JP2015152792A - Powder seal member - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide, at low cost, a powder seal member excellent in flexibility, and capable of suppressing leakage of powder to the outside.SOLUTION: A powder seal member includes: a support layer which has an adhesive layer formed on one side, and is made of a foam elastic material; and a fiber layer adhered and laminated to the other side of the support layer by frame laminating work. The fiber layer is one selected from: a fiber layer made of a raised fabric prepared by nap-raising, by card clothing, a knitted fabric whose ground yarn is warp knitted, or made of an unwoven fabric; a fiber layer having a cut-pile figure, which is formed by weaving two fabrics provided opposite to each other, weaving a pile yarn in the base fabrics to crosslink the two fabrics, and then cutting the intermediate part of the pile yarn between both the base fabrics to separate the two base fabrics from each other; a fiber layer made of a base fabric having thereon a pile yarn prepared by raising an ultra fine fiber which is formed by dividing a split fiber into a plurality of fibers; and a fiber layer made of a raised fabric prepared by nap-raising a textile by card clothing.

Description

  The present invention relates to a powder seal member.

  An intermediate layer is interposed between the upper layer made of the fiber material and the lower layer made of the elastic body in order to prevent wrinkles from being generated on the surface of the upper layer when the surface of the upper layer is curved in a concave shape. A laminated structure is known (Patent Document 1).

  In a laminate comprising a breathable skin material and a polyurethane foam obtained by foaming a raw material containing polyols, polyisocyanates, foaming agent, catalyst and deodorant, the deodorant carries a metal compound. Made of an inorganic porous material, the metal compound oxidizes and decomposes the volatile organic compound and also oxidizes itself, and after oxidation and decomposition, the metal compound returns to the original metal compound after being oxidized and decomposed. A laminate in which a polyurethane foam is bonded by frame lamination is also known (Patent Document 2).

JP 2009-15226 A JP 2009-286026 A

  An object of the present invention is to provide a low-cost powder seal member that is excellent in flexibility and can suppress leakage of powder to the outside.

In order to solve the above problem, the powder seal member according to claim 1 is:
A support layer made of a foamed elastic material having an adhesive layer formed on one surface side;
A fiber layer bonded and laminated to the other side of the support layer by frame lamination,
It is characterized by that.

The invention according to claim 2 is the powder seal member according to claim 1,
The fiber layer is made of a raised fabric or a nonwoven fabric in which a knitted fabric warped with a ground yarn is subjected to a needle raising process,
It is characterized by that.

The invention according to claim 3 is the powder seal member according to claim 1,
The fiber layer is knitted in a state where the two layers are arranged opposite to each other, and after pile yarn is knitted into each of the base fabrics so as to bridge between the two base fabrics, Having a cut pile form formed by cutting an intermediate portion of the pile yarn and cutting off the two base fabrics,
It is characterized by that.

The invention according to claim 4 is the powder seal member according to claim 1,
The fiber layer comprises a pile yarn in which ultrafine fibers formed by dividing a divided fiber into a plurality of pieces on a base fabric are raised,
It is characterized by that.

The invention according to claim 5 is the powder seal member according to claim 1,
The fiber layer is formed by performing a backing treatment on the surface of the raised fabric obtained by subjecting a woven fabric to a raised fabric.
It is characterized by that.

The invention according to claim 6 is the powder seal member according to any one of claims 1 to 5,
The adhesive layer is a double-sided adhesive tape or a coated acrylic adhesive that does not use a substrate,
It is characterized by that.

The invention according to claim 7 is the powder seal member according to any one of claims 1 to 6,
The fiber layer is disposed in contact with both side edges of the cleaning member for cleaning the surface of the image carrier and the surface of the image carrier, and leakage of the toner scraped off by the cleaning member to the outside is caused by the fiber layer. Used in suppressing image forming apparatus,
It is characterized by that.

The invention according to claim 8 is the powder seal member according to any one of claims 1 to 6,
The fiber layer is disposed in contact with the surface of the developing roller between a developing roller that conveys the toner to the image carrier and a support member that supports the developing roller, and leakage of the toner to the outside is arranged in the fiber layer. Used in image forming apparatus suppressed by
It is characterized by that.

