JP2013125204A - Resist composition and resist pattern formation method - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a resist composition and a resist pattern formation method which are capable of forming a resist pattern with a good shape and reduced roughness.SOLUTION: The resist composition contains a resin component (A1') whose solubility in a developer is changed by effect of acid and which generates acid by exposure to light. The resin component contains: a constituent unit containing a group represented by the general formula (a5-10), where Q is a single bond or divalent linking group and Ris a hydrogen atom, fluorine atom, alkyl group, or fluorinated alkyl group; a constituent unit which is derived from acrylic ester and increases its polarity by effect of acid; and a constituent unit containing a specific polar group.

Description

  The present invention relates to a resist composition and a resist pattern forming method.

In lithography technology, for example, a resist film made of a resist material is formed on a substrate, and the resist film is selectively exposed to radiation such as light or an electron beam through a mask on which a predetermined pattern is formed. And a development process is performed to form a resist pattern having a predetermined shape on the resist film.
A resist material in which the exposed portion changes to a property that dissolves in the developer is referred to as a positive type, and a resist material that changes to a property in which the exposed portion does not dissolve in the developer is referred to as a negative type.
In recent years, in the manufacture of semiconductor elements and liquid crystal display elements, pattern miniaturization has been rapidly progressing due to advances in lithography technology.
As a technique for miniaturization, the exposure light source is generally shortened in wavelength (increased energy). Specifically, conventionally, ultraviolet rays typified by g-line and i-line have been used, but at present, mass production of semiconductor elements using a KrF excimer laser or an ArF excimer laser has started. Further, studies have been made on electron beams having shorter wavelengths (higher energy) than these excimer lasers, EUV (extreme ultraviolet rays), X-rays, and the like.

Resist materials are required to have lithography characteristics such as sensitivity to these exposure light sources and resolution capable of reproducing patterns with fine dimensions.
As a resist material satisfying such requirements, a chemically amplified resist composition containing a base material component whose solubility in a developing solution is changed by the action of an acid and an acid generator component that generates an acid upon exposure is used. ing.
For example, when the developer is an alkali developer (alkali development process), the chemically amplified resist composition includes a resin component (base resin) whose solubility in an alkali developer is increased by the action of an acid, an acid generator component, The thing containing is generally used. When a resist film formed using such a chemically amplified resist composition is selectively exposed at the time of resist pattern formation, an acid is generated from the acid generator component in the exposed portion, and the action of the acid causes the resin component The solubility in an alkali developer increases, and the exposed portion becomes soluble in the alkali developer. Then, a positive pattern in which an unexposed portion remains as a pattern is formed. Here, as the base resin, a resin whose polarity is increased by the action of an acid is used, and the solubility in an alkali developer is increased while the solubility in an organic solvent is decreased. Therefore, when a process using a developer containing an organic solvent (organic developer) (hereinafter sometimes referred to as a solvent development process or a negative development process) is applied instead of an alkali development process, the exposed portion of the resist film Then, since the solubility with respect to the organic developer is relatively lowered, the unexposed portion is dissolved and removed by the organic developer to form a negative pattern in which the exposed portion remains as a pattern. For example, Patent Document 1 proposes a negative development process.

  At present, as a base resin of a resist composition used in ArF excimer laser lithography and the like, a resin (acrylic resin) having a structural unit derived from a (meth) acrylate ester in its main chain because of its excellent transparency near 193 nm. And the like are generally used (see, for example, Patent Document 2).

In recent years, chemically amplified resist compositions have been proposed in which the structure contains a resin component having an acid-generating group that generates an acid upon exposure and an acid-decomposable group that increases in polarity by the action of an acid. (For example, see Patent Documents 3 to 5).
Such a resin component has both a function as an acid generator and a function as a base material component, and a chemical amplification resist composition can be constituted by only one component. In other words, when the resin component is exposed to light, an acid is generated from the acid-generating group in the structure, the acid-decomposable group is decomposed by the action of the acid, and a polar group such as a carboxy group is generated to increase the polarity. To do. Therefore, if selective exposure is performed on a resin film (resist film) formed using the resin component, the polarity of the exposed portion increases. A positive resist pattern is formed by dissolution and removal.

  In addition, with the miniaturization of patterns, a radiation sensitive resin composition containing a polymer having an acid dissociable group, a radiation sensitive acid generator, and a photodegradable base as an acid diffusion inhibitor has also been proposed. (See Patent Document 6).

JP 2008-292975 A JP 2003-241385 A JP-A-10-221852 JP 2006-045311 A JP 2006-215526 A International Publication No. 2010/029965

According to the resin component having an acid-generating group and an acid-decomposable group as described above, the resolution is improved as compared with the case where the acid generator and the base material component are separately blended. The reason why the resolution is improved is that the resin component as a base component has an acid generating group, and the acid generating group is easily distributed uniformly in the resist film. It is conceivable that the acid to be easily diffused uniformly in the resist film.
However, when such a resin component is used, the sensitivity at the time of forming the resist pattern is low, and the roughness of the formed resist pattern is improved, but it is still insufficient. Roughness means a rough surface of the resist pattern and causes a defective shape of the resist pattern. For example, line width roughness (line width roughness (LWR)) causes a shape defect typified by non-uniform line width in a line-and-space pattern. Such a shape defect may adversely affect the formation of a fine semiconductor element, and the improvement becomes more important as the pattern becomes finer.
Further, in the technique described in Patent Document 6, it is desired that a reduction in line width roughness particularly in a line-and-space pattern is not sufficiently suppressed along with pattern miniaturization, and a resist pattern having a more uniform width can be formed. .
The present invention has been made in view of the above circumstances, and an object thereof is to provide a resist composition and a resist pattern forming method capable of forming a resist pattern having a good shape with reduced roughness.

In order to solve the above problems, the present invention employs the following configuration.
That is, the first aspect of the present invention is a resist composition containing a base component (A ′) that changes the solubility in a developer by the action of an acid and generates an acid upon exposure, In the substrate component (A ′), a structural unit (a5) containing a group represented by the following general formula (a5-10) and an atom or substituent other than a hydrogen atom are bonded to the α-position carbon atom. A structural unit derived from an acrylate ester that contains an acid-decomposable group that increases polarity by the action of an acid, and a structural unit represented by the following general formula (a3-1) ( a resist composition comprising a resin component (A1 ′) having a3).

［式（ａ５−１０）中、Ｑは単結合又は２価の連結基であり、Ｒ^Ｘは水素原子、フッ素原子、アルキル基、又はフッ素化アルキル基であり、ｐは１〜１０の整数である。Ａ^＋は有機カチオンである。式（ａ３−１）中、Ｒは水素原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基である。Ｐ^０は−Ｃ（＝Ｏ）−Ｏ−、−Ｃ（＝Ｏ）−ＮＲ^０−（Ｒ^０は水素原子又は炭素数１〜５のアルキル基である）又は単結合である。Ｗ^０は置換基として−ＯＨ、−ＣＯＯＨ、−ＣＮ、−ＳＯ_２ＮＨ_２及び−ＣＯＮＨ_２からなる群より選択される少なくとも一種の基を有する環状の炭化水素基であり、任意の位置に酸素原子又は硫黄原子を有していてもよい。］

[In Formula (a5-10), Q is a single bond or a divalent linking group, R ^X is a hydrogen atom, a fluorine atom, an alkyl group, or a fluorinated alkyl group, and p is an integer of 1 to 10. is there. A ⁺ is an organic cation. In formula (a3-1), R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. P ⁰ is —C (═O) —O—, —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms) or a single bond. W ⁰ is a cyclic hydrocarbon group having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent, and oxygen at any position. You may have an atom or a sulfur atom. ]

  According to a second aspect of the present invention, a resist film is formed on a support using the resist composition of the first aspect, the resist film is exposed, and the resist film is developed to form a resist. It is a resist pattern formation method including the process of forming a pattern.

In the present specification and claims, the “alkyl group” includes linear, branched and cyclic monovalent saturated hydrocarbon groups unless otherwise specified.
Unless otherwise specified, the “alkylene group” includes linear, branched and cyclic divalent saturated hydrocarbon groups.
“Fluorinated alkyl group” or “fluorinated alkylene group” refers to a group in which part or all of the hydrogen atoms of an alkyl group or alkylene group are substituted with fluorine atoms.
The “lower alkyl group” is an alkyl group having 1 to 5 carbon atoms.
The “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of the alkyl group are substituted with a halogen atom, and examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
A “hydroxyalkyl group” is a group in which some or all of the hydrogen atoms of an alkyl group have been substituted with hydroxyl groups.
“Aliphatic” is a relative concept with respect to aromatics, and is defined to mean groups, compounds, etc. that do not have aromaticity.
The “structural unit” means a monomer unit (monomer unit) constituting a polymer compound (polymer, copolymer).
“Exposure” is a concept including general irradiation of radiation.

“(Meth) acrylic acid” means one or both of acrylic acid having a hydrogen atom bonded to the α-position and methacrylic acid having a methyl group bonded to the α-position.
“(Meth) acrylic acid ester” means one or both of an acrylic acid ester having a hydrogen atom bonded to the α-position and a methacrylic acid ester having a methyl group bonded to the α-position.
“(Meth) acrylate” means one or both of an acrylate having a hydrogen atom bonded to the α-position and a methacrylate having a methyl group bonded to the α-position.

  ADVANTAGE OF THE INVENTION According to this invention, roughness can be reduced more and the resist composition which can form a resist pattern of a favorable shape, and a resist pattern formation method can be provided.

≪Resist composition≫
The resist composition of the present invention contains a base material component (A ′) (hereinafter referred to as “(A ′) component”) that changes the solubility in a developing solution by the action of an acid and generates an acid upon exposure. To do.
When selective exposure is performed on a resist film formed using such a resist composition, an acid is generated from the component (A ′) in the exposed portion, and the acid acts on the developer of the component (A ′). On the other hand, since the solubility of the component (A ′) in the developer does not change in the unexposed area, there is a difference in solubility in the developer between the exposed area and the unexposed area. . Therefore, when the resist film is developed using an alkali developer, the exposed portion is dissolved and removed, and a positive resist pattern is formed. Further, when the resist film is developed using a developer containing an organic solvent (organic developer), the unexposed portion is dissolved and removed, and a negative resist pattern is formed.
In this specification, a resist composition that forms a positive resist pattern is referred to as a positive resist composition, and a resist composition that forms a negative resist pattern is referred to as a negative resist composition.
The resist composition of the present invention is a positive resist composition in an alkali development process using an alkali developer for development during the formation of a resist pattern, and a developer containing an organic solvent in the development (organic developer) In a solvent development process (also referred to as a negative development process) using a negative resist composition.
The resist composition of the present invention may be used for an alkali development process or a solvent development process.

<(A ') component>
In the present specification and claims, the “base component” is an organic compound having a film forming ability, and preferably an organic compound having a molecular weight of 500 or more is used. When the molecular weight of the organic compound is 500 or more, it has a sufficient film forming ability and can easily form a nano-level resist pattern.
“Organic compounds having a molecular weight of 500 or more” are roughly classified into non-polymers and polymers.
As the non-polymer, those having a molecular weight of 500 or more and less than 4000 are usually used. Hereinafter, the “low molecular compound” refers to a non-polymer having a molecular weight of 500 or more and less than 4000.
As the polymer, those having a molecular weight of 1000 or more are usually used. In the present specification and claims, the term “polymer compound” or “resin” refers to a polymer having a molecular weight of 1000 or more.
In the case of a polymer compound, the “molecular weight” is a polystyrene-equivalent mass average molecular weight measured by GPC (gel permeation chromatography).

In the present invention, the component (A ′) includes a structural unit (a5) containing a group represented by the general formula (a5-10), and an atom or substituent other than a hydrogen atom bonded to the α-position carbon atom. A structural unit derived from an acrylate ester which may be contained, a structural unit (a1) containing an acid-decomposable group whose polarity is increased by the action of an acid, and a structure represented by the general formula (a3-1) A resin component (A1 ′) having a unit (a3) (hereinafter referred to as “(A1 ′) component”) is contained.
Since the component (A1 ′) has the structural unit (a5), an acid can be generated by exposure. Further, by having the structural unit (a1), the polarity increases due to the action of an acid (an acid generated from the structural unit (a5) or the like). Furthermore, the polarity of a resin component increases more by having a structural unit (a3).
In addition to the structural units (a5), (a1), and (a3), the component (A1 ′) is an acrylic acid in which an atom other than a hydrogen atom or a substituent may be further bonded to the α-position carbon atom. It is preferable to have a structural unit (a0) that is a structural unit derived from an ester and includes a —SO ₂ — containing cyclic group.
The component (A1 ′) is added to the structural units (a5), (a1), and (a3), or to the structural units (a5), (a1), (a3), and (a0). And a structural unit (a2) that is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to the α-position carbon atom and includes a lactone-containing cyclic group It is preferable.

Here, in the present specification and claims, the “structural unit derived from an acrylate ester” means a structural unit formed by cleavage of an ethylenic double bond of an acrylate ester.
“Acrylic acid ester” refers to a compound in which the hydrogen atom at the terminal of the carboxy group of acrylic acid (CH ₂ ═CH—COOH) is substituted with an organic group.
In the “acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position”, examples of the atom other than a hydrogen atom include a halogen atom, and the substituent includes 1 carbon atom. -5 alkyl groups, C1-C5 halogenated alkyl groups, hydroxyalkyl groups, and the like.
The α-position carbon atom of the acrylate ester is a carbon atom to which a carbonyl group is bonded unless otherwise specified.
Hereinafter, an acrylate ester in which an atom other than a hydrogen atom or a substituent is bonded to the α-position carbon atom may be referred to as an “α-substituted acrylate ester”. Further, the acrylate ester and the α-substituted acrylate ester may be collectively referred to as “(α-substituted) acrylate ester”.
In the α-substituted acrylate ester, examples of the halogen atom that may be bonded to the α-position carbon atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
The alkyl group that may be bonded to the α-position carbon atom is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, Examples include isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like.
Further, the halogenated alkyl group that may be bonded to the α-position carbon atom specifically includes a part or all of the hydrogen atoms of the above-mentioned “alkyl group that may be bonded to the α-position carbon atom”. And a group substituted with a halogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
Further, the hydroxyalkyl group that may be bonded to the α-position carbon atom is a group in which a part or all of the hydrogen atoms of the “alkyl group that may be bonded to the α-position carbon atom” are substituted with a hydroxyl group. Can be mentioned.
Bonded to the α-position of the α-substituted acrylate ester is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, and a hydrogen atom having 1 to 5 carbon atoms. An alkyl group or a fluorinated alkyl group having 1 to 5 carbon atoms is more preferred, and a hydrogen atom or a methyl group is particularly preferred from the viewpoint of industrial availability.

[Structural unit (a5)]
The structural unit (a5) is a structural unit containing a group represented by the following general formula (a5-10).

［式中、Ｑは単結合又は２価の連結基であり、Ｒ^Ｘは水素原子、フッ素原子、アルキル基、又はフッ素化アルキル基であり、ｐは１〜１０の整数である。Ａ^＋は有機カチオンである。］

[Wherein, Q is a single bond or a divalent linking group, R ^X is a hydrogen atom, a fluorine atom, an alkyl group, or a fluorinated alkyl group, and p is an integer of 1 to 10. A ⁺ is an organic cation. ]

In said formula (a5-10), Q is a single bond or a bivalent coupling group.
Examples of the divalent linking group for Q include an alkylene group and a group containing a hetero atom (hereinafter referred to as “hetero atom-containing linking group”).
The “hetero atom” in the hetero atom-containing linking group is an atom other than a carbon atom and a hydrogen atom, and examples thereof include an oxygen atom, a sulfur atom, and a nitrogen atom.

The alkylene group for Q may be linear or branched, and the alkylene group preferably has 1 to 12 carbon atoms, more preferably 1 to 5 carbon atoms, and 1 to 3 carbon atoms. Particularly preferred.
Specific examples of the alkylene group include a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ) ₂ —, —C ( _{CH 3) (CH 2 CH 3} ) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene group _[-CH 2 CH _2— ]; —CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH ₃ ) CH ₂ —, Alkylethylene groups such as —CH (CH ₂ CH ₃ ) CH ₂ —; trimethylene group (n-propylene group) [—CH ₂ CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ CH ₂ —, —CH _{2 CH (CH 3) CH 2} - alkyl trimethylene group and the like; Toramechiren group _{[-CH 2 CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 CH 2 - alkyl tetramethylene group and the like; penta And methylene group [—CH ₂ CH ₂ CH ₂ CH ₂ CH ₂ —] and the like.

Examples of the hetero atom-containing linking group in Q include an oxygen atom (ether bond; —O—), a sulfur atom (thioether bond; —S—), a —NH— bond (H is an alkyl group, an acyl group, etc.) Group (which may be substituted with a group), an ester bond (—C (═O) —O—), an amide bond (—C (═O) —NH—), a carbonyl group (—C (═O) —), Non-hydrocarbon hetero atom-containing linking groups such as carbonate bonds (—O—C (═O) —O—); combinations of the non-hydrocarbon hetero atom-containing linking groups and the alkylene groups, and the like.
Examples of the combination include —R ⁹¹ —O—, —R ⁹² —O—C (═O) — (wherein R ⁹¹ and R ⁹² are each independently an alkylene group). As the alkylene group for R ⁹¹ and R ^92, the same alkylene groups as those described above for Q can be used.

  Among the above, Q is preferably an alkylene group.

In the formula (a5-10), R ^X represents a hydrogen atom, a fluorine atom, an alkyl group, or a fluorinated alkyl group.
In particular, it is preferable that R ^X is a fluorine atom or a fluorinated alkyl group because the strength of the acid generated is increased.
Alkyl group in R ^X preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms.
^Examples of the fluorinated alkyl group for R ^X include groups in which part or all of the hydrogen atoms of the alkyl group for R ^X have been substituted with fluorine atoms. The fluorination rate of the fluorinated alkyl group (the ratio of the number of fluorine atoms to the total number of fluorine atoms and hydrogen atoms (%)) is preferably 50 to 100%, more preferably 80 to 100%, and more preferably 85 to 100 % Is more preferable.
Any of the alkyl group or the fluorinated alkyl group in R ^X may have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group for the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and more preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group of the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group. A group and an ethoxy group are particularly preferred.
Examples of the halogen atom for the substituent include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom, and a fluorine atom is preferred.
Examples of the halogenated alkyl group for the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

In said formula (a5-10), p is an integer of 1-10. Especially, it is more preferable that p is an integer of 1-4, and it is especially preferable that it is 1 or 2.
The portion of “R ^X — (CF ₂ ) _p —SO ₂ —” in which p is an integer of 1 to 4 is decomposable, for example, while a perfluoroalkyl chain having 6 to 10 carbon atoms is hardly decomposable. Is good, and the effect that the handleability considering the bioaccumulation property is further improved is also obtained.

In the formula (a5-10), A ⁺ is an organic cation.
Examples of the A ⁺ organic cation include a sulfonium ion, an iodonium ion, a phosphonium ion, a diazonium ion, an ammonium ion, and a pyridinium ion.
Especially, the cation part of the onium salt type | system | group acid generator quoted by description of (B) component mentioned later is preferable, and specifically, the onium represented by the general formula (b-1) or (b-2) mentioned later. A sulfonium ion represented by a cation part (S ⁺ (R ¹ ″) (R ² ″) (R ³ ″) or an iodonium represented by I ⁺ (R ⁵ ″) (R ⁶ ″) of a salt-based acid generator And the same as the cation represented by formulas (b-5) to (b-8).
Among these, a sulfonium ion represented by S ⁺ (R ¹ ″) (R ² ″) (R ³ ″) is preferable, and at least one of R ¹ ″ to R ³ ″ has a substituent. Those which may be aryl groups are more preferable, and all of R ¹ ″ to R ³ ″ are particularly preferably aryl groups which may have a substituent.

  Specific examples of the group represented by formula (a5-10) are shown below.

  As the structural unit (a5) containing a group represented by the general formula (a5-10), the following general formula (a5-1) is particularly preferable in terms of polymerizability, lithography characteristics, ease of synthesis, and the like. The structural unit represented is preferred.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基であり、Ｑは単結合又は２価の連結基であり、Ｒ^Ｘは水素原子、フッ素原子、アルキル基、又はフッ素化アルキル基であり、ｐは１〜１０の整数である。Ａ^＋は有機カチオンである。］

[Wherein, R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, Q is a single bond or a divalent linking group, and R ^X is a hydrogen atom. , A fluorine atom, an alkyl group, or a fluorinated alkyl group, and p is an integer of 1 to 10. A ⁺ is an organic cation. ]

In said formula (a5-1), R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group.
The alkyl group for R is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, A pentyl group, an isopentyl group, a neopentyl group, etc. are mentioned.
Examples of the halogenated alkyl group for R include groups in which some or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms have been substituted with halogen atoms. Specific examples of the alkyl group include the same alkyl groups as those described above for R. Examples of the halogen atom that replaces the hydrogen atom of the alkyl group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
As R, a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms is more preferable, and a hydrogen atom or a methyl group is most preferable in terms of industrial availability.
Wherein ^{(a5-1), Q, R X} , p, A + is, ^Q of the formula (a5-10) in the same R X, p, ^{A +} respectively.

As the structural unit (a5) contained in the component (A1 ′), 1 type of structural unit may be used, or 2 or more types may be used.
In the component (A1 ′), the proportion of the structural unit (a5) is preferably 1 to 50 mol%, more preferably 1 to 40 mol%, based on all structural units constituting the component (A1 ′). More preferred is mol%.
By setting it to the lower limit value or more, a pattern can be easily obtained when a resist composition is obtained, and lithography properties such as sensitivity, resolution, and LWR are also improved. Moreover, the balance with another structural unit can be taken by making it below an upper limit.

[Structural unit (a1)]
The structural unit (a1) is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and the acid decomposition whose polarity is increased by the action of an acid A structural unit containing a sex group.

The “acid-decomposable group” has acid-decomposability that at least a part of bonds in the structure of the acid-decomposable group can be cleaved by the action of an acid (an acid generated from the structural unit (a5) by exposure). It is a group.
Examples of the acid-decomposable group whose polarity increases by the action of an acid include a group that decomposes by the action of an acid to generate a polar group.
Examples of the polar group include a carboxy group, a hydroxyl group, an amino group, a sulfo group (—SO ₃ H), and the like. Among these, a polar group containing —OH in the structure (hereinafter sometimes referred to as “OH-containing polar group”) is preferable, a carboxy group or a hydroxyl group is preferable, and a carboxy group is particularly preferable.
More specifically, examples of the acid-decomposable group include a group in which the polar group is protected with an acid-dissociable group (for example, a group in which a hydrogen atom of an OH-containing polar group is protected with an acid-dissociable group).
The “acid-dissociable group” means that at least a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group is generated by the action of an acid (an acid generated from the structural unit (a5) by exposure). It is a group having acid dissociability that can be cleaved. The acid-dissociable group constituting the acid-decomposable group must be a group having a lower polarity than the polar group generated by dissociation of the acid-dissociable group. Is dissociated, a polar group having a polarity higher than that of the acid dissociable group is generated to increase the polarity. As a result, the polarity of the entire component (A1 ′) increases. As the polarity increases, the solubility in the developer changes relatively. When the developer is an alkaline developer, the solubility increases. On the other hand, the developer contains an organic solvent (organic type). In the case of a developer, the solubility decreases.

