JP2013018919A - Polyurethane foam for seat pad - Google Patents
Polyurethane foam for seat pad Download PDFInfo
- Publication number
- JP2013018919A JP2013018919A JP2011155182A JP2011155182A JP2013018919A JP 2013018919 A JP2013018919 A JP 2013018919A JP 2011155182 A JP2011155182 A JP 2011155182A JP 2011155182 A JP2011155182 A JP 2011155182A JP 2013018919 A JP2013018919 A JP 2013018919A
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane foam
- stock solution
- foam
- seat pad
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、シートパッド用ポリウレタンフォームに関し、さらに詳しくは共振周波数と共振倍率を同時に低減することができ、乗り心地性能を向上させた車両用シートパッドに最適なシートパッド用ポリウレタンフォームに関する。 The present invention relates to a polyurethane foam for a seat pad, and more particularly to a polyurethane foam for a seat pad that is capable of simultaneously reducing a resonance frequency and a resonance magnification and is optimal for a vehicle seat pad with improved riding comfort performance.
ポリウレタンフォームは、用途に応じて、機械的特性、断熱性及び振動吸収性等の様々な特性が求められているが、とりわけ車両用のシートパッド等においては高い反発弾性や座り心地感等の快適性が求められている。このような快適性の向上を目指し、一般に人体の内臓の共振点といわれる6Hz付近(約4〜8Hz)の振動吸収特性を高めるため、ポリウレタン発泡原料の主成分の構造や充填材等の副原料について見直しが図られ、得られるポリウレタンフォームの共振周波数及び共振倍率を下げる試みがなされてきた。
シートパッドの乗り心地性能として、振動特性は非常に重要な特性であり、振動特性向上では、上記のように共振周波数と共振倍率を下げることが求められるが、これらは二律背反の関係にあり、同時に低くすることは困難である。
Polyurethane foam is required to have various properties such as mechanical properties, heat insulation and vibration absorption depending on the application, but especially in vehicle seat pads, etc., comfort such as high rebound resilience and sitting comfort. Sex is required. Aiming at such comfort improvement, in order to improve vibration absorption characteristics in the vicinity of 6 Hz (about 4 to 8 Hz), which is generally called the resonance point of the internal organs of the human body, the main component structure of polyurethane foam raw materials and auxiliary materials such as fillers Has been reviewed, and attempts have been made to lower the resonance frequency and resonance magnification of the resulting polyurethane foam.
As the ride performance of the seat pad, the vibration characteristic is a very important characteristic.To improve the vibration characteristic, it is required to lower the resonance frequency and the resonance magnification as described above, but these are in a trade-off relationship, and at the same time It is difficult to lower.
一方、近年の環境負荷軽減に対する意識の高まりから、車両においては燃費向上が求められ、その一環として構成部品に対する軽量化が図られてきた。軽量化に対する試みは車両の外装や内装等のあらゆる構成部品に及び、シートパッド等についても例外ではない。しかし、軽量化の観点から発泡材の低密度化を実現しようとすると、快適性に影響する振動吸収特性が低下するという問題があり、低密度化と振動吸収特性の両立が困難であった。そのため、乗り心地感、燃費向上などのニーズから軽量且つ適度な反発力及び良好な振動吸収特性を有するシートやクッション材が求められていた。
このような要求に対し、出願人は、ポリオール成分とイソシアネート成分とを主成分とするポリウレタン発泡原液を発泡成形してなるポリウレタンフォームにおいて、前記ポリオールとして分子量が3,000〜12,000、不飽和度が0.03ミリ当量/g以下であり、且つ分子量/官能基数が1,000〜3,000であるポリエーテルポリオールを用いると共に、有機化処理された無機充填材を配合することを特徴とするポリウレタンフォームを提案した(特許文献1参照)。ここで提案されたポリウレタンフォームは、軽量且つ振動吸収特性に優れたものである。
On the other hand, with the recent increase in awareness of environmental load reduction, vehicles have been required to improve fuel efficiency, and as part of this, weight reduction of component parts has been attempted. The attempt to reduce the weight covers all components such as the exterior and interior of the vehicle, and the seat pad is no exception. However, when attempting to reduce the density of the foam material from the viewpoint of weight reduction, there is a problem that the vibration absorption characteristics that affect the comfort are lowered, and it is difficult to achieve both the reduction in density and the vibration absorption characteristics. For this reason, there has been a demand for a seat and cushioning material having a light weight, an appropriate repulsive force, and good vibration absorption characteristics from needs such as a feeling of riding comfort and improved fuel efficiency.
In response to such a requirement, the applicant has a polyurethane foam formed by foaming a polyurethane foam stock solution mainly composed of a polyol component and an isocyanate component, and has a molecular weight of 3,000 to 12,000, unsaturated as the polyol. A polyether polyol having a degree of 0.03 meq / g or less and a molecular weight / number of functional groups of 1,000 to 3,000 is used, and an organically treated inorganic filler is blended. A polyurethane foam was proposed (see Patent Document 1). The polyurethane foam proposed here is lightweight and excellent in vibration absorption characteristics.
特許文献1に開示されるポリウレタンフォームは、共振周波数4Hz以下、共振倍率3倍以下という優れた振動特性を有しているが、このような振動特性は、ポリウレタンフォームの成形に用いる発泡原液において、特定のポリオールを用い、かつ水の配合量を特定することで、さらには成形方法として、時限圧力開放(Timed Pressure Release、以下「TPR」と記載することがある。)を用いることで、得られたものであって、シートパッドのセル構造を規定することにより、乗り心地性能を向上させる技術ではない。なお、このような技術は、これまで知られていないのが実状である。
本発明は、このような状況下になされたもので、共振周波数と共振倍率を同時に低減することができ、乗り心地性能を向上させた車両用シートパッドに最適なシートパッド用ポリウレタンフォームを提供することを目的とするものである。
The polyurethane foam disclosed in Patent Document 1 has excellent vibration characteristics such as a resonance frequency of 4 Hz or less and a resonance magnification of 3 times or less. Such a vibration characteristic is obtained in a foaming stock solution used for molding polyurethane foam. By using a specific polyol and specifying the blending amount of water, it is further obtained by using timed pressure release (hereinafter sometimes referred to as “TPR”) as a molding method. However, it is not a technique for improving ride comfort performance by defining the cell structure of the seat pad. In fact, such a technique has not been known so far.
The present invention has been made under such circumstances, and provides a polyurethane foam for a seat pad that is capable of simultaneously reducing the resonance frequency and the resonance magnification and is optimal for a vehicle seat pad with improved riding comfort performance. It is for the purpose.
本発明者は、前記課題を解決するために鋭意研究を重ねた結果、ポリウレタンフォームのセル構造を規定することにより、その課題を解決し得ることを見出した。本発明は、かかる知見に基づいて完成したものである。 As a result of intensive studies to solve the above problems, the present inventor has found that the problems can be solved by defining the cell structure of the polyurethane foam. The present invention has been completed based on such findings.
