JP2016204788A - Collar core, and shirt using the same - Google Patents
Collar core, and shirt using the same Download PDFInfo
- Publication number
- JP2016204788A JP2016204788A JP2015089601A JP2015089601A JP2016204788A JP 2016204788 A JP2016204788 A JP 2016204788A JP 2015089601 A JP2015089601 A JP 2015089601A JP 2015089601 A JP2015089601 A JP 2015089601A JP 2016204788 A JP2016204788 A JP 2016204788A
- Authority
- JP
- Japan
- Prior art keywords
- collar
- thin plate
- elastic thin
- shirt
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、上衣の襟元に固定して使用する襟芯及びそれを用いてなるシャツに関する。 The present invention relates to a collar core used by being fixed to a neck of an upper garment and a shirt using the same.
従来から、シャツなどの上衣の襟羽根の形状を維持するために、襟羽根先端部分にプラスチック製の芯材を入れることがある。 Conventionally, in order to maintain the shape of the collar wing of an upper garment such as a shirt, a plastic core material is sometimes placed at the tip of the collar wing.
例えば、特許文献１や特許文献２には、襟羽根の端部にポリエステル製の芯材を入れることが記載されている。特許文献３には、への字状の芯材をポケットに収納することが記載されている。特許文献４には、厚さが１００μｍのポリエステルフィルムを保形材として襟羽根先端部分に挿入して固定することが記載されている。 For example, Patent Literature 1 and Patent Literature 2 describe that a core material made of polyester is placed at the end of a collar feather. Patent Document 3 describes storing a U-shaped core material in a pocket. Patent Document 4 describes that a polyester film having a thickness of 100 μm is inserted into the tip of the collar feather as a shape-retaining material and fixed.
襟芯以外に関するものでは特許文献５や特許文献６がある。特許文献５には、襟先を面ファスナー等で固定して襟先のはね上がりを防止することが記載されている。特許文献６には、襟生地の内側に２枚の芯地を、ホットメルト接着剤を介して重ねて熱プレスすることが記載されている。 There exist patent document 5 and patent document 6 regarding things other than a collar core. Patent Document 5 describes that the collar tip is fixed with a hook-and-loop fastener or the like to prevent the collar tip from springing up. Patent Document 6 describes that two interlinings are placed on the inner side of a collar fabric and hot-pressed with a hot melt adhesive.
特許文献１、特許文献２、及び特許文献４の襟芯はポリエステル製であるが、低弾性薄板と高弾性薄板とを組み合わせることについては開示されておらず、着心地については配慮されていない。 The collar cores of Patent Document 1, Patent Document 2, and Patent Document 4 are made of polyester, but there is no disclosure about combining a low elastic thin plate and a high elastic thin plate, and no consideration is given to comfort.
最近では、襟芯としてポリエチレン樹脂の芯材が使用されている。しかし、ポリエチレン樹脂は耐熱性が低いため、当該芯材はアイロンによる加熱で折れ曲がりやすい。また、当該芯材はコシが弱く洗濯、クリーニング、アイロン掛けの際に負荷される応力によっても折れ曲がりやすい。 Recently, a polyethylene resin core material has been used as a collar core. However, since polyethylene resin has low heat resistance, the core material is easily bent by heating with an iron. Further, the core material is weak and easily bends due to stress applied during washing, cleaning, and ironing.
特許文献３については、可撓性を有する素材で襟芯を構成することが記載されているが、具体的にいかなる素材を使用するのかが記載されておらず襟芯の耐久性等については不明である。同様に特許文献６においても襟芯の詳細は不明である。特許文献５には襟芯を使用することが記載されていない。 Patent Document 3 describes that the collar core is made of a flexible material, but it does not describe what material is used specifically, and the durability of the collar core is unknown. It is. Similarly, in Patent Document 6, details of the collar core are unknown. Patent Document 5 does not describe the use of a collar core.
本発明は、アイロン掛け等による熱や曲げ応力に対して変形し難く、着心地のよいシャツを作製することが可能な襟芯を提供することを目的とする。そして、洗濯、クリーニング、アイロン掛け等による熱や曲げ応力によって変形し難く、着心地のよい襟を備えたシャツを提供することを目的とする。 An object of the present invention is to provide a collar core that is less likely to be deformed by heat or bending stress due to ironing or the like and that can produce a comfortable shirt. It is another object of the present invention to provide a shirt having a comfortable collar that is not easily deformed by heat or bending stress due to washing, cleaning, ironing, or the like.
ポリエチレン又はポリプロピレンからなる低弾性薄板とポリエステルからなり低弾性薄板に比較してコシのある高弾性薄板とを重ねてなる襟芯であって、低弾性薄板は、低弾性薄板と高弾性薄板とを重ねた状態の平面視において、高弾性薄板の外縁に対して低弾性薄板の外縁が突出した部分を有する襟芯、及び当該襟芯を襟羽根部分に固定してなるシャツにより、上記の課題を解決する。襟芯は低弾性薄板の外縁が高弾性薄板から突出した部分を有するため、着用者の首や胸部などに低弾性版の外縁が高弾性薄板よりも先に接触する。このため、シャツの襟周りにおいて着心地を軟らかくすることができる。一方で高弾性薄板はポリエステルからなるので、洗濯やクリーニングの際に負荷される応力やアイロン等の加熱、加圧に対して襟芯を折れ曲がったり変形したりしにくくすることができる。 A collar core made of a low elastic thin plate made of polyethylene or polypropylene and a high elastic thin plate made of polyester, which is firmer than a low elastic thin plate, wherein the low elastic thin plate comprises a low elastic thin plate and a high elastic thin plate. In a plan view of the stacked state, the collar core having a portion in which the outer edge of the low elastic thin plate protrudes from the outer edge of the high elastic thin plate, and a shirt formed by fixing the collar core to the collar blade portion, Solve. Since the collar core has a portion in which the outer edge of the low elastic thin plate protrudes from the high elastic thin plate, the outer edge of the low elastic plate contacts the wearer's neck, chest, etc. before the high elastic thin plate. For this reason, comfort can be softened around the collar of the shirt. On the other hand, since the highly elastic thin plate is made of polyester, it can be made difficult to bend or deform the collar core against stress applied during washing or cleaning, heating with an iron or the like, and pressurization.
