JP2016014147A - Polycarbonate resin composition and molded article - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a polycarbonate resin composition excellent in weather resistance, transparency, hue, heat resistance, thermal stability, moldability, and mechanical strength, and a molded article thereof.SOLUTION: A polycarbonate resin composition (X) comprises: a polycarbonate resin (A) which contains a structural unit (a) derived from a dihydroxy compound having a moiety represented by general formula (1) as a part of its structure, and a dihydroxy compound (b) of an alicyclic hydrocarbon; and an aromatic polycarbonate resin (B). The proportion of the dihydroxy compound (b) of the alicyclic hydrocarbon in the polycarbonate resin (A) is 35 mol% or more. (The case where the moiety represented by the general formula (1) is a part of -CH-O-H is excluded.)

Description

  The present invention relates to a polycarbonate resin composition excellent in weather resistance, transparency, hue, heat resistance, thermal stability, moldability, and mechanical strength, and a molded article thereof.

Polycarbonate resins are generally composed of bisphenols as monomer components, taking advantage of transparency, heat resistance, mechanical strength, etc., and electrical / electronic parts, automotive parts, medical parts, building materials, films, sheets, bottles It is widely used as so-called engineering plastics in the fields of optical recording media and lenses.
However, conventional polycarbonate resins are limited in use outdoors or in the vicinity of lighting devices, because their hue, transparency, and mechanical strength deteriorate when used in places exposed to ultraviolet rays or visible light for a long time. . Further, when used as various molded products, there has been a problem that the releasability is poor at the time of melt molding and it is difficult to use it for a transparent material or an optical material.

In order to solve such problems, a method of adding a benzophenone ultraviolet absorber, a benzotriazole ultraviolet absorber, or a benzoxazine ultraviolet absorber to a polycarbonate resin is widely known (for example, Non-Patent Document 1).
However, when such an ultraviolet absorber is added, although the hue after UV irradiation is improved, the hue, heat resistance and transparency of the resin are deteriorated in the first place. There were problems such as contamination of the mold.

In addition, adding a hindered amine (HALS) light stabilizer to the polycarbonate resin is not practical because the polycarbonate resin is unstable to basic components such as alkalis at room temperature, and is subject to hydrolysis against HALS. It is widely known that there is no.
Since the bisphenol compound used in the conventional polycarbonate resin has a benzene ring structure, it absorbs a large amount of ultraviolet rays. This causes a deterioration in the light resistance of the polycarbonate resin. Therefore, an aliphatic dihydroxy compound having no benzene ring structure in the molecular skeleton. If a cyclic dihydroxy compound monomer unit having an ether bond in the molecule, such as a compound, an alicyclic dihydroxy compound, or isosorbide, is used, it is expected that light resistance is improved in principle. Among them, a polycarbonate resin using isosorbide obtained from biomass resources as a monomer is excellent in heat resistance and mechanical strength, so that many studies have been made in recent years (for example, Patent Documents 1 to 7). .

However, cyclic dihydroxy compounds having an ether bond in the molecule, such as the above aliphatic dihydroxy compounds, alicyclic dihydroxy compounds, and isosorbide, do not have phenolic hydroxyl groups, and thus are widely known as methods for producing polycarbonate resins using bisphenol A as a raw material. It is difficult to polymerize by the conventional interface method, and it is usually produced by a method called a transesterification method or a melting method. In this method, the dihydroxy compound and a carbonic acid diester such as diphenyl carbonate are transesterified at a high temperature of 200 ° C. or higher in the presence of a basic catalyst, and the polymerization proceeds by removing by-product phenol and the like out of the system, A polycarbonate resin is obtained. However, a polycarbonate resin obtained using a monomer having no phenolic hydroxyl group as described above is inferior in thermal stability to a polycarbonate resin obtained using a monomer having a phenolic hydroxyl group such as bisphenol A. In addition, there is a problem that coloring occurs during polymerization or molding that is exposed to high temperatures, and as a result, ultraviolet light and visible light are absorbed, resulting in deterioration of light resistance. In particular, when a monomer having an ether bond in the molecule, such as isosorbide, is used, the hue is remarkably deteriorated and a great improvement has been demanded. Furthermore, when it is used as various molded products, it is melt-molded at a high temperature. At that time, a material having good thermal stability and excellent moldability and mold release properties has been demanded.

In addition, a polycarbonate resin composition having an ether bond in the molecule such as isosorbide, isomannide, isoitide, etc. that does not have a benzene ring structure in the molecular skeleton, benzotriazole, benzophenone, It is widely known to add a cyanoacrylate system (Patent Document 8).
However, when such an ultraviolet absorber is added, there is a problem that the hue, heat resistance and transparency of the resin are deteriorated in the first place.

International Publication No. 04/111106 Pamphlet Japanese Patent Laid-Open No. 2006-232897 JP 2006-28441 A JP 2008-24919 A JP 2009-91404 A JP 2009-91417 A JP 2008-274007 A JP 2007-70391 A

Polycarbonate resin handbook (issued by Seiichi Honma, published by Nikkan Kogyo Shimbun, August 28, 1992)

  An object of the present invention is to provide a polycarbonate resin composition excellent in weather resistance, transparency, hue, heat resistance, thermal stability, moldability, and mechanical strength, and a molded product thereof, by solving the above-mentioned conventional problems. There is to do.

  As a result of intensive studies to solve the above-mentioned problems, the present inventor has a structural unit (a) derived from a dihydroxy compound having a site represented by the following general formula (1) in a part of the structure and an alicyclic ring. A polycarbonate resin composition (X) comprising a polycarbonate resin (A) containing a dihydroxy compound (b) of the formula hydrocarbon and an aromatic polycarbonate resin (B), the fat occupying in the polycarbonate resin (A) The polycarbonate resin composition in which the dihydroxy compound (b) of the cyclic hydrocarbon is 35 mol% or more has not only excellent light resistance, but also excellent transparency, hue, heat resistance, thermal stability, moldability, and It has been found that it has mechanical strength, and the present invention has been reached.

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)
That is, the gist of the present invention resides in the following [1] to [9].
[1] A polycarbonate resin (A) containing a structural unit (a) derived from a dihydroxy compound having a site represented by the following general formula (1) as a part of the structure and an alicyclic hydrocarbon dihydroxy compound (b) ) And an aromatic polycarbonate resin (B), the alicyclic hydrocarbon dihydroxy compound (b) in the polycarbonate resin (A) being 35 mol% or more A polycarbonate resin composition characterized by that.

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)
[2] A sunshine carbon arc is applied to a molded body (thickness 3 mm) molded from the polycarbonate resin composition in an environment where the black panel temperature is 63 ° C., the relative humidity is 50%, and the rainfall spraying time is 12 minutes per hour. The total light transmittance is 85% or more after 500 hours of irradiation treatment at a discharge voltage of 50 V and a discharge current of 60 A, and the difference in yellow index (YI) values before and after the irradiation treatment is 10 or less. The polycarbonate resin composition according to [1], which is characterized.
[3] Notched Charpy impact strength measured in accordance with ISO 179 is 10 kJ / m ²
It is the above, The polycarbonate resin composition as described in [1] or [2] characterized by the above-mentioned. [4] The dihydroxy compound having a part represented by the following general formula (1) in a part of the structure is a dihydroxy compound represented by the following general formula (2): 3]. The polycarbonate resin composition according to any one of [3].

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)

[5] The composition further includes 0.0001 part by weight or more and 1 part by weight or less of an ultraviolet absorber with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B). The polycarbonate resin composition according to any one of [1] to [4]. [6] The composition further comprises 0.001 part by weight or more and 1 part by weight or less of a hindered amine light stabilizer with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B). The polycarbonate resin composition according to any one of [1] to [5].
[7] An antioxidant is contained in an amount of 0.0001 to 1 part by weight with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) [1] ] To the polycarbonate resin composition according to any one of [6].
[8] The composition further comprises 0.0001 part by weight or more and 2 parts by weight or less of a release agent with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B). The polycarbonate resin composition according to any one of [1] to [7].
[9] A polycarbonate resin molded article obtained by molding the polycarbonate resin composition according to any one of [1] to [8].

ADVANTAGE OF THE INVENTION According to this invention, the polycarbonate resin composition excellent in a weather resistance, transparency, a hue, heat resistance, heat stability, a moldability, and mechanical strength and its molded article can be provided.

DESCRIPTION OF EMBODIMENTS Hereinafter, embodiments of the present invention will be described in detail. However, the description of the constituent elements described below is an example (representative example) of an embodiment of the present invention. It is not limited to the contents.
<Polycarbonate resin (A)>
The polycarbonate resin (A) used in the present invention is composed of a dihydroxy compound having a part represented by the following general formula (1) in a part of the structure (hereinafter, sometimes simply referred to as “dihydroxy compound”) and an alicyclic carbonization. It can be obtained by polycondensation by a transesterification reaction using a dihydroxy compound containing hydrogen dihydroxy compound (b) and a carbonic acid diester as raw materials. That is, the polycarbonate resin (A) used in the present invention contains a structural unit (a) derived from a dihydroxy compound having a site represented by the following general formula (1) and an alicyclic hydrocarbon dihydroxy compound (b). .

