JP2015224284A - Colored single-sided tacky-adhesive tape - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a colored single-sided tacky-adhesive tape which is used suitably for fixing/covering a ferrite sheet or a graphite sheet when a portable information terminal is produced, which hardly gets wrinkled even if it is thin when stuck to the ferrite sheet or the graphite sheet, and which can prevent adhesion of a fingerprint or foreign matter to the surface of ferrite sheet or the graphite sheet, which surface becomes the outside surface finally.SOLUTION: The colored single-sided tacky-adhesive tape is obtained by arranging a tacky adhesive layer on one surface of a support layer having 1-4 μm thickness, and arranging a colored layer and a surface protection film for protecting the colored layer on the other surface thereof. The overall thickness of the support layer, the tacky adhesive layer and the colored layer is 3-10 μm. A ratio (A/B) of the peel force (A) of the surface protection film to the peel tacky power (B) in the 180° direction of the tacky adhesive layer to a SUS plate is 0.6 or lower.

Description

The present invention is suitably used for fixing and covering a ferrite sheet or graphite sheet in the manufacture of a portable information terminal, etc., and even if it is thin, it does not easily wrinkle when bonded, and the fingerprint on the surface that will eventually become the outer surface Or it is related with the colored single-sided adhesive tape which can prevent adhesion of a foreign material.

With the spread of electronic money, automatic ticket gates, etc., mobile information terminals such as mobile phones, smartphones, tablets, etc. have a non-contact communication (NFC: Near Field Communication) function that allows communication by simply holding it over a reader or writer. It comes to be installed.
In NFC, antenna coils are provided on both the reader / writer side and the portable information terminal side, and communication is performed by electromagnetic induction generated between both antenna coils. At this time, since communication performance may be greatly reduced due to the generation of eddy current, a magnetic sheet having magnetic permeability such as a ferrite sheet is attached to the inside or the outer surface of the component of the portable information terminal to suppress the influence of the eddy current. It is being considered.

When a ferrite sheet is affixed to the inside or the outer surface of a component of a portable information terminal, a single-sided adhesive tape is used to fix the brittle ferrite sheet and to protect the surface of the ferrite sheet (for example, Patent Documents 1 and 2). . In particular, when a ferrite sheet is attached to the outer surface of a component (for example, the inner surface of a battery cover), the single-sided adhesive tape touches the eyes of the user of the portable information terminal. In combination, it is often colored black, white, red or the like.

In recent years, heat radiation sheets such as graphite sheets have been used to suppress the heat generation of portable information terminals in accordance with the increasing needs for downsizing, thinning or lightening portable information terminals or reducing power consumption. . A colored single-sided adhesive tape is also used when a graphite sheet is attached to the inside or the outside of a part of a portable information terminal.

In these applications, it is desired to make the colored single-sided adhesive tape extremely thin. However, when the colored single-sided pressure-sensitive adhesive tape is thinned, it has been a problem that it tends to be wrinkled when the release film for protecting the pressure-sensitive adhesive layer is peeled off and bonded.
In addition, since thin colored single-sided adhesive tape is often attached by hand, the operator's fingerprints may adhere to the outer surface on the opposite side of the adhesive layer, impairing the appearance. It was.
In addition, when fixing and coating the ferrite sheet, ferrite powder is produced in the process of manufacturing the ferrite sheet, and this ferrite powder moves around, and the ferrite powder and the outer surface of the colored single-sided adhesive tape rub against each other. It is known that scratches occur on the outer surface of the adhesive tape. In particular, when the colored single-sided adhesive tape is black, the scratches are noticeable as whitish scratches, and the appearance is remarkably impaired.

JP 2013-56968 A JP 2013-112695 A

The present invention is suitably used for fixing and covering a ferrite sheet or graphite sheet in the manufacture of a portable information terminal, etc., and even if it is thin, it does not easily wrinkle when bonded, and the fingerprint on the surface that will eventually become the outer surface Alternatively, an object of the present invention is to provide a colored single-sided adhesive tape that can prevent adhesion of foreign matters.

In the present invention, a pressure-sensitive adhesive layer is provided on one surface of a support layer having a thickness of 1 to 4 μm, a colored layer and a surface protective film for protecting the colored layer are provided on the other surface, and the support layer, The total thickness of the pressure-sensitive adhesive layer and the colored layer is 3 to 10 μm, and the peel strength (A) of the surface protective film and the peel strength (B) in the 180 ° direction of the pressure-sensitive adhesive layer with respect to the SUS plate It is a colored single-sided adhesive tape having a ratio (A / B) of 0.6 or less.
The present invention is described in detail below.