襟芯は、襟芯先端部分の左右の端部において高弾性薄板の外縁に対して低弾性薄板の外縁が突出した形状であることが好ましい。襟芯の先端は、着用者の体に触れやすく、また力も集中しやすい。襟芯先端部分の左右の端部において低弾性薄板の外縁が突出するようにすることで、シャツの着用者にとって襟周りの着心地が軟らかいものとなる。襟芯の基端部分も、着用者の体に触れやすく、また力が集中しやすい。同様の理由から、襟芯は、襟芯基端部分の左右の端部において高弾性薄板の外縁に対して低弾性薄板の外縁が突出した形状であることが好ましい。 The collar core preferably has a shape in which the outer edge of the low elastic thin plate protrudes from the outer edge of the high elastic thin plate at the left and right ends of the front end portion of the collar core. The tip of the collar core is easy to touch the wearer's body and concentrates the force. By allowing the outer edges of the low elastic thin plate to protrude at the left and right ends of the collar core tip, the wearer around the collar is soft for the shirt wearer. The proximal end of the collar core is also easy to touch the wearer's body and concentrate the force. For the same reason, the collar core preferably has a shape in which the outer edge of the low elastic thin plate protrudes from the outer edge of the high elastic thin plate at the left and right ends of the base end portion of the collar core.
襟芯は、襟羽根の基端部から襟羽根の剣先部分にかけて設けられた閉じたポケットに収納することが好ましい。これにより襟芯の位置ずれを防止して襟先が真っ直ぐに張った状態を長期に維持することが可能になる。このとき、剣先部分に第１固定具を設け、シャツの前身頃の剣先部分に対応する位置に第２固定具を設けることが好ましい。第１固定具及び第２固定具によって剣先の位置を固定し、閉じたポケットに収納された襟芯によって襟羽根の端部が真っ直ぐに張った状態とすることで、襟が美しく起立した状態を維持することができる。このとき、第１固定具及び第２固定具を隠し釦とすることで、襟元をフォーマルでスマートに見せることができる。 The collar core is preferably stored in a closed pocket provided from the base end of the collar feather to the sword tip of the collar feather. As a result, it is possible to prevent the misalignment of the collar core and maintain a state in which the collar tip is straightened for a long time. At this time, it is preferable to provide a 1st fixing tool in a sword tip part, and to provide a 2nd fixing tool in the position corresponding to the sword tip part of the front body of a shirt. By fixing the position of the tip of the sword with the first fixing tool and the second fixing tool and making the end of the collar feather straight with the collar core stored in the closed pocket, the state where the collar stands up beautifully Can be maintained. At this time, by using the first fixing tool and the second fixing tool as hidden buttons, the neck can be formal and smart.
本発明の襟芯を使用すれば、熱や曲げ応力に対して変形し難く、しかも着心地のよいシャツを提供することが可能になる。熱や曲げ応力に対して変形し難いので、美しい襟元の形状を長期にわたって保つことが可能である。 By using the collar core of the present invention, it is possible to provide a shirt that is not easily deformed by heat and bending stress and that is comfortable to wear. Since it is difficult to deform against heat and bending stress, it is possible to maintain a beautiful collar shape for a long time.
図面を参照しつつ本発明を実施するための形態について説明する。図１は、本発明の襟芯の一実施形態である。この襟芯１は、襟の表地側に位置するポリエステル樹脂からなる１枚の高弾性薄板１１と、襟の裏地側に位置するポリエチレン樹脂からなる１枚の低弾性薄板１２とからなる。この実施形態は低弾性薄板１枚と高弾性薄板１枚とからなる襟芯であるが、低弾性薄板及び高弾性薄板の枚数は特に限定されない。図２においては、説明の便宜から高弾性薄板１１にはハッチングを付して示した（図３ないし図５において同じ。）。図３ないし５は、襟芯２の別の実施形態であるが、同様にポリエステルからなる１枚の高弾性薄板１３、１５、１７と、ポリエチレンからなる低弾性薄板１４、１６、１８とからなる。各実施形態の低弾性薄板は、ポリプロピレン樹脂から構成してもよい。 DESCRIPTION OF EMBODIMENTS Embodiments for carrying out the present invention will be described with reference to the drawings. FIG. 1 is an embodiment of a collar core of the present invention. The collar core 1 is composed of one high elastic thin plate 11 made of polyester resin located on the outer side of the collar and one low elastic thin plate 12 made of polyethylene resin located on the lining side of the collar. This embodiment is a collar core composed of one low elastic thin plate and one high elastic thin plate, but the number of low elastic thin plates and high elastic thin plates is not particularly limited. In FIG. 2, the highly elastic thin plate 11 is hatched for convenience of explanation (the same applies to FIGS. 3 to 5). FIGS. 3 to 5 show another embodiment of the collar core 2, which is similarly composed of one high elastic thin plate 13, 15, 17 made of polyester and a low elastic thin plate 14, 16, 18 made of polyethylene. . The low elastic thin plate of each embodiment may be made of polypropylene resin.
