JP2013175488A - Copper foil for current collector of lithium secondary battery - Google Patents
Copper foil for current collector of lithium secondary battery Download PDFInfo
- Publication number
- JP2013175488A JP2013175488A JP2013123723A JP2013123723A JP2013175488A JP 2013175488 A JP2013175488 A JP 2013175488A JP 2013123723 A JP2013123723 A JP 2013123723A JP 2013123723 A JP2013123723 A JP 2013123723A JP 2013175488 A JP2013175488 A JP 2013175488A
- Authority
- JP
- Japan
- Prior art keywords
- copper foil
- plane
- secondary battery
- current collector
- lithium secondary
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、リチウム二次電池の集電体として用いられる銅箔に関するものであって、より詳しくは、銅箔表面にしわ（ｗｒｉｎｋｌｅ）が発生することを防止することができる構造を有したリチウム二次電池の集電体用銅箔に関する。 The present invention relates to a copper foil used as a current collector for a lithium secondary battery, and more specifically, lithium having a structure capable of preventing wrinkles from being generated on the surface of the copper foil. The present invention relates to a copper foil for a current collector of a secondary battery.
リチウム二次電池は、他の二次電池に比べて相対的にエネルギー密度が高く、作動電圧が高いだけでなく優れた保存及び寿命特性を示すなど多くの長所があって、ＰＣ、カムコーダー、携帯電話機、携帯用ＣＤプレーヤー、ＰＤＡなど各種の携帯用電子機器に広く用いられている。 Lithium secondary batteries have many advantages such as relatively high energy density and high operating voltage as well as excellent storage and life characteristics compared to other secondary batteries. Widely used in various portable electronic devices such as telephones, portable CD players, and PDAs.
一般に、リチウム二次電池は、セパレータを挟んで配置されたカソード及びアノードと、電解質とを備える。前記カソード及びアノードは、それぞれカソード活物質及びアノード活物質と、前記カソード活物質及びアノード活物質にそれぞれ接触するカソード集電体及びアノード集電体とを備えた構造を有する。 Generally, a lithium secondary battery includes a cathode and an anode disposed with a separator interposed therebetween, and an electrolyte. The cathode and the anode have a structure including a cathode active material and an anode active material, respectively, and a cathode current collector and an anode current collector that are in contact with the cathode active material and the anode active material, respectively.
リチウム二次電池において、アノード集電体の素材としては主に銅箔が用いられ、通常この銅箔にはカーボン（ｃａｒｂｏｎ）系スラリーの活物質がコートされる。ここで、銅箔は、電気めっき法で電解銅箔を製造する製箔工程と、原箔に剥離強度（ｐｅｅｌ ｓｔｒｅｎｇｔｈ）などを付与するための後処理工程とを通じて製造される。電気めっきによって電解銅箔の一面には製箔機のドラム（ｄｒｕｍ）の表面形状に沿った、いわゆる光沢面（ｓｈｉｎｙ ｓｉｄｅ）が形成され、他面には山（ｍｏｕｎｔａｉｎ）構造によって相対的に粗度が高いマット面（ｍａｔｔｅ ｓｉｄｅ）が形成される。また、電解銅箔は、後処理工程において、耐食性及び耐変色性を確保するために、保護性コーティングをさらに行う。 In a lithium secondary battery, a copper foil is mainly used as a material for the anode current collector, and this copper foil is usually coated with a carbon-based slurry active material. Here, the copper foil is manufactured through a foil manufacturing process for manufacturing an electrolytic copper foil by an electroplating method and a post-processing process for imparting peel strength to the original foil. By electroplating, one surface of the electrolytic copper foil is formed with a so-called shiny side along the surface shape of the drum of the foil making machine, and the other surface is relatively rough due to a mountain structure. A matte surface having a high degree is formed. Moreover, in order to ensure corrosion resistance and discoloration resistance, the electrolytic copper foil is further subjected to protective coating in the post-treatment process.
リチウム二次電池は集電体として用いられる銅箔の表面状態によって電池特性が大きく変わるので、歩留まりの向上のためにはしわ特性（ｗｒｉｎｋｌｅ ｃｈａｒａｃｔｅｒｉｓｔｉｃｓ）のような表面特性を改善することが非常に重要である。 Lithium secondary batteries have battery characteristics that vary greatly depending on the surface condition of the copper foil used as a current collector. Therefore, it is very important to improve surface characteristics such as wrinkle characteristics to improve yield. It is.
