JP2012187307A

JP2012187307A - Bristle material for brush

Info

Publication number: JP2012187307A
Application number: JP2011054279A
Authority: JP
Inventors: Shigehiro Nakajima; 滋裕中島
Original assignee: Kowa Co Ltd
Current assignee: Kowa Co Ltd
Priority date: 2011-03-11
Filing date: 2011-03-11
Publication date: 2012-10-04
Also published as: CN102669934A

Abstract

PROBLEM TO BE SOLVED: To provide a bristle material for a brush, which can be used for various brushes having high performance in cleaning without giving dents or fine scratches.SOLUTION: The bristle material 1 is formed in a multifilament form having joining parts 2a and 2b, at which a plural number of approximately columnar shape monofilament foam strings 2, 3 composed of a thermoplastic resin are melt joined and bundled together. Also, by outside force, joined monofilament foamed strings 2, 2 (3) can be separated from each other from the joining parts 2a, 2b or from the periphery of 2a, 2b.

Description

本発明は、例えば、自動車や車両等を洗浄する自動洗車機、各種ガラス洗浄機等に搭載される回転ブラシに使用するブラシ用毛材や、食器洗浄ブラシ、食品洗浄ブラシ等の各種洗浄用ブラシに使用するブラシ用毛材、各種清掃用ブラシ用毛材に関するものである。 The present invention relates to brushes for use in rotating brushes mounted on, for example, automatic car wash machines for washing automobiles and vehicles, various glass washers, etc., and various washing brushes such as dish washing brushes and food washing brushes. The present invention relates to a bristle material for a brush used for the cleaning, and a bristle material for various cleaning brushes.

各種の洗浄、清掃等に使用するブラシ用毛材に関しては、使用目的に応じて、さまざまな改良がなされている。例えば、断面に複数の凹凸を有する多葉断面モノフィラメントのブリッスルからなり、少なくとも一方の先端には、多葉断面の境界部分を介して分岐した複数の先割れ部を有する研磨のためのブラシ用毛材がある（特許文献１）。 Various improvements have been made regarding brush hair materials used for various types of cleaning, cleaning, and the like, depending on the purpose of use. For example, brush hair for polishing comprising a multi-leaf cross-section monofilament bristle having a plurality of irregularities in the cross section and having a plurality of tip cracks branching through a boundary portion of the multi-leaf cross section at at least one tip. There is a material (Patent Document 1).

また、断面が複数の芯部と、該複数の芯部間を連結する結合部とにより構成され、少なくとも長手方向の一端は、前記結合部において分割されているブラシ用毛材がある（特許文献２）。このブラシ用毛材は、結合部の肉厚と芯部の肉厚との差を任意に設定する事によって、毛腰を強く設定することができるものであった。 In addition, there is a bristle material for a brush whose cross section includes a plurality of core parts and a joint part that connects the core parts, and at least one end in the longitudinal direction is divided at the joint part (Patent Document) 2). This bristle material for brushes was able to set the bristle and waist strongly by arbitrarily setting the difference between the thickness of the joint portion and the thickness of the core portion.

また、剛性度が１２００kg/cm²〜５０００kg/cm²の熱可塑性樹脂で構成された分岐形状の断面をなす発泡糸で、発泡倍率が１．１〜１．７倍であるブラシ用毛材に使用する発泡糸がある（特許文献３）。 Further, a foamed yarn stiffness forms a section of branch shape made of a thermoplastic resin ^{^{1200kg / cm 2 ~5000kg / cm 2}} , the bristles brush expansion ratio is 1.1 to 1.7 times There is a foam yarn to be used (Patent Document 3).

特開２００９−１７２７２４号公報JP 2009-172724 A 特開２００７−５０４９７号公報JP 2007-50497 A 特公平６−２１３７１号公報Japanese Examined Patent Publication No. 6-21371

しかしながら、上記特許文献１に開示されている技術においては、先割れ部を形成するために、ある程度大きな機械的応力（バリ取りや研磨などにおける機械的応力）を負荷させる必要があるので、軽度な洗浄や磨き、清掃等の小さな機械的応力では先割れ部が形成され難いという課題を有していた。また、特許文献１に開示されているブラシ用毛材は、多葉断面のモノフィラメントである為、機械的応力の負荷のかかり方により、先割れ部の形成状態にばらつきや不均一さが発生するという課題を有していた。 However, in the technique disclosed in Patent Document 1, it is necessary to apply a certain degree of mechanical stress (mechanical stress in deburring, polishing, etc.) to form the cracked portion. There was a problem that the cracked portion was difficult to be formed by a small mechanical stress such as cleaning, polishing, and cleaning. Moreover, since the bristle material for brushes disclosed in Patent Document 1 is a monofilament having a multi-leafed cross section, variation and non-uniformity occur in the formation state of the cracked portion depending on how mechanical stress is applied. It had the problem that.

また、上記特許文献２に開示されている技術においては、先割れ部が結合部に限定されるため、微細な先割れ部を形成することが困難であるという課題を有していた。 Moreover, in the technique currently disclosed by the said patent document 2, since the tip crack part is limited to a coupling | bond part, it had the subject that it was difficult to form a fine tip crack part.

また、上記特許文献３に開示されている技術においては、発泡糸が分岐形状の断面をなしているので、ブラシ回転時に加わる衝撃を吸収、分散することが難しいことから、発泡糸が摩耗し易くなり、分岐形状の断面を維持することが難しかった。その為、水付着性が悪くなり、洗浄効果を低下させると共に、被洗浄面に打痕傷を発生させ易くなるという課題を有していた。 In the technique disclosed in Patent Document 3, since the foamed yarn has a branched cross section, it is difficult to absorb and disperse the impact applied during the rotation of the brush. Therefore, it was difficult to maintain a branched cross section. For this reason, there is a problem that the water adhesion is deteriorated, the cleaning effect is lowered, and a dent scar is easily generated on the surface to be cleaned.

