JP2013127577A - Resist composition and resist pattern formation method - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a resist composition and a resist pattern formation method that can form a resist pattern with a large light exposure margin and reduced roughness.SOLUTION: There is provided a resist composition containing: a base component (A) having solubility characteristics to a developing solution that is changed by the action of an acid; and an acid generator composition (B) that generates an acid by being exposed to light, the base component (A) containing a resin component (A1) having a constituent unit (a1) containing an acid decomposition group of which polarity is increased by the action of an acid, the unit (a1) containing a composition (a10) having a specific acid-dissociative polycyclic hydrocarbon group, and the generator composition (B) containing an acid generator (B1) formed of a compound expressed by a general formula (b1-1) where Qdenotes a divalent linking group or single bond, Ydenotes an alkylene group or fluorinated alkylene group, O denotes an oxygen atom, Xdenotes a 3-30C cyclic group, and Ais organic cation. [Chemical Formula 1]

Description

  The present invention relates to a resist composition and a resist pattern forming method.

In lithography technology, for example, a resist film made of a resist material is formed on a substrate, and the resist film is selectively exposed and developed to form a resist pattern having a predetermined shape on the resist film. The process to perform is performed. A resist material in which the exposed portion of the resist film changes to a property that dissolves in the developer is referred to as a positive type, and a resist material that changes to a property in which the exposed portion does not dissolve in the developer is referred to as a negative type.
In recent years, in the manufacture of semiconductor elements and liquid crystal display elements, pattern miniaturization has been rapidly progressing due to advances in lithography technology.
As a technique for miniaturization, the exposure light source is generally shortened in wavelength (increased energy). Specifically, conventionally, ultraviolet rays typified by g-line and i-line have been used, but at present, mass production of semiconductor elements using a KrF excimer laser or an ArF excimer laser has started. Further, studies have been made on EUV (extreme ultraviolet), EB (electron beam), X-rays, and the like having shorter wavelengths (higher energy) than these excimer lasers.
Resist materials are required to have lithography characteristics such as sensitivity to these exposure light sources and resolution capable of reproducing patterns with fine dimensions.
Conventionally, as a resist material satisfying such requirements, a chemically amplified resist composition containing an acid generator component that generates an acid upon exposure and a base material component whose solubility in a developing solution is changed by the action of the acid. Is used.

As a base component used in the chemically amplified resist composition, a resin (base resin) is generally used.
For example, as a chemically amplified resist composition for forming a positive resist pattern in an alkali development process using an alkali developer as a developer, an acid generator component and solubility in an alkali developer due to the action of an acid are included. What contains the resin component which increases is generally used. When a resist film formed using such a resist composition is selectively exposed at the time of resist pattern formation, an acid is generated from the acid generator component in the exposed portion, and the alkali developer of the resin component is generated by the action of the acid. As a result, the exposed area becomes soluble in an alkaline developer. Therefore, by performing alkali development, a positive pattern in which an unexposed portion remains as a pattern is formed.
As the resin component, one that increases the polarity of the resin by the action of an acid is generally used. As the resin whose polarity is increased by the action of an acid, for example, a resin having a structural unit containing an acid-decomposable group (hereinafter also referred to as a protecting group) whose polarity is increased by the action of an acid is used.
As the polarity increases, solubility in an alkaline developer increases while solubility in an organic solvent decreases. Therefore, when a solvent development process using an organic solvent-containing developer (organic developer) is applied instead of an alkali development process, the solubility in the organic developer is relatively reduced in the exposed area. In the solvent development process, the unexposed portion of the resist film is dissolved and removed by the organic developer, and a negative resist pattern is formed in which the exposed portion remains as a pattern. Such a solvent development process for forming a negative resist pattern is sometimes referred to as a negative development process (see, for example, Patent Document 1).

At present, as a base resin of a chemically amplified resist composition used in ArF excimer laser lithography and the like, it has a structural unit derived from (meth) acrylic acid ester in its main chain because of its excellent transparency near 193 nm. Resins (acrylic resins) and the like are generally used (see, for example, Patent Document 2 and Patent Document 3).
Here, “(meth) acrylic acid ester” means one or both of an acrylic acid ester having a hydrogen atom bonded to the α-position and a methacrylic acid ester having a methyl group bonded to the α-position. “(Meth) acrylate” means one or both of an acrylate having a hydrogen atom bonded to the α-position and a methacrylate having a methyl group bonded to the α-position. “(Meth) acrylic acid” means one or both of acrylic acid having a hydrogen atom bonded to the α-position and methacrylic acid having a methyl group bonded to the α-position.

Various acid generators used in chemically amplified resist compositions have been proposed so far, such as onium salt acid generators, oxime sulfonate acid generators, diazomethane acid generators, nitro acid generators, and nitro acid generators. Benzyl sulfonate acid generators, imino sulfonate acid generators, disulfone acid generators and the like are known.
Among these, as an onium salt acid generator, an iodonium salt having an iodonium ion as a cation and a sulfonium salt having a sulfonium ion as a cation have been conventionally used. As anions (acids) that form salts with these cations, fluorinated alkyl sulfonate ions are common (see, for example, Patent Document 4).
Further, a chemically amplified resist composition using a combination of two acid generators having different anion (acid) structures has been proposed (see, for example, Patent Documents 5 and 6).

JP 2008-292975 A JP 2003-241385 A JP 2009-169228 A JP 2005-037888 A JP 2009-008777 A JP 2009-157040 A

In the future, there is a demand for new materials that can be used for lithography applications as further advancement of lithography technology and expansion of application fields are expected.
However, with the progress of pattern miniaturization, the conventional resist composition has a problem that the exposure margin (EL margin) and line width roughness (line width roughness (LWR)) are still insufficiently reduced. It was.
Here, the “EL margin” indicates that the larger the value, the smaller the change amount of the pattern size accompanying the fluctuation of the exposure amount, and the higher the process margin.
Roughness (line width roughness (LWR)) is a phenomenon in which the line width of a line pattern becomes non-uniform when a resist pattern is formed using a resist composition. It causes the shape failure represented.
As a result of investigations by the present inventors, a monocyclic protecting group that is not so bulky as 5 to 6-membered ring is preferable for reducing roughness as compared with a bulky protecting group of 10-membered ring or more such as adamantane. The present invention has a problem that the margin and mask error factor (MEF) deteriorate. The present invention has been made in view of the above circumstances, and forms a resist pattern having a large exposure margin and a reduced roughness. An object is to provide a resist composition and a resist pattern forming method.

  The first aspect of the present invention that solves the above-mentioned problems includes a base material component (A) whose solubility in a developing solution is changed by the action of an acid, and an acid generator component (B) that generates an acid upon exposure. In the resist composition, the base component (A) includes a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid, and the structural unit (a1) is represented by the following general formula (a10). ), And the acid generator component (B) contains an acid generator (B1) composed of a compound represented by the following general formula (b1-1). The resist composition is characterized.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基であり、Ｒ^２は下記一般式（ａ１０−１）又は下記式（ａ１０−２）で表される基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, and R ² represents the following general formula (a10-1) or the following formula (a10-2 ). ]

［式中、破線は結合手であり、Ｒ^３は炭素数１〜５の直鎖状又は分岐状のアルキル基であり、ｎ”は０または１であり、Ｘは酸素原子又はＣＨ_２であり、ｐは１又は２である。］

[In the formula, the broken line is a bond, R ³ is a linear or branched alkyl group having 1 to 5 carbon atoms, n ″ is 0 or 1, and X is an oxygen atom or CH ₂ . , P is 1 or 2.]

［式中、Ｑ^１は２価の連結基又は単結合であり、Ｙ^１は置換基を有してもよい炭素数１〜４のアルキレン基又は置換基を有してもよい炭素数１〜４のフッ素化アルキレン基であり、Ｏは酸素原子であり、Ｘ^３は置換基を有してもよい炭素数３〜３０の環式基であり、Ａ^＋は有機カチオンである。］

[Wherein, Q ¹ is a divalent linking group or a single bond, and Y ¹ is an alkylene group having 1 to 4 carbon atoms which may have a substituent or 1 to 1 carbon atoms which may have a substituent. 4 is a fluorinated alkylene group, O is an oxygen atom, X ³ is an optionally substituted cyclic group having 3 to 30 carbon atoms, and A ⁺ is an organic cation. ]

  The second aspect of the present invention includes a step of forming a resist film using the resist composition of the first aspect, a step of exposing the resist film, and a step of developing the resist film to form a resist pattern. Is a resist pattern forming method.

In the present specification and claims, “aliphatic” is a relative concept with respect to aromatics, and is defined to mean groups, compounds, etc. that do not have aromaticity.
The “alkyl group” includes linear, branched and cyclic monovalent saturated hydrocarbon groups unless otherwise specified. The same applies to the alkyl group in the alkoxy group.
Unless otherwise specified, the “alkylene group” includes linear, branched and cyclic divalent saturated hydrocarbon groups.
The “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of the alkyl group are substituted with halogen atoms. The halogen atom includes a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
A “hydroxyalkyl group” is a group in which part or all of the hydrogen atoms of an alkyl group are substituted with a hydroxyl group.
The “structural unit” means a repeating unit (monomer unit) constituting a polymer compound (resin, polymer, copolymer).
“Exposure” is a concept including general irradiation of radiation.

  According to the present invention, it is possible to provide a resist composition and a resist pattern forming method capable of forming a resist pattern with a large exposure margin and reduced roughness.

≪Resist composition≫
The resist composition of the present invention comprises a base material component (A) whose solubility in a developing solution is changed by the action of an acid (hereinafter referred to as “component (A)”), and an acid generator component that generates an acid upon exposure ( B) (hereinafter referred to as “component (B)”).
When a resist film formed using such a resist composition undergoes selective exposure at the time of resist pattern formation, an acid is generated from the component (B), and the acid changes the solubility of the component (A) in the developer. Let As a result, while the solubility of the exposed portion of the resist film in the developer changes, the unexposed portion does not change the solubility in the developer, so by developing, the exposed portion in the case of a positive pattern, In the case of a negative pattern, the unexposed portions are dissolved and removed to form a resist pattern.
The resist composition of the present invention may be a negative resist composition or a positive resist composition.
In this specification, a resist composition that forms a positive pattern in which an exposed portion is dissolved and removed is referred to as a positive resist composition, and a resist composition that forms a negative pattern in which an unexposed portion is dissolved and removed is referred to as a negative. This is referred to as a type resist composition.

<(A) component>
The component (A) is a base material component whose solubility in a developer is changed by the action of an acid.
Here, the “base material component” is an organic compound having a film forming ability, and an organic compound having a molecular weight of 500 or more is preferably used. When the molecular weight of the organic compound is 500 or more, the film-forming ability is improved and a nano-level resist pattern is easily formed.
“Organic compounds having a molecular weight of 500 or more” used as the base component are roughly classified into non-polymers and polymers.
As the non-polymer, those having a molecular weight of 500 or more and less than 4000 are usually used. Hereinafter, a nonpolymer having a molecular weight of 500 or more and less than 4000 is referred to as a low molecular compound.
As the polymer, those having a molecular weight of 1000 or more are usually used. Hereinafter, a polymer having a molecular weight of 1000 or more is referred to as a polymer compound. In the case of a polymer compound, the “molecular weight” is a polystyrene-reduced mass average molecular weight measured by GPC (gel permeation chromatography). Hereinafter, the polymer compound may be simply referred to as “resin”.

[(A1) component]
In the present invention, the component (A) contains a resin component (A1) having a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid (hereinafter referred to as “(A1) component”). .
In addition to the structural unit (a1), the component (A1) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent. A structural unit derived from a structural unit containing a —SO ₂ -containing cyclic group (a2 ^S ) and an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, those having at least one constituent unit selected from the group consisting of structural units containing a lactone-containing cyclic group (a2 ^{L) (a2)} are preferred.
In the component (A1), in addition to the structural unit (a1) or in addition to the structural units (a1) and (a2), a hydrogen atom bonded to the carbon atom at the α-position is further substituted with a substituent. A structural unit derived from an acrylate ester that may contain a polar group-containing aliphatic hydrocarbon group (a3) (however, those corresponding to the structural unit (a1) and the structural unit (a2)) Are preferred).

[Structural unit (a1)]
The structural unit (a1) is a structural unit containing an acid-decomposable group whose polarity is increased by the action of an acid.
The “acid-decomposable group” is an acid-decomposable group capable of cleaving at least some of the bonds in the structure of the acid-decomposable group by the action of an acid generated from the acid generator component (B) upon exposure. is there.
Examples of the acid-decomposable group whose polarity increases by the action of an acid include a group that decomposes by the action of an acid to generate a polar group.
Examples of the polar group include a carboxy group, a hydroxyl group, an amino group, a sulfo group (—SO ₃ H), and the like. Among these, a polar group containing —OH in the structure (hereinafter sometimes referred to as “OH-containing polar group”) is preferable, a carboxy group or a hydroxyl group is preferable, and a carboxy group is particularly preferable.
More specifically, examples of the acid-decomposable group include a group in which the polar group is protected with an acid-dissociable group (for example, a group in which a hydrogen atom of an OH-containing polar group is protected with an acid-dissociable group).
The “acid-dissociable group” is an acid capable of cleaving at least a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group by the action of an acid generated from the acid generator component (B). It is a group having dissociation properties. The acid-dissociable group constituting the acid-decomposable group must be a group having a lower polarity than the polar group generated by dissociation of the acid-dissociable group. Is dissociated, a polar group having a polarity higher than that of the acid dissociable group is generated to increase the polarity. As a result, the polarity of the entire polymer increases. As the polarity increases, the solubility in the developer changes relatively. When the developer is an alkaline developer, the solubility increases. On the other hand, the developer contains an organic solvent (organic type). In the case of a developer, the solubility decreases.

  In the present invention, the structural unit (a1) needs to contain a structural unit (a10) represented by the following general formula (a10).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基であり、Ｒ^２は下記一般式（ａ１０−１）又は下記式（ａ１０−２）で表される基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, and R ² represents the following general formula (a10-1) or the following formula (a10-2 ). ]

［式中、破線は結合手であり、Ｒ^３は炭素数１〜４の直鎖状又は分岐鎖状のアルキル基であり、ｎ”は０又は１であり、Ｘは酸素原子又はＣＨ_２であり、ｐは１又は２である。］

[In the formula, a broken line is a bond, R ³ is a linear or branched alkyl group having 1 to 4 carbon atoms, n ″ is 0 or 1, and X is an oxygen atom or CH ₂ . Yes, p is 1 or 2.]

In formula (a10), R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms.
The alkyl group for R is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, A pentyl group, an isopentyl group, a neopentyl group, etc. are mentioned.
Examples of the halogenated alkyl group for R include groups in which some or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms have been substituted with halogen atoms. Specific examples of the alkyl group include the same alkyl groups as those described above for R. Examples of the halogen atom that replaces the hydrogen atom of the alkyl group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
As R, a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms is more preferable, and a hydrogen atom or a methyl group is most preferable in terms of industrial availability.

In Formula (a10), R ² is a group represented by General Formula (a10-1) or General Formula (a10-2).
In the formula (a10-1) and the formula (a10-2), the broken line is a bond, and is bonded to the oxygen atom at the terminal of the carbonyloxy group (—C (═O) O) in the formula (a10). .

In the formula (a10-1), R ³ is a linear or branched alkyl group having 1 to 4 carbon atoms, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, or n-butyl. Group, sec-butyl group, tert-butyl group and the like. R ³ is preferably a linear alkyl group having 1 to 4 carbon atoms, more preferably a methyl group or an ethyl group, and particularly preferably an ethyl group. When R ³ is an ethyl group, the acid-decomposable group represented by the formula (a10-1) has an optimum decomposition performance by acid (that is, energy necessary for deprotection).
In formula (a10-1), n ″ is 0 or 1, and preferably 1.

In formula (a10-2), X represents an oxygen atom (O) or CH ₂ and is preferably an oxygen atom. When X is an oxygen atom, the affinity with the component (B) is higher than when CH ₂ and the component (B) is closer to the acid-decomposable group represented by the formula (a10-2). It becomes easy. As a result, the acid diffusion distance is shortened, the acid dissociation property is excellent, and the roughness is reduced.
In formula (a10-2), p is 1 or 2, and is preferably 1.

  Preferred specific examples of the structural unit (a10) are shown below. In the following formulas, R is the same as described above.

  In the present invention, as the structural unit (a10), the structural unit represented by the formula (a10-1-2), (a10-1-11), (a10-2-2), or (a10-2-3) It preferably has at least one selected from the group consisting of: a structural unit represented by the formula (a10-1-1) or a structural unit represented by the formula (a10-2-1) Is particularly preferred.

The structural unit (a10) contained in the structural unit (a1) may be one type or two or more types.
In the structural unit (a1), the proportion of the structural unit (a10) is preferably 40 to 100 mol%, more preferably 60 to 100 mol%, still more preferably 90 to 100 mol%, and most preferably 100 mol%. preferable.

In the present invention, the structural unit (a1) is a structural unit other than the above (a10), and includes a structural unit containing an acid-decomposable group whose polarity increases by the action of an acid (hereinafter referred to as “structural unit (a1 ′)”). .)).
The acid dissociable group in the structural unit (a1 ′) is not particularly limited, and those that have been proposed as acid dissociable groups of base resins for chemically amplified resists can be used. In general, a group that forms a cyclic or chain tertiary alkyl ester with a carboxy group in (meth) acrylic acid or the like, an acetal type acid dissociable group such as an alkoxyalkyl group, and the like are widely known.
Here, the “tertiary alkyl ester” is an ester formed by replacing a hydrogen atom of a carboxy group with a chain or cyclic alkyl group, and the carbonyloxy group (—C (═O The structure in which the tertiary carbon atom of the chain or cyclic alkyl group is bonded to the terminal oxygen atom of) -O-). In this tertiary alkyl ester, when an acid acts, a bond is cut between an oxygen atom and a tertiary carbon atom to form a carboxy group.
The chain or cyclic alkyl group may have a substituent.
Hereinafter, a group that is acid dissociable by constituting a carboxy group and a tertiary alkyl ester is referred to as a “tertiary alkyl ester type acid dissociable group” for convenience.

Examples of the tertiary alkyl ester type acid dissociable group include an aliphatic branched acid dissociable group and an acid dissociable group containing an aliphatic cyclic group.
Here, “aliphatic branched” means having a branched structure having no aromaticity. The structure of the “aliphatic branched acid dissociable group” is not limited to a group consisting of carbon and hydrogen (hydrocarbon group), but is preferably a hydrocarbon group. The “hydrocarbon group” may be either saturated or unsaturated, but is usually preferably saturated.
Examples of the aliphatic branched acid dissociable group include a group represented by —C (R ⁷¹ ) (R ⁷² ) (R ⁷³ ). ^Wherein, R 71 ^{to R 73} each independently represents a linear alkyl group of 1 to 5 carbon atoms. The group represented by —C (R ⁷¹ ) (R ⁷² ) (R ⁷³ ) preferably has 4 to 8 carbon atoms, specifically a tert-butyl group or a 2-methyl-2-butyl group. , 2-methyl-2-pentyl group, 3-methyl-3-pentyl group and the like. A tert-butyl group is particularly preferable.

The “aliphatic cyclic group” means a monocyclic group or a polycyclic group having no aromaticity.
The aliphatic cyclic group in the “acid-dissociable group containing an aliphatic cyclic group” may or may not have a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms, and an oxygen atom (= O).
The basic ring structure excluding the substituent of the aliphatic cyclic group is not limited to a group consisting of carbon and hydrogen (hydrocarbon group), but is preferably a hydrocarbon group. The hydrocarbon group may be either saturated or unsaturated, but is usually preferably saturated.
The aliphatic cyclic group may be monocyclic or polycyclic.
As the aliphatic cyclic group, those having 3 to 30 carbon atoms are preferable, those having 5 to 30 are more preferable, 5 to 20 are more preferable, 6 to 15 are particularly preferable, and 6 to 12 is most preferable. . As the monocyclic aliphatic cyclic group, a group in which one or more hydrogen atoms have been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclobutane, cyclopentane, and cyclohexane. The polycyclic aliphatic cyclic group is preferably a group obtained by removing one or more hydrogen atoms from a polycycloalkane, and the polycycloalkane preferably has 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like. Moreover, a part of carbon atoms constituting the ring of these aliphatic cyclic groups may be substituted with an ether group (—O—).

Examples of the acid dissociable group containing an aliphatic cyclic group include:
(I) a substituent on a carbon atom bonded to an atom (for example, —O— in —C (═O) —O—) adjacent to the acid dissociable group on the ring skeleton of the monovalent aliphatic cyclic group A group in which (atom or group other than hydrogen atom) is bonded to form a tertiary carbon atom;
(Ii) a group having a monovalent aliphatic cyclic group and a branched alkylene having a tertiary carbon atom bonded thereto.
In the group (i), examples of the substituent bonded to the carbon atom bonded to the atom adjacent to the acid dissociable group on the ring skeleton of the aliphatic cyclic group include an alkyl group. Examples of the alkyl group include those similar to R ¹⁴ in formulas (1-1) to (1-7) described later.
Specific examples of the group (i) include groups represented by the following general formulas (1-1) to (1-7).
Specific examples of the group (ii) include groups represented by the following general formulas (2-1) to (2-6).

