JP2012206877A - Intermediate film for laminated glass, and laminated glass - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an intermediate film for a laminated glass having high insulation.SOLUTION: The intermediate film 2 for a laminated glass partially has a transparent or opaque colored region R1. In the colored region R1, the film contains a thermoplastic resin, a plasticizer, a heat insulating particle 5, at least one component of a phthalocyanine compound, a naphthalocyanine compound and an anthracyanine compound, and a yellow dye. In the colored region R1, the content of the heat insulating particle 5 with respect to 100 pts.wt. of the thermoplastic resin is in the range of 0.01 to 2 pts.wt., and the content of the total of the above component and the above yellow dye is ≤0.5 pt.wt.

Description

  The present invention relates to an interlayer film for laminated glass used for laminated glass such as an automobile or a building, and more specifically, an interlayer film for laminated glass capable of enhancing the heat shielding property of laminated glass, and the interlayer film for laminated glass. It is related with the laminated glass using.

  Laminated glass is excellent in safety because it has less scattering of glass fragments even if it is damaged by external impact. For this reason, the said laminated glass is widely used for a motor vehicle, a rail vehicle, an aircraft, a ship, a building, etc. The laminated glass is manufactured by sandwiching an interlayer film for laminated glass between a pair of glass plates. High heat-insulating properties are required for laminated glass used in such vehicle and building openings.

  Infrared rays having a wavelength longer than 780 nm longer than visible light have a smaller amount of energy than ultraviolet rays. However, infrared rays have a large thermal effect, and once infrared rays are absorbed by a substance, they are released as heat. For this reason, infrared rays are generally called heat rays. Therefore, in order to improve the heat shielding property of the laminated glass, it is necessary to sufficiently block infrared rays.

  In recent years, in order to effectively block the infrared rays (heat rays), heat shielding particles such as tin-doped indium oxide particles (ITO particles) or antimony-doped tin oxide particles (ATO particles) have been used for interlayer films for laminated glass. ing.

  In addition, as an example of the interlayer film for laminated glass that does not contain the heat shielding particles, the following Patent Document 1 includes 96.5 to 99.6% by weight of a synthetic resin and 0.2 to 3.0% by weight of an ultraviolet absorber. % And an intermediate film for laminated glass containing 0.02 to 0.5% by weight of a yellow dye. Here, it is described that pests can be prevented from flying on the laminated glass.

JP 2000-300149 A

  In recent years, it has been required to further improve the heat shielding properties of conventional interlayer films containing ITO particles or ATO particles. However, ITO particles or ATO particles do not absorb near infrared rays sufficiently. Therefore, it is difficult to greatly enhance the heat shielding property of the laminated glass only by adding ITO particles or ATO particles to the intermediate film.

  In addition, in laminated glass for vehicles such as automobiles, especially windshields, a band-like colored region is formed on the intermediate film for the purpose of preventing the driver during driving from feeling dazzled by sunlight or outdoor lighting. May be provided. This colored region is called a shade band. In general, the colored region is often provided by coloring the upper edge of the intermediate film into a strip shape. Even in a laminated glass using an intermediate film having such a colored region, high heat shielding properties are desired.

  The objective of this invention is providing the laminated glass using the intermediate film for laminated glasses which can obtain a laminated glass with high heat-shielding property, and this intermediate film for laminated glasses.

  According to a wide aspect of the present invention, the colored region has a transparent or opaque colored region and a second region different from the colored region, and in the colored region, a thermoplastic resin, a plasticizer, and a heat shielding particle, It contains at least one component of a phthalocyanine compound, a naphthalocyanine compound, and an anthracocyanine compound, and a yellow dye, and in the colored region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is 0.01. There is provided an interlayer film for laminated glass having a content of ˜2 parts by weight and a total content of the above components and the yellow dye of 0.5 parts by weight or less. The heat shielding particles are preferably metal oxide particles.

  On the specific situation with the intermediate film for laminated glasses which concerns on this invention, content of the said component with respect to 100 weight part of said thermoplastic resins is in the range of 0.001-0.1 weight part in the said coloring area | region.

  In another specific aspect of the interlayer film for laminated glass according to the present invention, in the colored region, the content of the yellow dye with respect to 100 parts by weight of the thermoplastic resin is within a range of 0.005 to 0.24 parts by weight. is there.

According to another broad aspect of the present invention, there is a transparent or opaque colored region and a second region different from the colored region, and in the colored region, a thermoplastic resin, a plasticizer, and a heat shielding particle. And at least one component of a phthalocyanine compound, a naphthalocyanine compound, and an anthracocyanine compound, and a yellow dye, and in the colored region, the thermal barrier particles are contained at a ratio of 0.05 to 12 g / m ^2. And the intermediate film for laminated glasses which contains the said component and the said yellow dye in the ratio of 1.5 g / m < ² > or less in total is provided. The heat shielding particles are preferably metal oxide particles.

On the specific situation with the intermediate film for laminated glasses which concerns on this invention, the said component is contained in the said coloring area | region in the ratio of 0.005-1.0 g / m < ² >.

In another specific aspect of the interlayer film for laminated glass according to the present invention, the yellow dye is contained in the colored region at a ratio of 0.025 to 1.45 g / m ² .

  In still another specific aspect of the interlayer film for laminated glass according to the present invention, the visible light transmittance of the second region is higher than the visible light transmittance of the colored region.

  In another specific aspect of the interlayer film for laminated glass according to the present invention, a thermoplastic resin and a plasticizer are contained in the second region.

  In still another specific aspect of the interlayer film for laminated glass according to the present invention, the colored region is present in a belt shape at least at the edge on one end side.

  In another specific aspect of the interlayer film for laminated glass according to the present invention, the interlayer film for laminated glass is an interlayer film for laminated laminated glass on the front of an automobile, and the colored region has an edge on the upper end side or an edge on the lower end side. It exists in at least one of the parts in a strip shape.

  The laminated glass according to the present invention includes first and second laminated glass constituent members, and a single-layer or multilayer intermediate film sandwiched between the first and second laminated glass constituent members, The single-layer or multilayer interlayer film includes an interlayer film for laminated glass constructed according to the present invention.

  The interlayer film for laminated glass according to the present invention has a transparent or opaque colored region and a second region different from the colored region, and in the colored region, a thermoplastic resin, a plasticizer, and a heat shielding particle. And at least one component of a phthalocyanine compound, a naphthalocyanine compound and an anthracocyanine compound, and a yellow dye, and further, in the colored region, the heat shielding particles for the thermoplastic resin or in the interlayer film for laminated glass Since the content and the total content of the components and the yellow dye are within the specific range, the heat shielding property of the colored region can be enhanced. For this reason, it originates in the said coloring area | region with high heat-shielding property, and can improve the heat-shielding property of a laminated glass.

