JP2013091780A - Colored curable resin composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a colored curable resin composition that has low viscosity.SOLUTION: The colored curable resin composition comprises a colorant, a resin, a polymerizable compound, a polymerization initiator, and a solvent. The colorant contains a dye and a pigment. The solvent contains: a cyclic ketone; and propylene glycol monomethylether acetate. The content of the cyclic ketone is 25 to 75 mass% based on the total amount of the solvent. The content of the propylene glycol monomethylether acetate is 25 to 75 mass% based on the total amount of the solvent. The content of the solvent is 80 to 90 mass% based on the total amount of the colored curable resin composition.

Description

  The present invention relates to a colored curable resin composition.

Colored curable resin compositions are used in the manufacture of color filters used in display devices such as liquid crystal display panels, electroluminescence panels, and plasma display panels. As such a colored curable resin composition, a colored curable resin composition containing cyclohexanone, propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether and ethyl lactate as a solvent is known (Patent Document 1).
A slit nozzle coater is used as an apparatus for applying a colored curable resin composition to a large-sized substrate. It is known that when a colored curable resin composition is applied using a slit nozzle coater, the coating speed can be increased when the viscosity of the colored curable resin composition is low, so that the tact time can be shortened (Non-Patent Document). 1).

JP 2010-211198 A

“Color Filter Latest Technology Trends-Construction Materials, Manufacturing, Evaluation, Overseas Trends”, Information Organization Co., Ltd., May 2005, p. 159

  The above-described colored curable resin composition known in the past may not always be sufficiently satisfactory in viscosity.

The present invention includes the following inventions.
[1] including a colorant, a resin, a polymerizable compound, a polymerization initiator, and a solvent,
The colorant is a colorant comprising a dye and a pigment;
The solvent is a solvent containing a cyclic ketone and propylene glycol monomethyl ether acetate,
The cyclic ketone content is 25% by mass or more and 75% by mass or less with respect to the total amount of the solvent,
The content of propylene glycol monomethyl ether acetate is 25% by mass or more and 75% by mass or less with respect to the total amount of the solvent,
The colored curable resin composition whose content of a solvent is 80 to 90 mass% with respect to the total amount of a colored curable resin composition.
[2] The colored curable resin composition according to [1], wherein the total amount of the cyclic ketone and propylene glycol monomethyl ether acetate is 80% by mass or more and 100% by mass or less based on the total amount of the solvent.
[3] The colored curable resin composition according to [1] or [2], wherein the cyclic ketone is at least one selected from the group consisting of cyclohexanone and cyclopentanone.
[4] A color filter formed from the colored curable resin composition according to any one of [1] to [3].
[5] A display device including the color filter according to [4].

  The colored curable resin composition of the present invention has a low viscosity.

The colored curable resin composition of the present invention includes a colorant (A), a resin (B), a polymerizable compound (C), a polymerization initiator (D), and a solvent (E).
The colorant (A) includes a dye (A1) and a pigment (A2).
The solvent (E) includes a cyclic ketone and propylene glycol monomethyl ether acetate,
The cyclic ketone content is 25% by mass or more and 75% by mass or less based on the total amount of the solvent (E),
The content of propylene glycol monomethyl ether acetate is 25% by mass or more and 75% by mass or less based on the total amount of the solvent (E),
The content of the solvent (E) is 80% by mass or more and 90% by mass or less with respect to the total amount of the colored curable resin composition.
Moreover, the colored curable resin composition of this invention may also contain at least 1 sort (s) chosen from the group which consists of a polymerization start adjuvant (D1) and surfactant (F) as needed.
In addition, as long as there is no notice in particular, each component may be used individually by 1 type, and may use 2 or more types together.

<Colorant (A)>
Examples of the colorant (A) include a dye (A1) and a pigment (A2).

The dye (A1) is not particularly limited, and a known dye can be used. Examples thereof include solvent dyes, acid dyes, direct dyes, mordant dyes, and the like, and dyes that are soluble in an organic solvent are preferable.
Examples of the dye (A1) include compounds classified as dyes by the Color Index (published by The Society of Dyers and Colorists) and known dyes described in dyeing notes (Color Dyeing). Also, according to chemical structure, azo dye, cyanine dye, triphenylmethane dye, phthalocyanine dye, anthraquinone dye, naphthoquinone dye, quinoneimine dye, methine dye, azomethine dye, squarylium dye, acridine dye, styryl dye, coumarin dye, quinoline And dyes and nitro dyes. Of these, organic solvent-soluble dyes are preferred.

Specifically, C.I. I. Solvent Yellow 4 (hereinafter, description of CI Solvent Yellow is omitted, and only the number is described), 14, 15, 23, 24, 38, 62, 63, 68, 82, 94, 98, 99 117, 162, 163, 167, 189;
C. I. Solvent Red 45, 49, 111, 125, 130, 143, 145, 146, 150, 151, 155, 168, 169, 172, 175, 181, 207, 218, 222, 227, 230, 245, 247;
C. I. Solvent orange 2, 7, 11, 15, 26, 56, 77, 86;
C. I. Solvent violet 11, 13, 14, 26, 31, 36, 37, 38, 45, 47, 48, 51, 59, 60;
C. I. Solvent Blue 4, 5, 14, 18, 35, 36, 37, 45, 58, 59, 59: 1, 63, 67, 68, 69, 70, 78, 79, 83, 90, 94, 97, 98, 100, 101, 102, 104, 105, 111, 112, 122, 128, 132, 136, 139;
C. I. Solvent Green 1, 3, 4, 5, 7, 28, 29, 32, 33, 34, 35, etc. I. Solvent dyes,
C. I. Acid Yellow 1, 3, 7, 9, 11, 17, 23, 25, 29, 34, 36, 38, 40, 42, 54, 65, 72, 73, 76, 79, 98, 99, 111, 112, 113, 114, 116, 119, 123, 128, 134, 135, 138, 139, 140, 144, 150, 155, 157, 160, 161, 163, 168, 169, 172, 177, 178, 179, 184, 190, 193, 196, 197, 199, 202, 203, 204, 205, 207, 212, 214, 220, 221, 228, 230, 232, 235, 238, 240, 242, 243, 251;
C. I. Acid Red 1, 4, 8, 14, 17, 18, 26, 27, 29, 31, 33, 34, 35, 37, 40, 42, 44, 50, 51, 52, 57, 66, 73, 76, 80, 87, 88, 91, 92, 94, 95, 97, 98, 103, 106, 111, 114, 129, 133, 134, 138, 143, 145, 150, 151, 155, 158, 160, 172, 176, 182, 183, 195, 198, 206, 211, 215, 216, 217, 227, 228, 249, 252, 257, 258, 260, 261, 266, 268, 270, 274, 277, 280, 281, 289, 308, 312, 315, 316, 339, 341, 345, 346, 349, 382, 383, 388, 394, 401, 412, 41 , 418,422,426;
C. I. Acid Orange 6, 7, 8, 10, 12, 26, 50, 51, 52, 56, 62, 63, 64, 74, 75, 94, 95, 107, 108, 169, 173;
C. I. Acid Violet 6B, 7, 9, 17, 19, 30, 34, 102;
C. I. Acid Blue 1, 7, 9, 15, 18, 22, 23, 25, 27, 29, 40, 41, 42, 43, 45, 51, 54, 59, 60, 62, 70, 72, 74, 78, 80, 82, 83, 86, 87, 90, 92, 93, 96, 100, 102, 103, 104, 112, 113, 117, 120, 126, 127, 129, 130, 131, 138, 140, 142, 143, 147, 150, 151, 154, 158, 161, 166, 167, 168, 170, 171, 175, 182, 183, 184, 187, 192, 199, 203, 204, 205, 210, 229, 234, 236, 242, 243, 256, 259, 267, 278, 280, 285, 290, 296, 315, 324: 1, 335, 340;
C. I. Acid Green 1, 3, 5, 9, 16, 25, 27, 28, 41, 50, 58, 63, 65, 80, 104, 105, 106, 109, etc. I. Acid dyes,
C. I. Direct Yellow 2, 33, 34, 35, 38, 39, 43, 47, 50, 54, 58, 68, 69, 70, 71, 86, 93, 94, 95, 98, 102, 108, 109, 129, 136, 138, 141;
C. I. Direct Red 79, 82, 83, 84, 91, 92, 96, 97, 98, 99, 105, 106, 107, 172, 173, 176, 177, 179, 181, 182, 184, 204, 207, 211, 213, 218, 220, 221, 222, 232, 233, 234, 241, 243, 246, 250;
C. I. Direct Orange 26, 34, 39, 41, 46, 50, 52, 56, 57, 61, 64, 65, 68, 70, 96, 97, 106, 107;
C. I. Direct violet 47, 52, 54, 59, 60, 65, 66, 79, 80, 81, 82, 84, 89, 90, 93, 95, 96, 103, 104;
C. I. Direct Blue 1, 2, 6, 8, 15, 22, 25, 40, 41, 57, 71, 76, 77, 78, 80, 81, 84, 85, 86, 90, 93, 94, 95, 97, 98, 99, 100, 101, 106, 107, 108, 109, 113, 114, 115, 117, 119, 120, 137, 149, 150, 153, 155, 156, 158, 159, 160, 161, 162, 163, 164, 165, 166, 167, 168, 170, 171, 172, 173, 188, 189, 190, 192, 193, 194, 195, 196, 198, 199, 200, 201, 202, 203, 207, 209, 210, 212, 213, 214, 222, 225, 226, 228, 229, 236, 237, 238, 242, 243 244,245,246,247,248,249,250,251,252,256,257,259,260,268,274,275,293;
C. I. Direct green 25, 27, 31, 32, 34, 37, 63, 65, 66, 67, 68, 69, 72, 77, 79, 82, etc. I. Direct dyes,
C. I. Disperse Yellow 51, 54, 76;
C. I. Disperse violet 26, 27;
C. I. Disperse dyes such as Disperse Blue 1, 14, 56, 60;
C. I. Basic Red 1, 10;
C. I. Basic Blue 1, 3, 5, 7, 9, 19, 21, 22, 24, 25, 26, 28, 29, 40, 41, 45, 47, 54, 58, 59, 60, 64, 65, 66, 67, 68;
C. I. C. such as Basic Green 1; I. Basic dyes C.I. I. Reactive Yellow 2, 76, 116;
C. I. Reactive Orange 16;
C. I. Reactive Red 36; I. Reactive dyes C.I. I. Modern yellow 5, 8, 10, 16, 20, 26, 30, 31, 33, 42, 43, 45, 56, 61, 62, 65;
C. I. Modern Red 1, 2, 3, 4, 9, 11, 12, 14, 17, 18, 19, 22, 23, 24, 25, 26, 27, 30, 32, 33, 36, 37, 38, 39 41, 43, 45, 46, 48, 53, 56, 63, 71, 74, 85, 86, 88, 90, 94, 95;
C. I. Modern orange 3, 4, 5, 8, 12, 13, 14, 20, 21, 23, 24, 28, 29, 32, 34, 35, 36, 37, 42, 43, 47, 48;
C. I. Modern violet 1, 2, 4, 5, 7, 14, 22, 24, 30, 31, 32, 37, 40, 41, 44, 45, 47, 48, 53, 58;
C. I. Modern Blue 1, 2, 3, 7, 8, 9, 12, 13, 15, 16, 19, 20, 21, 22, 23, 24, 26, 30, 31, 32, 39, 40, 41, 43 44, 48, 49, 53, 61, 74, 77, 83, 84;
C. I. Modern Green 1, 3, 4, 5, 10, 15, 19, 26, 29, 33, 34, 35, 41, 43, 53, etc. I. Modern dyes C.I. I. C. of Bat Green 1 etc. I. Examples include vat dyes.
These dyes may be appropriately selected according to the desired spectral spectrum of the color filter.

As the dye (A1), a xanthene dye (Aa) is preferable.
The xanthene dye (Aa) is a dye containing a compound having a xanthene skeleton in the molecule. Examples of the xanthene dye (Aa) include C.I. I. Acid Red 51 (hereinafter, the description of CI Acid Red is omitted, and only the number is described), 52, 87, 92, 94, 289, 388, C.I. I. Acid Violet 9, 30, 102, C.I. I. Basic Red 1 (Rhodamine 6G), 2, 3, 4, 8, C.I. I. Basic Red 10 (Rhodamine B), 11, C.I. I. Basic violet 10, 11, 25, C.I. I. Solvent Red 218, C.I. I. Modern Tread 27, C.I. I. Reactive red 36 (rose bengal B), sulforhodamine G, xanthene dyes described in JP 2010-32999 A, xanthene dyes described in Japanese Patent No. 4492760, and the like. Those that are soluble in organic solvents are preferred.

