JP2013177726A - Synthetic fiber structure - Google Patents

Synthetic fiber structure Download PDF

Info

Publication number
JP2013177726A
JP2013177726A JP2013101298A JP2013101298A JP2013177726A JP 2013177726 A JP2013177726 A JP 2013177726A JP 2013101298 A JP2013101298 A JP 2013101298A JP 2013101298 A JP2013101298 A JP 2013101298A JP 2013177726 A JP2013177726 A JP 2013177726A
Authority
JP
Japan
Prior art keywords
synthetic fiber
fiber structure
fluorine
aqueous solution
water repellent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2013101298A
Other languages
Japanese (ja)
Other versions
JP5892973B2 (en
Inventor
Yoshihisa Kawakami
吉久 川上
Original Assignee
Mitsui Chemicals Inc
三井化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Chemicals Inc, 三井化学株式会社 filed Critical Mitsui Chemicals Inc
Priority to JP2013101298A priority Critical patent/JP5892973B2/en
Publication of JP2013177726A publication Critical patent/JP2013177726A/en
Application granted granted Critical
Publication of JP5892973B2 publication Critical patent/JP5892973B2/en
Application status is Active legal-status Critical
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a synthetic fiber structure that is superior in alcohol repelling property and oil repelling property, and also has water resistance.SOLUTION: The synthetic fiber structure is obtained by immersing a synthetic fiber structure made of a polyolefin nonwoven fabric in an aqueous solution or aqueous dispersion element which contains a fluorine-based water repellent, a nonionic antistatic agent and isopropyl alcohol, and does not contain a crosslinkable compound and a metal salt compound.

Description

本発明は、撥アルコール性及び撥油性に優れ、且つ耐水性を有する、衛生材料、医療用材料、衣料用材料等に好適な合成繊維構造物に関する。 The present invention is excellent in alcohol repellency and oil repellency, and has a water-resistant, sanitary materials, medical materials, of a preferred synthetic fiber structure in clothing materials.

近年、合成繊維からなる織布、不織布等の合成繊維構造物は、通気性、柔軟性に優れることから各種用途に幅広く用いられている。 Recently, synthetic fiber structures of woven fabric, non-woven fabric made of synthetic fibers, breathable, it is widely used in various applications due to excellent flexibility. そのため、合成繊維構造物には、その用途に応じた各種の特性が求められるとともに、その特性の向上が要求されている。 Therefore, the synthetic fiber structure, various characteristics together sought in accordance with the application, the improvement of its properties is required.

また、合成繊維からなる織布、不織布等の合成繊維構造物は、一般に疎水性であり、親油性を有している。 Further, woven fabric made of synthetic fibers, synthetic fiber structures such as nonwoven are generally hydrophobic, have a lipophilic. また、疎水性は有しているものの、撥水性は不十分である。 Although hydrophobic has water repellency is insufficient.
合成繊維構造物に撥水性を付与する方法として、合成繊維構造物をカチオン系帯電防止剤、アニオン系帯電防止剤及びフッ素系撥水剤を一浴に含む処理液で処理する方法(特許文献1:特公平2−55550号公報)、合成繊維構造体を、撥水剤、アニオン系帯電防止剤及び架橋剤で処理する方法(特許文献2;特開平11−189976号公報)等種々の方法が提案されている。 As a method for imparting water repellency to the synthetic fiber structure, synthetic fiber structures of cationic antistatic agent, a method of treating an anionic antistatic agent and a fluorine-based water repellent with a processing solution containing one bath (Patent Document 1 : Kokoku 2-55550 discloses), a synthetic fiber structure, water repellent, a method (Patent Document 2 to be processed by anionic antistatic agent and crosslinking agent; the Japanese Patent Laid-Open No. 11-189976), etc. various methods Proposed.

しかしながら、合成繊維構造物に撥水性を付与することは容易であるが、特にポリプロピレン等のポリオレフィンからなる繊維は親油性に優れることから、撥油性をも付与することは困難である。 However, although possible to impart water repellency to the synthetic fiber structure is easy, fibers especially polyolefins such as polypropylene is excellent in lipophilic, it is difficult even to impart oil repellency.

