JP2015062600A - Hook-and-loop fastener having both hook and loop engaging elements on one side - Google Patents
Hook-and-loop fastener having both hook and loop engaging elements on one side Download PDFInfo
- Publication number
- JP2015062600A JP2015062600A JP2013199100A JP2013199100A JP2015062600A JP 2015062600 A JP2015062600 A JP 2015062600A JP 2013199100 A JP2013199100 A JP 2013199100A JP 2013199100 A JP2013199100 A JP 2013199100A JP 2015062600 A JP2015062600 A JP 2015062600A
- Authority
- JP
- Japan
- Prior art keywords
- hook
- loop
- constituting
- engagement element
- multifilament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、フック状係合素子およびループ状係合素子が面ファスナーの同一面に共存している布製面ファスナーに関する。より詳細には、本発明は、フック状係合素子およびループ状係合素子が面ファスナーの同一面に共存している布製面ファスナーであって、係合力と耐久性に優れ、さらに極めて柔軟な布製の面ファスナーに関する。 The present invention relates to a cloth surface fastener in which a hook-shaped engagement element and a loop-shaped engagement element coexist on the same surface of a surface fastener. More specifically, the present invention is a cloth surface fastener in which a hook-like engagement element and a loop-like engagement element coexist on the same surface of a surface fastener, and has excellent engagement force and durability, and is extremely flexible. The present invention relates to a cloth fastener.
従来から、布製の織物基布を有する面ファスナーとして、モノフィラメント糸からなるフック状係合素子を織物基布の表面に有するフック面ファスナーや、該フック状係合素子と係合し得るマルチフィラメント糸からなるループ状係合素子を織物基布の表面に有するループ面ファスナーは広く知られており、これらは、フック面ファスナーとループ面ファスナーのペアで用いられ、衣類、靴、帽子、ベルト、サポーター、枕カバー、鞄バッグ類、血圧計、その他日用雑貨、結束テープ、梱包用資材、土木建築用資材、農漁業用資材、玩具等の多くの分野に広く用いられている。 Conventionally, as a hook-and-loop fastener having a cloth base fabric, a hook hook-and-loop fastener having a hook-like engaging element made of a monofilament yarn on the surface of the base cloth, or a multifilament yarn that can be engaged with the hook-like engaging element. Loop hook-and-loop fasteners having a loop-like engagement element made of woven fabric on the surface are widely known, and these are used as a pair of hook hook-and-loop hook fasteners, clothing, shoes, hats, belts, supporters It is widely used in many fields such as pillow covers, bag bags, sphygmomanometers, other daily necessities, binding tapes, packing materials, civil engineering and building materials, agricultural and fishery materials, and toys.
このようなフック面ファスナーやループ面ファスナーは、縫製の際に、フック面ファスナーとループ面ファスナーを間違って取り付けたり、同一面ファスナーを折り重ね合わせても殆ど係合力が発現しないことから、使用形態が制限される等の問題点を有している。 Such hook surface fasteners and loop surface fasteners are used when sewing, because hook surface fasteners and loop surface fasteners are attached incorrectly or even if the same surface fasteners are folded and overlapped. Has a problem such as being limited.
このような問題点を解消する面ファスナーとして、フック状係合素子とループ状係合素子が同一基布面に共存している、いわゆるフック・ループ混在型の面ファスナーが公知である（特許文献１）。 As a hook-and-loop fastener that solves such a problem, a hook-and-loop mixed type hook-and-loop fastener in which a hook-like engaging element and a loop-like engaging element coexist on the same base fabric surface is known (Patent Document). 1).
そして、このような公知のフック・ループ混在型面ファスナーにおいて、フック状係合素子を構成するモノフィラメントがポリエチレンテレフタレート系のポリエステルから形成されており、かつループ状係合素子を構成するマルチフィラメントがポリブチレンテレフタレート系のポリエステルから形成されている場合には、高い係合強力が得られ、さらに基布を構成している地経糸および地緯糸がともにポリエステル系樹脂から形成されている糸であり、かつ地緯糸が芯鞘型の熱融着性繊維を含み、さらにフック状係合素子およびループ状係合素子が、基布を構成する地緯糸により融着固定されている場合には、高い係合耐久性と優れた柔軟性が得られることが公知である（特許文献２）。 In such a known hook / loop mixed surface fastener, the monofilament constituting the hook-like engagement element is made of polyethylene terephthalate polyester, and the multifilament constituting the loop-like engagement element is made of poly. When formed from butylene terephthalate-based polyester, high engagement strength is obtained, and the ground warp and the weft constituting the base fabric are both formed from a polyester-based resin, and High engagement when the ground weft includes a core-sheath type heat-fusible fiber and the hook-like engagement element and the loop-like engagement element are fused and fixed by the ground weft constituting the base fabric. It is known that durability and excellent flexibility can be obtained (Patent Document 2).
この特許文献２に記載されたフック・ループ混在型の布製面ファスナーは、従来のフック・ループ混在型の布製面ファスナーと比べて、上記したような優れた性能を有しているが、最近、より一層基布が柔軟であるフック・ループ混在型の布製面ファスナーが、衣類、日用雑貨等の分野や、カーテン等の美しいひだ形成性を要求される分野において強く求められるようになっている。
本発明者等は、このような要求を満足する布製のフック・ループ混在型面ファスナーについて研究を行った結果、本発明に到達した。
The hook-and-loop mixed type cloth surface fastener described in Patent Document 2 has excellent performance as described above compared to the conventional hook-and-loop mixed type cloth surface fastener. Hook and loop mixed type hook-and-loop fasteners with even more flexible base fabrics are strongly demanded in the fields of clothing, daily necessities, etc., and fields that require beautiful pleat formation such as curtains. .
The inventors of the present invention have reached the present invention as a result of research on a hook-and-loop mixed surface fastener that satisfies such requirements.
本発明は、上記特許文献２に記載されているフック・ループ混在型面ファスナーにおいて、基布がより一層柔軟性に優れており、衣類の止め具や日用雑貨やカーテン等の柔軟性が要求される分野により好適に用いることができるフック・ループ混在型の布製面ファスナーを提供することを目的とするものである。 In the hook / loop mixed surface fastener described in Patent Document 2, the present invention is more flexible in the base fabric, and requires flexibility such as clothes fasteners, sundries and curtains. An object of the present invention is to provide a hook-and-loop mixed-type surface fastener made of cloth that can be used more suitably in the field.
すなわち本発明は、モノフィラメントからなるフック状係合素子およびマルチフィラメントからなるループ状係合素子を織物基布の同一面に有する面ファスナーにおいて、下記１）〜５）を全て満足することを特徴とする同一面にフック・ループが共存している面ファスナーである。
１）該モノフィラメントがポリエチレンテレフタレート系ポリエステルから形成されており、該マルチフィラメントがポリブチレンテレフタレート系ポリエステルから形成されていること、
２）該織物基布を構成する地経糸がポリエチレンテレフタレート系ポリエステルからなるマルチフィラメント糸であること、
３）該織物基布を構成する地緯糸が、低融点ポリエステルを鞘成分とする芯鞘型の熱融着性フィラメントからなるマルチフィラメント糸であること、
４）該熱融着性フィラメントの鞘成分には、鞘成分構成樹脂に対して０．０３〜１質量％の無機微粒子が添加されていること、
５）該係合素子を構成するモノフィラメントおよびマルチフィラメントが該織物基布を構成している地緯糸により融着固定されていること、
That is, the present invention is characterized in that all of the following 1) to 5) are satisfied in a hook-and-loop fastener having a hook-like engaging element made of monofilament and a loop-like engaging element made of multifilament on the same surface of the fabric base fabric. The hook and loop coexist on the same surface.
1) The monofilament is formed from a polyethylene terephthalate polyester, and the multifilament is formed from a polybutylene terephthalate polyester.
2) The ground warp yarn constituting the woven fabric is a multifilament yarn made of polyethylene terephthalate polyester,
3) The ground weft constituting the woven fabric is a multifilament yarn comprising a core-sheath type heat-fusible filament having a low melting point polyester as a sheath component,
4) 0.03 to 1% by mass of inorganic fine particles are added to the sheath component of the heat-fusible filament with respect to the sheath component constituent resin;
5) The monofilament and multifilament constituting the engaging element are fused and fixed by the ground weft constituting the fabric base fabric,
そして、好ましくは、このような同一面にフック・ループが共存している面ファスナーにおいて、フック状係合素子の高さよりもループ状係合素子の高さの方が高い場合であり、またフック状係合素子を構成するモノフィラメントの直径が０．１０〜０．２５ｍｍであり、ループ状係合素子を構成するマルチフィラメント糸が、５〜９本のフィラメントからなるトータルデシテックスが１５０〜３５０デシテックスのマルチフィラメント糸である場合である。 Preferably, in such a hook-and-loop fastener in which hooks and loops coexist on the same surface, the height of the loop-shaped engagement element is higher than the height of the hook-shaped engagement element. The diameter of the monofilament composing the mesh-like engaging element is 0.10 to 0.25 mm, and the multifilament yarn constituting the loop-shaped engaging element is 5 to 9 filaments in total decitex of 150 to 350 decitex This is a case of multifilament yarn.
