JP2015168661A - solid cosmetic composition - Google Patents
solid cosmetic composition Download PDFInfo
- Publication number
- JP2015168661A JP2015168661A JP2014046343A JP2014046343A JP2015168661A JP 2015168661 A JP2015168661 A JP 2015168661A JP 2014046343 A JP2014046343 A JP 2014046343A JP 2014046343 A JP2014046343 A JP 2014046343A JP 2015168661 A JP2015168661 A JP 2015168661A
- Authority
- JP
- Japan
- Prior art keywords
- cosmetic composition
- solid cosmetic
- magnesium
- oil
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、固体化粧料組成物に関する。 The present invention relates to a solid cosmetic composition.
近年、分子状水素の健康への効能についての検討が行われつつある。分子状水素を含有する組成物は、酸化還元電位（ＯＲＰ）が還元側にシフトしていて、抗酸化能が付与された機能水（水素水）になるとされている。 In recent years, studies have been conducted on the health effects of molecular hydrogen. In the composition containing molecular hydrogen, the oxidation-reduction potential (ORP) is shifted to the reduction side, and functional water (hydrogen water) to which antioxidant ability is imparted is supposed.
このような機能性を有する水素水を化粧料分野において利用することも試みられている。特許文献１には、水素化マグネシウムと吸湿性成分とを含有する浴用化粧料が記載されている。水素化マグネシウム自体は安定な化合物であるが、水との反応性が高く、水存在下では水素を発生しながら徐々に分解してしまう。このため、アルミパウチ容器等の密閉容器中で保存すると、保管・流通の過程において水素ガスを発生して容器が膨張し、場合によっては破裂等を起こすことがある。 Attempts have also been made to use hydrogen water having such functionality in the cosmetics field. Patent Document 1 describes a bath cosmetic containing magnesium hydride and a hygroscopic component. Magnesium hydride itself is a stable compound, but is highly reactive with water and gradually decomposes in the presence of water while generating hydrogen. For this reason, if it preserve | saves in airtight containers, such as an aluminum pouch container, hydrogen gas will be generated in the process of storage and distribution | swelling, and a container may expand | swell and may cause a burst etc. depending on the case.
従って、水素化マグネシウムを含有する固体化粧料組成物を実用化することが困難になっており、水素化マグネシウムの化粧料分野への使用に関する重要な課題となっている。 Therefore, it is difficult to put a solid cosmetic composition containing magnesium hydride into practical use, which is an important issue regarding the use of magnesium hydride in the cosmetic field.
本発明は、上述した課題を解決することを目的とするものであり、より具体的には、水素化マグネシウムを含有し、かつ、安定性に優れた固体化粧料組成物を得ることを目的とするものである。 An object of the present invention is to solve the above-described problems, and more specifically, to obtain a solid cosmetic composition containing magnesium hydride and having excellent stability. To do.
本発明は、水素化マグネシウム及びマグネシウム塩化合物を含有することを特徴とする固形化粧料組成物である。
上記マグネシウム塩化合物は、塩化マグネシウム、海水乾燥物及び塩水湖乾燥物からなる群から選択される少なくとも１であることが好ましい。
上記固体化粧料組成物は、更に、炭酸水素ナトリウム、炭酸ナトリウム及び固形有機酸からなる群より選択される少なくとも１の成分を含有することが好ましい。
上記固体化粧料組成物は、浴用組成物であることが好ましい。
The present invention is a solid cosmetic composition comprising magnesium hydride and a magnesium salt compound.
The magnesium salt compound is preferably at least one selected from the group consisting of magnesium chloride, seawater dried product and salt lake dried product.
The solid cosmetic composition preferably further contains at least one component selected from the group consisting of sodium hydrogen carbonate, sodium carbonate and a solid organic acid.
The solid cosmetic composition is preferably a bath composition.
本発明によって、安定性において優れた固体化粧料組成物を得ることができる。これによって、保管時に水素ガスの発生を抑制することができ、好適に使用することができる固体化粧料組成物を得ることができる。 According to the present invention, a solid cosmetic composition excellent in stability can be obtained. Thereby, generation | occurrence | production of hydrogen gas can be suppressed at the time of storage, and the solid cosmetic composition which can be used conveniently can be obtained.