  Among these, as the xanthene dye (Aa), a dye containing a compound represented by the formula (1a) (hereinafter sometimes referred to as “compound (1a)”) is preferable. When using the compound (1a), the content of the compound (1a) in the xanthene dye (Aa) is preferably 50% by mass or more, more preferably 70% by mass or more, and further preferably 90% by mass or more. In particular, it is preferable to use only the compound (1a) as the xanthene dye (Aa).

［式（１ａ）中、Ｒ¹〜Ｒ⁴は、それぞれ独立に、水素原子、−Ｒ⁸又は置換基を有していてもよい炭素数６〜１０の１価の芳香族炭化水素基を表す。Ｒ¹及びＲ^２は、窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ^３及びＲ^４は、窒素原子と一緒になって窒素原子を含む環を形成してもよい。
Ｒ⁵は、−ＯＨ、−ＳＯ₃ ^-、−ＳＯ₃Ｈ、−ＳＯ₃ ^-Ｚ⁺、−ＣＯ₂Ｈ、−ＣＯ₂ ^-Ｚ⁺、−ＣＯ₂Ｒ⁸、−ＳＯ₃Ｒ⁸又は−ＳＯ₂ＮＲ⁹Ｒ¹⁰を表す。
Ｒ⁶及びＲ⁷は、それぞれ独立に、水素原子又は炭素数１〜６のアルキル基を表す。
ｍは、０〜５の整数を表す。ｍが２以上の整数である場合、複数のＲ⁵は同一であるか相異なる。但し、Ｒ^５が−ＳＯ₃ ^-の場合、ｍは１である。
ａは、０又は１の整数を表す。
Ｘは、ハロゲン原子を表す。
Ｒ⁸は、炭素数１〜２０の１価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、ハロゲン原子で置換されていてもよい。
Ｚ⁺は、⁺Ｎ（Ｒ¹¹）₄、Ｎａ⁺又はＫ⁺を表す。
Ｒ⁹及びＲ¹⁰は、それぞれ独立に、水素原子又は炭素数１〜２０の１価の飽和炭化水素基を表し、Ｒ⁹及びＲ¹⁰は、互いに結合して窒素原子と一緒に３〜１０員環の窒素含有複素環を形成していてもよい。
Ｒ¹¹は、それぞれ独立に、水素原子、炭素数１〜２０の１価の飽和炭化水素基又は炭素数７〜１０のアラルキル基を表す。］

[In Formula (1a), R ^{1 to} R ⁴ each independently represents a hydrogen atom, —R ^8, or a monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms that may have a substituent. . R ¹ and R ² may be combined with a nitrogen atom to form a ring containing a nitrogen atom, and R ³ and R ⁴ may be combined with a nitrogen atom to form a ring containing a nitrogen atom. Good.
R ^{5 _{is, -OH, -SO 3 -, -SO}} 3 H, -SO 3 - Z +, -CO 2 H, -CO 2 - Z +, -CO 2 R 8, -SO 3 R 8 or -SO ₂ represents NR ⁹ R ¹⁰
R ⁶ and R ⁷ each independently represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms.
m represents an integer of 0 to 5. When m is an integer of 2 or more, the plurality of R ⁵ are the same or different. However, when R ⁵ is —SO ₃ ^— , m is 1.
a represents an integer of 0 or 1.
X represents a halogen atom.
R ⁸ represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a halogen atom.
Z ⁺ represents ⁺ N (R ¹¹ ) ₄ , Na ⁺ or K ⁺ .
R ⁹ and R ¹⁰ each independently represents a hydrogen atom or a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, and R ⁹ and R ¹⁰ are bonded to each other to form 3 to 10 members together with a nitrogen atom. A ring-containing nitrogen-containing heterocyclic ring may be formed.
R ¹¹ each independently represents a hydrogen atom, a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms or an aralkyl group having 7 to 10 carbon atoms. ]

Examples of the monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms representing R ^{1 to} R ⁴ include a phenyl group, a toluyl group, a xylyl group, a mesityl group, a propylphenyl group, and a butylphenyl group.

In the monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms in R ^{1 to} R ^4, the hydrogen atom contained in the aromatic hydrocarbon group is a halogen atom, —R ⁸ , —OH, —OR ⁸ , — _{^{SO 3 -, -SO 3 H,}} -SO 3 - Z +, -CO 2 H, -CO 2 R 8, -SR 8, optionally substituted by -SO ₃ R ⁸ or -SO ₂ NR ⁹ R ¹⁰ Good. Among these _{^{substituents, -SO 3 -, -SO 3 H}} , -SO 3 - is preferably at least one selected from Z ⁺ and the group consisting of _{^{-SO 2 NR 9 R 10, -SO}} 3 - Z + and More preferred is at least one selected from the group consisting of —SO ₂ NR ⁹ R ¹⁰ . In this case, —SO ₃ ^{− +} N (R ¹¹ ) ₄ is preferable as —SO ₃ ⁻ Z ⁺ . When R ^{1 to} R ⁴ are these groups, the colored curable resin composition containing the compound (1a) can form a color filter with less generation of foreign matters and excellent heat resistance.
R ¹ and R ² may be combined with a nitrogen atom to form a ring containing a nitrogen atom, and R ³ and R ⁴ may be combined with a nitrogen atom to form a ring containing a nitrogen atom. Good. Examples of the ring containing a nitrogen atom include the following.

Examples of the monovalent saturated hydrocarbon group having 1 to 20 carbon atoms representing R ^{8 to} R ¹¹ include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, Linear alkyl groups such as decyl group, dodecyl group, hexadecyl group, icosyl group; branched alkyl groups such as isopropyl group, isobutyl group, isopentyl group, neopentyl group, 2-ethylhexyl group; cyclopropyl group, cyclopentyl group, C3-C20 alicyclic saturated hydrocarbon groups, such as a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a tricyclodecyl group, are mentioned.

Examples of —OR ⁸ include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a heptyloxy group, an octyloxy group, a 2-ethylhexyloxy group, and an icosyloxy group.

Examples of —CO ₂ R ⁸ include a methoxycarbonyl group, an ethoxycarbonyl group, a propoxycarbonyl group, a tert-butoxycarbonyl group, a hexyloxycarbonyl group, and an icosyloxycarbonyl group.

Examples of —SR ⁸ include a methylsulfanyl group, an ethylsulfanyl group, a butylsulfanyl group, a hexylsulfanyl group, a decylsulfanyl group, and an icosylsulfanyl group.
Examples of —SO ₂ R ⁸ include a methylsulfonyl group, an ethylsulfonyl group, a butylsulfonyl group, a hexylsulfonyl group, a decylsulfonyl group, and an icosylsulfonyl group.
Examples of —SO ₃ R ⁸ include a methoxysulfonyl group, an ethoxysulfonyl group, a propoxysulfonyl group, a tert-butoxysulfonyl group, a hexyloxysulfonyl group, and an icosyloxysulfonyl group.

—SO ₂ NR ⁹ R ¹⁰ includes, for example, a sulfamoyl group;
N-methylsulfamoyl group, N-ethylsulfamoyl group, N-propylsulfamoyl group, N-isopropylsulfamoyl group, N-butylsulfamoyl group, N-isobutylsulfamoyl group, N- sec-butylsulfamoyl group, N-tert-butylsulfamoyl group, N-pentylsulfamoyl group, N- (1-ethylpropyl) sulfamoyl group, N- (1,1-dimethylpropyl) sulfamoyl group, N- (1,2-dimethylpropyl) sulfamoyl group, N- (2,2-dimethylpropyl) sulfamoyl group, N- (1-methylbutyl) sulfamoyl group, N- (2-methylbutyl) sulfamoyl group, N- (3 -Methylbutyl) sulfamoyl group, N-cyclopentylsulfamoyl group, N-hexylsulfamoyl N- (1,3-dimethylbutyl) sulfamoyl group, N- (3,3-dimethylbutyl) sulfamoyl group, N-heptylsulfamoyl group, N- (1-methylhexyl) sulfamoyl group, N- (1 , 4-Dimethylpentyl) sulfamoyl group, N-octylsulfamoyl group, N- (2-ethylhexyl) sulfamoyl group, N- (1,5-dimethyl) hexylsulfamoyl group, N- (1,1,2, , 2-tetramethylbutyl) sulfamoyl group and the like N-1 substituted sulfamoyl group;
N, N-dimethylsulfamoyl group, N, N-ethylmethylsulfamoyl group, N, N-diethylsulfamoyl group, N, N-propylmethylsulfamoyl group, N, N-isopropylmethylsulfa Moyl group, N, N-tert-butylmethylsulfamoyl group, N, N-butylethylsulfamoyl group, N, N-bis (1-methylpropyl) sulfamoyl group, N, N-heptylmethylsulfamoyl And N, N-2-substituted sulfamoyl groups such as a group.

In the monovalent saturated hydrocarbon group having 1 to 20 carbon atoms representing R ⁹ and R ¹⁰ , a hydrogen atom contained in the saturated hydrocarbon group may be substituted with —OH or a halogen atom, and the saturated —CH ₂ — contained in the hydrocarbon group may be replaced by —O—, —CO—, —NH— or —NR ⁸ —.

R ⁹ and R ¹⁰ may be bonded to each other to form a 3- to 10-membered nitrogen-containing heterocycle together with the nitrogen atom. Examples of the heterocyclic ring include the following.

The alkyl group having 1 to 6 carbon atoms that represents the R ⁶ and R ^7, of the linear alkyl groups and branched alkyl groups listed above, include those having 1 to 6 carbon atoms.

Examples of the aralkyl group having 7 to 10 carbon atoms representing R ¹¹ include a benzyl group, a phenylethyl group, and a phenylbutyl group.

Z ⁺ is ⁺ N (R ¹¹ ) ₄ , Na ⁺ or K ⁺ , preferably ⁺ N (R ¹¹ ) ₄ .
As the ⁺ N (R ¹¹ ) ₄ , at least two of the four R ¹¹ are preferably monovalent saturated hydrocarbon groups having 5 to 20 carbon atoms. The total number of carbon atoms of the four R ¹¹ is preferably 20 to 80, 20 to 60 is more preferable. When R ¹¹ is these groups, the colored curable resin composition containing the compound (1a) can form a color filter with few foreign matters.

  m is preferably 1 to 4, and more preferably 1 or 2.

  As the xanthene dye (Aa), a dye containing a compound represented by the formula (2a) (hereinafter sometimes referred to as “compound (2a)”) is more preferable. When the compound (2a) is used, the content of the compound (2a) in the xanthene dye (Aa) is preferably 50% by mass or more, more preferably 70% by mass or more, and further preferably 90% by mass or more.

