JP2018028050A - Polyarylate resin and electrophotographic photoreceptor - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an electrophotographic photoreceptor excellent in wear resistance.SOLUTION: The electrophotographic photoreceptor includes a conductive substrate and a photosensitive layer. The photosensitive layer contains a charge generating agent, a hole transport agent, and a binder resin. The binder resin contains a polyarylate resin. The polyarylate resin is represented by formula (1) (r and s are each an integer of 0-49; t and u are each an integer of 1-50; r+s+t+u=100 and r+t=s+u are satisfied; and X and Y are each independently a bisphenyl ether, diphenyl, 1,4-diphenoxybenzene, or a divalent group having a naphthalene skeleton).SELECTED DRAWING: Figure 1

Description

  The present invention relates to a polyarylate resin and an electrophotographic photosensitive member.

  The electrophotographic photosensitive member is used as an image carrier in an electrophotographic image forming apparatus (for example, a printer or a multifunction machine). The electrophotographic photoreceptor includes a photosensitive layer. As the electrophotographic photosensitive member, for example, a single layer type electrophotographic photosensitive member or a multilayer type electrophotographic photosensitive member is used. The single-layer type electrophotographic photosensitive member includes a photosensitive layer having a charge generation function and a charge transport function. In the multilayer electrophotographic photosensitive member, the photosensitive layer includes a charge generation layer having a charge generation function and a charge transport layer having a charge transport function.

  Patent Document 1 describes a polyarylate resin having a repeating unit represented by the chemical formula (E-1). Further, an electrophotographic photoreceptor containing the polyarylate resin is described.

  Patent Document 2 describes a polyarylate resin having a repeating unit represented by the chemical formula (E-2). Further, an electrophotographic photoreceptor containing the polyarylate resin is described.

JP-A-56-135844 JP 2005-189716 A

  However, the polyarylate resin described in Patent Document 1 has low solubility in a solvent, and it is difficult to prepare a photosensitive layer coating solution. Moreover, although the polyarylate resin described in Patent Document 2 is soluble in a non-halogen solvent, the entanglement between molecular chains in the polyarylate resin is reduced, the packing property of the polyarylate resin is reduced, and the wear resistance is reduced. Cannot be improved sufficiently.

  The present invention has been made in view of the above problems, and is to provide a polyarylate resin that exhibits excellent wear resistance in an electrophotographic photosensitive member. Another object is to provide an electrophotographic photoreceptor provided with a photosensitive layer having excellent wear resistance.

  The polyarylate resin of the present invention is represented by the following general formula (1).

  In the general formula (1), p and l each independently represent 2 or 3. r and s represent an integer of 0 or more and 49 or less. t and u represent an integer of 1 to 50. r + s + t + u = 100. r + t = s + u. X and Y each independently represent a divalent group represented by chemical formula (1-1), chemical formula (1-2), chemical formula (1-3), or chemical formula (1-4).

  The electrophotographic photosensitive member of the present invention includes a conductive substrate and a photosensitive layer. The photosensitive layer contains a charge generator, a hole transport agent, and a binder resin. The binder resin includes the polyarylate resin described above.

  According to the polyarylate resin of the present invention, excellent abrasion resistance can be exhibited in the electrophotographic photosensitive member. In addition, according to the electrophotographic photosensitive member of the present invention, excellent wear resistance can be exhibited.

(A), (b), and (c) are each a schematic sectional drawing which shows an example of the structure of the electrophotographic photoreceptor which concerns on embodiment of this invention. 1 is a ¹ H-NMR spectrum of a polyarylate resin represented by a chemical formula (Resin-1). ^{1 is} a ¹ H-NMR spectrum of a polyarylate resin represented by a chemical formula (Resin-2). ^{1 is} a ¹ H-NMR spectrum of a polyarylate resin represented by a chemical formula (Resin-3). ^{1 is} a ¹ H-NMR spectrum of a polyarylate resin represented by a chemical formula (Resin-4).

  Hereinafter, embodiments of the present invention will be described in detail. However, the present invention is not limited to the following embodiments, and can be implemented with appropriate modifications within the scope of the object of the present invention. In addition, although description may be abbreviate | omitted suitably about the location where description overlaps, the summary of invention is not limited. In the present specification, a compound and its derivatives may be generically named by adding “system” after the compound name. When the name of a polymer is expressed by adding “system” after the compound name, it means that the repeating unit of the polymer is derived from the compound or a derivative thereof.

  Hereinafter, an alkyl group having 1 to 8 carbon atoms, an alkyl group having 1 to 6 carbon atoms, an alkyl group having 1 to 4 carbon atoms, an alkyl group having 1 to 3 carbon atoms, and 1 carbon atom The alkoxy group having 8 or less or less, the alkoxy group having 1 to 4 carbon atoms, and the cycloalkane having 5 to 7 carbon atoms have the following meanings.

  The alkyl group having 1 to 8 carbon atoms is linear or branched and unsubstituted. Examples of the alkyl group having 1 to 8 carbon atoms include methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, s-butyl group, t-butyl group, pentyl group, isopentyl group, and neopentyl group. Hexyl group, heptyl group, or octyl group.

  The alkyl group having 1 to 6 carbon atoms is linear or branched and unsubstituted. Examples of the alkyl group having 1 to 6 carbon atoms include methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, s-butyl group, t-butyl group, pentyl group, isopentyl group, and neopentyl group. Or a hexyl group.

  The alkyl group having 1 to 4 carbon atoms is linear or branched and unsubstituted. Examples of the alkyl group having 1 to 4 carbon atoms include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, a s-butyl group, and a t-butyl group.

  The alkyl group having 1 to 3 carbon atoms is linear or branched and unsubstituted. Examples of the alkyl group having 1 to 3 carbon atoms include a methyl group, an ethyl group, a propyl group, and an isopropyl group.

  The alkoxy group having 1 to 8 carbon atoms is linear or branched and unsubstituted. Examples of the alkoxy group having 1 to 8 carbon atoms include methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, s-butoxy, t-butoxy, pentyloxy, Examples include a pentyloxy group, a neopentyloxy group, a hexyloxy group, a heptyloxy group, and an octyloxy group.

  The alkoxy group having 1 to 4 carbon atoms is linear or branched and unsubstituted. Examples of the alkoxy group having 1 to 4 carbon atoms include methoxy group, ethoxy group, n-propoxy group, isopropoxy group, n-butoxy group, s-butoxy group, and t-butoxy group.

  The cycloalkane having 5 to 7 carbon atoms is, for example, an unsubstituted cycloalkane having 5 to 7 carbon atoms. Examples of the cycloalkane having 5 to 7 carbon atoms include cyclopentane, cyclohexane, and cycloheptane.

<First embodiment: polyarylate resin>
The polyarylate resin according to the first embodiment of the present invention is represented by the following general formula (1). Hereinafter, such polyarylate resin may be referred to as polyarylate resin (1).

  In general formula (1), p and l each independently represent 2 or 3. r and s represent an integer of 0 or more and 49 or less. t and u represent an integer of 1 to 50. r + s + t + u = 100. r + t = s + u. X and Y each independently represent a divalent group represented by chemical formula (1-1), chemical formula (1-2), chemical formula (1-3), or chemical formula (1-4).

  X and Y may be the same or different. p and l may be the same as or different from each other. p and l are different from each other when one of p and l represents 2 and the other of p and l represents 3. r and s may be different from each other, and r and u may be different from each other. t and s may be different from each other, and t and u may be different from each other.

  X and Y each independently preferably represent a divalent group selected from the group consisting of General Formula (1-1), General Formula (1-2), and General Formula (1-3). In addition to this, it is more preferable that X and Y are different from each other.

  From the viewpoint of further improving the wear resistance of the photoreceptor, it is preferable that one of X and Y represents a divalent group represented by the general formula (1-4).

  The polyarylate resin (1) has a repeating unit represented by the chemical formula (1-5) in terms of a mole fraction r / (r + t) (hereinafter sometimes referred to as a repeating unit (1-5)) and a general formula ( 1-7) (hereinafter sometimes referred to as repeating unit (1-7)), and repeating unit represented by formula (1-6) in terms of mole fraction s / (s + u) A unit (hereinafter, sometimes referred to as a repeating unit (1-6)) and a repeating unit represented by the general formula (1-8) (hereinafter, sometimes referred to as a repeating unit (1-8)); Have That is, when r and s represent 0, polyarylate resin (1) has a repeating unit (1-7) and a repeating unit (1-8). In the case where r and s each represent an integer of 1 or more, the polyarylate resin (1) includes, in addition to the repeating unit (1-7) and the repeating unit (1-8), the repeating unit (1-5) and the repeating unit. (1-6).