The acid-dissociable group is not particularly limited, and those that have been proposed as acid-dissociable groups for base resins for chemically amplified resists can be used. In general, a group that forms a cyclic or chain tertiary alkyl ester with a carboxy group in (meth) acrylic acid or the like; an acetal-type acid dissociable group such as an alkoxyalkyl group is widely known.
Here, the “tertiary alkyl ester” is an ester formed by replacing a hydrogen atom of a carboxy group with a chain or cyclic alkyl group, and the carbonyloxy group (—C (═O The structure in which the tertiary carbon atom of the chain or cyclic alkyl group is bonded to the terminal oxygen atom of) -O-). In this tertiary alkyl ester, when an acid acts, a bond is cut between an oxygen atom and a tertiary carbon atom to form a carboxy group.
The chain or cyclic alkyl group may have a substituent.
Hereinafter, a group that is acid dissociable by constituting a carboxy group and a tertiary alkyl ester is referred to as a “tertiary alkyl ester type acid dissociable group” for convenience.

Examples of the tertiary alkyl ester type acid dissociable group include an aliphatic branched acid dissociable group and an acid dissociable group containing an aliphatic cyclic group.
Here, “aliphatic branched” means having a branched structure having no aromaticity. The structure of the “aliphatic branched acid dissociable group” is not limited to a group consisting of carbon and hydrogen (hydrocarbon group), but is preferably a hydrocarbon group. The “hydrocarbon group” may be either saturated or unsaturated, but is usually preferably saturated.
Examples of the aliphatic branched acid dissociable group include a group represented by —C (R ⁷¹ ) (R ⁷² ) (R ⁷³ ). ^Wherein, R 71 ^{to R 73} each independently represents a linear alkyl group of 1 to 5 carbon atoms. The group represented by —C (R ⁷¹ ) (R ⁷² ) (R ⁷³ ) preferably has 4 to 8 carbon atoms, specifically a tert-butyl group or a 2-methyl-2-butyl group. , 2-methyl-2-pentyl group, 3-methyl-3-pentyl group and the like. A tert-butyl group is particularly preferable.

The “aliphatic cyclic group” means a monocyclic group or a polycyclic group having no aromaticity.
The aliphatic cyclic group in the “acid-dissociable group containing an aliphatic cyclic group” may or may not have a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, an oxygen atom (= O), and the like. Is mentioned.
The basic ring structure excluding the substituent of the aliphatic cyclic group is not limited to a group consisting of carbon and hydrogen (hydrocarbon group), but is preferably a hydrocarbon group. The hydrocarbon group may be either saturated or unsaturated, but is usually preferably saturated.
The aliphatic cyclic group may be monocyclic or polycyclic.
Examples of the aliphatic cyclic group include one or more hydrogens from a monocycloalkane which may or may not be substituted with an alkyl group having 1 to 5 carbon atoms, a fluorine atom or a fluorinated alkyl group. A group in which one or more hydrogen atoms have been removed from a polycycloalkane such as bicycloalkane, tricycloalkane, or tetracycloalkane; More specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane; one or more polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. An alicyclic hydrocarbon group such as a group excluding a hydrogen atom is exemplified. Moreover, a part of carbon atoms constituting the ring of these alicyclic hydrocarbon groups may be substituted with an ether group (—O—).

Examples of the acid dissociable group containing an aliphatic cyclic group include:
(I) On the ring skeleton of the monovalent aliphatic cyclic group, the substituent ( An atom or group other than a hydrogen atom) to form a tertiary carbon atom;
(Ii) a group having a monovalent aliphatic cyclic group and a branched alkylene having a tertiary carbon atom bonded thereto.
In the group (i), examples of the substituent bonded to the carbon atom bonded to the atom adjacent to the acid dissociable group on the ring skeleton of the aliphatic cyclic group include an alkyl group. Examples of the alkyl group include those similar to R ¹⁴ in formulas (1-1) to (1-9) described later.
Specific examples of the group (i) include groups represented by the following general formulas (1-1) to (1-9).
Specific examples of the group (ii) include groups represented by the following general formulas (2-1) to (2-6).

［式中、Ｒ^１４はアルキル基であり、ｇは０〜８の整数である。］

[Wherein, R ¹⁴ represents an alkyl group, and g represents an integer of 0 to 8. ]

［式中、Ｒ^１５およびＲ^１６は、それぞれ独立してアルキル基である。］

[Wherein, R ¹⁵ and R ¹⁶ each independently represents an alkyl group. ]

In formulas (1-1) to (1-9), the alkyl group of R ¹⁴ may be linear, branched or cyclic, and is preferably linear or branched.
The linear alkyl group preferably has 1 to 5 carbon atoms, more preferably 1 to 4, and still more preferably 1 or 2. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, and an n-pentyl group. Among these, a methyl group, an ethyl group, or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.
The branched alkyl group preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include isopropyl group, isobutyl group, tert-butyl group, isopentyl group, neopentyl group and the like, and isopropyl group is most preferable.
g is preferably an integer of 0 to 3, more preferably an integer of 1 to 3, and still more preferably 1 or 2.
In formulas (2-1) to (2-6), examples of the alkyl group for R ^{15 to} R ¹⁶ include the same alkyl groups as those described above for R ¹⁴ .
In the formulas (1-1) to (1-9) and (2-1) to (2-6), a part of the carbon atoms constituting the ring is substituted with an etheric oxygen atom (—O—). May be.
In formulas (1-1) to (1-9) and (2-1) to (2-6), a hydrogen atom bonded to a carbon atom constituting the ring may be substituted with a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorine atom, and a fluorinated alkyl group.

The “acetal-type acid dissociable group” is generally bonded to an oxygen atom by substituting a hydrogen atom at the terminal of an OH-containing polar group such as a carboxy group or a hydroxyl group. Then, when an acid is generated by exposure, this acid acts to break the bond between the acetal type acid dissociable group and the oxygen atom to which the acetal type acid dissociable group is bonded, and a carboxy group, a hydroxyl group, etc. OH-containing polar groups are formed.
Examples of the acetal type acid dissociable group include a group represented by the following general formula (p1).

［式中、Ｒ^１’，Ｒ^２’はそれぞれ独立して水素原子または炭素数１〜５のアルキル基を表し、ｎは０〜３の整数を表し、Ｙは炭素数１〜５のアルキル基または脂肪族環式基を表す。］

[Wherein, R ¹ 'and R ² ' each independently represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, n represents an integer of 0 to 3, and Y represents an alkyl group having 1 to 5 carbon atoms. Or represents an aliphatic cyclic group. ]

In formula (p1), n is preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 0.
Examples of the alkyl group for R ¹ ′ and R ² ′ include the same alkyl groups listed as the substituents that may be bonded to the α-position carbon atom in the description of the α-substituted acrylate ester. A methyl group or an ethyl group is preferred, and a methyl group is most preferred.
In the present invention, at least one of ¹ ′ and R ² ′ is preferably a hydrogen atom. That is, the acid dissociable group (p1) is preferably a group represented by the following general formula (p1-1).

［式中、Ｒ^１’、ｎ、Ｙは上記と同じである。］

[Wherein R ¹ ′, n and Y are the same as described above. ]

Examples of the alkyl group for Y include the same alkyl groups as those described above for the substituent that may be bonded to the carbon atom at the α-position in the description of the α-substituted acrylate ester.
The aliphatic cyclic group for Y can be appropriately selected from monocyclic or polycyclic aliphatic cyclic groups that have been proposed in a number of conventional ArF resists. For example, the above “aliphatic ring” Examples thereof are the same as the aliphatic cyclic groups mentioned in “Acid-dissociable groups containing formula groups”.

  Examples of the acetal type acid dissociable group also include a group represented by the following general formula (p2).

［式中、Ｒ^１７、Ｒ^１８はそれぞれ独立して直鎖状若しくは分岐鎖状のアルキル基または水素原子であり；Ｒ^１９は直鎖状、分岐鎖状若しくは環状のアルキル基である。または、Ｒ^１７およびＲ^１９がそれぞれ独立に直鎖状若しくは分岐鎖状のアルキレン基であって、Ｒ^１７の末端とＲ^１９の末端とが結合して環を形成していてもよい。］

[Wherein, R ¹⁷ and R ¹⁸ each independently represents a linear or branched alkyl group or a hydrogen atom; and R ¹⁹ represents a linear, branched or cyclic alkyl group. Alternatively, R ¹⁷ and R ¹⁹ may be each independently a linear or branched alkylene group, and the end of R ^{17 and} the end of R ¹⁹ may be bonded to form a ring. ]

In R ¹⁷ and R ¹⁸ , the alkyl group preferably has 1 to 15 carbon atoms, may be linear or branched, and is preferably an ethyl group or a methyl group, and most preferably a methyl group.
In particular, it is preferable that one of R ¹⁷ and R ¹⁸ is a hydrogen atom and the other is a methyl group.
R ¹⁹ is a linear, branched or cyclic alkyl group, preferably having 1 to 15 carbon atoms, and may be any of linear, branched or cyclic.
When R ¹⁹ is linear or branched, it preferably has 1 to 5 carbon atoms, more preferably an ethyl group or a methyl group, and most preferably an ethyl group.
When R ¹⁹ is cyclic, it preferably has 4 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, one or more polycycloalkanes such as monocycloalkane, bicycloalkane, tricycloalkane, and tetracycloalkane, which may or may not be substituted with a fluorine atom or a fluorinated alkyl group. And the like, in which a hydrogen atom is removed. Specific examples include monocycloalkanes such as cyclopentane and cyclohexane, and groups obtained by removing one or more hydrogen atoms from polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.
In the formula (p2), R ¹⁷ and R ¹⁹ are each independently a linear or branched alkylene group (preferably an alkylene group having 1 to 5 carbon atoms), and the end of R ¹⁹ is The terminal of R ¹⁷ may be bonded.
In this case, a cyclic group is formed by R ¹⁷ , R ¹⁹ , the oxygen atom to which R ¹⁹ is bonded, and the carbon atom to which the oxygen atom and R ¹⁷ are bonded. The cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

  More specifically, examples of the structural unit (a1) include structural units represented by general formula (a1-0-1) shown below, structural units represented by general formula (a1-0-2) shown below, and the like. .

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり；Ｘ^１は酸解離性基であり；Ｙ^２は２価の連結基であり；Ｘ^２は酸解離性基である。］

Wherein R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms; X ¹ is an acid dissociable group; Y ² is a divalent linking group. Yes; X ² is an acid-dissociable group. ]

In general formula (a1-0-1), the alkyl group and the halogenated alkyl group of R are each exemplified as the substituent that may be bonded to the carbon atom at the α-position in the description of the α-substituted acrylate ester. And the same alkyl groups and halogenated alkyl groups. R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms, and most preferably a hydrogen atom or a methyl group.
X ¹ is not particularly limited as long as it is an acid dissociable group, and examples thereof include the above-described tertiary alkyl ester type acid dissociable groups, acetal type acid dissociable groups, and the like. An ester type acid dissociable group is preferred.
In general formula (a1-0-2), R is the same as defined above.
X ² is the same as X ¹ in formula (a1-0-1).

Examples of the divalent linking group of Y ^2, but are not limited to, divalent hydrocarbon group which may have a substituent group, and a divalent linking group containing a hetero atom as preferred.
The hydrocarbon group having “substituent” means that part or all of the hydrogen atoms in the hydrocarbon group are substituted with a substituent (a group or atom other than a hydrogen atom).
The hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.
An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity.
The aliphatic hydrocarbon group as the divalent hydrocarbon group in A may be saturated or unsaturated, and is usually preferably saturated.
More specific examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like.

The linear or branched aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, more preferably 1 to 4, and most preferably 1 to 3.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.
The linear or branched aliphatic hydrocarbon group may or may not have a substituent. Examples of the substituent include a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and an oxygen atom (═O).

Examples of the aliphatic hydrocarbon group containing a ring in the structure include an alicyclic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and an alicyclic hydrocarbon group that is linear or branched. Examples thereof include a group bonded to the end of a chain aliphatic hydrocarbon group and a group in which an alicyclic hydrocarbon group is interposed in the middle of a linear or branched aliphatic hydrocarbon group. Examples of the linear or branched aliphatic hydrocarbon group include those described above.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.
The alicyclic hydrocarbon group may or may not have a substituent. Examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, and an oxygen atom (= O).

The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring.
The aromatic hydrocarbon group as the divalent hydrocarbon group in A preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, still more preferably 5 to 20 carbon atoms, and 6 to 15 carbon atoms. Is particularly preferable, and 6 to 10 is most preferable. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic ring possessed by the aromatic hydrocarbon group include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene; some of the carbon atoms constituting the aromatic hydrocarbon ring are heterogeneous. Aromatic heterocycles substituted with atoms; and the like. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group is a group obtained by removing two hydrogen atoms from the aromatic hydrocarbon ring (arylene group); a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring (aryl group) ) In which one of the hydrogen atoms is substituted with an alkylene group (for example, arylalkyl such as benzyl, phenethyl, 1-naphthylmethyl, 2-naphthylmethyl, 1-naphthylethyl, 2-naphthylethyl, etc.) Group obtained by further removing one hydrogen atom from the aryl group in the group); and the like. The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.
The aromatic hydrocarbon group may or may not have a substituent. For example, a hydrogen atom bonded to the aromatic hydrocarbon ring of the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

The hetero atom in the “divalent linking group containing a hetero atom” is an atom other than a carbon atom and a hydrogen atom, and examples thereof include an oxygen atom, a nitrogen atom, a sulfur atom, and a halogen atom.
As the divalent linking group containing a hetero atom, —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O—, —C (= O) —NH—, —NH— (H may be substituted with a substituent such as an alkyl group, an acyl group, etc.), —S—, —S (═O) ₂ —, —S (═O) _{2 -O -, - NH-C} (= O) -, = N-, the formula ^{-Y 21 -O-Y 22 -,} - [Y 21 -C (= O) -O] m '-Y 22 - Or a group represented by —Y ²¹ —O—C (═O) —Y ²² —, wherein Y ²¹ and Y ²² are each independently a divalent hydrocarbon group optionally having a substituent. O is an oxygen atom, and m ′ is an integer of 0 to 3. ] Etc. are mentioned.
When Y ² is —NH—, H may be substituted with a substituent such as an alkyl group or an aryl group (aromatic group). The substituent (alkyl group, aryl group, etc.) preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and particularly preferably 1 to 5 carbon atoms.
Formula ^{-Y 21 -O-Y 22 -,} - [Y 21 -C (= O) -O] m '-Y 22 - or ^{-Y 21 -O-C (= O} ) -Y 22 - ^{In, Y 21} And Y ²² are each independently a divalent hydrocarbon group which may have a substituent. Examples of the divalent hydrocarbon group include the same groups as those described above as the “divalent hydrocarbon group which may have a substituent” for Y ² .
Y ²¹ is preferably a linear aliphatic hydrocarbon group, more preferably a linear alkylene group, still more preferably a linear alkylene group having 1 to 5 carbon atoms, and particularly preferably a methylene group or an ethylene group. preferable.
Y ²² is preferably a linear or branched aliphatic hydrocarbon group, and more preferably a methylene group, an ethylene group or an alkylmethylene group. The alkyl group in the alkylmethylene group is preferably a linear alkyl group having 1 to 5 carbon atoms, more preferably a linear alkyl group having 1 to 3 carbon atoms, and most preferably a methyl group.
In the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² —, m ′ is an integer of 0 to 3, preferably an integer of 0 to 2, Or 1 is more preferable, and 1 is particularly preferable. That is, the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² — is represented by the formula —Y ²¹ —C (═O) —O—Y ²² —. The group is particularly preferred. Among these, a group represented by the formula — (CH ₂ ) _{a ′} —C (═O) —O— (CH ₂ ) _{b ′} — is preferable. In the formula, a ′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, further preferably 1 or 2, and most preferably 1. b ′ is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, more preferably 1 or 2, and most preferably 1.
Examples of the divalent linking group containing a hetero atom, a linear group containing an oxygen atom as a hetero atom, for example, a group containing an ether bond or an ester bond, are preferred, the formula -Y 21 ^-O-Y 22 ^-, A group represented by — [Y ²¹ —C (═O) —O] _{m ′} —Y ²² — or —Y ²¹ —O—C (═O) —Y ²² — is more preferable.

Among these, as the divalent linking group for Y ² , in particular, a linear or branched alkylene group, a divalent alicyclic hydrocarbon group, or a divalent linking group containing a hetero atom is included. preferable. Among these, a linear or branched alkylene group or a divalent linking group containing a hetero atom is preferable.

  More specifically, examples of the structural unit (a1) include structural units represented by the following general formulas (a1-1) to (a1-4).

［式中、Ｒ、Ｒ^１’、Ｒ^２’、ｎ、ＹおよびＹ^２はそれぞれ前記と同じであり、Ｘ’は第３級アルキルエステル型酸解離性基を表す。］’

[Wherein, R, R ¹ ′, R ² ′, n, Y and Y ² are the same as defined above, and X ′ represents a tertiary alkyl ester-type acid dissociable group. ] '

In the formula, X ′ is the same as the tertiary alkyl ester-type acid dissociable group.
^{R 1 ', R 2',} n, as the Y, respectively, ^{R 1} in the general formula listed in the description of "acetal-type acid dissociable group" described above ^{(p1) ', R 2'} , n, similarly to the Y Can be mentioned.
The Y ^2, the same groups as those described above for ^{Y 2} in the general formula (a1-0-2).
Specific examples of the structural units represented by the general formulas (a1-1) to (a1-4) are shown below.
In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

In the present invention, as the structural unit (a1), a structural unit represented by the following general formula (a1-0-11), a structural unit represented by the following general formula (a1-0-12), and the following general formula ( a1-0-13), a structural unit represented by the following general formula (a1-0-14), a structural unit represented by the following general formula (a1-0-15), and the following general unit It is preferable to have at least one selected from the group consisting of structural units represented by formula (a1-0-2).
Especially, the structural unit represented by the following general formula (a1-0-11), the structural unit represented by the following general formula (a1-0-12), and the following general formula (a1-0-13) And at least one selected from the group consisting of structural units represented by the following general formula (a1-0-14) and structural units represented by the following general formula (a1-0-15) It is more preferable.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり、Ｒ^２１はアルキル基であり；Ｒ^２２は、当該Ｒ^２２が結合した炭素原子と共に脂肪族単環式基を形成する基であり；Ｒ^２３は分岐鎖状のアルキル基であり；Ｒ^２４は、当該Ｒ^２４が結合した炭素原子と共に脂肪族多環式基を形成する基であり；Ｒ^２５は炭素数１〜５の直鎖状のアルキル基である。Ｒ^１５およびＲ^１６は、それぞれ独立してアルキル基である。Ｙ^２は２価の連結基であり、Ｘ^２は酸解離性基である。］

Wherein R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, R ²¹ is an alkyl group; R ²² is a carbon to which R ²² is bonded. A group that forms an aliphatic monocyclic group together with an atom; R ²³ is a branched alkyl group; and R ²⁴ is a group that forms an aliphatic polycyclic group together with the carbon atom to which R ²⁴ is bonded. R ²⁵ is a linear alkyl group having 1 to 5 carbon atoms. R ¹⁵ and R ¹⁶ are each independently an alkyl group. Y ² is a divalent linking group, and X ² is an acid dissociable group. ]

In each formula, the description of R, Y ² and X ² is the same as described above.
In formula (a1-0-11), examples of the alkyl group for R ²¹ include the same alkyl groups as those described above for R ¹⁴ in formulas (1-1) to (1-9). Group or isopropyl group is preferred.
R ²² is, the aliphatic monocyclic group formed together with the carbon atom to which R ²² is bonded, the same aliphatic cyclic groups as those in the aforementioned tertiary alkyl ester-type acid dissociable groups, a monocyclic group The thing similar to what is is mentioned. Specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably a 3- to 11-membered ring, more preferably a 3- to 8-membered ring, further preferably a 4- to 6-membered ring, and particularly preferably a 5- or 6-membered ring.
In the monocycloalkane, a part of carbon atoms constituting the ring may or may not be substituted with an ether group (—O—).
Moreover, this monocycloalkane may have a C1-C5 alkyl group, a fluorine atom, or a C1-C5 fluorinated alkyl group as a substituent.
Examples of R ²² constituting such an aliphatic monocyclic group include a linear alkylene group in which an ether group (—O—) may be interposed between carbon atoms.

Specific examples of the structural unit represented by the formula (a1-0-11) include the formulas (a1-1-16) to (a1-1-23), (a1-1-27), and (a1-1 -31). Among these, the formulas (a1-1-16) to (a1-1-17), (a1-1-20) to (a1-1-23), (a1-1-27), (a1-1-1- The structural unit represented by the following (a1-1-02) including the structural units represented by 31), (a1-1-32), and (a1-1-33) is preferable. Moreover, the structural unit represented by the following (a1-1-02 ′) is also preferable.
In each formula, h is an integer of 1 to 4, and 1 or 2 is preferable.

［式中、Ｒ、Ｒ^２１はそれぞれ前記と同じであり、ｈは１〜４の整数である。］

[Wherein, R and R ²¹ are the same as defined above, and h is an integer of 1 to 4. ]

In formula (a1-0-12), as the branched alkyl group for R ²³ , the branched alkyl group described for the alkyl group for R ¹⁴ in formulas (1-1) to (1-9) above. Examples thereof are the same as those described above, and an isopropyl group is most preferable.
R ²⁴ is, the aliphatic polycyclic group formed together with the carbon atom to which R ²⁴ is bonded, the same aliphatic cyclic groups as those in the aforementioned tertiary alkyl ester-type acid dissociable group, polycyclic group The thing similar to what is is mentioned.
Specific examples of the structural unit represented by the formula (a1-0-12) include those represented by the formulas (a1-1-26) and (a1-1-28) to (a1-1-30). Units are listed.
As the structural unit represented by the formula (a1-0-12), those in which R ²⁴ is an aliphatic polycyclic group formed together with the carbon atom to which R ²⁴ is bonded are preferably a 2-adamantyl group, The structural unit represented by the formula (a1-1-26) is preferable.

In formula (a1-0-13), R and R ²⁴ are the same as defined above.
Examples of the linear alkyl group for R ²⁵ include the same linear alkyl groups as those described above for the alkyl group for R ^{14 in} the formulas (1-1) to (1-9), and methyl Most preferred are groups or ethyl groups.
Specific examples of the structural unit represented by the formula (a1-0-13) include formulas (a1-1-1) to (a1-1-2) exemplified as specific examples of the general formula (a1-1). ), Structural units represented by (a1-1-7) to (a1-1-15).
As the structural unit represented by the formula (a1-0-13), those in which R ²⁴ is an aliphatic polycyclic group formed together with the carbon atom to which R ²⁴ is bonded are preferably a 2-adamantyl group, The structural unit represented by the formula (a1-1-1) or (a1-1-2) is preferable.

In formula (a1-0-14), R and R ²² are the same as defined above. R ¹⁵ and ^{R 16} are the same as ^{R 15} and ^{R 16} in each of the general formulas (2-1) to (2-6).
Specific examples of the structural unit represented by the formula (a1-0-14) include the formulas (a1-1-35) and (a1-1-36) exemplified as specific examples of the general formula (a1-1). ).

In formula (a1-0-15), R and R ²⁴ are the same as defined above. R ¹⁵ and ^{R 16} are the same as ^{R 15} and ^{R 16} in each of the general formulas (2-1) to (2-6).
Specific examples of the structural unit represented by formula (a1-0-15) include formulas (a1-1-4) to (a1-1-6) exemplified as specific examples of general formula (a1-1). ) And (a1-1-34).

Examples of the structural unit represented by the formula (a1-0-2) include the structural unit represented by the formula (a1-3) or (a1-4), and particularly represented by the formula (a1-3). Are preferred.
As the structural unit represented by the formula (a1-0-2), in particular, Y ^{2 in} the formula is the aforementioned —Y ²¹ —O—Y ²² — or —Y ²¹ —C (═O) —O—Y ^22. Those represented by-are preferred.
Preferred examples of the structural unit include a structural unit represented by the following general formula (a1-3-01); a structural unit represented by the following general formula (a1-3-02); 3-03) and the like.