本発明は、上記のような課題を解決する為になされたもので、被洗浄面に打痕傷や細かな傷を付けることが無く、高い洗浄性が発揮される各種洗浄ブラシ、各種清掃ブラシに使用されるブラシ用毛材を提供することを目的としている。 The present invention has been made in order to solve the above-described problems. Various cleaning brushes and various cleaning brushes that exhibit high detergency without causing scratches or fine scratches on the surface to be cleaned. It aims at providing the bristle material for brushes used for the hair.

上記従来の課題を解決する為に、請求項１の発明は、熱可塑性樹脂で構成された複数本の概柱形状からなるモノフィラメント発泡糸が溶融接合された接合部を有して集束されマルチフィラメント状に形成されていると共に、外力によって、接合された前記モノフィラメント発泡糸同士が前記接合部あるいは前記接合部近傍から分離可能であることを特徴としている。したがって、ブラシ用毛材に外力が加わると、接合部が分離して再びモノフィラメント発泡糸が形成される。その為、被洗浄面への衝撃を吸収、分散させることができるため、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。 In order to solve the above-mentioned conventional problems, the invention of claim 1 is characterized in that a plurality of monofilament foamed yarns made of a thermoplastic resin and having a substantially columnar shape are joined together by a fusion joint and are multifilaments. The monofilament foamed yarns joined together can be separated from the joined part or the vicinity of the joined part by an external force. Therefore, when an external force is applied to the bristle material for the brush, the joint portion is separated and a monofilament foam yarn is formed again. For this reason, the impact on the surface to be cleaned can be absorbed and dispersed, so that it is difficult to generate dents or fine scratches on the surface to be cleaned.

請求項２の発明は、請求項１に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材の断面は複数のモノフィラメント発泡糸の間に空隙部が形成されていることを特徴としている。したがって、空隙部によって外力を吸収、分散させることができる。 According to a second aspect of the present invention, in the bristle material for a brush having the configuration according to the first aspect, a cross section of the bristle material for the brush has a gap formed between a plurality of monofilament foamed yarns. . Therefore, the external force can be absorbed and dispersed by the gap.

請求項３の発明は、請求項１又は２に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材の断面はモノフィラメント発泡糸の外縁に表皮層が形成されていると共に、隣接する前記モノフィラメント発泡糸の表皮層同士が互いに接合された接合部を有することを特徴としている。したがって、表皮層からなる接合部は、互いの表皮層がはがれやすく弱いことから、外力によって分離し易くすることができる。 According to a third aspect of the present invention, in the bristle material for a brush having the structure according to the first or second aspect, the cross-section of the bristle material for the brush has an outer skin layer formed on the outer edge of the monofilament foam yarn, and the adjacent The skin layers of the monofilament foamed yarn have a joint part joined to each other. Therefore, the joint portion composed of the skin layers can be easily separated by an external force because the skin layers are easily peeled off and weak.

請求項４の発明は、請求項１〜３のいずれか１項に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材の断面は中央部にモノフィラメント発泡糸を有し、該中央部のモノフィラメント発泡糸の周りに複数のモノフィラメント発泡糸が接合部を有して形成されていることを特徴としている。したがって、ブラシ毛材の曲げ方向への方向性が無く、均等な曲げ反発性を保持することができる為、被洗浄面をムラなく洗浄することが出来、洗い残しを低減させることができる。 The invention of claim 4 is the bristle material for brushes having the configuration according to any one of claims 1 to 3, wherein the cross-section of the bristle material for brushes has a monofilament foamed yarn at the center part, and the center part A plurality of monofilament foamed yarns are formed with joints around the monofilament foamed yarn. Therefore, the brush bristle material does not have a direction in the bending direction, and uniform bending resilience can be maintained, so that the surface to be cleaned can be cleaned evenly, and unwashed residue can be reduced.

請求項５の発明は、請求項１〜４のいずれか１項に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材の断面は中央部にモノフィラメント発泡糸を有し、該中央部のモノフィラメント発泡糸の周りに複数のモノフィラメント発泡糸が接合部を有して形成されていると共に、隣接する前記複数のモノフィラメント発泡糸が互いに接触した接触部を有することを特徴としている。したがって、接合部と接触部とを有することによって、マルチフィラメント状における断面変形を容易にし、接合されていない接触部にて外力を吸収、分散させることができる。 A fifth aspect of the present invention is the brush bristle material having the structure according to any one of the first to fourth aspects, wherein a cross section of the brush bristle material has a monofilament foamed yarn at a central portion, and the central portion. A plurality of monofilament foamed yarns are formed around the monofilament foamed yarn with joints, and adjacent monofilament foamed yarns have contact portions in contact with each other. Therefore, by having a joint part and a contact part, cross-sectional deformation in a multifilament shape can be facilitated, and an external force can be absorbed and dispersed at the contact part that is not joined.

請求項６の発明は、請求項１〜３のいずれか１項に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材の断面は複数のモノフィラメント発泡糸を数珠状に形成し、中央部に中空部を設けたことを特徴としている。したがって、中空部によって外力を吸収、分散させることができると共に、扁平等の断面変形が容易となり、被洗浄面への接触面積を増加させることができる。 The invention according to claim 6 is the bristle material for brushes having the configuration according to any one of claims 1 to 3, wherein the cross-section of the bristle material for brushes is formed with a plurality of monofilament foamed yarns in a bead shape, It is characterized in that a hollow part is provided in the part. Therefore, external force can be absorbed and dispersed by the hollow portion, and cross-sectional deformation such as flattening is facilitated, and the contact area to the surface to be cleaned can be increased.

請求項７の発明は、請求項１〜３のいずれか１項に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材の断面は複数のモノフィラメント発泡糸を略Ｃ字形状に形成し、開口部を設けたことを特徴としている。したがって、開口部によって、外力を吸収、分散させることができると共に、水分を保持することができる。 A seventh aspect of the present invention is the brush bristle material having the structure according to any one of the first to third aspects, wherein a cross section of the bristle material for the brush is formed with a plurality of monofilament foamed yarns in a substantially C shape. The opening portion is provided. Accordingly, the opening can absorb and disperse external force and can retain moisture.

