JP2015107955A - Salt, resist composition and manufacturing method of resist pattern - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a salt capable of manufacturing a resist pattern with excellent line edge roughness (LER).SOLUTION: A compound is expressed by a formula (I). [In the formula (I), Qand Qare independently a fluorine atom or a perfluoroalkyl group having 1-6 carbon atoms. Lis a divalent saturated hydrocarbon group having 1-24 carbon atoms. Ris an alkanediyl group having 1-12 carbon atoms. Ris a hydrogen atom or an acid-labile group. W is an aliphatic ring having 3-36 carbon atoms. A methylene group forming the aliphatic ring may be substituted by an oxygen atom, a sulfur atom, a carbonyl group or a sulfonyl group. A hydrogen atom included in the aliphatic ring may be substituted by a hydroxy group, an alkyl group having 1-12 carbon atoms or an alkoxy group having 1-12 carbon atoms. m is 0 or 1. Zis an organic counterion.]

Description

  The present invention relates to a salt used for semiconductor microfabrication, a resist composition, and a method for producing a resist pattern.

Patent Document 1 describes a resist composition containing a salt represented by the following formula (B ′) and a salt represented by the formula (B ′).

JP 2006-257078 A

  In the resist composition containing the salt represented by the formula (B ′), the line edge roughness (LER) of the resist pattern may not always be sufficiently satisfied.

［式（Ｉ）中、
Ｑ¹及びＱ²は、それぞれ独立に、フッ素原子又は炭素数１〜６のペルフルオロアルキル基を表す。
Ｌ^b1は、炭素数１〜２４の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基で置換されていてもよい。
Ｒ^１は、炭素数１〜１２のアルカンジイル基を表し、アルカンジイル基に含まれる水素原子は、ヒドロキシ基又は炭素数１〜１２のアルコキシ基に置換されていてもよく、アルカンジイル基を構成するメチレン基は、酸素原子に置き換わっていてもよい。
Ｒ^２は、水素原子又は酸不安定基を表す。
Ｗは、炭素数３〜３６の脂肪族環を表し、該脂肪族環を構成するメチレン基は、酸素原子、硫黄原子、カルボニル基又はスルホニル基に置き換わっていてもよく、該脂肪族環に含まれる水素原子は、ヒドロキシ基、炭素数１〜１２のアルキル基又は炭素数１〜１２のアルコキシ基に置換されていてもよい。
ｍは、０又は１を表す。
Ｚ^＋は、有機対イオンを表す。］
〔２〕Ｗが、炭素数５〜１８の脂肪族環である〔１〕記載の塩。
〔３〕Ｗが、アダマンタン環である〔１〕又は〔２〕記載の塩。
〔４〕Ｌ^b1が、＊−ＣＯ−Ｏ−（ＣＨ_２）_ｎ−（ｎは、０又は１を表す。＊はＣＱ¹Ｑ²との結合位置を表す。）である〔１〕〜〔３〕のいずれか記載の塩。
〔５〕Ｒ^１が、炭素数１〜６のアルカンジイル基である前記〔１〕〜〔４〕のいずれか記載の塩。
〔６〕Ｒ^２が水素原子である前記〔１〕〜〔５〕のいずれか記載の塩。
〔７〕Ｚ^＋が、アリールスルホニウムカチオンである〔１〕〜〔６〕のいずれか記載の塩。
〔８〕〔１〕〜〔７〕のいずれか記載の塩と酸不安定基を有する樹脂とを含有するレジスト組成物。
〔９〕（１）〔８〕記載のレジスト組成物を基板上に塗布する工程、
（２）塗布後の組成物を乾燥させて組成物層を形成する工程、
（３）組成物層に露光する工程、
（４）露光後の組成物層を加熱する工程、及び
（５）加熱後の組成物層を現像する工程
を含むレジストパターンの製造方法。 The present invention includes the following inventions.
[1] A salt represented by the formula (I).

[In the formula (I),
Q ¹ and Q ² each independently represents a fluorine atom or a C 1-6 perfluoroalkyl group.
L ^b1 represents a divalent saturated hydrocarbon group having 1 to 24 carbon atoms, and the methylene group contained in the saturated hydrocarbon group may be replaced by an oxygen atom or a carbonyl group. The hydrogen atom contained may be substituted with a fluorine atom or a hydroxy group.
R ¹ represents an alkanediyl group having 1 to 12 carbon atoms, and a hydrogen atom contained in the alkanediyl group may be substituted with a hydroxy group or an alkoxy group having 1 to 12 carbon atoms to form an alkanediyl group. The methylene group may be replaced by an oxygen atom.
R ² represents a hydrogen atom or an acid labile group.
W represents an aliphatic ring having 3 to 36 carbon atoms, and the methylene group constituting the aliphatic ring may be replaced by an oxygen atom, a sulfur atom, a carbonyl group or a sulfonyl group, and is included in the aliphatic ring. The hydrogen atom to be substituted may be substituted with a hydroxy group, an alkyl group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
m represents 0 or 1.
Z ⁺ represents an organic counter ion. ]
[2] The salt according to [1], wherein W is an aliphatic ring having 5 to 18 carbon atoms.
[3] The salt according to [1] or [2], wherein W is an adamantane ring.
[4] L ^b1 is * —CO—O— (CH ₂ ) _n — (n represents 0 or 1; * represents the bonding position with CQ ¹ Q ² ) [1] to [ 3]. The salt according to any one of 3).
[5] The salt according to any one of [1] to [4], wherein R ¹ is an alkanediyl group having 1 to 6 carbon atoms.
[6] The salt according to any one of [1] to [5], wherein R ² is a hydrogen atom.
[7] The salt according to any one of [1] to [6], wherein Z ⁺ is an arylsulfonium cation.
[8] A resist composition comprising the salt according to any one of [1] to [7] and a resin having an acid labile group.
[9] A step of applying the resist composition according to (1) [8] on a substrate,
(2) The process of drying the composition after application | coating and forming a composition layer,
(3) a step of exposing the composition layer;
(4) A method for producing a resist pattern, comprising a step of heating the composition layer after exposure, and (5) a step of developing the composition layer after heating.

  A salt capable of producing a resist pattern having good line edge roughness (LER) is provided.

In the present specification, "(meth) acrylic monomer" means at least one monomer having a "CH ₂ = CH-CO-" or _{"CH 2 = C (CH 3)} -CO- " structure of To do. Similarly, “(meth) acrylate” and “(meth) acrylic acid” mean “at least one of acrylate and methacrylate” and “at least one of acrylic acid and methacrylic acid”, respectively.

［式（Ｉ）中、
Ｑ¹及びＱ²は、それぞれ独立に、フッ素原子又は炭素数１〜６のペルフルオロアルキル基を表す。
Ｌ^b1は、炭素数１〜２４の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基で置換されていてもよい。
Ｒ^１は、炭素数１〜１２のアルカンジイル基を表し、アルカンジイル基に含まれる水素原子は、ヒドロキシ基又は炭素数１〜１２のアルコキシ基に置換されていてもよく、アルカンジイル基を構成するメチレン基は、酸素原子に置き換わっていてもよい。
Ｒ^２は、水素原子又は酸不安定基を表す。
Ｗは、炭素数３〜３６の脂肪族環を表し、該脂肪族環を構成するメチレン基は、酸素原子、硫黄原子、カルボニル基又はスルホニル基に置き換わっていてもよく、該脂肪族環に含まれる水素原子は、ヒドロキシ基、炭素数１〜１２のアルキル基又は炭素数１〜１２のアルコキシ基に置換されていてもよい。
ｍは、０又は１を表す。
Ｚ^＋は、有機対イオンを表す。］ <Salt represented by formula (I)>
The salt of the present invention is a salt represented by the formula (I) (hereinafter sometimes referred to as “salt (I)”).

[In the formula (I),
Q ¹ and Q ² each independently represents a fluorine atom or a C 1-6 perfluoroalkyl group.
L ^b1 represents a divalent saturated hydrocarbon group having 1 to 24 carbon atoms, and the methylene group contained in the saturated hydrocarbon group may be replaced by an oxygen atom or a carbonyl group. The hydrogen atom contained may be substituted with a fluorine atom or a hydroxy group.
R ¹ represents an alkanediyl group having 1 to 12 carbon atoms, and a hydrogen atom contained in the alkanediyl group may be substituted with a hydroxy group or an alkoxy group having 1 to 12 carbon atoms to form an alkanediyl group. The methylene group may be replaced by an oxygen atom.
R ² represents a hydrogen atom or an acid labile group.
W represents an aliphatic ring having 3 to 36 carbon atoms, and the methylene group constituting the aliphatic ring may be replaced by an oxygen atom, a sulfur atom, a carbonyl group or a sulfonyl group, and is included in the aliphatic ring. The hydrogen atom to be substituted may be substituted with a hydroxy group, an alkyl group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
m represents 0 or 1.
Z ⁺ represents an organic counter ion. ]

  Hereinafter, the anion contained in the salt represented by the formula (I) may be referred to as “sulfonate anion”.

Examples of the perfluoroalkyl group represented by Q ¹ and Q ² include trifluoromethyl group, perfluoroethyl group, perfluoropropyl group, perfluoroisopropyl group, perfluorobutyl group, perfluoro sec-butyl group, perfluorotert-butyl group, perfluoropentyl. Group and perfluorohexyl group.
Q ¹ and Q ² are each independently preferably a fluorine atom or a trifluoromethyl group, and both Q ¹ and Q ² are more preferably a fluorine atom.

Examples of the divalent saturated hydrocarbon group represented by L ^b1 include a linear alkanediyl group, a branched alkanediyl group, and a monocyclic or polycyclic divalent alicyclic saturated hydrocarbon group. A combination of two or more of these groups may be used.
Specifically, methylene group, ethylene group, propane-1,3-diyl group, butane-1,4-diyl group, pentane-1,5-diyl group, hexane-1,6-diyl group, heptane-1 , 7-diyl group, octane-1,8-diyl group, nonane-1,9-diyl group, decane-1,10-diyl group, undecane-1,11-diyl group, dodecane-1,12-diyl group , Tridecane-1,13-diyl group, tetradecane-1,14-diyl group, pentadecane-1,15-diyl group, hexadecane-1,16-diyl group and heptadecane-1,17-diyl group Alkanediyl group;
Ethane-1,1-diyl group, propane-1,1-diyl group, propane-1,2-diyl group, propane-2,2-diyl group, pentane-2,4-diyl group, 2-methylpropane- Branched alkanediyl groups such as 1,3-diyl group, 2-methylpropane-1,2-diyl group, pentane-1,4-diyl group, 2-methylbutane-1,4-diyl group;
Monocyclic 2 which is a cycloalkanediyl group such as cyclobutane-1,3-diyl group, cyclopentane-1,3-diyl group, cyclohexane-1,4-diyl group, cyclooctane-1,5-diyl group Valent alicyclic saturated hydrocarbon group;
Polycyclic divalent alicyclic saturated hydrocarbon such as norbornane-1,4-diyl group, norbornane-2,5-diyl group, adamantane-1,5-diyl group, adamantane-2,6-diyl group, etc. Groups and the like.

Examples of the group in which —CH ₂ — contained in the divalent saturated hydrocarbon group represented by L ^b1 is replaced by —O— or —CO— include any of formulas (b1-1) to (b1-3). The group represented by is mentioned. In the formulas (b1-1) to (b1-3) and the following specific examples, * represents a bond with -W.

式（ｂ１−１）中、
Ｌ^b2は、単結合又は炭素数１〜２２の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
Ｌ^b3は、単結合又は炭素数１〜２２の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよく、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。
ただし、Ｌ^b2とＬ^b3との炭素数合計は、２２以下である。
式（ｂ１−２）中、
Ｌ^b４は、単結合又は炭素数１〜２２の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
Ｌ^b５は、単結合又は炭素数１〜２２の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよく、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。
ただし、Ｌ^b4とＬ^b5との炭素数合計は、２２以下である。
式（ｂ１−３）中、
Ｌ^b6は、単結合又は炭素数１〜２３の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
Ｌ^b7は、単結合又は炭素数１〜２３の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよく、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。
ただし、Ｌ^b6とＬ^b7との炭素数合計は、２３以下である。

In formula (b1-1),
L ^b2 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b3 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, The methylene group contained in the hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.
However, the total number of carbon atoms of L ^b2 and L ^b3 is 22 or less.
In formula (b1-2),
L ^b4 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b5 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, The methylene group contained in the hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.
However, the total carbon number of L ^b4 and L ^b5 is 22 or less.
In formula (b1-3),
L ^b6 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
L ^b7 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group, The methylene group contained in the hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.
However, the total carbon number of L ^b6 and L ^b7 is 23 or less.

In formulas (b1-1) to (b1-3), when the methylene group contained in the saturated hydrocarbon group is replaced with an oxygen atom or a carbonyl group, the number of carbons before the replacement is represented by the saturated hydrocarbon group. The number of carbons.
Examples of the divalent saturated hydrocarbon group include the same divalent saturated hydrocarbon group of L ^b1.

L ^b2 is preferably a single bond.
L ^b3 is preferably an alkanediyl group having 1 to 4 carbon atoms.
L ^b4 is preferably a C 1-8 divalent saturated hydrocarbon group, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b5 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^b6 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 4 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b7 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group The methylene group contained in the saturated hydrocarbon group may be replaced with an oxygen atom or a carbonyl group.

  Among these, a group represented by the formula (b1-1) or the formula (b1-3) is preferable.

式（ｂ１−４）中、
Ｌ^b8は、単結合又は炭素数１〜２２の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
式（ｂ１−５）中、
Ｌ^b9は、炭素数１〜２０の２価の飽和炭化水素基を表す。
Ｌ^b10は、単結合又は炭素数１〜１９の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b9及びＬ^b10の合計炭素数は２０以下である。
式（ｂ１−６）中、
Ｌ^b11は、炭素数１〜２１の２価の飽和炭化水素基を表す。
Ｌ^b12は、単結合又は炭素数１〜２０の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b11及びＬ^b12の合計炭素数は２１以下である。
式（ｂ１−７）中、
Ｌ^b13は、炭素数１〜１９の２価の飽和炭化水素基を表す。
Ｌ^b14は、単結合又は炭素数１〜１８の２価の飽和炭化水素基を表す。
Ｌ^b15は、単結合又は炭素数１〜１８の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b13、Ｌ^b14及びＬ^b15の合計炭素数は１９以下である。
式（ｂ１−８）中、
Ｌ^b16は、炭素数１〜１８の２価の飽和炭化水素基を表す。
Ｌ^b17は、炭素数１〜１８の２価の飽和炭化水素基を表す。
Ｌ^b18は、単結合又は炭素数１〜１７の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子又はヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b16、Ｌ^b17及びＬ^b18の合計炭素数は１９以下である。 Examples of formula (b1-1) include groups represented by formula (b1-4) to formula (b1-8).

In formula (b1-4),
L ^b8 represents a single bond or a divalent saturated hydrocarbon group having 1 to 22 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
In formula (b1-5),
L ^b9 represents a divalent saturated hydrocarbon group having 1 to 20 carbon atoms.
L ^b10 represents a single bond or a divalent saturated hydrocarbon group having 1 to 19 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
However, the total carbon number of L ^b9 and L ^b10 is 20 or less.
In formula (b1-6),
L ^b11 represents a divalent saturated hydrocarbon group having 1 to 21 carbon atoms.
L ^b12 represents a single bond or a ^C 1-20 divalent saturated hydrocarbon group, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
However, the total carbon number of L ^b11 and L ^b12 is 21 or less.
In formula (b1-7),
L ^b13 represents a divalent saturated hydrocarbon group having 1 to 19 carbon atoms.
L ^b14 represents a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms.
L ^b15 represents a single bond or a C 1-18 divalent saturated hydrocarbon group, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
However, the total carbon number of L ^b13 , L ^b14 and L ^b15 is 19 or less.
In formula (b1-8),
L ^b16 represents a divalent saturated hydrocarbon group having 1 to 18 carbon atoms.
L ^b17 represents a divalent saturated hydrocarbon group having 1 to 18 carbon atoms.
L ^b18 represents a single bond or a divalent saturated hydrocarbon group having 1 to 17 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom or a hydroxy group.
However, the total carbon number of L ^b16 , L ^b17 and L ^b18 is 19 or less.

L ^b8 is preferably an alkanediyl group having 1 to 4 carbon atoms.
L ^b9 is preferably a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^b10 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 19 carbon atoms, and more preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^b11 is preferably a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^b12 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^b13 is preferably a divalent saturated hydrocarbon group having 1 to 12 carbon atoms.
L ^b14 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 6 carbon atoms.
L ^b15 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and more preferably a single bond or a divalent saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^b16 preferably represents a divalent saturated hydrocarbon group having 1 to 12 carbon atoms.
L ^b17 preferably represents a ^C 1-6 divalent saturated hydrocarbon group.
L ^b18 is preferably a single bond or a divalent saturated hydrocarbon group having 1 to 17 carbon atoms, more preferably a single bond or a divalent saturated hydrocarbon group having 1 to 4 carbon atoms,

式（ｂ１−９）中、
Ｌ^b19は、単結合又は炭素数１〜２３の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
Ｌ^b20は、単結合又は炭素数１〜２３の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子、ヒドロキシ基又はアシルオキシ基に置換されていてもよい。該アシルオキシ基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該アシルオキシ基に含まれる水素原子は、ヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b19及びＬ^b20の合計炭素数は２３以下である。
式（ｂ１−１０）中、
Ｌ^b21は、単結合又は炭素数１〜２１の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
Ｌ^b22は、単結合又は炭素数１〜２１の２価の飽和炭化水素基を表す。
Ｌ^b23は、単結合又は炭素数１〜２１の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子、ヒドロキシ基又はアシルオキシ基に置換されていてもよい。該アシルオキシ基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該アシルオキシ基に含まれる水素原子は、ヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b21、Ｌ^b22及びＬ^b23の合計炭素数は２１以下である。
式（ｂ１−１１）中、
Ｌ^b24は、単結合又は炭素数１〜２０の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子に置換されていてもよい。
Ｌ^b25は、炭素数１〜２１の２価の飽和炭化水素基を表す。
Ｌ^b26は、単結合又は炭素数１〜２０の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、フッ素原子、ヒドロキシ基又はアシルオキシ基に置換されていてもよい。該アシルオキシ基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよく、該アシルオキシ基に含まれる水素原子は、ヒドロキシ基に置換されていてもよい。
ただし、Ｌ^b24、Ｌ^b25及びＬ^b26の合計炭素数は２１以下である。 Examples of formula (b1-3) include groups represented by formula (b1-9) to formula (b1-11), respectively.

