JP2012197645A - Daylighting heat-insulating material - Google Patents

Daylighting heat-insulating material Download PDF

Info

Publication number
JP2012197645A
JP2012197645A JP2011063787A JP2011063787A JP2012197645A JP 2012197645 A JP2012197645 A JP 2012197645A JP 2011063787 A JP2011063787 A JP 2011063787A JP 2011063787 A JP2011063787 A JP 2011063787A JP 2012197645 A JP2012197645 A JP 2012197645A
Authority
JP
Japan
Prior art keywords
resin
heat insulating
insulating material
daylighting
spacer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2011063787A
Other languages
Japanese (ja)
Inventor
Hitomi Muraoka
仁美 村岡
Yasushi Nakada
泰詩 中田
Makoto Hishida
誠 菱田
Masahiko Goto
昌彦 五藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP2011063787A priority Critical patent/JP2012197645A/en
Publication of JP2012197645A publication Critical patent/JP2012197645A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a daylighting heat-insulating material having high heat insulation, high flame retardancy, and high breakdown resistance.SOLUTION: A daylighting heat-insulating material 1 includes plural resin sheets 2 laminated through plural resin spacers 3, in which the resin sheet 2 and the resin spacer 3 are composed of a flame-retardant resin composition, and a 180-degree direction peel strength when peeling the resin sheet 2 from the resin spacer 3 is within the range of 1.5 N/mm to 5 N/mm and a shearing direction peel strength when peeling the resin sheet 2 from the resin spacer 3 is within the range of 5.0 N/mm to 30 N/mm.

Description

本発明は、建築物等に用いられる採光断熱材に関し、より詳細には、複数の樹脂シートが空気層を介して積層された構造を備える採光断熱材に関する。   The present invention relates to a daylighting heat insulating material used for a building or the like, and more particularly to a daylighting heat insulating material having a structure in which a plurality of resin sheets are laminated via an air layer.

近年の建築物では、省エネルギーの観点から、外界に対する断熱性を高めることにより、冷暖房の効率を極限にまで高める試みがなされている。このような目的のために、断熱性の高い壁材等が種々提案されている。   In recent years, from the viewpoint of energy saving, attempts have been made to increase the efficiency of cooling and heating to the limit by enhancing the heat insulation from the outside. For this purpose, various wall materials having high heat insulation properties have been proposed.

現在の建築物においては、採光部としてガラス窓を設置するのが一般的である。しかしながら、壁材等に比べて、ガラス窓の断熱性を高めることは困難であった。「省エネルギー技術戦略報告書」(平成14年6月12日、経済産業省)によれば、全消費エネルギーの45%が窓等の開口部から損失しているといわれている。そのため、ガラス窓の断熱性を高める方法が求められている。   In a current building, it is common to install a glass window as a lighting part. However, it has been difficult to enhance the heat insulation of the glass window as compared with wall materials and the like. According to the “Energy Conservation Technology Strategy Report” (June 12, 2002, Ministry of Economy, Trade and Industry), it is said that 45% of all energy consumed is lost through openings such as windows. Therefore, a method for improving the heat insulating property of the glass window is required.

ガラス窓の断熱性を高める方法としては、例えば、採光断熱材をガラス窓に取り付ける方法が挙げられる。このような採光断熱材は、消防法上の防炎性能基準をクリアすることで、建物の種別や立地条件にかかわらず、広い範囲での適用が可能となる。例えば、特許文献1には、難燃性を有する採光断熱材が開示されている。上記採光断熱材では、複数のフィルムが、複数の樹脂製スペーサを介して積層されている。   As a method for improving the heat insulating property of the glass window, for example, a method of attaching a daylighting heat insulating material to the glass window can be mentioned. Such a daylighting heat insulating material can be applied in a wide range regardless of the type of building and location conditions by clearing the flameproof performance standard in the Fire Service Act. For example, Patent Literature 1 discloses a lighting heat insulating material having flame retardancy. In the above-described lighting heat insulating material, a plurality of films are laminated via a plurality of resin spacers.

特開2007−327320号JP 2007-327320 A

特許文献1には、難燃性の仕様が提案されている。しかしながら、特許文献1の採光断熱材では、樹脂製スペーサとフィルムとの接合強度が不十分であった。そのため、採光断熱材を製作する際に、フィルムのしわ等によるテンションで、スペーサのずれが生じて意匠性に影響を及ぼしたり加工する際に、外力が加わって、採光断熱材が破壊し、断熱構造を維持できなくなることがあるという問題があった。   Patent Document 1 proposes a flame retardant specification. However, in the daylighting heat insulating material of Patent Document 1, the bonding strength between the resin spacer and the film was insufficient. Therefore, when manufacturing the lighting insulation material, the spacer is displaced by the tension caused by the wrinkles of the film, etc., and when the design is affected or processed, an external force is applied and the lighting insulation material breaks down. There was a problem that the structure could not be maintained.

本発明の目的は、断熱性が高く、難燃性が高く、破壊耐性が高い採光断熱材を提供することにある。   An object of the present invention is to provide a daylighting heat insulating material having high heat insulating properties, high flame retardancy, and high fracture resistance.

本発明の採光断熱材は、複数の樹脂スペーサを介して積層された複数の樹脂シートを備える採光断熱材であって、前記樹脂シート及び前記樹脂スペーサが難燃性樹脂組成物により構成されており、前記樹脂スペーサから前記樹脂シートを剥離する際の180度方向の剥離強度が1.5N/mm〜5N/mmの範囲であり、前記樹脂スペーサから前記樹脂シートを剥離する際の剪断方向の剥離強度が5.0N/mm〜30N/mmの範囲である。   The daylighting heat insulating material of the present invention is a daylighting heat insulating material comprising a plurality of resin sheets laminated via a plurality of resin spacers, wherein the resin sheet and the resin spacer are made of a flame-retardant resin composition. The peeling strength in the 180-degree direction when peeling the resin sheet from the resin spacer is in the range of 1.5 N / mm to 5 N / mm, and the peeling in the shearing direction when peeling the resin sheet from the resin spacer. The strength is in the range of 5.0 N / mm to 30 N / mm.