［式（２ａ）中、Ｒ²¹〜Ｒ²⁴は、それぞれ独立に、水素原子、−Ｒ²⁶又は炭素数６〜１０の１価の置換基を有していてもよい芳香族炭化水素基を表す。Ｒ²¹及びＲ²²は、窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ²³及びＲ²⁴は、窒素原子と一緒になって窒素原子を含む環を形成してもよい。
Ｒ²⁵は、−ＳＯ₃ ^-、−ＳＯ₃Ｈ、−ＳＯ₃ ^-Ｚ１⁺又は−ＳＯ₂ＮＨＲ²⁶を表す。
ｍ１は、０〜５の整数を表す。ｍ１が２以上の整数である場合、複数のＲ²⁵は同一であるか相異なる。但し、Ｒ²⁵が−ＳＯ₃ ^-の場合、ｍ１は１である。
ａ１は、０又は１の整数を表す。
Ｘ１は、ハロゲン原子を表す。
Ｒ²⁶は、炭素数１〜２０の１価の飽和炭化水素基を表す。
Ｚ１⁺は、⁺Ｎ（Ｒ²⁷）₄、Ｎａ⁺又はＫ⁺を表す。
Ｒ²⁷は、それぞれ独立に、炭素数１〜２０の１価の飽和炭化水素基又はベンジル基を表す。］

[In Formula (2a), R ^{21 to} R ²⁴ each independently represents a hydrogen atom, —R ^26, or an aromatic hydrocarbon group that may have a monovalent substituent having 6 to 10 carbon atoms. . R ²¹ and R ²² may form a ring containing a nitrogen atom together with a nitrogen atom, and R ²³ and R ²⁴ may form a ring containing a nitrogen atom together with a nitrogen atom. Good.
R ²⁵ is, -SO ₃ ^- represents a Z1 ⁺ or _{^{-SO 2 NHR 26 -, -SO 3}} H, -SO 3.
m1 represents the integer of 0-5. When m1 is an integer of 2 or more, the plurality of R ²⁵ are the same or different. However, when R ²⁵ is —SO ₃ ^— , m1 is 1.
a1 represents an integer of 0 or 1.
X1 represents a halogen atom.
R ²⁶ represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms.
Z1 ⁺ represents ⁺ N (R ²⁷ ) ₄ , Na ⁺ or K ⁺ .
R ²⁷ each independently represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms or a benzyl group. ]

Examples of the monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms representing R ^{21 to} R ²⁴ include the same groups as those exemplified as the aromatic hydrocarbon group in R ^{1 to} R ⁴ . Hydrogen atoms contained in the aromatic hydrocarbon _{^{group, -SO 3 -, -SO 3 H}} , -SO 3 - Z1 +, may be substituted by -SO ₃ R ²⁶ or -SO ₂ NHR ^26.
As a combination of R ^{21 to} R ²⁴ , R ²¹ and R ²³ are hydrogen atoms, R ²² and R ²⁴ are monovalent aromatic hydrocarbon groups having 6 to 10 carbon atoms, and the aromatic hydrocarbons hydrogen atoms contained in the _{^{groups, -SO 3 -, -SO 3 H}} , -SO 3 - Z1 +, those substituted by -SO ₃ R ²⁶ or -SO ₂ NHR ²⁶ preferred. A more preferred combination is that R ²¹ and R ²³ are hydrogen atoms, R ²² and R ²⁴ are monovalent aromatic hydrocarbon groups having 6 to 10 carbon atoms, and hydrogen contained in the aromatic hydrocarbon group atom, -SO ₃ ^- in which are substituted with Z1 ⁺ or -SO ₂ NHR ^26.
R ²¹ and R ²² together with the nitrogen atom form an aliphatic heterocycle containing a nitrogen atom, and R ²³ and R ²⁴ together with the nitrogen atom contain an aliphatic heterocycle containing a nitrogen atom. Those forming a ring are preferred.
When R ^{21 to} R ²⁴ are these groups, the colored curable resin composition containing the compound (2a) can form a color filter having excellent heat resistance.

Examples of the aliphatic heterocycle include the following.

Examples of the monovalent saturated hydrocarbon group having 1 to 20 carbon atoms representing R ²⁶ and R ²⁷ include the same groups as those exemplified as the saturated hydrocarbon group in R ^{8 to} R ¹¹ .
-R ²⁶ in R ²¹ to R ²⁴ each independently represent a hydrogen atom, a methyl group or an ethyl group. As the R ²⁶ in -SO ₃ R ²⁶ and -SO ₂ NHR ^26, preferably branched alkyl group having 3 to 20 carbon atoms, more preferably a branched alkyl group having 6 to 12 carbon atoms, A 2-ethylhexyl group is more preferred. When R ²⁶ is these groups, the colored curable resin composition containing the compound (2a) can form a color filter with less generation of foreign matters.

Z1 ⁺ is ⁺ N (R ²⁷ ) ₄ , Na ⁺ or K ⁺ , preferably ⁺ N (R ²⁷ ) ₄ .
As the ⁺ N (R ²⁷ ) ₄ , at least two of the four R ²⁷ are preferably monovalent saturated hydrocarbon groups having 5 to 20 carbon atoms. The total number of carbon atoms of the four R ²⁷ is preferably 20 to 80, 20 to 60 is more preferable. The colored curable resin composition containing the compound (2a) in which R ²⁷ is any of these groups can form a color filter with less generation of foreign matters.

  m1 is preferably 1 to 4, and more preferably 1 or 2.

Examples of the compound (2a) include compounds represented by the formula (1-1) to the formula (1-25). In the formula, R ²⁶ represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, preferably a branched alkyl group having 6 to 12 carbon atoms, and more preferably a 2-ethylhexyl group. Among these, C.I. I. Acid red 289 sulfonamidation product, C.I. I. Quaternary ammonium salt of Acid Red 289, C.I. I. Acid violet 102 sulfonamidate or C.I. I. The quaternary ammonium salt of Acid Violet 102 is preferred. Examples of such a compound include compounds represented by formula (1-1) to formula (1-8), formula (1-11), and formula (1-12).

  Moreover, as a xanthene dye (Aa), the dye containing the compound (henceforth "compound (3a)") represented by Formula (3a) is also more preferable. When the compound (3a) is used, the content of the compound (3a) in the xanthene dye (Aa) is preferably 50% by mass or more, more preferably 70% by mass or more, and further preferably 90% by mass or more.

［式（３ａ）中、Ｒ³¹及びＲ³²は、互いに独立に、炭素数１〜４のアルキル基を表す。
Ｒ³³及びＲ³⁴は、互いに独立に、炭素数１〜４のアルキル基、炭素数１〜４のアルキルスルファニル基又は炭素数１〜４のアルキルスルホニル基を表す。
Ｒ³¹及びＲ³³は、窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ³²及びＲ³⁴は、窒素原子と一緒になって窒素原子を含む環を形成してもよい。
ｐ及びｑは、互いに独立に、０〜５の整数を表す。ｐが２以上である場合、複数のＲ³³は同一でも異なってもよく、ｑが２以上である場合、複数のＲ³⁴は同一でも異なってもよい。］

[In formula (3a), R ³¹ and R ³² each independently represent an alkyl group having 1 to 4 carbon atoms.
R ^<33> and R ^<34 > represent a C1-C4 alkyl group, a C1-C4 alkylsulfanyl group, or a C1-C4 alkylsulfonyl group mutually independently.
R ³¹ and R ³³ may form a ring containing a nitrogen atom together with a nitrogen atom, and R ³² and R ³⁴ may form a ring containing a nitrogen atom together with a nitrogen atom. Good.
p and q represent the integer of 0-5 mutually independently. When p is 2 or more, the plurality of R ³³ may be the same or different, and when q is 2 or more, the plurality of R ³⁴ may be the same or different. ]

Examples of the alkyl group having 1 to 4 carbon atoms representing R ³¹ , R ³² , R ³³ and R ³⁴ include a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, an isobutyl group, a sec-butyl group, and a tert-butyl group. Groups and the like.
Examples of the alkylsulfanyl group having 1 to 4 carbon atoms representing R ³³ and R ³⁴ include a methylsulfanyl group, an ethylsulfanyl group, a propylsulfanyl group, a butylsulfanyl group, and an isopropylsulfanyl group.
Examples of the alkylsulfonyl group having 1 to 4 carbon atoms representing R ³³ and R ³⁴ include a methylsulfonyl group, an ethylsulfonyl group, a propylsulfonyl group, a butylsulfonyl group, and an isopropylsulfonyl group.
R ³¹ and R ³² are preferably each independently a methyl group or an ethyl group. R ³³ and R ³⁴ are preferably an alkyl group having 1 to 4 carbon atoms, and more preferably a methyl group.
m and n are preferably integers of 0 to 2, and are preferably 0 or 1.

  Examples of compound (3a) include compounds represented by formula (1-26) to formula (1-32), respectively. Especially, the compound represented by Formula (1-26) is preferable at the point which is excellent in the solubility to an organic solvent.

  As the xanthene dye (Aa), a commercially available xanthene dye (for example, “Chugai Aminol Fast Pink RH / C” manufactured by Chugai Kasei Co., Ltd., “Rhodamin 6G” manufactured by Taoka Chemical Industry Co., Ltd.) may be used. it can. Moreover, it can also synthesize | combine with reference to Unexamined-Japanese-Patent No. 2010-32999 using the commercially available xanthene dye as a starting material.

Examples of the pigment (A2) include compounds classified as pigments according to the color index (published by The Society of Dyers and Colorists).
Examples of the pigment (A2) include C.I. I. Pigment Yellow 1, 3, 12, 13, 14, 15, 16, 17, 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 128, 137, 138, 139, Yellow pigments such as 147, 148, 150, 153, 154, 166, 173, 180, 185, 194, 214, 219;
C. I. Orange pigments such as CI Pigment Orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73;
C. I. Pigment Red 9, 97, 105, 122, 123, 144, 149, 166, 168, 175, 176, 177, 180, 192, 209, 215, 216, 224, 242, 254, 255, 264, 265, etc. Pigments;
C. I. Blue pigments such as CI Pigment Blue 15, 15: 3, 15: 4, 15: 6, 60, 80; I. Violet color pigments such as CI Pigment Violet 1, 19, 23, 29, 32, 36, 38;
C. I. Green pigments such as CI Pigment Green 7, 36, 58;
C. I. Brown pigments such as CI Pigment Brown 23 and 25;
C. I. And black pigments such as CI Pigment Black 1 and 7.

When the colored curable resin composition of the present invention is prepared as a blue colored curable resin composition, examples of the pigment include C.I. I. Pigment Blue 15, 15: 3, 15: 4, 15: 6, 60 and the like, and C.I. I. Violet color pigments such as CI Pigment Violet 1, 19, 23, 29, 32, 36, and 38 are preferred. I. Pigment blue 15: 3, 15: 6 and C.I. I. Pigment Violet 23 is more preferable, and C.I. I. Pigment Blue 15: 6 is more preferable.
When the colored curable resin composition of the present invention is prepared as a green colored curable resin composition, the pigment is C.I. I. Green pigments such as CI Pigment Green 7, 36, and 58; I. Yellow pigments such as CI Pigment Yellow 138, 139 and 150 are preferred.
When the colored curable resin composition of the present invention is prepared as a red colored curable resin composition, the pigment is C.I. I. Red pigments such as C.I. Pigment Red 177, 209, 242, 254, 255; I. Orange pigments such as CI Pigment Orange 38, 43, 71, and C.I. I. Yellow pigments such as CI Pigment Yellow 138, 139 and 150 are preferred.
By including the pigment, it is easy to optimize the transmission spectrum, and the light resistance and chemical resistance of the color filter are improved.

Pigment (A2) is optionally treated with rosin, surface treatment using a pigment derivative having an acidic group or basic group introduced, grafting onto the pigment surface with a polymer compound, sulfuric acid atomization method, etc. May be subjected to the atomization treatment by, cleaning treatment with an organic solvent or water for removing impurities, removal treatment of ionic impurities by an ion exchange method, or the like.
The pigment (A2) preferably has a uniform particle size. By carrying out a dispersion treatment by containing a pigment dispersant, a pigment dispersion in which the pigment is uniformly dispersed in the solution can be obtained.

Examples of the pigment dispersant include cationic, anionic, nonionic, amphoteric, polyester, polyamine, and acrylic surfactants. These pigment dispersants may be used alone or in combination of two or more. Examples of the pigment dispersant include KP (manufactured by Shin-Etsu Chemical Co., Ltd.), Floren (manufactured by Kyoeisha Chemical Co., Ltd.), Solsperse (manufactured by Geneca Co., Ltd.), EFKA (manufactured by CIBA), and Ajispur (Ajinomoto Fine). (Techno Co., Ltd.), Disperbyk (Bic Chemie) and the like.
When the pigment dispersant is used, the amount used is preferably 1% by mass or more and 100% by mass or less, and more preferably 5% by mass or more and 50% by mass or less with respect to the pigment (A2). When the amount of the pigment dispersant used is in the above range, a pigment dispersion with a uniform dispersion tends to be obtained.

  The content ratio of the dye (A1) and the pigment (A2) is, on a mass basis, preferably 1:99 to 99: 1, more preferably 1:99 to 70:30, and even more preferably 2:98 to 50:50. . By setting such a ratio, the transmission spectrum can be easily optimized, and the resulting color filter tends to be excellent in contrast, brightness, heat resistance, and chemical resistance.

  In particular, the colorant (A) is preferably a colorant containing a xanthene dye (Aa) and a blue pigment. I. A coloring agent containing CI Pigment Blue 15: 6 is more preferable. The content ratio of the xanthene dye (Aa) and the blue pigment is, on a mass basis, preferably 1:99 to 70:30, more preferably 2:98 to 50:50.