ポリエステルは、ポリエチレンやポリプロピレンに比較して、耐熱性が高く、引張弾性率が高い。ポリエステルを襟芯として使用することで、シャツを洗濯又はクリーニングする際に負荷される応力やアイロンによる熱や応力などに対してシャツの襟芯を曲りにくくすることができる。一方でポリエステルは、ポリエチレンやポリプロピレンに比較してコシが強いため、シャツの襟元周りの着心地が硬くなるし、襟芯によって襟の生地が摩耗したり破れやすくなったりする。例えば、襟芯が胸や首に接触して着用者に不快感を与えることがある。特に第１ボタンを留めてネクタイを締めたときなどは顕著である。そこで、実施形態に示す襟芯１、２、３、４では、ポリエチレン又はポリプロピレンからなる低弾性薄板１２、１４、１６、１８をポリエステルからなる高弾性薄板１１、１３、１５、１７と重ねて、平面視において高弾性薄板の外縁に対して低弾性版の外縁を突出させることで襟周りの着心地が軟らかくなるようにしている。低弾性薄板の外縁は、高弾性薄板の外縁よりも外側に突出しているため、着用者の体に高弾性薄板よりも先に接触して、低弾性薄板の外縁部分が曲がる。これによって、シャツの着心地を軟らかくする。また、襟芯による襟の生地の摩耗を低減する。 Polyester has higher heat resistance and higher tensile elastic modulus than polyethylene and polypropylene. By using polyester as a collar core, it is possible to make the collar core of the shirt difficult to bend against the stress applied when washing or cleaning the shirt, the heat or stress of the iron, and the like. On the other hand, polyester is stronger than polyethylene or polypropylene, so the comfort around the neck of the shirt is hardened, and the collar fabric is easily worn or torn by the collar core. For example, the collar core may come into contact with the chest and neck, causing discomfort to the wearer. This is particularly noticeable when the first button is fastened and the tie is fastened. Therefore, in the collar cores 1, 2, 3, 4 shown in the embodiment, the low elastic thin plates 12, 14, 16, 18 made of polyethylene or polypropylene are overlapped with the high elastic thin plates 11, 13, 15, 17 made of polyester, By projecting the outer edge of the low-elastic plate with respect to the outer edge of the highly elastic thin plate in plan view, the comfort around the collar is softened. Since the outer edge of the low elastic thin plate protrudes outward from the outer edge of the high elastic thin plate, the outer edge portion of the low elastic thin plate bends by contacting the wearer's body before the high elastic thin plate. This softens the comfort of the shirt. It also reduces the wear of the collar fabric by the collar core.
図１及び図２の襟芯１の場合は、襟芯先端部分の左右の端部において低弾性薄板１２の外縁が高弾性薄板１１の外縁に対して突出した形状となっている。これによって、襟芯の先端部分の左右の端部が着用者の胸部を圧迫することを防止することができる。図３の襟芯２のように、襟芯２の基端部分の左右の端部において低弾性薄板１４の外縁が高弾性薄板１３の外縁に対して突出する形状としてもよい。これによって、襟芯２の基端部分の左右の端部が着用者の首を圧迫することを防止することができる。 In the case of the collar core 1 shown in FIGS. 1 and 2, the outer edge of the low elastic thin plate 12 protrudes from the outer edge of the high elastic thin plate 11 at the left and right ends of the collar core tip. Thereby, it is possible to prevent the left and right end portions of the distal end portion of the collar core from pressing the wearer's chest. 3, the outer edge of the low elastic thin plate 14 may protrude from the outer edge of the high elastic thin plate 13 at the left and right ends of the base end portion of the collar core 2. Thereby, it is possible to prevent the left and right end portions of the base end portion of the collar core 2 from pressing the wearer's neck.
図２の襟芯１は、高弾性薄板１１及び低弾性薄板１２共に、基端部分を円弧状とし先端部分を先細部分１９、２０（テーパー部分）を有する円弧状とした短冊状の薄板である。ただし、低弾性薄板１２の先端側の円弧の半径は高弾性薄板１１の先端側の円弧の半径よりも大きくして、余部２１を構成している。図３の襟芯２は、短冊状であり、先端部分は図２の襟芯と同様である。低弾性薄板１４の基端部分は円弧状とし、高弾性薄板１３の基端部分は先細部分２２を有する円弧状とし、低弾性薄板１４の基端側の円弧の半径を高弾性薄板１３の基端側の円弧の半径よりも大きくして、余部２３を構成している。図４の襟芯３は、短冊状であり、先端部分および基端部分共に図３の基端部分の形状と同様にして余部２３を構成している。図５の襟芯は、短冊状であり、基端部分及び先端部分は図４の襟芯と同様であるが、左右側面にさらに余部２４を有する。 The collar core 1 of FIG. 2 is a strip-like thin plate in which both the high elastic thin plate 11 and the low elastic thin plate 12 are arc-shaped at the base end and arc-shaped at the tip end with tapered portions 19 and 20 (tapered portions). . However, the radius of the arc on the distal end side of the low elastic thin plate 12 is made larger than the radius of the arc on the distal end side of the high elastic thin plate 11 to constitute the surplus portion 21. The collar core 2 in FIG. 3 has a strip shape, and the tip portion is the same as the collar core in FIG. The base end portion of the low elastic thin plate 14 has an arc shape, the base end portion of the high elastic thin plate 13 has an arc shape having a tapered portion 22, and the radius of the arc on the base end side of the low elastic thin plate 14 is the base of the high elastic thin plate 13. The surplus portion 23 is configured to be larger than the radius of the arc on the end side. The collar core 3 in FIG. 4 has a strip shape, and both the distal end portion and the proximal end portion constitute a surplus portion 23 in the same manner as the shape of the proximal end portion in FIG. The collar core of FIG. 5 has a strip shape, and the proximal end portion and the distal end portion are the same as the collar core of FIG.