In formula (b1-9),
L ^b19 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b20 represents a single bond or a divalent saturated hydrocarbon group having 1 to 23 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom, a hydroxy group or an acyloxy group. . The methylene group contained in the acyloxy group may be replaced with an oxygen atom or a carbonyl group, and the hydrogen atom contained in the acyloxy group may be substituted with a hydroxy group.
However, the total carbon number of L ^b19 and L ^b20 is 23 or less.
In formula (b1-10),
L ^b21 represents a single bond or a divalent saturated hydrocarbon group having 1 to ²¹ carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b22 represents a single bond or a divalent saturated hydrocarbon group having 1 to 21 carbon atoms.
L ^b23 represents a single bond or a divalent saturated hydrocarbon group having 1 to ²¹ carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom, a hydroxy group or an acyloxy group. . The methylene group contained in the acyloxy group may be replaced with an oxygen atom or a carbonyl group, and the hydrogen atom contained in the acyloxy group may be substituted with a hydroxy group.
However, the total carbon number of L ^b21 , L ^b22 and L ^b23 is 21 or less.
In formula (b1-11),
L ^b24 represents a single bond or a divalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom.
L ^b25 represents a divalent saturated hydrocarbon group having 1 to 21 carbon atoms.
L ^b26 represents a single bond or a divalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a fluorine atom, a hydroxy group or an acyloxy group. . The methylene group contained in the acyloxy group may be replaced with an oxygen atom or a carbonyl group, and the hydrogen atom contained in the acyloxy group may be substituted with a hydroxy group.
However, L ^b24, the total number of carbon atoms of L ^b25 and L ^b26 is 21 or less.

  In formulas (b1-10) and (b1-11), when a hydrogen atom contained in a saturated hydrocarbon group is substituted with an acyloxy group, the number of carbon atoms in the acyloxy group, CO and O in the ester bond And the number of carbon atoms of the saturated hydrocarbon group.

Examples of the acyloxy group include an acetyloxy group, a propionyloxy group, a butyryloxy group, a cyclohexylcarbonyloxy group, and an adamantylcarbonyloxy group.
Examples of the acyloxy group having a substituent include an oxoadamantylcarbonyloxy group, a hydroxyadamantylcarbonyloxy group, an oxocyclohexylcarbonyloxy group, and a hydroxycyclohexylcarbonyloxy group.

Of the groups represented by formula (b1-1), examples of the group represented by formula (b1-4) include the following.

Of the groups represented by the formula (b1-1), examples of the group represented by the formula (b1-5) include the following.

Of the groups represented by formula (b1-1), examples of the group represented by formula (b1-6) include the following.

Of the groups represented by the formula (b1-1), examples of the group represented by the formula (b1-7) include the following.

Of the groups represented by the formula (b1-1), examples of the group represented by the formula (b1-8) include the following.

Examples of the group represented by the formula (b1-2) include the following.

Of the groups represented by formula (b1-3), examples of the group represented by formula (b1-9) include the following.

Of the groups represented by the formula (b1-3), examples of the group represented by the formula (b1-10) include the following.

Of the groups represented by formula (b1-3), examples of the group represented by formula (b1-11) include the following.

The aliphatic ring of W may be any of monocyclic, polycyclic, condensed ring and bridged ring.
Examples of the monocyclic aliphatic ring include cycloalkane rings represented by the following formulas (KA-1) to (KA-7).

Examples of the polycyclic aliphatic hydrocarbon group include cycloalkanes represented by the following formulas (KA-8) to (KA-22).

The hydrogen atom in the aliphatic ring having 3 to 36 carbon atoms represented by W may be substituted with a hydroxy group, an alkyl group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
Examples of the alkyl group include methyl group, ethyl group, isopropyl group, tert-butyl group, 2,2-dimethylethyl group, propyl group, 1-methylpropyl group, 2,2-dimethylpropyl group, 1-ethylpropyl group, Butyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-propylbutyl, pentyl, 1-methylpentyl, hexyl, 1,4-dimethylhexyl, heptyl, 1-methyl Heptyl, octyl, methyloctyl, methylnonyl, 2-ethylhexyl, nonyl, decyl, undecyl, dodecyl, cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl , Cyclononyl group, cyclodecyl group, norbornyl group, 1-adaman Group, 2-adamantyl group, etc. isobornyl group.

  As the alkoxy group, methoxy group, ethoxy group, n-propoxy group, isopropoxy group, n-butoxy group, sec-butoxy group, tert-butoxy group, n-pentoxy group, n-hexoxy group, heptoxy group, octoxy group , 2-ethylhexoxy group, nonyloxy group, decyloxy group, undecyloxy group, dodecyloxy group and the like.

Examples of the alkanediyl group having 1 to 12 carbon atoms represented by R ¹ include a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, and a pentane-1,5-diyl group. Hexane-1,6-diyl group, heptane-1,7-diyl group, octane-1,8-diyl group, nonane-1,9-diyl group, decane-1,10-diyl group, undecane-1, Linear alkanediyl groups such as 11-diyl group, dodecane-1,12-diyl group;
Ethane-1,1-diyl group, propane-1,1-diyl group, propane-1,2-diyl group, propane-2,2-diyl group, pentane-2,4-diyl group, 2-methylpropane- Examples thereof include branched alkanediyl groups such as 1,3-diyl group, 2-methylpropane-1,2-diyl group, pentane-1,4-diyl group, and 2-methylbutane-1,4-diyl group.

The hydrogen atom contained in the alkanediyl group having 1 to 12 carbon atoms represented by R ¹ may be substituted with a hydroxy group or an alkoxy group having 1 to 12 carbon atoms. Examples of the alkoxy group having 1 to 12 carbon atoms are the same as those described above.

R ² represents a hydrogen atom or an acid labile group. An acid labile group has a leaving group, and the leaving group is eliminated by contact with an acid, and the group represented by —OR ² is converted into a hydrophilic group (for example, a hydroxy group or a carboxy group). Represents a group. Examples of the acid labile group include a group represented by the formula (1A) and a group represented by the formula (2A). Among these, the group represented by the formula (2A) is preferable.

［式（１Ａ）中、Ｒ^a1〜Ｒ^a3は、それぞれ独立に、炭素数１〜８のアルキル基、炭素数３〜２０の脂環式炭化水素基又はこれらを組合わせた基を表すか、Ｒ^a1及びＲ^a2は互いに結合して炭素数２〜２０の２価の炭化水素基を形成する。
ｎａは、０又は１を表す。
＊は結合手を表す。］

［式（２Ａ）中、Ｒ^a1’及びＲ^a2’は、それぞれ独立に、水素原子又は炭素数１〜１２の炭化水素基を表し、Ｒ^a3’は、炭素数１〜２０の炭化水素基を表すか、Ｒ^a2’及びＲ^a3’は互いに結合して炭素数２〜２０の２価の炭化水素基を形成し、該炭化水素基及び該２価の炭化水素基に含まれる−ＣＨ_２−は、−Ｏ−又は−Ｓ−で置き換わってもよい。
Ｘは、酸素原子又は硫黄原子を表す。
＊は結合手を表す。］

[In the formula (1A), R ^{a1 to} R ^a3 each independently represents an alkyl group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 20 carbon atoms, or a group obtained by combining these, R ^a1 and R ^a2 are bonded to each other to form a divalent hydrocarbon group having 2 to 20 carbon atoms.
na represents 0 or 1.
* Represents a bond. ]

[In Formula (2A), R ^{a1 ′} and R ^{a2 ′} each independently represent a hydrogen atom or a hydrocarbon group having 1 to 12 carbon atoms, and R ^{a3 ′} represents a hydrocarbon group having 1 to 20 carbon atoms. R ^{a2 ′} and R ^{a3 ′} are bonded to each other to form a divalent hydrocarbon group having 2 to 20 carbon atoms, and —CH ₂ — contained in the hydrocarbon group and the divalent hydrocarbon group. May be replaced by -O- or -S-.
X represents an oxygen atom or a sulfur atom.
* Represents a bond. ]

アルキル基と脂環式炭化水素基とを組合わせた基としては、メチルシクロヘキシル基、ジメチルシクロへキシル基、メチルノルボルニル基、シクロヘキシルメチル基、アダマンチルメチル基、ノルボルニルエチル基等が挙げられる。
ｎａは、好ましくは０である。 ^Examples of the alkyl group represented by R ^{a1 to} R ^a3 include a methyl group, an ethyl group, a propyl group, an n-butyl group, an n-pentyl group, an n-hexyl group, an n-heptyl group, and an n-octyl group.
The alicyclic hydrocarbon group for R ^{a1 to} R ^a3 may be monocyclic or polycyclic. Examples of the monocyclic alicyclic hydrocarbon group include cycloalkyl groups such as a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, and a cyclooctyl group. Examples of the polycyclic alicyclic hydrocarbon group include decahydronaphthyl group, adamantyl group, norbornyl group, and the following groups (* represents a bond). The alicyclic hydrocarbon group of R ^{a1 to} R ^a3 is preferably an alicyclic hydrocarbon group having 3 to 16 carbon atoms.

Examples of the group in which an alkyl group and an alicyclic hydrocarbon group are combined include a methylcyclohexyl group, a dimethylcyclohexyl group, a methylnorbornyl group, a cyclohexylmethyl group, an adamantylmethyl group, and a norbornylethyl group. It is done.
na is preferably 0.

Examples of —C (R ^a1 ) (R ^a2 ) (R ^a3 ) in the case where R ^a1 and R ^a2 are bonded to each other to form a divalent hydrocarbon group include the following groups. The divalent hydrocarbon group preferably has 3 to 12 carbon atoms. * Represents a bond with -O-.

Examples of the group represented by the formula (1A) include a 1,1-dialkylalkoxycarbonyl group (a group in which R ^{a1 to} R ^a3 are alkyl groups in the formula (1A), preferably a tert-butoxycarbonyl group), 2- An alkyladamantan-2-yloxycarbonyl group (in the formula (1A), R ^a1 , R ^a2 and the carbon atom to which they are bonded form an adamantyl group, and R ^a3 is an alkyl group) and 1- (adamantane- 1-yl) -1-alkylalkoxycarbonyl group (in the formula (1A), R ^a1 and R ^a2 are alkyl groups, and R ^a3 is an adamantyl group).

Examples of the hydrocarbon group of R ^{a1 ′ to} R ^{a3 ′} include an alkyl group, an alicyclic hydrocarbon group, an aromatic hydrocarbon group, and a group formed by combining these.
Examples of the alkyl group and alicyclic hydrocarbon group are the same as those described above.
Aromatic hydrocarbon groups include phenyl, naphthyl, anthryl, p-methylphenyl, p-tert-butylphenyl, p-adamantylphenyl, tolyl, xylyl, cumenyl, mesityl, biphenyl Groups, phenanthryl groups, 2,6-diethylphenyl groups, aryl groups such as 2-methyl-6-ethylphenyl, and the like.
Examples of the divalent hydrocarbon group formed by combining R ^{a2 ′} and R ^{a3 ′} include groups in which one hydrogen atom has been removed from the hydrocarbon groups of R ^{a1 ′ to} R ^{a3 ′} .
At least one of R ^{a1 ′} and R ^{a2 ′} is preferably a hydrogen atom.

Specific examples of the group represented by the formula (2A) include the following groups. * Represents a bond.

R ¹ is preferably an alkanediyl group having 1 to 6 carbon atoms.
R ² is preferably a hydrogen atom.

Examples of the sulfonate anion include the following anions.

Examples of the organic cation represented by Z ⁺ include organic onium cations such as an organic sulfonium cation, an organic iodonium cation, an organic ammonium cation, a benzothiazolium cation, and an organic phosphonium cation. Among these, an organic sulfonium cation and an organic iodonium cation are preferable, and an arylsulfonium cation is more preferable.
Z ⁺ in formula (I) is preferably a cation represented by any one of formulas (b2-1) to (b2-4) [hereinafter referred to as “cation (b2-1)” or the like depending on the formula number, etc. There is a case. ].

In formula (b2-1) to formula (b2-4),
R ^{b4 to} R ^b6 each independently represents an aliphatic hydrocarbon group having 1 to 30 carbon atoms, an alicyclic hydrocarbon group having 3 to 36 carbon atoms, or an aromatic hydrocarbon group having 6 to 36 carbon atoms, The hydrogen atom contained in the aliphatic hydrocarbon group is a hydroxy group, an alkoxy group having 1 to 12 carbon atoms, an alicyclic hydrocarbon group having 3 to 12 carbon atoms, or an aromatic hydrocarbon group having 6 to 18 carbon atoms. The hydrogen atom contained in the alicyclic hydrocarbon group may be substituted with a halogen atom, an aliphatic hydrocarbon group having 1 to 18 carbon atoms, an acyl group having 2 to 4 carbon atoms, or a glycidyloxy group. The hydrogen atom contained in the aromatic hydrocarbon group may be substituted with a halogen atom, a hydroxy group or an alkoxy group having 1 to 12 carbon atoms.
R ^b4 and R ^b5 may together form a ring containing a sulfur atom to which they are bonded, and —CH ₂ — contained in the ring is —O—, —SO— or —CO—. May be replaced.

R ^b7 and R ^b8 each independently represent a hydroxy group, an aliphatic hydrocarbon group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
m2 and n2 each independently represent an integer of 0 to 5.
When m2 is 2 or more, the plurality of R ^b7 may be the same or different, and when n2 is 2 or more, the plurality of R ^b8 may be the same or different.

R ^b9 and R ^b10 each independently represent an aliphatic hydrocarbon group having 1 to 36 carbon atoms or an alicyclic hydrocarbon group having 3 to 36 carbon atoms.
R ^b9 and R ^b10 together may form a ring containing a sulfur atom to which they are bonded, and —CH ₂ — contained in the ring is —O—, —SO— or —CO—. May be replaced.
R ^b11 represents a hydrogen atom, an aliphatic hydrocarbon group having 1 to 36 carbon atoms, an alicyclic hydrocarbon group having 3 to 36 carbon atoms, or an aromatic hydrocarbon group having 6 to 18 carbon atoms.
R ^b12 represents an aliphatic hydrocarbon group having 1 to 12 carbon atoms, an alicyclic hydrocarbon group having 3 to 18 carbon atoms, or an aromatic hydrocarbon group having 6 to 18 carbon atoms, and is included in the aliphatic hydrocarbon The hydrogen atom may be substituted with an aromatic hydrocarbon group having 6 to 18 carbon atoms, and the hydrogen atom contained in the aromatic hydrocarbon group is an alkoxy group having 1 to 12 carbon atoms or 1 to 1 carbon atoms. It may be substituted with 12 alkylcarbonyloxy groups.
R ^b11 and R ^b12 may together form a ring containing —CH—CO— to which they are bonded, and —CH ₂ — contained in the ring is —O—, —SO—. Alternatively, it may be replaced by -CO-.

R ^{b13 to} R ^b18 each independently represent a hydroxy group, an aliphatic hydrocarbon group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
L ^b11 represents -S- or -O-.
o2, p2, s2, and t2 each independently represents an integer of 0 to 5.
q2 and r2 each independently represents an integer of 0 to 4.
u2 represents 0 or 1.
When o2 is 2 or more, multiple R ^b13 are the same or different, when p2 is 2 or more, multiple R ^b14 are the same or different, and when q2 is 2 or more, multiple R ^b15 are the same or different , When r2 is 2 or more, a plurality of R ^b16 are the same or different, when s2 is 2 or more, a plurality of R ^b17 are the same or different, and when t2 is 2 or more, a plurality of R ^b18 are the same or different Different.

特に、Ｒ^b9〜Ｒ^b12の脂環式炭化水素基は、好ましくは炭素数３〜１８、より好ましくは炭素数４〜１２である。 Examples of the aliphatic hydrocarbon group include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, pentyl group, hexyl group, octyl group and 2-ethylhexyl group. Of the alkyl group. In particular, the aliphatic hydrocarbon group represented by R ^{b9 to} R ^b12 preferably has 1 to 12 carbon atoms.
The alicyclic hydrocarbon group may be monocyclic or polycyclic. Examples of the monocyclic alicyclic hydrocarbon group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, and a cyclohexyl group. Cycloalkyl groups such as cycloheptyl group, cyclooctyl group, and cyclodecyl group. Examples of the polycyclic alicyclic hydrocarbon group include decahydronaphthyl group, adamantyl group, norbornyl group, and the following groups.

