JP2017013822A - Manufacturing method for display suspension package - Google Patents
Manufacturing method for display suspension package Download PDFInfo
- Publication number
- JP2017013822A JP2017013822A JP2015131171A JP2015131171A JP2017013822A JP 2017013822 A JP2017013822 A JP 2017013822A JP 2015131171 A JP2015131171 A JP 2015131171A JP 2015131171 A JP2015131171 A JP 2015131171A JP 2017013822 A JP2017013822 A JP 2017013822A
- Authority
- JP
- Japan
- Prior art keywords
- mount
- article
- hot melt
- melt adhesive
- peeling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、陳列吊り下げ用包装体の製造方法に関する。 The present invention relates to a method for manufacturing a display suspension packaging.
従来より、物品の情報等を記載した台紙にプラスチックフィルム又はプラスチックシートで外装された物品を固定した陳列吊り下げ用包装体が使用されている。このような陳列吊り下げ用包装体は意匠性に優れ、台紙の表面又は裏面に物品の情報等を記載することができる。 2. Description of the Related Art Conventionally, a display hanging packaging body in which an article covered with a plastic film or a plastic sheet is fixed on a mount on which information on the article is described has been used. Such a display-hanging package is excellent in design, and information on articles can be described on the front or back surface of the mount.
陳列吊り下げ用包装体の製造方法として、例えば、プラスチックフィルム又はプラスチックシートで外装された物品が接着剤層を介して台紙表面に固定されている陳列吊り下げ用包装体であって、接着剤層として熱により溶融と固化とを可逆的に繰り返し得るホットメルト接着剤に気泡を含有する発泡ホットメルト接着剤層を用いる陳列吊り下げ用包装体の製造方法が開示されている(特許文献1)。 As a method for manufacturing a display suspension package, for example, an article packaged with a plastic film or a plastic sheet is fixed to the surface of the mount through an adhesive layer, and the adhesive layer is an adhesive layer. As a hot melt adhesive that can reversibly repeat melting and solidification by heat, a method for producing a display suspending package using a foamed hot melt adhesive layer containing bubbles is disclosed (Patent Document 1).
また、プラスチックフィルム又はプラスチックシートを熱収縮する工程と、ホットメルト接着剤を用いて接着剤層を形成する工程とを含む陳列吊り下げ用包装体の製造方法が開示されている(特許文献2)。 In addition, a method for manufacturing a display-suspended package including a step of thermally shrinking a plastic film or a plastic sheet and a step of forming an adhesive layer using a hot melt adhesive is disclosed (Patent Document 2). .
陳列吊り下げ用包装体において、台紙には物品の情報等が記載されており、需要者がプラスチックフィルム又はプラスチックシートで外装された物品を台紙から剥離した場合であっても、台紙に記載された物品の情報等が物品の剥離によって紛失しない陳列吊り下げ用包装体が求められる。台紙に記載された物品の情報等が剥離によって紛失せずに需要者が容易に物品を台紙から剥離可能とするためには、例えば物品と台紙との接着強度を弱めることによって実現することができる。しかし、物品と台紙との接着強度を弱めた場合、陳列吊り下げ用包装体の耐久強度が問題となる。特に質量の大きい物品を含む陳列吊り下げ用包装体の場合には、物品の質量によって台紙と物品とが剥離するという問題が生じる。 In the display suspension packaging, information on the article is described on the mount, and even if the customer peels off the article covered with a plastic film or plastic sheet, it is described on the mount. There is a need for a display-hanging package that does not lose article information due to peeling of the article. In order to make it possible for a consumer to easily peel off an article from the mount without losing information on the article on the mount due to peeling, for example, it can be realized by weakening the adhesive strength between the article and the mount. . However, when the adhesive strength between the article and the mount is weakened, the durability of the display hanging packaging becomes a problem. In particular, in the case of a display suspension packaging including an article having a large mass, there arises a problem that the mount and the article are peeled off due to the mass of the article.
また、接着剤層以外の層を剥離可能な構成とし、物品と台紙との接着強度を十分な強度にすることによっても台紙に記載された物品の情報等が物品の剥離によって紛失しない陳列吊り下げ用包装体を製造することができる。しかしながら、物品に外装されるプラスチックフィルム又はプラスチックシート(以下、物品に外装されたプラスチックフィルムを外装フィルム、物品に外装されたプラスチックシートを外装シートと呼ぶことがある。)は、ポリエチレン樹脂等の平滑で極性も小さいフィルム又はシートであるため、物理的アンカー効果も不十分で、かつ、化学的な接合力も期待できない。そのため、外装フィルム又は外装シートと接着剤層との密着強度が不十分となり、外装フィルム又は外装シートと接着剤層との界面での剥離が生じるとの問題が生じる。 In addition, it is possible to peel off the layers other than the adhesive layer, and the display hanging so that the information on the article on the mount is not lost due to the peeling of the article by making the adhesive strength between the article and the mount sufficient. A package can be produced. However, a plastic film or plastic sheet that is packaged on an article (hereinafter, a plastic film that is packaged on an article may be referred to as an exterior film, and a plastic sheet that is packaged on an article may be referred to as an exterior sheet) is a smooth film such as polyethylene resin. In addition, since the film or sheet has a small polarity, the physical anchor effect is insufficient and the chemical bonding force cannot be expected. Therefore, the adhesion strength between the exterior film or exterior sheet and the adhesive layer becomes insufficient, and there arises a problem that peeling at the interface between the exterior film or exterior sheet and the adhesive layer occurs.