As a method of thinning the colored single-sided adhesive tape, for example, a method of thinning the pressure-sensitive adhesive layer can be considered. However, if the pressure-sensitive adhesive layer is thinned, the pressure-sensitive adhesive property is lowered. Therefore, in order to thin the colored single-sided pressure-sensitive adhesive tape while ensuring sufficient pressure-sensitive adhesiveness, a method of thinning layers other than the pressure-sensitive adhesive layer is preferable. For this reason, as a method for preventing the adhesion of foreign substances such as fingerprints or ferrite powder to the outer surface of the colored single-sided adhesive tape, it is not preferable to employ a method of further providing a contamination prevention coating layer or the like on the outer surface.
The inventors of the present invention have a colored single-sided adhesive tape having a configuration in which an adhesive layer is provided on one side of a support layer, a colored layer is provided on the other side, and a surface protective film that protects the colored layer, Even if it is thin, the ratio (A / B) of the peel strength (A) of the surface protective film and the peel strength (B) in the 180 ° direction of the pressure-sensitive adhesive layer to the SUS plate is adjusted to a specific range. The present inventors have found that a colored single-sided adhesive tape that can be prevented from wrinkling at the time of joining and can prevent the adhesion of fingerprints or foreign matters to the surface that eventually becomes the outer surface has been completed.
That is, since such a colored single-sided adhesive tape is supported by the surface protective film, it is difficult to be wrinkled at the time of bonding, and since it is covered and protected by the surface protective film, the surface protective film is peeled off. After that, it is possible to prevent fingerprints or foreign matters from adhering to the surface that finally becomes the outer surface (for example, the surface of the colored layer). And after bonding the colored single-sided adhesive tape, the surface protective film is peeled off, so that only the thin colored single-sided adhesive tape from which the surface protective film has been removed remains on the adherend. .

In the colored single-sided pressure-sensitive adhesive tape of the present invention, an adhesive layer is provided on one side of a support layer having a thickness of 1 to 4 μm, a colored layer and a surface protective film for protecting the colored layer are provided on the other side. .
By having such a configuration, the colored single-sided pressure-sensitive adhesive tape of the present invention is less likely to be wrinkled at the time of bonding even if it is thin, and can prevent adhesion of fingerprints or foreign matters to the surface that eventually becomes the outer surface. .
That is, since the colored single-sided adhesive tape of the present invention is supported by the surface protective film, it is not easily wrinkled at the time of bonding, and is covered and protected by the surface protective film, so that the surface protective film is peeled off. After that, it is possible to prevent fingerprints or foreign matters from adhering to the surface that finally becomes the outer surface (for example, the surface of the colored layer). And after pasting together the colored single-sided adhesive tape of the present invention, the thin protective single-sided adhesive tape from which the surface protective film has been removed remains on the adherend by peeling off the surface protective film. become.

The resin constituting the support layer is not particularly limited, but a resin having a weight average molecular weight of 5000 to 70000 and / or a glass transition temperature (Tg) of 50 to 150 ° C. is preferable. Examples of such a resin include a crystalline polyester resin, an amorphous urethane resin, an amorphous polyester resin, and an amorphous polyester urethane resin. Of these, crystalline polyester resins are preferred.
The weight average molecular weight is a value measured as a polystyrene equivalent molecular weight by a GPC (Gel Permeation Chromatography) method, and the glass transition temperature (Tg) is DSC (Differential Scanning Calorimetry). It is a value measured by the method.

The crystalline polyester resin is not particularly limited, and examples thereof include polyethylene terephthalate, polybutylene terephthalate, and polyethylene naphthalate. These may be used alone or in combination of two or more. Among them, polyethylene terephthalate is preferable because it is strong and has excellent elastic recovery.

The non-crystalline urethane resin is not particularly limited, and examples thereof include a urethane resin obtained by reacting an aliphatic diisocyanate and an aliphatic diol, and a urethane resin obtained by reacting a polyfunctional isocyanate and an aliphatic diol.
Examples of the aliphatic diisocyanate include dimethylene diisocyanate, diethylene diisocyanate, and hexamethylene diisocyanate. These may be used alone or in combination of two or more.
Examples of the aliphatic diol include polyethylene glycols such as ethylene diol and propylene diol. These may be used independently and 2 or more types may be used together.

The non-crystalline polyester resin is not particularly limited, and examples thereof include a polyester resin obtained by reacting an aliphatic dicarboxylic acid or a methyl ester of an aliphatic dicarboxylic acid with an aliphatic diol.
Examples of the aliphatic dicarboxylic acid include phthalic acid and adipic acid. Examples of the methyl ester of the aliphatic dicarboxylic acid include dimethyl phthalate and dimethyl adipate. These may be used alone or in combination of two or more.

The thickness of the support layer has a lower limit of 1 μm and an upper limit of 4 μm. When the thickness is less than 1 μm, the strength of the support layer is lowered, and the colored single-sided adhesive tape tends to wrinkle during bonding. When the thickness exceeds 4 μm, the colored single-sided adhesive tape becomes thick and is not suitable for portable information terminal applications. The minimum with said preferable thickness is 1.2 micrometers, a preferable upper limit is 3.5 micrometers, a more preferable minimum is 1.5 micrometers, and a more preferable upper limit is 3 micrometers.

The adhesive which comprises the said adhesive layer is not specifically limited, For example, an acrylic resin adhesive, a urethane resin adhesive, a synthetic rubber adhesive, a polyester resin adhesive, etc. are mentioned.