さらに、このような同一面にフック・ループが共存している面ファスナーにおいて、好ましくは、フック状係合素子の密度（Ａ）とループ状係合素子の密度（Ｂ）がともにそれぞれ２０〜４０個／ｃｍ２の範囲であり、かつ（Ａ）：（Ｂ）が１：０．７５〜１．２５の範囲である場合であり、また芯鞘型の熱融着性フィラメントの芯成分と鞘成分の質量比率が６０：４０〜８０：２０で、２００℃の乾熱収縮率が１２％以上である場合である。 Further, in such a hook-and-loop fastener in which hooks and loops coexist on the same surface, the density of hook-like engagement elements (A) and the density of loop-like engagement elements (B) are preferably 20 to 40 respectively. in the range of pieces / cm 2, and (a) :( B) is 1: 0.75 to 1.25 a case in the range of, also the core component of the heat-fusible filaments of sheath-core and sheath This is a case where the mass ratio of the components is 60:40 to 80:20 and the dry heat shrinkage at 200 ° C. is 12% or more.
本発明の同一面にフック・ループが共存している面ファスナーは、高い係合力と高い係合耐久性を有し、さらに、特に基布の柔軟性に優れている。 The hook-and-loop fastener in which hooks and loops coexist on the same surface of the present invention has high engagement force and high engagement durability, and is particularly excellent in flexibility of the base fabric.
詳しくは、本発明の同一面にフック・ループが共存している面ファスナーは、ループ状係合素子のマルチフィラメントがポリブチレンテレフタレート（ＰＢＴと略す）系のポリエステルから構成されていることから、ループ状係合素子のフィラメントはバラケやすく、ループ状係合素子のフィラメントにフック状係合素子が引っかかり易くなり、軽度な押え付けでも高い係合力を得られる。
またフック状係合素子を構成するモノフィラメントはポリエチレンテレフタレート（ＰＥＴと略す）系のポリエステルであることから、剛性が高く、ループ状係合素子から抜けにくく、この点からも高い係合力が得られる。
Specifically, the hook-and-loop co-existing hook-and-loop fastener of the present invention has a loop-shaped engaging element multifilament made of polybutylene terephthalate (abbreviated as PBT) polyester. The filaments of the hook-like engagement elements are easily broken, and the hook-like engagement elements are easily caught on the filaments of the loop-like engagement elements, and a high engagement force can be obtained even with a slight pressing.
Further, since the monofilament constituting the hook-like engagement element is a polyethylene terephthalate (abbreviated as PET) type polyester, it has high rigidity and is difficult to come out of the loop-like engagement element, and a high engagement force can be obtained from this point.
そして、基布を構成する地緯糸および地経糸および係合素子がいずれもポリエステル系の繊維であることから、地緯糸を溶融させると、フック状係合素子およびループ状係合素子が強固に基布に融着され、繰り返しの係合・剥離によっても、係合素子が基布から引き抜かれることがなく、優れた耐久性のある係合力がいつまでも保持されることとなる。しかも本発明では、該織物基布を構成する地経糸がＰＥＴ系ポリエステルからなるマルチフィラメント糸であることから形態安定性にも優れている。 Since the ground weft, the ground warp and the engaging element constituting the base fabric are all polyester-based fibers, when the ground weft is melted, the hook-shaped engaging element and the loop-shaped engaging element are firmly fixed. Even if it is fused to the cloth and repeatedly engaged and peeled, the engaging element is not pulled out from the base cloth, and an excellent and durable engaging force is maintained indefinitely. In addition, in the present invention, the ground warp yarn constituting the woven fabric is a multifilament yarn made of PET polyester, so that the shape stability is also excellent.
さらに、本発明の同一面にフック・ループが共存している面ファスナーは、係合素子を構成するモノフィラメントおよびマルチフィラメントが該織物基布を構成している地緯糸により融着固定されていることから、従来の面ファスナーのように、基布裏面に係合素子を固定するための接着剤層（バックコート層）を塗布する必要がなく、したがってバックコート層が存在しないことから面ファスナーの基布が柔軟であり、柔軟性が要求される衣類の分野においてボタンやスライドファスナーやスナップ等の代わりとして使用できる。 Furthermore, in the hook-and-loop fastener in which hooks and loops coexist on the same surface of the present invention, the monofilament and multifilament constituting the engaging element are fusion-fixed by the ground weft constituting the woven fabric. Therefore, unlike the conventional surface fastener, it is not necessary to apply an adhesive layer (back coat layer) for fixing the engaging element to the back surface of the base fabric, and therefore there is no back coat layer, so The cloth is flexible and can be used in place of buttons, slide fasteners, snaps, etc. in the field of clothing requiring flexibility.
さらに本発明では、織物基布を構成する地緯糸が、低融点ポリエステルを鞘成分とする芯鞘型の熱融着性フィラメントからなるマルチフィラメント糸であり、かつ該熱融着性フィラメントの鞘成分には無機微粒子が添加されている。これにより、熱融着性フィラメントの鞘成分を溶融させてバインダーとして働かせた後において、バインダー成分（すなわち鞘成分樹脂）の流れ出しが少ない。したがって、従来の無機微粒子を添加していないバインダー樹脂のように溶融した樹脂が基布内に流れ込んで、基布がバインダー樹脂により固められることが少なく、基布が極めて柔軟となり、ＰＢＴ系樹脂からなるループ状係合素子が極めて柔軟であることと相まって、極めて優れた柔軟性が得られることとなる。 Further, in the present invention, the weft constituting the woven fabric is a multifilament yarn comprising a core-sheath type heat-fusible filament having a low-melting polyester as a sheath component, and the sheath component of the heat-fusible filament Inorganic fine particles are added. Thereby, after melt | dissolving the sheath component of a heat-fusible filament and making it work | function as a binder, there is little outflow of a binder component (namely, sheath component resin). Therefore, a molten resin such as a binder resin to which conventional inorganic fine particles are not added flows into the base fabric, and the base fabric is rarely hardened by the binder resin, so that the base fabric becomes extremely flexible, and from the PBT resin Combined with the fact that the loop-shaped engaging element is extremely flexible, extremely excellent flexibility can be obtained.
さらに、本発明では、面ファスナーを構成する繊維はほぼ全てポリエステル系の繊維であることから、染色した場合に同一の染色工程でほぼ均一に染色でき、従来の面ファスナーのように異種の繊維が混入されていることによる染色性の相違に基づく色斑の発生や染色工程の複雑化の問題も生じない。 Furthermore, in the present invention, since the fibers constituting the surface fastener are almost all polyester fibers, when dyed, they can be dyed almost uniformly in the same dyeing process. The problem of the occurrence of color spots based on the difference in dyeability due to mixing and the complication of the dyeing process does not occur.
まず、本発明の面ファスナーは、図１に示すように基布の表面に、フック状係合素子とループ状係合素子が共存している、いわゆるフック・ループ混在型の布製面ファスナーである。すなわち、面ファスナーの係合素子が存在している部分から１ｃｍ四方の大きさを切り出した場合に、その切り出した部分にフック状係合素子とループ状係合素子の両方が存在している面ファスナーを意味する。
本発明の面ファスナーは、主として、フック状係合素子用モノフィラメント、ループ状係合素子用マルチフィラメント、地経糸および地緯糸から構成される。
First, the surface fastener of the present invention is a so-called hook / loop mixed type surface fastener in which a hook-like engaging element and a loop-like engaging element coexist on the surface of a base fabric as shown in FIG. . That is, when a 1 cm square size is cut out from the portion where the hook-and-loop fastener engaging element is present, both the hook-like engaging element and the loop-like engaging element are present in the cut-out portion. Means a fastener.
The hook-and-loop fastener of the present invention is mainly composed of a hook-shaped engaging element monofilament, a loop-shaped engaging element multifilament, a ground warp and a ground weft.
フック状係合素子には、剛直性および軽い力ではフック形状が伸展されない、いわゆるフック形状保持性が求められ、そのために太い剛直な合成繊維製のモノフィラメントが用いられる。本発明では、このモノフィラメントとして、ＰＥＴ系ポリエステルから構成されるモノフィラメントが用いられる。 The hook-shaped engagement element is required to have a hook shape retaining property that does not extend the hook shape with rigidity and light force. For this purpose, a monofilament made of a thick, rigid synthetic fiber is used. In the present invention, a monofilament composed of PET polyester is used as the monofilament.
ＰＥＴ系ポリエステルとは、エチレンテレフタレート単位を主たる繰り返し単位とするポリエステルであり、主としてテレフタル酸とエチレングリコールから縮重合反応により得られるポリエステルであり、若干ならばテレフタル酸やエチレングリコール以外の重合単位が付加されていてもよい。このような重合単位の代表例としては、イソフタル酸、フタル酸、ナフタレンジカルボン酸等の芳香族ジカルボン酸、アジピン酸、セバチン酸等の脂肪族ジカルボン酸、プロピレングリコール、ブチレングリコール等のジオール類、安息香酸、乳酸等のオキシカルボン酸等が挙げられる。 PET polyester is a polyester mainly composed of ethylene terephthalate units, and is a polyester mainly obtained by condensation polymerization reaction from terephthalic acid and ethylene glycol. In some cases, polymer units other than terephthalic acid and ethylene glycol are added. May be. Representative examples of such polymerized units include aromatic dicarboxylic acids such as isophthalic acid, phthalic acid and naphthalenedicarboxylic acid, aliphatic dicarboxylic acids such as adipic acid and sebacic acid, diols such as propylene glycol and butylene glycol, and benzoic acid. Examples thereof include oxycarboxylic acids such as acid and lactic acid.