本発明の固体化粧料組成物は、水素化マグネシウム及びマグネシウム塩化合物を含有するものである。原因は不明であるが、マグネシウム塩化合物を併用することによって、水素化マグネシウムは安定性が高まり、製造してから実際に使用するまでの期間に、水素を発生しながら分解する反応を抑制することができる。これによって、水素化マグネシウムを含有する化粧料を安定的に保管することができる。 The solid cosmetic composition of the present invention contains magnesium hydride and a magnesium salt compound. The cause is unknown, but the combined use of magnesium salt compounds increases the stability of magnesium hydride and suppresses the decomposition reaction while generating hydrogen during the period from production to actual use. Can do. Thereby, cosmetics containing magnesium hydride can be stably stored.
本発明において使用するマグネシウム塩化合物としては特に限定されず、塩化マグネシウム、臭化マグネシウム、硫酸マグネシウム、水酸化マグネシウム、炭酸マグネシウム等を挙げることができる。また、海水乾燥物、塩水湖乾燥物等のマグネシウム塩化合物を含有する天然のミネラル分を使用することもできる。 The magnesium salt compound used in the present invention is not particularly limited, and examples thereof include magnesium chloride, magnesium bromide, magnesium sulfate, magnesium hydroxide, and magnesium carbonate. Moreover, the natural mineral content containing magnesium salt compounds, such as seawater dried material and salt lake dried material, can also be used.
原因は不明であるが、マグネシウム塩化合物のなかでも、塩化マグネシウムは水素化マグネシウムの安定化効果が特に優れたものである。海水乾燥物、塩水湖乾燥物等の塩化マグネシウムを多く含有する天然ミネラルや塩化マグネシウムを使用した場合には、安定化の効果が特に高いものとなるため、好ましい。 The cause is unknown, but among the magnesium salt compounds, magnesium chloride is particularly excellent in the stabilizing effect of magnesium hydride. The use of natural minerals and magnesium chloride containing a large amount of magnesium chloride such as seawater dried products and salt lake dried products is preferable because the effect of stabilization is particularly high.
海水乾燥物及び塩水湖乾燥物は天然由来であることから、化粧料の分野における使用に際しては、消費者のイメージ、安全性等の観点から特に好ましいものである。海水乾燥物及び塩水湖乾燥物中には、塩化マグネシウム等のマグネシウム塩化合物が多く含まれていることから、これを混合物の状態でそのまま使用しても本発明の効果を得ることができる。 Since seawater dried products and salted lake dried products are naturally derived, they are particularly preferred for use in the field of cosmetics from the viewpoint of consumer image, safety, and the like. Since the seawater dried product and the saltwater lake dried product contain a large amount of magnesium salt compounds such as magnesium chloride, the effects of the present invention can be obtained even if they are used as they are in a mixture state.
上記海水乾燥物は、海水の水分を乾燥させて得られた成分である。必要に応じて成分を調整するために、塩化ナトリウム量を低減させたものを使用してもよい。上記海水乾燥物としては、例えば、ＤＳＡ社が販売しているリヨメール（登録商標）、オーメール等の名称で販売されているものを使用することができる。上記塩水湖乾燥物は、塩水湖の水を乾燥させて得られた成分である。海水乾燥物と同様に、必要に応じて塩化ナトリウム量を低減させたものを使用してもよい。上記塩水湖乾燥物としては、例えば、死海水乾燥物、グレートソルトレイク水乾燥物等を挙げることができる。市販のものとしては、マグネシウムを３〜１５％の割合で含有するネイチャーミネラル（グリーンハート社）等を挙げることができる。 The seawater dried product is a component obtained by drying the water of seawater. You may use what reduced the amount of sodium chloride in order to adjust a component as needed. As the seawater dried product, for example, those sold under the names such as Lyomail (registered trademark) and Omail sold by DSA can be used. The dried salt lake is a component obtained by drying the water of the salt lake. Similarly to the seawater dried product, a product with a reduced amount of sodium chloride may be used as necessary. Examples of the saltwater lake dried product include a dead seawater dried product and a great salt lake water dried product. Examples of commercially available products include Nature Mineral (Green Heart) containing 3 to 15% magnesium.
