, and then the hydroxyl terminal may be aminated. If necessary, the terminal can be made into a hydrogen atom by cleaving the alkyl ether with an acid.
For these production methods, reference can be made to JP-A-3-181448.

In addition, commercially available products are also preferably used. Specific examples include Jeffa manufactured by HUNTSMAN.
mine M-2070, Jeffamine M-2005, Jeffamine M
-1000, Surfamine B200, Surfamine L100, Su
rfoamine L200, Surfamine L207, Surfamine
L300, XTJ-501, XTJ-506, XTJ-507, XTJ-508; BA
SF made M3000, Jeffamine ED-900, Jeffamine ED
-2003, Jeffamine D-2000, Jeffamine D-4000,
XTJ-510, Jeffamine T-3000, Jeffamine T-5000
, XTJ-502, XTJ-509, XTJ-510 and the like. These may be used alone or in combination of two or more.

Average binding amount of EO / PO copolymer part in fine cellulose fiber composite (mmol / g)
Is preferably 0.01 mmol / g or more, more preferably 0, from the viewpoint of the strength of the shaped article.
. 05 mmol / g or more, more preferably 0.1 mmol / g or more, more preferably 0.
3 mmol / g or more, more preferably 0.5 mmol / g or more, more preferably 0.8 m
mol / g or more, more preferably 1 mmol / g or more. From the viewpoint of reactivity,
Preferably it is 3 mmol / g or less, More preferably, it is 2 mmol / g or less, More preferably, it is 1
. 5 mmol / g or less.

The average binding amount (parts by mass) of the EO / PO copolymer part in the fine cellulose fiber composite is preferably 5 parts by mass or more, more preferably 100 parts by mass with respect to 100 parts by mass of the fine cellulose fibers. Is 10 parts by mass or more, more preferably 20 parts by mass or more. Moreover, from a reactive viewpoint, Preferably it is 500 mass parts or less, More preferably, it is 400 mass parts or less,
More preferably, it is 300 parts by mass or less.

The average binding amount (% by mass) of the EO / PO copolymer part in the fine cellulose fiber composite is preferably 5% by mass or more, more preferably 10% by mass or more, and still more preferably 20% by mass from the viewpoint of the strength of the molded article. % Or more. Moreover, from a reactive viewpoint, Preferably it is 99 mass% or less, More preferably, it is 95 mass% or less, More preferably, it is 90 mass% or less.

The introduction ratio of the EO / PO copolymer part in the fine cellulose fiber composite is preferably 10% or more, more preferably 20% or more, and still more preferably 30 from the viewpoint of the strength of the shaped article.
% Or more, more preferably 40% or more, more preferably 50% or more, more preferably 60%
Above, more preferably 70% or more, more preferably 80% or more, from the same viewpoint,
Preferably it is 95% or less.

The modifying group may have a substituent. For example, it is preferable that the total number of carbon atoms of the hydrocarbon group including the substituent is within the above range. Examples of the substituent include a methoxy group, an ethoxy group, a propoxy group, an isopropoxy group, a butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group, an isopentyloxy group, and a hexyloxy group. C1-C6 alkoxy group; methoxycarbonyl group, ethoxycarbonyl group, propoxycarbonyl group, isopropoxycarbonyl group, butoxycarbonyl group, isobutoxycarbonyl group, sec-butoxycarbonyl group, tert-butoxycarbonyl group, pentyloxycarbonyl Group, an alkoxy-carbonyl group having 1 to 6 carbon atoms of an alkoxy group such as isopentyloxycarbonyl group; a halogen atom such as a fluorine atom, a chlorine atom, a bromine atom or an iodine atom; 1 carbon atom such as an acetyl group or a propionyl group ~ 6 Sill group; an aralkyl group; an aralkyloxy group; an alkylamino group having 1 to 6 carbon atoms; the carbon number of the alkyl group have dialkylamino group having 1 to 6. In addition, the above-described hydrocarbon group itself may be bonded as a substituent.

In the present specification, the average bonding amount of the modifying group can be adjusted by the amount of amine added, the type of amine, the reaction temperature, the reaction time, the solvent, and the like. Further, the average binding amount (mmol / g, parts by mass, mass%) and introduction rate (%) of the modifying group in the fine cellulose fiber composite are the amount of the modifying group introduced into the carboxy group on the surface of the fine cellulose fiber, and It is a ratio and can be calculated by measuring the carboxy group content of fine cellulose fibers according to a known method (for example, titration, IR measurement, etc.).

<Method for producing fine cellulose fiber composite>
If the fine cellulose fiber composite can introduce a modifying group into the fine cellulose fiber,
It can manufacture in accordance with a well-known method without limitation. For example, a reaction for introducing a modifying group into fine cellulose fibers prepared in advance may be performed, or a reaction for introducing a modifying group may be performed when preparing fine cellulose fibers. The fine cellulose fiber is a known method,
For example, it can be produced by the method described in JP2011-140632A.

The following two modes may be mentioned depending on the mode of introduction of the modifying group into the fine cellulose fiber. That is, there are an embodiment (embodiment A) in which the modifying group is bonded to the fine cellulose fiber by ionic bond and an embodiment (embodiment B) in which the modifying group is bonded to the fine cellulose fiber by amide bond.
[Aspect A]
Step (1): Oxidation of natural cellulose fibers in the presence of an N-oxyl compound to obtain carboxy group-containing cellulose fibers Step (2A): Carboxy group-containing cellulose fibers obtained in step (1), and modifying groups A step of mixing with an amine having [Aspect B]
Step (1): Natural cellulose fiber is oxidized in the presence of an N-oxyl compound to obtain a carboxy group-containing cellulose fiber Step (2B): Carboxy group-containing cellulose fiber obtained in step (1) and a modifying group The step of amidation reaction with an amine having the following: As the preferred production method, the step (2A or 2B) is performed after the step (1) is followed by a finer step, which will be described later, to obtain a carboxy group-containing fine cellulose fiber. Examples include a method of performing (first manufacturing mode) and a method of performing step (2A or 2B) after step (1) and then performing a miniaturization step (second manufacturing mode).

Hereinafter, based on the 1st manufacture form of aspect A, the manufacturing method of a fine cellulose fiber composite is demonstrated.

[Step (1)]
Step (1) is a step of oxidizing a natural cellulose fiber in the presence of an N-oxyl compound to obtain a carboxy group-containing cellulose fiber.