すなわち、本発明は、
[1]シートパッド用ポリウレタンフォームであって、該ポリウレタンフォームを形成するセルの平均径が550〜1,000μm、セル一つ当たりが有する穴個数が10以下、及びセルを形成するリブの平均厚みが90〜200μmであることを特徴とするシートパッド用ポリウレタンフォーム、
[2](A)ポリオール成分、(B)ポリイソシアネート成分、(C)水、及び(D)触媒を含有する発泡原液を発泡成形してなる、上記[1]に記載のシートパッド用ポリウレタンフォーム、
[3](A)ポリオール成分として、エチレンオキシド及びプロピレンオキシドの開環重合により得られ、エチレンオキシドとプロピレンオキシドに由来する繰り返し単位のモル比が10/90〜25/75であり、かつ数平均分子量が6,000〜12,000であるポリエーテルポリオールを含むものを用いる、上記[2]に記載のシートパッド用ポリウレタンフォーム、
[4](A)ポリオール成分中のポリエーテルポリオールの含有量が40質量%以上である、上記[3]に記載のシートパッド用ポリウレタンフォーム、
[5](B)ポリイソシアネート成分が、トリレンジイソシアネート及びジフェニルメタンジイソシアネートから選択される少なくとも1種を含む、上記[2]〜[4]のいずれかに記載のシートパッド用ポリウレタンフォーム、
[6]発泡原液における(C)水の含有量が、(A)ポリオール成分100質量部に対して2.0質量部以上である、上記[2]〜[5]のいずれかに記載のシートパッド用ポリウレタンフォーム、
[7]発泡原液中に(B)ポリイソシアネート成分を、該ポリイソシアネート成分中のイソシアネート基と、前記発泡原液中の活性水素基とのモル比が60:100〜120:100になるように含む、上記[2]〜[6]のいずれかに記載のシートパッド用ポリウレタンフォーム、
[8]さらに、発泡原液中に(E)整泡剤及び(F)架橋剤から選択される少なくとも1種を含む、上記[2]〜[7]のいずれかに記載のシートパッド用ポリウレタンフォーム、及び
[9]発泡成形が、発泡原液を金型内に形成されたキャビティ内に供給する工程、及びゲルタイムより20〜50秒間経過した後に、金型内の圧力を0.15〜0.25MPa低下させる工程を有する、上記[2]〜[8]のいずれかに記載のシートパッド用ポリウレタンフォーム、
を提供するものである。
That is, the present invention
[1] Polyurethane foam for seat pad, the average diameter of cells forming the polyurethane foam is 550 to 1,000 μm, the number of holes per cell is 10 or less, and the average thickness of ribs forming the cells Polyurethane foam for seat pad, characterized in that is 90 to 200 μm,
[2] Polyurethane foam for seat pad according to the above [1], which is obtained by foaming a foaming stock solution containing (A) a polyol component, (B) a polyisocyanate component, (C) water, and (D) a catalyst. ,
[3] (A) The polyol component is obtained by ring-opening polymerization of ethylene oxide and propylene oxide, the molar ratio of the repeating units derived from ethylene oxide and propylene oxide is 10/90 to 25/75, and the number average molecular weight is The polyurethane foam for a seat pad according to the above [2], which uses a polyether polyol that is 6,000 to 12,000,
[4] The polyurethane foam for a seat pad according to the above [3], wherein the content of the polyether polyol in the polyol component (A) is 40% by mass or more,
[5] The polyurethane foam for a seat pad according to any one of the above [2] to [4], wherein the (B) polyisocyanate component contains at least one selected from tolylene diisocyanate and diphenylmethane diisocyanate,
[6] The sheet according to any one of [2] to [5], wherein the content of water (C) in the foaming stock solution is 2.0 parts by mass or more with respect to 100 parts by mass of the (A) polyol component. Polyurethane foam for pads,
[7] The foaming stock solution contains (B) the polyisocyanate component so that the molar ratio of the isocyanate group in the polyisocyanate component and the active hydrogen group in the foaming stock solution is 60: 100 to 120: 100. , A polyurethane foam for a seat pad according to any one of the above [2] to [6],
[8] The polyurethane foam for a seat pad according to any one of the above [2] to [7], further comprising at least one selected from (E) a foam stabilizer and (F) a crosslinking agent in the foaming stock solution. And [9] In the foam molding, the step of supplying the foaming stock solution into the cavity formed in the mold, and after 20 to 50 seconds have elapsed from the gel time, the pressure in the mold is 0.15 to 0.25 MPa. The polyurethane foam for seat pad according to any one of the above [2] to [8], which comprises a step of reducing,
Is to provide.
本発明によれば、ポリウレタンフォームのセル構造を規定することにより、共振周波数と共振倍率を同時に低減することができ、乗り心地性能を向上させた車両用シートパッドに最適なシートパッド用ポリウレタンフォームを提供することができる。
このようなセル構造を有するポリウレタンフォームは、例えばポリオール成分、ポリイソシアネート成分、水及び触媒を含有する発泡原液を発泡成形することにより、作製することができる。特に、ポリオール成分として、エチレンオキシド(EO)及びプロピレンオキシド(PO)の開環重合により得られ、EOとPO由来の繰り返し単位のモル比、及び数平均分子量が、それぞれ特定の範囲にあるポリエーテルポリオールを含むものを用いることにより、所望のセル構造を有するポリウレタンフォームが効果的に得られる。
According to the present invention, by defining the cell structure of the polyurethane foam, the resonance frequency and the resonance magnification can be reduced at the same time, and the polyurethane foam for a seat pad optimal for a vehicle seat pad with improved riding comfort performance is provided. Can be provided.
A polyurethane foam having such a cell structure can be produced, for example, by foaming a foaming stock solution containing a polyol component, a polyisocyanate component, water and a catalyst. In particular, as a polyol component, a polyether polyol obtained by ring-opening polymerization of ethylene oxide (EO) and propylene oxide (PO), wherein the molar ratio of EO and PO-derived repeating units and the number average molecular weight are in specific ranges, respectively. A polyurethane foam having a desired cell structure can be effectively obtained by using a material containing.
本発明のシートパッド用ポリウレタンフォームは、当該ポリウレタンフォームを形成するセルの平均径が550〜1,000μm、セル一つ当たりが有する穴個数が10以下、及びセルを形成するリブの平均厚みが90〜200μmであることを特徴とする。 In the polyurethane foam for seat pad of the present invention, the average diameter of the cells forming the polyurethane foam is 550 to 1,000 μm, the number of holes per cell is 10 or less, and the average thickness of the ribs forming the cells is 90. It is -200 micrometers.
[ポリウレタンフォームのセル構造]
ポリウレタンフォームにおいて、フォームを形成するセルの平均径、セルの一つ当たりが有する穴個数、及びセルを形成するリブの平均厚みが、それぞれ上記範囲にあれば、該ポリウレタンフォームは、共振周波数と共振倍率を同時に低減することができ、乗り心地性能を向上させたシートパッド用ポリウレタンフォームとなる。
この場合、共振周波数は、通常3〜3.5Hz程度であり、共振倍率は、通常2.8〜3.5倍程度である。
[Cellular structure of polyurethane foam]
In polyurethane foam, if the average diameter of the cells forming the foam, the number of holes per cell, and the average thickness of the ribs forming the cells are within the above ranges, the polyurethane foam will resonate with the resonance frequency. It becomes a polyurethane foam for seat pads that can reduce the magnification at the same time and has improved riding comfort performance.
