JP2018127558A - Solid water color composition - Google Patents
Solid water color composition Download PDFInfo
- Publication number
- JP2018127558A JP2018127558A JP2017022585A JP2017022585A JP2018127558A JP 2018127558 A JP2018127558 A JP 2018127558A JP 2017022585 A JP2017022585 A JP 2017022585A JP 2017022585 A JP2017022585 A JP 2017022585A JP 2018127558 A JP2018127558 A JP 2018127558A
- Authority
- JP
- Japan
- Prior art keywords
- paint composition
- watercolor paint
- water
- solid watercolor
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
この発明は、固形水彩絵具組成物に関するものである。 The present invention relates to a solid watercolor paint composition.
従来から、水を含ませた筆でその表面を擦って筆に顔料成分を含ませ、画用紙等の描画対象に描画することができる固形水彩絵具組成物が、特開昭５８−９６６６１号公報（特許文献１）および特開２００７−９１９８号公報（特許文献２）に開示されている。 Conventionally, a solid watercolor paint composition that can be drawn on a drawing target such as drawing paper by rubbing the surface with a brush soaked in water and containing a pigment component is disclosed in JP-A-58-96661. Patent Document 1) and Japanese Patent Application Laid-Open No. 2007-9198 (Patent Document 2).
固形水彩絵具組成物はブロック状の形態を有しており、仕切りが設けられたパレットに色毎に配置されている。ユーザーは描画をする際に描画したい色に相当する固形水彩絵具組成物を目視で選択し、水を含ませた筆で固形水彩絵具組成物の表面を擦って固形水彩絵具組成物を筆に含ませることとしている。そして、固形水彩絵具組成物を含ませた筆により描画対象となる画用紙等に描画する。 The solid watercolor paint composition has a block-like form and is arranged for each color on a palette provided with partitions. The user visually selects a solid watercolor paint composition corresponding to the color to be drawn when drawing, and rubs the surface of the solid watercolor paint composition with a brush soaked in water to include the solid watercolor paint composition in the brush. I am trying to make it. And it draws on the drawing paper etc. which become drawing object with the brush containing the solid watercolor paint composition.
ここで、固形水彩絵具組成物自体の発色性が不十分であると、目視によって色が確認しづらい場合が生ずるおそれがある。特に、光が多重層反射されるパール顔料や蛍光を発する蛍光顔料を用いる場合には、その傾向が顕著である。すなわち、実際にパレットに配置されているパール顔料や蛍光顔料の固形水彩絵具組成物の見た目と、この固形水彩絵具組成物を用いて描画した際の発色の程度が異なると、ユーザーが違和感を覚えることとなり好ましくない。 Here, when the color developability of the solid watercolor paint composition itself is insufficient, there is a possibility that it may be difficult to visually confirm the color. In particular, when a pearl pigment that reflects light in multiple layers or a fluorescent pigment that emits fluorescence is used, the tendency is remarkable. In other words, the user feels uncomfortable when the appearance of the solid watercolor paint composition of the pearl pigment or fluorescent pigment actually placed on the palette differs from the degree of color development when drawn with this solid watercolor paint composition. That is not preferable.
この発明の目的は、描画の際にユーザーの利用しやすい固形水彩絵具組成物を提供することである。 An object of the present invention is to provide a solid watercolor paint composition that is easy for a user to use when drawing.
この発明に係る固形水彩絵具組成物は、３０質量％以上の顔料と、２５質量％以下の水と、セルロースエーテル系水溶性樹脂とを含む。 The solid watercolor paint composition according to the present invention includes 30% by mass or more of pigment, 25% by mass or less of water, and a cellulose ether-based water-soluble resin.
この発明に係る固形水彩絵具組成物は、３０質量％以上の顔料と、２５質量％以下の水とを含む。そして、セルロースエーテル系水溶性樹脂を含むため、ブロック状の固形水彩絵具組成物としての発色性が良好である。また、水を含ませた筆で擦って筆に固形水彩絵具組成物を含ませる際の水溶け性も良好である。さらに、セルロースエーテル系水溶性樹脂は固結性も良好であり、乾燥後も固化するため、高い湿度の環境下においても溶出しにくい。したがって、描画の際に、ユーザーが利用しやすいものとなる。 The solid watercolor paint composition according to the present invention contains 30% by mass or more of pigment and 25% by mass or less of water. And since the cellulose ether type water-soluble resin is included, the color developability as a block-shaped solid watercolor paint composition is favorable. In addition, the water-solubility when the solid watercolor paint composition is contained in the brush by rubbing with a brush soaked in water is also good. Furthermore, the cellulose ether-based water-soluble resin has good caking properties and solidifies even after drying, so that it is difficult to elute even in a high humidity environment. Therefore, it is easy for the user to use when drawing.
この発明に係る固形水彩絵具組成物に含まれる顔料は、パール顔料および蛍光顔料のうちの少なくとも一方を含むことが好ましい。このような固形水彩絵具組成物は、パール顔料や蛍光顔料について発色性を良好にすることができる。すなわち、実際にパレットに配置されているパール顔料や蛍光顔料の固形水彩絵具組成物の見た目と、この固形水彩絵具組成物を用いて描画した際の発色の程度の差を小さくすることができる。したがって、このような色をユーザーが選択する際に、ユーザーが利用しやすくすることができる。 The pigment contained in the solid watercolor paint composition according to the present invention preferably contains at least one of a pearl pigment and a fluorescent pigment. Such a solid watercolor paint composition can improve the color developability of pearl pigments and fluorescent pigments. That is, it is possible to reduce the difference between the appearance of the pearl pigment or fluorescent pigment solid watercolor paint composition actually arranged on the palette and the degree of color development when drawn using this solid watercolor paint composition. Therefore, when the user selects such a color, the user can easily use the color.