更に、上記ＰＥＴ系ポリエステルには、それ以外のポリマーが少量添加されていても良い。好ましくは、ＰＥＴホモポリマー単独から形成されている場合である。いずれにしても、後述する熱処理温度で、モノフィラメントが溶融しない融点を有するＰＥＴ系ポリエステルがモノフィラメントを構成する主成分であることが好ましい。 Furthermore, a small amount of other polymers may be added to the PET polyester. Preferably, it is formed from a PET homopolymer alone. In any case, it is preferable that a PET-based polyester having a melting point at which the monofilament does not melt at the heat treatment temperature described later is a main component constituting the monofilament.
このようなＰＥＴ系ポリエステルからなるフック状係合素子用モノフィラメントの太さとしては、直径０．１０〜０．２５ｍｍがフック状係合素子を形成する製織性の点で好ましく、より好ましくは直径０．１２〜０．２２ｍｍの範囲である。この太さは、従来の一般的な面ファスナーのフック状係合素子の太さと比べて若干細いが、この細さが、同一面にフック・ループが共存している面ファスナーに柔軟性をもたらし、更には、衣料用途に特に適するという性能をもたらす。 As a thickness of such a monofilament for hook-shaped engagement element made of PET polyester, a diameter of 0.10 to 0.25 mm is preferable from the viewpoint of weaving to form the hook-shaped engagement element, and more preferably a diameter of 0 The range is from 12 to 0.22 mm. This thickness is slightly thinner than that of the hook-type engagement element of a conventional general hook-and-loop fastener, but this thinness gives flexibility to hook-and-loop fasteners where hooks and loops coexist on the same surface. Furthermore, it provides performance that is particularly suitable for clothing applications.
次に本発明において、ループ状係合素子は、ＰＢＴ系のポリエステルから構成されたマルチフィラメント糸からなる。ＰＢＴ系のポリエステルとは、ブチレンテレフタレート単位を主たる繰り返し単位とするポリエステルであり、主としてテレフタル酸と１，４−ブタンジオールから縮重合反応により得られるポリエステルである。若干ならばテレフタル酸や１，４−ブタンジオール以外の重合単位が付加されていてもよい。 Next, in the present invention, the loop-shaped engaging element is made of a multifilament yarn made of PBT polyester. The PBT-based polyester is a polyester having a butylene terephthalate unit as a main repeating unit, and is a polyester mainly obtained by a condensation polymerization reaction from terephthalic acid and 1,4-butanediol. If some, polymerization units other than terephthalic acid and 1,4-butanediol may be added.
このような重合単位の代表例としては、イソフタル酸、フタル酸、ナフタレンジカルボン酸等の芳香族ジカルボン酸、アジピン酸、セバチン酸等の脂肪族ジカルボン酸、エチレングリコール、プロピレングリコール等のジオール類、安息香酸、乳酸等のオキシカルボン酸等が挙げられる。更に、上記ＰＢＴ系ポリエステルには、それ以外のポリマーが少量添加されていても良い。 Representative examples of such polymerized units include aromatic dicarboxylic acids such as isophthalic acid, phthalic acid and naphthalenedicarboxylic acid, aliphatic dicarboxylic acids such as adipic acid and sebacic acid, diols such as ethylene glycol and propylene glycol, and benzoic acid. Examples thereof include oxycarboxylic acids such as acid and lactic acid. Furthermore, a small amount of other polymers may be added to the PBT polyester.
このようなポリエステルからなるループ状係合素子用マルチフィラメントとしては、５〜９本のフィラメントからなるトータルデシテックスが１５０〜３５０デシテックスのマルチフィラメント糸が好ましい。熱融着によりループ状係合素子を基布に強固に固定するためには、ループ状係合素子を構成するフィラメントの本数を少なくする方が好ましく、本発明を構成するループ状係合素子用マルチフィラメントのフィラメント本数は、従来一般に用いられているループ状係合素子を構成するマルチフィラメントのフィラメント本数である１０〜２４本より若干低い。より好ましくは、６〜８本のフィラメントからなるトータルデシテックスが２３０〜３３０デシテックスのマルチフィラメントである。 As such a multi-filament for loop-shaped engaging element made of polyester, a multifilament yarn having a total decitex of 5 to 9 filaments of 150 to 350 dtex is preferable. In order to firmly fix the loop-like engagement element to the base fabric by heat fusion, it is preferable to reduce the number of filaments constituting the loop-like engagement element. For the loop-like engagement element constituting the present invention The number of filaments of the multifilament is slightly lower than 10 to 24, which is the number of filaments of the multifilament constituting the loop-like engagement element that is generally used conventionally. More preferably, the total decitex composed of 6 to 8 filaments is a multifilament having 230 to 330 decitex.
なお、本発明において、ループ状係合素子を構成するマルチフィラメントには、ＰＢＴ系ポリエステルのマルチフィラメントに、少数の他のフィラメント糸が引きそろえられていてもよい。 In the present invention, the multifilament constituting the loop-like engagement element may have a small number of other filament yarns aligned with the PBT polyester multifilament.
一般に、ポリエステル系のマルチフィラメントからなるループ状係合素子は、面ファスナーの製造工程中の加圧ロールによるループ倒れ及びマルチフィラメントの集束が起こり易く、その結果、基布が透けて見え、見栄えが劣るという問題が生じ易い。それを防ぐために、従来の面ファスナーでは、ループ状係合素子を構成するマルチフィラメントのフィラメント本数を１０本以上、通常は１４〜２４本と多くし、更にマルチフィラメント糸をバラケさせるための処理を行い、それにより基布が透けて見えることを防止している。 In general, a loop-shaped engagement element made of a polyester-based multifilament is liable to cause loop collapse and multifilament focusing due to a pressure roll during the manufacturing process of a hook-and-loop fastener. The problem of inferiority is likely to occur. In order to prevent this, in the conventional surface fastener, the number of multifilaments constituting the loop-shaped engagement element is increased to 10 or more, usually 14 to 24, and further processing for breaking the multifilament yarn is performed. This prevents the base fabric from being seen through.
ところが、ＰＢＴ系マルチフィラメントの場合には、マルチフィラメント糸が本来バラけ易く、かつループが押し付けられても倒れ難いことから、フィラメント本数を従来のＰＥＴ系の場合と比べて、５〜９本と減らすことができる。またループ状係合素子を構成するマルチフィラメント糸のフィラメント本数が少ないことにより、フック状係合素子がループ状係合素子のループ内に嵌入し易く、係合強力が高くなる。さらに、個々のフィラメントがバインダー樹脂により強固に固定され易く、係合・剥離の繰り返しによるループ状係合素子の基布からの引き抜きが生じ難くなるという効果も得られる。 However, in the case of the PBT multifilament, the multifilament yarn is inherently easy to be separated and is not easily collapsed even if the loop is pressed, so the number of filaments is 5 to 9 as compared with the case of the conventional PET system. Can be reduced. Further, since the number of filaments of the multifilament yarn constituting the loop-shaped engagement element is small, the hook-shaped engagement element is easily fitted in the loop of the loop-shaped engagement element, and the engagement strength is increased. Furthermore, the individual filaments can be easily fixed firmly with the binder resin, and the effect that pulling out of the loop-like engagement element from the base fabric due to repeated engagement and separation is less likely to occur.
本発明において、フック状係合素子の高さとしては１．５〜３．０ｍｍ、ループ状係合素子の高さとしては１．６〜４．０ｍｍ、そしてフック状係合素子よりもループ状係合素子の方が０．１〜１．０ｍｍ高いのが、面ファスナー表面に触れた場合に柔軟なループ状係合素子が主として触れることとなり、柔軟な肌触り感を与える点で好ましい。そして手に触れ易いループ状係合素子が柔軟なＰＢＴ系ポリエステルから形成されていることから、より一層柔軟な肌触り感を与える。
より好ましくは、フック状係合素子の高さが１．８〜２．５ｍｍ、ループ状係合素子高さが２．０〜３．３ｍｍ、そしてフック状係合素子よりもループ状係合素子の方が０．２〜０．８ｍｍ高い場合である。
In the present invention, the height of the hook-shaped engaging element is 1.5 to 3.0 mm, the height of the loop-shaped engaging element is 1.6 to 4.0 mm, and the loop shape is more than the hook-shaped engaging element. It is preferable that the engagement element is higher by 0.1 to 1.0 mm because the flexible loop-shaped engagement element mainly comes into contact with the surface fastener surface and gives a soft touch feeling. And since the loop-shaped engagement element which is easy to touch a hand is formed from the flexible PBT type | system | group polyester, a much softer touch feeling is given.