本発明の採光断熱材のある特定の局面では、前記難燃性樹脂組成物が後硬化性樹脂組成物の硬化物により構成されている。その場合には、樹脂スペーサの難燃性が高くなる。樹脂シートと樹脂スペーサの接着強度が高くなる。従って、採光断熱材の難燃性及び破壊耐性をより高める事ができる。   On the specific situation with the lighting heat insulating material of this invention, the said flame-retardant resin composition is comprised with the hardened | cured material of the post-curing resin composition. In that case, the flame retardance of the resin spacer is increased. The adhesive strength between the resin sheet and the resin spacer is increased. Therefore, the flame retardancy and destruction resistance of the daylighting heat insulating material can be further increased.

本発明の採光断熱材の他の特定の局面では、前記難燃性樹脂組成物がシリコーン樹脂を含んでいる。その場合には、採光断熱材の難燃性をより高めることができる。   In another specific aspect of the daylighting heat insulating material of the present invention, the flame retardant resin composition contains a silicone resin. In that case, the flame retardance of the lighting heat insulating material can be further increased.

本発明の採光断熱材の別の特定の局面では、前記樹脂シートがポリカーボネートを含んでいる。その場合には、採光断熱材の難燃性をさらに高めることができる。   In another specific aspect of the daylighting heat insulating material of the present invention, the resin sheet contains polycarbonate. In that case, the flame retardancy of the daylighting heat insulating material can be further enhanced.

本発明の採光断熱材のさらに他の特定の局面では、前記樹脂シートの厚さが10μm〜300μmの範囲である。その場合には、必要以上に採光断熱材を厚くすることなく、採光断熱材の強度を充分に高めることができる。   In still another specific aspect of the daylighting heat insulating material of the present invention, the resin sheet has a thickness in the range of 10 μm to 300 μm. In that case, the strength of the daylighting heat insulating material can be sufficiently increased without making the daylighting heat insulating material thicker than necessary.

本発明の採光断熱材のさらに別の特定の局面では、本発明の採光断熱材は前記樹脂シートを3枚以上備えている。その場合には、採光断熱材の断熱性をより高めることができる。   In still another specific aspect of the daylighting heat insulating material of the present invention, the daylighting heat insulating material of the present invention includes three or more resin sheets. In that case, the heat insulating property of the lighting heat insulating material can be further improved.

本発明の採光断熱材のまた他の特定の局面では、前記複数の樹脂スペーサが、前記樹脂シートを介して前記樹脂シートの積層方向に重なりあっている。その場合には、採光断熱材の意匠性及び透光性を高めることができる。   In still another specific aspect of the daylighting heat insulating material of the present invention, the plurality of resin spacers overlap in the stacking direction of the resin sheets via the resin sheets. In that case, the designability and translucency of a lighting heat insulating material can be improved.

本発明の採光断熱材のまた別の特定の局面では、前記複数の樹脂スペーサが、格子状に配置されている。その場合には、前記複数の樹脂シートの間の気密性が高くなる。従って、採光断熱材の断熱性をより高めることができる。   In another specific aspect of the daylighting heat insulating material of the present invention, the plurality of resin spacers are arranged in a lattice shape. In that case, the airtightness between the plurality of resin sheets is increased. Therefore, the heat insulating property of the daylighting heat insulating material can be further improved.

本発明の採光断熱材では、複数の樹脂シートが複数の樹脂スペーサを介して積層されているため、隣り合う樹脂シート間に形成される空気層によって、採光断熱材は高い断熱性を有する。また、樹脂シート及び樹脂スペーサが難燃性樹脂組成物により構成されているため、採光断熱材は高い難燃性を有する。さらに、樹脂スペーサから樹脂シートを剥離する際の180度方向の剥離強度が1.5N/mm〜5N/mmの範囲であり、樹脂スペーサから樹脂シートを剥離する際の剪断方向の剥離強度が5.0N/mm〜30N/mmの範囲であるため、採光断熱材は高い破壊耐性を有する。従って、本発明によれば、断熱性が高く、難燃性が高く、かつ破壊耐性が高い採光断熱材を提供することができる。   In the daylighting heat insulating material of the present invention, since the plurality of resin sheets are laminated via the plurality of resin spacers, the daylighting heat insulating material has high heat insulating properties due to the air layer formed between adjacent resin sheets. Moreover, since the resin sheet and the resin spacer are comprised with the flame-retardant resin composition, the lighting heat insulating material has high flame retardance. Further, the peel strength in the 180-degree direction when peeling the resin sheet from the resin spacer is in the range of 1.5 N / mm to 5 N / mm, and the peel strength in the shearing direction when peeling the resin sheet from the resin spacer is 5 Since it is in the range of 0.0 N / mm to 30 N / mm, the daylighting heat insulating material has high fracture resistance. Therefore, according to the present invention, it is possible to provide a daylighting heat insulating material having high heat insulating properties, high flame retardancy, and high fracture resistance.

本発明の一実施形態に係る採光断熱材の一部分を拡大した略図的断面図である。It is the schematic sectional drawing to which a part of lighting insulation material concerning one embodiment of the present invention was expanded.

以下、図面を参照しつつ、本発明の具体的な実施形態を説明することにより、本発明を明らかにする。   Hereinafter, the present invention will be clarified by describing specific embodiments of the present invention with reference to the drawings.

図1に示すように、採光断熱材1では、複数枚の樹脂シート2が間に空気層5を介して積層されている。好ましくは、採光断熱材1は、3枚以上の樹脂シート2を備えている。その場合には、採光断熱材1は後述する空気層5を複数備えるため、断熱性をより高めることができる。本実施形態では、採光断熱材1は、6枚の樹脂シート2を備えている。   As shown in FIG. 1, in the lighting heat insulating material 1, a plurality of resin sheets 2 are laminated with an air layer 5 interposed therebetween. Preferably, the daylighting insulating material 1 includes three or more resin sheets 2. In that case, since the daylighting heat insulating material 1 includes a plurality of air layers 5 to be described later, the heat insulating property can be further improved. In the present embodiment, the daylighting heat insulating material 1 includes six resin sheets 2.

