JP2015090903A - Curing type composition for printed wiring boards, cured coating film arranged by use thereof, and printed wiring board - Google Patents
Curing type composition for printed wiring boards, cured coating film arranged by use thereof, and printed wiring board Download PDFInfo
- Publication number
- JP2015090903A JP2015090903A JP2013229680A JP2013229680A JP2015090903A JP 2015090903 A JP2015090903 A JP 2015090903A JP 2013229680 A JP2013229680 A JP 2013229680A JP 2013229680 A JP2013229680 A JP 2013229680A JP 2015090903 A JP2015090903 A JP 2015090903A
- Authority
- JP
- Japan
- Prior art keywords
- printed wiring
- meth
- curable composition
- carboxyl group
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、プリント配線板用の硬化型組成物、特にインクジェット方式に用いられる紫外線硬化型の組成物、これを用いたレジストおよびマーキングの少なくとも何れか一種のプリント配線板用塗膜、及びこれを用いて得られたパターンを有するプリント配線板に関する。 The present invention relates to a curable composition for a printed wiring board, in particular, an ultraviolet curable composition used in an ink jet system, a coating film for printed wiring board of at least one of resist and marking using the composition, and The present invention relates to a printed wiring board having a pattern obtained by use.
プリント配線板にエッチングレジスト、ソルダーレジスト、シンボルマーキングなどを形成する方法として、硬化型組成物からなるインキを用い、活性エネルギー線の照射によってインキを硬化させる手法が知られている（特許文献１、２）。 As a method of forming an etching resist, a solder resist, symbol marking, etc. on a printed wiring board, a method is known in which an ink made of a curable composition is used and the ink is cured by irradiation with active energy rays (Patent Document 1, 2).
プリント配線板上に形成されるレジストインキやマーキングインキなどの各種プリント配線板用硬化型組成物は、はんだ耐熱等といった諸特性を維持しつつ、プラスチック基材及び導体層上での密着性と高い硬度が求められる。しかしながら、上記のような活性エネルギー線の照射によって硬化させる硬化型組成物、特に、印刷直後にインキを硬化させる手法に適したプリント配線板用組成物では、プラスチック基材及び導体層上での密着性と、高い硬度とを両立する事は困難であった。 Various printed wiring board curable compositions such as resist ink and marking ink formed on printed wiring boards have high adhesion on plastic substrates and conductor layers while maintaining various properties such as solder heat resistance. Hardness is required. However, in a curable composition that is cured by irradiation with active energy rays as described above, particularly in a printed wiring board composition that is suitable for a method of curing ink immediately after printing, adhesion on a plastic substrate and a conductor layer. It has been difficult to achieve both high performance and high hardness.
本発明は上記のような従来技術の問題を解消するためになされたものであり、その主たる目的は、はんだ耐熱性等といった諸特性を維持しつつ、プラスチック基材及び導体層上での密着性と、高い硬度とを両立するプリント配線板用硬化型組成物を提供することにある。 The present invention has been made to solve the above-described problems of the prior art, and its main purpose is to maintain adhesive properties on plastic substrates and conductor layers while maintaining various properties such as solder heat resistance. Another object of the present invention is to provide a curable composition for printed wiring boards that achieves both high hardness and low hardness.
本発明の他の目的は、かかるプリント配線板用硬化型組成物を用いて形成された、はんだ耐熱性等といった諸特性を維持しつつ、プラスチック基材及び導体層上での密着性と、高い硬度とを両立するパターン硬化塗膜を有するプリント配線板を提供することにある。 Another object of the present invention is to use the curable composition for printed wiring boards, while maintaining various properties such as solder heat resistance, and high adhesion on the plastic substrate and conductor layer. An object of the present invention is to provide a printed wiring board having a pattern cured coating film that is compatible with hardness.
本発明の上記目的は、光塩基発生剤と、カルボキシル基を有する（メタ）アクリレート化合物と、光重合開始剤と、熱硬化成分と、を含むことを特徴とするプリント配線板用硬化型組成物により達成されることが見出された。 The object of the present invention is to provide a curable composition for a printed wiring board comprising a photobase generator, a (meth) acrylate compound having a carboxyl group, a photopolymerization initiator, and a thermosetting component. Was found to be achieved.
即ち、本発明のプリント配線板用硬化型組成物は、（Ａ）光塩基発生剤と、（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物と、（Ｃ）光重合開始剤と、（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）と、を含むことを特徴とするものである。
また、本発明のプリント配線板用硬化型組成物は、（Ａ−１）光重合開始剤としての機能を有する光塩基発生剤と、（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物と、（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）と、を含むことを特徴とするものである。
That is, the curable composition for printed wiring boards of the present invention comprises (A) a photobase generator, (B) a (meth) acrylate compound having a carboxyl group, (C) a photopolymerization initiator, and (D). And a thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group).
Moreover, the curable composition for printed wiring boards of this invention is (A-1) the photobase generator which has a function as a photoinitiator, (B) the (meth) acrylate compound which has a carboxyl group, ( D) a thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group).
本発明のプリント配線板用硬化型組成物は、前記（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）がカルボキシル基と反応しうる官能基を少なくとも２つ有する化合物であることが好ましい。 In the curable composition for printed wiring boards of the present invention, the (D) thermosetting component (excluding the (B) carboxyl group-containing (meth) acrylate compound) has at least two functional groups capable of reacting with the carboxyl group. A compound is preferred.
また、本発明のプリント配線板用硬化型組成物は、前記カルボキシル基と反応しうる官能基を少なくとも２つ有する化合物がエポキシ化合物であることが好ましい。 In the curable composition for printed wiring boards of the present invention, the compound having at least two functional groups capable of reacting with the carboxyl group is preferably an epoxy compound.
また、本発明のプリント配線板用硬化型組成物は、前記エポキシ化合物が結晶性を有することが好ましい。 Moreover, it is preferable that the said epoxy compound has crystallinity in the curable composition for printed wiring boards of this invention.
また、本発明のプリント配線板用硬化型組成物は、さらに、２官能（メタ）アクリレート化合物（カルボキシル基を有するものを除く）を含むことが好ましい。 Moreover, it is preferable that the curable composition for printed wiring boards of this invention contains bifunctional (meth) acrylate compound (except what has a carboxyl group) further.
また、本発明のプリント配線板用硬化型組成物は、前記２官能（メタ）アクリレート化合物の２５℃における粘度が５〜５０ｍＰａ・ｓであることが好ましい。 Moreover, it is preferable that the viscosity at 25 degreeC of the said bifunctional (meth) acrylate compound is 5-50 mPa * s in the curable composition for printed wiring boards of this invention.
また、本発明のプリント配線板用硬化型組成物は、５０℃における粘度が５〜５０ｍＰａ・ｓであることが好ましい。 Moreover, it is preferable that the viscosity at 50 degreeC is 5-50 mPa * s in the curable composition for printed wiring boards of this invention.
本発明の硬化塗膜は、上記のプリント配線板用硬化型組成物に対して光照射することにより得られることを特徴とするものである。 The cured coating film of the present invention is obtained by irradiating light to the above curable composition for printed wiring boards.
本発明のプリント配線板は、上記のプリント配線板用硬化型組成物が基板上に印刷され、これを光照射することにより得られるパターン硬化塗膜を有することを特徴とするものである。 The printed wiring board of the present invention is characterized by having a pattern cured coating film obtained by printing the curable composition for a printed wiring board on a substrate and irradiating it with light.
本発明のプリント配線板は、上記のプリント配線板用硬化型組成物がインクジェット印刷法により基板上に印刷され、これを光照射することにより得られるパターン硬化塗膜を有することを特徴とするものである。 The printed wiring board of the present invention is characterized in that the above-mentioned curable composition for printed wiring boards is printed on a substrate by an ink jet printing method and has a pattern cured coating film obtained by irradiating it with light. It is.
本発明のプリント配線板は、前記基板がプラスチック基板であることが好ましい。 In the printed wiring board of the present invention, the substrate is preferably a plastic substrate.
本発明により、はんだ耐熱性等といった諸特性を維持しつつ、プラスチック基材及び導体層上での密着性と、高い硬度とを両立するプリント配線板用硬化型組成物を提供することが可能となる。また、かかるプリント配線板用硬化型組成物を用いて形成された、はんだ耐熱性等といった諸特性を維持しつつ、プラスチック基材及び導体層上での密着性と、高い硬度とを両立するパターン硬化塗膜を有するプリント配線板を提供することが可能となる。 According to the present invention, it is possible to provide a curable composition for a printed wiring board that achieves both high adhesion and adhesion on a plastic substrate and a conductor layer while maintaining various properties such as solder heat resistance. Become. In addition, a pattern that is formed using such a curable composition for printed wiring boards, while maintaining various properties such as solder heat resistance and the like, and having both high adhesion and adhesion on the plastic substrate and conductor layer. A printed wiring board having a cured coating film can be provided.
本発明のプリント配線板用硬化型組成物（以下、硬化型組成物ともいう）は、（Ａ）光塩基発生剤（成分Ａ）と、（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物（成分Ｂ）と、（Ｃ）光重合開始剤（成分Ｃ）と、（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）と、を含む。また、本発明の他のプリント配線板用硬化型組成物は、（Ａ−１）光重合開始剤としての機能を有する光塩基発生剤と、（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物と、（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）と、を含む。これは、（Ａ）成分として、（Ａ−１）光重合開始剤としての機能を有する光塩基発生剤を含む組成物であり、この場合、（Ｃ）光重合開始剤は含まれていても含まれていなくてもよい。 The curable composition for printed wiring boards of the present invention (hereinafter also referred to as curable composition) comprises (A) a photobase generator (component A) and (B) a (meth) acrylate compound having a carboxyl group (component). B), (C) a photopolymerization initiator (component C), and (D) a thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group). Moreover, the other curable composition for printed wiring boards of this invention is (A-1) the photobase generator which has a function as a photoinitiator, (B) (meth) acrylate compound which has a carboxyl group, And (D) a thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group). This is a composition containing (A-1) a photobase generator having a function as a photopolymerization initiator as component (A), and in this case, (C) a photopolymerization initiator is contained. It does not have to be included.
なお、本明細書において、（メタ）アクリレートとは、アクリレート、メタアクリレートおよびそれらの混合物を総称する用語で、他の類似の表現についても同様である。 In the present specification, “(meth) acrylate” is a general term for acrylate, methacrylate, and a mixture thereof, and the same applies to other similar expressions.
［（Ａ）光塩基発生剤］
（Ａ）光塩基発生剤は、紫外線や可視光等の光照射により分子構造が変化するか、または、分子が開裂することにより、カルボキシル基を有する（メタ）アクリレートと熱硬化成分との付加反応の触媒として機能しうる１種以上の塩基性物質を生成する化合物である。発生する塩基性物質として、例えば２級アミン、３級アミンが挙げられる。
[(A) Photobase generator]
(A) The photobase generator is an addition reaction between a (meth) acrylate having a carboxyl group and a thermosetting component by changing the molecular structure upon irradiation with light such as ultraviolet rays or visible light, or by cleaving the molecule. A compound that produces one or more basic substances that can function as a catalyst for Examples of the basic substance to be generated include secondary amines and tertiary amines.
光塩基発生剤として、例えば、α−アミノアセトフェノン化合物、オキシムエステル化合物や、アシルオキシイミノ基，Ｎ−ホルミル化芳香族アミノ基、Ｎ−アシル化芳香族アミノ基、ニトロベンジルカーバメイト基、アルコオキシベンジルカーバメート基等の置換基を有する化合物等が挙げられる。なかでも、オキシムエステル化合物、α−アミノアセトフェノン化合物が好ましい。α−アミノアセトフェノン化合物としては、特に、２つ以上の窒素原子を有するものが好ましい。 その他の光塩基発生剤として、WPBG-018(商品名：9-anthrylmethyl N,N’-diethylcarbamate和光純薬製),WPBG-027(商品名：(E)-1-[3-(2-hydroxyphenyl)-2-propenoyl]piperidine),WPBG-082(商品名：guanidinium2-(3-benzoylphenyl)propionate), WPBG-140 (商品名：1-(anthraquinon-2-yl)ethyl imidazolecarboxylate)等を使用することもできる。 Examples of photobase generators include α-aminoacetophenone compounds, oxime ester compounds, acyloxyimino groups, N-formylated aromatic amino groups, N-acylated aromatic amino groups, nitrobenzyl carbamate groups, and alkoxyoxybenzyl carbamates. And compounds having a substituent such as a group. Of these, oxime ester compounds and α-aminoacetophenone compounds are preferred. As the α-aminoacetophenone compound, those having two or more nitrogen atoms are particularly preferable. Other photobase generators include WPBG-018 (trade name: 9-anthrylmethyl N, N'-diethylcarbamate Wako Pure Chemicals), WPBG-027 (trade name: (E) -1- [3- (2-hydroxyphenyl) ) -2-propenoyl] piperidine), WPBG-082 (trade name: guanidinium2- (3-benzoylphenyl) propionate), WPBG-140 (trade name: 1- (anthraquinon-2-yl) ethyl imidazolecarboxylate) You can also.
