JP2014029107A - Transparent composite sheet for repairing or reinforcing concrete structure - Google Patents

Transparent composite sheet for repairing or reinforcing concrete structure Download PDF

Info

Publication number
JP2014029107A
JP2014029107A JP2013133430A JP2013133430A JP2014029107A JP 2014029107 A JP2014029107 A JP 2014029107A JP 2013133430 A JP2013133430 A JP 2013133430A JP 2013133430 A JP2013133430 A JP 2013133430A JP 2014029107 A JP2014029107 A JP 2014029107A
Authority
JP
Japan
Prior art keywords
transparent
composite sheet
biaxially stretched
stretched film
reinforcing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2013133430A
Other languages
Japanese (ja)
Other versions
JP6082666B2 (en
Inventor
Takayuki Wakahara
貴之 若原
Hiroyasu Hayashi
容靖 林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ube Exsymo Co Ltd
Original Assignee
Ube Exsymo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ube Exsymo Co Ltd filed Critical Ube Exsymo Co Ltd
Priority to JP2013133430A priority Critical patent/JP6082666B2/en
Publication of JP2014029107A publication Critical patent/JP2014029107A/en
Application granted granted Critical
Publication of JP6082666B2 publication Critical patent/JP6082666B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a transparent reinforcing-sheet with which a cracking portion of a deteriorated concrete construction is repaired or reinforced and then it can be visually observed whether a defect such as cracking of the concrete construction is progressed in the repaired or reinforced portion.SOLUTION: A transparent composite sheet for repairing or reinforcing a concrete construction of which the visible light transmissivity is 80% or more, comprises: (i) a gas non-permeable layer configured by curing a soft curable transparent resin composition (A); at least one layer of (ii) a transparent biaxial drawing film of which one-side surface is laminated on the gas non-permeable layer and in which a round hole having an inner diameter of 1 to 2 mm is deployed continuously in a zigzag manner at 60° or 45° and an aperture of the round hole is 5 to 30%; and (iii) a transparent main body resin layer configured by curing a soft curable transparent resin composition (B) having compatibility with the gas non-permeable layer so as to fill the round hole part of the biaxial drawing film and to cover another-side surface of the biaxial drawing film.

Description

本発明は、コンクリート製のトンネル、高架車道、橋梁、建築物などのコンクリート構造物の補修又は補強用透明複合シートに関するものである。   The present invention relates to a transparent composite sheet for repairing or reinforcing concrete structures such as concrete tunnels, elevated carriageways, bridges, and buildings.

コンクリート構造物は風雨に曝されるため経年劣化し、約30〜40年で変状を来たすようになる。しかし、造り直すには莫大な費用がかかるため、ひび割れやがれた部分を補修又は補強をしながら使用しているのが現状である。
一方で橋梁やトンネルなどの検査は目視確認や打音調査が主流となっている。
従来において、コンクリート構造物の補修又は補強は、繊維シートやフッ素シートを接着剤で貼り付けるため、これらは不透明であり、施工を行った後は、目視検査が出来ないという問題があった。
また、一部には、目視確認が出来るように透明性を上げる工法も開発されているが、ガラス繊維やビニロン繊維を用いたメッシュ状物をコンクリートに直接貼り付け、それに屈折率を合わせたエポキシ樹脂やアクリル樹脂などの硬化性樹脂を含浸するため、紫外線硬化設備を必要とし、気泡が入り込んだり、繊維が白く浮いて見えるなど問題があった。
Since concrete structures are exposed to wind and rain, they deteriorate over time and become deformed in about 30 to 40 years. However, since the reshaping takes enormous cost, at present, it is used with the repair or reinforce the cracking and peeling are a part.
On the other hand, the inspection of bridges and tunnels mainly consists of visual confirmation and hammering investigation.
Conventionally, since repair or reinforcement of a concrete structure is performed by attaching a fiber sheet or a fluorine sheet with an adhesive, they are opaque and have a problem that visual inspection cannot be performed after construction.
In addition, some methods have been developed to increase transparency so that visual confirmation can be made, but an epoxy with a glass fiber or vinylon fiber mesh attached directly to concrete and with a refractive index matched to it. In order to impregnate a curable resin such as a resin or an acrylic resin, an ultraviolet curing facility is required, and there are problems such as bubbles entering and fibers appear to float white.

一方、本出願人は、コンクリート構造物の補修又は補強用繊維強化樹脂シートについて鋭意検討し、少なくとも(i)透明樹脂からなる非通気性層、及び(ii)補強繊維によって所定の開口部が形成されたメッシュ体に該非通気性層と相溶性を有する硬化性透明樹脂を含浸して硬化した繊維強化樹脂本体層を備える繊維強化樹脂シートを提案した(特許文献1参照)。
特許文献1により提案された繊維強化樹脂シートは、メッシュ体の開口部は透明であるが、メッシュ体を構成する繊維が不透明であるため、この部分の陰のコンクリート表面は観察することができず、小さなひび割れを見落とす可能性があった。
また、これまでに防煙垂壁用途などでは、高透明な繊維強化樹脂(FRP)は存在していたが、天井面等のコンクリート剥落防止用途では、コンクリートに固着させる必要から、ガラス繊維等の補強繊維を現地現場で含浸硬化させる工法しかなかった。
On the other hand, the present applicant has intensively studied a fiber reinforced resin sheet for repairing or reinforcing a concrete structure, and at least (i) a non-breathable layer made of a transparent resin, and (ii) a predetermined opening is formed by the reinforcing fiber. A fiber reinforced resin sheet provided with a fiber reinforced resin main body layer obtained by impregnating the cured mesh body with a curable transparent resin having compatibility with the air-impermeable layer and curing it was proposed (see Patent Document 1).
In the fiber reinforced resin sheet proposed by Patent Document 1, the opening of the mesh body is transparent, but the fibers constituting the mesh body are opaque, so the concrete surface behind this part cannot be observed. There was the possibility of overlooking small cracks.
In addition, a highly transparent fiber reinforced resin (FRP) has existed so far for smoke-proof wall applications, but for concrete peeling prevention applications such as ceiling surfaces, it is necessary to adhere to concrete. There was only a method to impregnate and harden the reinforcing fiber on site.

特開2010−242493号公報JP 2010-242493 A

そこで、本発明者らは、コンクリート剥落防止用の補強シートについて鋭意検討した結果、FRPなど補強繊維を用いたもので補強するという概念を捨て、強度を備えた透明な延伸フィルムで覆うという新しい着想に到達した。ただし、コンクリートの剥落防止の補強シートとしては、コンクリート片の剥落部分が分かるように後述する押抜き試験において、10mm以上の伸びが必要とされているため、延伸フィルムを用いて、種々の実験を行った。
まず、二軸延伸ポリエチレンテレフタレート(PET)フィルム(以下、単に「PETフィルム」ということがある。)単体を接着剤でコンクリートに貼り付けて押抜き試験を行ったところ、早い段階で亀裂が入り、亀裂を起点に裂けていく為、押抜き試験で必要な耐力が出ないことが判明した。
これは、接着剤(エポキシ系)自体に伸びが無いため、PETフィルムを接着剤で貼り付けるとPETフィルムのどこか一点に応力が集中して裂けるのが原因であった。
この応力集中を回避し、応力を分散させるために、PETフィルムにパンチング処理をして丸孔を設けると少しは伸びによる変形に対して追従するが、この場合も一旦亀裂が発生するとマジックカットのようになって、亀裂が速く進行した。
次にパンチング処理無しのPETフィルムの両面を軟質樹脂で挟み込んだが、当然ながら応力集中による亀裂の発生を抑える効果は認められなかった。
そもそも、二軸延伸PETフィルムは、それ自体は強靭であり、引張試験においても連続繊維工法に使用されるFRPと同等の強度、弾性率、伸びを有している。しかし、難点はフィルムであるが故に応力集中しやすく、応力集中した部分に亀裂が発生し、さらに延伸しているため裂けやすいことが上記の実験から確認できた。
Therefore, as a result of intensive studies on the reinforcing sheet for preventing concrete peeling, the present inventors have abandoned the concept of reinforcing with a reinforcing fiber such as FRP and covered it with a transparent stretched film having strength. Reached. However, as a reinforcing sheet for preventing concrete from peeling off, it is necessary to elongate 10 mm or more in a push-out test to be described later so that the peeling part of the concrete piece can be seen. went.
First, when a biaxially stretched polyethylene terephthalate (PET) film (hereinafter sometimes simply referred to as “PET film”) was stuck to concrete with an adhesive and subjected to a punching test, cracks occurred at an early stage. It was found that the required strength was not obtained in the punching test because it cracked from the crack.
This is because the adhesive (epoxy system) itself does not stretch, and when the PET film is pasted with the adhesive, the stress concentrates on one point of the PET film and tears.
In order to avoid this stress concentration and disperse the stress, if the PET film is punched and provided with a round hole, it will follow the deformation due to elongation. As a result, the crack progressed faster.
Next, both sides of the PET film without punching treatment were sandwiched between soft resins, but naturally, the effect of suppressing the occurrence of cracks due to stress concentration was not recognized.
In the first place, the biaxially stretched PET film itself is tough and has the same strength, elastic modulus, and elongation as the FRP used in the continuous fiber construction method in the tensile test. However, it was confirmed from the above experiment that the difficulty was that the film was easily stress concentrated because of the film, cracks were generated at the stress concentrated part, and the film was further stretched and thus easily cracked.

本発明は、劣化したコンクリート構造物のひび割れ部分を補修又は補強した後、その後当該補修又は補強部位のコンクリート構造物のひび割れ等の欠陥の進展の有無を目視観察できる透明な補強用シートを提供することを目的とする。
上記目的を達成するため、本発明者は、延伸フィルムを用いても亀裂の進行のない補強シートの構成について鋭意検討し、二軸延伸フィルムにパンチング処理(加工)した場合、パンチング孔はエッジ部分が僅かにギザギザしているので、そこを起点に亀裂が発生するが、パンチング穴に埋めるように軟質な透明樹脂で包んで複合シートにすると、亀裂の進行が抑えられ、コンクリート構造物の補修又は補強シートの機能を発現することを見出し、本発明を完成した。
The present invention provides a transparent reinforcing sheet capable of visually observing the progress of defects such as cracks in a concrete structure at a repaired or reinforced part after repairing or reinforcing a cracked part of a deteriorated concrete structure. For the purpose.
In order to achieve the above object, the present inventor has intensively studied the configuration of a reinforcing sheet that does not progress even if a stretched film is used, and when punching (processing) the biaxially stretched film, the punching hole has an edge portion. However, if it is wrapped in a soft transparent resin so as to fill in the punching hole and made into a composite sheet, the progress of the crack can be suppressed and repair of the concrete structure or It discovered that the function of a reinforcement sheet was expressed, and completed this invention.