In particular, the alicyclic hydrocarbon group of R ^{b9 to} R ^b12 preferably has 3 to 18 carbon atoms, more preferably 4 to 12 carbon atoms.

  Examples of the alicyclic hydrocarbon group in which a hydrogen atom is substituted with an aliphatic hydrocarbon group include a methylcyclohexyl group, a dimethylcyclohexyl group, a 2-alkyladamantan-2-yl group, a methylnorbornyl group, and an isobornyl group. Groups and the like. In the alicyclic hydrocarbon group in which a hydrogen atom is substituted with an aliphatic hydrocarbon group, the total number of carbon atoms of the alicyclic hydrocarbon group and the aliphatic hydrocarbon group is preferably 20 or less.

As aromatic hydrocarbon group, phenyl group, tolyl group, xylyl group, cumenyl group, mesityl group, p-ethylphenyl group, p-tert-butylphenyl group, p-cyclohexylphenyl group, p-adamantylphenyl group , Aryl groups such as a biphenylyl group, a naphthyl group, a phenanthryl group, a 2,6-diethylphenyl group, and a 2-methyl-6-ethylphenyl group.
When the aromatic hydrocarbon group includes an aliphatic hydrocarbon group or an alicyclic hydrocarbon group, the aliphatic hydrocarbon group having 1 to 18 carbon atoms and the alicyclic hydrocarbon having 3 to 18 carbon atoms Groups are preferred.
Examples of the aromatic hydrocarbon group in which a hydrogen atom is substituted with an alkoxy group include a p-methoxyphenyl group.
Examples of the aliphatic hydrocarbon group in which a hydrogen atom is substituted with an aromatic hydrocarbon group include aralkyl groups such as a benzyl group, a phenethyl group, a phenylpropyl group, a trityl group, a naphthylmethyl group, and a naphthylethyl group.

Examples of the alkoxy group include methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, heptyloxy group, octyloxy group, decyloxy group and dodecyloxy group.
Examples of the acyl group include an acetyl group, a propionyl group, and a butyryl group.
Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.
Examples of the alkylcarbonyloxy group include a methylcarbonyloxy group, an ethylcarbonyloxy group, an n-propylcarbonyloxy group, an isopropylcarbonyloxy group, an n-butylcarbonyloxy group, a sec-butylcarbonyloxy group, a tert-butylcarbonyloxy group, Examples thereof include a pentylcarbonyloxy group, a hexylcarbonyloxy group, an octylcarbonyloxy group, and a 2-ethylhexylcarbonyloxy group.

The ring containing a sulfur atom formed by combining R ^b4 and R ^b5 may be any of monocyclic, polycyclic, aromatic, non-aromatic, saturated and unsaturated rings. . Examples of the ring include a ring having 3 to 18 carbon atoms, and a ring having 4 to 18 carbon atoms is preferable. Examples of the ring containing a sulfur atom include a 3-membered ring to a 12-membered ring, preferably a 3-membered ring to a 7-membered ring. The following rings are mentioned.

The ring formed by combining R ^b9 and R ^b10 may be any of monocyclic, polycyclic, aromatic, non-aromatic, saturated and unsaturated rings. This ring includes a 3-membered ring to a 12-membered ring, preferably a 3-membered ring to a 7-membered ring. Examples thereof include a thiolane-1-ium ring (tetrahydrothiophenium ring), a thian-1-ium ring, and a 1,4-oxathian-4-ium ring.
The ring formed by ^combining R ^b11 and R ^b12 may be any of monocyclic, polycyclic, aromatic, non-aromatic, saturated and unsaturated rings. This ring includes a 3-membered ring to a 12-membered ring, preferably a 3-membered ring to a 7-membered ring. Examples thereof include an oxocycloheptane ring, an oxocyclohexane ring, an oxonorbornane ring, and an oxoadamantane ring.

  Among the cation (b2-1) to cation (b2-4), the cation (b2-1) is preferable.

Examples of the cation (b2-1) include the following cations.

Examples of the cation (b2-2) include the following cations.

Examples of the cation (b2-3) include the following cations.

  The salt (I) is a combination of the above-described sulfonate anion and organic cation. These anions and cations can be arbitrarily combined. Specific examples of the salt (I) are shown in Tables 1 and 2.

As salt (I), the salt of Table 1 is mentioned, for example. In Table 1, salt (I-1) is a salt shown below.

  Among them, salt (I-1), salt (I-2), salt (I-11), salt (I-12), salt (I-21), salt (I-22), salt (I-31) ), Salt (I-32), salt (I-41), salt (I-42), salt (I-51), salt (I-52), salt (I-61) and salt (I-62) Is preferred.

（式中、全ての符号は、それぞれ前記と同じ意味を表す。）
この反応の塩基触媒としては、トリエチルアミン等が挙げられる。この反応の溶媒としては、クロロホルム、テトラヒドロフラン等が挙げられる。
式（Ｉ−ｂ）で表される化合物としては、例えば、下記式で表される塩等が挙げられ、市場より容易に入手することができる。下記式で表される塩は、塩酸塩として、入手することも出来る。

The salt represented by the formula (I) is obtained by, for example, reacting a salt represented by the formula (Ia) with a compound represented by the formula (Ib) in a solvent under a base catalyst. Can be manufactured.

(In the formula, all symbols have the same meaning as described above.)
Examples of the base catalyst for this reaction include triethylamine. Examples of the solvent for this reaction include chloroform and tetrahydrofuran.
Examples of the compound represented by the formula (Ib) include salts represented by the following formula, and can be easily obtained from the market. The salt represented by the following formula can also be obtained as a hydrochloride.

（式中、全ての符号は、それぞれ前記と同じ意味を表す。）
この反応の塩基触媒としては、トリエチルアミン等が挙げられる。この反応の溶媒としては、クロロホルム、テトラヒドロフラン等が挙げられる。
式（Ｉ−ｃ）で表される化合物は、例えば、下記式で表される塩等が挙げられ、例えば、特開２００６−２５７０７８号公報、特開２０１１−１１６７４７号公報に記載された方法で製造することができる。

塩（Ｉ）は、２種以上を用いてもよい。 The compound represented by the formula (Ia) is obtained by reacting the compound represented by the formula (Ic) and the compound represented by the formula (Id) in a solvent under a base catalyst. Can be obtained.

(In the formula, all symbols have the same meaning as described above.)
Examples of the base catalyst for this reaction include triethylamine. Examples of the solvent for this reaction include chloroform and tetrahydrofuran.
Examples of the compound represented by the formula (Ic) include salts represented by the following formulas, and the like, for example, by the methods described in JP-A-2006-257078 and JP-A-2011-116747. Can be manufactured.

Two or more salts (I) may be used.

<Resist composition>
The resist composition of the present invention includes a salt (I) and a resin having an acid labile group (hereinafter sometimes referred to as “resin (A)”), and further, a known acid generator (hereinafter referred to as “acid generator ( B) "may be included. The resist composition preferably further contains a quencher (hereinafter sometimes referred to as “quencher (C)”) and / or a solvent (hereinafter sometimes referred to as “solvent (D)”).

<Resin (A)>
The resin of the present invention (hereinafter sometimes referred to as “resin (A)”) includes a structural unit having an acid labile group (hereinafter sometimes referred to as “structural unit (a1)”). Further, the resin (A) may contain a structural unit having no acid labile group (hereinafter sometimes referred to as “structural unit (s)”).
The acid labile group as used herein refers to a group having a leaving group, which is removed by contact with an acid and the structural unit is converted into a hydrophilic group (for example, a hydroxy group or a carboxy group). means.

<Structural unit (a1)>
The structural unit (a1) is derived from a monomer having an acid labile group (hereinafter sometimes referred to as “monomer (a1)”).
The acid labile group in the resin (A) is preferably a group represented by the formula (IA) and a group represented by the formula (2A).

  The monomer (a1) is preferably a monomer having an acid labile group and an ethylenically unsaturated bond, more preferably a (meth) acrylic monomer having an acid labile group.

  Among the (meth) acrylic monomers having an acid labile group, those having an alicyclic hydrocarbon group having 5 to 20 carbon atoms are preferable. If the resin (A) having a structural unit derived from the monomer (a1) having a bulky structure such as an alicyclic hydrocarbon group is used in the resist composition, the resolution of the resist pattern can be improved.

  As a structural unit derived from a (meth) acrylic monomer having a group represented by the formula (1A), a structural unit represented by the formula (a1-0) is preferably represented by the formula (a1-1). And a structural unit represented by the structural unit and formula (a1-2). These may be used alone or in combination of two or more. In this specification, the structural unit represented by formula (a1-0), the structural unit represented by formula (a1-1), and the structural unit represented by formula (a1-2) are each represented by structural unit (a1). -0), structural unit (a1-1), and structural unit (a1-2) in some cases, a monomer for deriving structural unit (a1-0), a monomer for deriving structural unit (a1-1), and a structural unit The monomer for deriving (a1-2) may be referred to as monomer (a1-0), monomer (a1-1), and monomer (a1-2), respectively.

［式（ａ１−０）中、
Ｌ^a01は、酸素原子又は＊−Ｏ−（ＣＨ₂）_k01−ＣＯ−Ｏ−を表し、ｋ０１は１〜７の整数を表し、＊はカルボニル基との結合手を表す。
Ｒ^a01は、それぞれ独立に、水素原子又はメチル基を表す。
Ｒ^a02、Ｒ^a03及びＲ^a04は、それぞれ独立に、炭素数１〜８のアルキル基、炭素数３〜１８の脂環式炭化水素基又はこれらを組合わせた基を表す。］

[In the formula (a1-0),
L ^a01 represents an oxygen atom or * —O— (CH ₂ ) _k01 —CO—O—, k01 represents an integer of 1 to 7, and * represents a bond to a carbonyl group.
R ^a01 independently represents a hydrogen atom or a methyl group.
R ^a02 , R ^a03 and R ^a04 each independently ^represent an alkyl group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 18 carbon atoms, or a group obtained by combining these. ]

L ^a01 is preferably an oxygen atom. k01 is preferably an integer of 1 to 4, more preferably 1.
Examples of the alkyl group of R ^a02 , R ^a03, and R ^a04 , the alicyclic hydrocarbon group, and the group obtained by combining these include the same groups as those described for R ^{a1 to} R ^a3 in formula (1).
The alkyl group of R ^a02 , R ^a03 and R ^a04 is preferably an alkyl group having 6 or less carbon atoms.
The alicyclic hydrocarbon group of R ^a02 , R ^a03 and R ^a04 is preferably an alicyclic hydrocarbon group having 10 or less carbon atoms, and more preferably an alicyclic hydrocarbon group having 6 or less carbon atoms.
The group combining the alkyl group and the alicyclic hydrocarbon group preferably has a total carbon number of 18 or less, combining the alkyl group and the alicyclic hydrocarbon group. Examples of such a group include a methylcyclohexyl group, a dimethylcyclohexyl group, and a methylnorbornyl group.
R ^a02 , R ^a03 and R ^a04 each independently ^represent an alkyl group having 1 to 8 carbon atoms, or two of R ^a02 , R ^a03 and R ^a04 each independently ^represent a carbon number It is preferable that it is a 1-8 alkyl group, and the remaining one is a C3-C18 alicyclic hydrocarbon group.
R ^a02 , R ^a03 and R ^a04 are each independently an alkyl group having 1 to 6 carbon atoms, or two of R ^a02 , R ^a03 and R ^a04 are each independently It is more preferable that it is a 1-6 alkyl group, and the remaining one is a C5-C12 alicyclic hydrocarbon group.
R ^a02 , R ^a03 and R ^a04 are each independently a methyl group, an ethyl group or a propyl group, or two of R ^a02 , R ^a03 and R ^a04 are each independently a methyl group More preferably, they are an ethyl group or a propyl group, and the remaining one is a cyclohexyl group or an adamantyl group.

As the monomer (a1-0), the monomer represented by the formula (a1-0-1) to the formula (a1-0-12) and the formula (a1-0-1) to the formula (a1-0-12) Monomers in which the methacryloyl group is replaced by an acryloyl group are exemplified, and monomers represented by the formulas (a1-0-1) to (a1-0-10) are preferable.

  When the resin (A) contains the structural unit (a1-0), the content is preferably 1 to 70 mol%, more preferably 3 to 65 mol, based on all the structural units of the resin (A). %.

［式（ａ１−１）及び式（ａ１−２）中、
Ｌ^a1及びＬ^a2は、それぞれ独立に、−Ｏ−又は^＊−Ｏ−（ＣＨ₂）_k1−ＣＯ−Ｏ−を表し、ｋ１は１〜７の整数を表し、＊は−ＣＯ−との結合手を表す。
Ｒ^a4及びＲ^a5は、それぞれ独立に、水素原子又はメチル基を表す。
Ｒ^a6及びＲ^a7は、それぞれ独立に、炭素数１〜８のアルキル基、炭素数３〜１８の脂環式炭化水素基又はこれらを組合わせた基を表す。
ｍ１は０〜１４の整数を表す。
ｎ１は０〜１０の整数を表す。
ｎ１’は０〜３の整数を表す。］

[In Formula (a1-1) and Formula (a1-2),
L ^a1 and L ^a2 each independently represent —O— or ^* —O— (CH ₂ ) _k1 —CO—O—, k1 represents an integer of 1 to 7, and * represents a bond to —CO—. Represents a hand.
R ^a4 and R ^a5 each independently represent a hydrogen atom or a methyl group.
R ^a6 and R ^a7 each independently represent an alkyl group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 18 carbon atoms, or a group obtained by combining these.
m1 represents the integer of 0-14.
n1 represents an integer of 0 to 10.
n1 ′ represents an integer of 0 to 3. ]

L ^a1 and L ^a2 are preferably —O— or ^* —O— (CH ₂ ) _k1 —CO—O—, more preferably —O—. k1 is preferably an integer of 1 to 4, more preferably 1.
R ^a4 and R ^a5 are preferably methyl groups.
Examples of the alkyl group of R ^a6 and R ^a7 , the alicyclic hydrocarbon group, and a group obtained by combining these include the same groups as those described for R ^{11 to} R ¹³ in the formula (1).
The alkyl group for R ^a6 and R ^a7 preferably has 6 or less carbon atoms.
The alicyclic hydrocarbon group of R ^a6 and R ^a7 is preferably an alicyclic hydrocarbon group having 8 or less carbon atoms, more preferably an alicyclic hydrocarbon group having 6 or less carbon atoms.
m1 is preferably an integer of 0 to 3, more preferably 0 or 1.
n1 is preferably an integer of 0 to 3, more preferably 0 or 1.
n1 ′ is preferably 0 or 1.

As a monomer (a1-1), the monomer described in Unexamined-Japanese-Patent No. 2010-204646 is mentioned, for example. Among these, a monomer represented by any one of formula (a1-1-1) to formula (a1-1-8) is preferable, and any one of formula (a1-1-1) to formula (a1-1-4) is preferable. The monomer represented by is more preferable.

Examples of the monomer (a1-2) include 1-methylcyclopentan-1-yl (meth) acrylate, 1-ethylcyclopentan-1-yl (meth) acrylate, and 1-methylcyclohexane-1-yl (meth). Acrylate, 1-ethylcyclohexane-1-yl (meth) acrylate, 1-ethylcycloheptan-1-yl (meth) acrylate, 1-ethylcyclooctane-1-yl (meth) acrylate, 1-isopropylcyclopentane-1 -Il (meth) acrylate and 1-isopropylcyclohexane-1-yl (meth) acrylate. A monomer represented by any one of the formulas (a1-2-1) to (a1-2-12) is preferable, and the formula (a1-2-3), the formula (a1-2-4), the formula (a1- 2-9) and a monomer represented by formula (a1-2-10) are more preferred, and a monomer represented by formula (a1-2-3) and formula (a1-2-9) is more preferred.

  When the resin (A) contains the structural unit (a1-1) and / or the structural unit (a1-2), the total content thereof is usually 10 to 95 mol with respect to all the structural units of the resin (A). %, Preferably 15 to 90 mol%, more preferably 20 to 85 mol%.

式（ａ１−３）中、
Ｒ^a9は、ヒドロキシ基を有していてもよい炭素数１〜３の脂肪族炭化水素基、カルボキシ基、シアノ基、水素原子又は−ＣＯＯＲ^a13を表す。
Ｒ^a13は、炭素数１〜８の脂肪族炭化水素基、炭素数３〜２０の脂環式炭化水素基、又はこれらを組み合わせた基を表し、該脂肪族炭化水素基及び該脂環式炭化水素基に含まれる水素原子は、ヒドロキシ基で置換されていてもよく、該脂肪族炭化水素基及び該脂環式炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基で置き換わっていてもよい。
Ｒ^a10、Ｒ^a11及びＲ^a12は、それぞれ独立に、炭素数１〜８のアルキル基、炭素数３〜２０の脂環式炭化水素基又はこれらを組合わせた基を表すか、Ｒ^a10及びＲ^a11は互いに結合して炭素数２〜２０の２価の炭化水素基を形成する。 Furthermore, examples of the structural unit (a1) having a group represented by the formula (1A) also include a structural unit represented by the formula (a1-3). In this specification, the structural unit represented by the formula (a1-3) may be referred to as the structural unit (a1-3) and the monomer that derives the structural unit (a1-3) may be referred to as a monomer (a1-3). is there.