請求項８の発明は、請求項１〜７のいずれか１項に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材は接合されている複数のモノフィラメント発泡糸が互いに分離した分岐部を有することを特徴としている。したがって、マルチフィラメント状の腰の強さと、分岐部により分離されたモノフィラメント状の柔らかさ、しなやかさ等の作用が相まって、こびりついたしつこい汚れ等を洗浄、除去できると共に、被洗浄面への衝撃を吸収、分散させることができるため、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。 Invention of Claim 8 is a bristle material for brushes which comprises the composition according to any one of claims 1 to 7, wherein the bristle material for brushes is a branched portion where a plurality of monofilament foamed yarns joined to each other are separated from each other It is characterized by having. Therefore, the strength of the multifilament waist and the softness and suppleness of the monofilament separated by the branching part combine to wash and remove stubborn and persistent dirt, etc., while also impacting the surface to be cleaned. Since they can be absorbed and dispersed, it is possible to make it difficult to generate dents and fine scratches on the surface to be cleaned.

請求項９の発明は、請求項１〜８のいずれか１項に記載の構成よりなるブラシ用毛材において、前記ブラシ用毛材はモノフィラメント発泡糸が長手方向に長尺な気泡を有することを特徴としている。したがって、長尺な気泡により、モノフィラメント発泡糸を、さらに微細に分岐させた先割れ部を形成させることが容易となり、この先割れ部によって、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。 The invention of claim 9 is the bristle material for brushes having the structure according to any one of claims 1 to 8, wherein the bristle material for brushes has a monofilament foamed yarn having long bubbles in the longitudinal direction. It is a feature. Therefore, it becomes easy to form a cracked portion where the monofilament foamed yarn is further finely branched due to the long air bubbles, and it is difficult for the cracked portion to generate a dent or a fine scratch on the surface to be cleaned. can do.

請求項１の発明は、分岐部で被洗浄面への衝撃を吸収、分散させることができるため、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。また、請求項２の発明は、空隙部によって外力を吸収、分散させることができる。また、請求項３の発明は、外力によって分岐部を形成し易くすることができる。また、請求項４の発明は、洗浄面をムラなく洗浄することが出来、洗い残しを低減させることができる。また、請求項５の発明は、接合されていない接触部にて外力を吸収、分散させることができる。また、請求項６の発明は、中空部によって外力を吸収、分散させることができると共に、接触面積を増加できる。また、請求項７の発明は、略Ｃ字形状のモノフィラメント発泡糸によって、外力を吸収、分散させることができると共に、水分を保持することができる。また、請求項８及び９の発明は、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。 The invention according to claim 1 can absorb and disperse the impact on the surface to be cleaned at the branch portion, so that it is difficult to generate dents and fine scratches on the surface to be cleaned. Moreover, the invention of claim 2 can absorb and disperse the external force by the gap. Further, the invention of claim 3 can facilitate the formation of the branch portion by an external force. Further, the invention of claim 4 can clean the cleaning surface without unevenness, and can reduce unwashed residue. Moreover, the invention of claim 5 can absorb and disperse the external force at the non-joined contact portion. The invention according to claim 6 can absorb and disperse the external force by the hollow portion and can increase the contact area. Further, the invention of claim 7 can absorb and disperse external force and retain moisture by the substantially C-shaped monofilament foam yarn. In the inventions of claims 8 and 9, it is possible to make it difficult to generate dents and fine scratches on the surface to be cleaned.

本発明の第１実施形態を示す斜視図The perspective view which shows 1st Embodiment of this invention. （ａ）本発明の第１実施形態を示す断面図（ｂ）本発明の第２実施形態を示す断面図(A) Cross-sectional view showing the first embodiment of the present invention (b) Cross-sectional view showing the second embodiment of the present invention 本発明の第３実施形態を示す断面図Sectional drawing which shows 3rd Embodiment of this invention. 本発明の第４実施形態を示す断面図Sectional drawing which shows 4th Embodiment of this invention 本発明の第５実施形態を示す斜視図The perspective view which shows 5th Embodiment of this invention. 本発明の第６実施形態を示す斜視図The perspective view which shows 6th Embodiment of this invention. （ａ）本発明の第７実施形態における延伸前を示す断面図、（ｂ）（ａ）の延伸後を示す断面図(A) Sectional drawing which shows before extending | stretching in 7th Embodiment of this invention, (b) Sectional drawing which shows after extending | stretching of (a) 本発明の第８実施形態を示す断面図Sectional drawing which shows 8th Embodiment of this invention. 本発明の第９実施形態を示す斜視図The perspective view which shows 9th Embodiment of this invention. 本発明に係るブラシ用毛材を使用した回転ブラシを示す斜視図The perspective view which shows the rotating brush which used the bristle material for brushes concerning this invention 本発明に係るブラシ用毛材を使用したチャンネルブラシを示す断面図Sectional drawing which shows the channel brush which uses the bristle material for brushes concerning this invention 本発明に係るブラシ用毛材を使用した洗車機を示す正面図The front view which shows the car wash machine using the bristle material for brushes concerning this invention 本発明の第１０実施形態を示す断面図Sectional drawing which shows 10th Embodiment of this invention. 本発明の第１１実施形態を示す断面図Sectional drawing which shows 11th Embodiment of this invention 本発明の第１２実施形態を示す断面図Sectional drawing which shows 12th Embodiment of this invention 本発明の第１３実施形態を示す断面図Sectional drawing which shows 13th Embodiment of this invention