本発明の固体化粧料組成物は、上記水素化マグネシウムを０．０５〜１０重量％の割合で含有するものであることが好ましい。水素化マグネシウムの配合量を上記範囲内のものとすることで、上述した分子状水素による健康への効能を充分に得ることができる点で好ましい。 The solid cosmetic composition of the present invention preferably contains the magnesium hydride in a proportion of 0.05 to 10% by weight. By making the blending amount of magnesium hydride within the above range, it is preferable in that the health effect by the molecular hydrogen described above can be sufficiently obtained.
更に、上記マグネシウム塩化合物を固形化粧料組成物全量に対して０．９５〜９９．５重量％の割合で含有することが好ましい。上記範囲内のものとすることで、水素化マグネシウムによる健康への効果を充分に得つつ、水素ガスの発生を抑制することができる点で好ましい。上記配合量の上限は、８０重量％であることがより好ましく、５０重量％であることが更に好ましい。上記下限は、０．１重量％であることがより好ましく、１重量％であることが更に好ましい。 Furthermore, it is preferable to contain the said magnesium salt compound in the ratio of 0.95 to 99.5 weight% with respect to the solid cosmetic composition whole quantity. By setting it within the above-mentioned range, it is preferable in that generation of hydrogen gas can be suppressed while sufficiently obtaining health effects from magnesium hydride. The upper limit of the amount is more preferably 80% by weight, still more preferably 50% by weight. The lower limit is more preferably 0.1% by weight, still more preferably 1% by weight.
本発明の固体化粧料組成物は、さらに、炭酸水素ナトリウム、炭酸ナトリウム及び固形有機酸からなる群より選択される少なくとも１の成分を含有するものであることが好ましい。炭酸水素ナトリウム、炭酸ナトリウム及び固形有機酸は、それぞれ浴用組成物において汎用される成分である。 It is preferable that the solid cosmetic composition of the present invention further contains at least one component selected from the group consisting of sodium hydrogen carbonate, sodium carbonate and a solid organic acid. Sodium hydrogen carbonate, sodium carbonate and solid organic acid are components commonly used in bath compositions.
炭酸水素ナトリウム、炭酸ナトリウム及び固形有機酸からなる群より選択される少なくとも１の成分と水素化マグネシウムを併用して使用した場合には特に気体発生による問題が顕著なものとなりやすい。このため、上述したマグネシウム塩化合物と併用することによって、気体の発生を抑制することが望まれる。 When at least one component selected from the group consisting of sodium hydrogen carbonate, sodium carbonate and solid organic acid is used in combination with magnesium hydride, problems due to gas generation tend to be particularly noticeable. For this reason, it is desired to suppress generation of gas by using in combination with the magnesium salt compound described above.
上記炭酸水素ナトリウム及び／又は炭酸ナトリウムを含有する場合、固体化粧料組成物全量に対してこれらの合計量で２０重量％以下の割合で含有することが好ましい。２０重量％を超えて配合した場合は、安定性が低下するおそれがあるため、本発明の目的を達成することができない場合がある。 When it contains the said sodium hydrogencarbonate and / or sodium carbonate, it is preferable to contain in the ratio of 20 weight% or less by these total amounts with respect to the solid cosmetic composition whole quantity. When the blending amount exceeds 20% by weight, the object of the present invention may not be achieved because the stability may be lowered.
上記固体有機酸としては特に限定されず、クエン酸、フマル酸、酒石酸、リンゴ酸、サリチル酸、アスコルビン酸等を挙げることができる。上記固体有機酸は、固体化粧料組成物中に５０重量％以下の割合で含まれることが好ましい。 It does not specifically limit as said solid organic acid, Citric acid, fumaric acid, tartaric acid, malic acid, salicylic acid, ascorbic acid etc. can be mentioned. The solid organic acid is preferably contained in the solid cosmetic composition in a proportion of 50% by weight or less.