［式中、Ｒ^１４は直鎖状、又は分岐鎖状のアルキル基であり、ｇは０〜８の整数である。］

[Wherein, R ¹⁴ represents a linear or branched alkyl group, and g represents an integer of 0 to 8. ]

［式中、Ｒ^１５およびＲ^１６は、それぞれ独立してアルキル基である。］

[Wherein, R ¹⁵ and R ¹⁶ each independently represents an alkyl group. ]

In formulas (1-1) to (1-7), the alkyl group for R ¹⁴ is linear or branched.
The linear alkyl group preferably has 1 to 5 carbon atoms, more preferably 1 to 4, and still more preferably 1 or 2. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, and an n-pentyl group. Among these, a methyl group, an ethyl group, or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.
The branched alkyl group preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include isopropyl group, isobutyl group, tert-butyl group, isopentyl group, neopentyl group and the like, and isopropyl group is most preferable.
g is preferably an integer of 0 to 3, more preferably an integer of 1 to 3, and still more preferably 1 or 2.
In formulas (2-1) to (2-6), examples of the alkyl group for R ^{15 to} R ¹⁶ include the same alkyl groups as those described above for R ¹⁴ .
In the formulas (1-1) to (1-7) and (2-1) to (2-6), part of the carbon atoms constituting the ring is substituted with an etheric oxygen atom (—O—). May be.
In formulas (1-1) to (1-7) and (2-1) to (2-6), a hydrogen atom bonded to a carbon atom constituting the ring may be substituted with a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorine atom, and a fluorinated alkyl group.

The “acetal-type acid dissociable group” is generally bonded to an oxygen atom by substituting a hydrogen atom at the terminal of an OH-containing polar group such as a carboxy group or a hydroxyl group. Then, when an acid is generated by exposure, this acid acts to break the bond between the acetal type acid dissociable group and the oxygen atom to which the acetal type acid dissociable group is bonded, and a carboxy group, a hydroxyl group, etc. OH-containing polar groups are formed.
Examples of the acetal type acid dissociable group include a group represented by the following general formula (p1).

［式中、Ｒ^１’，Ｒ^２’はそれぞれ独立して水素原子または炭素数１〜５のアルキル基を表し、ｎは０〜３の整数を表し、Ｙは炭素数１〜５のアルキル基または脂肪族環式基を表す。］

[Wherein, R ¹ 'and R ² ' each independently represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, n represents an integer of 0 to 3, and Y represents an alkyl group having 1 to 5 carbon atoms. Or represents an aliphatic cyclic group. ]

In formula (p1), n is preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 0.
Examples of the alkyl group for R ¹ ′ and R ² ′ include the same alkyl groups listed as the substituents that may be bonded to the α-position carbon atom in the description of the α-substituted acrylate ester. A methyl group or an ethyl group is preferred, and a methyl group is most preferred.
In the present invention, it is preferable that at least one of R ¹ ′ and R ² ′ is a hydrogen atom. That is, the acid dissociable group (p1) is preferably a group represented by the following general formula (p1-1).

［式中、Ｒ^１’、ｎ、Ｙは上記と同じである。］

[Wherein R ¹ ′, n and Y are the same as described above. ]

Examples of the alkyl group for Y include the same alkyl groups as those described above for the substituent that may be bonded to the carbon atom at the α-position in the description of the α-substituted acrylate ester.
The aliphatic cyclic group for Y can be appropriately selected from monocyclic or polycyclic aliphatic cyclic groups that have been proposed in a number of conventional ArF resists. For example, the above “aliphatic ring” Examples thereof are the same as the aliphatic cyclic groups mentioned in “Acid-dissociable groups containing formula groups”.

  Examples of the acetal type acid dissociable group also include a group represented by the following general formula (p2).

［式中、Ｒ^１７、Ｒ^１８はそれぞれ独立して直鎖状若しくは分岐鎖状のアルキル基または水素原子であり；Ｒ^１９は直鎖状、分岐鎖状若しくは環状のアルキル基である。または、Ｒ^１７およびＲ^１９がそれぞれ独立に直鎖状若しくは分岐鎖状のアルキレン基であって、Ｒ^１７とＲ^１９とが結合して環を形成していてもよい。］

[Wherein, R ¹⁷ and R ¹⁸ each independently represents a linear or branched alkyl group or a hydrogen atom; and R ¹⁹ represents a linear, branched or cyclic alkyl group. Alternatively, R ¹⁷ and R ¹⁹ may each independently be a linear or branched alkylene group, and R ¹⁷ and R ¹⁹ may be bonded to form a ring. ]

In R ¹⁷ and R ¹⁸ , the alkyl group preferably has 1 to 15 carbon atoms, may be linear or branched, and is preferably an ethyl group or a methyl group, and most preferably a methyl group.
In particular, it is preferable that one of R ¹⁷ and R ¹⁸ is a hydrogen atom and the other is a methyl group.
R ¹⁹ is a linear, branched or cyclic alkyl group, preferably having 1 to 15 carbon atoms, and may be any of linear, branched or cyclic.
When R ¹⁹ is linear or branched, it preferably has 1 to 5 carbon atoms, more preferably an ethyl group or a methyl group, and most preferably an ethyl group.
When R ¹⁹ is cyclic, it preferably has 4 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, one or more polycycloalkanes such as monocycloalkane, bicycloalkane, tricycloalkane, and tetracycloalkane, which may or may not be substituted with a fluorine atom or a fluorinated alkyl group. Examples similar to the above “aliphatic cyclic group”, such as a group in which a hydrogen atom is removed, can be exemplified. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.
In the formula (p2), R ¹⁷ and R ¹⁹ are each independently a linear or branched alkylene group (preferably an alkylene group having 1 to 5 carbon atoms), and R ¹⁹ and R ¹⁷ And may be combined.
In this case, a cyclic group is formed by R ¹⁷ , R ¹⁹ , the oxygen atom to which R ¹⁹ is bonded, and the carbon atom to which the oxygen atom and R ¹⁷ are bonded. The cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

  In the polymer of the present invention, the structural unit (a1) is a structural unit derived from an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position may be substituted with a substituent, At least a part of the hydrogen atoms in the hydroxyl group of the structural unit (a11) containing an acid-decomposable group whose polarity increases by action and derived from hydroxystyrene or a hydroxystyrene derivative is protected by a substituent containing an acid-decomposable group At least a part of the hydrogen atoms in —C (═O) —OH of the structural unit derived from the structural unit (a12), vinyl benzoic acid or vinyl benzoic acid derivative is protected by a substituent containing an acid-decomposable group. And the structural unit (a13).

Here, in the present specification and claims, the “structural unit derived from an acrylate ester” means a structural unit formed by cleavage of an ethylenic double bond of an acrylate ester.
“Acrylic acid ester” is a compound in which the hydrogen atom at the carboxy group end of acrylic acid (CH ₂ ═CH—COOH) is substituted with an organic group.
In the acrylate ester, the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent. The substituent that replaces the hydrogen atom bonded to the α-position carbon atom is an atom or group other than a hydrogen atom, such as an alkyl group having 1 to 5 carbon atoms, a halogenated alkyl group having 1 to 5 carbon atoms, or carbon. Examples thereof include hydroxyalkyl groups of 1 to 5. The α-position carbon atom of the acrylate ester is a carbon atom to which a carbonyl group is bonded unless otherwise specified.
Hereinafter, an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position is substituted with a substituent may be referred to as an α-substituted acrylate ester. Further, the acrylate ester and the α-substituted acrylate ester may be collectively referred to as “(α-substituted) acrylate ester”.
In the α-substituted acrylate ester, the alkyl group as a substituent at the α-position is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, n- Examples thereof include a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group.
Specific examples of the halogenated alkyl group as the substituent at the α-position include groups in which part or all of the hydrogen atoms of the above-mentioned “alkyl group as the substituent at the α-position” are substituted with a halogen atom. It is done. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
Specific examples of the hydroxyalkyl group as the substituent at the α-position include groups in which part or all of the hydrogen atoms of the above-mentioned “alkyl group as the substituent at the α-position” are substituted with a hydroxy group. .
Bonded to the α-position of the α-substituted acrylate ester is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, and a hydrogen atom or an alkyl group having 1 to 5 carbon atoms. An alkyl group or a fluorinated alkyl group having 1 to 5 carbon atoms is more preferred, and a hydrogen atom or a methyl group is most preferred from the viewpoint of industrial availability.

“A structural unit derived from hydroxystyrene or a hydroxystyrene derivative” means a structural unit formed by cleavage of an ethylenic double bond of hydroxystyrene or a hydroxystyrene derivative.
“Hydroxystyrene derivative” is a concept including those in which the hydrogen atom at the α-position of hydroxystyrene is substituted with another substituent such as an alkyl group or an alkyl halide group, and derivatives thereof. The α-position (α-position carbon atom) means a carbon atom to which a benzene ring is bonded unless otherwise specified.
The “structural unit derived from vinyl benzoic acid or a vinyl benzoic acid derivative” means a structural unit configured by cleavage of an ethylenic double bond of vinyl benzoic acid or a vinyl benzoic acid derivative.
The “vinyl benzoic acid derivative” is a concept including a compound in which the hydrogen atom at the α-position of vinyl benzoic acid is substituted with another substituent such as an alkyl group or an alkyl halide group, and derivatives thereof. The α-position (α-position carbon atom) means a carbon atom to which a benzene ring is bonded unless otherwise specified.

・ Structural unit (a11)
Specific examples of the structural unit (a11) include structural units represented by general formula (a11-0-1) shown below, structural units represented by general formula (a11-0-2) shown below, and the like. .

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり；Ｘ^１は酸解離性基であり；Ｙ^２は２価の連結基であり；Ｘ^２は酸解離性基である。］

Wherein R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms; X ¹ is an acid dissociable group; Y ² is a divalent linking group. Yes; X ² is an acid-dissociable group. ]

In the general formula (a11-0-1), the alkyl group and the halogenated alkyl group of R are each exemplified as the substituent which may be bonded to the α-position carbon atom in the description of the α-substituted acrylate ester. And the same alkyl groups and halogenated alkyl groups. R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms, and most preferably a hydrogen atom or a methyl group.
X ¹ is not particularly limited as long as it is an acid dissociable group, and examples thereof include the above-described tertiary alkyl ester type acid dissociable groups, acetal type acid dissociable groups, and the like. An ester type acid dissociable group is preferred.
In general formula (a11-0-2), R is the same as defined above.
X ² is the same as X ¹ in formula (a11-0-1).

Examples of the divalent linking group of Y ^2, but are not limited to, divalent hydrocarbon group which may have a substituent group, and a divalent linking group containing a hetero atom as preferred.
The hydrocarbon group having “substituent” means that part or all of the hydrogen atoms in the hydrocarbon group are substituted with a substituent (a group or atom other than a hydrogen atom).
The hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.
An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity.
The aliphatic hydrocarbon group as the divalent hydrocarbon group in Y ² may be saturated or unsaturated, and is usually preferably saturated.
More specific examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like.

The linear or branched aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, more preferably 1 to 4, and most preferably 1 to 3.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.
The linear or branched aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and an oxygen atom (═O).

Examples of the aliphatic hydrocarbon group containing a ring in the structure include an alicyclic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and an alicyclic hydrocarbon group that is linear or branched. Examples thereof include a group bonded to the end of a chain aliphatic hydrocarbon group and a group in which an alicyclic hydrocarbon group is interposed in the middle of a linear or branched aliphatic hydrocarbon group. Examples of the linear or branched aliphatic hydrocarbon group include those described above.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.
The alicyclic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and an oxygen atom (= O).

The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring.
The aromatic hydrocarbon group as the divalent hydrocarbon group in Y ² preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, still more preferably 5 to 20 carbon atoms, and 6 to 6 carbon atoms. 15 is particularly preferable, and 6 to 10 is most preferable. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic ring possessed by the aromatic hydrocarbon group include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene; some of the carbon atoms constituting the aromatic hydrocarbon ring are heterogeneous. Aromatic heterocycles substituted with atoms; and the like. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group is a group obtained by removing two hydrogen atoms from the aromatic hydrocarbon ring (arylene group); a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring (aryl group) ) In which one of the hydrogen atoms is substituted with an alkylene group (for example, arylalkyl such as benzyl, phenethyl, 1-naphthylmethyl, 2-naphthylmethyl, 1-naphthylethyl, 2-naphthylethyl, etc.) Group obtained by further removing one hydrogen atom from the aryl group in the group); and the like. The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.
The aromatic hydrocarbon group may or may not have a substituent. For example, a hydrogen atom bonded to the aromatic hydrocarbon ring of the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

The hetero atom in the “divalent linking group containing a hetero atom” of Y ² is an atom other than a carbon atom and a hydrogen atom, and examples thereof include an oxygen atom, a nitrogen atom, a sulfur atom, and a halogen atom.
As the divalent linking group containing a hetero atom, —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O—, —C (= O) —NH—, —NH— (H may be substituted with a substituent such as an alkyl group, an acyl group, etc.), —S—, —S (═O) ₂ —, —S (═O) _{2 -O -, - NH-C} (= O) -, = N-, the formula ^{-Y 21 -O-Y 22 -,} - [Y 21 -C (= O) -O] m '-Y 22 - Or a group represented by —Y ²¹ —O—C (═O) —Y ²² —, wherein Y ²¹ and Y ²² are each independently a divalent hydrocarbon group optionally having a substituent. O is an oxygen atom, and m ′ is an integer of 0 to 3. ] Etc. are mentioned.
When Y ² is —NH—, H may be substituted with a substituent such as an alkyl group or an aryl group (aromatic group). The substituent (alkyl group, aryl group, etc.) preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and particularly preferably 1 to 5 carbon atoms.
Formula ^{-Y 21 -O-Y 22 -,} - [Y 21 -C (= O) -O] m '-Y 22 - or ^{-Y 21 -O-C (= O} ) -Y 22 - ^{In, Y 21} And Y ²² are each independently a divalent hydrocarbon group which may have a substituent. Examples of the divalent hydrocarbon group include the same groups as those described above as the “divalent hydrocarbon group which may have a substituent” for Y ² .
Y ²¹ is preferably a linear aliphatic hydrocarbon group, more preferably a linear alkylene group, still more preferably a linear alkylene group having 1 to 5 carbon atoms, and particularly preferably a methylene group or an ethylene group. preferable.
Y ²² is preferably a linear or branched aliphatic hydrocarbon group, and more preferably a methylene group, an ethylene group or an alkylmethylene group. The alkyl group in the alkylmethylene group is preferably a linear alkyl group having 1 to 5 carbon atoms, more preferably a linear alkyl group having 1 to 3 carbon atoms, and most preferably a methyl group.
In the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² —, m ′ is an integer of 0 to 3, preferably an integer of 0 to 2, Or 1 is more preferable, and 1 is particularly preferable. That is, the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² — is represented by the formula —Y ²¹ —C (═O) —O—Y ²² —. The group is particularly preferred. Among these, a group represented by the formula — (CH ₂ ) _{a ′} —C (═O) —O— (CH ₂ ) _{b ′} — is preferable. In the formula, a ′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, further preferably 1 or 2, and most preferably 1. b ′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, more preferably 1 or 2, and most preferably 1.
Examples of the divalent linking group containing a hetero atom, a linear group containing an oxygen atom as a hetero atom, for example, a group containing an ether bond or an ester bond, are preferred, the formula -Y 21 ^-O-Y 22 ^-, A group represented by — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² — or —Y ²¹ —O—C (═O) —Y ²² — is more preferable.

Among these, as the divalent linking group for Y ² , in particular, a linear or branched alkylene group, a divalent alicyclic hydrocarbon group, or a divalent linking group containing a hetero atom is included. preferable. Among these, a linear or branched alkylene group or a divalent linking group containing a hetero atom is preferable.

  More specifically, examples of the structural unit (a11) include structural units represented by general formulas (a1-1) to (a1-4) shown below.

［式中、Ｒ、Ｒ^１’、Ｒ^２’、ｎ、ＹおよびＹ^２はそれぞれ前記と同じであり、Ｘ’は第３級アルキルエステル型酸解離性基を表す。］’

[Wherein, R, R ¹ ′, R ² ′, n, Y and Y ² are the same as defined above, and X ′ represents a tertiary alkyl ester-type acid dissociable group. ] '

In the formula, X ′ is the same as the tertiary alkyl ester-type acid dissociable group.
^{R 1 ', R 2',} n, as the Y, respectively, ^{R 1} in the general formula listed in the description of "acetal-type acid dissociable group" described above ^{(p1) ', R 2'} , n, similarly to the Y Can be mentioned.
The Y ^2, the same groups as those described above for ^{Y 2} in the above general formula (a11-0-2).
Specific examples of the structural units represented by the general formulas (a1-1) to (a1-4) are shown below.
In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

In the present invention, as the structural unit (a11), a structural unit represented by the following general formula (a11-0-11), a structural unit represented by the following general formula (a11-0-12), and the following general formula ( a11-0-13), a structural unit represented by the following general formula (a11-0-14), a structural unit represented by the following general formula (a11-0-15), and the following general unit It is preferable to have at least one selected from the group consisting of structural units represented by formula (a11-0-2).
Among them, the structural unit represented by the following general formula (a11-0-11), the structural unit represented by the following general formula (a11-0-12), and the following general formula (a11-0-13) A structural unit represented by the following general formula (a11-0-14) and at least one selected from the group consisting of the structural unit represented by the following general formula (a11-0-15) It is more preferable.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり、Ｒ^８１は直鎖状、又は分岐鎖状のアルキル基であり；Ｒ^８２は、当該Ｒ^８２が結合した炭素原子と共に脂肪族単環式基を形成する基であり；Ｒ^８３は分岐鎖状のアルキル基であり；Ｒ^８４は、当該Ｒ^８４が結合した炭素原子と共に脂肪族多環式基を形成する基であり；Ｒ^８５は炭素数１〜５の直鎖状のアルキル基である。Ｒ^１５およびＲ^１６は、それぞれ独立してアルキル基である。Ｙ^２は２価の連結基であり、Ｘ^２は酸解離性基である。］

Wherein R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, R ⁸¹ is a linear or branched alkyl group; R ⁸² Is a group that forms an aliphatic monocyclic group together with the carbon atom to which R ⁸² is bonded; R ⁸³ is a branched alkyl group; R ⁸⁴ is an aliphatic group together with the carbon atom to which R ⁸⁴ is bonded. R ⁸⁵ is a linear alkyl group having 1 to 5 carbon atoms. R ¹⁵ and R ¹⁶ are each independently an alkyl group. Y ² is a divalent linking group, and X ² is an acid dissociable group. ]

In each formula, the description of R, Y ² and X ² is the same as described above.
In formula (a11-0-11), the alkyl group for R ⁸¹ is the same as the linear or branched alkyl group for R ¹⁴ in formulas (1-1) to (1-7). And a methyl group, an ethyl group or an isopropyl group is preferable.
R ⁸² is, the aliphatic monocyclic group formed together with the carbon atom to which R ⁸² is bonded, the same aliphatic cyclic groups as those in the aforementioned tertiary alkyl ester-type acid dissociable groups, a monocyclic group The thing similar to what is is mentioned. Specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably a 3- to 11-membered ring, more preferably a 3- to 8-membered ring, further preferably a 4- to 6-membered ring, and particularly preferably a 5- or 6-membered ring.
In the monocycloalkane, a part of carbon atoms constituting the ring may or may not be substituted with an ether group (—O—).
Moreover, this monocycloalkane may have a C1-C5 alkyl group, a fluorine atom, or a C1-C5 fluorinated alkyl group as a substituent.
Examples of R ⁸² constituting the aliphatic monocyclic group include a linear alkylene group in which an ether group (—O—) may be interposed between carbon atoms.

Specific examples of the structural unit represented by the formula (a11-0-11) include the formulas (a1-1-16) to (a1-1-23), (a1-1-27), and (a1-1 -31). Among these, the formulas (a1-1-16) to (a1-1-17), (a1-1-20) to (a1-1-23), (a1-1-27), (a1-1-1- The structural unit represented by the following (a11-1-02) including the structural units represented by 31), (a1-1-32), and (a1-1-33) is preferable. Moreover, the structural unit represented by the following (a11-1-02 ′) is also preferable.
In each formula, h is an integer of 1 to 4, and 1 or 2 is preferable.

［式中、Ｒ、Ｒ^８１はそれぞれ前記と同じであり、ｈは１〜４の整数である。］

[Wherein, R and R ⁸¹ are the same as defined above, and h is an integer of 1 to 4. ]

Wherein ^(A11-0-12), as the branched alkyl group ^{R 83,} the alkyl of the formula (1-1) to (1-7) branched chain mentioned by an alkyl group ^{R 14} in Examples thereof are the same as those described above, and an isopropyl group is most preferable.
R ⁸⁴ is, the aliphatic polycyclic group formed together with the carbon atom to which R ⁸⁴ is bonded, the same aliphatic cyclic groups as those in the aforementioned tertiary alkyl ester-type acid dissociable group, polycyclic group The thing similar to what is is mentioned.
Specific examples of the structural unit represented by the formula (a11-0-12) include those represented by the formulas (a1-1-26) and (a1-1-28) to (a1-1-30). Units are listed.
The constitutional unit represented by formula ^{(a11-0-12), R 84} is preferably the aliphatic polycyclic group which forms together with the carbon atom to which ^{R 84} is bonded is a 2-adamantyl group, especially The structural unit represented by the formula (a1-1-26) is preferable.

In formula (a11-0-13), R and R ⁸⁴ are the same as defined above.
^Examples of the linear alkyl group for R ⁸⁵ include the same linear alkyl groups as those described above for the alkyl group for R ¹⁴ in formulas (1-1) to (1-7). Most preferred are groups or ethyl groups.
Specific examples of the structural unit represented by the formula (a11-0-13) include formulas (a1-1-1) to (a1-1-2) exemplified as specific examples of the general formula (a1-1). ), Structural units represented by (a1-1-7) to (a1-1-15).
As the structural unit represented by the formula (a11-0-13), those in which R ⁸⁴ is an aliphatic polycyclic group formed together with the carbon atom to which R ⁸⁴ is bonded are preferably a 2-adamantyl group, The structural unit represented by the formula (a1-1-1) or (a1-1-2) is preferable. Further, R ⁸⁴ is also preferably the aliphatic polycyclic group which forms together with the carbon atom to which R ⁸⁴ is bonded is a "group obtained by removing one or more hydrogen atoms from tetracyclododecane", the formula (a1 The structural unit represented by (-1-8), (a1-1-9) or (a1-1-30) is also preferable.