The content of the colorant (A) is preferably 5 to 60% by mass, more preferably 8 to 50% by mass, and further preferably 10 to 40% by mass with respect to the total amount of the solid content. When the content of the colorant (A) is within the above range, the color density when it is used as a color filter is sufficient, and the resin (B) and the polymerizable compound (C) are contained in a necessary amount in the composition. Therefore, a color filter having sufficient mechanical strength can be formed.
Here, the “total amount of solid content” in this specification refers to an amount obtained by removing the content of the solvent from the total amount of the colored curable resin composition. The total amount of solids and the content of each component relative thereto can be measured by known analytical means such as liquid chromatography or gas chromatography, for example.

<Resin (B)>
The resin (B) is not particularly limited, but is preferably an alkali-soluble resin. Examples of the resin (B) include the following resins [K1] to [K6].
Resin [K1] At least one (a) selected from the group consisting of an unsaturated carboxylic acid and an unsaturated carboxylic acid anhydride (hereinafter sometimes referred to as “(a)”), and a cyclic ether structure having 2 to 4 carbon atoms And a copolymer of a monomer (b) having an ethylenically unsaturated bond (hereinafter sometimes referred to as “(b)”);
Resin [K2] (a) and (b), monomer (c) copolymerizable with (a) (however, different from (a) and (b)) (hereinafter referred to as “(c)”) In some cases)
Resin [K3] Copolymer of (a) and (c);
Resin [K4] A resin obtained by reacting (b) with a copolymer of (a) and (c);
Resin [K5] A resin obtained by reacting (a) with a copolymer of (b) and (c);
Resin [K6] A resin obtained by reacting (a) with a copolymer of (b) and (c) and further reacting with a carboxylic acid anhydride.

Specific examples of (a) include unsaturated monocarboxylic acids such as acrylic acid, methacrylic acid, crotonic acid, o-, m-, and p-vinylbenzoic acid;
Maleic acid, fumaric acid, citraconic acid, mesaconic acid, itaconic acid, 3-vinylphthalic acid, 4-vinylphthalic acid, 3,4,5,6-tetrahydrophthalic acid, 1,2,3,6-tetrahydrophthalic acid, dimethyl Unsaturated dicarboxylic acids such as tetrahydrophthalic acid and 1,4-cyclohexene dicarboxylic acid;
Methyl-5-norbornene-2,3-dicarboxylic acid, 5-carboxybicyclo [2.2.1] hept-2-ene, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene, 5-carboxy-5-methylbicyclo [2.2.1] hept-2-ene, 5-carboxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-carboxy-6-methylbicyclo Bicyclounsaturated compounds containing a carboxy group such as [2.2.1] hept-2-ene, 5-carboxy-6-ethylbicyclo [2.2.1] hept-2-ene;
Maleic anhydride, citraconic anhydride, itaconic anhydride, 3-vinylphthalic anhydride, 4-vinylphthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, 1,2,3,6- Unsaturated dicarboxylic acid anhydrides such as tetrahydrophthalic anhydride, dimethyltetrahydrophthalic anhydride, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene anhydride;
Unsaturated mono [(meth) acryloyloxyalkyl] esters of polyvalent carboxylic acids such as succinic acid mono [2- (meth) acryloyloxyethyl] and phthalic acid mono [2- (meth) acryloyloxyethyl] Kind;
Examples thereof include unsaturated acrylates containing a hydroxy group and a carboxy group in the same molecule, such as α- (hydroxymethyl) acrylic acid.

Among these, acrylic acid, methacrylic acid, maleic anhydride and the like are preferable from the viewpoint of copolymerization reactivity and solubility in an aqueous alkali solution.
In the present specification, “(meth) acryloyl” represents at least one selected from the group consisting of acryloyl and methacryloyl. Notations such as “(meth) acrylic acid” and “(meth) acrylate” have the same meaning.

(B) is a polymerizable compound having, for example, a C2-C4 cyclic ether structure (for example, at least one selected from the group consisting of an oxirane ring, an oxetane ring and a tetrahydrofuran ring) and an ethylenically unsaturated bond. is there. (B) is preferably a monomer having a C2-C4 cyclic ether structure and a (meth) acryloyloxy group.
In the present specification, “(meth) acrylic acid” represents at least one selected from the group consisting of acrylic acid and methacrylic acid. Notations such as “(meth) acryloyl” and “(meth) acrylate” have the same meaning.

  Examples of (b) include a monomer (b1) having an oxiranyl group and an ethylenically unsaturated bond (hereinafter sometimes referred to as “(b1)”), and a single monomer having an oxetanyl group and an ethylenically unsaturated bond. Monomer (b2) (hereinafter sometimes referred to as “(b2)”), monomer (b3) having a tetrahydrofuryl group and an ethylenically unsaturated bond (hereinafter sometimes referred to as “(b3)”), etc. Can be mentioned.

  (B1) is, for example, a monomer (b1-1) having a structure in which a linear or branched unsaturated aliphatic hydrocarbon is epoxidized (hereinafter referred to as “(b1-1)”) And a monomer (b1-2) having a structure in which an unsaturated alicyclic hydrocarbon is epoxidized (hereinafter may be referred to as “(b1-2)”).

  Examples of (b1-1) include glycidyl (meth) acrylate, β-methylglycidyl (meth) acrylate, β-ethylglycidyl (meth) acrylate, glycidyl vinyl ether, o-vinylbenzyl glycidyl ether, and m-vinylbenzyl glycidyl ether. P-vinylbenzyl glycidyl ether, α-methyl-o-vinylbenzyl glycidyl ether, α-methyl-m-vinylbenzyl glycidyl ether, α-methyl-p-vinylbenzyl glycidyl ether, 2,3-bis (glycidyloxymethyl) ) Styrene, 2,4-bis (glycidyloxymethyl) styrene, 2,5-bis (glycidyloxymethyl) styrene, 2,6-bis (glycidyloxymethyl) styrene, 2,3,4-tris (glycidyloxymethyl) ) Styrene, 2,3,5-tris (glycidyloxymethyl) styrene, 2,3,6-tris (glycidyloxymethyl) styrene, 3,4,5-tris (glycidyloxymethyl) styrene, 2,4,6 -Tris (glycidyloxymethyl) styrene etc. are mentioned.

  Examples of (b1-2) include vinylcyclohexene monooxide, 1,2-epoxy-4-vinylcyclohexane (for example, Celoxide 2000; manufactured by Daicel Chemical Industries, Ltd.), 3,4-epoxycyclohexylmethyl (meth). Acrylate (for example, Cyclomer A400; manufactured by Daicel Chemical Industries, Ltd.), 3,4-epoxycyclohexylmethyl (meth) acrylate (for example, Cyclomer M100; manufactured by Daicel Chemical Industries, Ltd.), represented by formula (I) And a compound represented by the formula (II).

[In Formula (I) and Formula (II), R ^b1 and R ^b2 represent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, and the hydrogen atom contained in the alkyl group is substituted with a hydroxy group. May be.
X ^b1 and X ^b2 represents a single ^{bond, -R b3 -, * - R} b3 -O -, * - R b3 -S- or * -R ^b3 represents a -NH-.
R ^b3 represents an alkanediyl group having 1 to 6 carbon atoms.
* Represents a bond with O. ]

Examples of the alkyl group having 1 to 4 carbon atoms include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, a sec-butyl group, and a tert-butyl group.
Examples of the alkyl group in which a hydrogen atom is substituted with hydroxy include hydroxymethyl group, 1-hydroxyethyl group, 2-hydroxyethyl group, 1-hydroxypropyl group, 2-hydroxypropyl group, 3-hydroxypropyl group, 1-hydroxy Examples include a -1-methylethyl group, a 2-hydroxy-1-methylethyl group, a 1-hydroxybutyl group, a 2-hydroxybutyl group, a 3-hydroxybutyl group, and a 4-hydroxybutyl group.
R ^b1 and R ^b2 are preferably a hydrogen atom, a methyl group, a hydroxymethyl group, a 1-hydroxyethyl group or a 2-hydroxyethyl group, and more preferably a hydrogen atom or a methyl group.

Examples of alkanediyl groups include methylene group, ethylene group, propane-1,2-diyl group, propane-1,3-diyl group, butane-1,4-diyl group, pentane-1,5-diyl group, hexane- Examples include 1,6-diyl group.
X ^b1 and X ^b2 are preferably a single bond, a methylene group, an ethylene group, * —CH ₂ —O— or * —CH ₂ CH ₂ —O—, more preferably a single bond or * —CH ₂ CH. ₂ -O- (* represents a bond with O).

  Examples of the compound represented by the formula (I) include compounds represented by any one of the formulas (I-1) to (I-15). Among them, Formula (I-1), Formula (I-3), Formula (I-5), Formula (I-7), Formula (I-9), and Formula (I-11) to Formula (I-15) A compound represented by any one of formula (I-1), formula (I-7), formula (I-9) and formula (I-15) is more preferred.

  Examples of the compound represented by the formula (II) include compounds represented by any one of the formulas (II-1) to (II-15). Among them, formula (II-1), formula (II-3), formula (II-5), formula (II-7), formula (II-9) and formula (II-11) to formula (II-15) A compound represented by any one of formulas (II-1), (II-7), (II-9) and (II-15) is more preferred.

  The compound represented by the formula (I) and the compound represented by the formula (II) may be used singly or as a mixture in any ratio. When used as a mixture, the content ratio of the compound represented by the formula (I) and the compound represented by the formula (II) is preferably 5:95 to 95: 5, more preferably 10:90 to 5 on a molar basis. 90:10, more preferably 20:80 to 80:20.

  As the monomer (b2) having an oxetanyl group and an ethylenically unsaturated bond, a monomer having an oxetanyl group and a (meth) acryloyloxy group is more preferable. (B2) includes 3-methyl-3-methacryloyloxymethyloxetane, 3-methyl-3-acryloyloxymethyloxetane, 3-ethyl-3-methacryloyloxymethyloxetane, 3-ethyl-3-acryloyloxymethyloxetane , 3-methyl-3-methacryloyloxyethyl oxetane, 3-methyl-3-acryloyloxyethyl oxetane, 3-ethyl-3-methacryloyloxyethyl oxetane, 3-ethyl-3-acryloyloxyethyl oxetane, and the like.

  As the monomer (b3) having a tetrahydrofuryl group and an ethylenically unsaturated bond, a monomer having a tetrahydrofuryl group and a (meth) acryloyloxy group is more preferable. Specific examples of (b3) include tetrahydrofurfuryl acrylate (for example, Biscoat V # 150, manufactured by Osaka Organic Chemical Industry Co., Ltd.), tetrahydrofurfuryl methacrylate, and the like.

  (B) is preferably (b1) in that the color filter obtained can have higher reliability such as heat resistance and chemical resistance. Furthermore, (b1-2) is more preferable in that the storage stability of the colored curable resin composition is excellent.