In formula (a1-3),
R ^a9 represents an aliphatic hydrocarbon group having 1 to 3 carbon atoms which may have a hydroxy group, a carboxy group, a cyano group, a hydrogen atom, or —COOR ^a13 .
R ^a13 represents an aliphatic hydrocarbon group having 1 to 8 carbon atoms, an alicyclic hydrocarbon group having 3 to 20 carbon atoms, or a combination thereof, and the aliphatic hydrocarbon group and the alicyclic carbon group. The hydrogen atom contained in the hydrogen group may be substituted with a hydroxy group, and the methylene group contained in the aliphatic hydrocarbon group and the alicyclic hydrocarbon group may be replaced with an oxygen atom or a carbonyl group. Good.
R ^a10, R ^a11 and R ^a12 are each independently an alkyl group having 1 to 8 carbon atoms, or an alicyclic hydrocarbon group or a group obtained by combining these C3-20, R ^a10 and R ^a11 are bonded to each other to form a divalent hydrocarbon group having 2 to 20 carbon atoms.

Here, examples of —COOR ^a13 in R ^a9 include a group in which a carbonyl group is bonded to an alkoxy group such as a methoxycarbonyl group and an ethoxycarbonyl group.

Examples of the aliphatic hydrocarbon group which may have a hydroxy group of R ^a9 include a methyl group, an ethyl group, a propyl group, a hydroxymethyl group and a 2-hydroxyethyl group.
^Examples of the group ^{consisting of} an aliphatic hydrocarbon group represented by R ^a13 , an alicyclic hydrocarbon group, and an aliphatic hydrocarbon group having 1 to 8 carbon atoms and an alicyclic hydrocarbon group having 3 to 20 carbon atoms include, for example, methyl Group, ethyl group, propyl group, cyclopentyl group, cyclopropyl group, adamantyl group, adamantylmethyl group, 1-adamantyl-1-methylethyl group, 2-oxo-oxolan-3-yl group and 2-oxo-oxolane-4 -An yl group etc. are mentioned.
^{Examples of} R ^{a10 to} R ^a12 include the same groups as R ^{11 to} R ¹³ in formula (1).
As —C (R ^a10 ) (R ^a11 ) (R ^a12 ) when R ^a10 and R ^a11 are bonded to each other to form a divalent hydrocarbon group, the following groups are preferred.

  Specific examples of the monomer (a1-3) include 5-norbornene-2-carboxylic acid-tert-butyl, 5-norbornene-2-carboxylic acid 1-cyclohexyl-1-methylethyl, and 5-norbornene-2-carboxylic acid. Acid 1-methylcyclohexyl, 5-norbornene-2-carboxylic acid 2-methyl-2-adamantyl, 5-norbornene-2-carboxylic acid 2-ethyl-2-adamantyl, 5-norbornene-2-carboxylic acid 1- (4 -Methylcyclohexyl) -1-methylethyl, 5-norbornene-2-carboxylic acid 1- (4-hydroxycyclohexyl) -1-methylethyl, 5-norbornene-2-carboxylic acid 1-methyl-1- (4-oxo (Cyclohexyl) ethyl and 1- (1-adamantyl) -1-methyl 5-norbornene-2-carboxylate Chill, and the like.

  Since the resin (A) containing the structural unit (a1-3) includes a sterically bulky structural unit, the resist composition of the present invention containing such a resin (A) is more expensive. A resist pattern can be obtained with resolution. Further, since a rigid norbornane ring is introduced into the main chain, the resulting resist pattern tends to be excellent in dry etching resistance.

  When the resin (A) contains the structural unit (a1-3), the content thereof is preferably 10 to 95 mol%, more preferably 15 to 90 mol%, based on all the structural units of the resin (A). 20-85 mol% is more preferable.

［式（ａ１−４）中、
Ｒ^a32は、水素原子、ハロゲン原子、又は、ハロゲン原子を有してもよい炭素数１〜６のアルキル基を表す。
Ｒ^a33は、ハロゲン原子、ヒドロキシ基、炭素数１〜６のアルキル基、炭素数１〜６のアルコキシ基、炭素数２〜４のアシル基、炭素数２〜４のアシルオキシ基、アクリロイルオキシ基又はメタクリロイルオキシ基を表す。
ｌａは０〜４の整数を表す。ｌａが２以上である場合、複数のＲ^a33は互いに同一であっても異なってもよい。
Ｒ^a34及びＲ^a35はそれぞれ独立に、水素原子又は炭素数１〜１２の炭化水素基を表し、Ｒ^a36は、炭素数１〜２０の炭化水素基を表すか、Ｒ^a35及びＲ^a36は互いに結合して炭素数２〜２０の２価の炭化水素基を形成し、該炭化水素基及び該２価の炭化水素基に含まれる−ＣＨ_２−は、−Ｏ−又は−Ｓ−で置き換わってもよい。］ As the structural unit (a1) having a group represented by the formula (2A), a structural unit represented by the formula (a1-4) (hereinafter may be referred to as “structural unit (a1-4)”). Can be mentioned.

[In the formula (a1-4),
R ^a32 represents a hydrogen atom, a halogen atom, or an alkyl group having 1 to 6 carbon atoms which may have a halogen atom.
R ^a33 is a halogen atom, a hydroxy group, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an acyl group having 2 to 4 carbon atoms, an acyloxy group having 2 to 4 carbon atoms, an acryloyloxy group, or Represents a methacryloyloxy group.
la represents an integer of 0 to 4. When la is 2 or more, the plurality of R ^a33 may be the same as or different from each other.
R ^a34 and R ^a35 each independently represent a hydrogen atom or a hydrocarbon group having 1 to 12 carbon atoms, R ^a36 may represent a hydrocarbon group having 1 to 20 carbon atoms, R ^a35 and R ^a36 are bonded to each other To form a divalent hydrocarbon group having 2 to 20 carbon atoms, and —CH ₂ — contained in the hydrocarbon group and the divalent hydrocarbon group may be replaced by —O— or —S—. Good. ]

^Examples of the alkyl group for R ^a32 and R ^a33 include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, a pentyl group, and a hexyl group. The alkyl group is preferably an alkyl group having 1 to 4 carbon atoms, more preferably a methyl group or an ethyl group, and further preferably a methyl group.
Examples of the halogen atom for R ^a32 and R ^a33 include a fluorine atom, a chlorine atom and a bromine atom.
The R ^a34 and R ^a35, include the same groups as R ¹⁴ and R ¹⁵ of formula (2).
As R ^a36 , the same group as R ¹⁶ in the formula (2) can be mentioned.

In formula (a1-2), R ^a32 is preferably a hydrogen atom.
R ^a33 is preferably an alkoxy group having 1 to 4 carbon atoms, more preferably a methoxy group or an ethoxy group, and further preferably a methoxy group.
la is preferably 0 or 1, more preferably 0.
R ^a34 is preferably a hydrogen atom.
R ^a35 is preferably a hydrocarbon group having 1 to 12 carbon atoms, more preferably a methyl group or an ethyl group.
The hydrocarbon group for ^Ra36 is preferably an alkyl group having 1 to 18 carbon atoms, an alicyclic hydrocarbon group having 3 to 18 carbon atoms, an aromatic hydrocarbon group having 6 to 18 carbon atoms, or a combination thereof. More preferably, they are a C1-C18 alkyl group, a C3-C18 alicyclic aliphatic hydrocarbon group, or a C7-C18 aralkyl group. The alkyl group and the alicyclic hydrocarbon group are preferably unsubstituted. When the aromatic hydrocarbon group has a substituent, the substituent is preferably an aryloxy group having 6 to 10 carbon atoms.

Examples of the monomer for deriving the structural unit monomer (a1-4) include monomers described in JP2010-204646A. Especially, the monomer respectively represented by Formula (a1-4-1)-Formula (a1-4-7) is preferable, and each is represented by Formula (a1-4-1)-Formula (a1-4-5). Monomers are more preferred.

  When resin (A) has a structural unit (a1-4), the content rate is preferable with respect to all the structural units of resin (A), and 10-95 mol% is preferable, and 15-90 mol% is more preferable. 20 to 85 mol% is more preferable.

式（ａ１−５）中、
Ｒ^a8は、ハロゲン原子を有してもよい炭素数１〜６のアルキル基、水素原子又はハロゲン原子を表す。
Ｚ^ａ１は、単結合又は＊−（ＣＨ₂）_h3−ＣＯ−Ｌ⁵⁴−を表し、ｈ３は１〜４の整数を表し、＊は、Ｌ⁵¹との結合手を表す。
Ｌ⁵¹、Ｌ⁵²、Ｌ⁵³及びＬ⁵⁴は、それぞれ独立に、酸素原子又は硫黄原子を表す。
ｓ１は、１〜３の整数を表す。
ｓ１’は、０〜３の整数を表す。 Examples of the structural unit (a1) include a structural unit represented by the formula (a1-5) (hereinafter may be referred to as “structural unit (a1-5)”).

In formula (a1-5),
R ^a8 represents a C 1-6 alkyl group optionally having a halogen atom, a hydrogen atom, or a halogen atom.
Z ^a1 represents a single bond or * — (CH ₂ ) _h3 —CO—L ⁵⁴ —, h3 represents an integer of 1 to 4, and * represents a bond to L ⁵¹ .
L ⁵¹ , L ⁵² , L ⁵³ and L ⁵⁴ each independently represents an oxygen atom or a sulfur atom.
s1 represents an integer of 1 to 3.
s1 ′ represents an integer of 0 to 3.

Examples of the halogen atom include a fluorine atom and a chlorine atom, and a fluorine atom is preferable. Examples of the alkyl group having 1 to 6 carbon atoms which may have a halogen atom include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a fluoromethyl group and a trifluoromethyl group. Groups.
In formula (a1-5), R ^a8 is preferably a hydrogen atom, a methyl group or a trifluoromethyl group.
L ⁵¹ is preferably an oxygen atom.
One of L ⁵² and L ⁵³ is preferably an oxygen atom, and the other is preferably a sulfur atom.
s1 is preferably 1.
s1 ′ is preferably an integer of 0 to 2.
Z ^a1 is preferably a single bond or * —CH ₂ —CO—O—.

As a monomer which introduce | transduces structural unit (a1-5), the monomer described in Unexamined-Japanese-Patent No. 2010-61117 is mentioned, for example. Among these, monomers represented by formulas (a1-5-1) to (a1-5-4) are preferable, and monomers represented by formula (a1-5-1) or formula (a1-5-2) are preferable. Is more preferable.

  When resin (A) has a structural unit (a1-5), the content rate is preferable 1-50 mol% with respect to all the structural units of resin (A), and 3-45 mol% is more preferable. 5 to 40 mol% is more preferable.

The structural unit (a1) is preferably at least one selected from the group consisting of the structural unit (a1-0), the structural unit (a1-1), the structural unit (a1-2), and the structural unit (a1-5). More preferably, it is at least one selected from the group consisting of the structural unit (a1-1), the structural unit (a1-2) and the structural unit (a1-5), and more preferably the structural unit (a1). -1), structural unit (a1-2), and structural unit (a1-5), at least two selected from the group consisting of structural unit (a1-5), particularly preferably structural unit (a1-1) and structural unit (a1- 2) and / or structural unit (a1-5).
The structural unit (a1) preferably includes the structural unit (a1-1).

<Structural unit without acid labile group>
The structural unit (s) is derived from a monomer having no acid labile group (hereinafter sometimes referred to as “monomer (s)”). The monomer for deriving the structural unit (s) (hereinafter sometimes referred to as “monomer (s)”) is not particularly limited as long as it does not have an acid labile group, and monomers known in the resist field can be used.
As the structural unit (s), a structural unit having a hydroxy group or a lactone ring and having no acid labile group is preferable. A structure having a hydroxy group and having no acid labile group (hereinafter sometimes referred to as “structural unit (a2)”) and / or a lactone ring and having no acid labile group If a resin having a unit (hereinafter sometimes referred to as “structural unit (a3)”) is used in the resist composition of the present invention, the resolution of the resist pattern and the adhesion to the substrate can be improved.

<Structural unit (a2)>
The hydroxy group contained in the structural unit (a2) may be an alcoholic hydroxy group or a phenolic hydroxy group.
When a resist pattern is produced from the resist composition of the present invention, when a high energy beam such as a KrF excimer laser (248 nm), an electron beam or EUV (ultra-ultraviolet light) is used as an exposure light source, the structural unit (a2) It is preferable to use the structural unit (a2) having a phenolic hydroxy group. When an ArF excimer laser (193 nm) or the like is used, the structural unit (a2) having an alcoholic hydroxy group is preferable as the structural unit (a2), and the structural unit (a2-1) is more preferable. As a structural unit (a2), 1 type may be included independently and 2 or more types may be included.

［式（ａ２−０）中、
Ｒ^a30は、水素原子、ハロゲン原子又はハロゲン原子を有してもよい炭素数１〜６のアルキル基を表す。
Ｒ^a31は、ハロゲン原子、ヒドロキシ基、炭素数１〜６のアルキル基、炭素数１〜６のアルコキシ基、炭素数２〜４のアシル基、炭素数２〜４のアシルオキシ基、アクリロイルオキシ基又はメタクリロイルオキシ基を表す。
ｍａは０〜４の整数を表す。ｍａが２以上の整数である場合、複数のＲ^a31は互いに同一であっても異なってもよい。］ Examples of the structural unit (a2) having a phenolic hydroxy group include a structural unit represented by the formula (a2-0) (hereinafter sometimes referred to as “structural unit (a2-0)”).

[In the formula (a2-0),
R ^a30 represents a hydrogen atom, a halogen atom or an alkyl group having 1 to 6 carbon atoms which may have a halogen atom.
R ^a31 is a halogen atom, a hydroxy group, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an acyl group having 2 to 4 carbon atoms, an acyloxy group having 2 to 4 carbon atoms, an acryloyloxy group, or Represents a methacryloyloxy group.
ma represents an integer of 0 to 4. When ma is an integer of 2 or more, the plurality of R ^a31 may be the same as or different from each other. ]

^Examples of the alkyl group having 1 to 6 carbon atoms which may have a halogen atom of R ^{a30 include} the same groups as R ^{31 in} formula (a1-5). Among them, R ^a30 is preferably a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, more preferably a hydrogen atom, a methyl group or an ethyl group, and even more preferably a hydrogen atom or a methyl group.
The alkoxy group of R ^a31 is preferably an alkoxy group having 1 to 4 carbon atoms, more preferably a methoxy group or an ethoxy group, and further preferably a methoxy group.
ma is preferably 0, 1 or 2, more preferably 0 or 1, and particularly preferably 0.

Examples of the monomer that derives the structural unit (a2-0) include monomers described in JP 2010-204634 A.
Among them, the structural unit (a2-0) is represented by formula (a2-0-1), formula (a2-0-2), formula (a2-0-3), and formula (a2-0-4), respectively. What is represented is preferable, and what is represented by a formula (a2-0-1) or a formula (a2-0-2) is more preferable.

  The resin (A) containing the structural unit (a2-0) is subjected to a polymerization reaction using a monomer in which the phenolic hydroxy group of the monomer that derives the structural unit (a2-0) is protected with a protective group, and then deprotected. It can be manufactured by processing. However, when the deprotection treatment is performed, the acid labile group of the structural unit (a1) needs to be not significantly impaired. Examples of such protecting groups include acetyl groups.

  When the resin (A) has the structural unit (a2-0), the content is preferably from 5 to 95 mol%, more preferably from 10 to 80 mol%, based on all the structural units of the resin (A). 15-80 mol% is more preferable.

式（ａ２−１）中、
Ｌ^a3は、−Ｏ−又は^＊−Ｏ−（ＣＨ₂）_k2−ＣＯ−Ｏ−を表し、
ｋ２は１〜７の整数を表す。＊は−ＣＯ−との結合手を表す。
Ｒ^a14は、水素原子又はメチル基を表す。
Ｒ^a15及びＲ^a16は、それぞれ独立に、水素原子、メチル基又はヒドロキシ基を表す。
ｏ１は、０〜１０の整数を表す。 Examples of the structural unit (a2) having an alcoholic hydroxy group include a structural unit represented by the formula (a2-1) (hereinafter sometimes referred to as “structural unit (a2-1)”).

In formula (a2-1),
L ^a3 represents —O— or ^* —O— (CH ₂ ) _k2 —CO—O—,
k2 represents an integer of 1 to 7. * Represents a bond with -CO-.
R ^a14 represents a hydrogen atom or a methyl group.
R ^a15 and R ^a16 each independently represent a hydrogen atom, a methyl group or a hydroxy group.
o1 represents an integer of 0 to 10.

In the formula (a2-1), L ^a3 is preferably, -O -, - O- (CH 2) f1 -CO-O- and is (wherein f1 is an integer from 1 to 4), more preferably Is —O—.
R ^a14 is preferably a methyl group.
R ^a15 is preferably a hydrogen atom.
R ^a16 is preferably a hydrogen atom or a hydroxy group.
o1 is preferably an integer of 0 to 3, more preferably 0 or 1.

Examples of the monomer that derives the structural unit (a2-1) include monomers described in JP 2010-204646 A. A monomer represented by any one of formula (a2-1-1) to formula (a2-1-6) is preferable, and represented by any one of formula (a2-1-1) to formula (a2-1-4). The monomer represented by Formula (a2-1-1) or Formula (a2-1-3) is more preferable.

  When resin (A) contains a structural unit (a2-1) structural unit, the content rate is 1-45 mol% normally with respect to all the structural units of resin (A), Preferably it is 1-40 mol. %, More preferably 1 to 35 mol%, and still more preferably 2 to 20 mol%.