More preferably, the height of the hook-like engagement element is 1.8 to 2.5 mm, the height of the loop-like engagement element is 2.0 to 3.3 mm, and the loop-like engagement element is more than the hook-like engagement element. Is higher by 0.2 to 0.8 mm.
そして、本発明において、フック状係合素子の密度（Ａ）としては、２０〜４０個／ｃｍ２が好ましく、特に好ましくは２５〜３５個／ｃｍ２である。そしてループ状係合素子の密度（Ｂ）としては、マルチフィラメント単位で２０〜４０個／ｃｍ２が好ましく、特に好ましくは２５〜３５個／ｃｍ２である。さらに、（Ａ）：（Ｂ）が１：０．７５〜１．２５の範囲であるのが高い係合力を得る点で好ましく、より好ましくは１：０．８〜１．２の範囲である。 In the present invention, the density (A) of the hook-like engagement elements is preferably 20 to 40 / cm 2 , particularly preferably 25 to 35 / cm 2 . And as the density of the loop-like engaging element (B), preferably 20 to 40 / cm 2 multifilament units, particularly preferably 25 to 35 pieces / cm 2. Further, (A) :( B) is preferably in the range of 1: 0.75 to 1.25 from the viewpoint of obtaining a high engagement force, and more preferably in the range of 1: 0.8 to 1.2. .
本発明において、フック状係合素子を構成するモノフィラメントおよびループ状係合素子を構成するマルチフィラメントはともに地経糸に平行に基布に挿入され、所々で、特にフック状係合素子の場合には地経糸を跨いでループが形成され、一方ループ状係合素子の場合には地経糸を跨ぐことなく基布表面にループが形成される。そしてこれらループ形状を固定するために、熱が加えられる。 In the present invention, the monofilament constituting the hook-like engagement element and the multifilament constituting the loop-like engagement element are both inserted into the base fabric in parallel with the ground warp, and in some cases particularly in the case of the hook-like engagement element. A loop is formed straddling the ground warp. On the other hand, in the case of a loop-shaped engagement element, a loop is formed on the surface of the base fabric without straddling the ground warp. Heat is then applied to fix these loop shapes.
本発明の面ファスナーにおいては、ループ形状を固定するために加えられる熱が同時に基布を構成する地緯糸の熱融着性繊維を融着させ、ループ状係合素子およびフック状係合素子を基布に固定することとなる。したがって、加えられる熱の温度としては、熱融着性繊維が溶融する温度で、かつフック状係合素子用モノフィラメントおよびループ状係合素子用マルチフィラメントが熱固定される温度である１６０〜２２０℃が一般的に用いられ、より好ましくは１７０〜２１０℃の範囲である。 In the hook-and-loop fastener of the present invention, heat applied to fix the loop shape is simultaneously fused to the heat-fusible fiber of the ground weft constituting the base fabric, and the loop-like engagement element and the hook-like engagement element are provided. It will be fixed to the base fabric. Accordingly, the temperature of the applied heat is a temperature at which the heat-fusible fiber melts and a temperature at which the hook-like engagement element monofilament and the loop-like engagement element multifilament are heat-set. Is generally used, more preferably in the range of 170-210 ° C.
そして、フック状係合素子用ループは、そのループ脚部の片側部が切断され、フック状係合素子とされる。そして、フック状係合素子を形成するためにフック状係合素子用ループの側部を切断するために用いられる切断装置は、２本の固定刃の間を1本の可動切断刃が往復運動する構造を有するものが好ましく、ループ状係合素子部分には刃を設けない構造となっているのが好ましい。 And the loop for hook-like engagement elements is cut off at one side of the loop leg portion to form a hook-like engagement element. The cutting device used to cut the side portion of the hook-like engagement element loop to form the hook-like engagement element is such that one movable cutting blade reciprocates between two fixed blades. It is preferable to have a structure that does not have a blade in the loop-shaped engaging element portion.
そのために、フック状係合素子用のループは図１に示すように２列連続して設けると、隣接するループ状係合素子を切断せずにフック状係合素子用ループのループ状係合素子から離れた方の脚部の側部のみを容易に切断でき、ループ状係合素子を損なうことなくフック状係合素子を形成することができる。 For this purpose, when two loops for hook-like engagement elements are provided continuously as shown in FIG. 1, the loop-like engagement of the loops for hook-like engagement elements is performed without cutting adjacent loop-like engagement elements. Only the side part of the leg part far from the element can be easily cut, and the hook-like engagement element can be formed without damaging the loop-like engagement element.
特に、本発明の面ファスナーでは、ループ状係合素子を構成するマルチフィラメントが反発弾性の高いＰＢＴ系ポリエステルから構成されていることから、ループ状係合素子がバラケて横に広がり易く、フック状係合素子の脚部の片側部を切断する際に、ループ状係合素子のマルチフィラメントも傷つけ易い。それを防ぐためには、図１に示すように、フック状係合素子を緯糸方向に最低２列続けて存在させ（図１では２列）、そしてその隣にループ状係合素子列を存在させるような配列とし、ループ状係合素子から離れている方のフック状係合素子用ループの脚部を切断するのが、ループ状係合素子を傷付けることがないため、高い係合強力を得るためには好ましい。 In particular, in the hook-and-loop fastener of the present invention, since the multifilament constituting the loop-shaped engagement element is composed of PBT polyester having high rebound resilience, the loop-shaped engagement element is likely to break apart and spread laterally, and is hook-shaped. When cutting one side portion of the leg portion of the engagement element, the multifilament of the loop engagement element is easily damaged. In order to prevent this, as shown in FIG. 1, at least two rows of hook-like engagement elements are continuously provided in the weft direction (two rows in FIG. 1), and a loop-like engagement element row is present next thereto. Cutting the leg of the loop for the hook-like engagement element that is away from the loop-like engagement element in such an arrangement does not damage the loop-like engagement element, so that high engagement strength is obtained. It is preferable for this purpose.
また、上記配列から、ループ状係合素子列に隣接して少なくとも１条のフック状係合素子列が存在していることが高い係合強力を得る点で好ましい。
以上のことから、ループ状係合素子列を２列配列した隣にフック状係合素子列を２列配列し、２列存在しているフック状係合素子列の中央部分に近い方の脚部が切断されている構造の配列を基本の繰り返し単位とするのが好ましい。
Further, from the above arrangement, it is preferable that at least one hook-like engagement element row is present adjacent to the loop-like engagement element row in order to obtain a high engagement strength.
From the above, two hook-like engagement element rows are arranged next to two loop-like engagement element rows, and the leg closer to the central portion of the two hook-like engagement element rows exists. It is preferable that an arrangement of a structure in which a part is cut is a basic repeating unit.
次に、本発明の面ファスナーにおいて、基布を構成する地経糸としては、ＰＥＴ系ポリエステルからなるマルチフィラメント糸が用いられる。もちろん、若干の共重合成分や他のポリマーや他のフィラメントを含んでいてもよいが、地経糸は、面ファスナーの長さ方向に連続して存在することにより、面ファスナーを製造する上で工程安定性をもたらす糸であることから、製造工程において寸法変化が生じにくく、特に熱処理条件において、収縮等の変化が少ない糸であることが好ましく、したがってＰＥＴホモポリマーから形成されているのがより好ましい。 Next, in the surface fastener of the present invention, a multifilament yarn made of PET polyester is used as the ground warp yarn constituting the base fabric. Of course, some copolymer components and other polymers and other filaments may be included, but the ground warp yarn is a process in producing a hook-and-loop fastener because it is continuously present in the length direction of the hook-and-loop fastener. Since it is a yarn that brings about stability, dimensional change is less likely to occur in the manufacturing process, and it is preferably a yarn that is less susceptible to changes such as shrinkage, particularly under heat treatment conditions, and is therefore more preferably formed from a PET homopolymer. .
地経糸を構成するマルチフィラメントの太さとしては、１２〜９６本のフィラメントからなり、トータルデシテックスが７５〜２５０デシテックスであるマルチフィラメントが好ましく、特に２４〜４８本のフィラメントからなるトータルデシテックスが１００〜１７０デシテックスであるマルチフィラメントが好ましい。そして、このようなマルチフィラメント糸を熱処理後の地経糸織密度として６０〜９０本／ｃｍとなるように基布を構成する。 The thickness of the multifilament constituting the ground warp yarn is preferably a multifilament composed of 12 to 96 filaments and having a total decitex of 75 to 250 decitex, and particularly a total decitex composed of 24 to 48 filaments of 100 to 100. Multifilaments that are 170 dtex are preferred. And a base fabric is comprised so that the ground warp woven density after such heat processing may become 60-90 yarn / cm.