  P in the general formula (1-5), X in the general formula (1-6), l in the general formula (1-7), and Y in the general formula (1-8) are respectively represented by the general formula ( It is synonymous with p, X, l, and Y in 1).

  The polyarylate resin (1) may have only the repeating units (1-5) to (1-8) when r and s represent an integer of 1 or more. Moreover, the polyarylate resin (1) may have a repeating unit other than the repeating units (1-5) to (1-8). The ratio (molar fraction) of the total amount of the repeating units (1-5) to (1-8) to the total amount of the repeating units in the polyarylate resin (1) is preferably 0.80 or more, 0.90 or more is more preferable, and 1.00 is still more preferable.

  The arrangement of the repeating units (1-5) to (1-8) in the polyarylate resin (1) is not particularly limited as long as the repeating unit derived from the aromatic diol and the repeating unit derived from the aromatic dicarboxylic acid are adjacent to each other. . For example, the repeating unit (1-5) is bonded to each other adjacent to the repeating unit (1-6) or the repeating unit (1-8). Similarly, the repeating unit (1-7) is bonded to each other adjacent to the repeating unit (1-6) or the repeating unit (1-8). The polyarylate resin (1) may have a repeating unit other than the repeating units (1-5) to (1-8).

  R and s in General formula (1) represent the integer of 0 or more and 49 or less. t and u represent an integer of 1 to 50. r + s + t + u = 100. r + t = s + u. r / (r + t) is preferably 0.20 or more and 0.80 or less. s / (s + u) is preferably 0.20 or more and 0.80 or less. r / (r + t) is the ratio of the amount of the repeating unit (1-5) to the total amount of the repeating unit (1-5) and the repeating unit (1-7) in the polyarylate resin (1). (Molar fraction). When r / (r + t) is 0.20 or more and 0.80 or less, the photoreceptor is excellent in wear resistance. s / (s + u) is the ratio of the amount of the repeating unit (1-6) to the total amount of the repeating unit (1-6) and the repeating unit (1-8) in the polyarylate resin (1) (Molar fraction). When s / (s + u) is 0.20 or more and 0.80 or less, the wear resistance of the photoreceptor is liable to be lowered.

  The viscosity average molecular weight of the binder resin is preferably 10,000 or more from the viewpoint of wear resistance, more preferably more than 20,000, still more preferably more than 30,000, and more than 45,000. Is particularly preferred. When the viscosity average molecular weight of the binder resin is 10,000 or more, the wear resistance of the binder resin is increased and the charge transport layer is hardly worn. On the other hand, the viscosity average molecular weight of the binder resin is preferably 80,000 or less, and more preferably 51,000 or less. When the viscosity average molecular weight of the binder resin is 80,000 or less, the binder resin tends to be dissolved in a solvent when the charge transport layer is formed, and the charge transport layer tends to be easily formed.

  The method for producing the binder resin is not particularly limited as long as the polyarylate resin (1) can be produced. Examples of these production methods include a method of polycondensing an aromatic diol and an aromatic dicarboxylic acid for constituting a repeating unit of a polyarylate resin. The synthesis method of the polyarylate resin (1) is not particularly limited, and a known synthesis method (more specifically, solution polymerization, melt polymerization, interfacial polymerization, or the like) can be employed. Here, other than the aromatic dicarboxylic acid, an aromatic dicarboxylic acid derivative (more specifically, a halogenated alkanoyl or dicarboxylic anhydride) may be used.

  The aromatic dicarboxylic acid has two carboxyl groups and is represented by general formulas (1-9) to (1-10). X in general formula (1-9) and Y in general formula (1-10) are synonymous with X and Y in general formula (1), respectively.

  As the aromatic dicarboxylic acid, for example, an aromatic dicarboxylic acid having two carboxyl groups bonded on the aromatic ring (more specifically, 2,6-naphthalenedicarboxylic acid, 4,4′-dicarboxydiphenyl ether, or 4,4′-dicarboxybiphenyl and the like). In synthesizing the polyarylate resin, the aromatic dicarboxylic acid can be used as a derivative such as diacid chloride, dimethyl ester, or diethyl ester. The aromatic dicarboxylic acid may contain other aromatic dicarboxylic acids (for example, terephthalic acid or isophthalic acid) in addition to the aromatic dicarboxylic acids represented by the general formulas (1-9) and (1-10).

  The aromatic diol has two phenolic hydroxyl groups and is represented by chemical formula (1-11) and general formula (1-12). P in the general formula (1-11) and l in the general formula (1-12) are respectively synonymous with p and l in the general formula (1).

  Examples of the aromatic diol include 1,1-bis (4-hydroxyphenyl) cyclohexane or 1,1-bis (4-hydroxyphenyl) cyclopentane. In synthesizing the polyarylate resin, the aromatic diol can be used as a derivative such as diacetate. As the aromatic diol, in addition to the aromatic diol represented by the chemical formula (1-11) and the general formula (1-12), other aromatic diols (for example, bisphenol A, bisphenol S, bisphenol E, or bisphenol F) may be used. May be included.

  As polyarylate resin (1), it describes as polyarylate resin (henceforth, polyarylate resin (Resin-1)-(Resin-17)) represented by chemical formula (Resin-1)-(Resin-17), for example. May be included).

<Second Embodiment: Photoconductor>
The electrophotographic photoreceptor according to the second embodiment of the present invention (hereinafter sometimes referred to as a photoreceptor) includes a photosensitive layer. Examples of the photoreceptor include a multilayer electrophotographic photoreceptor (hereinafter sometimes referred to as a multilayer photoreceptor) or a single layer electrophotographic photoreceptor (hereinafter referred to as a single layer photoreceptor). ).

  The multilayer photoreceptor includes a charge generation layer and a charge transport layer. Hereinafter, the structure of the multilayer photoreceptor 1 according to the present embodiment will be described with reference to FIG. FIG. 1 is a schematic cross-sectional view showing the structure of the multilayer photoreceptor 1. As shown in FIG. 1A, the multilayer photoreceptor 1 includes a conductive substrate 2 and a photosensitive layer 3, for example. The photosensitive layer 3 includes a charge generation layer 3a and a charge transport layer 3b. As shown in FIG. 1A, the multilayer photoconductor 1 may include a charge generation layer 3a on a conductive substrate 2, and a charge transport layer 3b on the charge generation layer 3a. As shown in FIG. 1B, the multilayer photoreceptor 1 may include a charge transport layer 3b on the conductive substrate 2, and may further include a charge generation layer 3a on the charge transport layer 3b. As shown in FIG. 1A, the charge transport layer 3 b may be disposed as the outermost surface layer of the multilayer photoreceptor 1. The charge transport layer 3b may be a single layer (single layer).

  As shown in FIG. 1A, the photosensitive layer 3 may be disposed directly on the conductive substrate 2. As shown in FIG. 1C, the multilayer photoreceptor 1 includes, for example, a conductive substrate 2, an intermediate layer 4 (undercoat layer), and a photosensitive layer 3. As shown in FIG. 1C, the photosensitive layer 3 may be indirectly disposed on the conductive substrate 2. As shown in FIG. 1C, the intermediate layer 4 may be provided between the conductive substrate 2 and the charge generation layer 3a. The intermediate layer 4 may be provided, for example, between the charge generation layer 3a and the charge transport layer 3b. The charge generation layer 3a may be a single layer or a plurality of layers.

  The single layer type photoreceptor includes a single photosensitive layer. The single layer type photoreceptor includes, for example, a conductive substrate and a photosensitive layer, similarly to the multilayer type photoreceptor. The single layer type photoreceptor may include an intermediate layer. The photosensitive layer may be disposed as the outermost surface layer of the single layer type photoreceptor.

  The photoreceptor according to this embodiment is excellent in wear resistance. The reason is presumed as follows. The photoreceptor according to this embodiment includes a polyarylate resin (1) as a binder resin. The polyarylate resin (1) has a cyclopentylidene group or a cyclohexylidene group. Furthermore, the molar fraction r / (r + t) of the repeating unit derived from the aromatic diol is 0.00 or more and 0.90 or less. The molar fraction s / (s + u) of the repeating unit derived from the aromatic dicarboxylic acid is 0.00 or more and 0.90 or less. In the polyarylate resin (1) having such a structure, the entanglement between the molecular chains is difficult to decrease, and the packing property of the molecules is difficult to decrease. Further, since the polyarylate resin (1) having such a structure has high solubility in a solvent, it is easy to prepare a coating solution for forming a photosensitive layer. As a result, it is easy to obtain a photosensitive layer having a high layer density. Therefore, the photoreceptor according to this embodiment is excellent in wear resistance.