図１は、本発明の第１実施形態を示す斜視図であり、図２（ａ）は、同断面図である。第１実施形態に係るブラシ用毛材１は、断面略円形の中央のモノフィラメント発泡糸３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸２、３は、概柱形状を有している。そして、中央のモノフィラメント発泡糸３は、周囲のモノフィラメント発泡糸２との間に接合部２ａを有している。また、周囲のモノフィラメント発泡糸２、２同士の間にも接合部２ｂを有している。上記構成からなるブラシ用毛材１は、外力が加わると、接合部２ａ及び２ｂが分離してモノフィラメント状の分岐部が形成され、この分岐部で被洗浄面への衝撃を吸収、分散させることができるため、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。また、ブラシ用毛材１は、モノフィラメント発泡糸２、３が溶融接合されて接合部２ａ及び２ｂが形成されているが、溶融接合とは、モノフィラメント発泡糸同士が完全固化する前に、互いに接合される状態をいう。また、溶融接合の方法として、完全固化後の状態でモノフィラメント発泡糸同士に振動を与え、互いに溶融させて接合する方法も採用できる。さらにまた、ブラシ用毛材１は、外力にて接合されたモノフィラメント発泡糸同士が接合部あるいは接合部近傍から分離可能であるが、外力についての方法は、例えば、ブラシ用毛材の使用時の衝撃とか、モノフィラメント発泡糸同士が、接合された状態で、押し潰し等により、先端部をほぐし、接合部を分離させる方法等がある。 FIG. 1 is a perspective view showing a first embodiment of the present invention, and FIG. 2A is a cross-sectional view thereof. The bristle material 1 for brushes according to the first embodiment has a monofilament foam yarn 2 having a substantially circular cross section around the central monofilament foam yarn 3 having a substantially circular cross section, and is converged to form a multifilament shape. Is formed. The monofilament foamed yarns 2 and 3 have a substantially columnar shape. The central monofilament foamed yarn 3 has a joint 2 a between the peripheral monofilament foamed yarn 2. Moreover, it has the junction part 2b also between the surrounding monofilament foaming yarns 2 and 2. FIG. When an external force is applied to the brush bristle material 1 having the above-described configuration, the joint portions 2a and 2b are separated to form a monofilament-shaped branch portion, and this branch portion absorbs and disperses the impact on the surface to be cleaned. Therefore, it is possible to make it difficult to generate dents and fine scratches on the surface to be cleaned. Further, the bristle material 1 for brushes is formed by melting and joining the monofilament foamed yarns 2 and 3 to form joined portions 2a and 2b. In the melt joining, the monofilament foamed yarns are joined together before they are completely solidified. The state to be done. Further, as a method of fusion bonding, a method of applying vibration to the monofilament foamed yarns after being completely solidified and melting them to join can also be adopted. Furthermore, the bristle material 1 for brushes can separate the monofilament foamed yarns joined by external force from the joint part or the vicinity of the joint part. The method for the external force is, for example, when using the bristle material for brushes. For example, there is a method of loosening the tip part by crushing or the like and separating the joined part in a state where the impact or the monofilament foamed yarns are joined together.

また、ブラシ用毛材１の、モノフィラメント発泡糸２、３間には、空隙部２ｃが形成されている。この空隙部２ｃによって、外力を吸収、分散させることができる。 A gap 2c is formed between the monofilament foamed yarns 2 and 3 of the brush bristle material 1. The void 2c can absorb and disperse external force.

図２（ｂ）は、本発明の第２実施形態を示す断面図である。第２実施形態に係るブラシ用毛材１１は、断面略六角形の中央のモノフィラメント発泡糸１３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸１２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸１２、１３は、第１実施形態と同様に、概柱形状を有している。そして、中央のモノフィラメント発泡糸１３は、周囲のモノフィラメント発泡糸１２との間に接合部１２ａを有している。また、周囲のモノフィラメント発泡糸１２、１２同士の間にも接合部１２ｂを有している。 FIG. 2B is a cross-sectional view showing a second embodiment of the present invention. In the brush bristle material 11 according to the second embodiment, a monofilament foam yarn 12 having a substantially circular cross section is disposed so as to surround the center of the monofilament foam yarn 13 having a substantially hexagonal cross section. It is formed in a shape. Moreover, the monofilament foaming yarns 12 and 13 have a substantially columnar shape as in the first embodiment. The central monofilament foam yarn 13 has a joint 12 a between the monofilament foam yarn 12 and the surrounding monofilament foam yarn 12. Moreover, it has the junction part 12b also between the surrounding monofilament foaming yarns 12 and 12.

図３は、本発明の第３実施形態を示す断面図である。第３実施形態に係るブラシ用毛材２１は、断面略円形の中央のモノフィラメント発泡糸２３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸２２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸２２、２３は、概柱形状を有している。また、中央のモノフィラメント発泡糸２３と、周囲のモノフィラメント発泡糸２２の外周面には、表皮層２４が形成されている。そして、中央のモノフィラメント発泡糸２３は、周囲のモノフィラメント発泡糸２２との間に接合部２２ａを有している。また、周囲のモノフィラメント発泡糸２２、２２同士の間にも接合部２２ｂを有している。この接合部２２ａ及び２２ｂは、表皮層２４、２４同士が接合しているものである。また、モノフィラメント発泡糸２２、２３は、外部から冷却されていく為、表皮層２４は、内部よりも密度が高い状態にて形成される。 FIG. 3 is a cross-sectional view showing a third embodiment of the present invention. The bristle material 21 for brushes according to the third embodiment has a monofilament foam yarn 22 having a substantially circular cross section surrounding the monofilament foam yarn 23 having a substantially circular cross section. Is formed. Moreover, the monofilament foaming yarns 22 and 23 have a substantially columnar shape. A skin layer 24 is formed on the outer peripheral surfaces of the central monofilament foam yarn 23 and the surrounding monofilament foam yarn 22. The central monofilament foam yarn 23 has a joint 22 a between the monofilament foam yarn 22 and the surrounding monofilament foam yarn 22. Moreover, it has the junction part 22b also between the surrounding monofilament foaming yarns 22 and 22. The joint portions 22a and 22b are formed by joining the skin layers 24 and 24 together. Moreover, since the monofilament foamed yarns 22 and 23 are cooled from the outside, the skin layer 24 is formed in a state where the density is higher than the inside.