According to the first aspect of the present invention, it is possible to provide a low-cost powder seal member that is excellent in flexibility and capable of suppressing leakage of the powder to the outside as compared with the case where the present configuration is not provided. .
According to the second to fifth aspects of the present invention, it is possible to suppress the leakage of the powder to the outside by forming a space between the fibers of the fiber layer as compared with the case where the present configuration is not provided.
According to invention of Claim 6, compared with the case where it does not have this structure, the softness | flexibility of a powder seal member can be improved and the leakage to the exterior of a powder can be suppressed.
According to the seventh and eighth aspects of the present invention, the powder seal member can be improved in flexibility and the leakage of the toner to the outside of the image forming apparatus can be suppressed as compared with the case where the present configuration is not provided.

(A) is a schematic cross-sectional view showing the configuration of the powder seal member 1, and (b) is an enlarged partial cross-sectional schematic diagram showing the configuration of the fiber layer 20. 3 is a schematic diagram showing a structure of a knitted fabric constituting the base fabric portion 21. FIG. It is a schematic diagram which shows the state which performs a knitted fabric raising process. It is a schematic diagram which shows the state which forms the fiber layer 20A which concerns on the modification 1 which has a cut pile form with the double Russell knitting machine. (A) is a schematic diagram which shows the structure of the fiber layer 20B which concerns on the modification 2, (b) is an expanded sectional schematic diagram which shows an example of the cross-sectional shape of a division | segmentation fiber, (c) is the fiber layer 20C which concerns on the modification 3. It is a schematic diagram which shows a structure. It is a schematic diagram for demonstrating the process process which adhere | attaches and laminate | stacks the support layer 10 and the fiber layer 20 by frame lamination process. (A) is a schematic cross-sectional view for explaining attachment of the toner seal SA arranged in contact with both side ends of the cleaning blade 126 and the surface of the photosensitive drum 121, and (b) is a toner seal function of the toner seal SA. It is a schematic diagram to explain. (A) is a schematic cross-sectional view for explaining the attachment of the toner seal SB disposed in contact with both ends of the layer regulating blade 136 and the surface of the developing roller 132, and (b) shows the toner seal function of the toner seal SB. It is a schematic diagram to explain. 1 is a schematic cross-sectional view showing an image forming unit of an image forming apparatus 100 as an example in which a powder seal member 1 is used. (A) is an expanded sectional schematic diagram which shows the structure of the powder seal member 200 of a comparative example, (b) is an enlarged schematic diagram for demonstrating the surface state of the powder seal member 200 of the comparative example bent and affixed. is there.

Next, the present invention will be described in more detail with reference to the drawings with reference to embodiments and specific examples. However, the present invention is not limited to these embodiments and specific examples.
Also, in the description using the following drawings, it should be noted that the drawings are schematic and the ratio of each dimension and the like are different from the actual ones, and are necessary for the description for easy understanding. Illustrations other than the members are omitted as appropriate.

(1) Configuration of Powder Seal Member FIG. 1A is a schematic cross-sectional view showing the configuration of the powder seal member 1 according to this embodiment, and FIG. 1B is an enlarged partial cross-sectional schematic diagram showing the configuration of the fiber layer 20. Is a schematic view showing the structure of the knitted fabric constituting the base fabric portion 21, FIG. 3 is a schematic view showing a state in which the knitted fabric is subjected to a needle cloth raising process, and FIG. 4 is a deformation having a cut pile form by the double raschel knitting machine 40 FIG. 5A is a schematic diagram illustrating a state of forming the fiber layer 20A according to Example 1, FIG. 5A is a schematic diagram illustrating the configuration of the fiber layer 20B according to Modification 2, and FIG. 5B illustrates an example of the cross-sectional shape of the split fiber. FIG. 6C is a schematic enlarged view, FIG. 6C is a schematic diagram showing a configuration of the fiber layer 20C according to the modification 3, and FIG. 6 illustrates a processing step in which the support layer 10 and the fiber layer 20 are bonded and laminated by frame lamination. FIG. 10 (a) is a powder seal member 200 of a comparative example. FIG. 4B is an enlarged schematic diagram for explaining the surface state of a powder seal member 200 of a comparative example that is bent and pasted.
Hereinafter, the configuration of the powder seal member 1 according to the present embodiment will be described with reference to the drawings.

(1.1) Overall Configuration of Powder Seal Member The powder seal member 1 includes a support layer 10 made of a foamed elastic material having an adhesive layer formed on one surface side,
The fiber layer 20 is configured to be laminated on the other surface side of the support layer 10 by a frame laminating process.