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)
<Dihydroxy compound>
The dihydroxy compound used in the present invention includes a structural unit (a) derived from a dihydroxy compound having a site represented by the general formula (1) in a part of the structure, and a dihydroxy compound (b) of an alicyclic hydrocarbon. If it contains, it will not specifically limit. Specific examples of the dihydroxy compound containing the structural unit (a) derived from the dihydroxy compound having a site represented by the general formula (1) in a part of the structure include diethylene glycol, triethylene glycol, tetraethylene glycol, and the like. Oxyalkylene glycols, 9,9-bis (4- (2-hydroxyethoxy) phenyl) fluorene, 9,9-bis (4- (2-hydroxyethoxy) -3-methylphenyl) fluorene, 9,9- Bis (4- (2-hydroxyethoxy) -3-isopropylphenyl) fluorene, 9,9-bis (4- (2-hydroxyethoxy) -3-isobutylphenyl) fluorene, 9,9-bis (4- (2 -Hydroxyethoxy) -3-tert-butylphenyl) fluorene, 9,9-bis (4- (2- Droxyethoxy) -3-cyclohexylphenyl) fluorene, 9,9-bis (4- (2-hydroxyethoxy) -3-phenylphenyl) fluorene, 9,9-bis (4- (2-hydroxyethoxy) -3 , 5-dimethylphenyl) fluorene, 9,9-bis (4- (2-hydroxyethoxy) -3-tert-butyl-6-methylphenyl) fluorene 9,9-bis (4- (3-hydroxy-2, 2-dimethylpropoxy) phenyl) fluorene and the like, which are represented by compounds having an aromatic group in the side chain and an ether group bonded to the aromatic group in the main chain, and dihydroxy compounds represented by the following general formula (2) Anhydrosugar alcohols, and compounds having a cyclic ether structure such as spiroglycol represented by the following general formula (3) are mentioned. From the viewpoint of handling, reactivity during polymerization, and hue of the polycarbonate resin (A) to be obtained, diethylene glycol and triethylene glycol are preferable. From the viewpoint of heat resistance, the dihydroxy compound represented by the following general formula (2) An anhydrosugar alcohol represented by the formula (1) and a compound having a cyclic ether structure represented by the following general formula (3) are preferred.

  These may be used alone or in combination of two or more depending on the required performance of the polycarbonate resin (A) to be obtained.

Examples of the dihydroxy compound represented by the general formula (2) include isosorbide, isomannide and isoidet which are in a stereoisomeric relationship, and these may be used alone or in combination of two or more. It may be used.
Among these dihydroxy compounds, it is preferable to use a dihydroxy compound having no aromatic ring structure from the viewpoint of the light resistance of the polycarbonate resin (A). Among them, various kinds that are abundant and easily available as plant-derived resources are used. Isosorbide obtained by dehydrating condensation of sorbitol produced from starch is most preferable from the viewpoints of availability and production, light resistance, optical properties, moldability, heat resistance, and carbon neutral.

  The alicyclic hydrocarbon dihydroxy compound (b) is a compound having a cyclic structure hydrocarbon skeleton and two hydroxy groups, and the hydroxy group may be directly bonded to the cyclic structure or via a substituent. And may be bonded to a ring structure. The cyclic structure may be monocyclic or polycyclic. Specifically, hexanediols such as 1,2-cyclohexanediol, 1,3-cyclohexanediol, 1,4-cyclohexanediol, 2-methyl-1,4-cyclohexanediol, 4-cyclohexene-1,2- Cyclohexenediols such as diol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, cyclohexanedimethanol such as 1,4-cyclohexanedimethanol, 4-cyclohexene-1,2-diol Such as cyclohexene dimethanol, 2,3-norbornane dimethanol, norbornane dimethanol such as 2,5-norbornane dimethanol, tricyclodecane dimethanol, pentacyclopentadecane dimethanol, 1,3-adamantanediol, 2, 2-Adamantane All, and the like. Of these, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, and 1,4-cyclohexanedimethanol are preferred.

By using a dihydroxy compound containing a structural unit (a) derived from a dihydroxy compound having a site represented by the general formula (1) as a part of the structure and a dihydroxy compound (b) of an alicyclic hydrocarbon, It is also possible to obtain the effects of improving the flexibility, heat resistance, moldability and the like of the polycarbonate resin (A). Furthermore, the alicyclic hydrocarbon dihydroxy compound ( When the ratio of b) is a predetermined amount or more, it becomes possible to obtain a polycarbonate resin composition excellent in weather resistance, hue and mechanical strength. The proportion of the alicyclic hydrocarbon dihydroxy compound (b) in the polycarbonate resin (A) is usually 35 mol% or more, preferably 40 mol% or more, more preferably 50 mol% or more, and particularly preferably 55 mol% or more. On the other hand, it is preferably 90 mol% or less, more preferably 80 mol% or less, and particularly preferably 70 mol% or less.

  The dihydroxy compound used in the present invention may contain a stabilizer such as a reducing agent, antioxidant, oxygen scavenger, light stabilizer, antacid, pH stabilizer, heat stabilizer, etc. Since the dihydroxy compound used in the invention is easily altered, it is preferable to include a basic stabilizer. Basic stabilizers include Group 1 or Group 2 metal hydroxides, carbonates, phosphates, phosphites, hypophosphites in the Long Periodic Periodic Table (Nomenclature of Inorganic Chemistry IUPAC Recommendations 2005). Salts, borates, fatty acid salts, tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, trimethylethylammonium hydroxide, trimethylbenzylammonium hydroxide, trimethylphenylammonium hydroxide, Triethylmethylammonium hydroxide, triethylbenzylammonium hydroxide, triethylphenylammonium hydroxide, tributylbenzylammonium hydroxide, tributylphenylan Basic ammonium compounds such as nium hydroxide, tetraphenylammonium hydroxide, benzyltriphenylammonium hydroxide, methyltriphenylammonium hydroxide, butyltriphenylammonium hydroxide, 4-aminopyridine, 2-aminopyridine, N, N -Dimethyl-4-aminopyridine, 4-diethylaminopyridine, 2-hydroxypyridine, 2-methoxypyridine, 4-methoxypyridine, 2-dimethylaminoimidazole, 2-methoxyimidazole, imidazole, 2-mercaptoimidazole, 2-methylimidazole And amine compounds such as aminoquinoline. Of these, sodium or potassium phosphates and phosphites are preferred, and disodium hydrogen phosphate and disodium hydrogen phosphite are particularly preferred because of their effects and ease of distillation removal described below.

  Although there is no restriction | limiting in particular in content in the dihydroxy compound used by this invention of these basic stabilizers, if there is too little, the effect which prevents the quality change of the dihydroxy compound used by this invention may not be acquired, and if too much, Since it may cause modification of the dihydroxy compound used in the present invention, it is usually 0.0001% by weight to 1% by weight, preferably 0.001% by weight to 0.1% by weight, based on the dihydroxy compound used in the present invention. It is.

  In addition, when the dihydroxy compound used in the present invention containing these basic stabilizers is used as a raw material for producing polycarbonate resin, the basic stabilizer itself becomes a polymerization catalyst, and it becomes difficult to control the polymerization rate and quality. In order to deteriorate the initial hue and consequently deteriorate the light resistance of the molded product, it is preferable to remove the basic stabilizer by ion exchange resin or distillation before using it as a raw material for producing the polycarbonate resin.

  When the dihydroxy compound used in the present invention has a cyclic ether structure such as isosorbide, it is easily oxidized by oxygen. Therefore, during storage and production, in order to prevent decomposition by oxygen, water should not be mixed, It is important to use an oxygen scavenger or handle under a nitrogen atmosphere. When isosorbide is oxidized, decomposition products such as formic acid may be generated. For example, when isosorbide containing these decomposition products is used as a polycarbonate resin production raw material, the resulting polycarbonate resin may be colored, and not only the physical properties may be significantly degraded, but also the polymerization reaction may be affected. In some cases, a high molecular weight polymer cannot be obtained.

  In order to obtain the dihydroxy compound used in the present invention which does not contain the above oxidative decomposition product, and in order to remove the aforementioned basic stabilizer, it is preferable to carry out distillation purification. The distillation in this case may be simple distillation or continuous distillation, and is not particularly limited. As distillation conditions, it is preferable to carry out distillation under reduced pressure in an inert gas atmosphere such as argon or nitrogen. In order to suppress thermal denaturation, it is 250 ° C. or lower, preferably 200 ° C. or lower, particularly 180 °. It is preferable to carry out under the conditions of ℃ or less.

By such distillation purification, the dihydroxy compound used in the present invention is adjusted to a formic acid content in the dihydroxy compound used in the present invention of 20 ppm by weight or less, preferably 10 ppm by weight or less, particularly preferably 5 ppm by weight or less. When a dihydroxy compound containing is used as a raw material for producing a polycarbonate resin, it is possible to produce a polycarbonate resin (A) excellent in hue and thermal stability without impairing polymerization reactivity. The formic acid content is measured by ion chromatography.
<Carbonated diester>
The polycarbonate resin (A) used in the present invention can be obtained by polycondensation by a transesterification reaction using the above-mentioned dihydroxy compound containing the dihydroxy compound used in the present invention and a carbonic acid diester as raw materials.

As a carbonic acid diester used, what is normally represented by following General formula (4) is mentioned. These carbonic acid diesters may be used alone or in combination of two or more.

(In the above general formula (4), A ¹ and A ² are each independently a substituted or unsubstituted aliphatic group having 1 to 18 carbon atoms, or a substituted or unsubstituted aromatic group. Examples of the carbonic acid diester represented by the general formula (4) include substituted diphenyl carbonates such as diphenyl carbonate and ditolyl carbonate, dimethyl carbonate, diethyl carbonate, and di-t-butyl carbonate. Is diphenyl carbonate or substituted diphenyl carbonate, particularly preferably diphenyl carbonate. Carbonic acid diesters may contain impurities such as chloride ions, which may hinder the polymerization reaction or worsen the hue of the resulting polycarbonate resin. It is preferable to use what was done.

