JP2019089585A - Packaging body - Google Patents
Packaging body Download PDFInfo
- Publication number
- JP2019089585A JP2019089585A JP2017219587A JP2017219587A JP2019089585A JP 2019089585 A JP2019089585 A JP 2019089585A JP 2017219587 A JP2017219587 A JP 2017219587A JP 2017219587 A JP2017219587 A JP 2017219587A JP 2019089585 A JP2019089585 A JP 2019089585A
- Authority
- JP
- Japan
- Prior art keywords
- lid
- layer
- heat
- flange
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
この発明は、食品、医薬品、化粧品、ウェットティッシュ、電子部品等の内容物が充填された容器のフランジに蓋をシールしてなる包装体に関し、より詳細には、未開封時には内容物を密封状態で包装することができるとともに、開封後に蓋を再シールすることができる、再封可能な包装体に関する。 The present invention relates to a package in which a lid is sealed on a flange of a container filled with contents such as food, pharmaceuticals, cosmetics, wet tissues, electronic parts, etc. More specifically, the contents are sealed when unopened And a reclosable package that can be resealed and the lid can be resealed after opening.
例えば、食品等を内容物とする再封可能な包装体として、下記の特許文献１に記載のものが知られている。
この包装体は、開口周縁にフランジを有している容器と、内容物が充填された容器の開口を塞ぐようにフランジに剥離可能に熱融着されかつ外周部における周方向の一部にフランジよりも外方に突出した開封用タブを有している蓋とを備えているものであって、蓋が、内層（熱融着性樹脂層）、粘着剤層、および外層（アルミニウム箔層、外側樹脂層等）を有しており、蓋材の内層における熱融着部の外側部分および内側部分にそれぞれハーフカットラインが形成されたものである。
上記の包装体によれば、開封用タブを引き上げると、蓋が、外側のハーフカットの位置から内側のハーフカットの位置まで、内層と粘着剤層との間で剥離し、容器のフランジから分離されることにより、開封が行われる。この開封に伴い、蓋の内層における内側のハーフカットよりも外側部分が容器のフランジ側に残るとともに、同部分の粘着剤層が露出させられる。そして、露出した粘着剤層の部分を容器のフランジ上面に重ねることにより、再封が行われる。
しかしながら、上記の包装体の場合、いったん開封した後でも、蓋を閉じて再封すれば開封に気が付かないこともあるため、衛生面や安全面で問題があった。
For example, the thing of the following patent document 1 is known as a reclosable package which makes a food etc. a content.
This package is releasably heat-sealable to the flange so as to close the opening of the container filled with the contents and the container having the flange at the opening periphery, and the flange in a circumferential direction at the outer peripheral portion And a lid having an opening tab projecting more outward than the lid, the lid comprising an inner layer (heat fusible resin layer), an adhesive layer, and an outer layer (aluminum foil layer, An outer resin layer or the like is provided, and a half cut line is formed on each of the outer and inner portions of the heat-sealed portion in the inner layer of the lid.
According to the above package, when the opening tab is pulled up, the lid peels between the inner layer and the adhesive layer from the outer half cut position to the inner half cut position and separates from the container flange Opening is performed by being done. With this opening, the outer portion of the inner layer of the lid remains on the flange side of the container rather than the inner half cut, and the adhesive layer of the same portion is exposed. And resealing is performed by overlapping the part of the exposed adhesive layer on the flange upper surface of a container.
However, in the case of the above-mentioned package, even if it is once opened, if the lid is closed and resealed, it may not be noticed that the package is opened, so there were problems in terms of hygiene and safety.
下記の特許文献２には、開封検知機能を備えた再封可能な包装体が開示されている。この包装体は、蓋が表面樹脂層、粘着樹脂層、剥離樹脂層およびヒートシール樹脂層を有しており、ヒートシール部において粘着樹脂層と剥離樹脂層とを層間剥離させることにより蓋を開封した後、再封する際に再封箇所が白く見えるようにしたものである。
しかしながら、上記特許文献２記載の包装体の場合、蓋の材料として不透明なアルミニウム箔等の金属箔を使用すると開封検知機能が損なわれてしまうので、使用することができなかった。従って、上記特許文献２記載の包装体では、蓋のバリア性を確保することが難しく、長期保存が必要な内容物の包装には適していなかった。
However, in the case of the package described in
この発明は、上記の課題に鑑みてなされたものであって、蓋の材料としてバリア性に優れた金属を使用しながら、開封検知機能を備えている、再封可能な包装体を提供することを目的としている。 This invention is made in view of said subject, Comprising: While using the metal excellent in the barrier property as a material of a lid, providing the resealable package provided with the opening detection function. It is an object.
この発明は、上記の目的を達成するために、以下の態様からなる。 This invention consists of the following aspects, in order to achieve said objective.