すなわち、本発明は、(1)可視光線透過率が80%以上のコンクリート構造物の補修又は補強用透明複合シートであって、該透明複合シートは、(i)軟質な硬化性透明樹脂組成物(A)を硬化してなる非通気性層、(ii)一方の面が該非通気性層に積層され、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開し、丸孔の開口率が5〜30%である透明な二軸延伸フィルム、及び(iii)該二軸延伸フィルムの丸孔部を充填し、かつ二軸延伸フィルムの他方の面を覆うように、非通気性層と相溶性を有する軟質な硬化性透明樹脂組成物(B)を硬化してなる透明本体樹脂層、を備えることを特徴とするコンクリート構造物の補修又は補強用透明複合シート、
(2)前記軟質な硬化性透明樹脂組成物(A)及び(B)が、共にウレタンアクリレート樹脂を主成分としてなる、(1)に記載の透明複合シート、及び
(3)二軸延伸フィルムがフィルム厚み50〜250μmのポリエステル製二軸延伸フィルムである(1)又は(2)に記載の透明複合シート、
を提供するものである。
That is, the present invention provides (1) a transparent composite sheet for repairing or reinforcing a concrete structure having a visible light transmittance of 80% or more, the transparent composite sheet comprising: (i) a soft curable transparent resin composition (A) a non-breathable layer obtained by curing (A), (ii) one surface is laminated on the non-breathable layer, and round holes having an inner diameter of 1 to 2 mm are continuously developed in a zigzag pattern of 60 ° or 45 °. A transparent biaxially stretched film having a round hole opening ratio of 5 to 30%, and (iii) filling the round hole portion of the biaxially stretched film and covering the other surface of the biaxially stretched film A transparent composite sheet for repairing or reinforcing a concrete structure, comprising a transparent main body resin layer obtained by curing a soft curable transparent resin composition (B) having compatibility with a non-breathable layer,
(2) The soft composite curable transparent resin composition (A) and (B) are both composed of a urethane acrylate resin as a main component, the transparent composite sheet according to (1), and (3) a biaxially stretched film The transparent composite sheet according to (1) or (2), which is a polyester biaxially stretched film having a film thickness of 50 to 250 μm,
Is to provide.

本発明のコンクリート構造物の補修又は補強用透明複合シートは、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開し、丸孔の開口率が5〜30%である透明な二軸延伸フィルムを補強材とし、該二軸延伸フィルムと軟質な硬化性透明樹脂組成物の硬化物との複合シートとすることで、二軸延伸フィルムの強度における方向性がなく、かつ複合シートに作用した応力が均等に分散され、繊維状メッシュ材を補強材とした場合と同様に、補修又は補強性能を発現でき、かつ、可視光線透過率が80%以上なので、コンクリート構造物表面の視認が可能な透明複合シートを提供できる。
本発明のコンクリート構造物の補修又は補強用透明複合シートは、軟質な硬化性透明樹脂組成物(A)を硬化してなる非通気性層を有しているので、透明複合シートを工事対象箇所に貼するに際して、コンクリート表面に塗布された未硬化状の接着剤が、透明複合シートの透明本体樹脂層に不可避的に存在する気泡等に起因する貫通孔から滴下することが無いので、施工時に表面を養生シートで覆い、硬化後に補強シート表面に垂れ下がった接着剤を除去する等の付随的な作業が不要であり、非常に簡易化された施工法とすることができ、かつ、ピンホールや気泡による欠陥部分がないので、コンクリート面を外気から遮断して、塩化物イオン等によるコンクリート表面の劣化を防止できる。
The transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention has a round hole with an inner diameter of 1 to 2 mm continuously developed in a staggered shape of 60 ° or 45 °, and the opening ratio of the round hole is 5 to 30%. By using a transparent biaxially stretched film as a reinforcing material and a composite sheet of the biaxially stretched film and a soft curable transparent resin composition, there is no directionality in the strength of the biaxially stretched film, In addition, the stress acting on the composite sheet is evenly distributed, and, as in the case where the fibrous mesh material is used as a reinforcing material, the repair or reinforcing performance can be expressed and the visible light transmittance is 80% or more. A transparent composite sheet capable of visually recognizing the surface can be provided.
The transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention has a non-breathable layer formed by curing a soft curable transparent resin composition (A). in that pasting, the uncured adhesive applied to the concrete surface, since there is no dripping from the through-hole due to the air bubbles that inevitably present in the transparent body resin layer of the transparent composite sheet construction Sometimes the surface is covered with a curing sheet, and additional work such as removing the adhesive hanging on the surface of the reinforcing sheet after curing is unnecessary, and a very simplified construction method can be achieved, and a pinhole Since there are no defects due to or bubbles, the concrete surface can be shielded from the outside air to prevent deterioration of the concrete surface due to chloride ions or the like.

(A)本発明のコンクリート構造物の補修又は補強用透明複合シートの一例の上面模式図、(B)X−X線拡大断面模式図である。(A) The upper surface schematic diagram of an example of the transparent composite sheet for repair or reinforcement of the concrete structure of this invention, (B) XX line expanded sectional schematic diagram. (A)本発明のコンクリート構造物の補修又は補強用透明複合シートの層構成を示す模式斜視図、(B)丸孔を有する二軸延伸フィルムの模式斜視図である。(A) The model perspective view which shows the laminated constitution of the transparent composite sheet for repair or reinforcement of the concrete structure of this invention, (B) A model perspective view of the biaxially stretched film which has a round hole. (A)丸孔を有する二軸延伸フィルムのおける60°千鳥状丸孔パターンの説明図、(B)同45°千鳥状丸孔パターンの説明図である。(A) It is explanatory drawing of the 60 degree zigzag round hole pattern in the biaxially stretched film which has a round hole, (B) It is explanatory drawing of the 45 degree zigzag round hole pattern. 実施例1による透明複合シートの押抜き試験における荷重−変位曲線を示すチャートである。2 is a chart showing a load-displacement curve in a punching test of a transparent composite sheet according to Example 1. FIG. (A)本発明のコンクリート構造物の補修又は補強用透明複合シートの他の例の上面模式図、(B)X−X線拡大断面模式図である。(A) The upper surface schematic diagram of the other example of the transparent composite sheet for repair or reinforcement of the concrete structure of this invention, (B) XX expanded sectional schematic diagram.

以下、本発明の好適な実施形態について説明する。なお、添付図面に示された各実施形態は、本発明に係わる代表的な実施形態の一例を示したものであり、これにより本発明の範囲が狭く解釈されることはない。   Hereinafter, preferred embodiments of the present invention will be described. Each embodiment shown in the accompanying drawings shows an example of a typical embodiment according to the present invention, and the scope of the present invention is not interpreted narrowly.

本発明のコンクリート構造物の補修又は補強用透明複合シートは、(1)可視光線透過率が80%以上のコンクリート構造物の補修又は補強用透明複合シートであって、(i)軟質な硬化性透明樹脂組成物(A)を硬化してなる非通気性層、(ii)一方の面が該非通気性層に積層され、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開し、丸孔の開口率が5〜30%である透明な二軸延伸フィルム、及び(iii)該二軸延伸フィルムの丸孔部を充填し、かつ二軸延伸フィルムの他方の面を覆うように、非通気性層と相溶性を有する軟質な硬化性透明樹脂組成物(B)を硬化してなる透明本体樹脂層、を備えることを特徴とする。   The transparent composite sheet for repair or reinforcement of a concrete structure of the present invention is (1) a transparent composite sheet for repair or reinforcement of a concrete structure having a visible light transmittance of 80% or more, and (i) a soft curability. A non-breathable layer formed by curing the transparent resin composition (A), (ii) one surface is laminated on the non-breathable layer, and round holes having an inner diameter of 1 to 2 mm are continuously formed in a zigzag pattern of 60 ° or 45 ° A transparent biaxially stretched film having a round hole opening ratio of 5 to 30%, and (iii) filling the round hole portion of the biaxially stretched film, and the other side of the biaxially stretched film And a transparent main body resin layer formed by curing a soft curable transparent resin composition (B) having compatibility with the air-impermeable layer.

本発明のコンクリート構造物の補修又は補強用透明複合シートは、施工後のコンクリート構造物の表面のひび割れなど微細な変化を経時的に観察できる透明性を確保する観点から、可視光線透過率が80%以上であることを要する。
本発明において、非通気性層とは、施工時にコンクリート構造物に透明複合シートを接着剤により貼り付ける際に、ピンホール等がなく、接着剤が浸透漏出することのない程度の非通気性層を意味する。非通気性層は、接着剤を浸透漏出させない観点から25〜125μmの厚みであることが好ましい。
非通気性層は、軟質な硬化性樹脂組成物(A)を硬化して形成された層であり、軟質な硬化性樹脂組成物(A)は、硬化後の該非通気性層に積層される二軸延伸フィルムの丸孔(開口)部を通して接触し、硬化後に当該丸孔開口部を充填し、かつ二軸延伸フィルムの他方の面を覆う透明本体樹脂層を形成する軟質な硬化性樹脂組成物(B)と相溶性を有するものから選択され、軟質な硬化性透明樹脂組成物(A)と(B)は同一であってもよい。
硬化性樹脂組成物(A)及び(B)は、硬化した後にあっては、丸孔開口部を有する二軸延伸フィルムと一体的に接着して、透明複合シートを構成する。
The transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention has a visible light transmittance of 80 from the viewpoint of ensuring transparency that allows fine changes such as cracks on the surface of the concrete structure after construction to be observed over time. % Or more.
In the present invention, the non-breathable layer is a non-breathable layer that does not have pinholes or the like and prevents the adhesive from penetrating and leaking when the transparent composite sheet is attached to the concrete structure with an adhesive during construction. Means. The non-breathable layer preferably has a thickness of 25 to 125 μm from the viewpoint of preventing the adhesive from penetrating and leaking.
The non-breathable layer is a layer formed by curing the soft curable resin composition (A), and the soft curable resin composition (A) is laminated on the non-breathable layer after curing. A soft curable resin composition that contacts through a round hole (opening) portion of a biaxially stretched film, fills the round hole opening after curing, and forms a transparent main body resin layer that covers the other surface of the biaxially stretched film It is selected from those having compatibility with the product (B), and the soft curable transparent resin compositions (A) and (B) may be the same.
After the curable resin compositions (A) and (B) are cured, they are integrally bonded with a biaxially stretched film having a round hole opening to constitute a transparent composite sheet.