FIG. 1 is a partially cutaway side sectional view schematically showing an example of a laminated glass using an interlayer film for laminated glass according to an embodiment of the present invention. FIG. 2 is a front view for explaining the interlayer film for laminated glass used in the laminated glass shown in FIG.

  Details of the present invention will be described below.

  The interlayer film for laminated glass according to the present invention has a transparent or opaque colored region (first region) and a second region different from the colored region. The interlayer film for laminated glass according to the present invention has a transparent or opaque colored region in part.

  The interlayer film for laminated glass according to the present invention includes, in the colored region, a thermoplastic resin, a plasticizer, a heat shielding particle, at least one component of a phthalocyanine compound, a naphthalocyanine compound, and an anthocyanin compound, and a yellow color Contains a dye. Hereinafter, at least one component of the phthalocyanine compound, naphthalocyanine compound and anthracocyanine compound may be referred to as component X.

In the interlayer film for laminated glass according to the present invention, in the colored region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is in the range of 0.01 to 2 parts by weight, and the component X and The total content of the yellow dye is 0.5 parts by weight or less. Or the intermediate film for laminated glasses which concerns on this invention contains the said thermal-insulation particle | grain in the ratio of 0.05-12 g / m < ² > in the said coloring area | region, and adds the said component X and the said yellow dye in total. It is contained at a ratio of 5 g / m ² or less.

  The main feature of the present invention is that in the colored region, the heat shielding particles, the component X, and the yellow dye are used in combination, and the content of these thermoplastic resins or the interlayer film for laminated glass The content ratio is to satisfy the above relationship in the colored region. Thereby, the heat-shielding property in the said coloring area | region part of a laminated glass becomes high, As a result, the heat-shielding property of a laminated glass can be improved effectively. That is, by using the interlayer film for laminated glass according to the present invention, the heat shielding property of the laminated glass can be enhanced.

  By the way, in recent years, for example, in the United States, the California Air Resources Board (CARB) has proposed reducing the amount of carbon dioxide emitted from automobiles in order to reduce greenhouse gases. It was. In order to reduce the amount of carbon dioxide emitted from automobiles, the CARB regulates the heat energy that passes through the laminated glass and flows into the automobile, reducing the fuel consumed by the air conditioner and reducing the fuel consumption of the automobile. I was considering improving it. Specifically, the CARB had planned to introduce cool car regulations (Cool Cars Standards).

  Specifically, in the above-mentioned cool car regulation, in 2012, Tts (Total Solar Transmission) of laminated glass used for automobiles was expected to be 50% or less. In 2016, it was expected that the Tts of the laminated glass was 40% or less. The Tts is an index of heat ray shielding.

  In addition, the heat ray reflective laminated glass using the glass which vapor-deposited the metal thin film or heat ray reflective PET generally called a thermoreflex type reflects the communication wave of not only infrared rays but a communication wavelength range. When the heat ray reflective laminated glass is used for the windshield, it is necessary to cut out the heat ray reflective portion in order to cope with many sensors. As a result, the average Tts of the entire windshield using the heat ray reflective laminated glass having a Tts of 50% is about 53%. Therefore, in a type of laminated glass that transmits communication waves and absorbs infrared rays, Tts was expected to be allowed up to 53%.

  As of September 2010, the introduction of the cool car regulations has been postponed, but there is still a tendency for laminated glass having a low Tts.

  By using the interlayer film for laminated glass according to the present invention, it becomes easy to obtain a laminated glass satisfying the required performance of the above-mentioned cool car regulations (Cool Cars Standards). Specifically, it becomes easy to make the Tts of the laminated glass 53% or less.

  Conventionally, when an interlayer film for laminated glass containing heat shielding particles such as ITO particles is used, it has been extremely difficult to obtain a laminated glass having a Tts of 53% or less. On the other hand, by using the interlayer film for laminated glass according to the present invention, a laminated glass in which the heat shielding property of the laminated glass is derived from the colored region and the Tts of the colored region portion is 53% or less. As a result, it is easy to obtain a laminated glass having a Tts of 53% or less.

  In the present specification, the performance of the Tts is the performance required by the cool car regulation. The Tts is measured, for example, by a measurement method defined by cool car regulations that are scheduled to be introduced.

  The second region different from the transparent or opaque colored region preferably contains a thermoplastic resin and a plasticizer. In this case, the compatibility at the boundary between the colored region and the second region is increased.

  Hereinafter, in the interlayer film for laminated glass according to the present invention, details of each component that can be used in the colored region or the second region will be described.

(Thermoplastic resin)
In the interlayer film for laminated glass according to the present invention, the thermoplastic resin that can be used in the colored region or the second region is not particularly limited. A conventionally well-known thermoplastic resin can be used as said thermoplastic resin. As for the said thermoplastic resin, only 1 type may be used and 2 or more types may be used together.

  Examples of the thermoplastic resin include polyvinyl acetal resin, ethylene-vinyl acetate copolymer resin, ethylene-acrylic copolymer resin, polyurethane resin, and polyvinyl alcohol resin. Thermoplastic resins other than these may be used.

  The thermoplastic resin is preferably a polyvinyl acetal resin. By the combined use of the polyvinyl acetal resin and the plasticizer, the adhesive force of the interlayer film to the laminated glass constituent member can be further increased.

  The polyvinyl acetal resin can be produced, for example, by acetalizing polyvinyl alcohol with an aldehyde. The polyvinyl alcohol can be obtained, for example, by saponifying polyvinyl acetate. The degree of saponification of the polyvinyl alcohol is generally in the range of 80 to 99.8 mol%.

  The preferable lower limit of the polymerization degree of the polyvinyl alcohol is 200, the more preferable lower limit is 500, the preferable upper limit is 3,000, and the more preferable upper limit is 2,500. When the said polymerization degree is too low, there exists a tendency for the penetration resistance of a laminated glass to fall. When the said polymerization degree is too high, shaping | molding of the intermediate film for laminated glasses may become difficult.