１）開口周縁にフランジを有している容器と、内容物が充填された容器の開口を塞ぐようにフランジに剥離可能に熱融着されかつ外周部における周方向の一部に開封用タブを有している蓋とを備えており、蓋は、下面側から順次積層された熱融着性樹脂層、再封用粘着層および金属層を有しており、容器のフランジの上面が、蓋の熱融着性樹脂層と熱融着可能な熱融着性樹脂層によって構成されており、開封用タブを引き上げて蓋を剥離させることにより、蓋の下面の外周部に再封用粘着層が露出するようになされている包装体であって、
蓋のうち平面よりみて容器のフランジと蓋との熱融着部に重なる環状帯域に、その一部を蓋の上面側から押圧して少なくとも金属層を分断させる型押し部が形成されており、蓋の剥離に伴い金属層における型押し部に対応する箇所に生じた欠落部を蓋の上面側から視認しうるようになされている、包装体。
1) A container having a flange at the periphery of the opening, and the flange releasably heat-sealed to the flange so as to close the opening of the container filled with contents and an opening tab at a part in the circumferential direction at the outer peripheral portion And a lid having a heat-sealable resin layer, an adhesive layer for resealing and a metal layer sequentially laminated from the lower surface side, and the upper surface of the flange of the container is the lid. The heat-sealable resin layer and the heat-sealable heat-sealable resin layer, and by pulling up the opening tab and peeling the lid, the pressure-sensitive adhesive layer for resealing on the outer peripheral portion of the lower surface of the lid Is a package that is made to be exposed,
In the annular zone of the lid overlapping the heat fusion between the flange of the container and the lid as viewed from the top, a stamped portion is formed that presses a part of the lid from the upper surface side of the lid to divide at least the metal layer; The package which is made to be able to visually recognize from the upper surface side of a lid the missing part which arose in the location corresponding to the embossing part in a metal layer with peeling of a lid.
２）型押し部は、前記環状帯域の幅方向の大きさが、１ｍｍ以上かつ前記環状帯域の幅の２分の１未満となされている、上記１）の包装体。 2) The package according to the above 1), wherein the size of the annular zone in the width direction is 1 mm or more and less than half the width of the annular zone.
３）蓋が、金属層の上面に積層された外側樹脂層をさらに有しており、外側樹脂層は、金属層のヤング率よりも小さいヤング率を有している、上記１）または２）の包装体。 3) The lid further has an outer resin layer laminated on the upper surface of the metal layer, and the outer resin layer has a Young's modulus smaller than that of the metal layer, 1) or 2). Package body.
上記１）の包装体によれば、蓋がバリア性に優れた金属層を有しているので、内容物の劣化や変質を防止して長期保存することが可能である。
しかも、上記１）の包装体によれば、蓋のうち平面よりみて熱融着部に重なる環状帯域に、その一部を蓋の上面側から押圧して少なくとも金属層を分断させる型押し部が形成されており、蓋の剥離に伴い金属層の型押し部対応箇所に生じた欠落部を蓋の上面側から視認することができるので、例えば店舗において、いたずら行為等により、蓋がいったん開封された後で再封されたとしても、開封を確実に検知することができ、衛生面および安全面での問題を回避することができる。
According to the package of the above 1), since the lid has the metal layer excellent in the barrier property, it is possible to prevent deterioration and deterioration of the contents and to save for a long time.
And according to the package of said 1), the embossing part which presses a part from the upper surface side of a lid and divides at least a metal layer into an annular zone which overlaps with a heat sealing part seeing from a plane among the lids The lid is formed, and the missing part produced at the location corresponding to the embossed part of the metal layer can be viewed from the upper surface side of the lid as the lid is peeled off. For example, in a store, the lid is once opened by mischief etc. Even if it is resealed after that, the opening can be reliably detected, and the problems in terms of hygiene and safety can be avoided.
上記２）の包装体によれば、型押し部の環状帯域幅方向の大きさが、１ｍｍ以上かつ環状帯域の幅の２分の１未満となされているので、以下のような問題を回避することができる。すなわち、型押し部の前記大きさが１ｍｍ未満であると、蓋の剥離によって金属層に生じる欠落部が小さくなりすぎて、蓋の上面側から視認しにくくなるおそれがある。一方、型押し部の前記大きさが環状帯域の幅の２分の１以上になると、蓋の剥離によって蓋の下面に生じる再封用粘着部の面積が小さくなり、蓋の再シールが不十分となって再封性が損なわれるおそれがある。 According to the package of the above 2), the size in the annular band width direction of the stamped portion is 1 mm or more and less than half the width of the annular band, so the following problems are avoided. be able to. That is, when the size of the embossed portion is less than 1 mm, the missing part produced in the metal layer due to peeling of the lid becomes too small, which may make it difficult to visually recognize from the upper surface side of the lid. On the other hand, when the size of the embossed portion is at least a half of the width of the annular zone, the area of the resealing adhesive portion produced on the lower surface of the lid due to peeling of the lid becomes small, and resealing of the lid is insufficient. And the resealability may be impaired.
上記３）の包装体によれば、蓋が、金属層の上面に積層された外側樹脂層をさらに有しており、外側樹脂層は、金属層のヤング率よりも小さいヤング率を有しているので、蓋が剥離された際、蓋の型押し部対応箇所において金属層が欠落したとしても、その上層の外側樹脂層は欠落せずに蓋に残りやすくなり、蓋の強度が保持される。 According to the package of the above 3), the lid further has an outer resin layer laminated on the upper surface of the metal layer, and the outer resin layer has a Young's modulus smaller than that of the metal layer Therefore, when the lid is peeled off, even if the metal layer is missing at the location corresponding to the embossed part of the lid, the outer resin layer of the upper layer is likely to remain on the lid without being missing, and the strength of the lid is maintained .