本発明の固体化粧料組成物は、粉体、顆粒、タブレット等の任意の形状のものであることが好ましい。また、使用直前に水と混合して、発生した水素による効能を得るために使用するものであることが好ましい。 The solid cosmetic composition of the present invention is preferably in an arbitrary shape such as powder, granule, tablet and the like. Moreover, it is preferable to use in order to obtain the effect by the generated hydrogen by mixing with water immediately before use.
本発明の固体化粧料組成物は、洗浄剤、水と混合して使用する皮膚化粧料、浴用組成物等を挙げることができるが、特に浴用組成物において好適に使用することができる。 Examples of the solid cosmetic composition of the present invention can include a detergent, a skin cosmetic used by mixing with water, a bath composition, and the like. Particularly, the solid cosmetic composition can be suitably used in a bath composition.
本発明の固体化粧料組成物は、発明の効果を損なわない範囲で、上述した以外の成分を配合するものであってもよい。配合してもよい成分としては特に限定されず、オリーブ油、大豆油、アーモンド油、ひまし油、やし油、パーム油、タートル油、米ヌカ油、ホホバ油、ミンク油、卵黄油、スクワラン、アボガド油、ラノリン、流動パラフィン、白色ワセリン、ＤＨＡ、ＥＰＡ等の油脂類、カルボキシメチルセルロースナトリウム、メチルセルロース、カゼイン、ぺクチン、デンプン、アルギン酸ナトリウム、ポリビニルアルコール、ポリビニルピロリドン、ローカストビーンガム、カラギナン、寒天、カルボキシビニルポリマーおよびグルコマンナン等の粘結剤類；グリセリン、プロピレングリコール、ソルビトール、ポリエチレングリコール、１，３−ブチレングリコール、ビタミンＣ及びその誘導体、加水分解シルク、コラーゲン、コンドロイチン及びその蛋白複合体、グリチルリチンおよびその誘導体等の多価アルコール類、保湿剤類；ラベンダー油、ジャスミン油、ローズ油、レモン油、オレンジ油、ハッカ油、タイム油、ショウブ油、ウイキョウ油、スギ油、ヒバ油、ヒノキ油、バラ油、ユーカリ油、カンファー、ペパーミント油、スペアミント油、ゲラニオール、ミカン油、ラズベリー油、トウヒ、シトロネロール等の天然及び合成香料等の香料類；殺菌剤、界面活性剤、ビタミン類、アミノ酸および医薬品、医薬部外品、並びに化粧品用タール系色素等を適宜含むことができる。また、血行促進剤、発汗促進剤を併用するものであってもよい。 The solid cosmetic composition of the present invention may be blended with components other than those described above as long as the effects of the invention are not impaired. The ingredients that may be blended are not particularly limited, but olive oil, soybean oil, almond oil, castor oil, palm oil, palm oil, turtle oil, rice bran oil, jojoba oil, mink oil, egg yolk oil, squalane, avocado oil , Lanolin, liquid paraffin, white petrolatum, oils such as DHA, EPA, sodium carboxymethylcellulose, methylcellulose, casein, pectin, starch, sodium alginate, polyvinyl alcohol, polyvinylpyrrolidone, locust bean gum, carrageenan, agar, carboxyvinyl polymer And binders such as glucomannan; glycerin, propylene glycol, sorbitol, polyethylene glycol, 1,3-butylene glycol, vitamin C and its derivatives, hydrolyzed silk, collagen, chondroitin and Protein complexes, polyhydric alcohols such as glycyrrhizin and its derivatives, humectants; lavender oil, jasmine oil, rose oil, lemon oil, orange oil, peppermint oil, thyme oil, ginger oil, fennel oil, cedar oil, Perfumes such as natural and synthetic fragrances such as Hiba oil, cypress oil, rose oil, eucalyptus oil, camphor, peppermint oil, spearmint oil, geraniol, mandarin oil, raspberry oil, spruce, citronellol; fungicides, surfactants, vitamins , Amino acids and pharmaceuticals, quasi-drugs, and tar-type pigments for cosmetics. In addition, a combination of a blood circulation promoter and a sweat promoter may be used.