  Hereinafter, the elements (conductive substrate, photosensitive layer, and intermediate layer) of the photoreceptor according to this embodiment will be described. Further, a method for producing a photoreceptor will be described.

[1. Conductive substrate]
The conductive substrate is not particularly limited as long as it can be used as the conductive substrate of the photoreceptor. The conductive substrate can be made of at least a surface portion with a conductive material. Examples of the conductive substrate include a conductive substrate made of a material having conductivity, or a conductive substrate coated with a conductive material. Examples of the conductive material include aluminum, iron, copper, tin, platinum, silver, vanadium, molybdenum, chromium, cadmium, titanium, nickel, palladium, and indium. Among these materials having conductivity, one kind may be used alone, or two or more kinds may be used in combination. Examples of the combination of two or more include an alloy (more specifically, an aluminum alloy, stainless steel, or brass).

  Among these materials having conductivity, conductivity, aluminum, or an aluminum alloy is preferable because charge transfer from the photosensitive layer to the conductive substrate is good.

  The shape of the conductive substrate can be appropriately selected according to the structure of the image forming apparatus to be used. For example, a sheet-like conductive substrate or a drum-shaped conductive substrate can be used. Further, the thickness of the conductive substrate can be appropriately selected according to the shape of the conductive substrate.

[2. Photosensitive layer]
The photosensitive layer contains a charge generator, a hole transport agent, and a binder resin. The binder resin includes a polyarylate resin (1). The photosensitive layer may contain an additive. The photosensitive layer of the multilayer photoreceptor includes a charge generation layer and a charge transport layer. The charge generation layer contains a charge generation agent. The charge transport layer contains a hole transport agent and a binder resin. The thickness of the charge generation layer is not particularly limited as long as it can sufficiently function as the charge generation layer. Specifically, the thickness of the charge generation layer is preferably 0.01 μm or more and 5 μm or less, and more preferably 0.1 μm or more and 3 μm or less. The thickness of the charge transport layer is not particularly limited as long as it can sufficiently function as the charge transport layer. Specifically, the thickness of the charge transport layer is preferably 2 μm or more and 100 μm or less, and more preferably 5 μm or more and 50 μm or less.

  The photosensitive layer (single layer type photosensitive layer) of the single layer type photoreceptor contains a charge generating agent, a hole transport agent, and a binder resin. The thickness of the photosensitive layer is not particularly limited as long as the function as the photosensitive layer can be sufficiently expressed. Specifically, the thickness of the photosensitive layer may be 5 μm or more and 100 μm or less, and is preferably 10 μm or more and 50 μm or less.

[2-1. Common components]
Hereinafter, the charge generator, the hole transport agent, and the binder resin will be described. Furthermore, an additive is demonstrated.

[2-1-1. Charge generator]
The charge generator is not particularly limited as long as it is a charge generator for a photoreceptor. Examples of the charge generator include phthalocyanine pigments, perylene pigments, bisazo pigments, dithioketopyrrolopyrrole pigments, metal-free naphthalocyanine pigments, metal naphthalocyanine pigments, squaraine pigments, trisazo pigments, indigo pigments, azurenium pigments, cyanine Pigments, powders of inorganic photoconductive materials such as selenium, selenium-tellurium, selenium-arsenic, cadmium sulfide, amorphous silicon, pyrylium salts, ansanthrone pigments, triphenylmethane pigments, selenium pigments, toluidine pigments, pyrazolines Pigments or quinacridone pigments. Examples of the phthalocyanine pigment include phthalocyanine or phthalocyanine derivatives. Examples of phthalocyanines include metal-free phthalocyanine pigments (more specifically, X-type metal-free phthalocyanine (x-H ₂ Pc) and the like). Examples of the phthalocyanine derivative include metal phthalocyanine pigments (more specifically, titanyl phthalocyanine or V-type hydroxygallium phthalocyanine). The crystal shape of the phthalocyanine pigment is not particularly limited, and phthalocyanine pigments having various crystal shapes are used. Examples of the crystal shape of the phthalocyanine pigment include α-type, β-type, and Y-type. A charge generating agent may be used individually by 1 type, and may be used in combination of 2 or more type.

  A charge generator having an absorption wavelength in a desired region may be used alone, or two or more charge generators may be used in combination. Further, for example, in a digital optical image forming apparatus, it is preferable to use a photoconductor having sensitivity in a wavelength region of 700 nm or more. Examples of the digital optical image forming apparatus include a laser beam printer or a facsimile using a light source such as a semiconductor laser. Therefore, for example, phthalocyanine pigments are preferable, and Y-type titanyl phthalocyanine (Y-TiOPc) is more preferable. Y-type titanyl phthalocyanine may have one peak at a Bragg angle of 2θ ± 0.2 ° = 27.2 ° in a Cu-Kα characteristic X-ray diffraction spectrum.

  An ansanthrone pigment or a perylene pigment is preferably used as a charge generating agent in a photoreceptor applied to an image forming apparatus using a short wavelength laser light source. The short wavelength laser light source has a wavelength of about 350 nm to 550 nm, for example.

  The charge generator is, for example, a phthalocyanine pigment represented by chemical formulas (CGM-1) to (CGM-4) (hereinafter referred to as charge generators (CGM-1) to (CGM-4), respectively). There).

  The content of the charge generating agent is preferably 5 parts by mass or more and 1000 parts by mass or less with respect to 100 parts by mass of the binder resin for charge generation layer (hereinafter sometimes referred to as a base resin), and 30 parts by mass. The amount is more preferably 500 parts by mass or less.

[2-1-2. Hole transport agent]
Examples of the hole transporting agent include trilylamine derivatives and diamine derivatives (more specifically, N, N, N ′, N′-tetraphenylphenylenediamine derivatives, N, N, N ′, N′-tetra). Phenylnaphthylene diamine derivatives or N, N, N ′, N′-tetraphenylphenanthrylenediamine derivatives, etc.); oxadiazole compounds (more specifically, 2,5-di (4-methylaminophenyl) ) -1,3,4-oxadiazole, etc.]; styryl compounds (more specifically, 9- (4-diethylaminostyryl) anthracene, etc.); carbazole compounds (more specifically, polyvinyl carbazole, etc.) Organic polysilane compounds; pyrazoline-based compounds (more specifically, 1-phenyl-3- (p-dimethylaminophenyl) pyrazoline and the like); hydra Emissions based compounds; indole-based compound; oxazole-based compounds; isoxazole compounds; thiazole compounds; thiadiazole compounds; imidazole compounds; pyrazole compound; triazole compounds. Of these hole transport agents, compounds represented by the general formula (2), the general formula (3), or the general formula (4) are preferable. From the viewpoint of improving the wear resistance of the photoreceptor, the hole transport agent preferably contains a compound represented by the general formulas (2) to (4). From the viewpoint of improving the electrical characteristics of the photoreceptor in addition to the wear resistance of the photoreceptor, the hole transport agent preferably contains a compound represented by the general formula (2) or the general formula (3). . It is more preferable that the hole transport agent contains a compound represented by the general formula (3).

In general formula (2), Q ₁ is substituted with a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or an alkyl group having 1 to 8 carbon atoms. Represents an optionally substituted phenyl group. Q ₂ is each independently an alkyl group having 1 to 8 carbon atoms,
An alkoxy group having 1 to 8 carbon atoms or a phenyl group is represented. Q ₃ , Q ₄ , Q ₅ , Q ₆ , and Q ₇ are each independently a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or a phenyl group. Represent. Two adjacent ones of Q ₃ , Q ₄ , Q ₅ , Q ₆ , and Q ₇ may be bonded to each other to form a ring. a represents an integer of 0 or more and 5 or less. When a represents an integer of 2 or more and 5 or less, a plurality of Q ₂ bonded to the same phenyl group are
They may be the same or different from each other.