  The aldehyde is not particularly limited. In general, an aldehyde having 1 to 10 carbon atoms is preferably used as the aldehyde. Examples of the aldehyde having 1 to 10 carbon atoms include propionaldehyde, n-butyraldehyde, isobutyraldehyde, n-valeraldehyde, 2-ethylbutyraldehyde, n-hexylaldehyde, n-octylaldehyde, and n-nonylaldehyde. , N-decylaldehyde, formaldehyde, acetaldehyde, benzaldehyde and the like. Among these, propionaldehyde, n-butyraldehyde, isobutyraldehyde, n-hexylaldehyde or n-valeraldehyde is preferable, n-butyraldehyde, n-hexylaldehyde or n-valeraldehyde is preferable, and n-butyraldehyde is more preferable. . As for the said aldehyde, only 1 type may be used and 2 or more types may be used together.

  It is preferable that the hydroxyl group content (hydroxyl group amount) of the polyvinyl acetal resin is in the range of 15 to 40 mol%. The more preferable lower limit of the hydroxyl group content is 18 mol%, and the more preferable upper limit is 35 mol%. If the hydroxyl group content is too low, the adhesion of the interlayer film may be lowered. On the other hand, if the hydroxyl group content is too high, the flexibility of the intermediate film is lowered, and problems in handling the intermediate film are likely to occur.

  The content of hydroxyl groups in the polyvinyl acetal resin is a value obtained by dividing the amount of ethylene groups to which the hydroxyl groups are bonded by the total amount of ethylene groups in the main chain, as a percentage (mol%). . The amount of ethylene group to which the hydroxyl group is bonded can be determined, for example, by measuring the amount of ethylene group to which the hydroxyl group of polyvinyl alcohol as a raw material is bonded in accordance with JIS K6726 “Testing method for polyvinyl alcohol”. it can.

  The preferable lower limit of the degree of acetylation (acetyl group amount) of the polyvinyl acetal resin is 0.1 mol%, the more preferable lower limit is 0.3 mol%, the still more preferable lower limit is 0.5 mol%, and the preferable upper limit is 30 mol%. A more preferred upper limit is 25 mol%, a still more preferred upper limit is 20 mol%, and a particularly preferred upper limit is 10 mol%. If the degree of acetylation is too low, the compatibility between the polyvinyl acetal resin and the plasticizer may be reduced. If the degree of acetylation is too high, the moisture resistance of the interlayer film may be lowered.

  The degree of acetylation is obtained by subtracting the amount of ethylene groups to which acetal groups are bonded and the amount of ethylene groups to which hydroxyl groups are bonded from the total amount of ethylene groups of the main chain, It is a value indicating the mole fraction obtained by dividing by the percentage (mol%). The amount of ethylene group to which the acetal group is bonded can be measured, for example, according to JIS K6728 “Testing method for polyvinyl butyral”.

  The preferable lower limit of the degree of acetalization of the polyvinyl acetal resin is 60 mol%, the more preferable lower limit is 63 mol%, the preferable upper limit is 85 mol%, the more preferable upper limit is 75 mol%, and the further preferable upper limit is 70 mol%. If the degree of acetalization is too low, the compatibility between the polyvinyl acetal resin and the plasticizer may be low. When the said acetalization degree is too high, reaction time required in order to manufacture polyvinyl acetal resin may become long.

  The degree of acetalization is a value obtained by dividing the amount of ethylene group to which an acetal group is bonded by the total amount of ethylene groups in the main chain, as a percentage (mol%).

  The degree of acetalization was determined by measuring the amount of acetyl groups and the amount of vinyl alcohol (hydroxyl content) by a method based on JIS K6728 “Testing methods for polyvinyl butyral”, and calculating the mole fraction from the obtained measurement results. Then, it can be calculated by subtracting the amount of acetyl groups and the amount of vinyl alcohol from 100 mol%.

  When the polyvinyl acetal resin is a polyvinyl butyral resin, the degree of acetalization (degree of butyralization) and the amount of acetyl group can be calculated from the results measured by a method according to JIS K6728 “Testing methods for polyvinyl butyral”. .

(Plasticizer)
In the interlayer film for laminated glass according to the present invention, the plasticizer that can be used in the colored region or the second region is not particularly limited. A conventionally known plasticizer can be used as the plasticizer. As for the said plasticizer, only 1 type may be used and 2 or more types may be used together.

  Examples of the plasticizer include organic ester plasticizers such as monobasic organic acid esters and polybasic organic acid esters, and phosphate plasticizers such as organic phosphate plasticizers and organic phosphorous acid plasticizers. It is done. Of these, organic ester plasticizers are preferred. The plasticizer is preferably a liquid plasticizer.

  The monobasic organic acid ester is not particularly limited. For example, a glycol ester obtained by reaction of glycol with a monobasic organic acid, and triethylene glycol or tripropylene glycol with a monobasic organic acid. Examples include esters. Examples of the glycol include triethylene glycol, tetraethylene glycol, and tripropylene glycol. Examples of the monobasic organic acid include butyric acid, isobutyric acid, caproic acid, 2-ethylbutyric acid, heptylic acid, n-octylic acid, 2-ethylhexylic acid, n-nonylic acid, and decylic acid.

  The polybasic organic acid ester is not particularly limited, and examples thereof include an ester compound of a polybasic organic acid and an alcohol having a linear or branched structure having 4 to 8 carbon atoms. Examples of the polybasic organic acid include adipic acid, sebacic acid, and azelaic acid.

  The organic ester plasticizer is not particularly limited, and triethylene glycol di-2-ethylbutyrate, triethylene glycol di-2-ethylhexanoate, triethylene glycol dicaprylate, triethylene glycol di-n- Octanoate, triethylene glycol di-n-heptanoate, tetraethylene glycol di-n-heptanoate, dibutyl sebacate, dioctyl azelate, dibutyl carbitol adipate, ethylene glycol di-2-ethyl butyrate, 1,3-propylene glycol di 2-ethyl butyrate, 1,4-butylene glycol di-2-ethyl butyrate, diethylene glycol di-2-ethyl butyrate, diethylene glycol di-2-ethyl hexanoate, dipropylene glycol Di-2-ethylbutyrate, triethylene glycol di-2-ethylpentanoate, tetraethylene glycol di-2-ethylbutyrate, diethylene glycol dicapryate, dihexyl adipate, dioctyl adipate, hexylcyclohexyl adipate, adipine Examples include a mixture of heptyl acid and nonyl adipate, diisononyl adipate, diisodecyl adipate, heptylnonyl adipate, dibutyl sebacate, alkyd oil-modified sebacic acid, and a mixture of phosphate ester and adipate. Organic ester plasticizers other than these may be used. Other adipic acid esters other than the above-mentioned adipic acid esters may be used.

  The organophosphate plasticizer is not particularly limited, and examples thereof include tributoxyethyl phosphate, isodecylphenyl phosphate, triisopropyl phosphate, and the like.