<Structural unit (a3)>
The lactone ring included in the structural unit (a3) may be a monocycle such as a β-propiolactone ring, γ-butyrolactone ring, or δ-valerolactone ring, and may be a monocyclic lactone ring and another ring. A condensed ring may be used. Among these lactone rings, a γ-butyrolactone ring or a bridged ring containing a γ-butyrolactone ring structure is preferable.

  The structural unit (a3) is preferably a structural unit represented by the formula (a3-1), the formula (a3-2), the formula (a3-3), or the formula (a3-4). These 1 type may be contained independently and 2 or more types may be contained.

［式（ａ３−１）中、
Ｌ^a4は、酸素原子又は^＊−Ｏ−（ＣＨ₂）_k3−ＣＯ−Ｏ−（ｋ３は１〜７の整数を表す。）で表される基を表す。＊はカルボニル基との結合手を表す。
Ｒ^a18は、水素原子又はメチル基を表す。
Ｒ^a21は炭素数１〜４の脂肪族炭化水素基を表す。
ｐ１は０〜５の整数を表す。ｐ１が２以上のとき、複数のＲ^a21は互いに同一又は相異なる。
式（ａ３−２）中、
Ｌ^a5は、酸素原子又は^＊−Ｏ−（ＣＨ₂）_k3−ＣＯ−Ｏ−（ｋ３は１〜７の整数を表す。）で表される基を表す。＊はカルボニル基との結合手を表す。
Ｒ^a19は、水素原子又はメチル基を表す。
Ｒ^a22は、カルボキシ基、シアノ基又は炭素数１〜４の脂肪族炭化水素基を表す。
ｑ１は、０〜３の整数を表す。ｑ１が２以上のとき、複数のＲ^a22は互いに同一又は相異なる。
式（ａ３−３）中、
Ｌ^a6は、酸素原子又は^＊−Ｏ−（ＣＨ₂）_k3−ＣＯ−Ｏ−（ｋ３は１〜７の整数を表す。）で表される基を表す。＊はカルボニル基との結合手を表す。
Ｒ^a20は、水素原子又はメチル基を表す。
Ｒ^a23は、カルボキシ基、シアノ基又は炭素数１〜４の脂肪族炭化水素基を表す。
ｒ１は、０〜３の整数を表す。ｒ１が２以上のとき、複数のＲ^a23は互いに同一又は相異なる。
式（ａ３−４）中、
Ｒ^a24は、ハロゲン原子を有してもよい炭素数１〜６のアルキル基、水素原子又はハロゲン原子を表す。
Ｌ^a7は、単結合、^＊−Ｌ^a8−Ｏ−、^＊−Ｌ^a8−ＣＯ−Ｏ−、^＊−Ｌ^a8−ＣＯ−Ｏ−Ｌ^a9−ＣＯ−Ｏ−又は^＊−Ｌ^a8−Ｏ−ＣＯ−Ｌ^a9−Ｏ−を表す。
＊は−Ｏ−との結合手を表す。
Ｌ^a8及びＬ^a9は、互いに独立に、炭素数１〜６のアルカンジイル基を表す。］

[In the formula (a3-1),
L ^a4 represents an oxygen atom or a group represented by ^* —O— (CH ₂ ) _k3 —CO—O— (k3 represents an integer of 1 to 7). * Represents a bond with a carbonyl group.
R ^a18 represents a hydrogen atom or a methyl group.
R ^a21 represents an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
p1 represents an integer of 0 to 5. When p1 is 2 or more, the plurality of R ^a21 are the same or different from each other.
In formula (a3-2),
L ^a5 represents an oxygen atom or a group represented by ^* —O— (CH ₂ ) _k3 —CO—O— (k3 represents an integer of 1 to 7). * Represents a bond with a carbonyl group.
R ^a19 represents a hydrogen atom or a methyl group.
R ^a22 represents a carboxy group, a cyano group, or an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
q1 represents an integer of 0 to 3. When q1 is 2 or more, the plurality of R ^a22 are the same or different from each other.
In formula (a3-3),
L ^a6 represents an oxygen atom or a group represented by ^* —O— (CH ₂ ) _k3 —CO—O— (k3 represents an integer of 1 to 7). * Represents a bond with a carbonyl group.
R ^a20 represents a hydrogen atom or a methyl group.
R ^a23 represents a carboxy group, a cyano group, or an aliphatic hydrocarbon group having 1 to 4 carbon atoms.
r1 represents an integer of 0 to 3. When r1 is 2 or more, the plurality of R ^a23 are the same or different from each other.
In formula (a3-4),
R ^a24 represents an alkyl group having 1 to 6 carbon atoms which may have a halogen atom, a hydrogen atom or a halogen atom.
L ^a7 is a single bond, ^* —L ^a8 —O—, ^* —L ^a8 —CO—O—, ^* —L ^a8 —CO—O—L ^a9 —CO—O— or ^* —L ^a8 —O—CO —L ^a9 —O— is represented.
* Represents a bond with -O-.
L ^a8 and L ^a9 each independently represent an alkanediyl group having 1 to 6 carbon atoms. ]

Examples of the halogen atom for R ^a24 include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
^Examples of the alkyl group for R ^a24 include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, n-pentyl group, and n-hexyl group. , Preferably it is a C1-C4 alkyl group, More preferably, it is a methyl group or an ethyl group.
Examples of the alkyl group having a halogen atom of R ^a24 include trifluoromethyl group, perfluoroethyl group, perfluoropropyl group, perfluoroisopropyl group, perfluorobutyl group, perfluorosec-butyl group, perfluorotert-butyl group, perfluoropentyl group, perfluoro group. A hexyl group, a trichloromethyl group, a tribromomethyl group, a triiodomethyl group, etc. are mentioned.

^Examples of the alkanediyl group represented by L ^a8 and L ^a9 include a methylene group, an ethylene group, a propane-1,3-diyl group, a propane-1,2-diyl group, a butane-1,4-diyl group, and a pentane-1,5. -Diyl group, hexane-1,6-diyl group, butane-1,3-diyl group, 2-methylpropane-1,3-diyl group, 2-methylpropane-1,2-diyl group, pentane-1, 4-diyl group, 2-methylbutane-1,4-diyl group, etc. are mentioned.

In the formula (a3-1) to the formula (a3-3), L ^{a4 to} L ^a6 are each independently preferably an oxygen atom or * —O— (CH ₂ ) in which k3 is an integer of 1 to 4. A group represented by _{k 3} —CO—O—, more preferably an oxygen atom and * —O—CH ₂ —CO—O—, still more preferably an oxygen atom.
R ^{a18 to} R ^a21 are preferably methyl groups.
R ^a22 and R ^a23 are each independently preferably a carboxy group, a cyano group or a methyl group.
p1, q1 and r1 are each independently preferably an integer of 0 to 2, more preferably 0 or 1.

In formula (a3-4),
R ^a24 is preferably a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, more preferably a hydrogen atom, a methyl group or an ethyl group, and still more preferably a hydrogen atom or a methyl group.
L ^a7 is preferably a single bond or ^* -L ^a8 —CO—O—, and more preferably a single bond, —CH ₂ —CO—O— or —C ₂ H ₄ —CO—O—. .

  As monomers for deriving the structural unit (a3), monomers described in JP 2010-204646 A, monomers described in JP 2000-122294 A, monomers described in JP 2012-41274 A are listed. Can be mentioned. As the structural unit (a3), the formula (a3-1-1) to the formula (a3-1-6), the formula (a3-2-1) to the formula (a3-2-4), and the formula (a3-3) 1) to a structural unit represented by any one of the formula (a3-3-4) and the formula (a3-4-1) to the formula (a3-4-6), the formula (a3-1-1), The structural unit represented by any one of the formula (a3-1-2) and the formula (a3-2-3) to the formula (a3-2-4) is more preferable, and the formula (a3-1-1) or the formula ( The structural unit represented by a3-2-3) is more preferable.

In the following structural units, compounds in which the methyl group corresponding to R ^a24 is replaced with a hydrogen atom can also be given as specific examples of the structural unit (a3-4).

When the resin (A2) contains the structural unit (a3), the content is usually 5 to 70 mol%, preferably 10 to 65 mol%, based on all the structural units of the resin (A2). More preferably, it is 10-60 mol%.
Moreover, the content rate of a structural unit (a3-1), a structural unit (a3-2), a structural unit (a3-3), and a structural unit (a3-4) is respectively with respect to all the structural units of resin (A). 5 to 60 mol% is preferable, 5 to 50 mol% is more preferable, and 10 to 50 mol% is more preferable.

<Other structural units (s)>
Examples of the structural unit (s) include a structural unit having a halogen atom in addition to the structural unit (a2) and the structural unit (a3) (hereinafter sometimes referred to as “structural unit (a4)”).

Examples of the structural unit (a4) include those represented below.

  When the resin (A) has a structural unit (a4), the content is preferably 1 to 20 mol%, more preferably 2 to 15 mol%, based on all structural units of the resin (A). More preferably, it is 10 mol%.

<Other structural units (t)>
Examples of the structural unit (t) include the structural unit (a2), the structural unit (a3), and the structural unit (s) having a non-leaving hydrocarbon group in addition to the structural unit (a4) (hereinafter referred to as “structural unit (a5)”). In some cases).

［式（ａ５−１）中、
Ｒ⁵¹は、水素原子又はメチル基を表す。
Ｒ⁵²は、炭素数３〜１８の脂環式炭化水素基を表し、該脂環式炭化水素基に含まれる水素原子は炭素数１〜８の脂肪族炭化水素基又はヒドロキシ基で置換されていてもよい。但し、Ｌ⁵¹との結合位置にある炭素原子に結合する水素原子は、炭素数１〜８の脂肪族炭化水素基で置換されない。
Ｌ⁵¹は、単結合又は炭素数１〜１８の２価の飽和炭化水素基を表し、該飽和炭化水素基に含まれるメチレン基は、酸素原子又はカルボニル基に置き換わっていてもよい。］ <Structural unit (a5)>
Examples of the non-leaving hydrocarbon group that the structural unit (a5) has include a linear, branched, or cyclic hydrocarbon group. Especially, it is preferable that a structural unit (a5) is an alicyclic hydrocarbon group.
Examples of the structural unit (a5) include a structural unit represented by the formula (a5-1).

[In the formula (a5-1),
R ⁵¹ represents a hydrogen atom or a methyl group.
R ⁵² represents an alicyclic hydrocarbon group having 3 to 18 carbon atoms, and a hydrogen atom contained in the alicyclic hydrocarbon group is substituted with an aliphatic hydrocarbon group or hydroxy group having 1 to 8 carbon atoms. May be. However, the hydrogen atom bonded to the carbon atom at the bonding position with L ⁵¹ is not substituted with an aliphatic hydrocarbon group having 1 to 8 carbon atoms.
L ⁵¹ represents a single bond or a divalent saturated hydrocarbon group having 1 to 18 carbon atoms, and the methylene group contained in the saturated hydrocarbon group may be replaced with an oxygen atom or a carbonyl group. ]

The alicyclic hydrocarbon group for R ⁵² may be monocyclic or polycyclic. Examples of the monocyclic alicyclic hydrocarbon group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, and a cyclohexyl group. Examples of the polycyclic alicyclic hydrocarbon group include an adamantyl group and a norbornyl group.
Examples of the aliphatic hydrocarbon group having 1 to 8 carbon atoms include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, pentyl group, hexyl group, Examples thereof include alkyl groups such as octyl group and 2-ethylhexyl group.
Examples of the alicyclic hydrocarbon group having a substituent include a 3-hydroxyadamantyl group and a 3-methyladamantyl group.
R ⁵² is preferably an unsubstituted alicyclic hydrocarbon group having 3 to 18 carbon atoms, and more preferably an adamantyl group, a norbornyl group, or a cyclohexyl group.

Examples of the divalent saturated hydrocarbon group for L ⁵¹ include a divalent aliphatic saturated hydrocarbon group and a divalent alicyclic saturated hydrocarbon group, preferably a divalent aliphatic saturated hydrocarbon group. .
Examples of the divalent aliphatic saturated hydrocarbon group include alkanediyl groups such as a methylene group, an ethylene group, a propanediyl group, a butanediyl group, and a pentanediyl group.
The divalent alicyclic saturated hydrocarbon group may be monocyclic or polycyclic. Examples of the monocyclic alicyclic saturated hydrocarbon group include cycloalkanediyl groups such as cyclopentanediyl group and cyclohexanediyl group. Examples of the polycyclic divalent alicyclic saturated hydrocarbon group include an adamantanediyl group and a norbornanediyl group.

式（Ｌ１−１）中、
Ｘ^x1は、カルボニルオキシ基又はオキシカルボニル基を表す。
Ｌ^x1は、炭素数１〜１６の２価の脂肪族飽和炭化水素基を表す。
Ｌ^x2は、単結合又は炭素数１〜１５の２価の脂肪族飽和炭化水素基を表す。
ただし、Ｌ^x1及びＬ^x2の合計炭素数は、１６以下である。
式（Ｌ１−２）中、
Ｌ^x3は、炭素数１〜１７の２価の脂肪族飽和炭化水素基を表す。
Ｌ^x4は、単結合又は炭素数１〜１６の２価の脂肪族飽和炭化水素基を表す。
ただし、Ｌ^x1及びＬ^x2の合計炭素数は、１７以下である。
式（Ｌ１−３）中、
Ｌ^x5は、炭素数１〜１５の２価の脂肪族飽和炭化水素基を表す。
Ｌ^x6及びＬ^x７は、それぞれ独立に、単結合又は炭素数１〜１４の２価の脂肪族飽和炭化水素基を表す。
ただし、Ｌ^x5、Ｌ^x6及びＬ^x7の合計炭素数は、１５以下である。
式（Ｌ１−４）中、
Ｌ^x8及びＬ^x9は、単結合又は炭素数１〜１２の２価の脂肪族飽和炭化水素基を表す。
Ｗ^x1は、炭素数３〜１５の２価の脂環式飽和炭化水素基を表す。
ただし、Ｌ^x8、Ｌ^x9及びＷ^x1の合計炭素数は、１５以下である。 Examples of the group in which the methylene group contained in the saturated hydrocarbon group is replaced with an oxygen atom or a carbonyl group include groups represented by formulas (L1-1) to (L1-4). In the following formula, * represents a bond with an oxygen atom.

In formula (L1-1),
X ^x1 represents a carbonyloxy group or an oxycarbonyl group.
L ^x1 represents a divalent aliphatic saturated hydrocarbon group having 1 to 16 carbon atoms.
L ^x2 represents a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 15 carbon atoms.
However, the total carbon number of L ^x1 and L ^x2 is 16 or less.
In formula (L1-2),
L ^x3 represents a divalent aliphatic saturated hydrocarbon group having 1 to 17 carbon atoms.
L ^x4 represents a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 16 carbon atoms.
However, the total carbon number of L ^x1 and L ^x2 is 17 or less.
In formula (L1-3),
L ^x5 represents a divalent aliphatic saturated hydrocarbon group having 1 to 15 carbon atoms.
L ^x6 and L ^x7 each independently represent a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 14 carbon atoms.
However, the total carbon number of L ^x5 , L ^x6 and L ^x7 is 15 or less.
In formula (L1-4),
L ^x8 and L ^x9 represent a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 12 carbon atoms.
W ^x1 represents a divalent alicyclic saturated hydrocarbon group having 3 to 15 carbon atoms.
However, the total carbon number of L ^x8 , L ^x9 and W ^x1 is 15 or less.

L ^x1 is preferably a C 1-8 divalent aliphatic saturated hydrocarbon group, more preferably a methylene group or an ethylene group.
L ^x2 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a single bond.
L ^x3 is preferably a C 1-8 divalent aliphatic saturated hydrocarbon group.
L ^x4 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^x5 is preferably a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a methylene group or an ethylene group.
L ^x6 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a methylene group or an ethylene group.
L ^x7 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms.
L ^x8 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a single bond or a methylene group.
L ^x9 is preferably a single bond or a divalent aliphatic saturated hydrocarbon group having 1 to 8 carbon atoms, more preferably a single bond or a methylene group.
W ^x1 is preferably a C 3-10 divalent alicyclic saturated hydrocarbon group, more preferably a cyclohexanediyl group or an adamantanediyl group.

As group represented by a formula (L1-1), the bivalent group shown below is mentioned, for example.

As group represented by a formula (L1-2), the bivalent group shown below is mentioned, for example.

As group represented by a formula (L1-3), the bivalent group shown below is mentioned, for example.

As group represented by a formula (L1-4), the bivalent group shown below is mentioned, for example.

L ⁵¹ is preferably a single bond or a group represented by the formula (L1-1).

Examples of the structural unit (a5-1) include the following.

In the above structural unit, a structural unit in which a methyl group corresponding to R ⁵¹ is replaced with a hydrogen atom can also be given as a specific example of the structural unit (a5-1).

  The resin (A) may have a structural unit other than the above-described structural unit, and examples of the structural unit include structural units well known in the art.

The resin (A) is preferably a resin composed of the structural unit (a1) and the structural unit (s), that is, a copolymer of the monomer (a1) and the monomer (s).
The structural unit (a1) is preferably at least one of the structural unit (a1-1) and the structural unit (a1-2) (preferably the structural unit having a cyclohexyl group or a cyclopentyl group), more preferably the structural unit (a1- 1).
The structural unit (s) is preferably at least one of the structural unit (a2) and the structural unit (a3). The structural unit (a2) is preferably a structural unit represented by the formula (a2-1).
The structural unit (a3) is preferably at least one of a structural unit represented by the formula (a3-1), a structural unit represented by the formula (a3-2), and a structural unit represented by the formula (a3-4). It is.