In General Formula (3), Q ₈ , Q ₁₀ , Q ₁₁ , Q ₁₂ , Q ₁₃ , and Q ₁₄ are each independently a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, or 1 or more carbon atoms. It represents an alkoxy group of 8 or less or a phenyl group. Q ₉ and Q ₁₅ each independently represents an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or a phenyl group. b represents an integer of 0 or more and 5 or less. When b represents an integer of 2 or more and 5 or less, a plurality of Q ₉ bonded to the same phenyl group may be the same as or different from each other. c represents an integer of 0 or more and 4 or less. When c represents an integer of 2 or more and 4 or less, the plurality of Q ₁₅ bonded to the same phenyl group may be the same as or different from each other. k represents 0 or 1.

In general formula (4), R _a , R _b and R _c each independently represents an alkyl group having 1 to 8 carbon atoms, a phenyl group, or an alkoxy group having 1 to 8 carbon atoms. q represents an integer of 0 or more and 4 or less. When q represents an integer of 2 or more and 4 or less, a plurality of R _c bonded to the same phenyl group may be the same or different from each other. m and n each independently represent an integer of 0 or more and 5 or less. When m represents an integer of 2 or more and 5 or less, a plurality of R _b bonded to the same phenyl group may be the same or different from each other. When n represents an integer of 2 or more and 5 or less, a plurality of R _a bonded to the same phenyl group may be the same or different from each other.

In general formula (2), the phenyl group represented by Q ₁ is preferably a phenyl group substituted with an alkyl group having 1 to 8 carbon atoms, more preferably a phenyl group substituted with a methyl group. preferable.

In general formula (2), the alkyl group having 1 to 8 carbon atoms represented by Q ₂ is preferably an alkyl group having 1 to 6 carbon atoms, and is an alkyl group having 1 to 4 carbon atoms. More preferably, it is more preferably a methyl group. It is preferable that a represents 0 or 1.

In general formula (2), the alkyl group having 1 to 8 carbon atoms represented by Q _{3 to} Q ₇ is preferably an alkyl group having 1 to 4 carbon atoms, and preferably an n-butyl group. More preferred. In general formula (2), the alkoxy group having 1 to 8 carbon atoms represented by Q _{3 to} Q ₇ is preferably an alkoxy group having 1 to 4 carbon atoms, and more preferably a methoxy group or an ethoxy group. . In the general formula (2), Q _{3 to} Q ₇ preferably each independently represent a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, or an alkoxy group having 1 to 8 carbon atoms, More preferably, it represents an atom, an alkyl group having 1 to 4 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms.

In general formula (2), two adjacent ones of Q _{3 to} Q ₇ are bonded to each other to form a ring (more specifically, a benzene ring or a cycloalkane having 5 to 7 carbon atoms). May be. For example, Q ₆ and Q ₇ adjacent to each other among Q _{3 to} Q ₇ may be bonded to each other to form a benzene ring or a cycloalkane having 5 to 7 carbon atoms. When two adjacent Q _{3 to} Q ₇ are bonded to each other to form a benzene ring, this benzene ring is condensed with a phenyl group to which Q _{3 to} Q ₇ are bonded to form a bicyclic condensed ring group (naphthyl group). Form. When two adjacent Q _{3 to} Q ₇ are bonded to each other to form a cycloalkane having 5 to 7 carbon atoms, Q _{3 to} Q ₇ are bonded to the cycloalkane having 5 to 7 carbon atoms. To form a bicyclic fused ring group. In this case, the condensation site between the cycloalkane having 5 to 7 carbon atoms and the phenyl group may contain a double bond. Two adjacent Q _{3 to} Q ₇ are preferably bonded to each other to form a cycloalkane having 5 to 7 carbon atoms, more preferably cyclohexane.

In general formula (2), Q ₁ preferably represents a hydrogen atom or a phenyl group substituted with an alkyl group having 1 to 8 carbon atoms. Q ₂ preferably represents an alkyl group having 1 to 8 carbon atoms. Q _{3 to} Q ₇ each independently preferably represent a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, or an alkoxy group having 1 to 8 carbon atoms. It is preferable that two adjacent Q _{3 to} Q ₇ are bonded to each other to form a ring. It is preferable that a represents 0 or 1.

In general formula (3), the alkyl group having 1 to 8 carbon atoms represented by Q ₈ and Q _{10 to} Q ₁₄ is preferably an alkyl group having 1 to 4 carbon atoms, and may be a methyl group or an ethyl group. It is more preferable that In general formula (3), Q ₈ and Q _{10 to} Q ₁₄ preferably each independently represent a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, or a phenyl group. In general formula (3), b and c preferably represent 0.

In general formula (4), the alkyl group having 1 to 8 carbon atoms represented by R _a and R _b is preferably an alkyl group having 1 to 4 carbon atoms, and represents a methyl group or an ethyl group. Is more preferable. It is preferable that m and n each independently represent an integer of 0 or more and 2 or less. q preferably represents 0.

  The hole transport agent is specifically a hole transport agent represented by the formulas (HTM-1) to (HTM-9) (hereinafter referred to as hole transport agents (HTM-1) to (HTM-9). )). In addition, hole transport agents (HTM-1) to (HTM-4) are specific examples of the compound represented by the general formula (2). The hole transport agents (HTM-5) to (HTM-7) are specific examples of the compound represented by the general formula (3). The hole transport agent (HTM-8) and the hole transport agent (HTM-9) are specific examples of the compound represented by the general formula (4).

  In the multilayer photoreceptor, the content of the hole transport agent is preferably 10 parts by mass or more and 200 parts by mass or less, and more preferably 20 parts by mass or more and 100 parts by mass or less with respect to 100 parts by mass of the binder resin. More preferred.

[2-1-3. Binder resin]
The binder resin is used for a charge transport layer of a multilayer photoreceptor or a photosensitive layer of a single-layer photoreceptor. The binder resin includes a polyarylate resin (1). When the photoconductor contains the polyarylate resin (1), the wear resistance of the photoconductor can be improved.

  As binder resin used for this embodiment, polyarylate resin (1) may be used independently, and other resin other than polyarylate resin (1) is included in the range which does not impair the effect of this invention. May be. Examples of other resins include thermoplastic resins (polyarylate resins other than polyarylate resin (1), polycarbonate resins, styrene resins, styrene-butadiene copolymers, styrene-acrylonitrile copolymers, and styrene-maleic acid copolymers. Polymer, styrene-acrylic acid copolymer, acrylic copolymer, polyethylene resin, ethylene-vinyl acetate copolymer, chlorinated polyethylene resin, polyvinyl chloride resin, polypropylene resin, ionomer, vinyl chloride-vinyl acetate copolymer Polyester resin, alkyd resin, polyamide resin, polyurethane resin, polysulfone resin, diallyl phthalate resin, ketone resin, polyvinyl butyral resin, polyether resin, or polyester resin), thermosetting resin (silicone resin, epoxy resin, phenol resin) Lumpur resins, urea resins, melamine resins, or other crosslinking thermosetting resins), or light-curing resin (epoxy - acrylic acid resin, or urethane - acrylic acid copolymer). These may be used alone or in combination of two or more. The content of the polyarylate resin (1) is preferably 80 parts by mass or more, more preferably 90 parts by mass or more, and still more preferably 100 parts by mass with respect to 100 parts by mass of the binder resin.

  In the present embodiment, the content ratio of the binder resin is preferably 40% by mass or more based on the total mass of all the components (for example, a hole transport agent or a binder resin) included in the charge transport layer, 80 mass% or more is more preferable.

[2-1-4. Additive]
At least one of the charge generation layer, the charge transport layer, the photosensitive layer and the intermediate layer of the single-layer type photoreceptor may contain various additives as long as the electrophotographic characteristics are not adversely affected. Examples of the additive include a deterioration inhibitor (more specifically, an antioxidant, a radical scavenger, a quencher, or an ultraviolet absorber), a softener, a surface modifier, a bulking agent, a thickener, A dispersion stabilizer, a wax, an electron acceptor compound, a donor, a surfactant, or a leveling agent can be used.

  Examples of the antioxidant include a hindered phenol compound, a hindered amine compound, a thioether compound, or a phosphite compound. Among these antioxidants, hindered phenol compounds and hindered amine compounds are preferred.

  Examples of the softening agent include metaterphenyl.

  The addition amount of the antioxidant in the charge transport layer is preferably 0.1 parts by mass or more and 10 parts by mass or less with respect to 100 parts by mass of the binder resin. When the addition amount of the antioxidant is within such a range, it is easy to suppress deterioration of electrical characteristics due to oxidation of the photoreceptor.