In the step (1), first, a slurry in which natural cellulose fibers are dispersed in water is prepared.
The slurry is about 10 to 1000 times (mass basis) relative to the natural cellulose fiber (absolute drying basis: mass of natural cellulose fiber after being heated and dried at 150 ° C. for 30 minutes) as a raw material.
It is obtained by adding water and processing with a mixer or the like. As natural cellulose fiber,
For example, wood pulp such as coniferous pulp and hardwood pulp; cotton pulp such as cotton linter and cotton lint; non-wood pulp such as straw pulp and bagasse pulp; bacterial cellulose and the like. Or two or more types can be used in combination. The natural cellulose fiber may be subjected to a treatment for increasing the surface area such as beating. Further, the cellulose I type crystallinity of the commercially available pulp is usually 80% or more.

(Oxidation process)
Next, the natural cellulose fiber is oxidized in the presence of an N-oxyl compound to obtain a carboxy group-containing cellulose fiber (hereinafter sometimes simply referred to as “oxidation treatment”).

As the N-oxyl compound, one or more heterocyclic N-oxyl compounds selected from piperidine oxyl compounds having 1 or 2 carbon atoms, pyrrolidine oxyl compounds, imidazoline oxyl compounds, and azaadamantane compounds are preferable. . Among these, piperidineoxyl compounds having an alkyl group having 1 or 2 carbon atoms are preferable from the viewpoint of reactivity, and 2,2,6,6-tetraalkylpiperidine-1-oxyl (TEMP)
O), 4-hydroxy-2,2,6,6-tetraalkylpiperidine-1-oxyl, 4
-Alkoxy-2,2,6,6-tetraalkylpiperidine-1-oxyl, 4-benzoyloxy-2,2,6,6-tetraalkylpiperidine-1-oxyl, 4-amino-
Di-tert-alkylnitroxyl compounds such as 2,2,6,6-tetraalkylpiperidine-1-oxyl, 4-acetamido-TEMPO, 4-carboxy-TEMPO, 4
-Phosphonoxy-TEMPO etc. are mentioned. Among these piperidine oxyl compounds, 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO), 4-hydroxy-2,2,6,6-tetramethylpiperidine-1-oxyl, 4- Methoxy-2
2,6,6-tetramethylpiperidine-1-oxyl is preferred, and 2,2,6,6 tetramethylpiperidine-1-oxyl (TEMPO) is more preferred.

The amount of the N-oxyl compound may be a catalytic amount, and is preferably 0.001 to 10% by mass, more preferably 0.01 to 9% by mass, with respect to natural cellulose fiber (absolute dry basis),
More preferably, it is 0.1-8 mass%, More preferably, it is 0.5-5 mass%.

An oxidizing agent can be used in the oxidation treatment of natural cellulose fibers. As the oxidizing agent, from the viewpoint of solubility and reaction rate when the solvent is adjusted to an alkaline region, oxygen or air, peroxides; halogens, hypohalous acids, halous acids, perhalogen acids and their alkali metals Salt or alkaline earth metal salt; halogen oxide, nitrogen oxide and the like.
Among these, alkali metal hypohalites are preferable, and specific examples include sodium hypochlorite and sodium hypobromite. The amount of the oxidizing agent used may be selected according to the degree of carboxy group substitution (oxidation degree) of the natural cellulose fiber, and the oxidation reaction yield varies depending on the reaction conditions. Preferably it is the range used as about 1-100 mass% with respect to a cellulose fiber (absolute dry reference | standard).

In order to perform the oxidation reaction more efficiently, bromides such as sodium bromide and potassium bromide and iodides such as sodium iodide and potassium iodide can be used as a co-catalyst. The amount of the promoter is not particularly limited as long as it is an effective amount that can exhibit its function.

The reaction temperature in the oxidation treatment is preferably 5 from the viewpoint of reaction selectivity and suppression of side reactions.
0 ° C. or lower, more preferably 40 ° C. or lower, still more preferably 20 ° C. or lower.
Preferably it is −5 ° C. or higher.

The pH of the reaction system is preferably matched to the nature of the oxidizing agent. For example, when sodium hypochlorite is used as the oxidizing agent, the pH of the reaction system is preferably on the alkali side,
pH 7-13 is preferable, and pH 10-13 is more preferable. The reaction time is 1 to 240.
Minutes are desirable.

By performing the oxidation treatment, a carboxy group-containing cellulose fiber having a carboxy group content of 0.1 mmol / g or more is obtained.

(Purification process)
The carboxy group-containing cellulose fiber obtained by the oxidation reaction is a TEM used as a catalyst.
Includes N-oxyl compounds such as PO and by-product salts. The next step may be carried out as it is, but purification can also be carried out to obtain a highly purified carboxy group-containing cellulose fiber. As the purification method, an optimum method can be employed depending on the type of solvent in the oxidation reaction, the degree of oxidation of the product, and the degree of purification. For example, reprecipitation using water as a good solvent, methanol, ethanol, acetone, etc. as a poor solvent, extraction of TEMPO into a solvent that is phase-separated from water such as hexane, purification by ion exchange of salts, dialysis, etc. Can be mentioned.

(Miniaturization process)
In the first production mode, after the purification step, a step of refining the carboxy group-containing cellulose fiber obtained in the step (1) is performed. In the refinement process, it is preferable to perform the refinement process by dispersing the carboxy group-containing cellulose fiber that has undergone the purification process in a solvent. By performing this refinement step, fine cellulose fibers having a number average fiber diameter in the above range are obtained.

The solvent as the dispersion medium is water, as well as carbon number 1 such as methanol, ethanol, propanol, etc.
-6, preferably an alcohol having 1 to 3 carbon atoms; a ketone having 3 to 6 carbon atoms such as acetone, methyl ethyl ketone, methyl isobutyl ketone; linear or branched saturated hydrocarbon or unsaturated hydrocarbon having 1 to 6 carbon atoms Aromatic hydrocarbons such as benzene and toluene; halogenated hydrocarbons such as methylene chloride and chloroform; lower alkyl ethers having 2 to 5 carbon atoms; N, N-dimethylformamide, N, N-dimethylacetamide, dimethyl sulfoxide, and aqua Examples include polar solvents such as diesters of acid and triethylene glycol monomethyl ether.
These can be used alone or in admixture of two or more, but from the viewpoint of the operability of the micronization treatment, water, alcohol having 1 to 6 carbon atoms, ketone having 3 to 6 carbon atoms, carbon number 2 Polar solvents such as -5 lower alkyl ethers, N, N-dimethylformamide, N, N-dimethylacetamide, dimethyl sulfoxide, succinic acid methyltriglycol diester are preferable, and water is more preferable from the viewpoint of reducing environmental burden. The amount of the solvent used is not particularly limited as long as it is an effective amount capable of dispersing the carboxy group-containing cellulose fiber, but is preferably 1 to 500 times by mass, more preferably 2 to 200 times with respect to the carboxy group-containing cellulose fiber. It is more preferable to use mass times.