The pressure-sensitive adhesive layer may be crosslinked with a crosslinking agent.
The said crosslinking agent is not specifically limited, According to the said adhesive, it selects suitably. When the pressure-sensitive adhesive is an acrylic resin pressure-sensitive adhesive, examples of the crosslinking agent include an isocyanate crosslinking agent and an epoxy crosslinking agent. These may be used alone or in combination of two or more.
As a commercial item of the said isocyanate crosslinking agent, Coronate L55E (made by a Japan polyurethane company) etc. are mentioned, for example.

The content of the crosslinking agent is not particularly limited, but a preferable lower limit with respect to 100 parts by weight of the pressure-sensitive adhesive is 0.3 parts by weight, a preferable upper limit is 5 parts by weight, and a more preferable lower limit is 0.5 parts by weight. Is 3 parts by weight.

Although the thickness of the said adhesive layer is not specifically limited, A preferable minimum is 1 micrometer and a preferable upper limit is 4 micrometers. When the thickness is less than 1 μm, the adhesiveness of the pressure-sensitive adhesive layer is lowered and may not be suitable for portable information terminal applications. When the thickness exceeds 4 μm, the colored single-sided adhesive tape becomes thick and may not be suitable for portable information terminal applications. The more preferable lower limit of the thickness is 1.5 μm, and the more preferable upper limit is 3.5 μm.

The colored layer is not particularly limited as long as it is colored black, white, red (magenta) or the like according to the color of the portable information terminal, but is preferably black.
When the colored layer is black, the black material is not particularly limited, and examples thereof include conventionally known pigments and dyes such as carbon black. When the colored layer is white, the white material is not particularly limited, and examples thereof include conventionally known pigments and dyes such as titanium dioxide, barium sulfate, zinc white, and lead white. When the colored layer is magenta, the magenta material is not particularly limited. I. Pigment red 1, C.I. I. Pigment violet 3, C.I. I. Conventionally known pigments and dyes such as Vat Red 1 can be used.

The content of these coloring materials in the colored layer is not particularly limited, but a preferable lower limit with respect to 100 parts by weight of the binder resin is 50 parts by weight, a preferable upper limit is 150 parts by weight, and a more preferable lower limit is 75 parts by weight. Is 125 parts by weight.

The colored layer preferably further contains a binder resin.
Examples of the binder resin include urethane resin, epoxy resin, polyester resin, polyester urethane resin, and the like. These may be used alone or in combination of two or more. Of these, urethane resin is preferred because of its excellent flexibility.

The colored layer is preferably cured with a curing agent.
The said hardening | curing agent is not specifically limited, According to the said binder resin, it selects suitably. When the binder resin is a urethane resin, examples of the curing agent include an isocyanate curing agent. In addition, when a hydroxyl group or an isocyanate group exists in the urethane resin, an amine curing agent may be used as the curing agent. These may be used alone or in combination of two or more.
As a commercial item of the said isocyanate hardening | curing agent, Lamic B hardener (made by Dainichi Seika Co., Ltd.) etc. are mentioned, for example.

The content of the curing agent is not particularly limited, but the isocyanate group in the curing agent and the reactive group such as a hydroxyl group in the binder resin are within a range where the equivalent ratio is 0.5 to 2.0. Practically preferred.

The colored layer may further contain additives such as a transparent resin (medium), an antioxidant, an ultraviolet absorber, and a light stabilizer as necessary.
As a commercial item of the said transparent resin (medium), Lamic F220 medium (made by Dainichi Seika Co., Ltd.) etc. are mentioned, for example.

The method for forming the colored layer is not particularly limited. For example, a coloring layer forming resin solution is prepared by mixing a curing material, a diluent, or the like with an ink containing a coloring material, a binder resin, and a solvent as necessary. In addition, after applying this colored layer forming resin solution, a method of drying and curing by heating can be used.
Among the above inks, examples of commercially available black ink include SKK black (manufactured by Dainichi Seika Co., Ltd.).
Examples of the diluent include ethyl acetate, isopropyl alcohol, and the like. 2 solvent (made by Dainichi Seika Co., Ltd.) etc. are mentioned.

Although the thickness of the said colored layer is not specifically limited, A preferable minimum is 0.5 micrometer and a preferable upper limit is 3 m. When the thickness is less than 0.5 μm, coloring may be reduced and the adherend may be seen through. When the thickness exceeds 3 μm, the colored single-sided adhesive tape becomes thick and may not be suitable for portable information terminal applications. The more preferable lower limit of the thickness is 1 μm, and the more preferable upper limit is 2 μm.

The colored single-sided pressure-sensitive adhesive tape of the present invention has a total lower limit of 3 μm and an upper limit of 10 μm of the thickness of the support layer, the pressure-sensitive adhesive layer, and the colored layer.
By having such a total thickness, the colored single-sided adhesive tape of the present invention becomes a thin colored single-sided adhesive tape suitable for portable information terminal applications. A preferable lower limit of the total thickness is 4 μm, and a preferable upper limit is 9 μm. A more preferable lower limit is 5 μm, and a more preferable upper limit is 8 μm.