(1.2) Support layer The support layer 10 includes a polyurethane foam material 11 as an example of a foamed elastic material and a double-sided adhesive tape 12 as an example of an adhesive layer.
The polyurethane foam material 11 is preferably mainly a flexible polyurethane foam having elasticity and heat resistance, high durability against deformation (sagging), and suitable for frame laminating.
As will be described later, the frame laminating process utilizes the property that the polyurethane foam melts with a flame, and the surface of the urethane foam is melted by bringing the flame of the gas burner into contact with the surface of the long urethane foam. The fiber layer 20 is bonded together, and is pressure-cooled to bond and laminate.

The flexible polyurethane foam as the material of the polyurethane foam material 11 is preferably one having a 25% compressive load value of 0.3 to 3 MPa in accordance with the hardness test A method of JIS K6400.
When the compression load value of the polyurethane foam material 11 is lower than 0.3 MPa, the contact force of the fiber layer 20 to the photosensitive drum or the developing roller as an example of the contacted member becomes low, and the toner leaks as an example of the powder. May not be able to be suppressed.
Further, when the compression load value of the polyurethane foam material 11 is higher than 3 MPa, the contact force to the photosensitive drum or the developing roller becomes high, and the rotational torque due to the frictional force between the photosensitive drum or the developing roller and the fiber layer 20. Or the surface of the photosensitive drum or the surface of the developing roller may be easily worn.

  The double-sided adhesive tape 12 forming the adhesive layer is preferably a double-sided tape coated with an adhesive made of an acrylic resin having no base material such as a nonwoven fabric. When the double-sided adhesive tape 12 having no base material is used as the adhesive layer, the followability when the powder seal member 1 is attached to the curved surface portion of the adherend member is improved, and the adherend member of the powder seal member 1 is improved. Peeling from can be suppressed.

(1.3) Fiber Layer The fiber layer 20 includes a base fabric portion 21 and raised yarns 22.
As shown in FIG. 2, the base fabric portion 21 is knitted by warp knitting (indicated by halftone dots in FIG. 2) that continuously connects the loops in the warp direction while forming a continuous loop with the ground yarn 21a. It is formed from the resulting knitted fabric.
In the case of forming a knitted fabric, there is a method of knitting the ground yarn 21a with a weft knitting, but the knitted fabric knitted with the weft knitting easily loosens the ground yarn 21a at the cut end when cut, It has the property of easily extending in the direction.
Accordingly, when a knitted fabric knitted by weft knitting is used as the fiber layer 20 of the powder seal member 1, fraying and elongation occur when cutting by a die cutting method or the like, and the powder seal member 1 is cut into an accurate shape. Therefore, a knitted fabric knitted by warp knitting is used for the base fabric portion 21.

A highly durable and flexible yarn is used for the ground yarn 21a. Examples of such a yarn include a filament yarn and a spun yarn. As the fiber forming the ground yarn 21a, a fiber having a low dynamic friction coefficient, wear resistance and appropriate heat resistance, which can be bonded by frame laminating described later is used.
Such fibers include ultra-high molecular polyethylene, polypropylene, polyamide, aramid resin, polyester, nylon, acrylic resin, synthetic fiber made of polyethylene terephthalate (PET), semi-synthetic fiber made of rayon, etc., natural made of cotton, etc. Examples thereof include fibers. In the present embodiment, filament yarn made of ultrahigh molecular weight polyethylene fiber is used for the ground yarn 21a.

The base fabric portion 21 made of a knitted fabric knitted by weft knitting is subjected to a fiber opening process by using a fiber opening device 30 as shown in FIG. 3, and each loop of the ground yarn 21a is cut and raised. Is done.
Specifically, the opening device 30 includes a cloth roller 32 as a needle-like body formed from a support body 31 having a substantially columnar shape and a plurality of needles 32 a protruding from the peripheral surface of the support body 31. have.
The needle cloth roller 32 is disposed so as to be able to rotate while the tip of the needle 32a is in sliding contact with each loop of the ground yarn 21a (see arrow R1 in FIG. 3).
The needle cloth roller 32 rotates and scratches each loop of the ground yarn 21a with the needle 32a, whereby the base fabric portion 21 is cut and raised by each loop of the ground yarn 21a.