In formula (a11-0-14), R and R ⁸² are the same as defined above. R ¹⁵ and ^{R 16} are the same as ^{R 15} and ^{R 16} in each of the general formulas (2-1) to (2-6).
Specific examples of the structural unit represented by the formula (a11-0-14) include the formulas (a1-1-35) and (a1-1-36) exemplified as specific examples of the general formula (a1-1). ).

In formula (a11-0-15), R and R ⁸⁴ are the same as defined above. R ¹⁵ and ^{R 16} are the same as ^{R 15} and ^{R 16} in each of the general formulas (2-1) to (2-6).
Specific examples of the structural unit represented by the formula (a11-0-15) include formulas (a1-1-4) to (a1-1-6) exemplified as specific examples of the general formula (a1-1). ) And (a1-1-34).

Examples of the structural unit represented by the formula (a11-0-2) include the structural unit represented by the formula (a1-3) or (a1-4), particularly represented by the formula (a1-3). Are preferred.
As the structural unit represented by the formula (a11-0-2), in particular, Y ^{2 in} the formula is —Y ²¹ —O—Y ²² — or —Y ²¹ —C (═O) —O—Y ^22. Those represented by-are preferred.
Preferred examples of the structural unit include a structural unit represented by the following general formula (a1-3-01); a structural unit represented by the following general formula (a1-3-02); 3-03) and the like.

［式中、Ｒは前記と同じであり、Ｒ^１３は水素原子またはメチル基であり、Ｒ^１４は直鎖状、又は分岐鎖状のアルキル基であり、ｅは１〜１０の整数であり、ｎ’は０〜３の整数である。］

[Wherein, R is the same as above, R ¹³ is a hydrogen atom or a methyl group, R ¹⁴ is a linear or branched alkyl group, e is an integer of 1 to 10, n 'is an integer of 0-3. ]

［式中、Ｒは前記と同じであり、Ｙ^２’およびＹ^２”はそれぞれ独立して２価の連結基であり、Ｘ’は酸解離性基であり、ｗは０〜３の整数である。］

[Wherein, R is as defined above, Y ² ′ and Y ² ″ are each independently a divalent linking group, X ′ is an acid-dissociable group, and w is an integer of 0 to 3] is there.]

In formulas (a1-3-01) to (a1-3-02), R ¹³ is preferably a hydrogen atom.
R ¹⁴ is the same as ^{R 14} in the formula (1-1) to (1-7) in.
e is preferably an integer of 1 to 8, more preferably an integer of 1 to 5, and most preferably 1 or 2.
n ′ is preferably 1 or 2, and most preferably 2.
Specific examples of the structural unit represented by the formula (a1-3-01) include structural units represented by the formulas (a1-3-25) to (a1-3-26).
Specific examples of the structural unit represented by the formula (a1-3-02) include structural units represented by the formulas (a1-3-27) to (a1-3-28).

In formula (a1-3-03), examples of the divalent linking group for Y ² ′ and Y ² ″ include the same groups as those described above for Y ² in formula (a1-3).
Y ² ′ is preferably a divalent hydrocarbon group which may have a substituent, more preferably a linear aliphatic hydrocarbon group, and even more preferably a linear alkylene group. Among these, a linear alkylene group having 1 to 5 carbon atoms is preferable, and a methylene group and an ethylene group are most preferable.
Y ² ″ is preferably a divalent hydrocarbon group which may have a substituent, more preferably a linear aliphatic hydrocarbon group, and still more preferably a linear alkylene group. A linear alkylene group of 1 to 5 is preferable, and a methylene group and an ethylene group are most preferable.
Examples of the acid dissociable group in X ′ include the same groups as described above, and are preferably tertiary alkyl ester-type acid dissociable groups, and the ring skeleton of the above-described (i) monovalent aliphatic cyclic group In addition, a group in which a substituent is bonded to a carbon atom bonded to an atom adjacent to the acid dissociable group to form a tertiary carbon atom is more preferable, and among them, the group represented by the general formula (1-1) is preferable. Preferred are the groups
w is an integer of 0 to 3, and w is preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 1.
As the structural unit represented by the formula (a1-3-03), a structural unit represented by the following general formula (a1-3-03-1) or (a1-3-03-2) is preferable. The structural unit represented by the formula (a1-3-03-1) is preferable.

［式中、ＲおよびＲ^１４はそれぞれ前記と同じであり、ａ’は１〜１０の整数であり、ｂ’は１〜１０の整数であり、ｔは０〜３の整数である。］

[Wherein, R and R ¹⁴ are the same as defined above, a ′ is an integer of 1 to 10, b ′ is an integer of 1 to 10, and t is an integer of 0 to 3, respectively. ]

In formulas (a1-3-03-1) to (a1-3-03-2), a ′ is the same as described above, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, or 1 or 2 is particularly preferred.
b ′ is the same as described above, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, and particularly preferably 1 or 2.
t is preferably an integer of 1 to 3, and 1 or 2 is particularly preferable.
Specific examples of the structural unit represented by formula (a1-3-03-1) or (a1-3-03-2) include those represented by formulas (a1-3-29) to (a1-3-32). The structural unit represented is mentioned.

Structural unit (a12), structural unit (a13)
In the present specification, the structural unit (a12) is a structural unit in which at least a part of hydrogen atoms in the phenolic hydroxyl group of the structural unit derived from hydroxystyrene or a hydroxystyrene derivative is protected by a substituent containing an acid-decomposable group. It is.
In addition, the structural unit (a13) is protected by a substituent in which at least a part of the hydrogen atoms in —C (═O) —OH of the structural unit derived from vinylbenzoic acid or a vinylbenzoic acid derivative contains an acid-decomposable group. Unit.
In the structural unit (a12) and the structural unit (a13), examples of the substituent containing an acid-decomposable group include a group represented by the formula (a10-1) or the formula (a10-2) in the structural unit (a10), Preferred examples include the tertiary alkyl ester type acid dissociable group and the acetal type acid dissociable group described in the structural unit (a11).

As the structural unit (a1) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
Among these, the structural unit (a1) is preferably a structural unit (a11) derived from an acrylate ester in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent. .
In the component (A1), the proportion of the structural unit (a1) is preferably from 15 to 70 mol%, more preferably from 15 to 60 mol%, more preferably from 20 to 55 mol%, based on all the structural units constituting the component (A1). Is more preferable.
By setting the proportion of the structural unit (a1) to the lower limit value or more, a pattern can be easily obtained when a resist composition is formed, and the lithography properties such as sensitivity, resolution, and LWR are also improved. Moreover, it becomes easy to balance with another structural unit by setting it as an upper limit or less.

(Structural unit (a2))
In addition to the structural unit (a1), the component (A) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent. A structural unit derived from a structural unit (a2 ^S ) containing an SO ₂ -containing cyclic group, and an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, and a lactone it may contain at least one constituent unit selected from the group consisting of structural units including a containing cyclic group (a2 ^{L) (a2).}
The structural unit (a2) contains a —SO ₂ -containing cyclic group or a lactone cyclic group so that the resist film formed using the resist composition containing the polymer of the present invention has adhesion to the substrate. And increase the affinity with a developer containing water (especially in the case of an alkali development process), thereby contributing to the improvement of lithography properties.

-Structural unit (a2 ^S ):
The structural unit (a2 ^S ) is a structural unit derived from an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position may be substituted with a substituent, and includes a —SO ₂ — containing cyclic group. It is a structural unit.
Here, -SO ₂ - and containing cyclic group, -SO ₂ - within the ring skeleton thereof shows a cyclic group containing a ring containing, in particular, -SO ₂ - in the sulfur atom (S) Are cyclic groups that form part of the ring skeleton of the cyclic group. The ring containing —SO ₂ — in the ring skeleton is counted as the first ring, and when it is only the ring, it is a monocyclic group, and when it has another ring structure, it is a polycyclic group regardless of the structure. Called. The —SO ₂ — containing cyclic group may be monocyclic or polycyclic.
-SO ₂ - containing cyclic group, in particular, -O-SO ₂ - within the ring skeleton cyclic group containing, i.e. -O-SO ₂ - -O-S- medium is a part of the ring skeleton It is preferably a cyclic group containing a sultone ring to be formed.
The —SO ₂ — containing cyclic group preferably has 3 to 30 carbon atoms, more preferably 4 to 20 carbon atoms, still more preferably 4 to 15 carbon atoms, and particularly preferably 4 to 12 carbon atoms. preferable. However, the carbon number is the number of carbon atoms constituting the ring skeleton, and does not include the carbon number in the substituent.
The —SO ₂ — containing cyclic group may be an —SO ₂ — containing aliphatic cyclic group or an —SO ₂ — containing aromatic cyclic group. Preferably -SO ₂ - containing aliphatic cyclic group.
The —SO ₂ -containing aliphatic cyclic group includes at least a hydrogen atom from an aliphatic hydrocarbon ring in which a part of carbon atoms constituting the ring skeleton is substituted with —SO ₂ — or —O—SO ₂ —. One group is excluded. More specifically, a group obtained by removing at least one hydrogen atom from an aliphatic hydrocarbon ring in which —CH ₂ — constituting the ring skeleton is substituted with —SO ₂ —, —CH ₂ — constituting the ring And a group obtained by removing at least one hydrogen atom from an aliphatic hydrocarbon ring in which CH ₂ — is substituted with —O—SO ₂ —.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms are removed from a monocycloalkane having 3 to 6 carbon atoms. Examples of the monocycloalkane include cyclopentane and cyclohexane. As the polycyclic alicyclic hydrocarbon group, a group in which two hydrogen atoms have been removed from a polycycloalkane having 7 to 12 carbon atoms is preferable. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane. , Tricyclodecane, tetracyclododecane and the like.

The —SO ₂ — containing cyclic group may have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O), —COOR ″, —OC (═O) R ″, a hydroxyalkyl group, a cyano group, and the like. Is mentioned.
The alkyl group as the substituent is preferably an alkyl group having 1 to 6 carbon atoms. The alkyl group is preferably linear or branched. Specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, a neopentyl group, and a hexyl group. Among these, a methyl group or an ethyl group is preferable, and a methyl group is particularly preferable.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 6 carbon atoms. The alkoxy group is preferably linear or branched. Specifically, the group couple | bonded with the oxygen atom (-O-) to the alkyl group quoted as the alkyl group as the said substituent is mentioned.
Examples of the halogen atom as the substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group for the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group mentioned as the alkyl group as the substituent are substituted with the halogen atom. As the halogenated alkyl group, a fluorinated alkyl group is preferable, and a perfluoroalkyl group is particularly preferable.
R ″ in —COOR ″ and —OC (═O) R ″ is a hydrogen atom or a linear, branched or cyclic alkyl group having 1 to 15 carbon atoms.
When R ″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and particularly preferably a methyl group or an ethyl group. preferable.
When R ″ is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, a fluorine atom Alternatively, one or more hydrogen atoms are removed from a polycycloalkane such as a monocycloalkane, bicycloalkane, tricycloalkane, or tetracycloalkane, which may or may not be substituted with a fluorinated alkyl group. More specifically, one or more hydrogen atoms are removed from a monocycloalkane such as cyclopentane or cyclohexane, or a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane. Group.
The hydroxyalkyl group as the substituent is preferably one having 1 to 6 carbon atoms. Specifically, at least one of the hydrogen atoms of the alkyl group mentioned as the alkyl group as the substituent is substituted with a hydroxyl group. Group.
More specifically, examples of the —SO ₂ -containing cyclic group include groups represented by the following general formulas (3-1) to (3-4).

［式中、Ａ’は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり、ｚは０〜２の整数であり、Ｒ^２７はアルキル基、アルコキシ基、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり、Ｒ”は水素原子またはアルキル基である。］

[In the formula, A ′ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, z is an integer of 0 to 2, and R ²⁷ is an alkyl group. , An alkoxy group, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group, and R ″ is a hydrogen atom or an alkyl group.]

In the general formulas (3-1) to (3-4), A ′ represents an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom (—O—) or a sulfur atom (—S—), An oxygen atom or a sulfur atom.
The alkylene group having 1 to 5 carbon atoms in A ′ is preferably a linear or branched alkylene group, and examples thereof include a methylene group, an ethylene group, an n-propylene group, and an isopropylene group.
When the alkylene group contains an oxygen atom or a sulfur atom, specific examples thereof include a group in which —O— or —S— is interposed between the terminal or carbon atoms of the alkylene group, such as —O—CH _{2. -, - CH 2 -O-CH} 2 -, - S-CH 2 -, - CH 2 -S-CH 2 - , and the like.
A ′ is preferably an alkylene group having 1 to 5 carbon atoms or —O—, more preferably an alkylene group having 1 to 5 carbon atoms, and most preferably a methylene group.
z may be any of 0 to 2, and is most preferably 0.
When z is 2, the plurality of R ²⁷ may be the same or different.
As the alkyl group, alkoxy group, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in R ²⁷ , the —SO ₂ — containing cyclic group has the above-mentioned, respectively. And the same alkyl groups, alkoxy groups, halogenated alkyl groups, —COOR ″, —OC (═O) R ″, and hydroxyalkyl groups as those which may be substituted.
Below, the specific cyclic group represented by the said general formula (3-1)-(3-4) is illustrated. In the formula, “Ac” represents an acetyl group.

Among the above, the —SO ₂ -containing cyclic group is preferably a group represented by the general formula (3-1), and the chemical formulas (3-1-1), (3-1-18), ( It is more preferable to use at least one selected from the group consisting of groups represented by any of 3-3-1) and (3-4-1), and represented by the chemical formula (3-1-1). Are most preferred.

More specifically, examples of the structural unit (a2 ^S ) include structural units represented by general formula (a2-0) shown below.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり、Ｒ^２８は−ＳＯ_２−含有環式基であり、Ｒ^２９は単結合または２価の連結基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, R ²⁸ represents a —SO ₂ — containing cyclic group, and R ²⁹ represents a single bond. Or it is a bivalent coupling group. ]

In formula (a2-0), R is the same as defined above.
R ²⁸ is the same as the —SO ₂ — containing cyclic group mentioned above.
R ²⁹ may be a single bond or a divalent linking group. Since it is excellent in the effect of this invention, it is preferable that it is a bivalent coupling group.
Examples of the divalent linking group for R ^29, not particularly limited, for example, those similar to the divalent linking group for X of the formula (I-1) in the like. Among these, those containing an alkylene group or an ester bond (—C (═O) —O—) are preferable.
The alkylene group is preferably a linear or branched alkylene group. Specifically, the same as the linear alkylene group and the branched alkylene group mentioned as the aliphatic hydrocarbon group for Y ² can be used.
As the divalent linking group containing an ester bond, in particular, the general formula: —R ³⁰ —C (═O) —O— [wherein R ³⁰ is a divalent linking group. ] Is preferable. That is, the structural unit (a2 ^S ) is preferably a structural unit represented by the following general formula (a2-0-1).

［式中、ＲおよびＲ^２８はそれぞれ前記と同様であり、Ｒ^３０は２価の連結基である。］

[Wherein, R and R ²⁸ are the same as defined above, and R ³⁰ is a divalent linking group. ]

R ³⁰ is not particularly limited, and examples thereof include the same as those for Y ² in the general formula (a11-0-2) mentioned in the description of the structural unit (a1).
The divalent linking group for R ³⁰ is preferably a linear or branched alkylene group, an aliphatic hydrocarbon group containing a ring in the structure, or a divalent linking group containing a hetero atom.
Examples of the linear or branched alkylene group, the aliphatic hydrocarbon group containing a ring in the structure, and the divalent linking group containing a hetero atom are the same as those for R ² in the formula (a0-1). Examples thereof include linear or branched alkylene groups, aliphatic hydrocarbon groups containing a ring in the structure, and divalent linking groups containing a hetero atom.
Among these, a linear or branched alkylene group or a divalent linking group containing an oxygen atom as a hetero atom is preferable.
As the linear alkylene group, a methylene group or an ethylene group is preferable, and a methylene group is particularly preferable.
As the branched alkylene group, an alkylmethylene group or an alkylethylene group is preferable, and —CH (CH ₃ ) —, —C (CH ₃ ) ₂ — or —C (CH ₃ ) ₂ CH ₂ — is particularly preferable.
The divalent linking group containing an oxygen atom is preferably a divalent linking group containing an ether bond or an ester bond, and has the formula -AO-B-,-[A-C (= O) -O] _{m '.} A group represented by —B— or —A—O—C (═O) —B— is more preferable. A and B are each independently a divalent hydrocarbon group which may have a substituent, and are the same as A and B described above. m 'is an integer of 0-3.
Among them, preferred is a group represented by the formula -A-O-C (= O ) -B-, - represented by _{- (CH 2) c -O-} C (= O) - (CH 2) d The group is particularly preferred. c is an integer of 1 to 5, and 1 or 2 is preferable. d is an integer of 1-5, and 1 or 2 is preferable.

As the structural unit (a2 ^S ), a structural unit represented by general formula (a2-0-11) or (a2-0-12) shown below is particularly desirable, and represented by formula (a2-0-12). A structural unit is more preferable.

［式中、Ｒ、Ａ’、Ｒ^２７、ｚおよびＲ^３０はそれぞれ前記と同じである。］

[Wherein, R, A ′, R ²⁷ , z and R ³⁰ are the same as defined above. ]

In formula (a2-0-11), A ′ is preferably a methylene group, an oxygen atom (—O—) or a sulfur atom (—S—).
R ³⁰ is preferably a linear or branched alkylene group or a divalent linking group containing an oxygen atom. As the linear or branched alkylene group and the divalent linking group containing an oxygen atom in R ^30, the linear or branched alkylene group mentioned above and a divalent linking group containing an oxygen atom are mentioned. Examples are the same as the linking group.
As the structural unit represented by the formula (a2-0-12), a structural unit represented by the following general formula (a2-0-12a) or (a2-0-12b) is particularly preferable.

［式中、ＲおよびＡ’はそれぞれ前記と同じであり、ｃ〜ｅはそれぞれ独立に１〜３の整数である。］

[Wherein, R and A ′ are the same as defined above, and c to e are each independently an integer of 1 to 3.] ]

-Structural unit (a2 ^L ):
The structural unit (a2 ^L ) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, and includes a lactone-containing cyclic group. is there.
Here, the lactone-containing cyclic group refers to a cyclic group containing a ring (lactone ring) containing —O—C (═O) — in the ring skeleton. The lactone ring is counted as the first ring. When only the lactone ring is present, it is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The lactone-containing cyclic group may be a monocyclic group or a polycyclic group.
The lactone cyclic group in the structural unit (a2 ^L ) is not particularly limited, and any one can be used. Specifically, the lactone-containing monocyclic group is a group obtained by removing one hydrogen atom from a 4- to 6-membered ring lactone, such as a group obtained by removing one hydrogen atom from β-propionolactone, or γ-butyrolactone. Examples thereof include a group in which one hydrogen atom has been removed and a group in which one hydrogen atom has been removed from δ-valerolactone. Examples of the lactone-containing polycyclic group include groups in which one hydrogen atom has been removed from a bicycloalkane, tricycloalkane, or tetracycloalkane having a lactone ring.
Examples of the structural unit (a2 ^L ) include those obtained by substituting R ²⁸ in the general formula (a2-0) with a lactone-containing cyclic group, and more specifically, the following general formula (a2- The structural unit represented by 1)-(a2-5) is mentioned.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり；Ｒ’はそれぞれ独立に水素原子、炭素数１〜５のアルキル基、炭素数１〜５のアルコキシ基、シアノ基または−ＣＯＯＲ”であり、Ｒ”は水素原子またはアルキル基であり；Ｒ^２９は単結合または２価の連結基であり、ｓ”は０〜２の整数であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり；ｍは０または１である。］

[Wherein, R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms; R ′ is independently a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, carbon An alkoxy group having a number of 1 to 5, a cyano group or —COOR ″, R ″ is a hydrogen atom or an alkyl group; R ²⁹ is a single bond or a divalent linking group, and s ″ is an integer of 0 to 2. A ″ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom; m is 0 or 1. ]

R in the general formulas (a2-1) to (a2-5) is the same as described above.
Examples of the alkyl group having 1 to 5 carbon atoms of R ′ include a methyl group, an ethyl group, a propyl group, an n-butyl group, and a tert-butyl group.
Examples of the alkoxy group having 1 to 5 carbon atoms of R ′ include a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, and a tert-butoxy group.
R ′ is preferably a hydrogen atom in view of industrial availability.
The alkyl group in R ″ may be linear, branched or cyclic.
When R ″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, and more preferably 1 to 5 carbon atoms.
When R ″ is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, a fluorine atom Or a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as monocycloalkane, bicycloalkane, tricycloalkane, and tetracycloalkane, which may or may not be substituted with a fluorinated alkyl group Specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane, or a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Etc.
Examples of A ″ include the same as A ′ in the general formula (3-1). A ″ represents an alkylene group having 1 to 5 carbon atoms, an oxygen atom (—O—) or a sulfur atom (— S-) is preferable, and an alkylene group having 1 to 5 carbon atoms or -O- is more preferable. The alkylene group having 1 to 5 carbon atoms is more preferably a methylene group or dimethylmethylene group, and most preferably a methylene group.
R ²⁹ is the same as ^{R 29} in the aforementioned general formula (a2-0).
In formula (a2-1), s ″ is preferably 1 to 2.
Specific examples of the structural units represented by the general formulas (a2-1) to (a2-5) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a2 ^L ), at least one selected from the group consisting of structural units represented by the general formulas (a2-1) to (a2-5) is preferable, and the general formula (a2-1) to More preferably, at least one selected from the group consisting of structural units represented by (a2-3) is selected from the group consisting of structural units represented by the general formula (a2-1) or (a2-3) Particularly preferred is at least one of the above.
Among them, the formulas (a2-1-1), (a2-1-2), (a2-2-1), (a2-2-7), (a2-2-12), (a2-2-2-) 14), (a2-3-1), at least one selected from the group consisting of structural units represented by (a2-3-5) is preferred.