以下、この発明の実施形態を、図１〜図４を参照して説明する。
図示の包装体(1)は、食品や医薬品等の内容物(5)を、容器(2)および蓋(3)を用いて密封包装してなるものである。
Hereinafter, an embodiment of the present invention will be described with reference to FIGS. 1 to 4.
The illustrated package body (1) is formed by sealing and packaging contents (5) such as food and medicine using a container (2) and a lid (3).
容器(2)は、複合シート(20)を深絞り成形してなるカップ状のものである。より具体的には、容器(2)は、底壁（図示略）と、底壁の周縁から立ち上がった周壁(2a)とを備えている。また、容器(2)は、その上方開口周縁にフランジ(2b)を有している。フランジ(2b)は、周壁(2a)の上端縁から径方向外方に向かって水平に張り出したフラットな形状のものである。なお、容器は、図示の形状には限定されない。 The container (2) is in the form of a cup formed by deep drawing the composite sheet (20). More specifically, the container (2) comprises a bottom wall (not shown) and a peripheral wall (2a) rising from the periphery of the bottom wall. Moreover, the container (2) has a flange (2b) in the upper opening periphery. The flange (2b) has a flat shape horizontally projecting radially outward from the upper end edge of the peripheral wall (2a). The container is not limited to the illustrated shape.
蓋(3)は、所定の寸法および形状にカットされた複合シート(30)からなり、内容物(5)が充填された容器(2)の上方開口を塞ぐように、その下面の外周部が容器(2)のフランジ(2b)の上面に剥離可能に熱融着されている。
蓋(3)には、外周部における周方向の一部にフランジ(2b)よりも外方に突出した開封用タブ(3a)が設けられている。図示のタブ(3a)は、蓋(3)の外周部の一部から径方向外方に向かって張り出すように形成された平面より見て略三角形状のものであって、蓋(3)の開封時に手指で摘めるようになっている。
The lid (3) is composed of a composite sheet (30) cut to a predetermined size and shape, and the outer peripheral portion of the lower surface is closed so as to close the upper opening of the container (2) filled with the contents (5). Peelably heat-sealed to the upper surface of the flange (2b) of the container (2).
The lid (3) is provided with an opening tab (3a) which protrudes outward beyond the flange (2b) in a part of the outer peripheral portion in the circumferential direction. The illustrated tab (3a) has a substantially triangular shape as viewed from a plane formed to project radially outward from a part of the outer peripheral portion of the lid (3), and the lid (3) It is possible to pick it with your fingers when opening the container.
図２および図３に示すように、容器(2)を構成している複合シート(20)は、基材層(21)と、基材層(21)の内面に積層された熱融着性樹脂層(22)とを備えている。
基材層(21)は、片面が熱融着性樹脂層(22)に接着剤層(23)を介して積層された金属箔層(211)と、金属箔層(211)の他面に接着剤層(24)を介して積層された外側樹脂層(212)とよりなる。
金属箔層(211)は、内容物(5)の保存性を高めるバリア層として機能するものであって、例えば、アルミニウム（アルミニウム合金を含む。以下同じ。）箔、ステンレス鋼箔、銅箔、ニッケル箔、鉄箔によって構成される。
外側樹脂層(212)は、例えば、ポリエチレンテレフタレート樹脂（ＰＥＴ）、ポリブチレンテレフタレート樹脂（ＰＢＴ）、ポリアミド樹脂（ＰＡ）、ポリエチレンナフタレート樹脂（ＰＥＮ）、ポリブチレンナフタレート樹脂（ＰＢＮ）、ポリプロピレン樹脂（ＰＰ）からなる単層または多層のフィルムによって構成される。
金属箔層(211)と熱融着性樹脂層(22)との間に介在される接着剤層(23)、および金属箔層(211)と外側樹脂層(212)との間に介在される接着剤層(24)は、それぞれ、２液硬化型のポリエステル−ポリウレタン樹脂系接着剤やポリエーテル−ポリウレタン樹脂系接着剤等によって構成される。
熱融着性樹脂層(22)は、容器(2)の最内層、すなわち、底壁の上面、周壁(2a)の内面、およびフランジ(2b)の上面を構成するものであって、フランジ(2b)に熱融着（ヒートシール）性を付与する役割を担っており、また、金属箔層(211)が内容物(5)との接触によって腐食するのを防止する機能も有している。この熱融着性樹脂層(22)は、例えば、ポリエチレン樹脂（ＰＥ）フィルム、ポリプロピレン樹脂（ＰＰ）フィルム等の汎用性フィルム、または、これらの複合フィルムによって構成される。
As shown in FIG. 2 and FIG. 3, the composite sheet (20) constituting the container (2) has a heat-sealing property laminated on the base material layer (21) and the inner surface of the base material layer (21) And a resin layer (22).
The base layer (21) is formed on the other side of the metal foil layer (211) and the metal foil layer (211), one side of which is laminated on the heat-fusible resin layer (22) with the adhesive layer (23) interposed. And an outer resin layer (212) laminated via an adhesive layer (24).
The metal foil layer (211) functions as a barrier layer that enhances the storage stability of the contents (5), and, for example, aluminum (including an aluminum alloy, hereinafter the same) foil, stainless steel foil, copper foil, Composed of nickel foil and iron foil.