［式中、Ｒは前記と同じであり、Ｒ^１３は水素原子またはメチル基であり、Ｒ^１４はアルキル基であり、ｙは１〜１０の整数であり、ｎ’は０〜３の整数である。］

[Wherein, R is the same as above, R ¹³ is a hydrogen atom or a methyl group, R ¹⁴ is an alkyl group, y is an integer of 1 to 10, and n ′ is an integer of 0 to 3] is there. ]

［式中、Ｒは前記と同じであり、Ｙ^２’およびＹ^２”はそれぞれ独立して２価の連結基であり、Ｘ’は酸解離性基であり、ｗは０〜３の整数である。］

[Wherein, R is as defined above, Y ² ′ and Y ² ″ are each independently a divalent linking group, X ′ is an acid-dissociable group, and w is an integer of 0 to 3] is there.]

In formulas (a1-3-01) to (a1-3-02), R ¹³ is preferably a hydrogen atom.
R ¹⁴ is the same as ^{R 14} in the formula (1-1) to (1-9).
y is preferably an integer of 1 to 8, more preferably an integer of 1 to 5, and most preferably 1 or 2.
n ′ is preferably 1 or 2, and most preferably 2.
Specific examples of the structural unit represented by the formula (a1-3-01) include structural units represented by the formulas (a1-3-25) to (a1-3-26).
Specific examples of the structural unit represented by the formula (a1-3-02) include structural units represented by the formulas (a1-3-27) to (a1-3-28).

In formula (a1-3-03), examples of the divalent linking group for Y ² ′ and Y ² ″ include the same groups as those described above for Y ² in formula (a1-3).
Y ² ′ is preferably a divalent hydrocarbon group which may have a substituent, more preferably a linear aliphatic hydrocarbon group, and even more preferably a linear alkylene group. Among these, a linear alkylene group having 1 to 5 carbon atoms is preferable, and a methylene group and an ethylene group are most preferable.
Y ² ″ is preferably a divalent hydrocarbon group which may have a substituent, more preferably a linear aliphatic hydrocarbon group, and still more preferably a linear alkylene group. A linear alkylene group of 1 to 5 is preferable, and a methylene group and an ethylene group are most preferable.
Examples of the acid dissociable group in X ′ include the same groups as described above, and are preferably tertiary alkyl ester-type acid dissociable groups, and the ring skeleton of the above-described (i) monovalent aliphatic cyclic group In addition, a group in which a substituent is bonded to a carbon atom bonded to an atom adjacent to the acid dissociable group to form a tertiary carbon atom is more preferable, and among them, the group represented by the general formula (1-1) is preferable. Preferred are the groups
w is an integer of 0 to 3, and w is preferably an integer of 0 to 2, more preferably 0 or 1, and most preferably 1.
As the structural unit represented by the formula (a1-3-03), a structural unit represented by the following general formula (a1-3-03-1) or (a1-3-03-2) is preferable. The structural unit represented by the formula (a1-3-03-1) is preferable.

［式中、ＲおよびＲ^１４はそれぞれ前記と同じであり、ａ’は１〜１０の整数であり、ｂ’は１〜１０の整数であり、ｔは０〜３の整数である。］

[Wherein, R and R ¹⁴ are the same as defined above, a ′ is an integer of 1 to 10, b ′ is an integer of 1 to 10, and t is an integer of 0 to 3, respectively. ]

In formulas (a1-3-03-1) to (a1-3-03-2), a ′ is preferably an integer of 1 to 8, more preferably an integer of 1 to 5, and particularly preferably 1 or 2.
b ′ is preferably an integer of 1 to 8, more preferably an integer of 1 to 5, and particularly preferably 1 or 2.
t is preferably an integer of 1 to 3, and 1 or 2 is particularly preferable.
Specific examples of the structural unit represented by formula (a1-3-03-1) or (a1-3-03-2) include those represented by formulas (a1-3-29) to (a1-3-32). The structural unit represented is mentioned.

As the structural unit (a1) contained in the component (A1 ′), 1 type of structural unit may be used, or 2 or more types may be used.
In particular, in the present invention, since the polarity is easily increased by the action of an acid and a high dissolution contrast is easily obtained with respect to an organic developer, the structural unit (a1) is a carbon atom at the α-position other than a hydrogen atom. It is preferable to contain 2 or more types of structural units derived from an acrylate ester to which any atom or substituent may be bonded, and containing a cyclic group-containing acid-decomposable group. The “cyclic group-containing acid-decomposable group” means a group having a cyclic group in the structure of the acid-decomposable group, and the cyclic group is a monocyclic group or a polycyclic group. May be. Those having a monocyclic group are called monocyclic group-containing acid-decomposable groups, and those having a polycyclic group are called polycyclic group-containing acid-decomposable groups.
Among them, as the structural unit containing the cyclic group-containing acid-decomposable group, since it is easy to balance the lithography properties, the structural unit containing the monocyclic group-containing acid-decomposable group and the polycyclic group-containing acid are included. A combination with a structural unit containing a degradable group is more preferred.
In addition, since a high contrast is easily obtained, a combination of a structural unit containing a polycyclic group-containing acid-decomposable group and a structural unit containing a polycyclic group-containing acid-decomposable group is more preferable.
In the component (A1 ′), the proportion of the structural unit (a1) is preferably from 15 to 70 mol%, more preferably from 15 to 60 mol%, more preferably from 20 to 55 mol, based on all structural units constituting the component (A1 ′). More preferred is mol%. By setting it to the lower limit value or more, a pattern can be easily obtained when a resist composition is obtained, and lithography properties such as sensitivity, resolution, and LWR are also improved. Moreover, the balance with another structural unit can be taken by making it below an upper limit.

[Structural unit (a3)]
The structural unit (a3) is a structural unit represented by the following general formula (a3-1).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基である。Ｐ^０は−Ｃ（＝Ｏ）−Ｏ−、−Ｃ（＝Ｏ）−ＮＲ^０−（Ｒ^０は水素原子又は炭素数１〜５のアルキル基である）又は単結合である。Ｗ^０は置換基として−ＯＨ、−ＣＯＯＨ、−ＣＮ、−ＳＯ_２ＮＨ_２及び−ＣＯＮＨ_２からなる群より選択される少なくとも一種の基を有する環状の炭化水素基であり、任意の位置に酸素原子又は硫黄原子を有していてもよい。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. P ⁰ is —C (═O) —O—, —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms) or a single bond. W ⁰ is a cyclic hydrocarbon group having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent, and oxygen at any position. You may have an atom or a sulfur atom. ]

In the formula (a3-1), the alkyl group of R is preferably a linear or branched alkyl group, specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, Examples include isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like.
Examples of the halogenated alkyl group for R include groups in which some or all of the hydrogen atoms of the aforementioned R alkyl group have been substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and particularly preferably a hydrogen atom or a methyl group.
In the formula (a3-1), P ⁰ is —C (═O) —O—, —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms. ) Or a single bond. The alkyl group for R ⁰ is the same as the alkyl group for R.

In the formula (a3-1), W ⁰ is a cyclic carbonization having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent. It is a hydrogen group and may have an oxygen atom or a sulfur atom at an arbitrary position.
The “cyclic hydrocarbon group having a substituent” means that at least a part of hydrogen atoms bonded to the cyclic hydrocarbon group is substituted with a substituent.
The cyclic hydrocarbon group for W ⁰ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.
The cyclic aliphatic hydrocarbon group for W ⁰ is an aliphatic cyclic group (monocyclic group or polycyclic group), or an aliphatic cyclic group having 1 carbon atom bonded to the aliphatic cyclic group. And a group consisting of 10 to 10 linear or branched hydrocarbon groups.
As the aliphatic cyclic group (monocyclic group, polycyclic group), for example, a resin for a resist composition for ArF excimer laser can be appropriately selected from those proposed. The aliphatic cyclic group preferably has 3 to 30 carbon atoms, more preferably 5 to 30, more preferably 5 to 20, particularly preferably 6 to 15, and most preferably 6 to 12. Specifically, for example, a group in which two or more hydrogen atoms have been removed from a monocycloalkane; a group in which two or more hydrogen atoms have been removed from a polycycloalkane such as bicycloalkane, tricycloalkane, tetracycloalkane, etc. Can be mentioned. More specifically, a group in which two or more hydrogen atoms are removed from a monocycloalkane such as cyclopentane or cyclohexane; two or more groups from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Examples include a group excluding a hydrogen atom. The aliphatic cyclic group may or may not have a substituent other than —OH, —COOH, —CN, —SO ₂ NH _2, and —CONH ₂ . As this substituent, a C1-C5 alkyl group, a fluorine atom, a C1-C5 fluorinated alkyl group, etc. are mentioned.

The aromatic hydrocarbon group for W ⁰ is a hydrocarbon group having an aromatic ring, preferably having 5 to 30 carbon atoms, more preferably 6 to 20, still more preferably 6 to 15, and particularly preferably 6 to 10 Is most preferred. However, the carbon number does not include the carbon number in the substituent.
The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n + 2 (where n is 0 and a natural number) π electrons, and may be monocyclic or polycyclic. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; aromatic heterocycles in which a part of carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms, and the like. Can be mentioned. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom. Specific examples of the aromatic heterocycle include a pyridine ring and a thiophene ring.
Specifically, the aromatic hydrocarbon group as the divalent hydrocarbon group is a group obtained by removing two hydrogen atoms from the aromatic hydrocarbon ring or aromatic heterocyclic ring (arylene group or heteroarylene group); A group in which two hydrogen atoms have been removed from an aromatic compound (for example, biphenyl, fluorene, etc.) containing one aromatic ring; a group in which one hydrogen atom has been removed from the aromatic hydrocarbon ring or aromatic heterocycle (aryl group or hetero group) A group in which one of the hydrogen atoms of the aryl group is substituted with an alkylene group (for example, a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group, a 2-naphthylethyl group, etc. And a group obtained by further removing one hydrogen atom from the aryl group in the arylalkyl group. The alkylene group bonded to the aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.
The aromatic hydrocarbon group may or may not have a substituent. For example, a hydrogen atom bonded to the aromatic hydrocarbon ring of the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

However, W ⁰ may have an oxygen atom or a sulfur atom at an arbitrary position. The phrase “may have an oxygen atom or a sulfur atom at any position” means a carbon atom constituting a hydrocarbon group or a hydrocarbon group having a substituent (including the carbon atom of the substituent portion). ) May be substituted with an oxygen atom or a sulfur atom, or a hydrogen atom bonded to a hydrocarbon group may be substituted with an oxygen atom or a sulfur atom.

The following is an example of W ⁰ having an oxygen atom (O) at an arbitrary position.

［式中、Ｗ^００は環状の炭化水素基であり、Ｒ^ｍは炭素数１〜５のアルキレン基である。］

[Wherein W ⁰⁰ is a cyclic hydrocarbon group, and R ^m is an alkylene group having 1 to 5 carbon atoms. ]

In the above formula, W ⁰⁰ is a cyclic hydrocarbon group, and examples thereof include the same cyclic hydrocarbon groups exemplified in the description of W ⁰ in the formula (a3-1). Among these, W ⁰⁰ is preferably a cyclic aliphatic hydrocarbon group, and more preferably an aliphatic cyclic group (monocyclic group or polycyclic group).
R ^m is preferably linear or branched, preferably an alkylene group having 1 to 3 carbon atoms, and more preferably a methylene group or an ethylene group.

  More preferable examples of the structural unit (a3) include structural units represented by any one of the following general formulas (a3-11) to (a3-13).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基である。Ｗ^０１は置換基として−ＯＨ、−ＣＯＯＨ、−ＣＮ、−ＳＯ_２ＮＨ_２及び−ＣＯＮＨ_２からなる群より選択される少なくとも一種の基を有する芳香族炭化水素基である。Ｐ^０２及びＰ^０３はそれぞれ−Ｃ（＝Ｏ）−Ｏ−又は−Ｃ（＝Ｏ）−ＮＲ^０−（Ｒ^０は水素原子又は炭素数１〜５のアルキル基である）である。Ｗ^０２は置換基として−ＯＨ、−ＣＯＯＨ、−ＣＮ、−ＳＯ_２ＮＨ_２及び−ＣＯＮＨ_２からなる群より選択される少なくとも一種の基を有する、脂肪族環式基又は芳香族炭化水素基であり、任意の位置に酸素原子又は硫黄原子を有していてもよい。Ｗ^０３は置換基として−ＯＨ、−ＣＯＯＨ、−ＣＮ、−ＳＯ_２ＮＨ_２及び−ＣＯＮＨ_２からなる群より選択される少なくとも一種の基を有する、脂肪族環式基と該脂肪族環式基に結合する鎖状の炭化水素基とからなる基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. W ⁰¹ is an aromatic hydrocarbon group having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent. P ⁰² and P ⁰³ are each —C (═O) —O— or —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms). W ⁰² is an aliphatic cyclic group or an aromatic hydrocarbon group having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent. Yes, it may have an oxygen atom or a sulfur atom at any position. W ⁰³ has at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent, and the aliphatic cyclic group. It is a group consisting of a chain-like hydrocarbon group bonded to. ]

(Structural unit represented by general formula (a3-11))
In the formula (a3-11), R is the same as described for R in the formula (a3-1).
The aromatic hydrocarbon group for W ⁰¹ is the same as that described for the aromatic hydrocarbon group for W ⁰ in formula (a3-1).
Specific examples of preferable structural units represented by general formula (a3-11) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

(Structural unit represented by general formula (a3-12))
In the formula (a3-12), R is the same as described for R in the formula (a3-1).
P ⁰² is —C (═O) —O— or —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms), and —C (═O ) -O-. The alkyl group for R ⁰ is the same as the alkyl group for R.
The aliphatic cyclic group and aromatic hydrocarbon group for W ⁰² are the aliphatic cyclic group (monocyclic group and polycyclic group) exemplified in the description of W ⁰ in the formula (a3-1). ) And aromatic hydrocarbon groups.
W ⁰² may have an oxygen atom or a sulfur atom at an arbitrary position, and this description is the same as the description of W ⁰ in the formula (a3-1).
Specific examples of preferred structural units represented by general formula (a3-12) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

(Structural unit represented by general formula (a3-13))
In the formula (a3-13), R is the same as described for R in the formula (a3-1).
P ⁰³ is —C (═O) —O— or —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms), and —C (═O ) -O-. The alkyl group for R ⁰ is the same as the alkyl group for R.
In W ⁰³ , —OH, —COOH, —CN, —SO ₂ NH ₂ or —CONH ₂ may be bonded only to one of an aliphatic cyclic group or a chain hydrocarbon group, and to both You may do it.
The aliphatic cyclic group in W ⁰³ is the same as the aliphatic cyclic group (monocyclic group or polycyclic group) exemplified in the description of W ⁰ in the formula (a3-1). Can be mentioned.
The chain hydrocarbon group in W ⁰³ preferably has 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and still more preferably 1 to 3 carbon atoms.
^Also, in the ^{W 03,} group consisting of a chain hydrocarbon group attached to the aliphatic cyclic group and the aliphatic cyclic _{group, -OH, -COOH, -CN, -SO} 2 NH 2 and -CONH _It may further have a substituent (a) other than ₂ . As this substituent (a), a C1-C5 alkyl group, a fluorine atom, a C1-C5 fluorinated alkyl group, etc. are mentioned.

Specific examples of preferable structural units represented by general formula (a3-13) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a3) contained in the component (A1 ′), 1 type of structural unit may be used, or 2 or more types may be used.
In the component (A1 ′), the proportion of the structural unit (a3) is preferably 1 to 50 mol%, more preferably 1 to 40 mol% with respect to all the structural units constituting the component (A1 ′). 1 to 30 mol% is more preferable, and 3 to 30 mol% is particularly preferable.
By setting the proportion of the structural unit (a3) to be equal to or higher than the lower limit value, the effects (resolution, lithography characteristics, pattern shape improvement effect) due to the inclusion of the structural unit (a3) can be sufficiently obtained, and the upper limit value or less. This makes it easier to balance with other structural units.

[Structural unit (a0)]
The structural unit (a0) is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and includes a —SO ₂ — containing cyclic group. It is a structural unit.
The structural unit (a0) includes an —SO ₂ — containing cyclic group, thereby improving the adhesion of the resist film formed using the resist composition containing the component (A1 ′) to the substrate. Further, it contributes to the improvement of lithography characteristics such as sensitivity, resolution, exposure margin (EL margin), LWR (line width roughness), LER (line edge roughness), mask reproducibility and the like.

Here _- as "-SO 2 containing cyclic group", -SO 2 _- within the ring skeleton thereof shows a cyclic group containing a ring containing, in particular, -SO 2 _- in the sulfur atom (S ) Is a cyclic group that forms part of the ring skeleton of the cyclic group.
In-containing cyclic group, within the ring skeleton thereof -SO 2 _{- -} -SO 2 counted ring containing as the first ring, in the case of the ring only a monocyclic group, and groups containing other ring structures In some cases, it is referred to as a polycyclic group regardless of its structure.
The —SO ₂ — containing cyclic group may be monocyclic or polycyclic.
The —SO ₂ — containing cyclic group is particularly a cyclic group containing —O—SO ₂ — in the ring skeleton, that is, a ring skeleton in which —O—S— in —O—SO ₂ — is a cyclic group. It is preferable that it is a sultone ring which forms a part of.
The —SO ₂ — containing cyclic group preferably has 3 to 30 carbon atoms, preferably 4 to 20 carbon atoms, more preferably 4 to 15 carbon atoms, and particularly preferably 4 to 12 carbon atoms. . However, the carbon number is the number of carbon atoms constituting the ring skeleton, and does not include the carbon number in the substituent.
The —SO ₂ — containing cyclic group may be an —SO ₂ — containing aliphatic cyclic group or an —SO ₂ — containing aromatic cyclic group. Preferably -SO ₂ - containing aliphatic cyclic group.
The —SO ₂ -containing aliphatic cyclic group includes at least a hydrogen atom from an aliphatic hydrocarbon ring in which a part of carbon atoms constituting the ring skeleton is substituted with —SO ₂ — or —O—SO ₂ —. One group is excluded. More specifically, a group obtained by removing at least one hydrogen atom from an aliphatic hydrocarbon ring in which —CH ₂ — constituting the ring skeleton is substituted with —SO ₂ —, —CH ₂ — constituting the ring And a group obtained by removing at least one hydrogen atom from an aliphatic hydrocarbon ring in which CH ₂ — is substituted with —O—SO ₂ —.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms are removed from a monocycloalkane having 3 to 6 carbon atoms. Examples of the monocycloalkane include cyclopentane and cyclohexane. As the polycyclic alicyclic hydrocarbon group, a group in which two hydrogen atoms have been removed from a polycycloalkane having 7 to 12 carbon atoms is preferable. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane. , Tricyclodecane, tetracyclododecane and the like.

The —SO ₂ — containing cyclic group may have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O), —COOR ″, —OC (═O) R ″ (R ″ represents a hydrogen atom or an alkyl group). Group), a hydroxyalkyl group, a cyano group, and the like.
The alkyl group as the substituent is preferably an alkyl group having 1 to 6 carbon atoms. The alkyl group is preferably linear or branched. Specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, a neopentyl group, and a hexyl group. Among these, a methyl group or an ethyl group is preferable, and a methyl group is particularly preferable.
The alkoxy group as the substituent is preferably an alkoxy group having 1 to 6 carbon atoms. The alkoxy group is preferably linear or branched. Specifically, the group couple | bonded with the oxygen atom (-O-) to the alkyl group quoted as the alkyl group as the said substituent is mentioned.
Examples of the halogen atom as the substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group for the substituent include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.
Examples of the halogenated alkyl group as the substituent include groups in which part or all of the hydrogen atoms of the alkyl group mentioned as the alkyl group as the substituent are substituted with the halogen atom. As the halogenated alkyl group, a fluorinated alkyl group is preferable, and a perfluoroalkyl group is particularly preferable.
R ″ in —COOR ″ and —OC (═O) R ″ is preferably a hydrogen atom or a linear, branched or cyclic alkyl group having 1 to 15 carbon atoms.
When R ″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and particularly preferably a methyl group or an ethyl group. preferable.
When R ″ is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, a fluorine atom Or a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as monocycloalkane, bicycloalkane, tricycloalkane, and tetracycloalkane, which may or may not be substituted with a fluorinated alkyl group More specifically, one or more hydrogen atoms are removed from a monocycloalkane such as cyclopentane or cyclohexane, or a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Group and the like.
The hydroxyalkyl group as the substituent is preferably one having 1 to 6 carbon atoms. Specifically, at least one of the hydrogen atoms of the alkyl group mentioned as the alkyl group as the substituent is substituted with a hydroxyl group. Group.
More specifically, examples of the —SO ₂ -containing cyclic group include groups represented by the following general formulas (3-1) to (3-4).

［式中、Ａ’は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり、ｚは０〜２の整数であり、Ｒ^６はアルキル基、アルコキシ基、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基またはシアノ基であり、Ｒ”は水素原子またはアルキル基である。］

[In the formula, A ′ is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom or a sulfur atom, z is an integer of 0 to 2, and R ⁶ is an alkyl group. , An alkoxy group, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group or a cyano group, and R ″ is a hydrogen atom or an alkyl group.]

In the general formulas (3-1) to (3-4), A ′ represents an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom (—O—) or a sulfur atom (—S—), An oxygen atom or a sulfur atom.
The alkylene group having 1 to 5 carbon atoms in A ′ is preferably a linear or branched alkylene group, and examples thereof include a methylene group, an ethylene group, an n-propylene group, and an isopropylene group.
When the alkylene group contains an oxygen atom or a sulfur atom, specific examples thereof include a group in which —O— or —S— is interposed between the terminal or carbon atoms of the alkylene group, such as —O—CH _{2. -, - CH 2 -O-CH} 2 -, - S-CH 2 -, - CH 2 -S-CH 2 - , and the like.
A ′ is preferably an alkylene group having 1 to 5 carbon atoms or —O—, more preferably an alkylene group having 1 to 5 carbon atoms, and most preferably a methylene group.
z may be any of 0 to 2, and is most preferably 0.
When z is 2, the plurality of R ⁶ may be the same or different.
As the alkyl group, alkoxy group, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in R ⁶ , the —SO ₂ — containing cyclic group has the above-mentioned, respectively. And the same alkyl groups, alkoxy groups, halogenated alkyl groups, —COOR ″, —OC (═O) R ″, and hydroxyalkyl groups as those which may be substituted.
Below, the specific cyclic group represented by the said general formula (3-1)-(3-4) is illustrated. In the formula, “Ac” represents an acetyl group.

Among the above, the —SO ₂ -containing cyclic group is preferably a group represented by the general formula (3-1), and the chemical formulas (3-1-1), (3-1-18), ( It is more preferable to use at least one selected from the group consisting of groups represented by any of 3-3-1) and (3-4-1), and represented by the chemical formula (3-1-1). Are most preferred.

  More specifically, examples of the structural unit (a0) include structural units represented by general formula (a0-0) shown below.

［式中、Ｒは水素原子、炭素数１〜５のアルキル基または炭素数１〜５のハロゲン化アルキル基であり、Ｒ^３は−ＳＯ_２−含有環式基であり、Ｒ^２９’は単結合または２価の連結基である。］

[Wherein, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, R ³ represents a —SO ₂ — containing cyclic group, and R ²⁹ ′ represents a single atom. A bond or a divalent linking group. ]

In formula (a0-0), R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms.
The alkyl group having 1 to 5 carbon atoms in R is preferably a linear or branched alkyl group having 1 to 5 carbon atoms. Specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, n- Examples thereof include a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group.
The halogenated alkyl group in R is a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with a halogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and is most preferably a hydrogen atom or a methyl group in terms of industrial availability.

