JP2017526758A - Pvcを着色するための、コーティングされた顔料と脂肪酸塩との混合物 - Google Patents
Pvcを着色するための、コーティングされた顔料と脂肪酸塩との混合物 Download PDFInfo
- Publication number
- JP2017526758A JP2017526758A JP2016573947A JP2016573947A JP2017526758A JP 2017526758 A JP2017526758 A JP 2017526758A JP 2016573947 A JP2016573947 A JP 2016573947A JP 2016573947 A JP2016573947 A JP 2016573947A JP 2017526758 A JP2017526758 A JP 2017526758A
- Authority
- JP
- Japan
- Prior art keywords
- magnesium
- mixture
- calcium
- pigment
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
・ 酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物を含む、少なくとも1種の顔料であって、その少なくとも1種の無機化合物は、少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物を含むコーティングを備えたものである、少なくとも1種の顔料、および
・ 少なくとも1種の、一般式CnH2n+1COOH(I)、CnH2n−1COOH(II)、CnH2n−3COOH(III)および/またはCnH2n−5COOH(IV)(ここでn=10〜20、好ましくは15〜19)の脂肪酸のカルシウム塩またはマグネシウム塩、
を含む混合物が、この目的を達成し、上述のような従来技術の顔料の欠点を克服できることが今や見出された。
・ 酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物を含む、少なくとも1種の顔料であって、その少なくとも1種の無機化合物は、少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物を含むコーティングを備えたものである、少なくとも1種の顔料、
・ ステアリン酸カルシウムおよび/またはステアリン酸マグネシウム。
a)酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物の水性懸濁液を準備する工程、
および
b)工程a)からの懸濁液に対して、マグネシウム塩および/またはカルシウム塩を好ましくは溶解させた形態で添加し、次いで、その懸濁液に対して、アルカリ金属水酸化物、アルカリ土類金属水酸化物およびアンモニアの群から選択される沈降剤を、好ましくは溶解させた形態で添加することによって、その無機化合物の上に、少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物のコーティングを沈降させる工程、または
b’)工程a)からの懸濁液に対して、アルカリ金属水酸化物、アルカリ土類金属水酸化物、およびアンモニアの群から選択される沈降剤を、好ましくは溶解させた形態で添加し、次いで、その懸濁液に対して、マグネシウム塩および/またはカルシウム塩を、好ましくは溶解させた形態で添加することによって、その無機化合物の上に少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物のコーティングを沈降させる工程。
c)顔料を単離する工程、
c’)顔料を洗浄する工程、
c’’)顔料を乾燥させる工程、および
c’’’)顔料を微粉砕する工程。
a)酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物の水性懸濁液を準備する工程、
および
b)工程a)からの懸濁液に対して、マグネシウム塩および/またはカルシウム塩を好ましくは溶解させた形態で添加し、次いで、その懸濁液に対して、アルカリ金属水酸化物、アルカリ土類金属水酸化物およびアンモニアの群から選択される沈降剤を、好ましくは溶解させた形態で添加することによって、無機化合物の上に、少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物のコーティングを沈降させる工程、または