<Transesterification reaction catalyst>
The polycarbonate resin (A) used in the present invention produces a polycarbonate resin by transesterifying the dihydroxy compound containing the dihydroxy compound used in the present invention and the carbonic acid diester represented by the general formula (4) as described above. More specifically, it can be obtained by transesterification and removing by-product monohydroxy compounds and the like out of the system. In this case, polycondensation is usually carried out by transesterification in the presence of a transesterification catalyst.

The transesterification catalyst that can be used in the production of the polycarbonate resin (A) used in the present invention (hereinafter sometimes simply referred to as a catalyst or a polymerization catalyst) has an effect on the light transmittance at a wavelength of 350 nm and the yellow index value. Can give.
As the catalyst used, as long as the light resistance, transparency, hue, heat resistance, thermal stability, and mechanical strength of the manufactured polycarbonate resin (A) can satisfy the light resistance, Although not limited, a metal compound, a basic boron compound, a basic phosphorus compound, and a basic ammonium of Group 1 or 2 (hereinafter, simply referred to as “Group 1” or “Group 2”) in the long-period periodic table Examples thereof include basic compounds such as compounds and amine compounds. Preferably, Group 1 metal compounds and / or Group 2 metal compounds are used.

It is possible to use a basic compound such as a basic boron compound, a basic phosphorus compound, a basic ammonium compound, and an amine compound in combination with the Group 1 metal compound and / or the Group 2 metal compound. It is particularly preferred to use only Group 1 metal compounds and / or Group 2 metal compounds.
In addition, the group 1 metal compound and / or the group 2 metal compound are usually used in the form of a hydroxide or a salt such as a carbonate, a carboxylate, or a phenol salt. From the viewpoint of easiness, a hydroxide, carbonate, and acetate are preferable, and acetate is preferable from the viewpoint of hue and polymerization activity.

  Examples of the Group 1 metal compound include sodium hydroxide, potassium hydroxide, lithium hydroxide, cesium hydroxide, sodium hydrogen carbonate, potassium hydrogen carbonate, lithium hydrogen carbonate, cesium hydrogen carbonate, sodium carbonate, potassium carbonate, lithium carbonate, Cesium carbonate, sodium acetate, potassium acetate, lithium acetate, cesium acetate, sodium stearate, potassium stearate, lithium stearate, cesium stearate, sodium borohydride, potassium borohydride, lithium borohydride, cesium borohydride , Sodium borohydride, potassium borohydride, lithium phenide boron, cesium phenide boron, sodium benzoate, potassium benzoate, lithium benzoate, cesium benzoate, 2 sodium hydrogen phosphate 2 potassium potassium phosphate, 2 lithium hydrogen phosphate, 2 cesium hydrogen phosphate, 2 sodium phenyl phosphate, 2 potassium phenyl phosphate, 2 lithium phenyl phosphate, 2 cesium phenyl phosphate, sodium, potassium, lithium, Examples include cesium alcoholate, phenolate, disodium salt of bisphenol A, 2 potassium salt, 2 lithium salt, 2 cesium salt, etc. Among them, lithium compounds are preferable.

  Examples of the Group 2 metal compound include calcium hydroxide, barium hydroxide, magnesium hydroxide, strontium hydroxide, calcium hydrogen carbonate, barium hydrogen carbonate, magnesium hydrogen carbonate, strontium hydrogen carbonate, calcium carbonate, barium carbonate, magnesium carbonate, Examples include strontium carbonate, calcium acetate, barium acetate, magnesium acetate, strontium acetate, calcium stearate, barium stearate, magnesium stearate, strontium stearate, etc. From the viewpoint of the hue of the polycarbonate resin obtained, a magnesium compound and / or a calcium compound is more preferable, and a calcium compound is most preferable.

  Examples of the basic boron compound include tetramethyl boron, tetraethyl boron, tetrapropyl boron, tetrabutyl boron, trimethylethyl boron, trimethylbenzyl boron, trimethylphenyl boron, triethylmethyl boron, triethylbenzyl boron, triethylphenyl boron, tributylbenzyl. Examples include sodium, potassium, lithium, calcium, barium, magnesium, or strontium salts such as boron, tributylphenylboron, tetraphenylboron, benzyltriphenylboron, methyltriphenylboron, butyltriphenylboron, etc. It is done.

Examples of the basic phosphorus compound include triethylphosphine, tri-n-propylphosphine, triisopropylphosphine, tri-n-butylphosphine, triphenylphosphine, tributylphosphine, and quaternary phosphonium salts.
Examples of the basic ammonium compound include tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, trimethylethylammonium hydroxide, trimethylbenzylammonium hydroxide, trimethylphenylammonium hydroxide, Triethylmethylammonium hydroxide, triethylbenzylammonium hydroxide, triethylphenylammonium hydroxide, tributylbenzylammonium hydroxide, tributylphenylammonium hydroxide, tetraphenylammonium hydroxide, benzyltriphenylammonium hydroxide, methyltriphenylammonium hydroxide Sid, butyl triphenyl ammonium hydroxide, and the like.

  Examples of the amine compound include 4-aminopyridine, 2-aminopyridine, N, N-dimethyl-4-aminopyridine, 4-diethylaminopyridine, 2-hydroxypyridine, 2-methoxypyridine, 4-methoxypyridine, 2 -Dimethylaminoimidazole, 2-methoxyimidazole, imidazole, 2-mercaptoimidazole, 2-methylimidazole, aminoquinoline and the like.

  The amount of the polymerization catalyst used is preferably 0.1 μmol to 300 μmol, more preferably 0.5 μmol to μmol 100 μmol per 1 mol of all dihydroxy compounds used in the polymerization, among which lithium and the second group in the long-period type periodic table. When a compound containing at least one metal selected from the group is used, particularly when a magnesium compound and / or a calcium compound is used, the metal amount is preferably 0.1 μmol or more per 1 mol of the total dihydroxy compound. More preferably 0.5 μmol or more, particularly preferably 0.7 μmol or more. The upper limit is preferably 20 μmol, more preferably 10 μmol, particularly preferably 3 μmol, most preferably 1.5 μmol, and most preferably 1.0 μmol.

  When the amount of the catalyst is too small, the polymerization rate is slowed down. As a result, when trying to obtain a polycarbonate resin (A) having a desired molecular weight, the polymerization temperature must be increased, and the resulting polycarbonate resin (A) The hue and light resistance are deteriorated, the unreacted raw material is volatilized during the polymerization, and the molar ratio between the dihydroxy compound containing the dihydroxy compound used in the present invention and the carbonic acid diester represented by the general formula (4) collapses. May not reach the molecular weight of. On the other hand, when there is too much usage-amount of a polymerization catalyst, the hue of the polycarbonate resin (A) obtained will be deteriorated and the light resistance of a polycarbonate resin (A) may deteriorate.

  Furthermore, when the polycarbonate resin (A) used in the present invention is produced using a substituted diphenyl carbonate such as diphenyl carbonate or ditolyl carbonate as the carbonic acid diester represented by the general formula (4), phenol and substituted phenol are used. By-product and remaining in the polycarbonate resin (A) are inevitable, but not only phenol and substituted phenol also have an aromatic ring, which absorbs ultraviolet rays and may cause deterioration of light resistance, May cause odor during molding. The polycarbonate resin (A) contains an aromatic monohydroxy compound having an aromatic ring such as by-product phenol of 1000 ppm by weight or more after a normal batch reaction, from the viewpoint of light resistance and odor reduction. Is preferably 700 ppm by weight or less, more preferably 500 ppm by weight or less, and particularly preferably 300 ppm by weight or less, using a horizontal reactor excellent in devolatilization performance or an extruder with a vacuum vent. However, it is difficult to remove completely industrially, and the lower limit of the content of the aromatic monohydroxy compound is usually 1 ppm by weight.

These aromatic monohydroxy compounds may naturally have a substituent depending on the raw material used, and may have, for example, an alkyl group having 5 or less carbon atoms.
Further, Group 1 metals, especially sodium, potassium, and cesium, especially lithium, sodium, potassium, and cesium, may have an adverse effect on the hue when contained in the polycarbonate resin (A) in large quantities. The total amount of these in the polycarbonate resin (A) is usually 1 ppm by weight or less, preferably 0.8 ppm by weight or less as the amount of metal, because it may be mixed not only from the catalyst to be used, but also from raw materials and reactors. More preferably, it is 0.7 ppm by weight or less.

The amount of metal in the polycarbonate resin (A) should be measured using a method such as atomic emission, atomic absorption, or inductively coupled plasma (ICP) after recovering the metal in the polycarbonate resin by a method such as wet ashing. I can do it.
<Polycarbonate resin (A) production method>
The polycarbonate resin (A) used in the present invention is obtained by polycondensation of the dihydroxy compound containing the dihydroxy compound used in the present invention and the carbonic acid diester of the general formula (4) by a transesterification reaction. The compound and the carbonic acid diester are preferably mixed uniformly before the transesterification reaction.