α―アミノアセトフェノン化合物は、分子中にベンゾインエーテル結合を有し、光照射を受けると分子内で開裂が起こり、硬化触媒作用を奏する塩基性物質（アミン）が生成する。α−アミノアセトフェノン化合物の具体例としては、（４−モルホリノベンゾイル）−１−ベンジル−１−ジメチルアミノプロパン（イルガキュア３６９、商品名、ＢＡＳＦジャパン社製）や４−（メチルチオベンゾイル）−１−メチル−１−モルホリノエタン（イルガキュア９０７、商品名、ＢＡＳＦジャパン社製）、２−（ジメチルアミノ）−２−［（４−メチルフェニル）メチル］−１−［４−（４−モルホリニル）フェニル］−１−ブタノン（イルガキュア３７９、商品名、ＢＡＳＦジャパン社製）などの市販の化合物またはその溶液を用いることができる。 The α-aminoacetophenone compound has a benzoin ether bond in the molecule, and when irradiated with light, cleavage occurs in the molecule to produce a basic substance (amine) that exhibits a curing catalytic action. Specific examples of the α-aminoacetophenone compound include (4-morpholinobenzoyl) -1-benzyl-1-dimethylaminopropane (Irgacure 369, trade name, manufactured by BASF Japan Ltd.) and 4- (methylthiobenzoyl) -1-methyl. -1-morpholinoethane (Irgacure 907, trade name, manufactured by BASF Japan Ltd.), 2- (dimethylamino) -2-[(4-methylphenyl) methyl] -1- [4- (4-morpholinyl) phenyl]- A commercially available compound such as 1-butanone (Irgacure 379, trade name, manufactured by BASF Japan Ltd.) or a solution thereof can be used.
オキシムエステル化合物としては、光照射により塩基性物質を生成する化合物であればいずれをも使用することができる。かかるオキシムエステル化合物としては、市販品として、ＢＡＳＦジャパン社製のＣＧＩ−３２５、イルガキュアーＯＸＥ０１、イルガキュアーＯＸＥ０２、アデカ社製Ｎ−１９１９、ＮＣＩ−８３１などが挙げられる。また、特許第４３４４４００号公報に記載された、分子内に２個のオキシムエステル基を有する化合物も好適に用いることができる。 Any oxime ester compound can be used as long as it is a compound that generates a basic substance by light irradiation. Examples of such oxime ester compounds include CGI-325, Irgacure OXE01, Irgacure OXE02 manufactured by BASF Japan, N-1919, and NCI-831 manufactured by Adeka. Moreover, the compound which has two oxime ester groups in the molecule | numerator described in the patent 4344400 gazette can also be used suitably.
その他、特開２００４−３５９６３９号公報、特開２００５−０９７１４１号公報、特開２００５−２２００９７号公報、特開２００６−１６０６３４号公報、特開２００８−０９４７７０号公報、特表２００８−５０９９６７号公報、特表２００９−０４０７６２号公報、特開２０１１−８００３６号公報記載のカルバゾールオキシムエステル化合物等を挙げることができる。 In addition, JP-A-2004-359639, JP-A-2005-097141, JP-A-2005-220097, JP-A-2006-160634, JP-A-2008-094770, JP-A-2008-509967, Specific examples include carbazole oxime ester compounds described in JP2009-040762A and JP2011-80036A.
このような（Ａ）光塩基発生剤は、紫外線や可視光等の照射により、光重合開始剤としても作用するもの、すなわち、（Ａ−１）光重合開始剤としての機能を有する光塩基発生剤が、（Ｃ）光重合開始剤の使用量を抑えることが出来る為、好ましい。（Ａ）成分として、（Ａ−１）を用いる場合、（Ｃ）成分を配合しない組成とすることも可能である。
また、光塩基発生剤が光重合開始剤としても作用する場合、光塩基発生剤の吸収波長と光重合開始剤の吸収波長とが異なるものを選択する事で、より効果的に組成物の硬化性を高める事が出来る。
Such (A) photobase generator acts as a photopolymerization initiator by irradiation with ultraviolet rays or visible light, that is, (A-1) photobase generation having a function as a photopolymerization initiator. An agent is preferable because the amount of the (C) photopolymerization initiator used can be suppressed. When (A-1) is used as the component (A), it is possible to have a composition in which the component (C) is not blended.
In addition, when the photobase generator also acts as a photopolymerization initiator, it is possible to cure the composition more effectively by selecting a photobase generator having a different absorption wavelength from that of the photopolymerization initiator. You can increase the sex.
このような（Ａ）光塩基発生剤は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。硬化型組成物中の光塩基発生剤の配合量は、好ましくは熱硬化成分１００質量部に対して０．１〜４０質量部であり、さらに好ましくは、０．１〜３５質量部である。光塩基発生剤の配合量が０．１質量部以下の場合、導体層上での密着性及び鉛筆硬度が低下し好ましくない。一方、４０質量部を超えて大量に配合しても期待される効果が飽和状態となるために経済的でなく、また組成物中に完全に溶解せず、組成物が不均一となり特性を低下させるおそれがあるからである。 Such (A) photobase generator may be used individually by 1 type, and may be used in combination of 2 or more type. The compounding amount of the photobase generator in the curable composition is preferably 0.1 to 40 parts by mass, more preferably 0.1 to 35 parts by mass with respect to 100 parts by mass of the thermosetting component. When the blending amount of the photobase generator is 0.1 parts by mass or less, the adhesion on the conductor layer and the pencil hardness are unfavorable. On the other hand, even if blended in a large amount exceeding 40 parts by mass, the expected effect becomes saturated, so it is not economical, it does not dissolve completely in the composition, the composition becomes non-uniform, and the properties deteriorate It is because there is a possibility of making it.
［（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物］
（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物は、モノマー又はオリゴマー等の低分子量の材料が使用され、具体的には分子量１００〜１０００の範囲、好ましくは分子量１１０〜７００の範囲の材料が用いられる。
[(B) (Meth) acrylate compound having carboxyl group]
(B) As the (meth) acrylate compound having a carboxyl group, a low molecular weight material such as a monomer or an oligomer is used. Specifically, a material having a molecular weight of 100 to 1000, preferably a molecular weight of 110 to 700 is used. It is done.
（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物の具体的例としては、2-アクリロイルオキシエチルサクシネート（商品名：NKエステルA-SA）、2-メタクリロイロキシエチルフタル酸（商品名：NKエステルCB-1）、2-メタクリロイルオキシエチルサクシネート（商品名：NKエステル SA）、ω-カルボキシ-ポリカプロラクトンモノアクリレート（ＣＨ２＝ＣＨＣＯＯ−（Ｃ５Ｈ１０ＣＯＯ）ｎ−Ｈ、ｎ≒２、商品名：アロニックス M-5300）、フタル酸モノヒドロキシエチルアクリレート（商品名：アロニックスM-5400）などが挙げられる。等が挙げられる。市販品としてはＮＫエステルＡ−ＳＡ（新中村化学工業社製の商品名）等がある。（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物は１種類又は複数種類を組み合わせて用いることができる。 (B) Specific examples of (meth) acrylate compounds having a carboxyl group include 2-acryloyloxyethyl succinate (trade name: NK ester A-SA), 2-methacryloyloxyethyl phthalate (trade name: NK Ester CB-1), 2-methacryloyloxyethyl succinate (trade name: NK ester SA), ω-carboxy-polycaprolactone monoacrylate (CH 2 ═CHCOO— (C 5 H 10 COO) n—H, n≈2 , Trade name: Aronix M-5300), monohydroxyethyl acrylate phthalate (trade name: Aronix M-5400), and the like. Etc. Examples of commercially available products include NK ester A-SA (trade name manufactured by Shin-Nakamura Chemical Co., Ltd.). (B) The (meth) acrylate compound which has a carboxyl group can be used 1 type or in combination of multiple types.
このうち、粘度調整の容易さ等から単官能（メタ）アクリレート化合物が好ましく用いられる。 Among these, a monofunctional (meth) acrylate compound is preferably used from the viewpoint of easy viscosity adjustment.
（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物の配合量は、本発明の硬化型組成物１００質量部中、好ましくは５〜５０質量部、より好ましくは１０〜３０質量部である。カルボキシル基を有する（メタ）アクリレートの配合量が、５質量部以上の場合、本発明の組成物の特徴である密着性がより良好となる。一方、配合量が５０質量部以下の場合、インキの粘度の上昇を抑え、良好な印刷性を得る事が出来る。 (B) The compounding quantity of the (meth) acrylate compound which has a carboxyl group is 5-50 mass parts preferably in 100 mass parts of curable compositions of this invention, More preferably, it is 10-30 mass parts. When the blending amount of the (meth) acrylate having a carboxyl group is 5 parts by mass or more, the adhesiveness that is a feature of the composition of the present invention becomes better. On the other hand, when the amount is 50 parts by mass or less, an increase in the viscosity of the ink can be suppressed and good printability can be obtained.
本発明の硬化型組成物は、このような（Ａ）成分、（Ｂ）成分、及び、後述する（Ｄ）成分の組み合わせにより、プラスチック基板と導体回路金属の双方に対して優れた密着性を有し、例えばプリント配線板用のレジストインキ（エッチングレジストインキ、ソルダーレジストインキ、メッキレジストインキ）として、優れた基板保護性能を発揮する。また、低露光量であっても、はんだ耐熱性等優れた硬化塗膜特性を発揮する。 The curable composition of the present invention has excellent adhesion to both the plastic substrate and the conductor circuit metal by a combination of the component (A), the component (B), and the component (D) described later. For example, as a resist ink (etching resist ink, solder resist ink, plating resist ink) for printed wiring boards, it exhibits excellent substrate protection performance. Moreover, even if it is a low exposure amount, it exhibits excellent cured film properties such as solder heat resistance.
［（Ｃ）光重合開始剤］
（Ｃ）光重合開始剤としては、特に限定されるものではなく、例えば光ラジカル重合開始剤を用いることができる。この光ラジカル重合開始剤としては、光、レーザー、電子線等によりラジカルを発生し、ラジカル重合反応を開始させられる化合物であればいずれも用いることができる。
[(C) Photopolymerization initiator]
(C) It does not specifically limit as a photoinitiator, For example, a photoradical polymerization initiator can be used. As this radical photopolymerization initiator, any compound can be used as long as it generates radicals by light, laser, electron beam or the like and can initiate radical polymerization reaction.
（Ｃ）光重合開始剤としては、例えば、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル等のベンゾインとベンゾインアルキルエーテル類；２−ヒドロキシ−２−メチル−１−フェニル−プロパン−１−オン等のアルキルフェノン系；アセトフェノン、２，２−ジメトキシ−２−フェニルアセトフェノン、２，２−ジエトキシ−２−フェニルアセトフェノン、１，１−ジクロロアセトフェノン等のアセトフェノン類；２−メチル−１−［４−（メチルチオ）フェニル］−２−モルホリノプロパン−１−オン、２−ベンジル−２−ジメチルアミノ−１−（４−モルホリノフェニル）−ブタン−１−オン、Ｎ，Ｎ−ジメチルアミノアセトフェノン等のアミノアセトフェノン類；２−メチルアントラキノン、２−エチルアントラキノン、２−ｔ−ブチルアントラキノン、１−クロロアントラキノン等のアントラキノン類；２，４−ジメチルチオキサントン、２，４−ジエチルチオキサントン、２−クロロチオキサントン、２，４−ジイソプロピルチオキサントン等のチオキサントン類；アセトフェノンジメチルケタール、ベンジルジメチルケタール等のケタール類；２，４，５−トリアリールイミダゾール二量体；リボフラビンテトラブチレート；２−メルカプトベンゾイミダゾール、２−メルカプトベンゾオキサゾール、２−メルカプトベンゾチアゾール等のチオール化合物；２，４，６−トリス−ｓ−トリアジン、２，２，２−トリブロモエタノール、トリブロモメチルフェニルスルホン等の有機ハロゲン化合物；ベンゾフェノン、４，４’−ビスジエチルアミノベンゾフェノン等のベンゾフェノン類又はキサントン類；２，４，６−トリメチルベンゾイルジフェニルホスフィンオキサイド、ビス（２，４，６−トリメチルベンゾイル）−フェニルフォスフィンオキサイド等のアシルフォスフィンオキサイド系；ビス（シクロペンタジエニル）−ジ−フェニル−チタニウム、ビス（シクロペンタジエニル）−ジ−クロロ−チタニウム、ビス（シクロペンタジエニル）−ビス（２，３，４，５，６ペンタフルオロフェニル）チタニウム、ビス（シクロペンタジエニル）−ビス（２、６−ジフルオロ−３−（ピロール−１−イル）フェニル）チタニウムなどのチタノセン類などが挙げられる。 (C) Examples of the photopolymerization initiator include benzoin and benzoin alkyl ethers such as benzoin, benzoin methyl ether, benzoin ethyl ether, and benzoin isopropyl ether; 2-hydroxy-2-methyl-1-phenyl-propane-1- Alkylphenones such as ON; acetophenones such as acetophenone, 2,2-dimethoxy-2-phenylacetophenone, 2,2-diethoxy-2-phenylacetophenone, 1,1-dichloroacetophenone; 2-methyl-1- [4 Amino such as-(methylthio) phenyl] -2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butan-1-one, N, N-dimethylaminoacetophenone Acetophenones; 2-methyla Anthraquinones such as traquinone, 2-ethylanthraquinone, 2-t-butylanthraquinone, 1-chloroanthraquinone; 2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2-chlorothioxanthone, 2,4-diisopropylthioxanthone, etc. Thioxanthones; Ketals such as acetophenone dimethyl ketal and benzyl dimethyl ketal; 2,4,5-triarylimidazole dimer; Riboflavin tetrabutyrate; 2-mercaptobenzimidazole, 2-mercaptobenzoxazole, 2-mercaptobenzothiazole Thiol compounds such as 2,4,6-tris-s-triazine, 2,2,2-tribromoethanol, tribromomethylphenylsulfone and other organic halogen compounds; benzopheno Benzophenones such as 4,4′-bisdiethylaminobenzophenone or xanthones; acylphosphine such as 2,4,6-trimethylbenzoyldiphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide Oxides; bis (cyclopentadienyl) -di-phenyl-titanium, bis (cyclopentadienyl) -di-chloro-titanium, bis (cyclopentadienyl) -bis (2,3,4,5,6) And titanocenes such as pentafluorophenyl) titanium and bis (cyclopentadienyl) -bis (2,6-difluoro-3- (pyrrol-1-yl) phenyl) titanium.