[2-2. Non-common components]
In the multilayer photoreceptor, the charge generation layer may contain a charge generation layer binder resin (hereinafter sometimes referred to as a base resin). The base resin is not particularly limited as long as it can be applied to the photoreceptor. Examples of the base resin include a thermoplastic resin, a thermosetting resin, and a photocurable resin. Examples of thermoplastic resins include styrene resins, styrene-butadiene copolymers, styrene-acrylonitrile copolymers, styrene-maleic acid copolymers, styrene-acrylic acid copolymers, acrylic copolymers, and polyethylene resins. , Ethylene-vinyl acetate copolymer, chlorinated polyethylene resin, polyvinyl chloride resin, polypropylene resin, ionomer, vinyl chloride-vinyl acetate copolymer, alkyd resin, polyamide resin, urethane resin, polycarbonate resin, polyarylate resin, polysulfone Examples of the resin include diallyl phthalate resin, ketone resin, polyvinyl butyral resin, polyether resin, and polyester resin. Examples of the thermosetting resin include silicone resins, epoxy resins, phenol resins, urea resins, melamine resins, and other crosslinkable thermosetting resins. Examples of the photocurable resin include an epoxy acrylic acid resin or a urethane-acrylic acid resin. These may be used individually by 1 type and may be used in combination of 2 or more type.

  As the base resin, the same resin as the above-described binder resin is also exemplified. However, in the same laminated photoreceptor, a resin different from the binder resin is usually selected. This is based on the following reasons. When manufacturing a multilayer photoreceptor, usually, a charge generation layer and a charge transport layer are formed in this order, and therefore a charge transport layer coating solution is applied to the charge generation layer. During the formation of the charge transport layer, the charge generation layer is preferably not dissolved in the solvent of the charge transport layer coating solution. Therefore, as the base resin, a resin different from the binder resin is usually selected in the same laminated photoreceptor.

[3. Middle layer]
The photoreceptor according to the exemplary embodiment may include an intermediate layer (for example, an undercoat layer). An intermediate | middle layer contains the resin (resin for intermediate | middle layers) used for an inorganic particle and an intermediate | middle layer, for example. When the intermediate layer is interposed, an increase in electrical resistance can be suppressed by smoothing the flow of current generated when the photosensitive member is exposed while maintaining an insulating state capable of suppressing the occurrence of leakage.

  Examples of the inorganic particles include metal (more specifically, aluminum, iron, copper, etc.) particles, metal oxide (more specifically, titanium oxide, alumina, zirconium oxide, tin oxide, or zinc oxide). Etc.) or non-metal oxide (more specifically, silica etc.) particles. These inorganic particles may be used individually by 1 type, and may use 2 or more types together.

  The intermediate layer resin is not particularly limited as long as it can be used as a resin for forming the intermediate layer.

[4. Photoconductor manufacturing method]
A method for manufacturing the photoreceptor will be described. The method for producing a photoreceptor includes, for example, a photosensitive layer forming step.

[4-1. Method for producing laminated photoreceptor]
In the method for producing a multilayer photoreceptor, the photosensitive layer forming step includes a charge generation layer forming step and a charge transport layer forming step. In the charge generation layer forming step, first, a coating liquid for forming the charge generation layer (hereinafter, sometimes referred to as a charge generation layer coating liquid) is prepared. A charge generation layer coating solution is applied onto the conductive substrate. Next, by drying by an appropriate method, at least a part of the solvent contained in the applied charge generation layer coating solution is removed to form a charge generation layer. The charge generation layer coating solution includes, for example, a charge generation agent, a base resin, and a solvent. Such a coating solution for charge generation layer is prepared by dissolving or dispersing a charge generation agent in a solvent. Various additives may be added to the charge generation layer coating solution as necessary.

  In the charge transport layer forming step, first, a coating liquid for forming the charge transport layer (hereinafter, sometimes referred to as a charge transport layer coating liquid) is prepared. A charge transport layer coating solution is applied onto the charge generation layer. Next, by drying by an appropriate method, at least a part of the solvent contained in the applied charge transport layer coating solution is removed to form a charge transport layer. The coating solution for charge transport layer contains a hole transport agent, a polyarylate resin (1) as a binder resin, and a solvent. The coating solution for the charge transport layer can be prepared by dissolving or dispersing the hole transport agent and the polyarylate resin (1) in a solvent. Various additives may be added to the charge transport layer coating solution as necessary.

[4-2. Manufacturing method of single layer type photoreceptor]
In the method for producing a single-layer type photoreceptor, in the photosensitive layer forming step, a coating solution for forming a photosensitive layer (hereinafter sometimes referred to as a photosensitive layer coating solution) is prepared. A photosensitive layer coating solution is applied onto the conductive substrate. Next, by drying by an appropriate method, at least a part of the solvent contained in the applied photosensitive layer coating solution is removed to form a photosensitive layer. The photosensitive layer coating solution contains, for example, a charge generating agent, a hole transport agent, a polyarylate resin (1) as a binder resin, and a solvent. Such a coating solution for a photosensitive layer is prepared by dissolving or dispersing a charge generator, a hole transport agent, and a binder resin in a solvent. Various additives may be added to the photosensitive layer coating solution as necessary.

  Hereinafter, details of the photosensitive layer forming step will be described. The solvent contained in the charge generation layer coating solution, the charge transport layer coating solution, and the photosensitive layer coating solution (hereinafter, these three coating solutions may be described together) is a coating solution. If each component contained in can be dissolved or dispersed, it is not particularly limited. Examples of the solvent include alcohol (more specifically, methanol, ethanol, isopropanol, butanol, etc.), aliphatic hydrocarbon (more specifically, n-hexane, octane, cyclohexane, etc.), aromatic carbonization, and the like. Hydrogen (more specifically, benzene, toluene, xylene, etc.), halogenated hydrocarbon (more specifically, dichloromethane, dichloroethane, carbon tetrachloride, chlorobenzene, etc.), ether (more specifically, dimethyl ether) , Diethyl ether, tetrahydrofuran, ethylene glycol dimethyl ether, or diethylene glycol dimethyl ether), ketones (more specifically, acetone, methyl ethyl ketone, or cyclohexanone), esters (more specifically, ethyl acetate or methyl acetate, etc.), Methyl formaldehyde, dimethylformamide, or dimethyl sulfoxide. These solvents may be used alone or in combination of two or more. Of these solvents, non-halogen solvents are preferably used.

  Furthermore, the solvent contained in the charge transport layer coating solution is preferably different from the solvent contained in the charge generation layer coating solution. When manufacturing a laminated photoreceptor, usually, a charge generation layer and a charge transport layer are formed in this order, and therefore a charge transport layer coating solution is applied on the charge generation layer. This is because the charge generation layer is required not to be dissolved in the solvent of the charge transport layer coating solution when the charge transport layer is formed.

  The charge generation layer coating solution, the charge transport layer coating solution, and the photosensitive layer coating solution are prepared by mixing each component and dispersing in a solvent. For mixing or dispersing, for example, a bead mill, a roll mill, a ball mill, an attritor, a paint shaker, or an ultrasonic disperser can be used.

  The coating liquid may contain, for example, a surfactant or a leveling agent in order to improve the dispersibility of each component or the surface smoothness of each layer formed.

  The method for applying the coating solution is not particularly limited as long as the method can uniformly apply the coating solution. Examples of the coating method include a dip coating method, a spray coating method, a spin coating method, and a bar coating method.

  The method for removing at least a part of the solvent contained in the coating solution is not particularly limited as long as it is a method capable of evaporating the solvent in the charge generation layer coating solution and the charge transport layer coating solution. Examples of the removal method include heating, reduced pressure, or combined use of heating and reduced pressure. More specifically, a method of performing heat treatment (hot air drying) using a high-temperature dryer or a vacuum dryer can be mentioned. The heat treatment conditions are, for example, a temperature of 40 ° C. or higher and 150 ° C. or lower and a time of 3 minutes or longer and 120 minutes or shorter.

  Note that the method for manufacturing a photoreceptor may further include a step of forming an intermediate layer as necessary. A known method can be selected as appropriate for the step of forming the intermediate layer.

  The electrophotographic photosensitive member of the present invention described above is excellent in wear resistance and can be suitably used in various image forming apparatuses.

  Hereinafter, the present invention will be described more specifically with reference to examples. The present invention is not limited to the scope of the examples.