本発明のコンクリート構造物の補修又は補強用透明複合シートを製造するには、一例として、キャリアフィルム上に軟質な硬化性透明樹脂(A)を塗布しこれを硬化する非通気性層形成工程と、形成された非通気性層上で、丸孔の開口率が5〜30%二軸延伸フィルム、及び非通気性層に対して相溶性を有する軟質な硬化性透明樹脂(B)とをカバーフィルムとの間に挟み込んで、前記二軸延伸フィルムの丸孔開口部に前記硬化性透明樹脂(B)を含浸・硬化し、透明本体樹脂層を形成する工程とを備える、製造方法を提案することができる。
また、非通気性層は、施工時に未硬化状の接着剤等の液体を通さないという機能の点からは、透明複合シートの少なくとも片面に1層あればよいが、カバーフィルムを既に硬化した軟質な透明樹脂フィルムとし、その上で二軸延伸フィルムに硬化性透明樹脂(B)を含浸・硬化することもできる。
なお、キャリアフィルム上への硬化性透明樹脂組成物(A)の塗布や、形成された非通気性層上、もしくは非通気性層上に導入された二軸延伸フィルム上への硬化性透明樹脂組成物(B)の塗布には、一般的な塗工装置が使用でき、例えばグラビアリバース、グラビアダイレクト、三本リバース、ダイコートなどの中から選んで使用できる。
In order to manufacture a transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention, as an example, a non-breathable layer forming step of applying a soft curable transparent resin (A) on a carrier film and curing it, A biaxially stretched film having a round hole opening ratio of 5 to 30% on the formed non-breathable layer and a soft curable transparent resin (B) having compatibility with the non-breathable layer And a step of impregnating and curing the curable transparent resin (B) in a round hole opening of the biaxially stretched film to form a transparent main body resin layer, sandwiched between the film and the film. be able to.
The non-breathable layer may be a single layer on at least one side of the transparent composite sheet from the viewpoint of the function of preventing liquid such as uncured adhesive during construction, but the cover film has already been cured. It is also possible to impregnate and cure the biaxially stretched film with the curable transparent resin (B).
In addition, curable transparent resin on the biaxially stretched film introduce | transduced on application | coating of the curable transparent resin composition (A) on a carrier film, the formed air-impermeable layer, or an air-impermeable layer For application of the composition (B), a general coating apparatus can be used, for example, gravure reverse, gravure direct, triple reverse, die coating, etc. can be used.

非通気性層に用いられる軟質な硬化性透明樹脂組成物(A)としては、透明本体樹脂層に用いられる軟質な硬化性透明樹脂組成物(B)と相溶性(接着性を含む)を有し、かつ、機械的物性において透明複合シートの構成材料としての機能を有する硬化性透明樹脂から選択される。この種の軟質な硬化性透明樹脂組成物(A)及び(B)〔以下、軟質な硬化性透明樹脂組成物(A)及び(B)を区分することなく「硬化性透明樹脂組成物」ということがある。〕として、具体的には、ウレタンアクリレート樹脂(a)、ビニルエステル樹脂(b)、重合性単量体(c)、光重合開始剤(d)、及び熱重合開始剤(e)を含むものから構成されるものを挙げることができる。
さらに、本発明に用いられる軟質な硬化性透明樹脂組成物は、ウレタンアクリレート樹脂を主成分とするものが好ましい。
具体的には、ウレタンアクリレート樹脂(a)及びビニルエステル樹脂(b)は、軟質な硬化性透明樹脂の本体を構成するものであり、ウレタンアクリレート樹脂(a)とビニルエステル樹脂(b)との質量比は、ウレタンアクリレート樹脂(a)/ビニルエステル樹脂(b)で概ね10/0〜5/5とするのが好ましい。質量比が5/5を超えてビニルエステル樹脂(b)の比が高くなると柔軟性が低下する。
The soft curable transparent resin composition (A) used for the non-breathable layer has compatibility (including adhesiveness) with the soft curable transparent resin composition (B) used for the transparent main body resin layer. And it selects from the curable transparent resin which has a function as a constituent material of a transparent composite sheet in a mechanical physical property. This type of soft curable transparent resin composition (A) and (B) [hereinafter referred to as “curable transparent resin composition” without distinguishing soft curable transparent resin compositions (A) and (B)] Sometimes. ], Specifically, containing urethane acrylate resin (a), vinyl ester resin (b), polymerizable monomer (c), photopolymerization initiator (d), and thermal polymerization initiator (e) Can be mentioned.
Further, the soft curable transparent resin composition used in the present invention preferably has a urethane acrylate resin as a main component.
Specifically, the urethane acrylate resin (a) and the vinyl ester resin (b) constitute a main body of a soft curable transparent resin, and the urethane acrylate resin (a) and the vinyl ester resin (b) The mass ratio is preferably about 10/0 to 5/5 in terms of urethane acrylate resin (a) / vinyl ester resin (b). When the mass ratio exceeds 5/5 and the ratio of the vinyl ester resin (b) increases, the flexibility decreases.

本発明において前記ウレタンアクリレート樹脂(a)とは、不飽和ポリエステル製造時に使用される多価アルコール類、または不飽和ポリエステル製造時に使用される飽和2塩基酸またはその無水物と該多価アルコールとのエステル化反応で得られる飽和のポリエステルポリオールと、トリレンジイソシアナート(一般にTDIと呼ばれている)、4,4−ジフェニルメタンジイソシアナート(一般にMDIと呼ばれている)または3−イソシアナートメチル−3,5,5−トリメチルシクロヘキシル−イソシアナート(一般にIPDIと呼ばれている)とを、付加反応させて分子の末端にイソシアナート基を有するウレタン化合物を合成し、次に2−ヒドロキシエチルメタクリレートまたは2−ヒドロキシエチルアクリレートを付加反応させるか、または先ず2−ヒドロキシエチルメタクリレートまたは2−ヒドロキシエチルアクリレートとTDI,MDIまたはIPDIとを付加反応させて分子の片方の端にイソシアナート基を有する化合物を合成し、次にこれと該多価アルコールまたは該飽和のポリエステルポリオールとを付加反応させて得られるウレタンアクリレートを、架橋剤として使用される重合性単量体に溶解した液状の樹脂である。   In the present invention, the urethane acrylate resin (a) is a polyhydric alcohol used in the production of an unsaturated polyester, or a saturated dibasic acid or anhydride thereof used in the production of an unsaturated polyester and the polyhydric alcohol. Saturated polyester polyols obtained by esterification reaction with tolylene diisocyanate (commonly called TDI), 4,4-diphenylmethane diisocyanate (commonly called MDI) or 3-isocyanate methyl- 3,5,5-Trimethylcyclohexyl-isocyanate (generally called IPDI) is subjected to an addition reaction to synthesize a urethane compound having an isocyanate group at the end of the molecule, and then 2-hydroxyethyl methacrylate or Addition reaction of 2-hydroxyethyl acrylate First, 2-hydroxyethyl methacrylate or 2-hydroxyethyl acrylate and TDI, MDI or IPDI are subjected to an addition reaction to synthesize a compound having an isocyanate group at one end of the molecule, It is a liquid resin in which a urethane acrylate obtained by addition reaction of a monohydric alcohol or the saturated polyester polyol is dissolved in a polymerizable monomer used as a crosslinking agent.

本発明に使用できるビニルエステル樹脂(b)としては、例えばエポキシ樹脂と(メタ)アクリル酸との反応によって製造されるエポキシ(メタ)アクリレート樹脂、末端カルボキシル基を有するポリブタジエンとグリシジル(メタ)アクリレートとの反応によって製造されるポリブタジエンタイプのビニルエステル樹脂などが挙げられ、耐食性及び機械的強度が優れるものである。
なお、本発明において(メタ)アクリレートとは、アクリレート又はメタクリレートを意味する表記である。
Examples of the vinyl ester resin (b) that can be used in the present invention include an epoxy (meth) acrylate resin produced by a reaction between an epoxy resin and (meth) acrylic acid, polybutadiene having a terminal carboxyl group, and glycidyl (meth) acrylate. And polybutadiene type vinyl ester resin produced by the above reaction, and has excellent corrosion resistance and mechanical strength.
In the present invention, (meth) acrylate is a notation meaning acrylate or methacrylate.

かかるエポキシ(メタ)アクリレート樹脂としては、ビスフェノールタイプのエポキシ樹脂と(メタ)アクリロリル基を有するカルボン酸とを反応させたもの、ノボラックタイプのエポキシ樹脂と(メタ)アクリロリル基を有するカルボン酸とを反応させたものを挙げることができる。   As such an epoxy (meth) acrylate resin, a reaction of a bisphenol type epoxy resin and a carboxylic acid having a (meth) acrylol group, a reaction of a novolac type epoxy resin and a carboxylic acid having a (meth) acrylol group Can be mentioned.

上記ビスフェノールタイプのエポキシ樹脂としては、例えばエピクロルヒドリンとビスフェノールA若しくはビスフェノールFとの反応により得られる実質的に1分子中に2個以上のエポキシ基を有するグリシジルエーテル型のエポキシ樹脂、メチルエピクロルヒドリンとビスフェノールA若しくはビスフェノールFとの反応により得られるジメチルグリシジルエーテル型のエポキシ樹脂、あるいはビスフェノールAのアルキレンオキサイド付加物とエピクロルヒドリン若しくはメチルエピクロルヒドリンとから得られるエポキシ樹脂などが挙げられる。   Examples of the bisphenol type epoxy resin include glycidyl ether type epoxy resins having substantially two or more epoxy groups in one molecule obtained by the reaction of epichlorohydrin and bisphenol A or bisphenol F, methyl epichlorohydrin and bisphenol A. Or the dimethyl glycidyl ether type epoxy resin obtained by reaction with bisphenol F, the epoxy resin obtained from the alkylene oxide adduct of bisphenol A, and epichlorohydrin or methyl epichlorohydrin, etc. are mentioned.

また、上記ノボラックタイプのエポキシ樹脂としては、例えばノボラック型フェノール樹脂又はノボラック型クレゾール樹脂とエピクロルヒドリン又はメチルエピクロルヒドリンとの反応により得られるエポキシ樹脂などが挙げられる。   Examples of the novolac type epoxy resin include an epoxy resin obtained by a reaction of a novolac type phenol resin or a novolac type cresol resin with epichlorohydrin or methyl epichlorohydrin.