図１に示すように、銅箔の表面にしわが存在する場合、表面形状の不均一によって活物質が均一にコートされず、ゆえに充・放電するとき短絡が発生するか、銅箔から活物質が剥離される現象が発生する。 As shown in FIG. 1, when wrinkles are present on the surface of the copper foil, the active material is not uniformly coated due to non-uniformity of the surface shape. Therefore, a short circuit occurs when charging / discharging, or the active material is removed from the copper foil. Peeling phenomenon occurs.
本発明は前記のような問題点を解決するために創案されたものであって、銅箔表面にしわを低減することができる結晶構造を有したリチウム二次電池の集電体用銅箔を提供することにその目的がある。 The present invention was devised to solve the above-described problems, and a copper foil for a current collector of a lithium secondary battery having a crystal structure capable of reducing wrinkles on the surface of the copper foil. The purpose is to provide.
本発明の他の目的は、銅箔表面にしわをより有効に低減するために、表面粗度（ｓｕｒｆａｃｅ ｒｏｕｇｈｎｅｓｓ）、重量偏差、引張強度、延伸率、厚さなどの因子が最適化されたリチウム二次電池の集電体用銅箔を提供することにある。 Another object of the present invention is to provide lithium having optimized factors such as surface roughness, weight deviation, tensile strength, stretch ratio, and thickness in order to more effectively reduce wrinkles on the copper foil surface. It is providing the copper foil for the collectors of a secondary battery.
前記のような目的を達成するために、本発明によるリチウム二次電池の集電体用銅箔は、重量偏差特性が３％以下であり、引張強度が３０〜４０ｋｇｆ／ｍｍ２であるリチウム二次電池の集電体として用いられる銅箔であって、
結晶構造において、（１１１）面、（２００）面、（２２０）面の集合組職係数の全体合計の中で（１１１）面と（２００）面との集合組職係数の合計が占める比率が６０〜８５％であり、前記（１１１）面、（２００）面、（２２０）面の集合組職係数の全体合計に対する（１１１）面の集合組職係数の比率が１８〜３８％、（２００）面の集合組職係数の比率が２８〜６２％、（２２０）面の集合組職係数の比率が１５〜４０％であることを特徴とする。
In order to achieve the above object, the copper foil for a current collector of a lithium secondary battery according to the present invention has a weight deviation characteristic of 3% or less and a tensile strength of 30 to 40 kgf / mm 2. A copper foil used as a current collector for a secondary battery,
In the crystal structure, the ratio of the total assembly coefficient of the (111) plane and the (200) plane occupies the total sum of the assembly organization coefficients of the (111) plane, the (200) plane, and the (220) plane. 60 to 85%, and the ratio of the collective organization coefficient of the (111) plane to the total sum of the collective organization coefficients of the (111) plane, the (200) plane, and the (220) plane is 18 to 38%, (200 ) The ratio of the collective organization coefficient of the plane is 28 to 62%, and the ratio of the collective organization coefficient of the (220) plane is 15 to 40%.
表面粗度（Ｒｚ‐ＪＩＳ）が２μｍ以下であることが望ましい。 The surface roughness (Rz-JIS) is desirably 2 μm or less.
延伸率が３〜２０％であることが望ましい。 It is desirable that the stretching ratio is 3 to 20%.
銅箔厚さが１〜３５μｍであることが望ましい。 The copper foil thickness is desirably 1 to 35 μm.
本発明によるリチウム二次電池の集電体用銅箔は、表面にしわが実質的に発生しないので、活物質をコートするとき均一なコーティング面を形成することができ、短絡の発生を防止することができる。 The copper foil for the current collector of the lithium secondary battery according to the present invention is substantially free of wrinkles on the surface, so that a uniform coating surface can be formed when the active material is coated, and the occurrence of short circuits can be prevented. Can do.
本明細書に添付される下記の図面は本発明の望ましい実施例を例示するものであって、発明の詳細な説明とともに本発明の技術思想をさらに理解させる役割を果たすものであるため、本発明はそのような図面に記載された事項にのみ限定されて解釈されてはいけない。
以下、添付した図面を参照しながら本発明の望ましい実施例を詳しく説明する。これに先立って、本明細書及び請求範囲に使われた用語や単語は通常的や辞書的な意味に限定して解釈されてはいけず、発明者は自らの発明を最善の方法で説明するために用語の概念を適切に定義することができるという原則に則して、本発明の技術的思想に符合する意味と概念とに解釈されなければならない。従って、本明細書に記載された実施例は本発明の最も望ましい一実施例に過ぎず、本発明の技術的思想の全てを代弁するものではないため、本出願時点においてこれらに代替できる多様な均等物と変形例があり得ることを理解しなければならない。 Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. Prior to this, the terms and words used in the specification and claims should not be construed in a normal or lexicographic sense, and the inventor will explain his invention in the best possible way. Therefore, in accordance with the principle that the concept of a term can be appropriately defined, it should be interpreted as a meaning and a concept consistent with the technical idea of the present invention. Therefore, the embodiment described in the present specification is only the most preferred embodiment of the present invention, and does not represent all the technical ideas of the present invention. It should be understood that there can be equivalents and variations.