複数の樹脂シート2は、難燃性樹脂組成物により構成されている。本発明において「難燃性」とは、消防法上の防炎性を満たすものを言う。複数の樹脂シート2は難燃性樹脂組成物により構成されているため、複数の樹脂シート2は難燃性を有する。それによって、採光断熱材1の難燃性が高められる。   The some resin sheet 2 is comprised by the flame-retardant resin composition. In the present invention, “flame retardant” refers to a material that satisfies the flame retardant property under the Fire Service Law. Since the plurality of resin sheets 2 are made of a flame retardant resin composition, the plurality of resin sheets 2 have flame retardancy. Thereby, the flame retardance of the daylighting heat insulating material 1 is enhanced.

上記難燃性樹脂組成物としては、例えば、自消性を有するポリカーボネート、ポリ塩化ビニル、ポリ塩素化塩化ビニル及びそれらの組み合わせ等が挙げられる。複数の樹脂シート2の材料となる上記難燃性樹脂組成物は全て同じであってもよく、異なっていてもよい。また、複数の樹脂シート2の材料となる上記難燃性樹脂組成物と、後述する複数の樹脂スペーサ3に用いられる難燃性樹脂組成物とは同じであってもよく、異なっていてもよい。   Examples of the flame retardant resin composition include self-extinguishing polycarbonate, polyvinyl chloride, polychlorinated vinyl chloride, and combinations thereof. The flame retardant resin compositions used as the material for the plurality of resin sheets 2 may all be the same or different. Moreover, the said flame-retardant resin composition used as the material of the some resin sheet 2 and the flame-retardant resin composition used for the some resin spacer 3 mentioned later may be the same, and may differ. .

複数の樹脂シート2の材料となる樹脂は、採光断熱材1の採光性を確保するために、透光性を有することが好ましい。なお、本発明において「透光性を有する」とは、可視光線透過率が20%以上であることをいう。さらに採光断熱を開口部に設置後も、窓面を介して相対する側の状況を判断できる視認性があることが望ましい。この場合には、可視光線透過率は50%以上、より好ましくは55%以上である。   The resin as the material of the plurality of resin sheets 2 preferably has translucency in order to ensure the daylighting property of the daylighting heat insulating material 1. In the present invention, “having translucency” means that the visible light transmittance is 20% or more. Furthermore, it is desirable that visibility be able to determine the situation on the opposite side through the window surface even after the daylight insulation is installed in the opening. In this case, the visible light transmittance is 50% or more, more preferably 55% or more.

複数の樹脂シート2の厚さは特に限定されないが、好ましい下限は10μm、好ましい上限は300μmである。複数の樹脂シート2の厚さが10μm未満であると、得られる採光断熱材の強度が劣ることがある。複数の樹脂シート2の厚さが300μmを超えると、同じ断熱効果を得るのに必要以上に採光断熱材が厚くなることがある。より好ましくは、複数の樹脂シート2の厚さの下限は20μm、上限は200μmである。複数の樹脂シート2の厚さは全て同じであってもよく、異なっていてもよい。   Although the thickness of the some resin sheet 2 is not specifically limited, A preferable minimum is 10 micrometers and a preferable upper limit is 300 micrometers. When the thickness of the plurality of resin sheets 2 is less than 10 μm, the strength of the obtained lighting heat insulating material may be inferior. If the thickness of the plurality of resin sheets 2 exceeds 300 μm, the daylighting heat insulating material may become thicker than necessary to obtain the same heat insulating effect. More preferably, the minimum of the thickness of the some resin sheet 2 is 20 micrometers, and an upper limit is 200 micrometers. The thicknesses of the plurality of resin sheets 2 may all be the same or different.

複数の樹脂シート2は、複数の樹脂スペーサ3を介して積層されている。複数の樹脂スペーサ3により、隣り合う樹脂シート2の間には、空気層5が形成されている。空気層5により、採光断熱材1の断熱性が高められる。また、本実施形態のように、採光断熱材1に複数の空気層5が形成される場合には、採光断熱材1の断熱性をより高めることができる。   The plurality of resin sheets 2 are stacked via a plurality of resin spacers 3. An air layer 5 is formed between the adjacent resin sheets 2 by the plurality of resin spacers 3. The air layer 5 enhances the heat insulating property of the daylighting heat insulating material 1. Moreover, when the several air layer 5 is formed in the lighting insulation material 1 like this embodiment, the heat insulation of the lighting insulation material 1 can be improved more.

本発明の樹脂シート2と樹脂スペーサ3の接着強度については、樹脂スペーサ3から樹脂シート2を剥離する際の180度方向の剥離強度が1.5N/mm〜5N/mm、かつ樹脂スペーサ3から樹脂シート2を剥離する際の剪断剥離強度が5.0N/mm〜30N/mmの範囲とされる。上記剥離強度を上記範囲とすることによって、採光断熱材1が製作、施工する際及び使用されている内に破壊されることを防ぐことができる。すなわち、採光断熱材1の破壊耐性が高められる。   Regarding the adhesive strength between the resin sheet 2 and the resin spacer 3 of the present invention, the peel strength in the 180-degree direction when the resin sheet 2 is peeled from the resin spacer 3 is 1.5 N / mm to 5 N / mm, and from the resin spacer 3 The shear peeling strength at the time of peeling the resin sheet 2 is set in a range of 5.0 N / mm to 30 N / mm. By making the said peeling strength into the said range, when making and constructing the lighting insulation material 1 and being destroyed, it can prevent being destroyed. That is, the destruction resistance of the daylighting heat insulating material 1 is increased.

樹脂スペーサ3から樹脂シート2を剥離する際の180度方向の剥離強度が1.5N/mmより小さいと、採光断熱材1の破壊耐性が充分に高められないことがある。樹脂スペーサ3から樹脂シート2を剥離する際の180度方向の剥離強度が5N/mmより大きいと、採光断熱材を緩い曲面箇所に施工する場合、追従性が低く、施工じわを生じ、意匠性を損なうことが考えられる。   If the peel strength in the 180-degree direction when peeling the resin sheet 2 from the resin spacer 3 is smaller than 1.5 N / mm, the fracture resistance of the daylighting heat insulating material 1 may not be sufficiently increased. If the peel strength in the 180-degree direction when peeling the resin sheet 2 from the resin spacer 3 is greater than 5 N / mm, when the daylighting heat insulating material is applied to a loose curved surface, the followability is low, resulting in wrinkles. It is possible to impair the sex.