  The mixing temperature is usually 80 ° C. or higher, preferably 90 ° C. or higher, and the upper limit is usually 250 ° C. or lower, preferably 200 ° C. or lower, more preferably 150 ° C. or lower. Among these, 100 ° C. or higher and 120 ° C. or lower is preferable. If the mixing temperature is too low, the dissolution rate may be slow or the solubility may be insufficient, often resulting in problems such as solidification. If the mixing temperature is too high, the dihydroxy compound may be thermally deteriorated, resulting in a deterioration of the hue of the polycarbonate resin thus obtained, which may adversely affect light resistance.

  The operation of mixing the dihydroxy compound containing the dihydroxy compound used in the present invention, which is the raw material of the polycarbonate resin (A) used in the present invention, and the carbonic acid diester represented by the general formula (4) is performed at an oxygen concentration of 10 vol% or less, Is preferably carried out in an atmosphere of 0.0001 vol% to 10 vol%, particularly 0.0001 vol% to 5 vol%, particularly 0.0001 vol% to 1 vol%, from the viewpoint of preventing hue deterioration.

In order to obtain the polycarbonate resin (A) used in the present invention, the carbonic acid diester represented by the general formula (4) is 0.90 to the dihydroxy compound including the dihydroxy compound used in the present invention used for the reaction. The molar ratio is preferably 1.20, more preferably 0.95 to 1.10.
When this molar ratio is decreased, the terminal hydroxyl group of the produced polycarbonate resin is increased, the thermal stability of the polymer is deteriorated, coloring occurs during molding, the rate of transesterification reaction is reduced, and the desired high molecular weight. The body may not be obtained.

Moreover, when this molar ratio becomes large, the speed | rate of transesterification may fall or manufacture of polycarbonate resin (A) of the desired molecular weight may become difficult. The decrease in the transesterification reaction rate may increase the heat history during the polymerization reaction, and may deteriorate the hue and light resistance of the resulting polycarbonate resin.
Furthermore, when the molar ratio of the carbonic acid diester represented by the general formula (4) is increased with respect to the dihydroxy compound including the dihydroxy compound used in the present invention, the amount of residual carbonic acid diester in the obtained polycarbonate resin (A) is increased. They increase, and these may absorb the ultraviolet rays and deteriorate the light resistance of the polycarbonate resin, which is not preferable. The concentration of the carbonic acid diester remaining in the polycarbonate resin (A) used in the present invention is preferably 200 ppm by weight or less, more preferably 100 ppm by weight or less, particularly preferably 60 ppm by weight or less, and particularly preferably 30 ppm by weight or less. . Actually, the polycarbonate resin (A) may contain an unreacted carbonic acid diester, and the lower limit of the concentration is usually 1 ppm by weight.

In the present invention, the method of polycondensing a dihydroxy compound and a carbonic acid diester is usually carried out in multiple stages using a plurality of reactors in the presence of the above-mentioned catalyst. The type of reaction may be any of batch type, continuous type, or a combination of batch type and continuous type.
In the initial stage of polymerization, it is preferable to obtain a prepolymer at a relatively low temperature and low vacuum, and in the latter stage of polymerization, it is preferable to increase the molecular weight to a predetermined value at a relatively high temperature and high vacuum, but the jacket temperature at each molecular weight stage. Appropriate selection of the internal temperature and pressure in the reaction system is important from the viewpoints of hue and light resistance. For example, if either the temperature or the pressure is changed too quickly before the polymerization reaction reaches a predetermined value, the unreacted monomer will be distilled, causing the molar ratio of the dihydroxy compound and the carbonic acid diester to change, resulting in a decrease in the polymerization rate. Or a polymer having a predetermined molecular weight or terminal group cannot be obtained, and as a result, the object of the present invention may not be achieved.

  Furthermore, it is effective to use a reflux condenser for the polymerization reactor in order to suppress the amount of the monomer to be distilled off, and the effect is particularly great in a reactor at the initial stage of polymerization where there are many unreacted monomer components. The temperature of the refrigerant introduced into the reflux cooler can be appropriately selected according to the monomer used. Usually, the temperature of the refrigerant introduced into the reflux cooler is 45 ° C. to 180 ° C. at the inlet of the reflux cooler. Preferably, it is 80 degreeC-150 degreeC, Most preferably, it is 100 degreeC-130 degreeC. If the temperature of the refrigerant introduced into the reflux condenser is too high, the reflux amount is reduced and the effect is reduced. If it is too low, the distillation efficiency of the monohydroxy compound to be originally distilled tends to be reduced. As the refrigerant, hot water, steam, heat medium oil or the like is used, and steam or heat medium oil is preferable.

In order to maintain the polymerization rate appropriately and suppress the distillation of the monomer, but not to impair the hue, thermal stability, light resistance, etc. of the final polycarbonate resin, Selection is important.
The polycarbonate resin (A) used in the present invention is preferably produced by polymerizing in a plurality of stages using a plurality of reactors using a catalyst. The reason for carrying out the polymerization in a plurality of reactors is a polymerization reaction. In the initial stage, since there are many monomers contained in the reaction solution, it is important to suppress the volatilization of the monomers while maintaining the necessary polymerization rate. In the latter stage of the polymerization reaction, the equilibrium is shifted to the polymerization side. Therefore, it is important to sufficiently distill off the monohydroxy compound produced as a by-product. Thus, in order to set different polymerization reaction conditions, it is preferable from the viewpoint of production efficiency to use a plurality of polymerization reactors arranged in series.

As described above, the number of reactors used in the method of the present invention may be at least two or more. However, from the viewpoint of production efficiency and the like, three or more, preferably 3 to 5, particularly preferably 4 are used. One.
In the present invention, if there are two or more reactors, a plurality of reaction stages having different conditions may be provided in the reactor, or the temperature and pressure may be continuously changed.

In the present invention, the polymerization catalyst can be added to the raw material preparation tank, the raw material storage tank, or can be added directly to the polymerization tank. From the viewpoint of supply stability and polymerization control, the polymerization catalyst is supplied to the polymerization tank. A catalyst supply line is installed in the middle of the raw material line before being fed, and preferably supplied as an aqueous solution.
If the temperature of the polymerization reaction is too low, the productivity is lowered and the thermal history of the product is increased. If it is too high, not only the monomer is volatilized but also decomposition and coloring of the polycarbonate resin may be promoted.

Specifically, the reaction in the first stage is performed at 140 to 270 ° C., preferably 180 to 240 ° C., more preferably 200 to 230 ° C. as the maximum internal temperature of the polymerization reactor. 1 kPa, preferably 70 kPa to 5 kPa, more preferably 30 kPa to 10 k
The reaction is carried out under a pressure of Pa (absolute pressure) for 0.1 hours to 10 hours, preferably 0.5 hours to 3 hours, while distilling off the generated monohydroxy compound to the outside of the reaction system.

  In the second and subsequent stages, the pressure in the reaction system is gradually reduced from the pressure in the first stage, and the monohydroxy compound that is subsequently generated is removed from the reaction system. 200 Pa or less, maximum internal temperature of 210 ° C. to 270 ° C., preferably 220 ° C. to 250 ° C., usually 0.1 hour to 10 hours, preferably 1 hour to 6 hours, particularly preferably 0.5 hour. Perform for ~ 3 hours.

  In particular, in order to obtain a polycarbonate resin (A) having good hue and light resistance by suppressing coloring and thermal deterioration of the polycarbonate resin (A), the maximum internal temperature in all reaction stages is less than 250 ° C, particularly from 225 ° C to It is preferable that it is 245 degreeC. In order to suppress the decrease in the polymerization rate in the latter half of the polymerization reaction and minimize degradation due to thermal history, it is necessary to use a horizontal reactor with excellent plug flow and interface renewability at the final stage of polymerization. preferable.

In order to obtain a polycarbonate resin (A) having a predetermined molecular weight, if the polymerization temperature is increased and the polymerization time is too long, the ultraviolet transmittance decreases and the YI value tends to increase.
The monohydroxy compound produced as a by-product is preferably reused as a raw material for diphenyl carbonate, bisphenol A, etc. after purification as necessary from the viewpoint of effective utilization of resources.
The polycarbonate resin (A) used in the present invention is usually cooled and solidified after polycondensation as described above, and pelletized with a rotary cutter or the like.

  The method of pelletization is not limited, but it is extracted from the final polymerization reactor in a molten state, cooled and solidified in the form of a strand, and pelletized, or from the final polymerization reactor in a molten state, uniaxial or biaxial extrusion. The resin is supplied to the machine, melt-extruded, cooled and solidified into pellets, or extracted from the final polymerization reactor in a molten state, cooled and solidified in the form of strands, once pelletized, and then uniaxially again Alternatively, a method may be mentioned in which resin is supplied to a biaxial extruder, melt-extruded, cooled and solidified, and pelletized.

At that time, in the extruder, the residual monomer under reduced pressure devolatilization, and generally known heat stabilizers, neutralizers, UV absorbers, mold release agents, colorants, antistatic agents, lubricants, lubricants, A plasticizer, a compatibilizer, a flame retardant, etc. can be added and kneaded.
The melt kneading temperature in the extruder depends on the glass transition temperature and molecular weight of the polycarbonate resin (A), but is usually 150 ° C to 300 ° C, preferably 200 ° C to 270 ° C, more preferably 230 ° C to 260 ° C. is there. When the melt kneading temperature is lower than 150 ° C., the melt viscosity of the polycarbonate resin (A) is high, the load on the extruder is increased, and the productivity is lowered. When the temperature is higher than 300 ° C., the thermal deterioration of the polycarbonate becomes severe, resulting in a decrease in mechanical strength due to a decrease in molecular weight, coloring, and gas generation.