The ground yarn 21a, which is scratched by the needle 32a and whose loops are cut, is opened by raising the interval between the fibers at the cut upper end portion, and the raised yarn 22 raised on the base fabric portion 21 and Become.
The raised yarns 22 raised on the base fabric portion 21 do not stand upright from the surface of the base fabric portion 21 and are intertwined in a complicated manner. For this reason, the fiber layer 20 composed of the base fabric portion 21 and the raised yarn 22 can easily hold the toner as a powder between the raised yarns 22 and can suppress the leakage of the toner.

In addition, the fiber layer 20 having the raised yarns 22 that have been opened and raised has increased surface volume and excellent cushioning properties in the thickness direction, and is softly in contact with the photosensitive drum and the developing roller. Further, it is possible to suppress streak scratches that are likely to occur on the surface of the photosensitive drum or the developing roller.
Furthermore, since the opened and raised raised yarns 22 are intertwined in a complicated manner, the direction of the slanted hair of the fiber layer 20 relative to the rotation direction of the photosensitive drum or developing roller, which is the contacted member of the powder seal member 1, is determined. There is no need to consider, and it becomes possible to omit the oblique hair processing.

  The fiber layer 20 is not limited to a raised fabric in which the base fabric portion 21 knitted in the weft knitting is subjected to the opening process using the opening device 30, and the nonwoven fabric is raised using the opening device 30. You may process and use.

"Modification 1"
As a first modification, the fiber layer 20A is knitted in a state where the two fiber layers are arranged opposite to each other, and pile yarns 22 are applied to the respective base fabric portions 21, 21 so as to bridge between the two base fabric portions 21. After the knitting, the intermediate portion of the pile yarn 22 may be cut between the base fabric portions 21, 21 and the two base fabric portions 21, 21 may be cut to form a cut pile.
Specifically, as shown in FIG. 4, it is formed using a double Russell knitting machine 40. The double raschel knitting machine 40 is provided with a pair of opposing knitting portions 41 for knitting the base fabric portion 21 on both sides thereof, and the base yarn 21a is fed to the both knitting portions 41 from above. The base fabric portion 21 is knitted by the both knitted portions 41 so as to face each other.

As shown by a solid line and a two-dot chain line in FIG. 4, the pile yarn 22 is fed while reciprocating between the two knitted portions 41 so as to bridge between the base fabrics knitted by the both knitted portions 41. Are knitted into the base fabric portions 21, 21. When the two base fabric portions 21 and 21 cross-linked by the pile yarn 22 are discharged downward from the both knitting portions 41, the intermediate portion of the pile yarn 22 is cut by the cutter 42, and the two pieces The base fabric parts 21 and 21 are cut off.
As a result, two fiber layers 20A in the form of a cut pile composed of the base fabric portion 21 and pile yarns 22 cut and arranged to a predetermined length are formed simultaneously, and the fiber layer 20A thus obtained has The powder seal member 1A (not shown) may be configured by bonding the support layer 10 by a frame laminating process described later.

"Modification 2"
FIG. 5A is a schematic diagram illustrating a configuration of a powder seal member 1B including a fiber layer 20B according to the second modification. The fiber layer 20B is formed by weaving a plurality of pile yarns 22B with a pile weave on a base fabric 21B.
As an example, the pile yarn 22B is made of a yarn made of split fibers 23 having a fineness of 340 dtex / 100 filaments. As shown as an example in FIG. 5B, the split fiber 23 was obtained by a composite spinning method in which a plurality of nozzles were used, and materials were discharged from these nozzles in a molten state and combined while spinning. Fiber.

The split fibers 23 are divided into a plurality of fine fibers 23a by separating different materials used for the split fibers 23, and the pile yarn 22B is made thin and dense by the opened fine fibers 23a. Therefore, the gap between the pile yarns 22B is closed, and leakage of toner to the outside is suppressed.
Further, the pile yarn 22B is formed by the split fibers 23 being opened to become fine fibers 23a, so that the pile yarns 22B support each other and suppress the settling of the pile yarn 22B even when used for a long time. However, the slidability with respect to the sliding contact member can be improved.