この発明に係る固形水彩絵具組成物は、さらにポリエチレングリコールを含むことが好ましい。こうすることにより、描画した際の塗膜の乾燥時間を調整して、描画のしやすさを確保することができる。 It is preferable that the solid watercolor paint composition according to the present invention further contains polyethylene glycol. By carrying out like this, the easiness of drawing can be ensured by adjusting the drying time of the coating film at the time of drawing.
この発明に係る固形水彩絵具組成物において、顔料のうち、体質顔料以外の顔料の割合は、２９質量％以上である。こうすることにより、体質顔料による色の濁り等を抑制して、発色性をさらに良好にすることができる。 In the solid watercolor paint composition according to the present invention, the proportion of the pigment other than the extender pigment is 29% by mass or more. By doing so, color turbidity due to the extender pigment can be suppressed, and the color developability can be further improved.
ここで、セルロースエーテル系水溶性樹脂は、カルボキシメチルセルロースナトリウムを含むことが好ましい。このようなセルロースエーテル系水溶性樹脂を用いることにより、より上記した発色性の向上を図ることができる。 Here, the cellulose ether-based water-soluble resin preferably contains sodium carboxymethyl cellulose. By using such a cellulose ether-based water-soluble resin, it is possible to further improve the color developability described above.
また、セルロースエーテル系水溶性樹脂の含有割合は、３０質量％以下であることが好ましい。このような含有割合とすることにより、より良好な水溶け性を確保することができる。 Moreover, it is preferable that the content rate of a cellulose ether type water-soluble resin is 30 mass% or less. By setting it as such a content rate, better water solubility can be ensured.
このような構成の固形水彩絵具組成物は、描画の際にユーザーが利用しやすい。 The solid watercolor paint composition having such a configuration is easy for the user to use when drawing.
以下、この発明の実施の形態を説明する。図１は、この発明の一実施形態に係る固形水彩絵具組成物の外観を示す斜視図である。図１を参照して、この発明の一実施形態に係る固形水彩絵具組成物１１は、直方体形状であって、いわゆるブロック状である。すなわち、未使用の状態において、直方体形状に成型される。使用されるに従い、その大きさは徐々に小さくなる。それぞれの角については、若干丸められた形状である。図１中の矢印Ｄ１で示す下向きに見た場合に、固形水彩絵具組成物１１の表側に位置する一つの面１２は、略正方形状である。
Embodiments of the present invention will be described below. FIG. 1 is a perspective view showing an appearance of a solid watercolor paint composition according to an embodiment of the present invention. With reference to FIG. 1, the solid
図２は、複数の固形水彩絵具組成物１１が収容されたパレットの外観の一部を示す斜視図である。図２を参照して、パレット１３には、固形水彩絵具組成物１１を収容する複数の凹部１４が形成されている。凹部１４の形状は、固形水彩絵具組成物１１の直方体形状に沿ったものである。それぞれの凹部１４に、色の異なる複数の固形水彩絵具組成物１１が収容されている。収容された固形水彩絵具組成物１１は、その直方体形状を構成する一つの面１２が表側に露出した状態である。
FIG. 2 is a perspective view showing a part of the appearance of a palette in which a plurality of solid
図３は、固形水彩絵具組成物１１を用いて描画する際の筆の外観を示す斜視図である。図３を参照して、筆１５は、描画する際に固形水彩絵具組成物１１を含ませる毛部１６と、描画時等に主にユーザーが握る胴部１７とを備える。胴部１７は、中央の領域で第一の部材１８、および第二の部材１９に分離可能な構成である。第二の部材１９の内方側には空洞が設けられており、胴部１７を分離して、第二の部材１９の内側に水を収容することができる。第二の部材１９の空洞に所定量の水を収容し、第一の部材１８と第二の部材１９を接合し、第二の部材１９の領域をユーザーの指等で押圧することにより、第二の部材１９内に収容させた水を第一の部材１８を通じて毛部１６側に染み出させることができる。すなわち、第二の部材１９内に収容させた水により毛部１６を適量の水で濡らすことができる。ユーザーは、胴部１７を持ち、水で濡らせた毛部１６により固形水彩絵具組成物１１のうちの表側に露出する面１２をある程度の圧力で数回擦って、固形水彩絵具組成物１１の一部を筆１５側に付着させる。そして、固形水彩絵具組成物１１を含まれた筆１５の毛部１６により、画用紙等の描画対象に塗って描画する。色の選択については、固形水彩絵具組成物１１の表面を見てユーザーが判断する。
FIG. 3 is a perspective view showing the appearance of a brush when drawing using the solid
なお、固形水彩絵具組成物１１の形状については、直方体形状であることとしたが、これに限らず、立方体形状や薄板状であってもよいし、柱状や棒状であってもよい。すなわち、使用される用途や求められる使い勝手等に応じて、任意にその形状が定められる。