<< Preparation of polyarylate resin >>
[Preparation of polyarylate resin (Resin-1)]
A three-necked flask was used as a reaction vessel. This reaction container is a 1 L three-necked flask equipped with a thermometer, a three-way cock, and a dropping funnel 200 mL. In a reaction vessel, 1,1-bis (4-hydroxy-3-methylphenyl) cyclohexane 12.24 g (41.28 mmol), t-butylphenol 0.062 g (0.413 mmol), and sodium hydroxide 3.92 g (98 mmol) and 0.120 g (0.384 mmol) of benzyltributylammonium chloride were added. Next, the inside of the reaction vessel was purged with argon. Thereafter, 300 mL of water was further added to the reaction vessel. The internal temperature of the reaction vessel was raised to 50 ° C. The content in the reaction vessel was stirred for 1 hour while maintaining the internal temperature of the reaction vessel at 50 ° C. Thereafter, the internal temperature of the reaction vessel was cooled to 10 ° C. As a result, an alkaline aqueous solution was obtained.

  On the other hand, 4.10 g (16.2 mmol) of 2,6-naphthalenedicarboxylic acid dichloride and 4.52 g (16.2 mmol) of biphenyl-4,4′-dicarboxylic acid dichloride were added with chloroform (Amilan (registered trademark)). Product) dissolved in 150 mL. As a result, a chloroform solution was obtained.

  Subsequently, the said chloroform solution was dripped slowly over 110 minutes from the dropping funnel to the said alkaline aqueous solution, and the polymerization reaction was started. The internal temperature in the reaction vessel was adjusted to 15 ± 5 ° C., and the contents in the reaction vessel were stirred for 4 hours to proceed the polymerization reaction.

  Then, the upper layer (water layer) in the contents of the reaction vessel was removed using a decant to obtain an organic layer. Next, 400 mL of ion exchange water was added to a 1 L three-necked flask, and then the obtained organic layer was added. Further, 400 mL of chloroform and 2 mL of acetic acid were added. The contents of the three-necked flask were stirred at room temperature (25 ° C.) for 30 minutes. Thereafter, the upper layer (aqueous layer) in the contents of the closed-mouth flask was removed using a decant to obtain an organic layer. The organic layer obtained using 1 L of water was washed 5 times with a separatory funnel. As a result, an organic layer washed with water was obtained.

  Next, the organic layer washed with water was filtered to obtain a filtrate. 1 L of methanol was charged into a 1 L Erlenmeyer flask. The obtained filtrate was slowly dropped into an Erlenmeyer flask to obtain a precipitate. The precipitate was filtered off. The obtained precipitate was vacuum-dried at a temperature of 70 ° C. for 12 hours. As a result, a polyarylate resin (Resin-1) was obtained. The yield of polyarylate resin (Resin-1) was 12.2 g, and the yield was 77 mol%.

[Production of Polyarylate Resins (Resin-2) to (Resin-14)]
1,1-bis (4-hydroxy-3-methylphenyl) cyclohexane was changed to an aromatic diol which is a starting material of polyarylate resins ((Resin-2) to (Resin-14)), and 2,6-naphthalene Dicarboxylic acid dichloride and biphenyl-4,4′-dicarboxylic acid dichloride were changed to halogenated alkanoyl which is a starting material of polyarylate resins ((Resin-2) to (Resin-14)). Furthermore, the content of the aromatic dicarboxylic acid was changed to a content corresponding to the molar fraction r / (r + t), and the content of the aromatic diol was changed to a content corresponding to the molar fraction s / (s + u). . Except for the above changes, polyarylate resins (Resin-2) to (Resin-14) were produced in the same manner as polyarylate resin (Resin-1).

Next, ¹ H-NMR spectra of the prepared polyarylate resins (Resin-1) to (Resin-12) were measured using a proton nuclear magnetic resonance spectrometer (manufactured by JASCO Corporation, 300 MHz). CDCl ₃ was used as the solvent. Tetramethylsilane (TMS) was used as an internal standard sample. Among these, polyarylate resins (Resin-1) to (Resin-4) are given as representative examples.

2 to 5 show ¹ H-NMR spectra of polyarylate resins (Resin-1) to (Resin-4), respectively. 2 to 5, the horizontal axis represents chemical shift (unit: ppm), and the vertical axis represents signal intensity (unit: arbitrary unit). ^{From the 1} H-NMR spectrum, it was confirmed that polyarylate resins (Resin-1) to (Resin-4) were obtained. In the same manner, other polyarylate resins (Resin-5) to (Resin-14) were obtained from ¹ H-NMR spectra, respectively, from polyarylate resins (Resin-5) to (Resin-17). confirmed.

<< Manufacture of photoconductor >>
[Production of Photosensitive Member (A-1)]
Hereinafter, the production of the photoreceptor (A-1) according to Example 1 will be described.

(Formation of intermediate layer)
First, surface-treated titanium oxide (“Prototype SMT-A” manufactured by Teika Co., Ltd., average primary particle size 10 nm) was prepared. Specifically, titanium oxide was surface-treated with alumina and silica, and further, surface-treated with methyl hydrogen polysiloxane was prepared while wet-dispersing the surface-treated titanium oxide. Next, a quaternary combination of surface-treated titanium oxide (2 parts by mass) and polyamide resin Amilan (registered trademark) (“CM8000” manufactured by Toray Industries, Inc.) (polyamide 6, polyamide 12, polyamide 66, and polyamide 610) Polymerized polyamide resin) (1 part by mass) was added to a solvent containing methanol (10 parts by mass), butanol (1 part by mass) and toluene (1 part by mass). These were mixed for 5 hours using a bead mill, and the material was dispersed in the solvent. This prepared the coating liquid for intermediate | middle layers.

  The obtained intermediate layer coating solution was filtered using a filter having an opening of 5 μm. Then, the intermediate layer coating solution was applied to the surface of an aluminum drum-shaped support (diameter 30 mm, total length 246 mm) as a conductive substrate using a dip coating method. Subsequently, the applied coating solution for intermediate layer was dried at 130 ° C. for 30 minutes to form an intermediate layer (film thickness: 1.5 μm) on the conductive substrate (drum-shaped support).

(Formation of charge generation layer)
Y-type titanyl phthalocyanine (1.5 parts by mass) and a polyvinyl acetal resin (“SREC BX-5” manufactured by Sekisui Chemical Co., Ltd.) (1 part by mass) as a base resin are mixed with propylene glycol monomethyl ether (40 parts by mass). ) And tetrahydrofuran (40 parts by mass). These were mixed for 12 hours using a bead mill, and the material was dispersed in a solvent to prepare a charge generation layer coating solution. The obtained coating solution for charge generation layer was filtered using a filter having an opening of 3 μm. Next, the obtained filtrate was applied on the intermediate layer formed as described above using a dip coating method and dried at 50 ° C. for 5 minutes. As a result, a charge generation layer (thickness: 0.3 μm) was formed on the intermediate layer.

(Formation of charge transport layer)
50 parts by mass of a hole transporting agent (HTM-1) as a hole transporting agent, 2 parts by mass of a hindered phenol antioxidant (“Irganox (registered trademark) 1010” manufactured by BASF Corporation) as an additive, 100 parts by mass of polyarylate resin (Resin-1) (viscosity average molecular weight 46,000) as a binder resin was added to a solvent containing 550 parts by mass of tetrahydrofuran and 150 parts by mass of toluene. These were mixed for 12 hours, and the material was dispersed in a solvent to prepare a coating solution for a charge transport layer.

  The charge transport layer coating solution was applied onto the charge generation layer in the same manner as the charge generation layer coating solution. Then, it was dried at 120 ° C. for 40 minutes to form a charge transport layer (film thickness 20 μm) on the charge generation layer. As a result, a photoreceptor (A-1) was obtained. The photoreceptor (A-1) had a configuration in which an intermediate layer, a charge generation layer, and a charge transport layer were laminated in this order on a conductive substrate.

[Photoreceptor (A-2)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transport agent (HTM-2) was used instead of the hole transport agent (HTM-1). -2).

[Photoreceptor (A-3)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transport agent (HTM-3) was used instead of the hole transport agent (HTM-1). -3) was produced.

[Photoreceptor (A-4)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transfer agent (HTM-4) was used instead of the hole transfer agent (HTM-1). -4) was produced.

[Photoreceptor (A-5)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transfer agent (HTM-5) was used instead of the hole transfer agent (HTM-1). -5) was produced.

[Photosensitive member (A-6)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transfer agent (HTM-6) was used instead of the hole transfer agent (HTM-1). -6) was produced.