上記構成からなるブラシ用毛材２１は、外力が加わると、接合部２２ａ及び２２ｂが分離してモノフィラメント状の分岐部が形成され、この分岐部で被洗浄面への衝撃を吸収、分散させることができるため、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。また、接合部２２ａ及び２２ｂは表皮層２４、２４同士が接合しているものなので互いの表皮層２４が剥がれやすく弱いことから、外力によって分岐部を形成し易くしている。ここで表皮層２４とは、モノフィラメント発泡糸２２、２３の表面に形成される内部よりも密度の高い層のことである。形成された表皮層２４は、表皮層２４と内部の境界より分離して分岐部を形成し易い傾向になる。また、接合部２２ａ及び２２ｂの接合力を設定する事により、互いの表皮層２４が分離するようにすることもできる。 When an external force is applied to the brush bristle material 21 having the above-described configuration, the joint portions 22a and 22b are separated to form a monofilament-shaped branch portion, and this branch portion absorbs and disperses the impact on the surface to be cleaned. Therefore, it is possible to make it difficult to generate dents and fine scratches on the surface to be cleaned. In addition, since the skin layers 24 and 24 are joined to each other in the joint portions 22a and 22b, the skin layers 24 are easily peeled off and weak, so that a branch portion is easily formed by an external force. Here, the skin layer 24 is a layer having a higher density than the inside formed on the surfaces of the monofilament foamed yarns 22 and 23. The formed skin layer 24 tends to be easily separated from the skin layer 24 and the inner boundary to form a branched portion. In addition, the skin layers 24 can be separated from each other by setting the bonding force of the bonding portions 22a and 22b.

また、ブラシ用毛材２１の、モノフィラメント発泡糸２２、２３間には、空隙部２２ｃが形成されている。この空隙部２２ｃによって、外力を吸収、分散させることができる。 Further, a gap 22c is formed between the monofilament foamed yarns 22 and 23 of the brush bristle material 21. The void 22c can absorb and disperse external force.

図４は、本発明の第４実施形態を示す断面図である。第４実施形態に係るブラシ用毛材３１は、断面多角形の中央のモノフィラメント発泡糸３３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸３２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸３２、３３は、第１実施形態と同様に、概柱形状を有している。そして、中央のモノフィラメント発泡糸３３は、周囲のモノフィラメント発泡糸３２との間に接合部３２ａを有している。また、周囲のモノフィラメント発泡糸３２、３２同士の間には接触部３２ｂが形成されている。また、ブラシ用毛材３１の、モノフィラメント発泡糸３２、３３間には、空隙部３２ｃが形成されている。この空隙部３２ｃによって、外力を吸収、分散させることができる。 FIG. 4 is a cross-sectional view showing a fourth embodiment of the present invention. The bristle material for brush 31 according to the fourth embodiment includes a monofilament foam yarn 32 having a substantially circular cross section arranged so as to surround the periphery of the monofilament foam yarn 33 having a polygonal cross section. Is formed. Moreover, the monofilament foaming yarns 32 and 33 have a substantially columnar shape as in the first embodiment. The central monofilament foam yarn 33 has a joint 32 a between the monofilament foam yarn 32 and the surrounding monofilament foam yarn 32. Further, a contact portion 32b is formed between the surrounding monofilament foamed yarns 32, 32. In addition, a gap 32c is formed between the monofilament foamed yarns 32 and 33 of the brush bristle material 31. The voids 32c can absorb and disperse external forces.

ここで、接合部３２ａは、ブラシ用毛材３１の長手方向に接触面が形成されることから、接合力は強い。一方、接触部３２ｂは、隣接する周囲のモノフィラメント発泡糸３２同士が互いに接触はしているが、接合はされていない状態である。 Here, since the contact surface is formed in the longitudinal direction of the bristle material 31 for brushes, the joining part 32a has a strong joining force. On the other hand, in the contact portion 32b, adjacent monofilament foam yarns 32 adjacent to each other are in contact with each other, but are not joined.

図５は、本発明の第５実施形態を示す斜視図である。第５実施形態に係るブラシ用毛材４１は、断面略円形の中央のモノフィラメント発泡糸４３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸４２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸４２、４３は、概柱形状を有している。そして、中央のモノフィラメント発泡糸４３は、周囲のモノフィラメント発泡糸４２との間に接合部４２ａを有している。また、周囲のモノフィラメント発泡糸４２、４２同士の間にも接合部４２ｂを有している。さらに、周囲のモノフィラメント発泡糸４２は、捩られて螺旋状部４４が形成されている。 FIG. 5 is a perspective view showing a fifth embodiment of the present invention. The bristle material 41 for brushes according to the fifth embodiment has a monofilament foam yarn 42 with a substantially circular cross section surrounding the periphery of the central monofilament foam yarn 43 with a substantially circular cross section. Is formed. The monofilament foamed yarns 42 and 43 have a substantially columnar shape. The central monofilament foam yarn 43 has a joint portion 42 a between the monofilament foam yarn 42 and the surrounding monofilament foam yarn 42. Moreover, it has the junction part 42b also between the surrounding monofilament foaming yarns 42 and 42 mutually. Further, the surrounding monofilament foam yarn 42 is twisted to form a spiral portion 44.

図６は、本発明の第６実施形態を示す斜視図である。第６実施形態に係るブラシ用毛材５１は、断面略円形の中央のモノフィラメント発泡糸５３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸５２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸５２、５３は、概柱形状を有している。そして、中央のモノフィラメント発泡糸５３は、周囲のモノフィラメント発泡糸５２との間に、接合部を有している。また、周囲のモノフィラメント発泡糸５２、５２同士の間にも接合部を有している。 FIG. 6 is a perspective view showing a sixth embodiment of the present invention. The bristle material for brush 51 according to the sixth embodiment has a monofilament foam yarn 52 having a substantially circular cross section surrounding the periphery of a monofilament foam yarn 53 having a substantially circular cross section, and is converged to form a multifilament shape. Is formed. The monofilament foamed yarns 52 and 53 have a substantially columnar shape. The central monofilament foam yarn 53 has a joint portion with the surrounding monofilament foam yarn 52. Moreover, it has a junction part also between the surrounding monofilament foaming yarns 52 and 52. FIG.