The shape of the solid
ここで、ユーザーが描画時において色を選択する際に、パレット１３の凹部１４に収容されている各色の固形水彩絵具組成物１１を見て色を判断する。したがって、固形水彩絵具組成物１１の見た目と、実際に描画時における発色が同一に近いことが望ましい。逆に、見た目の色と描画時の発色とが大きく異なっていると、ユーザーの描画の際に違和感を生じることとなり、ユーザーの利便性を損ねることになりかねない。したがって、描画する前のパレット１３等に収容された状態において、固形水彩絵具組成物１１の発色性が良好であることが望ましい。
Here, when the user selects a color at the time of drawing, the color is judged by looking at the solid
ここで、固形水彩絵具組成物１１は、３０質量％以上の顔料と、２５質量％以下の水と、セルロースエーテル系水溶性樹脂とを含む。以下、固形水彩絵具組成物１１を構成する成分の詳細について説明する。
Here, the solid
（１）顔料
顔料としては、固形水彩絵具組成物１１を着色する意味で、種々のものが用いられる。顔料としては、有機顔料、無機顔料、レーキ顔料、およびその他の固形水彩絵具組成物１１に用いられる顔料として一般的な着色剤などが挙げられる。すなわち、固形水彩絵具組成物１１を構成する顔料は、有機顔料、無機顔料、およびレーキ顔料からなる群から選択される一種または二種以上の物質とすることができる。
(1) Pigment As the pigment, various pigments are used in order to color the solid
顔料としては、光が多重層反射されるパール顔料や蛍光を発する蛍光顔料も用いられる。すなわち、顔料は、パール顔料および蛍光顔料のうちの少なくともいずれか一方を含む構成であってもよい。このようなパール顔料や蛍光顔料は、描画において昨今、特に要求される色である。 As the pigment, a pearl pigment that reflects light in multiple layers and a fluorescent pigment that emits fluorescence are also used. That is, the pigment may be configured to include at least one of a pearl pigment and a fluorescent pigment. Such pearl pigments and fluorescent pigments are particularly required colors for drawing these days.
顔料の含有割合については、３０質量％以上である。また、固形水彩絵具組成物１１に含まれる水は、２５質量％以下である。すなわち、固形水彩絵具組成物の全体に対して、３０質量％以上の顔料が含まれる。このような構成によれば、図１に示すような固形水彩絵具組成物１１としての形態を保つことができる。
About the content rate of a pigment, it is 30 mass% or more. Moreover, the water contained in the solid
顔料のうちの体質顔料については、色によっては、過剰な添加により発色性が損なわれるおそれがある。たとえば、上記したパール顔料や蛍光顔料と共に体質顔料を含有させる場合において、その傾向は顕著である。したがって、顔料のうち、体質顔料以外の顔料の含有割合を２９質量％以上とすることが好ましい。こうすることにより、色によらず、発色性を良好にすることができる。 Regarding the extender pigment among the pigments, depending on the color, there is a possibility that the color developability may be impaired by excessive addition. For example, when the extender pigment is contained together with the pearl pigment and the fluorescent pigment, the tendency is remarkable. Therefore, it is preferable that the content of the pigment other than the extender pigment is 29% by mass or more. By doing so, color developability can be improved regardless of the color.
（２）セルロースエーテル系水溶性樹脂
固形水彩絵具組成物１１に含まれるセルロースエーテル系水溶性樹脂は、主に紙に顔料を固結させる固結剤および展色剤として作用する。セルロースエーテル系水溶性樹脂としては、セルロースエーテルを含む水溶性樹脂であり、カルボキシメチルセルロースナトリウム、ヒドロキシエチルセルロース、メチルヒドロキシエチルセルロース、メチルヒドロキシプロピルセルロース等が挙げられる。固形水彩絵具組成物１１を構成するセルロースエーテル系水溶性樹脂は、カルボキシメチルセルロースナトリウム（ＣＭＣ（Ｓｏｄｉｕｍ Ｃａｒｂｏｘｙｍｅｔｈｙｌ Ｃｅｌｌｕｌｏｓｅ））、ヒドロキシエチルセルロース、メチルヒドロキシエチルセルロース、およびメチルヒドロキシプロピルセルロースからなる群から選択される一種または二種以上の物質とすることができる。
(2) Cellulose ether-based water-soluble resin The cellulose ether-based water-soluble resin contained in the solid
セルロースエーテル系水溶性樹脂の含有割合として、過剰に含有させると、色によっては発色性が低下したり、水溶け性が低下したりする場合がある。したがって、全体に対して３０質量％以下とすることが好ましい。 When the content of the cellulose ether-based water-soluble resin is excessive, the color developability may be lowered or the water solubility may be lowered depending on the color. Therefore, it is preferable to set it as 30 mass% or less with respect to the whole.