特公平2−55550号公報 Kokoku 2-55550 Patent Publication No. 特開平11−189976号公報 JP 11-189976 discloses

本発明は、撥アルコール性及び撥油性に優れ、且つ耐水性を有する合成繊維構造物を開発することを目的とする。 The present invention is excellent in alcohol repellency and oil repellency, and aims to develop a synthetic fiber structure having a water resistance.

本発明は、ポリオレフィン不織布からなる合成繊維構造体を、フッ素系撥水剤、ノニオン系帯電防止剤及びイソプロピルアルコールを含み、且つ架橋性化合物及び金属塩化合物を含まない水溶液あるいは水性分散体で浸漬処理してなることを特徴とする合成繊維構造物、及びその製造方法に係る。 The present invention is dipped in the synthetic fiber structure composed of a polyolefin nonwoven fabric, a fluorine-based water repellent agent comprises a nonionic antistatic agent and isopropyl alcohol, and aqueous solution does not contain a crosslinking compound and a metal salt compound or an aqueous dispersion synthetic fiber structure, characterized in that by comprising, and according to the method of manufacturing the same.

本発明の合成繊維構造物は、撥アルコール性及び撥油性に優れており、且つ耐水性を有するので衛生材料、医療用材料、衣料用材料等に好適に用い得る。 Synthetic fiber structure of the present invention is excellent in alcohol repellency and oil repellency, sanitary materials so and have a water-resistant, medical materials, can be suitably used for clothing materials.

<合成繊維構造体> <Synthetic fiber structure>
本発明に係る合成繊維構造体は、種々公知の熱可塑性樹脂、例えば、エチレン、プロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテンおよび1−オクテン等のα−オレフィンの単独若しくは共重合体である高圧法低密度ポリエチレン、線状低密度ポリエチレン(所謂LLDPE)、高密度ポリエチレン、ポリプロピレン、ポリプロピレンランダム共重合体、ポリ1−ブテン、ポリ4−メチル−1−ペンテン、エチレン・プロピレンランダム共重合体、エチレン・1−ブテンランダム共重合体、プロピレン・1−ブテンランダム共重合体等のポリオレフィン、ポリエステル(ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等)、ポリアミド(ナイロン−6、ナイロン−66、ポリメタキ Synthetic fibrous structure according to the present invention, various known thermoplastic resins, such as ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-such as pentene and 1-octene α- olefin alone or high-pressure low-density polyethylene which is a copolymer, linear low density polyethylene (so-called LLDPE), high density polyethylene, polypropylene, polypropylene random copolymers, poly-1-butene, poly-4-methyl-1-pentene, ethylene-propylene random copolymer, ethylene-1-butene random copolymer, a polyolefin such as propylene-1-butene random copolymer, polyester (polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate), polyamide (nylon-6, nylon -66, Porimetaki レンアジパミド等)、ポリ塩化ビニル、ポリイミド、エチレン・酢酸ビニル共重合体、ポリアクリロニトリル、ポリカーボネート、ポリスチレン、アイオノマー、熱可塑性ポリウレタンあるいはこれらの混合物等からなる一種以上の合成繊維からなる構造物であり、通常、織布、編布、不織布等の形状を有する。 Ren'ajipamido etc.), polyvinyl chloride, polyimide, ethylene-vinyl acetate copolymer, a polyacrylonitrile, polycarbonate, polystyrene, ionomer, structure comprised of a thermoplastic polyurethane, or one or more synthetic fibers consisting of mixtures, usually , with a woven fabric, a knitted fabric, the shape of the nonwoven fabric or the like.

本発明に係る合成繊維構造体は、単層であっても二種以上の積層体あるいは合成繊維構造体と透湿性フィルム、ガス不透過性フィルム、防湿性フィルム、ガス透過性フィルム等のフィルムあるいは合成紙等との複合体であってもよい。 Synthetic fibrous structure according to the present invention, a laminate of two or more may be a single layer or a synthetic fiber structure and the moisture-permeable film, a gas impermeable film, moistureproof film, or film of gas-permeable film or the like a complex of a synthetic paper may be.

