JP2015190179A - Confirmation method for construction state of sprayed mortar - Google Patents
Confirmation method for construction state of sprayed mortar Download PDFInfo
- Publication number
- JP2015190179A JP2015190179A JP2014067861A JP2014067861A JP2015190179A JP 2015190179 A JP2015190179 A JP 2015190179A JP 2014067861 A JP2014067861 A JP 2014067861A JP 2014067861 A JP2014067861 A JP 2014067861A JP 2015190179 A JP2015190179 A JP 2015190179A
- Authority
- JP
- Japan
- Prior art keywords
- mortar
- spray
- sprayed
- mass
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、乾式吹付け工法によって吹付けられてなる吹付けモルタルの施工状態を確認するための吹付けモルタルの施工状態の確認方法に関する。 The present invention relates to a method for confirming the construction state of a spraying mortar for confirming the construction state of a spraying mortar that is sprayed by a dry spraying method.
コンクリート構造物にモルタルを吹付けることによって、コンクリート構造物の補修や補強が行われている。具体的には、セメントおよび骨材等の粉体材料と、水および液体混和剤等の液体材料とを、別々に調製した後、それらを吹付け対象となるコンクリート構造物の近傍までホース等で移送する。そして、粉体材料と液体材料とを吹付け用ノズル内で混合しつつ圧縮空気と共に噴射することで、コンクリート構造物にモルタルを吹付ける方法が知られている（乾式吹付け工法）。 The concrete structure is repaired or reinforced by spraying mortar on the concrete structure. Specifically, powder materials such as cement and aggregate and liquid materials such as water and liquid admixture are prepared separately, and then they are hose to the vicinity of the concrete structure to be sprayed. Transport. And the method of spraying mortar on a concrete structure is known by spraying with compressed air, mixing powder material and liquid material within the nozzle for spraying (dry spraying method).
このような乾式吹付け工法では、吹付けられたモルタル（以下、吹付けモルタルとも記す）の施工状態を確認することによって、吹付けモルタルの品質（例えば、流動性や硬化後の圧縮強度等）の管理が行われる。具体的には、施工部位に付着している吹付けモルタルの質量（吹付け量）や吹付けモルタルの液粉体比を確認し、その結果に基づいて吹付け用ノズルから噴射される液体材料の量を調節することで、吹付けモルタルの品質管理が行われている（特許文献１参照）。 In such a dry-type spraying method, the quality of sprayed mortar (for example, fluidity and compressive strength after curing, etc.) is confirmed by confirming the construction state of the sprayed mortar (hereinafter also referred to as sprayed mortar). Management is performed. Specifically, the mass of the sprayed mortar (spray amount) adhering to the construction site and the liquid / powder ratio of the sprayed mortar are confirmed, and the liquid material sprayed from the spray nozzle based on the result The quality control of the sprayed mortar is performed by adjusting the amount of (see Patent Document 1).
しかしながら、上記のような乾式吹付け工法では、吹付け用ノズルから噴射された粉体材料および液体材料の一部がリバウンドとして施工箇所から落下したり飛散したりするため、実際に噴射された量（具体的には、計器等で把握される量）に基づいて吹付け量や液粉体比を算出することができない。このため、吹付け量や液粉体比に関する施工状態を確認する際には、施工現場において採取し、又は、作製したサンプルを用いて吹付け量や液粉体比の測定を行う必要があるため、施工状態を確認するのに長時間を要すると共に、繁雑な作業が必要となる。 However, in the dry spray method as described above, the amount of powder material and liquid material sprayed from the spray nozzle falls from the construction site as a rebound and scatters. The spray amount and the liquid powder ratio cannot be calculated based on (specifically, the amount grasped by a meter or the like). For this reason, when confirming the construction state related to the spraying amount and the liquid / powder ratio, it is necessary to collect the spraying amount and the liquid / powder ratio using the sample collected at the construction site. For this reason, it takes a long time to check the construction state, and complicated work is required.
そこで、本発明は、乾式吹付け工法によって吹付けられてなる吹付けモルタルの施工状態を迅速かつ容易に確認することができる吹付けモルタルの施工状態の確認方法を提供することを課題とする。 Then, this invention makes it a subject to provide the confirmation method of the construction state of the spraying mortar which can confirm the construction state of the spraying mortar sprayed by the dry-type spraying construction method quickly and easily.
本発明に係る吹付けモルタルの施工状態の確認方法は、乾式吹付け工法によって吹付けられてなる吹付けモルタルの施工状態を確認する吹付けモルタルの施工状態の確認方法であって、粉体材料と液体材料とを所定の割合で吹付け用ノズルから噴射して所定厚みの基準モルタルを形成する基準形成工程と、該基準形成工程において吹付け用ノズルから噴射された粉体材料と液体材料との合計質量に対する基準モルタルの質量割合をモルタル吹付け率として算出する吹付け率算出工程と、吹付けモルタルを形成する際に吹付け用ノズルから噴射される粉体材料と液体材料との合計質量にモルタル吹付け率を乗じて吹付けモルタルの質量の推定値を算出する吹付け量推定工程とを備えることを特徴とする。 The method for confirming the construction state of the spraying mortar according to the present invention is a method for confirming the construction state of the spraying mortar for confirming the construction state of the spraying mortar that is sprayed by the dry spraying method. Forming a reference mortar having a predetermined thickness by spraying the liquid material and the liquid material from the spray nozzle at a predetermined ratio, and the powder material and the liquid material sprayed from the spray nozzle in the reference forming step The total mass of the powder material and the liquid material sprayed from the spray nozzle when forming the spray mortar, and the spray rate calculation step of calculating the mass ratio of the reference mortar with respect to the total mass of the mortar And a spray amount estimating step of calculating an estimated value of the mass of the sprayed mortar by multiplying by the mortar spray rate.