本発明は、ホットメルト接着剤を介して台紙の表面に固定されている陳列吊り下げ用包装体の製造方法であって、台紙に記載された物品の情報等が陳列吊り下げ用包装体から物品を剥離することによって紛失せず、且つ、外装フィルム又は外装シートと接着剤層との界面での剥離が生じることのない陳列吊り下げ用包装体の製造方法を提供することを目的とする。 The present invention relates to a method for manufacturing a display suspension package that is fixed to the surface of a mount through a hot melt adhesive, and information on the article and the like described on the mount is transferred from the display suspension package to the article. It is an object of the present invention to provide a method for producing a display-suspended package that is not lost by peeling and that does not peel off at the interface between the outer film or the outer sheet and the adhesive layer.
本発明者らは、上記課題を解決すべく鋭意検討を行った結果、陳列吊り下げ用包装体に用いられる台紙の構造を特定の構造とし、且つホットメルト接着剤を、外装フィルム又は外装シート上に形成した後に台紙表面の剥離部と接合することで上記課題を解決できることを見出し、本発明を完成するに至った。 As a result of intensive studies to solve the above-mentioned problems, the present inventors have made the structure of the mount used for the display suspension packaging body a specific structure, and applied the hot melt adhesive on the exterior film or exterior sheet. It was found that the above-mentioned problems can be solved by bonding with a peeling portion on the surface of the mount after forming the sheet, and the present invention has been completed.
(1)プラスチックフィルム又はプラスチックシートで外装された物品が、ホットメルト接着剤を介して台紙の表面に固定されている陳列吊り下げ用包装体の製造方法であって、前記台紙の表面には、前記台紙の厚さ方向未満の深さのハーフカット溝で形成される周状の剥離部が形成されており、前記ホットメルト接着剤を、前記物品の外装フィルム又は外装シート上に形成した後に、前記台紙表面の剥離部と接合することを特徴とする陳列吊り下げ用包装体の製造方法。 (1) An article covered with a plastic film or a plastic sheet is a method for producing a display-hanging packaging body that is fixed to a surface of a mount through a hot-melt adhesive, and the surface of the mount includes A circumferential peeling portion formed by a half cut groove with a depth less than the thickness direction of the mount is formed, and after forming the hot melt adhesive on the exterior film or exterior sheet of the article, A method for manufacturing a display-hanging package, characterized by joining to a peeling portion on the surface of the mount.
(2)前記ホットメルト接着剤が発泡ホットメルト接着剤である、(1)に記載の陳列吊り下げ用包装体の製造方法。 (2) The method for producing a display-hanging package according to (1), wherein the hot-melt adhesive is a foamed hot-melt adhesive.
(3)前記外装された物品を前記台紙から剥離した際に、前記外装された物品は、前記ホットメルト接着剤及び前記剥離部の表面層と共に剥離し、剥離後の前記台紙には、前記剥離部の裏面層が残部として存在するように、前記外装された物品と前記剥離部との接合強度を、前記剥離部における前記表面層及び裏面層の層間剥離強度より高くする、(1)又は(2)に記載の陳列吊り下げ用包装体の製造方法。 (3) When the packaged article is peeled off from the mount, the packaged article is peeled off together with the hot melt adhesive and the surface layer of the peeling part, and the peeled board has the peeling off (1) or (1) or (1) or (1) or (1) or (2), wherein the bonding strength between the packaged article and the peeling portion is higher than the delamination strength between the surface layer and the back surface layer in the peeling portion. The manufacturing method of the packaging body for display hanging as described in 2).
本発明によれば、台紙に記載された物品の情報等が物品の剥離によって紛失せず、且つ、外装フィルム又は外装シートと接着剤層との界面での剥離が生じることのない陳列吊り下げ用包装体の製造方法を提供することができる。 According to the present invention, the information on the article described on the mount is not lost due to the peeling of the article, and the display hanging is not caused at the interface between the exterior film or the exterior sheet and the adhesive layer. A method for producing a package can be provided.
以下、本発明の実施形態について詳細に説明する。本発明は以下の実施形態に何ら限定されるものではなく、本発明の目的の範囲内において、適宜変更を加えて実施することができる。 Hereinafter, embodiments of the present invention will be described in detail. The present invention is not limited to the following embodiments, and can be implemented with appropriate modifications within the scope of the object of the present invention.