これら公知慣用の光重合開始剤は、単独で又は２種類以上の混合物として使用でき、さらにはＮ，Ｎ−ジメチルアミノ安息香酸エチルエステル、Ｎ，Ｎ−ジメチルアミノ安息香酸イソアミルエステル、ペンチル−４−ジメチルアミノベンゾエート、トリエチルアミン、トリエタノールアミン等の三級アミン類などの光開始助剤を加えることができる。 These known and commonly used photopolymerization initiators can be used alone or as a mixture of two or more thereof. Further, N, N-dimethylaminobenzoic acid ethyl ester, N, N-dimethylaminobenzoic acid isoamyl ester, pentyl-4- Photoinitiator aids such as tertiary amines such as dimethylaminobenzoate, triethylamine, triethanolamine can be added.
市販されているものとしては、イルガキュア２６１、１８４、３６９、６５１、５００、８１９、９０７、７８４、２９５９、ダロキュア１１１６、１１７３、ＣＧＩ１７００、ＣＧＩ１７５０、ＣＧＩ１８５０、ＣＧ−２４−６１、ルシリンＴＰＯ、ＣＧＩ−７８４（以上、ＢＡＳＦジャパン社製の商品名）、ＤＡＩＣＡＴＩＩ（ダイセル化学工業社製の商品名）、ＵＶＡＣ１５９１（ダイセル・ユーシービー社製の商品名）、ロードシル フォトイニシエーター２０７４（ローディア社製の商品名）、ユベクリルＰ３６（ＵＣＢ社製の商品名）、エザキュアーＫＩＰ１５０、ＫＩＰ６５ＬＴ、ＫＩＰ１００Ｆ、ＫＴ３７、ＫＴ５５、ＫＴＯ４６、ＫＩＰ７５／Ｂ、ＯＮＥ（フラテツリ・ランベルティ社製の商品名）等が挙げられる。 As commercially available products, Irgacure 261, 184, 369, 651, 500, 819, 907, 784, 2959, Darocur 1116, 1173, CGI 1700, CGI 1750, CGI 1850, CG-24-61, Lucyrin TPO, CGI-784 (Above, product name manufactured by BASF Japan), DAICATII (product name manufactured by Daicel Chemical Industries), UVAC1591 (product name manufactured by Daicel UCB), Rhodesil Photoinitiator 2074 (product name manufactured by Rhodia) , Ubekrill P36 (trade name, manufactured by UCB), Ezacure KIP150, KIP65LT, KIP100F, KT37, KT55, KTO46, KIP75 / B, ONE (trade names, manufactured by Fratelli Lamberti), and the like.
（Ｃ）光重合開始剤の配合割合は、本発明の硬化型組成物１００質量部中、０．５〜１０質量部の範囲が好ましい。 (C) As for the mixture ratio of a photoinitiator, the range of 0.5-10 mass parts is preferable in 100 mass parts of curable compositions of this invention.
［（Ｄ）熱硬化成分］
本発明の硬化型組成物には、（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）を加えることにより密着性や耐熱性が向上することが期待できる。本発明に用いられる熱硬化成分としては、メラミン樹脂、ベンゾグアナミン樹脂、メラミン誘導体、ベンゾグアナミン誘導体等のアミノ樹脂、ブロックイソシアネート化合物、シクロカーボネート化合物、環状（チオ）エーテル基を有する熱硬化成分、ビスマレイミド、カルボジイミド樹脂等の公知の熱硬化性樹脂が使用できる。また、密着性や耐熱性がより向上することより、カルボキシル基と反応しうる官能基を少なくとも２つ有する化合物が好ましい。カルボキシル基と反応しうる官能基とは（チオ）エーテル基、イソシアネート基、水酸基、アミノ基、チオール基、オキサゾリン基などが挙げられる。特に好ましいのは、カルボキシル基との反応性の高さや、密着性の高さからエポキシ化合物である。
[(D) Thermosetting component]
By adding (D) a thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group) to the curable composition of the present invention, it can be expected that adhesion and heat resistance are improved. Examples of thermosetting components used in the present invention include amino resins such as melamine resins, benzoguanamine resins, melamine derivatives, and benzoguanamine derivatives, blocked isocyanate compounds, cyclocarbonate compounds, thermosetting components having a cyclic (thio) ether group, bismaleimide, Known thermosetting resins such as carbodiimide resins can be used. In addition, a compound having at least two functional groups capable of reacting with a carboxyl group is preferable because adhesion and heat resistance are further improved. Examples of the functional group capable of reacting with a carboxyl group include a (thio) ether group, an isocyanate group, a hydroxyl group, an amino group, a thiol group, and an oxazoline group. Particularly preferred is an epoxy compound because of its high reactivity with the carboxyl group and high adhesion.
上記の分子中に複数の環状（チオ）エーテル基を有する熱硬化成分は、分子中に３、４または５員環の環状（チオ）エーテル基のいずれか一方または２種類の基を複数有する化合物であり、例えば、分子内に複数のエポキシ基を有する化合物、すなわち多官能エポキシ化合物、分子内に複数のオキセタニル基を有する化合物、すなわち多官能オキセタン化合物、分子内に複数のチオエーテル基を有する化合物、すなわちエピスルフィド樹脂等が挙げられる。 The thermosetting component having a plurality of cyclic (thio) ether groups in the molecule is a compound having any one of the three, four or five-membered cyclic (thio) ether groups in the molecule or a plurality of two types of groups. For example, a compound having a plurality of epoxy groups in the molecule, that is, a polyfunctional epoxy compound, a compound having a plurality of oxetanyl groups in the molecule, that is, a polyfunctional oxetane compound, a compound having a plurality of thioether groups in the molecule, That is, episulfide resin etc. are mentioned.
上記多官能エポキシ化合物としては、ＡＤＥＫＡ社製のアデカサイザーＯ−１３０Ｐ、アデカサイザーＯ−１８０Ａ、アデカサイザーＤ−３２、アデカサイザーＤ−５５等のエポキシ化植物油；三菱化学社製のｊＥＲ８２８、ｊＥＲ８３４、ｊＥＲ１００１、ｊＥＲ１００４、ダイセル化学工業社製のＥＨＰＥ３１５０、ＤＩＣ社製のエピクロン８４０、エピクロン８５０、エピクロン１０５０、エピクロン２０５５、東都化成社製のエポトートＹＤ−０１１、ＹＤ−０１３、ＹＤ−１２７、ＹＤ−１２８、ダウケミカル社製のＤ．Ｅ．Ｒ．３１７、Ｄ．Ｅ．Ｒ．３３１、Ｄ．Ｅ．Ｒ．６６１、Ｄ．Ｅ．Ｒ．６６４、住友化学工業社製のスミ−エポキシＥＳＡ−０１１、ＥＳＡ−０１４、ＥＬＡ−１１５、ＥＬＡ−１２８、旭化成工業社製のＡ．Ｅ．Ｒ．３３０、Ａ．Ｅ．Ｒ．３３１、Ａ．Ｅ．Ｒ．６６１、Ａ．Ｅ．Ｒ．６６４等（何れも商品名）のビスフェノールＡ型エポキシ樹脂；ＹＤＣ−１３１２、ハイドロキノン型エポキシ樹脂、ＹＳＬＶ−８０ＸＹビスフェノール型エポキシ樹脂、ＹＳＬＶ−１２０ＴＥチオエーテル型エポキシ樹脂（いずれも東都化成社製）；三菱化学社製のｊＥＲＹＬ９０３、ＤＩＣ社製のエピクロン１５２、エピクロン１６５、東都化成社製のエポトートＹＤＢ−４００、ＹＤＢ−５００、ダウケミカル社製のＤ．Ｅ．Ｒ．５４２、住友化学工業社製のスミ−エポキシＥＳＢ−４００、ＥＳＢ−７００、旭化成工業社製のＡ．Ｅ．Ｒ．７１１、Ａ．Ｅ．Ｒ．７１４等（何れも商品名）のブロム化エポキシ樹脂；三菱化学社製のｊＥＲ１５２、ｊＥＲ１５４、ダウケミカル社製のＤ．Ｅ．Ｎ．４３１、Ｄ．Ｅ．Ｎ．４３８、ＤＩＣ社製のエピクロンＮ−７３０、エピクロンＮ−７７０、エピクロンＮ−８６５、東都化成社製のエポトートＹＤＣＮ−７０１、ＹＤＣＮ−７０４、日本化薬社製のＥＰＰＮ−２０１、ＥＯＣＮ−１０２５、ＥＯＣＮ−１０２０、ＥＯＣＮ−１０４Ｓ、ＲＥ−３０６、住友化学工業社製のスミ−エポキシＥＳＣＮ−１９５Ｘ、ＥＳＣＮ−２２０、旭化成工業社製のＡ．Ｅ．Ｒ．ＥＣＮ−２３５、ＥＣＮ−２９９等（何れも商品名）のノボラック型エポキシ樹脂；日本化薬社製ＮＣ−３０００、ＮＣ−３１００等のビフェノールノボラック型エポキシ樹脂；ＤＩＣ社製のエピクロン８３０、三菱化学社製ｊＥＲ８０７、東都化成社製のエポトートＹＤＦ−１７０、ＹＤＦ−１７５、ＹＤＦ−２００４等（何れも商品名）のビスフェノールＦ型エポキシ樹脂；東都化成社製のエポトートＳＴ−２００４、ＳＴ−２００７、ＳＴ−３０００（商品名）等の水添ビスフェノールＡ型エポキシ樹脂；三菱化学社製のｊＥＲ６０４、東都化成社製のエポトートＹＨ−４３４、住友化学工業社製のスミ−エポキシＥＬＭ−１２０等（何れも商品名）のグリシジルアミン型エポキシ樹脂；ヒダントイン型エポキシ樹脂；ダイセル化学工業社製のセロキサイド２０２１等（何れも商品名）の脂環式エポキシ樹脂；三菱化学社製のＹＬ−９３３、ダウケミカル社製のＴ．Ｅ．Ｎ．、ＥＰＰＮ−５０１、ＥＰＰＮ−５０２等（何れも商品名）のトリヒドロキシフェニルメタン型エポキシ樹脂；三菱化学社製のＹＬ−６０５６、ＹＸ−４０００、ＹＬ−６１２１（何れも商品名）等のビキシレノール型もしくはビフェノール型エポキシ樹脂またはそれらの混合物；日本化薬社製ＥＢＰＳ−２００、ＡＤＥＫＡ社製ＥＰＸ−３０、ＤＩＣ社製のＥＸＡ−１５１４（商品名）等のビスフェノールＳ型エポキシ樹脂；三菱化学社製のｊＥＲ１５７Ｓ（商品名）等のビスフェノールＡノボラック型エポキシ樹脂；三菱化学社製のｊＥＲＹＬ−９３１等（何れも商品名）のテトラフェニロールエタン型エポキシ樹脂；日産化学工業社製のＴＥＰＩＣ等（何れも商品名）の複素環式エポキシ樹脂；日本油脂社製ブレンマーＤＧＴ等のジグリシジルフタレート樹脂；東都化成社製ＺＸ−１０６３等のテトラグリシジルキシレノイルエタン樹脂；新日鐵化学社製ＥＳＮ−１９０、ＥＳＮ−３６０、ＤＩＣ社製ＨＰ−４０３２、ＥＸＡ−４７５０、ＥＸＡ−４７００等のナフタレン基含有エポキシ樹脂；ＤＩＣ社製ＨＰ−７２００、ＨＰ−７２００Ｈ等のジシクロペンタジエン骨格を有するエポキシ樹脂；日本油脂社製ＣＰ−５０Ｓ、ＣＰ−５０Ｍ等のグリシジルメタアクリレート共重合系エポキシ樹脂；さらにシクロヘキシルマレイミドとグリシジルメタアクリレートの共重合エポキシ樹脂；エポキシ変性のポリブタジエンゴム誘導体（例えばダイセル化学工業製ＰＢ−３６００等）、ＣＴＢＮ変性エポキシ樹脂（例えば東都化成社製のＹＲ−１０２、ＹＲ−４５０等）等が挙げられるが、これらに限られるものではない。これらのエポキシ樹脂は、単独でまたは２種以上を組み合わせて用いることができる。これらの中でも特にノボラック型エポキシ樹脂、ビキシレノール型エポキシ樹脂、ビフェノール型エポキシ樹脂、ビフェノールノボラック型エポキシ樹脂、ナフタレン型エポキシ樹脂またはそれらの混合物が好ましい。また、反応性の高さや密着性の高さがより顕著となることから、結晶性を有するエポキシ化合物が好ましい。結晶性を有するエポキシ化合物の市販品としては、ＹＸ−４０００（三菱化学社製）などが挙げられる。 Examples of the polyfunctional epoxy compound include epoxidized vegetable oils such as Adekasizer O-130P, Adekasizer O-180A, Adekasizer D-32, and Adekasizer D-55 manufactured by ADEKA; jER828 and jER834 manufactured by Mitsubishi Chemical jER1001, jER1004, EHPE3150 manufactured by Daicel Chemical Industries, Epicron 840, Epicron 850, Epicron 1050, Epicron 1050, Epitolon 2055, Epototo YD-011, YD-013, YD-127, YD-128 manufactured by Tohto Kasei Co., Ltd. D. Chemicals manufactured by Dow Chemical Company. E. R. 317, D.E. E. R. 331, D.D. E. R. 661, D.E. E. R. 664, Sumitomo Epoxy ESA-011, ESA-014, ELA-115, ELA-128, manufactured by Sumitomo Chemical Co., Ltd., A.A. E. R. 330, A.I. E. R. 331, A.I. E. R. 661, A.I. E. R. 664phenol (all trade names) bisphenol A type epoxy resin; YDC-1312, hydroquinone type epoxy resin, YSLV-80XY bisphenol type epoxy resin, YSLV-120TE thioether type epoxy resin (all manufactured by Tohto Kasei Co., Ltd.); JERYL903 manufactured by DIC, Epicron 152, Epicron 165 manufactured by DIC, Epototo YDB-400, YDB-500 manufactured by Tohto Kasei Co., Ltd., D.C. E. R. 542, Sumitomo Epoxy ESB-400, ESB-700 manufactured by Sumitomo Chemical Co., Ltd., A.A. E. R. 711, A.I. E. R. Brominated epoxy resins