The outer resin layer (212) may be, for example, polyethylene terephthalate resin (PET), polybutylene terephthalate resin (PBT), polyamide resin (PA), polyethylene naphthalate resin (PEN), polybutylene naphthalate resin (PBN), polypropylene resin It is comprised by the film of the single layer or multilayer which consists of (PP).
An adhesive layer (23) interposed between the metal foil layer (211) and the heat sealable resin layer (22), and between the metal foil layer (211) and the outer resin layer (212) The adhesive layer (24) is composed of a two-part curable polyester-polyurethane resin adhesive, a polyether-polyurethane resin adhesive, and the like.
The heat fusible resin layer (22) constitutes the innermost layer of the container (2), ie, the upper surface of the bottom wall, the inner surface of the peripheral wall (2a), and the upper surface of the flange (2b) It plays a role of imparting heat sealing property to 2b), and also has a function of preventing corrosion of the metal foil layer (211) due to contact with the contents (5) . The heat fusible resin layer (22) is made of, for example, a versatile film such as a polyethylene resin (PE) film, a polypropylene resin (PP) film, or a composite film thereof.
蓋(3)を構成する複合シート(30)は、蓋(3)の上面となる側から順次積層された外側樹脂層(31)、金属層(32)、再封用粘着層(33)、熱融着性樹脂層(34)を備えている（図２，３参照）。
外側樹脂層(31)は、蓋(3)の上面を構成するものであって、例えば、ポリエチレンテレフタレート樹脂（ＰＥＴ）、ポリブチレンテレフタレート樹脂（ＰＢＴ）、ポリアミド樹脂（ＰＡ）、ポリエチレンナフタレート樹脂（ＰＥＮ）、ポリブチレンナフタレート樹脂（ＰＢＮ）、ポリプロピレン樹脂（ＰＰ）からなる単層または多層の透明なフィルムによって構成される。外側樹脂層(31)の厚さは、通常５〜２００μｍ程度（好適には１０〜３０μｍ程度）となされる。また、外側樹脂層(31)は、上記フィルムに代えて、例えばエポキシ樹脂、アクリル樹脂等の熱硬化性架橋性樹脂よりなるオーバーコート層によって構成することもできる。
金属層(32)は、内容物(5)の保存性を高めるバリア層として機能するものであって、例えば、アルミニウム箔、ステンレス鋼箔、銅箔、ニッケル箔、鉄箔によって構成される。金属層(32)をアルミニウム箔によって構成する場合、その厚さは、好適には３０μｍ以下（より好適には５〜３０μｍ）となされる。その他、金属層(32)は、アルミニウム等の金属蒸着膜によって構成されていてもよい。金属蒸着膜の場合、好適には０．２〜１μｍ程度の膜厚となされる。
また、外側樹脂層(31)は、金属層(32)のヤング率よりも小さいヤング率を有するものを使用するのが好ましく、それによって型押し時の金属層(32)の切断が早く起きやすくなり、開封検知機能を付加させやすくすることができる。例えば、金属層(32)としてヤング率が７０ＧＰａであるアルミニウムを用いた場合、外側樹脂層(31)には、ポリプロピレン樹脂（ＰＰ）（ヤング率：２ＧＰａ）やポリエチレンテレフタレート樹脂（ＰＥＴ）（ヤング率：４ＧＰａ）のようなアルミウムに比べてヤング率が十分に小さい熱可塑性樹脂を用いることが好ましい。
外側樹脂層(31)を構成するフィルムと金属層(32)を構成する金属箔との積層は、例えば２液硬化型のポリエステル−ポリウレタン樹脂系接着剤やポリエーテル−ポリウレタン樹脂系接着剤等よりなる透明な接着剤層(35)を介して行われる。
再封用粘着層(33)は、開封後の蓋(3)を容器(2)のフランジ(2b)上面に再シールするためのものである。粘着層(33)を構成する粘着剤としては、再シール時に要求される粘着強度等に応じて、天然ゴム系、アクリル樹脂系、シリコン樹脂、ウレタン樹脂系などの粘着剤の中から適宜のものが用いられる。
熱融着性樹脂層(34)は、蓋(3)の最下層（最内層）を構成しており、蓋(3)に熱融着（ヒートシール）性を付与するものである。熱融着性樹脂層(34)は、例えば、ポリエチレン樹脂（ＰＥ）フィルム、ポリプロピレン樹脂（ＰＰ）フィルム等の汎用性フィルム、または、これらの複合フィルムであって、容器(2)の熱融着性樹脂層(22)との熱融着による強接着が可能なものによって構成されるが、好適には、容器(2)の熱融着性樹脂層(22)と同一の材料によって構成される。熱融着性樹脂層(34)の厚さは、通常１５〜１００μｍ程度となされる。
The composite sheet (30) constituting the lid (3) is an outer resin layer (31), a metal layer (32), an adhesive layer for resealing (33), sequentially laminated from the side to be the upper surface of the lid (3) A heat fusible resin layer (34) is provided (see FIGS. 2 and 3).
The outer resin layer (31) constitutes the upper surface of the lid (3), and for example, polyethylene terephthalate resin (PET), polybutylene terephthalate resin (PBT), polyamide resin (PA), polyethylene naphthalate resin ( PEN), a polybutylene naphthalate resin (PBN), and a polypropylene resin (PP) are constituted by a single-layer or multilayer transparent film. The thickness of the outer resin layer (31) is usually about 5 to 200 μm (preferably about 10 to 30 μm). Also, the outer resin layer (31) may be made of an overcoat layer made of a thermosetting crosslinkable resin such as an epoxy resin or an acrylic resin, instead of the above-mentioned film.