The surface protective film supports the colored single-sided adhesive tape of the present invention and covers and protects the colored layer, and is removed after the colored single-sided adhesive tape of the present invention is bonded.
The surface protective film is not particularly limited, and examples thereof include a film in which an adhesive layer is formed on a resin film substrate such as biaxially stretched polypropylene (OPP), polyethylene, or polyethylene terephthalate. Especially, since the rigidity is calculated | required as said resin film base material so that it may be hard to wrinkle at the time of bonding with a to-be-adhered body, a polyethylene terephthalate is preferable.
The adhesive which comprises the said adhesive layer is not specifically limited, For example, a natural rubber adhesive, a synthetic rubber adhesive, an acrylic resin adhesive, a urethane resin adhesive, a silicone resin adhesive etc. are mentioned.

Examples of commercially available products for the surface protective film include protect tape 6312B-60 (thickness 60 μm, manufactured by Sekisui Chemical Co., Ltd.), E-212 (thickness 60 μm, manufactured by Sumilon), and the like.

Although the thickness of the said surface protective film is not specifically limited, A preferable minimum is 25 micrometers and a preferable upper limit is 100 micrometers. When the thickness is less than 25 μm, the surface protective film cannot sufficiently support the colored single-sided adhesive tape, and the colored single-sided adhesive tape may become wrinkled at the time of bonding. When the said thickness exceeds 100 micrometers, material cost will become high and versatility may become scarce. A more preferable lower limit of the thickness is 30 μm, and a more preferable upper limit is 80 μm.

In the colored single-sided pressure-sensitive adhesive tape of the present invention, a layer containing particles is preferably laminated between the colored layer and the surface protective film. Hereinafter, the layer containing particles is referred to as a mat layer. When the mat layer is outside the colored layer, even if foreign matter such as ferrite powder adheres to the surface of the colored single-sided pressure-sensitive adhesive tape, the scratch is not noticeable and a good appearance is obtained. In addition, the said mat layer may be laminated | stacked directly on the said colored layer, and may be laminated | stacked through another layer between the said colored layers.
Examples of the particles include organic particles and inorganic particles. From the viewpoint of not conspicuously scratching, organic particles are preferable. In addition, inorganic particles are preferable from the viewpoints of hardness and heat resistance.
The organic particles are not particularly limited, and examples thereof include acrylic resin particles such as polymethyl methacrylate particles, polystyrene particles, polycarbonate particles, urethane resin beads, epoxy resin beads, polyester resin beads, and polyester urethane resin beads. These may be used alone or in combination of two or more. Of these, urethane resin beads are preferred because of their excellent flexibility.
The inorganic particles are not particularly limited, and examples thereof include particles made of silicon dioxide, titanium dioxide, barium sulfate, silica, calcium carbonate, and the like. These may be used alone or in combination of two or more. Among these, silica particles are preferable because of easy particle size adjustment and availability.

The average particle diameter of the particles is not particularly limited, but a preferable lower limit is 0.5 μm and a preferable upper limit is 12 μm. If the average particle diameter is less than 0.5 μm, the scratches may be noticeable when foreign matter such as ferrite powder adheres to the surface of the colored single-sided adhesive tape. When the average particle diameter exceeds 12 μm, the printability or coatability when forming the mat layer may be lowered. A more preferable lower limit of the average particle diameter is 0.7 μm, and a more preferable upper limit is 10 μm.
Here, the average particle size is a value obtained by measuring the particle size distribution by a laser diffraction method and arithmetically averaging the diameters.

The content of the particles is not particularly limited, but a preferable lower limit with respect to 100 parts by weight of the binder resin is 10 parts by weight, and a preferable upper limit is 60 parts by weight. If the content is outside the above range, scratches may be noticeable when foreign matter such as ferrite powder adheres to the surface of the colored single-sided adhesive tape and scratches occur. The minimum with more preferable content of the said particle | grain is 20 weight part, and a more preferable upper limit is 50 weight part.

The mat layer preferably contains the same binder resin and curing agent as those contained in the colored layer. The mat layer may contain additives such as a transparent resin (medium) similar to that contained in the colored layer, an antioxidant, an ultraviolet absorber, and a light stabilizer, as necessary.

The method for forming the mat layer is not particularly limited. For example, a mat agent containing particles, a binder resin, and a solvent is mixed with a curing agent, a diluent, and the like as necessary to prepare a mat layer forming resin solution. In addition, after applying the mat layer forming resin solution, a method of drying and curing by heating may be used.
As a commercial product of the matting agent, for example, SKK mat OP varnish (a matting agent containing urethane resin, silica particles and an organic solvent, silica particles are contained in an amount of about 50% by weight based on solid content, manufactured by Dainichi Seika Co., Ltd.), etc. Is mentioned.
Examples of the diluent include ethyl acetate, isopropyl alcohol, and the like. 2 solvent (made by Dainichi Seika Co., Ltd.) etc. are mentioned.