Examples of (c) include methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, sec-butyl (meth) acrylate, tert-butyl (meth) acrylate, and 2-ethylhexyl (meth). Acrylate, dodecyl (meth) acrylate, lauryl (meth) acrylate, stearyl (meth) acrylate, cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-methylcyclohexyl (meth) acrylate, tricyclo [5.2.1.0 ^2,6 ] decan-8-yl (meth) acrylate (in this technical field, it is called “dicyclopentanyl (meth) acrylate” as a common name. In the case of “tricyclodecyl (meth) acrylate”) There is a bird) Black (in the art, it is said that "dicyclopentenyl (meth) acrylate" as trivial name.) [5.2.1.0 ^2,6] decene-8-yl (meth) acrylate, dicyclopenta Nyloxyethyl (meth) acrylate, isobornyl (meth) acrylate, adamantyl (meth) acrylate, allyl (meth) acrylate, propargyl (meth) acrylate, phenyl (meth) acrylate, naphthyl (meth) acrylate, benzyl (meth) acrylate, etc. (Meth) acrylic acid esters of
Hydroxy group-containing (meth) acrylic acid esters such as 2-hydroxyethyl (meth) acrylate and 2-hydroxypropyl (meth) acrylate;
Dicarboxylic acid diesters such as diethyl maleate, diethyl fumarate, diethyl itaconate;
Bicyclo [2.2.1] hept-2-ene, 5-methylbicyclo [2.2.1] hept-2-ene, 5-ethylbicyclo [2.2.1] hept-2-ene, 5- Hydroxybicyclo [2.2.1] hept-2-ene, 5-hydroxymethylbicyclo [2.2.1] hept-2-ene, 5- (2′-hydroxyethyl) bicyclo [2.2.1] Hept-2-ene, 5-methoxybicyclo [2.2.1] hept-2-ene, 5-ethoxybicyclo [2.2.1] hept-2-ene, 5,6-dihydroxybicyclo [2.2 .1] Hept-2-ene, 5,6-di (hydroxymethyl) bicyclo [2.2.1] hept-2-ene, 5,6-di (2′-hydroxyethyl) bicyclo [2.2. 1] hept-2-ene, 5,6-dimethoxybicyclo [2.2 1] hept-2-ene, 5,6-diethoxybicyclo [2.2.1] hept-2-ene, 5-hydroxy-5-methylbicyclo [2.2.1] hept-2-ene, 5 -Hydroxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-hydroxymethyl-5-methylbicyclo [2.2.1] hept-2-ene, 5-tert-butoxycarbonylbicyclo [ 2.2.1] Hept-2-ene, 5-cyclohexyloxycarbonylbicyclo [2.2.1] hept-2-ene, 5-phenoxycarbonylbicyclo [2.2.1] hept-2-ene, 5 , 6-bis (tert-butoxycarbonyl) bicyclo [2.2.1] hept-2-ene, 5,6-bis (cyclohexyloxycarbonyl) bicyclo [2.2.1] hept-2-ene, etc. Bicyclounsaturated compounds;
N-phenylmaleimide, N-cyclohexylmaleimide, N-benzylmaleimide, N-succinimidyl-3-maleimidobenzoate, N-succinimidyl-4-maleimidobutyrate, N-succinimidyl-6-maleimidocaproate, N-succinimidyl-3 -Dicarbonylimide derivatives such as maleimide propionate, N- (9-acridinyl) maleimide;
Styrene, α-methylstyrene, m-methylstyrene, p-methylstyrene, vinyl toluene, p-methoxystyrene, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, acrylamide, methacrylamide, vinyl acetate, 1,3-butadiene , Isoprene, 2,3-dimethyl-1,3-butadiene and the like.
Of these, styrene, vinyltoluene, N-phenylmaleimide, N-cyclohexylmaleimide and N-benzylmaleimide are preferable from the viewpoint of copolymerization reactivity and heat resistance.

In the resin [K1], the ratio of the structural unit derived from each is the total structural unit constituting the resin [K1]
Structural unit derived from (a); 2 to 60 mol%
Structural unit derived from (b); 40-98 mol%
It is preferable that
Structural unit derived from (a); 10-50 mol%
Structural unit derived from (b); 50-90 mol%
It is more preferable that
When the ratio of the structural unit of the resin [K1] is in the above range, the storage stability of the colored curable resin composition, the developability when forming a colored pattern, and the solvent resistance of the resulting colored pattern are excellent. Tend.

  The resin [K1] is, for example, a method described in the document “Experimental Method for Polymer Synthesis” (Takayuki Otsu, published by Kagaku Dojin Co., Ltd., First Edition, First Edition, issued March 1, 1972) and the document Can be produced with reference to the cited references described in 1.

  Specifically, a predetermined amount of (a) and (b), a polymerization initiator, a solvent, and the like are placed in a reaction vessel, for example, by substituting oxygen with nitrogen to create a deoxygenated atmosphere, with stirring, The method of heating and heat retention is mentioned. In addition, the polymerization initiator, the solvent, and the like used here are not particularly limited, and those usually used in the field can be used. For example, as polymerization initiators, azo compounds (2,2'-azobisisobutyronitrile, 2,2'-azobis (2,4-dimethylvaleronitrile), etc.) and organic peroxides (benzoyl peroxide, etc.) As the solvent, any solvent capable of dissolving each monomer may be used, and examples thereof include a solvent (E) described later as a solvent for the colored curable resin composition.

  In addition, the obtained copolymer may use the solution after reaction as it is, a concentrated or diluted solution may be used, and it took out as solid (powder) by methods, such as reprecipitation. Things may be used. In particular, by using a solvent (E) described later as a solvent in the polymerization, the solution after the reaction can be used as it is, and the manufacturing process can be simplified.

In the resin [K2], the ratio of the structural units derived from each of the structural units in the resin [K2]
Structural unit derived from (a); 2-45 mol%
Structural unit derived from (b); 2 to 95 mol%
Structural unit derived from (c); 1 to 65 mol%
It is preferable that
Structural unit derived from (a); 5 to 40 mol%
Structural unit derived from (b); 5 to 80 mol%
Structural unit derived from (c); 5 to 60 mol%
It is more preferable that
When the ratio of the structural unit of the resin [K2] is in the above range, the storage stability of the colored curable resin composition, the developability when forming the colored pattern, and the solvent resistance of the resulting colored pattern, There is a tendency to be excellent in heat resistance and mechanical strength.

  Resin [K2] can be produced, for example, in the same manner as the method described as the production method of resin [K1].

In the resin [K3], the proportion of structural units derived from each of the structural units constituting the resin [K3]
Structural unit derived from (a); 2 to 60 mol%
Structural unit derived from (c); 40 to 98 mol%
It is preferable that
Structural unit derived from (a); 10-50 mol%
Structural unit derived from (c); 50-90 mol%
It is more preferable that
Resin [K3] can be produced, for example, in the same manner as described for the production method of resin [K1].

Resin [K4] obtains a copolymer of (a) and (c), and (a) has a carboxylic acid and / or carboxylic acid anhydride having (a) a cyclic ether having 2 to 4 carbon atoms that (b) has It can manufacture by adding to.
First, a copolymer of (a) and (c) is produced in the same manner as described in the method for producing resin [K1]. In this case, the ratio of the structural units derived from each is preferably the same as that described for the resin [K3].

Next, the C2-C4 cyclic ether which (b) has is reacted with a part of the carboxylic acid and / or carboxylic anhydride derived from (a) in the copolymer.
Subsequent to the production of the copolymer of (a) and (c), the atmosphere in the flask is replaced from nitrogen to air, and (b) a reaction catalyst of carboxylic acid or carboxylic anhydride and cyclic ether (for example, tris ( Dimethylaminomethyl) phenol, etc.) and a polymerization inhibitor (eg, hydroquinone, etc.) are placed in a flask and reacted, for example, at 60-130 ° C. for 1-10 hours to produce resin [K4]. it can.
The amount of (b) used is preferably 5 to 80 mol, more preferably 10 to 75 mol, per 100 mol of (a). By making it within this range, the storage stability of the colored curable resin composition, the developability when forming the pattern, and the balance of the solvent resistance, heat resistance, mechanical strength and sensitivity of the resulting pattern are improved. Tend. Since the reactivity of the cyclic ether is high and unreacted (b) hardly remains, (b1) is preferable as (b) used for the resin [K4], and (b1-1) is more preferable.
The amount of the reaction catalyst used is preferably 0.001 to 5 parts by mass with respect to 100 parts by mass of the total amount of (a), (b) and (c). The amount of the polymerization inhibitor used is preferably 0.001 to 5 parts by mass with respect to 100 parts by mass of the total amount of (a), (b) and (c).
The reaction conditions such as the charging method, reaction temperature, and time can be appropriately adjusted in consideration of the production equipment and the amount of heat generated by polymerization. In addition, like the polymerization conditions, the charging method and the reaction temperature can be appropriately adjusted in consideration of the production equipment, the amount of heat generated by the polymerization, and the like.

Resin [K5] obtains a copolymer of (b) and (c) as a first step in the same manner as in the method for producing resin [K1] described above. Similarly to the above, the obtained copolymer may be used as it is after the reaction, or may be a concentrated or diluted solution, or may be solid (powder) by a method such as reprecipitation. You may use what was taken out as.
The ratio of the structural units derived from (b) and (c) is preferably in the following range with respect to the total number of moles of all structural units constituting the copolymer.
Structural unit derived from (b); 5-95 mol%
Structural unit derived from (c); 5-95 mol%
It is preferable that
Structural unit derived from (b); 10-90 mol%
Structural unit derived from (c); 10 to 90 mol%
It is more preferable that

Further, under the same conditions as in the method for producing the resin [K4], the cyclic ether derived from (b) of the copolymer of (b) and (c) is added to the carboxylic acid or carboxylic acid anhydride of (a). Resin [K5] can be obtained by reacting the product.
As for the usage-amount of (a) made to react with the said copolymer, 5-80 mol is preferable with respect to 100 mol of (b). Since the reactivity of the cyclic ether is high and unreacted (b) hardly remains, (b1) is preferable as (b) used for the resin [K5], and (b1-1) is more preferable.

Resin [K6] is a resin obtained by further reacting carboxylic anhydride with resin [K5]. Carboxylic anhydride is reacted with a hydroxy group generated by reaction of cyclic ether with carboxylic acid or carboxylic anhydride.
Carboxylic anhydrides include maleic anhydride, citraconic anhydride, itaconic anhydride, 3-vinylphthalic anhydride, 4-vinylphthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, 1 2,3,6-tetrahydrophthalic anhydride, dimethyltetrahydrophthalic anhydride, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene anhydride (highmic acid anhydride) and the like. It is done. As for the usage-amount of carboxylic acid anhydride, 0.5-1 mol is preferable with respect to 1 mol of usage-amount of (a).

Specific examples of the resin (B) include 3,4-epoxycyclohexylmethyl (meth) acrylate / (meth) acrylic acid copolymer, 3,4-epoxytricyclo [5.2.1.0 ^2.6. ] Resin such as decyl acrylate / (meth) acrylic acid copolymer [K1]; glycidyl (meth) acrylate / benzyl (meth) acrylate / (meth) acrylic acid copolymer, glycidyl (meth) acrylate / styrene / (meta ) Acrylic acid copolymer, 3,4-epoxytricyclo [5.2.1.0 ^2.6 ] decyl acrylate / (meth) acrylic acid / N-cyclohexylmaleimide copolymer, 3,4-epoxytricyclo [5.2.1.0 ^2.6] decyl acrylate / (meth) acrylic acid / vinyl toluene / dicyclopentenyl (meth) acrylate Polymer, resin such as 3-methyl-3- (meth) acryloyloxymethyloxetane / (meth) acrylic acid / styrene copolymer [K2]; benzyl (meth) acrylate / (meth) acrylic acid copolymer, Resin [K3] such as styrene / (meth) acrylic acid copolymer; resin obtained by adding glycidyl (meth) acrylate to benzyl (meth) acrylate / (meth) acrylic acid copolymer, tricyclodecyl (meth) acrylate / Styrene / (meth) acrylic acid copolymer added with glycidyl (meth) acrylate, tricyclodecyl (meth) acrylate / benzyl (meth) acrylate / (meth) acrylic acid copolymer with glycidyl (meth) Resin such as acrylate-added resin [K4]; Tricyclodecyl (meth) acrylate / g Residue obtained by reacting (meth) acrylic acid with a copolymer of sidyl (meth) acrylate, and (meth) acrylic acid reacted with a copolymer of tricyclodecyl (meth) acrylate / styrene / glycidyl (meth) acrylate Resins such as resin [K5]; resins obtained by reacting a copolymer of tricyclodecyl (meth) acrylate / glycidyl (meth) acrylate with (meth) acrylic acid and further reacting with tetrahydrophthalic anhydride Resin [K6] etc. are mentioned.

  Especially, as resin (B), resin [K1], resin [K2], and resin [K3] are preferable.

The polystyrene equivalent weight average molecular weight of the resin (B) is preferably 3,000 to 100,000, more preferably 5,000 to 50,000, and further preferably 5,000 to 30,000. . When the molecular weight is in the above range, the coating film hardness is improved, the residual film ratio is high, the solubility of the unexposed portion in the developer is good, and the resolution tends to be improved.
The molecular weight distribution [weight average molecular weight (Mw) / number average molecular weight (Mn)] of the resin (B) is preferably 1.1 to 6, and more preferably 1.2 to 4.

  The acid value of the resin (B) is preferably 50 to 170 mg-KOH / g, more preferably 60 to 150 mg-KOH / g, and still more preferably 70 to 135 mg-KOH / g. Here, the acid value is a value measured as the amount (mg) of potassium hydroxide necessary to neutralize 1 g of the resin, and can be determined by titration using, for example, an aqueous potassium hydroxide solution.

  Content of resin (B) becomes like this. Preferably it is 7-65 mass% with respect to the total amount of solid content, More preferably, it is 13-60 mass%, More preferably, it is 17-55 mass%. When content of resin (B) exists in the said range, there exists a tendency for the resolution of a coloring pattern and the remaining film rate of a coloring pattern to improve.