合成繊維構造体の積層体あるいは複合体の例としては、例えば、スパンボンド不織布/メルトブローン不織布、スパンボンド不織布/メルトブローン不織布/スパンボンド不織布、スパンボンド不織布/透湿性フィルム、スパンボンド不織布/メルトブローン不織布/スパンボンド不織布/透湿性フィルムを挙げることができる。 Examples of the laminate or composite of synthetic fibrous structure, for example, spunbonded nonwoven fabric / meltblown nonwoven fabric, spunbonded nonwoven fabric / meltblown nonwoven fabric / spunbonded nonwoven fabric, spunbonded nonwoven fabric / breathable film, spunbonded nonwoven fabric / meltblown nonwoven fabric / it can be exemplified spunbonded nonwoven / breathable film.

合成繊維構造体を構成する合成繊維としては、ポリオレフィン繊維が疎水性、耐水性に優れるので好ましく、特にポリプロピレン繊維が疎水性、耐水性、剛性、嵩高性、通気性に優れるので好ましい。 The synthetic fibers constituting the synthetic fiber structure, polyolefin fibers hydrophobic, preferably excellent in water resistance, especially polypropylene fibers hydrophobic, water resistance, stiffness, bulkiness, preferred because of excellent ventilation.

合成繊維には、本発明の目的を損なわない範囲で、通常用いられる酸化防止剤、耐候安定剤、耐光安定剤、ブロッキング防止剤、無機あるいは有機の充填剤、滑剤、核剤、顔料、染料等の添加剤を必要に応じて添加されていてもよい。 Synthetic fibers, in amounts not detrimental to the objects of the present invention, antioxidants usually used, weathering stabilizers, light stabilizers, antiblocking agents, inorganic or organic fillers, lubricants, nucleating agents, pigments, dyes, etc. additives may be added as necessary.

合成繊維としては、特に限定はされず、短繊維(ステープルファイバー)、撚糸、長繊維、スプリットファイバーあるいは単繊維、異型断面繊維、連糸、芯鞘構造あるいはサイドバイサイド等の複合繊維等種々の形状であってもよい。 As the synthetic fibers, not particularly limited, short fibers (staple fibers), twisting, long fibers, split fibers or a single fiber, modified cross-section fibers, continuous threads, in various forms such as a composite fiber such as a core-sheath structure or side-by-side it may be.
本発明に係る合成繊維構造体は、合成繊維以外に他の成分、例えば、天然繊維、再生繊維あるいは無機繊維等を含んでいてもよい。 Synthetic fibrous structure according to the present invention may contain other components in addition to the synthetic fibers, for example, natural fibers may include recycled fibers or inorganic fibers.

<フッ素系撥水剤> <Fluorine-based water repellent>
本発明に係るフッ素系撥水剤は、種々公知のフッ素系撥水剤、例えば、フルオロアルキルカルボン酸、パーフルオロアルキルカルボン酸、パーフルオロアルキルスルホン酸およびその塩(リチウム、ナトリウム、カリウム等)、モノパーフルオロアルキルエチルフォスフェイト塩、パーフルオロアルキルスルホン酸ジエタノールアミド等のフロロカーボン類、ポリテトラフルオロエチレン、テトラフルオロエチレン−ヘキサフルオロプロピレン共重合体、ポリトリフルオロモノクロルエチレン、ポリビニルフロライド、テトラフルオロエチレン−パーフルオロアルコキシエチレン共重合体、ポリクロロトリフルオロエチレン等のフッ素系重合体、一般式CH 2 =CR 1 COOR 2 Rf(式中RfはC n2n+1で表されるパーフルオロアルキル Fluorine-based water repellent according to the present invention, various known fluorine-based water repellent, for example, fluoroalkyl carboxylic acids, perfluoroalkyl carboxylic acids, perfluoroalkyl sulfonic acids and salts thereof (lithium, sodium, potassium, etc.), mono perfluoroalkylethyl phosphate salts, fluorocarbon such as perfluoroalkylsulfonic acid diethanolamide, polytetrafluoroethylene, tetrafluoroethylene - hexafluoropropylene copolymer, polytrifluoroethylene monochlorobenzene ethylene, polyvinyl fluoride, tetrafluoroethylene - perfluoroalkoxy ethylene copolymer, fluorine-based polymers such as polychlorotrifluoroethylene, general formula CH 2 = CR 1 COOR 2 Rf ( wherein Rf is a perfluoroalkyl represented by C n F 2n + 1 、R 1は水素原子又はメチル基、R 2は−C m2m −で表されるアルキレン基であり、nは5〜16の正の整数、mは1〜10の正の整数である)で表されるパーフルオロアルキル基を有する化合物を含む(共)重合体等のフッ素系化合物を挙げることができる。 , R 1 represents a hydrogen atom or a methyl group, R 2 is -C m H 2m - an alkylene group represented, n represents a positive integer of 5 to 16, m is a positive integer of 1 to 10) in represented by comprising a compound having a perfluoroalkyl group (co) fluorine compound of the polymer, and the like.