“Modification 3”
FIG. 5C is a schematic cross-sectional view showing a configuration of a powder seal member 1C provided with a fiber layer 20C according to Modification 3. The fiber layer 20 </ b> C is subjected to a backing process on the back side of a raised cloth obtained by weaving warp and weft yarns, and a coated layer 21 </ b> Ca is formed.
As the backing treatment, a coating agent made of an acrylic synthetic resin emulsion or a vinyl acetate synthetic resin emulsion is preferably used from the viewpoint of adhesiveness to a material, versatility, etc., and between the ground yarns forming the woven fabric 21C. So as to prevent fraying at the cut end when the powder seal member is cut into a desired shape and used.
According to the fiber layer 20 </ b> C made of the woven fabric 21 </ b> C subjected to the needle cloth raising process, a low-cost powder seal member can be provided.

(1.4) Adhesion of Support Layer 10 and Fiber Layer 20 The powder seal member 1 is configured as a laminate in which the support layer 10 and the fiber layer 20 are bonded and laminated by frame lamination.
The frame laminating process is also referred to as flame treatment. As shown in FIG. 6, the surface (surface to be a laminated surface) 11a of the polyurethane foam material 11 is blown with a flame F of a gas burner using city gas, propane gas or the like. This is a processing method in which the fiber layer 20 is stacked on the surface of the molten polyurethane foam material 11 by heat melting, and is fused and laminated.

  The flame of the gas burner is preferably 600 to 1000 ° C. Further, the adhesive strength of the fiber layer 20 to the polyurethane foam material 11 is adjusted by appropriately selecting the distance between the gas burner and the surface of the polyurethane foam material 11, the gas burner arrangement angle, the conveyance speed of the polyurethane foam material 11, and the like. Can do.

  The thickness of the polyurethane foam material 11 whose surface is thermally melted by the flame F of the gas burner is reduced by about 0.3 mm to 0.5 mm. Therefore, the polyurethane foam material 11 to be subjected to the frame laminating process is set in anticipation of a decrease in thickness according to the thickness required as the powder seal member 1.

An adhesive layer is not formed between the support layer 10 and the fiber layer 20 laminated by the frame laminating process. Therefore, the powder seal member 1 is formed on a powder seal 200 (see FIG. 10) of a comparative example in which a support layer 101 and a fiber layer 201 having a coating layer 202 are laminated through a double-sided adhesive tape 102. Compared to a curved surface having a small bending resistance and a large curvature, the ability to follow a curved surface is high, and the generation of wrinkles on the surface of the curvature center can be suppressed.
Moreover, since the back surface of the fiber layer 20 is fused and laminated with the support layer 10 in which the surface is thermally melted by the flame F of the gas burner, it is not necessary to provide a coating layer by a backing process on the back surface. . Therefore, the fiber layer 20 can improve the followability to a curved surface more, when it is affixed on the sticking surface with small bending resistance and a large curvature.

(2) Action / Effect of Powder Seal Member FIG. 7A is a schematic cross-sectional view for explaining attachment of the toner seal SA arranged in contact with both side ends of the cleaning blade 126 and the surface of the photosensitive drum 121. FIG. 8B is a schematic diagram illustrating the toner seal function of the toner seal SA, and FIG. 8A illustrates the attachment of the toner seal SB disposed in contact with both ends of the layer regulating blade 136 and the surface of the developing roller 132. FIG. 9B is a schematic diagram illustrating the toner seal function of the toner seal SB, and FIG. 9 is a schematic cross-sectional view illustrating an image forming unit of the image forming apparatus 100 as an example in which the powder seal member 1 is used. It is.
Hereinafter, the operation of the powder seal member 1 according to the present embodiment will be described using the image forming apparatus 100 as an application example.

(2.1) Schematic Configuration and Operation of Image Forming Apparatus The image forming unit of the image forming apparatus 100 includes an exposure device 110, a photosensitive unit 120, a developing device 130, a transfer device 140, a paper transport device 150, and a fixing device 160. The image information received from the image processing unit (not shown) is formed as a toner image on the paper P sent from the paper feeding device (not shown).

  The photosensitive unit 120 includes a photosensitive drum 121 that is provided below the exposure apparatus 110 in parallel and is driven to rotate. A charging roller 122, an exposure device 110, a developing device 130, a primary transfer roller 142, and a cleaning device 124 are arranged along the rotation direction of the photosensitive drum 121.