The metal layer (32) functions as a barrier layer that enhances the storability of the contents (5), and is made of, for example, aluminum foil, stainless steel foil, copper foil, nickel foil, iron foil. When the metal layer (32) is made of aluminum foil, its thickness is preferably 30 μm or less (more preferably 5 to 30 μm). In addition, the metal layer (32) may be formed of a metal vapor deposition film of aluminum or the like. In the case of a metal deposition film, the film thickness is preferably about 0.2 to 1 μm.
In addition, it is preferable to use the outer resin layer (31) having a Young's modulus smaller than the Young's modulus of the metal layer (32), whereby cutting of the metal layer (32) at the time of embossing tends to occur quickly. This makes it easy to add the unsealing detection function. For example, when aluminum having a Young's modulus of 70 GPa is used as the metal layer (32), polypropylene resin (PP) (Young's modulus: 2 GPa) or polyethylene terephthalate resin (PET) (Young's modulus) is used for the outer resin layer (31). It is preferable to use a thermoplastic resin having a Young's modulus sufficiently smaller than that of aluminum such as 4 GPa).
The lamination of the film constituting the outer resin layer (31) and the metal foil constituting the metal layer (32) is carried out, for example, from a two-component curing type polyester-polyurethane resin adhesive or polyether-polyurethane resin adhesive etc. Through a transparent adhesive layer (35).
The resealable pressure-sensitive adhesive layer (33) is for resealing the opened lid (3) on the upper surface of the flange (2b) of the container (2). As the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer (33), an appropriate pressure-sensitive adhesive selected from natural rubber-based, acrylic resin-based, silicone resin, urethane resin-based and the like depending on adhesive strength required at the time of resealing Is used.
The heat fusible resin layer (34) constitutes the lowermost layer (innermost layer) of the lid (3), and imparts heat sealing (heat sealing) property to the lid (3). The heat fusible resin layer (34) is, for example, a versatile film such as a polyethylene resin (PE) film, a polypropylene resin (PP) film, or a composite film thereof, and heat fusible of the container (2) Of the heat-sealable resin layer (22), but it is preferably made of the same material as the heat-sealable resin layer (22) of the container (2) . The thickness of the heat fusible resin layer (34) is usually about 15 to 100 μm.
容器(2)のフランジ(2b)と蓋(3)との熱融着は、例えば、熱板方式、すなわち、容器(2)のフランジ(2b)の上面に蓋(3)の下面の外周部が重ねられた状態で、同重ね合わせ部分に、所定温度に加熱された熱板を所定時間、所定圧力で押し当てることによって行われる。 The thermal fusion between the flange (2b) and the lid (3) of the container (2) is, for example, a hot plate method, that is, the outer periphery of the lower surface of the lid (3) on the upper surface of the flange (2b) of the container (2) In a state in which the heat plates are stacked, a heat plate heated to a predetermined temperature is pressed against the same overlapping portion for a predetermined time at a predetermined pressure.
図２に示すように、蓋(3)には、平面よりみて容器(2)のフランジ(2b)と蓋(3)との熱融着部(4)に重なる環状帯域(3X)に、その一部を蓋(3)の上面側から押圧して少なくとも金属層(32)を分断させる型押し部(36)が形成されている。この型押し部(36)により、後述するように、蓋(3)の剥離に伴って金属層(32)の型押し部対応箇所に欠落部(321)が生じ、この欠落部(321)を蓋(3)の上面側から視認することができる。
型押し部(36)は、環状帯域(3X)の全周にわたって円環状に形成される場合（図４（ａ）参照）や、環状帯域(3X)の周方向の一部、特に開封用タブ(3a)がある側の部分に円弧状に形成される場合がある（図４（ｂ）参照）。また、型押し部(36)は、例えば星形やハート形といったデザイン性のある形状のものとして、環状帯域(3X)の周方向に所定間隔をおいて複数個形成するようにしてもよい（図４（ｃ）参照）。
型押し部(36)の大きさは、少なくとも環状帯域(3X)内に収まるものであればよいが、好適には、環状帯域(3X)の幅方向の大きさが、１ｍｍ以上でかつ環状帯域(36)の幅の２分の１未満となされ、それによって金属層欠落部(321)の視認性（開封検知性）および再封性が確保される。
型押し部(36)の形成は、容器(2)のフランジ(2b)に熱融着された蓋(3)の上面の所要箇所に、所定形状の押し型(6)を押し付けることにより行われる。この際、例えば押し型(6)を予め所定温度に加熱しておいて、蓋(3)の押し付け箇所に熱を加えるようにしてもよい。押し型(6)による蓋(3)の押圧は、少なくとも金属層(32)を分断させる程度のものであればよいが、金属層(32)に加えて外側樹脂層(31)および接着剤層(35)も分断させるようにしてもよい。
As shown in FIG. 2, the lid (3) comprises an annular zone (3X) overlapping the heat sealing portion (4) of the flange (2b) of the container (2) and the lid (3) in plan view A stamped portion (36) is formed which presses a portion from the upper surface side of the lid (3) to divide at least the metal layer (32). By this embossing part (36), as will be described later, a missing part (321) is produced at the location corresponding to the embossing part of the metal layer (32) as the lid (3) is peeled off. It can be viewed from the top side of the lid (3).