また、マグネシウム塩化合物、水素化マグネシウム以外の無機化合物を含有するものであってもよい。このような無機化合物としては、例えば、塩化ナトリウム、ホウ酸、ほう砂、硫酸ナトリウム、硫化ナトリウム、硫化カリウム、硝酸ナトリウム、硝酸カルシウム、硫酸アンモニウム、チオ硫酸ナトリウム、リン酸水素カルシウム、塩化カリウム、塩化アンモニウム、リン酸ナトリウム、次亜硫酸ナトリウム、チオ硫酸カルシウム、硫黄、無水ケイ酸、メタケイ酸、ケイ酸アルミニウム、ベントナイト、アルミナ、ゼオライト等が挙げられる。 Moreover, you may contain inorganic compounds other than a magnesium salt compound and magnesium hydride. Examples of such inorganic compounds include sodium chloride, boric acid, borax, sodium sulfate, sodium sulfide, potassium sulfide, sodium nitrate, calcium nitrate, ammonium sulfate, sodium thiosulfate, calcium hydrogen phosphate, potassium chloride, and ammonium chloride. Sodium phosphate, sodium hyposulfite, calcium thiosulfate, sulfur, anhydrous silicic acid, metasilicic acid, aluminum silicate, bentonite, alumina, zeolite and the like.
更に、生薬を配合するものであってもよい。生薬としては、各種植物の粉砕物及びその乾燥物、又は、抽出物である。一般に薬用として知られる各種植物を使用することができる。具体的には例えば、チンピ、レモンの皮、海藻、ヒノキ、ヒバ、フッカス、米ヌカ、ハトムギ、ショウブ、ショウキョウ、ウイキョウ、カンゾウ、ユズ、トウキ、ニンジン、ハッカ、ケイヒ、ウバイ、ヨモギ、ドクダミ、モモノハ、カミツレ、アロエ、ジャスミン、ローズヒップ、ラベンダー、グァバ、オウゴン、クコ、レイシ、ニワトコ、アシタバ、ウコギ、ゴボウ、黒ゴマ、黒米、藤三七人参、高麗人参、田七人参、セッコツ草、センキュウ等の粉砕物及びその乾燥物が挙げられる。 Furthermore, you may mix | blend a crude drug. Herbal medicines are pulverized products of various plants and dried products or extracts thereof. Various plants generally known as medicinal can be used. Specifically, for example, chimney, lemon peel, seaweed, cypress, hiba, fukkas, rice bran, pearl barley, shobu, ginger, fennel, licorice, yuzu, touki, carrots, mint, keihi, Japanese mugwort, mugwort, dokudami, Momonoha, Chamomile, Aloe, Jasmine, Rosehip, Lavender, Guava, Ougon, Cuco, Ganoderma, Elderberry, Ashitaba, Uguigi, Burdock, Black Sesame, Black Rice, Fujisan Ginseng, Ginseng, Taba Ginseng, Ginseng Grass, Gypsophila Etc. and dried products thereof.
上記生薬は、固体化粧料組成物全量に対して０．０１〜５質量％の割合で含まれることが好ましい。上記下限は、０．１質量％であることがより好ましい。 The herbal medicine is preferably contained in a proportion of 0.01 to 5% by mass with respect to the total amount of the solid cosmetic composition. The lower limit is more preferably 0.1% by mass.
本発明の固体化粧料組成物は、固体状のものであるが、粉末、顆粒、錠剤等の公知の任意の剤形とすることができる。また、本発明の固体化粧料組成物は、アルミパウチ容器等、高いガスバリア性を有する容器中に包装されたものであることが好ましい。これによって、空気中の水分と反応することによって長期保存後の性能が低下するという問題を生じにくくなる点で好ましい。 The solid cosmetic composition of the present invention is in a solid state, but may be any known dosage form such as powder, granule, tablet and the like. The solid cosmetic composition of the present invention is preferably packaged in a container having high gas barrier properties such as an aluminum pouch container. This is preferable in that it hardly causes a problem that the performance after long-term storage is deteriorated by reacting with moisture in the air.