斯かる構成によれば、吹付け率算出工程で得られるモルタル吹付け率は、吹付け用ノズルから噴射される粉体材料と液体材料との合計質量のうち、どの程度の量が基準モルタルとして形成されるかを示すものである。そして、斯かるモルタル吹付け率を用いて吹付け量推定工程を行うことで、例えば、実際の施工現場において基準モルタルと同等の条件で吹付けられた吹付けモルタルの質量（以下、吹付け量とも記す）を吹付け用ノズルから噴射される粉体材料および液体材料の合計質量から推定することができる。これにより、施工現場で吹付けモルタルのサンプルを採取し又は作製して吹付け量を実際に測定する場合よりも、迅速且つ容易に、吹付け量に関する吹付けモルタルの施工状態を確認することができる。 According to such a configuration, the mortar spray rate obtained in the spray rate calculation step is the amount of the total mass of the powder material and the liquid material injected from the spray nozzle as the reference mortar. It shows whether it is formed. And by performing a spraying amount estimation process using such a mortar spraying rate, for example, the mass of sprayed mortar (hereinafter referred to as spraying amount) sprayed under the same conditions as the standard mortar at the actual construction site. Can also be estimated from the total mass of the powder material and the liquid material ejected from the spray nozzle. This makes it possible to quickly and easily confirm the spraying mortar construction state with respect to the spraying amount, compared to the case where the spraying mortar sample is collected or produced at the construction site and the spraying amount is actually measured. it can.
発明に係る吹付けモルタルの施工状態の確認方法は、乾式吹付け工法によって吹付けられてなる吹付けモルタルの施工状態を確認する吹付けモルタルの施工状態の確認方法であって、粉体材料と液体材料とを所定の割合で吹付け用ノズルから噴射して所定厚みの基準モルタルを形成する基準形成工程と、該基準形成工程において吹付け用ノズルから噴射された粉体材料の質量に対する基準モルタル中の粉体材料の質量割合を粉体吹付け率として算出し、基準形成工程において吹付け用ノズルから噴射された液体材料の質量に対する基準モルタル中の液体材料の質量割合を液体吹付け率として算出する吹付け率算出工程と、吹付けモルタルを形成する際に吹付け用ノズルから噴射される粉体材料の質量に粉体吹付け率を乗じて吹付けモルタル中の粉体材料の質量の推定値を算出し、吹付けモルタルを形成する際に吹付け用ノズルから噴射される液体材料の質量に液体吹付け率を乗じて吹付けモルタル中の液体材料の質量の推定値を算出し、粉体材料の質量の推定値と液体材料の質量の推定値とから吹付けモルタルの液粉体比の推定値を算出する液粉体比推定工程とを備えることを特徴とする。 The method for confirming the construction state of the spraying mortar according to the invention is a method for confirming the construction state of the spraying mortar for confirming the construction state of the spraying mortar that is sprayed by the dry spraying method. A reference forming step for forming a reference mortar having a predetermined thickness by spraying a liquid material from a spray nozzle at a predetermined ratio, and a reference mortar for the mass of the powder material injected from the spray nozzle in the reference forming step The mass ratio of the powder material in the inside is calculated as the powder spray rate, and the mass ratio of the liquid material in the reference mortar with respect to the mass of the liquid material injected from the spray nozzle in the reference forming step is used as the liquid spray rate. In the spraying mortar, multiplying the mass of the powder material sprayed from the spray nozzle when forming the spraying mortar by the powder spraying rate Calculate the estimated value of the mass of the powder material and multiply the mass of the liquid material sprayed from the spray nozzle when forming the spray mortar by the liquid spray rate to determine the mass of the liquid material in the spray mortar. A liquid-powder ratio estimation step of calculating an estimated value and calculating an estimated value of the liquid-powder ratio of the sprayed mortar from the estimated value of the mass of the powder material and the estimated value of the mass of the liquid material And
斯かる構成によれば、吹付け率算出工程で得られる粉体吹付け率および液体吹付け率は、吹付け用ノズルから噴射される粉体材料および液体材料のそれぞれの質量のうち、どの程度の量が基準モルタルとして形成されるかを示すものである。そして、斯かる粉体吹付け率および液体吹付け率を用いて液粉体比推定工程を行うことで、例えば、実際の施工現場において基準モルタルと同等の条件で吹付けられた吹付けモルタル中の粉体材料および液体材料の質量を吹付け用ノズルから噴射される粉体材料および液体材料の合計質量から推定することができる。これにより、吹付けモルタルのサンプルを採取し又は作製して吹付けモルタル中の粉体材料および液体材料の質量を実際に測定し、液粉体比を算出する場合よりも、迅速且つ容易に、液粉体比に関する吹付けモルタルの施工状態を確認することができる。 According to such a configuration, the powder spray rate and the liquid spray rate obtained in the spray rate calculation step are the extent of the respective masses of the powder material and the liquid material ejected from the spray nozzle. It is shown whether the amount of is formed as a reference mortar. And by performing the liquid powder ratio estimation process using such powder spray rate and liquid spray rate, for example, in the sprayed mortar sprayed under the same conditions as the standard mortar at the actual construction site The mass of the powder material and the liquid material can be estimated from the total mass of the powder material and the liquid material ejected from the spray nozzle. Thus, it is quicker and easier than taking a sample of sprayed mortar and actually measuring the mass of the powder material and liquid material in the sprayed mortar and calculating the liquid powder ratio, It is possible to confirm the application state of the sprayed mortar related to the liquid powder ratio.