樹脂スペーサ3から樹脂シート2を剥離する際の剪断剥離強度が5.0N/mmより小さいと、採光断熱材1の破壊耐性が充分に高められないことがある。樹脂スペーサ3から樹脂シート2を剥離する際の剪断剥離強度が30N/mmより大きいと、フィルムの貼付始点ばらつきにより、フィルム貼付時に、しわが生じることが考えられる。   If the shear peeling strength when peeling the resin sheet 2 from the resin spacer 3 is smaller than 5.0 N / mm, the fracture resistance of the daylighting heat insulating material 1 may not be sufficiently increased. If the shear peel strength when the resin sheet 2 is peeled from the resin spacer 3 is greater than 30 N / mm, wrinkles may occur when the film is stuck due to variations in the starting point of the film.

複数の樹脂スペーサ3は、難燃性樹脂組成物により構成されている。上記「難燃性」とは、前述の通りである。本発明において、複数の樹脂スペーサ3は難燃性樹脂組成物により構成されているため、複数の樹脂スペーサ3は難燃性を有する。それによって、採光断熱材1の難燃性が高められる。   The plurality of resin spacers 3 are made of a flame retardant resin composition. The “flame retardant” is as described above. In this invention, since the some resin spacer 3 is comprised with the flame-retardant resin composition, the some resin spacer 3 has a flame retardance. Thereby, the flame retardance of the daylighting heat insulating material 1 is enhanced.

上記難燃性樹脂組成物は、好ましくは、後硬化性樹脂組成物を後硬化反応により硬化してなる硬化物からなる。その場合には、上記硬化物は後硬化により硬くなるため、樹脂スペーサ3から樹脂シート2を剥離する際の剥離強度及び樹脂シート2と樹脂スペーサ3との接着強度が高くなる。   The flame retardant resin composition preferably comprises a cured product obtained by curing the post-curing resin composition by a post-curing reaction. In that case, since the said hardened | cured material becomes hard by postcure, the peeling strength at the time of peeling the resin sheet 2 from the resin spacer 3 and the adhesive strength of the resin sheet 2 and the resin spacer 3 become high.

また、後硬化性樹脂組成物を使用すると、フィルム面への塗工時の粘度調整が容易となるため、特に粘度を小さくすることで、フィルム面へのミクロな浸透が生じ、フィルム界面への接着強度が向上する。   In addition, when a post-curing resin composition is used, viscosity adjustment at the time of coating on the film surface is facilitated. Particularly, by reducing the viscosity, micro penetration into the film surface occurs, and the film interface Adhesive strength is improved.

通常、熱可塑性樹脂を使用する場合には、粘度を小さくしてフィルム面への流れ性、あるいは、なじみ性を向上させるためには、樹脂の塗工温度(樹脂温度)を上げるのが常套手段であるが、この場合には、フィルムの熱収縮温度以下でないと、樹脂塗工部にしわが生じ、意匠性が損なわれるため、意匠と接着力の両立が困難となる。   Usually, when a thermoplastic resin is used, it is a common practice to increase the resin coating temperature (resin temperature) in order to reduce the viscosity and improve the flowability to the film surface or the conformability. However, in this case, if the temperature is not lower than the heat shrinkage temperature of the film, the resin-coated portion is wrinkled and the design properties are impaired, so that it is difficult to achieve both the design and the adhesive force.

それによって、採光断熱材1の破壊耐性をより高めることができる。上記後硬化性樹脂組成物を後硬化させる方法は特に限定されず、上記後硬化性樹脂組成物によって適宜選択される。後硬化方法としては、例えば、熱硬化、紫外線硬化、湿気硬化等が挙げられる。   Thereby, the destruction resistance of the daylighting heat insulating material 1 can be further increased. The method for post-curing the post-curing resin composition is not particularly limited, and is appropriately selected depending on the post-curing resin composition. Examples of the post-curing method include thermal curing, ultraviolet curing, moisture curing, and the like.

上記難燃性樹脂組成物は、難燃性を有する硬化物となる樹脂組成物である限り特に限定されない。上記難燃性樹脂組成物用の樹脂成分としては、好ましくは、難燃性を有するシリコーン樹脂または塩化ビニル樹脂が用いられる。複数の樹脂スペーサ3に用いられる上記難燃性樹脂組成物は全て同じであってもよく、異なっていてもよい。また、複数の樹脂スペーサ3に用いられる上記難燃性樹脂組成物と、複数の樹脂シート2の材料となる難燃性樹脂組成物とは同じであってもよく、異なっていてもよい。   The flame retardant resin composition is not particularly limited as long as it is a resin composition that becomes a cured product having flame retardancy. As the resin component for the flame retardant resin composition, preferably, a flame retardant silicone resin or vinyl chloride resin is used. The flame retardant resin compositions used for the plurality of resin spacers 3 may all be the same or different. Moreover, the said flame retardant resin composition used for the some resin spacer 3 and the flame retardant resin composition used as the material of the some resin sheet 2 may be the same, and may differ.

上記難燃性樹脂組成物は、上記樹脂以外に種々の他の成分を含んでいてもよい。例えば、上記難燃性樹脂組成物が上記硬化物からなり、上記後硬化性樹脂組成物が光硬化により後硬化する場合には、光ラジカル重合剤や、光カチオン重合開始剤を含むことが好ましい。   The flame retardant resin composition may contain various other components in addition to the resin. For example, when the flame retardant resin composition is composed of the cured product and the post-curable resin composition is post-cured by photocuring, it preferably contains a radical photopolymerization agent or a cationic photopolymerization initiator. .