such as 714 (both trade names); jER152 and jER154 manufactured by Mitsubishi Chemical Corporation, and D.C. E. N. 431, D.D. E. N. 438, Epicron N-730, Epicron N-770, Epicron N-865 manufactured by DIC, Epototo YDCN-701, YDCN-704 manufactured by Tohto Kasei Co., Ltd., EPPN-201, EOCN-1025, EOCN manufactured by Nippon Kayaku Co., Ltd. -1020, EOCN-104S, RE-306, Sumitomo Epoxy ESCN-195X, ESCN-220, manufactured by Sumitomo Chemical Co., Ltd. E. R. Novolak type epoxy resins such as ECN-235 and ECN-299 (both are trade names); biphenol novolac type epoxy resins such as NC-3000 and NC-3100 manufactured by Nippon Kayaku; Epicron 830 manufactured by DIC, Mitsubishi Chemical JER807 manufactured by Toto Kasei Co., Ltd. Etototo YDF-170, YDF-175, YDF-2004, etc. (all trade names) bisphenol F type epoxy resin; Toto Kasei Co., Ltd. Epototo ST-2004, ST-2007, ST- Hydrogenated bisphenol A type epoxy resin such as 3000 (trade name); jER604 manufactured by Mitsubishi Chemical Co., Ltd., Epotot YH-434 manufactured by Tohto Kasei Co., Ltd., Sumi-epoxy ELM-120 manufactured by Sumitomo Chemical Co., Ltd. ) Glycidylamine type epoxy resin; hydantoin type epoxy resin; Alicyclic epoxy resins GMBH made CELLOXIDE 2021, etc. (all trade names); manufactured by Mitsubishi Chemical Corporation YL-933, Dow Chemical Co. of T. E. N. , EPPN-501, EPPN-502, etc. (all trade names) trihydroxyphenylmethane type epoxy resin; Mitsubishi Chemical Corporation YL-6056, YX-4000, YL-6121 (all trade names) Type or biphenol type epoxy resin or a mixture thereof; Nippon Kayaku EBPS-200, ADEKA EPX-30, DIC EXA-1514 (trade name), etc .; bisphenol S type epoxy resin; Bisphenol A novolac type epoxy resin such as jER157S (trade name); tetraphenylolethane type epoxy resin such as jERYL-931 (all trade name) made by Mitsubishi Chemical; TEPIC made by Nissan Chemical Industries (all) Product name) heterocyclic epoxy resin; Jig such as Bremer DGT manufactured by NOF Corporation Shidyl phthalate resin; Tetraglycidyl xylenoyl ethane resin such as ZX-1063 manufactured by Tohto Kasei Co., Ltd .; ESN-190, ESN-360 manufactured by Nippon Steel Chemical Co., Ltd. HP-4032, EXA-4750, EXA-4700 manufactured by DIC Naphthalene group-containing epoxy resin; epoxy resin having a dicyclopentadiene skeleton such as HP-7200 and HP-7200H manufactured by DIC; glycidyl methacrylate copolymer epoxy resin such as CP-50S and CP-50M manufactured by NOF Corporation; Further, a copolymerized epoxy resin of cyclohexylmaleimide and glycidyl methacrylate; an epoxy-modified polybutadiene rubber derivative (for example, PB-3600 manufactured by Daicel Chemical Industries), a CTBN-modified epoxy resin (for example, YR-102, YR-450 manufactured by Toto Kasei Co., Ltd.) ) Etc. That is, the present invention is not limited to these. These epoxy resins can be used alone or in combination of two or more. Among these, novolak-type epoxy resins, bixylenol-type epoxy resins, biphenol-type epoxy resins, biphenol novolac-type epoxy resins, naphthalene-type epoxy resins or mixtures thereof are particularly preferable. In addition, an epoxy compound having crystallinity is preferable since the high reactivity and the high adhesiveness become more remarkable. YX-4000 (made by Mitsubishi Chemical Corporation) etc. are mentioned as a commercial item of the epoxy compound which has crystallinity.
多官能オキセタン化合物としては、例えば、ビス［（３−メチル−３−オキセタニルメトキシ）メチル］エーテル、ビス［（３−エチル−３−オキセタニルメトキシ）メチル］エーテル、１，４−ビス［（３−メチル−３−オキセタニルメトキシ）メチル］ベンゼン、１，４−ビス［（３−エチル−３−オキセタニルメトキシ）メチル］ベンゼン、（３−メチル−３−オキセタニル）メチルアクリレート、（３−エチル−３−オキセタニル）メチルアクリレート、（３−メチル−３−オキセタニル）メチルメタクリレート、（３−エチル−３−オキセタニル）メチルメタクリレートやそれらのオリゴマーまたは共重合体等の多官能オキセタン類の他、オキセタンアルコールとノボラック樹脂、ポリ（ｐ−ヒドロキシスチレン）、カルド型ビスフェノール類、カリックスアレーン類、カリックスレゾルシンアレーン類、またはシルセスキオキサン等の水酸基を有する樹脂とのエーテル化物等が挙げられる。その他、オキセタン環を有する不飽和モノマーとアルキル（メタ）アクリレートとの共重合体等も挙げられる。 Examples of the polyfunctional oxetane compound include bis [(3-methyl-3-oxetanylmethoxy) methyl] ether, bis [(3-ethyl-3-oxetanylmethoxy) methyl] ether, 1,4-bis [(3- Methyl-3-oxetanylmethoxy) methyl] benzene, 1,4-bis [(3-ethyl-3-oxetanylmethoxy) methyl] benzene, (3-methyl-3-oxetanyl) methyl acrylate, (3-ethyl-3- In addition to polyfunctional oxetanes such as oxetanyl) methyl acrylate, (3-methyl-3-oxetanyl) methyl methacrylate, (3-ethyl-3-oxetanyl) methyl methacrylate and oligomers or copolymers thereof, oxetane alcohol and novolak resin , Poly (p-hydroxystyrene), cardo-type bis Phenol ethers, calixarenes, calix resorcin arenes or etherified products such as the resin having a hydroxyl group such as silsesquioxane and the like. In addition, a copolymer of an unsaturated monomer having an oxetane ring and an alkyl (meth) acrylate is also included.
分子中に複数の環状チオエーテル基を有する化合物としては、例えば、三菱化学社製のビスフェノールＡ型エピスルフィド樹脂 ＹＬ７０００等が挙げられる。また、同様の合成方法を用いて、ノボラック型エポキシ樹脂のエポキシ基の酸素原子を硫黄原子に置き換えたエピスルフィド樹脂なども用いることができる。 Examples of the compound having a plurality of cyclic thioether groups in the molecule include bisphenol A type episulfide resin YL7000 manufactured by Mitsubishi Chemical Corporation. Moreover, episulfide resin etc. which replaced the oxygen atom of the epoxy group of the novolak-type epoxy resin with the sulfur atom using the same synthesis method can be used.
メラミン誘導体、ベンゾグアナミン誘導体等のアミノ樹脂としては、例えばメチロールメラミン化合物、メチロールベンゾグアナミン化合物、メチロールグリコールウリル化合物およびメチロール尿素化合物等がある。さらに、アルコキシメチル化メラミン化合物、アルコキシメチル化ベンゾグアナミン化合物、アルコキシメチル化グリコールウリル化合物およびアルコキシメチル化尿素化合物は、それぞれのメチロールメラミン化合物、メチロールベンゾグアナミン化合物、メチロールグリコールウリル化合物およびメチロール尿素化合物のメチロール基をアルコキシメチル基に変換することにより得られる。このアルコキシメチル基の種類については特に限定されるものではなく、例えばメトキシメチル基、エトキシメチル基、プロポキシメチル基、ブトキシメチル基等とすることができる。特に人体や環境に優しいホルマリン濃度が０．２％以下のメラミン誘導体が好ましい。 Examples of amino resins such as melamine derivatives and benzoguanamine derivatives include methylol melamine compounds, methylol benzoguanamine compounds, methylol glycoluril compounds, and methylol urea compounds. Furthermore, the alkoxymethylated melamine compound, the alkoxymethylated benzoguanamine compound, the alkoxymethylated glycoluril compound and the alkoxymethylated urea compound have the methylol group of the respective methylolmelamine compound, methylolbenzoguanamine compound, methylolglycoluril compound and methylolurea compound. Obtained by conversion to an alkoxymethyl group. The type of the alkoxymethyl group is not particularly limited and can be, for example, a methoxymethyl group, an ethoxymethyl group, a propoxymethyl group, a butoxymethyl group, or the like. In particular, a melamine derivative having a formalin concentration which is friendly to the human body and the environment is preferably 0.2% or less.
これらの市販品としては、例えば、サイメル３００、同３０１、同３０３、同３７０、同３２５、同３２７、同７０１、同２６６、同２６７、同２３８、同１１４１、同２７２、同２０２、同１１５６、同１１５８、同１１２３、同１１７０、同１１７４、同ＵＦＲ６５、同３００（いずれも三井サイアナミッド社製）、ニカラックＭｘ−７５０、同Ｍｘ−０３２、同Ｍｘ−２７０、同Ｍｘ−２８０、同Ｍｘ−２９０、同Ｍｘ−７０６、同Ｍｘ−７０８、同Ｍｘ−４０、同Ｍｘ−３１、同Ｍｓ−１１、同Ｍｗ−３０、同Ｍｗ−３０ＨＭ、同Ｍｗ−３９０、同Ｍｗ−１００ＬＭ、同Ｍｗ−７５０ＬＭ、（いずれも三和ケミカル社製）等を挙げることができる。このような熱硬化成分は１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。 Examples of these commercially available products include Cymel 300, 301, 303, 370, 325, 327, 701, 266, 267, 238, 1141, 272, 202, 1156. 1158, 1123, 1170, 1174, UFR65, 300 (all manufactured by Mitsui Cyanamid), Nicalak Mx-750, Mx-032, Mx-270, Mx-280, Mx- 290, Mx-706, Mx-708, Mx-40, Mx-31, Ms-11, Mw-30, Mw-30HM, Mw-390, Mw-100LM, Mw- 750LM (all manufactured by Sanwa Chemical Co., Ltd.). Such a thermosetting component may be used individually by 1 type, and may be used in combination of 2 or more type.