  The resin (A) may contain a structural unit derived from a monomer having an adamantyl group (particularly the structural unit (a1-1)) in an amount of 15 mol% or more based on the content of the structural unit (a1). preferable. When the content of the structural unit having an adamantyl group is increased, the dry etching resistance of the resist pattern is improved.

Each structural unit constituting the resin (A) may be used alone or in combination of two or more, and is produced by a known polymerization method (for example, radical polymerization method) using a monomer that derives these structural units. can do. The content rate of each structural unit which resin (A) has can be adjusted with the usage-amount of the monomer used for superposition | polymerization.
The weight average molecular weight of the resin (A) is preferably 2,000 or more (more preferably 2,500 or more, more preferably 3,000 or more), 50,000 or less (more preferably 30,000 or less, further preferably 15,000 or less).

<Resin other than resin (A)>
The resist composition of the present invention may contain a resin other than the resin (A). As such a resin, for example, a resin composed only of the structural unit (s) can be mentioned.

As the resin other than the resin (A), a resin containing the structural unit (a4) (however,
The structural unit (a1) is not included. Hereinafter referred to as “resin (X)”. ) Is preferred.
Examples of the structural unit that the resin (X) may further include a structural unit derived from the structural unit (a2), the structural unit (a3), and other known monomers.
The weight average molecular weight of the resin (X) is preferably 8,000 or more (more preferably 10,000 or more) and 80,000 or less (more preferably 60,000 or less). The means for measuring the weight average molecular weight of the resin (X) is the same as that for the resin (A).
When the resist composition of this invention contains resin (X), the content becomes like this. Preferably it is 1-60 mass parts with respect to 100 mass parts of resin (A), More preferably, it is 3-50 mass parts More preferably, it is 5-40 mass parts, Most preferably, it is 7-30 mass parts.

<Acid generator (B)>
A known acid generator can be used as the acid generator (B). The known acid generator may be an ionic acid generator or a nonionic generator, but an ionic acid generator is preferred.
Examples of the acid generator (B) include organic sulfonium salts of organic sulfonic acids. For example, acid generators described in JP2013-68914A, JP2013-3155A, and JP2013-11905A1. Etc. Specifically, salts represented by formula (B1-1) to formula (B1-28) can be given. Among them, those containing an arylsulfonium cation are preferable. Formula (B1-1), Formula (B1-2), Formula (B1-3), Formula (B1-6), Formula (B1-7), Formula (B1-11) ), Formula (B1-12), formula (B1-13), formula (B1-14), formula (B1-20), formula (B1-21), formula (B1-22), formula (B1-23) , A salt represented by any one of formula (B1-24), formula (B1-25) and formula (B1-26) is more preferable.

  Two or more acid generators (B) may be used.

In the resist composition, the salt (I) is usually 1 to 30 parts by weight, preferably 2 to 20 parts by weight, more preferably 2 to 10 parts by weight with respect to 100 parts by weight of the resin (A). is there. In the resist composition, the salt (I) may act as an acid generator.
When a resist composition contains an acid generator (B), an acid generator (B) is 1-30 weight part normally with respect to 100 weight part of resin (A), Preferably it is 2-20. Parts by weight, more preferably 3 to 10 parts by weight.
When the resist composition contains the acid generator (B), the content ratio (mass) of the salt (I) and the acid generator (B) is usually 1:99 to 99: 1, preferably Is from 5:95 to 95: 5, more preferably from 10:90 to 90:10.

  In the resist composition of the present invention, the total solid content of the resist composition is such that the content of the resin [total of resin (A) and resin other than resin (A)] in the resist composition of the present invention is the resist 80 mass% or more and 99 mass% or less are preferable with respect to solid content of a composition. In the present specification, the “solid content of the resist composition” means the total of components excluding the solvent (E) described later from the total amount of the resist composition of the present invention. The solid content of the resist composition and the resin content relative thereto can be measured by a known analysis means such as liquid chromatography or gas chromatography.

<Solvent (E)>
The content of the solvent (E) is usually 90% by mass or more, preferably 92% by mass or more, more preferably 94% by mass or more, and usually 99.9% by mass or less, preferably 99% by mass or less in the resist composition. It is. The content rate of a solvent (E) can be measured by well-known analysis means, such as a liquid chromatography or a gas chromatography.

  Examples of the solvent (E) include glycol ether esters such as ethyl cellosolve acetate, methyl cellosolve acetate and propylene glycol monomethyl ether acetate; glycol ethers such as propylene glycol monomethyl ether; ethyl lactate, butyl acetate, amyl acetate and ethyl pyruvate Esters; ketones such as acetone, methyl isobutyl ketone, 2-heptanone and cyclohexanone; cyclic esters such as γ-butyrolactone; A solvent (E) may contain 1 type independently, and may contain 2 or more types.

<Quencher (C)>
Examples of the quencher (C) include a salt of a weaker acid than a basic nitrogen-containing organic compound or an acid generator (B). Examples of the basic nitrogen-containing organic compound include amines and ammonium salts. Examples of amines include aliphatic amines and aromatic amines. Aliphatic amines include primary amines, secondary amines and tertiary amines.

  As the quencher (C), 1-naphthylamine, 2-naphthylamine, aniline, diisopropylaniline, 2-, 3- or 4-methylaniline, 4-nitroaniline, N-methylaniline, N, N-dimethylaniline, diphenylamine , Hexylamine, heptylamine, octylamine, nonylamine, decylamine, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, triethylamine, trimethylamine, tripropylamine, tributylamine, tripentylamine, tri Hexylamine, triheptylamine, trioctylamine, trinonylamine, tridecylamine, methyldibutylamine, methyldipentylamine, methyldihexyl Amine, methyldicyclohexylamine, methyldiheptylamine, methyldioctylamine, methyldinonylamine, methyldidecylamine, ethyldibutylamine, ethyldipentylamine, ethyldihexylamine, ethyldiheptylamine, ethyldioctylamine, ethyldinonylamine Ethyldidecylamine, dicyclohexylmethylamine, tris [2- (2-methoxyethoxy) ethyl] amine, triisopropanolamine, ethylenediamine, tetramethylenediamine, hexamethylenediamine, 4,4′-diamino-1,2-diphenyl Ethane, 4,4′-diamino-3,3′-dimethyldiphenylmethane, 4,4′-diamino-3,3′-diethyldiphenylmethane, 2,2′-methylenebisaniline, imida , 4-methylimidazole, pyridine, 4-methylpyridine, 1,2-di (2-pyridyl) ethane, 1,2-di (4-pyridyl) ethane, 1,2-di (2-pyridyl) ethene 1,2-di (4-pyridyl) ethene, 1,3-di (4-pyridyl) propane, 1,2-di (4-pyridyloxy) ethane, di (2-pyridyl) ketone, 4,4 ′ -Dipyridyl sulfide, 4,4'-dipyridyl disulfide, 2,2'-dipyridylamine, 2,2'-dipycolylamine, bipyridine and the like, preferably diisopropylaniline, particularly preferably 2,6- Diisopropylaniline is mentioned.

  As ammonium salts, tetramethylammonium hydroxide, tetraisopropylammonium hydroxide, tetrabutylammonium hydroxide, tetrahexylammonium hydroxide, tetraoctylammonium hydroxide, phenyltrimethylammonium hydroxide, 3- (trifluoromethyl) phenyltrimethyl Ammonium hydroxide, tetra-n-butylammonium salicylate, choline and the like can be mentioned.

The acidity in a salt having a weaker acidity than the acid generated from the acid generator (B) is represented by an acid dissociation constant (pKa). The salt having a lower acidity than the acid generated from the salt (a) and the acid generator (B) is a salt in which the acid dissociation constant of the acid generated from the salt is usually −3 <pKa, preferably −1. <PKa <7 salt, more preferably 0 <pKa <5 salt. Examples of the salt having a lower acidity than the acid generated from the acid generator (B) include a salt represented by the following formula, a weak acid inner salt represented by the formula (D), and JP 2012-229206 A: Examples thereof include salts described in JP 2012-6908 A, JP 2012-72109 A, JP 2011-39502 A, and JP 2011-191745 A. Preferably, it is a weak acid salt represented by the formula (D).

［式（Ｄ）中、
Ｒ^Ｄ１及びＲ^Ｄ２は、それぞれ独立に、炭素数１〜１２の１価の炭化水素基、炭素数１〜６のアルコキシ基、炭素数２〜７のアシル基、炭素数２〜７のアシルオキシ基、炭素数２〜７のアルコキシカルボニル基、ニトロ基又はハロゲン原子を表す。
ｍ’及びｎ’は、それぞれ独立に、０〜４の整数を表し、ｍ’が２以上の場合、複数のＲ^Ｄ１は同一又は相異なり、ｎ’が２以上の場合、複数のＲ^Ｄ２は同一又は相異なる。］ <Weak acid inner salt (D)>
The weak acid inner salt (D) is a compound represented by the formula (D).

[In the formula (D),
R ^D1 and R ^D2 are each independently a monovalent hydrocarbon group having 1 to 12 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, an acyl group having 2 to 7 carbon atoms, or an acyloxy group having 2 to 7 carbon atoms. Represents an alkoxycarbonyl group having 2 to 7 carbon atoms, a nitro group, or a halogen atom.
m ′ and n ′ each independently represents an integer of 0 to 4, and when m ′ is 2 or more, the plurality of R ^D1 are the same or different, and when n ′ is 2 or more, the plurality of R ^D2 are Same or different. ]

In the compound represented by the formula (D), the hydrocarbon groups of R ^D1 and R ^D2 are a monovalent aliphatic hydrocarbon group, a monovalent alicyclic hydrocarbon group, and a monovalent aromatic hydrocarbon. And groups formed by combining these groups.
Examples of the monovalent aliphatic hydrocarbon group include alkyl groups such as methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, t-butyl group, pentyl group, hexyl group, and nonyl group.
The monovalent alicyclic hydrocarbon group may be monocyclic or polycyclic, and may be either saturated or unsaturated. Examples thereof include cycloalkyl groups such as cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, cyclononyl group, and cyclododecyl group, norbornyl group, adamantyl group, and the like.
Examples of the monovalent aromatic hydrocarbon group include phenyl group, 1-naphthyl group, 2-naphthyl group, 2-methylphenyl group, 3-methylphenyl group, 4-methylphenyl group, 4-ethylphenyl group, 4- Propylphenyl group, 4-isopropylphenyl group, 4-butylphenyl group, 4-t-butylphenyl group, 4-hexylphenyl group, 4-cyclohexylphenyl group, anthryl group, p-adamantylphenyl group, tolyl group, xylyl group , Aryl groups such as cumenyl group, mesityl group, biphenyl group, phenanthryl group, 2,6-diethylphenyl group, 2-methyl-6-ethylphenyl, and the like.
Examples of the group formed by combining these include an alkyl-cycloalkyl group, a cycloalkyl-alkyl group, an aralkyl group (for example, phenylmethyl group, 1-phenylethyl group, 2-phenylethyl group, 1-phenyl-1 -Propyl group, 1-phenyl-2-propyl group, 2-phenyl-2-propyl group, 3-phenyl-1-propyl group, 4-phenyl-1-butyl group, 5-phenyl-1-pentyl group, 6 -Phenyl-1-hexyl group, etc.).

Examples of the alkoxy group include a methoxy group and an ethoxy group.
Examples of the acyl group include an acetyl group, a propanoyl group, a benzoyl group, and a cyclohexanecarbonyl group.
Examples of the acyloxy group include a group in which an oxy group (—O—) is bonded to the acyl group.
Examples of the alkoxycarbonyl group include a group in which a carbonyl group (—CO—) is bonded to the above alkoxy group.
Examples of the halogen atom include a fluorine atom, a chlorine atom, and a bromine atom.

In the formula (D), R ^D1 and R ^D2 are each independently an alkyl group having 1 to 8 carbon atoms, a cycloalkyl group having 3 to 10 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or 2 to 2 carbon atoms. Preferred are an acyl group having 4 carbon atoms, an acyloxy group having 2 to 4 carbon atoms, an alkoxycarbonyl group having 2 to 4 carbon atoms, a nitro group, or a halogen atom.
m ′ and n ′ are each independently preferably an integer of 0 to 2, and more preferably 0. When m ′ is 2 or more, the plurality of R ^D1 are the same or different, and when n ′ is 2 or more, the plurality of R ^D2 are the same or different.

Examples of the compound (D) include the following compounds.

  Compound (D) can be produced by the method described in “Tetrahedron Vol. 45, No. 19, p6281-6296”. Moreover, the compound (D) can use the compound marketed.

  The content of the quencher (C) is preferably 0.01 to 5% by mass, more preferably 0.01 to 3% by mass, and particularly preferably 0.01 to 1% in the solid content of the resist composition. % By mass.

<Other ingredients>
The resist composition of the present invention may contain components other than the above components (hereinafter sometimes referred to as “other components (F)”) as necessary. The other component (F) is not particularly limited, and additives known in the resist field, such as sensitizers, dissolution inhibitors, surfactants, stabilizers, dyes, and the like can be used.

<Preparation of resist composition>
The resist composition of the present invention comprises a resin (A), an acid generator of the present invention, and a resin other than the resin (A) used as necessary, a solvent (E), a quencher (C) and other components. It can be prepared by mixing (F). The mixing order is arbitrary and is not particularly limited. The temperature at the time of mixing can select an appropriate temperature from 10-40 degreeC according to the kind etc. of resin etc., the solubility with respect to solvents (E), such as resin. An appropriate mixing time can be selected from 0.5 to 24 hours depending on the mixing temperature. The mixing means is not particularly limited, and stirring and mixing can be used.
After mixing each component, it is preferable to filter using a filter having a pore size of about 0.003 to 0.2 μm.

<Method for producing resist pattern>
The method for producing a resist pattern of the present invention comprises:
(1) The process of apply | coating the resist composition of this invention on a board | substrate,
(2) The process of drying the composition after application | coating and forming a composition layer,
(3) a step of exposing the composition layer;
(4) a step of heating the composition layer after exposure, and (5) a step of developing the composition layer after heating.

  The resist composition can be applied onto the substrate by a commonly used apparatus such as a spin coater. Examples of the substrate include an inorganic substrate such as a silicon wafer. Before applying the resist composition, the substrate may be washed, or an antireflection film or the like may be formed on the substrate.

By drying the composition after coating, the solvent is removed and a composition layer is formed. Drying is performed, for example, by evaporating the solvent using a heating device such as a hot plate (so-called pre-baking), or using a decompression device. The heating temperature is preferably 50 to 200 ° C., for example, and the heating time is preferably 10 to 180 seconds, for example. The pressure during drying under reduced pressure is preferably about 1 to 1.0 × 10 ⁵ Pa.

The obtained composition layer is usually exposed using an exposure machine. The exposure machine may be an immersion exposure machine. Exposure light sources include those that emit laser light in the ultraviolet region such as KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), F ₂ excimer laser (wavelength 157 nm), solid-state laser light source (YAG or semiconductor laser) Etc.) Using various lasers such as those that convert wavelength of laser light from the laser and emit harmonic laser light in the far-ultraviolet region or vacuum ultraviolet region, those that irradiate electron beams or extreme ultraviolet light (EUV), etc. Can do. In this specification, the irradiation of these radiations may be collectively referred to as “exposure”. At the time of exposure, exposure is usually performed through a mask corresponding to a required pattern. When the exposure light source is an electron beam, exposure may be performed by direct drawing without using a mask.

  The composition layer after exposure is subjected to heat treatment (so-called post-exposure baking) in order to promote the deprotection reaction in the acid labile group. The heating temperature is usually about 50 to 200 ° C, preferably about 70 to 150 ° C.

  The heated composition layer is usually developed using a developer using a developing device. Examples of the developing method include a dipping method, a paddle method, a spray method, and a dynamic dispensing method. The development temperature is preferably 5 to 60 ° C., for example, and the development time is preferably 5 to 300 seconds, for example. A positive resist pattern or a negative resist pattern can be produced by selecting the type of developer as follows.

When producing a positive resist pattern from the resist composition of the present invention, an alkaline developer is used as the developer. The alkaline developer may be various alkaline aqueous solutions used in this field. Examples thereof include an aqueous solution of tetramethylammonium hydroxide and (2-hydroxyethyl) trimethylammonium hydroxide (commonly called choline).
The alkali developer may contain a surfactant.
It is preferable to wash the resist pattern with ultrapure water after development, and then remove the water remaining on the substrate and the pattern.

In the case of producing a negative resist pattern from the resist composition of the present invention, a developer containing an organic solvent as a developer (hereinafter sometimes referred to as “organic developer”) is used.
Organic solvents contained in the organic developer include ketone solvents such as 2-hexanone and 2-heptanone; glycol ether ester solvents such as propylene glycol monomethyl ether acetate; ester solvents such as butyl acetate; glycols such as propylene glycol monomethyl ether Examples include ether solvents; amide solvents such as N, N-dimethylacetamide; aromatic hydrocarbon solvents such as anisole.
In the organic developer, the content of the organic solvent is preferably 90% by mass or more and 100% by mass or less, more preferably 95% by mass or more and 100% by mass or less, and still more preferably only the organic solvent.
Among them, the organic developer is preferably a developer containing butyl acetate and / or 2-heptanone. In the organic developer, the total content of butyl acetate and 2-heptanone is preferably 50% by mass to 100% by mass, more preferably 90% by mass to 100% by mass, and substantially butyl acetate and / or 2 -More preferred is heptanone alone.
The organic developer may contain a surfactant. The organic developer may contain a trace amount of water.
At the time of development, the development may be stopped by substituting a solvent of a different type from the organic developer.