上記の各実施形態の襟芯は、図６に模式的に示したように、例えば、襟羽根２５の基端部２６から剣先２７にかけて設けられた閉じたポケット２８に収納して使用する。図６では襟芯１を固定したシャツ５の一例を示す。図６及び図７において閉じたポケット２８を破線で示した。これにより襟芯１の位置ずれを防止して襟羽根２５の端部の基端側から先端側（剣先２７の付け根から剣先２７の先端）が真っ直ぐに張った状態を長期に維持することが可能になる。閉じたポケット２８の基端は襟羽根２５の基端部２６から少しは離れた部分に位置させてあり、襟芯が着用者の首を圧迫しないようになっている。 As schematically shown in FIG. 6, the collar core of each of the above embodiments is used by being housed in a closed pocket 28 provided from the base end portion 26 of the collar blade 25 to the sword tip 27, for example. FIG. 6 shows an example of the shirt 5 to which the collar core 1 is fixed. 6 and 7, the closed pocket 28 is indicated by a broken line. As a result, it is possible to prevent the collar 1 from being displaced and to maintain a state where the base end side of the end portion of the collar feather 25 is stretched straight (from the base of the sword tip 27 to the tip of the sword tip 27) straight. become. The proximal end of the closed pocket 28 is located at a position slightly away from the proximal end portion 26 of the collar wing 25 so that the collar core does not press the wearer's neck.
図６のシャツ５では、低弾性薄板１２の長さと高弾性薄板１１の長手方向の長さを同じにした襟芯１を略同形の閉じたポケット２８に収納している。略同形とは襟芯１に無理な力が加わらない程度の遊びをもたせた状態である。このため、高弾性薄板１１の位置が低弾性薄板１２に対して長さ方向に対してずれにくい。高弾性板１１が長さ方向にずれにくいので襟の端部を安定して支えて真っ直ぐに張った状態を維持することができる。長さ方向に直交する方向に対しては余部を備えているので高弾性薄板１２が着用者の体を圧迫することを防止することができる。 In the shirt 5 of FIG. 6, a collar core 1 in which the length of the low elastic thin plate 12 and the length of the high elastic thin plate 11 in the longitudinal direction are the same is accommodated in a closed pocket 28 having substantially the same shape. The “substantially the same shape” refers to a state where the collar core 1 has a play that does not apply excessive force. For this reason, the position of the highly elastic thin plate 11 is not easily displaced in the length direction with respect to the low elastic thin plate 12. Since the highly elastic plate 11 is not easily displaced in the length direction, the end of the collar can be stably supported and kept in a straight state. Since the surplus portion is provided in the direction orthogonal to the length direction, the highly elastic thin plate 12 can be prevented from pressing the wearer's body.
図６のシャツ５では、左右の剣先２７の部分にそれぞれ第１固定具２９を設け、シャツ５の前身頃の対応する位置に第２固定具３０を設けている。第１固定具２９及び第２固定具３０によって剣先２７の位置を固定すると、襟芯の効果と相まって襟羽根２５の端部の基端側から先端側が真っ直ぐに張った状態で襟が美しく起立した状態を長期にわたって維持することができる。特にネクタイを締めない状態において第１ボタンを外した状態で襟を美しく見せることができる。 In the shirt 5 of FIG. 6, the 1st fixing tool 29 is provided in the part of the right and left sword tip 27, respectively, and the 2nd fixing tool 30 is provided in the position corresponding to the front body of the shirt 5. In FIG. When the position of the sword tip 27 was fixed by the first fixing tool 29 and the second fixing tool 30, the collar stood beautifully in a state in which the distal end side was stretched straight from the base end side of the end of the collar feather 25 in combination with the effect of the collar core. The state can be maintained for a long time. In particular, the collar can be seen beautifully with the first button removed when the tie is not fastened.
図６のシャツ５では、第１固定具２９及び第２固定具３０は、隠し釦から構成している。より具体的には、襟先部分の裏側にスナップボタンの雄側を縫着して、シャツの前身頃の襟先部分に対応する位置にスナップボタンの雌側を縫着している。スナップボタンの雄雌は相互に入れ替え可能である、襟先部分の裏側に雌側を逢着して、前身頃に雄側を縫着してもよい。隠し釦は、襟芯の効果と相まって剣先２７が真っ直ぐに張った状態を長期にわたって維持し、フォーマルで清潔感のある襟に見せることができる。 In the shirt 5 of FIG. 6, the 1st fixing tool 29 and the 2nd fixing tool 30 are comprised from the hidden button. More specifically, the male side of the snap button is sewn to the back side of the collar tip portion, and the female side of the snap button is sewn to a position corresponding to the collar tip portion of the front body of the shirt. The male and female of the snap button can be interchanged with each other. The female side may be attached to the back side of the collar portion and the male side may be sewn to the front body. The hidden button, combined with the effect of the collar core, maintains the state where the sword tip 27 is stretched for a long period of time, and can show a formal and clean collar.