以上のように、本発明によれば、乾式吹付け工法によって吹付けられてなる吹付けモルタルの施工状態を迅速かつ容易に確認することができる。 As mentioned above, according to this invention, the construction state of the spraying mortar sprayed by the dry spraying method can be confirmed quickly and easily.
以下、本発明の実施形態について説明する。 Hereinafter, embodiments of the present invention will be described.
本実施形態に係る吹付けモルタルの施工状態の確認方法（以下、施工確認方法とも記す）は、乾式吹付け工法によって吹付けられた吹付けモルタルの施工状態として、施工位置に形成された吹付けモルタルの質量（吹付け量）、又は、形成された吹付けモルタルの液粉体比の推定値を確認するものである。 The method for confirming the construction state of the spray mortar according to the present embodiment (hereinafter also referred to as construction confirmation method) is a spray formed at the construction position as the construction state of the spray mortar sprayed by the dry spray method. The estimated value of the mass (spraying amount) of the mortar or the liquid powder ratio of the formed spraying mortar is confirmed.
具体的には、斯かる施工確認方法は、粉体材料と液体材料とを所定の割合で吹付け用ノズルから噴射して所定厚みの基準モルタルを形成する基準形成工程と、基準形成工程において吹付け用ノズルから噴射された粉体材料および液体材料に対する吹付け率を算出する吹付け率算出工程と、該吹付け率を用いて実際に吹付ける粉体材料および液体材料から吹付けモルタルの施工状態を推定する施工状態推定工程とを備える。 Specifically, such a construction confirmation method includes a reference forming step in which a powder material and a liquid material are sprayed from a spray nozzle at a predetermined ratio to form a reference mortar having a predetermined thickness. A spray rate calculation step for calculating the spray rate for the powder material and the liquid material sprayed from the nozzle for spraying, and the construction of the spray mortar from the powder material and the liquid material actually sprayed using the spray rate A construction state estimation step for estimating the state.
基準形成工程では、乾式吹付け工法によって粉体材料および液体材料を所定サイズの型枠内に吹付けて基準モルタルを形成する。この際、基準モルタルが所定の厚みとなるまでの時間（以下、吹付け時間とも記す）を測定する。具体的には、深さの異なる複数の型枠のそれぞれに厚みの異なる基準モルタルを形成する際の吹付け時間を型枠毎に測定する。 In the reference forming step, the reference mortar is formed by spraying the powder material and the liquid material into a mold having a predetermined size by a dry spraying method. At this time, the time until the reference mortar reaches a predetermined thickness (hereinafter also referred to as spraying time) is measured. Specifically, the spraying time for forming a reference mortar having a different thickness on each of a plurality of molds having different depths is measured for each mold.
吹付け率算出工程では、基準形成工程において吹付け用ノズルから噴射された粉体材料と液体材料との合計質量に対する基準モルタルの質量割合がモルタル吹付け率として算出される。又は、吹付け率算出工程では、基準形成工程において吹付け用ノズルから噴射された粉体材料の質量に対する基準モルタル中の粉体材料の質量割合が粉体吹付け率として算出される。また、基準形成工程において吹付け用ノズルから噴射された液体材料の質量に対する基準モルタル中の液体材料の質量割合が液体吹付け率として算出される。 In the spray rate calculating step, the mass ratio of the reference mortar to the total mass of the powder material and the liquid material injected from the spray nozzle in the reference forming step is calculated as the mortar spray rate. Alternatively, in the spray rate calculation step, the mass ratio of the powder material in the reference mortar to the mass of the powder material sprayed from the spray nozzle in the reference forming step is calculated as the powder spray rate. Moreover, the mass ratio of the liquid material in the reference mortar to the mass of the liquid material ejected from the spray nozzle in the reference forming step is calculated as the liquid spray rate.