b’)工程a)からの懸濁液に対して、アルカリ金属水酸化物、アルカリ土類金属水酸化物、またはアンモニアの群からの沈降剤を、好ましくは溶解させた形態で添加し、次いで、その懸濁液に対して、マグネシウム塩および/またはカルシウム塩を、好ましくは溶解させた形態で添加することによって、その顔料の上に少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物のコーティングを沈降させる工程、
または
b’’)工程a)からの水性懸濁液に、好ましくは溶解させた形態の、アルカリ金属水酸化物、アルカリ土類金属水酸化物およびアンモニアの群から選択される沈降剤と、好ましくは溶解させた形態の、マグネシウム塩および/またはカルシウム塩とを同時に添加することによって、その無機化合物の上に少なくとも1種の、マグネシウムまたはカルシウムの水酸化物または酸化物のコーティングを沈降させる工程、
および
c)液相から顔料を分離する工程、および
c’)顔料を洗浄する工程、および
c’’)顔料を乾燥させる工程、および
c’’’)顔料を微粉砕する工程、
および
d)工程c’’’)から得られた顔料を、少なくとも1種の、一般式(I)、(II)、(III)、および/または(IV)の脂肪酸のカルシウム塩またはマグネシウム塩、好ましくはステアリン酸マグネシウムおよび/またはステアリン酸カルシウムと混合する工程。
I.使用した測定方法および試験方法の説明
実施例についての測定結果を表1にまとめた。
顔料のマグネシウム含量およびカルシウム含量は、誘導結合プラズマで励起させた後の発光分析法(ICP−OES:誘導結合プラズマ−発光分析法)によって、元素の含量として測定した。
オイル価は、DIN ISO 787/5標準に従い、gオイル/100g試料の単位で求めた。「試料」は、顔料または混合物のいずれかを意味している。
50重量%のVestolit B 7021 Ultraプラス50重量%のSorVyl DB 6668 Natur 3/03からなる粉体状のPVC混合物を、試験対象の混合物と均質に混合する(100%PVC組成物を基準にして4重量%)。
II.1 使用した無機顔料およびプラスチックの性質
Bayferrox(登録商標)110顔料粉体:LANXESS Deutschland GmbH製:ヘマタイト(赤色酸化鉄、α−Fe2O3)、BET表面積(DIN ISO 9277):13〜16m2/g。
Bayferrox(登録商標)920:ゲータイト、α−FeOOHのペースト:LANXESS Deutschland GmbH製、これを乾燥、摩砕することにより、Bayferrox(登録商標)920粉体が製造される。その粉体状の顔料は、11〜15m2/gのBET表面積(DIN ISO 9277)を有している。別な方法として、粉体状のBayferrox(登録商標)920顔料を水と混合して、適切な顔料濃度を有するスラリーを得ることもまた可能である(実施例参照)。
ステアリン酸カルシウム:VWR BDH PROLABO(登録商標)からの粉体、Ca含量:9重量%〜11重量%(CaOとして計算)。
SorVyl DB 6668 Natur 3/03:硬質PVCコンパウンド物:Polymerchemie製(粉体の形態、Ca/Znを用いて安定化されており、ここで、ビス(ペンタン−2,4−ジオナト)カルシウムの含量が1重量%未満、軟化点が120℃より高く、引火点が190℃よりも高く、発火温度が300℃よりも高く、密度(DIN EN ISO 1183−1、方法A)が1.39g/cm3、嵩密度(DIN EN ISO 60)が0.54g/mL、熱安定性(DIN EN 60811−3−2)が25分以上)。
VESTOLIT(登録商標)B 7021 Ultra:Vestolit製のMikro−S−PVCホモポリマー(粉体の形態、K値(DIN EN ISO 1628−2)が70、粘度数(DIN EN ISO 1628−2)が125cm3/g、嵩密度(DIN EN ISO 60)が0.3g/cm3、篩分け試験(DIN EN ISO 1624、0.063mm篩上)が1%未満、水分含量(K.Fischer法、DIN 53 715)が0.3%以下、水抽出物のpHDIN EN ISO 1264)が8、1.5/sのペースト粘度が1.8Pa・s、45/sのペースト粘度が2.2Pa・s)。
例1(比較例):
145.5gのBayferrox(登録商標)110顔料および4.5gのステアリン酸カルシウムを、Henschel FM4ミキサー(Thyssen Henschel製)に加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