これらフッ素系化合物の中でも、パーフルオロアルキル基を有する化合物を含む(共)重合体が撥水、撥油性能で好ましい。 Among these fluorine-based compounds include compounds having a perfluoroalkyl group (co) polymer is water-repellent, preferably in oil repellency. かかるパーフルオロアルキル基を有する化合物を含む(共)重合体は、デュポン社からZonyl 7040の商品名、旭硝子社からAG−5850の商品名で製造・販売されている。 Such perfluoroalkyl group having comprising a compound (co) polymer, trade name Zonyl 7040 from DuPont, are manufactured and sold under the trade name AG-5850 from Asahi Glass Company.

<ノニオン系帯電防止剤> <Nonionic antistatic agents>
本発明に係るノニオン系帯電防止剤は、非イオン界面活性剤とも呼ばれる界面活性剤であり、種々公知のノニオン系帯電防止剤、例えば、ポリオキシエチレアルキルエーテル(略称:AE);ポリオキシエチレンアルキルフェノールエーテル(略称:APE);アルキルグルコキシド(AG);モノステアリン酸ポリエチレングリコール、ポリエチレングリコールラウレート、ポリエチレングリコールモノオレート、ポリエチレングリコールジステアレート等のポリオキシエチレン脂肪酸エステル;ショ糖脂肪酸エステル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、脂肪酸ペンタエリスリット等の多価アルコールエステル;脂肪酸アルカノールアミド等が挙げられる。 Nonionic antistatic agents of the present invention is a surfactant, also known as non-ionic surface active agent, various known nonionic antistatic agent, for example, polyoxyethylenated alkyl ethers (abbreviated: AE); polyoxyethylene alkyl phenol ether (abbreviation: APE); alkyl glucosides sulfoxide (AG); polyethylene glycol monostearate, polyethylene glycol laurate, polyethylene glycol monooleate, polyoxyethylene fatty acid esters such as polyethylene glycol distearate; sucrose fatty acid esters, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyhydric alcohol esters such as fatty acid pentaerythritol; such as fatty acid alkanolamides.

これらノニオン系界面活性剤の中でも、ポリオキシエチレアルキルエーテル、ポリオキシエチレンアルキルフェノールエーテル、ポリオキシエチレン脂肪酸エステル及び多価アルコールエステルが前記フッ素系撥水剤及びイソプロピルアルコールとの親和性が特に良好で、しかも肌への刺激が無い点で好ましい。 Among these nonionic surfactants, polyoxyethylenated alkyl ethers, polyoxyethylene alkylphenol ethers, polyoxyethylene fatty acid esters and polyhydric alcohol esters are the fluorine-based water repellent and affinity of isopropyl alcohol is particularly favorable, Moreover, preferable in that there is no irritation to the skin.

<合成繊維構造物> <Synthetic fiber structure>
本発明の合成繊維構造物は、前記合成繊維構造体を、前記フッ素系撥水剤、前記ノニオン系帯電防止剤及びイソプロピルアルコールを含む水溶液あるいは水性分散体で処理してなることを特徴とする合成繊維構造物である。 Synthetic fiber structure of the present invention, the composite fiber structure, characterized in the fluorine-based water repellent, be treated with an aqueous solution or an aqueous dispersion containing the nonionic antistatic agent and isopropyl alcohol synthesis it is a fiber structure.

本発明の合成繊維構造物は、好ましくは撥アルコール性が9級以上、より好ましくは10級であり、且つ、好ましくは撥油性が7級以上の性能を有する。 Synthetic fiber structure of the present invention is preferably alcohol repellency of 9 or higher grade, more preferably from 10 primary, and preferably has a oil repellency grade 7 or better performance.
本発明における撥アルコール性は、JIS L 1912医療用不織布試験法で測定した値である。 Alcohol repellency in the present invention is a value measured by JIS L 1912 medical nonwoven test method.