The thickness of the mat layer is not particularly limited, but a preferable lower limit is 0.5 μm and a preferable upper limit is 2 μm. When the thickness is less than 0.5 μm, scratches may be noticeable when foreign matters such as ferrite powder adhere to the surface of the colored single-sided pressure-sensitive adhesive tape and cause scratches. When the thickness exceeds 2 μm, the colored single-sided adhesive tape becomes thick and may not be suitable for portable information terminal applications. The more preferable lower limit of the thickness is 0.8 μm, and the more preferable upper limit is 1.8 μm.

In the colored single-sided pressure-sensitive adhesive tape of the present invention, the peel strength (A) of the surface protective film and the peel strength in the 180 ° direction of the pressure-sensitive adhesive layer with respect to the SUS plate (hereinafter also simply referred to as “SUS180 ° peel strength”). ) The ratio (A / B) to (B) is 0.6 or less. Note that the peeling force (A) of the surface protective film is, for example, the peeling force for the colored layer when the surface protective film is provided on the colored layer, and the surface protective film on the mat layer. Is provided, it means a peeling force for the mat layer.
When the ratio A / B is 0.6 or less, the surface protection film is peeled off after the colored single-sided pressure-sensitive adhesive tape of the present invention is bonded, so that the surface protection is finally formed on the adherend. Only the thin colored single-sided adhesive tape from which the film has been removed remains. If the ratio A / B exceeds 0.6, the adhesive layer will be peeled off from the adherend when the surface protective film is peeled off after the colored single-sided adhesive tape is bonded. The ratio A / B is preferably 0.5 or less, and more preferably 0.3 or less.
The lower limit of the ratio A / B is not particularly limited, but is preferably 0.01 or more, and more preferably 0.03 or more.

In the colored single-sided adhesive tape of the present invention, a release film is preferably provided on the pressure-sensitive adhesive layer. In this case, the release film (C) of the release film and the release force of the surface protective film ( The ratio (C / A) to A) is preferably 0.7 or less. In addition, the peeling force (C) of the said release film means the peeling force with respect to the said adhesive layer.
The release film is for protecting the pressure-sensitive adhesive layer until use. When the ratio C / A is 0.7 or less, the colored single-sided pressure-sensitive adhesive tape of the present invention can peel the release film from the pressure-sensitive adhesive layer during use. When the ratio C / A exceeds 0.7, if the release film is to be peeled off during use, the surface protective film may be peeled off instead of the release film. The ratio C / A is more preferably 0.65 or less.
Although the minimum of the said ratio C / A is not specifically limited, 0.01 or more are preferable and 0.03 or more are more preferable.

As a method of adjusting the ratio A / B and the ratio C / A to the above ranges, a method of adjusting the peeling force of each film by selecting the material and thickness of each film, the type of the adhesive, and the adhesive A method of adjusting the adhesive force of the pressure-sensitive adhesive layer by selecting the thickness of the layer, a method of adjusting both the peeling force and the adhesive force, and the like are preferable.
Specifically, the peeling force (A) of the surface protective film has a preferable lower limit of 0.1 N / 25 mm, a preferable upper limit of 2.5 N / 25 mm, a more preferable lower limit of 0.15 N / 25 mm, and a more preferable upper limit. Is 1.5 N / 25 mm.
Specifically, the SUS plate 180 ° peeling adhesive strength (B) has a preferable lower limit of 2.5 N / 25 mm and a more preferable lower limit of 3 N / 25 mm.
Specifically, the peeling force (C) of the release film has a preferable lower limit of 0.01 N / 25 mm, a preferable upper limit of 0.5 N / 25 mm, a more preferable lower limit of 0.02 N / 25 mm, and a more preferable upper limit. Is 0.2 N / 25 mm.
The peel strength of the surface protective film or the release film and the 180 ° peel adhesive strength of the SUS plate are measured according to JIS Z using a tensile tester (for example, Autograph Universal Tester AGS-X manufactured by Shimadzu Corporation). It can be measured according to the adhesion test method of 0237.

The method for producing the colored single-sided adhesive tape of the present invention is not particularly limited, and examples thereof include the following methods.
First, the colored layer is formed on the support layer by a casting method or the like to obtain a laminate (colored support layer). At this time, if necessary, the mat layer may be further formed on the colored layer by a casting method or the like. Separately, the pressure-sensitive adhesive layer is formed on the release film by a casting method or the like. Next, the pressure-sensitive adhesive layer formed on the release film is bonded to the surface of the support layer of the colored support layer (the surface on which the colored layer is not formed). Then, the said surface protection film is bonded together on the surface of the said colored layer or the said mat layer formed as needed.
Specific examples of the casting method include a method in which each resin solution is applied using a gravure method, a roll coating method or the like and then heated.
In addition, the colored layer, the support layer, and the pressure-sensitive adhesive layer may be sequentially formed on the surface protective film by a casting method or the like. Since the support layer is thin, when the casting method or the like is performed directly on the support layer, it tends to be wrinkled and the productivity is poor. Since the layer and the support layer can be sequentially formed, productivity is improved.