<陳列吊り下げ用包装体>
本実施形態に関する陳列吊り下げ用包装体(以下、単に包装体と表記することがある)の全体構造について図1及び図3を用いて説明する。包装体1は、図1に示すように、プラスチックフィルム又はプラスチックシートで外装された物品12と台紙11からなる。また、包装体1は、図3に示すように、プラスチックフィルム又はプラスチックシートで外装された物品12が接着剤層13を介して台紙11の表面に固定されている。
<Package for hanging display>
The overall structure of a display hanging packaging body (hereinafter, simply referred to as a packaging body) according to this embodiment will be described with reference to FIGS. As shown in FIG. 1, the package 1 includes an
また、本実施形態に関する包装体1の台紙11の表面には、図3に示すように台紙11の厚さ方向未満の深さのハーフカット溝111が設けられている。物品12を台紙11から剥離した際には、ハーフカット溝111を起点として剥離部112の表面層が剥離される。物品12を台紙11から剥離した際におけるハーフカット溝111の役割については後述する。
Further, as shown in FIG. 3, a half-
以下、本実施形態の包装体1を構成する台紙11と、プラスチックフィルム又はプラスチックシートで外装された物品12と、物品12と台紙11とを固定する接着剤層13について各々説明する。
Hereinafter, the
[台紙]
本実施形態に関する台紙11について図2及び図3を用いて説明する。なお、本発明に関する台紙は、図2に記載した台紙11に限定されるものではなく、図2に記載した台紙11は本発明に関する台紙を具体的に説明するための一例である。台紙11には、図2に示すように、台紙11の厚さ方向未満の深さのハーフカット溝111が台紙11の一側辺上の2点を起点111a及び終点111bとして連続的に形成されている。また、ハーフカット溝111及び台紙11の一側辺で囲まれる剥離部112の表面には、図3に示すように、接着剤層13が形成される。なお、本発明に関する台紙11は、図2の台紙11に限定されるものではなく、台紙11の表面に、台紙11の厚さ方向未満の深さのハーフカット溝111で形成される周状の剥離部112が形成されており、剥離部112が物品12の剥離とともに、ハーフカット溝111を起点として剥離可能であればよい。例えば、台紙の表面上のハーフカット溝111が一側辺上の2点を起点111a及び終点111bとして連続的に形成されてなくとも、台紙の表面にハーフカット溝111が楕円状、長円状、卵形状等、或いはその一部の形状のみがU字状等の形状であってもよい。
[Mount]
The
本実施形態に関するハーフカット溝111の役割について図3〜図5を用いて説明する。図3は物品12を台紙11から剥離する前の包装体1の断面図である。物品12を台紙11から剥離した場合、ハーフカット溝111を起点として、台紙11表面の水平方向に台紙11が切断される。そして、図5のように物品12は、接着剤層13及び剥離部112の表面層と共に剥離する。一方、図4は物品12を台紙11から剥離した後の包装体1の断面図である。図4で示すように、物品12の剥離後の包装体1は、ハーフカット溝111を起点として、台紙11表面の水平方向に台紙11が切断されているため、物品12と接着剤層13と剥離部112の表面層とが剥離した状態になる。
The role of the
本実施形態に関する包装体1は、ハーフカット溝111を起点として、物品12と台紙11とが剥離可能な包装体であるため、接着剤層13の接着強度を弱めなくとも、物品12と台紙11とを容易に剥離することができる。また、ハーフカット溝111を起点として、台紙11表面の水平方向に台紙11が切断され、台紙11には、剥離部112の裏面層が残部として存在し、剥離部112の表面層のみを綺麗に剥離することができる。そのため、剥離部112以外の表面層や、裏面の全面に物品の情報等が記載されている場合でも、物品12の剥離により剥離部112以外の表面層や、裏面の全面に記載された物品12の情報等が紛失することがない。
Since the packaging body 1 according to the present embodiment is a packaging body in which the
ハーフカット溝111の深さは、台紙11の厚さの33%以上75%以下であることが好ましい。ハーフカット溝111の深さをこのような範囲とすることで、剥離部112の裏面層が残部として存在し、剥離部112の表面層のみを綺麗に剥離することができる。
The depth of the
また、本実施形態に関する台紙11表面のハーフカット溝111の形状は、図2で示すような吊り下げ方向の鉛直下方の底辺を前記一側辺とする、縦長の逆U字状であることが好ましい。図5のように、物品12を吊り下げ方向の鉛直上方から剥離する際に縦長の逆U字状を起点に剥離することが可能となるため、剥離部112のみを綺麗に剥離することができる。
Further, the shape of the half-