そして、ブラシ用毛材５１の長手方向の一方の端部には、モノフィラメント発泡糸５２、５３の接合部が分離され、分岐部５４が形成されている。さらに、分岐部５４よりも先端側には先割れ部５５が形成されている。したがって、分岐部５４により、被洗浄面への衝撃を吸収、分散させることができる。また、分岐部５４及び先割れ部５５によって、被洗浄面に打痕傷や細かな傷を発生し難くすることができる。 Then, at one end portion in the longitudinal direction of the bristle material 51 for the brush, the joint portion of the monofilament foamed yarns 52 and 53 is separated, and a branch portion 54 is formed. Furthermore, a tip crack portion 55 is formed on the tip side of the branch portion 54. Therefore, the branch part 54 can absorb and disperse the impact on the surface to be cleaned. Further, the branch portion 54 and the tip crack portion 55 can make it difficult to generate dents and fine scratches on the surface to be cleaned.

図７は、本発明の第７実施形態を示す縦断面図である。第７実施形態に係るブラシ用毛材を構成するモノフィラメント発泡糸２又は３の内部には、図７（ａ）に示すように、多数の気泡４、４が形成されている。この気泡４、４は、後述する延伸を施すことによって、図７（ｂ）に示すように、モノフィラメント発泡糸２又は３の長手方向に延びる長尺な気泡４ａ、４ａに変形される。このように長尺な気泡４ａ、４ａとなることによって、ブラシ用毛材に外力が加わると、裂け易くなり、第６実施形態で説明した先割れ部５５を容易に形成させることができる。 FIG. 7 is a longitudinal sectional view showing a seventh embodiment of the present invention. As shown in FIG. 7A, a large number of bubbles 4 and 4 are formed inside the monofilament foam yarn 2 or 3 constituting the bristle material for a brush according to the seventh embodiment. The bubbles 4 and 4 are deformed into elongated bubbles 4a and 4a extending in the longitudinal direction of the monofilament foam yarn 2 or 3 as shown in FIG. Thus, when it becomes long bubble 4a, 4a, when external force is added to the bristle material for brushes, it will become easy to tear and the tip crack part 55 demonstrated in 6th Embodiment can be formed easily.

尚、ブラシ用毛材には低密度ポリエチレン樹脂が使用されているが、ブラシ用毛材を形成する低密度ポリエチレン樹脂の曲げ弾性率は、約３７０ＭＰａであるが、使用目的に応じて、１２０ＭＰａ〜１０００ＭＰａの熱可塑性樹脂を、適宜、採用できる。 In addition, although the low density polyethylene resin is used for the bristle material for brushes, although the bending elastic modulus of the low density polyethylene resin which forms the bristle material for brushes is about 370 MPa, depending on a use purpose, 120 MPa- A 1000 MPa thermoplastic resin can be appropriately employed.

また、ブラシ用毛材は、約５０００デニールであるが、使用目的に応じて、３０００デニール〜２００００デニールの設定を、適宜、採用できる。なお、デニールとは合成樹脂あるいは化学繊維の太さを示す単位のことであり、９０００m当たりの重さが１ｇのものを１デニールという。 Moreover, although the bristle material for brushes is about 5000 denier, the setting of 3000 denier-20000 denier can be suitably employ | adopted according to the intended purpose. Denier is a unit indicating the thickness of a synthetic resin or chemical fiber, and one having a weight per 9000 m of 1 g is referred to as 1 denier.

ブラシ用毛材を形成する樹脂は、低密度ポリエチレン樹脂以外にも、各種ポリエチレン樹脂、ポリプロピレン樹脂、エチレン酢酸ビニル樹脂、エチレンメチルアクリレート樹脂、エチレンブチルアクリレート樹脂等のポリオレフィン系樹脂、あるいはウレタン樹脂が採用できる。 In addition to low-density polyethylene resin, polyolefin resin such as various polyethylene resins, polypropylene resin, ethylene vinyl acetate resin, ethylene methyl acrylate resin, ethylene butyl acrylate resin, or urethane resin is used as the resin that forms the brush hair material. it can.

次に、ブラシ用毛材の製造方法について説明する。まず、ブラシ用毛材を形成する低密度ポリエチレン樹脂に、あらかじめ発泡剤を混入しておき、押出機（図示せず）の先端に取り付けられた複数の口金を通して押し出されることにより複数のモノフィラメント発泡糸が形成される。押し出し後、互いのモノフィラメント発泡糸同士を完全固化前の状態にて接合させる。その後、加熱しながら延伸機にて長手方向に延伸をかけ、延伸後、アニーリングと呼ばれる工程にて冷却固化させることにより形成される。ところで、一般的には、樹脂の成形技術には、溶融成形、固層成形、注型成形、射出成形、真空成形、圧空成形、プレス成形等があるが、前記の如くの製造方法は、溶融成形の一種の押出成形と呼ばれている。 Next, the manufacturing method of the bristle material for brushes is demonstrated. First, a foaming agent is mixed in the low-density polyethylene resin forming the hair material for the brush, and a plurality of monofilament foamed yarns are extruded through a plurality of caps attached to the tip of an extruder (not shown). Is formed. After extrusion, the monofilament foamed yarns are joined together in a state before complete solidification. Thereafter, the film is stretched in the longitudinal direction with a stretching machine while being heated, and after stretching, it is formed by cooling and solidifying in a process called annealing. By the way, in general, resin molding techniques include melt molding, solid layer molding, cast molding, injection molding, vacuum molding, pressure forming, press molding, and the like. This is called extrusion molding.