The colored single-sided adhesive tape of the present invention is suitably used for fixing and covering a ferrite sheet or a graphite sheet in the production of a portable information terminal or the like.
FIG. 1 is a cross-sectional view schematically showing an example of a method for fixing and covering a ferrite sheet or a graphite sheet using the colored single-sided adhesive tape of the present invention.
In the colored single-sided pressure-sensitive adhesive tape 1 of the present invention shown in FIG. 1 (a), the pressure-sensitive adhesive layer 3 is provided on one side of the support layer 2, the colored layer 4, the mat layer 5 and the surface protective film on the other side. 6 are provided. Further, a release film 7 is provided on the pressure-sensitive adhesive layer 3.

In the method shown in FIG. 1, first, the release film 7 is peeled off from the pressure-sensitive adhesive layer 3 during use as shown in FIG. 1 (b), and then the coloring of the present invention as shown in FIG. 1 (c). The single-sided adhesive tape 1 is bonded to a ferrite sheet or graphite sheet 8. Thereafter, as shown in FIG. 1 (d), the surface protective film 6 is peeled off, so that the surface protective film 6 is finally removed on the ferrite sheet or graphite sheet 8 which is an adherend. Only the adhesive tape will remain.

The ferrite sheet is not particularly limited, and examples thereof include a sheet having a thickness of about 10 to 300 μm made of Ni ferrite powder, Mg ferrite powder, Mn ferrite powder, Ba ferrite powder, Sr ferrite powder or the like.

The graphite sheet has a high thermal conductivity in the plane direction, and has a large anisotropy in the thermal conductivity in the plane direction and the thermal conductivity in the thickness direction. It can effectively diffuse heat.
The graphite sheet is not particularly limited, and examples thereof include a natural graphite sheet obtained by sheeting natural graphite powder, an artificial graphite sheet obtained by heat-treating a polymer film, and the like. Among them, an artificial graphite sheet obtained by heat-treating a polymer film is preferable because it is thin and has high thermal conductivity in the surface direction.

Examples of the polymer film include polyimide, polyamide, polyoxadiazole, polybenzothiazole, polybenzobisthiazole, polybenzoxazole, polybenzobisoxazole, polyparaphenylene vinylene, polybenzimidazole, polybenzobisimidazole, poly A film made of thiazole or the like can be mentioned. Of these, a polyimide film is preferable.
The polyimide film is more susceptible to carbonization and graphitization than other polymer films, so the thermal diffusivity, thermal conductivity and electrical conductivity are likely to be uniformly high at low temperatures, and the thermal diffusivity and thermal conductivity. The rate and electrical conductivity itself tend to be high. Further, in addition to the case where the thickness is small, graphite having high thermal conductivity can be obtained even when the thickness is large. Moreover, when the obtained graphite is excellent in crystallinity, excellent in heat resistance and bendability, and bonded to a colored single-sided adhesive tape, it is easy to obtain a graphite sheet in which graphite does not easily fall from the surface.

When heat-treating the polymer film, first, the polymer film is carbonized by preheating treatment under reduced pressure or in an inert gas. This carbonization is usually performed at a temperature of about 1000 ° C. For example, when the temperature is increased at a rate of 10 ° C./min, it is preferable to hold the temperature for about 30 minutes in a temperature region of about 1000 ° C. The graphitization step is then performed under reduced pressure or in an inert gas. Argon and helium are suitable as the inert gas.
When heat-treating the polymer film, the heat treatment temperature should be at least 2000 ° C. or higher, and eventually 2400 ° C. or higher, more preferably 2600 ° C. or higher, and even more preferably 2800 ° C. or higher. preferable. By setting such a heat treatment temperature, graphite having excellent thermal conductivity can be obtained. The higher the heat treatment temperature is, the higher the quality can be converted to graphite, but from the viewpoint of economy, it is preferable that the conversion to high quality graphite is possible at the lowest possible temperature. In order to obtain an ultra-high temperature of 2500 ° C. or higher, usually, a current is directly applied to the graphite heater, and heating using the Joule heat is performed.

The graphite sheet preferably has a thermal conductivity in the plane direction of 200 W / mK or more and a thermal conductivity in the thickness direction of 20 W / mK or less.

As a commercial item of the said graphite sheet, a graphicity (made by Kaneka), a PGS sheet (made by Panasonic) etc. are mentioned, for example.

According to the present invention, it is suitably used for fixing and covering a ferrite sheet or a graphite sheet in the manufacture of a portable information terminal, etc. It is possible to provide a colored single-sided adhesive tape that can prevent adhesion of fingerprints or foreign matters.

It is sectional drawing which showed typically an example of the method of fixing and coat | covering a ferrite sheet or a graphite sheet using the coloring single-sided adhesive tape of this invention.

Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.