Moreover, a well-known disperser is used suitably as an apparatus used by refinement | miniaturization processing. For example,
A disaggregator, a beating machine, a low pressure homogenizer, a high pressure homogenizer, a grinder, a cutter mill, a ball mill, a jet mill, a short screw extruder, a twin screw extruder, an ultrasonic stirrer, a household juicer mixer, and the like can be used. Further, the solid content concentration of the reactant fiber in the refinement treatment is preferably 50% by mass or less.

As the form of the carboxy group-containing fine cellulose fiber obtained after the refining process, the solid content concentration is adjusted as required (sustainedly colorless transparent or opaque liquid), or dried powder (however, Or a powder form in which fine cellulose fibers are aggregated, and does not mean cellulose particles). In addition, when making into suspension form, you may use only water as a dispersion medium, and water and other organic solvents (for example, alcohols, such as ethanol).
Alternatively, a mixed solvent with a surfactant, an acid, a base, or the like may be used.

By such oxidation treatment and refinement treatment of natural cellulose fiber, the hydroxyl group at the C6 position of the cellulose constituent unit is selectively oxidized to a carboxy group via an aldehyde group, and the carboxy group content is 0.1 mmol / The number average fiber diameter is 0.
Cellulose fibers having a finer aspect ratio of 5 nm to 200 nm, preferably an aspect ratio of 10 to 1000, and preferably a crystallinity of 30% or more can be obtained. Here, the said carboxy-group containing fine cellulose fiber has a cellulose I type crystal structure. This means that the carboxy group-containing fine cellulose fiber used in the present invention is a fiber obtained by surface-oxidizing and refining a naturally-derived cellulose solid raw material having an I-type crystal structure. In step (1), after the natural cellulose fiber is oxidized, an acid (for example, hydrochloric acid) can be further reacted to adjust the carboxy group content, and the reaction can be performed before or after the refining treatment. You may go to either of them.

[Step (2A)]
In the first production mode, the step (2A) is a step of obtaining a fine cellulose fiber composite by mixing the carboxy group-containing fine cellulose fiber obtained through the above-mentioned finening step and an amine having a modifying group. is there. Specifically, the carboxy group-containing fine cellulose fiber and an amine having a modifying group are mixed in a solvent.

Examples of the amine having a modifying group used in the step (2A) include those described above in the fine cellulose fiber composite.

The amount of amine used can be determined by the amount of the desired amine salt bound in the fine cellulose fiber composite, but from the viewpoint of reactivity, with respect to 1 mol of carboxy group contained in the carboxy group-containing fine cellulose fiber, The amine group is preferably 0.01 mol or more, more preferably 0.1 mol or more, still more preferably 0.5 mol or more, still more preferably 0.7 mol or more, and from the viewpoint of product purity, preferably 50 mol or less, more preferably Is used in an amount of 20 mol or less, more preferably 10 mol or less. In addition, you may use for the reaction of the quantity of amine contained in the said range at once, or you may divide | segment and use for reaction. Amines
In the case of monoamine, the above amine group and amine are the same.

As the solvent, it is preferable to select a solvent in which the amine to be used is dissolved. For example, ethanol, isopropanol (IPA), N, N-dimethylformamide (DMF), dimethyl sulfoxide (DMSO), N, N-dimethylacetamide, tetrahydrofuran (
THF), diester of succinic acid and triethylene glycol monomethyl ether, acetone, methyl ethyl ketone (MEK), acetonitrile, dichloromethane, chloroform, toluene, acetic acid, water, etc., one of these alone or two or more They can be used in combination. Among these polar solvents, diester of succinic acid and triethylene glycol monomethyl ether, ethanol, DMF, and water are preferable.

The mixing temperature is preferably 0 ° C. or more, more preferably 5 from the viewpoint of amine reactivity.
More than 10 degreeC, More preferably, it is 10 degreeC or more. Moreover, from a viewpoint of coloring of a composite, Preferably it is 50 degrees C or less, More preferably, it is 40 degrees C or less, More preferably, it is 30 degrees C or less. The mixing time can be appropriately set according to the type of amine and solvent used, but from the viewpoint of amine reactivity, it is preferably 0.01 hours or longer, more preferably 0.1 hours or longer, and even more preferably 1 It is more than time, Preferably it is 48 hours or less, More preferably, it is 24 hours or less.

After the salt formation, an appropriate post-treatment may be performed in order to remove unreacted amine and the like. As the post-treatment method, for example, filtration, centrifugation, dialysis and the like can be used.

Moreover, about the manufacturing method of aspect B, since a process (1) can be performed similarly to aspect A, it describes below about the process (2B) in a 1st manufacturing form. For example, it can manufacture by the method as described in Unexamined-Japanese-Patent No. 2013-151661.

[Step (2B)]
In the first production mode, in the step (2B), a carboxy group-containing fine cellulose fiber obtained through the above-mentioned finening step and an amine having a modifying group are amidated to obtain a fine cellulose fiber composite. It is a process. As the mixing method, there is no particular problem as long as the raw material reacts. Specifically, the raw material is mixed in the presence of a condensing agent, and the carboxy group contained in the carboxy group-containing fine cellulose fiber and Then, the amino group of the amine having a modifying group is subjected to a condensation reaction to form an amide bond.

Examples of the amine having a modifying group used in the step (2B) include those described above in the fine cellulose fiber composite.

In the step (2B), a carboxy group-containing fine cellulose fiber and an amine having a modifying group are amidated in the presence of a condensing agent.

From the viewpoint of reactivity, the amount of the amine used is preferably 0.1 mol or more, more preferably 0.5 mol or more, with respect to 1 mol of the carboxy group contained in the carboxy group-containing fine cellulose fiber. From the viewpoint of product purity, preferably 50 mol or less,
More preferably, it is used in an amount of 20 mol or less, more preferably 10 mol or less. In addition,
An amount of the amine included in the above range may be subjected to the reaction at once, or may be divided and subjected to the reaction.

The condensing agent is not particularly limited, but synthetic chemistry series peptide synthesis (Maruzensha)
Examples include condensing agents described in P116 or Tetrahedron, 57, 1551 (2001), such as 4- (4,6-dimethoxy-1,3,5-triazin-2-yl) -4-methylmorpholine. And nitrochloride (hereinafter sometimes referred to as “DMT-MM”).

In the above-mentioned amidation reaction, the solvent in the above-mentioned refinement step is mentioned, and it is preferable to select a solvent in which the amine to be used is dissolved.

The reaction time and reaction temperature in the amidation reaction can be appropriately selected according to the type of amine and solvent to be used, but from the viewpoint of the reaction rate, preferably 1 to 24 hours, more preferably 10 to 20 hours. It is. The reaction temperature is preferably 0 from the viewpoint of reactivity.
° C or higher, more preferably 5 ° C or higher, still more preferably 10 ° C or higher. Further, from the viewpoint of coloring the composite, it is preferably 200 ° C. or lower, more preferably 80 ° C. or lower, and further preferably 3 ° C.
0 ° C. or lower.