（３）他の水溶性樹脂
固形水彩絵具組成物１１に含まれる他の水溶性樹脂として、展色剤として用いられる水溶性樹脂をさらに含むことが好ましい。具体的には、アラビアガム、デキストリン、ポリビニルアルコール（ＰＶＡ（Ｐｏｌｙｖｉｎｙｌ Ａｌｃｏｈｏｌ））、ポリビニルピロリドン（ＰＶＰ（Ｐｏｌｙｖｉｎｙｌｐｙｒｒｏｌｉｄｏｎｅ））等が挙げられる。固形水彩絵具組成物１１を構成する他の水溶性樹脂は、アラビアガム、デキストリン、ポリビニルアルコール（ＰＶＡ）、およびポリビニルピロリドン（ＰＶＰ）からなる群から選択される一種または二種以上の物質とすることができる。
(3) Other water-soluble resins As the other water-soluble resins contained in the solid
（４）湿潤剤
固形水彩絵具組成物１１は、凍結防止剤、乾燥遅延剤として作用する湿潤剤を含むことが好ましい。湿潤剤は、描画を終えた後の塗膜のひび割れ防止にも作用する。湿潤剤としては、ポリエチレングリコール（ＰＥＧ（Ｐｏｌｙｅｔｈｙｌｅｎｅ ｇｌｙｃｏｌ））、グリセリン、エチレングリコール、プロピレングリコール、ジプロピレングリコール、ソルビトール、尿素等が挙げられる。固形水彩絵具組成物１１を構成する湿潤剤は、ポリエチレングリコール（ＰＥＧ）、グリセリン、エチレングリコール、プロピレングリコール、ジプロピレングリコール、ソルビトール、および尿素からなる群から選択される一種または二種以上の物質とすることができる。なお、上記したＰＥＧ等の含有の有無については、たとえば、ガスクロマトグラフィーによる分析で判断することができる。
(4) Wetting agent It is preferable that the solid
（５）界面活性剤（分散剤）
固形水彩絵具組成物１１は、顔料の分散助剤として作用する界面活性剤を含むことが好ましい。界面活性剤としては、アニオン系界面活性剤やノニオン系界面活性剤等が挙げられる。なお、このような界面活性剤の含有の有無については、たとえば、ＦＴ−ＩＲ（Ｆｏｕｒｉｅｒ Ｔｒａｎｓｆｏｒｍ Ｉｎｆｒａｒｅｄ Ｓｐｅｃｔｒｏｓｃｏｐｙ）分析により判断することができる。
(5) Surfactant (dispersant)
The solid
（６）界面活性剤（消泡剤）
固形水彩絵具組成物１１は、消泡効果を奏する界面活性剤を含むことが好ましい。消泡効果を奏する界面活性剤としては、シリコーン系界面活性剤、疎水性シリカ系界面活性剤、金属石鹸系界面活性剤、ポリエーテル系界面活性剤等が挙げられる。固形水彩絵具組成物１１を構成する界面活性剤は、シリコーン系界面活性剤、疎水性シリカ系界面活性剤、金属石鹸系界面活性剤、およびポリエーテル系界面活性剤からなる群から選択される一種または二種以上の物質とすることができる。
(6) Surfactant (antifoaming agent)
It is preferable that the solid
（７）その他の成分
固形水彩絵具組成物１１は、上記（１）〜（６）の成分のほか、例えば、防腐剤、防黴剤、酸化防止剤等を含んでいてもよい。
(7) Other components The solid
次に、この発明の一実施形態に係る固形水彩絵具組成物１１の製造方法の概略について、説明する。図４は、この発明の一実施形態に係る固形水彩絵具組成物１１の代表的な製造工程を示すフローチャートである。
Next, the outline of the manufacturing method of the solid
図４を参照して、まず顔料、セルロースエーテル系水溶性樹脂、他の水溶性樹脂、湿潤剤、界面活性剤、防腐剤、および水をそれぞれ所定量準備する。そして、ニーダーで準備した材料を混練する（Ｓ１１：混練工程）。 Referring to FIG. 4, first, a predetermined amount of pigment, cellulose ether water-soluble resin, other water-soluble resin, wetting agent, surfactant, preservative, and water are prepared. And the material prepared with the kneader is knead | mixed (S11: kneading process).
次に、混練した混練物を土練機で成型する（Ｓ１２：成型工程）。この場合、細長い棒状、具体的には、四角柱状となるよう成型する。なお、成型後、４５℃の状態で２４時間乾燥させる。この段階における成形物に含まれる水の含有割合は、色によって多少の差異はあるものの、５．０質量％〜１６．０質量％程度である。 Next, the kneaded kneaded product is molded with a kneader (S12: molding step). In this case, it is molded so as to have an elongated rod shape, specifically, a quadrangular prism shape. In addition, after shaping | molding, it is made to dry for 24 hours in the state of 45 degreeC. The content of water contained in the molded product at this stage is about 5.0% by mass to 16.0% by mass, although there are some differences depending on the color.
その後、成型したものを、所定の大きさに切断する（Ｓ１３：切断工程）。この時に、上記した図１に示す固形水彩絵具組成物１１の形状に近い形状となる。
Thereafter, the molded product is cut into a predetermined size (S13: cutting step). At this time, the shape is close to the shape of the solid
そして、得られたものを乾燥させる（Ｓ１４：乾燥工程）。乾燥工程については、自然乾燥である。このようにして、この発明の一実施形態に係る固形水彩絵具組成物１１を得る。
And what was obtained is dried (S14: drying process). The drying process is natural drying. Thus, the solid
成分組成の異なる固形水彩絵具組成物を実施例１〜実施例１２に示す配合に沿って作製し、評価試験を実施した。具体的な評価試験の内容については、後述する。また、この発明の範囲外であり、成分組成の異なる固形水彩絵具組成物を比較例１〜比較例４に示す配合に沿って作製した。そして、同様に評価試験を実施した。実施例１〜実施例１２、および比較例１〜比較例４の配合および評価結果については、表１および表２に示す。なお、表１および表２中の「−」は、材料が含まれていないことを示している。また、表１および表２中の数値の単位は、質量％である。以下に、実施例１〜実施例１２、および比較例１〜比較例４の配合の詳細について説明する。 Solid watercolor paint compositions having different component compositions were prepared according to the formulations shown in Examples 1 to 12, and an evaluation test was performed. Details of the evaluation test will be described later. Moreover, it was outside the scope of the present invention, and solid watercolor paint compositions having different component compositions were prepared according to the formulations shown in Comparative Examples 1 to 4. And the evaluation test was implemented similarly. The formulations and evaluation results of Examples 1 to 12 and Comparative Examples 1 to 4 are shown in Table 1 and Table 2. In Tables 1 and 2, “-” indicates that no material is contained. Moreover, the unit of the numerical value in Table 1 and Table 2 is the mass%. Below, the detail of the mixing | blending of Example 1- Example 12 and Comparative Example 1- Comparative Example 4 is demonstrated.