(Examples 1-9, Comparative Examples 1-3)
(1) Preparation of a resin solution for forming a mat layer and a resin solution for forming a colored layer The materials (a) to (d) shown below are mixed so as to have the solution weight ratio composition shown in Table 1 to form a mat layer. A resin solution and a colored layer forming resin solution were respectively prepared.
Table 1 shows the weight ratio of each layer-forming resin solution and the weight ratio of the dried layer obtained by the operation described below. The weight ratio indicated as “liquid / liquid ratio” in Table 1 means a weight ratio based on the weight of each liquid to be mixed. The weight ratio indicated as “solid / solid ratio” in Table 1 means a weight ratio based on the solid content weight of each component. In addition, when it is a solid material, it is the weight.
(A) Matting agent SKK mat OP varnish (a matting agent containing urethane resin, silica particles and an organic solvent, manufactured by Dainichi Seika Co., Ltd.)
SKK Hi-mat OP Varnish (Murting agent containing urethane resin, silica particles and organic solvent, manufactured by Dainichi Seika)
(B) Black ink SKK black (black ink, manufactured by Dainichi Seika)
(C) Hardener Lamic B Hardener (Isocyanate hardener, manufactured by Dainichi Seika Co., Ltd.)
(D) Diluent Ramic No. 2 solvents (manufactured by Dainichi Seika)

(2) Support layer Lumirror 4AF53 (polyethylene terephthalate film, thickness 3.5 μm, manufactured by Toray Industries, Inc.) or Lumirror 2F51N (polyethylene terephthalate film, thickness 2.0 μm, manufactured by Toray Industries, Inc.) was used as the support layer.

(3) Adhesive layer material TS adhesive (acrylic resin adhesive, manufactured by Seiden Chemical Co., Ltd.) 100 parts by weight, 1 part by weight of Coronate L55E (isocyanate cross-linking agent, manufactured by Nippon Polyurethane Co., Ltd.) is mixed to form an adhesive layer forming resin. A solution was prepared.

(4) Surface protective film As the surface protective film, the following single-sided tape A or protect tape 6312B-60 (thickness 60 μm, manufactured by Sekisui Chemical Co., Ltd., indicated as “# 6312B-60” in the table), protect tape 6328B-60 (60 μm thickness, manufactured by Sekisui Chemical Co., Ltd., indicated as “# 6328B-60” in the table), E-212 (60 μm thickness, manufactured by Sumilon, indicated as “# 212” in the table) or E-200 (65 μm thickness, Any of Sumilon Co., Ltd. (shown as “# 200” in the table) was used.
Single-sided tape A:
0.9 parts by weight of Coronate L55E (isocyanate crosslinking agent, manufactured by Nippon Polyurethane Co., Ltd.) was mixed with 100 parts by weight of SK1498B (acrylic adhesive, manufactured by Soken Chemical Co., Ltd.) to obtain a pressure-sensitive adhesive coating solution. Next, an adhesive coating solution was applied to the corona-treated surface of E5100-50 (polyethylene terephthalate film, thickness 50 μm, single-sided corona-treated product, manufactured by Toyobo Co., Ltd.) with a roll coater so that the thickness of the adhesive layer after drying was 5 μm. did. After drying at 105 ° C. for 2 minutes, an Si release film SP3000-38 (release film, thickness 38 μm, manufactured by Toyo Cloth Co., Ltd.) was attached to the surface of the obtained pressure-sensitive adhesive layer, and single-sided tape A (thickness 55 μm) was attached. Obtained. In addition, the obtained single-sided tape A was used after curing at 40 ° C. for 48 hours.

(5) Release film SP3000-38 (thickness 38 μm, manufactured by Toyo Cloth), SP4020-38 (thickness 38 μm, manufactured by Toyo Cloth) or PET38 × 1 X08 (thickness 38 μm, manufactured by Nippers) was used as a release film.

(6) Preparation of colored support layer On the support layer shown in Table 2 or 3, the colored layer forming resin solution was applied using a gravure coater, and then dried at 80 ° C. for 10 seconds. A colored layer having the thickness shown was formed. Next, the mat layer forming resin solution was applied onto the colored layer using a gravure coater, and then dried at 80 ° C. for 10 seconds to form a mat layer having a thickness shown in Table 2 or 3. This obtained the laminated body (colored support layer) by which support layer / colored layer / mat layer was laminated | stacked.

(7) Preparation of colored single-sided adhesive tape On the release film shown in Table 2 or 3, the adhesive layer forming resin solution was applied using a roll coater, and then heated at 90 ° C for 2 minutes. Or the adhesive layer of the thickness shown in 3 was formed. Next, the pressure-sensitive adhesive layer formed on the release film was bonded to the surface of the support layer of the colored support layer (the surface where the colored layer was not formed). Then, the surface protection film shown in Table 2 or 3 was bonded to the surface of the mat layer, and a pressure roll having a pressure of 0.4 MPa was passed through to obtain a colored single-sided adhesive tape.

(8) Measurement of peel strength (A) of surface protective film A colored single-sided adhesive tape was cut into a 25 mm width strip to prepare a test piece, and the release film was peeled off to expose the adhesive layer. Next, the test piece was bonded to a steel plate (SUS304). Then, the edge part of the surface protection film was grasped with the tensile tester, and according to JISZ0237, the 180 degree direction tensile test was done at the peeling speed of 300 mm / min, and the peeling force (N / 25 mm) was measured.