After the reaction, in order to remove unreacted amine, condensing agent and the like, post-treatment may be appropriately performed. As the post-treatment method, for example, filtration, centrifugation, dialysis and the like can be used.

Note that, in any of the aspects A and B, in the second manufacturing mode, the steps described above are performed in the order of the step (1), the step (2A) or the step (2B), and the miniaturization step. , First
It can carry out by the method similar to this manufacturing form.

Moreover, the fine cellulose fiber composite obtained by combining aspect A and aspect B may be sufficient, ie, the fine cellulose fiber composite which has the modification group connected through the ionic bond and the modification group connected through the amide bond It may be a body. In this case, step (2A) and step (2B)
Either of these may be performed first.

Thus, a fine cellulose fiber composite in which the modifying group is linked to the fine cellulose fiber via an ionic bond and / or an amide bond can be obtained. In the present invention, from the viewpoint of the strength of the molded article to be obtained, a fine cellulose fiber composite in which modifying groups are connected via an amide bond is preferable.

The obtained fine cellulose fiber composite can be used in the state of the dispersion after the above-mentioned post-treatment, or by removing the solvent from the dispersion by a drying treatment or the like, A fine cellulose fiber composite can be obtained and used. Here, “powder” is a powder in which fine cellulose fiber composites are aggregated, and does not mean cellulose particles.

Examples of the powdered fine cellulose fiber composite include, for example, a dried product obtained by directly drying the dispersion of the fine cellulose fiber composite; a powder obtained by pulverizing the dried product by mechanical processing; and a dispersion of the fine cellulose fiber composite. Examples include those obtained by pulverizing a liquid by a known spray drying method; those obtained by pulverizing a dispersion of the fine cellulose fiber composite by a known freeze drying method, and the like. The spray drying method is a method in which a dispersion of the fine cellulose fiber composite is sprayed in the air and dried.

The fine cellulose fiber composite preferably has a number average fiber diameter of 0.5 nm or more, more preferably 0.8 nm or more, and still more preferably 1 nm or more from the viewpoint of improving the strength of the resulting molded article at high temperature. is there. Moreover, from the intensity | strength under the high temperature of the molded article obtained, Preferably it is 20
It is 0 nm or less, more preferably 100 nm or less, still more preferably 50 nm or less, still more preferably 20 nm or less, still more preferably 10 nm or less.

In addition, since the crystallinity does not fall by reaction of a process (2A) or a process (2B), a fine cellulose fiber composite has a crystallinity degree comparable as the crystallinity degree of the said fine cellulose fiber. Is preferred.

As described above, the fine cellulose fiber composite contained in the resin composition of the present invention has a number average fiber diameter of 0.5 nm to 200 nm and a carboxy group content of 0.1 mmo.
Since the hydrocarbon group and / or the EO / PO copolymerization part is connected to the fine cellulose fiber of 1 / g or more via an ionic bond and / or an amide bond, the number average fiber diameter is 0.
. The thing of 5 nm or more and 200 nm or less is preferable.

  The content of each component in the resin composition of the present invention is as follows.

The content of the photocurable resin precursor in the resin composition of the present invention is preferably 50% by mass or more, more preferably 75% by mass or more, and more preferably 90% by mass or more from the viewpoint of the strength of the modeled article and the modelability. More preferred is 93% by mass or more. From the same viewpoint, 99.9% by mass
The following is preferable, 99 mass% or less is more preferable, and 98 mass% or less is still more preferable.

The content of the fine cellulose fiber or the modified product thereof in the resin composition of the present invention is preferably from the viewpoint of improving the heat resistance of the resulting molded product with respect to 100 parts by mass of the photocurable resin precursor. 01 parts by mass or more, more preferably 0.1 parts by mass or more, still more preferably 0.5 parts by mass or more, still more preferably 1.0 parts by mass or more, still more preferably 2.0 parts by mass or more. From the viewpoint, it is preferably 20 parts by mass or less, more preferably 15 parts by mass or less, still more preferably 10 parts by mass or less, and still more preferably 7 parts by mass or less. In addition, content of the fine cellulose fiber here is content of the fine cellulose fiber in which the modification group is not introduce | transduced.

Moreover, when the resin composition of this invention contains the modified product of a fine cellulose fiber, content (equivalent amount) of a fine cellulose fiber is the molded article obtained with respect to 100 mass parts of photocurable resin precursors. From the viewpoint of improving heat resistance, preferably 0.01 parts by mass or more, more preferably 0
. 1 part by mass or more, more preferably 0.5 part by mass or more, further preferably 1.0 part by mass or more, and from the viewpoint of handleability, it is preferably 20 parts by mass or less, more preferably 15 parts by mass or less, still more preferably. Is 10 parts by mass or less, more preferably 7 parts by mass or less.

The content of the fine cellulose fiber or the modified product thereof in the resin composition of the present invention is preferably 0.01% by mass or more, more preferably 0.00%, from the viewpoint of improving the heat resistance of the resulting molded article.
1% by mass or more, more preferably 0.5% by mass or more, further preferably 1.0% by mass or more, more preferably 2.0% by mass or more, and from the viewpoint of handling, preferably 20% by mass or less, More preferably, it is 15 mass% or less, More preferably, it is 10 mass% or less, More preferably, it is 7 mass% or less.

Moreover, the resin composition of this invention can use a photoinitiator as components other than the above.

The photopolymerization initiator may be any known one, such as acetophenones, benzophenones, ketals, anthraquinones, thioxanthones, azo compounds, peroxides,
Examples include 2,3-dialkylcion compounds, disulfide compounds, thiuram compounds, and fluoroamine compounds. In addition, what is necessary is just to set suitably content of a photoinitiator by the kind of photoinitiator to be used.

The resin composition of the present invention includes a crystal nucleating agent, a filler (inorganic filler,
Organic fillers), hydrolysis inhibitors, flame retardants, antioxidants, hydrocarbon waxes and anionic surfactant lubricants, UV absorbers, antistatic agents, antifogging agents, light stabilizers, pigments, An antifungal agent, an antibacterial agent, a foaming agent, a surfactant, and the like can be contained as long as the effects of the present invention are not impaired. In addition, other polymer materials and other resin compositions can be added within a range that does not impair the effects of the present invention. The content of any additive may be appropriately contained as long as the effects of the present invention are not impaired. For example, the content is preferably about 10% by mass or less in the resin composition,
About 5 mass% or less is more preferable.