In this case, the resonance frequency is usually about 3 to 3.5 Hz, and the resonance magnification is usually about 2.8 to 3.5 times.
前記セルの平均径が550μm未満では低通気となり過ぎるため、共振倍率が下がるが、共振周波数が高くなり、両立できない。1,000μmを超えると高通気となり過ぎるため、共振周波数が低くなるが共振倍率が上がり、両立できない。この観点から、セルの平均径は、好ましくは580〜800μm、より好ましくは580〜750μmである。
前記セル一つ当たりが有する穴個数が10を超えると高通気となる。この観点から、該穴個数は、好ましくは8個以下、より好ましくは7個以下、さらに好ましくは5個以下である。また、該穴個数の下限値は、通常好ましくは2個、より好ましくは3個である。
前記セルを形成するリブの平均厚みが90μm未満では高通気となり過ぎ、共振周波数が低くなるが共振倍率が上がり、両立できない。一方、200μmを超えると低通気となり過ぎるため、共振倍率が下がるが、共振周波数が高くなり、両立できない。この観点から、リブの平均厚みは、好ましくは90〜150μm、より好ましくは90〜130μmである。
なお、本発明において、セルを形成する「リブ」とは、セルを形成する柱の部分、つまり、セルからセル穴を除いた部分を指す。
If the average diameter of the cell is less than 550 μm, the air permeability becomes too low, so that the resonance magnification is lowered, but the resonance frequency becomes high and cannot be compatible. If it exceeds 1,000 μm, the air flow becomes too high, so that the resonance frequency is lowered, but the resonance magnification is increased and both cannot be achieved. From this viewpoint, the average cell diameter is preferably 580 to 800 μm, more preferably 580 to 750 μm.
When the number of holes per cell exceeds 10, high ventilation is achieved. From this viewpoint, the number of holes is preferably 8 or less, more preferably 7 or less, and even more preferably 5 or less. In addition, the lower limit value of the number of holes is usually preferably 2, and more preferably 3.
If the average thickness of the ribs forming the cell is less than 90 μm, the air flow becomes excessively high and the resonance frequency is lowered, but the resonance magnification is increased, which is incompatible. On the other hand, if it exceeds 200 μm, the air permeability becomes too low and the resonance magnification decreases, but the resonance frequency becomes high and cannot be compatible. From this viewpoint, the average thickness of the rib is preferably 90 to 150 μm, more preferably 90 to 130 μm.
In the present invention, the “rib” forming the cell refers to a column portion forming the cell, that is, a portion obtained by removing the cell hole from the cell.
ポリウレタンフォームのセル構造を決定するリブの平均厚み、セルの個数、セルの平均径、セル一つ当たりが有する穴個数、膜の破れ度合いは、表1に示すようにポリウレタンフォームの作製において、原料の一つとして用いる後述のポリエーテルポリオールの数平均分子量と相関関係にある。
なお、上記各特性値の測定方法については、後で説明する。
The average thickness of the ribs that determine the cell structure of the polyurethane foam, the number of cells, the average diameter of the cells, the number of holes per cell, and the degree of film breakage are shown in Table 1. There is a correlation with the number average molecular weight of a polyether polyol described later used as one of the following.
The method for measuring each characteristic value will be described later.
したがって、ポリウレタンフォームの作製に用いるポリエーテルポリオールの数平均分子量を変動させることが、該ポリウレタンフォームのセル構造を制御する手段の一つとなり得る。 Therefore, varying the number average molecular weight of the polyether polyol used for producing the polyurethane foam can be one of means for controlling the cell structure of the polyurethane foam.
本発明のポリウレタンフォームは、前述したセル構造を有することにより、共振周波数と共振倍率を同時に低減することができ、乗り心地性能を向上させた車両用シートパッドに適するものとなる。
このようなポリウレタンフォームを形成させる方法としては、前記のセル構造を有するポリウレタンフォームを形成し得る方法であればよく、特に制限されず、例えば(A)ポリオール成分、(B)ポリイソシアネート成分、(C)水、及び(D)触媒を含有する発泡原液を発泡成形する方法を採用することができる。
次に、当該発泡原液における各成分について詳述する。
Since the polyurethane foam of the present invention has the above-described cell structure, the resonance frequency and the resonance magnification can be reduced at the same time, and the polyurethane foam is suitable for a vehicle seat pad with improved riding comfort performance.
A method for forming such a polyurethane foam is not particularly limited as long as it is a method capable of forming a polyurethane foam having the above-described cell structure. For example, (A) a polyol component, (B) a polyisocyanate component, ( A method of foaming a foaming stock solution containing C) water and (D) a catalyst can be employed.
Next, each component in the foaming stock solution will be described in detail.
[(A)ポリオール成分]
(A)ポリオール成分としては、エチレンオキシド(以下「EO」と記載する。)及びプロピレンオキシド(以下「PO」と記載する。)の開環重合により得られ、EOとPOに由来する繰り返し単位のモル比が10/90〜25/75(EO/PO)であり、かつ数平均分子量が6,000〜12,000であるポリエーテルポリオールを含むものが好ましい。このポリエーテルポリオールは1種を単独で、又は2種以上を併用してもよい。
[(A) Polyol component]
(A) The polyol component is obtained by ring-opening polymerization of ethylene oxide (hereinafter referred to as “EO”) and propylene oxide (hereinafter referred to as “PO”), and is a mole of repeating units derived from EO and PO. It is preferable to include a polyether polyol having a ratio of 10/90 to 25/75 (EO / PO) and a number average molecular weight of 6,000 to 12,000. This polyether polyol may be used alone or in combination of two or more.
(ポリエーテルポリオール)
このポリエーテルポリオールにおけるEO/POモル比は、所望のセル構造を有するポリウレタンフォームを形成し得る観点から、10/90〜25/75が好ましく、16/84〜25/75がより好ましく、18/82〜25/75がさらに好ましい。
一方、前記数平均分子量は、得られるポリウレタンフォームのセル構造に大きな影響を与え、例えば該数平均分子量が大きくなると、(1)セルの個数は少なくなって、セル径が大きくなる、(2)セル穴の個数が多くなって、リブの太さが大きくなる、(3)膜の破れ度合いが多くなり、通気性が高くなる、などの傾向が見られる。なお、本発明のポリウレタンフォームのセル構造における膜の破れ度合いは、通常、好ましくは65〜85%である。
ポリエーテルポリオールの数平均分子量が大きくなると、上述のようなセル構造をもたらす傾向が見られ、その結果、振動特性は、共振周波数及び共振倍率が共に低下する効果を奏する。
本発明において、(A)ポリオール成分として用いられるポリエーテルポリオールの数平均分子量としては、前記効果及び製造上の容易さなどの観点から、6,000〜12,000の範囲にあることが好ましく、6,000〜11,000の範囲にあることがより好ましい。
なお、本発明において数平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC法)によりポリスチレン換算値として算出した値である。
(Polyether polyol)
The EO / PO molar ratio in this polyether polyol is preferably 10/90 to 25/75, more preferably 16/84 to 25/75, from the viewpoint of forming a polyurethane foam having a desired cell structure. 82-25 / 75 is more preferable.