  When the polycarbonate resin (A) used in the present invention is produced, it is desirable to install a filter in order to prevent foreign substances from entering. The filter installation position is preferably on the downstream side of the extruder, and the foreign matter removal size (opening) of the filter is preferably 100 μm or less as the filtration accuracy for 99% removal. In particular, in the case of disagreeing with the entry of minute foreign matters for film use etc., it is preferably 40 μm or less, more preferably 10 μm or less.

Extrusion of the polycarbonate resin (A) used in the present invention is preferably a clean room having a higher degree of cleanliness than Class 7 as defined in JIS B 9920 (2002), more preferably a clean room in order to prevent foreign matter from being mixed after extrusion. It is desirable to implement in.
Moreover, when cooling the extruded polycarbonate resin into chips, it is preferable to use a cooling method such as air cooling or water cooling. As the air used for air cooling, it is desirable to use air from which foreign substances in the air have been removed in advance with a hepa filter or the like to prevent reattachment of foreign substances in the air. When water cooling is used, it is desirable to use water from which metal in water has been removed with an ion exchange resin or the like, and foreign matter in water has been removed with a filter. The opening of the filter to be used is preferably 10 μm to 0.45 μm as 99% removal filtration accuracy.

The molecular weight of the polycarbonate resin (A) used in the present invention thus obtained can be represented by a reduced viscosity, and the reduced viscosity is usually 0.30 dL / g or more, preferably 0.35 dL / g or more. The upper limit of the reduced viscosity is more preferably 1.20 dL / g or less and 1.00 dL / g or less, and still more preferably 0.80 dL / g or less.
If the reduced viscosity of the polycarbonate resin (A) is too low, the mechanical strength of the molded product may be small. If it is too large, the fluidity at the time of molding tends to decrease and the productivity and moldability tend to decrease. .

The reduced viscosity is measured using a Ubbelohde viscometer at a temperature of 20.0 ° C. ± 0.1 ° C., precisely prepared at a polycarbonate concentration of 0.6 g / dL using methylene chloride as a solvent.
Further, the lower limit of the concentration of the terminal group represented by the following general formula (5) in the polycarbonate resin (A) used in the present invention is usually 20 μeq / g, preferably 40 μeq / g, particularly preferably 50 μeq / g. The upper limit is usually 160 μeq / g, preferably 140 μeq / g, particularly preferably 100 μeq / g.

If the concentration of the terminal group represented by the following general formula (5) is too high, even if the hue at the time of polymerization or at the time of molding is good, the hue after UV exposure may be deteriorated. Thermal stability may be reduced.
In order to control the concentration of the terminal group represented by the following general formula (5), the molar ratio of the dihydroxy compound containing the dihydroxy compound used in the present invention as a raw material and the carbonic acid diester represented by the general formula (4) is set. In addition to controlling, a method for controlling the kind and amount of the catalyst at the time of the transesterification reaction, the polymerization pressure and the polymerization temperature can be used.

In addition, when the number of moles of H bonded to the aromatic ring in the polycarbonate resin (A) used in the present invention is (C) and the number of moles of H bonded to other than the aromatic ring is (D), it is bonded to the aromatic ring. The ratio of the number of moles of H to the number of moles of total H is expressed by C / (C + D). However, as described above, there is a possibility that an aromatic ring having an ultraviolet absorbing ability affects the light resistance. Therefore, C / (C + D) is preferably 0.1 or less, more preferably 0.05 or less, particularly preferably 0.02 or less, and preferably 0.01 or less. C / (C + D) can be quantified by ¹ H-NMR.

The polycarbonate resin composition of the present invention can be formed into a molded product by a generally known method such as an injection molding method, an extrusion molding method, or a compression molding method.
In addition, the polycarbonate resin (A) used in the present invention is, as necessary, a heat stabilizer, a neutralizer, an ultraviolet absorber, a release agent, a colorant, an antistatic agent, and a lubricant before performing various moldings. Additives such as lubricants, plasticizers, compatibilizers, and flame retardants can also be mixed with a tumbler, super mixer, floater, V-type blender, nauter mixer, Banbury mixer, extruder or the like.

The glass transition temperature of the polycarbonate resin (A) is preferably 75 ° C. or higher and 105 ° C. or lower, more preferably 80 ° C. or higher and 105 ° C. or lower, and 85 ° C. or higher and 105 ° C. or lower. preferable. By using the polycarbonate resin (A) within the range where the glass transition temperature is applied, a molded product having excellent heat resistance can be provided.
<Aromatic polycarbonate resin (B)>
The aromatic polycarbonate resin (B) used in the present invention is a polycarbonate resin in which structural units derived from a dihydroxy compound are connected by a carbonate bond, and has any conventionally known one as long as it has an aromatic ring in the structure. May also be used, and may include a structural unit derived from a dihydroxy compound having a site represented by the general formula (1). Preferably, among all structural units derived from a dihydroxy compound, a polycarbonate resin having the largest number of structural units derived from a dihydroxy compound having an aromatic ring, more preferably aromatic to all structural units derived from a dihydroxy compound. A polycarbonate resin having a structure derived from a dihydroxy compound having a ring of 50 mol% or more, more preferably 70 mol% or more, particularly preferably 90 mol% or more is used. However, when it contains a structural unit derived from a dihydroxy compound having a site represented by the general formula (1), a polycarbonate resin having a structure different from that of the polycarbonate resin (A) is used.
The aromatic polycarbonate resin (B) used in the present invention may be either a homopolymer or a copolymer. Moreover, the aromatic polycarbonate resin (B) may have a branched structure.

  More specifically, it is a polycarbonate resin having a repeating structure represented by the following general formula (6).

(In the general formula (6), Ar ¹ and Ar ² each independently represent an arylene group which may have a substituent, and X represents a single bond or a divalent group.)
The arylene group which may have a substituent is not particularly limited as long as it is an arylene group, but is preferably an arylene group having 3 or less aromatic rings, more preferably a phenylene group. is there. As the substituent that Ar ¹ and Ar ² may independently have, the alkyl group having 1 to 10 carbon atoms which may have a substituent and the carbon number which may have a substituent Examples thereof include an alkoxy group having 1 to 10 carbon atoms, a halogen group, a halogenated alkyl group having 1 to 10 carbon atoms, and an aromatic group having 6 to 20 carbon atoms which may have a substituent. Among these substituents, an alkyl group having 1 to 10 carbon atoms which may have a substituent or an aromatic group having 6 to 20 carbon atoms which may have a substituent is preferable, and more preferably. An alkyl group having 1 to 10 carbon atoms, particularly preferably a methyl group.

As the divalent group, an alkylene group having a chain structure having 1 to 6 carbon atoms which may have a substituent, an alkylidene group having a chain structure having 1 to 6 carbon atoms which may have a substituent, A C3-C6 cyclic structure alkylene group which may have a substituent, a C3-C6 cyclic structure alkylidene group which may have a substituent, -O-, -S-, -CO- or -SO ₂ - and the like. As the substituent that the alkylene group having a chain structure having 1 to 6 carbon atoms has, an aryl group is preferable, and a phenyl group is particularly preferable.

The structural unit derived from the dihydroxy compound constituting the aromatic polycarbonate resin (B) used in the present invention is obtained by removing a hydrogen atom from the hydroxyl group of the dihydroxy compound. Specific examples of the corresponding dihydroxy compound include the following.
4,4′-biphenol, 2,4′-biphenol, 3,3′-dimethyl-4,4′-dihydroxy-1,1′-biphenyl, 3,3′-dimethyl-2,4′-dihydroxy-1 , 1′-biphenyl, 3,3′-di- (t-butyl) -4,4′-dihydroxy-1,1′-biphenyl, 3,3 ′, 5,5′-tetramethyl-4,4 ′ -Dihydroxy-1,1'-biphenyl, 3,3 ', 5,5'-tetra- (t-butyl) -4,4'-dihydroxy-1,1'-biphenyl, 2,2', 3,3 ', 5,5'-Hexamethyl-4,4
Biphenyl compounds such as'-dihydroxy-1,1'-biphenyl.