本発明によるリチウム二次電池の集電体用銅箔は、結晶構造、表面粗度、重量偏差、引張強度、延伸率などの因子が最適化されてしわが発生しない表面特性を提供する。 The copper foil for a current collector of a lithium secondary battery according to the present invention provides surface characteristics in which wrinkles are not generated by optimizing factors such as crystal structure, surface roughness, weight deviation, tensile strength, and stretch ratio.
望ましくは、本発明によるリチウム二次電池の集電体用銅箔は、硫酸銅、硫酸及び塩素から構成された硫酸銅めっき液を基本にし、微量の有機添加剤を添加して製造される。ここで、添加剤としては、めっき表面に光沢を付与し微細なめっき層を得るための光沢剤（ｂｒｉｇｈｔｅｎｅｒ）としてスルフィド（ｓｕｌｆｉｄｅ）を含有したスルホネート（ｓｕｌｐｈｏｎａｔｅ）系列の添加剤と、低粗度の銅箔を得るために添加するレベラー（ｌｅｖｅｌｅｒ）として分子量１，０００〜１００，０００程度の低分子量を有するゼラチン（ｇｅｌａｔｉｎ）と、安定した低粗度を具現するためのサプレッサー（ｓｕｐｐｒｅｓｓｏｒ）としてセルロース（ｃｅｌｌｕｌｏｓｅ）系列の添加剤とが用いられる。工程条件としては、３０〜８０ＡＳＤ（Ａ／ｄｍ２の電流密度及び３０〜６０℃の温度において製箔機のドラム表面に銅を電着して原箔を製造し、防錆処理のために銅箔表面をクロメート（ｃｈｒｏｍａｔｅ）処理する工程を経て製造される。 Preferably, the copper foil for a current collector of a lithium secondary battery according to the present invention is manufactured by adding a small amount of an organic additive based on a copper sulfate plating solution composed of copper sulfate, sulfuric acid and chlorine. Here, as an additive, a sulfonate (sulfonate) series additive containing sulfide as a brightener for imparting gloss to the plating surface and obtaining a fine plating layer, and a low roughness Gelatin having a low molecular weight of about 1,000 to 100,000 as a leveler added to obtain a copper foil, and cellulose (suppressor) for realizing a stable low roughness as a leveler. cellulose) series additives. Process conditions include 30 to 80 ASD (A / dm 2 current density and 30 to 60 ° C.). The foil surface is manufactured through a chromate treatment process.
銅箔の結晶構造は、（１１１）面、（２００）面、（２２０）面の集合組職係数の全体合計の中で（１１１）面と（２００）面との集合組職係数の合計が占める比率が６０〜８５％を満たす。また、（１１１）面、（２００）面、（２２０）面の集合組職係数の全体合計に対する（１１１）面の集合組職係数の比率は１８〜３８％、（２００）面の集合組職係数の比率は２８〜６２％、（２２０）面の集合組職係数の比率は１５〜４０％を満たす。 The crystal structure of the copper foil is the sum of the aggregate organization coefficients of the (111) plane and the (200) plane among the total aggregate organization coefficients of the (111) plane, (200) plane, and (220) plane. The proportion occupied is 60 to 85%. Further, the ratio of the collective organization coefficient of the (111) plane to the total sum of the collective organization coefficients of the (111) plane, the (200) plane, and the (220) plane is 18 to 38%, and the collective organization of the (200) plane The ratio of the coefficient satisfies 28 to 62%, and the ratio of the collective organization coefficient for the (220) plane satisfies 15 to 40%.