（実施例１）
実施例１に係る固形水彩絵具組成物の製造に際し、以下の材料を準備した。具体的には、顔料としてパール顔料である商品名「Ｉｒｉｏｄｉｎ ３００ Ｇｏｌｄ Ｐｅａｒｌ」（メルク パフォーマンス マテリアル社製）、セルロースエーテル系水溶性樹脂としてカルボキシメチルセルロースである商品名「セロゲン５Ａ」（第一工業製薬株式会社製）、水溶性樹脂としてアラビアガムである商品名「インスタントガム ＢＡ」（ネキシラ社製）、湿潤剤としてグリセリンである商品名「精製グリセリン」（新日本理化株式会社製）、同じく湿潤剤としてポリエチレングリコールである商品名「ＰＥＧ−６０００Ｓ」（三洋化成工業株式会社製、平均分子量８６００）、分散剤として直鎖ドデシルベンゼンスルホン酸ナトリウムである商品名「ニューレックス ソフトタイプ ３０」（日油株式会社製）、消泡剤として疎水性シリカ系界面活性剤である商品名「ノプコ８０３４−Ｌ」（サンノプコ株式会社製）、防腐剤として商品名「サンアイバックＳＡ」（三愛石油株式会社製）、および水を準備した。各材料を表１に示す配合割合で混ぜ、図４に示す製造工程に従い、実施例１に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
Example 1
In producing the solid watercolor paint composition according to Example 1, the following materials were prepared. Specifically, the trade name “Iriodin 300 Gold Pearl” (manufactured by Merck Performance Materials Co., Ltd.), which is a pearl pigment as a pigment, and the trade name “Serogen 5A” (Daiichi Kogyo Seiyaku Co., Ltd.), which is a carboxymethyl cellulose as a water-soluble cellulose ether resin Company name), gum arabic as a water-soluble resin, “Instant Gum BA” (manufactured by Nexira), glycerin as a wetting agent, “purified glycerin” (manufactured by Shin Nippon Rika Co., Ltd.), also as a wetting agent The product name “PEG-6000S” (manufactured by Sanyo Chemical Industries, Ltd., average molecular weight 8600), which is polyethylene glycol, and the product name “Newrex soft type 30”, which is linear sodium dodecylbenzenesulfonate as a dispersant (NOF CORPORATION) Manufactured), hydrophobic as antifoaming agent Trade name of silica-based surfactant "Nopco 8034-L" (manufactured by San Nopco Ltd.), trade name as a preservative "Sanai back SA" (San-Ai Oil Co., Ltd.), and was prepared water. Each material was mixed at the blending ratio shown in Table 1, and the solid watercolor paint composition according to Example 1 was obtained according to the production process shown in FIG. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例２）
実施例２に係る固形水彩絵具組成物の製造に際し、以下の材料を準備した。顔料として蛍光顔料である商品名「ＳＩＮＬＯＩＨＩ ＣＯＬＯＲ ＦＬ−１５」（シンロイヒ株式会社製）、分散剤としてノニオン系界面活性剤である商品名「プライサーフＡ−２１２Ｅ」（第一工業製薬株式会社製）を準備した。セルロースエーテル系水溶性樹脂、他の水溶性樹脂、湿潤剤、分散剤、消泡剤、および防腐剤については、実施例１と同じものを用いた。各材料を表１に示す配合割合で混ぜ、図４に示す製造工程に従い、実施例２に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 2)
In manufacturing the solid watercolor paint composition according to Example 2, the following materials were prepared. Trade name “SINLOIHI COLOR FL-15” (manufactured by Shinroihi Co., Ltd.) which is a fluorescent pigment as a pigment, and trade name “Pricesurf A-212E” (manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) which is a nonionic surfactant as a dispersant. Prepared. The same cellulose ether water-soluble resin, other water-soluble resin, wetting agent, dispersant, antifoaming agent, and preservative as those in Example 1 were used. Each material was mixed at the blending ratio shown in Table 1, and a solid watercolor paint composition according to Example 2 was obtained according to the production process shown in FIG. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例３）
実施例１に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合と他の水溶性樹脂の含有割合とを表１に示す配合割合とした以外は実施例１と同様の工程で実施例３に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 3)
In the production process of the solid watercolor paint composition according to Example 1, the content ratio of the cellulose ether-based water-soluble resin and the content ratio of the other water-soluble resin were the same as in Example 1 except that the blending ratios shown in Table 1 were used. The solid watercolor paint composition according to Example 3 was obtained by the above process. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例４）
実施例２に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合と他の水溶性樹脂の含有割合とを表１に示す配合割合とした以外は実施例２と同様の工程で実施例４に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
Example 4
In the production process of the solid watercolor paint composition according to Example 2, the content ratio of the cellulose ether-based water-soluble resin and the content ratio of the other water-soluble resin were the same as in Example 2 except that the blending ratios shown in Table 1 were used. The solid watercolor paint composition which concerns on Example 4 was obtained by the process of. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例５）
実施例１に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合と他の水溶性樹脂の含有割合とを表１に示す配合割合とした以外は実施例１と同様の工程で実施例５に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 5)
In the production process of the solid watercolor paint composition according to Example 1, the content ratio of the cellulose ether-based water-soluble resin and the content ratio of the other water-soluble resin were the same as in Example 1 except that the blending ratios shown in Table 1 were used. Thus, the solid watercolor paint composition according to Example 5 was obtained. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例６）
実施例２に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合と他の水溶性樹脂の含有割合とを表１に示す配合割合とした以外は実施例２と同様の工程で実施例６に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 6)