  The plasticizer is preferably a diester plasticizer represented by the following formula (1).

  In said formula (1), R1 and R2 respectively represent a C5-C10 organic group, R3 represents an ethylene group, an isopropylene group, or n-propylene group, p represents the integer of 3-10. . R1 and R2 in the above formula (1) are each preferably an organic group having 6 to 10 carbon atoms.

  The plasticizer is preferably at least one of triethylene glycol di-2-ethylhexanoate (3GO) and triethylene glycol di-2-ethylbutyrate (3GH), and triethylene glycol di-2 -More preferred is ethylhexanoate.

  The interlayer film for laminated glass according to the present invention comprises triethylene glycol di-2-ethylhexanoate (3GO) and triethylene glycol di-2-ethylbutyrate (3GH) as the plasticizer in the colored region. It is preferable that at least one of them is included, and it is more preferable that triethylene glycol di-2-ethylhexanoate is included.

  The content of the plasticizer in the colored region or the second region is not particularly limited. In the colored region, the preferred lower limit of the plasticizer content relative to 100 parts by weight of the thermoplastic resin is 25 parts by weight, the more preferred lower limit is 30 parts by weight, the still more preferred lower limit is 35 parts by weight, and the preferred upper limit is 75 parts by weight. A more preferred upper limit is 60 parts by weight, and a still more preferred upper limit is 50 parts by weight. The lower limit and upper limit of the preferable content of the plasticizer in the second region are the same as the lower limit and the upper limit of the preferable content of the plasticizer in the first region. When content of the said plasticizer satisfy | fills the said preferable minimum, the penetration resistance of a laminated glass can be improved further. When content of the said plasticizer satisfy | fills the said preferable upper limit, transparency of an intermediate film can be improved further.

(Heat shielding particles)
The interlayer film for laminated glass according to the present invention includes heat shielding particles in the colored region. The heat shielding particles are preferably particles formed of a metal oxide. Moreover, it is preferable that the intermediate film for laminated glasses which concerns on this invention also contains a heat-shielding particle also in the said 2nd area | region. Only 1 type may be used for a heat-shielding particle and 2 or more types may be used together.

  Infrared rays having a wavelength longer than that of visible light having a wavelength of 780 nm or more have a smaller energy amount than ultraviolet rays. However, infrared rays have a large thermal effect, and once infrared rays are absorbed by a substance, they are released as heat. For this reason, infrared rays are generally called heat rays. By using the heat shielding particles, infrared rays (heat rays) can be effectively blocked. In addition, a heat shielding particle means the particle | grains which can absorb infrared rays.

Specific examples of the heat shielding particles include aluminum-doped tin oxide particles, indium-doped tin oxide particles, antimony-doped tin oxide particles (ATO particles), gallium-doped zinc oxide particles (GZO particles), and indium-doped zinc oxide particles (IZO particles). ), Aluminum-doped zinc oxide particles (AZO particles), niobium-doped titanium oxide particles, sodium-doped tungsten oxide particles, tungsten oxide particles such as cesium-doped tungsten oxide particles, thallium-doped tungsten oxide particles, rubidium-doped tungsten oxide particles, tin-doped indium oxide particles And metal oxide particles such as particles (ITO particles), tin-doped zinc oxide particles and silicon-doped zinc oxide particles, and lanthanum hexaboride (LaB ₆ ) particles. Heat shielding particles other than these may be used. Especially, since the heat ray shielding function is high, the heat shielding particles are preferably metal oxide particles, more preferably ATO particles, GZO particles, ITO particles or tungsten oxide particles, and ITO particles. Further preferred. The tungsten oxide particles are preferably cesium-doped tungsten oxide particles.

  Since the shielding property of the heat ray can be sufficiently enhanced, the crystal lattice constant of the ITO particles is preferably in the range of 10.11 to 10.16. In general, the crystal lattice constant of the ITO particles is included in the range of 10.11 to 10.16 cm, and the crystal lattice constant of the ITO particles used in Examples described later is also 10.11 to 10. It is included in the range of 16cm.

  From the viewpoint of further improving the transparency and heat shielding properties of the laminated glass, the preferred lower limit of the average particle diameter of the heat shielding particles is 10 nm, the more preferred lower limit is 20 nm, the preferred upper limit is 100 nm, the more preferred upper limit is 80 nm, and the still more preferred upper limit. Is 50 nm. When the average particle diameter satisfies the above preferable lower limit, the heat ray shielding property can be sufficiently enhanced. When the average particle diameter satisfies the preferable upper limit, the transparency of the laminated glass can be increased.

  The “average particle diameter” indicates a volume average particle diameter. The average particle diameter can be measured using a particle size distribution measuring apparatus (“UPA-EX150” manufactured by Nikkiso Co., Ltd.) or the like.

In the colored region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is preferably in the range of 0.01 to 2 parts by weight. Or it is preferable that the intermediate film for laminated glasses which concerns on this invention contains the said heat-shielding particle in the ratio of 0.05-12 g / m < ² > in the said colored area | region. In the present invention, in the colored region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is in the range of 0.01 to 2 parts by weight, or the interlayer film for laminated glass is in the colored region. In this case, the heat shielding particles may be contained at a rate of 0.05 to 12 g / m ² . In the colored region, one of the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin, and the content of the heat shielding particles in the interlayer film for laminated glass is within the above range. The heat shielding property of the laminated glass can be sufficiently increased. For example, the Tts of the laminated glass in the colored region portion can be 53% or less. However, in the present invention, in the colored region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is in the range of 0.01 to 2 parts by weight, and the interlayer film for laminated glass is colored. In the area | region, you may contain the said heat shielding particle in the ratio of 0.05-12 g / m < ² >. In addition, when there is too much content of the said heat-shielding particle, the haze value of the laminated glass obtained will become high.

In the second region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is preferably in the range of 0.01 to 2 parts by weight. Or it is preferable that the intermediate film for laminated glasses which concerns on this invention contains the said heat-shielding particle in the ratio of 0.05-12 g / m < ² > in the said 2nd area | region. In the present invention, in the second region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is in the range of 0.01 to 2 parts by weight, or the interlayer film for laminated glass is In the second region, the heat shielding particles are preferably contained at a rate of 0.05 to 12 g / m ² . In the second region, one of the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin and the content ratio of the heat shielding particles in the interlayer film for laminated glass is within the above range. Thus, the heat shielding property can be sufficiently increased. For example, the Tts of the laminated glass in the second region portion can be 53% or less. However, in the present invention, in the second region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is in the range of 0.01 to 2 parts by weight, and the interlayer film for laminated glass is In the said 2nd area | region, you may contain the said heat shielding particle in the ratio of 0.05-12 g / m < ² >. In addition, when there is too much content of the said heat-shielding particle, the haze value of the laminated glass obtained will become high.