イソシアネート化合物、ブロックイソシアネート化合物は、１分子内に複数のイソシアネート基またはブロック化イソシアネート基を有する化合物である。このような１分子内に複数のイソシアネート基またはブロック化イソシアネート基を有する化合物としては、ポリイソシアネート化合物、またはブロックイソシアネート化合物等が挙げられる。なお、ブロック化イソシアネート基とは、イソシアネート基がブロック剤との反応により保護されて一時的に不活性化された基であり、所定温度に加熱されたときにそのブロック剤が解離してイソシアネート基が生成する。上記ポリイソシアネート化合物、またはブロックイソシアネート化合物を加えることにより硬化性および得られる硬化物の強靭性を向上することが確認された。 An isocyanate compound and a blocked isocyanate compound are compounds having a plurality of isocyanate groups or blocked isocyanate groups in one molecule. Examples of such a compound having a plurality of isocyanate groups or blocked isocyanate groups in one molecule include polyisocyanate compounds or blocked isocyanate compounds. The blocked isocyanate group is a group in which the isocyanate group is protected by the reaction with the blocking agent and temporarily inactivated, and the blocking agent is dissociated when heated to a predetermined temperature. Produces. It was confirmed that the curability and toughness of the resulting cured product were improved by adding the polyisocyanate compound or the blocked isocyanate compound.
このようなポリイソシアネート化合物としては、例えば、芳香族ポリイソシアネート、脂肪族ポリイソシアネートまたは脂環式ポリイソシアネートが用いられる。
芳香族ポリイソシアネートの具体例としては、例えば、４，４’−ジフェニルメタンジイソシアネート、２，４−トリレンジイソシアネート、２，６−トリレンジイソシアネート、ナフタレン−１，５−ジイソシアネート、ｏ−キシリレンジイソシアネート、ｍ−キシリレンジイソシアネートおよび２，４−トリレンダイマー等が挙げられる。
As such a polyisocyanate compound, for example, aromatic polyisocyanate, aliphatic polyisocyanate or alicyclic polyisocyanate is used.
Specific examples of the aromatic polyisocyanate include, for example, 4,4′-diphenylmethane diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, naphthalene-1,5-diisocyanate, o-xylylene diisocyanate, Examples thereof include m-xylylene diisocyanate and 2,4-tolylene dimer.
脂肪族ポリイソシアネートの具体例としては、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、メチレンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、４，４−メチレンビス（シクロヘキシルイソシアネート）およびイソホロンジイソシアネート等が挙げられる。 Specific examples of the aliphatic polyisocyanate include tetramethylene diisocyanate, hexamethylene diisocyanate, methylene diisocyanate, trimethylhexamethylene diisocyanate, 4,4-methylenebis (cyclohexyl isocyanate), and isophorone diisocyanate.
脂環式ポリイソシアネートの具体例としてはビシクロヘプタントリイソシアネートが挙げられる。並びに先に挙げられたイソシアネート化合物のアダクト体、ビューレット体およびイソシアヌレート体等が挙げられる。 Specific examples of the alicyclic polyisocyanate include bicycloheptane triisocyanate. In addition, adducts, burettes and isocyanurates of the above-mentioned isocyanate compounds can be used.
ブロックイソシアネート化合物としては、イソシアネート化合物とイソシアネートブロック剤との付加反応生成物が用いられる。ブロック剤と反応し得るイソシアネート化合物としては、例えば、上述のポリイソシアネート化合物等が挙げられる。 As the blocked isocyanate compound, an addition reaction product of an isocyanate compound and an isocyanate blocking agent is used. As an isocyanate compound which can react with a blocking agent, the above-mentioned polyisocyanate compound etc. are mentioned, for example.
イソシアネートブロック剤としては、例えば、フェノール、クレゾール、キシレノール、クロロフェノールおよびエチルフェノール等のフェノール系ブロック剤；ε−カプロラクタム、δ−パレロラクタム、γ−ブチロラクタムおよびβ−プロピオラクタム等のラクタム系ブロック剤；アセト酢酸エチルおよびアセチルアセトン等の活性メチレン系ブロック剤；メタノール、エタノール、プロパノール、ブタノール、アミルアルコール、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテル、ベンジルエーテル、グリコール酸メチル、グリコール酸ブチル、ジアセトンアルコール、乳酸メチルおよび乳酸エチル等のアルコール系ブロック剤；ホルムアルデヒドキシム、アセトアルドキシム、アセトキシム、メチルエチルケトキシム、ジアセチルモノオキシム、シクロヘキサンオキシム等のオキシム系ブロック剤；ブチルメルカプタン、ヘキシルメルカプタン、ｔ−ブチルメルカプタン、チオフェノール、メチルチオフェノール、エチルチオフェノール等のメルカプタン系ブロック剤；酢酸アミド、ベンズアミド等の酸アミド系ブロック剤；コハク酸イミドおよびマレイン酸イミド等のイミド系ブロック剤；キシリジン、アニリン、ブチルアミン、ジブチルアミン等のアミン系ブロック剤；イミダゾール、２−エチルイミダゾール等のイミダゾール系ブロック剤；メチレンイミンおよびプロピレンイミン等のイミン系ブロック剤等が挙げられる。 Examples of the isocyanate blocking agent include phenolic blocking agents such as phenol, cresol, xylenol, chlorophenol and ethylphenol; lactam blocking agents such as ε-caprolactam, δ-palerolactam, γ-butyrolactam and β-propiolactam; Active methylene blocking agents such as ethyl acetoacetate and acetylacetone; methanol, ethanol, propanol, butanol, amyl alcohol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, propylene glycol monomethyl ether, benzyl Ether, methyl glycolate, butyl glycolate, diacetone alcohol, milk Alcohol-based blocking agents such as methyl and ethyl lactate; oxime-based blocking agents such as formaldehyde oxime, acetaldoxime, acetoxime, methylethyl ketoxime, diacetyl monooxime, cyclohexane oxime; butyl mercaptan, hexyl mercaptan, t-butyl mercaptan, thiophenol, Mercaptan block agents such as methylthiophenol and ethylthiophenol; Acid amide block agents such as acetic acid amide and benzamide; Imide block agents such as succinimide and maleic imide; Amines such as xylidine, aniline, butylamine and dibutylamine Blocking agents; imidazole blocking agents such as imidazole and 2-ethylimidazole; imine blocking agents such as methyleneimine and propyleneimine Etc.
ブロックイソシアネート化合物は市販のものであってもよく、例えば、スミジュールＢＬ−３１７５、ＢＬ−４１６５、ＢＬ−１１００、ＢＬ−１２６５、デスモジュールＴＰＬＳ−２９５７、ＴＰＬＳ−２０６２、ＴＰＬＳ−２０７８、ＴＰＬＳ−２１１７、デスモサーム２１７０、デスモサーム２２６５（いずれも住友バイエルウレタン社製）、コロネート２５１２、コロネート２５１３、コロネート２５２０（いずれも日本ポリウレタン工業社製）、Ｂ−８３０、Ｂ−８１５、Ｂ−８４６、Ｂ−８７０、Ｂ−８７４、Ｂ−８８２（いずれも三井武田ケミカル社製）、ＴＰＡ−Ｂ８０Ｅ、１７Ｂ−６０ＰＸ、Ｅ４０２−Ｂ８０Ｔ（いずれも旭化成ケミカルズ社製）等が挙げられる。なお、スミジュールＢＬ−３１７５、ＢＬ−４２６５はブロック剤としてメチルエチルオキシムを用いて得られるものである。このような１分子内に複数のイソシアネート基、またはブロック化イソシアネート基を有する化合物は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。 The block isocyanate compound may be commercially available, for example, Sumidur BL-3175, BL-4165, BL-1100, BL-1265, Desmodur TPLS-2957, TPLS-2062, TPLS-2078, TPLS-2117. , Desmotherm 2170, Desmotherm 2265 (all manufactured by Sumitomo Bayer Urethane Co., Ltd.), Coronate 2512, Coronate 2513, Coronate 2520 (all manufactured by Nippon Polyurethane Industry Co., Ltd.), B-830, B-815, B-846, B-870, B-874, B-882 (all manufactured by Mitsui Takeda Chemical Co., Ltd.), TPA-B80E, 17B-60PX, E402-B80T (all manufactured by Asahi Kasei Chemicals Co., Ltd.) and the like. Sumijoules BL-3175 and BL-4265 are obtained using methyl ethyl oxime as a blocking agent. Such a compound having a plurality of isocyanate groups or blocked isocyanate groups in one molecule may be used alone or in combination of two or more.
このような（Ｄ）熱硬化成分の配合量は、本発明の硬化型組成物１００質量部中、１〜３０質量部が好ましい。配合量が１質量部以上であれば、十分な塗膜の強靭性、耐熱性が得られる。一方、３０質量部以下であれば、保存安定性が低下することを抑制できる。 As for the compounding quantity of such (D) thermosetting component, 1-30 mass parts is preferable in 100 mass parts of curable compositions of this invention. When the blending amount is 1 part by mass or more, sufficient toughness and heat resistance of the coating film can be obtained. On the other hand, if it is 30 mass parts or less, it can suppress that storage stability falls.
（２官能（メタ）アクリレート化合物）
本発明のプリント配線板用硬化型組成物は、更に、２官能（メタ）アクリレート化合物（カルボキシル基を有するものを除く）を含むことが好ましい。２官能（メタ）アクリレート化合物（カルボキシル基を有するものを除く）を添加することにより、プリント配線板用硬化型組成物における各成分の相溶性をさらに向上させることができる。
(Bifunctional (meth) acrylate compound)
The curable composition for printed wiring boards of the present invention preferably further contains a bifunctional (meth) acrylate compound (excluding those having a carboxyl group). By adding a bifunctional (meth) acrylate compound (excluding those having a carboxyl group), the compatibility of each component in the curable composition for printed wiring boards can be further improved.
２官能（メタ）アクリレート（カルボキシル基を有するものを除く）の具体例としては、１，４−ブタンジオールジアクリレート、１，６−ヘキサンジオールジアクリレート、１，９−ノナンジオールジアクリレート、１，１０−デカンジオールジアクリレートなどのジオールのジアクリレート、エチレングリコールジアクリレート、ジエチレングリコールジアクリレート、トリエチレングリコールジアクリレート、テトラエチレングリコールジアクリレート、ポリエチレングリコールジアクリレート、ジプロピレングリコールジアクリレート、トリプロピレングリコールジアクリレート、ポリプロピレングリコールジアクリレート、ネオペンチルグリコールジアクリレート、ネオペンチルグリコールにエチレンオキサイドおよびプロピレンオキサイドの少なくとも何れか１種を付加して得たジオールのジアクリレート、カプロラクトン変性ヒドロキシピバリン酸ネオペンチルグリコールジアクリレートなどのグリコールのジアクリレート、ビスフェノールＡ ＥＯ付加物ジアクリレート、ビスフェノールＡ ＰＯ付加物ジアクリレート、トリシクロデカンジメタノールジアクリレート、水添ジシクロペンタジエニルジアクリレート、シクロヘキシルジアクリレートなどの環状構造を有するジアクリレート、などが挙げられる。 Specific examples of the bifunctional (meth) acrylate (excluding those having a carboxyl group) include 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, 1,9-nonanediol diacrylate, 1, Diacrylates of diols such as 10-decanediol diacrylate, ethylene glycol diacrylate, diethylene glycol diacrylate, triethylene glycol diacrylate, tetraethylene glycol diacrylate, polyethylene glycol diacrylate, dipropylene glycol diacrylate, tripropylene glycol diacrylate , Polypropylene glycol diacrylate, neopentyl glycol diacrylate, neopentyl glycol with ethylene oxide and propylene Diacrylate of diol obtained by adding at least one of xylene, glycol diacrylate such as caprolactone-modified hydroxypivalic acid neopentyl glycol diacrylate, bisphenol A EO adduct diacrylate, bisphenol A PO adduct diacrylate And diacrylates having a cyclic structure such as tricyclodecane dimethanol diacrylate, hydrogenated dicyclopentadienyl diacrylate, cyclohexyl diacrylate, and the like.