図６のシャツ５は、襟台３１、襟羽根２５に芯地を使用している。芯地は、襟芯の効果と相まって襟全体が起立した立体的な状態を長期にわたって維持して襟元を美しく見せることができる。図８に図７のＡＡ部分の端面図を示したように、襟羽根２５の端部付近は、２枚の芯地３２、３３が入っている。この芯地３２、３３は、シャツ５の裏地３４及び表地３５に比較して、コシのある織布などで構成すればよい。図６のシャツ５ではシャツの裏地３４及び表地３５に比較して厚手で単位面積当たりの糸の打ち込み本数が多い織布を使用している。襟羽根２５の端部付近は、厚手の芯地３２と薄手の芯地３３の間にホットメルト接着剤を適用し、熱圧着して積層芯地３６としている。図７においては、二点鎖線で積層芯地３６と芯地３２の境界を示した。 The shirt 5 in FIG. 6 uses interlining for a collar base 31 and a collar feather 25. The interlining allows the collar to look beautiful while maintaining a three-dimensional state in which the entire collar stands up in combination with the effect of the collar core. As shown in the end view of the AA portion of FIG. 7 in FIG. 8, two interlinings 32 and 33 are included near the end of the collar feather 25. The interlinings 32 and 33 may be made of a woven fabric having a firmness compared to the lining 34 and the outer surface 35 of the shirt 5. The shirt 5 shown in FIG. 6 uses a woven fabric that is thicker and has a larger number of yarns driven per unit area than the shirt lining 34 and the outer surface 35. A hot melt adhesive is applied between the thick interlining 32 and the thin interlining 33 in the vicinity of the end portion of the collar feather 25, and the laminated interlining 36 is formed by thermocompression bonding. In FIG. 7, the boundary between the laminated interlining 36 and the interlining 32 is indicated by a two-dot chain line.
図７及び図８に示したように、裏地３４の上に低弾性薄板１２及び高弾性薄板１１を重ねて、襟羽根２５と同じ形状に裁断したポケット形成用の中地３７を低弾性薄板１２及び高弾性薄板１１の上に重ねて、低弾性薄板１２の縁に沿って遊びをもたせた状態で糸３８で縫ってある。糸３８によって閉じたポケット２８を形成し、その中に低弾性薄板１２及び高弾性薄板１１が収納されている。上記の中地３７に積層芯地３６、表地３５を記載した順に重ねて、表地３５及び積層芯地３６の端部と中地３７及び裏地３４の端部とをそれぞれ内側に折り返して糸３９で縫って襟羽根２５としている。なお、図８は、襟を折り返した状態の端面図であるので上下が逆さまの状態となっている。 As shown in FIGS. 7 and 8, the low-elastic thin plate 12 includes a pocket forming center 37 that is formed by overlapping the low-elastic thin plate 12 and the high-elastic thin plate 11 on the backing 34 and cutting into the same shape as the collar blade 25. In addition, it is sewed with a thread 38 in a state of being overlaid on the high elastic thin plate 11 and having play along the edge of the low elastic thin plate 12. A closed pocket 28 is formed by the thread 38, and the low elastic thin plate 12 and the high elastic thin plate 11 are accommodated therein. The layered interlining 36 and the outer surface 35 are overlapped on the inner base 37 in the order described, and the end portions of the outer surface 35 and the upper layered interlining 36 and the end portions of the inner surface 37 and the inner side lining 34 are folded back inwardly with a thread 39. The collar feather 25 is sewn. In addition, since FIG. 8 is an end view in a state where the collar is folded, the top and bottom are upside down.
図９のＢＢ部分の端面図に示したように襟羽根２５の内側では、裏地３４、積層芯地３６、表地３５が記載した順に重なっており、表地３５及び積層芯地３６の端部と裏地３４の端部とをそれぞれ内側に折り返して左右の端部が糸３９で縫着されている。積層芯地３６は、襟羽根２５の端部付近では２枚として剣先を含む襟の端部が立った状態を維持して、襟羽根２５の内側では１枚として首回りの着心地が過度に硬くならないようにしてある。図８に示したように、襟台３１は、裏地４０、芯地４１、襟羽根２５、及び表地４２を記載した順に重ねて、表地４２の端部と裏地４０及び芯地４１の端部とをそれぞれ内側に折り返して糸４３で縫って襟台３１の形状としている。襟台３１では芯地を１枚として首回りの着心地が過度に硬くならないようにしてある。 As shown in the end view of the BB portion in FIG. 9, the inner side of the collar wing 25 overlaps the lining 34, the laminated interlining 36, and the outer covering 35 in the order described, and the end portions and the lining of the outer covering 35 and the laminated interlining 36. The end portions of 34 are folded inward, and the left and right end portions are sewn with a thread 39. The laminated interlining 36 maintains a state in which the end of the collar including the sword tip is standing as two pieces near the end of the collar feather 25, and the comfort around the neck is excessive as one piece inside the collar feather 25. It doesn't become hard. As shown in FIG. 8, the collar base 31 is formed by stacking the lining 40, the interlining 41, the collar feather 25, and the outer covering 42 in the order described, and the end of the outer covering 42 and the end of the lining 40 and the interlining 41. Are folded inward and sewed with a thread 43 to form a collar 31. The collar base 31 has a single interlining so that the comfort around the neck does not become excessively hard.