On the other hand, the number average molecular weight greatly affects the cell structure of the resulting polyurethane foam. For example, when the number average molecular weight increases, (1) the number of cells decreases and the cell diameter increases. (2) There is a tendency that the number of cell holes increases, the thickness of the ribs increases, (3) the degree of film tearing increases, and the air permeability increases. The degree of film breakage in the cell structure of the polyurethane foam of the present invention is usually preferably 65 to 85%.
When the number average molecular weight of the polyether polyol increases, a tendency to bring about the cell structure as described above is observed, and as a result, the vibration characteristic has an effect of reducing both the resonance frequency and the resonance magnification.
In the present invention, the number average molecular weight of the polyether polyol used as the (A) polyol component is preferably in the range of 6,000 to 12,000 from the viewpoints of the above effects and ease of production. More preferably, it is in the range of 6,000 to 11,000.
In the present invention, the number average molecular weight is a value calculated as a polystyrene equivalent value by gel permeation chromatography (GPC method).
本発明において用いられる上記ポリエーテルポリオールの一分子中に含まれるヒドロキシル基の数としては、通常2〜4個、特に3個であることが好ましい。ヒドロキシル基の数が多すぎると当該発泡原液の粘度が上昇する場合があり、少なすぎると所望物性が低下する場合がある。 The number of hydroxyl groups contained in one molecule of the polyether polyol used in the present invention is usually 2 to 4, particularly preferably 3. If the number of hydroxyl groups is too large, the viscosity of the foaming stock solution may increase, and if it is too small, the desired physical properties may decrease.
上記ポリエーテルポリオールとしては、不飽和度の小さなものを用いることが好ましい。より具体的には、不飽和度として通常0.03ミリ当量/g以下であることが好ましい。ポリエーテルポリオール中の不飽和度が0.03ミリ当量/g以下であると、本発明のポリウレタンフォームの耐久性や硬度が損なわれにくい。なお、本発明において「不飽和度」とは、JIS K 1557−1970に準拠し、試料中の不飽和度結合に酢酸第二水銀を作用させて遊離する酢酸を水酸化カリウムで滴定する方法にて測定した、総不飽和度(ミリ当量/g)を意味するものである。 As the polyether polyol, it is preferable to use one having a low degree of unsaturation. More specifically, the degree of unsaturation is usually preferably 0.03 meq / g or less. When the degree of unsaturation in the polyether polyol is 0.03 meq / g or less, the durability and hardness of the polyurethane foam of the present invention are hardly impaired. In the present invention, “unsaturation” refers to a method in which acetic acid released by acting mercuric acetate on the unsaturated bond in the sample is titrated with potassium hydroxide in accordance with JIS K 1557-1970. Means the total degree of unsaturation (milli equivalent / g).
本発明においては、(A)ポリオール成分中の当該ポリエーテルポリオールの含有量は、得られるポリウレタンフォームの共振周波数と共振倍率を同時に低減させ、車両用シートパッドとしての乗り心地性を向上させる観点から、40質量%以上が好ましく、40〜70質量%がより好ましく、40〜60質量%がさらに好ましい。 In the present invention, the content of the polyether polyol in the polyol component (A) is to reduce the resonance frequency and the resonance magnification of the resulting polyurethane foam at the same time, from the viewpoint of improving the riding comfort as a vehicle seat pad. 40 mass% or more is preferable, 40-70 mass% is more preferable, and 40-60 mass% is further more preferable.
(ポリマーポリオール)
本発明における上記(A)成分として、必要に応じて上記ポリエーテルポリオールとポリマーポリオールを併用しても良い。ポリマーポリオールとしては、ポリウレタン発泡成形体用として汎用のポリマーポリオールを用いることが可能である。より具体的には、例えば、ポリアルキレンオキシドからなる好ましくは平均分子量が3,000〜8,000、より好ましくは4,000〜7,000のポリエーテルポリオールにポリアクリロニトリル、アクリロニトリル−スチレン共重合体等のポリマー成分をグラフト共重合させたポリマーポリオール等が挙げられる。ポリアルキレンオキシドの原料となるアルキレンオキシドとしては、プロピレンオキシドを含むことが好ましく、プロピレンオキシド単独のもの、又はプロピレンオキシド及びエチレンオキシドを共に含むものであることが特に好ましい。また、上記ポリマーポリオール中に占める上記のようなポリマー成分の割合としては、通常25〜50質量%である。
(Polymer polyol)
As said (A) component in this invention, you may use together the said polyether polyol and polymer polyol as needed. As the polymer polyol, it is possible to use a general-purpose polymer polyol for polyurethane foam moldings. More specifically, for example, a polyacrylonitrile, an acrylonitrile-styrene copolymer made of a polyalkylene oxide, preferably a polyether polyol having an average molecular weight of 3,000 to 8,000, more preferably 4,000 to 7,000. And polymer polyols obtained by graft copolymerization of polymer components such as The alkylene oxide used as the raw material for the polyalkylene oxide preferably includes propylene oxide, and particularly preferably includes propylene oxide alone or includes both propylene oxide and ethylene oxide. Moreover, as a ratio of the above polymer components in the said polymer polyol, it is 25-50 mass% normally.
上記(A)成分としてポリエーテルポリオールとポリマーポリオールとの混合物を用いる場合、その両者の配合比としては、ポリエーテルポリオール/ポリマーポリオール(質量比)として、通常、好ましくは30/70〜100/0、より好ましくは40/60〜80/20、さらに好ましくは40/60〜60/40である。両者の配合比が上記範囲を逸脱すると、所望物性が得られにくかったり、反応不具合を生じたりする場合がある。 When a mixture of a polyether polyol and a polymer polyol is used as the component (A), the mixing ratio of the two is usually as a polyether polyol / polymer polyol (mass ratio), preferably 30/70 to 100/0. More preferably, it is 40 / 60-80 / 20, More preferably, it is 40 / 60-60 / 40. If the blending ratio of the two deviates from the above range, it may be difficult to obtain desired physical properties or a reaction failure may occur.