本発明に使用できる重合性単量体(c)としては、前記のウレタンアクリレート樹脂(a)及びビニルエステル樹脂(b)と重合可能な液状重合性単量体であって、例えばメチルメタクリレート、エチルメタクリレート、プロピルメタクリレート、イソプロピルメタクリレート、ブチルメタクリレート、及びヒドロキシエチルメタクリレート等のメタクリル酸エステル、(メタ)アクリル酸、スチレン等挙げられる。これらのうち、低温で反応させる観点から、メチルメタクリレート、あるいは高沸点である観点からスチレンが好ましく、これらは単独又は2種以上を併用して用いることができる。   The polymerizable monomer (c) that can be used in the present invention is a liquid polymerizable monomer that can be polymerized with the urethane acrylate resin (a) and the vinyl ester resin (b), and includes, for example, methyl methacrylate, ethyl And methacrylates such as methacrylate, propyl methacrylate, isopropyl methacrylate, butyl methacrylate, and hydroxyethyl methacrylate, (meth) acrylic acid, and styrene. Of these, methyl methacrylate is preferred from the viewpoint of reacting at a low temperature, or styrene is preferred from the viewpoint of high boiling point, and these can be used alone or in combination of two or more.

本発明に使用できる硬化性透明樹脂組成物は、光重合開始剤(d)を含有することができる。
使用できる光重合開始剤(d)としては、光の作用または増感色素の電子励起状態との相互作用を経て、化学変化を生じ、ラジカル、酸、および塩基のうちの少なくともいずれか1種を生成する化合物である。本発明において光重合開始剤は、照射される活性光線、例えば、400〜200nmの紫外線、遠紫外線、g線、h線、i線、KrFエキシマレーザー光、ArFエキシマレーザー光、電子線、X線、分子線、またはイオンビーム等に感度を有するものを適宜選択して使用することができる。ただし、カバーフィルムを透過することが条件として挙げられる。
The curable transparent resin composition that can be used in the present invention can contain a photopolymerization initiator (d).
As the photopolymerization initiator (d) that can be used, a chemical change occurs through the action of light or interaction with the electronically excited state of the sensitizing dye, and at least one of radical, acid, and base is selected. It is a compound to be formed. In the present invention, the photopolymerization initiator is an actinic ray to be irradiated, for example, 400 to 200 nm ultraviolet ray, far ultraviolet ray, g ray, h ray, i ray, KrF excimer laser beam, ArF excimer laser beam, electron beam, X ray. Those having sensitivity to a molecular beam, an ion beam, or the like can be appropriately selected and used. However, it is mentioned as conditions that permeate | transmits a cover film.

光重合開始剤(d)としては、例えば、芳香族ケトン類、芳香族オニウム塩化合物、有機過酸化物、ヘキサアリールビイミダゾール化合物、ケトオキシムエステル化合物、ボレート化合物、アジニウム化合物、メタロセン化合物、活性エステル化合物、炭素ハロゲン結合を有する化合物等を挙げることができる。
より具体的には、例えば、ベンゾフェノン、ベンゾインメチルエーテル、ベンゾインプロピルエーテル、ジエトキシアセトフェノン、1−ヒドロキシシクロヘキシルフェニルケトン、2,6−ジメチルベンゾイルジフェニルホスフィンオキシド、2,4,6−トリメチルベンゾイルジフェニルホシフィンオキシド等が挙げられる。これらの中でも、1−ヒドロキシシクロヘキシルフェニルケトン、2,4,6−トリメチルベンゾイルジフェニルホスフィンオキシド、などの光重合開始剤が特に好ましい。これらの光重合開始剤は単独で用いても、2種以上を併用してもよい。
Examples of the photopolymerization initiator (d) include aromatic ketones, aromatic onium salt compounds, organic peroxides, hexaarylbiimidazole compounds, ketoxime ester compounds, borate compounds, azinium compounds, metallocene compounds, and active esters. Examples thereof include compounds and compounds having a carbon halogen bond.
More specifically, for example, benzophenone, benzoin methyl ether, benzoin propyl ether, diethoxyacetophenone, 1-hydroxycyclohexyl phenyl ketone, 2,6-dimethylbenzoyldiphenylphosphine oxide, 2,4,6-trimethylbenzoyldiphenylphosphine And oxides. Among these, photopolymerization initiators such as 1-hydroxycyclohexyl phenyl ketone and 2,4,6-trimethylbenzoyldiphenylphosphine oxide are particularly preferable. These photopolymerization initiators may be used alone or in combination of two or more.

光重合開始剤(d)は、ウレタンアクリレート樹脂(a)とビニルエステル樹脂(b)との合計100質量部に対して、0.1〜2質量部の範囲で使用するのが好適である。光重合開始剤(d)が0.1〜2質量部の範囲であれば、硬化速度と生産速度のバランスが取れ、気泡の発生も抑止でき、透明複合シートが硬化不足となることもなく、多すぎて不経済となることもない。   The photopolymerization initiator (d) is preferably used in the range of 0.1 to 2 parts by mass with respect to 100 parts by mass in total of the urethane acrylate resin (a) and the vinyl ester resin (b). If the photopolymerization initiator (d) is in the range of 0.1 to 2 parts by mass, the curing rate and production rate can be balanced, the generation of bubbles can be suppressed, and the transparent composite sheet is not insufficiently cured. Too much is not uneconomical.

本発明に用いられる硬化性透明樹脂組成物は、熱重合開始剤(e)を含有することができる。使用できる熱重合開始剤としては、50〜120℃程度で硬化可能な中温硬化型の有機過酸化物及びそのエステル類、有機アゾ化合物などを挙げることができる。
有機過酸化物としては、1,1−ビス(t−ブチルペルオキシ)−2,2,5−トリメチルシクロヘキサン(日油社製パーヘキサ3M−95)、1,1−ビス(t−ブチルペルオキシ)シクロドデカン(日油社製パーヘキサCD)、1,1,3,3−テトラメチルヒドロペルオキシド(日油社製パーオクタH)、1,1−ジメチルブチルペルオキシド(日油社製パーヘキシルH)、ビス(1−t−ブチルペルオキシ−1−メチルエチル)ベンゼン(日油社製パーブチルP)、ジクミルペルオキシド(日油社製パークミルD)、2,5−ジメチル−2,5−ビス(t−ブチルペルオキシ)ヘキサン(日油社製パーヘキサ25
B)、t−ブチルクミルペルオキシド(日油社製パーブチルC)、ジ−t−ブチルペルオキシド(日油社製パーブチルD)、2,5−ジメチル−2,5−ビス(t−ブチルペルオキシ)ヘキシン(日油社製パーヘキシン25B)、過酸化ベンゾイル、過酸化ラウロイル(日油社製パーロイルL)、過酸化デカノイル(三建化工社製サンペロックス−DPO)、ジシクロヘキシルペルオキシジカーボネート(三建化工社製サンペロックス−CD)、ビス(4−t−ブチルシクロヘキシル)ペルオキシジカーボネート(日油社製パーロイルTCP)、t−ブチル2−エチルペルヘキサノエート(日油社製パーブチルO)、(1,1−ジメチルプロピル)2−エチルペルヘキサノエート(化薬アクゾ社製トリゴノックス121)、(1,1−ジメチルブチル)2−エチルペルヘキサノエート(化薬アクゾ社製カヤエステルHO)、t−ブチル3,5,5−トリメチルペルヘキサノエート(日油社製パーブチル355)、t−ヘキシルパーオキシイソプロピルモノカーボネート(日油社製パーヘキシルI)、t−ブチルパーオキシイソプロピルモノカーボネート(日油社製パーブチルI)、t−ブチルパーオキシ2−エチルヘキシルモノカーボネート(日油社製パーブチルE)、過マレイン酸t−ブチル(日油社製パーブチルMA)、1,1,3,3−テトラメチルブチルパーオキシ−2−エチルヘキサノエート(日油社製パーオクタO)、過ラウリン酸t−ブチル(日油社製パーブチルL)、過安息香酸t−ブチル(日油社製パーブチルZ)などを例示することができる。これらの熱重合開始剤は単独でも、複数混合して用いてもよい。
The curable transparent resin composition used in the present invention can contain a thermal polymerization initiator (e). Examples of the thermal polymerization initiator that can be used include medium temperature curable organic peroxides that can be cured at about 50 to 120 ° C., esters thereof, and organic azo compounds.
As the organic peroxide, 1,1-bis (t-butylperoxy) -2,2,5-trimethylcyclohexane (Perhexa 3M-95 manufactured by NOF Corporation), 1,1-bis (t-butylperoxy) cyclo Dodecane (Peroxa CD manufactured by NOF Corporation), 1,1,3,3-tetramethylhydroperoxide (Perocta H manufactured by NOF Corporation), 1,1-dimethylbutyl peroxide (Perhexyl H manufactured by NOF Corporation), bis (1 -T-Butylperoxy-1-methylethyl) benzene (Nippon Perbutyl P), Dicumyl peroxide (Nippon Park Mill D), 2,5-dimethyl-2,5-bis (t-butylperoxy) Hexane (Perhexa 25 manufactured by NOF Corporation)
B), t-butyl cumyl peroxide (Perbutyl C manufactured by NOF Corporation), di-t-butyl peroxide (Perbutyl D manufactured by NOF Corporation), 2,5-dimethyl-2,5-bis (t-butylperoxy) Hexin (Nippon Perhexine 25B), benzoyl peroxide, lauroyl peroxide (Nippon Parroyl L), decanoyl peroxide (Sanpelox-DPO, Sanken Chemicals), dicyclohexyl peroxydicarbonate (Sanken Chemicals) Sanperox-CD), bis (4-t-butylcyclohexyl) peroxydicarbonate (Perroyl TCP manufactured by NOF Corporation), t-butyl 2-ethylperhexanoate (Perbutyl O manufactured by NOF Corporation), (1, 1-dimethylpropyl) 2-ethylperhexanoate (Trigonox 121 manufactured by Kayaku Akzo), (1,1-dimethyl) (Butyl) 2-ethylperhexanoate (Kaya ester HO manufactured by Kayaku Akzo), t-butyl 3,5,5-trimethylperhexanoate (Perbutyl 355 manufactured by NOF Corporation), t-hexylperoxyisopropyl mono Carbonate (Perhexyl I, NOF Corporation), t-butyl peroxyisopropyl monocarbonate (Perbutyl I, NOF Corporation), t-butyl peroxy 2-ethylhexyl monocarbonate (Perbutyl E, NOF Corporation), t maleic acid t -Butyl (Nippon Perbutyl MA), 1,1,3,3-tetramethylbutyl peroxy-2-ethylhexanoate (Nippon Perocta O), t-butyl perlaurate (Nippon) Examples thereof include Perbutyl L) and t-butyl perbenzoate (Perbutyl Z manufactured by NOF Corporation). These thermal polymerization initiators may be used alone or in combination.