台紙11に用いられる材質は陳列吊り下げ用包装体に一般に用いられる紙を用いることができる。また、紙は、一般的にパルプから取り出された繊維が紙の製造中で機械の流れ方向(紙目)に紙繊維が揃うが、台紙11の紙目が、台紙11の鉛直方向に沿っていることが好ましい。台紙11に用いられる紙の紙目を台紙11の鉛直方向とすることで、台紙11の鉛直方向に剥離部112の表面層を剥離することが容易となる。
As a material used for the
また、台紙11は、紙からなる単層の台紙でもよいが、必要に応じて、PETにアルミを蒸着させたものに紙と貼り合わせた台紙や、アルミ箔と紙を貼り合わせた台紙でもよい。台紙11をPETやアルミ等により形成された層を設けることで、台紙11の耐久性をより好ましいものとすることができる。
In addition, the
また、図2に示す台紙11のように、ハーフカット溝111に略直交する、別のハーフカット溝113がさらに形成されていることが好ましい。別のハーフカット溝113を設けることで、剥離部112以外の表面層が剥離されるリスクをより軽減することができる。
Moreover, it is preferable that another half-
[物品]
本実施形態に関する物品12は、プラスチックフィルム又はプラスチックシートで外装される。なお、本明細書において、プラスチックフィルムとは、フィルム状の樹脂フィルムを意味し、プラスチックシートとは、フィルム状の樹脂フィルムよりも厚く樹脂フィルムよりも堅牢性の高い樹脂シートを意味する。
[Goods]
The
本実施形態に関する外装フィルム又は外装シートは、接着剤層13を介して台紙11の剥離部112の表面に固定される。本実施形態に関する外装フィルムは、シュリンク包装により包装されることが好ましい。シュリンク包装とは、あらかじめ樹脂フィルム等に包まれた物品を加熱して、物品の形状に密着させる包装である。
The exterior film or the exterior sheet according to this embodiment is fixed to the surface of the peeling
物品12の質量は、20g以上500g以下であることが好ましい。本実施形態に関する包装体1は、台紙の表面にハーフカット溝で形成される周状の剥離部112を設けているため、物品12の質量を20g以上としても十分使用することができる。なお、物品12の質量が500gを超えると、物品12の質量によって物品の質量により台紙と物品とが剥離するおそれがある。そのため、物品12の質量が500g以下であることが好ましい。
The mass of the
[接着剤層]
本実施形態に関する接着剤層13は、ホットメルト接着剤を用いることにより形成される。ホットメルト接着剤とは、接着剤を溶融することにより接着させる接着剤である。本実施形態に関するホットメルト接着剤は、例えば、熱可塑性樹脂と粘着付与樹脂とを含有するホットメルト接着剤を挙げることができる。また、本実施形態に関するホットメルト接着剤は、粘度を適切に調整する観点から、ワックスを含有することが好ましい。さらに、本実施形態に関するホットメルト接着剤は、必要に応じて、充填剤、軟化剤、可塑剤、着色剤、ブロッキング防止剤、酸化防止剤、紫外線吸収剤、シランカップリング剤、チキソ付与剤、発泡剤等を含有してもよい。ホットメルト接着剤は、溶剤を含有しないことが好ましい。ホットメルト接着剤の材料は、本発明に趣旨を逸脱しない限りにおいて特に制限されない。
[Adhesive layer]
The
本実施形態に関するホットメルト接着剤に含有される熱可塑性樹脂としては、スチレン系ポリマー、エチレン酢酸ビニル(EVA)、エチレン−不飽和エステル共重合体、ポリアミド、ポリエステル、ポリオレフィン等が挙げられる。これらは、ブロック共重合体であってもよい。スチレン系ポリマーとしては、スチレン−エチレン・ブチレン−スチレンブロックポリマー(SEBS)、スチレン−エチレン・プロピレン−スチレンブロックポリマー(SEPS),スチレン−イソプレン−スチレンブロックポリマー(SIS),スチレン−ブチレン・ブタジエン−スチレンブロックポリマー(SBBS)等が例示できる。熱可塑性樹脂は、単独もしくは2種類以上を組み合わせて使用してもよい。 Examples of the thermoplastic resin contained in the hot melt adhesive according to this embodiment include styrene polymers, ethylene vinyl acetate (EVA), ethylene-unsaturated ester copolymers, polyamides, polyesters, polyolefins, and the like. These may be block copolymers. Styrene polymers include styrene-ethylene-butylene-styrene block polymer (SEBS), styrene-ethylene-propylene-styrene block polymer (SEPS), styrene-isoprene-styrene block polymer (SIS), styrene-butylene-butadiene-styrene. A block polymer (SBBS) etc. can be illustrated. You may use a thermoplastic resin individually or in combination of 2 or more types.