In the colored region, the more preferable lower limit of the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is 0.1 parts by weight, the still more preferable lower limit is 0.14 parts by weight, and the still more preferable lower limit is 0.5 parts by weight. Parts, even more preferred lower limit is 0.55 parts by weight, particularly preferred lower limit is 0.6 parts by weight, more preferred upper limit is 1.5 parts by weight, even more preferred upper limit is 1.2 parts by weight, and still more preferred upper limit is 1 part by weight, an even more preferred upper limit is 0.9 part by weight, and a particularly preferred upper limit is 0.8 part by weight. In the colored areas, combined more preferable lower limit is 0.5 g / ^{m 2} of the content of the heat shielding particles in the glass interlayer film for more preferred lower limit is 0.8 g / ^{m 2,} still more preferred lower limit 1.2g / M ² , a still more preferable lower limit is 1.5 g / m ² , a particularly preferable lower limit is 2 g / m ² , a more preferable upper limit is 9 g / m ² , a still more preferable upper limit is 8 g / m ² , and a further preferable upper limit is 7 g / m ² , an even more preferred upper limit is 5 g / m ² , and a particularly preferred upper limit is 4 g / m ² . The lower limit and upper limit of the preferable content of the heat shielding particles in the second region are the same as the lower limit and the upper limit of the preferable content of the heat shielding particles in the first region. When content of the said heat-shielding particle satisfy | fills the said preferable minimum, the heat-shielding property of a laminated glass can be improved further, and the said Tts can be made still lower. When the content of the heat shielding particles satisfies the preferable upper limit, the visible light transmittance can be further increased.

(Component X)
The component X is at least one component among phthalocyanine compounds, naphthalocyanine compounds, and anthracocyanine compounds. The interlayer film for laminated glass according to the present invention contains the component X in the colored region. The interlayer film for laminated glass according to the present invention preferably contains the component X also in the second region.

  The component X is not particularly limited. As the component X, conventionally known phthalocyanine compounds, naphthalocyanine compounds and anthracocyanine compounds can be used. As for the said component X, only 1 type may be used and 2 or more types may be used together.

  The combined use of the heat shielding particles, the component X, and the yellow dye can sufficiently block infrared rays (heat rays).

  Examples of the component X include phthalocyanine, a derivative of phthalocyanine, naphthalocyanine, a derivative of naphthalocyanine, anthracyanine, an anthracocyanine derivative, and the like. The phthalocyanine compound and the phthalocyanine derivative preferably each have a phthalocyanine skeleton. The naphthalocyanine compound and the naphthalocyanine derivative preferably each have a naphthalocyanine skeleton. It is preferable that each of the anthocyanin compound and the derivative of the anthracyanine has an anthracyanine skeleton.

  From the viewpoint of further increasing the heat shielding property of the laminated glass and further lowering the Tts, the component X is at least one selected from the group consisting of phthalocyanine, phthalocyanine derivatives, naphthalocyanine, and naphthalocyanine derivatives. Preferably, it is at least one of phthalocyanine and phthalocyanine derivatives. Since the said component X can fully improve the heat-shielding property, it is preferable that the said component X contains a metal, and it is more preferable that it contains copper. The component X preferably contains a metal or copper as a central metal. Moreover, since the shielding property of a heat ray can be improved further, the said component X is preferably a naphthalocyanine compound containing a metal, and more preferably a naphthalocyanine compound containing copper.

In the colored region, the total content of the component X and the yellow dye with respect to 100 parts by weight of the thermoplastic resin is preferably 0.5 parts by weight or less, and more preferably 0.25 parts by weight or less. . Or it is preferable that the intermediate film for laminated glasses which concerns on this invention contains the said component X and the said yellow dye in the said coloring area | region in the ratio of 1.5 g / m < ² > or less in total. In the present invention, in the colored region, the total content of the component X and the yellow dye with respect to 100 parts by weight of the thermoplastic resin is 0.5 parts by weight or less, or the interlayer film for laminated glass is colored. In the region, the component X and the yellow dye may be contained in a ratio of 1.5 g / m ² or less in total. In the colored region, the total content of the component X and the yellow dye relative to 100 parts by weight of the thermoplastic resin, and the total content ratio of the component X and the yellow dye in the interlayer film for laminated glass are not more than the above values. By being, it can fully improve the heat-shielding property of a laminated glass, and it can fully make the said Tts low. For example, the Tts in the colored region can be 53% or less. However, in the present invention, in the colored region, the total content of the component X and the yellow dye with respect to 100 parts by weight of the thermoplastic resin is 0.5 parts by weight or less, and the interlayer film for laminated glass is the above In the colored region, the component X and the yellow dye may be contained in a proportion of 1.5 g / m ² or less in total.

In the colored region, a preferable lower limit of the total content of the component X and the yellow dye with respect to 100 parts by weight of the thermoplastic resin is 0.005 parts by weight, a more preferable lower limit is 0.03 parts by weight, and a still more preferable lower limit is 0. 0.04 parts by weight, particularly preferred lower limit is 0.07 parts by weight, more preferred upper limit is 0.24 parts by weight, still more preferred upper limit is 0.2 parts by weight, particularly preferred upper limit is 0.18 parts by weight, and most preferred upper limit. Is 0.15 parts by weight. The sum of component A preferred lower limit of the content of the X and yellow dye 0.005 g / ^{m 2} in the interlayer film for a laminated glass, and more preferable lower limit is 0.03 g / ^{m 2,} still more preferred lower limit 0.2 g / ^{m 2} The particularly preferred lower limit is 0.25 g / m ² , the preferred upper limit is 1.5 g / m ² , the more preferred upper limit is 1.2 g / m ² , the still more preferred upper limit is 1 g / m ² , and the particularly preferred upper limit is 0.00. 7 g / m ² . When the total content of the component X and the yellow dye satisfies the preferable lower limit, the heat shielding property of the laminated glass can be further improved, and the Tts can be further reduced. When the total content of the component X and the yellow dye satisfies the preferable upper limit, the visible light transmittance can be further increased.