図６のシャツ５では、カフスにも襟台３１と同じ構成の芯地を１枚入れてある。また、前身頃の胸部に設けたポケット生地の上端部分にシャツ５の生地と同色でアルファベットのＤの文字の刺繍が施してある。人と対面したときに襟から胸元を経てカフスに視線が流れることが多く、襟、ポケット、及びカフスの３点は特に目につきやすい。図６のシャツ５では襟を真っ直ぐに張った状態を維持すると共に、カフスの芯地によって袖口も張った状態を維持し、ポケットの刺繍も相まって、清潔な印象を与えることができる。ポケットの刺繍は、刺繍に目が行きやすくなるという心理的な効果を利用しており、ポケットに物を入れても目立ちにくい。 In the shirt 5 of FIG. 6, one piece of interlining having the same configuration as that of the collar base 31 is also put in the cuff. Further, the upper end portion of the pocket fabric provided on the chest of the front body is embroidered with the letter D of the alphabet in the same color as the fabric of the shirt 5. When facing a person, the line of sight often flows from the collar through the chest to the cuff, and the collar, pocket, and cuff are particularly noticeable. In the shirt 5 of FIG. 6, while maintaining a state where the collar is stretched straight, a state where the cuffs are also stretched by the cuffs interlining is combined with the embroidery of the pocket, and a clean impression can be given. Pocket embroidery takes advantage of the psychological effect of making it easier to see the embroidery.
高弾性薄板を構成するポリエステルとしては、ポリエチレンテレフタレート、ポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレートなどが使用可能である。このようなポリエルテル類を１５０〜２００℃程度の高温で加熱したりフィルムを延伸したりして結晶化した結晶化ポリエステルを使用することが好ましい。ポリエステルとしては、例えば、引張弾性率(JIS K 7113）が２８０〜４３０kgf/mm2のものを使用することが好ましい。さらに、熱変形温度（JIS K 7206）が１２０〜２７０℃であるものを使用することが好ましく、２００〜２７０℃であるものを使用することがより好ましい。 As the polyester constituting the highly elastic thin plate, polyethylene terephthalate, polytrimethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polybutylene naphthalate and the like can be used. It is preferable to use crystallized polyester obtained by crystallizing such polyertels by heating at a high temperature of about 150 to 200 ° C. or stretching the film. As the polyester, for example, it is preferable to use a polyester having a tensile elastic modulus (JIS K 7113) of 280 to 430 kgf / mm 2 . Further, it is preferable to use a material having a heat distortion temperature (JIS K 7206) of 120 to 270 ° C., and more preferably 200 to 270 ° C.
低弾性薄板を構成するポリエチレンとしては、低密度から高密度のポリエチレンを使用すればよい。高密度ポリエチレンや超高分子量ポリエチレンについては引張弾性率の小さいものを使用することが好ましい。ポリプロピレンについても引張弾性率を基に使用するものを選択することができる。ポリエチレン及びポリプロピレンとしては、例えば、引張弾性率(JIS K 7113）が９〜２４０kgf/mm2のものを使用することが好ましく、９〜１２０kgf/mm2のものを使用することがより好ましい。ポリプロピレンは、ポリエチレンに比較して耐ヒンジ特性が強く折り曲げに対して強い点で好ましい。 As the polyethylene constituting the low elastic thin plate, low density to high density polyethylene may be used. For high-density polyethylene and ultrahigh molecular weight polyethylene, it is preferable to use one having a low tensile elastic modulus. As for polypropylene, one to be used can be selected based on the tensile elastic modulus. As polyethylene and polypropylene, for example, those having a tensile elastic modulus (JIS K 7113) of 9 to 240 kgf / mm 2 are preferably used, and those having 9 to 120 kgf / mm 2 are more preferably used. Polypropylene is preferable in that it has strong hinge resistance compared to polyethylene and is strong against bending.
以下、本発明の実施例を挙げてより詳細に説明する。
[実施例１]
厚さ０．２５mm、密度０．９１、融点１０５℃、引張弾性率(JIS K 7113）２４kgf/mm2、熱変形温度（JIS K 7206）５６.３℃の低密度ポリエチレンのシートから図２の形状の低弾性薄板を切り出した。厚さ０．５mm、密度１．３９、融点２４５℃、引張弾性率(JIS K 7113）３８０kgf/mm2、熱変形温度２２０℃の結晶性ポリエチレンテレフタレートのシートから図２の形状の高弾性薄板を切り出した。
Examples of the present invention will be described in detail below.
[Example 1]
2 from a low density polyethylene sheet having a thickness of 0.25 mm, a density of 0.91, a melting point of 105 ° C., a tensile modulus (JIS K 7113) of 24 kgf / mm 2 , and a thermal deformation temperature (JIS K 7206) of 56.3 ° C. A shaped low elastic thin plate was cut out. A highly elastic thin plate having the shape shown in FIG. 2 is formed from a sheet of crystalline polyethylene terephthalate having a thickness of 0.5 mm, a density of 1.39, a melting point of 245 ° C., a tensile elastic modulus (JIS K 7113) of 380 kgf / mm 2 , and a heat distortion temperature of 220 ° C. Cut out.
上記のようにして得た低弾性薄板１枚及び高弾性薄板１枚を低弾性薄板が着用者の胸側になるようにして図２のように重ねて、図６のように左右の襟羽根の基端部から剣先に設けた閉じたポケットによって固定した。 One low elastic thin plate and one high elastic thin plate obtained as described above are stacked as shown in FIG. 2 so that the low elastic thin plate is on the chest side of the wearer, and left and right collar feathers as shown in FIG. It was fixed by a closed pocket provided at the tip of the sword from the base end.