The resin composition of the present invention can be prepared without particular limitation as long as it contains a photocurable resin precursor and fine cellulose fibers or a modified product thereof, for example, a photocurable resin precursor and fine cellulose fibers. Or a modified material thereof, and further, if necessary, a raw material containing various additives is stirred with a Henschel mixer, an ultrasonic homogenizer, a high-pressure homogenizer or the like, or a closed kneader, a single or twin screw extruder, an open roll kneader, etc. Can be prepared by melt kneading or solvent casting using a known kneader. If necessary, solvent (
For example, ethanol) may be added and stirred, and then the solvent may be removed.

The resin composition of this invention is used for manufacture of a photocurable three-dimensional structure. As a method for preparing a photocurable three-dimensional structure, an inkjet ultraviolet curing method and an optical modeling method are known. In the inkjet ultraviolet curing method, after discharging a liquid resin composition, light is irradiated and cured to form. On the other hand, in stereolithography, after irradiating the surface of the pooled liquid resin composition with light,
Cured and shaped. Therefore, when applying the resin composition of the present invention to these methods,
It is preferable to use a resin composition having a viscosity corresponding to them.

Specifically, when using the resin composition of the present invention by inkjet ultraviolet curing method,
In the resin composition of the present invention, the viscosity at 25 ° C. is preferably 500 mPa · s or less, more preferably 300 mPa · s or less, even more preferably 150 mPa · s or less, and 130 mPa from the viewpoint of improving ejection from the nozzle of the ink cartridge. -S or less is still more preferable. Moreover, although a minimum is not specifically limited, From a handling viewpoint, 1 mPa * s or more is preferable. Moreover, when using the resin composition of the present invention in an optical modeling method, the resin composition of the present invention is
From the viewpoint of stably maintaining the cured product in the resin composition, the viscosity at 25 ° C. is 50 mPa
· S or more is preferable, 100 mPa · s or more is more preferable, 200 mPa · s or more is more preferable, and from the viewpoint of handleability, 20000 mPa · s or less is preferable and 15000 m.
Pa · s or less is more preferable, and 12000 mPa · s or less is even more preferable. In order to have the above-described viscosity, in the present invention, for example, if the content of fine cellulose fiber or a modified product thereof is increased, the viscosity can be increased, and if the content is decreased, the viscosity can be decreased. . Moreover, if the aspect ratio of the fine cellulose fiber to be used is large, the viscosity can be increased, and if the aspect ratio is small, the viscosity can be decreased. In the present specification, the viscosity is a value measured using a B-type viscometer.

Moreover, the specific gravity of the resin composition of the present invention is preferably 0.5 or more, more preferably 0.8 or more, and still more preferably 1.0 or more, from the viewpoint of improving the strength of the shaped article. There is no particular upper limit, but it may be 2.0 or less. In addition, specific gravity means ratio with the mass of 4 degreeC water of the same volume here, and can measure according to the method as described in JISZ8804.

Since the resin composition of the present invention has good handleability and the resulting molded article exhibits good strength at high temperatures, it is a precision instrument, an electrical / electronic product, a product such as an automobile, or a component or casing thereof. Can be suitably used as a material for three-dimensional modeling. Therefore, this invention also provides the manufacturing method of the optical modeling thing characterized by using the resin composition (photocurable composition of this invention) of this invention for an optical modeling apparatus.

[Method for producing stereolithography]
If the photocurable composition of this invention is used for an optical modeling apparatus, the manufacturing method of the optical modeling thing of this invention will not be specifically limited. As the optical modeling apparatus, a known apparatus can be used, and the photocurable composition of the present invention is applied according to the specifications of the apparatus, and light is irradiated according to the technical field, so that the photocurable composition of the present invention is applied. An optically shaped article can be prepared by curing. As light that can be irradiated, ultraviolet rays, electron beams, X-rays, radiation, high frequencies, and the like can be used. In addition, application of a photocurable composition and hardening by light irradiation can be performed repeatedly.

Specifically, for example, when a part or a housing is manufactured using the photocurable composition of the present invention by an ink jet method, the photocurable composition is filled in a cartridge of an inkjet apparatus, and a desired shape is formed from a nozzle. It is obtained by irradiating light and irradiating light to form a cured product layer, and then repeating the ejection and light irradiation on the layer to laminate a cured product layer.

The optically shaped product of the photocurable composition of the present invention thus obtained is excellent in mechanical strength and exhibits good strength at a high temperature. Therefore, the present invention also provides the photocurable composition of the present invention. Provides an optically shaped object. Since the optically modeled article of the present invention is optically modeled with the photocurable composition of the present invention, it can be suitably used for various applications mentioned in the above-described photocurable composition.

Hereinafter, the present invention will be specifically described with reference to examples. Note that this example is merely illustrative of the present invention and is not meant to be limiting. The parts in the examples are parts by mass unless otherwise specified. “Normal pressure” indicates 101.3 kPa, and “normal temperature” indicates 25 ° C.

[Number average fiber diameter of fine cellulose fibers]
Water is added to fine cellulose fibers to prepare a dispersion having a concentration of 0.0001% by mass,
An atomic force microscope (AFM, Nanoscope III Tapping mode AFM, Digi) was prepared by dropping the dispersion liquid onto mica (mica) and drying it.
Tal instrument, probe is Nano Sensors Point Pro
be (NCH) is used to measure the fiber height of the cellulose fibers in the observed sample. In that case, in the microscope image which can confirm this cellulose fiber, five or more fine cellulose fibers are extracted, and a number average fiber diameter is calculated from those fiber heights.

[Aspect ratio of fine cellulose fiber]
The average aspect ratio is obtained by calculating back the aspect ratio of the cellulose fiber according to the following formula (1) from the relationship between the concentration of the cellulose fiber in the dispersion and the specific viscosity of the dispersion with respect to water. In addition,
The following formula (1) is obtained from The Theory of Polymer Dynamics, M .; D
OI and D.C. F. EDWARDS, CLARENDON PRES · OXFORD
, 1986, p. 312 and the viscosity formula (8.138) of the rigid rod-like molecule and Lb ² × ρ = M
/ Relationship N _A wherein, L is the fiber length, b is the fiber width (cellulose fiber cross section is a square),
ρ is the cellulose fiber concentration (kg / m 3), ^M is the molecular weight, N _A are those derived from the representative of Avogadro's number]. Moreover, in said viscosity formula (8.138), let a rigid rod-shaped molecule | numerator be a cellulose fiber. In the following formula (1), η _SP is the specific viscosity, π is the circumference, ln is the natural logarithm, P is the aspect ratio (L / b), γ = 0.8, ρ _S is the density of the dispersion medium (kg / m ³ ), ρ
₀ is the density of cellulose crystals (kg / m ³ ), C is the mass concentration of cellulose (C = ρ / ρ _S )
Represents.