Bis- (4-hydroxy-3,5-dimethylphenyl) methane, bis- (4-hydroxyphenyl) methane, bis- (4-hydroxy-3-methylphenyl) methane, 1,1-bis- (4-hydroxy) Phenyl) ethane, 1,1-bis- (4-hydroxyphenyl) propane, 2,2-bis- (4-hydroxyphenyl) propane, 2,2-bis- (4-hydroxy-3-methylphenyl) propane, 2,2-bis- (4-hydroxyphenyl) butane, 2,2-bis- (4-hydroxyphenyl) pentane, 2,2-bis- (4-hydroxyphenyl) -3-methylbutane, 2,2-bis -(4-hydroxyphenyl) hexane, 2,2-bis- (4-hydroxyphenyl) -4-methylpentane, 1,1-bis- (4-hydroxyphenyl) ) Cyclopentane, 1,1-bis- (4-hydroxyphenyl) cyclohexane, bis- (3-phenyl-4-hydroxyphenyl) methane, 1,1-bis- (3-phenyl-4-hydroxyphenyl) ethane, 1,1-bis- (3-phenyl-4-hydroxyphenyl) propane, 2,2-bis- (3-phenyl-4-hydroxyphenyl) propane, 1,1-bis- (4-hydroxy-3-methyl) Phenyl) ethane, 2,2-bis- (4-hydroxy-3-ethylphenyl) propane, 2,2-bis- (4-hydroxy-3-isopropylphenyl) propane, 2,2-bis- (4-hydroxy) -3-sec-butylphenyl) propane, 1,1-bis- (4-hydroxy-3,5-dimethylphenyl) ethane, 2,2-bis- (4- Droxy-3,5-dimethylphenyl) propane, 1,1-bis- (4-hydroxy-3,6-dimethylphenyl) ethane, bis- (4-hydroxy-2,3,5-trimethylphenyl) methane, , 1-bis- (4-hydroxy-2,3,5-trimethylphenyl) ethane, 2,2-bis- (4-hydroxy-2,3,5-trimethylphenyl) propane, bis- (4-hydroxy- 2,3,5-trimethylphenyl) phenylmethane, 1,1-bis- (4-hydroxy-2,3,5-trimethylphenyl) phenylethane, 1,1-bis- (4-hydroxy-2,3, 5-trimethylphenyl) cyclohexane, bis- (4-hydroxyphenyl) phenylmethane, 1,1-bis- (4-hydroxyphenyl) -1-phenylethane, 1 , 1-bis- (4-hydroxyphenyl) -1-phenylpropane, bis- (4-hydroxyphenyl) diphenylmethane, bis- (4-hydroxyphenyl) dibenzylmethane, 4,4 ′-[1,4-phenylene Bis (1-methylethylidene)] bis- [phenol], 4,4 ′-[1,4-phenylenebismethylene] bis- [phenol], 4,4 ′-[1,
4-phenylenebis (1-methylethylidene)] bis- [2,6-dimethylphenol],
4,4 '-[1,4-phenylene bismethylene] bis- [2,6-dimethylphenol], 4,4'-[1,4-phenylene bismethylene] bis- [2,3,6-trimethylphenol ], 4,4 '-[1,4-phenylenebis (1-methylethylidene)] bis- [2,3,6-
Trimethylphenol], 4,4 ′-[1,3-phenylenebis (1-methylethylidene)] bis- [2,3,6-trimethylphenol], 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy Diphenyl sulfone, 4,4′-dihydroxydiphenyl sulfide, 3,3 ′, 5,5′-tetramethyl-4,4′-dihydroxydiphenyl ether, 3,3 ′, 5,5′-tetramethyl-4,4 ′ -Dihydroxydiphenylsulfone, 3,3 ', 5,5'-tetramethyl-4,4'-dihydroxydiphenyl sulfide, phenolphthalein, 4,4'-[1,4-phenylenebis (1-methylvinylidene)]
Bisphenol, 4,4 ′-[1,4-phenylenebis (1-methylvinylidene)] bis [2-methylphenol], (2-hydroxyphenyl) (4-hydroxyphenyl) methane, (2-hydroxy-5- Methylphenyl) (4-hydroxy-3-methylphenyl) methane, 1,1- (2-hydroxyphenyl) (4-hydroxyphenyl) ethane, 2,2- (2-hydroxyphenyl) (4-hydroxyphenyl) propane Bisphenol compounds such as 1,1- (2-hydroxyphenyl) (4-hydroxyphenyl) propane.

Halogenated bisphenol compounds such as 2,2-bis (3,5-dibromo-4-hydroxyphenyl) propane and 2,2-bis (3,5-dichloro-4-hydroxyphenyl) propane.
Among these, preferred dihydroxy compounds are bis- (4-hydroxy-3,5-dimethylphenyl) methane, bis- (4-hydroxyphenyl) methane, bis- (4-hydroxy-3-methylphenyl) methane, 1 , 1-bis- (4-hydroxyphenyl) ethane, 2,2-bis- (4-hydroxyphenyl) propane, 2,2-bis- (4-hydroxy-3-methylphenyl) propane, 2,2-bis -(4-hydroxy-3,5-dimethylphenyl) propane, 1,1-bis- (4-hydroxyphenyl) cyclohexane, bis- (4-hydroxyphenyl) phenylmethane, 1,1-bis- (4-hydroxy) Phenyl) -1-phenylethane, 1,1-bis- (4-hydroxyphenyl) -1-phenylpropane, bis- (4-hydride) Examples thereof include bisphenol compounds in which phenols are linked by an alkylidene group, such as xylphenyl) diphenylmethane, 2-hydroxyphenyl (4-hydroxyphenyl) methane, and 2,2- (2-hydroxyphenyl) (4-hydroxyphenyl) propane. .

  Among these, in particular, bis- (4-hydroxyphenyl) methane, bis- (4-hydroxy-3-methylphenyl) methane, bis- (4-hydroxy-3,5-dimethylphenyl) methane, 2,2-bis -(4-hydroxyphenyl) propane, 2,2-bis- (4-hydroxy-3-methylphenyl) propane, 2,2-bis- (4-hydroxy-3,5-dimethylphenyl) propane, 1,1 Bisphenol compounds having an alkylidene group having 6 or less carbon atoms, such as -bis- (4-hydroxyphenyl) cyclohexane, are preferred.

  As a method for producing the aromatic polycarbonate resin (B) used in the present invention, any conventionally known method such as a phosgene method, a transesterification method, a pyridine method or the like may be used. As an example, a method for producing an aromatic polycarbonate resin (B) by a transesterification method will be described below. The transesterification method is a production method in which a dihydroxy compound and a carbonic acid diester are added with a basic catalyst, and further an acidic substance that neutralizes the basic catalyst is added, and melt transesterification condensation polymerization is performed. Examples of the dihydroxy compound include the biphenyl compounds and bisphenol compounds exemplified above.

  Representative examples of carbonic acid diesters include diaryl carbonates such as diphenyl carbonate, ditolyl carbonate, bis (chlorophenyl) carbonate, m-cresyl carbonate, dinaphthyl carbonate, bis (biphenyl) carbonate, diethyl carbonate, dimethyl carbonate, and dibutyl carbonate. And dialkyl carbonates such as dicyclohexyl carbonate. Of these, diphenyl carbonate is particularly preferably used.

The viscosity average molecular weight of the aromatic polycarbonate resin (B) used in the present invention is usually 8,000 or more and 30,000 or less, preferably 10,000 or more and 25,000, from the balance of mechanical properties and molding processability. The range is as follows. The reduced viscosity of the aromatic polycarbonate resin (B) was measured at a temperature of 20.0 ° C. ± 0.1 ° C. using methylene chloride as a solvent and the polycarbonate concentration was precisely adjusted to 0.60 g / dl. Usually 0.23 dl /
g or more and 0.72 dl / g or less, preferably 0.27 dl / g or more and 0.61 dl / g or less.

In the present invention, the aromatic polycarbonate resin (B) may be used alone or in combination of two or more.
<Polycarbonate resin composition (X)>
The polycarbonate resin composition (X) in the present invention comprises a structural unit (a) derived from a dihydroxy compound having a site represented by the following general formula (1) as part of the structure and a dihydroxy compound of an alicyclic hydrocarbon ( A polycarbonate resin composition (X) comprising a polycarbonate resin (A) containing b) and an aromatic polycarbonate resin (B).

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)
In the polycarbonate resin composition (X), the proportion of the alicyclic hydrocarbon dihydroxy compound (b) in the polycarbonate resin (A) is usually 35 mol% or more, preferably 40 mol% or more, more preferably. It is 50 mol% or more, and particularly preferably 55 mol% or more. On the other hand, it is preferably 90 mol% or less, more preferably 80 mol% or less, and particularly preferably 70 mol% or less.

  If the proportion of the alicyclic hydrocarbon dihydroxy compound (b) in the polycarbonate resin (A) is too small, the total light transmittance of the polycarbonate resin composition (X) becomes small, and the initial yellow index (YI) The value tends to increase. Moreover, when the ratio of the polycarbonate resin (A) in the polycarbonate resin composition (X) is too small, the yellow index (YI) value after the sunshine weatherometer irradiation test described later tends to increase.

The polycarbonate resin composition (X) in the present invention preferably has a single glass transition temperature from the viewpoint of maintaining the transparency of the polycarbonate resin composition and the polycarbonate resin molded product.
The polycarbonate resin (A) and the aromatic polycarbonate resin (B) in the polycarbonate resin composition (X) need only be different types, and the polycarbonate resin (A) has a ring structure. Among them, a compound containing isosorbide as a dihydroxy compound having a site represented by the general formula (1) in a part of the structure is particularly preferable.

<Resin other than polycarbonate resin>
The polycarbonate resin composition and the polycarbonate resin molded article of the present invention can be blended with resins other than polycarbonate resins and additives other than resins.
Specific examples of resins other than polycarbonate resins that are compounded for the purpose of further improving and adjusting molding processability and various physical properties include resins such as polyester resins, polyethers, polyamides, polyolefins, polymethyl methacrylates, and core-shell types. And rubber-like modifiers such as graft-type or linear random and block copolymers. The compounding amount of the resin other than the polycarbonate resin is 1 part by weight or more with respect to 100% by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) used in the present invention.
It is preferable to mix | blend in the ratio of 30 weight part or less, It is more preferable to mix | blend in the ratio of 3 weight part or more and 20 weight part or less, It is more preferable to mix | blend in the ratio of 5 weight part or more and 10 weight part or less. .