好ましくは、上記難燃性樹脂組成物には、後硬化反応系のシリコーン系樹脂組成物が用いられる。このような後効果反応をし得るシリコーン系樹脂組成物としては、例えば、信越化学社製、商品名:シーラント45、セメダイン社製、シリコーン樹脂組成物品番:♯8060などを挙げることができる。このような後硬化性組成物としてのシリコーン系樹脂組成物は、湿気等により後硬化するものである。   Preferably, a post-curing reaction type silicone resin composition is used for the flame retardant resin composition. Examples of the silicone resin composition capable of undergoing such a post-effect reaction include trade name: sealant 45, manufactured by Shin-Etsu Chemical Co., Ltd., Cemedine, silicone resin composition article number: # 8060, and the like. The silicone-based resin composition as such a post-curable composition is post-cured by moisture or the like.

複数の樹脂スペーサ3は、可撓性を備えていることが好ましい。樹脂スペーサ3の可撓性が低いと、樹脂スペーサ3が脆くなり、割れやすくなることがある。   The plurality of resin spacers 3 are preferably provided with flexibility. If the flexibility of the resin spacer 3 is low, the resin spacer 3 may become brittle and easily break.

複数の樹脂スペーサ3は、透光性を有することが好ましい。その場合には、採光断熱材1の透光性を高めることができる。もっとも、樹脂スペーサ3は、採光断熱材1の意匠性を高めるために、着色されていてもよい。   The plurality of resin spacers 3 preferably have translucency. In that case, the translucency of the lighting heat insulating material 1 can be improved. However, the resin spacer 3 may be colored in order to improve the design of the daylighting heat insulating material 1.

複数の樹脂スペーサ3は、採光断熱材1の断熱性能を阻害しないために、高い断熱性を備えていることが好ましい。   The plurality of resin spacers 3 preferably have high heat insulating properties so as not to hinder the heat insulating performance of the daylighting heat insulating material 1.

複数の樹脂スペーサ3の形状は、空気層5を形成できる限り特に限定されず、例えば、粒子状、線状、格子状等とすることができる。複数の樹脂スペーサ3の形状は全て同じであってもよく、異なっていてもよい。また、複数の樹脂スペーサ3の形状により、採光断熱材1に意匠性を付与してもよい。   The shape of the plurality of resin spacers 3 is not particularly limited as long as the air layer 5 can be formed, and may be, for example, a particle shape, a linear shape, a lattice shape, or the like. The plurality of resin spacers 3 may all have the same shape or different shapes. Moreover, you may provide the designability to the lighting heat insulating material 1 with the shape of the some resin spacer 3. FIG.

なかでも、複数の樹脂スペーサ3の形状は、格子状とすることが好ましい。その場合には、空気層5を効率的に分割すること、及び空気層5の周辺部を効率的に封止することができる。それによって、分割された空気層5の独立性及び気密性を高めることができる。従って、採光断熱材1の断熱性をより高めることができる。   Especially, it is preferable that the shape of the plurality of resin spacers 3 is a lattice shape. In that case, the air layer 5 can be efficiently divided, and the periphery of the air layer 5 can be efficiently sealed. Thereby, the independence and airtightness of the divided air layer 5 can be enhanced. Accordingly, the heat insulating property of the daylighting heat insulating material 1 can be further improved.

採光断熱材1が3枚以上の樹脂シート2を備えている場合には、複数の樹脂スペーサ3は、樹脂シート2を介して積層方向に重なりあっていることが好ましい。その場合には、樹脂スペーサ3による採光断熱材1の透光性の減少を最小限に抑えることができる。   When the daylighting insulating material 1 includes three or more resin sheets 2, the plurality of resin spacers 3 are preferably overlapped in the stacking direction via the resin sheets 2. In that case, a decrease in translucency of the daylighting heat insulating material 1 due to the resin spacer 3 can be minimized.

空気層5は、複数の樹脂スペーサ3により複数のセルに分割されていることが好ましい。それによって、空気層5の個別のセルの独立性及び気密性を高めることができる。従って、採光断熱材1の断熱性をより高めることができる。また、空気層5の分割に用いる樹脂スペーサ3によって、採光断熱材1の強度をより高めることができる。   The air layer 5 is preferably divided into a plurality of cells by a plurality of resin spacers 3. Thereby, the independence and airtightness of the individual cells of the air layer 5 can be enhanced. Accordingly, the heat insulating property of the daylighting heat insulating material 1 can be further improved. Moreover, the strength of the daylighting heat insulating material 1 can be further increased by the resin spacer 3 used for dividing the air layer 5.

空気層5を複数のセルに分割する場合には、空気層5の各セルの大きさの好ましい下限は4cm、好ましい上限は1800cmである。空気層5の各セルの大きさが4cm未満であると、得られる採光断熱材1の可視光線透過率が劣ることがある。空気層5の各セルの大きさが1800cmを超えると、得られる採光断熱材1の強度が劣ることがある。より好ましくは、空気層5の各セルの大きさの下限は25cmであり、上限は600cmである。 When dividing the air layer 5 into a plurality of cells, preferred lower limit is 4 cm 2 in size for each cell in the air layer 5, the upper limit thereof is preferably 1800 cm 2. When the size of each cell of the air layer 5 is less than 4 cm 2 , the visible light transmittance of the obtained lighting insulation 1 may be inferior. When the size of each cell of the air layer 5 exceeds 1800 cm 2 , the strength of the obtained lighting heat insulating material 1 may be inferior. More preferably, the lower limit of the size of each cell of the air layer 5 is 25 cm 2 and the upper limit is 600 cm 2 .

本発明の採光断熱材1は、例えば、樹脂スペーサ3の材料として難燃性樹脂組成物を用いて、樹脂シート2の積層体を公知の方法で製造することにより得られる。上記樹脂シート2の積層体は、例えば、特許第4608595号に記載の製造装置及び製造方法により製造することができる。   The lighting heat insulating material 1 of the present invention is obtained, for example, by manufacturing a laminate of the resin sheet 2 by a known method using a flame retardant resin composition as the material of the resin spacer 3. The laminated body of the said resin sheet 2 can be manufactured with the manufacturing apparatus and manufacturing method of patent 4608595, for example.