前記集合組職係数の数値範囲を外れる場合、銅箔の幅方向にしわが多数発生することになり、このため活物質をコートするとき銅箔表面に対する活物質の密着性が低下する問題がある。ここで、集合組職係数（ＴＣ）は、Ｘ線回折法（ＸＲＤ）を適用して図２に示すように各結晶面の回折強度ピーク（ｐｅａｋ）値を得た後、基準ピーク値と比較して以下の数学式１に従う範囲内で換算することで定められる。数学式１において、Ｉ（ｈｋｌ）は、（ｈｋｌ）面に対する測定回折強度を示し、Ｉｏ（ｈｋｌ）は、ＡＳＴＭ（Ａｍｅｒｉｃａｎ Ｓｏｃｉｅｔｙ ｏｆ Ｔｅｓｔｉｎｇ Ｍａｔｅｒｉａｌｓ）標準の粉末状回折データの標準回折強度を示す。 When outside the numerical range of the collective organization coefficient, many wrinkles are generated in the width direction of the copper foil. For this reason, when the active material is coated, there is a problem that the adhesion of the active material to the copper foil surface is lowered. Here, the aggregate organization coefficient (TC) is compared with the reference peak value after obtaining the diffraction intensity peak (peak) value of each crystal plane as shown in FIG. 2 by applying the X-ray diffraction method (XRD). Then, it is determined by converting within the range according to the following mathematical formula 1. In Equation 1, I (hkl) represents the measured diffraction intensity with respect to the (hkl) plane, and I o (hkl) represents the standard diffraction intensity of powdery diffraction data of ASTM (American Society of Testing Materials) standard.
銅箔の表面粗度（Ｒｚ）は、日本工業標準規格（ＪＩＳ）を基準にして２μｍ以下を満たす。表面粗度（Ｒｚ）が２μｍを超える場合、表面が不均一であるのでリチウム二次電池を充・放電するとき短絡が発生する恐れがあり、アノード活物質のコーティング状態が不均一になる問題が発生する。 The surface roughness (R z ) of the copper foil satisfies 2 μm or less based on Japanese Industrial Standard (JIS). When the surface roughness (R z ) exceeds 2 μm, since the surface is non-uniform, a short circuit may occur when charging / discharging the lithium secondary battery, and the coating state of the anode active material becomes non-uniform Will occur.
銅箔の重量偏差特性は、３％以下を満たす。重量偏差特性が３％を超える場合、銅箔表面に物性偏差が発生してしわ数が増加し、集電体の物性が不均一になる問題が発生する。
ここで、重量偏差は、銅箔を５ｃｍ×５ｃｍのサイズに切り出して試片を作った後その重量を測定して単位面積当たりの銅箔の重量値を換算し、銅箔の幅方向に沿って前記試片を切り出す過程を繰り返して行って各試片に対する銅箔重量値を測定した後標準偏差を計算することで算出する。このとき、銅箔は、クロメート表面処理を通じて防錆処理された電解銅箔を用いることが望ましい。
The weight deviation characteristic of the copper foil satisfies 3% or less. When the weight deviation characteristic exceeds 3%, the physical property deviation occurs on the surface of the copper foil, the number of wrinkles increases, and the physical property of the current collector becomes non-uniform.
Here, the weight deviation is obtained by cutting the copper foil into a size of 5 cm × 5 cm, making a test piece, measuring the weight, converting the weight value of the copper foil per unit area, and along the width direction of the copper foil. Then, the process of cutting out the specimen is repeated, and the copper foil weight value for each specimen is measured, and then the standard deviation is calculated. At this time, as the copper foil, it is desirable to use an electrolytic copper foil that has been rust-proofed through a chromate surface treatment.
その他に、銅箔の引張強度は３０〜４０ｋｇｆ／ｍｍ２、延伸率は３〜２０％、厚さは１〜３５μｍを満たす。このような範囲を外れた場合、銅箔の物性偏差が発生してしわ数が増加し、集電体の物性が不均一になる問題が発生する。 In addition, the copper foil has a tensile strength of 30 to 40 kgf / mm 2 , a stretching ratio of 3 to 20%, and a thickness of 1 to 35 μm. When outside this range, the physical property deviation of the copper foil occurs, the number of wrinkles increases, and the physical property of the current collector becomes non-uniform.
下記表１は、本発明の実施例１ないし７と比較例１ないし９によるリチウム二次電池の集電体用銅箔に対してしわ特性を測定した結果を示す。表１において、引張強度はＵＴＭ（Ｕｎｉｖｅｒｓａｌ Ｔｅｓｔｉｎｇ Ｍａｃｈｉｎｅ）を利用して測定し、このときゲージ長（ｇａｕｇｅ ｌｅｎｇｔｈ）は５ｃｍに設定した。 Table 1 below shows the results of measuring the wrinkle characteristics of the copper foils for the current collectors of the lithium secondary batteries according to Examples 1 to 7 and Comparative Examples 1 to 9 of the present invention. In Table 1, the tensile strength was measured using UTM (Universal Testing Machine), and at this time, the gauge length was set to 5 cm.