In formula (a0-0), R ³ is the same as the —SO ₂ — containing cyclic group mentioned above.
R ²⁹ ′ may be either a single bond or a divalent linking group. Since it is excellent in the effect of this invention, it is preferable that it is a bivalent coupling group.
Examples of the divalent linking group for R ²⁹ ′ include those listed as the divalent linking group for Y ² in the general formula (a1-0-2) given in the description of the structural unit (a1). The same thing is mentioned.
The divalent linking group for R ²⁹ ′ is preferably an alkylene group, a divalent alicyclic hydrocarbon group, or a divalent linking group containing a hetero atom. Among these, those containing an alkylene group and an ester bond (—C (═O) —O—) are preferable.
The alkylene group is preferably a linear or branched alkylene group. Specifically, the same as the linear alkylene group and the branched alkylene group mentioned as the aliphatic hydrocarbon group for Y ² can be used.
As the divalent linking group containing an ester bond, in particular, the general formula: —R ² —C (═O) —O— [wherein R ² is a divalent linking group. ] Is preferable. That is, the structural unit (a0) is preferably a structural unit represented by the following general formula (a0-0-1).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基であり、Ｒ^２は２価の連結基であり、Ｒ^３は−ＳＯ_２−含有環式基である。］

[Wherein, R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms, R ² is a divalent linking group, and R ³ is —SO ₂ — containing] It is a cyclic group. ]

R ² is not particularly limited, and examples thereof include those similar to those exemplified as the divalent linking group in R ²⁹ ′ in the general formula (a0-0).
The divalent linking group for R ² is preferably a linear or branched alkylene group, a divalent alicyclic hydrocarbon group, or a divalent linking group containing a hetero atom.
Examples of the linear or branched alkylene group, divalent alicyclic hydrocarbon group, and divalent linking group containing a hetero atom include the linear groups mentioned above as preferred for R ²⁹ ′. Or the same thing as the branched alkylene group, the bivalent alicyclic hydrocarbon group, and the bivalent coupling group containing a hetero atom is mentioned.
Among these, a linear or branched alkylene group or a divalent linking group containing an oxygen atom as a hetero atom is preferable.
As the linear alkylene group, a methylene group or an ethylene group is preferable, and a methylene group is particularly preferable.
As the branched alkylene group, an alkylmethylene group or an alkylethylene group is preferable, and —CH (CH ₃ ) —, —C (CH ₃ ) ₂ — or —C (CH ₃ ) ₂ CH ₂ — is particularly preferable.
The divalent linking group containing an oxygen atom is preferably a divalent linking group containing an ether bond or an ester bond, and the above formulas -A-O-B-,-[A-C (= O) -O] _{m '} A group represented by -B- or -AOC (= O) -B- is more preferred. m 'is an integer of 0-3.
Among them, preferably a group represented by the formula -A-O-C (= O ) -B-, - represented by _{- (CH 2) c -C (} = O) -O- (CH 2) d The group is particularly preferred. c is an integer of 1 to 5, and 1 or 2 is preferable. d is an integer of 1-5, and 1 or 2 is preferable.

  As the structural unit (a0), a structural unit represented by general formula (a0-0-11) or (a0-0-12) shown below is preferable, and a structural unit represented by formula (a0-0-12) is preferable. Units are more preferred.

［式中、Ｒ、Ａ’、Ｒ^６、ｚおよびＲ^２はそれぞれ前記と同じである。］

[Wherein, R, A ′, R ⁶ , z and R ² are the same as defined above. ]

In formula (a0-0-11), A ′ is preferably a methylene group, an ethylene group, an oxygen atom (—O—) or a sulfur atom (—S—).
R ² is preferably a linear or branched alkylene group or a divalent linking group containing an oxygen atom. As the linear or branched alkylene group and the divalent linking group containing an oxygen atom in R ^2, the linear or branched alkylene group mentioned above and a divalent linking group containing an oxygen atom are mentioned. Examples are the same as the linking group.
As the structural unit represented by the formula (a0-0-12), a structural unit represented by the following general formula (a0-0-12a) or (a0-0-12b) is particularly preferable.

［式中、ＲおよびＡ’はそれぞれ前記と同じであり、ｃ〜ｅはそれぞれ独立に１〜３の整数である。］

[Wherein, R and A ′ are the same as defined above, and c to e are each independently an integer of 1 to 3.] ]

As the structural unit (a0) contained in the component (A1 ′), 1 type of structural unit may be used, or 2 or more types may be used.
The proportion of the structural unit (a0) in the component (A1 ′) is such that the resist pattern shape formed using the resist composition containing the component (A1 ′) becomes good, and EL margin, LWR, mask reproducibility, etc. Therefore, it is preferably 1 to 60 mol%, more preferably 5 to 55 mol%, more preferably 10 to 50 mol%, based on the total of all structural units constituting the component (A1 ′). Is more preferable, and 15 to 45 mol% is most preferable.

[Structural unit (a2)]
The structural unit (a2) is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and includes a lactone-containing cyclic group. is there.
Here, the lactone-containing cyclic group refers to a cyclic group containing one ring (lactone ring) containing a —O—C (═O) — structure. The lactone ring is counted as the first ring, and when it is only the lactone ring, it is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure.
When the lactone cyclic group of the structural unit (a2) is used for forming a resist film, the component (A1 ′) is used to improve the adhesion of the resist film to the substrate, or a developer containing water (particularly alkaline development). It is effective in increasing the affinity with the process).

As the structural unit (a2), any unit can be used without any particular limitation.
Specifically, as the lactone-containing monocyclic group, a group in which one hydrogen atom is removed from a 4- to 6-membered ring lactone, for example, a group in which one hydrogen atom is removed from β-propionolactone, or γ-butyrolactone. Examples thereof include a group in which one hydrogen atom has been removed and a group in which one hydrogen atom has been removed from δ-valerolactone. Examples of the lactone-containing polycyclic group include groups in which one hydrogen atom has been removed from a bicycloalkane, tricycloalkane, or tetracycloalkane having a lactone ring.

  More specifically, examples of the structural unit (a2) include structural units represented by general formulas (a2-1) to (a2-5) shown below.

［式中、Ｒは水素原子、低級アルキル基またはハロゲン化低級アルキル基であり；Ｒ’はそれぞれ独立に水素原子、炭素数１〜５のアルキル基、炭素数１〜５のアルコキシ基または−ＣＯＯＲ”であり、Ｒ”は水素原子またはアルキル基であり；Ｒ^２９は単結合または２価の連結基であり、ｓ”は０または１〜２の整数であり；Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子または硫黄原子であり；ｍは０または１の整数である。］

[Wherein, R represents a hydrogen atom, a lower alkyl group or a halogenated lower alkyl group; R ′ each independently represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, or —COOR; R "is a hydrogen atom or an alkyl group; R ²⁹ is a single bond or a divalent linking group; s" is 0 or an integer of 1 to 2; A "is an oxygen atom or a sulfur atom. An alkylene group having 1 to 5 carbon atoms, an oxygen atom or a sulfur atom, and m is an integer of 0 or 1. ]

R in the general formulas (a2-1) to (a2-5) is the same as R in the structural unit (a1).
Examples of the alkyl group having 1 to 5 carbon atoms of R ′ include a methyl group, an ethyl group, a propyl group, an n-butyl group, and a tert-butyl group.
Examples of the alkoxy group having 1 to 5 carbon atoms of R ′ include a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, and a tert-butoxy group.
R ′ is preferably a hydrogen atom in view of industrial availability.
R ″ is preferably a hydrogen atom or a linear, branched or cyclic alkyl group having 1 to 15 carbon atoms.
When R ″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, and more preferably 1 to 5 carbon atoms.
When R ″ is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, a fluorine atom Or a monocycloalkane which may or may not be substituted with a fluorinated alkyl group; a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as a bicycloalkane, tricycloalkane or tetracycloalkane Specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane, or a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Etc.
A ″ is preferably an alkylene group having 1 to 5 carbon atoms or —O—, more preferably an alkylene group having 1 to 5 carbon atoms, and most preferably a methylene group.
R ²⁹ is a single bond or a divalent linking group. The divalent linking group is the same as the divalent linking group described for Y ² in the general formula (a1-0-2), and among them, an alkylene group and an ester bond (—C (═O ) -O-) or a combination thereof. The alkylene group as the divalent linking group for R ²⁹ is more preferably a linear or branched alkylene group. Specifically, the same as the linear alkylene group and the branched alkylene group mentioned as the aliphatic hydrocarbon group for A in Y ² can be used.
s ″ is preferably an integer of 1 to 2.
Specific examples of the structural units represented by the general formulas (a2-1) to (a2-5) are illustrated below.
In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a2) contained in the component (A1 ′), 1 type of structural unit may be used, or 2 or more types may be used.
As the structural unit (a2), at least one selected from the group consisting of structural units represented by the general formulas (a2-1) to (a2-5) is preferable, and the general formulas (a2-1) to ( At least one selected from the group consisting of structural units represented by a2-3) is more preferred. Among them, chemical formulas (a2-1-1), (a2-1-2), (a2-2-1), (a2-2-7), (a2-3-1) and (a2-3-5) It is preferable to use at least one selected from the group consisting of structural units represented by

  The proportion of the structural unit (a2) in the component (A1 ′) is preferably 5 to 60 mol%, more preferably 10 to 50 mol%, based on the total of all structural units constituting the component (A1 ′). 10 to 45 mol% is more preferable. By setting it to the lower limit value or more, the effect of containing the structural unit (a2) can be sufficiently obtained, and by setting it to the upper limit value or less, it is possible to balance with other structural units.

[Other structural units]
The component (A1 ′) may have other structural units other than the structural units (a5), (a1), (a3), (a0), and (a2) as long as the effects of the present invention are not impaired. Good.
Such other structural unit is not particularly limited as long as it is a structural unit not classified into the above structural units (a5), (a1), (a3), (a0), and (a2). For ArF excimer laser A number of hitherto known materials can be used for resist resins such as for KrF excimer laser (preferably for ArF excimer laser).
Such other structural unit is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and is a non-acid-dissociable aliphatic polycycle And a structural unit (a4) containing a formula group.

(Structural unit (a4))
The structural unit (a4) is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and is a non-acid-dissociable aliphatic polycyclic group A structural unit containing a group.
In the structural unit (a4), examples of the polycyclic group include those similar to those exemplified in the case of the structural unit (a1). For ArF excimer laser, KrF excimer laser ( A number of hitherto known materials can be used as the resin component of the resist composition (preferably for ArF excimer laser).
In particular, at least one selected from a tricyclodecyl group, an adamantyl group, a tetracyclododecyl group, an isobornyl group, and a norbornyl group is preferable in terms of industrial availability. These polycyclic groups may have a linear or branched alkyl group having 1 to 5 carbon atoms as a substituent.
Specific examples of the structural unit (a4) include those represented by the following general formulas (a4-1) to (a4-5).

（式中、Ｒは前記と同じである。）

(In the formula, R is as defined above.)

  When the structural unit (a4) is contained in the component (A1 ′), the structural unit (a4) is contained in an amount of 1 to 30 mol% based on the total of all the structural units constituting the component (A1 ′). Is preferable, and it is more preferable to make it contain 10-20 mol%.

In the resist composition of the present invention, the component (A1 ′) is a resin component having the structural unit (a5), the structural unit (a1), and the structural unit (a3), and the structural unit (a5) and the structural unit (a1). ) And the structural unit (a3) are preferably contained (A1′-1) (hereinafter referred to as “(A1′-1) component”).
Specifically, the component (A1′-1) is a polymer compound composed of structural units (a5), (a1) and (a3); from structural units (a5), (a1), (a3) and (a0). A polymer compound comprising the structural units (a5), (a1), (a3) and (a2); from the structural units (a5), (a1), (a3), (a0) and (a2) The high molecular compound etc. which become can be illustrated.

  In the component (A ′), as the component (A1 ′), one type may be used alone, or two or more types may be used in combination.

The mass average molecular weight (Mw) of the component (A1 ′) (polystyrene conversion standard by gel permeation chromatography (GPC)) is not particularly limited, preferably 1000 to 50000, more preferably 1500 to 30000, 2000 ˜20,000 is most preferred. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent to be used as a resist, and if it is above the lower limit of this range, dry etching resistance and resist pattern cross-sectional shape are good.
The dispersity (Mw / Mn) is not particularly limited, but is preferably 1.0 to 5.0, more preferably 1.0 to 4.0, and most preferably 1.0 to 3.0. In addition, Mn shows a number average molecular weight.

The component (A1 ′) can be obtained by polymerizing a monomer that derives each structural unit by a known radical polymerization using a radical polymerization initiator such as azobisisobutyronitrile (AIBN). .
In addition, for the component (A1 ′), a chain transfer agent such as HS—CH ₂ —CH ₂ —CH ₂ —C (CF ₃ ) ₂ —OH is used in combination in the above polymerization, -C terminated _{(CF 3)} may be introduced 2 -OH group. As described above, a copolymer introduced with a hydroxyalkyl group in which a part of hydrogen atoms of the alkyl group is substituted with a fluorine atom reduces development defects and LER (line edge roughness: uneven unevenness of line side walls). It is effective in reducing
A commercially available monomer may be used as the monomer for deriving each structural unit, or the monomer may be synthesized using a known method.

In the resist composition of the present invention, the component (A1 ′) can be used as a base resin for forming a resist film. In addition, an organic compound having a film forming ability other than the component (A1 ′) (such as the component (C) described later) can be used as a substrate component, and the substrate component and the component (A1 ′) can be used in combination.
In the resist composition of the present invention, as the component (A ′), one type may be used alone, or two or more types may be used in combination.
In the resist composition of the present invention, the content of the component (A ′) may be adjusted according to the resist film thickness to be formed.

<(B) component>
The resist composition of the present invention may further contain an acid generator component (B) (hereinafter referred to as component (B)) that does not correspond to the component (A ′) and generates an acid upon exposure.
The component (B) is not particularly limited, and those that have been proposed as acid generators for chemically amplified resists can be used. Examples of such acid generators include onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators, bisalkyl or bisarylsulfonyldiazomethanes, and poly (bissulfonyl) diazomethanes. There are various known diazomethane acid generators, nitrobenzyl sulfonate acid generators, imino sulfonate acid generators, disulfone acid generators, and the like.
As the onium salt acid generator, for example, a compound represented by the following general formula (b-1) or (b-2) can be used.

［式中、Ｒ^１”〜Ｒ^３”，Ｒ^５”〜Ｒ^６”はそれぞれ独立に置換基を有していてもよいアリール基、アルキル基又はアルケニル基を表す。式（ｂ−１）におけるＲ^１”〜Ｒ^３”のうち、いずれか二つが相互に結合して式中のイオウ原子と共に環を形成してもよい。Ｒ^４”は、置換基を有していてもよいアルキル基、ハロゲン化アルキル基、アリール基、またはアルケニル基を表す。］

[Wherein, R ¹ ″ to R ³ ″ and R ⁵ ″ to R ⁶ ″ each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent. Any two of R ¹ ″ to R ³ ″ in formula (b-1) may be bonded to each other to form a ring together with the sulfur atom in the formula. R ⁴ ″ represents an alkyl group, a halogenated alkyl group, an aryl group, or an alkenyl group which may have a substituent.

In formula (b-1), R ¹ ″ to R ³ ″ each independently represents an aryl group, alkyl group or alkenyl group which may have a substituent. Any two of R ¹ ″ to R ³ ″ may be bonded to each other to form a ring together with the sulfur atom in the formula.
Moreover, it is preferable that at least one of R ¹ ″ to R ³ ″ is an aryl group, and two or more of R ¹ ″ to R ³ ″ since the lithography characteristics and the resist pattern shape are further improved. Is more preferably an aryl group, and it is particularly preferred that all of R ¹ ″ to R ³ ″ are aryl groups.

As the aryl group for R ¹ ″ to R ³ ″, an unsubstituted aryl group having 6 to 20 carbon atoms; some or all of the hydrogen atoms of the unsubstituted aryl group are alkyl groups, alkoxy groups, halogen atoms, hydroxyl groups , An oxo group (═O), an aryl group, an alkoxyalkyloxy group, an alkoxycarbonylalkyloxy group, —C (═O) —O—R ⁶ ′, —O—C (═O) —R ⁷ ′, —O And a substituted aryl group substituted with —R ⁸ ′ and the like. R ⁶ ′, R ⁷ ′ and R ⁸ ′ are each a linear, branched or cyclic saturated hydrocarbon group having 1 to 25 carbon atoms, or a C 2 to 5 carbon atoms. It is a linear or branched aliphatic unsaturated hydrocarbon group.
In R ¹ ″ to R ³ ″, the unsubstituted aryl group is preferably an aryl group having 6 to 10 carbon atoms because it can be synthesized at a low cost. Specific examples include a phenyl group and a naphthyl group.
The alkyl group as a substituent in the substituted aryl group of R ¹ ″ to R ³ ″ is preferably an alkyl group having 1 to 5 carbon atoms, and is a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. Most preferably.
As the alkoxy group as a substituent in the substituted aryl group, an alkoxy group having 1 to 5 carbon atoms is preferable, and a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group. Most preferably it is.
The halogen atom as a substituent in the substituted aryl group is preferably a fluorine atom.
Examples of the aryl group as a substituent in the substituted aryl group include the same aryl groups as those described above for R ¹ ″ to R ³ ″, preferably an aryl group having 6 to 20 carbon atoms, and an aryl group having 6 to 10 carbon atoms. Group is more preferable, and phenyl group and naphthyl group are more preferable.

As the alkoxyalkyloxy group in the substituted aryl group, for example,
General formula: -O-C ( ^R47 ) ( ^R48 ) -O- ^R49
[Wherein, R ⁴⁷ and R ⁴⁸ each independently represent a hydrogen atom or a linear or branched alkyl group, and R ⁴⁹ represents an alkyl group. ] Is represented.
In R ⁴⁷ and R ⁴⁸ , the alkyl group preferably has 1 to 5 carbon atoms, may be linear or branched, and is preferably an ethyl group or a methyl group, and most preferably a methyl group.
At least one of R ⁴⁷ and R ⁴⁸ is preferably a hydrogen atom. In particular, it is more preferable that one is a hydrogen atom and the other is a hydrogen atom or a methyl group.
The alkyl group for R ⁴⁹ preferably has 1 to 15 carbon atoms and may be linear, branched or cyclic.
The linear or branched alkyl group for R ⁴⁹ preferably has 1 to 5 carbon atoms, and examples thereof include a methyl group, an ethyl group, a propyl group, an n-butyl group, and a tert-butyl group. Can be mentioned.
The cyclic alkyl group for R ⁴⁹ preferably has 4 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, monocycloalkane, bicycloalkane, tricycloalkane, tetracycloalkane, etc., which may or may not be substituted with an alkyl group having 1 to 5 carbon atoms, a fluorine atom or a fluorinated alkyl group, etc. And a group obtained by removing one or more hydrogen atoms from the polycycloalkane. Examples of the monocycloalkane include cyclopentane and cyclohexane. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.

As the alkoxycarbonylalkyloxy group in the substituted aryl group, for example,
General formula: —O—R ⁵⁰ —C (═O) —O—R ⁵⁶
[Wherein, R ⁵⁰ represents a linear or branched alkylene group, and R ⁵⁶ represents a tertiary alkyl group. ] Is represented.
The linear or branched alkylene group for R ⁵⁰ preferably has 1 to 5 carbon atoms, such as a methylene group, an ethylene group, a trimethylene group, a tetramethylene group, or a 1,1-dimethylethylene group. Etc.
As the tertiary alkyl group for R ⁵⁶ , 2-methyl-2-adamantyl group, 2-ethyl-2-adamantyl group, 1-methyl-1-cyclopentyl group, 1-ethyl-1-cyclopentyl group, 1-methyl -1-cyclohexyl group, 1-ethyl-1-cyclohexyl group, 1- (1-adamantyl) -1-methylethyl group, 1- (1-adamantyl) -1-methylpropyl group, 1- (1-adamantyl) -1-methylbutyl group, 1- (1-adamantyl) -1-methylpentyl group; 1- (1-cyclopentyl) -1-methylethyl group, 1- (1-cyclopentyl) -1-methylpropyl group, 1- (1-cyclopentyl) -1-methylbutyl group, 1- (1-cyclopentyl) -1-methylpentyl group; 1- (1-cyclohexyl) -1-methylethyl Group, 1- (1-cyclohexyl) -1-methylpropyl group, 1- (1-cyclohexyl) -1-methylbutyl group, 1- (1-cyclohexyl) -1-methylpentyl group, tert-butyl group, tert -Pentyl group, tert-hexyl group and the like.
Moreover, the general ^formula: the ^{R 56} in the -O-R 50 -C (= O ) -O-R 56, also include groups replaced by ^{R 56} '. R ⁵⁶ ′ is a hydrogen atom, an alkyl group, a fluorinated alkyl group, or an aliphatic cyclic group that may contain a hetero atom.
^Examples of the alkyl group for R ⁵⁶ ′ include the same alkyl groups as those described above for R ⁴⁹ .
^Examples of the fluorinated alkyl group for R ⁵⁶ ′ include groups in which some or all of the hydrogen atoms within the alkyl group for R ⁴⁹ have been substituted with fluorine atoms.
Examples of the aliphatic cyclic group which may contain a hetero atom in R ⁵⁶ ′ include an aliphatic cyclic group containing no hetero atom, an aliphatic cyclic group containing a hetero atom in the ring structure, and an aliphatic cyclic group. Examples include those in which a hydrogen atom in the group is substituted with a heteroatom.
Regarding R ⁵⁶ ′, the aliphatic cyclic group containing no hetero atom includes a group obtained by removing one or more hydrogen atoms from a polycycloalkane such as monocycloalkane, bicycloalkane, tricycloalkane, tetracycloalkane, and the like. Can be mentioned. Examples of the monocycloalkane include cyclopentane and cyclohexane. Examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among them, a group obtained by removing one or more hydrogen atoms from adamantane is preferable.
Specific examples of the aliphatic cyclic group containing a hetero atom in the ring structure for R ⁵⁶ ′ include groups represented by the following formulas (L1) to (L6) and (S1) to (S4). It is done.
As for R ⁵⁶ ′, the hydrogen atom in the aliphatic cyclic group is specifically substituted with a hetero atom, specifically, the hydrogen atom in the aliphatic cyclic group is substituted with an oxygen atom (═O), etc. Is mentioned.