樹脂スペーサ3の材料に後硬化反応性樹脂組成物を用いる場合には、本発明の採光断熱材1は、樹脂シート2の積層体を公知の方法で製造した後、スペーサを後硬化させることにより製造することができる。上記スペーサを後硬化させる方法は、上記後硬化反応性樹脂組成物によって適宜選択される。例えば、上記後硬化反応性樹脂組成物が光反応性ホットメルト接着剤の場合には、上記樹脂シート2の積層体を製造した後に紫外線を照射することにより、本発明の採光断熱材1を得ることができる。   When the post-curing reactive resin composition is used as the material for the resin spacer 3, the lighting heat insulating material 1 of the present invention is manufactured by manufacturing the laminate of the resin sheet 2 by a known method and then post-curing the spacer. Can be manufactured. The method of post-curing the spacer is appropriately selected depending on the post-curing reactive resin composition. For example, when the post-curing reactive resin composition is a photoreactive hot-melt adhesive, the daylighting insulating material 1 of the present invention is obtained by irradiating with ultraviolet rays after the laminate of the resin sheet 2 is manufactured. be able to.

以上のように、本発明の採光断熱材では、複数の樹脂シートが複数の樹脂スペーサを介して積層されているため、隣り合う樹脂シート間に形成される空気層によって、採光断熱材は高い断熱性を有する。また、樹脂シート及び樹脂スペーサが難燃性樹脂組成物により構成されているため、採光断熱材は高い難燃性を有する。さらに、前記樹脂スペーサから前記樹脂シートを剥離する際の180度方向の剥離強度が1.5N/mm〜5N/mmの範囲であり、前記樹脂スペーサから前記樹脂シートを剥離する際の剪断方向の剥離強度が5.0N/mm〜30N/mmの範囲であるため、採光断熱材は高い破壊耐性を有する。従って、本発明によれば、断熱性が高く、透光性が高く、かつ破壊耐性が高い採光断熱材を提供することができる。   As described above, in the daylighting heat insulating material of the present invention, since the plurality of resin sheets are laminated via the plurality of resin spacers, the daylighting heat insulating material is highly insulated by the air layer formed between the adjacent resin sheets. Have sex. Moreover, since the resin sheet and the resin spacer are comprised with the flame-retardant resin composition, the lighting heat insulating material has high flame retardance. Further, the peel strength in the 180-degree direction when peeling the resin sheet from the resin spacer is in a range of 1.5 N / mm to 5 N / mm, and the shear direction when peeling the resin sheet from the resin spacer. Since the peel strength is in the range of 5.0 N / mm to 30 N / mm, the daylighting heat insulating material has high fracture resistance. Therefore, according to the present invention, it is possible to provide a daylighting heat insulating material having high heat insulating properties, high translucency, and high fracture resistance.

本発明の採光断熱材は、例えば、単独でまたは通常のガラスと併用して建築物の採光部に設置することにより、高い断熱性能を発揮することができる。   The daylighting heat insulating material of the present invention can exhibit high heat insulating performance, for example, by installing it in a daylighting part of a building alone or in combination with ordinary glass.

本発明の採光断熱材の設置態様としては特に限定されないが、例えば、通常のガラスによる出窓状の採光部において、該ガラスの内側に該ガラスから離して設置することが考えられる。本発明の採光断熱材を着脱可能なように設置することにより、季節や目的に合わせて本発明の採光断熱材を用いることができる。また、本発明の採光断熱材を、開閉可能な形としてもよい。   Although it does not specifically limit as an installation aspect of the lighting insulation material of this invention, For example, in the bay window-shaped daylighting part by a normal glass, installing away from this glass inside this glass can be considered. By installing the daylighting heat insulating material of the present invention so as to be removable, the daylighting heat insulating material of the present invention can be used according to the season and purpose. Moreover, it is good also as a shape which can open and close the lighting insulation material of this invention.

以下、本発明の具体的な実施例を挙げることにより、本発明を明らかにする。なお、本発明は以下の実施例に限定されるものではない。   Hereinafter, the present invention will be clarified by giving specific examples of the present invention. In addition, this invention is not limited to a following example.

(樹脂シートの積層方法)
装置としてサンツール社製XY塗工機を使用し、以下の方法で実施例1〜2及び比較例1に使用する樹脂シート積層体を製造した。
(Resin sheet lamination method)
The resin sheet laminated body used for Examples 1-2 and the comparative example 1 was manufactured with the following method using the XY coating machine by a sun tool company as an apparatus.

1枚の樹脂シートの上に、樹脂スペーサ用組成物を径0.57mm、50mmピッチで線状に塗工したものを5枚作製し、塗工ラインの両側に、長手方向に沿って0.56mm厚の木製線材を設置した。樹脂スペーサ用組成物が、樹脂シートを介して樹脂スペーサラインが重なるように、塗工した樹脂シートを5枚重ね合わせ、最後に、塗工していない樹脂シートをのせて、6枚の樹脂シートが積層された5層4tの積層体を得た。   Five sheets of the resin spacer composition coated in a linear shape with a diameter of 0.57 mm and a pitch of 50 mm are prepared on one resin sheet, and 0.005 along the longitudinal direction on both sides of the coating line. A 56 mm thick wooden wire was installed. The resin spacer composition is overlapped with five coated resin sheets so that the resin spacer lines overlap through the resin sheet, and finally the uncoated resin sheet is placed on the six resin sheets. A laminate of 5 layers 4t was obtained.

(実施例1)
樹脂シートとして上記ポリカーボネートフィルム(商品名 三菱ガス化学社製「ユーピロン FE−2000」、厚さ200μm)を使用し、樹脂スペーサ用組成物としてシリコーン樹脂組成物(信越化学社製「シーラント45」)を用いて、上述の製造方法により樹脂シート積層体を得た。
Example 1
The polycarbonate film (trade name “Iupilon FE-2000” manufactured by Mitsubishi Gas Chemical Co., Inc., thickness 200 μm) is used as the resin sheet, and the silicone resin composition (“Sealant 45” manufactured by Shin-Etsu Chemical Co., Ltd.) is used as the resin spacer composition. Using, the resin sheet laminated body was obtained by the above-mentioned manufacturing method.