吹付け用ノズルから噴射された粉体材料および液体材料それぞれの質量は、吹付け用ノズルから単位時間当たりに噴射される粉体材料および液体材料の質量（以下、噴射速度とも記す）が既知の場合には、該噴射速度に吹付け時間を乗じて得ることができる。または、吹付け用ノズルへ粉体材料を供給する流路に粉体流量計を設置し、吹付け用ノズルへ液体材料を供給する流路に液体流量計を設置し、単位時間当たりに吹付け用ノズルへ供給される粉体材料および液体材料の質量（以下、流量とも記す）を各流量計で測定し、該流量に吹付け時間を乗じることで、粉体材料および液体材料それぞれの質量を得てもよい。または、各流量計の測定値が変動する場合には吹付け時間における各流量計で測定される質量の積算量として粉体材料および液体材料それぞれの質量を得ることもできる。または、粉体材料および液体材料の消費量（例えば、原料タンク内の原料の減少量）を確認することで、吹付け用ノズルから噴射された質量を把握してもよい。 The masses of the powder material and the liquid material injected from the spray nozzle are known as the masses of the powder material and the liquid material (hereinafter also referred to as injection speed) injected per unit time from the spray nozzle. In some cases, the injection speed can be obtained by multiplying the spraying time. Alternatively, a powder flow meter is installed in the flow path that supplies the powder material to the spray nozzle, and a liquid flow meter is installed in the flow path that supplies the liquid material to the spray nozzle, and sprays per unit time. The mass of the powder material and the liquid material (hereinafter also referred to as the flow rate) supplied to the nozzle for the nozzle is measured with each flow meter, and the mass of the powder material and the liquid material is calculated by multiplying the flow rate by the spraying time. May be obtained. Or when the measured value of each flow meter fluctuates, the mass of each of the powder material and the liquid material can be obtained as the integrated amount of the mass measured by each flow meter during the spraying time. Or you may grasp | ascertain the mass injected from the nozzle for spraying by confirming the consumption (for example, reduction amount of the raw material in a raw material tank) of a powder material and a liquid material.
基準モルタルの質量は、型枠内に基準モルタルが充填された状態で質量を測定し、得られた測定結果から型枠の質量を差し引くことで算出することができる。また、液体材料が加熱することで蒸発する場合（例えば、液体材料が水のみから構成されている場合）には、基準モルタル中の液体材料の質量は、基準モルタルの一部または全部を質量変化が生じなくなるまで加熱した際の加熱前後の質量差となる。一方、斯かる場合における基準モルタル中の粉体材料の質量は、加熱後の基準モルタルの質量となる。又は、液体材料が、加熱することで蒸発する成分（例えば、水等）に対して蒸発しない成分（例えば、ポリマー固形分等）を所定の割合で含有している場合には、基準モルタル中の液体材料の質量は、型枠に吹付けた基準モルタルの一部または全部を質量変化が生じなくなるまで加熱した際の加熱前後の質量差（即ち、吹付けられた液体材料中の蒸発成分の質量）と、該質量差に対する蒸発しない成分の質量（吹付けられた液体材料中の蒸発しない成分の質量）との合計になる。一方、斯かる場合における基準モルタル中の粉体材料の質量は、加熱後の基準モルタルの質量と、上記の吹付けられた液体材料中の蒸発しない成分の質量との質量差となる。 The mass of the reference mortar can be calculated by measuring the mass in a state in which the mold is filled with the reference mortar and subtracting the mass of the mold from the obtained measurement result. In addition, when the liquid material evaporates by heating (for example, when the liquid material is composed only of water), the mass of the liquid material in the reference mortar changes in part or all of the reference mortar. It becomes a mass difference before and after heating when heating until no longer occurs. On the other hand, the mass of the powder material in the reference mortar in such a case is the mass of the reference mortar after heating. Or, when the liquid material contains a component (for example, polymer solid content) that does not evaporate with respect to a component that evaporates by heating (for example, water) in a predetermined ratio, The mass of the liquid material is the mass difference before and after heating when a part or all of the reference mortar sprayed on the mold is heated until mass change does not occur (that is, the mass of the evaporated component in the sprayed liquid material). ) And the mass of the component that does not evaporate with respect to the mass difference (the mass of the component that does not evaporate in the sprayed liquid material). On the other hand, the mass of the powder material in the reference mortar in such a case is a mass difference between the mass of the reference mortar after heating and the mass of the component that does not evaporate in the sprayed liquid material.
施工状態推定工程は、吹付けモルタルを形成する際に吹付け用ノズルから噴射される粉体材料と液体材料との合計質量にモルタル吹付け率を乗じて吹付けモルタルの質量（以下、モルタル吹付け量とも記す）の推定値を算出する吹付け量推定工程から構成される。または、施工状態推定工程は、吹付けモルタルを形成する際に吹付け用ノズルから噴射される粉体材料の質量に粉体吹付け率を乗じて吹付けモルタル中の粉体材料の質量（以下、粉体吹付け量とも記す）の推定値を算出し、吹付けモルタルを形成する際に吹付け用ノズルから噴射される液体材料の質量に液体吹付け率を乗じて吹付けモルタル中の液体材料の質量（以下、液体吹付け量とも記す）の推定値を算出し、粉体材料の質量の推定値と液体材料の質量の推定値とから吹付けモルタルの液粉体比の推定値を算出する液粉体比推定工程から構成される。または、施工状態推定工程は、前記吹付け量推定工程および前記液粉体比推定工程から構成されてもよい。 The construction state estimation process is performed by multiplying the total mass of the powder material and the liquid material sprayed from the spray nozzle when forming the spray mortar by the mortar spray rate (hereinafter referred to as mortar spray mortar). This is composed of a spray amount estimation step for calculating an estimated value). Alternatively, in the construction state estimation step, the mass of the powder material in the spraying mortar (hereinafter referred to as the powder material in the spraying mortar by multiplying the mass of the powder material sprayed from the spray nozzle when forming the spraying mortar by the powder spray rate) The liquid in the spray mortar is calculated by multiplying the mass of the liquid material sprayed from the spray nozzle when forming the spray mortar by the liquid spray rate. Calculate the estimated value of the mass of the material (hereinafter also referred to as the liquid spray amount) and calculate the estimated value of the liquid-to-powder ratio of the sprayed mortar from the estimated mass of the powder material and the estimated mass of the liquid material. It consists of the liquid powder ratio estimation process to calculate. Alternatively, the construction state estimation step may include the spray amount estimation step and the liquid powder ratio estimation step.