In the production process of the solid watercolor paint composition according to Example 2, the content ratio of the cellulose ether-based water-soluble resin and the content ratio of the other water-soluble resin were the same as in Example 2 except that the blending ratios shown in Table 1 were used. The solid watercolor paint composition according to Example 6 was obtained by the above process. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例７）
実施例１に係る固形水彩絵具組成物の製造工程において、顔料の含有割合とセルロースエーテル系水溶性樹脂の含有割合とを表１に示す配合割合とした以外は実施例１と同様の工程で実施例７に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４８％であり、水の含有割合は、０．３％であった。
(Example 7)
In the production process of the solid watercolor paint composition according to Example 1, the same process as in Example 1 was carried out except that the pigment content and the cellulose ether-based water-soluble resin content were set as shown in Table 1. A solid watercolor paint composition according to Example 7 was obtained. The content ratio of the pigment in the obtained solid watercolor paint composition was 48%, and the content ratio of water was 0.3%.
（実施例８）
実施例２に係る固形水彩絵具組成物の製造工程において、顔料の含有割合とセルロースエーテル系水溶性樹脂の含有割合とを表１に示す配合割合とした以外は実施例１と同様の工程で実施例８に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４８％であり、水の含有割合は、０．３％であった。
(Example 8)
In the manufacturing process of the solid watercolor paint composition according to Example 2, the same process as in Example 1 was performed except that the content ratio of the pigment and the content ratio of the cellulose ether-based water-soluble resin were changed to the mixing ratio shown in Table 1. A solid watercolor paint composition according to Example 8 was obtained. The content ratio of the pigment in the obtained solid watercolor paint composition was 48%, and the content ratio of water was 0.3%.
（実施例９）
実施例１に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合と他の水溶性樹脂の含有割合とを表２に示す配合割合とした以外は実施例１と同様の工程で実施例９に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
Example 9
In the production process of the solid watercolor paint composition according to Example 1, the content ratio of the cellulose ether-based water-soluble resin and the content ratio of the other water-soluble resin were the same as in Example 1 except that the blending ratios shown in Table 2 were used. The solid watercolor paint composition according to Example 9 was obtained by the above process. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例１０）
実施例２に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合と他の水溶性樹脂の含有割合とを表２に示す配合割合とした以外は実施例２と同様の工程で実施例１０に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 10)
In the production process of the solid watercolor paint composition according to Example 2, the content ratio of the cellulose ether-based water-soluble resin and the content ratio of the other water-soluble resin were the same as in Example 2 except that the blending ratios shown in Table 2 were used. The solid watercolor paint composition according to Example 10 was obtained by the above process. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例１１）
実施例１に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合を表２に示す配合割合とし、他の水溶性樹脂は含有しなかった以外は実施例１と同様の工程で実施例１１に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 11)
In the production process of the solid watercolor paint composition according to Example 1, the content ratio of the cellulose ether-based water-soluble resin was set to the blending ratio shown in Table 2, and other water-soluble resins were not included, as in Example 1. Thus, the solid watercolor paint composition according to Example 11 was obtained. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（実施例１２）
実施例２に係る固形水彩絵具組成物の製造工程において、セルロースエーテル系水溶性樹脂の含有割合を表２に示す配合割合とし、他の水溶性樹脂は含有しなかった以外は実施例１と同様の工程で実施例１２に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Example 12)
In the production process of the solid watercolor paint composition according to Example 2, the content ratio of the cellulose ether-based water-soluble resin was set to the blending ratio shown in Table 2, and other water-soluble resins were not included, as in Example 1. The solid watercolor paint composition according to Example 12 was obtained by the above process. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（比較例１）
実施例１に係る固形水彩絵具組成物の製造工程において、顔料のうちの体質顔料としてさらにモンモリロナイトである商品名「ベントナイト」（株式会社ホージュン製）を準備した。他の水溶性樹脂、湿潤剤、分散剤、消泡剤、および防腐剤については、実施例１と同じものを用いた。なお、比較例１においては、セルロースエーテル系水溶性樹脂は含有されていない。各材料を表２に示す配合割合で混ぜ、図４に示す製造工程に従い、比較例１に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４３％であり、水の含有割合は、０．３％であった。
(Comparative Example 1)
In the production process of the solid watercolor paint composition according to Example 1, a trade name “Bentonite” (manufactured by Hojun Co., Ltd.), which is montmorillonite, was further prepared as an extender pigment among the pigments. The same water-soluble resin, wetting agent, dispersant, antifoaming agent, and preservative as those in Example 1 were used. In Comparative Example 1, a cellulose ether-based water-soluble resin is not contained. Each material was mixed at the blending ratio shown in Table 2, and a solid watercolor paint composition according to Comparative Example 1 was obtained according to the production process shown in FIG. The content ratio of the pigment in the obtained solid watercolor paint composition was 43%, and the content ratio of water was 0.3%.