[Photosensitive member (A-7)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transfer agent (HTM-7) was used instead of the hole transfer agent (HTM-1). -7) was produced.

[Photoreceptor (A-8)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transfer agent (HTM-8) was used instead of the hole transfer agent (HTM-1). -8) was produced.

[Photosensitive member (A-9)]
The photoconductor (A-1) was prepared in the same manner as the photoconductor (A-1) except that the hole transfer agent (HTM-9) was used instead of the hole transfer agent (HTM-1). -9) was produced.

[Photosensitive member (A-10)]
A photoconductor (A-10) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-2) was used instead of the polyarylate resin (Resin-1).

[Photoreceptor (A-11)]
A photoconductor (A-11) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-3) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-12)]
A photoconductor (A-12) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-4) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-13)]
A photoconductor (A-13) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-5) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-14)]
A photoconductor (A-14) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-6) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-15)]
A photoconductor (A-15) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-7) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-16)]
A photoconductor (A-16) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-8) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-17)]
A photoconductor (A-17) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-9) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-18)]
A photoconductor (A-18) was produced in the same manner as the photoconductor (A-1) except that a polyarylate resin (Resin-10) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-19)]
A photoconductor (A-19) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-11) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-20)]
A photoconductor (A-20) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-12) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-21)]
A photoconductor (A-21) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-13) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-22)]
A photoconductor (A-22) was produced in the same manner as the photoconductor (A-1) except that the polyarylate resin (Resin-14) was used instead of the polyarylate resin (Resin-1).

[Photosensitive member (A-23)]
A photoconductor (A-23) was produced in the same manner as the photoconductor (A-1) except that the following items were changed. The dispersion time of the charge generation layer coating solution was changed from 12 hours to 2 hours. In preparing the coating solution for the charge transport layer, polyarylate resin (Resin-2) was used instead of polyarylate resin (Resin-1), and metaterphenyl was used as an additive instead of 2 parts by mass of hindered phenol antioxidant. 5 parts by mass was used, and 600 parts by mass of tetrahydrofuran and 100 parts by mass of toluene were used as a solvent instead of 550 parts by mass of tetrahydrofuran and 150 parts by mass of toluene. Further, after the charge transport layer coating solution was prepared and before coating on the charge generation layer, the charge transport layer coating solution was allowed to stand for 30 days. Drying conditions (temperature 120 ° C. and time 40 minutes) after coating the charge transport layer coating solution on the charge generation layer are changed to drying conditions (starting temperature 60 ° C. to final reaching temperature 130 ° C. + 1 ° C.) To 60 minutes / minute).

[Photosensitive member (A-24)]
A photoconductor (A-24) was produced in the same manner as the photoconductor (A-23) except that a polyarylate resin (Resin-15) was used instead of the polyarylate resin (Resin-2).

[Photosensitive member (A-25)]
A photoconductor (A-25) was produced in the same manner as the photoconductor (A-23) except that the polyarylate resin (Resin-16) was used instead of the polyarylate resin (Resin-2).

[Photosensitive member (A-26)]
A photoconductor (A-26) was produced in the same manner as the photoconductor (A-23) except that the polyarylate resin (Resin-17) was used instead of the polyarylate resin (Resin-2).

[Photoreceptor (B-1)]
As the binder resin, a polyarylate resin having a repeating unit represented by the chemical formula (Resin-B1) instead of the polyarylate resin (Resin-1) (hereinafter sometimes referred to as polyarylate resin (Resin-B1)). A photoconductor (B-1) was produced in the same manner as the photoconductor (A-1) except that was used.

[Performance evaluation of photoconductor]
(Electrical characteristics evaluation)
(Measurement of charging potential V ₀ )
Any of the photoconductors (A-1) to (A-26) and the photoconductor (B-1) is set to a rotation speed of 31 rpm using a drum sensitivity tester (manufactured by Juntec Corporation), and the drum inflow current is The surface potential at −10 μmA was measured. The measured surface potential was defined as the charging potential (V ₀ ). The measurement environment was a temperature of 23 ° C. and a humidity of 50% RH.

(Measurement of sensitivity potential V _L )
Any one of the photoconductors (A-1) to (A-26) and the photoconductor (B-1) is set to −600 V using a drum sensitivity tester (manufactured by Gentec Corporation) with a rotation speed of 31 rpm. It was charged so that Next, monochromatic light (wavelength: 780 nm, exposure amount: 0.8 μJ / cm ² ) was taken out from the light of the halogen lamp using a bandpass filter and irradiated on the surface of the photoreceptor. The surface potential after 80 milliseconds had elapsed after the end of monochromatic light irradiation was measured. The measured surface potential was defined as the sensitivity potential (V _L ). The measurement environment was a temperature of 23 ° C. and a relative humidity of 50% RH.

(Evaluation of abrasion resistance of photoconductor)
Polypropylene sheet in which the charge transport layer coating solution prepared in the production of any one of the photoreceptors (A-1) to (A-22) and the photoreceptor (B-1) is wound around an aluminum pipe (diameter: 78 mm). (Thickness 0.3 mm) was applied. This was dried at 120 ° C. for 40 minutes to produce a sheet for a wear evaluation test on which a charge transport layer having a thickness of 30 μm was formed. In the evaluation of abrasion resistance of the photoconductors (A-23) to (A-26), the charge transport layer coating solution prepared in the production of any of the photoconductors (A-23) to (A-26) was used. It was prepared by further adding 0.05 part by weight of a belling agent (dimethyl silicone oil “KF96-50CS” manufactured by Shin-Etsu Chemical Co., Ltd.).

  The charge transport layer was peeled off from this polypropylene sheet and attached to Wheel S-36 (manufactured by Taber) to prepare a sample. The prepared sample is set in a rotary abrasion tester (manufactured by Toyo Seiki Seisakusho Co., Ltd.), wear wheel CS-10 (manufactured by Taber), and rotated 1,000 times under conditions of a load of 500 gf and a rotational speed of 60 rpm, and a wear evaluation test. Carried out. Wear loss (mg / 1000 rotations), which is a change in mass of the sample before and after the wear evaluation test, was measured. The wear resistance of the photoreceptor was evaluated based on the obtained wear loss.

(Evaluation of liquid life of coating liquid for charge transport layer)
The charge transport layer coating solutions for the photoreceptors (A-1) to (A-26) and the photoreceptor (B-1) were allowed to stand for 30 days, and the presence or absence of gelation was visually confirmed. The liquid life property was evaluated based on the following criteria from the result of visual confirmation.
(Liquid life evaluation criteria)
○ (Good): The charge transport layer coating solution did not gel.
Δ (Normal): The charge transport layer coating solution was slightly gelled.
X (Poor): The charge transport layer coating solution gelled.

  Table 1 shows the configurations and performance evaluation results of the photoreceptors (A-1) to (A-26) and the photoreceptor (B-1). In Table 1, HTM-1 to HTM-9 in the column “Hole transporting agent” represent hole transporting agents (HTM-1) to (HTM-9), respectively. The molecular weight in the column “binder resin” represents the viscosity average molecular weight. Resin-1 to Resin-17 and Resin-B1 in the column “binder resin” represent polyarylate resins (Resin-1) to (Resin-17) and (Resin-B1), respectively.

  As shown in Table 1, in the photoreceptors (A-1) to (A-26), the charge transport layer contains any of polyarylate resins (Resin-1) to (Resin-17) as binder resins. Was. The polycarbonate resins (Resin-1) to (Resin-17) had a repeating unit represented by the general formula (1). As shown in Table 1, in the photoconductors (A-1) to (A-26), the wear loss was 3.0 mg to 4.6 mg.

  As shown in Table 1, in the photoreceptor (B-1), the charge transport layer contained a polyarylate resin (Resin-B1) as a binder resin. The polyarylate resin (Resin-B1) did not have the repeating unit represented by the general formula (1). As shown in Table 1, the wear loss of the photoreceptor (B-1) was 6.4 mg.

  As is apparent from Table 1, the photoconductors (photoconductors (A-1) to (A-26)) according to this embodiment have less wear loss in the wear resistance test than the photoconductor (B-1). It was. Therefore, it is clear that the photoreceptor according to the present invention is excellent in wear resistance.

  As shown in Table 1, in the photoconductors (A-10), (A-19), and (A-20), the photosensitive layer has polyarylate resins (Resin-2) and (Resin-11) as binder resins. , And (Resin-12). These binder resins had r / (r + t) of 0.20 or more and 0.80 or less, and s / (s + u) of 0.20 or more and 0.80 or less. Photoreceptors (A-2), (A-19), and (A-20) had a weight loss of 3.3 mg or more and 3.7 m or less, and the liquid life evaluation results were all “good”. It was.