[Carboxy group content of fine cellulose fiber and fine cellulose fiber composite]
Take a fine cellulose fiber or a fine cellulose fiber composite with a dry mass of 0.5 g in a 100 mL beaker, add ion-exchanged water or a mixed solvent of methanol / water = 2/1 to make a total of 55 mL, and 0.01M sodium chloride aqueous solution there Add 5 mL to prepare a dispersion,
The dispersion is stirred until the fine cellulose fiber or fine cellulose fiber composite is sufficiently dispersed. 0.1M hydrochloric acid was added to this dispersion to adjust the pH to 2.5-3, and 0.05M sodium hydroxide aqueous solution was added using an automatic titrator (trade name “AUT-50” manufactured by Toa DKK Corporation). The solution is dropped into the dispersion under the condition of a waiting time of 60 seconds, and the conductivity and pH values are measured every minute, and the measurement is continued until the pH is about 11 to obtain a conductivity curve. From this conductivity curve, the sodium hydroxide titration amount is obtained, and the carboxy group content of the fine cellulose fiber or fine cellulose fiber composite is calculated by the following formula.
Carboxy group content (mmol / g) = sodium hydroxide titration × sodium hydroxide aqueous solution concentration (0.05 M) / mass of cellulose fiber (0.5 g)

Preparation Example 1 of Fine Cellulose Fiber (Dispersion of carboxy group-containing fine cellulose fiber (long fiber) obtained by allowing N-oxyl compound to act on natural cellulose)
Bleached kraft pulp of conifers (Fletcher Challenge Canada, trade name “Ma
enchie ", CSF 650 ml) was used as natural cellulose fiber. TEMPO
As for, the commercial item (ALDRICH company make, Free radical, 98 mass%) was used. As sodium hypochlorite, a commercially available product (manufactured by Wako Pure Chemical Industries, Ltd.) was used. A commercially available product (manufactured by Wako Pure Chemical Industries, Ltd.) was used as sodium bromide.

First, 100 g of bleached kraft pulp fiber of coniferous trees was sufficiently stirred with 9900 g of ion-exchanged water, and then TEMPO 1.25 mass%, sodium bromide 12.5 mass%, sodium hypochlorite 28 with respect to 100 g of the pulp mass. .4% by weight was added in this order. Using a pH stud, 0.5 M sodium hydroxide was added dropwise to maintain the pH at 10.5. Reaction 12
After 0 minutes (20 ° C.), dropping of sodium hydroxide was stopped to obtain oxidized pulp. The oxidized pulp obtained using ion-exchanged water was sufficiently washed and then dehydrated. after that,
3.9 g of oxidized pulp and 296.1 g of ion-exchanged water were refined twice at 245 MPa using a high-pressure homogenizer (Sugino Machine, Starburst Lab HJP-2 5005), and a carboxy group-containing fine cellulose fiber dispersion (Solid content concentration 1.3 mass%) was obtained. This fine cellulose fiber has an average fiber diameter of 3.3 nm and a carboxy group content of 1.6 m.
mol / g and the aspect ratio were 300.

Preparation Example 2 of Fine Cellulose Fiber (Dispersion of carboxy group-containing fine cellulose fiber (short fiber))
Using a high-pressure homogenizer, 100 g of the carboxy group-containing fine cellulose fiber dispersion obtained in Preparation Example 1 for fine cellulose fibers in a beaker (solid content concentration 1.3% by mass) was added.
The refinement process was performed 50 times at 45 MPa to obtain a carboxy group-containing fine cellulose fiber dispersion (solid content concentration: 1.3% by mass). The average fiber diameter of the fine cellulose fibers was 3.3 nm, the carboxy group content was 1.6 mmol / g, and the aspect ratio was 50.

Preparation Example 3 of Fine Cellulose Fiber (Carboxy Group-Containing Fine Cellulose Fiber (Long Fiber) Dispersion Obtained by Acid-Type Treatment)
Add 4088.75 g of the carboxy group-containing fine cellulose fiber dispersion obtained in Preparation Example 1 of fine cellulose fibers (solid content concentration: 1.3% by mass) and 4085 g of ion-exchanged water to a beaker to obtain a 0.5% by mass aqueous solution, The mixture was stirred with a mechanical stirrer at room temperature (25 ° C.) for 30 minutes. Subsequently, 245 g of 1M hydrochloric acid aqueous solution was added and reacted at room temperature for 1 hour. After completion of the reaction, the solution was reprecipitated with acetone, filtered, and then washed with acetone / ion exchange water to remove hydrochloric acid and salts. Finally, acetone was added and filtered to obtain an acetone-containing acid-type cellulose fiber dispersion (solid content concentration: 5.0% by mass) in which carboxy group-containing fine cellulose fibers were swollen in acetone. After completion of the reaction, the mixture was filtered, and then washed with ion exchange water to remove hydrochloric acid and salts. After solvent substitution with acetone, the solvent substitution with dimethylformamide (DMF) was performed to obtain a DMF-containing acid-type cellulose fiber dispersion (solid content concentration 5.4% by mass) in a state where the carboxy group-containing fine cellulose fibers were swollen. The average fiber diameter of the fine cellulose fibers is 3.3n.
m, the carboxy group content was 1.6 mmol / g, and the aspect ratio was 300.

Preparation Example 4 of Fine Cellulose Fiber (Carboxy Group-Containing Fine Cellulose Fiber (Short Fiber) Dispersion Obtained by Acid Type Treatment)
Add 4088.75 g of the carboxy group-containing fine cellulose fiber dispersion obtained in Preparation Example 2 of fine cellulose fibers (solid content concentration: 1.3% by mass) and 4085 g of ion-exchanged water to a beaker to obtain a 0.5% by mass aqueous solution, The mixture was stirred with a mechanical stirrer at room temperature (25 ° C.) for 30 minutes. Subsequently, 245 g of 1M hydrochloric acid aqueous solution was added and reacted at room temperature for 1 hour. After completion of the reaction, the solution was reprecipitated with acetone, filtered, and then washed with acetone / ion exchange water to remove hydrochloric acid and salts. Finally, acetone was added and filtered to obtain an acetone-containing acid-type cellulose fiber dispersion (solid content concentration: 5.0% by mass) in which carboxy group-containing fine cellulose fibers were swollen in acetone. After completion of the reaction, the mixture was filtered, and then washed with ion exchange water to remove hydrochloric acid and salts. After solvent substitution with acetone, the solvent substitution with dimethylformamide (DMF) was performed to obtain a DMF-containing acid-type cellulose fiber dispersion (solid content concentration: 6.4% by mass) in a state where the carboxy group-containing fine cellulose fibers were swollen. The average fiber diameter of the fine cellulose fibers is 3.3n.
m, the carboxy group content was 1.6 mmol / g, and the aspect ratio was 50.