なお、フック状係合素子を構成するモノフィラメントおよびループ状係合素子を構成するマルチフィラメントは前述したように地経糸に平行に基布に打ち込まれる。フック状係合素子用モノフィラメントおよびループ状係合素子用マルチフィラメントの打ち込み本数は、合計で、地経糸本数２０本（フック状係合素子用モノフィラメントおよびループ状係合素子用マルチフィラメントを含む）に対して３〜６本位が好ましい。 Note that the monofilament constituting the hook-like engaging element and the multifilament constituting the loop-like engaging element are driven into the base fabric in parallel with the ground warp yarn as described above. The total number of hook-shaped engaging element monofilaments and loop-shaped engaging element multifilaments to be driven is 20 ground warps (including hook-shaped engaging element monofilaments and loop-shaped engaging element multifilaments). The number of 3 to 6 is preferable.
最後に、本発明の面ファスナーの基布に用いられる地緯糸としては、上記熱処理条件下で熱融着してフック状係合素子用モノフィラメントおよびループ状係合素子用マルチフィラメントの根元を基布に強固に固定できる低融点ポリエステル系樹脂を鞘成分とする芯鞘型複合繊維からなるマルチフィラメントが用いられる。 Finally, as the ground weft used for the base fabric of the surface fastener of the present invention, the base fabric of the base filaments of the hook-like engagement element monofilament and the loop-like engagement element multifilament is heat-sealed under the above heat treatment conditions. A multifilament made of a core-sheath composite fiber having a low melting point polyester resin that can be firmly fixed to the sheath as a sheath component is used.
しかも該鞘成分には、無機微粒子が０．０３〜１質量％添加されていなければならない。無機微粒子の例として、酸化チタン、酸化亜鉛、酸化ケイ素、硫酸バリウム等が挙げられ、なかでも酸化チタンが特に好ましい。 Moreover, 0.03 to 1% by mass of inorganic fine particles must be added to the sheath component. Examples of the inorganic fine particles include titanium oxide, zinc oxide, silicon oxide, barium sulfate and the like, and titanium oxide is particularly preferable.
この量の無機微粒子が添加されていることにより、鞘成分を溶融させてバインダーとして働かせた際に、溶融したバインダー樹脂が広く流れ出して基布内に広く浸透することを防止でき、その結果、基布を硬いものとなることを防止することができる。添加量が０．０３質量％より少ない場合には、樹脂の流れ出しを十分に防ぐことができず、１質量％を超える場合には、逆に溶融した樹脂がフック状係合素子用のモノフィラメントやループ状係合素子用のマルチフィラメントの根元を固定する能力が劣ることとなり、係合・剥離の繰り返しにより係合素子が引き抜かれ易くなる。好ましくは、０．０４〜０．８質量％の無機微粒子が添加されている場合である。 By adding this amount of inorganic fine particles, when the sheath component is melted and used as a binder, it is possible to prevent the molten binder resin from flowing out widely and penetrating into the base fabric. The cloth can be prevented from becoming hard. If the addition amount is less than 0.03% by mass, the resin cannot be sufficiently prevented from flowing out. If the addition amount exceeds 1% by mass, the melted resin, on the other hand, is a monofilament for hook-like engagement elements or The ability to fix the base of the multi-filament for the loop-shaped engagement element is inferior, and the engagement element is easily pulled out by repeated engagement and separation. Preferably, 0.04 to 0.8% by mass of inorganic fine particles are added.
なお、衣料用合成繊維などでは、合成繊維のぎらつきを抑制するために、合成繊維を構成する樹脂に酸化チタンを添加することは一般的に行われており、芯鞘型の熱融着性繊維の場合においても、それが衣料用途に用いられるような場合には、酸化チタンを添加することは一般的に行われている。 In addition, in synthetic fibers for clothing, etc., in order to suppress glare of synthetic fibers, it is generally performed to add titanium oxide to the resin constituting the synthetic fibers, and the core-sheath type heat-fusibility Even in the case of a fiber, when it is used for clothing, it is generally performed to add titanium oxide.
しかしながら、そのような場合、酸化チタンが添加されるのは熱融着後も繊維形状を保って衣料に残る芯成分側の樹脂の方であり、溶けてしまう鞘成分には、酸化チタンを添加することは一般的に行われていない。本発明は、このように従来は一般的に添加されていない鞘成分側に無機微粒子を添加すると、鞘成分樹脂が溶けて基布中に流れ込んで浸透することを無機微粒子が防いでくれることを見出したものである。 However, in such a case, the titanium oxide is added to the resin on the side of the core component that remains in the garment while maintaining the fiber shape even after heat fusion, and titanium oxide is added to the sheath component that melts. It is not generally done. In the present invention, when inorganic fine particles are added to the sheath component side that is not generally added conventionally, the inorganic fine particles prevent the sheath component resin from melting and flowing into the base fabric. It is what I found.
なお、地緯糸となる芯鞘型の熱融着性繊維の鞘成分樹脂は、フック状係合素子用のモノフィラメントやループ状係合素子用のマルチフィラメント、さらには地経糸、該芯鞘型熱融着性繊維の芯成分樹脂のいずれよりも低い融点または軟化点を有していることが必要であり、好ましくは、融点または軟化点が２０℃以上、より好ましくは３０℃以上低い樹脂であるのが好ましい。 The sheath component resin of the core-sheath type heat-fusible fiber used as the ground weft includes monofilaments for hook-like engagement elements, multi-filaments for loop-like engagement elements, ground warp, and core-sheath type heat. It is necessary to have a melting point or softening point lower than any of the core component resins of the fusible fiber, preferably a resin having a melting point or softening point of 20 ° C or higher, more preferably 30 ° C or higher. Is preferred.
具体的には、鞘成分樹脂は、１５０〜２００℃の融点または軟化点を有しているポリエステル系樹脂である。たとえば、イソフタル酸やスルホイソフタル酸ソーダ、エチレングリコールやプロピレングリコール等が１５〜３０モル％共重合されたＰＢＴ系のポリエステル樹脂がループ状係合素子の耐引抜性の点で好適例として挙げられる。 Specifically, the sheath component resin is a polyester-based resin having a melting point or softening point of 150 to 200 ° C. For example, a PBT polyester resin obtained by copolymerization of 15 to 30 mol% of isophthalic acid, sodium sulfoisophthalate, ethylene glycol, propylene glycol, or the like is a preferable example in terms of the pull-out resistance of the loop-shaped engagement element.
そして芯成分としては、鞘成分樹脂との耐剥離性の点および同一染色性の点でポリエステル系の樹脂が好ましく、さらに高融点を有していることが求められることからＰＥＴホモポリマーやＰＢＴホモポリマーが挙げられ、なかでも形体安定性の点でＰＥＴホモポリマーが特に好ましい。 The core component is preferably a polyester-based resin in terms of resistance to peeling from the sheath component resin and the same dyeability, and since it is required to have a high melting point, a PET homopolymer or PBT homopolymer is required. Among them, a PET homopolymer is particularly preferable from the viewpoint of shape stability.
芯鞘複合繊維における芯成分と鞘成分の比率は質量比で６０：４０〜８０：２０の範囲が好ましい。そして地緯糸を構成する繊維中に占める芯鞘型熱融着性繊維の割合は２５〜１００質量％が好ましく、特に地緯糸の全てが実質的に熱融着性繊維で形成されている場合には、芯成分割合が少ないと面ファスナーが長手方向に引き裂け易く、鞘成分が少ないと融着固定力が低くなる。したがって芯成分と鞘成分の比率は上記範囲が好ましいこととなる。 The ratio of the core component to the sheath component in the core-sheath composite fiber is preferably in the range of 60:40 to 80:20 by mass ratio. And the ratio of the core-sheath type heat-fusible fiber occupying in the fibers constituting the weft yarn is preferably 25 to 100% by mass, especially when all the weft yarns are substantially made of heat-fusible fiber. When the core component ratio is small, the surface fastener is easy to tear in the longitudinal direction, and when the sheath component is small, the fusion fixing force is low. Therefore, the ratio of the core component to the sheath component is preferably in the above range.
さらに、フック状係合素子およびループ状係合素子を共に強固に基布に固定するためには、地緯糸として用いられた熱融着性繊維が熱融着すると共に、地緯糸繊維自身が収縮してフック状係合素子およびループ状係合素子の根元を締め付けるのが好ましく、そのためには、地緯糸として用いられる熱融着性繊維は熱処理条件下で大きく熱収縮を生じる繊維が好ましい。具体的には、２００℃で１分間加熱した場合の乾熱収縮率が１２％以上である繊維が好適に用いられ、特に同収縮率が１３〜２０％％である繊維が好適である。 Furthermore, in order to firmly fix both the hook-like engagement element and the loop-like engagement element to the base fabric, the heat-fusible fiber used as the ground weft is thermally fused, and the weft fiber itself contracts. Then, it is preferable to fasten the bases of the hook-like engagement element and the loop-like engagement element. For this purpose, the heat-fusible fiber used as the ground weft is preferably a fiber that undergoes large thermal shrinkage under heat treatment conditions. Specifically, a fiber having a dry heat shrinkage of 12% or more when heated at 200 ° C. for 1 minute is suitably used, and a fiber having the shrinkage of 13 to 20% is particularly preferred.