熱重合開始剤は、ウレタンアクリレート樹脂(a)とビニルエステル樹脂(b)との合計100質量部に対して、0.1〜5質量部の範囲で使用するのが好適である。熱重合開始剤が0.1〜5質量部の範囲であれば、透明複合シートが硬化不足となることもなく、多すぎて不経済となることもない。   The thermal polymerization initiator is preferably used in the range of 0.1 to 5 parts by mass with respect to 100 parts by mass in total of the urethane acrylate resin (a) and the vinyl ester resin (b). If the thermal polymerization initiator is in the range of 0.1 to 5 parts by mass, the transparent composite sheet will not be insufficiently cured and will not be uneconomical because it is too much.

硬化性透明樹脂組成物(A)及び(B)には、さらに熱重合開始剤の反応性を制御するために、重合禁止剤や促進剤を加えることができる。重合禁止剤としては、2,6−ジ−t−ブチル−p−クレゾール、2,2'−メチレンビス(4−メチル−6−t−ブチルフェノール)、2,2'−メチレンビス(4−エチル−6−t−ブチルフェノール)、4,4'−チオビス(2−メチル−6−t−ブチルフェノール)、ヒドロキノン、2−t−ブチルヒドロキノン、2,5−ジ−t−ブチルヒドロキノン、p−ベンゾキノン、2−エチルアントラキノン、ジラウリルチオジプロピオネート、クペロンなどを例示することができる。
促進剤としては、遷移金属の塩、例えばナフテン酸コバルトなどを用いることができる。
A polymerization inhibitor and an accelerator can be added to the curable transparent resin compositions (A) and (B) to further control the reactivity of the thermal polymerization initiator. As the polymerization inhibitor, 2,6-di-t-butyl-p-cresol, 2,2′-methylenebis (4-methyl-6-t-butylphenol), 2,2′-methylenebis (4-ethyl-6) -T-butylphenol), 4,4'-thiobis (2-methyl-6-t-butylphenol), hydroquinone, 2-t-butylhydroquinone, 2,5-di-t-butylhydroquinone, p-benzoquinone, 2- Examples include ethyl anthraquinone, dilauryl thiodipropionate, and cuperone.
As the promoter, a transition metal salt such as cobalt naphthenate can be used.

また、硬化性透明樹脂組成物には、所望の透明性が得られる範囲内で、紫外線吸収剤、酸化防止剤などを更に含有していてもよい。透明本体樹脂層の硬化性透明樹脂組成物(B)の粘度は100〜2000cPであることが好ましく、800〜1000cPであることがより好ましい。
硬化性透明樹脂組成物の粘度が低いと液垂れが発生し易くなる傾向があり、硬化性透明樹脂組成物の粘度が高いと丸孔の開口部への含浸が不良となって、形成される透明樹脂層内に気泡が発生し易くなる傾向がある。
Moreover, the curable transparent resin composition may further contain an ultraviolet absorber, an antioxidant and the like within a range in which desired transparency is obtained. The viscosity of the curable transparent resin composition (B) of the transparent main body resin layer is preferably 100 to 2000 cP, and more preferably 800 to 1000 cP.
When the viscosity of the curable transparent resin composition is low, liquid dripping tends to occur. When the viscosity of the curable transparent resin composition is high, impregnation into the opening of the round hole is poor and formed. There is a tendency that bubbles are easily generated in the transparent resin layer.

また、紫外線吸収剤は、屋外での直射日光による二軸延伸フィルムを含む透明複合シートの劣化を防ぐのに有用である。かかる紫外線吸収剤の具体例としては、上記の硬化性透明樹脂組成物に溶解するものであれば特に限定されず、各種紫外線吸収剤を使用することができる。具体的には、サリチル酸エステル系、ベンゾフェノン系、トリアゾール系、ヒドロキシベンゾエート系、シアノアクリレート系などが挙げられる。これらの紫外線吸収剤は複数を組み合わせて用いてもよい。これらの中でも、ウレタンアクリレート系化合物との相溶性の点で、ベンゾフェノン系またはトリアゾール系、具体的には、(2−ヒドロキシ−4−オクチロキシ−フェニル)−フェニル−メタノン、2−ベンゾトリアゾール−2−イル−4−tert−オクチル−フェノール等の紫外線吸収剤が好ましい。
紫外線吸収剤の含有割合は、硬化性透明樹脂組成物100質量部に対して、通常0.1〜3質量部であることが好ましく、特に好ましくは1〜2質量部である。かかる紫外線吸収剤が少なすぎると耐光性が低下する傾向があり、多すぎると硬化性透明樹脂組成物を光硬化する場合には紫外線照射エネルギーを消費して硬化がし難くなる傾向がある。
In addition, the ultraviolet absorber is useful for preventing the deterioration of the transparent composite sheet including the biaxially stretched film due to direct sunlight outdoors. Specific examples of such ultraviolet absorbers are not particularly limited as long as they are soluble in the curable transparent resin composition described above, and various ultraviolet absorbers can be used. Specific examples include salicylic acid ester, benzophenone, triazole, hydroxybenzoate, and cyanoacrylate. These ultraviolet absorbers may be used in combination. Among these, in terms of compatibility with urethane acrylate compounds, benzophenone or triazole, specifically, (2-hydroxy-4-octyloxy-phenyl) -phenyl-methanone, 2-benzotriazole-2- Ultraviolet absorbers such as yl-4-tert-octyl-phenol are preferred.
It is preferable that the content rate of a ultraviolet absorber is 0.1-3 mass parts normally with respect to 100 mass parts of curable transparent resin compositions, Most preferably, it is 1-2 mass parts. When the amount of the ultraviolet absorber is too small, the light resistance tends to be lowered. When the amount is too large, when the curable transparent resin composition is photocured, the ultraviolet irradiation energy is consumed and the curing tends to be difficult.

本発明のコンクリート構造物の補修又は補強用透明複合シートにおいて、補強機能を担う透明な二軸延伸フィルムとして、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開し、丸孔の開口率が5〜30%のものが用いられる。
本発明に使用できる透明な二軸延伸フィルムとしては、ポリエチレンテレフタレート(PET)製二軸延伸フィルム、ポリエチレンナフタレート(PEN)製二軸延伸フィルムなどのポリエステル製二軸延伸フィルム、ポリプロピレン(PP)製二軸延伸フィルムが、透明性、パンチングによる丸孔加工性、機械物性、耐低温性、耐水性、経済性等の観点から好ましく、さらに耐熱性、等方性の観点からポリエステル製二軸延伸フィルムが特に好ましい。また、ポリエステル製二軸延伸フィルムにおいては、低温特性及び紫外線バリア性に優れ、機械的強度が高いという物性上の観点からPEN製二軸延伸フィルムが特に好ましい。
二軸延伸フィルムには、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開している。
かかる丸孔を60°又は45°の千鳥状に連続状に展開させるには、鋼板(ステンレス、鉄、アルミニウム等)にプレスでたくさんの孔を開けるパンチング処理の技術、設備を応用して穿孔すればよい。
In the transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention, as a transparent biaxially stretched film having a reinforcing function, round holes having an inner diameter of 1 to 2 mm are continuously developed in a staggered pattern of 60 ° or 45 °. In addition, those having a round hole opening ratio of 5 to 30% are used.
As a transparent biaxially stretched film that can be used in the present invention, a biaxially stretched film made of polyester such as a biaxially stretched film made of polyethylene terephthalate (PET), a biaxially stretched film made of polyethylene naphthalate (PEN), or a product made of polypropylene (PP) A biaxially stretched film is preferable from the viewpoints of transparency, round hole workability by punching, mechanical properties, low temperature resistance, water resistance, economy, and the like, and from the viewpoint of heat resistance and isotropy, a polyester biaxially stretched film Is particularly preferred. Moreover, in the polyester biaxially stretched film, the PEN biaxially stretched film is particularly preferable from the viewpoint of physical properties such as excellent low temperature characteristics and ultraviolet barrier properties and high mechanical strength.
In the biaxially stretched film, round holes having an inner diameter of 1 to 2 mm are continuously developed in a zigzag shape of 60 ° or 45 °.
In order to develop such round holes continuously in a zigzag shape of 60 ° or 45 °, drilling should be performed by applying punching technology and equipment that make a lot of holes in a steel plate (stainless steel, iron, aluminum, etc.) with a press. That's fine.

丸孔の内径は、直径1〜2mmとすることが、後述する開口率及び基準列と隣列とが千鳥状に展開する上で重要である。
図3(A)は60°千鳥状の丸孔の配列の上面を示す説明図である。同図では、丸孔2は、内径がDで二軸延伸フィルム3の厚みを突き抜けた開口部21を有しており、基準列間の丸孔のピッチはP1、基準列に隣り合う隣列間の丸孔のピッチP2、丸孔間の二軸延伸フィルムの実在(ホネ)部の距離を基準列内についてB1、基準列と隣列間をB2とし、基準列と隣列の各丸孔2の隣り合う中心を結ぶ線の角度を60°とすると、ピッチは、P2=P1×cos30°、実在部の距離は、B1=B2となって、丸孔2が、方向性がない全て均等の間隔で配列される。したがって、60°千鳥状に丸孔が連続的に展開された二軸延伸フィルムでは、荷重が一点に集中することなく分散されるので、さらに、丸孔の内径及び開口率が所定の条件を満たすようにすれば、従来の補強用メッシュ状物と同様にコンクリート構造物の補修又は補強用透明樹脂シートの補強材として使用することができる。
It is important that the inner diameter of the round hole is 1 to 2 mm in diameter in order to develop an aperture ratio and a reference row and a neighboring row, which will be described later, in a staggered manner.
FIG. 3A is an explanatory view showing the upper surface of an array of 60 ° staggered round holes. In the figure, the round hole 2 has an opening 21 that has an inner diameter D and penetrates the thickness of the biaxially stretched film 3, and the pitch of the round holes between the reference rows is P1, and the adjacent row adjacent to the reference row. The pitch P2 of the round holes between them, the distance of the real part of the biaxially stretched film between the round holes as B1 in the reference row, and B2 between the reference row and the adjacent row, each round hole in the reference row and the adjacent row Assuming that the angle of the line connecting the two adjacent centers is 60 °, the pitch is P2 = P1 × cos30 °, the distance of the real part is B1 = B2, and the round holes 2 are all evenly oriented. Are arranged at intervals of Therefore, in the biaxially stretched film in which round holes are continuously developed in a 60 ° zigzag pattern, the load is dispersed without concentrating on one point. Further, the inner diameter and the opening ratio of the round holes satisfy predetermined conditions. By doing so, it can be used as a reinforcing material for repairing concrete structures or reinforcing transparent resin sheets in the same manner as conventional reinforcing mesh-like materials.