表１を参照すれば、本発明の実施例１ないし７による銅箔は、前述した集合組職係数の比率、引張強度、重量偏差、銅箔厚さの条件をすべて満たすことで、しわが発生しない結果を示すことが確認できる。その反面、比較例１ないし９による銅箔は、しわが多数発生して、リチウム二次電池の集電体として用いるには不適な特性を示すことが確認できる。 Referring to Table 1, in the copper foils according to Examples 1 to 7 of the present invention, wrinkles are generated by satisfying all of the above-described conditions of the aggregate organization coefficient, tensile strength, weight deviation, and copper foil thickness. It can be confirmed that the results are not shown. On the other hand, it can be confirmed that the copper foils according to Comparative Examples 1 to 9 show a characteristic that is unsuitable for use as a current collector of a lithium secondary battery due to the occurrence of many wrinkles.
本発明によるリチウム二次電池の集電体用銅箔は、集合組職係数の比率の条件のみを満たしてもしわ特性が従来に比べて改善できるが、比較例１ないし９に示すように引張強度や重量偏差などの他の条件が該当の数値範囲を外れた場合には、改善した特性に悪影響を及ぼして最終的にしわ特性の低下をもたらすので、前述した集合組職係数の比率、引張強度、重量偏差、銅箔厚さなどの条件をすべて満たすことが最も望ましい。 The copper foil for the current collector of the lithium secondary battery according to the present invention can improve the wrinkle characteristics even if only the conditions of the assembly organization coefficient ratio are satisfied, but as shown in Comparative Examples 1 to 9, If other conditions such as strength and weight deviation are outside the numerical range, the improved properties will be adversely affected and ultimately the wrinkle properties will be reduced. It is most desirable to satisfy all the conditions such as strength, weight deviation, and copper foil thickness.
以上のように、本発明は、たとえ限定された実施例と図面とによって説明されたが、本発明はこれによって限定されず、本発明が属する技術分野において通常の知識を持つ者により本発明の技術思想と特許請求範囲の均等範囲内で多様な修正及び変形が可能なのは言うまでもない。 As described above, the present invention has been described with reference to the limited embodiments and drawings. However, the present invention is not limited thereto, and those skilled in the art to which the present invention belongs have ordinary knowledge. Needless to say, various modifications and variations are possible within the scope of the technical idea and the scope of claims.
本発明によるリチウム二次電池の集電体用銅箔は、カーボン系スラリーのようなアノード活物質と接触するとき密着力が十分確保されて剥離強度に優れているので、電池容量を安定して維持することができるリチウム二次電池を具現することができる。 The copper foil for the current collector of the lithium secondary battery according to the present invention has a sufficient adhesion when it comes into contact with an anode active material such as a carbon-based slurry and has excellent peel strength. A lithium secondary battery that can be maintained can be implemented.
Claims (4)
結晶構造において、（１１１）面、（２００）面、（２２０）面の集合組職係数の全体合計の中で（１１１）面と（２００）面との集合組職係数の合計が占める比率が６０〜８５％であり、前記（１１１）面、（２００）面、（２２０）面の集合組職係数の全体合計に対する（１１１）面の集合組職係数の比率が１８〜３８％、（２００）面の集合組職係数の比率が２８〜６２％、（２２０）面の集合組職係数の比率が１５〜４０％であることを特徴とするリチウム二次電池の集電体用銅箔。 A copper foil used as a current collector of a lithium secondary battery having a weight deviation characteristic of 3% or less and a tensile strength of 30 to 40 kgf / mm 2 ,
In the crystal structure, the ratio of the total assembly coefficient of the (111) plane and the (200) plane occupies the total sum of the assembly organization coefficients of the (111) plane, the (200) plane, and the (220) plane. 60 to 85%, and the ratio of the collective organization coefficient of the (111) plane to the total sum of the collective organization coefficients of the (111) plane, the (200) plane, and the (220) plane is 18 to 38%, (200 A copper foil for a current collector of a lithium secondary battery, characterized in that the ratio of the collective organization coefficient of the surface) is 28 to 62% and the ratio of the collective organization coefficient of the (220) plane is 15 to 40%.