なお、地緯糸を構成するマルチフィラメントの太さとしては、１２〜７２本のフィラメントからなるトータルデシテックスが１００〜３００デシテックスであるマルチフィラメントが好ましく、特に２４〜４８本のフィラメントからなるトータルデシテックスが１５０〜２５０デシテックスであるマルチフィラメントが好ましい。
そして、このような地緯糸用のマルチフィラメント糸を熱処理後の織密度として１５〜２５本／ｃｍとなるように基布に打ち込むのが好ましい。
The thickness of the multifilament constituting the weft is preferably a multifilament having a total decitex of 12 to 72 filaments of 100 to 300 dtex, particularly 150 to a total decitex of 24 to 48 filaments. Multifilaments of ~ 250 dtex are preferred.
And it is preferable to drive such a multifilament yarn for weft into a base fabric so that the weave density after heat treatment is 15 to 25 yarns / cm.
そして、地緯糸の質量割合としては、面ファスナーを構成するフック状係合素子用モノフィラメントとループ状係合素子用マルチフィラメントと地経糸および地緯糸の合計質量に対して１５〜４０％が好ましい。 The mass ratio of the ground weft is preferably 15 to 40% with respect to the total mass of the hook-shaped engaging element monofilament, the loop-shaped engaging element multifilament, the ground warp and the weft constituting the hook-and-loop fastener.
なお、上記したように、本発明は、基布構成繊維を熱融着させることにより係合素子用糸の根元を基布に強固に固定するものであり、したがって従来の面ファスナーのように基布裏面に接着剤を塗布する必要がないというよりも、接着剤層を塗布しない面ファスナーに適している。 In addition, as described above, the present invention firmly fixes the base of the engagement element yarn to the base fabric by heat-sealing the base fabric constituent fibers. Rather than having to apply an adhesive on the back of the fabric, it is suitable for a hook-and-loop fastener without applying an adhesive layer.
基布の織組織としては、フック状係合素子用モノフィラメントおよびループ状係合素子用マルチフィラメントを地経糸の一部とした平織りが好ましく、これら係合素子用糸のうちフック状係合素子用のモノフィラメントは、組織の途中で基布面から立ち上がり、ループを形成しつつ地経糸を１〜４本飛び越えて地緯糸間にもぐりこむような織組織が、ループ状係合素子ループを傷つけることなく、フック状係合素子用ループの側部を切断できることから好ましい。 The woven structure of the base fabric is preferably a plain weave in which a monofilament for a hook-like engagement element and a multifilament for a loop-like engagement element are part of the ground warp. Among these engagement element yarns, for a hook-like engagement element The monofilament of woven structure that rises from the base fabric surface in the middle of the structure, jumps between 1 to 4 ground warp yarns while forming a loop and is caught between the weft yarns, without damaging the loop-like engagement element loop, This is preferable because the side portion of the hook-like engaging element loop can be cut.
本発明の面ファスナーは、全てポリエステル系の繊維で構成されている場合には、色斑を生じることなく均一に染色することができ、特に衣類等に用いられるボタンやスナップやスライドファスナーの代わりに用いられた場合には、大半の衣類はポリエステル繊維が用いられていることから、従来のナイロン系繊維が用いられている面ファスナーやバックコート樹脂（通常はポリウレタンが使用されている）が塗布されている面ファスナー等に比べて、衣類と同一の色調に同時に染色できることから、染色性の点で極めて優位となる。 When the surface fastener of the present invention is composed entirely of polyester fibers, it can be uniformly dyed without causing color spots, especially in place of buttons, snaps and slide fasteners used for clothing etc. When used, most garments are made of polyester fiber, so surface fasteners and backcoat resins (usually polyurethane) that use conventional nylon fibers are applied. Compared with a hook-and-loop fastener, etc., it can be dyed simultaneously in the same color tone as clothing, which is extremely advantageous in terms of dyeability.
すなわち、今日、衣類はその殆どがポリエステル系繊維により形成されていることから、縫製後の衣類と同一の染色条件下で面ファスナーも同色に同時染色することができることから、従来のごとく、染色する色に合わせた多色の多くの面ファスナーを予め用意する必要がなく、極めて好ましいこととなる。 That is, today, most clothing is made of polyester fiber, so that the surface fastener can be dyed simultaneously in the same color under the same dyeing conditions as the clothing after sewing. It is not necessary to prepare many multi-color hook-and-loop fasteners according to colors, which is extremely preferable.
本発明のフック状係合素子およびループ状係合素子が面ファスナーの同一面に共存している布製の面ファスナーは、従来の面ファスナーが用いられている用途分野に用いることができ、例えば、靴、バッグ、帽子、手袋等の他、衣類、血圧計、サポーター類、荷造りの縛りバンド、各種おもちゃ類、土木用シートの固定、各種パネルや壁材の固定、太陽電池の屋根への固定、電気部品の固定、小物類、カーテン等に使用できる。 The hook-shaped engaging element and the loop-shaped engaging element of the present invention in which the hook-shaped engaging element and the loop-shaped engaging element coexist on the same surface of the hook-and-loop fastener can be used in application fields where conventional hook-and-loop fasteners are used. In addition to shoes, bags, hats, gloves, etc., clothing, sphygmomanometers, supporters, straps for packing, various toys, fixing civil engineering sheets, fixing panels and wall materials, fixing solar cells to the roof, Can be used for fixing electrical parts, accessories, curtains, etc.
特に本発明の面ファスナーは、柔軟性に特に優れていることから、柔らかさが求められる分野、例えば、衣類（特に肌に接する部分に用いられる各種留具）、特に肌着や寝具、要介護者や幼児用の衣類、手袋、靴、帽子、サポーター等の日用雑貨類、美しいひだ形成が求められるカーテン等に適している。 In particular, the hook-and-loop fastener of the present invention is particularly excellent in flexibility, so that it is required to be soft, for example, clothing (especially various fasteners used in contact with the skin), especially underwear and bedding, care recipients. It is suitable for clothes for children, daily goods such as gloves, shoes, hats, supporters, and curtains that require beautiful folds.
以下本発明を実施例により説明するが、本発明はこれら実施例に限定されるものではない。なお、実施例中、乾熱収縮率はＪＩＳ L １０１３にしたがって、また係合強力はＪＩＳ Ｌ ３４１６にしたがって面ファスナー幅１００ｍｍで測定した。 EXAMPLES The present invention will be described below with reference to examples, but the present invention is not limited to these examples. In Examples, the dry heat shrinkage rate was measured according to JIS L 1013, and the engagement strength was measured according to JIS L 3416 at a surface fastener width of 100 mm.
実施例１
基布を構成する地経糸および地緯糸、フック状係合素子用モノフィラメント、ループ状係合素子用マルチフィラメントとして次の糸を用意した。
Example 1
The following yarns were prepared as ground warp and weft yarns, monofilaments for hook-like engagement elements, and multifilaments for loop-like engagement elements constituting the base fabric.
［地経糸］
・融点２６０℃のポリエチレンテレフタレートからなるマルチフィラメント糸
・トータルデシテックスおよびフィラメント本数：１６７デシテックスで３０本
［地緯糸（芯鞘型複合繊維からなるマルチフィラメント系熱融着糸）］
・芯成分：ポリエチレンテレフタレート（融点：２６０℃）
・鞘成分：無機微粒子として酸化チタンを０．０８質量％含有するイソフタル酸２５モル％共重合ポリブチレンテレフタレート（軟化点：１８０℃）
・芯鞘比率（質量比）：７：３
・トータルデシテックスおよびフィラメント本数：２２０デシテックスで４８本
・２００℃で１分間の乾熱収縮率：１５％
[Ground warp]
・ Multifilament yarn made of polyethylene terephthalate with a melting point of 260 ° C. ・ Total decitex and number of filaments: 167 decitex and 30 strands [base weft (multifilament heat-sealed yarn made of core-sheath type composite fiber)]
-Core component: Polyethylene terephthalate (melting point: 260 ° C)
・ Sheath component: 25 mol% isophthalic acid copolymerized polybutylene terephthalate containing 0.08% by mass of titanium oxide as inorganic fine particles (softening point: 180 ° C.)
-Core-sheath ratio (mass ratio): 7: 3
-Total decitex and number of filaments: 48 at 220 decitex-Dry heat shrinkage at 200 ° C for 1 minute: 15%
［フック状係合素子用モノフィラメント］
・ポリエチレンテレフタレート繊維（融点：２６０℃）
・繊度：３９０デシテックス（直径：０．１９ｍｍ）
［ループ状係合素子用マルチフィラメント］
・ポリブチレンテレフタレート繊維（融点：２２０℃）
・トータルデシテックスおよびフィラメント本数：２６７デシテックスで７本
[Monofilament for hook-like engagement element]
-Polyethylene terephthalate fiber (melting point: 260 ° C)
・ Fineness: 390 dtex (diameter: 0.19 mm)
[Multifilament for loop-like engagement element]
・ Polybutylene terephthalate fiber (melting point: 220 ° C)
・ Total decitex and number of filaments: 7 at 267 decitex
上記４種の糸を使用し、フック状係合素子を長手方向に２列設け、隣接してループ状係合素子を２列設けた配列を繰り返すよう、フック状係合素子用モノフィラメントとループ状係合素子用マルチフィラメントを並べ、テープを織った。また、表面を触った時にループ状係合素子の方が触れるよう、ループ状係合素子が外側の両端に存在するように配列した。織組織は平織りで、織密度は地経糸７２本／ｃｍで地緯糸１６本／ｃｍで、地経糸８本に２本の割合でフック状係合素子用モノフィラメントを、また地経糸８本に２本の割合でループ状係合素子用マルチフィラメントをそれぞれ打ち込んだ。 Using the above four types of yarns, the hook-like engagement element monofilament and the loop form are repeated so that two rows of hook-like engagement elements are provided in the longitudinal direction and two rows of loop-like engagement elements are provided adjacent to each other. Multifilaments for engaging elements were arranged and tape was woven. Further, the loop-like engagement elements were arranged so as to be present at both ends on the outer side so that the loop-like engagement elements touched when touching the surface. The weaving structure is plain weave, the weaving density is 72 warps / cm, 16 wefts / cm, 8 hooks of monofilaments for hook-like engagement elements, and 2 for 8 warps. The multifilaments for loop-like engagement elements were respectively driven at the rate of the book.