^{-C (= O) -O-R} 6 ', -O-C (= O) -R 7', 'R 6 ^{in' -O-R 8, R 7} ', R 8' are each carbon atoms 1 to 25 linear, branched or cyclic saturated hydrocarbon group having 3 to 20 carbon atoms, or a linear or branched aliphatic unsaturated hydrocarbon group having 2 to 5 carbon atoms. .
The linear or branched saturated hydrocarbon group has 1 to 25 carbon atoms, preferably 1 to 15 carbon atoms, and more preferably 4 to 10 carbon atoms.
Examples of the linear saturated hydrocarbon group include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, and a decyl group.
Examples of the branched saturated hydrocarbon group excluding the tertiary alkyl group include, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3 -Methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like can be mentioned.
The linear or branched saturated hydrocarbon group may have a substituent. Examples of the substituent include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O), a cyano group, and a carboxy group.
As the alkoxy group as a substituent of the linear or branched saturated hydrocarbon group, an alkoxy group having 1 to 5 carbon atoms is preferable, and a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, An n-butoxy group and a tert-butoxy group are preferable, and a methoxy group and an ethoxy group are most preferable.
Examples of the halogen atom as a substituent of the linear or branched saturated hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
As the halogenated alkyl group as a substituent of the linear or branched saturated hydrocarbon group, part or all of the hydrogen atoms of the linear or branched saturated hydrocarbon group are the halogen atoms. And a group substituted with.
The cyclic saturated hydrocarbon group having 3 to 20 carbon atoms in R ⁶ ′, R ⁷ ′, and R ⁸ ′ may be either a polycyclic group or a monocyclic group. A group in which one hydrogen atom has been removed from a polycycloalkane such as bicycloalkane, tricycloalkane, tetracycloalkane, and the like. More specifically, one hydrogen atom was removed from a monocycloalkane such as cyclopentane, cyclohexane, cycloheptane, and cyclooctane, and a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Group and the like.
The cyclic saturated hydrocarbon group may have a substituent. For example, part of the carbon atoms constituting the ring of the cyclic alkyl group may be substituted with a heteroatom, or the hydrogen atom bonded to the ring of the cyclic alkyl group may be substituted with a substituent. Good.
Examples of the former include one or more hydrogen atoms from a heterocycloalkane in which a part of the carbon atoms constituting the ring of the monocycloalkane or polycycloalkane is substituted with a heteroatom such as an oxygen atom, a sulfur atom, or a nitrogen atom. Examples include groups other than atoms. The ring structure may have an ester bond (—C (═O) —O—). Specifically, a lactone-containing monocyclic group such as a group obtained by removing one hydrogen atom from γ-butyrolactone, or a group obtained by removing one hydrogen atom from a bicycloalkane, tricycloalkane, or tetracycloalkane having a lactone ring. And other lactone-containing polycyclic groups.
Examples of the substituent in the latter example include the same as those described above as the substituent that the linear or branched alkyl group may have, a lower alkyl group, and the like.
R ⁶ ′, R ⁷ ′, and R ⁸ ′ may be a combination of a linear or branched alkyl group and a cyclic alkyl group.
A combination of a linear or branched alkyl group and a cyclic alkyl group includes a group in which a cyclic alkyl group is bonded as a substituent to a linear or branched alkyl group, and a substituent to the cyclic alkyl group. And a group having a linear or branched alkyl group bonded thereto.
Examples of the linear aliphatic unsaturated hydrocarbon group for R ⁶ ′, R ⁷ ′, and R ⁸ ′ include a vinyl group, a propenyl group (allyl group), and a butynyl group.
Examples of the branched aliphatic unsaturated hydrocarbon group for R ⁶ ′, R ⁷ ′, and R ⁸ ′ include a 1-methylpropenyl group and a 2-methylpropenyl group.
The linear or branched aliphatic unsaturated hydrocarbon group may have a substituent. Examples of the substituent include the same ones as those exemplified as the substituent which the linear or branched alkyl group may have.
Among R ⁷ ′ and R ⁸ ′, among them, the lithography characteristics and the resist pattern shape are good, so that the linear or branched saturated hydrocarbon group having 1 to 15 carbon atoms, or the carbon number 3-20 cyclic saturated hydrocarbon groups are preferred.

The aryl groups for R ¹ ″ to R ³ ″ are each preferably a phenyl group or a naphthyl group.

Examples of the alkyl group for R ¹ ″ to R ³ ″ include a linear, branched, or cyclic alkyl group having 1 to 10 carbon atoms. Especially, it is preferable that it is C1-C5 from the point which is excellent in resolution. Specific examples include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, an n-pentyl group, a cyclopentyl group, a hexyl group, a cyclohexyl group, a nonyl group, and a decyl group. A methyl group is preferable because it is excellent in resolution and can be synthesized at low cost.

As an alkenyl group of R < ¹ >"-R< ³ >", it is preferable that it is C2-C10, for example, 2-5 are more preferable, and 2-4 are more preferable. Specific examples include a vinyl group, a propenyl group (allyl group), a butynyl group, a 1-methylpropenyl group, and a 2-methylpropenyl group.

When any two of R ¹ ″ to R ³ ″ are bonded to each other to form a ring together with the sulfur atom in the formula, it is preferable to form a 3 to 10 membered ring including the sulfur atom, It is particularly preferable to form a 5- to 7-membered ring.
When any two of R ¹ ″ to R ³ ″ are bonded to each other to form a ring together with the sulfur atom in the formula, the remaining one is preferably an aryl group. Examples of the aryl group include the same aryl groups as those described above for R ¹ ″ to R ³ ″.

  Specific examples of the cation moiety in the compound represented by the formula (b-1) include, for example, triphenylsulfonium, (3,5-dimethylphenyl) diphenylsulfonium, (4- (2-adamantoxymethyloxy)- 3,5-dimethylphenyl) diphenylsulfonium, (4- (2-adamantoxymethyloxy) phenyl) diphenylsulfonium, (4- (tert-butoxycarbonylmethyloxy) phenyl) diphenylsulfonium, (4- (tert-butoxycarbonyl) Methyloxy) -3,5-dimethylphenyl) diphenylsulfonium, (4- (2-methyl-2-adamantyloxycarbonylmethyloxy) phenyl) diphenylsulfonium, (4- (2-methyl-2-adamantyloxycarbonylmethyl) Xy) -3,5-dimethylphenyl) diphenylsulfonium, tri (4-methylphenyl) sulfonium, dimethyl (4-hydroxynaphthyl) sulfonium, monophenyldimethylsulfonium, diphenylmonomethylsulfonium, (4-methylphenyl) diphenylsulfonium, 4-methoxyphenyl) diphenylsulfonium, tri (4-tert-butyl) phenylsulfonium, diphenyl (1- (4-methoxy) naphthyl) sulfonium, di (1-naphthyl) phenylsulfonium, 1-phenyltetrahydrothiophenium, 1 -(4-Methylphenyl) tetrahydrothiophenium, 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiophenium, 1- (4-methoxynaphthalen-1-yl) Trahydrothiophenium, 1- (4-ethoxynaphthalen-1-yl) tetrahydrothiophenium, 1- (4-n-butoxynaphthalen-1-yl) tetrahydrothiophenium, 1-phenyltetrahydrothiopyranium, Examples include 1- (4-hydroxyphenyl) tetrahydrothiopyranium, 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiopyranium, 1- (4-methylphenyl) tetrahydrothiopyranium, and the like.

  Specific examples of the cation moiety in the compound represented by the formula (b-1) include those shown below.

［式中、ｇ１は繰返し数を示し、１〜５の整数である。］

[Wherein g1 represents the number of repetitions and is an integer of 1 to 5. ]

［式中、ｇ２、ｇ３は繰返し数を示し、ｇ２は０〜２０の整数であり、ｇ３は０〜２０の整数である。］

[Wherein g2 and g3 represent the number of repetitions, g2 is an integer of 0 to 20, and g3 is an integer of 0 to 20. ]

In the formula (b-1), R ⁴ ″ represents an alkyl group, a halogenated alkyl group, an aryl group, or an alkenyl group which may have a substituent.
The alkyl group for R ⁴ ″ may be linear, branched or cyclic.
The linear or branched alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 4 carbon atoms.
The cyclic alkyl group preferably has 4 to 15 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms.
Examples of the halogenated alkyl group for R ⁴ ″ include groups in which part or all of the hydrogen atoms of the linear, branched, or cyclic alkyl group have been substituted with halogen atoms. A fluorine atom, a chlorine atom, a bromine atom, an iodine atom, etc. are mentioned, A fluorine atom is preferable.
In the halogenated alkyl group, the ratio of the number of halogen atoms to the total number of halogen atoms and hydrogen atoms contained in the halogenated alkyl group (halogenation rate (%)) is preferably 10 to 100%. 50 to 100% is preferable, and 100% is most preferable. The higher the halogenation rate, the better the acid strength.
The aryl group for R ⁴ ″ is preferably an aryl group having 6 to 20 carbon atoms.
The alkenyl group in R ⁴ ″ is preferably an alkenyl group having 2 to 10 carbon atoms.
In the above R ⁴ ″, “may have a substituent” means that a part or all of the hydrogen atoms in the alkyl group, halogenated alkyl group, aryl group, or alkenyl group are a substituent (hydrogen atom). It may be substituted with other atoms or groups).
The number of substituents in R ⁴ ″ may be one, or two or more.

Examples of the substituent include a halogen atom, a hetero atom, an alkyl group, and a formula: XQ ^1- [wherein Q ¹ is a divalent linking group containing an oxygen atom, and X has a substituent. And a hydrocarbon group having 3 to 30 carbon atoms. ] Etc. which are represented by these.
Examples of the halogen atom and alkyl group include the same groups as those described as the halogen atom and alkyl group in the halogenated alkyl group in R ⁴ ″.
Examples of the hetero atom include an oxygen atom, a nitrogen atom, and a sulfur atom.

X-Q 1 ^- In the group represented by, Q ¹ represents a divalent linking group containing an oxygen atom.
Q ¹ may contain an atom other than an oxygen atom. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, oxygen atoms, sulfur atoms, and nitrogen atoms.
Examples of the divalent linking group containing an oxygen atom include an oxygen atom (ether bond; —O—), an ester bond (—C (═O) —O—), and an amide bond (—C (═O) —NH. -), A carbonyl group (-C (= O)-), a non-hydrocarbon oxygen atom-containing linking group such as a carbonate bond (-O-C (= O) -O-); the non-hydrocarbon oxygen atom Examples include a combination of a containing linking group and an alkylene group.
Examples of the combination include —R ⁹¹ —O—, —R ⁹² —O—C (═O) —, —C (═O) —O—R ⁹³ —O—C (═O) — , R ^{91 to} R ⁹³ are each independently an alkylene group.) And the like.
The alkylene group for R ^{91 to} R ⁹³ is preferably a linear or branched alkylene group, and the alkylene group preferably has 1 to 12 carbon atoms, more preferably 1 to 5 carbon atoms, and particularly preferably 1 to 3 carbon atoms. preferable.
Specific examples of the alkylene group include a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ) ₂ —, —C ( _{CH 3) (CH 2 CH 3} ) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene group _[-CH 2 CH _2— ]; —CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH ₃ ) CH ₂ — and the like. Alkylethylene groups; trimethylene groups (n-propylene groups) [—CH ₂ CH ₂ CH ₂ —]; alkyls such as —CH (CH ₃ ) CH ₂ CH ₂ — and —CH ₂ CH (CH ₃ ) CH ₂ — trimethylene; tetramethylene group _[-CH 2 _CH 2 C _{2 CH 2 -]; - CH} (CH 3) CH 2 CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 CH 2 - alkyl tetramethylene group and the like; pentamethylene group _[-CH 2 _CH 2 CH ₂ CH ₂ CH ₂ —] and the like.
Q ¹ is preferably a divalent linking group containing an ester bond or an ether bond, and in particular, —R ⁹¹ —O—, —R ⁹² —O—C (═O) — or —C (═O) — O—R ⁹³ —O—C (═O) — is preferred.

In the group represented by XQ ^1- , the hydrocarbon group of X may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group.

The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon group preferably has 3 to 30 carbon atoms, more preferably 5 to 30, more preferably 5 to 20, still more preferably 6 to 15, and most preferably 6 to 12. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic hydrocarbon group include a hydrogen atom from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, and a phenanthryl group. Aryl groups such as aryl group, benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, 2-naphthylethyl group, etc., from which one is removed. The number of carbon atoms in the alkyl chain in the arylalkyl group is preferably 1 to 4, more preferably 1 to 2, and particularly preferably 1.

The aromatic hydrocarbon group may have a substituent. For example, a part of carbon atoms constituting the aromatic ring of the aromatic hydrocarbon group may be substituted with a hetero atom, and the hydrogen atom bonded to the aromatic ring of the aromatic hydrocarbon group is substituted with the substituent. May be.
Examples of the former include heteroaryl groups in which some of the carbon atoms constituting the ring of the aryl group are substituted with heteroatoms such as oxygen atoms, sulfur atoms, nitrogen atoms, and aromatic hydrocarbons in the arylalkyl groups. Examples include heteroarylalkyl groups in which some of the carbon atoms constituting the ring are substituted with the above heteroatoms.
Examples of the substituent of the aromatic hydrocarbon group in the latter example include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
The alkyl group as a substituent of the aromatic hydrocarbon group is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. preferable.
The alkoxy group as a substituent of the aromatic hydrocarbon group is preferably an alkoxy group having 1 to 5 carbon atoms, and is a methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group, tert- A butoxy group is preferable, and a methoxy group and an ethoxy group are most preferable.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Examples of the halogenated alkyl group as the substituent of the aromatic hydrocarbon group include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms.

The aliphatic hydrocarbon group for X may be a saturated aliphatic hydrocarbon group or an unsaturated aliphatic hydrocarbon group. The aliphatic hydrocarbon group may be linear, branched or cyclic.
In X, the aliphatic hydrocarbon group may have a part of the carbon atoms constituting the aliphatic hydrocarbon group substituted by a substituent containing a hetero atom, and the hydrogen atom constituting the aliphatic hydrocarbon group May be substituted with a substituent containing a hetero atom.
The “heteroatom” in X is not particularly limited as long as it is an atom other than a carbon atom and a hydrogen atom, and examples thereof include a halogen atom, an oxygen atom, a sulfur atom, and a nitrogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, an iodine atom, and a bromine atom.
The substituent containing a hetero atom may be composed of only the hetero atom, or may be a group containing a group or atom other than the hetero atom.
Specific examples of the substituent for substituting a part of the carbon atom include —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O. —, —C (═O) —NH—, —NH— (H may be substituted with a substituent such as an alkyl group, an acyl group, etc.), —S—, —S (═O) ₂ —, — S (= O) ₂ —O— and the like can be mentioned. When the aliphatic hydrocarbon group is cyclic, these substituents may be included in the ring structure.
Specific examples of the substituent for substituting part or all of the hydrogen atoms include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O), and a cyano group.
The alkoxy group is preferably an alkoxy group having 1 to 5 carbon atoms, preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group or a tert-butoxy group, and a methoxy group or an ethoxy group. Is most preferred.
As said halogen atom, a fluorine atom, a chlorine atom, a bromine atom, an iodine atom, etc. are mentioned, A fluorine atom is preferable.
As the halogenated alkyl group, a part or all of hydrogen atoms of an alkyl group having 1 to 5 carbon atoms, such as a methyl group, an ethyl group, a propyl group, an n-butyl group, a tert-butyl group, etc. And a group substituted with a halogen atom.

Examples of the aliphatic hydrocarbon group include a linear or branched saturated hydrocarbon group, a linear or branched monovalent unsaturated hydrocarbon group, or a cyclic aliphatic hydrocarbon group (aliphatic ring). Formula group) is preferred.
The linear saturated hydrocarbon group (alkyl group) preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. Specifically, for example, methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, isotridecyl group, tetradecyl group Group, pentadecyl group, hexadecyl group, isohexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, icosyl group, heicosyl group, docosyl group and the like.
The branched saturated hydrocarbon group (alkyl group) preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10 carbon atoms. Specifically, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, Examples include 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like.

As an unsaturated hydrocarbon group, it is preferable that carbon number is 2-10, 2-5 are preferable, 2-4 are preferable, and 3 is especially preferable. Examples of the linear monovalent unsaturated hydrocarbon group include a vinyl group, a propenyl group (allyl group), and a butynyl group. Examples of the branched monovalent unsaturated hydrocarbon group include a 1-methylpropenyl group and a 2-methylpropenyl group.
Among the above, the unsaturated hydrocarbon group is particularly preferably a propenyl group.

The aliphatic cyclic group may be a monocyclic group or a polycyclic group. The carbon number is preferably 3 to 30, more preferably 5 to 30, further preferably 5 to 20, particularly preferably 6 to 15, and most preferably 6 to 12.
Specifically, for example, a group in which one or more hydrogen atoms have been removed from a monocycloalkane; a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as bicycloalkane, tricycloalkane, tetracycloalkane, etc. Can be mentioned. More specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane; one or more polycycloalkanes such as adamantane, norbornane, isobornane, tricyclodecane, or tetracyclododecane. Examples include a group excluding a hydrogen atom.
When the aliphatic cyclic group does not contain a substituent containing a hetero atom in the ring structure, the aliphatic cyclic group is preferably a polycyclic group, and has one or more hydrogen atoms from the polycycloalkane. Excluded groups are preferred, and most preferred are groups in which one or more hydrogen atoms have been removed from adamantane.
When the aliphatic cyclic group includes a substituent containing a hetero atom in the ring structure, examples of the substituent containing a hetero atom include —O—, —C (═O) —O—, —S—. , —S (═O) ₂ — and —S (═O) ₂ —O— are preferable. Specific examples of the aliphatic cyclic group include groups represented by the following formulas (L1) to (L6) and (S1) to (S4).

［式中、Ｑ”は炭素数１〜５のアルキレン基、−Ｏ−、−Ｓ−、−Ｏ−Ｒ^９４−または−Ｓ−Ｒ^９５−であり、Ｒ^９４およびＲ^９５はそれぞれ独立に炭素数１〜５のアルキレン基であり、ｍは０または１の整数である。］

[Wherein, Q ″ is an alkylene group having 1 to 5 carbon atoms, —O—, —S—, —O—R ⁹⁴ — or —S—R ⁹⁵ —, wherein R ⁹⁴ and R ⁹⁵ are each independently carbon. An alkylene group of 1 to 5, and m is an integer of 0 or 1.]

In the formula, examples of the alkylene group for Q ″, R ⁹⁴ and R ⁹⁵ include the same alkylene groups as those described above for R ^{91 to} R ⁹³ .
In these aliphatic cyclic groups, a part of hydrogen atoms bonded to carbon atoms constituting the ring structure may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, and an oxygen atom (═O).
As said alkyl group, a C1-C5 alkyl group is preferable, and it is especially preferable that they are a methyl group, an ethyl group, a propyl group, n-butyl group, and a tert- butyl group.
Examples of the alkoxy group and the halogen atom are the same as those exemplified as the substituent for substituting part or all of the hydrogen atoms.

Among the above, X is preferably a cyclic group which may have a substituent. The cyclic group may be an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a substituent. It is preferably an aliphatic cyclic group that may be used.
The aromatic hydrocarbon group is preferably a naphthyl group which may have a substituent or a phenyl group which may have a substituent.
As the aliphatic cyclic group which may have a substituent, a polycyclic aliphatic cyclic group which may have a substituent is preferable. Examples of the polycyclic aliphatic cyclic group include groups obtained by removing one or more hydrogen atoms from the polycycloalkane, groups represented by the above (L2) to (L5) and (S3) to (S4). Etc. are preferred.

Further, X is particularly preferably one having a polar site because the lithography properties and the resist pattern shape are further improved.
As what has a polar site | part, the carbon atom which comprises the aliphatic cyclic group of X mentioned above, for example, the substituent in which a hetero atom contains, ie, -O-, -C (= O) -O-. , —C (═O) —, —O—C (═O) —O—, —C (═O) —NH—, —NH— (H is substituted with a substituent such as an alkyl group or an acyl group) may _{be), - S -, - S} (= O) 2 -, - S (= O) 2 -O- , etc., in include those substituted.

Among the above, ^{R 4} "is, ^{X-Q 1} - as a substituent preferably has the case, ^{R 4." The, X-Q 1 -Y 1 -} [ wherein, ^{Q 1} and X are Y ¹ is the same as the above, and Y ¹ is an optionally substituted alkylene group having 1 to 4 carbon atoms or an optionally substituted fluorinated alkylene group having 1 to 4 carbon atoms. ] Is preferable.
In the group represented by XQ ¹ -Y ^1- , the alkylene group for Y ¹ includes the same alkylene groups as those described above for Q ¹ having 1 to 4 carbon atoms.
Examples of the fluorinated alkylene group for Y ¹ include groups in which some or all of the hydrogen atoms of the alkylene group have been substituted with fluorine atoms.
As Y ^1, _{specifically, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 -, - CF (CF 2 CF 3) -, _{-C (CF 3) 2 -,} - CF 2 CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 CF 2 -, - CF 2 CF (CF 3) CF 2 -, - CF (CF 3) CF (CF ₃ ) —, —C (CF ₃ ) ₂ CF ₂ —, —CF (CF ₂ CF ₃ ) CF ₂ —, —CF (CF ₂ CF ₂ CF ₃ ) —, —C (CF ₃ ) (CF _{2 CF 3) -; - CHF} -, - CH 2 CF 2 -, - CH 2 CH 2 CF 2 -, - CH 2 CF 2 CF 2 -, - CH (CF 3) CH 2 -, - CH (CF 2 _{CF 3) -, - C (} CH 3) (CF 3) -, - CH 2 CH 2 CH 2 CF 2 -, - C H ₂ CH ₂ CF ₂ CF ₂ —, —CH (CF ₃ ) CH ₂ CH ₂ —, —CH ₂ CH (CF ₃ ) CH ₂ —, —CH (CF ₃ ) CH (CF ₃ ) —, —C ( _{CF 3) 2 CH 2 -;} - CH 2 -, - CH 2 CH 2 -, - CH 2 CH 2 CH 2 -, - CH (CH 3) CH 2 -, - CH (CH 2 CH 3) -, - _{C (CH 3) 2 -,} - CH 2 CH 2 CH 2 CH 2 -, - CH (CH 3) CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 -, - CH (CH 3) CH _{(CH 3) -, - C} (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - CH (CH 2 CH 2 CH 3) -, - C (CH 3) (CH 2 CH ₃ ) — and the like.

Y ¹ is preferably a fluorinated alkylene group, and particularly preferably a fluorinated alkylene group in which the carbon atom bonded to the adjacent sulfur atom is fluorinated. Examples of such fluorinated alkylene _{group, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, - CF (CF 3) CF 2 -, - CF 2 CF 2 CF 2 CF 2 _{-, - CF (CF 3)} CF 2 CF 2 -, - CF 2 CF (CF 3) CF 2 -, - CF (CF 3) CF (CF 3) -, - C (CF 3) 2 CF 2 -, _{-CF (CF 2 CF 3) CF} 2 -; - CH 2 CF 2 -, - CH 2 CH 2 CF 2 -, - CH 2 CF 2 CF 2 -; - CH 2 CH 2 CH 2 CF 2 -, - CH ₂ CH ₂ CF ₂ CF ₂ —, —CH ₂ CF ₂ CF ₂ CF ₂ — and the like can be mentioned.
Of _{these, -CF 2 -, - CF 2} CF 2 -, - CF 2 CF 2 CF 2 -, or _CH 2 _CF 2 CF ₂ - is _{preferable, -CF 2 -, - CF 2} CF 2 - or -CF ₂ CF ₂ CF ₂ - is more preferable, -CF ₂ - is particularly preferred.

The alkylene group or fluorinated alkylene group may have a substituent. An alkylene group or a fluorinated alkylene group has a “substituent” means that part or all of the hydrogen atom or fluorine atom in the alkylene group or fluorinated alkylene group is substituted with an atom or group other than a hydrogen atom and a fluorine atom. Means that
Examples of the substituent that the alkylene group or fluorinated alkylene group may have include an alkyl group having 1 to 4 carbon atoms, an alkoxy group having 1 to 4 carbon atoms, and a hydroxyl group.