その後、上記樹脂シート積層体を常温で1日放置し、上記樹脂シート積層体に用いたシリコーン樹脂組成物を後硬化させて、採光断熱材を得た。   Thereafter, the resin sheet laminate was left at room temperature for 1 day, and the silicone resin composition used in the resin sheet laminate was post-cured to obtain a daylighting heat insulating material.

(実施例2)
次に、樹脂シートとして上記ポリカーボネートフィルム(商品名 三菱ガス化学社製「ユーピロン FE−2000」、厚さ200μm)を使用し、樹脂スペーサ用組成物としてシリコーン樹脂組成物(セメダイン社製「#8060」)を用いて、上述の製造方法により樹脂シート積層体を得た。
(Example 2)
Next, the polycarbonate film (trade name “Iupilon FE-2000” manufactured by Mitsubishi Gas Chemical Co., Inc., thickness: 200 μm) is used as the resin sheet, and the silicone resin composition (“# 8060” manufactured by Cemedine Co., Ltd.) is used as the resin spacer composition. ) Was used to obtain a resin sheet laminate by the above-described manufacturing method.

(比較例1)
次に、樹脂シートとして上記PETフィルム(東洋紡績社製 商品名「コスモシャインA4300」、厚さ188μm)を、樹脂スペーサ用組成物としてアクリル樹脂組成物を用いて、上述の製造方法により樹脂シート積層体を得た。上記樹脂シート積層体を、比較例の採光断熱材とした。
(Comparative Example 1)
Next, using the PET film (trade name “Cosmo Shine A4300” manufactured by Toyobo Co., Ltd., thickness: 188 μm) as the resin sheet and the acrylic resin composition as the resin spacer composition, the resin sheet is laminated by the above-described manufacturing method. Got the body. The said resin sheet laminated body was used as the lighting insulation material of the comparative example.

(評価)
実施例1〜2及び比較例1の採光断熱材について以下の試験を行った。
(Evaluation)
The following tests were conducted on the daylighting heat insulating materials of Examples 1 and 2 and Comparative Example 1.

(1)防炎性能
消防法告示の防炎性能試験に準拠し、実施例1〜2及び比較例1の採光断熱材を規定の大きさに裁断し、試験した。結果を表1に示した。
(1) Flameproof performance Based on the fireproof performance test of Notification of Fire Service Law, the daylighting heat insulating materials of Examples 1 and 2 and Comparative Example 1 were cut into a specified size and tested. The results are shown in Table 1.

その結果、実施例1〜2の採光断熱材は基準を満たし、合格であった。比較例1の採光断熱材は基準を満たさなかった。   As a result, the daylighting heat insulating materials of Examples 1 and 2 satisfied the standard and passed. The lighting insulation of Comparative Example 1 did not meet the criteria.

(2)断熱性(熱貫流率)
JIS R 3107に準拠して、実施例1〜2及び比較例1の採光断熱材について熱貫流率を算出した。結果を表1に示した。
(2) Thermal insulation (heat flow rate)
Based on JIS R 3107, the heat transmissivity was calculated for the daylighting heat insulating materials of Examples 1-2 and Comparative Example 1. The results are shown in Table 1.

その結果、実施例1〜2及び比較例1の採光断熱材の熱貫流率は、共に3.4W/mKであった。 As a result, the heat penetration rates of the daylighting heat insulating materials of Examples 1 and 2 and Comparative Example 1 were both 3.4 W / m 2 K.

(3)180度剥離強度
実施例1〜2及び比較例1の採光断熱材において、2枚の樹脂シートからなる層のみを使用し、直線状の樹脂スペーサ用組成物を中央にして、25mm巾×150mm長の試験片を作製した。オリエンテック社製万能試験機テンシロンにより50mm/minの剥離速度で、樹脂スペーサから樹脂シートを180度方向に剥離することにより、剥離強度を測定した。結果を表1に示した。
(3) 180 degree peel strength In the lighting heat insulating materials of Examples 1 and 2 and Comparative Example 1, only a layer composed of two resin sheets is used, and a linear resin spacer composition is used as the center, and the width is 25 mm. A test piece with a length of 150 mm was produced. The peel strength was measured by peeling the resin sheet from the resin spacer in the direction of 180 degrees at a peel speed of 50 mm / min with an orientec universal testing machine Tensilon. The results are shown in Table 1.

その結果、実施例1の採光断熱材では2.0N/mm、実施例2の採光断熱材では2.5N/mmであった。比較例1の採光断熱材では1.2N/mmであった。   As a result, it was 2.0 N / mm for the daylighting heat insulating material of Example 1, and 2.5 N / mm for the daylighting heat insulating material of Example 2. In the daylighting heat insulating material of Comparative Example 1, it was 1.2 N / mm.

ちなみに、180度剥離強度は、積層後に採光断熱材として、運搬や施工等に用いられる課程での破壊のしやすさの目安となる。   Incidentally, the 180-degree peel strength is a measure of the ease of destruction in a process used for transportation, construction, etc. as a daylighting heat insulating material after lamination.

(4)剪断剥離強度
実施例1〜2及び比較例1の採光断熱材において、2枚の樹脂シートからなる層のみを使用し、直線状の樹脂スペーサ用組成物を中央にして、25mm巾×150mm長の試験片を作製した。オリエンテック社製万能試験機テンシロンにより50mm/minの剥離速度で、樹脂スペーサから樹脂シートを剪断方向に剥離することにより、剥離強度を測定した。結果を表1に示した。
(4) Shear peel strength In the daylighting heat insulating materials of Examples 1 and 2 and Comparative Example 1, only a layer composed of two resin sheets was used, and a linear resin spacer composition was used as the center, with a width of 25 mm × A 150 mm long test piece was prepared. The peel strength was measured by peeling the resin sheet in the shear direction from the resin spacer at a peel speed of 50 mm / min with an orientec universal testing machine Tensilon. The results are shown in Table 1.