(9) Measurement of SUS plate 180 ° peel adhesion (B) Double-sided tape 3805 (tape thickness 50 μm, manufactured by Sekisui Chemical Co., Ltd.) on the surface of the mat layer of the laminate before the surface protective film was bonded in (7) above. ) And a polyethylene terephthalate (PET) film having a thickness of 25 μm were further pasted to prepare a laminate having a portion for gripping a tensile tester.
The laminate was cut into a 25 mm strip to produce a test piece, and the release film was peeled off to expose the pressure-sensitive adhesive layer. Next, after placing the test piece on the steel plate (SUS304) so that the adhesive layer of the test piece faces the SUS plate (SUS304), a 2 kg rubber roller was placed on the test piece at a speed of 300 mm / min. By making it reciprocate once, a test piece and a SUS board were stuck, and it left still at 23 degreeC for 30 minutes, and produced the measurement sample.
The grip margin part of this measurement sample was gripped with a tensile tester, and a tensile test in the direction of 180 ° was performed at a peeling speed of 300 mm / min according to JIS Z 0237 to measure the adhesive force (N / 25 mm).

(10) Measurement of Release Force (C) of Release Film A colored single-sided adhesive tape was cut into a 25 mm width strip to prepare a test piece, and the surface protective film side was double-sided tape 3805 (tape thickness 50 μm, Sekisui Chemical Co., Ltd.) It was bonded to a steel plate (SUS304) using an industrial company). Next, the end of the release film was gripped with a tensile tester, and a tensile test in the 180 ° direction was performed at a peeling speed of 300 mm / min according to JIS Z 0237, and the peeling force (N / 25 mm) was measured.

From the measured values obtained, the ratio A / B and the ratio C / A were calculated.

<Evaluation>
The following evaluation was performed about the coloring single-sided adhesive tape obtained by the Example and the comparative example. The results are shown in Table 2 or 3.

(1) Releasability of the release film When the release film is peeled off from the adhesive layer of the colored single-sided adhesive tape, only the release film is peeled off smoothly, and the surface protection film is slightly lifted The case where the surface protective film was peeled off instead of the release film was evaluated as x.

(2) Bondability to adherend When the release film is peeled off from the adhesive layer of the colored single-sided adhesive tape, it is bonded to the polycarbonate plate with a 2 kg rubber roller, and the bonded surface is observed from the polycarbonate plate side. The case where no entanglement or wrinkle was observed was evaluated as ◎, the case where no wrinkle was observed, but the case where slight air entrainment was observed was evaluated as ◯, and the case where wrinkle was generated was evaluated as ×.

(3) Releasability of surface protective film After peeling off the release film from the adhesive layer of the colored single-sided adhesive tape and pasting it to the polycarbonate plate with a 2 kg rubber roller, only the surface protective film is removed. ◎ when peeled off smoothly, no peeling from the adherend was observed, but ○ when the peeling mark of the surface protective film was found on the adhesive surface, the adhesive layer was peeled off from the adherend The case was evaluated as x.

(4) Fingerprint or dirt adhesion After pressing the surface protective film surface of the colored single-sided adhesive tape strongly with a human thumb, the surface protective film is peeled off, and the surface of the matte layer that is the outer surface is removed from the fingerprint or surface protective film. Visually check for smudges, ◎ if no fingerprints or smudges were found, fingerprints were not seen, but if the surface protective film was smudged by adhesive components, ○, fingerprints were seen The case was evaluated as x.

According to the present invention, it is suitably used for fixing and covering a ferrite sheet or a graphite sheet in the manufacture of a portable information terminal, etc. It is possible to provide a colored single-sided adhesive tape that can prevent adhesion of fingerprints or foreign matters.

DESCRIPTION OF SYMBOLS 1 Colored single-sided adhesive tape 2 of this invention Support layer 3 Adhesive layer 4 Colored layer 5 Matte layer 6 Surface protection film 7 Release film 8 Ferrite sheet or graphite sheet

Claims (6)

A pressure-sensitive adhesive layer is provided on one side of the support layer having a thickness of 1 to 4 μm, a colored layer on the other side, and a surface protective film for protecting the colored layer,
The total thickness of the support layer, the pressure-sensitive adhesive layer and the colored layer is 3 to 10 μm,
The ratio (A / B) between the peel strength (A) of the surface protective film and the peel strength (B) in the 180 ° direction with respect to the SUS plate of the pressure-sensitive adhesive layer is 0.6 or less. Colored single-sided adhesive tape. The colored single-sided pressure-sensitive adhesive tape according to claim 1, wherein the peel strength (A) of the surface protective film is 0.1 to 2.5 N / 25 mm. A release film is provided on the pressure-sensitive adhesive layer, and the ratio (C / A) between the peel force (C) of the release film and the peel force (A) of the surface protective film is 0.7 or less. The colored single-sided adhesive tape according to claim 1, wherein the colored single-sided adhesive tape is provided. The colored single-sided pressure-sensitive adhesive tape according to claim 3, wherein the release film has a peeling force (C) of 0.01 to 0.5 N / 25 mm. The colored single-sided adhesive tape according to claim 1, wherein the colored layer is black. 6. The colored single-sided adhesive tape according to claim 1, wherein the colored single-sided adhesive tape is used for fixing and coating a ferrite sheet or a graphite sheet.