本実施形態に関するホットメルト接着剤に含有される粘着付与樹脂としては、フェノール樹脂、変性フェノール樹脂、テルペンフェノール樹脂、キシレンフェノール樹脂、シクロペンタジエン−フェノール樹脂、キシレン樹脂が挙げられる。また、脂肪族系、脂環族系、芳香族系等の石油樹脂や、水素添加された脂肪族系、脂環族系、芳香族系等の石油樹脂や、フェノール−変性石油樹脂も好適である。また、ロジンエステル樹脂、水素添加されたロジンエステル樹脂等のロジン系樹脂も好適である。さらに、低分子量ポリスチレン系樹脂、テルペン樹脂、水素添加されたテルペン樹脂等も例示できる。粘着付与樹脂は、単独もしくは2種類以上を組み合わせて使用できる。 Examples of the tackifier resin contained in the hot melt adhesive according to this embodiment include phenol resins, modified phenol resins, terpene phenol resins, xylene phenol resins, cyclopentadiene-phenol resins, and xylene resins. Also suitable are aliphatic, alicyclic and aromatic petroleum resins, hydrogenated aliphatic, alicyclic and aromatic petroleum resins, and phenol-modified petroleum resins. is there. Also suitable are rosin resins such as rosin ester resins and hydrogenated rosin ester resins. Further examples include low molecular weight polystyrene resins, terpene resins, hydrogenated terpene resins, and the like. Tackifying resins can be used alone or in combination of two or more.
本実施形態に関するホットメルト接着剤は、ホットメルト接着剤100質量部中に、耐熱性を高める観点から熱可塑性樹脂が30質量部以上80質量部以下の範囲にあることが好ましく、接着力を向上させる観点から粘着付与樹脂が40質量部以上80質量部以下の範囲で含まれていることが好ましい。 In the hot melt adhesive according to this embodiment, the thermoplastic resin is preferably in the range of 30 parts by mass or more and 80 parts by mass or less from the viewpoint of improving heat resistance in 100 parts by mass of the hot melt adhesive, and the adhesive strength is improved. It is preferable that tackifying resin is contained in 40 to 80 mass parts from a viewpoint made to make it.
本実施形態に関するホットメルト接着剤の軟化点は、使用環境温度により変動し得るが、屋外での使用も考慮すると、80℃以上160℃以下であることが好ましい。軟化点が80℃以上になることで、接着力と凝集力のバランスが取りやすくなる。一方、軟化点を160℃以下とすることで低温雰囲気下でもタックを維持しやすくなる。なお、明細書中において軟化点とは、JIS K 6863に規定される方法により求められる温度である。本実施形態に関するホットメルト接着剤の軟化点のより好ましい範囲は90℃以上140℃以下であり、さらに好ましい範囲は100℃以上130℃以下である。 The softening point of the hot melt adhesive according to the present embodiment may vary depending on the use environment temperature, but it is preferably 80 ° C. or higher and 160 ° C. or lower in consideration of outdoor use. When the softening point is 80 ° C. or higher, it becomes easy to balance the adhesive force and the cohesive force. On the other hand, by setting the softening point to 160 ° C. or lower, it becomes easy to maintain tack even in a low temperature atmosphere. In the specification, the softening point is a temperature determined by a method defined in JIS K 6863. A more preferable range of the softening point of the hot melt adhesive according to this embodiment is 90 ° C. or higher and 140 ° C. or lower, and a more preferable range is 100 ° C. or higher and 130 ° C. or lower.
本実施形態に関するホットメルト接着剤は、発泡ホットメルト接着剤であることが好ましい。発泡ホットメルト接着剤を用いることで、接着剤層の弾力性を高め、物品12と、接着剤層13との追随性を向上させることができる。また、追随性を増加させることによって、剥離部112との接触面積を高め、接着力を向上させることができる。
The hot melt adhesive according to this embodiment is preferably a foamed hot melt adhesive. By using the foamed hot melt adhesive, the elasticity of the adhesive layer can be increased and the followability between the
ホットメルト接着剤を発泡させるタイミングは、特に限定されないが、生産性を高める観点や品質を高精度に管理する観点から、接着剤層13を形成する直前、塗工時、若しくは塗工直後にホットメルト接着剤を発泡させるのが好適である。これらの中でも塗工直前もしくは塗工時に発泡させることがより好ましい。接着剤層13は、溶融したホットメルト接着剤を外装フィルム又は外装シートの所定の位置に塗工することによって得られる。
The timing of foaming the hot melt adhesive is not particularly limited, but from the viewpoint of improving productivity and managing the quality with high accuracy, the hot melt adhesive is hot immediately before forming the
ホットメルト接着剤に気泡を含有させる方法や装置は、特に限定されないが、気体を吹き込むことによりホットメルト接着剤を発泡させる方法が好適である。また、加熱分解型発泡剤をホットメルト接着剤中に添加しておき、接着剤層13を形成させる際に微細な気泡を発生させるようにしてもよい。
The method and apparatus for incorporating air bubbles into the hot melt adhesive are not particularly limited, but a method of foaming the hot melt adhesive by blowing gas is suitable. Further, a heat decomposable foaming agent may be added to the hot melt adhesive so that fine bubbles are generated when the
ホットメルト接着剤に気体を吹き込んで発泡させる装置は、例えば、常圧もしくは加圧下でホットメルト接着剤を溶融加熱する加熱撹拌容器と、加熱撹拌容器内に気体等の揮発性物質を導入する揮発性物質供給手段と、加熱撹拌容器内の温度や粘度をモニターするセンサと、加熱撹拌容器内に設けられた撹拌手段と、ホットメルト接着剤の粘度等に応じて撹拌条件(回転数等)を制御可能な制御部等を有する装置を例示できる。揮発性物質は、特に限定されないが、窒素やアルゴン等の不活性ガスが例示でき、窒素を好適に使用できる。 For example, a device for blowing a gas into a hot melt adhesive and foaming it includes, for example, a heated stirring container that melts and heats the hot melt adhesive under normal pressure or pressure, and a volatile substance that introduces a volatile substance such as a gas into the heated stirring container. The agitation conditions (number of revolutions, etc.) according to the viscosity of the hot melt adhesive, etc., the substance supply means, the sensor for monitoring the temperature and viscosity in the heated stirring container, the stirring means provided in the heated stirring container An apparatus having a controllable control unit can be exemplified. Although a volatile substance is not specifically limited, Inert gas, such as nitrogen and argon, can be illustrated and nitrogen can be used conveniently.