市販されているものとしては、ライトアクリレート１，６ＨＸ−Ａ、１，９ＮＤ−Ａ、３ＥＧ−Ａ、４ＥＧ−Ａ、（共栄社化学社製の商品名）、ＨＤＤＡ、１，９−ＮＤＡ、ＤＰＧＤＡ、ＴＰＧＤＡ（ダイセル・サイテック社製の商品名）、ビスコート＃１９５、＃２３０、＃２３０Ｄ、＃２６０、＃３１０ＨＰ、＃３３５ＨＰ、＃７００ＨＶ、（大阪有機化学工業社製の商品名）、アロニックスＭ−２０８、Ｍ−２１１Ｂ、Ｍ−２２０、Ｍ−２２５、Ｍ−２４０、Ｍ−２７０（東亞合成社製の商品名）などが挙げられる。 Examples of commercially available products include light acrylate 1,6HX-A, 1,9ND-A, 3EG-A, 4EG-A (trade names manufactured by Kyoeisha Chemical Co., Ltd.), HDDA, 1,9-NDA, DPGDA, TPGDA (trade name manufactured by Daicel-Cytec), Biscote # 195, # 230, # 230D, # 260, # 310HP, # 335HP, # 700HV, (trade name manufactured by Osaka Organic Chemical Industry Co., Ltd.), Aronix M-208 , M-211B, M-220, M-225, M-240, M-270 (trade names manufactured by Toagosei Co., Ltd.) and the like.
これらの中でも、粘度及び相溶性の観点から、炭素数４〜１２のアルキル鎖を有するジオールのジアクリレート、特に１，４−ブタンジオールジアクリレート、１，６−ヘキサンジオールジアクリレート、１，９−ノナンジオールジアクリレート、１，１０−デカンジオールジアクリレートが好ましい。 Among these, from the viewpoint of viscosity and compatibility, diacrylates of diols having an alkyl chain having 4 to 12 carbon atoms, particularly 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, 1,9- Nonanediol diacrylate and 1,10-decanediol diacrylate are preferred.
これら２官能アクリレート化合物の配合量は、本発明の硬化型組成物１００質量部中、好ましくは２０〜８０質量部、より好ましくは４０〜７０質量部である。２官能（メタ）アクリレートの配合量が、２０質量部以上の場合、インキの相溶性が良好となる。一方、配合量が８０質量部以下の場合、インキの密着性が良好となる。 The blending amount of these bifunctional acrylate compounds is preferably 20 to 80 parts by mass, more preferably 40 to 70 parts by mass in 100 parts by mass of the curable composition of the present invention. When the blending amount of the bifunctional (meth) acrylate is 20 parts by mass or more, the ink compatibility is good. On the other hand, when the blending amount is 80 parts by mass or less, the ink adhesion is good.
２官能（メタ）アクリレート化合物の２５℃における粘度が５〜５０ｍＰａ・ｓ、特に５〜３０ｍＰａ・ｓであることが好ましい。この粘度範囲では、２官能（メタ）アクリレート化合物の希釈剤としての取り扱い性が良好となり、各成分を均一に混合することができる。その結果、塗膜の全面が基板に対して一様に密着することが期待できる。 The viscosity at 25 ° C. of the bifunctional (meth) acrylate compound is preferably 5 to 50 mPa · s, particularly 5 to 30 mPa · s. In this viscosity range, the handleability as a diluent of a bifunctional (meth) acrylate compound becomes good, and each component can be mixed uniformly. As a result, it can be expected that the entire surface of the coating film adheres uniformly to the substrate.
本発明のプリント配線板用硬化型組成物には、上記成分の他、必要に応じて、表面張力調整剤、界面活性剤、マット剤、膜物性を調整するためのポリエステル系樹脂、ポリウレタン系樹脂、ビニル系樹脂、アクリル系樹脂、ゴム系樹脂、ワックス類、フタロシアニン・ブルー、フタロシアニン・グリーン、アイオジン・グリーン、ジスアゾイエロー、クリスタルバイオレット、酸化チタン、カーボンブラック、ナフタレンブラックなどの公知慣用の着色剤、シリコーン系、フッ素系、高分子系等の消泡剤およびレベリング剤の少なくとも１種、イミダゾール系、チアゾール系、トリアゾール系、シランカップリング剤等の密着性付与剤のような公知慣用の添加剤類を配合することができる。 In the curable composition for printed wiring boards of the present invention, in addition to the above components, a surface tension adjuster, a surfactant, a matting agent, a polyester resin for adjusting film physical properties, and a polyurethane resin as necessary. , Vinyl resins, acrylic resins, rubber resins, waxes, phthalocyanine blue, phthalocyanine green, iodin green, disazo yellow, crystal violet, titanium oxide, carbon black, naphthalene black and the like, Known and commonly used additives such as adhesion-imparting agents such as at least one antifoaming agent and leveling agent such as silicone, fluorine and polymer, imidazole, thiazole, triazole and silane coupling agent Can be blended.
さらに、本発明のプリント配線板用硬化型組成物には、上記成分の他、特性を損なわない範囲で樹脂を配合することができる。樹脂としては公知慣用のものを用いることができるが、ポリエン骨格を有する（メタ）アクリレート化合物が好ましい。前記ポリエン骨格は、例えばポリブタジエンまたはイソプレン、またはこれらの双方を用いた重合により形成されることが好ましく、特に一般式（Ｉ）、
で表わされる繰り返し単位から構成されることが好ましい。このような繰り返し単位のオレフィン性二重結合に起因して、プリント配線板用硬化型レジスト組成物に柔軟性が与えられ、基材への追従性が増し、良好な密着性が得られる。
Furthermore, resin can be mix | blended with the curable composition for printed wiring boards of this invention in the range which does not impair a characteristic other than the said component. Although a well-known and usual thing can be used as resin, The (meth) acrylate compound which has polyene frame | skeleton is preferable. The polyene skeleton is preferably formed by polymerization using, for example, polybutadiene or isoprene, or both of them, in particular, the general formula (I),
It is preferable that it is comprised from the repeating unit represented by these. Due to the olefinic double bond of such repeating units, flexibility is imparted to the curable resist composition for printed wiring boards, the followability to the substrate is increased, and good adhesion is obtained.
上記（メタ）アクリレート化合物のポリエン骨格は、上記一般式Ｉで表記される繰り返し単位が５０％以上である事が好ましく、８０％以上である事がより好ましい。 In the polyene skeleton of the (meth) acrylate compound, the repeating unit represented by the general formula I is preferably 50% or more, and more preferably 80% or more.
さらに、（メタ）アクリレート化合物のポリエン骨格は、下記一般式（ＩＩ）、
具体例としては、以下の材料が好ましく使用される。すなわち、２−ヒドロキシエチル（メタ）アクリレートを、２，４−トリレンジイソシアネートを介して液状ポリブタジエンのヒドロキシル基とウレタン付加反応させることにより得られる液状ポリブタジエンウレタン（メタ）アクリレート、無水マレイン酸を付加したマレイン化ポリブタジエンに、２−ヒドロキシアクリレートをエステル化反応させて得られる液状ポリブタジエンアクリレート、マレイン化ポリブタジエンのカルボキシル基と、（メタ）アクリル酸グリシジルとのエポキシエステル化反応により得られる液状ポリブタジエン（メタ）アクリレート、液状ポリブタジエンにエポキシ化剤を作用させて得られるエポキシ化ポリブタジエンと、
（メタ）アクリル酸とのエステル化反応により得られる液状ポリブタジエン（メタ）アクリレート、ヒドロキシル基を有する液状ポリブタジエンと、（メタ）アクリル酸クロリドとの脱塩素反応によって得られる液状ポリブタジエン（メタ）アクリレート、分子両末端にヒドロキシル基を有する液状ポリブタジエンの不飽和二重結合を水素添加した液状水素化１，２ポリブタジエングリコールを、ウレタン（メタ）アクリレート変成した液状水素化１，２ポリブタジエン（メタ）アクリレート等である。
As specific examples, the following materials are preferably used. That is, 2-hydroxyethyl (meth) acrylate was added with liquid polybutadiene urethane (meth) acrylate and maleic anhydride obtained by urethane addition reaction with the hydroxyl group of liquid polybutadiene via 2,4-tolylene diisocyanate. Liquid polybutadiene acrylate obtained by esterifying 2-hydroxyacrylate to maleated polybutadiene, liquid polybutadiene (meth) acrylate obtained by epoxy esterification reaction between carboxyl group of maleated polybutadiene and glycidyl (meth) acrylate Epoxidized polybutadiene obtained by allowing an epoxidizing agent to act on liquid polybutadiene,
Liquid polybutadiene (meth) acrylate obtained by esterification reaction with (meth) acrylic acid, liquid polybutadiene (meth) acrylate obtained by dechlorination reaction between liquid polybutadiene having a hydroxyl group and (meth) acrylic acid chloride, molecule Liquid hydrogenated 1,2 polybutadiene (meth) acrylate obtained by modifying liquid hydrogenated 1,2 polybutadiene glycol obtained by hydrogenation of unsaturated double bonds of liquid polybutadiene having hydroxyl groups at both ends, urethane (meth) acrylate, etc. .
市販品の例としては、ＮＩＳＳＯ ＰＢ ＴＥ−２０００、ＮＩＳＳＯ ＰＢ ＴＥＡ−１０００、ＮＩＳＳＯ ＰＢ ＴＥ−３０００、ＮＩＳＳＯ ＰＢ ＴＥＡＩ−１０００（以上いずれも日本曹達社製）、ＣＮ３０１、ＣＮ３０３、ＣＮ３０７（ＳＡＲＴＯＭＥＲ社製）、ＢＡＣ−１５（大阪有機化学工業社製）、ＢＡＣ−４５（大阪有機化学工業社製）、ＥＹ ＲＥＳＩＮ ＢＲ−４５ＵＡＳ（ライトケミカル工業社製）などが挙げられる。 Examples of commercially available products include NISSO PB TE-2000, NISSO PB TEA-1000, NISSO PB TE-3000, NISSO PB TEAI-1000 (all manufactured by Nippon Soda Co., Ltd.), CN301, CN303, CN307 (manufactured by SARTOMER) , BAC-15 (manufactured by Osaka Organic Chemical Industry), BAC-45 (manufactured by Osaka Organic Chemical Industry), EY RESIN BR-45UAS (manufactured by Light Chemical Industry), and the like.
ポリエン骨格を有する（メタ）アクリレートは１種類又は複数種類を組み合わせて用いることができる。 The (meth) acrylate having a polyene skeleton can be used alone or in combination.
また、本発明のプリント配線板用硬化型組成物は、組成物の粘度を調整する事を目的として希釈剤を配合する事が出来る。
希釈剤としては、希釈溶剤、光反応性希釈剤、熱反応性希釈剤等が挙げられる。これらの希釈剤の中でも光反応性希釈剤が好ましい。
光反応性希釈剤としては、（メタ）アクリレート類、ビニルエーテル類、エチレン誘導体、スチレン、クロロメチルスチレン、α−メチルスチレン、無水マレイン酸、ジシクロペンタジエン、Ｎ−ビニルピロリドン、Ｎ−ビニルホルムアミド、キシリレンジオキセタン、オキセタンアルコール、３−エチル−３−（フェノキシメチル）オキセタン、レゾルシノールジグリシジルエーテル等の不飽和二重結合やオキセタニル基、エポキシ基を有する化合物が挙げられる。
これらの中でも（メタ）アクリレート類が好ましく、さらに好ましくは単官能（メタ）アクリレート類が好ましい。単官能（メタ）アクリレート類としては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ラウリル（メタ）アクリレート、ステアリル（メタ）アクリレート、２−ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート、ヒドロキシブチル（メタ）アクリレート、グリシジルメタクリレート等の（メタ）アクリレート類や、アクリロイルモルホリン等を挙げることができる。
これらの希釈剤の配合量は、本発明の硬化型組成物１００質量部中、１〜３０質量部が好ましい。
Moreover, the curable composition for printed wiring boards of this invention can mix | blend a diluent for the purpose of adjusting the viscosity of a composition.
Diluents include diluent solvents, photoreactive diluents, heat reactive diluents, and the like. Of these diluents, photoreactive diluents are preferred.
Photoreactive diluents include (meth) acrylates, vinyl ethers, ethylene derivatives, styrene, chloromethyl styrene, α-methyl styrene, maleic anhydride, dicyclopentadiene, N-vinyl pyrrolidone, N-vinyl formamide, xylates. Examples thereof include compounds having an unsaturated double bond, an oxetanyl group, and an epoxy group such as range oxetane, oxetane alcohol, 3-ethyl-3- (phenoxymethyl) oxetane, and resorcinol diglycidyl ether.
Among these, (meth) acrylates are preferable, and monofunctional (meth) acrylates are more preferable. Examples of monofunctional (meth) acrylates include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, isobutyl (meth) acrylate, lauryl (meth) acrylate, stearyl (meth) acrylate, 2- Examples include (meth) acrylates such as hydroxyethyl (meth) acrylate, hydroxypropyl (meth) acrylate, hydroxybutyl (meth) acrylate, and glycidyl methacrylate, acryloylmorpholine, and the like.