また、長手方向に延伸させる上記の如くの方法は、一軸延伸と呼ばれている。一軸延伸とは、一方向にのみ延伸応力をかける加工方法であり、延伸方向にたいして平行の方向は、分子配向が起こるので、引張強さが著しく向上するが、延伸方向にたいして直角の方向は、引張強さが向上しない為、延伸方向にたいして平行の方向に、裂けやすくなるという性質を有している。その為、ブラシ用毛材は、先割れ部を形成することが可能となる。なお、分子配向とは、線状分子が溶融または固体状態において、外力の作用により、一定方向に配列することである。また、先割れ部の形成方法は、ブラシ用毛材の両側先端部の所定長さを、所定回転速度の分割刃やカッターを有する先割れ加工機にて先割れ加工することにより形成される。 The above-described method of stretching in the longitudinal direction is called uniaxial stretching. Uniaxial stretching is a processing method in which stretching stress is applied only in one direction. In the direction parallel to the stretching direction, molecular orientation occurs, so the tensile strength is remarkably improved. However, the direction perpendicular to the stretching direction is tensile. Since the strength is not improved, it has the property of being easily torn in a direction parallel to the stretching direction. Therefore, the bristle material for brushes can form a tip crack portion. The molecular orientation means that linear molecules are arranged in a certain direction by the action of an external force in a molten or solid state. Moreover, the formation method of a front crack part is formed by carrying out the front crack processing of the predetermined length of the both-ends front part of the bristle material for brushes with the front crack processing machine which has the division blade and cutter of predetermined rotation speed.

ブラシ用毛材の製造時に使用する発泡剤には、重炭酸ナトリウム、重炭酸アンモニウム、アゾジカルボンアミド、ベンゼンスルホニルヒドラジド、Ｎ，Ｎ´−ジニトロソペンタメチレンテトラミン、トルエンスルホニルヒドラジド、４，４´−オキシビスベンゼンスルホニルヒドラジド等の熱分解型発泡剤がある。 Examples of the foaming agent used in the production of the brush hair material include sodium bicarbonate, ammonium bicarbonate, azodicarbonamide, benzenesulfonyl hydrazide, N, N'-dinitrosopentamethylenetetramine, toluenesulfonyl hydrazide, 4,4'- There are thermal decomposable foaming agents such as oxybisbenzenesulfonyl hydrazide.

また、ブラシ用毛材の発泡倍率は、１．１〜２．０倍程度が好適であり、１．３倍程度が、より好適である。尚、発泡倍率とは、ＪＩＳ−Ｋ７１１２（水中置換法）により、発泡でないもの（非発泡）と発泡の密度を各々測定して、発泡倍率＝ρ_０／ρ_１で求めた値をいう。但し、ρ_０は非発泡の密度で、ρ_１は発泡の密度である。 The foaming ratio of the brush hair material is preferably about 1.1 to 2.0 times, and more preferably about 1.3 times. The expansion ratio refers to a value obtained by measuring the density of non-foaming (non-foaming) and foaming according to JIS-K7112 (in-water substitution method) and obtaining the expansion ratio = ρ ₀ / ρ ₁ . However, ρ ₀ is the density of non-foaming and ρ ₁ is the density of foaming.

また、ブラシ用毛材の発泡における気泡率は、５〜３０％程度が好適であり、１０％程度が、より好適である。尚、気泡率とは、発泡部材の全体積中に占める気泡の体積の割合を示すものである。 Moreover, about 5-30% is suitable for the bubble rate in foaming of the bristle material for brushes, and about 10% is more suitable. In addition, a bubble rate shows the ratio of the volume of the bubble which occupies in the whole volume of a foaming member.

また、ブラシ用毛材の延伸倍率は、約５．０倍にて形成されているが、より好適には、５．０〜８．０倍程度である。 Moreover, although the draw ratio of the bristle material for brushes is formed at about 5.0 times, it is more preferably about 5.0 to 8.0 times.

ブラシ用毛材は、長手方向に高延伸させることで、高延伸させない通常品に比べ、延伸方向にたいして平行の方向に、分子配向が著しく起こるので、引張強さが著しく向上すると共に、延伸方向にたいして直角の方向は、引張強さが向上しない為、延伸方向にたいして平行の方向に、裂けやすくなるという性質を有している。その為、先割れ部が通常品に対し、より細かく細分割できる効果がある。先割れ部をより細かくすることで、洗浄面に対し洗浄時の衝撃を吸収、分散できる為、キズ、ブラシ痕が発生しない。また、先割れ部をより細かくすることで、被洗浄面の細かな凹凸部分にも当接することができ、洗浄性も良好である。なお、通常、高延伸とは、５倍以上の延伸倍率を指す。 As the brush bristle material is highly stretched in the longitudinal direction, molecular orientation occurs remarkably in a direction parallel to the stretching direction compared to a normal product that is not highly stretched. The perpendicular direction has the property that the tensile strength is not improved, so that it is easy to tear in a direction parallel to the stretching direction. Therefore, there is an effect that the cracked portion can be subdivided more finely than a normal product. By making the tip crack portion finer, it is possible to absorb and disperse the impact during cleaning on the cleaning surface, so scratches and brush marks do not occur. Further, by making the tip crack portion finer, it is possible to come into contact with fine uneven portions of the surface to be cleaned, and the cleaning property is also good. Normally, high stretching refers to a stretching ratio of 5 times or more.