In the colored region, the content of the component X with respect to 100 parts by weight of the thermoplastic resin is preferably in the range of 0.001 to 0.1 parts by weight. Or it is preferable that the intermediate film for laminated glasses which concerns on this invention contains the said component X in the said coloring area | region in the ratio of 0.005-1.0 g / m < ² >. In the colored region, when the content of the component X with respect to 100 parts by weight of the thermoplastic resin or the content ratio of the component X in the interlayer film for laminated glass is within the above range, the heat shielding property of the laminated glass is further increased. The Tts can be further lowered.

In the colored region, the more preferable lower limit of the content of the component X with respect to 100 parts by weight of the thermoplastic resin is 0.002 parts by weight, the still more preferable lower limit is 0.005 parts by weight, and the particularly preferable lower limit is 0.01 parts by weight. Yes, a more preferred upper limit is 0.025 parts by weight, a still more preferred upper limit is 0.022 parts by weight, and a particularly preferred upper limit is 0.02 parts by weight. In the colored region, the more preferable lower limit of the content of the component X in the interlayer film for laminated glass is 0.01 g / m ² , the still more preferable lower limit is 0.028 g / m ² , and the particularly preferable lower limit is 0.055 g / m. ^2, a more preferred upper limit is 0.15 g / ^{m 2,} still more preferred upper limit 0.13 g / ^{m 2,} particularly preferred upper limit is 0.12 g / ^{m 2.} When content of the said component X satisfy | fills the said preferable minimum, the heat-shielding property of a laminated glass can be improved further, and the said Tts can be made still lower.

(Yellow dye)
In the interlayer film for laminated glass according to the present invention, the yellow dye used in the colored region is not particularly limited. Only 1 type of yellow dye may be used and 2 or more types may be used together. The interlayer film for laminated glass according to the present invention may or may not contain a yellow dye in the second region. From the viewpoint of increasing the visible light transmittance in the second region and increasing the transparency, the interlayer film for laminated glass according to the present invention is better as the yellow dye content in the second region is smaller. It is preferable not to contain a dye. On the other hand, from the viewpoint of improving the heat shielding property in the second region portion, the interlayer film for laminated glass according to the present invention preferably contains a yellow dye in the second region.

  The yellow dye preferably absorbs transmitted light of 380 to 500 nm, more preferably absorbs transmitted light of 390 to 480 nm, and effectively absorbs transmitted light of 395 to 460 nm. More preferably, it is particularly preferable to effectively absorb transmitted light of 400 to 450 nm. As a result, by using a yellow dye in addition to the heat shielding particles and the component X, the heat shielding property of the laminated glass can be further enhanced, and the Tts can be further lowered. Since the shielding property of heat rays can be sufficiently increased, the preferable lower limit of the maximum absorption wavelength of the yellow dye is 380 nm, the more preferable lower limit is 390 nm, the still more preferable lower limit is 395 nm, the particularly preferable lower limit is 400 nm, and the preferable upper limit is 500 nm, more preferable. The upper limit is 480 nm, the more preferable upper limit is 460 nm, and the particularly preferable upper limit is 450 nm. For example, the maximum absorption wavelength of the yellow dye is a solution in which 0.01 part by weight of the yellow dye is dissolved in 100 parts by weight of triethylene glycol di-2-ethylhexanoate (3GO) (cell length: 1 mm, It can be measured with a spectrophotometer (Hitachi High-Tech "U-4100") using a quartz cell.

  Specific examples of the yellow dye include anthraquinone dye, quinoline dye, isoquinoline dye, isoindolinone dye, monoazo dye, disazo dye, quinophthalone dye, perylene dye, triphenylmethane dye, and methine dye. Of these, anthraquinone dyes are preferred from the viewpoint of further enhancing the heat shielding properties in the colored region of the interlayer film for laminated glass.

  As commercially available yellow dyes, “ORACEET Yellow GHS” manufactured by Ciba Japan (anthraquinone dye, maximum absorption wavelength 450 nm), “KP Last Yellow G” (methine dye, maximum absorption wavelength 400 nm) manufactured by Kiwa Chemical Industry Co., Ltd. ), “KP Plast Yellow 2G” (quinophthalone dye, maximum absorption wavelength 420 nm), “KP Plast Yellow 3G” (monoazo dye, maximum absorption wavelength 395 nm), “KP Plast Yellow F” (isoquinoline dye, maximum absorption wavelength 415 nm), And “KP Past Yellow 7G” (perylene dye, maximum absorption wavelength 460 nm).

In the colored region, the yellow dye content with respect to 100 parts by weight of the thermoplastic resin is preferably in the range of 0.005 to 0.24 parts by weight. Or it is preferable that the intermediate film for laminated glasses which concerns on this invention contains the said yellow dye in the said coloring area | region in the ratio of 0.025-1.45g / m < ² >. In the colored region, the content of the yellow dye relative to 100 parts by weight of the thermoplastic resin, or the content ratio of the yellow dye in the interlayer film for laminated glass is within the above range, thereby further improving the heat shielding property. The Tts can be further reduced.

In the colored region, the more preferable lower limit of the yellow dye content with respect to 100 parts by weight of the thermoplastic resin is 0.01 parts by weight, the still more preferable lower limit is 0.04 parts by weight, and the particularly preferable lower limit is 0.06 parts by weight. More preferred upper limit is 0.2 parts by weight, still more preferred upper limit is 0.15 parts by weight, and particularly preferred upper limit is 0.1 parts by weight. In the colored areas, combined more preferred lower limit of the content of the yellow dye in the glass interlayer film for 0.05 g / ^{m 2,} still more preferred lower limit 0.2 g / ^{m 2,} especially preferred lower limit is 0.3 g / m ² , a more preferred upper limit is 1.2 g / m ² , a still more preferred upper limit is 1 g / m ² , and a particularly preferred upper limit is 0.8 g / m ² . When content of the said yellow dye satisfy | fills the said preferable minimum, the heat-shielding property of a laminated glass can be improved further, and the said Tts can be made still lower.

(Other ingredients)
The interlayer film for laminated glass according to the present invention includes, as necessary, an ultraviolet absorber, an antioxidant, a light stabilizer, a flame retardant, an antistatic agent, a pigment, a dye, in the colored region or the second region. You may contain additives, such as an adhesive force regulator, a moisture-proof agent, a fluorescent whitening agent, and an infrared absorber. The interlayer film for laminated glass according to the present invention preferably contains an antioxidant. The interlayer film for laminated glass according to the present invention preferably contains an ultraviolet absorber in the colored region, and preferably contains an ultraviolet absorber in the second region.

(Laminated glass)
The laminated glass according to the present invention includes first and second laminated glass constituent members and a single-layer or multilayer interlayer film sandwiched between the first and second laminated glass constituent members. The single-layer or multilayer interlayer film includes the interlayer film for laminated glass according to the present invention.