In formula (b-2), R ⁵ ″ to R ⁶ ″ each independently represents an aryl group, alkyl group or alkenyl group which may have a substituent.
Moreover, it is preferable that at least one of R ⁵ ″ to R ⁶ ″ is an aryl group because lithography characteristics and the resist pattern shape are further improved, and any of R ⁵ ″ to R ⁶ ″ is an aryl group. More preferably.
As the aryl group for R ⁵ ″ to R ⁶ ″, the same as the aryl groups for R ¹ ″ to R ³ ″ can be used.
Examples of the alkyl group for R ⁵ ″ to R ⁶ ″ include the same as the alkyl group for R ¹ ″ to R ³ ″.
Examples of the alkenyl group for R ⁵ ″ to R ⁶ ″ include the same alkenyl groups for R ¹ ″ to R ³ ″.
Among these, it is most preferable that all of R ⁵ ″ to R ⁶ ″ are phenyl groups.
Specific examples of the cation moiety in the compound represented by the formula (b-2) include diphenyliodonium and bis (4-tert-butylphenyl) iodonium.
"The, ^{R 4} in the above formula (b-1)" ^{R 4} in the formula (b-2) include the same as.

  Specific examples of the onium salt acid generators represented by formulas (b-1) and (b-2) include diphenyliodonium trifluoromethanesulfonate or nonafluorobutanesulfonate, bis (4-tert-butylphenyl) iodonium. Trifluoromethane sulfonate or nonafluorobutane sulfonate, triphenylsulfonium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate, tri (4-methylphenyl) sulfonium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its Nonafluorobutanesulfonate, dimethyl (4-hydroxynaphthyl) sulfonium trifluoromethanesulfonate, its heptaful Lopropanesulfonate or its nonafluorobutanesulfonate, trifluoromethanesulfonate of monophenyldimethylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; trifluoromethanesulfonate of diphenylmonomethylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate (4-methylphenyl) diphenylsulfonium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate, (4-methoxyphenyl) diphenylsulfonium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate , Trifluoromethanesulfonate of tri (4-tert-butyl) phenylsulfonium, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate, trifluoromethanesulfonate of diphenyl (1- (4-methoxy) naphthyl) sulfonium, its heptafluoropropane Sulfonate or its nonafluorobutane sulfonate, di (1-naphthyl) phenyl sulphonium trifluoromethane sulphonate, its heptafluoropropane sulphonate or its nonafluorobutane sulphonate; 1-phenyltetrahydrothiophenium trifluoromethane sulphonate, its heptafluoropropane sulphonate Or nonafluorobutanesulfonate thereof; 1- (4-methylphenyl) ) Tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (3,5-dimethyl-4-hydroxyphenyl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropane sulfonate 1- (4-methoxynaphthalen-1-yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; 1- (4-ethoxynaphthalene-1- Yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nonaflu 1- (4-n-butoxynaphthalen-1-yl) tetrahydrothiophenium trifluoromethanesulfonate, its heptafluoropropanesulfonate or its nonafluorobutanesulfonate; 1-phenyltetrahydrothiopyranium trifluoromethanesulfonate , Its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (4-hydroxyphenyl) tetrahydrothiopyranium trifluoromethane sulfonate, its heptafluoropropane sulfonate or its nonafluorobutane sulfonate; 1- (3,5-dimethyl -4-Hydroxyphenyl) tetrahydrothiopyranium trifluoromethanesulfonate, its heptafluoropropanes Honeto or nonafluorobutanesulfonate; 1- (4-methylphenyl) trifluoromethanesulfonate tetrahydrothiophenium Pila chloride, heptafluoropropane sulfonate or its nonafluorobutane sulfonate, and the like.

  In addition, the anion portion of these onium salts may be substituted with methanesulfonate, n-propanesulfonate, n-butanesulfonate, n-octanesulfonate, 1-adamantansulfonate, 2-norbornanesulfonate, or the like; d-camphor-10-sulfonate Further, onium salts substituted with sulfonates such as benzenesulfonate, perfluorobenzenesulfonate, and p-toluenesulfonate can also be used.

  Moreover, the onium salt which replaced the anion part of these onium salts by the anion represented by either of following formula (b1)-(b9) can also be used.

［式中、ｙは１〜３の整数であり、ｑ１〜ｑ２はそれぞれ独立に１〜５の整数であり、ｑ３は１〜１２の整数であり、ｔ３は１〜３の整数であり、ｒ１〜ｒ２はそれぞれ独立に０〜３の整数であり、ｉは１〜２０の整数であり、Ｒ^５０は置換基であり、ｍ１〜ｍ６はそれぞれ独立に０または１であり、ｖ０〜ｖ６はそれぞれ独立に０〜３の整数であり、ｗ１〜ｗ６はそれぞれ独立に０〜３の整数であり、Ｑ”は前記と同じである。］

[Wherein y is an integer of 1 to 3, q1 and q2 are each independently an integer of 1 to 5, q3 is an integer of 1 to 12, t3 is an integer of 1 to 3, and r1 ~r2 are each independently an integer of 0 to 3, i is an integer of 1 to ^{20, R 50} is a substituent, m1 to m6 are each independently 0 or 1, v0~v6 each Are independently an integer of 0 to 3, w1 to w6 are each independently an integer of 0 to 3, and Q ″ is the same as above.]

Examples of the substituent for R ⁵⁰ are the same as those described above as the substituent that the aliphatic hydrocarbon group may have and the substituent that the aromatic hydrocarbon group may have in X. Can be mentioned.
Code (r1 and r2, W1 to W6) attached to R ⁵⁰ when it is 2 or more integer, a plurality of ^{R 50} in the compound may be the same, respectively, it may be different.

As the onium salt-based acid generator, in the general formula (b-1) or (b-2), the anion moiety ^(R 4 "SO ₃ ^-) of the following general formula (b-3) or (b- An onium salt acid generator substituted with the anion represented by 4) can also be used (the cation moiety is the same as the cation moiety in the formula (b-1) or (b-2)).

［式中、Ｘ”は、少なくとも１つの水素原子がフッ素原子で置換された炭素数２〜６のアルキレン基を表し；Ｙ”、Ｚ”は、それぞれ独立に、少なくとも１つの水素原子がフッ素原子で置換された炭素数１〜１０のアルキル基を表す。］

[Wherein X ″ represents an alkylene group having 2 to 6 carbon atoms in which at least one hydrogen atom is substituted with a fluorine atom; Y ″ and Z ″ each independently represent at least one hydrogen atom as a fluorine atom; Represents an alkyl group having 1 to 10 carbon atoms and substituted with

X ″ is a linear or branched alkylene group in which at least one hydrogen atom is substituted with a fluorine atom, and the alkylene group has 2 to 6 carbon atoms, preferably 3 to 5 carbon atoms, Most preferably, it has 3 carbon atoms.
Y ″ and Z ″ are each independently a linear or branched alkyl group in which at least one hydrogen atom is substituted with a fluorine atom, and the alkyl group has 1 to 10 carbon atoms, preferably Has 1 to 7 carbon atoms, more preferably 1 to 3 carbon atoms.
The carbon number of the alkylene group of X ″ or the carbon number of the alkyl group of Y ″ and Z ″ is preferably as small as possible because the solubility in the resist solvent is good within the above carbon number range.
In addition, in the alkylene group of X ″ or the alkyl group of Y ″ and Z ″, as the number of hydrogen atoms substituted with fluorine atoms increases, the strength of the acid increases, and high-energy light or electron beam of 200 nm or less This is preferable because the transparency to the surface is improved.
The proportion of fluorine atoms in the alkylene group or alkyl group, that is, the fluorination rate is preferably 70 to 100%, more preferably 90 to 100%, and most preferably all hydrogen atoms are substituted with fluorine atoms. A perfluoroalkylene group or a perfluoroalkyl group.

As the onium salt-based acid generator, in the general formula (b-1) or (b-2), anion ^{- a, R a -COO (R 4 "} SO 3) - [ wherein, ^{R a} Is an alkyl group or a fluorinated alkyl group.] An onium salt-based acid generator substituted with a cation moiety can also be used (the cation moiety is the same as the cation moiety in the formula (b-1) or (b-2)).
In the above formula, as R ^{a, the same} as R ⁴ ″ can be mentioned.
Specific examples of the “R ^a —COO ⁻ ” include trifluoroacetate ions, acetate ions, 1-adamantanecarboxylate ions and the like.

  Moreover, as an onium salt acid generator, a sulfonium salt having a cation represented by the following general formula (b-5) or (b-6) in the cation part can also be used.

［式中、Ｒ^８１〜Ｒ^８６はそれぞれ独立してアルキル基、アセチル基、アルコキシ基、カルボキシ基、水酸基またはヒドロキシアルキル基であり；ｎ_１〜ｎ_５はそれぞれ独立して０〜３の整数であり、ｎ_６は０〜２の整数である。］

[Wherein R ^{81 to} R ⁸⁶ are each independently an alkyl group, acetyl group, alkoxy group, carboxy group, hydroxyl group or hydroxyalkyl group; n _{1 to} n ₅ are each independently an integer of 0 to 3; There, _{n 6} is an integer of 0-2. ]

In R ^{81 to} R ⁸⁶ , the alkyl group is preferably an alkyl group having 1 to 5 carbon atoms, more preferably a linear or branched alkyl group, and a methyl group, an ethyl group, a propyl group, an isopropyl group, n A butyl group or a tert-butyl group is particularly preferable.
The alkoxy group is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a linear or branched alkoxy group, and particularly preferably a methoxy group or an ethoxy group.
The hydroxyalkyl group is preferably a group in which one or more hydrogen atoms in the alkyl group are substituted with a hydroxy group, and examples thereof include a hydroxymethyl group, a hydroxyethyl group, and a hydroxypropyl group.
When the symbols n _{1 to} n ₆ attached to R ^{81 to} R ⁸⁶ are integers of 2 or more, the plurality of R ^{81 to} R ⁸⁶ may be the same or different.
n ₁ is preferably 0 to 2, more preferably 0 or 1, and still more preferably 0.
n ₂ and n ₃ are preferably each independently 0 or 1, more preferably 0.
n ₄ is preferably 0 to 2, more preferably 0 or 1.
n ₅ is preferably 0 or 1, more preferably 0.
n ₆ is preferably 0 or 1, more preferably 1.

  Preferable examples of the cation represented by the formula (b-5) or the formula (b-6) include those shown below.

  Furthermore, the sulfonium salt which has the cation represented by the following general formula (b-7) or general formula (b-8) in a cation part can also be used.

In formulas (b-7) and (b-8), R ⁹ and R ¹⁰ are each independently a phenyl group, a naphthyl group, or an alkyl group having 1 to 5 carbon atoms, alkoxy, which may have a substituent. Group, hydroxyl group. Examples of the substituent include a substituent in the substituted aryl group exemplified in the description of the aryl group of R ¹ ″ to R ³ ″ (an alkyl group, an alkoxy group, an alkoxyalkyloxy group, an alkoxycarbonylalkyloxy group, a halogen atom). Atom, hydroxyl group, oxo group (═O), aryl group, —C (═O) —O—R ⁶ ′, —O—C (═O) —R ⁷ ′, —O—R ⁸ ′, the above general formula ^{: -O-R 50 -C (=} O) based on ^{R 56} is replaced by ^{R 56} 'in the ^{-O-R 56,} etc.) to be similar.
R ⁴ ′ is an alkylene group having 1 to 5 carbon atoms.
u is an integer of 1 to 3, and 1 or 2 is most preferable.
Preferable examples of the cation represented by the formula (b-7) or the formula (b-8) include those shown below. In the formula, R ^C represents a substituent (alkyl group, alkoxy group, alkoxyalkyloxy group, alkoxycarbonylalkyloxy group, halogen atom, hydroxyl group, oxo group (═O) exemplified in the description of the substituted aryl group. An aryl group, —C (═O) —O—R ⁶ ′, —O—C (═O) —R ⁷ ′, —O—R ⁸ ′).

The anion part of the sulfonium salt having a cation represented by formulas (b-5) to (b-8) in the cation part is not particularly limited, and the anion part of the onium salt acid generators proposed so far It may be similar. Examples of the anion moiety include fluorinated alkyl sulfonate ions such as the anion moiety (R ⁴ ″ SO ₃ ⁻ ) of the onium salt acid generator represented by the general formula (b-1) or (b-2). An anion represented by the general formula (b-3) or (b-4), an anion represented by any one of the formulas (b1) to (b9), and the like.

  In this specification, the oxime sulfonate acid generator is a compound having at least one group represented by the following general formula (B-1), and has a property of generating an acid upon irradiation (exposure) of radiation. It is what you have. Such oxime sulfonate-based acid generators are frequently used for chemically amplified resist compositions, and can be arbitrarily selected and used.

（式（Ｂ−１）中、Ｒ^３１、Ｒ^３２はそれぞれ独立に有機基を表す。）

(In formula (B-1), R ³¹ and R ³² each independently represents an organic group.)

The organic groups of R ³¹ and R ³² are groups containing carbon atoms, and atoms other than carbon atoms (for example, hydrogen atoms, oxygen atoms, nitrogen atoms, sulfur atoms, halogen atoms (fluorine atoms, chlorine atoms, etc.), etc.) You may have.
As the organic group for R ^31, a linear, branched, or cyclic alkyl group or aryl group is preferable. These alkyl groups and aryl groups may have a substituent. There is no restriction | limiting in particular as this substituent, For example, a fluorine atom, a C1-C6 linear, branched or cyclic alkyl group etc. are mentioned. Here, “having a substituent” means that part or all of the hydrogen atoms of the alkyl group or aryl group are substituted with a substituent.
As an alkyl group, C1-C20 is preferable, C1-C10 is more preferable, C1-C8 is more preferable, C1-C6 is especially preferable, and C1-C4 is the most preferable. As the alkyl group, a partially or completely halogenated alkyl group (hereinafter sometimes referred to as a halogenated alkyl group) is particularly preferable. The partially halogenated alkyl group means an alkyl group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated alkyl group means that all of the hydrogen atoms are halogen atoms. Means an alkyl group substituted with Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. That is, the halogenated alkyl group is preferably a fluorinated alkyl group.
The aryl group preferably has 4 to 20 carbon atoms, more preferably 4 to 10 carbon atoms, and most preferably 6 to 10 carbon atoms. As the aryl group, a partially or completely halogenated aryl group is particularly preferable. The partially halogenated aryl group means an aryl group in which a part of hydrogen atoms is substituted with a halogen atom, and the fully halogenated aryl group means that all of the hydrogen atoms are halogen atoms. Means an aryl group substituted with.
R ³¹ is particularly preferably an alkyl group having 1 to 4 carbon atoms having no substituent or a fluorinated alkyl group having 1 to 4 carbon atoms.
As the organic group for R ^32, a linear, branched, or cyclic alkyl group, aryl group, or cyano group is preferable. As the alkyl group and aryl group for R ^32, the same alkyl groups and aryl groups as those described above for R ³¹ can be used.
R ³² is particularly preferably a cyano group, an alkyl group having 1 to 8 carbon atoms having no substituent, or a fluorinated alkyl group having 1 to 8 carbon atoms.

  More preferable examples of the oxime sulfonate-based acid generator include compounds represented by the following general formula (B-2) or (B-3).

［式（Ｂ−２）中、Ｒ^３３は、シアノ基、置換基を有さないアルキル基またはハロゲン化アルキル基である。Ｒ^３４はアリール基である。Ｒ^３５は置換基を有さないアルキル基またはハロゲン化アルキル基である。］

[In Formula (B-2), R ³³ represents a cyano group, an alkyl group having no substituent, or a halogenated alkyl group. R ³⁴ is an aryl group. R ³⁵ represents an alkyl group having no substituent or a halogenated alkyl group. ]

［式（Ｂ−３）中、Ｒ^３６はシアノ基、置換基を有さないアルキル基またはハロゲン化アルキル基である。Ｒ^３７は２または３価の芳香族炭化水素基である。Ｒ^３８は置換基を有さないアルキル基またはハロゲン化アルキル基である。ｐ”は２または３である。］

[In Formula (B-3), R ³⁶ represents a cyano group, an alkyl group having no substituent, or a halogenated alkyl group. R ³⁷ is a divalent or trivalent aromatic hydrocarbon group. ^R38 is an alkyl group having no substituent or a halogenated alkyl group. p ″ is 2 or 3.]

In the general formula (B-2), the alkyl group or halogenated alkyl group having no substituent of R ³³ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and carbon atoms. Numbers 1 to 6 are most preferable.
R ³³ is preferably a halogenated alkyl group, more preferably a fluorinated alkyl group.
The fluorinated alkyl group for R ³³ is preferably such that the hydrogen atom of the alkyl group is 50% or more fluorinated, more preferably 70% or more fluorinated, and 90% or more fluorinated. Particularly preferred.
As the aryl group of R ³⁴ , one hydrogen atom is removed from an aromatic hydrocarbon ring such as a phenyl group, a biphenyl group, a fluorenyl group, a naphthyl group, an anthryl group, or a phenanthryl group. And a heteroaryl group in which a part of carbon atoms constituting the ring of these groups is substituted with a heteroatom such as an oxygen atom, a sulfur atom, or a nitrogen atom. Among these, a fluorenyl group is preferable.
The aryl group of R ³⁴ may have a substituent such as an alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or an alkoxy group. The alkyl group or halogenated alkyl group in the substituent preferably has 1 to 8 carbon atoms, and more preferably 1 to 4 carbon atoms. The halogenated alkyl group is preferably a fluorinated alkyl group.
The alkyl group or halogenated alkyl group having no substituent of R ³⁵ preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and most preferably 1 to 6 carbon atoms.
R ³⁵ is preferably a halogenated alkyl group, more preferably a fluorinated alkyl group.
The fluorinated alkyl group for R ³⁵ is preferably such that the hydrogen atom of the alkyl group is 50% or more fluorinated, more preferably 70% or more fluorinated, and 90% or more fluorinated. Particularly preferred is the strength of the acid generated. Most preferably, it is a fully fluorinated alkyl group in which a hydrogen atom is 100% fluorine-substituted.

In the general formula (B-3), the alkyl group or halogenated alkyl group having no substituent for R ³⁶ is the same as the alkyl group or halogenated alkyl group having no substituent for R ^33. Is mentioned.
Examples of the divalent or trivalent aromatic hydrocarbon group for R ³⁷ include groups obtained by further removing one or two hydrogen atoms from the aryl group for R ³⁴ .
Examples of the alkyl group or halogenated alkyl group having no substituent of R ³⁸ include the same alkyl groups or halogenated alkyl groups as those having no substituent of R ³⁵ .
p ″ is preferably 2.

Specific examples of the oxime sulfonate acid generator include α- (p-toluenesulfonyloxyimino) -benzyl cyanide, α- (p-chlorobenzenesulfonyloxyimino) -benzyl cyanide, α- (4-nitrobenzenesulfonyloxy). Imino) -benzylcyanide, α- (4-nitro-2-trifluoromethylbenzenesulfonyloxyimino) -benzylcyanide, α- (benzenesulfonyloxyimino) -4-chlorobenzylcyanide, α- (benzenesulfonyl) Oxyimino) -2,4-dichlorobenzyl cyanide, α- (benzenesulfonyloxyimino) -2,6-dichlorobenzyl cyanide, α- (benzenesulfonyloxyimino) -4-methoxybenzyl cyanide, α- ( 2-Chlorobenzenesulfonyloxyimino) 4-methoxybenzylcyanide, α- (benzenesulfonyloxyimino) -thien-2-ylacetonitrile, α- (4-dodecylbenzenesulfonyloxyimino) -benzylcyanide, α-[(p-toluenesulfonyloxyimino) -4-methoxyphenyl] acetonitrile, α-[(dodecylbenzenesulfonyloxyimino) -4-methoxyphenyl] acetonitrile, α- (tosyloxyimino) -4-thienyl cyanide, α- (methylsulfonyloxyimino) -1-cyclo Pentenyl acetonitrile, α- (methylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (methylsulfonyloxyimino) -1-cycloheptenylacetonitrile, α- (methylsulfonyloxyimino) -1-cyclooctene Acetonitrile, α- (trifluoromethylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (trifluoromethylsulfonyloxyimino) -cyclohexylacetonitrile, α- (ethylsulfonyloxyimino) -ethylacetonitrile, α- (propyl Sulfonyloxyimino) -propylacetonitrile, α- (cyclohexylsulfonyloxyimino) -cyclopentylacetonitrile, α- (cyclohexylsulfonyloxyimino) -cyclohexylacetonitrile, α- (cyclohexylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- ( Ethylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (isopropylsulfonyloxyimino) -1-cyclope N-tenyl acetonitrile, α- (n-butylsulfonyloxyimino) -1-cyclopentenylacetonitrile, α- (ethylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (isopropylsulfonyloxyimino) -1-cyclohexenylacetonitrile , Α- (n-butylsulfonyloxyimino) -1-cyclohexenylacetonitrile, α- (methylsulfonyloxyimino) -phenylacetonitrile, α- (methylsulfonyloxyimino) -p-methoxyphenylacetonitrile, α- (trifluoro Methylsulfonyloxyimino) -phenylacetonitrile, α- (trifluoromethylsulfonyloxyimino) -p-methoxyphenylacetonitrile, α- (ethylsulfonyloxyimino) -p- Butoxy phenylacetonitrile, alpha-(propylsulfonyl oxyimino)-p-methylphenyl acetonitrile, alpha-like (methylsulfonyloxyimino)-p-bromophenyl acetonitrile.
Further, an oxime sulfonate-based acid generator disclosed in JP-A-9-208554 (paragraphs [0012] to [0014] [chemical formula 18] to [chemical formula 19]), pamphlet of International Publication No. 04/074242, An oxime sulfonate-based acid generator disclosed in Examples 1 to 40) on pages 65 to 85 can also be suitably used.
Moreover, the following can be illustrated as a suitable thing.

Among diazomethane acid generators, specific examples of bisalkyl or bisarylsulfonyldiazomethanes include bis (isopropylsulfonyl) diazomethane, bis (p-toluenesulfonyl) diazomethane, bis (1,1-dimethylethylsulfonyl) diazomethane, Examples include bis (cyclohexylsulfonyl) diazomethane, bis (2,4-dimethylphenylsulfonyl) diazomethane, and the like.
Further, diazomethane acid generators disclosed in JP-A-11-035551, JP-A-11-035552, and JP-A-11-035573 can also be suitably used.
Examples of poly (bissulfonyl) diazomethanes include 1,3-bis (phenylsulfonyldiazomethylsulfonyl) propane and 1,4-bis (phenylsulfonyldiazo) disclosed in JP-A-11-322707. Methylsulfonyl) butane, 1,6-bis (phenylsulfonyldiazomethylsulfonyl) hexane, 1,10-bis (phenylsulfonyldiazomethylsulfonyl) decane, 1,2-bis (cyclohexylsulfonyldiazomethylsulfonyl) ethane, 1,3 -Bis (cyclohexylsulfonyldiazomethylsulfonyl) propane, 1,6-bis (cyclohexylsulfonyldiazomethylsulfonyl) hexane, 1,10-bis (cyclohexylsulfonyldiazomethylsulfonyl) decane, etc. Door can be.

As the component (B), one type of acid generator described above may be used alone, or two or more types may be used in combination.
The content of the component (B) in the resist composition of the present invention is preferably 0.5 to 40 parts by mass, and preferably 1 to 35 parts by mass with respect to 100 parts by mass in total of the component (A ′) and the component (C) described later. Part is more preferable, and 3 to 30 parts by mass is even more preferable. By setting it as the said range, when each component of a resist composition is melt | dissolved in the organic solvent, since a uniform solution is obtained and storage stability becomes favorable, it is preferable.