また、接着剤の成分と分子間で相互作用して接着剤層内部に保持可能なガスを用いてもよい。接着剤層の種類によるが、このような例として二酸化炭素が例示できる。ガスは、常圧で導入してもよいが、加圧下で行うことが効率的である。また、超臨界二酸化炭素等を用いることも可能である。 Moreover, you may use the gas which interacts between the component of an adhesive agent and a molecule | numerator, and can hold | maintain inside an adhesive bond layer. Depending on the type of the adhesive layer, carbon dioxide can be exemplified as such an example. The gas may be introduced at normal pressure, but it is efficient to carry out under pressure. It is also possible to use supercritical carbon dioxide or the like.
気体を吹き込むときのホットメルト接着剤の溶融粘度は、気泡を効率的に導入させる観点から、1,000〜50,000mPa・s以下の範囲に含まれることが好ましく、より好ましくは、5,000〜20,000mPa・sの範囲であり、特に好ましくは、5,000〜15,000mPa・sの範囲である。発泡させる温度は、用いるホットメルト接着剤の種類によるが、通常、120〜180℃であり、好ましくは、120〜150℃である。発泡ホットメルト接着剤を形成後、通常、常温に戻す。これにより、接着剤が固化し、発泡部も固定される。 From the viewpoint of efficiently introducing bubbles, the melt viscosity of the hot melt adhesive when the gas is blown is preferably in the range of 1,000 to 50,000 mPa · s, more preferably 5,000. It is the range of -20,000 mPa * s, Most preferably, it is the range of 5,000-15,000 mPa * s. The foaming temperature depends on the type of hot melt adhesive used, but is usually 120 to 180 ° C, and preferably 120 to 150 ° C. After forming the foamed hot melt adhesive, it is usually returned to room temperature. Thereby, an adhesive agent solidifies and a foaming part is also fixed.
ホットメルト接着剤の適切な発泡倍率は、用途やニーズに応じて変動し得るものであり、任意に設定できる。物品の形状に対する汎用性を高める観点からは、溶融状態で100ccの容器に充填させたときの質量の比において、以下の式において1.1〜10の範囲とすることが好ましい。より好ましくは1.5〜5であり、特に好ましくは1.5〜3の範囲である。
V1/V2・・・式
(式中V1は、未発泡のホットメルト接着剤の100ccの質量であり、V2は発泡ホットメルト接着剤の100ccの質量である。)
The appropriate foaming ratio of the hot melt adhesive can vary depending on the application and needs, and can be arbitrarily set. From the viewpoint of enhancing the versatility with respect to the shape of the article, it is preferable that the mass ratio when filled in a 100 cc container in the molten state is in the range of 1.1 to 10 in the following formula. More preferably, it is 1.5-5, Especially preferably, it is the range of 1.5-3.