Production Example 1 of Fine Cellulose Fiber Composite (Examples 1-4, 9, 10, 13, 19)
A beaker equipped with a magnetic stirrer and a stirrer was charged with 35 g of a carboxy group-containing fine cellulose fiber dispersion (solid content concentration 5.4% by mass) obtained in Preparation Example 3 of fine cellulose fibers. Subsequently, an amine of the type shown in Table 1, 2 or 4 is an amount corresponding to 1.0 mol of amine groups with respect to 1 mol of carboxy groups of fine cellulose fibers, and 4-
(4,6-dimethoxy-1,3,5-triazin-2-yl) -4-methylmorpholinium chloride (DMT-MM) was added in an amount of 2 to 1 mol of carboxy groups of fine cellulose fibers.
. An amount corresponding to 2 mol and an amount corresponding to 1.2 mol of N-methylmorpholine (NMM) with respect to the carboxy group of the fine cellulose fiber were charged and dissolved in 300 g of DMF, and the reaction solution was stirred at room temperature (25 ° C.) at 14 ° C. Reacted for hours. After completion of the reaction, filtration, washing with ion-exchanged water, removing the DMT-MM salt, washing with ethanol and solvent substitution, a fine cellulose fiber composite in which amines are linked to fine cellulose fibers via amide bonds. Obtained.

Production Example 2 of Fine Cellulose Fiber Composite (Examples 5-8, 11, 12)
A beaker equipped with a magnetic stirrer and a stirrer was charged with 35 g of a carboxy group-containing fine cellulose fiber dispersion (solid content concentration 6.4% by mass) obtained in Preparation Example 4 of fine cellulose fibers. Subsequently, DMT-M, which is a condensing agent, is added to the amine of the type shown in Table 1 or 2 in an amount corresponding to 1.0 mol of amine groups with respect to 1 mol of carboxy groups of fine cellulose fibers.
M is an amount corresponding to 2.2 mol with respect to 1 mol of carboxy group of fine cellulose fiber, N
MM was charged in an amount corresponding to 1.2 mol with respect to the carboxy group of the fine cellulose fiber, dissolved in 300 g of DMF, and the reaction solution was reacted at room temperature (25 ° C.) for 14 hours.
After completion of the reaction, filtration, washing with ion-exchanged water, removing the DMT-MM salt, washing with ethanol and solvent substitution, a fine cellulose fiber composite in which amines are linked to fine cellulose fibers via amide bonds. Obtained.

Production Example 3 of Fine Cellulose Fiber Composite (Examples 15 to 17, 20)
A beaker equipped with a magnetic stirrer and a stirrer was charged with 35 g of a carboxy group-containing fine cellulose fiber dispersion (solid content concentration 5.4% by mass) obtained in Preparation Example 3 of fine cellulose fibers. Subsequently, the amine shown in Table 3 or 4 was charged in an amount corresponding to 1.0 mol of amine groups with respect to 1 mol of carboxy groups of fine cellulose fibers, and 300 g of ion-exchanged water.
The reaction solution was reacted at room temperature (25 ° C.) for 14 hours. After completion of the reaction, the mixture was filtered, washed with ion-exchanged water, washed with ethanol, and replaced with a solvent to obtain a fine cellulose fiber composite in which amines were connected to fine cellulose fibers via ionic bonds.

Production Example 4 (Example 14) of fine cellulose fiber composite
A beaker equipped with a magnetic stirrer and a stirrer was charged with 35 g of a carboxy group-containing fine cellulose fiber dispersion (solid content concentration 5.4% by mass) obtained in Preparation Example 3 of fine cellulose fibers. Subsequently, aniline corresponds to 1.5 mol of amine groups with respect to 1 mol of carboxy groups of fine cellulose fibers, and DMT-MM as a condensing agent corresponds to 2.5 mol with respect to 1 mol of carboxy groups of fine cellulose fibers. The amount corresponding to 1.4 mol of NMM with respect to the carboxyl group of the fine cellulose fiber was charged, respectively, and DMF30
It was dissolved in 0 g, and the reaction solution was reacted at room temperature (25 ° C.) for 14 hours. After the reaction is complete, filter
By washing with ion-exchanged water, removing the DMT-MM salt, washing with ethanol and solvent substitution, a fine cellulose fiber composite in which phenyl groups were connected to fine cellulose fibers via amide bonds was obtained.
<EOPO group modification>
For 10 g of the obtained fine cellulose fiber composite dispersion (solid content concentration 5.0% by mass),
An amine having an EO / PO copolymer part (M-2070, manufactured by Mitsui Chemicals Fine Co., Ltd.) was charged in an amount corresponding to 0.06 mol of amine groups with respect to 1 mol of carboxy groups of fine cellulose fibers, and dissolved in 100 g of ion-exchanged water. The reaction solution was reacted at room temperature (25 ° C.) for 14 hours. After completion of the reaction, it is filtered, washed with ion-exchanged water, washed with ethanol, and solvent-replaced, whereby fine cellulose fibers in which phenyl groups are linked to fine cellulose fibers via amide bonds and EOPO copolymers are linked via ionic bonds. A complex was obtained.

Examples 1-17
<Acrylic resin composition>
As a photocurable resin precursor, 50 g (100 parts by mass) of OBJET FULLLCURE720 (manufactured by Stratasys, acrylic resin composition precursor), an amount shown in Tables 1 to 3 of the fine cellulose fiber composites shown in Tables 1 to 3, 20 g of ethanol was added to a beaker, stirred for 2 minutes with an ultrasonic homogenizer (US-300E, manufactured by Nippon Seiki Seisakusho), then 100 MP with a high-pressure homogenizer (Sugino Machine, Starburst Lab HJP-2 5005).
Fine processing was performed for 2 passes at a and 1 pass at 150 MPa. The homogeneous mixture was poured into a glass petri dish and vacuum-dried at 50 ° C. for 24 hours to remove the solvent component in the mixture, thereby producing a resin composition containing 0.1 part by mass of a fine cellulose fiber composite. The specific gravity and viscosity of the obtained resin composition are shown in Tables 1-3.
The viscosity is analyzed using a viscometer (Viscometer TV-35) manufactured by Toki Sangyo Co., Ltd. and a temperature control unit (ViscomateVM-150III) under the conditions of a measurement temperature of 25 ° C., a measurement time of 1 minute, a rotation speed of 1 rpm, and a rotor T1. It was. The specific gravity is JIS Z 8804.
The measurement was carried out using a 10 mL specific gravity bottle in accordance with the method described in 1. above.

<Curing of acrylic resin composition>
The obtained resin composition was uniformly coated on a polyimide film using a bar coater so as to have a thickness of about 0.4 mm, and then a UV irradiation device (Fusion Japan Light Haf).
mmer10, the light source is an H bulb manufactured by Heraeus), the lamp height is set to 67 mm, the belt speed is 15.8, and the output is set to 90% (the amount of emitted light is about 94 mJ / cm ² ).
By irradiation and curing the resin, an optically shaped article of an acrylic resin composition containing 0.1 parts by mass of a fine cellulose fiber composite was obtained. Nitrogen substitution was performed by setting an inert box in a nitrogen substitution apparatus and performing substitution for 1 minute.