図3(B)は、45°千鳥状の丸孔の配列の上面を示す説明図である。基準列と隣列の各丸孔2の隣り合う中心を結ぶ線の角度を45°とすると、ピッチは、P1=2×P2となり基準列と45°をなす方向の丸孔の密度が高く、60°の場合と比較して方向性があるが、45°千鳥状の丸孔の配列でも、従来の補強用メッシュ状物と同様にコンクリート構造物の補修又は補強用透明樹脂シートの補強材として使用することができることが確認された。   FIG. 3B is an explanatory view showing the upper surface of an array of 45 ° staggered round holes. If the angle of the line connecting the adjacent centers of the circular holes 2 in the reference row and the adjacent row is 45 °, the pitch is P1 = 2 × P2, and the density of round holes in the direction forming 45 ° with the reference row is high, Although there is directionality compared to the case of 60 °, even with an array of 45 ° staggered round holes, as a reinforcing material for repairing a concrete structure or a reinforcing transparent resin sheet in the same manner as a conventional reinforcing mesh-like material It was confirmed that it could be used.

丸孔の内径は、直径1〜2mmであることを要し、直径が1mm未満では、丸孔部を充填するための硬化性透明樹脂組成物(B)が含浸され難く、気泡発生の原因となって、透明複合シートの光線透過率を低下させ、また打ち抜きのための金型作製のコストも上昇するので実用的でない。
直径が2mmを超えると、開口率が大きくなって、二軸延伸フィルムの補強材としての機能が低下する。
本発明に使用する二軸延伸フィルムにおける丸孔の開口率は、5〜30%であることを要する。開口率が5%未満では、付着強度及び押抜き試験の最大荷重が規定値を満足せず、30%を超えると押抜き試験の最大変位長さが小さく、かつ最大荷重も規定値に達しない。
The inner diameter of the round hole is required to be 1 to 2 mm in diameter. If the diameter is less than 1 mm, the curable transparent resin composition (B) for filling the round hole portion is difficult to be impregnated, which causes the generation of bubbles. Thus, the light transmittance of the transparent composite sheet is lowered, and the cost for producing a die for punching is increased, which is not practical.
When the diameter exceeds 2 mm, the aperture ratio increases, and the function of the biaxially stretched film as a reinforcing material decreases.
The opening ratio of round holes in the biaxially stretched film used in the present invention is required to be 5 to 30%. If the opening ratio is less than 5%, the maximum strength of the adhesion strength and the punching test does not satisfy the specified value. If the opening ratio exceeds 30%, the maximum displacement length of the punching test is small and the maximum load does not reach the specified value. .

60°千鳥の場合のピッチP1は、開口率X(%)と丸孔の直径Dに基づき、関係式
開口率X(%)=(D2/P12)×90.6 から求めることができる。
同様に45°千鳥のピッチP1は、開口率X(%)と丸孔の直径Dに基づき、関係式
開口率X(%)=(D2/P12)×157 から求めることができる。
The pitch P1 in the case of 60 ° staggered is a relational expression based on the aperture ratio X (%) and the diameter D of the round hole.
The aperture ratio X (%) = (D 2 / P1 2 ) × 90.6.
Similarly, the 45 ° staggered pitch P1 is based on the aperture ratio X (%) and the diameter D of the round hole.
Aperture ratio X (%) = (D 2 / P1 2 ) × 157

以下、本発明を実施例及び比較例により説明するが、本発明はこれらの実施例に限定されるものではない。まず、本発明で使用した特性値の評価方法を下記に示す。   EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention, this invention is not limited to these Examples. First, the evaluation method of the characteristic values used in the present invention is shown below.

(1)二軸延伸フィルムの強伸度の測定
本発明の透明複合シートに用いる、丸孔が所定の直径及びピッチで45°又は60°の千鳥状に展開された二軸延伸フィルムについて、長手方向に沿って25mm幅のサンプルを用意し、JIS C2318−1997「引張強さ及び伸び率」に準じて25mm幅の強伸度を測定した。比較例6のPP/PE複合繊維によるメッシュ体についても、25mm幅のサンプルで同様に強伸度を測定した。
(1) Measurement of strong elongation of biaxially stretched film The biaxially stretched film used in the transparent composite sheet of the present invention is a biaxially stretched film in which round holes are expanded in a staggered shape of 45 ° or 60 ° at a predetermined diameter and pitch. A 25 mm wide sample was prepared along the direction, and the 25 mm wide strong elongation was measured according to JIS C2318-1997 “Tensile strength and elongation”. With respect to the mesh body of the PP / PE composite fiber of Comparative Example 6, the tensile strength was measured in the same manner using a 25 mm wide sample.

(2)コンクリート表面の視認性
コンクリート構造物の補修又は補強用透明複合シートとして施工した際に、その後のコンクリート表面のひび割れ等の経時観察が可能であるかを判定するため、後述の「はく落防止の押抜き試験方法」において、透明な接着剤を用いて上ぶた式U形側溝(ふた)に透明複合シートを貼り付け、接着剤を硬化した状態で、コンクリート表面の視認性を評価した。陰となる部分がなく、貼り付けた透明複合シートの全面においてコンクリートの表面を観察できる場合を「○」、ネットを構成する繊維等の陰でコンクリート表面の全面を観察できない場合を「×」とした。
(2) Visibility of concrete surface When it is constructed as a transparent composite sheet for repairing or reinforcing concrete structures, it will be described later in order to determine whether it is possible to observe cracks on the concrete surface over time. In the "Punching test method", a transparent composite sheet was attached to the upper lid U-shaped side groove (lid) using a transparent adhesive, and the visibility of the concrete surface was evaluated in a state where the adhesive was cured. “○” indicates that the surface of the concrete can be observed on the entire surface of the pasted transparent composite sheet with no shadow, and “×” indicates that the entire surface of the concrete cannot be observed in the shade of the fibers constituting the net. did.

(3)可視光線透過率
透明複合シートの可視光線透過率を日本分光(株)製の「紫外可視近赤外分光光度計V−670」を用い、可視光領域の波長で測定した。
(3) Visible light transmittance The visible light transmittance of the transparent composite sheet was measured at a wavelength in the visible light region using an "ultraviolet visible near infrared spectrophotometer V-670" manufactured by JASCO Corporation.

(4)シート厚み
テクロック(株)製「シックネスゲージSM−528」を用いて、各サンプルについて3点測定して、その平均を求めた。
(4) Sheet Thickness Using a “Sickness Gauge SM-528” manufactured by Teclock Co., Ltd., three points were measured for each sample, and the average was obtained.

(5)付着強度
得られた透明複合シートについて、NEXCO(旧日本道路公団)規格、試験法425−2004:「はく落防止の耐久性能試験方法」の7.3「付着強さ試験」に準じて、コンクリートとの付着強度試験を行なった。エポキシ樹脂(日米レジン社製:XL−1902)を用い、塗布量600g/m2で透明複合シートをコンクリートに貼り付け、硬化養生させ、付着強度試験を行なった。
なお、NEXCO規格では、1.5N/mm2以上が合格とされている。
(5) Adhesive strength For the obtained transparent composite sheet, in accordance with 7.3 “Adhesive strength test” in NEXCO (former Japan Highway Public Corporation) standard, test method 425-2004: “Durability prevention test method” An adhesion strength test with concrete was conducted. Using an epoxy resin (manufactured by Japan-US Resin Co., Ltd .: XL-1902), a transparent composite sheet was applied to concrete at a coating amount of 600 g / m 2 , cured and cured, and an adhesion strength test was performed.
In the NEXCO standard, 1.5 N / mm 2 or more is accepted.

(6)押抜き試験
NEXCO(旧日本道路公団)規格、試験法424−2004:「はく落防止の押抜き試験方法」に準じて、コンクリート片剥落における押し抜き性能の評価としての押抜き試験を行った。
なお、NEXCO規格では、最大変位10mm以上、最大荷重1.5kN以上を合格としている。
(6) Punching test NEXCO (formerly Japan Highway Public Corporation) standard, test method 424-2004: Punching test as an evaluation of punching performance in concrete stripping is performed in accordance with "Peeling prevention punching test method". It was.
In the NEXCO standard, a maximum displacement of 10 mm or more and a maximum load of 1.5 kN or more are acceptable.