本発明における撥油性は、AATCC 118−1992で測定した値である。 Oil repellency in the present invention is a value measured by AATCC 118-1992.
本発明の合成繊維構造物は、好ましくは表面固有抵抗が1.0×10 12 Ω以下、より好ましくは1.0×10 10 Ω以下であり、耐水圧が処理前の原反の60%以上を維持し、より好ましくは、80%以上のものである。 Synthetic fiber structure of the present invention are preferably surface resistivity of 1.0 × 10 12 Ω or less, and more preferably not more than 1.0 × 10 10 Ω, water pressure resistance more than 60% of the original fabric before treatment maintaining, more preferably of 80% or more. 表面固有抵抗値は、JIS K 6911 5.13、耐水圧は、JIS L 1092 Aに準拠して測定した値である。 Surface resistivity of, JIS K 6911 5.13, the water pressure resistance is the value measured according to JIS L 1092 A.

本発明に係る合成繊維構造体を処理する水溶液あるいは水性分散体におけるフッ素系撥水剤の濃度は、通常、5〜25重量%、好ましくは5〜15重量%の範囲にあり、ノニオン系帯電防止剤の濃度は、通常、2〜10重量%、好ましくは2〜5重量%の範囲にあり、イソプロピルアルコールの濃度は、通常、2〜10重量%、好ましくは2〜5重量%の範囲にある。 The concentration of the fluorine-based water repellent agent in the aqueous solution or aqueous dispersion processes the synthetic fibrous structure according to the present invention is usually 5-25 wt%, preferably in the range of 5 to 15 wt%, a nonionic antistatic the concentration of the agent is usually 2 to 10 wt%, preferably in the range of 2-5 wt%, the concentration of isopropyl alcohol is usually 2 to 10 wt%, preferably in the range of 2-5 wt% .

合成繊維構造体に対するフッ素系撥水剤の塗布量(付着量)はフッ素系撥水剤の固形分として、通常、1〜5g/m 2 、好ましくは1〜3g/m 2の範囲にあり、ノニオン系帯電防止剤の塗布量(付着量)はノニオン系帯電防止剤の固形分として、通常、0.2〜1.0g/m 2 、好ましくは0.2〜0.5g/m 2の範囲にある。 Synthetic fluorine-based coating amount of the water-repellent agent to the fibrous structure as a solid content of the (coating weight) of the fluorine-based water repellent, is usually, 1 to 5 g / m 2, preferably in the range of 1 to 3 g / m 2, the coating amount of the nonionic antistatic agent as a solid content of (deposition amount) of the nonionic antistatic agent, typically, 0.2 to 1.0 g / m 2, the range preferably of 0.2-0.5 g / m 2 It is in.

<合成繊維構造物の製造方法> <Method for synthetic fiber structure>
本発明の合成繊維構造物は、前記合成繊維構造体を、前記フッ素系撥水剤、前記ノニオン系帯電防止剤及びイソプロピルアルコールを含む水溶液あるいは水性分散体で処理することにより得られる。 Synthetic fiber structure of the present invention, the composite fiber structure, the fluorine-based water repellent, obtained by treatment with the nonionic antistatic agent and an aqueous solution or an aqueous dispersion containing isopropyl alcohol.

本発明に係る合成繊維構造体を水溶液あるいは水性分散体で処理する方法は、種々公知の方法、例えば、合成繊維構造体を水溶液等に浸漬した後乾燥する方法、合成繊維構造体に水溶液等をエアーナイフコーター、ダイレクトグラビアコーター、グラビアオフセット、アークグラビアコーター、グラビアリバースおよびジェットノズル方式等のグラビアコーター、トップフィードリバースコーター、ボトムフィードリバースコーターおよびノズルフィードリバースコーター等のリバースロールコーター、5本ロールコーター、リップコーター、バーコーター、バーリバースコーター、ダイコーター等種々公知の塗工機を用いて塗布した後乾燥する方法、合成繊維構造体に水溶液等をスプレーコート(その他の方法)した後乾燥する方法等によ Method of processing a synthetic fibrous structure according to the present invention in aqueous solution or aqueous dispersion, various known methods, for example, a method of drying after the synthetic fiber structure was immersed in an aqueous solution such as an aqueous solution or the like to the synthetic fiber structure air knife coater, direct gravure coater, gravure offset, arc gravure coater, gravure coater, such as gravure reverse and jet nozzle type, top feed reverse coater, bottom feed reverse coater and the nozzle feed reverse coater or the like of a reverse roll coater, 5-roll coater , a lip coater, a bar coater, a bar reverse coater, and drying after coating with a die coater or the like various known coating machine, and drying after the aqueous solution or the like and spray coating (otherwise) to the synthetic fiber structure to etc. 処理することができる。 It can be processed.