<Heat stabilizer>
In the polycarbonate resin composition and the polycarbonate resin molded product of the present invention, a heat stabilizer can be blended in order to prevent a decrease in molecular weight and a deterioration in hue during molding. Examples of the heat stabilizer include phosphorous acid, phosphoric acid, phosphonous acid, phosphonic acid, and esters thereof. Specifically, triphenyl phosphite, tris (nonylphenyl) phosphite, tris (2 , 4-di-tert-butylphenyl) phosphite, tridecyl phosphite, trioctyl phosphite, trioctadecyl phosphite, didecyl monophenyl phosphite, dioctyl monophenyl phosphite, diisopropyl monophenyl phosphite, monobutyl diphenyl Phosphite, monodecyl diphenyl phosphite, monooctyl diphenyl phosphite, bis (2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite, 2,2-methylenebis (4,6-di-) tert -Butylphenyl) octyl phosphite, bis (nonylphenyl) pentaerythritol diphosphite, bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite, distearyl pentaerythritol diphosphite, tributyl phosphate, triethyl Phosphate, trimethyl phosphate, triphenyl phosphate, diphenyl monoorthoxenyl phosphate, dibutyl phosphate, dioctyl phosphate, diisopropyl phosphate, 4,4′-biphenylenediphosphinic acid tetrakis (2,4-di-tert-butylphenyl), benzenephosphonic acid Examples thereof include dimethyl, diethyl benzenephosphonate, and dipropyl benzenephosphonate. Among them, trisnonylphenyl phosphite, trimethyl phosphate, tris (2,4-di-tert-butylphenyl) phosphite, bis (2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis (2 , 6-Di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite and dimethyl benzenephosphonate are preferably used.

  These heat stabilizers may be used alone or in combination of two or more. The blending amount of the heat stabilizer is 0.0001 parts by weight or more and 1 part by weight or less with respect to 100% by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) used in the present invention. It is preferable to mix, more preferably 0.0005 parts by weight or more and 0.5 parts by weight or less, and more preferably 0.001 parts by weight or more and 0.2 parts by weight or less. preferable. By blending the heat stabilizer within such a range, it is possible to prevent a decrease in molecular weight or discoloration of the resin without causing bleeding of the additive.

<Antioxidant>
Moreover, the antioxidant generally known for the purpose of antioxidant can be mix | blended with the polycarbonate resin composition and polycarbonate resin molded product of this invention. Examples of the antioxidant include pentaerythritol tetrakis (3-mercaptopropionate), pentaerythritol tetrakis (3-lauryl thiopropionate), glycerol-3-stearyl thiopropionate, triethylene glycol bis [3 -(3-tert-butyl-5-methyl-4-hydroxyphenyl) propionate], 1,6-hexanediol-bis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], Pentaerythritol-tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate, 1, 3,5-trimethyl-2,4 6-tris (3,5-di-tert-butyl-4-hydroxybenzyl) benzene, N, N-hexamethylenebis (3,5-di-tert-butyl-4-hydroxy-hydrocinnamide), 3, 5-di-tert-butyl-4-hydroxy-benzylphosphonate-diethyl ester, tris (3,5-di-tert-butyl-4-hydroxybenzyl) isocyanurate, 4,4′-biphenylenediphosphinic acid tetrakis (2, 4-di-tert-butylphenyl), 3,9-bis {1,1-dimethyl-2- [β- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionyloxy] ethyl} -2 , 4,8,10-tetraoxaspiro (5,5) undecane and the like. The blending amount of the antioxidant is 0.0001 parts by weight or more and 1 part by weight or less with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) used in the present invention. It is preferable to mix, more preferably 0.0005 parts by weight or more and 0.5 parts by weight or less, and more preferably 0.001 parts by weight or more and 0.2 parts by weight or less. preferable. By blending the antioxidant in such a range, the oxidation deterioration of the resin can be prevented without causing the bleeding of the antioxidant on the surface of the molded body and the deterioration of the mechanical properties of various molded products.

<Ultraviolet absorber>
In order to further improve the weather resistance of the polycarbonate resin composition and the polycarbonate resin molded product of the present invention, an ultraviolet absorber can be blended. Examples of the ultraviolet absorber include 2- (2′-hydroxy-5′-tert-octylphenyl) benzotriazole and 2- (3-tert-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzo. Triazole, 2- (5-methyl-2-hydroxyphenyl) benzotriazole, 2- [2-hydroxy-3,5-bis (α, α-dimethylbenzyl) phenyl] -2H-benzotriazole, 2,2′- Examples include methylene bis (4-cumyl-6-benzotriazolephenyl), 2,2′-p-phenylenebis (1,3-benzoxazin-4-one) and the like. The melting point of the ultraviolet absorber is particularly preferably in the range of 120 to 250 ° C. When an ultraviolet absorber having a melting point of 120 ° C. or higher is used, fogging due to gas on the surface of the molded article is reduced and improved. Specifically, 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2- (2′-hydroxy-3′-tert-butyl-5′-methylphenyl) -5-chlorobenzotriazole, 2- [2′-hydroxy-3 ′-(3 ″, 4 ″, 5 ″, 6 ″ -tetrahydrophthalimidomethyl) -5′-methylphenyl] benzotriazole,
2,2-methylenebis [4- (1,1,3,3-tetramethylbutyl) -6- (2H-benzotriazol-2-yl) phenol, 2- (2-hydroxy-3,5-dicumylphenyl) ) Benzotriazole-based UV absorbers such as benzotriazole are used, and among these, 2- (2-hydroxy-3,5-dicumylphenyl) benzotriazole, 2,2-methylenebis [4- (1 , 1,3,3-tetramethylbutyl) -6- (2
H-benzotriazol-2-yl) phenol is preferred. These UV absorbers, 1
A seed may be used independently and two or more sorts may be used together. The blending amount of the ultraviolet absorber is
It is preferably blended at a ratio of 0.0001 part by weight or more and 1 part by weight or less with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) used in the present invention. More preferably, it is blended at a ratio of not less than 0.5 parts by weight and not more than 0.5 parts by weight, and more preferably at a ratio of not less than 0.001 parts by weight and not more than 0.2 parts by weight. Within such a range, the weather resistance of the resin composition and the molded article can be improved without causing bleeding of the ultraviolet absorbent on the surface of the molded article of the ultraviolet absorbent and deterioration of mechanical properties of various molded articles.

<Hindered amine light stabilizer>
Moreover, a hindered amine light stabilizer can be mix | blended in order to further improve the weather resistance of the polycarbonate resin composition and the polycarbonate resin molded product of the present invention. Such hindered amine light stabilizers include bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis- (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, poly [[6- (1,1,3,3-tetramethylbutyl) amino-1,3,5-
Triazine-2,4-diyl] [(2,2,6,6-tetramethyl-4-piperidyl) imino] hexamethylene [(2,2,6,6-tetramethyl-4-piperidyl) imino]], N
, N′-bis (3-aminopropyl) ethylenediamine-2,4-bis [N-butyl-N- (1,2,2,6,6-pentamethyl-4-piperidylamino) -6-chloro-1, 3,5-triazine condensate, dibutylamine, 1,3,5-triazine, N, N′-bis (2,2,6,6) -tetramethyl-4-piperidyl-1,6-hexamethylenediamine Examples thereof include polycondensates of N- (2,2,6,6-tetramethyl-4-piperidyl) butylamine. Of these, bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate and bis- (1,2,2,6,6-pentamethyl-4-piperidyl) sebacate are preferred.

  The amount of the hindered amine light stabilizer is 0.001 part by weight or more and 1 part by weight or less based on 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) used in the present invention. It is preferable to mix | blend in a ratio, It is further more preferable to mix | blend in the ratio of 0.005 weight part or more and 0.5 weight part or less, It is blended in the ratio of 0.01 weight part or more and 0.2 weight part or less. Is particularly preferred. By blending the hindered amine light stabilizer within such a range, the polycarbonate resin composition of the present invention can be molded without causing bleeding of the hindered amine light stabilizer on the surface of the polycarbonate resin composition and deterioration of mechanical properties of various molded products. The weather resistance of the molded product formed can be improved.

<Release agent>
The polycarbonate resin composition of the present invention preferably further contains a release agent in order to further improve the releasability from the mold during melt molding. Release agents include higher fatty acids, higher fatty acid esters of mono- or polyhydric alcohols, natural animal waxes such as beeswax, natural plant waxes such as carnauba wax, natural petroleum waxes such as paraffin wax, and montan wax. Natural coal wax, olefin wax, silicone oil, organopolysiloxane and the like can be mentioned, and higher fatty acid and higher fatty acid ester of monohydric or polyhydric alcohol are particularly preferable.

  The higher fatty acid ester is preferably a partial ester or a total ester of a substituted or unsubstituted monovalent or polyhydric alcohol having 1 to 20 carbon atoms and a substituted or unsubstituted saturated fatty acid having 10 to 30 carbon atoms. . Such partial esters or total esters of monohydric or polyhydric alcohols and saturated fatty acids include stearic acid monoglyceride, stearic acid diglyceride, stearic acid triglyceride, stearic acid monosorbite, stearyl stearate, behenic acid monoglyceride, behenyl behenate, Pentaerythritol monostearate, pentaerythritol tetrastearate, pentaerythritol tetrapelargonate, propylene glycol monostearate, stearyl stearate, palmityl palmitate, butyl stearate, methyl laurate, isopropyl palmitate, biphenyl biphenate Sorbitan monostearate, 2-ethylhexyl stearate and the like. Of these, stearic acid monoglyceride, stearic acid triglyceride, pentaerythritol tetrastearate, and behenyl behenate are preferably used.