In the component (A1), as the structural unit (a2), one type of structural unit may be used, or two or more types may be used in combination. For example, as the structural unit (a2), only the structural unit (a2 ^S ) may be used, or only the structural unit (a2 ^L ) may be used, or they may be used in combination. As the structural unit (a2 ^S ) or the structural unit (a2 ^L ), one type may be used alone, or two or more types may be used in combination.

In the component (A1), the proportion of the structural unit (a2) is preferably 1 to 80 mol%, and preferably 10 to 70 mol%, based on the total of all structural units constituting the component (A1). More preferably, it is more preferably 10 to 65 mol%, particularly preferably 10 to 60 mol%.
By making it the lower limit value or more, the effect of containing the structural unit (a2) can be sufficiently obtained, and by making it the upper limit value or less, it is possible to balance with other structural units, and various lithography characteristics and patterns Good shape.

(Structural unit (a3))
The structural unit (a3) is a structural unit derived from an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position may be substituted with a substituent, and includes a polar group-containing aliphatic hydrocarbon group It is a unit (excluding those corresponding to the structural unit (a1) and the structural unit (a2)).
When the component (A1) has the structural unit (a3), the hydrophilicity of the component (A) increases, which contributes to the improvement of resolution.
Examples of the polar group include a hydroxyl group, a cyano group, a carboxy group, and a hydroxyalkyl group in which a part of hydrogen atoms of an alkyl group is substituted with a fluorine atom. A hydroxyl group is particularly preferable.
Examples of the aliphatic hydrocarbon group include a linear or branched hydrocarbon group having 1 to 10 carbon atoms (preferably an alkylene group) and a cyclic aliphatic hydrocarbon group (cyclic group). The cyclic group may be a monocyclic group or a polycyclic group. For example, a resin for a resist composition for an ArF excimer laser can be appropriately selected from those proposed. The cyclic group is preferably a polycyclic group, and more preferably 7 to 30 carbon atoms.
Among them, a structural unit derived from an acrylate ester containing an aliphatic polycyclic group containing a hydroxyalkyl group in which a part of hydrogen atoms of a hydroxyl group, a cyano group, a carboxy group, or an alkyl group is substituted with a fluorine atom Is more preferable. Examples of the polycyclic group include groups in which two or more hydrogen atoms have been removed from bicycloalkane, tricycloalkane, tetracycloalkane and the like. Specific examples include groups in which two or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among these polycyclic groups, there are groups in which two or more hydrogen atoms have been removed from adamantane, groups in which two or more hydrogen atoms have been removed from norbornane, and groups in which two or more hydrogen atoms have been removed from tetracyclododecane. Industrially preferable.

  The structural unit (a3) is derived from a hydroxyethyl ester of acrylic acid when the hydrocarbon group in the polar group-containing aliphatic hydrocarbon group is a linear or branched hydrocarbon group having 1 to 10 carbon atoms. When the hydrocarbon group is a polycyclic group, the structural unit represented by the following formula (a3-1), the structural unit represented by the formula (a3-2), the formula ( The structural unit represented by a3-3) is preferred.

（式中、Ｒは前記と同じであり、ｊは１〜３の整数であり、ｋは１〜３の整数であり、ｔ’は１〜３の整数であり、ｌは１〜５の整数であり、ｓは１〜３の整数である。）

(Wherein R is the same as above, j is an integer of 1 to 3, k is an integer of 1 to 3, t 'is an integer of 1 to 3, and l is an integer of 1 to 5) And s is an integer of 1 to 3.)

In formula (a3-1), j is preferably 1 or 2, and more preferably 1. When j is 2, it is preferable that the hydroxyl group is bonded to the 3rd and 5th positions of the adamantyl group. When j is 1, it is preferable that the hydroxyl group is bonded to the 3-position of the adamantyl group.
j is preferably 1, and it is particularly preferred that the hydroxyl group is bonded to the 3-position of the adamantyl group.

  In formula (a3-2), k is preferably 1. The cyano group is preferably bonded to the 5th or 6th position of the norbornyl group.

  In formula (a3-3), t ′ is preferably 1. l is preferably 1. s is preferably 1. In these, a 2-norbornyl group or a 3-norbornyl group is preferably bonded to the terminal of the carboxy group of acrylic acid. The fluorinated alkyl alcohol is preferably bonded to the 5th or 6th position of the norbornyl group.

As the structural unit (a3) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
In the component (A1), the proportion of the structural unit (a3) is preferably 5 to 50 mol%, more preferably 5 to 40 mol%, based on the total of all structural units constituting the component (A1). 5 to 25 mol% is more preferable.
By setting the proportion of the structural unit (a3) to the lower limit value or more, the effect of including the structural unit (a3) can be sufficiently obtained, and by setting the proportion of the structural unit (a3) to the upper limit value or less, balance with other structural units can be obtained. It becomes easy.

In addition to the structural unit (a1), the component (A) is a structural unit in addition to the structural units (a1) and (a2) or in addition to the structural units (a1), (a2) and (a3). Other structural units other than (a1), (2) and (a3) may be included.
The other structural unit is not particularly limited as long as it is another structural unit that is not classified into the structural unit structural units (a1), (2), and (a3) described above. For ArF excimer laser, KrF excimer laser A number of hitherto known materials can be used as those used for resist resins such as for use (preferably for ArF excimer laser).
Such other structural unit is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, and is a non-acid dissociable aliphatic polycyclic Examples thereof include a structural unit (a4) containing a group, a structural unit (a5) derived from hydroxystyrene, and a structural unit (a6) derived from styrene.

The “structural unit derived from hydroxystyrene” means a structural unit formed by cleavage of an ethylenic double bond of hydroxystyrene.
“Hydroxystyrene” refers to hydroxystyrene in which a hydrogen atom is bonded to the α-position carbon atom (carbon atom to which the phenyl group is bonded), and a substituent (an atom or group other than a hydrogen atom) to the α-position carbon atom. ) And the derivatives thereof. Specifically, at least a benzene ring and a hydroxyl group bonded to the benzene ring are maintained. For example, a hydrogen atom bonded to the α-position of hydroxystyrene is an alkyl group having 1 to 5 carbon atoms, 5 substituted with a substituent such as a halogenated alkyl group of 5 or a hydroxyalkyl group, a benzene ring to which a hydroxyl group of hydroxystyrene is bonded, and an alkyl group having 1 to 5 carbon atoms, And a benzene ring to which 1 to 2 hydroxyl groups are further bonded (in this case, the total number of hydroxyl groups is 2 to 3).
The “structural unit derived from styrene” means a structural unit formed by cleavage of an ethylenic double bond of styrene.
“Styrene” includes styrene and those having a substituent (atom or group other than a hydrogen atom) bonded to the α-position carbon atom of styrene and derivatives thereof (excluding the above-mentioned hydroxystyrene). Let it be a concept. Moreover, what substituted the hydrogen atom of the phenyl group with substituents, such as a C1-C5 alkyl group, etc. shall also be included.
In the hydroxystyrene or styrene, the alkyl group as a substituent at the α-position is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, n -Butyl group, isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like can be mentioned.
Specific examples of the halogenated alkyl group as the substituent at the α-position include groups in which part or all of the hydrogen atoms of the above-mentioned “alkyl group as the substituent at the α-position” are substituted with a halogen atom. It is done. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
Specific examples of the hydroxyalkyl group as a substituent at the α-position include a group in which part or all of the hydrogen atoms of the “alkyl group as the substituent at the α-position” are substituted with a hydroxyl group. 1-5 are preferable and, as for the number of the hydroxyl groups in this hydroxyalkyl group, 1 is the most preferable.

(Structural unit (a4))
The structural unit (a4) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent, and is a non-acid-dissociable aliphatic polycyclic group Is a structural unit including
In the structural unit (a4), examples of the polycyclic group include the same polycyclic groups as exemplified in the case of the structural unit (a1). For ArF excimer laser, KrF excimer Many things conventionally known as what is used for the resin component of resist compositions, such as for lasers (preferably for ArF excimer lasers), can be used.
In particular, at least one selected from a tricyclodecyl group, an adamantyl group, a tetracyclododecyl group, an isobornyl group, and a norbornyl group is preferable in terms of industrial availability. These polycyclic groups may have a linear or branched alkyl group having 1 to 5 carbon atoms as a substituent.
Specific examples of the structural unit (a4) include those represented by the following general formulas (a4-1) to (a4-5).

（式中、Ｒは前記と同じである。）

(In the formula, R is as defined above.)

  When the structural unit (a4) is contained in the component (A1), the structural unit (a4) is preferably contained in an amount of 1 to 30 mol% based on the total of all the structural units constituting the component (A1). 10 to 20 mol% is more preferable.

(Structural unit (a5))
As the structural unit (a5), the following general formula (a5-1) can be used because it has good solubility in organic solvents, has solubility in an alkaline developer, and has excellent etching resistance. The structural unit represented by can be illustrated suitably.

［式中、Ｒ^６０は水素原子又は炭素数１〜５のアルキル基であり；Ｒ^６１はハロゲン原子又は炭素数１〜５のアルキル基であり；ｐは１〜３の整数であり；ｑは０〜４の整数である。］

Wherein R ⁶⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms; R ⁶¹ is a halogen atom or an alkyl group having 1 to 5 carbon atoms; p is an integer of 1 to 3; It is an integer of 0-4. ]

In the formula (a5-1), as the alkyl group having 1 to 5 carbon atoms in R ⁶⁰ , specifically, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group, tert-butyl And linear or branched alkyl groups such as a group, a pentyl group, an isopentyl group, and a neopentyl group. R ⁶⁰ is particularly preferably a hydrogen atom or a methyl group.
p is an integer of 1 to 3, preferably 1.
The bonding position of the hydroxyl group may be any of the o-position, m-position and p-position of the phenyl group. When p is 1, the p-position is preferred because it is readily available and inexpensive. When p is 2 or 3, arbitrary substitution positions can be combined.
q is an integer of 0-2. Among these, q is preferably 0 or 1, and is preferably 0 industrially.
As the alkyl group for R ^61, the same alkyl groups for R ⁶⁰ can be mentioned.
When q is 1, the substitution position of R ⁶¹ may be any of the o-position, the m-position, and the p-position.
When q is 2, arbitrary substitution positions can be combined. At this time, the plurality of R ⁶¹ may be the same or different.

  When the structural unit (a5) is contained in the component (A1), the structural unit (a5) is preferably contained in an amount of 50 to 90 mol% based on the total of all the structural units constituting the component (A1). It is more preferable to make it contain 55-85 mol%, and it is still more preferable to contain 60-80 mol%.

(Structural unit (a6))
As the structural unit (a6), the solubility in an alkali developer can be adjusted, and since the heat resistance and dry etching resistance are improved, the structural unit represented by the following general formula (a6-1) is It can illustrate suitably.

［式中、Ｒ^６０は水素原子又は炭素数１〜５のアルキル基であり；Ｒ^６２はハロゲン原子又は炭素数１〜５のアルキル基であり；ｘは０〜５の整数である。］

[Wherein, R ⁶⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms; R ⁶² is a halogen atom or an alkyl group having 1 to 5 carbon atoms; x is an integer of 0 to 5]. ]

In the general formula ^{(a6-1), R 60} is the same as ^{R 60} in the general formula (a5-1).
In the formula ^(a6-1), the alkyl group of ^{R 62} is the same as the alkyl group of ^{R 61} in general formula (a5-1).
x is an integer of 0 to 3, preferably 0 or 1, and industrially particularly preferably 0.
When x is ^1, the substitution position of ^{R 62} is a phenyl group the o-, m- position may be any of p- position. When x is 2 or 3, any substitution position can be combined. At this time, the plurality of R ⁶² may be the same or different.

  When the structural unit (a6) is contained in the component (A1), the structural unit (a6) is preferably contained in an amount of 10 to 50 mol% based on the total of all the structural units constituting the component (A1). It is more preferable to make it contain 15-45 mol%, and it is still more preferable to contain 20-40 mol%.

In the resist composition of the present invention, the component (A) preferably contains a polymer compound having the structural unit (a1) as the component (A1).
Specifically, the component (A1) is a polymer compound composed of a repeating structure of the structural unit (a1) and the structural unit (a2); a repeating structure of the structural unit (a1), the structural unit (a2) and the structural unit (a3). Examples thereof include a polymer compound comprising a repeating structure of the structural unit (a1), the structural unit (a2), the structural unit (a3), and the structural unit (a4).

The mass average molecular weight (Mw) of the component (A1) (polystyrene conversion standard by gel permeation chromatography (GPC)) is not particularly limited, preferably 1000 to 50000, more preferably 1500 to 30000, and 2000 to 2000 20000 is most preferred. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent to be used as a resist, and if it is above the lower limit of this range, dry etching resistance and resist pattern cross-sectional shape are good.
The dispersity (Mw / Mn) is not particularly limited, but is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and most preferably 1.0 to 2.5. In addition, Mn shows a number average molecular weight.

The component (A1) can be obtained by polymerizing a monomer for deriving each structural unit by a known radical polymerization using a radical polymerization initiator such as azobisisobutyronitrile (AIBN).
Further, for the component (A1), in the polymerization, a chain transfer agent such as HS—CH ₂ —CH ₂ —CH ₂ —C (CF ₃ ) ₂ —OH is used in combination, so that the terminal A —C (CF ₃ ) ₂ —OH group may be introduced into the. As described above, a copolymer introduced with a hydroxyalkyl group in which a part of hydrogen atoms of the alkyl group is substituted with a fluorine atom reduces development defects and LER (line edge roughness: uneven unevenness of line side walls). It is effective in reducing
A commercially available monomer may be used as the monomer for deriving each structural unit, or the monomer may be synthesized using a known method.

In the component (A), as the component (A1), one type may be used alone, or two or more types may be used in combination.
The proportion of the component (A1) in the component (A) is preferably 25% by mass or more, more preferably 50% by mass, further preferably 75% by mass, and 100% by mass with respect to the total mass of the component (A). May be.

The component (A) may contain a base material component (hereinafter referred to as “component (A2)”) whose polarity is increased by the action of an acid other than the component (A1) as long as the effects of the present invention are not impaired. Good.
Examples of the component (A2) include low molecular compounds having a molecular weight of 500 or more and less than 2500 and having an acid dissociable group and a hydrophilic group as exemplified in the description of the component (A1). Specific examples include those in which some or all of the hydrogen atoms of the hydroxyl group of the compound having a plurality of phenol skeletons are substituted with the acid dissociable group.
Examples of the low molecular weight compound include a sensitizer in a non-chemically amplified g-line or i-line resist, and a part of the hydrogen atom of the hydroxyl group of a low molecular weight phenol compound known as a heat resistance improver. Those substituted with a dissociable group are preferred, and any of them can be used arbitrarily.
Examples of the low molecular weight phenol compound include bis (4-hydroxyphenyl) methane, bis (2,3,4-trihydroxyphenyl) methane, 2- (4-hydroxyphenyl) -2- (4′-hydroxyphenyl). ) Propane, 2- (2,3,4-trihydroxyphenyl) -2- (2 ′, 3 ′, 4′-trihydroxyphenyl) propane, tris (4-hydroxyphenyl) methane, bis (4-hydroxy-) 3,5-dimethylphenyl) -2-hydroxyphenylmethane, bis (4-hydroxy-2,5-dimethylphenyl) -2-hydroxyphenylmethane, bis (4-hydroxy-3,5-dimethylphenyl) -3, 4-dihydroxyphenylmethane, bis (4-hydroxy-2,5-dimethylphenyl) -3,4-dihydroxypheny Rumethane, bis (4-hydroxy-3-methylphenyl) -3,4-dihydroxyphenylmethane, bis (3-cyclohexyl-4-hydroxy-6-methylphenyl) -4-hydroxyphenylmethane, bis (3-cyclohexyl- 4-hydroxy-6-methylphenyl) -3,4-dihydroxyphenylmethane, 1- [1- (4-hydroxyphenyl) isopropyl] -4- [1,1-bis (4-hydroxyphenyl) ethyl] benzene, Examples include 2 to 6 nuclei of formalin condensates of phenols such as phenol, m-cresol, p-cresol and xylenol. Of course, it is not limited to these. In particular, a phenol compound having 2 to 6 triphenylmethane skeletons is preferable because of excellent resolution and line edge roughness (LWR). The acid dissociable group is not particularly limited, and examples thereof include those described above.

  In the resist composition of the present invention, the content of the component (A) may be adjusted according to the resist film thickness to be formed.

<(B) component>
(B) component contains the acid generator (B1) (henceforth "(B1) component") consisting of a compound denoted by the following general formula (b1).

［式中、Ｑ^１は２価の連結基又は単結合であり、Ｙ^１は置換基を有してもよい炭素数１〜４のアルキレン基又は置換基を有してもよい炭素数１〜４のフッ素化アルキレン基であり、Ｏは酸素原子であり、Ｘ^３は置換基を有してもよい炭素数３〜３０の環式基であり、Ａ^＋は有機カチオンである。］

[Wherein, Q ¹ is a divalent linking group or a single bond, and Y ¹ is an alkylene group having 1 to 4 carbon atoms which may have a substituent or 1 to 1 carbon atoms which may have a substituent. 4 is a fluorinated alkylene group, O is an oxygen atom, X ³ is an optionally substituted cyclic group having 3 to 30 carbon atoms, and A ⁺ is an organic cation. ]

[Anion part of component (B1)]
In formula (b1), Q ¹ is a divalent linking group or a single bond. The linking group may contain an oxygen atom or an atom other than an oxygen atom. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms.
Examples of the divalent linking group for Q ¹ include an ester bond (—C (═O) —O—), an amide bond (—C (═O) —NH—), and a carbonyl group (—C (═O)). -) Non-hydrocarbon oxygen atom-containing linking groups such as-); combinations of the non-hydrocarbon oxygen atom-containing linking groups and an alkylene group or fluorinated alkylene group which may have a substituent, etc. .

The alkylene group or fluorinated alkylene group is preferably linear or branched. 1-12 are respectively preferable, as for carbon number of this alkylene group or a fluorinated alkylene group, 1-5 are more preferable, 1-4 are more preferable, and 1-3 are especially preferable.
Specific examples of the alkylene group include, for example, a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ) ₂ —, —C (CH _{3 ) (CH 2 CH 3) -} , - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene group _{[-CH 2} CH 2 - _{]; - CH (CH 3)} CH 2 -, - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 - alkyl, such as Alkyl trimethylene such as ethylene group; trimethylene group (n-propylene group) [—CH ₂ CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ CH ₂ —, —CH ₂ CH (CH ₃ ) CH ₂ —, etc. Group; tetramethylene group [—CH ₂ CH ₂ CH ₂ CH ₂ —]; alkyltetramethylene groups such as —CH (CH ₃ ) CH ₂ CH ₂ CH ₂ —, —CH ₂ CH (CH ₃ ) CH ₂ CH ₂ —; pentamethylene group [—CH ₂ CH ₂ CH ₂ CH ₂ CH ₂ —] and the like.
As the fluorinated alkylene group, a part or all of the hydrogen atoms of the alkylene group include been substituted with fluorine atoms, _{specifically, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF ₂ CF ₂ —, —CF (CF ₃ ) CF ₂ —, —CF (CF ₂ CF ₃ ) —, —C (CF ₃ ) ₂ —, —CF ₂ CF ₂ CF ₂ CF ₂ —, —CF (CF _{3) CF 2 CF 2 -,} - CF 2 CF (CF 3) CF 2 -, - CF (CF 3) CF (CF 3) -, - C (CF 3) 2 CF 2 -, - CF (CF 2 CF _{3) CF 2 -, - CF} (CF 2 CF 2 CF 3) -, - C (CF 3) (CF 2 CF 3) -, - CHF -, - CH 2 CF 2 -, - CH 2 CH 2 CF 2 _{-, - CH 2 CF 2 CF} 2 -, - CH (CF 3) CH 2 -, _{CH (CF 2 CF 3) -} , - C (CH 3) (CF 3) -, - CH 2 CH 2 CH 2 CF 2 -, - CH 2 CH 2 CF 2 CF 2 -, - CH (CF 3) CH _{2 CH 2 -, - CH 2} CH (CF 3) CH 2 -, - CH (CF 3) CH (CF 3) -, - C (CF 3) 2 CH 2 - and the like.

Examples of the substituent that the alkylene group or fluorinated alkylene group may have include an alkoxy group having 1 to 4 carbon atoms and a hydroxyl group.
Examples of the divalent linking group comprising a combination of the non-hydrocarbon-based oxygen atom-containing linking group and an optionally substituted alkylene group or fluorinated alkylene group include -R ^9a -O- , -R ^9b -OC (= O)-, -C (= O) -R ^9c- , -R ^9d -OC (= O) -R ^9e- , -R ^9f -O-C ( ═O) —R ^9g —, —C (═O) —O—R ^9h —O—C (═O) —, —C (═O) —O—R ⁹ⁱ —O—C (═O) —R ^9j- and the like.
In each formula, R ^{9a to} R ^9j are each independently an alkylene group or a fluorinated alkylene group which may have a substituent. ^Examples of the alkylene group and fluorinated alkylene group for R ^{9a to} R ^9j include the same groups as those described above. R ^{9a to} R ^9j are each preferably an alkylene group.