  In FIG. 1, an example of the laminated glass using the intermediate film for laminated glasses which concerns on one Embodiment of this invention is typically shown with a partial notch side sectional drawing. FIG. 1 shows a cross-sectional view of the colored region portion of the interlayer film for laminated glass. Moreover, the intermediate film for laminated glasses used for the laminated glass shown in FIG. 1 is typically shown with a front view in FIG. In FIG. 1 and FIG. 2, the size and size are appropriately changed from the actual size and size for convenience of illustration.

  A laminated glass 1 shown in FIG. 1 includes an intermediate film 2 and first and second laminated glass constituting members 3 and 4. The intermediate film 2 is used to obtain a laminated glass. The interlayer film 2 is an interlayer film for laminated glass. The intermediate film 2 is sandwiched between the first and second laminated glass constituting members 3 and 4. Therefore, the laminated glass 1 is constituted by laminating the first laminated glass constituting member 3, the intermediate film 2, and the second laminated glass constituting member 4 in this order.

  As shown in FIG. 2, the intermediate film 2 includes a transparent or opaque colored region R1 (first region) and a second region R2 different from the colored region R1. In the intermediate film 2, the colored region R <b> 1 is provided at the edge on the upper end 2 a side of the intermediate film 2. In the intermediate film 2, the colored region R <b> 1 is not provided at the edge on the lower end 2 b side of the intermediate film 2. The colored region R1 may be provided in a region other than the edge portion on the upper end 2a side of the intermediate film 2, for example, may be provided in an edge portion on the lower end 2b side of the intermediate film 2. Further, the colored region R1 may be provided on both the edge on the upper end 2a side and the edge on the lower end 2b side of the intermediate film 2.

  The visible light transmittance of the second region R2 is preferably higher than the visible light transmittance of the colored region R1. In this case, the visual field can be improved in the second region R2. The colored region R1 is preferably darker than the second region R2.

  The colored region R1 is preferably present in a strip shape at least at the edge on one end side. Laminated glass for vehicles such as automobiles, especially windshields, may be provided with a band-like colored region for the purpose of preventing the driving driver from feeling dazzled by sunlight or outdoor lighting. is there.

  In the colored region R1, the intermediate film 2 contains a thermoplastic resin, a plasticizer, the heat shielding particles 5, the component X, and a yellow dye. The intermediate film 2 contains a plurality of heat shielding particles 5 in the colored region R1. The intermediate film 2 may have a multilayer structure of two or more layers. The intermediate film may be partially provided with a colored region R1 in the thickness direction.

  Examples of the first and second laminated glass constituting members 3 and 4 include glass plates and PET (polyethylene terephthalate) films. The laminated glass 1 includes not only laminated glass in which an intermediate film is sandwiched between two glass plates, but also laminated glass in which an intermediate film is sandwiched between a glass plate and a PET film or the like. The laminated glass 1 is a laminated body provided with a glass plate, and preferably at least one glass plate is used.

  Examples of the glass plate include inorganic glass and organic glass. Examples of the inorganic glass include float plate glass, heat ray absorbing plate glass, heat ray reflecting plate glass, polished plate glass, mold plate glass, mesh plate glass, wire plate glass, and green glass. Especially, it is preferable to use heat ray absorbing plate glass as said inorganic glass, and it is more preferable to use heat ray absorbing plate glass based on JISR3208. The organic glass is a synthetic resin glass substituted for inorganic glass. Examples of the organic glass include polycarbonate plates and poly (meth) acrylic resin plates. Examples of the poly (meth) acrylic resin plate include a polymethyl (meth) acrylate plate.

  The thickness of the first and second laminated glass constituent members 3 and 4 is preferably 1 mm or more, preferably 5 mm or less, more preferably 3 mm or less. Moreover, when the laminated glass structural members 3 and 4 are glass plates, the thickness of the glass plates is preferably 1 mm or more, preferably 5 mm or less, more preferably 3 mm or less. When the laminated glass constituent members 3 and 4 are PET films, the thickness of the PET film is preferably in the range of 0.03 to 0.5 mm.

  The manufacturing method of the laminated glass 1 is not specifically limited. For example, the intermediate film 2 is sandwiched between the first and second laminated glass constituent members 3 and 4 and passed through a pressing roll, or put in a rubber bag and sucked under reduced pressure. The air remaining between the laminated glass constituent members 3 and 4 and the intermediate film 2 is deaerated. Then, it pre-adheres at about 70-110 degreeC, and a laminated body is obtained. Next, the laminated body is put in an autoclave or pressed, and pressed at about 120 to 150 ° C. and a pressure of 1 to 1.5 MPa. Thus, the laminated glass 1 can be obtained.

  The laminated glass 1 can be used for automobiles, railway vehicles, aircraft, ships, buildings, and the like. The laminated glass 1 can be used for a windshield, side glass, rear glass, roof glass, or the like of an automobile. The interlayer film 2 is preferably an interlayer film for laminated glass for buildings or vehicles, more preferably an interlayer film for laminated glass for vehicles, and particularly an interlayer film for laminated glass for front of automobiles. preferable. The laminated glass 1 is preferably laminated glass for buildings or vehicles, more preferably laminated glass for vehicles, and particularly preferably front laminated glass for automobiles. The laminated glass 1 can be used for other purposes. Since the heat shielding property of the colored region portion of the laminated glass is high and the Tts is low, the laminated glass 1 is suitably used for an automobile.

  From the viewpoint of obtaining a laminated glass that is more excellent in heat shielding properties, the Tts of the colored region portion of the laminated glass 1 is preferably 53% or less, preferably 50% or less, and 40% or less. It is preferable.

  The present invention will be described in more detail with reference to the following examples. The present invention is not limited to these examples.

Example 1
(1) Preparation of dispersion 40 parts by weight of triethylene glycol di-2-ethylhexanoate (3GO), 0.28 parts by weight of ITO particles (manufactured by Mitsubishi Materials), naphthalocyanine compound (“FF- IRSORB 203 ") 0.004 parts by weight and 0.234 parts by weight of a yellow dye (anthraquinone dye, maximum absorption wavelength 450 nm," ORACE Yellow GHS "manufactured by Ciba Japan Co., Ltd.) and phosphorus as a dispersant. After adding the acid ester compound, it was mixed in a horizontal microbead mill to obtain a mixed solution. Thereafter, 0.1 part by weight of acetylacetone was added to the mixed solution with stirring to prepare a dispersion. The volume average particle diameter of the ITO particles in the dispersion was 35 nm. In addition, the naphthalocyanine compound ("FF-IRSORB 203" manufactured by Fuji Film Co., Ltd.) contains copper.