吹付け用ノズルから噴射された粉体材料および液体材料それぞれの質量は、噴射速度が既知の場合には、該噴射速度に吹付け時間（具体的には、基準モルタルの厚みと同等の厚みとなる間での時間）を乗じて得ることができる。または、吹付け用ノズルへ粉体材料を供給する流路に粉体流量計を設置し、吹付け用ノズルへ液体材料を供給する流路に液体流量計を設置し、粉体材料および液体材料の流量を各流量計で測定し、該流量に吹付け時間（具体的には、基準モルタルの厚みと同等の厚みとなる間での時間）を乗じて得ることもできる。または、粉体材料および液体材料の消費量（例えば、原料タンク内の原料の減少量）を確認することで、吹付け用ノズルから噴射された質量を把握してもよい。 When the injection speed is known, the mass of each of the powder material and the liquid material injected from the spray nozzle is equal to the spray time (specifically, the thickness equivalent to the thickness of the reference mortar). Multiply by the time between). Alternatively, a powder flow meter is installed in the flow path for supplying the powder material to the spray nozzle, and a liquid flow meter is installed in the flow path for supplying the liquid material to the spray nozzle. It is also possible to obtain the flow rate by multiplying the flow rate by a spraying time (specifically, the time required to achieve a thickness equivalent to the thickness of the reference mortar). Or you may grasp | ascertain the mass injected from the nozzle for spraying by confirming the consumption (for example, reduction amount of the raw material in a raw material tank) of a powder material and a liquid material.
吹付け量推定工程で得られるモルタル吹付け量の推定値は、基準モルタルを形成する際の吹付け条件と同等の条件（具体的には、同等の厚み）で吹付けられた吹付けモルタルの吹付け量に対応するものである。このため、モルタル吹付け量の推定を確認することで、実際に吹付けられた吹付けモルタルの吹付け量に関する施工状態を確認することが可能となる。 The estimated value of the mortar spray amount obtained in the spray amount estimation step is the same as that of the spray mortar sprayed under the same condition (specifically, the same thickness) as the spray condition when forming the reference mortar. This corresponds to the spray amount. For this reason, it becomes possible to confirm the construction state regarding the spraying amount of the sprayed mortar actually sprayed by confirming the estimation of the spraying amount of the mortar.
また、液粉体比推定工程で得られる粉体吹付け量および液体吹付け量の推定値は、基準モルタルを形成する際の吹付け条件と同等の条件（具体的には、同等の厚み）で吹付けられた吹付けモルタルの粉体吹付け量および液体吹付け量に対応するものである。このため、粉体吹付け量および液体吹付け量の推定値から算出される液粉体比の推定値は、実際に吹付けられた吹付けモルタルの液粉体比に対応するものとなる。これにより、液粉体比の推定値を確認することで、実際に吹付けられた吹付けモルタルの液粉体比に関する施工状態を確認することが可能となる。 Moreover, the estimated value of the powder spray amount and the liquid spray amount obtained in the liquid powder ratio estimation step is the same condition (specifically, the same thickness) as the spray condition when forming the reference mortar. This corresponds to the powder spray amount and the liquid spray amount of the spray mortar sprayed in (1). For this reason, the estimated value of the liquid powder ratio calculated from the estimated value of the powder spray amount and the liquid spray amount corresponds to the liquid powder ratio of the sprayed mortar actually sprayed. Thereby, it becomes possible to confirm the construction state regarding the liquid powder ratio of the sprayed mortar actually sprayed by confirming the estimated value of the liquid powder ratio.
そして、上記のような施工状態の推定値を確認し管理することで、吹付けモルタルの品質管理を行うことが可能となる。 And it becomes possible to perform quality control of spraying mortar by checking and managing the estimated value of the above construction states.
以上のように、本発明に係る吹付けモルタルの施工確認方法によれば、乾式吹付け工法によって吹付けられてなる吹付けモルタルの施工状態を迅速かつ容易に確認することができる。 As mentioned above, according to the construction confirmation method of the spraying mortar which concerns on this invention, the construction state of the spraying mortar sprayed by the dry-type spraying construction method can be confirmed quickly and easily.