In formula (b1), Y ¹ represents an optionally substituted alkylene group having 1 to 4 carbon atoms or an optionally substituted fluorinated alkylene group having 1 to 4 carbon atoms.
Examples of the alkylene group having 1 to 4 carbon atoms of Y ¹ include those similar to those having 1 to 4 carbon atoms among the alkylene groups exemplified in the description of Q ¹ described above. _2— ]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ) ₂ —, —C (CH ₃ ) (CH ₂ CH ₃ ) —, —CH (CH ₂₎ an ethylene group _{[-CH 2 CH 2 -];} ; - CH 2 CH 3) alkyl groups such as - CH (CH 3) CH 2 -, - CH (CH 3) CH (CH 3) -, - C (CH _{3) 2 CH 2 -, -} CH (CH 2 CH 3) CH 2 - alkyl groups such as, trimethylene group (n- propylene _{group) [- CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH _{2 CH 2 -, - CH 2} CH (CH 3) CH 2 - , etc. Alkyl trimethylene group; tetramethylene group _{[-CH 2 CH 2 CH 2 CH} 2 -] alkyl tetramethylene group, etc., such as.
As the fluorinated alkylene group having 1 to 4 carbon atoms Y ^1, groups in which a part or entirely substituted with fluorine atoms of the hydrogen atom of the alkylene group having 1 to 4 carbon atoms of the Y ¹ and the like, straight-chain It is preferably in the form of a chain or a branched chain, and the carbon number thereof is preferably 1 to 3, and more preferably 1 or 2. Specific examples the fluorinated alkylene _{group, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 -, - CF (CF 2 CF 3) _{-, - C (CF 3)} 2 -, - CF 2 CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 CF 2 -, - CF 2 CF (CF 3) CF 2 -, - CF (CF _{3) CF (CF 3) -} , - C (CF 3) 2 CF 2 -, - CF (CF 2 CF 3) CF 2 -, - CF (CF 2 CF 2 CF 3) -, - C (CF 3) (CF ₂ CF ₃ )-;
_{-CHF -, - CH 2 CF 2} -, - CH 2 CH 2 CF 2 -, - CH 2 CF 2 CF 2 -, - CH (CF 3) CH 2 -, - CH (CF 2 CF 3) -, - _{C (CH 3) (CF 3} ) -, - CH 2 CH 2 CH 2 CF 2 -, - CH 2 CH 2 CF 2 CF 2 -, - CH (CF 3) CH 2 CH 2 -, - CH 2 CH ( CF ₃ ) CH ₂ —, —CH (CF ₃ ) CH (CF ₃ ) —, —C (CF ₃ ) ₂ CH ₂ — and the like can be mentioned.

Y ¹ is preferably a fluorinated alkylene group having 1 to 4 carbon atoms, and particularly preferably a fluorinated alkylene group in which the carbon atom bonded to the adjacent sulfur atom is fluorinated. Examples of such fluorinated alkylene _{group, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 -, - CF 2 CF 2 CF 2 CF 2 _{-, - CF (CF 3)} CF 2 CF 2 -, - CF 2 CF (CF 3) CF 2 -, - CF (CF 3) CF (CF 3) -, - C (CF 3) 2 CF 2 -, _{-CF (CF 2 CF 3) CF} 2 -; - CH 2 CF 2 -, - CH 2 CH 2 CF 2 -, - CH 2 CF 2 CF 2 -; - CH 2 CH 2 CH 2 CF 2 -, - CH ₂ CH ₂ CF ₂ CF ₂ —, —CH ₂ CF ₂ CF ₂ CF ₂ — and the like can be mentioned.
Of _{these, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, or _{-CH 2 CF} 2 _CF 2 - is _{preferable, -CF 2 -, - CF 2} CF 2 - or - CF ₂ CF ₂ CF ₂ — is more preferable, and —CF ₂ — is particularly preferable.

The alkylene group or fluorinated alkylene group for Y ¹ may have a substituent.
An alkylene group or a fluorinated alkylene group has a “substituent” means that part or all of the hydrogen atom or fluorine atom in the alkylene group or fluorinated alkylene group is an atom or group other than a hydrogen atom or a fluorine atom. It means that it is replaced with.
Examples of the substituent that the alkylene group or fluorinated alkylene group may have include an alkoxy group having 1 to 4 carbon atoms and a hydroxyl group.

In the formula (b1), ^{X 3} is a cyclic group which may 3-30 carbon atoms have a substituent.
The cyclic group for X ³ may be an alicyclic hydrocarbon group or an aromatic hydrocarbon group, and is preferably an alicyclic hydrocarbon group.
The alicyclic hydrocarbon group for X ³ may be a monocyclic hydrocarbon group or a polycyclic hydrocarbon group, and is preferably a polycyclic hydrocarbon group.
Alicyclic hydrocarbon groups X ^3, that is the number of carbon atoms is 3 to 30, preferably from 5 to 30, more preferably from 5 to 20, more preferably 6 to 15, most preferably 6 to 12 .
The alicyclic hydrocarbon group may be saturated or unsaturated, and is preferably saturated.
Examples of the alicyclic hydrocarbon group include a group obtained by removing one or more hydrogen atoms from a monocycloalkane; and one or more hydrogen atoms from a polycycloalkane such as a bicycloalkane, tricycloalkane, or tetracycloalkane. Excluded groups and the like. More specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane; one or more polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Examples include a group excluding a hydrogen atom.

The alicyclic hydrocarbon group may have a substituent. For example, a part of carbon atoms constituting the alicyclic hydrocarbon group (for example, carbon atoms constituting the ring skeleton) may be substituted with a substituent containing a hetero atom, and the alicyclic hydrocarbon group is constituted. Some or all of the hydrogen atoms may be substituted with a substituent containing a hetero atom.
The hetero atom is not particularly limited as long as it is an atom other than a carbon atom and a hydrogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, an iodine atom, and a bromine atom.
The substituent containing a heteroatom (hereinafter sometimes referred to as a heteroatom-containing substituent) may be composed of only the heteroatom, or may be a group containing a group other than the heteroatom or an atom. Good.

Examples of the heteroatom-containing substituent that may substitute a part of carbon atoms constituting the alicyclic hydrocarbon group include —O—, —C (═O) —O—, and —C (═O). —, —O—C (═O) —O—, —C (═O) —NH—, —NH— (H may be substituted with a substituent such as an alkyl group or an acyl group), —S -, -S (= O) _2- , -S (= O) _2- O- and the like. In the case of -NH-, the substituent (alkyl group, acyl group, etc.) that may substitute for H preferably has 1 to 10 carbon atoms, and more preferably 1 to 8 carbon atoms. Particularly preferably, it has 1 to 5 carbon atoms. These substituents may be contained in the ring skeleton.

Examples of the substituent for substituting part or all of the hydrogen atoms constituting the alicyclic hydrocarbon group include a halogen atom, an alkoxy group, a hydroxyl group, —C (═O) —R ⁸⁰ [R ⁸⁰ is an alkyl group, is there. ], -COOR ⁸¹ [R ⁸¹ is a hydrogen atom or an alkyl group. ^{], - OC (= O)} -R 82 [R 82 is a hydrogen atom or an alkyl group. ], Halogenated alkyl groups, halogenated alkoxy groups, hydroxyalkyl groups, oxo groups (═O), sulfur atoms, sulfonyl groups (SO ₂ ) and the like.
Examples of the halogen atom as the substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an isopropoxy group, an n-butoxy group, or a tert-butoxy group. Most preferred is an ethoxy group.
In —C (═O) —R ⁸⁰ , —COOR ⁸¹ , —OC (═O) —R ⁸² as the substituent, the alkyl group in R ^{80 to} R ⁸² is linear, branched, or cyclic. Any of these may be used, or a combination thereof may be used. The carbon number is preferably 1-30. When the alkyl group is linear or branched, the carbon number is preferably 1-20, more preferably 1-17, still more preferably 1-15, 10 is particularly preferred. Specific examples include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, an n-pentyl group, a hexyl group, a nonyl group, and a decyl group. When the alkyl group is cyclic (when it is a cycloalkyl group), the carbon number is preferably 3 to 30, more preferably 3 to 20, still more preferably 3 to 15, and 4 to 12 carbon atoms. It is particularly preferred that the number of carbon atoms is 5-10. The alkyl group may be monocyclic or polycyclic. Specific examples include groups in which one or more hydrogen atoms have been removed from monocycloalkane, groups in which one or more hydrogen atoms have been removed from polycycloalkanes such as bicycloalkane, tricycloalkane, and tetracycloalkane. . Specific examples of the monocycloalkane include cyclopentane and cyclohexane. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms. As the halogenated alkyl group, a fluorinated alkyl group is particularly preferred.
Examples of the halogenated alkoxy group as the substituent include groups in which some or all of the hydrogen atoms of the alkoxy group have been substituted with the halogen atoms. The halogenated alkoxy group is preferably a fluorinated alkoxy group.
Examples of the hydroxyalkyl group as the substituent include a group in which at least one hydrogen atom of the alkyl group mentioned as the alkyl group as the substituent is substituted with a hydroxyl group. 1-3 are preferable and, as for the number of the hydroxyl groups which a hydroxyalkyl group has, 1 is the most preferable.

When the alicyclic hydrocarbon group does not include a heteroatom-containing substituent in the ring structure, the alicyclic hydrocarbon group is preferably a polycyclic group, and one or more polycycloalkanes are used. A group in which a hydrogen atom is removed is preferred, and a group in which one or more hydrogen atoms are removed from adamantane is most preferred.
When the alicyclic hydrocarbon group includes a heteroatom-containing substituent in the ring structure, the heteroatom-containing substituent includes —O—, —C (═O) —O—, —S—. , —S (═O) ₂ — and —S (═O) ₂ —O— are preferable. Specific examples of such alicyclic hydrocarbon groups include groups represented by the following formulas (L1) to (L6) and (S1) to (S4).

［式中、Ｑ”は炭素数１〜５のアルキレン基、−Ｏ−、−Ｓ−、−Ｏ−Ｒ^９４−または−Ｓ−Ｒ^９５−であり、Ｒ^９４およびＲ^９５はそれぞれ独立に炭素数１〜５のアルキレン基であり、ｍは０または１の整数である。］

[Wherein, Q ″ is an alkylene group having 1 to 5 carbon atoms, —O—, —S—, —O—R ⁹⁴ — or —S—R ⁹⁵ —, wherein R ⁹⁴ and R ⁹⁵ are each independently carbon. An alkylene group of 1 to 5, and m is an integer of 0 or 1.]

Wherein, Q ^", the alkylene group in ^{R 94} and ^{R 95,} include the same alkylene groups ^R 9a ^{to R 9k} mentioned in the description of the ^{Q 1.}
In these alicyclic hydrocarbon groups, a part of hydrogen atoms bonded to carbon atoms constituting the ring structure may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxo group (═O).
As said alkyl group, a C1-C5 alkyl group is preferable, and it is especially preferable that they are a methyl group, an ethyl group, a propyl group, n-butyl group, and a tert- butyl group.
Examples of the alkoxy group and the halogen atom are the same as those exemplified as the substituent for substituting part or all of the hydrogen atoms.

The aromatic hydrocarbon group for X ³ is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon group preferably has 3 to 30 carbon atoms, more preferably 5 to 30, more preferably 5 to 20, still more preferably 6 to 15, and most preferably 6 to 12. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic hydrocarbon group include a hydrogen atom from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, and a phenanthryl group. Aryl groups such as aryl group, benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, 2-naphthylethyl group, etc., from which one is removed. The number of carbon atoms in the alkyl chain in the arylalkyl group is preferably 1 to 4, more preferably 1 to 2, and particularly preferably 1.

The aromatic hydrocarbon group may have a substituent. For example, a part of carbon atoms constituting the aromatic ring of the aromatic hydrocarbon group may be substituted with a hetero atom, and the hydrogen atom bonded to the aromatic ring of the aromatic hydrocarbon group is substituted with the substituent. May be.
Examples of the former include heteroaryl groups in which some of the carbon atoms constituting the ring of the aryl group are substituted with heteroatoms such as oxygen atoms, sulfur atoms, nitrogen atoms, and aromatic hydrocarbons in the arylalkyl groups. Examples include heteroarylalkyl groups in which some of the carbon atoms constituting the ring are substituted with the above heteroatoms.
Examples of the substituent of the aromatic hydrocarbon group in the latter example include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group as a substituent of the aromatic hydrocarbon group is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. preferable.
The alkoxy group as a substituent of the aromatic hydrocarbon group is preferably an alkoxy group having 1 to 5 carbon atoms, and is a methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group, tert- A butoxy group is preferable, and a methoxy group and an ethoxy group are most preferable.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent of the aromatic hydrocarbon group include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

As the anion (X ³ —O—Q ¹ —Y ¹ —SO ₃ ^— ) of the compound represented by the general formula (b1), Q ¹ is a carbonyl group — (C (═O)). A divalent linking group containing-, an alkylene group which may have a substituent, or a fluorinated alkylene group or a single bond is preferred, and a divalent containing carbonyl group-(C (= O))- More preferred are alkylene groups or fluorinated alkylene groups that do not contain a linking group or ester bond.
As the divalent linking group containing a carbonyl group — (C (═O)) —, —R ^9a —O—, —R ^9b —O—C (═O) —, mentioned in the description of Q ¹ above, —C (═O) —R ^9c —, —R ^9d —O—C (═O) —R ^9e —, —R ^9f —O—C (═O) —R ^9g —, —C (═O) Only —O—R ^9h —O—C (═O) —, —C (═O) —O—R ⁹ⁱ —O—C (═O) —R ^9j —, or a carbonyl group is preferred. R ^{9b to} R ^9k are preferably alkylene groups.
As the alkylene group or fluorinated alkylene group which may have a substituent, —R ^9a —O— mentioned in the description of Q ¹ is preferable. R ^9a is preferably an alkylene group.

A more preferable example of the anion in which Q ¹ is a divalent linking group containing a carbonyl group — (C (═O)) — includes an anion represented by the following general formula (11a).

［式（１１）中、Ｘ^１０は置換基を有していてもよい炭素数３〜３０の脂環式炭化水素基であり、ｐは１〜４の整数である。］

Wherein ^{(11), X 10} is an alicyclic hydrocarbon group which may 3-30 carbon atoms which may have a substituent, p is an integer of 1 to 4. ]

In formula (11), X ¹⁰ is the same as X ³ in formula (b1).
X ¹⁰ is preferably an aliphatic cyclic group containing a heteroatom-containing substituent in the ring structure.
p is an integer of 1-4, the integer of 1-3 is preferable and 1 or 2 is more preferable.

As a preferable example of the anion in which Q ¹ in the general formula (b1) is an alkylene group, a fluorinated alkylene group or a single bond which may have a substituent, an anion represented by the following general formula (11b) Is mentioned.

［式（１１ｂ）中、Ｘ^１０およびｐはそれぞれ前記と同じであり、Ｑ^１２は単結合又はアルキレン基である。］

[In Formula (11b), X ¹⁰ and p are the same as defined above, and Q ¹² is a single bond or an alkylene group. ]

In the formula (11b), X ¹⁰ and p are the same as X ¹⁰ , Q ¹² and p in the formula (11), respectively.
As the alkylene group for Q ^12, the same alkylene groups as those described above for R ^{9a to} R ^9k in Q ¹ can be used.
Q ¹² is particularly preferably a single bond or a methylene group, and most preferably a single bond.

  Preferable examples of the anions represented by the general formulas (11a) to (11b) include anions represented by the following general formulas (b1-a1) to (b1-a5).

［式中、ｙは１〜３の整数であり、ｔ３は１〜３の整数であり、ｒ１〜ｒ２はそれぞれ独立に０〜３の整数であり、Ｒ^５０は置換基であり、ｍ１〜ｍ４はそれぞれ独立に０または１であり、ｗ１〜ｗ４はそれぞれ独立に０〜３の整数であり、Ｑ”は前記と同じである。］

Wherein, y is an integer of 1 to 3, t3 represents an integer of 1 to 3, r1 and r2 are each independently an integer of 0 to ^{3, R 50} is a substituent, m1 to m4 Are each independently 0 or 1, w1 to w4 are each independently an integer of 0 to 3, and Q ″ is the same as above.]

Examples of the substituent for R ⁵⁰ include the same substituents as those described as the substituent for substituting part or all of the hydrogen atoms of the alicyclic hydrocarbon group in the description of X ³ .
Code (r1 and r2, w1 to w4) attached to R ⁵⁰ when it is 2 or more integer, a plurality of ^{R 50} in the compound may be the same, respectively, it may be different.

[Cation part of component (B1)]
In the formula (b1), A ⁺ is an organic cation.
A ⁺ is not particularly limited, and any one that has been proposed as a cation part of an acid generator for a chemically amplified resist can be used.
As a suitable cation part, the cation part of onium salt type acid generators, such as an iodonium salt and a sulfonium salt, is mentioned, for example. Examples of the cation moiety include cations represented by the following general formula (b-c1) or (b-c2). Among these, a cation represented by the formula (b-c1) is preferable.

［式中、Ｒ^１”〜Ｒ^３”はそれぞれ独立に置換基を有していてもよいアリール基、アルキル基又はアルケニル基を表す。Ｒ^１”〜Ｒ^３”のうち、いずれか二つが相互に結合して式中のイオウ原子と共に環を形成してもよい。Ｒ^５”〜Ｒ^６”はそれぞれ独立に置換基を有していてもよいアリール基、アルキル基又はアルケニル基を表す。］

[Wherein, R ¹ ″ to R ³ ″ each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent. Any two of R ¹ ″ to R ³ ″ may be bonded to each other to form a ring together with the sulfur atom in the formula. R ⁵ ″ to R ⁶ ″ each independently represents an aryl group, alkyl group or alkenyl group which may have a substituent. ]

In formula (b-c1), R ¹ ″ to R ³ ″ each independently represents an aryl group, alkyl group or alkenyl group which may have a substituent. Any two of R ¹ ″ to R ³ ″ may be bonded to each other to form a ring together with the sulfur atom in the formula.
Examples of the aryl group for R ¹ ″ to R ³ ″ include an unsubstituted aryl group having 6 to 20 carbon atoms; a substituted aryl group in which part or all of the hydrogen atoms of the unsubstituted aryl group are substituted with a substituent, and the like Is mentioned.
In R ¹ ″ to R ³ ″, the unsubstituted aryl group is preferably an aryl group having 6 to 10 carbon atoms because it can be synthesized at a low cost. Specific examples include a phenyl group and a naphthyl group.
Examples of the substituent in the substituted aryl group of R ¹ ″ to R ³ ″ include an alkyl group, an alkoxy group, a halogen atom, a hydroxyl group, an oxo group (═O), an aryl group, an alkoxyalkyloxy group, an alkoxycarbonylalkyloxy group, — C (═O) —O—R ⁶ ′, —O—C (═O) —R ⁷ ′, —O—R ⁸ ′ and the like can be mentioned.
The alkyl group as a substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
As the alkoxy group as a substituent in the substituted aryl group, an alkoxy group having 1 to 5 carbon atoms is preferable, and a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group. Most preferably it is.
The halogen atom as a substituent in the substituted aryl group is preferably a fluorine atom.
Examples of the aryl group as a substituent in the substituted aryl group include the same aryl groups as those described above for R ¹ ″ to R ³ ″, preferably an aryl group having 6 to 20 carbon atoms, and an aryl group having 6 to 10 carbon atoms. Group is more preferable, and phenyl group and naphthyl group are more preferable.

As the alkoxyalkyloxy group in the substituted aryl group, for example,
General formula: -O-C ( ^R47 ) ( ^R48 ) -O- ^R49
[Wherein, R ⁴⁷ and R ⁴⁸ each independently represent a hydrogen atom or a linear or branched alkyl group, and R ⁴⁹ represents an alkyl group. ] Is represented.
In R ⁴⁷ and R ⁴⁸ , the alkyl group preferably has 1 to 5 carbon atoms, may be linear or branched, and is preferably an ethyl group or a methyl group, and most preferably a methyl group.
At least one of R ⁴⁷ and R ⁴⁸ is preferably a hydrogen atom. In particular, it is more preferable that one is a hydrogen atom and the other is a hydrogen atom or a methyl group.
The alkyl group for R ⁴⁹ preferably has 1 to 15 carbon atoms and may be linear, branched or cyclic.
The linear or branched alkyl group for R ⁴⁹ preferably has 1 to 5 carbon atoms, and examples thereof include a methyl group, an ethyl group, a propyl group, an n-butyl group, and a tert-butyl group. Can be mentioned.
The cyclic alkyl group for R ⁴⁹ preferably has 4 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, monocycloalkane, bicycloalkane, tricycloalkane, tetracycloalkane, etc., which may or may not be substituted with an alkyl group having 1 to 5 carbon atoms, a fluorine atom or a fluorinated alkyl group, etc. And a group obtained by removing one or more hydrogen atoms from the polycycloalkane. Examples of the monocycloalkane include cyclopentane and cyclohexane. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.