〔実施例２〕
厚さ０．１mmの低密度ポリエチレンのシートから低弾性薄板を切り出したこと、厚さ０．２mmの結晶性ポリエチレンテレフタレートのシートから高弾性薄板を切り出したこと、そしてこの低弾性薄板２枚と高弾性薄板２枚とを低弾性薄板２枚が着用者の胸側になるようにして図６のように左右の襟羽根の先端部分に閉じたポケットによって固定したこと以外は実施例１と同様にしてシャツを作製した。
[Example 2]
A low elastic thin plate was cut out from a 0.1 mm thick low density polyethylene sheet, a high elastic thin plate was cut out from a 0.2 mm thick crystalline polyethylene terephthalate sheet, and two low elastic thin plates Example 2 except that two elastic thin plates were fixed with closed pockets at the tips of the left and right collar feathers as shown in FIG. 6 with the two low elastic thin plates facing the wearer's chest. Made a shirt.
〔実施例３〕
厚さ０．２mm、密度０．９４、融点１２０℃、引張弾性率(JIS K 7113）４３kgf/mm2、熱変形温度（JIS K 7206）６２℃の高密度ポリエチレンのシートから図３の形状の低弾性薄板を切り出した。
Example 3
3 from a high-density polyethylene sheet having a thickness of 0.2 mm, a density of 0.94, a melting point of 120 ° C., a tensile modulus (JIS K 7113) of 43 kgf / mm 2 , and a heat distortion temperature (JIS K 7206) of 62 ° C. A low elastic thin plate was cut out.
厚さ０．２mm、密度１．３８、融点２４５℃、引張弾性率(JIS K 7113）３２０kgf/mm2、熱変形温度（JIS K 7206）２０５℃の結晶性ポリエチレンテレフタレートのシートから図３の形状の高弾性薄板を切り出した。 3 from a crystalline polyethylene terephthalate sheet having a thickness of 0.2 mm, a density of 1.38, a melting point of 245 ° C., a tensile modulus (JIS K 7113) of 320 kgf / mm 2 , and a heat distortion temperature (JIS K 7206) of 205 ° C. A highly elastic thin plate was cut out.
上記のようにして得た低弾性薄板１枚及び高弾性薄板１枚を低弾性薄板が着用者の胸側になるようにして図２のように重ねて、図６のように左右の襟羽根の先端部分に閉じたポケットによって固定してシャツを作製した。 One low elastic thin plate and one high elastic thin plate obtained as described above are stacked as shown in FIG. 2 so that the low elastic thin plate is on the chest side of the wearer, and left and right collar feathers as shown in FIG. The shirt was made by fixing it with a closed pocket at the tip.
〔実施例４〕
厚さ０．１mm、密度０．９１、融点１６８℃、引張弾性率(JIS K 7113）１４０kgf/mm2、熱変形温度（JIS K 7206）６３℃のポリプロピレンのシートから図２の形状の低弾性薄板を切り出して、図２の形状の低弾性薄板を得た。これ以外は実施例１のシャツと同様にしてシャツを作製した。
Example 4
Low elasticity of the shape shown in Fig. 2 from a polypropylene sheet with a thickness of 0.1mm, a density of 0.91, a melting point of 168 ° C, a tensile modulus (JIS K 7113) of 140kgf / mm 2 , and a heat distortion temperature (JIS K 7206) of 63 ° C The thin plate was cut out to obtain a low elastic thin plate having the shape shown in FIG. Other than this, a shirt was produced in the same manner as the shirt of Example 1.
〔比較例１〕
実施例１に示した芯材に替えて、厚さ０．２５mm、密度０．９１、融点１０５℃、引張弾性率(JIS K 7113）２４kgf/mm2、熱変形温度（JIS K 7206）５６.３℃の低密度ポリエチレンのシートから切り出した短冊状の芯材を１枚使用したこと以外は実施例１と同様にしてシャツを作製した。
[Comparative Example 1]
Instead of the core material shown in Example 1, thickness 0.25 mm, density 0.91, melting point 105 ° C., tensile modulus (JIS K 7113) 24 kgf / mm 2 , heat distortion temperature (JIS K 7206) 56. A shirt was produced in the same manner as in Example 1 except that one strip-shaped core material cut out from a 3 ° C. low-density polyethylene sheet was used.
〔比較例２〕
厚さ０．５mm、密度１．３９、融点２４５℃、引張弾性率(JIS K 7113）３８０kgf/mm2、熱変形温度（JIS K 7206）２２０℃の結晶性ポリエチレンテレフタレートのシートから切り出した短冊状の芯材を１枚使用したこと以外は実施例１と同様にしてシャツを作製した。
[Comparative Example 2]
Strip shape cut out from a sheet of crystalline polyethylene terephthalate with thickness 0.5mm, density 1.39, melting point 245 ° C, tensile modulus (JIS K 7113) 380kgf / mm 2 , heat distortion temperature (JIS K 7206) 220 ° C A shirt was produced in the same manner as in Example 1 except that one core material was used.
実施例１ないし４及び比較例１及び２のシャツについて、市販の洗濯機によって洗濯し、それを乾燥機にかけて、１６０℃でアイロン掛けを行った。これを５０回繰り返し後の襟の外観と着心地を確認した。結果を表１に示す。 The shirts of Examples 1 to 4 and Comparative Examples 1 and 2 were washed with a commercially available washing machine, and then subjected to ironing at 160 ° C. in a dryer. This was repeated 50 times to confirm the appearance and comfort of the collar. The results are shown in Table 1.