即ち、吹付け率算出工程で得られるモルタル吹付け率は、吹付け用ノズルから噴射される粉体材料と液体材料との合計質量のうち、どの程度の量が基準モルタルとして形成されるかを示すものである。そして、斯かるモルタル吹付け率を用いて吹付け量推定工程を行うことで、例えば、実際の施工現場において基準モルタルと同等の条件で吹付けられた吹付けモルタルの質量（以下、吹付け量とも記す）を吹付け用ノズルから噴射される粉体材料および液体材料の合計量から推定することができる。これにより、施工現場で吹付けモルタルのサンプルを採取し又は作製して吹付け量を実際に測定する場合よりも、迅速且つ容易に、吹付け量に関する吹付けモルタルの施工状態を確認することができる。 That is, the mortar spray rate obtained in the spray rate calculation step is the amount of the total mass of the powder material and the liquid material injected from the spray nozzle that is formed as the reference mortar. It is shown. And by performing a spraying amount estimation process using such a mortar spraying rate, for example, the mass of sprayed mortar (hereinafter referred to as spraying amount) sprayed under the same conditions as the standard mortar at the actual construction site. Can also be estimated from the total amount of powder material and liquid material ejected from the spray nozzle. This makes it possible to quickly and easily confirm the spraying mortar construction state with respect to the spraying amount, compared to the case where the spraying mortar sample is collected or produced at the construction site and the spraying amount is actually measured. it can.
また、吹付け率算出工程で得られる粉体吹付け率および液体吹付け率は、吹付け用ノズルから噴射される粉体材料および液体材料のそれぞれの質量のうち、どの程度の量が基準モルタルとして形成されるかを示すものである。そして、斯かる粉体吹付け率および液体吹付け率を用いて液粉体比推定工程を行うことで、例えば、実際の施工現場において基準モルタルと同等の条件で吹付けられた吹付けモルタル中の粉体材料および液体材料の質量を吹付け用ノズルから噴射される粉体材料および液体材料の合計質量から推定することができる。これにより、施工現場で吹付けモルタルのサンプルを採取し又は作製して吹付けモルタル中の粉体材料および液体材料の質量を実際に測定し、液粉体比を算出する場合よりも、迅速且つ容易に、液粉体比に関する吹付けモルタルの施工状態を確認することができる。 In addition, the powder spray rate and the liquid spray rate obtained in the spray rate calculation step are the same as the reference mortar of the mass of the powder material and liquid material injected from the spray nozzle. Is formed. And by performing the liquid powder ratio estimation process using such powder spray rate and liquid spray rate, for example, in the sprayed mortar sprayed under the same conditions as the standard mortar at the actual construction site The mass of the powder material and the liquid material can be estimated from the total mass of the powder material and the liquid material ejected from the spray nozzle. This makes it possible to collect or produce a sample of sprayed mortar at the construction site, actually measure the mass of the powder material and liquid material in the sprayed mortar, and calculate the liquid-to-powder ratio more quickly. The sprayed mortar construction state with respect to the liquid powder ratio can be easily confirmed.
また、施工現場において吹付け用ノズルに供給される粉体材料および液体材料の流量を流量計等を用いて把握することができる場合には、連続的に変動する流量毎や流量の合計に対して粉体吹付け率や液体吹付け率、又は、モルタル吹付け率を乗じることで、吹付け量の推定や、液粉体比の推定を連続的に行うことができる。 In addition, if the flow rate of the powder material and liquid material supplied to the spray nozzle at the construction site can be grasped using a flow meter, etc., for each continuously changing flow rate or the total flow rate, By multiplying the powder spray rate, the liquid spray rate, or the mortar spray rate, it is possible to continuously estimate the spray amount and estimate the liquid powder ratio.
以下、本発明の実施例について説明する。 Examples of the present invention will be described below.
１．基準形成工程
基準モルタルを形成する粉体材料および液体材料を深さの異なる５０ｃｍ角の複数の型枠内に乾式吹付け工法によって吹付けて厚みの異なる同一配合の基準モルタルを形成した。この際、基準モルタルが各型枠内で所定の厚さ（以下、吹付け厚みとも記す）になるまでの時間（以下、吹付け時間とも記す）を測定した。吹付け厚みは、下記表１に示す。
基準モルタルを形成する際に吹付け用ノズルから噴射された粉体材料および液体材料それぞれの質量は、吹付け用ノズルへ粉体材料を供給する流路に粉体流量計を設置し、吹付け用ノズルへ液体材料を供給する流路に液体流量計を設置することで、各流量計で把握される吹付け時間における質量の積算量である。各吹付け時間における粉体材料および液体材料の積算量は、下記表１に示す。
1. Reference Forming Step A powder material and a liquid material forming the reference mortar were sprayed into a plurality of 50 cm square molds having different depths by a dry spraying method to form a reference mortar having the same composition with different thicknesses. At this time, the time (hereinafter also referred to as spraying time) until the reference mortar reached a predetermined thickness (hereinafter also referred to as spraying thickness) in each mold was measured. The spray thickness is shown in Table 1 below.