The embossing portion (36) is formed in an annular shape over the entire circumference of the annular zone (3X) (see FIG. 4 (a)) or a part of the annular zone (3X) in the circumferential direction, particularly the opening tab (3a) It may be formed in the shape of a circular arc in the portion on the side (see FIG. 4 (b)). Further, a plurality of embossed portions (36) may be formed at predetermined intervals in the circumferential direction of the annular band (3X), for example, as a shape having a design property such as a star shape or a heart shape. See FIG. 4 (c)).
The size of the embossed portion (36) may be at least within the annular zone (3X), but preferably the size in the width direction of the annular zone (3X) is 1 mm or more and the annular zone The width is smaller than a half of the width of (36), whereby the visibility (open detection property) and the resealability of the metal layer missing portion (321) are secured.
The formation of the embossed portion (36) is carried out by pressing a pressing die (6) of a predetermined shape against a required place on the upper surface of the lid (3) heat-sealed to the flange (2b) of the container (2) . At this time, for example, the pressing mold (6) may be heated in advance to a predetermined temperature, and heat may be applied to the pressing portion of the lid (3). The pressing of the lid (3) by the pressing mold (6) may be at least a level that divides the metal layer (32), but in addition to the metal layer (32), the outer resin layer (31) and the adhesive layer (35) may also be divided.
上記の包装体(1)にあっては、未開封状態では、金属箔層(211)を有する容器(2)および金属層(32)を有する蓋(3)によって内容物(5)が密封包装されているので（図１，２参照）、内容物(5)を劣化、変質させることなく長期保存することができる。 In the case of the above package (1), in the unopened state, the container (2) having the metal foil layer (211) and the lid (3) having the metal layer (32) tightly seal the contents (5) As the contents (5, 2) are stored (see FIGS. 1 and 2), the contents (5) can be stored for a long time without deterioration or deterioration.
そして、内容物(5)を必要な数量ずつ取り出して使用する場合、蓋(3)の開封用タブ(3a)を手指で摘んで引き上げると、熱融着部(4)の外端縁付近において、蓋(3)の熱融着性樹脂層(34)が破断して、熱融着性樹脂層(34)と粘着層(33)との間で界面剥離が起こり、次いで、熱融着部(4)の内端縁付近で、蓋(3)の熱融着性樹脂層(34)が再び破断することにより、蓋(3)がフランジ(2b)上面から分離して開封される（図３参照）。そして、蓋(3)の剥離により、図３に示すように、蓋(3)下面の外周部に、粘着層(33)が、熱融着部(4)とほぼ等しい幅で露出させられる。
また、蓋(3)の剥離に伴い、蓋(3)の金属層(32)のうち型押し部(36)によって分断された部分（322）が、フランジ(2b)上面に付着したまま残る（図３（ａ）参照）。あるいは、金属層(32)の分断された部分（322）が、外側樹脂層(31)および接着剤層(35)の型押し部(36)によって分断された部分(312)(352)とともに、フランジ(2b)上面に付着したまま残る（図３（ｂ）参照）。
これにより、金属層(32)の環状帯域(32X)に欠落部(321)が生じるが、この欠落部(321)は、透明な外側樹脂層(31)および接着剤層(35)を通して（図３（ａ）参照）、あるいは、外側樹脂層(31)および接着剤層(35)の欠落した部分(311)(351)を通して（図３（ｂ）参照）、蓋(3)の上面側から視認することができる。実際には、欠落部(321)は、蓋(3)が金属層(32)の分断された部分(322)と重なった位置に再シールされたとしても、蓋(3)の他の部分と比べて白っぽく見えることが多い。
And when taking out and using the content (5) by a necessary quantity, when the opening tab (3a) of the lid (3) is picked up with fingers and pulled up, in the vicinity of the outer end edge of the heat sealing part (4) And the thermally fusible resin layer (34) of the lid (3) is fractured to cause interfacial peeling between the thermally fusible resin layer (34) and the adhesive layer (33), and then the thermally fused portion In the vicinity of the inner edge of (4), the heat fusible resin layer (34) of the lid (3) is broken again, so that the lid (3) is separated from the upper surface of the flange (2b) and opened (Figure 3). Then, by peeling off the lid (3), as shown in FIG. 3, the adhesive layer (33) is exposed on the outer peripheral portion of the lower surface of the lid (3) with a width substantially equal to that of the heat-sealing part (4).
Further, with the peeling of the lid (3), the part (322) of the metal layer (32) of the lid (3) divided by the embossing portion (36) remains attached to the upper surface of the flange (2b) ( See FIG. 3 (a)). Alternatively, the divided portion (322) of the metal layer (32) together with the portion (312) (352) divided by the embossing portion (36) of the outer resin layer (31) and the adhesive layer (35) It remains attached to the upper surface of the flange (2b) (see FIG. 3 (b)).
As a result, a missing portion (321) occurs in the annular zone (32X) of the metal layer (32), and this missing portion (321) passes through the transparent outer resin layer (31) and the adhesive layer (35) (see FIG. 3 (a)) or through the missing part (311) (351) of the outer resin layer (31) and the adhesive layer (35) (see FIG. 3 (b)), from the upper surface side of the lid (3) It can be viewed visually. In fact, the missing part (321), even if the lid (3) is resealed in a position where the lid (3) overlaps the split part (322) of the metal layer (32), It often looks whiter than it does.