As the alkoxycarbonylalkyloxy group in the substituted aryl group, for example,
General formula: —O—R ⁵⁵ —C (═O) —O—R ⁵⁶
[Wherein, R ⁵⁵ represents a linear or branched alkylene group, and R ⁵⁶ represents a tertiary alkyl group. ] Is represented.
The linear or branched alkylene group for R ⁵⁵ preferably has 1 to 5 carbon atoms, such as a methylene group, an ethylene group, a trimethylene group, a tetramethylene group, or a 1,1-dimethylethylene group. Etc.
As the tertiary alkyl group for R ⁵⁶ , 2-methyl-2-adamantyl group, 2-ethyl-2-adamantyl group, 1-methyl-1-cyclopentyl group, 1-ethyl-1-cyclopentyl group, 1-methyl -1-cyclohexyl group, 1-ethyl-1-cyclohexyl group, 1- (1-adamantyl) -1-methylethyl group, 1- (1-adamantyl) -1-methylpropyl group, 1- (1-adamantyl) -1-methylbutyl group, 1- (1-adamantyl) -1-methylpentyl group; 1- (1-cyclopentyl) -1-methylethyl group, 1- (1-cyclopentyl) -1-methylpropyl group, 1- (1-cyclopentyl) -1-methylbutyl group, 1- (1-cyclopentyl) -1-methylpentyl group; 1- (1-cyclohexyl) -1-methylethyl Group, 1- (1-cyclohexyl) -1-methylpropyl group, 1- (1-cyclohexyl) -1-methylbutyl group, 1- (1-cyclohexyl) -1-methylpentyl group, tert-butyl group, tert -Pentyl group, tert-hexyl group and the like.
Moreover, the general ^formula: the ^{R 56} in the -O-R 55 -C (= O ) -O-R 56, also include groups replaced by ^{R 56} '. R ⁵⁶ ′ is a hydrogen atom, an alkyl group, a fluorinated alkyl group, or an aliphatic cyclic group that may contain a hetero atom.
^Examples of the alkyl group for R ⁵⁶ ′ include the same alkyl groups as those described above for R ⁴⁹ .
^Examples of the fluorinated alkyl group for R ⁵⁶ ′ include groups in which some or all of the hydrogen atoms within the alkyl group for R ⁴⁹ have been substituted with fluorine atoms.
Examples of the aliphatic cyclic group which may contain a hetero atom in R ⁵⁶ ′ include an aliphatic cyclic group containing no hetero atom, an aliphatic cyclic group containing a hetero atom in the ring structure, and an aliphatic cyclic group. Examples include those in which a hydrogen atom in the group is substituted with a heteroatom.
Regarding R ⁵⁶ ′, the aliphatic cyclic group containing no hetero atom includes a group obtained by removing one or more hydrogen atoms from a polycycloalkane such as monocycloalkane, bicycloalkane, tricycloalkane, tetracycloalkane, and the like. Can be mentioned. Examples of the monocycloalkane include cyclopentane and cyclohexane. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.
Specific examples of the aliphatic cyclic group containing a hetero atom in the ring structure for R ⁵⁶ ′ include groups represented by the aforementioned formulas (L1) to (L6) and (S1) to (S4). It is done.
As for R ⁵⁶ ′, the hydrogen atom in the aliphatic cyclic group is specifically substituted with a hetero atom, specifically, the hydrogen atom in the aliphatic cyclic group is substituted with an oxygen atom (═O), etc. Is mentioned.

^{-C (= O) -O-R} 6 ', -O-C (= O) -R 7', 'R 6 ^{in' -O-R 8, R 7} ', R 8' are each carbon atoms 1 to 25 linear, branched or cyclic saturated hydrocarbon group having 3 to 20 carbon atoms, or a linear or branched aliphatic unsaturated hydrocarbon group having 2 to 5 carbon atoms. .
The linear or branched saturated hydrocarbon group has 1 to 25 carbon atoms, preferably 1 to 15 carbon atoms, and more preferably 4 to 10 carbon atoms.
Examples of the linear saturated hydrocarbon group include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, and a decyl group.
Examples of the branched saturated hydrocarbon group excluding the tertiary alkyl group include, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3 -Methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like can be mentioned.
The linear or branched saturated hydrocarbon group may have a substituent. Examples of the substituent include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O), a cyano group, and a carboxy group.
As the alkoxy group as a substituent of the linear or branched saturated hydrocarbon group, an alkoxy group having 1 to 5 carbon atoms is preferable, and a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, An n-butoxy group and a tert-butoxy group are preferable, and a methoxy group and an ethoxy group are most preferable.
Examples of the halogen atom as a substituent of the linear or branched saturated hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
As the halogenated alkyl group as a substituent of the linear or branched saturated hydrocarbon group, part or all of the hydrogen atoms of the linear or branched saturated hydrocarbon group are the halogen atoms. And a group substituted with.
The cyclic saturated hydrocarbon group having 3 to 20 carbon atoms in R ⁶ ′, R ⁷ ′, and R ⁸ ′ may be either a polycyclic group or a monocyclic group. A group in which one hydrogen atom has been removed from a polycycloalkane such as bicycloalkane, tricycloalkane, tetracycloalkane, and the like. More specifically, one hydrogen atom was removed from a monocycloalkane such as cyclopentane, cyclohexane, cycloheptane, and cyclooctane, and a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Group and the like.
The cyclic saturated hydrocarbon group may have a substituent. For example, part of the carbon atoms constituting the ring of the cyclic alkyl group may be substituted with a heteroatom, or the hydrogen atom bonded to the ring of the cyclic alkyl group may be substituted with a substituent. Good.
Examples of the former include one or more hydrogen atoms from a heterocycloalkane in which a part of the carbon atoms constituting the ring of the monocycloalkane or polycycloalkane is substituted with a heteroatom such as an oxygen atom, a sulfur atom, or a nitrogen atom. Examples include groups other than atoms. The ring structure may have an ester bond (—C (═O) —O—). Specifically, a lactone-containing monocyclic group such as a group obtained by removing one hydrogen atom from γ-butyrolactone, or a group obtained by removing one hydrogen atom from a bicycloalkane, tricycloalkane, or tetracycloalkane having a lactone ring. And other lactone-containing polycyclic groups.
Examples of the substituent in the latter example include the same as those described above as the substituent that the linear or branched saturated hydrocarbon group may have, a lower alkyl group, and the like.
R ⁶ ′, R ⁷ ′, and R ⁸ ′ may be a combination of a linear or branched alkyl group and a cyclic alkyl group.
A combination of a linear or branched alkyl group and a cyclic alkyl group includes a group in which a cyclic alkyl group is bonded as a substituent to a linear or branched alkyl group, and a substituent to the cyclic alkyl group. And a group having a linear or branched alkyl group bonded thereto.
Examples of the linear aliphatic unsaturated hydrocarbon group for R ⁶ ′, R ⁷ ′, and R ⁸ ′ include a vinyl group, a propenyl group (allyl group), and a butynyl group.
Examples of the branched aliphatic unsaturated hydrocarbon group for R ⁶ ′, R ⁷ ′, and R ⁸ ′ include a 1-methylpropenyl group and a 2-methylpropenyl group.
The linear or branched aliphatic unsaturated hydrocarbon group may have a substituent. Examples of the substituent include the same as those mentioned as the substituent that the linear or branched saturated hydrocarbon group may have.
Among R ⁷ ′ and R ⁸ ′, among them, the lithography characteristics and the resist pattern shape are good, so that the linear or branched saturated hydrocarbon group having 1 to 15 carbon atoms, or the carbon number 3-20 cyclic saturated hydrocarbon groups are preferred.

The aryl groups for R ¹ ″ to R ³ ″ are each preferably a phenyl group or a naphthyl group.

Examples of the alkyl group for R ¹ ″ to R ³ ″ include an unsubstituted alkyl group, a substituted alkyl group in which part or all of the hydrogen atoms of the unsubstituted alkyl group are substituted with a substituent, and the like.
The unsubstituted alkyl group may be linear, branched or cyclic, or a combination thereof. The carbon number is preferably 1-30.
When the alkyl group is linear or branched, the carbon number thereof is preferably 1-20, more preferably 1-15, still more preferably 1-10, and particularly preferably 1-5. Specific examples include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, an n-pentyl group, a hexyl group, a nonyl group, and a decyl group. Among these, a methyl group is particularly preferable because it is excellent in resolution and can be synthesized at low cost.
When the alkyl group is cyclic, the carbon number is preferably 3 to 30, more preferably 3 to 20, still more preferably 3 to 15, and particularly preferably 4 to 12 carbon atoms. Numbers 5 to 10 are most preferable. The alkyl group may be monocyclic or polycyclic. Specific examples include groups in which one or more hydrogen atoms have been removed from monocycloalkane, groups in which one or more hydrogen atoms have been removed from polycycloalkanes such as bicycloalkane, tricycloalkane, and tetracycloalkane. . Specific examples of the monocycloalkane include cyclopentane and cyclohexane. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane.
Examples of the substituent that the substituted alkyl group has are the same as those described as the substituent that the substituted aryl group has.

Examples of the alkenyl group for R ¹ ″ to R ³ ″ include an unsubstituted alkenyl group and a substituted alkenyl group in which part or all of the hydrogen atoms of the unsubstituted alkenyl group are substituted with a substituent.
The unsubstituted alkenyl group may be linear, branched or cyclic, or a combination thereof. The carbon number is preferably 2 to 10, more preferably 2 to 5, and still more preferably 2 to 4. Specific examples include a vinyl group, a propenyl group (allyl group), a butynyl group, a 1-methylpropenyl group, and a 2-methylpropenyl group.
Examples of the substituent that the substituted alkenyl group has are the same as those described as the substituent that the substituted aryl group has.

Any two of R ¹ ″ to R ³ ″ may be bonded to each other to form a ring together with the sulfur atom in the formula. The ring may be monocyclic or polycyclic.
The ring may be an aromatic ring or an aliphatic ring. The aliphatic ring may be a saturated aliphatic ring or an unsaturated aliphatic ring.
When two of R ¹ ″ to R ³ ″ are combined to form a ring, one ring containing a sulfur atom in the ring skeleton in the formula is a 3 to 10 membered ring including the sulfur atom. Of these, a 5- to 7-membered ring is particularly preferable.
The ring may have a hetero atom other than the sulfur atom to which R ¹ ″ to R ³ ″ are bonded as an atom constituting the ring skeleton. Examples of the hetero atom include a sulfur atom, an oxygen atom, and a nitrogen atom.
Specific examples of the ring formed include, for example, thiophene ring, thiazole ring, benzothiophene ring, thianthrene ring, benzothiophene ring, dibenzothiophene ring, 9H-thioxanthene ring, thioxanthone ring, thianthrene ring, phenoxathiin ring, tetrahydro A thiophenium ring, a tetrahydrothiopyranium ring, etc. are mentioned.

  Specific examples of the cation moiety represented by the formula (b-c1) include, for example, triphenylsulfonium, (3,5-dimethylphenyl) diphenylsulfonium, (4- (2-adamantoxymethyloxy) -3, 5-dimethylphenyl) diphenylsulfonium, (4- (2-adamantoxymethyloxy) phenyl) diphenylsulfonium, (4- (tert-butoxycarbonylmethyloxy) phenyl) diphenylsulfonium, (4- (tert-butoxycarbonylmethyloxy) ) -3,5-dimethylphenyl) diphenylsulfonium, (4- (2-methyl-2-adamantyloxycarbonylmethyloxy) phenyl) diphenylsulfonium, (4- (2-methyl-2-adamantyloxycarbonylmethyloxy)- 3 5-dimethylphenyl) diphenylsulfonium, tri (4-methylphenyl) sulfonium, dimethyl (4-hydroxynaphthyl) sulfonium, monophenyldimethylsulfonium, diphenylmonomethylsulfonium, (4-methylphenyl) diphenylsulfonium, (4-methoxyphenyl) Diphenylsulfonium, tri (4-tert-butyl) phenylsulfonium, diphenyl (1- (4-methoxy) naphthyl) sulfonium, di (1-naphthyl) phenylsulfonium, 1-phenyltetrahydrothiophenium, 1- (4-methyl Phenyl) tetrahydrothiophenium, 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiophenium, 1- (4-methoxynaphthalen-1-yl) tetrahydro Ofenium, 1- (4-ethoxynaphthalen-1-yl) tetrahydrothiophenium, 1- (4-n-butoxynaphthalen-1-yl) tetrahydrothiophenium, 1-phenyltetrahydrothiopyranium, 1- (4 -Hydroxyphenyl) tetrahydrothiopyranium, 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiopyranium, 1- (4-methylphenyl) tetrahydrothiopyranium and the like.

  Specific examples of suitable cations represented by the formula (b-c1) include cations represented by the following formulas (b-c1-1) to (b-c1-33).

［式中、ｇ１〜ｇ３はそれぞれ繰返し数を示し、ｇ１は１〜５の整数であり、ｇ２は０〜２０の整数であり、ｇ３は０〜２０の整数である。］

[Wherein, g1 to g3 each represent a number of repetitions, g1 is an integer of 1 to 5, g2 is an integer of 0 to 20, and g3 is an integer of 0 to 20. ]

In the cation represented by the formula (b-c1), any two of R ¹ ″ to R ³ ″ are bonded to each other to form a ring together with the sulfur atom in the formula. Specific examples include cations represented by the following formulas (b-c12) to (b-c15).

［式中、Ｒ^８１〜Ｒ^８６はそれぞれ独立してアルキル基、アセチル基、アルコキシ基、カルボキシ基、水酸基またはヒドロキシアルキル基であり；ｎ_１〜ｎ_５はそれぞれ独立して０〜３の整数であり、ｎ_６は０〜２の整数である。］

[Wherein R ^{81 to} R ⁸⁶ are each independently an alkyl group, acetyl group, alkoxy group, carboxy group, hydroxyl group or hydroxyalkyl group; n _{1 to} n ₅ are each independently an integer of 0 to 3; There, _{n 6} is an integer of 0-2. ]

［式中、Ｒ^９、Ｒ^１０は、それぞれ独立に、置換基を有していてもよいフェニル基、ナフチル基または炭素数１〜５のアルキル基、アルコキシ基、水酸基であり、Ｒ^４’は炭素数１〜５のアルキレン基であり、ｕは１〜３の整数である。］

[Wherein R ⁹ and R ¹⁰ are each independently a phenyl group, a naphthyl group, or an alkyl group having 1 to 5 carbon atoms, an alkoxy group, or a hydroxyl group, which may have a substituent, and R ⁴ ′ is It is a C1-C5 alkylene group, u is an integer of 1-3. ]

In formulas (b-c12) to (b-c13), the alkyl group in R ^{81 to} R ⁸⁶ is preferably an alkyl group having 1 to 5 carbon atoms, more preferably a linear or branched alkyl group, A methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, or a tert-butyl group is particularly preferable.
The alkoxy group is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a linear or branched alkoxy group, and particularly preferably a methoxy group or an ethoxy group.
The hydroxyalkyl group is preferably a group in which one or more hydrogen atoms in the alkyl group are substituted with a hydroxy group, and examples thereof include a hydroxymethyl group, a hydroxyethyl group, and a hydroxypropyl group.
When the symbols n _{1 to} n ₆ attached to R ^{81 to} R ⁸⁶ are integers of 2 or more, the plurality of R ^{81 to} R ⁸⁶ may be the same or different.
n ₁ is preferably 0 to 2, more preferably 0 or 1, and still more preferably 0.
n ₂ and n ₃ are preferably each independently 0 or 1, more preferably 0.
n ₄ is preferably 0 to 2, more preferably 0 or 1.
n ₅ is preferably 0 or 1, more preferably 0.
n ₆ is preferably 0 or 1, more preferably 1.

  Preferable examples of the cation represented by the formula (b-c12) or (b-c13) include those shown below.

In formulas (b-c14) to (b-c15), R ⁹ and R ¹⁰ are each independently a phenyl group, a naphthyl group, an alkyl group having 1 to 5 carbon atoms, an alkoxy group which may have a substituent. Group, hydroxyl group. Examples of the substituent include a substituent in the substituted aryl group exemplified in the description of the aryl group of R ¹ ″ to R ³ ″ (an alkyl group, an alkoxy group, an alkoxyalkyloxy group, an alkoxycarbonylalkyloxy group, a halogen atom). Atom, hydroxyl group, oxo group (═O), aryl group, —C (═O) —O—R ⁶ ′, —O—C (═O) —R ⁷ ′, —O—R ⁸ ′, the above general formula ^{: -O-R 55 -C (=} O) based on ^{R 56} is replaced by ^{R 56} 'in the ^{-O-R 56,} etc.) to be similar.
R ⁴ ′ is an alkylene group having 1 to 5 carbon atoms.
u is an integer of 1 to 3, and 1 or 2 is most preferable.
Preferable examples of the cation represented by the formula (b-c14) or (b-c15) include those shown below.
In the following formulae, R ^C represents a substituent (alkyl group, alkoxy group, alkoxyalkyloxy group, alkoxycarbonylalkyloxy group, halogen atom, hydroxyl group, oxo group (═O) exemplified in the description of the substituted aryl group. ), An aryl group, —C (═O) —O—R ⁶ ′, —O—C (═O) —R ⁷ ′, —O—R ⁸ ′).

In the formula (b-c2), R ⁵ ″ to R ⁶ ″ each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent.
As the aryl group for R ⁵ ″ to R ⁶ ″, the same as the aryl groups for R ¹ ″ to R ³ ″ can be used.
Examples of the alkyl group for R ⁵ ″ to R ⁶ ″ include the same as the alkyl group for R ¹ ″ to R ³ ″.
Examples of the alkenyl group for R ⁵ ″ to R ⁶ ″ include the same alkenyl groups for R ¹ ″ to R ³ ″.
Since the lithography properties and resist pattern shape is further improved, it among the R 5 ^{"~R 6",} it is preferable that at least one is an aryl group, are both aryl group R 5 ^{"~R 6"} Is more preferable.
Among these, it is most preferable that all of R ⁵ ″ to R ⁶ ″ are phenyl groups.
Specific examples of the cation represented by the formula (b-c2) include diphenyliodonium and bis (4-tert-butylphenyl) iodonium.

As the component (B1), one type may be used alone, or two or more types may be used in combination.
The proportion of the component (B1) in the component (B) is preferably 50% by mass or more, more preferably 70 to 100% by mass, still more preferably 80 to 100% by mass, based on the total mass of the component (B). It may be mass%.
Moreover, 5-25 mass parts is preferable with respect to 100 mass parts of (A) component, as for content of (B1) component, 10-20 mass parts is more preferable, and 10-15 mass parts is further more preferable.
By setting the ratio of the component (B1) within the above range, the exposure margin (EL margin) is increased and the LWR is reduced, and the lithography characteristics are further improved. Moreover, since pattern formation is fully performed, it is preferable.

The resist composition of the present invention is an acid generator (B2) that does not fall under the component (B1) and generates an acid upon exposure (hereinafter referred to as “component (B2)”), as long as the effects of the present invention are not impaired. May be contained).
The component (B2) is not particularly limited, and those that have been proposed as acid generators for chemically amplified resists can be used. Examples of such acid generators include onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators, bisalkyl or bisarylsulfonyldiazomethanes, and poly (bissulfonyl) diazomethanes. There are various known diazomethane acid generators, nitrobenzyl sulfonate acid generators, imino sulfonate acid generators, disulfone acid generators, and the like.

  As the onium salt acid generator in the component (B2), for example, a compound represented by the following general formula (b-1) or (b-2) can be used.

［式中、Ｒ^１”〜Ｒ^３”はそれぞれ独立に置換基を有していてもよいアリール基、アルキル基又はアルケニル基を表し、Ｒ^１”〜Ｒ^３”のうちのいずれか二つが相互に結合して式中のイオウ原子と共に環を形成してもよい。Ｒ^５”〜Ｒ^６”はそれぞれ独立に置換基を有していてもよいアリール基、アルキル基又はアルケニル基を表す。Ｒ^４”は、置換基を有していてもよいアルキル基、ハロゲン化アルキル基、アリール基、またはアルケニル基を表す。］

[Wherein, R ¹ ″ to R ³ ″ each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent, and any two of R ¹ ″ to R ³ ″ are mutually To form a ring together with the sulfur atom in the formula. R ⁵ ″ to R ⁶ ″ each independently represents an aryl group, alkyl group or alkenyl group which may have a substituent. R ⁴ ″ represents an alkyl group, a halogenated alkyl group, an aryl group, or an alkenyl group which may have a substituent.

^R 1 ^{"~R 3"} in formula (b-1) is the same as that of (B1) ^R 1 in the general mentioned components described formula ^{(b-c1) "~R 3} ".
Formula (b-2) ^R 5 in ", ^{R 6",} the (B1) ^R 5 in the general formula mentioned in component description ^{(b-c2) ", R} 6" is similar to.
R ⁴ ″ represents an alkyl group, a halogenated alkyl group, an aryl group, or an alkenyl group which may have a substituent.
The alkyl group for R ⁴ ″ may be linear, branched or cyclic.
The linear or branched alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms.
The cyclic alkyl group preferably has 4 to 15 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms.
Examples of the halogenated alkyl group for R ⁴ ″ include groups in which part or all of the hydrogen atoms of the aforementioned “linear, branched or cyclic alkyl group” have been substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
In the halogenated alkyl group, the ratio of the number of halogen atoms to the total number of halogen atoms and hydrogen atoms contained in the halogenated alkyl group (halogenation rate (%)) is preferably 10 to 100%. 50 to 100% is preferable, and 100% is most preferable. The higher the halogenation rate, the better the acid strength.
The aryl group for R ⁴ ″ is preferably an aryl group having 6 to 20 carbon atoms.
The alkenyl group in R ⁴ ″ is preferably an alkenyl group having 2 to 10 carbon atoms.
In the above R ⁴ ″, “may have a substituent” means that a part or all of the hydrogen atoms in the alkyl group, halogenated alkyl group, aryl group, or alkenyl group are a substituent (hydrogen atom). It may be substituted with other atoms or groups).
Examples of the substituent include a halogen atom, a hetero atom, and an alkyl group. Examples of the halogen atom and alkyl group include the same as those described as the halogen atom and alkyl group in the halogenated alkyl group in R ⁴ ″. Examples of the hetero atom include an oxygen atom, a nitrogen atom, and a sulfur atom. Etc.
The number of substituents in R ⁴ ″ may be one, or two or more.