本発明において上記(A)成分としては、粘度((A)成分として複数種のポリオールを混合して使用する場合には、その混合したポリオール全体の粘度)が液温25℃において3,000mPa・s以下、特に1,800mPa・s以下となる粘度範囲が好ましい。このような粘度範囲のポリオール成分を用いることにより、ポリウレタン発泡原液の増粘速度を抑制することが可能となって攪拌効率が上昇し、イソシアネート基とヒドロキシル基とがより均一に反応することが可能となるため、従来に比べて発生ガスの発生効率が増加するのみならず、その発生ガスの発生箇所としても、ポリウレタン発泡原液内で均一に発生することとなり、軽量かつ均質なポリウレタン発泡成形体を得ることが可能となる。なお、本発明において「粘度」とは、JIS Z 8803−1991に準拠し、液温25℃において、毛細管粘度計を用いて測定した粘度を意味する。 In the present invention, as the component (A), the viscosity (when using a mixture of a plurality of types of polyols as the component (A), the viscosity of the mixed polyol as a whole) is 3,000 mPa · s at a liquid temperature of 25 ° C. The viscosity range is preferably s or less, particularly 1,800 mPa · s or less. By using a polyol component in such a viscosity range, it is possible to suppress the viscosity increase rate of the polyurethane foam stock solution, increase the stirring efficiency, and allow the isocyanate groups and hydroxyl groups to react more uniformly. Therefore, not only the generation efficiency of the generated gas is increased compared to the conventional case, but also the generated gas is generated uniformly in the polyurethane foam stock solution, and a lightweight and homogeneous polyurethane foam molded product is obtained. Can be obtained. In the present invention, “viscosity” means the viscosity measured using a capillary viscometer at a liquid temperature of 25 ° C. in accordance with JIS Z 8803-1991.
[(B)ポリイソシアネート成分]
ポリイソシアネート成分としては、公知の各種多官能性の脂肪族、脂環族および芳香族のイソシアネートを用いることができる。例えば、トリレンジイソシアネート(TDI)、ジフェニルメタンジイソシアネート(MDI)、ジシクロヘキシルメタンジイソシアネート、トリフェニルジイソシアネート、キシレンジイソシアネート、ポリメチレンポリフェニレンポリイソシアネート、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、オルトトルイジンジイソシアネート、ナフチレンジイソシアネート、キシリレンジイソシアネート、リジンジイソシアネート等を挙げることができ、これらは1種を単独で、又は2種以上を併用して用いても良い。
本発明においては、得られるフォームの密度の観点から、トリレンジイソシアネート(TDI)及びジフェニルメタンジイソシアネート(MDI)から選択される少なくとも1種を含むことが好ましい。
[(B) Polyisocyanate component]
As the polyisocyanate component, various known polyfunctional aliphatic, alicyclic and aromatic isocyanates can be used. For example, tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), dicyclohexylmethane diisocyanate, triphenyl diisocyanate, xylene diisocyanate, polymethylene polyphenylene polyisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, orthotoluidine diisocyanate, naphthylene diisocyanate, xylylene diisocyanate , Lysine diisocyanate and the like, and these may be used alone or in combination of two or more.
In the present invention, from the viewpoint of the density of the foam obtained, it is preferable to include at least one selected from tolylene diisocyanate (TDI) and diphenylmethane diisocyanate (MDI).
上記(B)成分のポリイソシアネート(2種以上のイソシアネートを併用する場合には、その総量)が、上記ポリウレタン発泡原液中に占める割合としては、特に制限されるものではないが、その目安としてのイソシアネート当量(上記ポリウレタン発泡原液中の活性水素量(モル)を100とした時の、イソシアネート基の当量(モル)比)値として通常60以上、好ましくは70以上、上限として通常120以下、好ましくは115以下である。イソシアネート当量が60未満であると、攪拌不良が起こる場合があり、120を超えるとフォームダウンする場合がある。 The proportion of the (B) component polyisocyanate (when two or more isocyanates are used in combination, the total amount thereof) in the polyurethane foam stock solution is not particularly limited. Isocyanate equivalent (equivalent (molar) ratio of isocyanate group when the amount of active hydrogen (mole) in the polyurethane foam stock solution is 100) is usually 60 or more, preferably 70 or more, and the upper limit is usually 120 or less, preferably 115 or less. When the isocyanate equivalent is less than 60, poor stirring may occur, and when it exceeds 120, foam-down may occur.
[(C)水]
本発明においては、発泡剤として水を用いる。水はポリイソシアネートと反応して炭酸ガスを発生させることから、本発明において発泡剤として用いることができる。
水の配合量は、(A)ポリオール成分100質量部に対して、2.0質量部以上であることが好ましい。水の配合量が2.0質量部未満であると、ぐらつきを抑制する十分な効果が得られない。一方、上限値については、本発明の効果を奏する範囲であれば、特に限定されず、例えば、ポリオール成分100質量部に対して、15質量部程度配合することができる。
[(C) Water]
In the present invention, water is used as the foaming agent. Since water reacts with the polyisocyanate to generate carbon dioxide, it can be used as a foaming agent in the present invention.
The blending amount of water is preferably 2.0 parts by mass or more with respect to 100 parts by mass of the (A) polyol component. When the blending amount of water is less than 2.0 parts by mass, a sufficient effect for suppressing wobble cannot be obtained. On the other hand, the upper limit is not particularly limited as long as the effect of the present invention is achieved. For example, about 15 parts by mass can be blended with 100 parts by mass of the polyol component.
[(D)触媒]
本発明における上記ポリウレタン発泡原液は、発泡成形の際の反応性の観点から触媒を含むことが好ましい。(D)成分の触媒としては、ポリウレタンフォームの製造において汎用のものを用いることができ、用途や要求に応じて1種又は2種以上を組み合わせて使用することができる。具体的には、テトラメチルヘキサメチレンジアミン、ペンタメチルジエチレントリアミン、ジメチルシクロヘキシルアミン、ビス−(ジメチルアミノエチル)エーテル、テトラメチルプロピレンジアミン、トリメチルアミノエチルピペラジン、テトラメチルエチレンジアミン、ジメチルベンジルアミン、メチルモルフォリン、エチルモルフォリン、トリエチレンジアミン、ジエタノールアミン等のアミン触媒や、スタナスオクテート、ジブチルチンジラウレート等の錫系触媒を挙げることができる。上記(D)成分の触媒としては市販品を用いることができ、例えばトリエチレンジアミン(TEDA−L33:東ソー(株)製)、ビス(ジメチルアミノエチル)エーテル(TOYOCAT−ET:東ソー(株)製)等を好適に用いることができる。
なお、ポリウレタン発泡原液中の(D)成分の配合量としては、上記(A)成分のポリオール100質量部に対して通常0.1〜5質量部であり、より好ましくは0.2〜1質量部である。
[(D) Catalyst]
The polyurethane foam stock solution in the present invention preferably contains a catalyst from the viewpoint of reactivity during foam molding. (D) As a catalyst of a component, a general purpose thing can be used in manufacture of a polyurethane foam, According to a use and a request | requirement, it can use 1 type or in combination of 2 or more types. Specifically, tetramethylhexamethylenediamine, pentamethyldiethylenetriamine, dimethylcyclohexylamine, bis- (dimethylaminoethyl) ether, tetramethylpropylenediamine, trimethylaminoethylpiperazine, tetramethylethylenediamine, dimethylbenzylamine, methylmorpholine, Examples thereof include amine catalysts such as ethylmorpholine, triethylenediamine and diethanolamine, and tin-based catalysts such as stannous octate and dibutyltin dilaurate. Commercially available products can be used as the catalyst for the component (D). For example, triethylenediamine (TEDA-L33: manufactured by Tosoh Corporation), bis (dimethylaminoethyl) ether (TOYOCAT-ET: manufactured by Tosoh Corporation) Etc. can be used suitably.