V1 / V2 Formula (where V1 is the mass of 100 cc of the unfoamed hot melt adhesive, and V2 is the mass of 100 cc of the foamed hot melt adhesive)
本実施形態に関する接着剤層13において、外装された物品12と剥離部112との接合強度は、剥離部112における表面層及び裏面層の層間剥離強度より高くすることが好ましい。外装された物品12と剥離部112との接合強度をこのようにすることで、物品12を台紙11から剥離した場合に、ハーフカット溝111を起点として、台紙11表面の水平方向に台紙11が切断されるようになるためである。
In the
<陳列吊り下げ用包装体の製造方法>
本発明の包装体1の製造方法の一実施形態について図6を用いて説明する。本実施形態の包装体1の製造方法は、まずプラスチックフィルム又はプラスチックシートで外装された物品12に、ホットメルト接着剤(接着剤層13)を物品12の外装フィルム又は外装シート上に形成する。外装フィルム又は外装シートは、一般に平滑で極性も小さいフィルム又はシートであるため、物理的アンカー効果も不十分で、且つ、化学的な接合力も期待できない。そのため、ホットメルト接着剤を、最初に物品12の外装フィルム又は外装シート上に塗布し接着剤層13を形成することで、外装フィルム又は外装シートと接着剤層13との界面の接合強度を向上させることができる。
<Manufacturing method of display suspension packaging>
One Embodiment of the manufacturing method of the package 1 of this invention is described using FIG. In the manufacturing method of the package 1 of the present embodiment, first, a hot melt adhesive (adhesive layer 13) is formed on the exterior film or exterior sheet of the
そして、本実施形態の包装体1の製造方法は、物品12の外装フィルム又は外装シート上にホットメルト接着剤(接着剤層13)を形成した後に、台紙11の表面の剥離部112と接合することを特徴とする。台紙11の表面には紙、金属箔又はPET等の外装フィルム又は外装シートと比べ表面粗さ及び極性の大きいシート等が用いられるため、外装フィルム又は外装シートに比べ表面粗さ及び極性が大きい。そのため、ホットメルト接着剤(接着剤層13)を物品12の外装フィルム又は外装シート上に形成した後に、台紙11の表面の剥離部112と接合したとしても、台紙11の表面の剥離部112と接着剤層13との界面の接合強度の低下は少ない。そのため、物品12を台紙11から剥離した際であっても、物品12の外装フィルム又は外装シートと台紙11の剥離部112とが剥離することなく、ハーフカット溝111を起点として剥離部112の表面層から物品12を剥離することができる。
And the manufacturing method of the package 1 of this embodiment joins with the peeling
以下、実施例を示し、本発明を具体的に説明するが、本発明はこれらの実施例に限定されるものではない。 EXAMPLES Hereinafter, although an Example is shown and this invention is demonstrated concretely, this invention is not limited to these Examples.
<陳列吊り下げ用包装体の製造>
[実施例1]
台紙として、紙(450g/m2)に図2のようにハーフカット溝を設けた台紙(縦180mm、横94mmの台紙であって、剥離部が縦99mm、横10mmで縦長の逆U字状、ハーフカットの溝は、台紙11の厚さの66%)を用いた。また、プラスチックフィルムで外装された物品としてはポリエチレンフィルムで外装された物品(2000g)を用いた。
<Manufacture of display suspension packaging>
[Example 1]
As a baseboard, a baseboard (180 mm in length and 94 mm in width with a half-cut groove as shown in FIG. 2 on paper (450 g / m 2 ), with a peeled portion of 99 mm in length and 10 mm in width and a vertically inverted U-shape. The half-cut groove was 66% of the thickness of the mount 11). Further, as an article covered with a plastic film, an article (2000 g) covered with a polyethylene film was used.
市販の発泡ホットメルト塗布装置の溶融槽に市販の発泡ホットメルト接着剤を入れて175℃に加熱した。発泡倍率を2.5とし発泡ホットメルト接着剤を横10mm縦90mmの範囲で物品に塗布した。その後、台紙表面の剥離部と接合し、実施例1の包装体を得た。 A commercially available foamed hot melt adhesive was placed in a melting tank of a commercially available foamed hot melt coating apparatus and heated to 175 ° C. The foaming hot melt adhesive was applied to the article in a range of 10 mm wide and 90 mm long with an expansion ratio of 2.5. Then, it joined with the peeling part of the base_sheet | mounting_paper surface, and obtained the package of Example 1. FIG.
[実施例2]
台紙として、アルミ箔とPETと張り合わせたアルミ貼合紙(450g/m2)を用いたこと以外実施例1と同様に包装体を製造し、実施例2の陳列吊り下げ用包装体を得た。
[Example 2]
A packaging body was produced in the same manner as in Example 1 except that an aluminum bonding paper (450 g / m 2 ) laminated with aluminum foil and PET was used as the mount, and the display suspension packaging body of Example 2 was obtained. .
[実施例3]
台紙として、アルミが蒸着されたPETと紙とを貼り合わせたPET蒸着紙(450g/m2)を用いたこと以外実施例1と同様に包装体を製造し、実施例3の陳列吊り下げ用包装体を得た。
[Example 3]
A packaging body was manufactured in the same manner as in Example 1 except that PET vapor-deposited paper (450 g / m 2 ) obtained by bonding PET and paper on which aluminum was vapor-deposited was used as the mount. A package was obtained.