<Polymerizable compound (C)>
The polymerizable compound (C) is a compound that can be polymerized by heat or an active radical and / or acid generated from the polymerization initiator (D). For example, a compound having a polymerizable ethylenically unsaturated bond is used. Preferably, it is a (meth) acrylic acid ester compound.

Among these, the polymerizable compound (C) is preferably a polymerizable compound having three or more ethylenically unsaturated bonds. Examples of such polymerizable compounds include trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa ( (Meth) acrylate, tripentaerythritol octa (meth) acrylate, tripentaerythritol hepta (meth) acrylate, tetrapentaerythritol deca (meth) acrylate, tetrapentaerythritol nona (meth) acrylate, tris (2- (meth) acryloyloxyethyl) ) Isocyanurate, ethylene glycol modified pentaerythritol tetra (meth) acrylate, ethylene glycol modified dipentaerythritol Hexa (meth) acrylate, propylene glycol modified pentaerythritol tetra (meth) acrylate, propylene glycol modified dipentaerythritol hexa (meth) acrylate, caprolactone modified pentaerythritol tetra (meth) acrylate, caprolactone modified dipentaerythritol hexa (meth) acrylate, etc. Is mentioned. The photopolymerizable compound (C) may be used alone or in combination of two or more.
Of these, dipentaerythritol penta (meth) acrylate and dipentaerythritol hexa (meth) acrylate are preferable.

  The weight average molecular weight of the polymerizable compound (C) is preferably from 150 to 2,900, more preferably from 250 to 1,500.

  The content of the polymerizable compound (C) is preferably 7 to 65% by mass, more preferably 13 to 60% by mass, and further preferably 17 to 55% by mass with respect to the total amount of the solid content. is there. When the content of the polymerizable compound (C) is in the above range, the remaining film ratio and chemical resistance of the colored pattern tend to be improved.

<Polymerization initiator (D)>
The polymerization initiator (D) is not particularly limited as long as it is a compound capable of generating an active radical, an acid or the like by the action of light or heat and initiating polymerization, and a known polymerization initiator can be used.
Examples of the polymerization initiator (D) include alkylphenone compounds, triazine compounds, acylphosphine oxide compounds, O-acyloxime compounds, and biimidazole compounds.

Ｏ−アシルオキシム化合物としては、例えば、Ｎ−ベンゾイルオキシ−１−（４−フェニルスルファニルフェニル）ブタン−１−オン−２−イミン、Ｎ−ベンゾイルオキシ−１−（４−フェニルスルファニルフェニル）オクタン−１−オン−２−イミン、Ｎ−ベンゾイルオキシ−１−（４−フェニルスルファニルフェニル）−３−シクロペンチルプロパン−１−オン−２−イミン、Ｎ−アセトキシ−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］エタン−１−イミン、Ｎ−アセトキシ−１−［９−エチル−６−｛２−メチル−４−（３，３−ジメチル−２，４−ジオキサシクロペンタニルメチルオキシ）ベンゾイル｝−９Ｈ−カルバゾール−３−イル］エタン−１−イミン、Ｎ−アセトキシ−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］−３−シクロペンチルプロパン−１−イミン、Ｎ−ベンゾイルオキシ−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］−３−シクロペンチルプロパン−１−オン−２−イミン等が挙げられる。イルガキュア（登録商標）ＯＸＥ０１、ＯＸＥ０２（以上、ＢＡＳＦ社製）、Ｎ−１９１９（ＡＤＥＫＡ社製）等の市販品を用いてもよい。 The O-acyl oxime compound is a compound having a partial structure represented by the formula (d1). Hereinafter, * represents a bond.

Examples of the O-acyloxime compound include N-benzoyloxy-1- (4-phenylsulfanylphenyl) butan-1-one-2-imine, N-benzoyloxy-1- (4-phenylsulfanylphenyl) octane- 1-one-2-imine, N-benzoyloxy-1- (4-phenylsulfanylphenyl) -3-cyclopentylpropan-1-one-2-imine, N-acetoxy-1- [9-ethyl-6- ( 2-Methylbenzoyl) -9H-carbazol-3-yl] ethane-1-imine, N-acetoxy-1- [9-ethyl-6- {2-methyl-4- (3,3-dimethyl-2,4) -Dioxacyclopentanylmethyloxy) benzoyl} -9H-carbazol-3-yl] ethane-1-imine, N-acetoxy-1- [9 Ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] -3-cyclopentylpropane-1-imine, N-benzoyloxy-1- [9-ethyl-6- (2-methylbenzoyl)- 9H-carbazol-3-yl] -3-cyclopentylpropan-1-one-2-imine and the like. Commercial products such as Irgacure (registered trademark) OXE01, OXE02 (above, manufactured by BASF), N-1919 (manufactured by ADEKA) may be used.

The alkylphenone compound is a compound having a partial structure represented by the formula (d2) or a partial structure represented by the formula (d3). The benzene ring in these partial structures may have a substituent.

Examples of the compound having a partial structure represented by the formula (d2) include 2-methyl-2-morpholino-1- (4-methylsulfanylphenyl) propan-1-one, 2-dimethylamino-1- (4 -Morpholinophenyl) -2-benzylbutan-1-one, 2- (dimethylamino) -2-[(4-methylphenyl) methyl] -1- [4- (4-morpholinyl) phenyl] butan-1-one Etc. Commercial products such as Irgacure (registered trademark) 369, 907 and 379 (manufactured by BASF) may be used.
Examples of the compound having a partial structure represented by the formula (d3) include 2-hydroxy-2-methyl-1-phenylpropan-1-one, 2-hydroxy-2-methyl-1- [4- (2 -Hydroxyethoxy) phenyl] propan-1-one, 1-hydroxycyclohexyl phenyl ketone, oligomer of 2-hydroxy-2-methyl-1- (4-isopropenylphenyl) propan-1-one, α, α-diethoxy Examples include acetophenone and benzyl dimethyl ketal.
In terms of sensitivity, the alkylphenone compound is preferably a compound having a partial structure represented by the formula (d2).

  Examples of the triazine compound include 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxy Naphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6-piperonyl-1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxystyryl) ) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (5-methylfuran-2-yl) ethenyl] -1,3,5-triazine, 2,4- Bis (trichloromethyl) -6- [2- (furan-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (4-diethylamino-2) -Methylphenyl) Thenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (3,4-dimethoxyphenyl) ethenyl] -1,3,5-triazine.

  Examples of the acylphosphine oxide compound include 2,4,6-trimethylbenzoyldiphenylphosphine oxide. Commercial products such as Irgacure (registered trademark) 819 (manufactured by BASF) may be used.

  Examples of the biimidazole compound include 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole and 2,2′-bis (2,3-dichlorophenyl) -4. , 4 ′, 5,5′-tetraphenylbiimidazole (see, for example, JP-A-6-75372 and JP-A-6-75373), 2,2′-bis (2-chlorophenyl) -4, 4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetra (alkoxyphenyl) biimidazole, 2,2′-bis ( 2-chlorophenyl) -4,4 ′, 5,5′-tetra (dialkoxyphenyl) biimidazole, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetra (trialkoxy) Phenyl) biimidazole (for example, see JP-B-48-38403, JP-A-62-174204, etc.), and the phenyl group at the 4,4′5,5′-position is substituted with a carboalkoxy group. Examples thereof include imidazole compounds (for example, see JP-A-7-10913).

  Furthermore, examples of the polymerization initiator (D) include benzoin compounds such as benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, and benzoin isobutyl ether; benzophenone, methyl o-benzoylbenzoate, 4-phenylbenzophenone, 4-benzoyl- Benzophenone compounds such as 4′-methyldiphenyl sulfide, 3,3 ′, 4,4′-tetra (tert-butylperoxycarbonyl) benzophenone, 2,4,6-trimethylbenzophenone; 9,10-phenanthrenequinone, Examples include quinone compounds such as 2-ethylanthraquinone and camphorquinone; 10-butyl-2-chloroacridone, benzyl, methyl phenylglyoxylate, and titanocene compounds. These are preferably used in combination with a polymerization initiation assistant (D1) (particularly amines) described later.

  Examples of the acid generator include 4-hydroxyphenyldimethylsulfonium p-toluenesulfonate, 4-hydroxyphenyldimethylsulfonium hexafluoroantimonate, 4-acetoxyphenyldimethylsulfonium p-toluenesulfonate, 4-acetoxyphenyl methyl. Onium salts such as benzylsulfonium hexafluoroantimonate, triphenylsulfonium p-toluenesulfonate, triphenylsulfonium hexafluoroantimonate, diphenyliodonium p-toluenesulfonate, diphenyliodonium hexafluoroantimonate, nitrobenzyl tosylate, Examples thereof include benzoin tosylate.

  The polymerization initiator (D) is preferably a polymerization initiator containing at least one selected from the group consisting of alkylphenone compounds, triazine compounds, acylphosphine oxide compounds, O-acyloxime compounds and biimidazole compounds, and O-acyloxy compounds. More preferred is a polymerization initiator containing an oxime compound, and more preferred is a polymerization initiator containing an O-acyloxime compound and an alkylphenone compound.

  The content of the polymerization initiator (D) is preferably 0.1 to 40 parts by mass, more preferably 5 to 35, with respect to 100 parts by mass of the total amount of the resin (B) and the polymerizable compound (C). It is a mass part, More preferably, it is 10-30 mass parts. When the content of the polymerization initiator (D) is in the above range, the sensitivity is increased and the exposure time tends to be shortened, so that productivity is improved.

In addition to the polymerization initiator (D), a polymerization initiation assistant (D1) may further be included. The polymerization initiation assistant (D1) is a compound or a sensitizer used for accelerating the polymerization of the photopolymerizable compound that has been polymerized by the polymerization initiator.
Examples of the polymerization initiation aid (D1) include amine compounds, alkoxyanthracene compounds, thioxanthone compounds, and carboxylic acid compounds.

  Examples of amine compounds include triethanolamine, methyldiethanolamine, triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, isoamyl 4-dimethylaminobenzoate, 2-dimethylaminoethyl benzoate, 4- 2-ethylhexyl dimethylaminobenzoate, N, N-dimethylparatoluidine, 4,4′-bis (dimethylamino) benzophenone (commonly known as Michler's ketone), 4,4′-bis (diethylamino) benzophenone, 4,4′-bis ( Ethylmethylamino) benzophenone and the like, and 4,4′-bis (diethylamino) benzophenone is preferred. Commercial products such as EAB-F (Hodogaya Chemical Co., Ltd.) may be used.

  Examples of the alkoxyanthracene compound include 9,10-dimethoxyanthracene, 2-ethyl-9,10-dimethoxyanthracene, 9,10-diethoxyanthracene, 2-ethyl-9,10-diethoxyanthracene, and 9,10-dibutoxy. Anthracene, 2-ethyl-9,10-dibutoxyanthracene, etc. are mentioned.

  Examples of the thioxanthone compound include 2-isopropylthioxanthone, 4-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 1-chloro-4-propoxythioxanthone and the like.

  Carboxylic acid compounds include phenylsulfanyl acetic acid, methylphenylsulfanyl acetic acid, ethylphenylsulfanyl acetic acid, methylethylphenylsulfanyl acetic acid, dimethylphenylsulfanyl acetic acid, methoxyphenylsulfanyl acetic acid, dimethoxyphenylsulfanyl acetic acid, chlorophenylsulfanyl acetic acid, dichlorophenylsulfanyl acetic acid, N -Phenylglycine, phenoxyacetic acid, naphthylthioacetic acid, N-naphthylglycine, naphthoxyacetic acid and the like.

As the polymerization initiation assistant (D1), a thioxanthone compound is preferable.
When the polymerization initiation assistant (D1) is used, the amount used is preferably 0.1 to 30 parts by mass, more preferably 100 parts by mass of the total amount of the resin (B) and the polymerizable compound (C). 1 to 20 parts by mass. When the amount of the polymerization initiation assistant (D1) is within this range, a colored pattern can be formed with higher sensitivity and the productivity of the color filter tends to be improved.

<Solvent (E)>
The solvent (E) contains a cyclic ketone and propylene glycol monomethyl ether acetate.
Examples of the cyclic ketone include cyclopentanone, cyclohexanone, cyclooctanone, methylcyclohexanone, isophorone, and the like.