The mass of the powder material and the liquid material sprayed from the spray nozzle when forming the reference mortar is set by a powder flow meter installed in the flow path for supplying the powder material to the spray nozzle. By installing a liquid flow meter in the flow path for supplying the liquid material to the nozzle for use, it is an integrated amount of mass in the spraying time grasped by each flow meter. The accumulated amounts of the powder material and the liquid material at each spraying time are shown in Table 1 below.
２．吹付け率算出工程
基準形成工程において各吹付け厚みの基準モルタルを形成した際のモルタル吹付け率、粉体吹付け率、および、液体吹付け率を上記の方法で算出した。モルタル吹付け率、粉体吹付け率、および、液体吹付け率は、下記表１に示す。
また、各吹付け率とそれに対応する吹付け時間との関係をまとめたものを下記表２に示す。
2. Spraying rate calculation step The mortar spraying rate, powder spraying rate, and liquid spraying rate when the reference mortar of each spraying thickness was formed in the reference forming step were calculated by the above method. The mortar spray rate, powder spray rate, and liquid spray rate are shown in Table 1 below.
Table 2 below summarizes the relationship between each spray rate and the corresponding spray time.
３．施工状態推定工程
５０ｃｍ角の型枠に基準モルタルと同一配合で粉体材料および液体材料を乾式吹付け工法によって吹付けることで吹付けモルタルを形成した。吹付けモルタルを形成する際に吹付け用ノズルから噴射された粉体材料および液体材料それぞれの質量は、粉体材料および液体材料の各流量とした。該流量は、吹付け用ノズルへ粉体材料を供給する流路に粉体流量計を設置し、吹付け用ノズルへ液体材料を供給する流路に液体流量計を設置し、各流量計を用いて測定されたものである。具体的には、吹付け開始３０秒後および３００秒後の各流量を表３に示す。また、粉体材料の流量（流量計表示値）および液体材料の流量（流量計表示値）から算出された液粉体比を「液粉体比（流量計表示値）」として、下記表３に示す。
3. Construction state estimation process A spraying mortar was formed by spraying a powder material and a liquid material on a 50 cm square mold with the same composition as the reference mortar by a dry spraying method. The masses of the powder material and the liquid material ejected from the spray nozzle when forming the spray mortar were the respective flow rates of the powder material and the liquid material. The flow rate is determined by installing a powder flow meter in the flow path for supplying the powder material to the spray nozzle, installing a liquid flow meter in the flow path for supplying the liquid material to the spray nozzle, It was measured using. Specifically, Table 3 shows the flow rates 30 seconds and 300 seconds after the start of spraying. In addition, the liquid / powder ratio calculated from the flow rate of the powder material (flow meter display value) and the flow rate of the liquid material (flow meter display value) is referred to as “liquid powder ratio (flow meter display value)”. Shown in
粉体材料の流量（流量計表示値）と液体材料の流量（流量計表示値）との合計に表２の吹付け時間に対応するモルタル吹付け率を乗じてモルタル吹付け量の推定値を算出した。また、粉体材料の流量（流量計表示値）に表２の吹付け時間に対応する粉体吹付け率を乗じて単位時間当たりの粉体吹付け量の推定値を算出した。また、液体材料の流量（流量計表示値）に表２の吹付け時間に対応する液体吹付け率を乗じて単位時間当たりの液体吹付け量の推定値を算出した。算出した粉体吹付け量と液体吹付け量の各推定値から液粉体比の推定値を算出した。各推定値については、下記表３に示す。 Multiply the total flow rate of the powder material (flow meter display value) and the flow rate of the liquid material (flow meter display value) by the mortar spray rate corresponding to the spray time in Table 2 to obtain the estimated value of the mortar spray amount. Calculated. Moreover, the estimated value of the powder spraying amount per unit time was calculated by multiplying the powder material flow rate (flow meter display value) by the powder spraying rate corresponding to the spraying time in Table 2. Moreover, the estimated value of the amount of liquid spraying per unit time was calculated by multiplying the liquid material flow rate (flow meter display value) by the liquid spraying rate corresponding to the spraying time in Table 2. An estimated value of the liquid powder ratio was calculated from each estimated value of the calculated powder spray amount and liquid spray amount. Each estimated value is shown in Table 3 below.
４．まとめ
上記のように、各流量計の表示値から吹付けモルタルの吹付け量および液粉体比の推定値を得ることができる。このため、各流量計の表示値を連続的に把握し、該連続値から各推定値を算出することで、得られる各推定値を確認して管理することにより、吹付けモルタルの品質管理を連続的に行うことができる。
4). Summary As described above, the estimated value of the spray amount of the spray mortar and the liquid powder ratio can be obtained from the display value of each flow meter. For this reason, by continuously grasping the display value of each flow meter and calculating each estimated value from the continuous value, by checking and managing each estimated value obtained, quality control of the sprayed mortar is achieved. Can be done continuously.