実施例1
厚さ50μmのPET製二軸延伸フィルム(東レ(株)製:ルミラー50S10)に、直径1.3mm、ピッチ間隔3.5mmで45°千鳥状に連続状に丸孔が展開するパンチング孔加工を行ない、開口率が21.7%のパンチング処理PET製二軸延伸フィルムを得た。
非通気性層形成用の硬化性透明樹脂組成物(A)として、エポキシアクリレート8.0質量%、ウレタンアクリレート72質量%、及びメタクリル酸メチル20質量%の硬化性透明樹脂(日本ユピカ(株)製、製品名:ネオポール8136)100質量部(粘度1,000cP、25℃)に有機過酸化物(日油(株)製、商品名:パーオクタO−70S)を2質量部添加して、透明樹脂からなる非通気性層を形成するための硬化性透明樹脂組成物(A)を調製した。
この硬化性透明樹脂組成物(A)を、キャリアフィルムとしてのPETフィルム(厚さ25μm)上に塗付し、塗布厚み50μmに調製した。
次いで、加熱炉内にて100℃で10分間加熱によりモノマー(メタクリル酸メチル)を重合させ、非通気性層を形成した。当該非通気性層上に、前述のパンチング処理PET製二軸延伸フィルムと、透明硬化性樹脂組成物(B)(非通気性層を形成するための硬化性透明樹脂組成物(A)と同一組成)を供給し、カバーフィルム(PETフィルム(厚さ25μm))の間に挟みこみ、スクイズローラを用いて厚み300μmに調整した。次いで、加熱炉内にて100℃で10分間加熱によりモノマーを重合させパンチング処理済みの二軸延伸フィルムを積層した透明複合シートを得た。
得られた透明複合シートは、非通気性層の厚みが50μmで、その上にパンチング処理二軸延伸フィルムと透明本体樹脂層が一体に積層され、かつ、パンチングによる丸孔開口部にも透明硬化性樹脂組成物(B)が含浸・硬化しており、透明本体樹脂層の厚みが150μmで、全体厚みが250μm、単位質量270g/m2(キャリアフィルム及びカバーフィルムを除く)であった。
Example 1
Punching hole processing in which round holes are continuously developed in a 45 ° zigzag pattern with a diameter of 1.3 mm and a pitch interval of 3.5 mm on a PET biaxially stretched film (Toray Industries, Inc .: Lumirror 50S10) with a thickness of 50 μm. Then, a punched PET biaxially stretched film having an aperture ratio of 21.7% was obtained.
As a curable transparent resin composition (A) for forming a non-breathable layer, a curable transparent resin of 8.0% by mass of epoxy acrylate, 72% by mass of urethane acrylate, and 20% by mass of methyl methacrylate (Nippon Iupika Co., Ltd.) Product, product name: Neopol 8136) 2 parts by mass of organic peroxide (manufactured by NOF Corporation, trade name: Perocta O-70S) is added to 100 parts by mass (viscosity 1,000 cP, 25 ° C.), transparent A curable transparent resin composition (A) for forming a non-breathable layer made of resin was prepared.
This curable transparent resin composition (A) was applied on a PET film (thickness 25 μm) as a carrier film to prepare a coating thickness of 50 μm.
Next, the monomer (methyl methacrylate) was polymerized by heating at 100 ° C. for 10 minutes in a heating furnace to form a non-breathable layer. On the non-breathable layer, the above-mentioned punched PET biaxially stretched film and the transparent curable resin composition (B) (the same as the curable transparent resin composition (A) for forming the non-breathable layer) Composition) was supplied, sandwiched between cover films (PET film (thickness 25 μm)), and adjusted to a thickness of 300 μm using a squeeze roller. Subsequently, the transparent composite sheet which superposed | polymerized the monomer by heating at 100 degreeC for 10 minute (s) within a heating furnace, and laminated | stacked the punching-processed biaxially stretched film was obtained.
The resulting transparent composite sheet has a non-breathable layer thickness of 50 μm, on which a punching-treated biaxially stretched film and a transparent main body resin layer are laminated integrally, and transparently cured at the round hole opening by punching The resin composition (B) was impregnated and cured, and the thickness of the transparent main body resin layer was 150 μm, the total thickness was 250 μm, and the unit mass was 270 g / m 2 (excluding the carrier film and the cover film).

また、得られたシートの評価物性は、可視光線透過率が88%、コンクリートとの付着強度が3.73N/mm2、押抜き試験の最大荷重変位が12mm、最大荷重が2.23kNであり、10mm以上及び1.5kN以上の規格値を満足し、コンクリート構造物の補修又は補強用シートの機能を備えていた。本実施例の透明複合シートの押抜き試験の荷重−変位曲線を図4に示す。
以上、透明複合シートの構成及び評価結果をまとめて表1に示す。
Moreover, the evaluation physical properties of the obtained sheet are as follows. The visible light transmittance is 88%, the adhesion strength with concrete is 3.73 N / mm 2 , the maximum load displacement of the punching test is 12 mm, and the maximum load is 2.23 kN. It satisfies the standard values of 10 mm or more and 1.5 kN or more, and has a function of a sheet for repairing or reinforcing a concrete structure. FIG. 4 shows a load-displacement curve in the punching test of the transparent composite sheet of this example.
The structure and evaluation results of the transparent composite sheet are summarized in Table 1 above.

実施例2
実施例1において、透明本体樹脂層の単位面積質量を160g/m2から120g/m2として、シート厚みを220μmとした他は、実施例1と同様にして透明複合シートを得、性能評価を行った。評価結果をまとめて表1に示す。
Example 2
In Example 1, a transparent composite sheet was obtained in the same manner as in Example 1 except that the unit area mass of the transparent main body resin layer was changed from 160 g / m 2 to 120 g / m 2 and the sheet thickness was 220 μm. went. The evaluation results are summarized in Table 1.

実施例3
実施例1において、二軸延伸PET製フィルムのパンチングパターンを、丸孔直径2mm、ピッチ3.5mmの60°千鳥状に変更し、開口率を29.6%とした他は実施例1と同様にして透明複合シートを得、性能評価を行った。評価結果をまとめて表1に示す。
Example 3
In Example 1, the punching pattern of the biaxially stretched PET film was changed to a 60 ° zigzag pattern with a round hole diameter of 2 mm and a pitch of 3.5 mm, and the aperture ratio was set to 29.6%. Thus, a transparent composite sheet was obtained and performance evaluation was performed. The evaluation results are summarized in Table 1.

実施例4
実施例2において、二軸延伸PET製フィルムの厚みを125μmとした他は、実施例2と同様にして透明複合シートを得、性能評価を行った。評価結果をまとめて表1に示す。
Example 4
In Example 2, except that the thickness of the biaxially stretched PET film was 125 μm, a transparent composite sheet was obtained in the same manner as in Example 2, and performance evaluation was performed. The evaluation results are summarized in Table 1.

実施例5
実施例4において厚み125μmの二軸延伸PET製フィルムに替えて、ポリプロピレン(PP)製二軸延伸フィルム(東レ(株)製、トレファン2500H、厚み60μm)を2枚貼り合せて125μmとしたものを使用し、実施例4(実施例1にも同じ。)と同一のパンチングパターンを施した他は、実施例4と同様にして透明複合シートを得、性能評価を行った。評価結果をまとめて表1に示す。
Example 5
In Example 4, instead of the biaxially stretched PET film having a thickness of 125 μm, two biaxially stretched films made of polypropylene (PP) (Toray Industries, Inc., Trefan 2500H, thickness 60 μm) were bonded to 125 μm. A transparent composite sheet was obtained in the same manner as in Example 4 except that the same punching pattern as in Example 4 (same as in Example 1) was applied, and performance evaluation was performed. The evaluation results are summarized in Table 1.

実施例6
実施例1において、PETフィルム(厚み50μm、開口率21.7%)を2枚用い、シート厚みを250μmから300μmとして、非通気層/PETフィルム層/透明本体樹脂層/PETフィルム層/透明本体樹脂層の5層の構成の透明複合シートとした他は、実施例1と同様に得、性能評価を行った。評価結果をまとめて表1に示す。
Example 6
In Example 1, two PET films (thickness 50 μm, aperture ratio 21.7%) were used, the sheet thickness was 250 μm to 300 μm, and the non-breathable layer / PET film layer / transparent main body resin layer / PET film layer / transparent main body The evaluation was performed in the same manner as in Example 1 except that a transparent composite sheet having a five-layer structure of the resin layer was used. The evaluation results are summarized in Table 1.

実施例7
厚さ50μmのポリエチレンナフタレート(PEN)二軸延伸フィルム〔帝人デュポンフィルム(株)製:テオネックス〕に直径1.3mm、ピッチ間隔3.5mmで45°千鳥状に連続状に丸孔が展開するパンチング孔加工を行ない、開口率が21.7%のパンチング処理PEN製二軸延伸フィルムを得た。実施例1においてPETフィルムに替えて得られたPENフィルムを用いた他は、実施例1と同様にして透明複合シートを得、性能評価を行った。評価結果をまとめて表1に示す。
Example 7
Round holes are continuously developed in a 45 ° zigzag pattern with a diameter of 1.3 mm and a pitch interval of 3.5 mm on a 50 μm thick polyethylene naphthalate (PEN) biaxially stretched film (Teijin DuPont Films: Teonex). Punching holes were processed to obtain a punched PEN biaxially stretched film having an aperture ratio of 21.7%. A transparent composite sheet was obtained in the same manner as in Example 1 except that the PEN film obtained in place of the PET film in Example 1 was used, and performance evaluation was performed. The evaluation results are summarized in Table 1.

実施例8
実施例6において、PETフィルムの替わりにPENフィルム(厚み50μm、開口率21.7%)を2枚用い、非通気層/PENフィルム層/透明本体樹脂層/PENフィルム層/透明本体樹脂層の5層の構成の透明複合シートを実施例6と同様に得、性能評価を行った。評価結果をまとめて表1に示す。
Example 8
In Example 6, two PEN films (thickness 50 μm, aperture ratio 21.7%) were used instead of the PET film, and the non-breathing layer / PEN film layer / transparent main body resin layer / PEN film layer / transparent main body resin layer A transparent composite sheet having a five-layer structure was obtained in the same manner as in Example 6, and performance evaluation was performed. The evaluation results are summarized in Table 1.

Figure 2014029107
Figure 2014029107

比較例1及び比較例5
パンチング処理二軸延伸PETフィルムとして厚み23μm(東レ(株)製、ルミラー25S10)を用いた比較例1、厚み350μm(東レ(株)製、ルミラー350S10)を用いた比較例5において、その他は実施例1と同様にして、透明複合シートを得、性能評価を行った。評価結果をまとめて表2に示す。表2に示すように、PETフィルムの厚みが薄い比較例1では押抜き試験が不合格であり、厚みの厚い比較例5では付着強度が1.5N以上の基準に未達であった。
Comparative Example 1 and Comparative Example 5
In Comparative Example 1 using a thickness of 23 μm (manufactured by Toray Industries, Inc., Lumirror 25S10) as a perforated biaxially stretched PET film, Comparative Example 5 using a thickness of 350 μm (manufactured by Toray Industries, Inc., Lumirror 350S10) In the same manner as in Example 1, a transparent composite sheet was obtained and performance evaluation was performed. The evaluation results are summarized in Table 2. As shown in Table 2, in Comparative Example 1 where the PET film was thin, the punching test was rejected, and in Comparative Example 5 where the thickness was thick, the adhesion strength was less than 1.5 N.

比較例2
実施例3において、丸孔の直径を3mm、ピッチ5mmの60°千鳥状で、開口率が32.6%のパンチング処理二軸延伸PETフィルムに置き換えた他は、実施例3と同様にして、透明複合シートを得、性能評価を行った。評価結果をまとめて表2に示す。表2に示すように、PETフィルムの開口率が32.6%と高いため、押抜き試験が不合格であった。
Comparative Example 2
In Example 3, except that the diameter of the round holes was changed to a punching-treated biaxially stretched PET film having a diameter of 3 mm and a pitch of 5 mm and a punching treatment of 32.6%, the same as in Example 3, A transparent composite sheet was obtained and performance evaluation was performed. The evaluation results are summarized in Table 2. As shown in Table 2, since the aperture ratio of the PET film was as high as 32.6%, the punching test was rejected.