As for the compounding quantity of these diluents, 1-30 mass parts is preferable in 100 mass parts of curable compositions of this invention.
また、本発明のプリント配線板用硬化型組成物は、組成物のUV硬化後のタック性を向上させる事を目的として３官能以上の（メタ）アクリレート化合物（カルボキシル基を有するものを除く）を配合する事が出来る。
３官能以上の（メタ）アクリレート化合物としては、トリメチロールプロパントリアクリレート、トリメチロールメタントリアクリレート、エチレンオキシド変性トリメチロールプロパントリアクリレート、プロピレンオキシド変性トリメチロールプロパントリアクリレート、エピクロルヒドリン変性トリメチロールプロパントリアクリレート、ペンタエリスリトールテトラアクリレート、テトラメチロールメタンテトラアクリレート、エチレンオキシド変性リン酸トリアクリレート、プロピレンオキシド変性リン酸トリアクリレート、エピクロルヒドリン変性グリセロールトリアクリレート、ジペンタエリスリトールヘキサアクリレート、ジトリメチロールプロパンテトラアクリレート、あるいはこれらのシルセスキオキサン変性物等に代表される多官能アクリレート、あるいはこれらに対応するメタアクリレートモノマー、εカプロラクトン変性トリスアクリロキシエチルイソシアヌレートが挙げられる。当該３官能以上の多官能（メタ）アクリレート化合物の配合量は本発明の硬化型組成物１００質量部中、１〜４０質量部が好ましい。
Moreover, the curable composition for printed wiring boards of the present invention contains a tri- or higher functional (meth) acrylate compound (excluding those having a carboxyl group) for the purpose of improving the tackiness after UV curing of the composition. Can be blended.
Trifunctional or higher (meth) acrylate compounds include trimethylolpropane triacrylate, trimethylolmethane triacrylate, ethylene oxide modified trimethylolpropane triacrylate, propylene oxide modified trimethylolpropane triacrylate, epichlorohydrin modified trimethylolpropane triacrylate, penta Erythritol tetraacrylate, tetramethylol methane tetraacrylate, ethylene oxide modified phosphate triacrylate, propylene oxide modified phosphate triacrylate, epichlorohydrin modified glycerol triacrylate, dipentaerythritol hexaacrylate, ditrimethylolpropane tetraacrylate, or their silsesquioxanes For denatured products Polyfunctional acrylate or methacrylate monomers corresponding to these, are include ε-caprolactone-modified trisacryloxyethyl isocyanurate. The blending amount of the trifunctional or higher polyfunctional (meth) acrylate compound is preferably 1 to 40 parts by mass in 100 parts by mass of the curable composition of the present invention.
上記各成分を有する本発明のプリント配線板用硬化型組成物は、スクリーン印刷法、インクジェット法、ディップコート法、フローコート法、ロールコート法、バーコーター法、カーテンコート法などの印刷方法に適用可能である。特に、本発明のプリント配線板用硬化型組成物をインクジェット法に適用する場合、本発明のプリント配線板用硬化型組成物の５０℃における粘度が、５〜５０ｍＰａ・ｓであることが好ましく、５〜２０ｍＰａ・ｓであることがより好ましい。これにより、インクジェットプリンターに不要な負荷を与えることなく、円滑な印刷が可能となる。 The curable composition for a printed wiring board of the present invention having the above components is applied to a printing method such as a screen printing method, an inkjet method, a dip coating method, a flow coating method, a roll coating method, a bar coater method, or a curtain coating method. Is possible. In particular, when the curable composition for printed wiring boards of the present invention is applied to an inkjet method, the viscosity at 50 ° C. of the curable composition for printed wiring boards of the present invention is preferably 5 to 50 mPa · s, More preferably, it is 5-20 mPa * s. Thereby, smooth printing can be performed without applying an unnecessary load to the ink jet printer.
本発明において、粘度は、ＪＩＳ Ｋ２２８３に従って常温（２５℃）または５０℃で測定した粘度をいう。常温で１５０ｍＰａ・ｓ以下、又は５０℃における粘度が５〜５０ｍＰａ・ｓであれば、インクジェット印刷法での印刷が可能である。 In the present invention, the viscosity means a viscosity measured at normal temperature (25 ° C.) or 50 ° C. according to JIS K2283. If the viscosity at room temperature is 150 mPa · s or less, or the viscosity at 50 ° C. is 5 to 50 mPa · s, printing by the ink jet printing method is possible.
更に、本発明のプリント配線板用硬化型組成物は、上記の組成によりインクジェット方式用のインキとして適用された場合、フレキシブル配線板に対してロールトゥロール方式の印刷が可能である。この場合、インクジェットプリンター通過後に後述する光照射用光源を取り付ける事によってパターン硬化塗膜を高速で形成する事が可能である。 Furthermore, when the curable composition for a printed wiring board of the present invention is applied as an ink for an ink jet system with the above composition, it can be printed on a flexible wiring board in a roll-to-roll system. In this case, it is possible to form a pattern cured coating film at high speed by attaching a light irradiation light source described later after passing through the ink jet printer.
光照射は、紫外線又は活性エネルギーの照射により行われるが紫外線が好ましい。光照射の光源としては、低圧水銀灯、中圧水銀灯、高圧水銀灯、超高圧水銀灯、キセノンランプ、メタルハライドランプなどが適当である。その他、電子線、α線、β線、γ線、Ｘ線、中性子線なども利用可能である。かかる光照射にて硬化性樹脂組成物に含まれる光塩基発生剤を活性化して光照射部を硬化する。 Light irradiation is performed by irradiation with ultraviolet rays or active energy, but ultraviolet rays are preferable. As a light source for light irradiation, a low-pressure mercury lamp, a medium-pressure mercury lamp, a high-pressure mercury lamp, an ultrahigh-pressure mercury lamp, a xenon lamp, a metal halide lamp, or the like is appropriate. In addition, electron beams, α rays, β rays, γ rays, X rays, neutron rays, and the like can also be used. By such light irradiation, the photobase generator contained in the curable resin composition is activated to cure the light irradiation part.
更に加熱により光照射部を硬化する。かかる加熱によって、光照射で発生した塩基を触媒として深部まで硬化できる。
ここで、加熱温度は、例えば、８０〜２００℃である。かかる加熱温度範囲とすることにより、光照射部を十分に硬化できる。加熱時間は、例えば、１０〜１００分である。
Further, the light irradiation part is cured by heating. By such heating, the base generated by light irradiation can be cured to a deep part using the catalyst as a catalyst.
Here, the heating temperature is, for example, 80 to 200 ° C. By setting it as this heating temperature range, a light irradiation part can fully be hardened. The heating time is, for example, 10 to 100 minutes.
更に、本発明のプリント配線板用硬化型組成物は、ポリイミド等を主成分とするプラスチック基板と、その上に設けられた導体回路とを含むプリント配線板に対し密着性に優れ、かつ、はんだ耐熱性、耐薬品性、耐溶剤性、鉛筆硬度、無電解金めっき耐性、折り曲げ性等の諸特性に優れたパターン硬化塗膜を形成できる。 Furthermore, the curable composition for a printed wiring board of the present invention has excellent adhesion to a printed wiring board including a plastic substrate mainly composed of polyimide and the like and a conductor circuit provided thereon, and is a solder. Pattern cured coatings excellent in various properties such as heat resistance, chemical resistance, solvent resistance, pencil hardness, electroless gold plating resistance, and bendability can be formed.
以下、実施例を示して本発明について具体的に説明するが、本発明はこれらの実施例のみに限定されるものではない。なお、以下において特に断りのない限り、「部」は質量部を意味するものとする。 EXAMPLES Hereinafter, although an Example is shown and this invention is demonstrated concretely, this invention is not limited only to these Examples. In the following description, “part” means part by mass unless otherwise specified.
（実施例１〜６及び比較例１〜２）
表１に示す成分を、同表に示す割合（単位：部）にて配合し、攪拌機にて予備混合し、硬化型組成物を調製した。
(Examples 1-6 and Comparative Examples 1-2)
The components shown in Table 1 were blended in the proportions (unit: part) shown in the table, and premixed with a stirrer to prepare a curable composition.
上記のようにして作製した硬化型組成物、及びその硬化塗膜について以下の性質を評価した。 The following property was evaluated about the curable composition produced as mentioned above and its cured coating film.
１．５０℃における粘度
実施例１〜６及び比較例１〜２により得られた硬化型組成物の５０℃、１００ｒｐｍにおける粘度をコーンプレート型粘度計（東機産業社製ＴＶＨ−３３Ｈ）にて測定した。
評価基準
○：２０ｍＰａ・Ｓ未満
△：２０ｍＰａ・Ｓ以上５０ｍＰａ・Ｓ以下
×：５０ｍＰａ・Ｓ超
1. Viscosity at 50 ° C. Viscosity of the curable compositions obtained in Examples 1 to 6 and Comparative Examples 1 and 2 at 50 ° C. and 100 rpm was measured with a cone plate viscometer (TVH-33H manufactured by Toki Sangyo Co., Ltd.). It was measured.
Evaluation criteria ○: Less than 20 mPa · S Δ: 20 mPa · S or more and 50 mPa · S or less ×: More than 50 mPa · S
２．ＵＶ硬化後の指触乾燥性
実施例１〜６及び比較例１〜２により得られた硬化型組成物を３０ｕｍのアプリケーター（ＥＲＩＣＨＳＥＮ社製）を使って銅張積層板上に塗布し、高圧水銀灯（ＯＲＣ社製ＨＭＷ−７１３）１５０ｍＪ／ｃｍ２にて硬化を行った。得られたサンプルの指触乾燥性を評価した。
○：タックフリー
×：ベタ付きあり
2. Touch-drying property after UV curing The curable compositions obtained in Examples 1 to 6 and Comparative Examples 1 and 2 were applied onto a copper clad laminate using a 30 um applicator (manufactured by ERICHSEN), and a high-pressure mercury lamp. (HMW-713 manufactured by ORC) Curing was performed at 150 mJ / cm 2 . The touch dryness of the obtained sample was evaluated.
○: Tack free ×: Solid
３．ポリイミドとの密着性
実施例１〜６及び比較例１〜２により得られた組成物を３０ｕｍのアプリケーター（ＥＲＩＣＨＳＥＮ社製）を使ってポリイミド基材（ユーピレックス２５Ｓ）上に塗布し、高圧水銀灯（ＯＲＣ社製ＨＭＷ−７１３）１５０ｍＪ／ｃｍ２にて硬化を行った。その後、１５０℃の熱風循環式乾燥炉にて６０分間加熱処理を行った。作製したサンプルに対してクロスカットテープピール試験（ＪＩＳ Ｋ５６００）を実施した。
○：剥離なし
×：剥離あり
測定結果を表２に示す。
3. Adhesion with polyimide The compositions obtained in Examples 1 to 6 and Comparative Examples 1 and 2 were applied onto a polyimide substrate (Upilex 25S) using a 30 um applicator (manufactured by ERICHSEN), and a high-pressure mercury lamp (ORC). was cured at company made HMW-713) 150mJ / cm 2 . Thereafter, heat treatment was performed for 60 minutes in a hot air circulation drying furnace at 150 ° C. A cross-cut tape peel test (JIS K5600) was performed on the prepared sample.
○: No peeling ×: With peeling The measurement results are shown in Table 2.
４．ＦＲ−４との密着性
実施例１〜６及び比較例１〜２により得られた組成物を３０ｕｍのアプリケーター（ＥＲＩＣＨＳＥＮ社製）を使ってＦＲ−４基板上に塗布し、高圧水銀灯（ＯＲＣ社製ＨＭＷ−７１３）１５０ｍＪ／ｃｍ２にて硬化を行った。その後、１５０℃の熱風循環式乾燥炉にて６０分間加熱処理を行った。作製したサンプルに対してクロスカットテープピール試験（ＪＩＳ Ｋ５６００）を実施した。
○：剥離なし
×：剥離あり
測定結果を表２に示す。
4). Adhesiveness with FR-4 The compositions obtained in Examples 1 to 6 and Comparative Examples 1 and 2 were applied onto an FR-4 substrate using a 30 um applicator (manufactured by ERICHSEN), and a high-pressure mercury lamp (ORC) HMW-713) Cured at 150 mJ / cm 2 . Thereafter, heat treatment was performed for 60 minutes in a hot air circulation drying furnace at 150 ° C. A cross-cut tape peel test (JIS K5600) was performed on the prepared sample.
○: No peeling ×: With peeling The measurement results are shown in Table 2.