内容物(5)の取り出しが終わったら、開封した蓋(3)を未開封時の位置に戻すようにフランジ(2b)上面に重ねていくと、蓋(3)が、その下面の外周部に形成された再封用粘着層(33)の露出部(331)によって、フランジ(2b)上面に貼り付けられ、それによって蓋(3)の再シールが行われ、残った内容物(5)を再び密封状態で保存することが可能となる。
この再封状態において、図４に示すように、蓋(3)の上面側から金属層(32)の欠落部(321)を視認することができるので、例えば店舗でいたずら行為により蓋(3)が開封された後に再封された場合でも、開封されたことを簡単に検知することができる。
After taking out the contents (5), the lid (3) is put on the outer peripheral part of the lower surface when it is put on the upper surface of the flange (2b) so that the opened lid (3) is returned to the unopened position. The exposed portion (331) of the formed resealable adhesive layer (33) is attached to the upper surface of the flange (2b), whereby the lid (3) is resealed and the remaining contents (5) It is possible to store it in a sealed state again.
In this resealed state, as shown in FIG. 4, the missing part (321) of the metal layer (32) can be visually recognized from the upper surface side of the lid (3). For example, the lid (3) Even when resealed after being opened, it can be easily detected that it has been opened.
次に、この発明の具体的実施例について説明するが、この発明は、この実施例に限定されるものではない。 Next, specific examples of the present invention will be described, but the present invention is not limited to these examples.
まず、ＪＩＳ Ｈ４１６０で分類されたＡ８０７９Ｈ−Ｏよりなる厚さ１００μｍのアルミニウム箔（金属箔層）の片面に、厚さ２００μｍのポリプロピレン樹脂（ＰＰ）フィルム（熱融着性樹脂層）を、同他面に、厚さ３０μｍの無延伸ポリプロピレン樹脂（ＣＰＰ）フィルム（外側樹脂層）を、それぞれ２液硬化型接着剤を用いて貼り合せ、４０℃の環境下で５日間養生することにより、容器用複合シートを作製した。
そして、上記の容器用複合シートを所定形状にカットしてなるブランクの両面に微量のシロキサンを塗布しておいてから、雄型および雌型からなる金型を用いて深絞り加工することにより、フランジを有する丸型カップ状の容器（底径５６ｍｍφ、開口径６５ｍｍφ、高さ２５ｍｍ、フランジ幅８ｍｍ）を作製した。
First, a polypropylene resin (PP) film (heat fusible resin layer) having a thickness of 200 μm is formed on one side of an aluminum foil (metal foil layer) having a thickness of 100 μm made of A8079H-O classified according to JIS H4160. On the surface, a 30 μm-thick non-oriented polypropylene resin (CPP) film (outside resin layer) is bonded using a two-component curable adhesive, and aged for 5 days in an environment of 40 ° C. A composite sheet was made.
Then, a minute amount of siloxane is applied to both sides of the blank formed by cutting the composite sheet for a container into a predetermined shape, and then deep drawing processing is performed using a male and female mold. A round cup-shaped container (bottom diameter 56 mm, opening diameter 65 mm, height 25 mm, flange width 8 mm) having a flange was produced.
一方、ＪＩＳ Ｈ４１６０で分類されたＡ１Ｎ３０Ｈ-Ｏよりなる厚さ２０μｍのアルミニウム箔（金属層）の第１の面に、厚さ１２μｍのポリエチレンテレフタレート樹脂（ＰＥＴ）フィルム（外側樹脂層）を、２液硬化型のポリエステル−ポリウレタン樹脂系接着剤（接着剤層）を介してドライラミネート法により貼り合わせた。次いで、アルミニウム箔の第２の面に、ゴム系粘着剤（再封用粘着層）を膜厚１０μｍとなるようにグラビアコーティングして、その上に厚さ２０μｍの無延伸ポリプロピレン樹脂（ＣＰＰ)フィルム（熱融着性樹脂層）を貼り合わせることにより、複合シートを得た。そして、この複合シートをフランジに合わせて所要の形状およびサイズにカットすることにより、開封用タブ付きの蓋を作製した。 On the other hand, a 12 μm thick polyethylene terephthalate resin (PET) film (outside resin layer) was applied to the first surface of a 20 μm thick aluminum foil (metal layer) made of A1N30H-O classified according to JIS H4160. It bonded together by the dry lamination method via the curing type polyester-polyurethane resin adhesive (adhesive layer). Next, a rubber-based pressure-sensitive adhesive (pressure-sensitive adhesive layer for resealing) is gravure-coated on the second surface of the aluminum foil to a film thickness of 10 μm, and a 20 μm-thick non-oriented polypropylene resin (CPP) film is formed thereon A composite sheet was obtained by laminating (a heat-fusible resin layer). Then, the composite sheet was fitted to the flange and cut into a required shape and size to produce a lid with an opening tab.