  As the higher fatty acid, a substituted or unsubstituted saturated fatty acid having 10 to 30 carbon atoms is preferable. Examples of such saturated fatty acids include myristic acid, lauric acid, palmitic acid, stearic acid, behenic acid and the like. One of these release agents may be used alone, or two or more thereof may be mixed and used. The content of the release agent is preferably 0.0001 parts by weight or more, more preferably 0.01 parts by weight with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B) used in the present invention. Part by weight or more, particularly preferably 0.1 part by weight or more, on the other hand, preferably 2 parts by weight or less, more preferably 1 part by weight or less, particularly preferably 0.5 parts by weight or less.

  In this Embodiment, the addition time of the said mold release agent mix | blended with a polycarbonate resin composition and the addition method are not specifically limited. For example, when the polycarbonate resin is produced by the transesterification method, when the polymerization reaction is completed; the polycarbonate resin melted during mixing of the polycarbonate resin and other compounding agents regardless of the polymerization method. A case where it is blended and kneaded with a polycarbonate resin in a solid state such as pellets or powder using an extruder or the like. As an addition method, a method of directly mixing or kneading the release agent with a polycarbonate resin; a high-concentration masterbatch prepared using a small amount of a polycarbonate resin or other resin and the release agent can also be added. .

<Charpy impact strength with notch>
In the present invention, the polycarbonate resin composition has a notched Charpy impact strength measured according to ISO 179 of preferably 10 kJ / m ² or more, more preferably 12 k.
J / m ² or more. If the notched Charpy impact strength is too small, the injection-molded product tends to break easily at the stress concentration point. In consideration of the difficulty of realization, the upper limit is 200 kJ / m ² .

<Molding>
In the present embodiment, a polycarbonate resin molded product obtained by molding the above-described polycarbonate resin composition is obtained. The molding method of the polycarbonate resin molded product is not particularly limited, but the polycarbonate resin (A), the aromatic polycarbonate resin (B) and, if necessary, other raw materials such as resins and additives are directly mixed, and an extruder or an injection. Either put into a molding machine and mold, or melt and mix the raw materials using a twin-screw extruder, extrude into a strand shape to produce pellets, and then put these pellets into an extruder or injection molding machine Can be mentioned. Moreover, since the polycarbonate resin molded article of the present invention is excellent in light resistance and transparency, it can be used for road sound insulation walls, arcade ceiling sheets, arcade ceiling plates, facility roofs, facility wall materials, and the like.

  Although the irradiation process using the sunshine carbon arc in the present invention will be described later, a specific device is used and a specific filter or the like is used to mainly emit light having a wavelength of 300 nm to 1100 nm, a black panel temperature of 63 ° C., and a relative humidity of 50. % A sample is irradiated for 500 hours at a discharge voltage of 50 V and a discharge current of 60 A using a sunshine carbon arc in an environment where the rainfall spraying time per hour is 12 minutes.

  The total light transmittance after subjecting the molded body (thickness 3 mm) molded from the polycarbonate resin composition of the present invention to irradiation treatment for 500 hours using the sunshine carbon arc is preferably 85% or more, The upper limit is 99% or less, and the difference in yellow index (YI) values before and after the irradiation treatment is preferably 10 or less, more preferably 8 or less, and particularly preferably 6 or less.

EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited by a following example, unless the summary is exceeded.
In the following, evaluation of physical properties or characteristics of polycarbonate resin, polycarbonate resin composition, molded article and the like was performed by the following method.
(1) Measurement of reduced viscosity A polycarbonate resin sample was dissolved using methylene chloride as a solvent to prepare a polycarbonate solution having a concentration of 0.6 g / dL. Using Moritomo Rika Co. Ubbelohde viscometer tube was measured at a temperature of 20.0 ° C. ± 0.1 ° C., determine the relative viscosity ηrel using the following equation from the transit time t of the solvent passage time t ₀ and a solution,
ηrel = t / t ₀
From the relative viscosity, the specific viscosity ηsp was determined from the following formula.

ηsp = (η−η ₀ ) / η ₀ = ηrel−1
The reduced viscosity ηsp / c was determined by dividing the specific viscosity by the concentration c (g / dL). The higher this value, the higher the molecular weight.
(2) Hue measurement
Yellow index (YI) value of injection-molded piece (width 60 mm x length 60 mm x thickness 3 mm) by C light source transmission method using a spectral color difference meter (SE2000 manufactured by Nippon Denshoku Industries Co., Ltd.) in accordance with JIS K7105 Was measured. The smaller the YI value, the better the quality without yellowness.

(3) Total light transmittance measurement Based on JISK7105, the haze meter (NDH2000 by Nippon Denshoku Industries Co., Ltd.) was used, and the total light transmittance of the injection molded piece was measured with D65 light source.
(4) Notched Charpy impact strength A notched Charpy impact test was performed on the ISO test piece for mechanical properties in accordance with ISO179.

(5) Sunshine weatherometer irradiation test In accordance with JIS B7753, using a sunshine weatherometer S80 manufactured by Suga Test Instruments Co., Ltd., a sunshine carbon arc (4 pairs of ultra long life carbon) light source with a discharge voltage of 50 V and a discharge current of 60 A Set, irradiation and surface spray (rainfall) on a black surface of a flat panel (width 60 mm x length 60 mm x thickness 3 mm) on a black panel temperature of 63 ° C and relative humidity of 50% For 500 hours. The surface spray (rainfall) time was 12 minutes / 1 hour. A type glass filter was used. YI after irradiation treatment and total light transmittance were measured, and the difference between YI after treatment for 500 hours and YI before treatment was determined.

<Polycarbonate resin (A)>
PC1:
Structural unit derived from isosorbide / Structural unit derived from 1,4-cyclohexanedimethanol = 40/60 mol%, reduced viscosity 0.63 dl / g
PC2:
Structural unit derived from isosorbide / Structural unit derived from 1,4-cyclohexanedimethanol = 70/30 mol%, reduced viscosity 0.51 dl / g
<Aromatic polycarbonate resin (B)>
PC3:
Mitsubishi Engineering Plastics Novalex 7022J (2,2-bis- (4
-Hydroxyphenyl) aromatic polycarbonate resin having only a structure derived from propane, viscosity average molecular weight 22,000)
(Example 1)
After PC1 and PC3 were dry blended at a weight ratio of 80:20, they were extruded at a resin temperature of 250 ° C. using a twin screw extruder (TEX30HSS-32) manufactured by Nippon Steel, and solidified by cooling with water. Then, it pelletized with the rotary cutter. After the pellets were dried at 80 ° C. for 10 hours in a nitrogen atmosphere, the pellets were supplied to an injection molding machine (J75EII type manufactured by Nippon Steel Co., Ltd.). An injection molded plate (width 60 mm × length 60 mm × thickness 3 mm) and an ISO test piece for mechanical properties were molded.
Table 1 shows the results obtained by measuring the total light transmittance, YI, and notched Charpy impact strength of the obtained sample.

(Example 2)
Samples were prepared and evaluated in the same manner as in Example 1 except that PC1 and PC3 were mixed at a mixing weight ratio of 60:40. The results are shown in Table 1.
(Example 3)
Samples were prepared and evaluated in the same manner as in Example 1 except that PC1 and PC3 were mixed at a mixing weight ratio of 40:60. The results are shown in Table 1.

(Comparative Example 1)
Samples were prepared and evaluated in the same manner as in Example 1 except that PC2 and PC3 were mixed at a mixing weight ratio of 80:20. The results are shown in Table 1.

Claims (9)

A polycarbonate resin (A) containing a structural unit (a) derived from a dihydroxy compound having a site represented by the following general formula (1) as part of the structure and an alicyclic hydrocarbon dihydroxy compound (b); A polycarbonate resin composition (X) comprising an aromatic polycarbonate resin (B), characterized in that the alicyclic hydrocarbon dihydroxy compound (b) in the polycarbonate resin (A) is 35 mol% or more. A polycarbonate resin composition.

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)   A molded body (thickness 3 mm) molded from the polycarbonate resin composition was discharged using a sunshine carbon arc in an environment where the black panel temperature was 63 ° C., the relative humidity was 50%, and the rainfall spraying time per hour was 12 minutes. After 500 hours of irradiation treatment at a voltage of 50 V and a discharge current of 60 A, the total light transmittance is 85% or more, and the difference in yellow index (YI) values before and after the irradiation treatment is 10 or less. The polycarbonate resin composition according to claim 1. The polycarbonate resin composition according to claim 1, wherein the Charpy impact strength with notch measured in accordance with ISO 179 is 10 kJ / m ² or more. 4. The dihydroxy compound having a part represented by the following general formula (1) in a part of the structure is a dihydroxy compound represented by the following general formula (2). 2. The polycarbonate resin composition according to item 1.

(However, the site represented by the above general formula (1) unless it is part of _-CH 2 -O-H.)

  The composition further comprises 0.0001 parts by weight or more and 1 part by weight or less of an ultraviolet absorber with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B). 5. The polycarbonate resin composition according to any one of 4 above.   The composition further comprises 0.001 part by weight or more and 1 part by weight or less of a hindered amine light stabilizer based on 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B). The polycarbonate resin composition according to any one of 1 to 5. The antioxidant is contained in an amount of 0.0001 to 1 part by weight with respect to 100 parts by weight of the mixture of the polycarbonate resin (A) and the aromatic polycarbonate resin (B). The polycarbonate resin composition according to any one of the above.   2. From 100 weight part of mixture of said polycarbonate resin (A) and said aromatic polycarbonate resin (B), it further contains 0.0001 weight part or more and 2 weight part or less of mold release agent. 8. The polycarbonate resin composition according to any one of 7 above.   A polycarbonate resin molded article obtained by molding the polycarbonate resin composition according to any one of claims 1 to 8.