なお、吹付け用ノズルへの粉体の供給をロータリーガンで行う場合には、ローター回転数が３５Ｈｚで、無負荷圧力が１．２ＭＰａのとき、粉体材料の流量が概ね２５ｋｇ／ｍｉｎ以上３０ｋｇ／ｍｉｎ以下であることから、型枠に吹付けたモルタルの適正液粉体比を１０％以上２０％以下とすると、下記のような施工管理基準を設定することができる。具体的には、粉体材料の流量は、２５ｋｇ／ｍｉｎ以上３０ｋｇ／ｍｉｎ以下であることが好ましく、粉体吹付け量は、２０．８ｋｇ／ｍｉｎ以上２４．９ｋｇ／ｍｉｎ以下（流量の８３％）であることが好ましい。また、液体材料の流量は、２．６ｋｇ／ｍｉｎ以上４．３ｋｇ／ｍｉｎ以下であることが好ましく、液体吹付け量は、２．５ｋｇ／ｍｉｎ以上４．２ｋｇ／ｍｉｎ以下（流量の９８％）であることが好ましい。 When supplying the powder to the spray nozzle with a rotary gun, the flow rate of the powder material is approximately 25 kg / min to 30 kg when the rotor rotation speed is 35 Hz and the no-load pressure is 1.2 MPa. Therefore, when the appropriate liquid powder ratio of the mortar sprayed on the mold is 10% or more and 20% or less, the following construction management standard can be set. Specifically, the flow rate of the powder material is preferably 25 kg / min or more and 30 kg / min or less, and the powder spraying amount is 20.8 kg / min or more and 24.9 kg / min or less (83% of the flow rate). ) Is preferable. The flow rate of the liquid material is preferably 2.6 kg / min or more and 4.3 kg / min or less, and the liquid spray amount is 2.5 kg / min or more and 4.2 kg / min or less (98% of the flow rate). It is preferable that
Claims (2)
粉体材料と液体材料とを所定の割合で吹付け用ノズルから噴射して所定厚みの基準モルタルを形成する基準形成工程と、
該基準形成工程において吹付け用ノズルから噴射された粉体材料と液体材料との合計質量に対する基準モルタルの質量割合をモルタル吹付け率として算出する吹付け率算出工程と、
吹付けモルタルを形成する際に吹付け用ノズルから噴射される粉体材料と液体材料との合計質量にモルタル吹付け率を乗じて吹付けモルタルの質量の推定値を算出する吹付け量推定工程と
を備えることを特徴とする吹付けモルタルの施工状態の確認方法。 It is a method for confirming the construction state of a spraying mortar that confirms the construction state of the spraying mortar that is sprayed by a dry spraying method,
A reference forming step of forming a reference mortar of a predetermined thickness by spraying a powder material and a liquid material from a spray nozzle at a predetermined ratio;
A spray rate calculating step of calculating a mass ratio of the reference mortar as a mortar spray rate with respect to a total mass of the powder material and the liquid material sprayed from the spray nozzle in the reference forming step;
A spray amount estimation step of calculating an estimated value of the mass of the sprayed mortar by multiplying the total mass of the powder material and the liquid material sprayed from the spray nozzle when forming the spray mortar by the mortar spray rate A method for confirming the construction state of sprayed mortar, comprising:
粉体材料と液体材料とを所定の割合で吹付け用ノズルから噴射して所定厚みの基準モルタルを形成する基準形成工程と、
該基準形成工程において吹付け用ノズルから噴射された粉体材料の質量に対する基準モルタル中の粉体材料の質量割合を粉体吹付け率として算出し、基準形成工程において吹付け用ノズルから噴射された液体材料の質量に対する基準モルタル中の液体材料の質量割合を液体吹付け率として算出する吹付け率算出工程と、
吹付けモルタルを形成する際に吹付け用ノズルから噴射される粉体材料の質量に粉体吹付け率を乗じて吹付けモルタル中の粉体材料の質量の推定値を算出し、吹付けモルタルを形成する際に吹付け用ノズルから噴射される液体材料の質量に液体吹付け率を乗じて吹付けモルタル中の液体材料の質量の推定値を算出し、粉体材料の質量の推定値と液体材料の質量の推定値とから吹付けモルタルの液粉体比の推定値を算出する液粉体比推定工程と
を備えることを特徴とする吹付けモルタルの施工状態の確認方法。 It is a method for confirming the construction state of a spraying mortar that confirms the construction state of the spraying mortar that is sprayed by a dry spraying method,
A reference forming step of forming a reference mortar of a predetermined thickness by spraying a powder material and a liquid material from a spray nozzle at a predetermined ratio;
The mass ratio of the powder material in the reference mortar to the mass of the powder material injected from the spray nozzle in the reference forming step is calculated as the powder spray rate, and the powder material is injected from the spray nozzle in the reference forming step. A spray rate calculating step of calculating a mass ratio of the liquid material in the reference mortar with respect to the mass of the liquid material as a liquid spray rate;
Calculate the estimated value of the mass of the powder material in the spray mortar by multiplying the mass of the powder material sprayed from the spray nozzle when forming the spray mortar by the powder spray rate, To calculate the estimated value of the mass of the liquid material in the spray mortar by multiplying the mass of the liquid material ejected from the spray nozzle when forming the liquid by the liquid spray rate, and the estimated value of the mass of the powder material A method for confirming the construction state of spray mortar, comprising: a liquid powder ratio estimation step of calculating an estimated value of the liquid powder ratio of the spray mortar from the estimated value of the mass of the liquid material.