上記容器に３０ｍｌの水を入れてから、容器のフランジ上面に、上記蓋を無延伸ポリプロピレン樹脂（ＣＰＰ）フィルム面が接するように重ね、これらの重合面に、２００℃に加熱したドーナツ状の熱板（外径１００ｍｍφ、内径７３ｍｍφ）を、１５０ｋｇｆの加圧力で３秒間押し当てることにより、ヒートシール（熱融着）を行った。
次いで、上記容器を、開口径６５ｍｍφのドーナツ状の台座の内側に、フランジが台座の上面によって受けられるように配置し、蓋の上面におけるヒートシール（熱融着）部と重なる環状帯域に、押し型下面の横断面逆台形をした円環状突起（先端部の幅１ｍｍ、根本部の幅３ｍｍ、高さ３ｍｍ）を、３００ｋｇｆの加圧力で押し付けることにより、円環状の型押し部を形成した。
こうして、実施例の包装体を得た。
After putting 30 ml of water in the above container, the above lid is stacked on the upper surface of the flange of the container so that the non-oriented polypropylene resin (CPP) film surface is in contact, and donut shaped thermal heated to 200 ° C. on these polymerization surfaces. Heat sealing (heat fusion) was performed by pressing the plate (outer diameter 100 mmφ, inner diameter 73 mmφ) with a pressure of 150 kgf for 3 seconds.
The container is then placed inside a doughnut-shaped pedestal with an opening diameter of 65 mm so that the flange is received by the upper surface of the pedestal and pushed in the annular zone overlapping the heat seal (heat sealing) part on the upper surface of the lid. An annular embossed portion was formed by pressing an annular projection (width 1 mm at the tip,
Thus, the package of the example was obtained.
上記実施例の包装体について、蓋のタブを手指で摘んで引き上げることにより、蓋をフランジから剥離して開封したところ、蓋の下面の外周部にゴム系粘着剤が露出していた。また、容器のフランジの上面に、蓋のアルミニウム箔の一部が剥離してフランジの周方向に沿って円環状に付着していた。
次に、剥離した蓋の下面の外周部を容器のフランジの上面に重ねると、ゴム系粘着剤の露出部によって蓋がフランジに貼り付けられ、再封状態となった。この状態で、蓋の上面を観察したところ、アルミニウム箔の部分剥離によって生じた欠落部が、外周部に白っぽい円環状の模様として表れていることを目視で確認することができた。
When the lid of the package of the above example was peeled off from the flange by picking up the tab of the lid and pulling up, the rubber-based pressure sensitive adhesive was exposed at the outer peripheral portion of the lower surface of the lid. In addition, on the upper surface of the flange of the container, a part of the aluminum foil of the lid was peeled off and attached in an annular shape along the circumferential direction of the flange.
Next, when the outer periphery of the lower surface of the peeled lid was placed on the upper surface of the flange of the container, the lid was attached to the flange by the exposed portion of the rubber-based pressure sensitive adhesive, and the container was resealed. In this state, when the upper surface of the lid was observed, it could be visually confirmed that a missing part caused by partial peeling of the aluminum foil appeared as a whitish annular pattern on the outer peripheral part.
この発明は、長期保存が必要であってかつ一度に使い切らない食品、医薬品等の内容物を、容器および蓋を用いて再封可能に密封包装する包装体として、好適に使用することができる。 INDUSTRIAL APPLICABILITY The present invention can be suitably used as a package for resealably sealing and packaging contents of food, medicine and the like which require long-term storage and can not be used all at once, using a container and a lid.
(1)：包装体
(2)：容器
(2b)：フランジ
(22)：熱融着性樹脂層
(3)：蓋
(3a)：開封用タブ
(32)：金属層
(32X)：熱融着部に重なる環状帯域
(321)：欠落部
(33)：再封用粘着層
(34)：熱融着性樹脂層
(36)：型押し部
(4)：熱融着部
(5)：内容物
(1): Package
(2): container
(2b): Flange
(22): Heat fusible resin layer
(3): Lid
(3a): Opening tab
(32): Metal layer
(32X): An annular zone overlapping the heat sealing portion
(321): Missing part
(33): Adhesive layer for resealing
(34): Heat fusible resin layer
(36): embossed part
(4): Heat sealing portion
(5): Contents
Claims (3)
蓋のうち平面よりみて容器のフランジと蓋との熱融着部に重なる環状帯域に、その一部を蓋の上面側から押圧して少なくとも金属層を分断させる型押し部が形成されており、蓋の剥離に伴い金属層における型押し部に対応する箇所に生じた欠落部を蓋の上面側から視認しうるようになされている、包装体。 A container having a flange at the periphery of the opening, and releasably heat-sealed to the flange so as to close the opening of the container filled with contents, and having an opening tab at a circumferential portion in the outer peripheral portion The cover has a heat-fusing resin layer, a pressure-sensitive adhesive layer for resealing, and a metal layer sequentially stacked from the lower surface side, and the upper surface of the container flange is the heat of the cover It consists of a heat-sealable resin layer and a heat-sealable heat-sealable resin layer, and by pulling up the opening tab and peeling off the lid, the resealing adhesive layer is exposed on the outer peripheral portion of the lower surface of the lid. A package that is made to
In the annular zone of the lid overlapping the heat fusion between the flange of the container and the lid as viewed from the top, a stamped portion is formed that presses a part of the lid from the upper surface side of the lid to divide at least the metal layer; The package which is made to be able to visually recognize from the upper surface side of a lid the missing part which arose in the location corresponding to the embossing part in a metal layer with peeling of a lid.