It is preferable to wash the developed resist pattern with a rinse solution. The rinsing liquid is not particularly limited as long as it does not dissolve the resist pattern, and a solution containing a general organic solvent can be used, and an alcohol solvent or an ester solvent is preferable.
After the cleaning, it is preferable to remove the rinse solution remaining on the substrate and the pattern.

<Application>
The resist composition of the present invention includes a resist composition for KrF excimer laser exposure, a resist composition for ArF excimer laser exposure, a resist composition for electron beam (EB) exposure, or a resist composition for EUV exposure, particularly an electron. It is suitable as a resist composition for line (EB) exposure or a resist composition for EUV exposure, and is useful for fine processing of semiconductors.

The present invention will be described more specifically with reference to examples. In the examples, “%” and “parts” representing the content or amount used are based on mass unless otherwise specified.
The weight average molecular weight is a value determined by gel permeation chromatography under the following conditions.
Apparatus: HLC-8120GPC type (manufactured by Tosoh Corporation)
Column: TSKgel Multipore H _XL -M x 3 + guardcolumn (manufactured by Tosoh Corporation)
Eluent: Tetrahydrofuran Flow rate: 1.0 mL / min
Detector: RI detector Column temperature: 40 ° C
Injection volume: 100 μl
Molecular weight standard: Standard polystyrene (manufactured by Tosoh Corporation)

  The structure of the compound was confirmed by measuring molecular peaks using mass spectrometry (LC: Agilent model 1100, MASS: Agilent LC / MSD model). In the following examples, the value of this molecular peak is indicated by “MASS”.

式（Ｉ−１−ａ）で表される塩３．００部及びクロロホルム１５部を添加し、２３℃で３０分間攪拌した。得られた混合溶液に、トリエチルアミン１．４４部を添加後、５℃まで冷却し、式（Ｉ−１−ｂ）で表される化合物２．４７部及びクロロホルム２．４７部の混合溶液を滴下し、さらに、５℃で１時間攪拌することにより、式（Ｉ−１−ｃ）で表される塩を含む溶液を得た。
得られた式（Ｉ−１−ｃ）で表される塩を含む溶液に、式（Ｉ−１−ｄ）で表される化合物１５部を添加し、さらに、５０℃で４時間攪拌することにより、式（Ｉ−１−ｅ）で表される塩３．３０部を含む溶液を得た。

得られた式（Ｉ−１−ｅ）で表される塩３．３０部を含む溶液に、式（Ｉ−１−ｆ）で表される塩２．０３部、クロロホルム３０部及びイオン交換水１１．０７部を添加し、２３℃で１時間攪拌した後、分液し有機層を回収した。回収された有機層にクロロホルム３０部及びイオン交換水２０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。さらに、回収された有機層に、イオン交換水２０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。この水洗操作を５回繰り返した。回収された有機層に、活性炭１．００部を添加攪拌し、ろ過した。回収されたろ液を濃縮し、得られた残渣に、アセトニトリル１０部を添加攪拌し、濃縮した。得られた残渣に、酢酸エチル３０部を加えて２３℃で３０分間攪拌し、上澄み液を除去し、濃縮した。得られた残渣に、アセトニトリル１０部を加えて攪拌した後、濃縮することにより、式（Ｉ−１）で表される塩１．８２部を得た。 Example 1: Synthesis of a salt represented by the formula (I-1)

3.00 parts of the salt represented by the formula (I-1-a) and 15 parts of chloroform were added, and the mixture was stirred at 23 ° C. for 30 minutes. After adding 1.44 parts of triethylamine to the obtained mixed solution, the mixture was cooled to 5 ° C., and a mixed solution of 2.47 parts of the compound represented by the formula (I-1-b) and 2.47 parts of chloroform was added dropwise. Furthermore, the solution containing the salt represented by the formula (I-1-c) was obtained by stirring at 5 ° C. for 1 hour.
To the obtained solution containing the salt represented by the formula (I-1-c), 15 parts of the compound represented by the formula (I-1-d) is added and further stirred at 50 ° C. for 4 hours. To obtain a solution containing 3.30 parts of the salt represented by the formula (I-1-e).

In a solution containing 3.30 parts of the salt represented by the formula (I-1-e) thus obtained, 2.03 parts of the salt represented by the formula (I-1-f), 30 parts of chloroform and ion-exchanged water. After adding 11.07 parts and stirring at 23 degreeC for 1 hour, it liquid-separated and collect | recovered organic layers. To the recovered organic layer, 30 parts of chloroform and 20 parts of ion-exchanged water were added and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. Furthermore, 20 parts of ion-exchanged water was added to the collected organic layer and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 5 times. To the collected organic layer, 1.00 part of activated carbon was added and stirred, and filtered. The collected filtrate was concentrated, and 10 parts of acetonitrile was added to the resulting residue, stirred and concentrated. To the obtained residue, 30 parts of ethyl acetate was added and stirred at 23 ° C. for 30 minutes, and the supernatant was removed and concentrated. To the obtained residue, 10 parts of acetonitrile was added and stirred, and then concentrated to obtain 1.82 parts of the salt represented by the formula (I-1).

MASS (ESI (+) Spectrum): M ⁺ 263.1
MASS (ESI (−) Spectrum): M ^- 383.1

式（Ｉ−１−ａ）で表される塩２．９９部及びクロロホルム１５部を添加し、２３℃で３０分間攪拌した。得られた混合溶液に、トリエチルアミン１．３７部を添加後、５℃まで冷却し、式（Ｉ−１−ｂ）で表される化合物１．８５部及びクロロホルム３．７０部の混合溶液を滴下し、さらに、２３℃で３０分間攪拌することにより、式（Ｉ−１−ｃ）で表される塩を含む溶液を得た。
得られた式（Ｉ−１−ｃ）で表される塩を含む溶液に、式（Ｉ−８−ｄ）で表される化合物１５部及びトリエチルアミン１．３７部を添加し、さらに、５０℃で３８時間攪拌することにより、式（Ｉ−８−ｅ）で表される塩３．５８部を含む溶液を得た。

得られた式（Ｉ−８−ｅ）で表される塩３．５８部を含む溶液に、式（Ｉ−８−ｆ）で表される塩２．０２部、クロロホルム３０部及びイオン交換水１０部を添加し、２３℃で３時間攪拌した後、分液し有機層を回収した。回収された有機層にクロロホルム３０部及びイオン交換水２０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。さらに、回収された有機層に、イオン交換水２０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。この水洗操作を５回繰り返した。回収されたろ液を濃縮し、得られた残渣に、アセトニトリル１．９部及び酢酸エチル４１．２部を加えて２３℃で３０分間攪拌し、上澄み液を除去し、濃縮した。得られた残渣に、アセトニトリル１０部を加えて攪拌した後、濃縮することにより、式（Ｉ−８）で表される塩２．４６部を得た。 Example 2: Synthesis of a salt represented by the formula (I-8)

2.99 parts of the salt represented by the formula (I-1-a) and 15 parts of chloroform were added and stirred at 23 ° C. for 30 minutes. To the obtained mixed solution, 1.37 parts of triethylamine was added and then cooled to 5 ° C., and a mixed solution of 1.85 parts of the compound represented by the formula (I-1-b) and 3.70 parts of chloroform was dropped. Furthermore, the solution containing the salt represented by the formula (I-1-c) was obtained by stirring at 23 ° C. for 30 minutes.
To the obtained solution containing the salt represented by the formula (I-1-c), 15 parts of a compound represented by the formula (I-8-d) and 1.37 parts of triethylamine are added, and further, 50 ° C. Was stirred for 38 hours to obtain a solution containing 3.58 parts of the salt represented by the formula (I-8-e).

In a solution containing 3.58 parts of the salt represented by the formula (I-8-e) thus obtained, 2.02 parts of the salt represented by the formula (I-8-f), 30 parts of chloroform and ion-exchanged water. After adding 10 parts and stirring at 23 degreeC for 3 hours, it liquid-separated and collect | recovered organic layers. To the recovered organic layer, 30 parts of chloroform and 20 parts of ion-exchanged water were added and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. Furthermore, 20 parts of ion-exchanged water was added to the collected organic layer and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 5 times. The collected filtrate was concentrated, and 1.9 parts of acetonitrile and 41.2 parts of ethyl acetate were added to the resulting residue, followed by stirring at 23 ° C. for 30 minutes, and the supernatant was removed and concentrated. To the obtained residue, 10 parts of acetonitrile was added and stirred, and then concentrated to obtain 2.46 parts of the salt represented by the formula (I-8).

MASS (ESI (+) Spectrum): M ⁺ 263.1
MASS (ESI (-) Spectrum): M ^- 427.1

式（Ｉ−１）で表される化合物１．２８部及びアセトニトリル１０部を、反応器に仕込み、２３℃で３０分間攪拌した後、ｐ−トルエンスルホン酸０．００００７部をアセトニトリル０．０３６部に溶解した溶液を加え、次いで、式（Ｉ−６−ａ）で表される化合物０．２８部を滴下した後、２３℃で１２時間攪拌した。得られた反応混合物に、クロロホルム５０部及びイオン交換水２０部を添加し、２３℃で１時間攪拌した後、分液し有機層を回収した。回収された有機層に、イオン交換水２０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。この水洗操作を５回繰り返した。回収された有機層を濃縮し、得られた残渣に、アセトニトリル１０部を添加攪拌し、濃縮した。得られた残渣に、酢酸エチル３０部を加えて２３℃で３０分間攪拌し、上澄み液を除去し、濃縮した。得られた残渣に、アセトニトリル１０部を加えて攪拌した後、濃縮することにより、式（Ｉ−６）で表される塩１．０２部を得た。 Example 3: Synthesis of a salt represented by the formula (I-6)

1.28 parts of the compound represented by the formula (I-1) and 10 parts of acetonitrile were charged into a reactor and stirred at 23 ° C. for 30 minutes, and then 0.00007 part of p-toluenesulfonic acid was added to 0.036 part of acetonitrile. After adding 0.28 parts of the compound represented by the formula (I-6-a) dropwise, the mixture was stirred at 23 ° C. for 12 hours. To the obtained reaction mixture, 50 parts of chloroform and 20 parts of ion-exchanged water were added and stirred at 23 ° C. for 1 hour, followed by liquid separation to recover the organic layer. To the collected organic layer, 20 parts of ion-exchanged water was added and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 5 times. The collected organic layer was concentrated, and 10 parts of acetonitrile was added to the resulting residue, stirred, and concentrated. To the obtained residue, 30 parts of ethyl acetate was added and stirred at 23 ° C. for 30 minutes, and the supernatant was removed and concentrated. To the obtained residue, 10 parts of acetonitrile was added and stirred, and then concentrated to obtain 1.02 part of a salt represented by the formula (I-6).

MASS (ESI (+) Spectrum): M ⁺ 263.1
MASS (ESI (−) Spectrum): M ^- 455.2

式（Ｉ−１）で表される化合物１．１１部、アセトニトリル１０部及び４−ジメチルアミノピリジン０．３１部をそれぞれ仕込み、２３℃で攪拌下、溶解させた。得られた混合液に、式（Ｉ−７−ａ）で表される化合物０．４８部を滴下し、４０℃で５時間攪拌した。更に、２３℃で濃塩酸０．０９部を添加し、１時間攪拌した。得られた反応混合物に、クロロホルム５０部及びイオン交換水２０部を添加し、２３℃で１時間攪拌した後、分液し有機層を回収した。回収された有機層に、イオン交換水２０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。この水洗操作を５回繰り返した。回収された有機層を濃縮し、得られた残渣に、アセトニトリル１０部を添加攪拌し、濃縮した。得られた残渣に、酢酸エチル３０部を加えて２３℃で３０分間攪拌し、上澄み液を除去し、濃縮した。得られた残渣に、アセトニトリル１０部を加えて攪拌した後、濃縮することにより、式（Ｉ−７）で表される塩０．７８部を得た。 Example 4: Synthesis of salt represented by formula (I-7)

1.11 parts of the compound represented by the formula (I-1), 10 parts of acetonitrile and 0.31 part of 4-dimethylaminopyridine were charged and dissolved at 23 ° C. with stirring. To the obtained mixed liquid, 0.48 part of the compound represented by the formula (I-7-a) was dropped, and the mixture was stirred at 40 ° C. for 5 hours. Further, 0.09 part of concentrated hydrochloric acid was added at 23 ° C. and stirred for 1 hour. To the obtained reaction mixture, 50 parts of chloroform and 20 parts of ion-exchanged water were added and stirred at 23 ° C. for 1 hour, followed by liquid separation to recover the organic layer. To the collected organic layer, 20 parts of ion-exchanged water was added and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 5 times. The collected organic layer was concentrated, and 10 parts of acetonitrile was added to the resulting residue, stirred, and concentrated. To the obtained residue, 30 parts of ethyl acetate was added and stirred at 23 ° C. for 30 minutes, and the supernatant was removed and concentrated. To the obtained residue, 10 parts of acetonitrile was added and stirred, and then concentrated to obtain 0.78 part of a salt represented by the formula (I-7).

MASS (ESI (+) Spectrum): M ⁺ 263.1
MASS (ESI (−) Spectrum): M ^- 483.2

Synthesis of Resin The compound (monomer) used for the synthesis of the resin (A) is shown below. Hereinafter, these compounds are referred to as “monomer (a1-1-2)” or the like according to the formula number.

Synthesis Example 1 [Synthesis of Resin A1]
As the monomer, using monomer (a1-1-3), monomer (a1-2-9), monomer (a2-1-3), monomer (a3-2-3) and monomer (a3-4-2), The molar ratio [monomer (a1-1-3): monomer (a1-2-9): monomer (a2-1-3): monomer (a3-2-3)): monomer (a3-4-2)] However, it mixed so that it might become 45: 14: 2.5: 22: 16.5, and 1.5 mass times propylene glycol monomethyl ether acetate of the total monomer amount was added, and it was set as the solution. To this solution, azobisisobutyronitrile and azobis (2,4-dimethylvaleronitrile) as initiators were added in an amount of 0.95 mol% and 2.85 mol%, respectively, based on the total monomer amount, and these were added at 73 ° C. Heated for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The resin obtained was again dissolved in propylene glycol monomethyl ether acetate, and the resulting solution was poured into a methanol solvent to precipitate the resin, followed by two reprecipitation operations of filtering the resin, and a weight average molecular weight of 8. 8 × 10 ³ resin A1 was obtained with a yield of 71%. This resin A1 has the following structural units.

Synthesis Example 2 [Synthesis of Resin A2]
As the monomer, using monomer (a1-1-3), monomer (a1-5-1), monomer (a2-1-3), monomer (a3-2-3) and monomer (a3-4-2), The molar ratio [monomer (a1-1-3): monomer (a1-5-1): monomer (a2-1-3): monomer (a3-2-3)): monomer (a3-4-2)] However, it mixed so that it might become 45: 14: 2.5: 22: 16.5, and 1.5 mass times propylene glycol monomethyl ether acetate of the total monomer amount was added, and it was set as the solution. To this solution, 1% and 3 mol% of azobisisobutyronitrile and azobis (2,4-dimethylvaleronitrile) as initiators were added to the total monomer amount, respectively, and these were heated at 73 ° C. for about 5 hours. did. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The resin obtained was again dissolved in propylene glycol monomethyl ether acetate, and the resulting solution was poured into a methanol solvent to precipitate the resin, followed by two reprecipitation operations of filtering the resin, and a weight average molecular weight of 8. 2 × 10 ³ resin A2 was obtained with a yield of 66%. This resin A2 has the following structural units.

Synthesis Example 3 [Synthesis of Resin A3]
The monomer (a1-1-2), monomer (a2-1-1) and monomer (a3-1-1) are mixed in a molar ratio [monomer (a1-1-2): monomer (2-1-1): Monomer (a3-1-1)] was mixed so as to be 50:25:25, and 1.5 mass times dioxane was further mixed with respect to the total mass of all monomers. To the obtained mixture, azobisisobutyronitrile and azobis (2,4-dimethylvaleronitrile) were added as initiators in proportions of 1 mol% and 3 mol%, respectively, with respect to the total number of moles of all monomers. did. This was polymerized by heating at 80 ° C. for about 8 hours. Thereafter, the polymerization reaction solution was poured into a large amount of a mixed solvent of methanol and water (mass ratio methanol: water = 4: 1) to precipitate the resin. This resin was filtered and collected. Again, the resin is dissolved in dioxane, poured into a mixed solvent of a large amount of methanol and water, the resin is precipitated, and the precipitated resin is filtered and recovered three times for reprecipitation purification, and the weight average Resin A3 (copolymer) having a molecular weight of about 9.2 × 10 ³ was obtained in a yield of 60%. This resin A3 had the following structural units and was soluble in butyl acetate.