In addition, as a compounding quantity of (D) component in a polyurethane foam undiluted | stock solution, it is 0.1-5 mass parts normally with respect to 100 mass parts of polyols of the said (A) component, More preferably, it is 0.2-1 mass. Part.
[任意成分]
当該発泡原液には、任意成分として(E)整泡剤及び/又は(F)架橋剤を配合することができる。さらに必要に応じて各種添加剤を配合することができ、例えば、顔料等の着色剤、鎖延長剤、炭酸カルシウム等の充填材、難燃剤、酸化防止剤、紫外線吸収剤、光安定剤、カーボンブラック等の導電性物質、抗菌剤などを配合することができる。この場合、これらの添加剤の配合量は、通常使用される範囲で差し支えない。
[Optional ingredients]
The foaming stock solution may contain (E) a foam stabilizer and / or (F) a crosslinking agent as optional components. Furthermore, various additives can be blended as necessary, for example, colorants such as pigments, chain extenders, fillers such as calcium carbonate, flame retardants, antioxidants, ultraviolet absorbers, light stabilizers, carbon Conductive substances such as black, antibacterial agents and the like can be blended. In this case, the compounding amount of these additives may be within the range usually used.
((E)整泡剤)
この(E)成分の整泡剤としては、ポリウレタン発泡成形体用のものとして汎用のものを用いることができ、例えば、各種シロキサン−ポリエーテルブロック共重合体等のシリコーン系整泡剤を用いることができる。
ポリウレタン発泡原液中の整泡剤の配合量としては、上記(A)成分のポリオール100質量部に対して通常0.5〜5質量部、特に0.5〜3質量部とすることが好ましい。5質量部を超えても特に性能的に問題ないがコストが上がり、0.5質量部未満であるとポリオール成分とイソシアネート成分の攪拌性が低下し、所望のウレタンフォームが得られないおそれがあり好ましくない。
なお、この整泡剤として、高活性の整泡剤、例えば東レ・ダウコーニング社製「SZ1325」を使用することにより、低活性の整泡剤、例えばモメンティブ社製「L−3623」を使用する場合に比べて、得られるポリウレタンフォームの通気性が低減し、共振倍率が低くなるので、好ましい。
((E) foam stabilizer)
As the foam stabilizer for this component (E), general-purpose foam stabilizers can be used for polyurethane foam moldings, for example, silicone foam stabilizers such as various siloxane-polyether block copolymers. Can do.
As a compounding quantity of the foam stabilizer in a polyurethane foam undiluted | stock solution, it is 0.5-5 mass parts normally with respect to 100 mass parts of polyols of the said (A) component, It is preferable to set it as 0.5-3 mass parts especially. Even if it exceeds 5 parts by mass, there is no problem in performance, but the cost increases. If it is less than 0.5 parts by mass, the stirring property of the polyol component and the isocyanate component is lowered, and the desired urethane foam may not be obtained. It is not preferable.
As this foam stabilizer, a highly active foam stabilizer, for example, “SZ1325” manufactured by Toray Dow Corning, is used, and a low activity foam stabilizer, such as “L-3623,” manufactured by Momentive, is used. Compared with the case, the breathability of the resulting polyurethane foam is reduced, and the resonance magnification is reduced, which is preferable.
((F)架橋剤)
この(F)成分の架橋剤としては、ポリウレタン発泡成形体用のものとして汎用のものを用いることができる。なお、当該架橋剤は、本発明においては、(A)ポリオール成分に含まれる。
ポリウレタン発泡原液中の架橋剤の配合量としては、上記(A)のポリオール成分中の含有量が、通常0.5〜10質量%の範囲にあることが好ましい。0.5質量%以上であると、架橋剤の効果が十分に得られ、一方、10質量%以下であると独立気泡性が適度であり、成形性が確保できるとともに、フォームダウンすることがない。
((F) Crosslinking agent)
As the crosslinking agent for component (F), a general-purpose one can be used as a polyurethane foam molded article. In addition, the said crosslinking agent is contained in (A) polyol component in this invention.
As a compounding quantity of the crosslinking agent in a polyurethane foam undiluted | stock solution, it is preferable that content in the polyol component of the said (A) exists in the range of 0.5-10 mass% normally. When the content is 0.5% by mass or more, the effect of the crosslinking agent is sufficiently obtained. On the other hand, when the content is 10% by mass or less, the closed cell property is appropriate, the moldability can be ensured, and the foam does not go down. .
[発泡原液の調製]
本発明における発泡原液の調製方法としては、特に限定されるものではないが、前記(B)成分を除いた残りの各成分からなる混合物(以下、「ポリオール混合物」と略記することがある。)を調製し、その後(B)成分と混合する。
該ポリオール混合物の調製は、水と触媒とをなるべく接触させないという観点から、上記(A)ポリオール成分に対して、上記(D)触媒を配合し、次いで上記(E)整泡剤、(F)架橋剤などその他の成分を配合し、最後に発泡成分である上記(C)水を配合することが好適である。
本発明において、ポリオール混合物の液温25℃における粘度としては、2,400mPa・s以下が好ましい。該ポリウレタン発泡原液の攪拌効率を良好とし、発泡が均一且つ十分となって所望のポリウレタン発泡成形体が得られるためである。以上の観点から、ポリオール混合物の液温25℃における粘度は、1,800mPa・s以下が好ましい。
[Preparation of foaming stock solution]
The method for preparing the foaming stock solution in the present invention is not particularly limited, but a mixture composed of the remaining components excluding the component (B) (hereinafter sometimes abbreviated as “polyol mixture”). And then mixed with the component (B).
The polyol mixture is prepared by blending the catalyst (D) with the polyol component (A) and then (E) the foam stabilizer, (F) from the viewpoint of bringing water and the catalyst into contact as little as possible. It is preferable to blend other components such as a crosslinking agent, and finally blend the water (C) which is a foaming component.
In the present invention, the viscosity of the polyol mixture at a liquid temperature of 25 ° C. is preferably 2,400 mPa · s or less. This is because the polyurethane foam stock solution has a good stirring efficiency, and foaming is uniform and sufficient to obtain a desired polyurethane foam molded article. From the above viewpoint, the viscosity of the polyol mixture at a liquid temperature of 25 ° C. is preferably 1,800 mPa · s or less.