141gのBayferrox(登録商標)110顔料および9gのステアリン酸カルシウムを、Henschel FM4ミキサーに加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
Bayferrox(登録商標)110の水性懸濁液(6.26molのFe2O3、pH:4.8)の3.3dm3に、60℃で撹拌しながら、1443mLのMgSO4溶液(MgOの2.58mol/dm3に相当)を添加した。次いで、Fe2O3の1moleあたり3.98molのNaOHを、溶液として、撹拌しながら30分以内で添加した(16.6mol/dm3に濃縮して、2215g)。その懸濁液をさらに60分間撹拌した。その懸濁液のpHは11よりも高かった。反応が終了した後、その顔料は、サクションフィルターを通して濾過し、その濾液の導電率が300μS/cm未満になるまで洗浄し、乾燥キャビネット中120℃で恒量になるまで乾燥させ、Bauermeisterミル(シーブインサート付きクロス−ビーターミル、メッシュサイズ1mm)の中で摩砕した。
145.5gの顔料出発物質1および4.5gのステアリン酸カルシウムを、Henschel FM4ミキサーに加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
141gの顔料(出発物質1)および9gのステアリン酸カルシウムを、Henschel FM4ミキサーに加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
145.5gのBayferrox(登録商標)920顔料粉体および4.5gのステアリン酸カルシウムを、Henschel FM4ミキサーに加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
2.05dm3の、4のpHを有するバイフェロックス(Bayferrox)(登録商標)920の水性懸濁液(FeOOH、5.63mol)に、60℃で撹拌しながら、3571mLのMgSO4溶液(MgOとして、1.39mol/dm3)を添加した。次いで、FeOOHの1moleあたり1.41molのNaOHを、溶液として撹拌しながら、15分以内に添加する(濃度7.87mol/dm3で1283g)。その懸濁液をさらに60分間撹拌した。その懸濁液のpHは、約10であった。反応が終了した後、その顔料は、サクションフィルターを通して濾過し、その濾液の導電率が300μS/cm未満になるまで洗浄し、乾燥キャビネット中120℃で恒量になるまで乾燥させ、Bauermeisterミル(シーブインサート付きクロス−ビーターミル、メッシュサイズ1mm)の中で摩砕した。
145.5gの顔料(出発物質2)および4.5gのステアリン酸カルシウムを、Henschel FM4ミキサーに加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
141gの顔料(出発物質2)および9gのステアリン酸カルシウムを、Henschel FM4ミキサーに加えた。その二つの物質を、室温(20〜25℃)、1000rpmで20分かけて混ぜ合わせた。その粉体状の生成物を、さらに処理することなく、試験に使用する。
Claims (16)
- ・ 酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物を含み、前記少なくとも1種の無機化合物は、マグネシウムまたはカルシウムの水酸化物または酸化物の少なくとも1種を含むコーティングを備えたものである、少なくとも1種の顔料、および
・ 少なくとも1種の、一般式CnH2n+1COOH(I)、CnH2n−1COOH(II)、CnH2n−3COOH(III)および/またはCnH2n−5COOH(IV)(ここでn=10〜20、好ましくは15〜19である)の脂肪酸のカルシウム塩またはマグネシウム塩、
を含む混合物。 - 前記混合物の中に存在する前記顔料が、酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物からなり、前記少なくとも1種の無機化合物が、マグネシウムまたはカルシウムの水酸化物または酸化物の少なくとも1種を含むコーティング、好ましくは、マグネシウムまたはカルシウムの水酸化物の少なくとも1種を含むコーティングを備えている、請求項1に記載の混合物。
- 前記混合物の中に存在する前記顔料の中の前記コーティングが、前記少なくとも1種の無機化合物に直接結合されている、請求項1または2に記載の混合物。