水溶液等で処理した合成繊維構造体(合成繊維構造物)を乾燥する場合は、水分が蒸発する温度以上で合成繊維構造体(合成繊維構造物)が溶融しない温度未満、例えば、合成繊維構造体(合成繊維構造物)が、ポリプロピレン不織布であれば、通常、95〜120℃、好ましくは100〜105℃の温度で乾燥すればよい。 Synthetic fiber structure treated with an aqueous solution or when drying the (synthetic fiber structure), the temperature or a synthetic fiber structure water evaporates (synthetic fiber structure) is less than a temperature which does not melt, for example, synthetic fiber structures (synthetic fiber structure) is, if non-woven polypropylene fabric, usually, 95-120 ° C., preferably may be dried at a temperature of 100-105 ° C..

以下、実施例に基づいて本発明をさらに具体的に説明するが、本発明はこれらの実施例に限定されるものではない。 Hereinafter, a more detailed description of the present invention based on examples, the present invention is not limited to these examples.
なお、実施例及び比較例における物性値等は、前述の方法により測定した。 Incidentally, physical properties, etc. in the examples and comparative examples were measured by the method described above.

〔実施例1〕 Example 1
デュポン社製造のパーフルオロアルキル基含有フッ素系撥水剤(商品名 Zonyl 7040)5.0g、イソプロピルアルコール2.5g(和光純薬製)、ポリオキシエチレントリデシルエーテル型ノニオン系帯電防止剤(商品名;デスパノールTOC、日本油脂製)を含んだ混合水溶液1000gに、目付け55g/m 2のポリプロピレンスパンボンド不織布/ポリプロピレンメルトブローン不織布/ポリプロピレンスパンボンド不織布(SMS不織布)(目付け構成:S/M/S=22.5/10/22.5g/m 2 )を全体が含浸するまで3分間浸漬した。 DuPont production of perfluoroalkyl group-containing fluorine-based water repellent (trade name Zonyl 7040) 5.0 g, isopropyl alcohol 2.5 g (manufactured by Wako Pure Chemical), polyoxyethylene tridecyl ether type nonionic antistatic agent (trade name; Desupanoru TOC, the mixed aqueous solution 1000g containing NOF Corporation), the basis weight 55 g / m 2 polypropylene spunbond nonwoven / polypropylene meltblown nonwoven / polypropylene spunbond nonwoven fabric (SMS nonwoven fabric) (basis weight configuration: S / M / S = 22.5 / 10 / 22.5g / m 2 ) whole was immersed for 3 minutes until impregnation. 浸漬後、SMS不織布を取り出した後、3分間余分な水分を切り、乾燥機にて105℃で12分間乾燥して、撥アルコール処理不織布からなる合成繊維構造物を得た。 After immersion, after removal of the SMS nonwoven fabric, cut 3 minutes excess water, and dried for 12 minutes at at 105 ℃ dryer to obtain synthetic fiber structure consisting of alcohol repellency treatment nonwoven.

得られた合成繊維構造物の評価結果を表1に示す。 Evaluation results of the obtained synthetic fiber structure are shown in Table 1. 表1に記載したように、合成繊維構造物の撥アルコール性は10級及び、撥油性は8級であった。 As described in Table 1, alcohol repellency of synthetic fiber structure 10 primary and oil repellency was 8 grade. また、当該合成繊維構造物は、帯電性を有し、耐水圧も未処理(参考例1)に比較して、64%以上を維持している。 Moreover, the synthetic fiber structure has a charging resistance, water pressure as compared to the untreated (Reference Example 1), and maintained at least 64%.
なお、得られた合成繊維構造物をプレス成形して(フィルム状)赤外線吸収スペクトルを測定した結果、C−F伸縮振動に基く1074cm -1の吸収が観測された。 Incidentally, the obtained synthetic fiber structure by press-forming (film-like) results of measurement of infrared absorption spectrum, the absorption of 1074cm -1 based on C-F stretching vibration was observed.