Synthesis Example 4 [Synthesis of Resin A4]
As the monomer, the monomer (a1-1-3), the monomer (a1-2-9), the monomer (a2-1-1) and the monomer (a3-4-2) were used, and their molar ratio [monomer (a1-1 -3): Monomer (a1-2-9): Monomer (a2-1-1): Monomer (a3-4-2)] is mixed so as to be 40: 11: 4: 45. 1.5 mass times propylene glycol monomethyl ether acetate was added to prepare a solution. To this solution, 1 mol% and 3 mol% of azobisisobutyronitrile and azobis (2,4-dimethylvaleronitrile) as initiators were added to the total monomer amount, respectively, and these were heated at 75 ° C. for about 5 hours. did. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered. The obtained resin was again dissolved in propylene glycol monomethyl ether acetate, and the resulting solution was poured into a methanol / water mixed solvent to precipitate the resin, followed by reprecipitation operation of filtering the resin twice. Resin A4 (copolymer) having a molecular weight of 8.2 × 10 ³ was obtained in a yield of 70%. This resin A4 has the following structural units.

Synthesis Example 5 [Synthesis of Resin X1]
Monomer (a4-1-7) was used as a monomer, and 1.5 mass times dioxane of the total monomer amount was added to prepare a solution. Azobisisobutyronitrile and azobis (2,4-dimethylvaleronitrile) as initiators were added to the solution in an amount of 0.7 mol% and 2.1 mol%, respectively, with respect to the total monomer amount, and these were added at 75 ° C. Heated for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate the resin, and this resin was filtered.
The resin thus obtained was dissolved again in dioxane, and the solution obtained by pouring the solution into a methanol / water mixed solvent was precipitated twice, and the resin was filtered twice to perform the reprecipitation operation twice. 8 × 10 ⁴ of resin X1 was obtained with a yield of 77%. This resin X1 has the following structural units.

Synthesis Example 6 [Synthesis of Resin X2]
As the monomer, monomer (a5-1-1) and monomer (a4-0-1) were used, and the molar ratio (monomer (a5-1-1): monomer (a4-0-1)) was 75:25. Then, methyl isobutyl ketone 1.2 mass times the total monomer amount was added to make a solution. To this solution, 2 mol% of azobis (2,4-dimethylvaleronitrile) as an initiator was added with respect to the total amount of monomers, and heated at 70 ° C. for about 5 hours. The obtained reaction mixture was poured into a large amount of methanol / water mixed solvent to precipitate a resin, and this resin was filtered to obtain a resin X2 (copolymer) having a weight average molecular weight of 1.7 × 10 ^{4 in} a yield of 87%. Got in. This resin X2 has the following structural units.

式（Ｂ１−５−ａ）で表される塩５０．４９部及びクロロホルム２５２．４４部を反応器に仕込み、２３℃で３０分間攪拌した後、式（Ｂ１−５−ｂ）で表される化合物１６．２７部を滴下し、２３℃で１時間攪拌することにより、式（Ｂ１−５−ｃ）で表される塩を含む溶液を得た。得られた式（Ｂ１−５−ｃ）で表される塩を含む溶液に、式（Ｂ１−５−ｄ）で表される塩４８．８０部及びイオン交換水８４．１５部を添加し、２３℃で１２時間攪拌した。得られた反応液が２層に分離していたので、クロロホルム層を分液して取り出し、更に、該クロロホルム層にイオン交換水８４．１５部を添加し、水洗した。この操作を５回繰り返した。得られたクロロホルム層に、活性炭３．８８部を添加攪拌し、ろ過した。回収されたろ液を濃縮し、得られた残渣に、アセトニトリル１２５．８７部を添加攪拌し、濃縮した。得られた残渣に、アセトニトリル２０．６２部及びｔｅｒｔ−ブチルメチルエーテル３０９．３０部を加えて２３℃で３０分間攪拌し、上澄み液を除去し、濃縮した。得られた残渣に、ｎ−ヘプタン２００部を添加、２３℃で３０分間攪拌し、ろ過することにより、式（Ｂ１−５）で表される塩６１．５４部を得た。
ＭＡＳＳ（ＥＳＩ（＋）Ｓｐｅｃｔｒｕｍ）：Ｍ^＋ ３７５．２
ＭＡＳＳ（ＥＳＩ（−）Ｓｐｅｃｔｒｕｍ）：Ｍ⁻ ３３９．１ Synthesis Example 7: Synthesis of salt represented by formula (B1-5)

50.49 parts of the salt represented by the formula (B1-5-a) and 252.44 parts of chloroform are charged into a reactor, stirred at 23 ° C. for 30 minutes, and then represented by the formula (B1-5-b). 16.27 parts of the compound was added dropwise and stirred at 23 ° C. for 1 hour to obtain a solution containing a salt represented by the formula (B1-5-c). To the obtained solution containing the salt represented by the formula (B1-5-c), 48.80 parts of the salt represented by the formula (B1-5-d) and 84.15 parts of ion-exchanged water are added, The mixture was stirred at 23 ° C. for 12 hours. Since the resulting reaction solution was separated into two layers, the chloroform layer was separated and removed, and 84.15 parts of ion-exchanged water was further added to the chloroform layer and washed with water. This operation was repeated 5 times. To the obtained chloroform layer, 3.88 parts of activated carbon was added and stirred, followed by filtration. The collected filtrate was concentrated, and 125.87 parts of acetonitrile was added to the resulting residue, and the mixture was stirred and concentrated. To the obtained residue, 20.62 parts of acetonitrile and 309.30 parts of tert-butyl methyl ether were added and stirred at 23 ° C. for 30 minutes, and the supernatant was removed and concentrated. To the obtained residue, 200 parts of n-heptane was added, stirred at 23 ° C. for 30 minutes, and filtered to obtain 61.54 parts of the salt represented by the formula (B1-5).
MASS (ESI (+) Spectrum): M ⁺ 375.2
MASS (ESI (−) Spectrum): M ^- 339.1

特開２００８−２０９９１７号公報に記載された方法によって得られた式（Ｂ１−２１−ｂ）で表される化合物３０．００部、式（Ｂ１−２１−ａ）で表される塩３５．５０部、クロロホルム１００部及びイオン交換水５０部を仕込み、２３℃で１５時間攪拌した。
得られた反応液が２層に分離していたので、クロロホルム層を分液して取り出し、更に、該クロロホルム層にイオン交換水３０部を添加し、水洗した。この操作を５回繰り返した。クロロホルム層を濃縮し、得られた残渣に、ｔｅｒｔ−ブチルメチルエーテル１００部を加えて２３℃で３０分間攪拌した後、ろ過することにより、式（Ｂ１−２１−ｃ）で表される塩４８．５７部を得た。 Synthesis Example 8 [Synthesis of salt represented by formula (B1-21)]

30.00 parts of a compound represented by the formula (B1-21-b) obtained by the method described in JP-A-2008-209917, and a salt 35.50 represented by the formula (B1-21-a). Part, 100 parts of chloroform, and 50 parts of ion-exchanged water were stirred at 23 ° C. for 15 hours.
Since the obtained reaction solution was separated into two layers, the chloroform layer was separated and taken out, and 30 parts of ion-exchanged water was further added to the chloroform layer and washed with water. This operation was repeated 5 times. The chloroform layer was concentrated, 100 parts of tert-butyl methyl ether was added to the resulting residue, and the mixture was stirred at 23 ° C. for 30 minutes, and then filtered to obtain the salt 48 represented by the formula (B1-21-c). .57 parts were obtained.

式（Ｂ１−２１−ｃ）で表される塩２０．００部、式（Ｂ１−２１−ｄ）で表される化合物２．８４部及びモノクロロベンゼン２５０部を仕込み、２３℃で３０分間攪拌した。
得られた混合液に、二安息香酸銅（ＩＩ）０．２１部を添加した後、更に、１００℃で１時間攪拌した。得られた反応溶液を濃縮した後、得られた残渣に、クロロホルム２００部及びイオン交換水５０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。回収された有機層にイオン交換水５０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。この水洗操作を５回繰り返した。得られた有機層を濃縮した後、得られた残渣に、アセトニトリル５３．５１部に溶解し、濃縮した後、ｔｅｒｔ−ブチルメチルエーテル１１３．０５部を加えて攪拌した後、ろ過することにより、式（Ｂ１−２１）で表される塩１０．４７部を得た。

20.00 parts of a salt represented by the formula (B1-21-c), 2.84 parts of a compound represented by the formula (B1-21-d) and 250 parts of monochlorobenzene were charged and stirred at 23 ° C. for 30 minutes. .
After adding 0.21 part of copper (II) dibenzoate to the obtained liquid mixture, it stirred at 100 degreeC for further 1 hour. After concentrating the obtained reaction solution, 200 parts of chloroform and 50 parts of ion-exchanged water were added to the obtained residue and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out an organic layer. 50 parts of ion-exchanged water was added to the collected organic layer and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 5 times. After concentrating the obtained organic layer, the residue obtained was dissolved in 53.51 parts of acetonitrile, concentrated, 113.05 parts of tert-butyl methyl ether was added and stirred, and then filtered. 10.47 parts of the salt represented by the formula (B1-21) were obtained.

MASS (ESI (+) Spectrum): M ⁺ 237.1
MASS (ESI (−) Spectrum): M ^- 339.1

式（Ｂ１−２２−ａ）で表される塩１１．２６部、式（Ｂ１−２２−ｂ）で表される化合物１０．００部、クロロホルム５０部及びイオン交換水２５部を仕込み、２３℃で１５時間攪拌した。得られた反応液が２層に分離していたので、クロロホルム層を分液して取り出し、更に、該クロロホルム層にイオン交換水１５部を添加し、水洗した。この操作を５回繰り返した。クロロホルム層を濃縮し、得られた残渣に、ｔｅｒｔ−ブチルメチルエーテル５０部を加えて２３℃で３０分間攪拌した後、ろ過することにより、式（Ｂ１−２２−ｃ）で表される塩１１．７５部を得た。 Synthesis Example 9 [Synthesis of salt represented by formula (B1-22)]

11.26 parts of a salt represented by the formula (B1-22-a), 10.00 parts of a compound represented by the formula (B1-22-b), 50 parts of chloroform and 25 parts of ion-exchanged water were charged at 23 ° C. For 15 hours. Since the obtained reaction liquid was separated into two layers, the chloroform layer was separated and taken out, and further 15 parts of ion-exchanged water was added to the chloroform layer and washed with water. This operation was repeated 5 times. The chloroform layer was concentrated, 50 parts of tert-butyl methyl ether was added to the resulting residue, the mixture was stirred at 23 ° C. for 30 minutes, and then filtered to obtain the salt 11 represented by the formula (B1-22-c). .75 parts were obtained.

式（Ｂ１−２２−ｃ）で表される塩１１．７１部、式（Ｂ１−２２−ｄ）で表される化合物１．７０部及びモノクロロベンゼン４６．８４部を仕込み、２３℃で３０分間攪拌した。得られた混合液に、二安息香酸銅（ＩＩ）０．１２部を添加した後、更に、１００℃で３０分間攪拌した。得られた反応溶液を濃縮した後、得られた残渣に、クロロホルム５０部及びイオン交換水１２．５０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。回収された有機層にイオン交換水１２．５０部を加えて２３℃で３０分間攪拌した後、分液して有機層を取り出した。この水洗操作を８回繰り返した。得られた有機層を濃縮した後、得られた残渣に、ｔｅｒｔ−ブチルメチルエーテル５０部を加えて攪拌した後、ろ過することにより、式（Ｂ１−２２）で表される塩６．８４部を得た。

11.71 parts of a salt represented by the formula (B1-22-c), 1.70 parts of a compound represented by the formula (B1-22-d) and 46.84 parts of monochlorobenzene were charged, and the mixture was charged at 23 ° C. for 30 minutes. Stir. After adding 0.12 part of copper (II) dibenzoate to the obtained liquid mixture, it stirred at 100 degreeC for 30 minutes further. After concentrating the obtained reaction solution, 50 parts of chloroform and 12.50 parts of ion-exchanged water were added to the obtained residue and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out an organic layer. 12.50 parts of ion-exchanged water was added to the collected organic layer and stirred at 23 ° C. for 30 minutes, followed by liquid separation to take out the organic layer. This washing operation was repeated 8 times. After concentration of the obtained organic layer, 50 parts of tert-butyl methyl ether was added to the obtained residue, stirred, and then filtered to obtain 6.84 parts of the salt represented by the formula (B1-22). Got.

MASS (ESI (+) Spectrum): M ⁺ 237.1
MASS (ESI (-) Spectrum): M ^- 323.0

<Preparation of resist composition>
As shown in Tables 3 and 4, the following components were mixed, and the resulting mixture was filtered through a fluororesin filter having a pore size of 0.2 μm to prepare a resist composition.

<Resin>
A1-A4, X1, X2: Resin A1-Resin A4, Resin X1, Resin X2

<Acid generator>
I-1:

I-8:

I-6:

I-7:

Ｂ１−５：式（Ｂ１−５）で表される塩
Ｂ１−２１：式（Ｂ１−２１）で表される塩
Ｂ１−２２：式（Ｂ１−２２）で表される塩 B1-2: synthesized according to the example of JP-A-2006-257078

B1-5: salt represented by formula (B1-5) B1-21: salt represented by formula (B1-21) B1-22: salt represented by formula (B1-22)

<Compound (D)>
D1: (Tokyo Chemical Industry Co., Ltd.)

<Solvent>
Propylene glycol monomethyl ether acetate 265 parts Propylene glycol monomethyl ether 20 parts 2-heptanone 20 parts γ-butyrolactone 3.5 parts

<Immersion exposure evaluation of resist composition>
An organic antireflective coating composition [ARC-29; manufactured by Nissan Chemical Industries, Ltd.] was applied onto a 12-inch silicon wafer, and baked under the conditions of 205 ° C. and 60 seconds, whereby an organic layer having a thickness of 78 nm was obtained. An antireflection film was formed. Next, the resist composition was spin-coated on the organic antireflection film so that the film thickness of the composition layer after drying (pre-baking) was 100 nm. After coating, this silicon wafer was pre-baked on a direct hot plate for 60 seconds at the temperature described in the “PB” column of Tables 3 to 4 to form a composition layer on the silicon wafer.
ArF excimer laser stepper for immersion exposure [XT: 1900 Gi; manufactured by ASML, NA = 1.35, Annual σ _out = 0.85 σ _in = 0.65 XY− pol. Illumination], using a mask for forming a trench pattern (pitch 120 nm / trench width 40 nm), the exposure amount was changed stepwise to perform exposure. Note that ultrapure water was used as the immersion medium.
After the exposure, post-exposure baking was performed for 60 seconds on the hot plate at the temperature described in the “PEB” column of Tables 3 to 4. Next, the composition layer on the silicon wafer is developed by using a butyl acetate (manufactured by Tokyo Chemical Industry Co., Ltd.) as a developing solution by a dynamic dispensing method at 23 ° C. for 20 seconds, thereby forming a negative resist pattern. Manufactured.

  In the obtained resist pattern, the exposure amount at which the width of the trench pattern was 40 nm was defined as effective sensitivity.

<Line edge roughness evaluation (LER)>
About the obtained resist pattern, the fluctuation width of the unevenness | corrugation of a wall surface was observed and measured with the scanning electron microscope. When the fluctuation width was 3 nm or less, the LER was evaluated as good, and when the swing width was more than 3 nm, the LER was evaluated as poor, and was evaluated as x. The results are shown in Table 5. A numerical value in parentheses in the LER column indicates a swing width (nm).

  According to the resist composition containing the salt of the present invention, a resist pattern can be obtained with good line edge roughness (LER).

Claims (9)

A salt represented by the formula (I).

[In the formula (I),
Q ¹ and Q ² each independently represents a fluorine atom or a C 1-6 perfluoroalkyl group.
L ^b1 represents a divalent saturated hydrocarbon group having 1 to 24 carbon atoms, and the methylene group contained in the saturated hydrocarbon group may be replaced by an oxygen atom or a carbonyl group. The hydrogen atom contained may be substituted with a fluorine atom or a hydroxy group.
R ¹ represents an alkanediyl group having 1 to 12 carbon atoms, and a hydrogen atom contained in the alkanediyl group may be substituted with a hydroxy group or an alkoxy group having 1 to 12 carbon atoms to form an alkanediyl group. The methylene group may be replaced by an oxygen atom.
R ² represents a hydrogen atom or an acid labile group.
W represents an aliphatic ring having 3 to 36 carbon atoms, and the methylene group constituting the aliphatic ring may be replaced by an oxygen atom, a sulfur atom, a carbonyl group or a sulfonyl group, and is included in the aliphatic ring. The hydrogen atom to be substituted may be substituted with a hydroxy group, an alkyl group having 1 to 12 carbon atoms, or an alkoxy group having 1 to 12 carbon atoms.
m represents 0 or 1.
Z ⁺ represents an organic counter ion. ] The salt according to claim 1, wherein W is an aliphatic ring having 5 to 18 carbon atoms. The salt according to claim 1 or 2, wherein W is an adamantane ring. L ^b1 _{is, * - CO-O- (CH} 2) n - (n represents 0 or 1 * represents a bonding position to CQ ¹ Q ^2..) Any one of claims 1 to 3 is Salt. R ¹ is A salt according to any one of claims 1 to 4 alkanediyl group having 1 to 6 carbon atoms. The salt according to any one of claims 1 to 5, wherein R ² is a hydrogen atom. Z ^<+> is an arylsulfonium cation, The salt in any one of Claims 1-6.   A resist composition comprising the salt according to claim 1 and a resin having an acid labile group. (1) The process of apply | coating the resist composition of Claim 8 on a board | substrate,
(2) The process of drying the composition after application | coating and forming a composition layer,
(3) a step of exposing the composition layer;
(4) A method for producing a resist pattern, comprising a step of heating the composition layer after exposure, and (5) a step of developing the composition layer after heating.