<Other optional components>
The resist composition of the present invention does not fall under the component (A1 ′) as long as the effect of the present invention is not impaired, and is a base material component that increases polarity by the action of an acid (hereinafter referred to as “(C) component”). It may contain.
The “base component” means an organic compound having a film forming ability as described above.
The component (C) is not particularly limited, and can be appropriately selected from those conventionally used as the base component of the chemically amplified resist composition. As the component (C), a resin may be used, a low molecular compound may be used, or these may be used in combination. As the component (C), one type may be used alone, or two or more types may be used in combination.
Examples of the resin used as the component (C) include a chemically amplified resist composition used for forming a positive resist pattern in an alkali development process or a negative resist pattern in a solvent development process. Any number of conventionally known base components for the chemically amplified resist composition used (for example, base resins for ArF excimer laser, KrF excimer laser (preferably for ArF excimer laser), etc.) Select and use. For example, as a resin used as a base component for an ArF excimer laser, the structural unit (a1) is an essential structural unit, and the structural units (a0), (a2), (a3), Examples thereof include a resin further having (a4) and the like.
As the low molecular weight compound used as the component (C), for example, an acid dissociable group having a molecular weight of 500 or more and less than 4000 and exemplified in the above description of the component (A1 ′) and a hydrophilic group may be used. The thing which has. Specific examples of the low molecular weight compound include compounds in which a part of hydrogen atoms of a hydroxyl group in a compound having a plurality of phenol skeletons is substituted with the acid dissociable group.

The resist composition of the present invention further contains a nitrogen-containing organic compound component (D) (hereinafter referred to as “component (D)”) that does not correspond to the components (A ′), (B), and (C). Also good.
The component (D) is not particularly limited as long as it acts as an acid diffusion control agent, that is, a quencher that traps the acid generated from the component (A ′) or the component (B) by exposure. Any known one may be used arbitrarily. Examples thereof include amines such as aliphatic amines and aromatic amines, among which aliphatic amines, particularly secondary aliphatic amines and tertiary aliphatic amines are preferred.
An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 20 carbon atoms.
Examples of the aliphatic amine include an amine (alkylamine or alkyl alcohol amine) or a cyclic amine in which at least one hydrogen atom of ammonia NH ₃ is substituted with an alkyl group or hydroxyalkyl group having 20 or less carbon atoms. .
The alkyl group and the alkyl group in the hydroxyalkyl group may be linear, branched or cyclic.
When the alkyl group is linear or branched, the carbon number thereof is more preferably 2-20, and further preferably 2-8.
When the alkyl group is cyclic (when it is a cycloalkyl group), the carbon number is preferably 3 to 30, more preferably 3 to 20, still more preferably 3 to 15, and 4 to 12 carbon atoms. It is particularly preferred that the number of carbon atoms is 5-10. The alkyl group may be monocyclic or polycyclic. Specific examples include groups in which one or more hydrogen atoms have been removed from monocycloalkane, groups in which one or more hydrogen atoms have been removed from polycycloalkanes such as bicycloalkane, tricycloalkane, and tetracycloalkane. . Specific examples of the monocycloalkane include cyclopentane and cyclohexane. Specific examples of the polycycloalkane include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane.
Specific examples of the alkylamine include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decylamine; diethylamine, di-n-propylamine, di-n- Dialkylamines such as heptylamine, di-n-octylamine, dicyclohexylamine; trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine, tri- and trialkylamines such as n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decanylamine, and tri-n-dodecylamine.
Specific examples of the alkyl alcohol amine include diethanolamine, triethanolamine, diisopropanolamine, triisopropanolamine, di-n-octanolamine, tri-n-octanolamine, stearyl diethanolamine, lauryldiethanolamine and the like.
Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be monocyclic (aliphatic monocyclic amine) or polycyclic (aliphatic polycyclic amine).
Specific examples of the aliphatic monocyclic amine include piperidine and piperazine.
As the aliphatic polycyclic amine, those having 6 to 10 carbon atoms are preferable. Specifically, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5. 4.0] -7-undecene, hexamethylenetetramine, 1,4-diazabicyclo [2.2.2] octane, and the like.
Other aliphatic amines include tris (2-methoxymethoxyethyl) amine, tris {2- (2-methoxyethoxy) ethyl} amine, tris {2- (2-methoxyethoxymethoxy) ethyl} amine, tris {2- (1-methoxyethoxy) ethyl} amine, tris {2- (1-ethoxyethoxy) ethyl} amine, tris {2- (1-ethoxypropoxy) ethyl} amine, tris [2- {2- (2-hydroxyethoxy) ) Ethoxy} ethylamine and the like.
Examples of the aromatic amine include aniline, pyridine, 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, diphenylamine, triphenylamine, and tribenzylamine.
These may be used alone or in combination of two or more.
(D) component is normally used in 0.01-5.0 mass parts with respect to a total of 100 mass parts of (A ') component and (C) component. By setting the content in the above range, the resist pattern shape, the stability over time and the like are improved.

  The resist composition of the present invention is a monovalent group represented by the following general formula (h1) or the like for the purpose of improving MEF, preventing sensitivity deterioration, and improving the resist pattern shape, retention stability over time, etc. It is preferable to contain a compound having a monovalent group represented by the general formula (h2) (hereinafter, this compound is referred to as “component (H)”).

［式（ｈ１）中、Ｒ^４は単結合又は−Ｃ（＝Ｏ）−Ｏ−基である。Ｒ^７はフッ素原子で置換されていてもよい、炭素数１〜１０の直鎖状若しくは分岐鎖状の１価の炭化水素基、炭素数３〜２０の環状の１価の炭化水素基、又は炭素数３〜２０の環状の部分構造を有する１価の炭化水素基である。］

[In the formula (h1), R ⁴ represents a single bond or a —C (═O) —O— group. R ⁷ may be substituted with a fluorine atom, a linear or branched monovalent hydrocarbon group having 1 to 10 carbon atoms, a cyclic monovalent hydrocarbon group having 3 to 20 carbon atoms, or It is a monovalent hydrocarbon group having a cyclic partial structure having 3 to 20 carbon atoms. ]

In the formula (h1), R ⁴ is a single bond or a —C (═O) —O— group, and preferably a single bond.
The linear or branched monovalent hydrocarbon group for R ⁷ preferably has 1 to 5 carbon atoms, and more preferably 1 to 3 carbon atoms.
The cyclic monovalent hydrocarbon group for R ⁷ preferably has 3 to 12 carbon atoms.
Examples of the monovalent hydrocarbon group having a cyclic partial structure in R ⁷ include a group in which a cyclic hydrocarbon is bonded to the end of a linear or branched hydrocarbon group, and a cyclic hydrocarbon in a linear form. Or the group etc. which intervene in the middle of the branched hydrocarbon group are mentioned. The cyclic partial structure preferably has 3 to 12 carbon atoms.
In R ⁷ , a linear or branched monovalent hydrocarbon group, a cyclic monovalent hydrocarbon group, and a monovalent hydrocarbon group having a cyclic partial structure are each in the hydrocarbon group. Part or all of the hydrogen atoms may be substituted with fluorine atoms or may not be substituted. The substituent may be substituted with a substituent other than a fluorine atom, and examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorinated alkyl group having 1 to 5 carbon atoms, and an oxygen atom (= O). Can be mentioned.

  Specific examples of the component (H) include compounds (Hm-3) represented by the following general formula (h1-2) and compounds (Hm-4) represented by the general formula (h2-2). Examples include molecular compound components.

［式（ｈ１−２）中、Ｒ^５はフッ素原子、ヒドロキシ基、−Ｏ−Ｒ^１０基、−ＮＨ−Ｃ（＝Ｏ）−Ｒ^１０基、−Ｏ−Ｃ（＝Ｏ）−Ｒ^１０基、又は−Ｃ（＝Ｏ）−Ｏ−Ｒ^１０基（但し、Ｒ^１０は炭素数１〜１０の直鎖状若しくは分岐鎖状の１価の炭化水素基、炭素数３〜２０の環状の１価の炭化水素基、又は炭素数３〜２０の環状の部分構造を有する１価の炭化水素基を示す。）で置換されていてもよい、炭素数１〜２０の直鎖状若しくは分岐鎖状の１価の炭化水素基、炭素数３〜２０の環状の１価の炭化水素基、炭素数３〜２０の環状の部分構造を有する１価の炭化水素基、又は水素原子である。Ｒ^４は単結合又は−Ｃ（＝Ｏ）−Ｏ−基である。Ｒ^７はフッ素原子で置換されていてもよい、炭素数１〜１０の直鎖状若しくは分岐鎖状の１価の炭化水素基、炭素数３〜２０の環状の１価の炭化水素基、又は炭素数３〜２０の環状の部分構造を有する１価の炭化水素基である。式（ｈ２−２）中、Ｒ^８はフッ素原子、ヒドロキシ基、−Ｏ−Ｒ^１０基、−Ｏ−Ｃ（＝Ｏ）−Ｒ^１０基、又は−Ｃ（＝Ｏ）−Ｏ−Ｒ^１０基（但し、Ｒ^１０は炭素数１〜１０の直鎖状若しくは分岐鎖状の１価の炭化水素基、炭素数３〜２０の環状の１価の炭化水素基、又は炭素数３〜２０の環状の部分構造を有する１価の炭化水素基を示す。）で置換されていてもよい、炭素数１〜２０の直鎖状若しくは分岐鎖状の１価の炭化水素基、炭素数３〜２０の環状の１価の炭化水素基、又は炭素数３〜２０の環状の部分構造を有する１価の炭化水素基である。］

[In the formula (h1-2), R ⁵ represents a fluorine atom, a hydroxy group, —O—R ¹⁰ group, —NH—C (═O) —R ¹⁰ group, —O—C (═O) —R ¹⁰ group. , Or —C (═O) —O—R ¹⁰ group (where R ¹⁰ is a linear or branched monovalent hydrocarbon group having 1 to 10 carbon atoms, cyclic 1 having 3 to 20 carbon atoms, or A monovalent hydrocarbon group or a monovalent hydrocarbon group having a cyclic partial structure having 3 to 20 carbon atoms), which may be substituted with a linear or branched chain having 1 to 20 carbon atoms. These are monovalent hydrocarbon groups, cyclic monovalent hydrocarbon groups having 3 to 20 carbon atoms, monovalent hydrocarbon groups having a cyclic partial structure having 3 to 20 carbon atoms, or hydrogen atoms. R ⁴ is a single bond or a —C (═O) —O— group. R ⁷ may be substituted with a fluorine atom, a linear or branched monovalent hydrocarbon group having 1 to 10 carbon atoms, a cyclic monovalent hydrocarbon group having 3 to 20 carbon atoms, or It is a monovalent hydrocarbon group having a cyclic partial structure having 3 to 20 carbon atoms. In the formula (h2-2), R ⁸ is a fluorine atom, a hydroxy group, —O—R ¹⁰ group, —O—C (═O) —R ¹⁰ group, or —C (═O) —O—R ¹⁰ group. (However, R ¹⁰ is a linear or branched monovalent hydrocarbon group having 1 to ¹⁰ carbon atoms, a cyclic monovalent hydrocarbon group having 3 to 20 carbon atoms, or a cyclic group having 3 to 20 carbon atoms. A linear or branched monovalent hydrocarbon group having 1 to 20 carbon atoms, which may be substituted, and having 3 to 20 carbon atoms. A cyclic monovalent hydrocarbon group or a monovalent hydrocarbon group having a cyclic partial structure having 3 to 20 carbon atoms. ]

Compound (Hm-3):
In formula (h1-2), R ⁴ and R ⁷ are the same as R ⁴ and R ^{7 in} formula (h1).
In formula (h1-2), for R ⁵ , the linear or branched monovalent hydrocarbon group in R ¹⁰ has 1 to 10 carbon atoms, preferably 1 to 5, and preferably 1 to 3 More preferred. Examples of the linear or branched monovalent hydrocarbon group for R ¹⁰ include methyl group, ethyl group, n-propyl group, i-propyl group, n-butyl group, i-butyl group, sec-butyl. Group, tert-butyl group, n-pentyl group, i-pentyl group, n-hexyl group, n-heptyl group, n-octyl group, n-nonyl group, n-decyl group and the like.
The cyclic monovalent hydrocarbon group for R ¹⁰ has 3 to 20 carbon atoms, preferably 3 to 12 carbon atoms. The cyclic monovalent hydrocarbon group in R ¹⁰ is a group obtained by removing one or more hydrogen atoms from a monocycloalkane; one or more polycycloalkanes such as bicycloalkane, tricycloalkane, tetracycloalkane and the like. Examples include a group excluding a hydrogen atom. Specifically, a group in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane, cyclohexane or cyclooctane; one from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane Examples include groups in which the above hydrogen atoms have been removed.
Examples of the monovalent hydrocarbon group having a cyclic partial structure in R ¹⁰ include a group in which a cyclic hydrocarbon is bonded to the end of a linear or branched hydrocarbon group, and a cyclic hydrocarbon in a linear form. Or the group etc. which intervene in the middle of the branched hydrocarbon group are mentioned. The cyclic partial structure has 3 to 20 carbon atoms, preferably 3 to 12 carbon atoms, a group obtained by removing one or more hydrogen atoms from the above-mentioned monocycloalkane, and one or more groups from polycycloalkane. Examples include a group excluding a hydrogen atom.
In R ¹⁰ , a linear or branched monovalent hydrocarbon group, a cyclic monovalent hydrocarbon group, and a monovalent hydrocarbon group having a cyclic partial structure are each in the hydrocarbon group. Part or all of the hydrogen atoms may be substituted with fluorine atoms or may not be substituted. The substituent may be substituted with a substituent other than a fluorine atom, and examples of the substituent include an alkyl group having 1 to 5 carbon atoms, a fluorinated alkyl group having 1 to 5 carbon atoms, and an oxygen atom (= O). Can be mentioned.

The linear or branched monovalent hydrocarbon group for R ⁵ has 1 to 20 carbon atoms, preferably 1 to 15 carbon atoms, more preferably 1 to 10 carbon atoms, and further preferably 1 to 5 carbon atoms. However, the carbon number does not include the carbon number in the substituent.
Examples of the linear or branched monovalent hydrocarbon group in R ⁵ include methyl group, ethyl group, n-propyl group, i-propyl group, n-butyl group, i-butyl group, sec-butyl. Group, tert-butyl group, n-pentyl group, i-pentyl group, n-hexyl group, n-heptyl group, n-octyl group, n-nonyl group, n-decyl group, undecyl group, dodecyl group, tridecyl group I-tridecyl group, tetradecyl group, pentadecyl group, hexadecyl group, i-hexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, icosyl group and the like.
In R ⁵ , a cyclic monovalent hydrocarbon group having 3 to 20 carbon atoms and a monovalent hydrocarbon group having a cyclic partial structure having 3 to 20 carbon atoms are those having 3 to 20 carbon atoms in R ¹⁰ . Examples thereof include a cyclic monovalent hydrocarbon group and a monovalent hydrocarbon group having a cyclic partial structure having 3 to 20 carbon atoms. In addition, the cyclic hydrocarbon group may be an aromatic hydrocarbon group. The aromatic hydrocarbon group is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon group preferably has 5 to 20 carbon atoms, more preferably 6 to 15 carbon atoms, and particularly preferably 6 to 12 carbon atoms. However, the carbon number does not include the carbon number in the substituent.
Regarding the aromatic hydrocarbon group, the aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n + 2 (where n is 0 and a natural number) π electrons, and may be monocyclic or polycyclic. Good. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; aromatic heterocycles in which a part of carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms, and the like. Can be mentioned. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom. Specific examples of the aromatic heterocycle include a pyridine ring and a thiophene ring.
Specifically, the aromatic hydrocarbon group is a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring or aromatic heterocyclic ring (aryl group or heteroaryl group); an aromatic group containing two or more aromatic rings A group in which one hydrogen atom has been removed from a compound (for example, biphenyl, fluorene, etc.); a group in which one of the hydrogen atoms of the aromatic hydrocarbon ring or aromatic heterocyclic ring is substituted with an alkylene group (for example, a benzyl group, a phenethyl group) 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, arylalkyl groups such as 2-naphthylethyl group) and the like. The number of carbon atoms of the alkylene group bonded to the aromatic hydrocarbon ring or aromatic heterocyclic ring is preferably 1 to 4, more preferably 1 to 2, and particularly preferably 1.

The aromatic hydrocarbon group is a fluorine atom, a hydroxy group, -O-R ¹⁰ group, -NH-C (= O) -R ¹⁰ group, -O-C (= O) -R ¹⁰ group, or -C. In addition to the (= O) -O-R ¹⁰ group, it may have a substituent. For example, the hydrogen atom bonded to the aromatic ring of the aromatic hydrocarbon group may be substituted with a substituent.
Examples of the substituent of the aromatic hydrocarbon group include an alkyl group, a halogen atom other than a fluorine atom, a halogenated alkyl group, and an oxygen atom (═O).
As the alkyl group as a substituent of the aromatic hydrocarbon group, an alkyl group having 1 to 5 carbon atoms is preferable, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. preferable.
Examples of the halogen atom as a substituent for the aromatic hydrocarbon group include a chlorine atom, a bromine atom, and an iodine atom. Examples of the halogenated alkyl group as the substituent for the aromatic hydrocarbon group include groups in which part or all of the hydrogen atoms of the alkyl group have been substituted with chlorine, bromine or iodine atoms.

  Specific examples of the compound (Hm-3) include the following compounds.

Compound (Hm-4):
The compound (Hm-4) is a compound represented by the general formula (h2-2).
In formula (h2-2), R ⁸ is the same as described for R ⁵ in formula (h1-2). Specific examples of the compound (Hm-4) include the following compounds.

In the resist composition, the component (H) may be used alone or in combination of two or more.
In the resist composition, the content of the component (H) is preferably 0.1 to 15 parts by mass with respect to 100 parts by mass of the base component (total of the components (A ′) and (C)) of the resist composition. 0.3-7 parts by mass is more preferable, and 0.5-5 parts by mass is particularly preferable. (F) MEF improves more because content of a component exists in the said range.

The resist composition of the present invention may further contain a fluorine additive (hereinafter referred to as “component (F)”) in order to impart water repellency to the resist film.
As the component (F), for example, a fluorine-containing polymer compound described in JP 2010-002870 A can be used.
More specifically, examples of the component (F) include a polymer having a structural unit (f1) represented by the following formula (f1-1). As such a polymer, a polymer (homopolymer) consisting only of the structural unit (f1); a copolymer of the structural unit represented by the following formula (f1-1) and the structural unit (a1); It is preferable that it is a copolymer of the structural unit represented by (f1-1), the structural unit derived from acrylic acid or methacrylic acid, and the said structural unit (a1). Here, as the structural unit (a1) copolymerized with the structural unit represented by the following formula (f1-1), the structural unit represented by the formula (a1-0-11) is preferable. The structural unit represented by (a1-1-02) is more preferred, and the structural unit represented by the formula (a1-1-32) is particularly preferred.

［式中、Ｒは前記同様であり、Ｒ^４５およびＲ^４６はそれぞれ独立して水素原子、ハロゲン原子、炭素数１〜５のアルキル基、又は炭素数１〜５のハロゲン化アルキル基を表し、複数のＲ^４５またはＲ^４６は同じであっても異なっていてもよい。ａ１は１〜５の整数であり、Ｒ^７”はフッ素原子を含む有機基である。］

[Wherein, R is the same as defined above, and R ⁴⁵ and R ⁴⁶ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, The plurality of R ⁴⁵ or R ⁴⁶ may be the same or different. a1 is an integer of 1 to 5, and R ⁷ ″ is an organic group containing a fluorine atom.]

In formula (f1-1), R is the same as described above. R is preferably a hydrogen atom or a methyl group.
In formula (f1-1), examples of the halogen atom for R ⁴⁵ and R ⁴⁶ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. Examples of the alkyl group having 1 to 5 carbon atoms of R ⁴⁵ and R ⁴⁶ include the same as the alkyl group having 1 to 5 carbon atoms of R, and a methyl group or an ethyl group is preferable. Specific examples of the halogenated alkyl group having 1 to 5 carbon atoms of R ⁴⁵ and R ⁴⁶ include a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with a halogen atom. Can be mentioned. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. Especially, as R < ⁴⁵ >, R ^<46 >, a hydrogen atom, a fluorine atom, or a C1-C5 alkyl group is preferable, and a hydrogen atom, a fluorine atom, a methyl group, or an ethyl group is preferable.
In formula (f1-1), a1 is an integer of 1 to 5, preferably an integer of 1 to 3, and more preferably 1 or 2.

In formula (f1-1), R ⁷ ″ is an organic group containing a fluorine atom, and is preferably a hydrocarbon group containing a fluorine atom.
The hydrocarbon group containing a fluorine atom may be linear, branched or cyclic, and preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms. The carbon number of 1 to 10 is particularly preferable.
The hydrocarbon group containing a fluorine atom preferably has 25% or more of the hydrogen atoms in the hydrocarbon group fluorinated, more preferably 50% or more fluorinated, and 60% or more. Fluorination is particularly preferable because the hydrophobicity of the resist film during immersion exposure is increased.
Among these, as R ⁷ ″, a fluorinated hydrocarbon group having 1 to 5 carbon atoms is particularly preferable, and a methyl group, —CH ₂ —CF ₃ , —CH ₂ —CF ₂ —CF ₃ , —CH (CF ₃ ) _{2, -CH 2 -CH 2 -CF 3} , and most preferably _{-CH 2 -CH 2 -CF 2 -CF 2} -CF 2 -CF 3.

(F) As for the mass mean molecular weight (Mw) (polystyrene conversion reference | standard by gel permeation chromatography), 1000-50000 are preferable, 5000-40000 are more preferable, and 10000-30000 are the most preferable. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent to be used as a resist, and if it is above the lower limit of this range, dry etching resistance and resist pattern cross-sectional shape are good.
The dispersity (Mw / Mn) of the component (F) is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and most preferably 1.2 to 2.5.

(F) A component may be used individually by 1 type and may use 2 or more types together.
When the resist composition of the present invention contains the component (F), the content of the component (F) is 100 parts by mass of the base material component (total of the components (A ′) and (C)) of the resist composition. It is used at a ratio of 0.5 to 10 parts by mass.

  The resist composition of the present invention may further contain, if desired, miscible additives such as an additional resin for improving the performance of the resist film, a surfactant for improving coatability, a dissolution inhibitor, Plasticizers, stabilizers, colorants, antihalation agents, dyes, and the like can be added and contained as appropriate.

The resist composition of the present invention can be produced by dissolving the material in an organic solvent (hereinafter sometimes referred to as “(S) component”).
As the component (S), any component can be used as long as it can dissolve each component to be used to form a uniform solution. Conventionally, any one of known solvents for chemically amplified resists can be used. Two or more types can be appropriately selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone, cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, and 2-heptanone; Monohydric alcohols; compounds having an ester bond, such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, dipropylene glycol monoacetate, monomethyl ether, monoethyl of the polyhydric alcohols or compound having the ester bond Ether alkyl such as ether, monopropyl ether, monobutyl ether or monophenyl ether Derivatives of polyhydric alcohols such as compounds having a propylene glycol monomethyl ether acetate (PGMEA) or propylene glycol monomethyl ether (PGME) among these]; cyclic ethers such as dioxane, methyl lactate, Esters such as ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate; anisole, ethyl benzyl ether, cresyl methyl ether, diphenyl ether, Aromatic organics such as dibenzyl ether, phenetol, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene, mesitylene A solvent etc. can be mentioned.
These organic solvents may be used independently and may be used as 2 or more types of mixed solvents.
Among these, propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), cyclohexanone, and EL are preferable.
Moreover, the mixed solvent which mixed PGMEA and the polar solvent is also preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA and the polar solvent, preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. It is preferable to be within the range. For example, when EL is blended as a polar solvent, the mass ratio of PGMEA: EL is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3. Further, when PGME and cyclohexanone are blended as polar solvents, the mass ratio of PGMEA: (PGME + cyclohexanone) is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2, and even more preferably 3. : 7 to 7: 3.
In addition, as the component (S), PGMEA, EL or a mixed solvent of PGMEA and a polar solvent and a mixed solvent of γ-butyrolactone are also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
The amount of component (S) used is not particularly limited, but is a concentration that can be applied to a substrate or the like, and is appropriately set according to the coating film thickness. In general, the solid content concentration of the resist composition is 1 -20% by mass, preferably 2-15% by mass.