(2) Preparation of interlayer film for laminated glass Polyvinyl butyral resin (butyralization degree: 68.5 mol%, hydroxyl group content: 30.5 mol%) is added to 100 parts by weight of the obtained dispersion and mixed. After sufficiently melt-kneading with a roll, it was extruded using an extruder to obtain an interlayer film having a thickness of 0.76 mm.

(3) Production of laminated glass The obtained interlayer film for laminated glass is sandwiched between two heat ray absorbing plate glasses (length 30 cm × width 30 cm × thickness 2.0 mm) in accordance with JIS R3208 from both ends thereof, and the laminate is Obtained. This laminated body is put in a rubber bag, deaerated at a vacuum degree of 2.6 kPa for 20 minutes, transferred to an oven while being deaerated, and further kept at 90 ° C. for 30 minutes and vacuum-pressed. Crimped. The temporarily bonded laminate was pressure bonded for 20 minutes in an autoclave under conditions of 135 ° C. and a pressure of 1.2 MPa to obtain a laminated glass 1.

  Moreover, the obtained interlayer film for laminated glass was sandwiched by transparent glass (length 30 cm × width 30 cm × thickness 2.5 mm) from both ends to obtain a laminate. This laminated body is put in a rubber bag, deaerated at a vacuum degree of 2.6 kPa for 20 minutes, transferred to an oven while being deaerated, and further kept at 90 ° C. for 30 minutes and vacuum-pressed. Crimped. The laminated body temporarily bonded under pressure at 135 ° C. and a pressure of 1.2 MPa in an autoclave was pressed for 20 minutes to obtain a laminated glass 2.

(Examples 2-9 and Comparative Examples 1-5)
A dispersion, an interlayer film for laminated glass, and laminated glasses 1 and 2 were produced in the same manner as in Example 1 except that the composition of the interlayer film for laminated glass was changed as shown in Table 1 below.

(Evaluation)
(1) Measurement of Tts and Tds (Solar Direct Transmission) According to the measurement method defined by the cool car regulations, the Tts and the Tds of the obtained laminated glass 1 were measured. Specifically, the Tts and the Tds were measured using a spectrophotometer (“U-4100” manufactured by Hitachi High-Tech) in accordance with JIS R3106 (1998).

(2) Measurement of visible light transmittance Using a spectrophotometer ("U-4100" manufactured by Hitachi High-Tech), the above laminated glass 1 obtained at a wavelength of 380 to 780 nm according to JIS R3211 (1998). Visible light transmittance was measured.

(3) Measurement of haze value Using a haze meter (“TC-HIIIDPK” manufactured by Tokyo Denshoku Co., Ltd.), the haze value of the obtained laminated glass 1 was measured according to JIS K6714.

  The results are shown in Table 1 below.

  In addition, although the measurement result of the laminated glass 1 is shown in Table 1, the laminated glass with low Tts was able to be obtained similarly about the laminated glass 2. Therefore, by producing a laminated glass partially having the laminated glass 1 or the laminated glass 2 as a colored region, the heat shielding property of the entire laminated glass is also increased due to the colored region having a high heat shielding property. In the laminated glass which has the laminated glass 1 or the laminated glass 2 as a colored region partially, heat-shielding property becomes high compared with the laminated glass which does not have this colored region.

DESCRIPTION OF SYMBOLS 1 ... Laminated glass 2 ... Intermediate film for laminated glass 2a ... Upper end 2b ... Lower end 3 ... 1st laminated glass structural member 4 ... 2nd laminated glass structural member 5 ... Thermal insulation particle R1 ... Colored area | region R2 ... 2nd area | region

Claims (13)

A transparent or opaque colored region and a second region different from the colored region;
In the colored region, containing a thermoplastic resin, a plasticizer, a heat shielding particle, at least one component of a phthalocyanine compound, a naphthalocyanine compound, and an anthracocyanine compound, and a yellow dye,
In the colored region, the content of the heat shielding particles with respect to 100 parts by weight of the thermoplastic resin is in the range of 0.01 to 2 parts by weight, and the total content of the component and the yellow dye is 0.5. An interlayer film for laminated glass that is not more than parts by weight.   The interlayer film for laminated glass according to claim 1, wherein the heat shielding particles are metal oxide particles.   The interlayer film for laminated glass according to claim 1 or 2, wherein in the colored region, the content of the component with respect to 100 parts by weight of the thermoplastic resin is within a range of 0.001 to 0.1 parts by weight.   The laminated glass according to any one of claims 1 to 3, wherein in the colored region, a content of the yellow dye with respect to 100 parts by weight of the thermoplastic resin is within a range of 0.005 to 0.24 parts by weight. Interlayer film. A transparent or opaque colored region and a second region different from the colored region;
In the colored region, containing a thermoplastic resin, a plasticizer, a heat shielding particle, at least one component of a phthalocyanine compound, a naphthalocyanine compound, and an anthracocyanine compound, and a yellow dye,
In the colored region, the heat shielding particles in a proportion of 0.05~12g / ^{m 2,} and contains the component and the yellow dye at a rate of 1.5 g / ^{m 2} or less in total, the combined glass Interlayer film.   The interlayer film for laminated glass according to claim 5, wherein the heat shielding particles are metal oxide particles. In the colored region, containing the components at a rate of 0.005~1.0g / ^{m 2,} interlayer film for laminated glass according to claim 5 or 6. Wherein the colored region, the yellow dye in a proportion of 0.025~1.45g / ^{m 2,} interlayer film for laminated glass according to any one of claims 5-7.   The interlayer film for laminated glass according to any one of claims 1 to 8, wherein a visible light transmittance of the second region is higher than a visible light transmittance of the colored region.   The interlayer film for laminated glass according to any one of claims 1 to 9, wherein the second region contains a thermoplastic resin and a plasticizer.   The interlayer film for laminated glass according to any one of claims 1 to 10, wherein the colored region is present in a belt shape at least at an edge portion on one end side. It is an interlayer film for automotive front laminated glass,
The interlayer film for laminated glass according to any one of claims 1 to 11, wherein the colored region is present in a strip shape on at least one of an edge portion on the upper end side or an edge portion on the lower end side. First and second laminated glass components;
A single-layer or multilayer interlayer film sandwiched between the first and second laminated glass components,
The laminated glass in which the said single layer or multilayer intermediate film contains the intermediate film for laminated glasses of any one of Claims 1-12.