〔実施例2〕 Example 2
実施例1で用いたフッ素系撥水剤に替えて、旭硝子社製造のパーフルオロアルキル基含有フッ素系撥水剤(商品名 AG−5850)を用いる以外は実施例1と同様に行い、撥アルコール処理不織布からなる合成繊維構造物を得た。 Instead of the fluorine-based water repellent used in Example 1, except using Asahi Glass Co. production of perfluoroalkyl group-containing fluorine-based water repellent (trade name AG-5850) is performed in the same manner as in Example 1, repellent alcohol to obtain a synthetic fiber structure consisting of treatment nonwoven.

得られた合成繊維構造物の評価結果を表1に示す。 Evaluation results of the obtained synthetic fiber structure are shown in Table 1. 表1に記載したように合成繊維構造物の撥アルコール性は10級及び、撥油性は8級であった。 Alcohol repellency of synthetic fiber structure as described in Table 1 is 10 primary and oil repellency was 8 grade. また、当該合成繊維構造物は、帯電性を有し、耐水圧も未処理(参考例1)に比較して、64%以上を維持している。 Moreover, the synthetic fiber structure has a charging resistance, water pressure as compared to the untreated (Reference Example 1), and maintained at least 64%.
なお、得られた合成繊維構造物をプレス成形して(フィルム状)赤外線吸収スペクトルを測定した結果、C−F伸縮振動に基く1074cm -1の吸収が観測された。 Incidentally, the obtained synthetic fiber structure by press-forming (film-like) results of measurement of infrared absorption spectrum, the absorption of 1074cm -1 based on C-F stretching vibration was observed.

〔比較例1〕 Comparative Example 1
実施例1で用いたノニオン系帯電防止剤に替えて、リン酸エステル型アニオン系帯電防止剤(商品名 デレクトールLM−3、明成化学工業社製)を用いる以外は実施例1と同様に行い、撥アルコール処理不織布を得た。 Instead of nonionic antistatic agent used in Example 1, phosphate ester type anionic antistatic agent (trade name Derekutoru LM-3, Meisei Chemical Co., Ltd.) is performed in the same manner as in Example 1 except for using, to give the alcohol repellency processing non-woven fabric. 得られた撥アルコール処理不織布の評価結果を表1に示す。 Evaluation results of the obtained alcohol repellency treatment nonwoven are shown in Table 1. 表1に記載したように、撥アルコール処理不織布の撥アルコール性は7級及び、撥油性は4級であった。 As described in Table 1, alcohol repellency of alcohol repellency treatment nonwoven 7 primary and oil repellency was quaternary.

〔比較例2〕 Comparative Example 2
実施例1で用いたノニオン系帯電防止剤に替えて、スルホン酸ナトリウム型カチオン系帯電防止剤(商品名 エラガンT−501AN、日本油脂社製)を用いる以外は実施例1と同様に行い、撥アルコール処理不織布を得た。 Instead of nonionic antistatic agent used in Example 1, sodium sulfonate type cationic antistatic agent (trade name Eragan T-501AN, produced by NOF Corporation) is performed in the same manner as in Example 1 except for using, repellent to give the alcohol treatment non-woven fabric. 得られた撥アルコール処理不織布の評価結果を表1に示す。 Evaluation results of the obtained alcohol repellency treatment nonwoven are shown in Table 1. 表1に記載したように、撥アルコール処理不織布の撥アルコール性は8級及び、撥油性は5級であった。 As described in Table 1, alcohol repellency of alcohol repellency treatment nonwoven 8 primary and oil repellency was 5 grade.

〔参考例1〕 [Reference Example 1]
実施例1で用いた目付け55g/m 2のポリプロピレンスパンボンド不織布/ポリプロピレンメルトブローン不織布/ポリプロピレンスパンボンド不織布を撥アルコール処理せずに、物性を評価した。 Polypropylene spunbond nonwoven / polypropylene meltblown nonwoven / polypropylene spunbond nonwoven fabric having a basis weight of 55 g / m 2 was used in Example 1 without alcohol repellency treatment, physical properties were evaluated. 評価結果を表1に示す。 The evaluation results are shown in Table 1.