  Specific examples of the onium salt acid generator represented by the formula (b-1) or (b-2) include diphenyliodonium trifluoromethanesulfonate or nonafluorobutanesulfonate, bis (4-tert-butylphenyl) iodonium. Trifluoromethane sulfonate or nonafluorobutane sulfonate, triphenylsulfonium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate, tri (4-methylphenyl) sulfonium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its Nonafluorobutanesulfonate, dimethyl (4-hydroxynaphthyl) sulfonium trifluoromethanesulfonate, and its hepta Fluoropropanesulfonate or its nonafluorobutanesulfonate, trifluoromethanesulfonate of monophenyldimethylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; trifluoromethanesulfonate of diphenylmonomethylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutane Sulfonate, trifluoromethanesulfonate of (4-methylphenyl) diphenylsulfonium, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate, trifluoromethane sulfonate of (4-methoxyphenyl) diphenylsulfonium, its heptafluoropropane sulfonate or its nonafluorobutane Sulfonate, tri (4-tert-butyl) phenylsulfonium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutanesulfonate, diphenyl (1- (4-methoxy) naphthyl) sulfonium trifluoromethanesulfonate, its heptafluoropropane Sulfonate or its nonafluorobutane sulfonate, di (1-naphthyl) phenyl sulphonium trifluoromethane sulphonate, its heptafluoropropane sulphonate or its nonafluorobutane sulphonate; 1-phenyltetrahydrothiophenium trifluoromethane sulphonate, its heptafluoropropane sulphonate Or nonafluorobutanesulfonate thereof; 1- (4-methylphenol Nyl) tetrahydrothiophenium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiophenium trifluoromethane sulfonate, its heptafluoropropane Sulfonate or its nonafluorobutane sulfonate; 1- (4-methoxynaphthalen-1-yl) tetrahydrothiophenium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (4-ethoxynaphthalene-1 -Yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nona 1- (4-n-butoxynaphthalen-1-yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutanesulfonate; 1-phenyltetrahydrothiopyranium trifluoromethane Sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (4-hydroxyphenyl) tetrahydrothiopyranium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (3,5- Dimethyl-4-hydroxyphenyl) tetrahydrothiopyranium trifluoromethanesulfonate, its heptafluoropropan Sulfonate or nonafluorobutane sulfonate; 1- (4-methylphenyl) trifluoromethanesulfonate tetrahydrothiophenium Pila chloride, heptafluoropropane sulfonate or its nonafluorobutane sulfonate, and the like.

  In addition, the anion portion of these onium salts may be substituted with alkyl sulfonates such as methane sulfonate, n-propane sulfonate, n-butane sulfonate, n-octane sulfonate, 1-adamantane sulfonate, and 2-norbornane sulfonate; d-camphor-10-sulfonate Substituted alkyl sulfonates such as benzene salts, onium salts substituted with aromatic sulfonates such as perfluorobenzene sulfonate and p-toluene sulfonate can also be used.

As the onium salt-based acid generator, in the general formula (b-1) or (b-2), the anion moiety ^(R 4 "SO ₃ ^-) of the following general formula (b-3) or (b- An onium salt acid generator substituted with the anion represented by 4) can also be used (the cation moiety is the same as the cation moiety in the formula (b-1) or (b-2)).

［式中、Ｘ”は、少なくとも１つの水素原子がフッ素原子で置換された炭素数２〜６のアルキレン基を表し；Ｙ”、Ｚ”は、それぞれ独立に、少なくとも１つの水素原子がフッ素原子で置換された炭素数１〜１０のアルキル基を表す。］

[Wherein X ″ represents an alkylene group having 2 to 6 carbon atoms in which at least one hydrogen atom is substituted with a fluorine atom; Y ″ and Z ″ each independently represent at least one hydrogen atom as a fluorine atom; Represents an alkyl group having 1 to 10 carbon atoms and substituted with

X ″ is a linear or branched alkylene group in which at least one hydrogen atom is substituted with a fluorine atom, and the alkylene group has 2 to 6 carbon atoms, preferably 3 to 5 carbon atoms, Most preferably, it has 3 carbon atoms.
Y ″ and Z ″ are each independently a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and the alkyl group has 1 to 10 carbon atoms, preferably Has 1 to 7 carbon atoms, more preferably 1 to 3 carbon atoms.
The carbon number of the alkylene group of X ″ or the carbon number of the alkyl group of Y ″ and Z ″ is preferably as small as possible because the solubility in the resist solvent is good within the above carbon number range.
In addition, in the alkylene group of X ″ or the alkyl group of Y ″ and Z ″, as the number of hydrogen atoms substituted with fluorine atoms increases, the strength of the acid increases, and high-energy light or electron beam of 200 nm or less This is preferable because the transparency to the surface is improved.
The proportion of fluorine atoms in the alkylene group or alkyl group, that is, the fluorination rate is preferably 70 to 100%, more preferably 90 to 100%, and most preferably all hydrogen atoms are substituted with fluorine atoms. A perfluoroalkylene group or a perfluoroalkyl group.

As the onium salt-based acid generator, in the general formula (b-1) or (b-2), anion ^{- a, R a -COO (R 4 "} SO 3) - [ wherein, ^{R a} Is an alkyl group or a fluorinated alkyl group.] An onium salt-based acid generator substituted with a cation moiety can also be used (the cation moiety is the same as the cation moiety in the formula (b-1) or (b-2)).
In the above formula, examples of R ^a include the same alkyl groups or halogenated alkyl groups as those described above for R ⁴ ″ (when the halogen atom is a fluorine atom).
Specific examples of the “R ^a —COO ⁻ ” include trifluoroacetate ions, acetate ions, 1-adamantanecarboxylate ions and the like.

The oxime sulfonate acid generator in the component (B2) is a compound having at least one group represented by the following general formula (B-1), and has a property of generating an acid upon irradiation (exposure) of radiation. It is what you have.
Such an oxime sulfonate-based acid generator in the component (B2) is frequently used for chemically amplified resist compositions, and can be arbitrarily selected and used.

［式（Ｂ−１）中、Ｒ^３１、Ｒ^３２はそれぞれ独立に有機基を表す。］

[In formula (B-1), R ³¹ and R ³² each independently represents an organic group. ]

The organic groups of R ³¹ and R ³² are groups containing carbon atoms, and atoms other than carbon atoms (for example, hydrogen atoms, oxygen atoms, nitrogen atoms, sulfur atoms, halogen atoms (fluorine atoms, chlorine atoms, etc.), etc.) You may have.
As the organic group for R ^31, a linear, branched, or cyclic alkyl group or aryl group is preferable. These alkyl groups and aryl groups may have a substituent. There is no restriction | limiting in particular as this substituent, For example, a fluorine atom, a C1-C6 linear, branched or cyclic alkyl group etc. are mentioned. Here, “having a substituent” means that part or all of the hydrogen atoms of the alkyl group or aryl group are substituted with a substituent.
As an alkyl group, C1-C20 is preferable, C1-C10 is more preferable, C1-C8 is more preferable, C1-C6 is especially preferable, and C1-C4 is the most preferable. As the alkyl group, a partially or completely halogenated alkyl group (hereinafter sometimes referred to as a halogenated alkyl group) is particularly preferable. The partially halogenated alkyl group means an alkyl group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated alkyl group means that all of the hydrogen atoms are halogen atoms. Means an alkyl group substituted with Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. That is, the halogenated alkyl group is preferably a fluorinated alkyl group.
The aryl group preferably has 4 to 20 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms. As the aryl group, a partially or completely halogenated aryl group is particularly preferable. The partially halogenated aryl group means an aryl group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated aryl group means that all of the hydrogen atoms are halogen atoms. Means an aryl group substituted with.
R ³¹ is particularly preferably an alkyl group having 1 to 4 carbon atoms having no substituent or a fluorinated alkyl group having 1 to 4 carbon atoms.
As the organic group for R ^32, a linear, branched, or cyclic alkyl group, aryl group, or cyano group is preferable. As the alkyl group and aryl group for R ^32, the same alkyl groups and aryl groups as those described above for R ³¹ can be used.
R ³² is particularly preferably a cyano group, an alkyl group having 1 to 8 carbon atoms having no substituent, or a fluorinated alkyl group having 1 to 8 carbon atoms.

  More preferable examples of the oxime sulfonate-based acid generator include compounds represented by the following general formula (B-2) or (B-3).

［式（Ｂ−２）中、Ｒ^３３は、シアノ基、置換基を有さないアルキル基またはハロゲン化アルキル基である。Ｒ^３４はアリール基である。Ｒ^３５は置換基を有さないアルキル基またはハロゲン化アルキル基である。］

[In Formula (B-2), R ³³ represents a cyano group, an alkyl group having no substituent, or a halogenated alkyl group. R ³⁴ is an aryl group. R ³⁵ represents an alkyl group having no substituent or a halogenated alkyl group. ]

［式（Ｂ−３）中、Ｒ^３６はシアノ基、置換基を有さないアルキル基またはハロゲン化アルキル基である。Ｒ^３７は２または３価の芳香族炭化水素基である。Ｒ^３８は置換基を有さないアルキル基またはハロゲン化アルキル基である。ｐ”は２または３である。］

[In Formula (B-3), R ³⁶ represents a cyano group, an alkyl group having no substituent, or a halogenated alkyl group. R ³⁷ is a divalent or trivalent aromatic hydrocarbon group. ^R38 is an alkyl group having no substituent or a halogenated alkyl group. p ″ is 2 or 3.]

In the general formula (B-2), the alkyl group or halogenated alkyl group having no substituent of R ³³ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and carbon atoms. Numbers 1 to 6 are most preferable.
R ³³ is preferably a halogenated alkyl group, more preferably a fluorinated alkyl group.
The fluorinated alkyl group for R ³³ is preferably such that the hydrogen atom of the alkyl group is 50% or more fluorinated, more preferably 70% or more fluorinated, and 90% or more fluorinated. Particularly preferred.
As the aryl group of R ³⁴ , one hydrogen atom is removed from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, or a phenanthryl group. And a heteroaryl group in which a part of carbon atoms constituting the ring of these groups is substituted with a heteroatom such as an oxygen atom, a sulfur atom, or a nitrogen atom. Among these, a fluorenyl group is preferable.
The aryl group of R ³⁴ may have a substituent such as an alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or an alkoxy group. The alkyl group or halogenated alkyl group in the substituent preferably has 1 to 8 carbon atoms, and more preferably 1 to 4 carbon atoms. The halogenated alkyl group is preferably a fluorinated alkyl group.
The alkyl group or halogenated alkyl group having no substituent of R ³⁵ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 6 carbon atoms.
R ³⁵ is preferably a halogenated alkyl group, more preferably a fluorinated alkyl group.
The fluorinated alkyl group for R ³⁵ is preferably such that the hydrogen atom of the alkyl group is 50% or more fluorinated, more preferably 70% or more fluorinated, and 90% or more fluorinated. Particularly preferred is the strength of the acid generated. Most preferably, it is a fully fluorinated alkyl group in which a hydrogen atom is 100% fluorine-substituted.

In the general formula (B-3), the alkyl group or halogenated alkyl group having no substituent for R ³⁶ is the same as the alkyl group or halogenated alkyl group having no substituent for R ^33. Is mentioned.
Examples of the divalent or trivalent aromatic hydrocarbon group for R ³⁷ include groups obtained by further removing one or two hydrogen atoms from the aryl group for R ³⁴ .
Examples of the alkyl group or halogenated alkyl group having no substituent of R ³⁸ include the same alkyl groups or halogenated alkyl groups as those having no substituent of R ³⁵ .
p ″ is preferably 2.

Specific examples of the oxime sulfonate acid generator include α- (p-toluenesulfonyloxyimino) -benzyl cyanide, α- (p-chlorobenzenesulfonyloxyimino) -benzyl cyanide, α- (4-nitrobenzenesulfonyloxy). Imino) -benzylcyanide, α- (4-nitro-2-trifluoromethylbenzenesulfonyloxyimino) -benzylcyanide, α- (benzenesulfonyloxyimino) -4-chlorobenzylcyanide, α- (benzenesulfonyl) Oxyimino) -2,4-dichlorobenzyl cyanide, α- (benzenesulfonyloxyimino) -2,6-dichlorobenzyl cyanide, α- (benzenesulfonyloxyimino) -4-methoxybenzyl cyanide, α- ( 2-Chlorobenzenesulfonyloxyimino) 4-methoxybenzylcyanide, α- (benzenesulfonyloxyimino) -thien-2-ylacetonitrile, α- (4-dodecylbenzenesulfonyloxyimino) -benzylcyanide, α-[(p-toluenesulfonyloxyimino) -4-methoxyphenyl] acetonitrile, α-[(dodecylbenzenesulfonyloxyimino) -4-methoxyphenyl] acetonitrile, α- (tosyloxyimino) -4-thienyl cyanide, α- (methylsulfonyloxyimino) -1-cyclo Pentenyl acetonitrile, α- (methylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (methylsulfonyloxyimino) -1-cycloheptenylacetonitrile, α- (methylsulfonyloxyimino) -1-cyclooctene Acetonitrile, α- (trifluoromethylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (trifluoromethylsulfonyloxyimino) -cyclohexylacetonitrile, α- (ethylsulfonyloxyimino) -ethylacetonitrile, α- (propyl Sulfonyloxyimino) -propylacetonitrile, α- (cyclohexylsulfonyloxyimino) -cyclopentylacetonitrile, α- (cyclohexylsulfonyloxyimino) -cyclohexylacetonitrile, α- (cyclohexylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- ( Ethylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (isopropylsulfonyloxyimino) -1-cyclope N-tenyl acetonitrile, α- (n-butylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (ethylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (isopropylsulfonyloxyimino) -1-cyclohexenylacetonitrile , Α- (n-butylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (methylsulfonyloxyimino) -phenylacetonitrile, α- (methylsulfonyloxyimino) -p-methoxyphenylacetonitrile, α- (trifluoro Methylsulfonyloxyimino) -phenylacetonitrile, α- (trifluoromethylsulfonyloxyimino) -p-methoxyphenylacetonitrile, α- (ethylsulfonyloxyimino) -p- Butoxy phenylacetonitrile, alpha-(propylsulfonyl oxyimino)-p-methylphenyl acetonitrile, alpha-like (methylsulfonyloxyimino)-p-bromophenyl acetonitrile.
Further, an oxime sulfonate-based acid generator disclosed in JP-A-9-208554 (paragraphs [0012] to [0014] [chemical formula 18] to [chemical formula 19]), pamphlet of International Publication No. 04/074242, An oxime sulfonate-based acid generator disclosed in Examples 1 to 40) on pages 65 to 85 can also be suitably used.
Moreover, the following can be illustrated as a suitable thing.

Among the diazomethane acid generators in the component (B2), specific examples of bisalkyl or bisarylsulfonyldiazomethanes include bis (isopropylsulfonyl) diazomethane, bis (p-toluenesulfonyl) diazomethane, bis (1,1-dimethyl). And ethylsulfonyl) diazomethane, bis (cyclohexylsulfonyl) diazomethane, bis (2,4-dimethylphenylsulfonyl) diazomethane, and the like.
Further, diazomethane acid generators disclosed in JP-A-11-035551, JP-A-11-035552, and JP-A-11-035573 can also be suitably used.
Examples of poly (bissulfonyl) diazomethanes include 1,3-bis (phenylsulfonyldiazomethylsulfonyl) propane and 1,4-bis (phenylsulfonyldiazo) disclosed in JP-A-11-322707. Methylsulfonyl) butane, 1,6-bis (phenylsulfonyldiazomethylsulfonyl) hexane, 1,10-bis (phenylsulfonyldiazomethylsulfonyl) decane, 1,2-bis (cyclohexylsulfonyldiazomethylsulfonyl) ethane, 1,3 -Bis (cyclohexylsulfonyldiazomethylsulfonyl) propane, 1,6-bis (cyclohexylsulfonyldiazomethylsulfonyl) hexane, 1,10-bis (cyclohexylsulfonyldiazomethylsulfonyl) decane, etc. Door can be.

  In the resist composition, the content of the entire component (B) is preferably 0.5 to 80 parts by mass, more preferably 1 to 60 parts by mass, and 1 to 50 parts by mass with respect to 100 parts by mass of the component (A). Further preferred. By setting it in the above range, the EL margin is large and the roughness can be reduced, and the pattern formation is sufficiently performed.

<Optional component>
In the resist composition of the present invention, a nitrogen-containing organic compound component (D) (hereinafter referred to as “(D)” which does not fall under the components (A) and (B), as long as the effects of the present invention are not impaired. It is preferable to contain "component").
The component (D) is not particularly limited as long as it acts as an acid diffusion control agent, that is, a quencher that traps the acid generated from the component (B) by exposure, and a variety of components have already been proposed. Therefore, any known one may be used. Examples thereof include amines such as aliphatic amines and aromatic amines, among which aliphatic amines, particularly secondary aliphatic amines and tertiary aliphatic amines are preferred.
An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 20 carbon atoms.
Examples of the aliphatic amine include an amine (alkylamine or alkyl alcohol amine) or a cyclic amine in which at least one hydrogen atom of ammonia NH ₃ is substituted with an alkyl group or hydroxyalkyl group having 20 or less carbon atoms. .
The alkyl group and the alkyl group in the hydroxyalkyl group may be linear, branched or cyclic.
When the alkyl group is linear or branched, the carbon number thereof is more preferably 2-20, and further preferably 2-8.
When the alkyl group is cyclic (when it is a cycloalkyl group), the carbon number is preferably 3 to 30, more preferably 3 to 20, still more preferably 3 to 15, and 4 to 12 carbon atoms. It is particularly preferred that the number of carbon atoms is 5-10. The alkyl group may be monocyclic or polycyclic. Specific examples include groups in which one or more hydrogen atoms have been removed from monocycloalkane, groups in which one or more hydrogen atoms have been removed from polycycloalkanes such as bicycloalkane, tricycloalkane, and tetracycloalkane. . Specific examples of the monocycloalkane include cyclopentane and cyclohexane. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane.
Specific examples of the alkylamine include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decylamine; diethylamine, di-n-propylamine, di-n- Dialkylamines such as heptylamine, di-n-octylamine, dicyclohexylamine; trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine, tri- and trialkylamines such as n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decanylamine, and tri-n-dodecylamine.
Specific examples of the alkyl alcohol amine include diethanolamine, triethanolamine, diisopropanolamine, triisopropanolamine, di-n-octanolamine, tri-n-octanolamine, stearyl diethanolamine, lauryldiethanolamine and the like.
Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be monocyclic (aliphatic monocyclic amine) or polycyclic (aliphatic polycyclic amine).
Specific examples of the aliphatic monocyclic amine include piperidine and piperazine.
As the aliphatic polycyclic amine, those having 6 to 10 carbon atoms are preferable. Specifically, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5. 4.0] -7-undecene, hexamethylenetetramine, 1,4-diazabicyclo [2.2.2] octane, and the like.
Other aliphatic amines include tris (2-methoxymethoxyethyl) amine, tris {2- (2-methoxyethoxy) ethyl} amine, tris {2- (2-methoxyethoxymethoxy) ethyl} amine, tris {2- (1-methoxyethoxy) ethyl} amine, tris {2- (1-ethoxyethoxy) ethyl} amine, tris {2- (1-ethoxypropoxy) ethyl} amine, tris [2- {2- (2-hydroxyethoxy) ) Ethoxy} ethyl] amine and the like.
Examples of the aromatic amine include aniline, pyridine, 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, diphenylamine, triphenylamine, and tribenzylamine.
These may be used alone or in combination of two or more.
(D) component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component. By setting the content in the above range, the resist pattern shape, the stability over time and the like are improved.

The resist composition of the present invention is a group consisting of organic carboxylic acid, phosphorus oxo acid and derivatives thereof as optional components for the purpose of preventing sensitivity deterioration and improving the resist pattern shape, retention stability over time, etc. May contain at least one compound (E) (hereinafter referred to as “component (E)”) selected from:
As the organic carboxylic acid, for example, acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, salicylic acid and the like are suitable.
Examples of phosphorus oxo acids include phosphoric acid, phosphonic acid, and phosphinic acid. Among these, phosphonic acid is particularly preferable.
Examples of the oxo acid derivative of phosphorus include esters in which the hydrogen atom of the oxo acid is substituted with a hydrocarbon group, and the hydrocarbon group includes an alkyl group having 1 to 5 carbon atoms and 6 to 6 carbon atoms. 15 aryl groups and the like.
Examples of phosphoric acid derivatives include phosphoric acid esters such as di-n-butyl phosphate and diphenyl phosphate.
Examples of phosphonic acid derivatives include phosphonic acid esters such as phosphonic acid dimethyl ester, phosphonic acid-di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester.
Examples of the phosphinic acid derivatives include phosphinic acid esters such as phenylphosphinic acid.
(E) A component may be used individually by 1 type and may use 2 or more types together.
(E) A component is normally used in 0.01-5.0 mass parts with respect to 100 mass parts of (A) component.

  The resist composition of the present invention may further contain, if desired, miscible additives such as an additional resin for improving the performance of the resist film, a surfactant for improving coatability, a dissolution inhibitor, Plasticizers, stabilizers, colorants, antihalation agents, dyes, and the like can be added and contained as appropriate.