The content of the cyclic ketone is 25% by mass to 75% by mass, and preferably 30% by mass to 70% by mass with respect to the total amount of the solvent (E).
The content of propylene glycol monomethyl ether acetate is 25% by mass or more and 75% by mass or less, and preferably 28% by mass or more and 70% by mass or less with respect to the total amount of the solvent (E).
The total amount of cyclic ketone and propylene glycol monomethyl ether acetate is 80% by mass or more and 100% by mass or less, and preferably 88% by mass or more and 100% by mass or less, with respect to the total amount of the solvent.
When the content of the cyclic ketone and propylene glycol monomethyl ether acetate is within the above range, the viscosity of the colored curable resin composition is lowered, so when applying the colored curable resin composition using a slit nozzle coater, The coating speed can be increased.

  The solvent (E) may contain a solvent other than the cyclic ketone and propylene glycol monomethyl ether acetate. The solvent is not particularly limited, and a solvent usually used in the field can be used. For example, an ester solvent (a solvent containing —COO— in the molecule and not containing —O—), an ether solvent (a solvent containing —O— in the molecule and not containing —COO—), an ether ester solvent (intramolecular) Solvent containing -COO- and -O-), ketone solvent (solvent containing -CO- in the molecule and not containing -COO-), alcohol solvent, aromatic hydrocarbon solvent, amide solvent, dimethyl sulfoxide, etc. Can be selected and used.

  As ester solvents, methyl lactate, ethyl lactate, butyl lactate, methyl 2-hydroxyisobutanoate, ethyl acetate, n-butyl acetate, isobutyl acetate, pentyl formate, isopentyl acetate, butyl propionate, isopropyl butyrate, ethyl butyrate, butyl butyrate Methyl pyruvate, ethyl pyruvate, propyl pyruvate, methyl acetoacetate, ethyl acetoacetate, cyclohexanol acetate, γ-butyrolactone and the like.

  Ether solvents include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether , Propylene glycol monopropyl ether, propylene glycol monobutyl ether, 3-methoxy-1-butanol, 3-methoxy-3-methylbutanol, tetrahydrofuran, tetrahydropyran, 1,4-dioxane, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethyl Glycol methyl ethyl ether, diethylene glycol dipropyl ether, diethylene glycol dibutyl ether, anisole, phenetole, and the like methyl anisole.

  Examples of ether ester solvents include methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate, ethyl ethoxyacetate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, 3-ethoxy Ethyl propionate, methyl 2-methoxypropionate, ethyl 2-methoxypropionate, propyl 2-methoxypropionate, methyl 2-ethoxypropionate, ethyl 2-ethoxypropionate, methyl 2-methoxy-2-methylpropionate, Ethyl 2-ethoxy-2-methylpropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, propylene glycol monoethyl ether acetate, propylene glycol monopropyl acetate Le acetate, dipropylene glycol monomethyl ether acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monoethyl ether acetate, and the like diethylene glycol monobutyl ether acetate.

  Examples of the ketone solvent include 4-hydroxy-4-methyl-2-pentanone, acetone, 2-butanone, 2-heptanone, 3-heptanone, 4-heptanone, 4-methyl-2-pentanone, and the like.

  Examples of the alcohol solvent include methanol, ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol, propylene glycol, and glycerin.

  Examples of the aromatic hydrocarbon solvent include benzene, toluene, xylene, mesitylene and the like.

  Examples of the amide solvent include N, N-dimethylformamide, N, N-dimethylacetamide, N-methylpyrrolidone and the like.

  Among the above solvents, an organic solvent having a viscosity at 20 ° C. of 3.0 mPa · s or less is preferable and an organic solvent having a viscosity of 2.8 mPa · s or less is more preferable from the viewpoint of applicability. As such a solvent, propylene glycol monomethyl ether, ethyl lactate, ethyl 3-ethoxypropionate, ethylene glycol monomethyl ether and 4-hydroxy-4-methyl-2-pentanone are preferable, and propylene glycol monomethyl ether is more preferable.

  Content of a solvent (E) is 80 to 90 mass% with respect to the total amount of colored curable resin composition, Preferably it is 82 to 88 mass%. In other words, the solid content of the colored curable resin composition is 10% by mass or more and 20% by mass or less, preferably 12% by mass or more and 18% by mass or less. When the content of the solvent (E) is within the above range, the viscosity of the colored curable resin composition is lowered. Therefore, when the colored curable resin composition is applied using a slit nozzle coater, the coating speed is increased. be able to.

<Surfactant (F)>
Examples of the surfactant (F) include silicone surfactants, fluorine surfactants, and silicone surfactants having a fluorine atom. These may have a polymerizable group in the side chain.
Examples of the silicone surfactant include a surfactant having a siloxane bond in the molecule. Specifically, Torre Silicone DC3PA, SH7PA, DC11PA, SH21PA, SH28PA, SH29PA, SH30PA, SH8400 (trade names: manufactured by Toray Dow Corning Co., Ltd.), KP321, KP322, KP323, KP324 , KP326, KP340, KP341 (manufactured by Shin-Etsu Chemical Co., Ltd.), TSF400, TSF401, TSF410, TSF4300, TSF4440, TSF4445, TSF-4446, TSF4452 and TSF4460 (made by Momentive Performance Materials Japan GK) Can be mentioned.

  Examples of the fluorosurfactant include surfactants having a fluorocarbon chain in the molecule. Specifically, Florard (registered trademark) FC430, FC431 (manufactured by Sumitomo 3M Co., Ltd.), MegaFac (registered trademark) F142D, F171, F172, F173, F177, F183, F183, F554, R30, RS-718-K (manufactured by DIC Corporation), Ftop (registered trademark) EF301, EF303, EF351, EF352 (manufactured by Mitsubishi Materials Electronic Chemicals), Surflon (registered trademark) S381, S382, SC101, SC105 (Asahi Glass Co., Ltd.) and E5844 (Daikin Fine Chemical Laboratory Co., Ltd.).

  Examples of the silicone-based surfactant having a fluorine atom include surfactants having a siloxane bond and a fluorocarbon chain in the molecule. Specifically, Megafac (registered trademark) R08, BL20, F475, F477, F443 (manufactured by DIC Corporation), and the like can be given.

  The content of the surfactant (F) is preferably 0.001% by mass or more and 0.2% by mass or less, and preferably 0.002% by mass or more and 0.00% by mass or less with respect to the total amount of the colored curable resin composition. It is 1 mass% or less, More preferably, it is 0.01 mass% or more and 0.05 mass% or less. This content does not include the content of the pigment dispersant. When the content of the surfactant (F) is in the above range, the flatness of the color filter can be improved.

<Other ingredients>
The colored curable resin composition of the present invention includes additives known in the art, such as fillers, other polymer compounds, adhesion promoters, antioxidants, light stabilizers, chain transfer agents, etc., if necessary. May be included.

<Method for producing colored curable resin composition>
The colored curable resin composition of the present invention includes, for example, a dye (A1), a pigment (A2), a resin (B), a polymerizable compound (C), a polymerization initiator (D), and a polymerization used as necessary. The initiator (D1), the surfactant (F) and other components can be prepared by mixing with the solvent (E).
The pigment (A2) is preferably mixed with the solvent (E) in advance, and dispersed using a bead mill or the like until the average particle size of the pigment is about 0.2 μm or less. Under the present circumstances, you may mix | blend a part or all of the said pigment dispersant and resin (B) as needed. In the obtained pigment dispersion, the remainder of the resin (B) and the polymerizable compound (C), the polymerization initiator (D) used as necessary, the remainder of the solvent (E), the surfactant (F ) And other components and the like are mixed so as to have a predetermined concentration, whereby the desired colored curable resin composition can be prepared.
It is preferable to prepare a solution by dissolving the dye (A1) in the solvent (E) in advance. The solution is preferably filtered with a filter having a pore size of about 0.01 to 1 μm.
The colored curable resin composition prepared by mixing as described above is preferably filtered with a filter having a pore size of about 0.1 to 10 μm.

<Color filter manufacturing method>
Examples of the method for producing the color pattern of the color filter from the colored curable resin composition of the present invention include a photolithographic method, an ink jet method, and a printing method. Of these, the photolithographic method is preferable. The photolithographic method is a method in which the colored curable resin composition is applied to a substrate, dried to form a composition layer, and the composition layer is exposed through a photomask and developed. In the photolithography method, a colored coating film that is a cured product of the composition layer can be formed by not using a photomask and / or not developing during exposure.
The film thickness of the color filter to be produced is not particularly limited, and can be appropriately adjusted according to the purpose and application. ~ 6 μm.

  As the substrate, quartz glass, borosilicate glass, alumina silicate glass, glass plate such as soda lime glass coated with silica on the surface, resin plate such as polycarbonate, polymethyl methacrylate, polyethylene terephthalate, silicon, on the substrate In addition, aluminum, silver, or a silver / copper / palladium alloy thin film is used. On these substrates, another color filter layer, a resin layer, a transistor, a circuit, and the like may be formed.

Formation of each color pixel by the photolithographic method can be performed by a known or commonly used apparatus and conditions. For example, it can be produced as follows.
First, a colored curable resin composition is applied on a substrate, dried by heating (pre-baking) and / or drying under reduced pressure to remove volatile components such as a solvent, and a smooth composition layer is obtained.
Examples of the coating method include spin coating, slit coating, and slit and spin coating. In particular, since the colored curable resin composition of the present invention has a low viscosity, it is useful for a coating method using a coater having a slit nozzle, such as a slit coating method and a slit and spin coating method.
30-120 degreeC is preferable and the temperature in the case of performing heat drying has more preferable 50-110 degreeC. In addition, the heating time is preferably 10 seconds to 60 minutes, and more preferably 30 seconds to 30 minutes.
When performing vacuum drying, it is preferable to carry out in the temperature range of 20-25 degreeC under the pressure of 50-150 Pa.
The film thickness of the composition layer is not particularly limited, and may be appropriately selected according to the film thickness of the target color filter.

Next, the composition layer is exposed through a photomask for forming a target coloring pattern. The pattern on the photomask is not particularly limited, and a pattern according to the intended use is used.
The light source used for exposure is preferably a light source that generates light having a wavelength of 250 to 450 nm. For example, light less than 350 nm can be cut using a filter that cuts this wavelength range, or light near 436 nm, 408 nm, and 365 nm can be selectively extracted using a bandpass filter that extracts these wavelength ranges. Or you may. Specific examples include mercury lamps, light emitting diodes, metal halide lamps, halogen lamps, and the like.
It is preferable to use an exposure apparatus such as a mask aligner and a stepper because the entire exposure surface can be irradiated with parallel rays uniformly and accurate alignment between the photomask and the substrate can be performed.

By developing the exposed composition layer in contact with a developer, a colored pattern is formed on the substrate. By the development, the unexposed portion of the composition layer is dissolved and removed in the developer. As the developer, for example, an aqueous solution of an alkaline compound such as potassium hydroxide, sodium hydrogen carbonate, sodium carbonate, tetramethylammonium hydroxide is preferable. The concentration of these alkaline compounds in the aqueous solution is preferably 0.01 to 10% by mass, more preferably 0.03 to 5% by mass. Further, the developer may contain a surfactant.
The developing method may be any of paddle method, dipping method, spray method and the like. Further, the substrate may be tilted at an arbitrary angle during development.
After development, it is preferable to wash with water.

  Furthermore, it is preferable to post-bake the obtained colored pattern. The post-bake temperature is preferably 150 to 250 ° C, more preferably 160 to 235 ° C. The post-bake time is preferably 0.5 to 10 minutes, and more preferably 1 to 5 minutes.

The colored pattern and the colored coating film thus obtained are useful as a color filter.
According to the colored curable resin composition of the present invention, since a high-performance color filter can be produced with high productivity, the color filter can be used for a display device (for example, a liquid crystal display device, an organic EL device, etc.), an electronic device. It is useful as a color filter used for paper, solid-state imaging devices and the like.

  Next, the present invention will be described more specifically with reference to examples. In the examples, “%” and “part” representing the content or amount used are based on mass unless otherwise specified.