[比較例1]
実施例1において、発泡ホットメルト接着剤を横10mm縦90mmの範囲で台紙表面の剥離部に塗布し、その後、物品の外装フィルムと接合したこと以外実施例1と同様に陳列吊り下げ用包装体を製造し、比較例1の包装体を得た。
[Comparative Example 1]
In Example 1, the foamed hot melt adhesive was applied to the peeling part on the surface of the mount within a range of 10 mm wide and 90 mm long, and then bonded to the exterior film of the article, and then the display hanging packaging as in Example 1. And a package of Comparative Example 1 was obtained.
[比較例2]
実施例2において、発泡ホットメルト接着剤を横10mm縦90mmの範囲で台紙表面の剥離部に塗布し、その後、物品の外装フィルムと接合したこと以外実施例2と同様に陳列吊り下げ用包装体を製造し、比較例2の包装体を得た。
[Comparative Example 2]
In Example 2, the foamed hot melt adhesive was applied to the peeling part on the surface of the mount in the range of 10 mm in width and 90 mm in length, and then bonded to the exterior film of the article. And a package of Comparative Example 2 was obtained.
[比較例3]
実施例3において、発泡ホットメルト接着剤を横10mm縦90mmの範囲で台紙表面の剥離部に塗布し、その後、物品の外装フィルムと接合したこと以外実施例3と同様に陳列吊り下げ用包装体を製造し、比較例3の包装体を得た。
[Comparative Example 3]
In Example 3, the foaming hot melt adhesive was applied to the peeled portion on the surface of the mount in the range of 10 mm in width and 90 mm in length, and then bonded to the exterior film of the article. And a package of Comparative Example 3 was obtained.
<落下耐久試験>
実施例及び比較例の包装体について耐久試験を行った。具体的には、雰囲気温度4℃で実施例及び比較例の包装体を1mの高さから3サンプル(n=3)正落下させ、物品の外装フィルムと接着剤層との剥離しなかった包装体のサンプル数を確認した。結果を表1に示す。
<Drop endurance test>
Durability tests were conducted on the packaging bodies of the examples and comparative examples. Specifically, the packaging of Examples and Comparative Examples was dropped from 3 m (n = 3) from the height of 1 m at an atmospheric temperature of 4 ° C., and the packaging of the article and the adhesive layer did not peel off. The number of body samples was confirmed. The results are shown in Table 1.
表1より、実施例の包装体は、比較例の包装体と比べて落下耐久試験において、いずれも剥離が見られなかった。本試験結果から、ホットメルト接着剤を物品の外装フィルム又は外装シート上に形成した後に、台紙表面の剥離部と接合することを特徴とする本発明の包装体の製造方法は、ホットメルト接着剤を台紙表面上に形成する包装体の製造方法に比べ、外装フィルム又は外装シートと接着剤層との界面での剥離が生じることのない優れた包装体の製造方法であることが分かる。 From Table 1, in the drop durability test, none of the packaging bodies of the examples was observed in comparison with the packaging body of the comparative example. From this test result, after forming the hot melt adhesive on the exterior film or exterior sheet of the article, the method for producing the package of the present invention, which is bonded to the peeling portion on the surface of the mount, It can be seen that this is an excellent method for producing a package without causing peeling at the interface between the exterior film or the exterior sheet and the adhesive layer, as compared with the method for producing a package on the surface of the mount.
1 包装体
11 台紙
111 ハーフカット溝
112 剥離部
113 別のハーフカット溝
12 物品
13 接着剤層
DESCRIPTION OF SYMBOLS 1
Claims (3)
前記台紙の表面には、前記台紙の厚さ方向未満の深さのハーフカット溝で形成される周状の剥離部が形成されており、
前記ホットメルト接着剤を、前記物品の外装フィルム又は外装シート上に形成した後に、前記台紙表面の剥離部と接合することを特徴とする陳列吊り下げ用包装体の製造方法。 An article covered with a plastic film or a plastic sheet is a method for producing a display-hanging package in which a hot melt adhesive is used to fix the article to the surface of the mount,
On the surface of the mount, a circumferential peeling portion formed by a half cut groove having a depth less than the thickness direction of the mount is formed,
A method for producing a display suspension packaging body, wherein the hot melt adhesive is formed on an exterior film or an exterior sheet of the article and then joined to a peeling portion on the surface of the mount.
剥離後の前記台紙には、前記剥離部の裏面層が残部として存在するように、
前記外装された物品と前記剥離部との接合強度を、前記剥離部における前記表面層及び裏面層の層間剥離強度より高くする、請求項1又は2に記載の陳列吊り下げ用包装体の製造方法。 When the outer article is peeled from the mount, the outer article is peeled off together with the hot melt adhesive and the surface layer of the peeling portion,
In the mount after peeling, so that the back layer of the peeling portion exists as the remainder,
The manufacturing method of the display hanging packaging body according to claim 1 or 2, wherein a bonding strength between the packaged article and the peeling portion is higher than an interlayer peeling strength of the front surface layer and the back surface layer in the peeling portion. .