[ポリウレタンフォームの発泡成形]
ポリウレタンフォームを発泡成形する方法としては、金型内に形成されたキャビティ内にポリウレタン発泡原液を注入し、発泡成形する従来公知の方法を採用し得るが、時限圧力解放(TPR;Timed Pressure Release)を併用することが好ましい。
本発明におけるTPRは、金型内の圧力を低下させ、気泡の連通化を生じさせるものである。より具体的には、発泡原液を、金型内に形成されたキャビティ内に供給する工程の後に、ゲルタイムより20〜50秒経過した後に金型内の圧力を、0.15〜0.25MPa低下させる工程を有することが好ましい。
ここでゲルタイムとは、ポリオールとイソシアネートが混合され、増粘が起こってゲル強度が出始める時間をいう。
[Polyurethane foam foam molding]
As a method for foam-molding polyurethane foam, a conventionally known method of foam-molding by injecting a polyurethane foam stock solution into a cavity formed in a mold can be adopted, but timed pressure release (TPR) is possible. It is preferable to use together.
The TPR in the present invention lowers the pressure in the mold and causes communication of bubbles. More specifically, after the step of supplying the foaming stock solution into the cavity formed in the mold, the pressure in the mold is reduced by 0.15 to 0.25 MPa after 20 to 50 seconds have elapsed from the gel time. It is preferable to have the process to make.
Here, the gel time means a time when a polyol and an isocyanate are mixed, thickening occurs, and gel strength starts to appear.
ポリウレタン発泡原液の各成分の分離を防止する観点から、金型キャビティ内に上記ポリウレタン発泡原液を注入する直前に、上述の各成分を混合してポリウレタン発泡原液を調製することが好ましい。この際、上記原液の液温は通常10〜50℃、好ましくは20〜40℃、更に好ましくは25〜35℃である。ここで、ポリウレタン発泡原液を調製する前に不必要な粘度の上昇を抑制する観点から、少なくとも前記(A)成分のポリオールと、前記(B)成分のイソシアネートとが、最後に混合されることが好ましい。次いで、上記原液の調製直後にこれをキャビティ内の減圧が可能な金型のキャビティに大気圧下にて注入し、注入し終えた直後に減圧を開始する。その後、金型内にて発泡・硬化させ、脱型し、本発明品とする。型温は通常40〜80℃、好ましくは50〜70℃、更に好ましくは60〜65℃である。 From the viewpoint of preventing separation of each component of the polyurethane foam stock solution, it is preferable to prepare the polyurethane foam stock solution by mixing the above-mentioned components immediately before injecting the polyurethane foam stock solution into the mold cavity. Under the present circumstances, the liquid temperature of the said undiluted | stock solution is 10-50 degreeC normally, Preferably it is 20-40 degreeC, More preferably, it is 25-35 degreeC. Here, from the viewpoint of suppressing an unnecessary increase in viscosity before preparing the polyurethane foam stock solution, at least the polyol of the component (A) and the isocyanate of the component (B) may be mixed at the end. preferable. Next, immediately after preparation of the stock solution, it is injected into a cavity of a mold capable of depressurization in the cavity under atmospheric pressure, and depressurization is started immediately after the injection is completed. Then, it is made to foam and harden in a metal mold | die, and it demolds, and is set as the product of this invention. The mold temperature is usually 40 to 80 ° C, preferably 50 to 70 ° C, more preferably 60 to 65 ° C.
このようにして得られた本発明のポリウレタンフォームは、フォームを形成するセルの平均径が550〜1,000μm、セル一つ当たりが有する穴個数が10以下、及びセルを形成するリブの平均厚みが90〜200μmであるセル構造を有し、その特性として、車酔いを低減し、座り心地を良くする観点から、共振周波数が4Hz以下であることが好ましく、3.5Hz以下であることがより好ましい。4Hzを超えると、車酔いに影響する6Hz時の伝達率(倍率)が高くなり、車酔いし易くなる傾向にある。共振倍率は通常好ましくは3.5倍以下であり、3.3倍以下であることがより好ましい。3.5倍を超えると、シートに座ったからだの上下の揺れが大きくなり、座り心地が悪くなるおそれがある。本発明のシートパッド用ポリウレタンフォームは、共振周波数と共振倍率を共に低減することができており、具体的には、共振周波数を2.5〜4Hz(より詳細には2.8〜3.5Hz)に、共振倍率を2.5〜3.5倍(より詳細には2.7〜3.3倍)にまで低減されている。 The polyurethane foam of the present invention thus obtained has an average cell diameter of 550 to 1,000 μm, a number of holes per cell of 10 or less, and an average thickness of ribs forming the cell. Has a cell structure of 90 to 200 μm, and as its characteristics, the resonance frequency is preferably 4 Hz or less, more preferably 3.5 Hz or less, from the viewpoint of reducing car sickness and improving sitting comfort. preferable. If it exceeds 4 Hz, the transmission rate (magnification) at 6 Hz, which affects car sickness, becomes high, and it tends to cause car sickness. The resonance magnification is usually preferably 3.5 times or less, and more preferably 3.3 times or less. If it exceeds 3.5 times, the vertical shaking of the body sitting on the seat increases, and the seating comfort may be deteriorated. The polyurethane foam for seat pad according to the present invention can reduce both the resonance frequency and the resonance magnification. Specifically, the resonance frequency is 2.5 to 4 Hz (more specifically, 2.8 to 3.5 Hz). ), The resonance magnification is reduced to 2.5 to 3.5 times (more specifically, 2.7 to 3.3 times).
次に、本発明を実施例により、さらに詳細に説明するが、本発明は、これらの例によってなんら限定されるものではない。
(評価方法)
各実施例及び比較例にて製造されたウレタンフォームについて、以下の方法にて評価した。
<セル構造>
X線CTと走査型電子顕微鏡(SEM)により、ポリウレタンフォームのセル構造を観察し、セルの平均径、セル一つ当たりが有する穴個数、セルを形成するリブの平均厚みを求めた。
なお、SEMとしては、日立ハイテク株式会社製、機種名「S−3000N」を用い、倍率30〜200倍にてセル構造を観察した。
EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited at all by these examples.
(Evaluation method)
The urethane foam produced in each example and comparative example was evaluated by the following method.
<Cell structure>
The cell structure of the polyurethane foam was observed by X-ray CT and a scanning electron microscope (SEM), and the average cell diameter, the number of holes per cell, and the average thickness of ribs forming the cell were determined.
In addition, as SEM, Hitachi High-Tech Co., Ltd. make, model name "S-3000N" was used, and the cell structure was observed at 30-200 times magnification.
<共振周波数(Hz)及び共振倍率>
JASO B 407に準拠して測定した。測定は、ウレタンフォームの硬さが25%硬度で226N(23kgf)になるように調整したサンプルで行った。サンプルに402N(41kg)の加圧板を載せ、周波数を1〜10Hzまで加振させた。最大の伝達率を示した時の周波数を共振周波数(Hz)、共振周波数の伝達率を共振倍率とした。なお、25%硬度とは、ウレタンフォームを25%圧縮するのに要する荷重をいう。
<Resonance frequency (Hz) and resonance magnification>
Measured according to JASO B 407. The measurement was performed on a sample adjusted so that the hardness of the urethane foam was 226N (23 kgf) at 25% hardness. A 402N (41 kg) pressure plate was placed on the sample, and the frequency was vibrated to 1 to 10 Hz. The frequency at which the maximum transmission rate was shown was the resonance frequency (Hz), and the transmission rate of the resonance frequency was the resonance magnification. In addition, 25% hardness means the load required to compress 25% of urethane foam.