更に安定性を高めるためには、固体化粧料組成物は、製品の乾燥減量（１０５℃、３時間加熱後の重量の減少割合を乾燥前の組成物の質量に対して％で示した値）が、８％以下であることが好ましく、４％以下であることが更に好ましい。これによって、浴用組成物の水素発生による原料が抑制される。乾燥減量を上記範囲のものとするには、各原料について、１０５℃で３時間加熱後の乾燥減量が４％以下であるような原料を使用して製造を行うことが好ましい。また、混合・充填の工程においても、各成分が吸湿しない条件下で行うことが好ましい。 In order to further improve the stability, the solid cosmetic composition has a loss on drying of the product (value expressed as a percentage of the weight reduction after heating at 105 ° C. for 3 hours in%). However, it is preferably 8% or less, and more preferably 4% or less. Thereby, the raw material by hydrogen generation of the bath composition is suppressed. In order to make the loss on drying within the above range, it is preferable that each raw material is manufactured using a raw material whose loss on drying after heating at 105 ° C. for 3 hours is 4% or less. Also, the mixing / filling step is preferably performed under conditions where each component does not absorb moisture.
以下に、実施例を示して本発明を更に説明するが、本発明はこれらに限定されるものではない。なお、配合量はすべて質量％を表す。
（実施例１〜６、比較例１、２）
以下の表１に示す処方の粉末の浴用組成物を調製した。なお、以下、各実施例及び比較例においては、特に断りがない限り、各原料としては乾燥させて水分量が４％以下であるものを混合して製造した。
EXAMPLES The present invention will be further described below with reference to examples, but the present invention is not limited to these examples. In addition, all compounding quantities represent the mass%.
(Examples 1-6, Comparative Examples 1 and 2)
A powder bath composition having the formulation shown in Table 1 below was prepared. In the following examples and comparative examples, unless otherwise specified, each raw material was dried and mixed to have a water content of 4% or less.
表１中の各成分は具体的には以下のものである。
オーメール：ＤＳＡ社が販売：Ｍｇ ５．５〜１４．０％含有のＭｇ塩
リヨメール：ＤＳＡ社が販売：Ｍｇ ５．０〜１５．０％含有のＭｇ塩
サイロピュア２５：微粉末シリカ（富士シリシア化学社製）
クエン酸：クエン酸顆粒 ＴＢＡ−８０（九重化成社製）
Specifically, each component in Table 1 is as follows.
Omer: Sold by DSA: Mg salt containing 2.5 to 14.0% Mg Lyomer: Sold by DSA: Mg salt containing 5.0 to 15.0% Mg Silopure 25: Fine powder silica (Fuji (Made by Silysia Chemical)
Citric acid: Citric acid granule TBA-80 (manufactured by Kuju Kasei Co., Ltd.)
また、ｐＨは、水に対して１％となる重量の組成物を４０℃に加熱した水道水に溶解して測定した。 The pH was measured by dissolving a composition having a weight of 1% with respect to water in tap water heated to 40 ° C.
得られた組成物について、アルミパウチ中に密封し、室温、４０℃、６０℃の各条件で保管し、１週間経過後及び１カ月経過後にアルミパウチ容器の膨張状態を確認した。
その結果を表２に示す。
The obtained composition was sealed in an aluminum pouch and stored under conditions of room temperature, 40 ° C. and 60 ° C., and the expanded state of the aluminum pouch container was confirmed after one week and one month.
The results are shown in Table 2.
なお、評価基準は以下である。
◎：変化なし
○：軽微な膨らみが発生
△：中程度の膨張がみられるが、使用可能
×：容器全体に及ぶ膨張がみられ使用不可
The evaluation criteria are as follows.