その結果、実施例1の採光断熱材では7.0N/mm、実施例2の採光断熱材では8.0N/mmであった。比較例1の採光断熱材では5.0N/mmであった。   As a result, it was 7.0 N / mm for the daylighting heat insulating material of Example 1, and 8.0 N / mm for the daylighting heat insulating material of Example 2. In the daylighting heat insulating material of Comparative Example 1, it was 5.0 N / mm.

ちなみに、剪断剥離強度は、この積層体の作製する製造工程上のスペーサ樹脂とシートのすべりやすさ、位置のズレやすさなどの目安となる。   Incidentally, the shear peel strength is a measure of the ease of slipping and positional displacement of the spacer resin and the sheet in the production process for producing the laminate.

Figure 2012197645
Figure 2012197645

上記(1)から明らかなように、本発明に従う実施例1〜2により製造された採光断熱材は、比較例1により製造された採光断熱材と比較して、防炎性能が高められていることがわかる。これは、樹脂シートに自消性のポリカーボネートフィルムを、並びに樹脂スペーサ用組成物に難燃性のシリコーン樹脂を使用したことにより、実施例の採光断熱材の防炎性が高められたと考えられる。   As apparent from the above (1), the daylighting heat insulating material manufactured according to Examples 1 and 2 according to the present invention has improved flameproofing performance as compared with the daylighting heat insulating material manufactured according to Comparative Example 1. I understand that. This is considered that the flameproofness of the daylighting heat insulating material of the Example was improved by using a self-extinguishing polycarbonate film for the resin sheet and a flame-retardant silicone resin for the resin spacer composition.

また、上記(2)において、実施例1〜2、比較例1の採光断熱材はいずれも、高い断熱性(熱貫流率)を示している。これは、採光断熱材が複数の樹脂スペーサを介して積層された同じ樹脂シート積層構造を備えているための効果であり、樹脂シート間に形成された空気層により、断熱性が高められたと考えられる。   Moreover, in said (2), all the lighting insulation materials of Examples 1-2 and the comparative example 1 have shown high heat insulation (heat transmissivity). This is because the lighting insulation has the same resin sheet laminated structure laminated through a plurality of resin spacers, and the heat insulation is considered to be enhanced by the air layer formed between the resin sheets. It is done.

加えて、上記(3),(4)から明らかなように、実施例1〜2の採光断熱材は、比較例1の採光断熱材と比較して、剥離強度が高められていることがわかる。これは、樹脂スペーサ用組成物にシリコーン樹脂を使用し、樹脂シートの積層後にシリコーン樹脂を後硬化させたことにより、実施例の採光断熱材の剥離強度が高められたと考えられる。   In addition, as apparent from the above (3) and (4), it can be seen that the daylighting heat insulating materials of Examples 1 and 2 have higher peel strength than the daylighting heat insulating material of Comparative Example 1. . This is probably because the peel strength of the daylighting heat insulating material of the example was increased by using a silicone resin for the resin spacer composition and post-curing the silicone resin after laminating the resin sheets.

1…採光断熱材
2…樹脂シート
3…樹脂スペーサ
5…空気層
DESCRIPTION OF SYMBOLS 1 ... Daylight insulation material 2 ... Resin sheet 3 ... Resin spacer 5 ... Air layer

Claims (8)

複数の樹脂スペーサを介して積層された複数の樹脂シートを備える採光断熱材であって、前記樹脂シート及び前記樹脂スペーサが難燃性樹脂組成物により構成されており、前記樹脂スペーサと前記樹脂シートとを剥離する際の180度方向の剥離強度が1.5N/mm〜5N/mmの範囲であり、前記樹脂スペーサから前記樹脂シートを剪断方向に滑らせる際の剪断方向の剥離強度が5.0N/mm〜30N/mmの範囲である、採光断熱材。   A lighting heat insulating material comprising a plurality of resin sheets laminated via a plurality of resin spacers, wherein the resin sheet and the resin spacer are made of a flame retardant resin composition, and the resin spacer and the resin sheet The peel strength in the 180-degree direction when peeling the resin sheet is in the range of 1.5 N / mm to 5 N / mm, and the peel strength in the shear direction when sliding the resin sheet from the resin spacer in the shear direction is 5. A daylighting heat insulating material in a range of 0 N / mm to 30 N / mm. 前記難燃性樹脂組成物が後硬化性樹脂組成物の硬化物からなる、請求項1に記載の採光断熱材。   The daylighting heat insulating material according to claim 1, wherein the flame retardant resin composition is a cured product of a post-curing resin composition. 前記難燃性樹脂組成物がシリコーン樹脂を含んでいる、請求項1または2に記載の採光断熱材。   The daylighting heat insulating material according to claim 1 or 2, wherein the flame retardant resin composition contains a silicone resin. 前記樹脂シートがポリカーボネートを含んでいる、請求項1〜3のいずれか1項に記載の採光断熱材。   The lighting heat insulating material according to any one of claims 1 to 3, wherein the resin sheet contains polycarbonate. 前記樹脂シートの厚さが10μm〜300μmの範囲である、請求項1〜4のいずれか1項に記載の採光断熱材。   The lighting heat insulating material according to any one of claims 1 to 4, wherein the resin sheet has a thickness in a range of 10 µm to 300 µm. 前記樹脂シートを3枚以上備える、請求項1〜5のいずれか1項に記載の採光断熱材。   The lighting heat insulating material according to any one of claims 1 to 5, comprising three or more of the resin sheets. 前記複数の樹脂スペーサが、前記樹脂シートを介して前記樹脂シートの積層方向に重なりあっている、請求項6に記載の採光断熱材。   The lighting heat insulating material according to claim 6, wherein the plurality of resin spacers overlap with each other in the stacking direction of the resin sheets via the resin sheets. 前記複数の樹脂スペーサが、格子状に配置されている、請求項1〜7のいずれか1項に記載の採光断熱材。   The daylighting heat insulating material according to claim 1, wherein the plurality of resin spacers are arranged in a lattice shape.
JP2011063787A 2011-03-23 2011-03-23 Daylighting heat-insulating material Pending JP2012197645A (en)