  As shown in Table 1, in Photoreceptors (A-13), (A-18), and (A-21), the photosensitive layer is a polyarylate resin (Resin-5) or (Resin-10) as a binder resin. And (Resin-13). In these binder resins, r / (r + t) was not 0.20 or more and 0.80 or less, and s / (s + u) was not 0.20 or more and 0.80 or less. In the photoreceptors (A-13) and (A-21), the evaluation result of the liquid life property was Δ (normal). In the photoconductors (A-13) and (A-18), the weight loss on wear was 4.6 mg.

  The photoconductors (A-10), (A-19), and (A-20) are more resistant to abrasion and liquid than the photoconductors (A-13), (A-18), and (A-21). It is clear that it is excellent in life.

  As shown in Table 1, in the photoreceptors (A-1), (A-10), and (A-15) to (A-17), the photosensitive layer is a polyarylate resin (Resin-1) as a binder resin. , (Resin-2), and (Resin-7) to (Resin-10). In these polyarylate resins, Y represents a divalent group represented by the general formula (4). In the photoconductors (A-1), (A-10), and (A-15) to (A-17), the weight loss on abrasion was 3.0 mg to 3.6 mg.

  As shown in Table 1, in the photoreceptors (A-11) to (A-14), the photosensitive layer contained any of polyarylate resins (Resin-3) to (Resin-6) as a binder resin. . In these polyarylate resins, Y did not represent a divalent group represented by the general formula (4). In the photoconductors (A-11) to (A-13), the weight loss on abrasion was 4.3 mg or more and 4.6 mg or less. In the photoreceptors (A-13) and (A-14), the evaluation result of the liquid life property was Δ (normal).

  The photoconductors (A-1), (A-10), and (A-15) to (A-17) are more resistant to abrasion and liquid than the photoconductors (A-11) to (A-14). It is clear that it is excellent in performance.

  The electrophotographic photosensitive member according to the present invention can be used in an image forming apparatus such as a multifunction peripheral.

DESCRIPTION OF SYMBOLS 1 Multilayer electrophotographic photoreceptor 2 Conductive substrate 3 Photosensitive layer 3a Charge generation layer 3b Charge transport layer 4 Intermediate layer

Claims (12)

A polyarylate resin represented by the following general formula (1).

In the general formula (1),
p and l each independently represent 2 or 3,
r and s represent an integer of 0 to 49,
t and u represent an integer of 1 to 50,
r + s + t + u = 100,
r + t = s + u,
X and Y each independently represent a divalent group represented by chemical formula (1-1), chemical formula (1-2), chemical formula (1-3), or chemical formula (1-4).

In the general formula (1),
r / (r + t) is 0.20 or more and 0.80 or less,
The polyarylate resin according to claim 1, wherein s / (s + u) is 0.20 or more and 0.80 or less. In the general formula (1),
The polyarylate resin according to claim 1 or 2, wherein when s represents an integer of 1 or more, X and Y are different from each other. In the general formula (1),
When s represents an integer of 1 or more,
one of p and l represents 2,
The polyarylate resin according to any one of claims 1 to 3, wherein the other of p and l represents 3. In the general formula (1),
when s represents 0, Y represents the divalent group represented by the general formula (1-4);
When s represents an integer greater than or equal to 1, one of X and Y represents the said bivalent group represented by the said General formula (1-4), It is as described in any one of Claims 1-4. Polyarylate resin. In the general formula (1),
When s represents an integer of 1 or more,
X and Y each independently represent the divalent group selected from the group consisting of the chemical formula (1-1), the chemical formula (1-2), and the chemical formula (1-3). The polyarylate resin according to any one of 1 to 5. Chemical formula (Resin-1), chemical formula (Resin-2), chemical formula (Resin-3), chemical formula (Resin-4), chemical formula (Resin-5), chemical formula (Resin-6), chemical formula (Resin-7), chemical formula (Resin-8), chemical formula (Resin-9), chemical formula (Resin-10), chemical formula (Resin-11), chemical formula (Resin-12), chemical formula (Resin-13), chemical formula (Resin-14), chemical formula (resin-14) The polyarylate resin according to claim 1, which is represented by Resin-15), chemical formula (Resin-16), or chemical formula (Resin-17).

An electrophotographic photosensitive member comprising a conductive substrate and a photosensitive layer,
The photosensitive layer contains a charge generating agent, a hole transport agent, and a binder resin,
The electrophotographic photoreceptor, wherein the binder resin contains the polyarylate resin according to any one of claims 1 to 7. The electrophotographic photoreceptor according to claim 8, wherein the hole transport agent comprises a compound represented by the general formula (2), the general formula (3), or the general formula (4).

In the general formula (2),
Q ₁ represents a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or a phenyl group that may be substituted with an alkyl group having 1 to 8 carbon atoms. ,
Q ₂ represents an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or a phenyl group,
Q ₃ , Q ₄ , Q ₅ , Q ₆ , and Q ₇ are each independently a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or a phenyl group. And two adjacent ones of Q ₃ , Q ₄ , Q ₅ , Q ₆ , and Q ₇ may be bonded to each other to form a ring,
a represents an integer of 0 to 5, and when a represents an integer of 2 to 5, a plurality of Q ₂ bonded to the same phenyl group may be the same as or different from each other.

In the general formula (3),
Q ₈ , Q ₁₀ , Q ₁₁ , Q ₁₂ , Q ₁₃ and Q ₁₄ are each independently a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or Represents a phenyl group,
Q ₉ and Q ₁₅ each independently represents an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, or a phenyl group,
b represents an integer of 0 to 5, and when b represents an integer of 2 to 5, a plurality of Q ₉ bonded to the same phenyl group may be the same or different from each other;
c represents an integer of 0 or more and 4 or less, and when c represents an integer of 2 or more and 4 or less, a plurality of Q ₁₅ bonded to the same phenyl group may be the same or different from each other;
k represents 0 or 1.

In the general formula (4),
R _a , R _b , and R _c each independently represents an alkyl group having 1 to 8 carbon atoms, a phenyl group, or an alkoxy group having 1 to 8 carbon atoms,
q represents an integer of 0 or more and 4 or less, and when q represents an integer of 2 or more and 4 or less, a plurality of R _c bonded to the same phenyl group may be the same or different from each other;
m and n each independently represent an integer of 0 to 5, and when m represents an integer of 2 to 5, a plurality of R _b bonded to the same phenyl group may be the same or different from each other. Often,
When n represents an integer of 2 or more and 5 or less, a plurality of R _a bonded to the same phenyl group may be the same or different from each other. In the general formula (2),
Q ₁ represents a hydrogen atom or a phenyl group substituted with an alkyl group having 1 to 8 carbon atoms,
Q ₂ represents an alkyl group having 1 to 8 carbon atoms,
Q ₃ , Q ₄ , Q ₅ , Q ₆ , and Q ₇ each independently represent a hydrogen atom, an alkyl group having 1 to 8 carbon atoms, or an alkoxy group having 1 to 8 carbon atoms, ₃ , Q ₄ , Q ₅ , Q ₆ and Q ₇ may be bonded to each other to form a ring,
a represents 0 or 1,
In the general formula (3),
Q ₈ , Q ₁₀ , Q ₁₁ , Q ₁₂ , Q ₁₃ , and Q ₁₄ each independently represent a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, or a phenyl group,
b and c represent 0;
In the general formula (4),
R _a and R _b each independently represents an alkyl group having 1 to 8 carbon atoms,
m and n each independently represent an integer of 0 or more and 2 or less,
The electrophotographic photosensitive member according to claim 9, wherein q represents 0. The hole transport agent has chemical formula (HTM-1), chemical formula (HTM-2), chemical formula (HTM-3), chemical formula (HTM-4), chemical formula (HTM-5), chemical formula (HTM-6), chemical formula The electrophotographic photoreceptor according to claim 9 or 10, which is represented by (HTM-7), chemical formula (HTM-8), or chemical formula (HTM-9).

The photosensitive layer includes a charge generation layer containing the charge generation agent, a charge transport layer containing the hole transport agent, and the binder resin.
The electrophotographic photoreceptor according to any one of claims 8 to 11, wherein the charge transport layer is a single layer, and the charge transport layer is disposed as an outermost surface layer.

Images