◎: No change ○: Slight bulge occurs △: Moderate expansion is observed, but can be used ×: Cannot be used due to expansion over the entire container
表２の結果から、本発明の固体化粧料組成物は、長期保存性に優れていることが明らかである。 From the results of Table 2, it is clear that the solid cosmetic composition of the present invention is excellent in long-term storage stability.
（実施例７，８及び比較例３，４）
下記に示す表３に示す処方の粉末の浴用組成物を調製した。なお、実施例においては、各原料としては乾燥させて水分量が４％以下であるものを混合して製造した。比較例３，４においてはこのような乾燥を行っていない原料を用いて浴用組成物を調整した。
(Examples 7 and 8 and Comparative Examples 3 and 4)
A powder bath composition having the formulation shown in Table 3 shown below was prepared. In Examples, each raw material was dried and mixed with a water content of 4% or less. In Comparative Examples 3 and 4, bath compositions were prepared using raw materials that were not dried.
表３の各実施例、比較例についても実施例１〜６、比較例１、２の基準で評価を行った。更に、乾燥減量についても測定を行った。なお、乾燥減量の測定は、１０５℃、３時間加熱後の重量の減少割合を乾燥前の組成物の質量に対して％で示した値である。結果を表４に示す。表４の結果からも、本発明の固体化粧料組成物が長期保存性に優れていることが明らかである。 Each Example and Comparative Example in Table 3 were also evaluated on the basis of Examples 1 to 6 and Comparative Examples 1 and 2. Furthermore, the loss on drying was also measured. In addition, the measurement of loss on drying is the value which showed the decreasing rate of the weight after heating at 105 degreeC for 3 hours in% with respect to the mass of the composition before drying. The results are shown in Table 4. From the results shown in Table 4, it is clear that the solid cosmetic composition of the present invention is excellent in long-term storage.
（実施例９〜１１）
以下の表５に示す処方の粉末の浴用組成物を調製した。
(Examples 9 to 11)
A powder bath composition having the formulation shown in Table 5 below was prepared.
得られた組成物について、アルミパウチ中に密封し、室温、４０℃、６０℃の各条件で保管し、１週間経過後及び１カ月経過後にアルミパウチ容器の膨張状態を確認した。
その結果を表５に示す。
The obtained composition was sealed in an aluminum pouch and stored under conditions of room temperature, 40 ° C. and 60 ° C., and the expanded state of the aluminum pouch container was confirmed after one week and one month.
The results are shown in Table 5.
表５の結果から、マグネシウム塩化合物を水素化マグネシウムと併用した場合に優れた効果を有し、特に塩化マグネシウムを使用した場合に好適な効果が得られることが明らかとなった。 From the results shown in Table 5, it was revealed that when a magnesium salt compound was used in combination with magnesium hydride, an excellent effect was obtained, and particularly when magnesium chloride was used, a suitable effect was obtained.
（実施例１２〜１６）
以下の表６に示す処方の粉末の浴用組成物を調製した。
得られた組成物について、アルミパウチ中に密封し、室温、４０℃、６０℃の各条件で保管し、１週間経過後及び１カ月経過後にアルミパウチ容器の膨張状態を確認した。
その結果を表６に示す。
(Examples 12 to 16)
A powder bath composition having the formulation shown in Table 6 below was prepared.
The obtained composition was sealed in an aluminum pouch and stored under conditions of room temperature, 40 ° C. and 60 ° C., and the expanded state of the aluminum pouch container was confirmed after one week and one month.
The results are shown in Table 6.
表６の結果から、マグネシウム塩化合物を水素化マグネシウムと併用した場合、幅広い配合割合の範囲で優れた効果が得られることが明らかとなった。 From the results shown in Table 6, it was revealed that when a magnesium salt compound was used in combination with magnesium hydride, excellent effects were obtained within a wide range of blending ratios.
本発明の固体化粧料組成物は、洗浄剤、水と混合して使用する皮膚化粧料、浴用組成物等として利用することができる。 The solid cosmetic composition of the present invention can be used as a detergent, a skin cosmetic used by mixing with water, a bath composition or the like.
Claims (4)