（比較例２）
実施例２に係る固形水彩絵具組成物の製造工程において、顔料のうちの体質顔料としてさらにモンモリロナイトである商品名「ベントナイト」（株式会社ホージュン製）を準備した。他の水溶性樹脂、湿潤剤、分散剤、消泡剤、および防腐剤については、実施例１と同じものを用いた。なお、比較例２においては、セルロースエーテル系水溶性樹脂は含有されていない。各材料を表２に示す配合割合で混ぜ、図４に示す製造工程に従い、比較例２に係る固形水彩絵具組成物を得た。得られた固形水彩絵具組成物における顔料の含有割合は、４３％であり、水の含有割合は、０．３％であった。
(Comparative Example 2)
In the production process of the solid watercolor paint composition according to Example 2, a trade name “bentonite” (manufactured by Hojun Co., Ltd.), which is montmorillonite, was further prepared as an extender among the pigments. The same water-soluble resin, wetting agent, dispersant, antifoaming agent, and preservative as those in Example 1 were used. In Comparative Example 2, a cellulose ether water-soluble resin is not contained. Each material was mixed at the blending ratio shown in Table 2, and a solid watercolor paint composition according to Comparative Example 2 was obtained according to the production process shown in FIG. The content ratio of the pigment in the obtained solid watercolor paint composition was 43%, and the content ratio of water was 0.3%.
（比較例３）
比較例１に係る固形水彩絵具組成物の製造工程において、水溶性樹脂の含有割合を表２に示す配合割合とし、体質顔料は含有しなかった以外は比較例１と同様の工程で比較例３に係る固形水彩絵具組成物を得た。なお、比較例３においても、セルロースエーテル系水溶性樹脂は含有されていない。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Comparative Example 3)
In the manufacturing process of the solid watercolor paint composition according to Comparative Example 1, the content ratio of the water-soluble resin was set to the blending ratio shown in Table 2, and the extender pigment was not included. A solid watercolor paint composition was obtained. In Comparative Example 3, the cellulose ether-based water-soluble resin is not contained. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
（比較例４）
比較例２に係る固形水彩絵具組成物の製造工程において、水溶性樹脂の含有割合を表２に示す配合割合とし、体質顔料は含有しなかった以外は比較例２と同様の工程で比較例４に係る固形水彩絵具組成物を得た。なお、比較例４においても、セルロースエーテル系水溶性樹脂は含有されていない。得られた固形水彩絵具組成物における顔料の含有割合は、４２％であり、水の含有割合は、０．３％であった。
(Comparative Example 4)
In the production process of the solid watercolor paint composition according to Comparative Example 2, the content ratio of the water-soluble resin was changed to the blending ratio shown in Table 2, and the extender pigment was not contained. A solid watercolor paint composition was obtained. In Comparative Example 4, the cellulose ether water-soluble resin is not contained. The content ratio of the pigment in the obtained solid watercolor paint composition was 42%, and the content ratio of water was 0.3%.
次に、評価試験の内容について説明する。評価試験については、以下の三つの評価項目について実施した。 Next, the contents of the evaluation test will be described. About the evaluation test, it implemented about the following three evaluation items.
「発色性」については、固形水彩絵具組成物の外観の色および描画した際の塗り色が、顔料自体の色と比べて悪くなっているか否かを目視で判断した。塗り色については、上記した図３に示す筆１５で毛部１６に水をたっぷりと含ませ、固形水彩絵具組成物１１の面１２を５回擦り、画用紙に塗布して判断した。
Regarding “color development”, it was visually determined whether or not the color of the appearance of the solid watercolor paint composition and the paint color at the time of drawing were worse than the color of the pigment itself. The coating color was judged by thoroughly applying water to the
発色性の評価としては、外観色および塗り色共に顔料自体の色と同等であるものを「Ａ」、外観色および塗り色の一方または双方が顔料自体の色と比較して若干くすんでいるものを「Ｂ」、外観色および塗り色の一方または双方が顔料自体の色と比較してくすんでいるものを「Ｃ」として評価した。「Ａ」および「Ｂ」の評価までが、問題のないレベルである。 The evaluation of color developability is “A” when the appearance color and the coating color are equivalent to the color of the pigment itself, and one or both of the appearance color and the coating color are slightly dull compared to the color of the pigment itself. Was evaluated as “C” when one or both of the appearance color and the coating color were compared with the color of the pigment itself. The level up to the evaluation of “A” and “B” is a level with no problem.