本発明の合成繊維構造物は、撥アルコール性及び撥油性に極めて優れるので、かかる特性を活かして、種々の用途、例えば、医療用、衛生材用、包装材、産業用材料などの用途に好適に用いられ、具体的な用途として手術ガウン、作業着、電池の防水部材、化粧品部材、シューズの表面処理、防水テープ素材等に応用でき、特に使い捨ておむつや生理用ナプキンの防漏部材、液体導入経路部材として好ましく用いることができる。 Synthetic fiber structure of the present invention, since very excellent alcohol repellency and oil repellency, taking advantage of such characteristics, various applications, e.g., medical, sanitary materials, packaging materials, suitable for applications such as industrial materials used, surgical gown as specific applications, work clothes, waterproof member of the battery, cosmetic member, surface treatment of the shoe, can be applied to waterproof tape material such as, in particular, disposable diapers and sanitary napkins leak-barrier member, the liquid introduced it can be preferably used as a route member.

Claims (8)

  1. ポリオレフィン不織布からなる合成繊維構造体を、フッ素系撥水剤、ノニオン系帯電防止剤及びイソプロピルアルコールを含み、且つ架橋性化合物及び金属塩化合物を含まない水溶液あるいは水性分散体で浸漬処理してなることを特徴とする合成繊維構造物。 Synthetic fiber structures made of polyolefin nonwoven fabric, a fluorine-based water repellent agent comprises a nonionic antistatic agent and isopropyl alcohol, dipped and made things and with a cross-linkable compound and the aqueous solution or aqueous dispersion that is free of metal salt compound synthetic fiber structure characterized by.
  2. 浸漬処理後に95〜120℃の温度で乾燥してなる請求項1記載の合成繊維構造物。 After immersion treatment formed by drying at a temperature of 95-120 ° C. claim 1 synthetic fiber structure as claimed.
  3. 水溶液あるいは水性分散体におけるフッ素系撥水剤の濃度が5〜25重量%の範囲にある請求項1記載の合成繊維構造物。 Claim 1 synthetic fiber structure according to the aqueous solution or the concentration of the fluorine-based water repellent agent in the aqueous dispersion is in the range of 5 to 25 wt%.
  4. 水溶液あるいは水性分散体におけるノニオン系帯電防止剤の濃度が2〜10重量%の範囲にある請求項1記載の合成繊維構造物。 Claim 1 synthetic fiber structure according to the aqueous solution or the concentration of the nonionic antistatic agent in the aqueous dispersion is in the range of 2 to 10 wt%.
  5. 水溶液あるいは水性分散体におけるイソプロピルアルコールの濃度が2〜10重量%の範囲にある請求項1記載の合成繊維構造物。 Claim 1 synthetic fiber structure according to the concentration of isopropyl alcohol in aqueous solution or aqueous dispersion is in the range of 2 to 10 wt%.
  6. フッ素系撥水剤が、パーフルオロアルキル基を有する化合物を含む(共)重合体からなる請求項1記載の合成繊維構造物。 Fluorine-based water repellent, comprising a compound having a perfluoroalkyl group (co) comprising a polymer according to claim 1 synthetic fiber structure as claimed.
  7. ノニオン系帯電防止剤が、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェノールエーテル、ポリオキシエチレン脂肪酸エステル及び多価アルコールエステルから選ばれた一種以上である請求項1記載の合成繊維構造物。 Nonionic antistatic agent, polyoxyethylene alkyl ethers, polyoxyethylene alkylphenol ethers, polyoxyethylene fatty acid esters and synthetic fiber structure of claim 1, wherein at least one selected from polyhydric alcohol esters.
  8. ポリオレフィン不織布からなる合成繊維構造体を、フッ素系撥水剤、ノニオン系帯電防止剤及びイソプロピルアルコールを含み、且つ架橋性化合物及び金属塩化合物を含まない水溶液あるいは水性分散体で浸漬処理してなることを特徴とする合成繊維構造物の製造方法。 Synthetic fiber structures made of polyolefin nonwoven fabric, a fluorine-based water repellent agent comprises a nonionic antistatic agent and isopropyl alcohol, dipped and made things and with a cross-linkable compound and the aqueous solution or aqueous dispersion that is free of metal salt compound method for producing a synthetic fiber structure characterized by.
JP2013101298A 2013-05-13 2013-05-13 Synthetic fiber structure Active JP5892973B2 (en)