５．銅との密着性
実施例１〜６及び比較例１〜２により得られたプリント配線板用硬化型組成物を３０ｕｍのアプリケーター（ＥＲＩＣＨＳＥＮ社製）を使って銅箔上に塗布し、高圧水銀灯（ＯＲＣ社製ＨＭＷ−７１３）１５０ｍＪ／ｃｍ２にて硬化を行った。その後、１５０℃の熱風循環式乾燥炉にて６０分間加熱処理を行った。作製したサンプルに対してクロスカットテープピール試験を実施した。
○：剥離なし
×：剥離あり
測定結果を表２に示す。
5. Adhesion with copper The curable composition for printed wiring boards obtained in Examples 1 to 6 and Comparative Examples 1 and 2 was applied onto a copper foil using a 30 um applicator (manufactured by ERICHSEN), and a high-pressure mercury lamp ( Curing was performed at 150 mJ / cm 2 ( HMW-713 manufactured by ORC). Thereafter, heat treatment was performed for 60 minutes in a hot air circulation drying furnace at 150 ° C. A cross-cut tape peel test was performed on the prepared sample.
○: No peeling ×: With peeling The measurement results are shown in Table 2.
６．鉛筆硬度（表面硬度）
５．で得られた硬化塗膜を用いて、表面における鉛筆硬度をＪＩＳ Ｋ ５６００−５−４に準拠して測定を行った。
6). Pencil hardness (surface hardness)
5. Using the cured coating film obtained in step 1, the pencil hardness on the surface was measured according to JIS K 5600-5-4.
７．折り曲げ耐性
厚さ２５μｍのポリイミドフィルムと、厚さ１２μｍの銅箔により形成された櫛形の銅配線（配線パターン）とから構成されるフレキシブル銅張り積層板（長さ１１０ｍｍ、幅６０ｍｍ、銅配線幅／銅配線間幅＝２００μｍ／２００μｍ）を準備した。このフレキシブル銅張り積層板の基板にピエゾ型インクジェット印刷機を用いてインクジェット印刷により膜厚が１５μｍになるように塗布した。この時、印刷直後にインクジェットヘッドに付帯の高圧水銀灯にてＵＶ仮硬化を行った。その後１５０℃で１時間の加熱により硬化を行い試験片を得た。硬化後の試験片に対して、ＭＩＴ（Ｍａｓｓａｃｈｕｓｅｔｔｓ Ｉｎｓｔｉｔｕｔｅ ｏｆ Ｔｅｃｈｎｏｌｏｇｙ）試験機を用いて下記条件にて保護膜を内側にして折り曲げを繰り返し実施し、導通がとれなくなるサイクル数を求めた。１回の評価につき３試験片に対して試験を実施し、導通がとれなくなる平均値を計算した。試験基準と判定基準は以下に示す通りである。
耐ＭＩＴ試験条件
荷重：５００ｇｆ
角度：角対向１３５°
速度：１７５回／分
先端：Ｒ０．３８ｍｍ円筒
評価基準
○：５０回以上
×：５０回未満
7). Bending resistance Flexible copper-clad laminate (length: 110 mm, width: 60 mm, copper wiring width / width) composed of a polyimide film with a thickness of 25 μm and a comb-shaped copper wiring (wiring pattern) formed of a copper foil with a thickness of 12 μm Copper wiring width = 200 μm / 200 μm) was prepared. The flexible copper-clad laminate was coated on the substrate using a piezo-type inkjet printer so that the film thickness was 15 μm by inkjet printing. At this time, UV temporary curing was performed with a high-pressure mercury lamp attached to the inkjet head immediately after printing. Thereafter, curing was performed by heating at 150 ° C. for 1 hour to obtain a test piece. The cured test piece was repeatedly bent with the protective film on the inner side under the following conditions using a MIT (Masschus Institutes of Technology) tester, and the number of cycles at which electrical conduction could not be obtained was obtained. A test was performed on three test pieces per evaluation, and an average value at which continuity could not be obtained was calculated. Test criteria and judgment criteria are as shown below.
MIT test condition load: 500 gf
Angle: Angle facing 135 °
Speed: 175 times / min Tip: R 0.38 mm cylinder
Evaluation criteria ○: 50 times or more ×: less than 50 times
８．耐溶剤性
５．で得られた硬化塗膜をアセトンに３０分間浸漬した後の塗膜状態を目視にて観察し、以下の基準で評価した。
評価基準
○：全く変化が認められないもの。
×：塗膜の膨潤又は剥離が認められるもの。
8). 4. Solvent resistance The state of the coating film after visually immersing the cured coating film obtained in the above for 30 minutes was visually observed and evaluated according to the following criteria.
Evaluation criteria ○: No change is observed.
X: Swelling or peeling of the coating film is observed.
９． 耐薬品性
５．で得られた硬化塗膜を５ｗｔ％の硫酸水溶液に１０分間浸漬した後の塗膜状態を目視にて観察し、以下の基準で観察した。
評価基準
○：全く変化が認められないもの。
×：塗膜の膨潤又は剥離が認められるもの。
9. 4. Chemical resistance The state of the coating film after visually immersing the cured coating film obtained in step 10 in a 5 wt% sulfuric acid aqueous solution for 10 minutes was visually observed, and observed according to the following criteria.
Evaluation criteria ○: No change is observed.
X: Swelling or peeling of the coating film is observed.
１０．はんだ耐熱性
５．で得られた硬化塗膜を、ＪＩＳ Ｃ−５０１２の方法に準拠し、２６０℃のはんだ槽に１０秒間浸漬後、セロハン粘着テープによるピーリング試験を行った後の塗膜状態を目視にて観察し、以下の基準で評価した。
評価基準
○：塗膜に変化がないもの。
△：塗膜が変化しているもの。
×：塗膜が剥離したもの。
10. 4. Solder heat resistance In accordance with the method of JIS C-5012, after immersing the cured coating film obtained in JIS C-5012 for 10 seconds in a solder bath at 260 ° C., the state of the coating film was visually observed after a peeling test using a cellophane adhesive tape. The evaluation was based on the following criteria.
Evaluation criteria ○: No change in coating film.
Δ: The coating film has changed.
X: The film peeled off.
１１．無電解金めっき耐性
市販の無電解ニッケルめっき浴及び無電解金めっき浴を用いて、ニッケル０．５μｍ、金０．０３μｍの条件で５．で得られた硬化塗膜に金めっきを行ない、硬化塗膜表面状態の観察を行った。判定基準は以下の通りである。
評価基準
○：全く変化が認められないもの。
×：顕著に白化若しくは曇りが生じたもの。
11. 4. Electroless gold plating resistance 5. Using a commercially available electroless nickel plating bath and electroless gold plating bath, under conditions of nickel 0.5 μm and gold 0.03 μm. Gold plating was performed on the cured coating film obtained in, and the surface state of the cured coating film was observed. Judgment criteria are as follows.
Evaluation criteria ○: No change is observed.
X: Significant whitening or clouding occurred.
表１中の製品名および略号は以下のとおりである。
※１：ＴＰＧＤＡ、トリプロピレングリコールジアクリレート（ＢＡＳＦジャパン社製）
※２：ＮＫエステルＡ−ＳＡ、カルボキシル基含有単官能アクリレート（新中村化学工業社製）
※３：Ｌａｒｏｍｅｒ ＬＲ８８６３：ＥＯ変性トリメチロールプロパントリアクリレート（ＢＡＳＦジャパン社製）
※４：イルガキュア ８１９、ビス（２，４，６−トリメチルベンゾイル）−フェニルフォスフィンオキサイド（ＢＡＳＦジャパン社製）
※５：ＹＸ−４０００、ビフェニル型ジグリシジルエーテル（三菱化学社製）
※６：ｊＥＲ８２８、ビスフェノールＡ型ジグリシジルエーテル（三菱化学社製）
※７：ＢＹＫ−３０７、シリコン系添加剤（ビックケミー・ジャパン社製）
※８：イルガキュア ＯＸＥ０２、エタノン,1-[9-エチル-6-(2-メチルベンゾイル)-9H-カルバゾール-3-イル]-,1-(0-アセチルオキシム)（ＢＡＳＦジャパン社製）
※９：イルガキュア ９０７、2-メチル-1-(4-メチルチオフェニル)-2-モルフォリノプロパン-1-オン（ＢＡＳＦジャパン社製）
※１０：ＷＰＢＧ−０２７、(E)-1-[3-(2-hydroxyphenyl)-2-propenoyl]piperidine（和光純薬社製）
The product names and abbreviations in Table 1 are as follows.
* 1: TPGDA, tripropylene glycol diacrylate (manufactured by BASF Japan)
* 2: NK ester A-SA, carboxyl group-containing monofunctional acrylate (manufactured by Shin-Nakamura Chemical Co., Ltd.)
* 3: Laromer LR8863: EO-modified trimethylolpropane triacrylate (BASF Japan)
* 4: Irgacure 819, bis (2,4,6-trimethylbenzoyl) -phenylphosphine oxide (manufactured by BASF Japan)
* 5: YX-4000, biphenyl type diglycidyl ether (Mitsubishi Chemical Corporation)
* 6: jER828, bisphenol A type diglycidyl ether (Mitsubishi Chemical Corporation)
* 7: BYK-307, silicon additive (by Big Chemie Japan)
* 8: Irgacure OXE02, Ethanone, 1- [9-Ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl]-, 1- (0-acetyloxime) (BASF Japan)
* 9: Irgacure 907, 2-methyl-1- (4-methylthiophenyl) -2-morpholinopropan-1-one (manufactured by BASF Japan)
* 10: WPBG-027, (E) -1- [3- (2-hydroxyphenyl) -2-propenoyl] piperidine (Wako Pure Chemical Industries, Ltd.)
表２に示されるように、本発明に係る実施例１〜６のプリント配線板用光硬化型組成物は、ＵＶ硬化後の指触乾燥性、ポリイミドとの密着性、銅との密着性、鉛筆硬度、折り曲げ性、耐溶剤性、耐薬品性、はんだ耐熱性、無電解金めっき耐性のすべてにおいて良好な結果を示した。 As shown in Table 2, the photocurable compositions for printed wiring boards of Examples 1 to 6 according to the present invention are dry to touch after UV curing, adhesiveness with polyimide, adhesiveness with copper, Good results were shown in all of pencil hardness, bendability, solvent resistance, chemical resistance, solder heat resistance, and electroless gold plating resistance.
一方、本発明の成分ＡやＤを欠く比較例１〜２では、上記何れかの特性において十分な性能が得られなかった。 On the other hand, in Comparative Examples 1 and 2 lacking components A and D of the present invention, sufficient performance was not obtained in any of the above characteristics.
本発明は上記の実施の形態の構成及び実施例に限定されるものではなく、発明の要旨の範囲内で種々変形が可能である。 The present invention is not limited to the configurations and examples of the above-described embodiment, and various modifications are possible within the scope of the gist of the invention.
以上説明したように、本発明のプリント配線板用硬化型組成物は、プラスチック基板と導体回路金属の双方に対する密着性に優れ、かつ、はんだ耐熱性、耐溶剤性、耐薬品性、鉛筆硬度、無電解金めっき耐性等の諸特性に優れたファインパターンを形成できる。
また、インクジェット方式で噴射する場合、噴射可能とするには低粘度としなければならない。一般的に低粘度の光硬化型組成物は密着性・耐熱性などの特性が低いとされているが、本組成物は低粘度としても、プリント配線板のインクジェット方式によるソルダーレジストパターン形成に好適に用いることができる。そのため、レジストインキやマーキングインキなどのプリント配線版用材料以外にも、例えば、ＵＶ成形品材料、光造形用材料、３Ｄインクジェット用材料などの用途に利用可能である。
As described above, the curable composition for printed wiring boards of the present invention is excellent in adhesion to both a plastic substrate and a conductor circuit metal, and has solder heat resistance, solvent resistance, chemical resistance, pencil hardness, Fine patterns with excellent characteristics such as electroless gold plating resistance can be formed.
Further, when jetting by an ink jet method, the viscosity must be low to enable jetting. In general, low-viscosity photo-curable compositions are said to have low adhesion and heat resistance characteristics, but this composition is suitable for solder resist pattern formation by the inkjet method of printed wiring boards even when the viscosity is low. Can be used. Therefore, in addition to printed wiring plate materials such as resist inks and marking inks, it can be used for applications such as UV molded article materials, optical modeling materials, and 3D inkjet materials.
Claims (12)
（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物と、
（Ｃ）光重合開始剤と、
（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）と、を含むことを特徴とするプリント配線板用硬化型組成物。 (A) a photobase generator;
(B) a (meth) acrylate compound having a carboxyl group;
(C) a photopolymerization initiator;
(D) A thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group), and a curable composition for printed wiring boards.
（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物と、
（Ｄ）熱硬化成分（（Ｂ）カルボキシル基を有する（メタ）アクリレート化合物を除く）と、を含むことを特徴とするプリント配線板用硬化型組成物。 (A-1) a photobase generator having a function as a photopolymerization initiator;
(B) a (meth) acrylate compound having a carboxyl group;
(D) A thermosetting component (excluding (B) a (meth) acrylate compound having a carboxyl group), and a curable composition for printed wiring boards.