表１に示したように実施例１ないし４のシャツでは、襟の剣先が真っ直に張った状態で、襟が美しく起立した状態が維持されていた。ネクタイを締めずに第１ボタンを空けた状態では図１０の外観が維持されており、襟芯が着用者の体を圧迫するようなこともなく軟らかい着心地であった。ネクタイを締めた状態では図１１の状態が維持されており、やはり襟芯が着用者の身体を圧迫するような感じは感じられず着心地は良好であった。また、芯材による襟周りの生地の摩耗も見られなかった。 As shown in Table 1, in the shirts of Examples 1 to 4, the collar was maintained upright with the sword tip of the collar stretched straight. In the state where the first button was opened without tightening the tie, the appearance of FIG. 10 was maintained, and the collar core was soft and comfortable without pressing the wearer's body. When the tie is tightened, the state of FIG. 11 is maintained, and the feeling that the collar core presses the wearer's body is not felt and the comfort is good. In addition, no abrasion of the fabric around the collar due to the core material was observed.
比較例１のシャツは、着心地は軟らかいものであったが、襟の剣先が襟の内側に湾曲した状態となってしまった。襟芯の状態を手で触って確かめたところ、内側に折れ曲がっていた。比較例２のシャツが張った状態は維持されていたものの、襟芯が着用者の胸を圧迫するような感じがして着心地が硬いものであった。比較例２のシャツの剣先の裏地を見ると襟芯によって裏地が少し破れていた。 The shirt of Comparative Example 1 was soft to wear, but the sword tip of the collar was curved to the inside of the collar. When I checked the condition of the collar core by hand, it was bent inside. Although the state where the shirt of Comparative Example 2 was stretched was maintained, it felt that the collar core pressed the chest of the wearer and was hard to wear. When the lining of the sword tip of the shirt of Comparative Example 2 was seen, the lining was slightly torn by the collar core.
以上のように、実施例１ないし４の襟芯によれば、シャツの着心地を損なうことなく、剣先が真っ直ぐに張った状態を維持することができる。実施例１ないし４のシャツは、襟台及び襟羽根に１枚の芯地を備えており、襟羽根の先端部分には芯地を２枚備えている。このため、襟芯の効果と相まって襟全体が美しく起立した状態を維持することができる。さらに、実施例１ないし４のシャツは襟先部分に隠し釦を備えており、剣先の先端の位置が固定されている。図１０に示したように、隠し釦と襟芯によって、剣先が襟羽根の基端部から延びる角度を調節して剣先が略鉛直方向に真っ直ぐに延びるようにして位置を固定し、襟元をスマートに見せることが可能になる。他方、隠し釦を外すと図１２のようになり、ややラフな印象となる。シャツは、繰り返しクリーニング又は洗濯されるため襟芯が曲り易く、購入当初の形状を維持することが容易でないが、実施例１ないし４の襟芯によれば洗濯やクリーニングを繰り返しても購入当初の襟の形状を維持することが可能であり、襟周りの着心地も優れている。 As described above, according to the collar cores of Examples 1 to 4, the state where the sword tip is stretched straight can be maintained without impairing the comfort of the shirt. The shirts of Examples 1 to 4 have one interlining on the collar base and the collar wing, and two interlinings on the tip of the collar wing. For this reason, the state where the whole collar stood beautifully in combination with the effect of the collar core can be maintained. Furthermore, the shirts of Examples 1 to 4 are provided with a hidden button on the collar tip portion, and the position of the tip of the sword tip is fixed. As shown in FIG. 10, the position of the sword tip is adjusted so that the sword tip extends straightly in the vertical direction by adjusting the angle at which the sword tip extends from the base end of the collar feather by the hidden button and the collar core. It becomes possible to show to. On the other hand, when the hidden button is removed, the result is as shown in FIG. 12, giving a slightly rough impression. Since the shirt is repeatedly cleaned or washed, the collar core is easy to bend and it is not easy to maintain the original shape. However, according to the collar cores of Examples 1 to 4, even after repeated washing and cleaning, The shape of the collar can be maintained, and the comfort around the collar is excellent.
１ 襟芯
１１ 高弾性薄板
１２ 低弾性薄板
２１ 余部
５ シャツ
２５ 襟羽根
２６ 基端部
２７ 剣先
２８ 閉じたポケット
２９ 第１固定具
３０ 第２固定具
３１ 襟台
DESCRIPTION OF SYMBOLS 1 Collar core 11 High elastic thin plate 12 Low elastic thin plate 21 Extra part 5 Shirt 25 Collar feather 26 Base end part 27 Tip 28 Closed pocket 29 1st fixing tool 30 2nd fixing tool 31 Collar stand
Claims (7)
ポリエステルからなり低弾性薄板に比較してコシのある高弾性薄板とを重ねてなる襟芯であって、
低弾性薄板は、低弾性薄板と高弾性薄板とを重ねた状態の平面視において、高弾性薄板の外縁に対して低弾性薄板の外縁が突出した部分を有する襟芯。 A collar core comprising a low elastic thin plate made of polyethylene or polypropylene and a high elastic thin plate made of polyester compared to a low elastic thin plate,
The low elastic thin plate is a collar core having a portion in which the outer edge of the low elastic thin plate protrudes from the outer edge of the high elastic thin plate in a plan view in a state where the low elastic thin plate and the high elastic thin plate are overlapped.