- 前記混合物が、マグネシウムおよびカルシウム元素の含量の合計として計算して、0.3重量%〜30重量%、好ましくは0.5重量%〜25重量%、より好ましくは1重量%〜20重量%のマグネシウムおよびカルシウムを含み、ここで前記マグネシウムおよびカルシウム元素の含量の総合計は前記混合物の全重量を規準としたものである、請求項1〜3のいずれか一項に記載の混合物。
- 前記混合物が、0.2重量%〜15重量%の、少なくとも1種の、一般式CnH2n+1COOH(I)、CnH2n−1COOH(II)、CnH2n−3COOH(III)および/またはCnH2n−5COOH(IV)の脂肪酸のカルシウム塩またはマグネシウム塩、好ましくはステアリン酸カルシウムおよび/またはステアリン酸マグネシウムを含む、請求項1〜4のいずれか一項に記載の混合物。
- プラスチック製品であって、
・ 請求項1〜5のいずれか一項に記載の少なくとも1種の混合物、および
・ ポリマーの少なくとも50重量%、好ましくは少なくとも80重量%が、塩化ビニルのモノマーから形成されている、少なくとも1種のポリマー
を含み、上述の成分が、前記プラスチック製品の全重量を規準にして、合計して好ましくは40重量%〜100重量%、より好ましくは70重量%〜100重量%となる、プラスチック製品。 - 10重量%〜90重量%、好ましくは20重量%〜70重量%、または0.1重量%〜10重量%、好ましくは0.5重量%〜5重量%の、請求項1〜5のいずれか一項に記載の混合物を含む、請求項6に記載のプラスチック製品。
- 前記プラスチック製品の中に存在しているポリマーの量を基準にして、0重量%〜15重量%、好ましくは0重量%〜12重量%の可塑剤を含む、請求項6または7に記載のプラスチック製品。
- 粉体状のポリマーと、請求項1〜5のいずれか一項に記載の混合物との混合物を含む、請求項6〜8のいずれか一項に記載のプラスチック製品。
- 請求項1〜5のいずれか一項に記載の混合物を製造するための方法であって、前記混合物を得るために、少なくとも以下の工程:
a)酸化鉄、オキシ水酸化鉄、亜鉄酸亜鉛、酸化亜鉛、亜鉄酸マグネシウム、および亜鉄酸マンガンの群から選択される少なくとも1種の無機化合物の水性懸濁液を準備する工程、
および
b)工程a)からの前記懸濁液に対して、マグネシウム塩および/またはカルシウム塩を好ましくは溶解させた形態で追加し、次いで、該懸濁液に対して、アルカリ金属水酸化物、アルカリ土類金属水酸化物およびアンモニアの群から選択される沈降剤を、好ましくは溶解させた形態で追加することによって、前記無機化合物の上に、マグネシウムまたはカルシウムの水酸化物または酸化物の少なくとも1種のコーティングを沈降させる工程、または
b’)工程a)からの前記懸濁液に対して、アルカリ金属水酸化物、アルカリ土類金属水酸化物、およびアンモニアの群から選択される沈降剤を、好ましくは溶解させた形態で追加し、次いで、該懸濁液に対して、マグネシウム塩および/またはカルシウム塩を、好ましくは溶解させた形態で追加することによって、前記無機化合物の上に、マグネシウムまたはカルシウムの水酸化物または酸化物の少なくとも1種のコーティングを沈降させる工程、
および
c)前記顔料を単離する工程、および/または
c’)前記顔料を洗浄する工程、および/または
c’’)前記顔料を乾燥させる工程、および/または
c’’’)顔料を微粉砕する工程、
および
d)工程c’’’)から得られた前記顔料を、少なくとも1種の、一般式(I)、(II)、(III)、および/または(IV)の脂肪酸のカルシウム塩またはマグネシウム塩、好ましくはステアリン酸マグネシウムおよび/またはステアリン酸カルシウムと混合する工程、
を含む、方法。 - 焼成工程、好ましくは600℃より高温での焼成工程を実施しない、請求項10に記載の混合物を製造するための方法。
- 請求項1〜5のいずれか一項に記載の混合物と共に、ポリマーを混練加工または押出し加工することによる、請求項6〜9のいずれか一項に記載のプラスチック製品を製造するための方法。
- 請求項1〜5のいずれか一項に記載の少なくとも1種の混合物と粉体状のPVCとを混合することによる、好ましくは前記構成成分を前記プラスチックの融点よりも0.5〜20K低い温度で混合することによる、請求項9に記載のプラスチック製品を製造するための方法。
- PVC、好ましくは硬質PVCを着色するための、請求項1〜5のいずれか一項に記載の混合物の使用。
- 請求項6〜9のいずれか一項に記載の少なくとも1種のプラスチック製品を含む製品。
- 前記製品が、窓用形材、パイプ、床材、絶縁材料、または屋根用シートを含む、請求項15に記載の製品。