In the developing device 130, a developing roller 132 disposed to face the photosensitive drum 121 and a supply roller 133 that supplies toner in the developing housing 131 to the developing roller 132 side are disposed in contact with the developing roller 132. The toner is supplied from 133 to the developing roller 132. A layer regulating blade 136 that regulates the toner layer thickness is disposed in contact with the developing roller 132.
Each of the developing devices 130 is configured in substantially the same manner except for the developer contained in the developing housing 131, and each forms a toner image of yellow (Y), magenta (M), cyan (C), and black (K). To do.

  The surface of the rotating photosensitive drum 121 is charged by the charging roller 122, and an electrostatic latent image is formed by the latent image forming light emitted from the exposure device 110. The electrostatic latent image formed on the photosensitive drum 121 is developed as a toner image by the developing roller 132.

  The transfer device 140 includes an intermediate transfer belt 141 onto which each color toner image formed on the photosensitive drum 121 of each photoconductor unit 120 is transferred, and each color toner image formed on each photoconductor unit 120 to the intermediate transfer belt. 141 includes a primary transfer roller 142 that sequentially transfers (primary transfer) to 141, and a secondary transfer roller 143 that collectively transfers (secondary transfer) each color toner image transferred on the intermediate transfer belt 141 onto the paper P. Yes.

Each color toner image formed on the photoconductor drum 121 of each photoconductor unit 120 is sequentially electrostatically transferred (primary transfer) onto the intermediate transfer belt 141 by a primary transfer roller 142 to which a predetermined transfer voltage is applied, and each color toner. A superimposed toner image is formed by superimposing.
When the superimposed toner image on the intermediate transfer belt 141 is conveyed to the secondary transfer portion TR, the paper P is supplied from the paper feeding device to the secondary transfer portion TR in accordance with the timing. A predetermined transfer voltage is applied to the backup roller 146 that faces the secondary transfer roller 143 via the intermediate transfer belt 141, and the multiple toner images on the intermediate transfer belt 141 are collectively transferred to the paper P.

  Residual toner on the surface of the photosensitive drum 121 is removed by the cleaning device 124 and collected in a waste toner storage unit (not shown). The surface of the photosensitive drum 121 is recharged by the charging roller 122.

  The sheet P on which the toner image is transferred by the transfer device 140 is conveyed to the fixing device 160 via the sheet conveying device 150 in a state where the toner image is not fixed. The sheet P conveyed to the fixing device 160 is fixed with a toner image by the action of pressure bonding and heating by a pair of fixing belts 161 and a pressure roller 162.

In the image forming unit of the image forming apparatus 100 configured as described above, the toner seal SA in which the powder seal member 1 according to the present embodiment is disposed in contact with both side ends of the cleaning device 124 and the surface of the photosensitive drum 121. The toner seal SB is disposed between the developing roller 132 and the developing housing 131 that supports the developing roller 132 in contact with the surface of the developing roller 132.
Hereinafter, the operation of the powder seal member 1 according to the present embodiment will be described.

(2.2) Cleaning Device The cleaning device 124 is attached to the housing 123, the cleaning blade 126 disposed in contact with the surface of the photosensitive drum 121, and the lower edge of the opening provided in the housing 123. The toner scattering prevention film 127 and the inner edge SAa thereof are abutted against both ends of the cleaning blade 126, and the main part is composed of the toner seal SA attached to the housing 123 with the surface contacting the surface of the photosensitive drum 121. ing.

  In the opening portion of the housing 123, a cleaning blade 126, a toner seal SA, and a toner scattering prevention film 127 are provided in contact with the photosensitive drum 121 to form a closed space that communicates with the housing 123.

The cleaning blade 126 is made of a material having excellent mechanical properties such as wear resistance, chipping resistance, and creep resistance, for example, urethane rubber such as thermosetting polyurethane rubber, and a sheet metal having an L-shaped cross section in the housing 123. It is fixedly supported by. The tip 126a of the cleaning blade 126 contacts the surface of the photosensitive drum 121 with a predetermined contact pressure, and removes toner, paper dust, and the like from the surface of the photosensitive drum 121.
Both side ends 126 b of the cleaning blade 126 are in contact with the inner edge SAa of the toner seal SA attached to the housing 123, and the surface of the toner seal SA is disposed in contact with the surface of the photosensitive drum 121. ing.