<ポリエーテルポリオールの特性値>
(1)数平均分子量
ゲルパーミエーションクロマトグラフィー(GPC)法により測定した標準ポリスチレン換算の値である。
(2)EO単位/PO単位モル比
1H−NMRスペクトル測定により得られるプロトンシグナルの積分値に基づいて算出した。
(3)官能基数
13C−NMRスペクトル測定により得られるピークから開始剤を決定し、官能基数を決定した。
(4)不飽和度
JIS K 1557−1970に準拠し、試料中の不飽和度結合に酢酸第二水銀を作用させて遊離する酢酸を水酸化カリウムで測定する方法にて測定した、総不飽和度(ミリ当量/g)を意味する。
<Characteristic value of polyether polyol>
(1) Number average molecular weight It is the value of standard polystyrene conversion measured by the gel permeation chromatography (GPC) method.
(2) EO unit / PO unit molar ratio
It calculated based on the integral value of the proton signal obtained by < 1 > H-NMR spectrum measurement.
(3) Number of functional groups
The initiator was determined from the peak obtained by 13 C-NMR spectrum measurement, and the number of functional groups was determined.
(4) Unsaturation Total unsaturation measured by a method of measuring acetic acid liberated by acting mercuric acetate on the unsaturation bond in the sample in accordance with JIS K 1557-1970, and measuring with potassium hydroxide. Degree (milli equivalent / g).
実施例1、2及び比較例1〜6
表2に示した配合処方に従って、発泡原液を調製した。調製に際しては、(B)ポリイソシアネート成分以外の各成分からなるポリオール混合物を調製し、その後(B)ポリイソシアネート成分を配合することで行った。ポリオール組成物は、まず、(A)ポリオール成分と、(D)触媒を混合し、次いで整泡剤、架橋剤を配合して、最後に(C)水を混合して調製した。その時、ポリウレタン発泡原液の液温としては、実施例1及び比較例1〜3、5は30℃とし、実施例2及び比較例4、6は40℃とした。次いで、上記原液の調製直後にこれを、設定温度60℃のキャビティ内の減圧が可能な金型のキャビティに大気圧下にて注入し、注入し終えた直後に減圧を開始した。その後、金型内にて発泡・硬化させ、ゲルタイムより30秒経過した時に、金型内の圧力を、0.2MPa低下させた。その後、脱型し、ポリウレタンフォームを得た。得られたポリウレタンフォームを上記方法にて評価した。評価結果を表2に示す。
Examples 1 and 2 and Comparative Examples 1-6
A foaming stock solution was prepared according to the formulation shown in Table 2. In the preparation, a polyol mixture composed of each component other than (B) the polyisocyanate component was prepared, and then (B) the polyisocyanate component was blended. The polyol composition was prepared by first mixing (A) a polyol component and (D) catalyst, then blending a foam stabilizer and a crosslinking agent, and finally mixing (C) water. At that time, as the liquid temperature of the polyurethane foam stock solution, Example 1 and Comparative Examples 1 to 3 and 5 were set to 30 ° C, and Example 2 and Comparative Examples 4 and 6 were set to 40 ° C. Next, immediately after the preparation of the stock solution, this was injected under atmospheric pressure into a mold cavity capable of being reduced in pressure at a set temperature of 60 ° C., and pressure reduction was started immediately after the injection was completed. Thereafter, foaming and curing were performed in the mold, and when 30 seconds had elapsed from the gel time, the pressure in the mold was reduced by 0.2 MPa. Thereafter, it was demolded to obtain a polyurethane foam. The obtained polyurethane foam was evaluated by the above method. The evaluation results are shown in Table 2.
[注]
1)ポリエーテルポリオールA:EO/POモル比16/84、数平均分子量7,000、官能基数3、不飽和度0.04ミリ当量/g
2)ポリエーテルポリオールB:EO/POモル比20/80、数平均分子量7,000、官能基数3、不飽和度0.007ミリ当量/g
3)ポリエーテルポリオールC:EO/POモル比20/80、数平均分子量10,000、官能基数3、不飽和度0.007ミリ当量/g
4)ポリマーポリオール:EO/POモル比15/85、数平均分子量5,000、官能基数3
5)架橋剤:ポリエーテルポリオール(EO/POモル比100/0、数平均分子量400、官能基数4)
6)触媒A:トリエチレンジアミン[東ソー(株)製]
7)触媒B:ビス(2−ジメチルアミノエチル)エーテル10〜30質量%のジプロピレングリコール溶液(東ソー社製)
8)触媒C:ジエタノールアミン
9)シリコーン整泡剤A:[東レ・ダウコーニング社製、商品名「SZ1325」]
10)シリコーン整泡剤B:[モメンティブ社製、商品名「L−3623」]
11)TDI:「T−80」(三井化学ポリウレタン株式会社製)、MDI:「MR−200HR」(日本ポリウレタン株式会社製)
12)[NCO基]/[発泡原液中の活性水素基]モル比
[note]
1) Polyether polyol A: EO / PO molar ratio 16/84, number average molecular weight 7,000, functional group number 3, unsaturation degree 0.04 meq / g
2) Polyether polyol B: EO / PO molar ratio 20/80, number average molecular weight 7,000, number of functional groups 3, unsaturation degree 0.007 meq / g
3) Polyether polyol C: EO / PO molar ratio 20/80, number average molecular weight 10,000, number of functional groups 3, degree of unsaturation 0.007 meq / g
4) Polymer polyol: EO / PO molar ratio 15/85, number average molecular weight 5,000, number of functional groups 3
5) Crosslinking agent: polyether polyol (EO / PO molar ratio 100/0, number average molecular weight 400, number of functional groups 4)
6) Catalyst A: Triethylenediamine [manufactured by Tosoh Corporation]
7) Catalyst B: Dipropylene glycol solution of 10 to 30% by mass of bis (2-dimethylaminoethyl) ether (manufactured by Tosoh Corporation)
8) Catalyst C: Diethanolamine 9) Silicone foam stabilizer A: [trade name “SZ1325” manufactured by Toray Dow Corning Co., Ltd.]
10) Silicone foam stabilizer B: [product name “L-3623” manufactured by Momentive Co., Ltd.]
11) TDI: “T-80” (Mitsui Chemicals Polyurethane Co., Ltd.), MDI: “MR-200HR” (Nihon Polyurethane Co., Ltd.)
12) [NCO group] / [active hydrogen group in foaming stock solution] molar ratio
本発明のシートパッド用ポリウレタンフォームは、共振周波数と共振倍率を同時に低減することができ、乗り心地性能を向上させた車両用シートパッドとして最適である。 The polyurethane foam for seat pad according to the present invention can reduce the resonance frequency and the resonance magnification at the same time, and is optimal as a vehicle seat pad with improved riding comfort performance.
Claims (9)