比較例3
実施例1において、非通気性層を形成することなく、キャリアフィルム上に直接パンチング処理二軸延伸PETフィルム及び硬化性樹脂組成物(B)を供給しカバーフィルムで挟み込んだ他は、実施例1と同様にして、透明複合シートを得、性能評価を行った。評価結果をまとめて表2に示す。表2に示すように、付着強度、押抜き試験が不合格であった。
Comparative Example 3
Example 1 is the same as Example 1 except that the punching-treated biaxially stretched PET film and the curable resin composition (B) were directly supplied onto the carrier film and sandwiched between the cover films without forming an air-impermeable layer. In the same manner, a transparent composite sheet was obtained and performance evaluation was performed. The evaluation results are summarized in Table 2. As shown in Table 2, the adhesion strength and the punching test were unacceptable.

比較例4
実施例1において、非通気性層を形成した後、その上面にパンチング処理二軸延伸PETフィルムを載置し、硬化性透明樹脂組成物部(B)を供給することなく、カバーフィルムで挟み込んで加熱炉内にて100℃で10分間加熱して、パンチング処理二軸延伸フィルムを積層した透明複合シートを得、性能評価を行った。評価結果をまとめて表2に示す。表2に示すように、付着強度、押抜き試験がいずれも劣り、不合格であった。
Comparative Example 4
In Example 1, after forming an air-impermeable layer, a punched biaxially stretched PET film was placed on the upper surface, and sandwiched between cover films without supplying the curable transparent resin composition part (B). It heated at 100 degreeC for 10 minute (s) in the heating furnace, the transparent composite sheet which laminated | stacked the punching process biaxially stretched film was obtained, and performance evaluation was performed. The evaluation results are summarized in Table 2. As shown in Table 2, the adhesion strength and the punching test were both inferior and failed.

比較例6
実施例1において、パンチング処理二軸延伸フィルムに換えて、ポリプロピレン(PP)とポリエチレン(PE)からなる芯鞘複合繊維束の鞘部を融合一体化した海島繊維を三軸に積層した、厚み300μm、単位面積質量75g/m2、開口率54%のメッシュ体(宇部日東化成(株)製、シムメッシュ)の両面にコロナ放電処理を施したものを使用した他は、実施例1と同様にして繊維強化樹脂シートを得、性能評価を行った。評価結果をまとめて表2に示す。
表2に示すように、可視光線透過率が10〜70%であり、メッシュ体を構成する繊維の陰の部分のコンクリート表面を視認することができないので、付着強度や押抜き試験には優れているが、コンクリート表面の細かなひびを観察する必要がある部位の補強又は補修用シートとしては不向きであることが確認された。
Comparative Example 6
In Example 1, instead of the punching-treated biaxially stretched film, sea island fibers in which the sheath portions of the core-sheath composite fiber bundle made of polypropylene (PP) and polyethylene (PE) were fused and integrated were laminated in a triaxial manner, and the thickness was 300 μm. The same procedure as in Example 1 was used except that a mesh body having a unit area mass of 75 g / m 2 and an open area ratio of 54% (simbe mesh manufactured by Ube Nitto Kasei Co., Ltd.) was subjected to corona discharge treatment. Thus, a fiber reinforced resin sheet was obtained and performance evaluation was performed. The evaluation results are summarized in Table 2.
As shown in Table 2, the visible light transmittance is 10 to 70%, and the surface of the concrete behind the fibers constituting the mesh body cannot be visually recognized. However, it was confirmed that it is not suitable as a sheet for reinforcing or repairing a portion where it is necessary to observe fine cracks on the concrete surface.

比較例7
実施例1において、丸孔の直径を0.5mm、ピッチ3.5mmの60°千鳥状で開口率が1.8%のパンチング処理二軸延伸PETフィルムに置き換えた他は、実施例1と同様にして、透明複合シートを得、性能評価を行った。評価結果をまとめて表2に示す。表2に示すように、PETフィルムの開口率が1.8%と小さいため、付着強度及び押抜き試験の最大荷重が劣り、補強用シートとしては不合格であった。
Comparative Example 7
Example 1 was the same as Example 1 except that the hole was replaced with a punched biaxially stretched PET film having a round hole diameter of 0.5 mm and a pitch of 3.5 mm and a 60 ° staggered shape and an aperture ratio of 1.8%. Thus, a transparent composite sheet was obtained and performance evaluation was performed. The evaluation results are summarized in Table 2. As shown in Table 2, since the opening ratio of the PET film was as small as 1.8%, the adhesion load and the maximum load in the punching test were inferior, and the sheet for reinforcement was rejected.

Figure 2014029107
Figure 2014029107

本発明のコンクリート構造物の補修又は補強用透明複合シートは、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開し、丸孔の開口率が5〜30%である透明な二軸延伸フィルムを補強材とし、該二軸延伸フィルムと軟質な硬化性透明樹脂組成物の硬化物との複合シートであり、かつ、可視光線透過率が80%以上なので、コンクリート構造物表面の視認が可能な透明複合シートとして利用できる。
また、本発明のコンクリート構造物の補修又は補強用透明複合シートは、軟質な硬化性透明樹脂組成物(A)を硬化してなる非通気性層を有しているので、補強シート等を工事対象箇所に貼付するに際して、コンクリート表面に塗布された未硬化状の接着剤が、透明複合シートの透明本体樹脂層に不可避的に存在する気泡等に起因する貫通孔から滴下することが無いので、施工時に表面を養生シートで覆い、硬化後に補強シート表面に垂れ下がった接着剤を除去する等の付随的な作業が不要であり、非常に簡易化された施工が可能な透明複合シートとして、コンクリート構造物の補修又は補強に利用でできる。
さらに、本発明のコンクリート構造物の補修又は補強用透明複合シートは、ピンホールや気泡による欠陥部分がないので、コンクリート面を外気から遮断して、塩化物イオン等によるコンクリート表面の劣化を防止できる複合透明シートとして利用できる。
The transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention has a round hole with an inner diameter of 1 to 2 mm continuously developed in a staggered shape of 60 ° or 45 °, and the opening ratio of the round hole is 5 to 30%. A concrete sheet having a transparent biaxially stretched film as a reinforcing material, a composite sheet of the biaxially stretched film and a cured product of a soft curable transparent resin composition, and having a visible light transmittance of 80% or more. It can be used as a transparent composite sheet that allows visual recognition of the object surface.
The transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention has a non-breathable layer formed by curing the soft curable transparent resin composition (A). When affixed to the target location, the uncured adhesive applied to the concrete surface does not drop from the through-hole due to air bubbles inevitably present in the transparent main body resin layer of the transparent composite sheet, Concrete structure as a transparent composite sheet that does not require additional work such as covering the surface with a curing sheet at the time of construction and removing the adhesive hanging on the surface of the reinforcing sheet after curing, allowing for a very simplified construction Can be used to repair or reinforce objects.
Furthermore, since the transparent composite sheet for repairing or reinforcing a concrete structure according to the present invention has no defects due to pinholes or bubbles, the concrete surface can be shielded from the outside air to prevent deterioration of the concrete surface due to chloride ions or the like. It can be used as a composite transparent sheet.

1 非通気性層
2 丸孔
2′ 丸孔に充填された透明硬化性樹脂の硬化物
3 二軸延伸フィルム
4 透明本体樹脂層
10 透明複合シート
21 丸孔の開口部
31 二軸延伸フィルムの実在部
D 丸孔の直径
B1 基準列内の孔部間の実在(ホネ)部
B2 基準列と隣列の孔部間の実在(ホネ)部
P1 基準列(長手方向)内の丸孔の間隔(ピッチ)
P2 隣列との間隔
DESCRIPTION OF SYMBOLS 1 Non-air-permeable layer 2 Round hole 2 'Hardened | cured material of transparent curable resin with which the circular hole was filled 3 Biaxially stretched film 4 Transparent main body resin layer 10 Transparent composite sheet 21 Opening part of a round hole 31 Reality of biaxially stretched film Part D Diameter of round hole B1 Actual (horn) part between holes in reference row B2 Real (horn) part between hole in reference row and adjacent row P1 Spacing of round holes in reference row (longitudinal direction) pitch)
P2 Distance from adjacent row

Claims (3)

可視光線透過率が80%以上のコンクリート構造物の補修又は補強用透明複合シートであって、該透明複合シートは、(i)軟質な硬化性透明樹脂組成物(A)を硬化してなる非通気性層と、少なくとも1層の(ii)一方の面が該非通気性層に積層され、内径1〜2mmの丸孔が60°又は45°の千鳥状に連続状に展開し、丸孔の開口率が5〜30%である透明な二軸延伸フィルム、及び(iii)該二軸延伸フィルムの丸孔部を充填し、かつ二軸延伸フィルムの他方の面を覆うように、非通気性層と相溶性を有する軟質な硬化性透明樹脂組成物(B)を硬化してなる透明本体樹脂層、を備えることを特徴とするコンクリート構造物の補修又は補強用透明複合シート。   A transparent composite sheet for repairing or reinforcing a concrete structure having a visible light transmittance of 80% or more, wherein the transparent composite sheet is obtained by curing (i) a soft curable transparent resin composition (A). A breathable layer and at least one layer (ii) one surface is laminated on the non-breathable layer, and round holes having an inner diameter of 1 to 2 mm are continuously developed in a zigzag shape of 60 ° or 45 °. Transparent biaxially stretched film having an opening ratio of 5 to 30%, and (iii) non-breathable so as to fill the round hole portion of the biaxially stretched film and cover the other surface of the biaxially stretched film A transparent composite sheet for repairing or reinforcing a concrete structure, comprising: a transparent main body resin layer obtained by curing a soft curable transparent resin composition (B) having compatibility with a layer. 前記軟質な硬化性透明樹脂組成物(A)及び(B)が、共にウレタンアクリレート樹脂を主成分としてなる、請求項1に記載の透明複合シート。   The transparent composite sheet according to claim 1, wherein both of the soft curable transparent resin compositions (A) and (B) are mainly composed of a urethane acrylate resin. 二軸延伸フィルムがフィルム厚み50〜250μmのポリエステル製二軸延伸フィルムである請求項1又は2に記載の透明複合シート。   The transparent composite sheet according to claim 1, wherein the biaxially stretched film is a polyester biaxially stretched film having a film thickness of 50 to 250 μm.
JP2013133430A 2012-06-27 2013-06-26 Transparent composite sheet for repair or reinforcement of concrete structures Active JP6082666B2 (en)