The toner, paper dust, and the like scraped from the surface of the photosensitive drum 121 by the tip 126a of the cleaning blade 126 are collected into the housing 123 from the opening portion of the housing 123, but at both side ends 126b of the cleaning blade 126. Flows laterally and attempts to leak out of the housing 123.
In this state, the fiber layer 20 of the toner seal SA is formed on the base fabric portion 21 in a state where the ground yarn 21a opened by cutting each loop is widened at the cut upper end portion. Since the fibers are raised, toner, paper dust, or the like that flows laterally and leaks is collected between the raised fibers and dammed to suppress leakage to the outside of the housing 123.

In particular, in the toner seal SA, an adhesive layer such as a double-sided adhesive tape is not formed between the support layer 10 and the fiber layer 20 laminated by the frame laminating process, and a backing process for applying a coating agent is also performed. Absent. Therefore, in the small-sized image forming apparatus 100 that employs a small photosensitive drum 121 having a small bending resistance and, for example, an outer diameter of 20 mm to 30 mm, it may be attached to the housing 123 having an adhesive surface with a large curvature. Further, the followability to the curved surface is high, and the generation of wrinkles along the rotation axis direction of the photosensitive drum 121 on the contact surface with the photosensitive drum 121 can be suppressed.
As a result, it is possible to uniformly contact the surface of the photosensitive drum 121 without any gap and suppress the leakage of toner.

Further, the fiber layer 20 of the toner seal SA composed of the opened and raised base fabric portion 21 has a surface with an increased volume feeling and excellent cushioning properties in the thickness direction, and is soft against the photosensitive drum 121. It is possible to clean the surface of the photosensitive drum 121 while suppressing streak that is likely to occur on the surface of the photosensitive drum 121 due to contact with the surface.
Further, since the fiber layer 20 of the toner seal SA is raised by raising the base fabric portion 21 knitted by weft knitting, fraying hardly occurs even after being cut out by a die cutting method or the like. The fiber is difficult to detach from the cut end. As a result, it is possible to suppress a cleaning failure caused by the separated fibers entering the contact portion between the tip 126a of the cleaning blade 126 and the surface of the photosensitive drum 121.

(2.3) Developing Device The developing device 130 includes a developing housing 131, a developing roller 132 disposed to face the photosensitive drum 121, a supply roller 133 that supplies toner in the developing housing 131 to the developing roller 132 side, and toner A layer regulating blade 136 that regulates the layer thickness of the toner, a toner scattering prevention film 137 that is affixed to the lower edge portion of the opening provided in the developing housing 131, and an inner edge SBa thereof are abutted against both ends of the layer regulating blade 136 The main part is composed of a toner seal SB attached to the developing housing 131 with the surface contacting the surface of the developing roller 132.

In the opening portion of the developing housing 131, a layer regulating blade 136, a toner seal SB, and a toner scattering prevention film 137 are provided in contact with the developing roller 132 to form a closed space that communicates with the developing housing 131. Each of them contains yellow (Y), magenta (M), cyan (C), and black (K) toners.
The developing roller 132 has a cylindrical shape with an outer diameter of about 10 to 20 mm as an example, and the toner seal SB is bent so as to be in contact with a substantially half circumference portion of the rotating developing roller 132 and is attached to the developing housing 131. Attached.

The developing roller 132 conveys the toner supplied by the supply roller 133 and coated with a thin layer by the layer regulating blade 136 to the photosensitive drum 121.
Then, most of the toner regulated by the layer regulating blade 136 is collected in the developing housing 131 by the supply roller 133, but flows at the both ends 136 b of the layer regulating blade 136 in the lateral direction along with the rotation of the developing roller 132. It tries to leak out of the housing 131.
In the fiber layer 20 of the toner seal SB, the ground yarn 21a opened by cutting each loop is raised on the base fabric portion 21 in a state where the distance between the fibers is widened at the cut upper end portion. Therefore, the toner that flows in the lateral direction and leaks is collected between the raised fibers and is dammed to suppress leakage to the outside of the developing housing 131.

  The toner seal SB according to this embodiment is a backing process in which an adhesive layer such as a double-sided adhesive tape is not formed between the support layer 10 and the fiber layer 20 laminated by frame laminating, and a coating agent is applied. It has not been done. Therefore, the bending resistance is small, and the followability when the toner seal SB is attached to the curved surface portion of the developing housing 131 as a member to be attached is maintained. As a result, the small-diameter developing roller 132 can be easily bent and affixed to the developing housing 131 that rotatably supports the toner, and a toner sealing function can be ensured.