The resist composition of the present invention can be produced by dissolving the material in an organic solvent (hereinafter sometimes referred to as “(S) component”).
As the component (S), any component can be used as long as it can dissolve each component to be used to form a uniform solution. Conventionally, any one of known solvents for chemically amplified resists can be used. Two or more types can be appropriately selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone, cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, and 2-heptanone; Monohydric alcohols; compounds having an ester bond, such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, dipropylene glycol monoacetate, monomethyl ether, monoethyl of the polyhydric alcohols or compound having the ester bond Ether alkyl such as ether, monopropyl ether, monobutyl ether or monophenyl ether Derivatives of polyhydric alcohols such as compounds having a propylene glycol monomethyl ether acetate (PGMEA) or propylene glycol monomethyl ether (PGME) among these]; cyclic ethers such as dioxane, methyl lactate, Esters such as ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate; anisole, ethyl benzyl ether, cresyl methyl ether, diphenyl ether, Aromatic organics such as dibenzyl ether, phenetol, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene, mesitylene A solvent etc. can be mentioned.
These organic solvents may be used independently and may be used as 2 or more types of mixed solvents.
Among these, propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), cyclohexanone, and EL are preferable.
Moreover, the mixed solvent which mixed PGMEA and the polar solvent is also preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA and the polar solvent, preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. It is preferable to be within the range. For example, when EL is blended as a polar solvent, the mass ratio of PGMEA: EL is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3. Further, when PGME and cyclohexanone are blended as polar solvents, the mass ratio of PGMEA: (PGME + cyclohexanone) is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2, and even more preferably 3. : 7 to 7: 3.
In addition, as the component (S), PGMEA, EL or a mixed solvent of PGMEA and a polar solvent and a mixed solvent of γ-butyrolactone are also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
The amount of component (S) used is not particularly limited, but is a concentration that can be applied to a substrate or the like, and is appropriately set according to the coating film thickness. In general, the solid content concentration of the resist composition is 1 -20% by mass, preferably 2-15% by mass.

The resist composition of the present invention can form a resist pattern having a large exposure margin (EL margin) and a reduced LWR. The reason why such an effect is obtained is not clear, but is presumed as follows.
The resist composition of the present invention comprises an (A1) component having the structural unit (a1) as the (A) component, and an acid generator comprising the compound represented by the general formula (b1-1) as the (B) component. Contains agent (B1).
The structural unit (a1) contains the structural unit (a10). The acid-decomposable group represented by the formula (a10-1) or (a10-2) contained in the structural unit (a10) has a moderate bulkiness.
In the compounds of the formula (b1-1), the more polar of X ³ is high, increased affinity with polar portion of the component (A), acid diffusion is suppressed. In the present invention, in the compound represented by the formula (b1-1), X ³ is bonded to the oxygen atom (O), whereby the above effect is further enhanced.
For the above reasons, it is estimated that the effects of the components (A) and (B) can be combined to reduce roughness and optimize the EL margin. Also, an improvement in mask error factor (MEF) is expected.

≪Resist pattern formation method≫
The resist pattern forming method of the present invention includes a step of forming a resist film on a support using the resist composition of the present invention, a step of exposing the resist film, and developing the resist film to form a resist pattern. Forming.
The resist pattern forming method of the present invention can be performed, for example, as follows.
That is, first, the resist composition of the present invention is applied onto a support with a spinner or the like, and a baking (post-apply bake (PAB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably A resist film is formed by applying for 60 to 90 seconds.
Next, the resist film is exposed through a mask (mask pattern) on which a predetermined pattern is formed using an exposure apparatus such as an ArF exposure apparatus, an electron beam drawing apparatus, or an EUV exposure apparatus, or a mask pattern. After performing selective exposure by drawing or the like by direct irradiation with an electron beam without passing through, baking (post-exposure baking (PEB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably 60 Apply for ~ 90 seconds.
Next, the resist film is developed.
The development treatment is performed using an alkaline developer in the case of an alkali development process, and using a developer (organic developer) containing an organic solvent in the case of a solvent development process.
A rinsing treatment is preferably performed after the development treatment. The rinse treatment is preferably a water rinse using pure water in the case of an alkali development process, and is preferably a rinse solution containing an organic solvent in the case of a solvent development process.
In the case of a solvent development process, after the development process or the rinse process, a process of removing the developer or rinse liquid adhering to the pattern with a supercritical fluid may be performed.
Drying is performed after development or rinsing. In some cases, a baking process (post-bake) may be performed after the development process. In this way, a resist pattern can be obtained.

The support is not particularly limited, and a conventionally known one can be used, and examples thereof include a substrate for electronic components and a substrate on which a predetermined wiring pattern is formed. More specifically, a silicon substrate, a metal substrate such as copper, chromium, iron, and aluminum, a glass substrate, and the like can be given. As a material for the wiring pattern, for example, copper, aluminum, nickel, gold or the like can be used.
Further, the support may be a substrate in which an inorganic and / or organic film is provided on the above-described substrate. An inorganic antireflection film (inorganic BARC) is an example of the inorganic film. Examples of the organic film include organic films such as an organic antireflection film (organic BARC) and a lower organic film in a multilayer resist method.
Here, the multilayer resist method is a method in which at least one organic film (lower organic film) and at least one resist film (upper resist film) are provided on a substrate, and the resist pattern formed on the upper resist film is used as a mask. This is a method of patterning a lower organic film, and it is said that a pattern with a high aspect ratio can be formed. That is, according to the multilayer resist method, the required thickness can be secured by the lower organic film, so that the resist film can be thinned and a fine pattern with a high aspect ratio can be formed.
In the multilayer resist method, basically, a method of forming a two-layer structure of an upper resist film and a lower organic film (two-layer resist method), and one or more intermediate layers between the upper resist film and the lower organic film And a method of forming a multilayer structure of three or more layers (metal thin film etc.) (three-layer resist method).

The wavelength used for the exposure is not particularly limited, and ArF excimer laser, KrF excimer laser, F ₂ excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-ray, soft X-ray, etc. Can be done using radiation. The resist composition is highly useful for KrF excimer laser, ArF excimer laser, EB or EUV.

The exposure method of the resist film may be normal exposure (dry exposure) performed in an inert gas such as air or nitrogen, or may be immersion exposure (Liquid Immersion Lithography).
In immersion exposure, the space between the resist film and the lens at the lowest position of the exposure apparatus is previously filled with a solvent (immersion medium) having a refractive index larger than that of air, and exposure (immersion exposure) is performed in that state. It is an exposure method.
As the immersion medium, a solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film to be exposed is preferable. The refractive index of such a solvent is not particularly limited as long as it is within the above range.
Examples of the solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film include water, a fluorine-based inert liquid, a silicon-based solvent, and a hydrocarbon-based solvent.
Specific examples of the fluorine-based inert liquid include a fluorine-based compound such as C ₃ HCl ₂ F ₅ , C ₄ F ₉ OCH ₃ , C ₄ F ₉ OC ₂ H ₅ , and C ₅ H ₃ F ₇ as a main component. Examples thereof include liquids, and those having a boiling point of 70 to 180 ° C are preferable, and those having a boiling point of 80 to 160 ° C are more preferable. It is preferable that the fluorine-based inert liquid has a boiling point in the above range since the medium used for immersion can be removed by a simple method after the exposure is completed.
As the fluorine-based inert liquid, a perfluoroalkyl compound in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly preferable. Specific examples of the perfluoroalkyl compound include a perfluoroalkyl ether compound and a perfluoroalkylamine compound.
More specifically, examples of the perfluoroalkyl ether compound include perfluoro (2-butyl-tetrahydrofuran) (boiling point 102 ° C.). Examples of the perfluoroalkylamine compound include perfluorotributylamine ( Boiling point of 174 ° C.).
As the immersion medium, water is preferably used from the viewpoints of cost, safety, environmental problems, versatility, and the like.

Examples of the alkali developer used for the development treatment in the alkali development process include a 0.1 to 10% by mass tetramethylammonium hydroxide (TMAH) aqueous solution.
The organic solvent contained in the organic developer used for the development process in the solvent development process is not particularly limited as long as it can dissolve the component (A) (component (A) before exposure). It can be selected as appropriate. Specifically, polar solvents such as ketone solvents, ester solvents, alcohol solvents, amide solvents, ether solvents, and hydrocarbon solvents can be used.
A known additive can be blended in the organic developer as required. Examples of the additive include a surfactant. The surfactant is not particularly limited. For example, ionic or nonionic fluorine-based and / or silicon-based surfactants can be used.
When the surfactant is blended, the blending amount is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and 0.01 to 0. 0% with respect to the total amount of the organic developer. 5 mass% is more preferable.
The development process can be carried out by a known development method, for example, a method in which a support is immersed in a developer for a certain period of time (dip method), a developer is raised on the surface of the support by surface tension, and is left for a certain period of time. (Paddle method), spraying developer on the surface of the support (spray method), coating the developer while scanning the developer coating nozzle at a constant speed on the support rotating at a constant speed The method to continue (dynamic dispensing method) etc. are mentioned.

As the organic solvent contained in the rinsing liquid used for the rinsing treatment after the development process in the solvent development process, for example, among the organic solvents mentioned as the organic solvent contained in the organic developer, those which are difficult to dissolve the resist pattern are appropriately used. You can select and use. Usually, at least one solvent selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents is used. Among these, at least one selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents and amide solvents is preferable, and at least one selected from alcohol solvents and ester solvents is preferable. More preferred are alcohol solvents.
The rinsing treatment (washing treatment) using the rinsing liquid can be carried out by a known rinsing method. For example, the rinsing liquid is continuously applied onto a support rotating at a constant speed (rotary coating method). A method of immersing the support in a rinsing solution for a certain time (dip method), a method of spraying a rinsing solution on the surface of the support (spray method), and the like.

EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited by these examples.
In this example, a compound represented by (1) in the chemical formula is described as “compound (1)”, and the compounds represented by other formulas are also described in the same manner.
In the analysis by NMR, the internal standard of ¹ H-NMR and the internal standard of ¹³ C-NMR is tetramethylsilane (TMS). The internal standard of ¹⁹ F-NMR is hexafluorobenzene (however, the peak of hexafluorobenzene was set to −160 ppm).
The compounds used as monomers in the synthesis examples described below are shown below.

[Polymer Synthesis Example 1: Synthesis of Polymer Compound 1]
In a separable flask connected with a thermometer, a reflux tube, and a nitrogen introduction tube, 26.09 g (95.07 mmol) of compound (1), 7.64 g (32.32 mmol) of compound (4), 17.04 g (53 .87 mmol) of compound (3), 11.00 g (64.65 mmol) of compound (5) was dissolved in 79.36 g of methyl ethyl ketone (MEK). To this solution, 14.75 mmol of dimethyl azobisisobutyrate (V-601) was added and dissolved as a polymerization initiator.
The resultant was dropwise added to 43.05 g of MEK heated to 80 ° C. in a nitrogen atmosphere over 4 hours. After completion of dropping, the reaction solution was heated and stirred for 1 hour, and then the reaction solution was cooled to room temperature.
The obtained reaction polymerization solution was dropped into a large amount of n-heptane, and a polymer was precipitated. The precipitated white powder was filtered off, washed with methanol and dried to obtain the target polymer compound. 40.1g of (1) was obtained.
The mass average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement for this polymer compound (1) was 7,200, and the molecular weight dispersity (Mw / Mn) was 1.65.

[Polymer Synthesis Examples 2 to 4: Synthesis of Polymer Compounds 2 to 4]
Polymer compounds 2 to 4 were obtained in the same procedure as in Polymer Synthesis Example 1 except that the type and blending amount of the monomers used were changed.
For each polymer compound, the copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by carbon 13 nuclear magnetic resonance spectrum (600 MHz — ¹³ C-NMR), standard polystyrene determined by GPC measurement The converted mass average molecular weight (Mw) and molecular weight dispersity (Mw / Mn) are shown in Table 1.

[Acid Generator Synthesis Example 1: Synthesis of Compound (B) -1]
(I) To 192.1 g of methyl fluorosulfonyl (difluoro) acetate and 480 g of pure water, 440 g of a 30% by mass aqueous sodium hydroxide solution was added dropwise while maintaining the temperature at 10 ° C. or lower in an ice bath. After dropping, the mixture was refluxed at 100 ° C. for 3 hours, cooled, and neutralized with 10 mass% hydrochloric acid. The obtained solution was added dropwise to 9074 g of acetone, and the precipitate was filtered and dried to obtain 257.6 g of compound (7) as a white solid (purity: 80.7%, yield: 94.5%). .

(Ii) 56.2 g of compound (7) and 562.2 g of acetonitrile were charged, 77.4 g of p-toluenesulfonic acid monohydrate was added, and the mixture was refluxed at 110 ° C. for 3 hours. Then, it filtered and the filtrate was concentrated and dried. To the obtained solid, 900 g of t-butyl methyl ether (TBME) was added and stirred. Then, it filtered and the filtrate was dried, and 25.7 g (purity: 91.0%, yield: 52.0%) of compound (8) was obtained as a white solid.

(Iii) 5.00 g of compound (8) (purity: 91.0%), 4.80 g of sultone-OH (9), and 25.0 g of toluene are charged, and 0.935 g of p-toluenesulfonic acid monohydrate is added. And refluxed at 110 ° C. for 26 hours. Then, it filtered, 25.0g of toluene was added to the residue, it stirred at room temperature for 10 minutes, and the process of performing filtration was repeated twice, and white powder was obtained. The white powder was dried in vacuo overnight. The next day, 5 g of acetone was added to the white powder and stirred for 15 minutes at room temperature, followed by filtration. The obtained filtrate was slowly added dropwise to 25.0 g of TBME and 25.0 g of methylene chloride, and the precipitated solid was recovered by filtration. -By drying, 5.89 g (purity: 98.4%, yield: 68.1%) of the compound (10) was obtained as a white powder.

Compound (10) was analyzed by ¹ H-NMR and ¹⁹ F-NMR.
¹ H-NMR (DMSO-d6, 400 MHz): δ (ppm) 1.73-2.49 (m, 4H, Ha, Hb), 2.49 (m, 1H, Hc), 3.34 (m, 1H, Hd), 3.88 (t, 1H, He), 4.66 (t, 1H, Hf), 4.78 (m, 1H, Hg)
¹⁹ F-NMR (DMSO-d6, 400 MHz): δ (ppm) -107.7 (m, 2F, Fa) (however, the peak of hexafluorobenzene was set to −160 ppm)
From the results shown above, it was confirmed that the compound (10) had a structure shown below.

  (Iv) Dissolve 3.21 g of compound (10) in 32.1 g of pure water, add 3.72 g of 4-methylphenyldiphenylsulfonium bromide, add 32.1 g of methylene chloride, and stir at room temperature for 1 hour. It was. Thereafter, the organic layer was taken out by liquid separation. The organic layer was washed 3 times with a 1% by mass aqueous HCl solution, then washed 4 times with pure water, and the organic layer was concentrated to give 4.94 g of compound (11) (compound (B) -1) as a white solid. (Purity: 98.8%, yield: 86.8%) was obtained.

[Acid Generator Synthesis Example 2: Synthesis of Compound (B) -2]
In the acid generator synthesis example 1 (iii), sultone-OH (9) is changed to the following compound (12), and (iv) is changed from 4-methylphenyldiphenylsulfonium bromide to 3,4,5-trimethylphenyldiphenylsulfonium bromide. The following compound (B) -2 was synthesized by the same method as in Acid Generator Synthesis Example 1 except that the compound was changed.

[Acid Generator Synthesis Example 3: Synthesis of Compound (B) -3]
In the acid generator synthesis example 1 (iii), the following compound (B) -3 was synthesized by the same method as in the acid generator synthesis example 1 except that sultone-OH (9) was replaced with the following compound (13). .

[Acid Generator Synthesis Example 4: Synthesis of Compound (B) -4]
In the acid generator synthesis example 1 (iii), the following compound (B) -4 was synthesized by the same method as in the acid generator synthesis example 1 except that sultone-OH (9) was replaced with the following compound (14). .

[Examples 1-10, Comparative Examples 1-2]
Each component shown in Table 2 was mixed and dissolved to prepare a positive resist composition.

Each abbreviation in Table 2 has the following meaning. Moreover, the numerical value in [] is a compounding quantity (mass part). In addition, 12.0 mass parts of (B) -1 are 11.6 mass parts of (B) -2, and an equimolar amount.
(A) -1: the polymer compound 1
(A) -2: the polymer compound 2
(A) -3: the polymer compound 3
(A) -4: the polymer compound 4
(B) -1: Compound (B) -1
(B) -2: Compound (B) -2
(B) -3: Compound (B) -3
(B) -4: Compound (B) -4
(B) -5: Compound represented by the following chemical formula (B) -5 (D) -1: Tri-n-pentylamine (E) -1: Salicylic acid (S) -1: Propylene glycol monomethyl ether acetate (PGMEA )
(S) -2: Propylene glycol monomethyl ether (PGME)
(S) -3: γ-butyrolactone

The following evaluation was performed using the obtained resist composition.
[Formation of resist pattern]
An organic antireflection film composition “ARC29A” (trade name, manufactured by Brewer Science Co., Ltd.) is applied onto a 12-inch silicon wafer using a spinner and baked on a hot plate at 205 ° C. for 60 seconds to be dried. Thus, an organic antireflection film having a film thickness of 82 nm was formed.
Then, the positive resist composition obtained above is applied onto the organic antireflection film using a spinner, and baked (PAB) on a hot plate at 100 ° C. for 60 seconds. And a resist film having a thickness of 120 nm was formed by drying.
Next, with respect to the resist film, the ArF exposure apparatus NSR-S302 (manufactured by Nikon; NA (numerical aperture) = 0.60, 2/3 annular illumination) is applied to the resist film through a mask pattern. , ArF excimer laser (193 nm) was selectively irradiated.
Then, baking treatment (PEB) was performed for 60 seconds at the temperature conditions shown in Table 3, and further, a 2.38 mass% tetramethylammonium hydroxide (TMAH) aqueous solution “NMD-3” (trade name, Tokyo, Japan) at 23 ° C. (Oka Kogyo Co., Ltd.) was subjected to alkali development for 30 seconds, rinsed with pure water for 30 seconds, and further baked (post-baked) at 100 ° C. for 60 seconds.
As a result, in each example, a 1: 1 line and space (LS) pattern having a line width of 130 nm and a pitch of 260 nm was formed on the resist film. Moreover, the optimal exposure amount Eop (mJ / cm ² ) at this time was determined. The results are shown in Table 3.

[Evaluation of exposure margin (5% EL)]
In [Formation of resist pattern], the exposure amount when the line of the LS pattern is formed within a range of ± 5% (136.5 nm to 123.5 nm) of the target dimension (line width 130 nm) is obtained. The exposure margin (unit:%) was determined by the formula. The exposure margin indicates that the larger the value is, the smaller the change amount of the pattern size with the fluctuation of the exposure amount. The results are shown in Table 3 as “5% EL”.
Exposure margin (%) = (| E1-E2 | / Eop) × 100
In the formula, E1 is an exposure amount when an LS pattern having a line width of 136.5 nm is formed (mJ / cm ² ), E2 is an exposure amount when an LS pattern having a line width of 123.5 nm is formed (mJ / cm ² ).

[Evaluation of LWR (Line Width Roughness)]
In the LS pattern with a line width of 130 nm and a pitch of 260 nm formed by the above Eop, the line width is adjusted in the longitudinal direction of the line by a scanning electron microscope (acceleration voltage 800 V, product name S-9220, manufactured by Hitachi High-Technologies Corporation). Measurement was performed at 400 locations, and a triple value (3 s) (unit: nm) of the standard deviation (σ) obtained from the measurement result was calculated. The obtained results are shown in Table 3.
The smaller the value of 3s, the smaller the line width roughness, and the more uniform width LS pattern was obtained.

  As shown in Table 3, the positive resist compositions of Examples 1 to 10 have an exposure margin as compared with Comparative Examples 1 and 2 using an acid generator that does not correspond to the component (B1) in the present invention. It was confirmed that the LWR was also reduced.

Claims (9)

A resist composition containing a base material component (A) whose solubility in a developing solution is changed by the action of an acid, and an acid generator component (B) that generates an acid upon exposure,
The base component (A) includes a resin component (A1) having a structural unit (a1) containing an acid-decomposable group that increases in polarity by the action of an acid,
The structural unit (a1) contains a structural unit (a10) represented by the following general formula (a10),
The said acid generator component (B) contains the acid generator (B1) which consists of a compound represented by the following general formula (b1-1), The resist composition characterized by the above-mentioned.

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, and R ² represents the following general formula (a10-1) or the following formula (a10-2 ). ]

[In the formula, the broken line is a bond, R ³ is a linear or branched alkyl group having 1 to 5 carbon atoms, n ″ is 0 or 1, and X is an oxygen atom or CH ₂ . , P is 1 or 2.]

[Wherein, Q ¹ is a divalent linking group or a single bond, and Y ¹ is an alkylene group having 1 to 4 carbon atoms which may have a substituent or 1 to 1 carbon atoms which may have a substituent. 4 is a fluorinated alkylene group, O is an oxygen atom, X ³ is an optionally substituted cyclic group having 3 to 30 carbon atoms, and A ⁺ is an organic cation. ] The resist composition according to claim 1, wherein Q ¹ in the general formula (b1-1) is a divalent linking group containing a carbonyl group — (C (═O)) —. The resist composition according to claim 1, wherein the resin component (A1) further has a structural unit (a0) containing a —SO ₂ — containing cyclic group.     The resin component (A1) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent, and the polar group-containing aliphatic hydrocarbon group The resist composition as described in any one of Claims 1-3 which has the structural unit (a3) (However, except the thing applicable to the said structural unit (a1) and the said structural unit (a0).). The resist composition according to claim 3, wherein the structural unit (a0) contains a structural unit represented by the following general formula (a0-0).

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, R ²⁸ represents a —SO ₂ — containing cyclic group, and R ²⁹ represents a single bond. Or it is a bivalent coupling group. ] The resist composition according to claim 5, wherein R ²⁹ in the general formula (a0-0) is a divalent linking group.     The resin component (A1) further includes a lactone-containing cyclic group, which is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent. The resist composition as described in any one of Claims 1-6 which has a unit (a2).   Furthermore, the resist composition as described in any one of Claims 1-7 containing a nitrogen-containing organic compound component (D).   A step of forming a resist film on the support using the resist composition according to any one of claims 1 to 8, a step of exposing the resist film, and developing the resist film to form a resist pattern A resist pattern forming method including a forming step.