The resist composition of the present invention described above contains a base material component (A ′) that changes its solubility in a developing solution by the action of an acid and generates an acid upon exposure, and the (A ′) component contains: The resin component (A1 ′) having the structural unit (a5), the structural unit (a1), and the structural unit (a3) is contained.
When selective exposure is performed on a resist film formed using such a resist composition, an acid is generated from the structural unit (a5). Therefore, the component (A1 ′) can be used as an acid generator for a chemically amplified resist composition. In addition, since the component (A1 ′) is a resin, it also functions as a base component (base resin) of the resist composition, and a film (resist film) can be formed by the component (A1 ′) alone.
In addition, the component (A1 ′) can form a chemically amplified resist composition by itself having the structural unit (a1) together with the structural unit (a5). That is, when the (A1 ′) component is exposed, the acid generated from the structural unit (a5) decomposes the acid-decomposable group in the structural unit (a1) in the (A1 ′) component, and as a result. , (A1 ′) The polarity of the entire component increases. Therefore, a resist pattern can be formed by performing selective exposure and development even for a film composed only of the component (A ′).

Further, the resist composition of the present invention has good sensitivity, resolution, etc., and the shape of the formed resist pattern is also good with reduced LWR (line width roughness). The reason why such an effect is obtained is not clear, but is estimated as follows.
In the present invention, since the component (A1 ′), which is a resin component, has the structural unit (a5), the site of the structural unit (a5) is likely to be uniformly distributed in the resist film.
Furthermore, salt exchange occurs between the site of the structural unit (a5) in the (A1 ′) component of the unexposed portion and the acid generated from the acid generator or the like of the exposed portion, and the acid generated by exposure is unexposed. Decomposition of the acid-decomposable group in the component (A1 ′) is suppressed (a quenching effect by salt exchange is exhibited). In addition, the component (A1 ′) includes a cyclic hydrocarbon group having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent. By having the structural unit (a3) to be included, the polarity (hydrophilicity) of the polymer is further increased, and the hydrophilicity balance is easily obtained.
By these actions, diffusion of the acid generated in the exposed portion to the unexposed portion is suppressed, and decomposition of the acid-decomposable group in the unexposed portion is suppressed. Further, since the structural unit (a5) loses the function of decomposing at the exposed portion and quenching the acid, the contrast of the acid concentration is increased between the exposed portion and the unexposed portion. As a result, it is presumed that a resist pattern having a good shape with reduced LWR can be formed.

≪Resist pattern formation method≫
The resist pattern forming method of the present invention comprises a step of forming a resist film on a support using the resist composition of the present invention, a step of exposing the resist film, and developing the resist film to form a resist pattern. Forming.
The resist pattern forming method of the present invention can be performed, for example, as follows.
That is, first, the resist composition of the present invention is applied onto a support with a spinner or the like, and a baking (post-apply bake (PAB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably A resist film is formed by applying for 60 to 90 seconds.
Next, the resist film is exposed through a mask (mask pattern) on which a predetermined pattern is formed using an exposure apparatus such as an ArF exposure apparatus, an electron beam drawing apparatus, or an EUV exposure apparatus, or a mask pattern. After performing selective exposure by drawing or the like by direct irradiation with an electron beam without passing through, baking (post-exposure baking (PEB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably 60 Apply for ~ 90 seconds.
Next, the resist film is developed.
The development treatment is performed using an alkaline developer in the case of an alkali development process, and using a developer (organic developer) containing an organic solvent in the case of a solvent development process.
A rinsing treatment is preferably performed after the development treatment. The rinse treatment is preferably a water rinse using pure water in the case of an alkali development process, and is preferably a rinse solution containing an organic solvent in the case of a solvent development process.
In the case of a solvent development process, after the development process or the rinse process, a process of removing the developer or rinse liquid adhering to the pattern with a supercritical fluid may be performed.
Drying is performed after development or rinsing. In some cases, a baking process (post-bake) may be performed after the development process. In this way, a resist pattern can be obtained.

The support is not particularly limited, and a conventionally known one can be used, and examples thereof include a substrate for electronic components and a substrate on which a predetermined wiring pattern is formed. More specifically, a silicon substrate, a metal substrate such as copper, chromium, iron, and aluminum, a glass substrate, and the like can be given. As a material for the wiring pattern, for example, copper, aluminum, nickel, gold or the like can be used.
Further, the support may be a substrate in which an inorganic and / or organic film is provided on the above-described substrate. An inorganic antireflection film (inorganic BARC) is an example of the inorganic film. Examples of the organic film include organic films such as an organic antireflection film (organic BARC) and a lower organic film in a multilayer resist method.
Here, the multilayer resist method is a method in which at least one organic film (lower organic film) and at least one resist film (upper resist film) are provided on a substrate, and the resist pattern formed on the upper resist film is used as a mask. This is a method of patterning a lower organic film, and it is said that a pattern with a high aspect ratio can be formed. That is, according to the multilayer resist method, the required thickness can be secured by the lower organic film, so that the resist film can be thinned and a fine pattern with a high aspect ratio can be formed.
In the multilayer resist method, basically, a method of forming a two-layer structure of an upper resist film and a lower organic film (two-layer resist method), and one or more intermediate layers between the upper resist film and the lower organic film And a method of forming a multilayer structure of three or more layers (metal thin film etc.) (three-layer resist method).

The wavelength used for the exposure is not particularly limited, and ArF excimer laser, KrF excimer laser, F ₂ excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-ray, soft X-ray, etc. Can be done using radiation. The resist composition is highly useful for KrF excimer laser, ArF excimer laser, EB or EUV.

The exposure method of the resist film may be normal exposure (dry exposure) performed in an inert gas such as air or nitrogen, or may be immersion exposure (Liquid Immersion Lithography).
In immersion exposure, the space between the resist film and the lens at the lowest position of the exposure apparatus is previously filled with a solvent (immersion medium) having a refractive index larger than that of air, and exposure (immersion exposure) is performed in that state. It is an exposure method.
As the immersion medium, a solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film to be exposed is preferable. The refractive index of such a solvent is not particularly limited as long as it is within the above range.
Examples of the solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film include water, a fluorine-based inert liquid, a silicon-based solvent, and a hydrocarbon-based solvent.
Specific examples of the fluorine-based inert liquid include a fluorine-based compound such as C ₃ HCl ₂ F ₅ , C ₄ F ₉ OCH ₃ , C ₄ F ₉ OC ₂ H ₅ , and C ₅ H ₃ F ₇ as a main component. Examples thereof include liquids, and those having a boiling point of 70 to 180 ° C are preferable, and those having a boiling point of 80 to 160 ° C are more preferable. It is preferable that the fluorine-based inert liquid has a boiling point in the above range since the medium used for immersion can be removed by a simple method after the exposure is completed.
As the fluorine-based inert liquid, a perfluoroalkyl compound in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly preferable. Specific examples of the perfluoroalkyl compound include a perfluoroalkyl ether compound and a perfluoroalkylamine compound.
More specifically, examples of the perfluoroalkyl ether compound include perfluoro (2-butyl-tetrahydrofuran) (boiling point 102 ° C.). Examples of the perfluoroalkylamine compound include perfluorotributylamine ( Boiling point of 174 ° C.).
As the immersion medium, water is preferably used from the viewpoints of cost, safety, environmental problems, versatility, and the like.

Examples of the alkali developer used for the development treatment in the alkali development process include a 0.1 to 10% by mass tetramethylammonium hydroxide (TMAH) aqueous solution.
The organic solvent contained in the organic developer used in the development process in the solvent development process is not particularly limited as long as it can dissolve the component (A ′) (component (A ′) before exposure). It can select suitably from them. Specifically, polar solvents such as ketone solvents, ester solvents, alcohol solvents, amide solvents, ether solvents, or hydrocarbon solvents can be used.

A known additive can be blended in the organic developer as required. Examples of the additive include a surfactant. The surfactant is not particularly limited. For example, ionic or nonionic fluorine-based and / or silicon-based surfactants can be used.
When the surfactant is blended, the blending amount is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and 0.01 to 0. 0% with respect to the total amount of the organic developer. 5 mass% is more preferable.

  The development process can be carried out by a known development method, for example, a method in which a support is immersed in a developer for a certain period of time (dip method), a developer is raised on the surface of the support by surface tension, and is left for a certain period of time. (Paddle method), spraying developer on the surface of the support (spray method), coating the developer while scanning the developer coating nozzle at a constant speed on the support rotating at a constant speed The method to continue (dynamic dispensing method) etc. are mentioned.

As the organic solvent contained in the rinsing liquid used for the rinsing treatment after the development process in the solvent development process, for example, among the organic solvents mentioned as the organic solvent contained in the organic developer, those which are difficult to dissolve the resist pattern are appropriately used. You can select and use. Usually, at least one solvent selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents is used. Among these, at least one selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents and amide solvents is preferable, and at least one selected from alcohol solvents and ester solvents is preferable. More preferred are alcohol solvents.
The rinsing treatment (washing treatment) using the rinsing liquid can be carried out by a known rinsing method, for example, a method of continuously applying the rinsing liquid onto a support rotating at a constant speed (rotary coating method), Examples thereof include a method of immersing the support in a rinsing liquid for a certain period of time (dip method), a method of spraying the rinsing liquid on the surface of the support (spray method), and the like.

EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited by these examples.
In this example, the unit represented by the chemical formula (1) is referred to as “compound (1)”, and the same applies to compounds represented by other formulas.
In the analysis by NMR, the internal standard of ¹ H-NMR and the internal standard of ¹³ C-NMR is tetramethylsilane (TMS). The internal standard of ¹⁹ F-NMR is hexafluorobenzene (however, the peak of hexafluorobenzene was set to −160 ppm).

[Monomer Synthesis Example 1 (Synthesis of Compound (2))]
The compound (2) used in the polymer synthesis example described later was synthesized by the following procedure.
In a 500 mL three-necked flask, under a nitrogen atmosphere, 20 g (105.14 mmol) of alcohol (2), 30.23 g (157.71 mmol) of ethyldiisopropylaminocarbodiimide (EDCI) hydrochloride and 0.6 g of dimethylaminopyridine (DMAP) A THF solution (300 mL) of (5 mmol) was added, and after adding 16.67 g (115.66 mmol) of the precursor (2) under ice cooling (0 ° C.), the mixture was stirred at room temperature for 12 hours.
After confirming disappearance of the raw material by thin layer chromatography (TLC), 50 mL of water was added to stop the reaction. The reaction solvent was concentrated under reduced pressure, and the organic layer obtained by extraction three times with ethyl acetate was washed with water, saturated sodium bicarbonate and 1N-HClaq in this order. The product obtained by distilling off the solvent under reduced pressure was dried to obtain Compound (2).
The NMR analysis result of the obtained compound (2) was as follows.
¹ H-NMR (CDCl ₃ , 400 MHz): δ (ppm) = 6.22 (s, 1H, H ^a ), 5.70 (s, 1H, H ^b ), 4.71-4.85 (m, 2H, H ^{c, d} ), 4.67 (s, 2H, H ^k ), 3.40-3.60 (m, 2H, H ^{e, f} ), 2.58-2.70 (m, 1H, ^{H g), 2.11-2.21 (m,} 2H, H h), 2.00 (s, 3H, H i), 1.76-2.09 (m, 2H, H j).

[Polymer Synthesis Example 1 (Synthesis of Polymer Compound 1)]
In a separable flask in which a thermometer, a reflux tube, and a nitrogen introduction tube were connected, 1.00 g (5.88 mmol) of compound (1), 1.12 g (3.53 mmol) of compound (2), 1.44 g (5 .49 mmol) of compound (3), 0.41 g (2.45 mmol) of compound (4), 0.28 g (1.18 mmol) of compound (5), 0.56 g (1.08 mmol) of compound (6) Was dissolved in 11.14 g of methyl ethyl ketone (MEK). To this solution, 1.371 mmol of dimethyl azobisisobutyrate (V-601) was added and dissolved as a polymerization initiator.
This solution was heated and stirred at 80 ° C. for 6 hours under a nitrogen atmosphere, and then the reaction solution was cooled to room temperature. The obtained reaction polymerization solution was dropped into a large amount of n-heptane / isopropanol mixed solution to precipitate a polymer, and the precipitated white powder was filtered, washed with methanol and MEK, and dried. 2.7 g of the target polymer compound 1 was obtained.
About this high molecular compound 1, the mass mean molecular weight (Mw) of standard polystyrene conversion calculated | required by GPC measurement was 15600, and molecular weight dispersion degree (Mw / Mn) was 2.34. The copolymer composition ratio (ratio (molar ratio) of each structural unit in the structural formula) determined by carbon-13 nuclear magnetic resonance spectrum (600 MHz — ¹³ C-NMR) is 1 / m / n / o / p / It was q = 35.3 / 22.8 / 16.1 / 13.8 / 7.7 / 4.3.

[Polymer synthesis examples 2 to 29 (synthesis of polymer compounds 2 to 29)]
Polymer compounds 2 to 29 were prepared in the same manner as in the above polymer synthesis example 1 except that the following compounds (1) to (25) for deriving structural units constituting each polymer compound were used in a predetermined molar ratio. Synthesized.
For each polymer compound, a compound for deriving each structural unit, a copolymer composition ratio determined by carbon 13 nuclear magnetic resonance spectrum (600 MHz — ¹³ C-NMR), a mass average molecular weight in terms of standard polystyrene determined by GPC measurement, and a molecular weight Dispersity (Mw / Mn) is shown in Tables 1-3.

<Preparation of resist composition (1)>
[Examples 1 to 5, Comparative Examples 1 to 4]
A resist composition was prepared by mixing and dissolving the components shown in Table 4.

In Table 4, the numerical value in [] shows a compounding quantity (part by mass). The symbols in Table 4 indicate the following.
(A ′)-1: The polymer compound 1.
(A ′)-2: the polymer compound 2.
(A ′)-3: The polymer compound 3.
(A ′)-4: The polymer compound 4.
(C) -1: the polymer compound 5.
(C) -2: the polymer compound 6.
(C) -3: The polymer compound 7.
(C) -4: The polymer compound 8.
(B) -1: a compound represented by the following chemical formula (B) -1.

(D) -1: tri-n-pentylamine.
(S) -1: Propylene glycol monomethyl ether acetate.
(S) -2: Propylene glycol monomethyl ether.
(S) -3: Cyclohexanone.

<Preparation of resist composition (2)>
[Examples 6 to 22, Comparative Examples 5 to 8]
A resist composition was prepared in the same manner as in Example 1 except that the polymer compounds 9 to 29 were used in place of the polymer compound 1 as the component (A ′).

<Formation of resist pattern (1)>
An organic antireflection film composition “ARC29” (trade name, manufactured by Brewer Science Co., Ltd.) is applied onto an 8-inch silicon wafer using a spinner, and baked on a hot plate at 205 ° C. for 60 seconds to be dried. Thereby, an organic antireflection film having a thickness of 77 nm was formed.
Then, the resist composition obtained above was applied onto the organic antireflection film using a spinner, and pre-baked on a hot plate under the conditions of the PAB temperatures shown in Tables 5 and 6 for 60 seconds. By performing (PAB) treatment and drying, a resist film having a thickness of 120 nm was formed.
Next, an ArF excimer laser (193 nm) is applied to the resist film by an ArF exposure apparatus NSR-S302 (Nikon Corporation; NA (numerical aperture) = 0.60, 2/3 annular illumination) with a mask pattern (6 % Halftone mask).
Then, a post-exposure heating (PEB) treatment was performed for 60 seconds at the PEB temperatures shown in Tables 5 and 6, and a 2.38 mass% TMAH aqueous solution (trade name: NMD-3, Tokyo Ohka Kogyo Co., Ltd.) at 23 ° C. The product was alkali-developed under the conditions of 30 seconds, and then rinsed with pure water for 30 seconds and shaken and dried.
As a result, in each example, a 1: 1 line and space (L / S) pattern having a line width of 160 nm and a pitch of 320 nm was formed on the resist film. Moreover, the optimal exposure amount Eop (mJ / cm ² ) at this time was determined. The results are shown in Tables 5 and 6.

[LWR (line width roughness) evaluation]
In a 1: 1 L / S pattern with a line width of 160 nm formed by the above Eop, the space width was measured by a length measurement SEM (scanning electron microscope, acceleration voltage 800 V, product name: S-9220, manufactured by Hitachi, Ltd.). Five locations in the longitudinal direction of the space were measured, and from the results, a value (3s) that was three times the standard deviation (s) was calculated as a measure of LWR. The results are shown in Tables 5 and 6.
The smaller the value of 3s, the smaller the roughness of the line width, which means that a more uniform width L / S pattern was obtained.

Comparison between Examples 1 and 2 and Comparative Examples 1, 5 and 8 in Tables 5 to 6; Comparison between Example 3 and Comparative Example 2; Comparison between Example 4 and Comparative Example 3; Comparison with Example 5 Comparison with Examples 4 and 7: From the comparison between Example 18 and Comparative Example 6, the roughness of the resist compositions of the examples according to the present invention is further reduced as compared with the corresponding resist compositions of the comparative examples. It was confirmed that a resist pattern having a good shape could be formed.
Further, from the results of other examples shown in Table 6, it was confirmed that even when the resin component (A1 ′) was changed, the roughness was further reduced and a resist pattern having a good shape could be formed.

<Preparation of resist composition (3)>
[Examples 23 to 24, Comparative Example 9]
A resist composition was prepared by mixing and dissolving the components shown in Table 7.

In Table 7, the numerical value in [] shows a compounding quantity (part by mass). Moreover, the symbol in Table 7 shows the following, respectively.
(A ′)-1: The polymer compound 1.
(C) -1: the polymer compound 5.
(B) -2: A compound represented by the following chemical formula (B) -2.
(D) -1: tri-n-pentylamine.
(H) -1: a compound represented by the following chemical formula (H) -1.
(F) -1: A compound represented by the following chemical formula (F) -1. Mw13800, Mw / Mn1.5. m / n = 80/20 (molar ratio); In the chemical formula, the numerical value on the lower right of the structural unit () indicates the proportion (mol%) of the structural unit.
(S) -1: Propylene glycol monomethyl ether acetate.
(S) -2: Propylene glycol monomethyl ether.
(S) -3: Cyclohexanone.
(S) -4: γ-butyrolactone.

<Preparation of resist composition (4)>
[Examples 25 to 34]
(H) As in Example 24, except that the compounds represented by the following chemical formulas (H) -2 to (H) -11 were used in place of the compounds represented by the chemical formula (H) -1, respectively. Thus, a resist composition was prepared.

<Formation of resist pattern (2)>
An organic antireflection film composition “ARC29A” (trade name, manufactured by Brewer Science Co., Ltd.) is applied onto a 12-inch silicon wafer using a spinner and baked on a hot plate at 205 ° C. for 60 seconds to be dried. Thereby, an organic antireflection film having a film thickness of 89 nm was formed.
Then, the resist composition obtained above is applied onto the organic antireflection film using a spinner, and prebaked (PAB) is performed on a hot plate at 105 ° C. for 60 seconds. By drying, a resist film having a thickness of 80 nm was formed.
Next, an ArF excimer laser (193 nm) was applied to the resist film with a mask pattern (6% halftone) using an ArF immersion exposure apparatus NSR-S609B (Nikon Corporation; NA (numerical aperture) = 1.07, Annular). Selectively irradiated through a mask).
Then, a post-exposure heating (PEB) treatment is performed at 95 ° C. for 60 seconds, and further a 2.38 mass% TMAH aqueous solution (trade name: NMD-3, manufactured by Tokyo Ohka Kogyo Co., Ltd.) at 23 ° C. Alkali development was carried out for 10 seconds, followed by water rinsing with pure water for 30 seconds, followed by shake-off drying.
As a result, in each example, an approximately 1: 1.2 line and space (L / S) pattern having a line width of 45 nm and a pitch of 100 nm was formed on the resist film. Moreover, the optimal exposure amount Eop (mJ / cm ² ) at this time was determined. The results are shown in Table 8.

[LWR (line width roughness) evaluation]
In the L / S pattern with a line width of 45 nm and a pitch of 100 nm formed by the above Eop, the space width is measured by a length measuring SEM (scanning electron microscope, acceleration voltage 800 V, product name: S-9220, manufactured by Hitachi, Ltd.). Then, five locations in the longitudinal direction of the space were measured, and from the results, a value (3s) that was three times the standard deviation (s) was calculated as a measure of LWR. The results are shown in Table 8.

[MEF evaluation]
With respect to the line width 45 nm L / S pattern, an L / S pattern with a pitch of 100 nm was formed using the mask patterns with the target size of the line pattern of 42 to 48 nm (1 nm increments, 7 points in total) at the above Eop.
At this time, the slope of the straight line when the target size (nm) was plotted on the horizontal axis and the size (nm) of the pattern formed on the resist film using each mask pattern was plotted on the vertical axis was calculated as MEF. The results are shown in Table 8.
The MEF (straight line) means that the closer the value is to 1, the better the mask reproducibility.

From the results of Table 8, it was confirmed that the MEF was improved in addition to the LWR by using the component (H) in combination.
Even when the component (H) used in Examples 25 to 35 was used in combination with the resist composition of Comparative Example 9, no significant changes were observed in the values of LWR and MEF. From this result, it was confirmed that the combination of the component (A ′) and the component (H) was effective.

Claims (6)

A resist composition containing a base material component (A ′) whose solubility in a developer is changed by the action of an acid and which generates an acid upon exposure,
The base material component (A ′) is
A structural unit (a5) containing a group represented by the following general formula (a5-10);
A structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and a structural unit containing an acid-decomposable group whose polarity is increased by the action of an acid ( a1)
A resist composition comprising a resin component (A1 ′) having a structural unit (a3) represented by the following general formula (a3-1):

[In Formula (a5-10), Q is a single bond or a divalent linking group, R ^X is a hydrogen atom, a fluorine atom, an alkyl group, or a fluorinated alkyl group, and p is an integer of 1 to 10. is there. A ⁺ is an organic cation. In formula (a3-1), R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. P ⁰ is —C (═O) —O—, —C (═O) —NR ⁰ — (R ⁰ is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms) or a single bond. W ⁰ is a cyclic hydrocarbon group having at least one group selected from the group consisting of —OH, —COOH, —CN, —SO ₂ NH ₂ and —CONH ₂ as a substituent, and oxygen at any position. You may have an atom or a sulfur atom. ] The resist composition according to claim 1, wherein the structural unit (a5) is a structural unit represented by the following general formula (a5-1).

[Wherein, R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, Q is a single bond or a divalent linking group, and R ^X is a hydrogen atom. , A fluorine atom, an alkyl group, or a fluorinated alkyl group, and p is an integer of 1 to 10. A ⁺ is an organic cation. ]   The structural unit (a1) is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and a cyclic group-containing acid-decomposable group. The resist composition of Claim 1 or 2 containing 2 or more types of structural units to contain. The resin component (A1 ′) is a structural unit further derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and a —SO ₂ — containing ring The resist composition as described in any one of Claims 1-3 which has a structural unit (a0) containing a formula group.  The resin component (A1 ′) is a structural unit derived from an acrylate ester in which an atom other than a hydrogen atom or a substituent may be bonded to a carbon atom at the α-position, and a lactone-containing cyclic group The resist composition as described in any one of Claims 1-4 which has a structural unit (a2) to contain.   A step of forming a resist film on the support using the resist composition according to any one of claims 1 to 5, a step of exposing the resist film, and developing the resist film to form a resist pattern A resist pattern forming method including a forming step.