(3.4) Effect The toner seal SA and the toner seal SB as examples of use of the powder seal member 1 according to the present embodiment are a double-sided tape 12 and polyurethane coated with an adhesive made of an acrylic resin having no base material. The support layer 10 made of the foam material 11 and the fiber layer 20 made of the raised cloth subjected to the needle cloth raising process are configured as a laminated body bonded and laminated by a frame laminating process.
Therefore, even if it is attached to a housing having a bonding surface with a small bending resistance and a large curvature, the followability to the curved surface is high, and the photosensitive drum 121 and the development on the contact surface with the photosensitive drum 121 and the developing roller 132 are provided. Generation of wrinkles along the rotation axis direction of the roller 132 can be suppressed, and contact with the surface of the photoconductive drum 121 and the developing roller 132 without any gap can be suppressed and leakage of toner can be suppressed.

  As mentioned above, although embodiment concerning this invention was explained in full detail, this invention is not limited to the said embodiment, A various change is made within the range of the summary of this invention described in the claim. Is possible.

DESCRIPTION OF SYMBOLS 1, 1A, 1B, 1C, 200 ... Powder sealing member 10, 101 ... Support layer 11 ... Polyurethane foam material 12 ... Double-sided adhesive tape 20, 20A, 20B, 20C ... Fiber layer 21 , 21A, 21B, 21C ... base fabric part 21a ... ground yarn 22, 22B ... pile yarn 23 ... split fiber 23a ... fine fiber 30 ... fiber opening device 31 ... support Body 32 ... cloth roller 32a ... needle 40 ... double raschel knitting machine 41 ... knitting part 42 ... cutter 100 ... image forming apparatus 110 ... exposure apparatus 120 ... photosensitive Body unit 121... Photosensitive drum 122... Charging roller 123... Housing 124 .. cleaning device 126 .. cleaning blade 127, 137. SA ··· toner seal (cleaning device)
DESCRIPTION OF SYMBOLS 130 ... Development apparatus 131 ... Development housing 132 ... Development roller 133 ... Supply roller 136 ... Layer control blade SB ... Toner seal (development apparatus)
DESCRIPTION OF SYMBOLS 140 ... Transfer device 141 ... Intermediate transfer belt 142 ... Primary transfer roller 143 ... Secondary transfer roller

Claims (8)

A support layer made of a foamed elastic material having an adhesive layer formed on one surface side;
A fiber layer bonded and laminated to the other side of the support layer by frame lamination,
A powder seal member characterized by that. The fiber layer is made of a raised fabric or a nonwoven fabric in which a knitted fabric warped with a ground yarn is subjected to a needle raising process,
The powder seal member according to claim 1, The fiber layer is knitted in a state where the two layers are arranged opposite to each other, and after pile yarn is knitted into each of the base fabrics so as to bridge between the two base fabrics, Having a cut pile form formed by cutting an intermediate portion of the pile yarn and cutting off the two base fabrics,
The powder seal member according to claim 1. The fiber layer comprises a pile yarn in which ultrafine fibers formed by dividing a divided fiber into a plurality of pieces on a base fabric are raised,
The powder seal member according to claim 1. The fiber layer is formed by performing a backing treatment on the surface of the raised fabric obtained by subjecting a woven fabric to a raised fabric.
The powder seal member according to claim 1. The adhesive layer is a double-sided adhesive tape or a coated acrylic adhesive that does not use a substrate,
The powder seal member according to any one of claims 1 to 5, wherein the powder seal member is provided. The fiber layer is disposed in contact with both side edges of the cleaning member for cleaning the surface of the image carrier and the surface of the image carrier, and leakage of the toner scraped off by the cleaning member to the outside is caused by the fiber layer. Used in suppressing image forming apparatus,
The powder seal member according to any one of claims 1 to 6, wherein the powder seal member is provided. The fiber layer is disposed in contact with the surface of the developing roller between a developing roller that conveys the toner to the image carrier and a support member that supports the developing roller, and leakage of the toner to the outside is arranged in the fiber layer. Used in image forming apparatus suppressed by
The powder seal member according to any one of claims 1 to 6, wherein the powder seal member is provided.