水溶け性については、上記した図３に示す筆１５で毛部１６に水をたっぷりと含ませ、固形水彩絵具組成物１１の面１２を５回擦り、画用紙にまず塗布する。そして、色がはっきり目視で判別できる程度に着色する場合を「Ａ」、着色するが色がはっきり判別できない場合を「Ｂ」として評価した。「Ａ」および「Ｂ」の評価までが、問題のないレベルである。
With respect to water solubility, the
耐高湿度性については、固形水彩絵具組成物１１を温度２０℃、湿度１００％の条件下で保存した。そして、保存後の状態に変化がなかった場合を「Ａ」、溶け出すまではいかないが、やや変形した場合を「Ｂ」、保存後の状態において固形水彩絵具組成物１１が溶け出し、変形した場合を「Ｃ」として評価した。「Ａ」の評価が、問題のないレベルである。
For high humidity resistance, the solid
表１および表２を参照して、実施例１〜実施例８については、「発色性」、「水溶け性」、および「耐高湿度性」は全て「Ａ」の評価であり、優良なものとなっている。実施例９および実施例１０については、「発色性」および「水溶け性」について全て「Ａ」の評価であるが、「耐高湿度性」については、「Ｂ」の評価である。したがって、良好な耐高湿度性を確保したい場合には、セルロースエーテル系水溶性樹脂の含有割合を０．１００質量％よりも多くするのが良い。実施例１１および実施例１２については、「発色性」および「耐高湿度性」について全て「Ａ」の評価であるが、「水溶け性」については、「Ｂ」の評価である。したがって、良好な水溶け性を確保したい場合には、セルロースエーテル系水溶性樹脂の含有割合を４０．００質量％よりも少なくするのが良い。 Referring to Tables 1 and 2, for Examples 1 to 8, “color development”, “water solubility”, and “high humidity resistance” are all “A” evaluations, which are excellent. It has become a thing. Examples 9 and 10 are all evaluated as “A” for “color developability” and “water-solubility”, whereas “high humidity resistance” is evaluated as “B”. Therefore, when it is desired to ensure good high-humidity resistance, the content of the cellulose ether-based water-soluble resin is preferably set to more than 0.100% by mass. In Examples 11 and 12, the “color developability” and the “high humidity resistance” are all evaluated as “A”, whereas the “water solubility” is evaluated as “B”. Therefore, when it is desired to ensure good water solubility, the content ratio of the cellulose ether-based water-soluble resin is preferably less than 40.00% by mass.
これに対し、比較例１〜比較例４を見てみると、いずれかの項目で、「Ｃ」の評価となっている。具体的には、セルロースエーテル系水溶性樹脂を含有せず、体質顔料を含有した比較例１および比較例２については、「発色性」の項目で「Ｃ」の評価となっている。したがって、セルロースエーテル系水溶性樹脂を含有させず体質顔料を含有させた系については、「発色性」が不十分である。セルロースエーテル系水溶性樹脂および体質顔料を含有せず、他の水溶性樹脂の含有割合を多くした比較例３および比較例４については、「耐高湿度性」の項目で「Ｃ」の評価となっている。したがって、セルロースエーテル系水溶性樹脂および体質顔料を含有せず、他の水溶性樹脂の含有割合を多くした系については、「耐高湿度性」が不十分である。 On the other hand, when Comparative Examples 1 to 4 are seen, the evaluation is “C” in any item. Specifically, Comparative Example 1 and Comparative Example 2 which did not contain a cellulose ether-based water-soluble resin and contained extender pigments were evaluated as “C” in the “color development” item. Therefore, “color developability” is insufficient for a system that does not contain a cellulose ether-based water-soluble resin but contains extender pigments. About Comparative Example 3 and Comparative Example 4 which did not contain a cellulose ether-based water-soluble resin and extender and increased the content of other water-soluble resins, an evaluation of “C” in the item of “high humidity resistance” It has become. Therefore, the “high humidity resistance” is insufficient for a system that does not contain a cellulose ether-based water-soluble resin and extender and has a higher content of other water-soluble resins.
以上より、この発明に係る固形水彩絵具組成物によれば、描画の際にユーザーが利用しやすいものとなる。 As described above, according to the solid watercolor paint composition according to the present invention, it becomes easy for the user to use when drawing.
今回開示された実施の形態および実施例はすべての点で例示であって、どのような面からも制限的なものではないと理解されるべきである。本発明の範囲は上記した説明ではなく、特許請求の範囲によって規定され、特許請求の範囲と均等の意味および範囲内でのすべての変更が含まれることが意図される。 It should be understood that the embodiments and examples disclosed herein are illustrative in all respects and are not restrictive in any respect. The scope of the present invention is defined by the scope of the claims, rather than the description above, and is intended to include any modifications within the scope and meaning equivalent to the scope of the claims.
この発明に係る固形水彩絵具組成物は、描画の際のユーザーの利便性の向上が要求される場合に、特に有効に利用される。 The solid watercolor paint composition according to the present invention is particularly effectively used when improvement in user convenience at the time of drawing is required.
１１ 固形水彩絵具組成物、１２ 面、１３ パレット、１４ 凹部、１５ 筆、１６ 毛部、１７ 胴部、１８ 第一の部材、１９ 第二の部材。 11 solid watercolor paint composition, 12 surfaces, 13 palettes, 14 recesses, 15 brushes, 16 hairs, 17 trunks, 18 first member, 19 second member.
Claims (6)
２５質量％以下の水と、
セルロースエーテル系水溶性樹脂とを含む、固形水彩絵具組成物。 30% by weight or more of pigment,
25% by weight or less of water,
A solid watercolor paint composition comprising a cellulose ether-based water-soluble resin.