Example 18
Using the DMF-containing acid-type cellulose fiber dispersion obtained in Preparation Example 3 instead of the fine cellulose fiber composite, the resin composition and the resin composition were prepared in the same manner as in Example 1 except that the blending amount was changed as shown in Table 3. An optically shaped product of the composition was produced.

Comparative Example 1
A resin composition and an optically shaped article of the composition were produced in the same manner as in Example 1 except that the fine cellulose fiber composite was not used.

Examples 19 to 20 (epoxy resin)
Implemented except that the photo-curable resin precursor used was changed to SCR774 (epoxy resin composition precursor) manufactured by DEMEC and the type and amount of the fine cellulose fiber composite used were changed as shown in Table 4. A resin composition and an optically shaped product of the composition were produced in the same manner as in Example 1.

Comparative Example 2
A resin composition and an optically shaped article of the composition were produced in the same manner as in Example 19 except that the fine cellulose fiber composite was not used.

In addition, the raw material in Tables 1-4 is as follows.
[Photocurable resin precursor]
OBJET FULLLCURE 720: Acrylic resin composition precursor, manufactured by Stratasys, SCR774 for inkjet 3D printer: Epoxy resin composition precursor, manufactured by Deemeck, for stereolithography 3D printer [Amine]
EOPO amine: Jeffamine M-2070, manufactured by HUNTSMAN, EO / P
O (molar ratio) 32/10
C18 amine: stearylamine (octadecylamine), Tokyo Kasei C12 amine: dodecylamine, Wako Pure Chemical Industries TBAH: tetrabutylammonium hydroxide (tetrabutylammonium hydroxide)
, Wani Pure Chemical Industries aniline: Wako Pure Chemical Industries

The characteristics of the obtained optically shaped object (modeled object) were evaluated according to the method of Test Example 1 below. The results are shown in Tables 1-4.

Test example 1 (storage modulus)
Using a dynamic viscoelastic device (trade name “DMS6100” manufactured by SII), a strip-shaped sample having a width of 5 mm and a length of 20 mm is subjected to a frequency of 1 Hz in a nitrogen atmosphere at a frequency of 1 Hz for 1 minute. The temperature was increased at a rate of 2 ° C. and measured in the tensile mode. Storage modulus number is 1
A value of 00 ° C. (acrylic resin) or 200 ° C. (epoxy resin) was used. It shows that it is excellent in mechanical strength, so that the value of a storage elastic modulus is large, and it is preferable that it is 6 Mpa or more in the case of an acrylic resin composition, and 90 Mpa or more in the case of an epoxy resin composition.

As is clear from the results shown in Tables 1 to 4, the resin compositions obtained in the examples have a viscosity that is better in handling than the compositions of the comparative examples, and light obtained by photocuring. Compared to the optical modeling object obtained in the comparative example, the modeling object has a high temperature of Tg or more (90 ° C. with FullCure 720).
As described above, it can be seen that the strength is expressed by SCR774 at 180 ° C. or higher.

<Acrylic resin precursor composition>
A fine cellulose fiber composite obtained by connecting EOPO amines (M-2070, manufactured by Mitsui Chemicals Fine Co., Ltd.) through an amide bond in the same manner as in Production Example 2 of the fine cellulose fiber composite has a solid content of 0.5 g. In a beaker, as a photocurable resin precursor, Ful
lCure 720 (Stratasys, acrylic resin composition) 50 g, ethanol 20
g in succession, and 2 with an ultrasonic homogenizer (US-300E, manufactured by Nippon Seiki Seisakusho).
Stir for minutes, high pressure homogenizer (Sugino Machine, Starburst Lab HJP-2
In 5005), two passes are performed at 100 MPa and one pass is processed at 150 MPa. The homogeneous mixture is poured into a glass petri dish and vacuum-dried at 50 ° C. for 24 hours to remove the solvent component in the mixture, thereby producing a resin composition containing 1 part by mass of the fine cellulose fiber composite.

<Creation of stereolithography using inkjet stereolithography apparatus>
The obtained resin composition was used as an ink cartridge (Dimatix DMP) manufactured by Fujifilm Corporation.
-2831), the cartridge temperature is set to 70 ° C., and a waveform pattern of the Dimatix standard pattern is input and discharged. Then, using a UV irradiation device (Light Hammer 10 manufactured by Fusion Japan, the light source is an H bulb manufactured by Heraeus), the lamp height is 6
Set to 7 mm, belt speed 15.8, output 90% (radiated light intensity approx. 94 mJ / cm ² )
, UV irradiation after nitrogen substitution to cure the resin, 1 fine cellulose fiber composite
It is possible to obtain a heat-resistant thin-film optically shaped article made of an acrylic resin composition containing part by mass. Further, by repeating the above steps a predetermined number of times, it is possible to obtain a heat-resistant optically shaped object having a three-dimensional thickness.

The photocurable composition for three-dimensional modeling of the present invention can be suitably used as a material for three-dimensional modeling of products such as precision instruments, electrical / electronic products, automobiles, or parts or casings thereof.

Claims (8)

A) containing a photocurable resin precursor, and B) a fine cellulose fiber having a number average fiber diameter of 0.5 nm to 200 nm and a carboxy group content of 0.1 mmol / g or more and / or a modified product thereof. A photocurable composition for three-dimensional modeling. Fine cellulose fibers oxidize natural cellulose fibers in the presence of N-oxyl compounds,
The photocurable composition according to claim 1, which is obtained by a production method including a step of obtaining a carboxy-containing cellulose fiber. The photo-curing property according to claim 1 or 2, wherein the modified product of the fine cellulose fiber is obtained by introducing a hydrocarbon group or an ethylene oxide / propylene oxide (EO / PO) copolymer part into a carboxy group of the fine cellulose fiber. Composition. The photocurable composition according to claim 3, wherein the introduction of a hydrocarbon group or an ethylene oxide / propylene oxide (EO / PO) copolymerized part is via an amide bond and / or an ionic bond. The light according to any one of claims 1 to 4, wherein the A) photocurable resin precursor is one or more selected from the group consisting of acrylic resins, (meth) acrylic resins, and epoxy resins. Curable composition. B) Content of fine cellulose fiber and / or modified product thereof is A) photocurable resin precursor 1
The photocurable composition according to any one of claims 1 to 5, which is 0.01 parts by mass or more and 20 parts by mass or less with respect to 00 parts by mass. The photocurable composition according to any one of claims 1 to 6 is used in an optical modeling apparatus,
A manufacturing method of a stereolithography.   An optically shaped article obtained by the manufacturing method according to claim 7.