[Synthesis Example 1]
A mixture of a compound represented by the formula (A1-1a) and a compound represented by the formula (A1-1b) (trade name Chugai Aminol Fast Pink R; manufactured by Chugai Kasei Co., Ltd.) 15 in a flask equipped with a condenser and a stirrer. Part, 150 parts of chloroform and 8.9 parts of N, N-dimethylformamide were added dropwise and 10.9 parts of thionyl chloride was added dropwise while maintaining at 20 ° C. or lower with stirring. After completion of the dropwise addition, the temperature was raised to 50 ° C., the reaction was continued for 5 hours at the same temperature, and then cooled to 20 ° C. While maintaining the reaction solution after cooling at 20 ° C. or lower with stirring, a mixed solution of 12.5 parts of 2-ethylhexylamine and 22.1 parts of triethylamine was added dropwise. Then, it was made to react by stirring at the same temperature for 5 hours. Next, after the solvent of the obtained reaction mixture was distilled off with a rotary evaporator, a small amount of methanol was added and stirred vigorously. This mixture was added to a mixture of 375 parts of ion exchange water with stirring to precipitate crystals. The precipitated crystals are separated by filtration, washed well with ion-exchanged water, dried under reduced pressure at 60 ° C., and represented by the dye A1-1 (formula (A1-1-1) to formula (A1-1-8). Compound mixture) 11.3 parts were obtained.

一方、重合開始剤２，２’−アゾビス（２，４−ジメチルバレロニトリル）３０部をプロピレングリコールモノメチルエーテルアセテート２２５部に溶解した溶液を、別の滴下ロートを用いて４時間かけてフラスコ内に滴下した。重合開始剤の溶液の滴下が終了した後、４時間、７０℃に保持し、その後室温まで冷却して、重量平均分子量Ｍｗは、１．００×１０^４、固形分３７．５％、固形分酸価１０７ｍｇ−ＫＯＨ／ｇの共重合体（樹脂Ｂ１）溶液を得た。樹脂Ｂ１は、下記の構造単位を有する。

[Synthesis Example 2]
Nitrogen was flowed at 0.02 L / min into a flask equipped with a stirrer, thermometer, reflux condenser and dropping funnel to form a nitrogen atmosphere, 259 parts of propylene glycol monomethyl ether acetate was added, and the mixture was heated to 70 ° C. with stirring did. Next, 56 parts of acrylic acid, 83 parts of vinyltoluene, 3,4-epoxytricyclo [5.2.1.0 ^2.6 ] decyl acrylate (compound represented by formula (I-1) and formula (II- The compound represented by 1) is mixed at a molar ratio of 50:50.) 229 parts, and tricyclo [5.2.1.0 ^2.6 ] decen-8-yl acrylate (formula (c-1) The compound represented by formula (c-2) and the compound represented by formula (c-2) are mixed at a molar ratio of 50:50.) 8 parts are dissolved in 140 parts of propylene glycol monomethyl ether acetate to prepare a solution, The solution was dropped into a flask kept at 70 ° C. for 4 hours using a dropping funnel.

On the other hand, a solution prepared by dissolving 30 parts of a polymerization initiator 2,2′-azobis (2,4-dimethylvaleronitrile) in 225 parts of propylene glycol monomethyl ether acetate was placed in a flask using another dropping funnel over 4 hours. It was dripped. After completion of dropping of the polymerization initiator solution, the solution was kept at 70 ° C. for 4 hours, and then cooled to room temperature. The weight average molecular weight Mw was 1.00 × 10 ⁴ , solid content 37.5%, solid content. A copolymer (resin B1) solution having an acid value of 107 mg-KOH / g was obtained. Resin B1 has the following structural units.

[Synthesis Example 3]
The inside of the flask equipped with a stirrer, thermometer, reflux condenser, dropping funnel and nitrogen inlet tube was placed in a nitrogen atmosphere, 210 parts of propylene glycol monomethyl ether acetate was added, and the temperature was raised to 100 ° C. while stirring. Next, 106 parts of benzyl methacrylate, 22 parts of acrylic acid and 22 parts of dicyclopentanyl methacrylate (FA-513M manufactured by Hitachi Chemical Co., Ltd.) are dissolved in 215 parts of propylene glycol monomethyl ether acetate, and 2,2′-azobis is further added. A solution prepared by dissolving 3.6 parts of isobutyronitrile was dropped into the flask, and the mixture was continuously stirred at 100 ° C. for 5 hours, whereby a weight average molecular weight Mw of 1.00 × 10 ⁴ and a solid content of 34.1% were obtained. Then, a copolymer (resin B2) solution having a solid content acid value of 109 mgKOH / g was obtained. Resin B2 has the following structural units.

[Synthesis Example 4]
In a flask equipped with a reflux condenser, a dropping funnel and a stirrer, nitrogen was allowed to flow at 0.02 L / min to form a nitrogen atmosphere, 220 parts of ethyl lactate was added, and the mixture was heated to 70 ° C. with stirring. Next, 84 parts of methacrylic acid and 3,4-epoxytricyclo [5.2.1.0 ^2.6 ] decyl acrylate (a compound represented by formula (I-1) and a formula (II-1) The solution is prepared by dissolving 336 parts of the compound to be mixed at a molar ratio of 50:50 in 140 parts of ethyl lactate, and the solution is kept at 70 ° C. for 4 hours using a dropping funnel. The solution was dropped into the flask. On the other hand, a solution prepared by dissolving 30 parts of a polymerization initiator 2,2′-azobis (2,4-dimethylvaleronitrile) in 95 parts of ethyl lactate was dropped into the flask using another dropping funnel over 4 hours. After dropping of the solution of the polymerization initiator is completed, the temperature is kept at 70 ° C. for 4 hours, and then cooled to room temperature. The weight average molecular weight Mw is 8.0 × 10 ³ , the molecular weight distribution is 2.5, and the solid content is A copolymer (resin B3) solution having 48% and a solution acid value of 50 mg-KOH / g (acid value in terms of solid content was 104 mgKOH / g) was obtained. Resin B3 has the following structural units.

The weight average molecular weight (Mw) and the number average molecular weight (Mn) of the resin obtained in the synthesis example were measured using the GPC method under the following conditions.
Apparatus; K2479 (manufactured by Shimadzu Corporation)
Column; SHIMADZU Shim-pack GPC-80M
Column temperature: 40 ° C
Solvent; THF (tetrahydrofuran)
Flow rate: 1.0 mL / min
Detector; RI
Standard material for calibration: TSK STANDARD POLYSTYRENE F-40, F-4, F-288, A-2500, A-500 (manufactured by Tosoh Corporation)
The polystyrene-converted weight average molecular weight and number average molecular weight ratio (Mw / Mn) obtained above was defined as molecular weight distribution.

Examples 1-12, Comparative Examples 1 and 2
(Preparation of colored curable resin composition)
Each component was mixed so that it might become a composition shown in Table 1, and the colored curable resin composition was obtained. “(A2-1)” was mixed with an acrylic pigment dispersant and a solvent described in the “Solvent (E) **” column, and dispersed in advance using a bead mill. The “Solvent (E) *” column represents the total content of each solvent.

[Table 1-1]

[Table 1-2]

In Table 1, each component represents the following. The numerical values in the table represent the number of copies. The number of parts of the resin (B) represents the number of parts in terms of solid content.
Colorant (A); (A1-1); Dye A1-1
Colorant (A); (A1-2); C.I. I. Salt of direct blue 264 and dodecylbenzenesulfonic acid (manufactured by Orient Chemical Industry Co., Ltd.) (dye)
Colorant (A); (A2-1); C.I. I. Pigment Blue 15: 6 (Pigment)
Resin (B); (B1); Resin B1
Resin (B); (B2); Resin B2
Resin (B); (B3); Resin B3
Polymerizable compound (C); dipentaerythritol hexaacrylate (Kayarad (registered trademark) DPHA; manufactured by Nippon Kayaku Co., Ltd.)
Polymerization initiator (D); (D-1); N-benzoyloxy-1- (4-phenylsulfanylphenyl) octane-1-one-2-imine (Irgacure (registered trademark) OXE 01; manufactured by BASF; -Acyl oxime compound)
Polymerization initiator (D); (D-2); 2-methyl-2-morpholino-1- (4-methylsulfanylphenyl) propan-1-one (Irgacure (registered trademark) 907; manufactured by BASF Corp .; alkylphenone compound )
Polymerization initiation aid (D1); (D1-1); 2,4-diethylthioxanthone (Kayacure (registered trademark) DETX-S; manufactured by Nippon Kayaku Co., Ltd .; thioxanthone compound)
Solvent (E); (E-1); Cyclohexanone Solvent (E); (E-2); Cyclopentanone Solvent (E); (E-3); Propylene glycol monomethyl ether acetate Solvent (E); (E- 4); Propylene glycol monomethyl ether Solvent (E); (E-5); Ethyl lactate Surfactant (F); Polyether-modified silicone oil (Toray Silicone SH8400; manufactured by Toray Dow Corning Co., Ltd.)
Table 2 shows the solvent content and the solid content in the colored curable resin composition.

[Table 2]

(Viscosity measurement)
The viscosity of the obtained colored curable resin composition was measured using a viscometer (model: VISCOMETER TV-30; manufactured by Toki Sangyo Co., Ltd .; rotation speed: 100 rpm; measurement temperature: 23 ° C.). The results are shown in Table 3.

[Preparation of colored pattern]
A colored photosensitive resin composition was applied by spin coating on a 2-inch square glass substrate (Eagle XG; manufactured by Corning), and then pre-baked at 100 ° C. for 3 minutes to form a composition layer. After cooling, the distance between the substrate on which the composition layer is formed and the quartz glass photomask having a pattern is set to 100 μm, and an exposure machine (TME-150RSK; manufactured by Topcon Co., Ltd.) is used in an air atmosphere at 150 mJ / Light irradiation was performed with an exposure amount of cm ² (based on 365 nm). As a photomask, a mask on which a 100 μm line and space pattern was formed was used. After light irradiation, the exposed composition layer is developed by immersing it in an aqueous developer containing 0.12% of a nonionic surfactant and 0.04% of potassium hydroxide at 23 ° C. for 60 seconds, washed with water, Inside, post-baking was performed at 230 ° C. for 20 minutes to obtain a colored pattern.

[Film thickness measurement]
About the obtained coloring pattern, the film thickness was measured using the film thickness measuring apparatus (DEKTAK3; Nippon Vacuum Technology Co., Ltd. product). The results are shown in Table 3.

[Chromaticity evaluation]
About the obtained coloring pattern, spectrum was measured using the colorimeter (OSP-SP-200; Olympus Co., Ltd.), and the xy chromaticity coordinate in the XYZ color system of CIE using the characteristic function of C light source (X, y) and brightness Y were measured. The results are shown in Table 3.

[Applicability test]
A colored curable resin composition is applied to a 15 cm square glass substrate using a slit die coater (Takudai-100 manufactured by ITOCHU INDUSTRIAL CO., LTD.) At a coating speed of 70 mm / sec. The film thickness after curing was applied to 1.5 μm while adjusting the distance and the like. Then, it was dried with a vacuum dryer (manufactured by VCD Microtech Co., Ltd.) until the degree of vacuum reached 0.5 torr. After prebaking on a hot plate at 90 ° C. for 2 minutes and further drying, post baking was performed at 230 ° C. for 40 minutes to form a colored coating film. Illuminate the surface of the obtained colored coating film with a Na lamp, visually observe the coating film surface from various angles, and if there is no unevenness on the coating film surface, it is judged that the coating property is good, The thing where the nonuniformity was recognized was set as x. The results are shown in Table 3.

[Table 3]

  It was confirmed that the colored curable resin composition of an Example has a low viscosity. From this, according to the colored curable resin composition of this invention, a color filter can be manufactured with high productivity.

  Since the colored curable resin composition of the present invention has a low viscosity, a color filter can be produced with high productivity.

Claims (5)

Including colorants, resins, polymerizable compounds, polymerization initiators and solvents,
The colorant is a colorant comprising a dye and a pigment;
The solvent is a solvent containing a cyclic ketone and propylene glycol monomethyl ether acetate,
The cyclic ketone content is 25% by mass or more and 75% by mass or less with respect to the total amount of the solvent,
The content of propylene glycol monomethyl ether acetate is 25% by mass or more and 75% by mass or less with respect to the total amount of the solvent,
The colored curable resin composition whose content of a solvent is 80 to 90 mass% with respect to the total amount of a colored curable resin composition.   The colored curable resin composition according to claim 1, wherein the total amount of the cyclic ketone and the propylene glycol monomethyl ether acetate is 80% by mass or more and 100% by mass or less based on the total amount of the solvent.   The colored curable resin composition according to claim 1 or 2, wherein the cyclic ketone is at least one selected from the group consisting of cyclohexanone and cyclopentanone.   The color filter formed with the colored curable resin composition as described in any one of Claims 1-3.   A display device comprising the color filter according to claim 4.