上記条件にて織成されたテープを、地緯糸の鞘成分のみが熱溶融し、かつ、経糸、ループ係合素子用マルチフィラメント、フック係合素子用モノフィラメント、さらには地緯糸の芯成分が熱溶融しない温度域、すなわち摂氏２００℃で熱処理を施した。地緯糸は大きく収縮するとともに鞘成分が溶融して近隣に存在する糸を融着させた。その結果、基布は地緯糸方向に大きく収縮して、地緯糸方向に長さで１０％収縮した。そして、得られた織物を冷却させたのち、フック状係合素子用ループの片脚部（ループ状係合素子から離れている方の脚部）を切断してフック状係合素子を形成した。 In the tape woven under the above conditions, only the sheath component of the weft yarn is thermally melted, and the warp yarn, the multi-filament for the loop engaging element, the monofilament for the hook engaging device, and the core component of the weft yarn are heated. Heat treatment was performed in a temperature range where melting did not occur, that is, 200 ° C. The ground weft shrunk greatly and the sheath component melted to fuse the neighboring yarn. As a result, the base fabric contracted greatly in the direction of the weft yarn, and contracted 10% in length in the direction of the weft yarn. Then, after cooling the obtained fabric, one leg portion of the hook-like engagement element loop (the leg portion away from the loop-like engagement element) was cut to form a hook-like engagement element. .
得られたフック・ループ混在型面ファスナーのフック状係合素子密度は３０個／ ｃｍ２、ループ状係合素子密度は３１個／ｃｍ２であり、さらにフック状係合素子およびループ状係合素子の基布面からの高さはそれぞれ１．８ｍｍおよび２．４ｍｍであった。 The hook-and-loop mixed surface fastener thus obtained has a hook-like engaging element density of 30 pieces / cm 2 and a loop-like engaging element density of 31 pieces / cm 2 , and further has a hook-like engaging element and a loop-like engaging element. The height from the base fabric surface of the element was 1.8 mm and 2.4 mm, respectively.
得られたフック・ループ混在型面ファスナーの係合素子面を手で触れたところ、いずれもループ状係合素子に主として触れることから、柔らかい手触り感を有していた。さらに基布の柔軟性を手の平で握ることにより観測したところ、後述する芯鞘型繊維の鞘成分に酸化チタンを全く添加していない面ファスナーと比べて基布自体がはるかに柔軟であり、従来の面ファスナーのイメージ（すなわち、布製であるにもかかわらず、布とは全く異なる硬さを有し、布に取り付けると、布地の柔らかさが大きく損なわれるもの）とは異なる優れた柔軟性を有していた。 When the engagement element surface of the obtained hook / loop mixed surface fastener was touched by hand, both of them mainly touched the loop engagement element, and thus had a soft hand feeling. Furthermore, when the flexibility of the base fabric was observed by grasping with the palm of the hand, the base fabric itself was much more flexible than a hook-and-loop fastener that did not contain any titanium oxide in the sheath component of the core-sheath fiber described below. Excellent flexibility that is different from the image of a hook-and-loop fastener (that is, it is made of cloth but has a completely different hardness from cloth, and when attached to the cloth, the softness of the cloth is greatly impaired) Had.
染色は、ポリエチレンテレフタレート繊維が染色可能な高圧条件で紺色の分散染料を用いて実施したが、ポリブチレンテレフタレート繊維は、ポリエチレンテレフタレート繊維より染料が入り始める温度が約２０℃低いため、ループ状係合素子がフック状係合素子、地経糸、地緯糸に比べより一層濃色に発色し、面ファスナー上に広がって存在しているループ状係合素子が、面ファスナーに色の深みを有する高級感あるものとの印象を与えた。
次に、得られた面ファスナー同士の係合素子面側を重ね合わせて、その係合強力を求めた。その結果を表１に示す。なお、係合強力は１００ｍｍ幅の面ファスナーのせん断方向と剥離方向の両方向で測定した。
Dyeing was carried out using an amber disperse dye under high pressure conditions where polyethylene terephthalate fibers can be dyed, but polybutylene terephthalate fibers are about 20 ° C lower than the polyethylene terephthalate fibers, so loop engagement. A loop-like engagement element that has a deeper color than the hook-like engagement element, ground warp and ground weft and spreads on the hook-and-loop fastener has a high-quality feeling that the hook-and-loop fastener has a color depth. I gave the impression that there was something.
Next, the engagement element surface sides of the obtained surface fasteners were overlapped to determine the engagement strength. The results are shown in Table 1. The engagement strength was measured in both the shearing direction and peeling direction of a 100 mm wide surface fastener.
その結果、係合強力は、極めて高い価を示した。さらに、この面ファスナー同士を５０００回係合・剥離を繰り返し、その後の係合強力を測定した。その結果を表1に記載する。同表から明らかなように、係合・剥離を５０００回繰り返した後であっても、係合強力はあまり低下することなく、極めて耐久性に優れたものであることが分かる。
また剛軟度（JIS-L-1096 剛軟性D法 ハートループ法）においても、後述する酸化チタン無添加のもの（比較例１の面ファスナー）と比べて数値が大きいほど柔らかい優れた値を示し、測定値からも柔軟性に優れたものであることが確認された。
As a result, the engagement strength was extremely high. Furthermore, this hook-and-loop fastener was repeatedly engaged and peeled 5000 times, and the subsequent engagement strength was measured. The results are listed in Table 1. As is apparent from the table, even after the engagement / peeling is repeated 5000 times, the engagement strength does not decrease so much and it can be seen that the durability is extremely excellent.
Also, in the bending resistance (JIS-L-1096 bending resistance D method heart loop method), the larger the numerical value, the softer and superior the value, compared to the titanium oxide-free addition (surface fastener of Comparative Example 1) described later. From the measured values, it was confirmed to be excellent in flexibility.
実施例２〜３および比較例１〜２
上記実施例１において、地緯糸に用いる芯鞘型複合繊維からなる熱融着性繊維の鞘成分に添加する無機微粒子としての酸化チタンの量を、０質量％（すなわち、全く添加しないブライト繊維。比較例１）、０．０４質量％（実施例２）、０．７５質量％（実施例３）、１．５質量％（比較例２）と変更する以外は、実施例１と全く同一の方法によりフック状係合素子およびループ状係合素子が面ファスナーの同一面に共存している布製の面ファスナーを製造した。なお、上記熱融着性繊維の乾熱収縮率は実施例１の値と同一である。
Examples 2-3 and Comparative Examples 1-2
In Example 1 above, the amount of titanium oxide as inorganic fine particles added to the sheath component of the heat-fusible fiber composed of the core-sheath composite fiber used for the weft is 0% by mass (that is, bright fiber not added at all). Comparative Example 1) Except for changing to 0.04% by mass (Example 2), 0.75% by mass (Example 3), and 1.5% by mass (Comparative Example 2), exactly the same as Example 1. By the method, a hook-and-loop engaging element and a loop-shaped engaging element coexisting on the same surface of the hook-and-loop fastener were manufactured. In addition, the dry heat shrinkage rate of the said heat-fusible fiber is the same as the value of Example 1.
得られた、同一の酸化チタン添加量の面ファスナー同士を重ね合わせて係合させ、実施例１同様の測定方法により、初期係合強力、係合剥離耐久性、風合い（剛軟度）を測定した。その結果を表１に記載する。 The obtained surface fasteners with the same titanium oxide addition amount are overlapped and engaged with each other, and the initial engagement strength, the engagement peeling durability, and the texture (flexibility) are measured by the same measurement method as in Example 1. did. The results are listed in Table 1.
フック面ファスナーとループ面ファスナーの手触り感（表面の柔らかさ）に関しては、いずれも、実施例１のもの比べて殆ど差がなく、良好なものであった。
しかしながら、基布の剛軟度に関しては、比較例１のものは劣り、また比較例２のものは、基布の剛軟度に関しては問題ないものの、係合剥離耐久性の点で上記実施例のものより幾分劣るものであった。また、初期係合強力や係合剥離耐久性においても、本発明のものは優れていた。
Regarding the feeling of touch (softness of the surface) of the hook surface fastener and the loop surface fastener, both were almost the same as those of Example 1 and were good.
However, with respect to the bending resistance of the base fabric, the comparative example 1 is inferior, and the comparative example 2 has no problem with respect to the bending resistance of the base fabric. It was somewhat inferior to Moreover, the thing of this invention was excellent also in initial stage engagement strength and engagement peeling durability.
比較例３
地経糸として、ＰＢＴからなるマルチフィラメント糸（１６７デシテックスで３０フィラメント）を使用する以外は実施例１と同様に、フック・ループ混在型面ファスナーを作製した。このものは、製造工程で弛みを生じ、製造しやすさの点で実施例１のものよりはるかに劣り、さらに、得られた面ファスナーを衣類の胸部に高速ミシンを用いて縫製により取り付けたところ、縫製品の一部に縫製時の張力により歪みが生じ、それが原因により衣類に皺が発生しているものが一部見られた。
Comparative Example 3
A hook / loop mixed surface fastener was produced in the same manner as in Example 1 except that multifilament yarn made of PBT (30 filaments at 167 dtex) was used as the ground warp yarn. This product causes slack in the manufacturing process, and is far inferior to that of Example 1 in terms of ease of manufacturing. Further, the obtained hook-and-loop fastener is attached to the chest of the garment by sewing using a high-speed sewing machine. Some of the sewn products were distorted due to the tension during sewing, and some of the clothes were wrinkled.
比較例４
ループ状係合素子用の糸として、ＰＥＴからなるマルチフィラメント（融点２６０℃、トータルデシテックス：２６７ｄｔｅｘ、フィラメント本数：７本）を用いる以外は実施例１と同様の方法により、フック・ループ混在型面ファスナーを製造した。
Comparative Example 4
A hook / loop mixed surface is obtained in the same manner as in Example 1 except that a multifilament made of PET (melting point: 260 ° C., total decitex: 267 dtex, number of filaments: 7) is used as the thread for the loop engaging element. A fastener was manufactured.
この面ファスナーは、手触り感が実施例１のものと比べて硬く、さらに初期係合強力に関しても、せん断強力が１０．９Ｎ／ｃｍ２、剥離強力が０．９９Ｎ／ｃｍであり、５０００回係合・剥離を繰り返した後の係合強力もせん断強力が９．９Ｎ／ｃｍ２、剥離強力が１．１３Ｎ／ｃｍであり、実施例１のものよりもかなり劣るものであった。その原因として、ループ状係合素子のループ内での広がり（バラけ）が少なく、さらに倒れた係合素子が実施例のものより立ち上がりが悪く、それが係合力に影響を与えたものと予想される。 This hook-and-loop fastener is harder than that of Example 1 and has an initial engagement strength of 10.9 N / cm 2 and a peel strength of 0.99 N / cm. The engagement strength after repeated joining and peeling was 9.9 N / cm 2 for the shear strength and 1.13 N / cm for the peel strength, which was considerably inferior to that of Example 1. The reason for this is that the loop-like engagement element has less spread (unevenness) in the loop, and the fallen engagement element has a worse start-up than that of the example, which is expected to have affected the engagement force. Is done.
基布の柔軟性に関しても、実施例１のものより劣り、衣類に取り付けた場合には、衣類の風合いを損なうこと、さらにカーテンの止め具としてカーテンの端部に取り付けた場合にはカーテンのひだが面ファスナーにより妨げられて美しいひだが形成されないことが予想された。さらに染色物に関しても、ループ状係合素子の広がりが少なく、その結果、基布が露出して見え、見劣りのするものであった。 The flexibility of the base fabric is also inferior to that of Example 1, and when it is attached to clothing, the texture of the clothing is impaired, and when it is attached to the end of the curtain as a curtain stop, It was expected that no beautiful folds would be formed due to hindrance by the hook-and-loop fastener. Further, with respect to the dyed product, the loop-shaped engagement element did not spread widely, and as a result, the base fabric was exposed and looked inferior.
比較例５
フック状係合素子用の糸として、ＰＢＴからなるモノフィラメント：３９０デシテックス（直径：０．１９ｍｍ）を用いる以外は実施例１と同様の方法により、フック・ループ混在型面ファスナーを製造した。
Comparative Example 5
A hook / loop mixed surface fastener was manufactured in the same manner as in Example 1 except that monofilament made of PBT: 390 dtex (diameter: 0.19 mm) was used as the yarn for the hook-like engagement element.
この面ファスナーは、手触り感が実施例１のものも柔らかく、その点では優れていたが、面ファスナーの最重要性能である係合強力の点で劣るものであった。具体的には初期係合強力は、せん断強力が９．３Ｎ／ｃｍ２、剥離強力が０．６５Ｎ／ｃｍであり、５０００回係合・剥離を繰り返した後の係合強力もせん断強力が７．９Ｎ／ｃｍ２、剥離強力が０．６３Ｎ／ｃｍであり、実施例１のものよりもはるかに劣るものであった。その原因として、フック状係合素子が柔らかく、低い引張り力によりフック形状が伸びて、係合が外れ、それが係合力に影響を与えたものと予想される。基布の柔軟性に関しては、実施例１のものと同等またはそれ以上で優れていた。 This hook-and-loop fastener was soft in the feel of Example 1 and was excellent in that respect, but was inferior in terms of engagement strength, which is the most important performance of the hook-and-loop fastener. Specifically, the initial engagement strength is 9.3 N / cm 2 in shear strength and 0.65 N / cm in peel strength, and the engagement strength after repeated engagement and separation 5000 times is also 7 in shear strength. The peel strength was 0.93 N / cm 2 , which was far inferior to that of Example 1. The reason is that the hook-like engagement element is soft, and the hook shape is extended by a low tensile force, and the engagement is disengaged, which is considered to have influenced the engagement force. Regarding the flexibility of the base fabric, it was equal to or better than that of Example 1.
実施例４
芯鞘型複合繊維の鞘成分に添加する無機微粒子として、硫酸バリウムを鞘成分樹脂に対して、０．３質量％添加する以外は実施例１と同様の方法により、フック・ループ混在型の面ファスナーを作製した。
得られたフック・ループ混在型面ファスナーは、実施例１のものと比べて同等の優れた係合強力と係合耐久性を有し、柔軟性においても、実施例１のものと殆ど変わらない優れた性能を有していた。得られた面ファスナーはカーテンの端部に取り付けて、止め具として使用したところ、面ファスナーが取り付けられていることにより、ひだ形成が劣ることなく、自然な美しいひだを有するカーテンとすることができた。
Example 4
A hook-and-loop mixed surface is obtained in the same manner as in Example 1 except that 0.3% by mass of barium sulfate is added to the sheath component resin as inorganic fine particles to be added to the sheath component of the core-sheath composite fiber. A fastener was made.
The obtained hook / loop mixed surface fastener has the same superior engagement strength and engagement durability as those of the first embodiment, and the flexibility is almost the same as that of the first embodiment. It had excellent performance. The obtained hook-and-loop fastener is attached to the end of the curtain and used as a stopper. By attaching the hook-and-loop fastener, it is possible to obtain a curtain having natural beautiful folds without inferior fold formation. It was.
１：基布
２：フック状係合素子
３：ループ状係合素子
４：地経糸方向
５：地緯糸方向
1: base fabric 2: hook-like engagement element 3: loop-like engagement element 4: ground warp direction 5: ground weft direction
Claims (5)
１）該モノフィラメントがポリエチレンテレフタレート系ポリエステルから形成されており、該マルチフィラメントがポリブチレンテレフタレート系ポリエステルから形成されていること、
２）該織物基布を構成する地経糸がポリエチレンテレフタレート系ポリエステルからなるマルチフィラメント糸であること、
３）該織物基布を構成する地緯糸が、低融点ポリエステルを鞘成分とする芯鞘型の熱融着性フィラメントからなるマルチフィラメント糸であること、
４）該熱融着性フィラメントの鞘成分には、鞘成分構成樹脂に対して０．０３〜１質量％の無機微粒子が添加されていること、
５）該係合素子を構成するモノフィラメントおよびマルチフィラメントが該織物基布を構成している地緯糸により融着固定されていること、 A hook-and-loop fastener having a hook-like engagement element made of monofilament and a loop-like engagement element made of multifilament on the same surface of the woven fabric, and satisfying all of the following 1) to 5): -A hook-and-loop fastener with loops.
1) The monofilament is formed from a polyethylene terephthalate polyester, and the multifilament is formed from a polybutylene terephthalate polyester.
2) The ground warp yarn constituting the woven fabric is a multifilament yarn made of polyethylene terephthalate polyester,
3) The ground weft constituting the woven fabric is a multifilament yarn comprising a core-sheath type heat-fusible filament having a low melting point polyester as a sheath component,
4) 0.03 to 1% by mass of inorganic fine particles are added to the sheath component of the heat-fusible filament with respect to the sheath component constituent resin;
5) The monofilament and multifilament constituting the engaging element are fused and fixed by the ground weft constituting the fabric base fabric,