また、発泡剤を添加して高延伸させた場合には、先ず、材料の中に気泡が形成される。形成された気泡は高延伸工程で延伸方向に引き伸ばされる。引き伸ばされた気泡は植物の茎のように延伸方向に長尺な形状に形成される。長尺な形状に形成された気泡を有するブラシ用毛材は裂けやすくなり先割れ部が高延伸させない通常品に対し、よりいっそう細かく細分割できる効果がある。また、長尺な気泡が形成されている為、ブラシ用毛材先端の先割れ部が摩耗しても、洗浄時の車体への衝撃時に先割れ部より細かく裂けが進行するため、先割れ部として消滅することが無い。その為、ブラシ寿命まで、もしくは長期に渡って、先割れ部が継続的に形成される為、キズの発生が無く、先割れ部が消滅することがない為、安定した洗浄性能を長期に亘って維持することができる。 Moreover, when a foaming agent is added and highly stretched, first, bubbles are formed in the material. The formed bubbles are stretched in the stretching direction in a high stretching process. The stretched bubbles are formed in a shape elongated in the stretching direction like a plant stem. The bristle material for brushes having air bubbles formed in a long shape is easy to tear, and has an effect that can be subdivided more finely than a normal product in which the cracked portion is not highly stretched. In addition, since long bubbles are formed, even if the tip crack part at the tip of the brush bristle material wears, the tip crack part progresses more finely than the tip crack part during impact on the vehicle body during cleaning. Will not disappear. Therefore, since the cracked part is continuously formed until the brush life or over a long period of time, there is no generation of scratches and the cracked part will not disappear. Can be maintained.

また、ブラシ用毛材の線径については、マルチフィラメント状の仮想外径で０．３〜３ｍｍが好適である。０．３ｍｍ以下では、洗浄等に必要とされる毛腰の確保が困難となり、３ｍｍ以上では洗浄ムラが発生し易くなる。 Moreover, about the wire diameter of the bristle material for brushes, 0.3-3 mm is suitable with a multifilament-like virtual outer diameter. If the thickness is 0.3 mm or less, it is difficult to secure the fluff required for cleaning and the like, and if it is 3 mm or more, uneven cleaning tends to occur.

また、ブラシ用毛材を構成するモノフィラメント発泡糸の線径については、ブラシ用毛材を構成するモノフィラメント発泡糸の本数により、適宜設定できるが、好適には、モノフィラメント発泡糸の仮想外径で、０．０５〜１．５ｍｍが好適である。０．０５ｍｍ以下では、製造時に毛切れ等が発生し易く、一定の品質を確保することが困難となり、１．５ｍｍ以上では、洗浄ムラが発生し易くなる。 Further, the wire diameter of the monofilament foam yarn constituting the brush bristle material can be appropriately set according to the number of monofilament foam yarns constituting the brush bristle material, but preferably the virtual outer diameter of the monofilament foam yarn, 0.05 to 1.5 mm is preferred. If it is 0.05 mm or less, hair breakage or the like is likely to occur during production, and it is difficult to ensure a certain quality, and if it is 1.5 mm or more, cleaning unevenness is likely to occur.

図８は、本発明の第８実施形態を示す断面図である。第８実施形態に係るブラシ用毛材６１は、断面十字状の中央のモノフィラメント発泡糸６３の先端部に、断面略円形の周囲のモノフィラメント発泡糸６２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸６２、６３は、第１実施形態と同様に、概柱形状を有している。そして、中央のモノフィラメント発泡糸６３は、周囲のモノフィラメント発泡糸６２との間に接合部６２ａを有している。断面十字状の中央のモノフィラメント発泡糸６３が形成されている為、ブラシ用毛材の毛腰を強く設定できる。また、なお、前記実施例においては、中央のモノフィラメント発泡糸６３は断面十字状の断面に形成されているが、上記以外にも、概三日月型等、採用できる。 FIG. 8 is a sectional view showing an eighth embodiment of the present invention. The brush bristle material 61 according to the eighth embodiment has a monofilament foam yarn 62 having a substantially circular cross section disposed at the tip of a central monofilament foam yarn 63 having a cross-shaped cross section, and converges to form a multifilament shape. Has been. Moreover, the monofilament foaming yarns 62 and 63 have a substantially columnar shape as in the first embodiment. The central monofilament foam yarn 63 has a joint 62 a between the monofilament foam yarn 62 and the surrounding monofilament foam yarn 62. Since the center monofilament foam yarn 63 having a cross-shaped cross section is formed, the bristle of the bristle material for the brush can be set strongly. In addition, in the said Example, although the center monofilament foaming yarn 63 is formed in the cross-section of cross-section, in addition to the above, a substantially crescent moon type etc. can be employ | adopted.

図９は、本発明の第９実施形態を示す斜視図である。第９実施形態に係るブラシ用毛材７１は、断面略円形の中央のモノフィラメント発泡糸７３の周囲を囲むように、断面略円形の周囲のモノフィラメント発泡糸７２が配置され、集束してマルチフィラメント状に形成されている。また、モノフィラメント発泡糸７２、７３は、第１実施形態と同様に、概柱形状を有している。そして、中央のモノフィラメント発泡糸７３は、周囲のモノフィラメント発泡糸７２との間に接合部７２ａを有している。また、周囲のモノフィラメント発泡糸７２、７２同士の間にも接合部７２ｂを有している。さらに、モノフィラメント発泡糸７２、７３は、長手方向に波形状部７４が形成されている。 FIG. 9 is a perspective view showing a ninth embodiment of the present invention. In the bristle material 71 for brushes according to the ninth embodiment, a monofilament foam yarn 72 having a substantially circular cross section is disposed so as to surround the center of the monofilament foam yarn 73 having a substantially circular cross section. Is formed. Moreover, the monofilament foaming yarns 72 and 73 have a substantially columnar shape as in the first embodiment. The central monofilament foam yarn 73 has a joint 72 a between the monofilament foam yarn 72 and the surrounding monofilament foam yarn 72. Moreover, it has the junction part 72b also between the surrounding monofilament foaming yarns 72 and 72 mutually. Further, the monofilament foamed yarns 72 and 73 are formed with wave-shaped portions 74 in the longitudinal direction.

図１０は、本発明に係るブラシ用毛材を使用した洗車機用洗浄ブラシを示す斜視図である。また、図１１は、本発明に係るブラシ用毛材を使用したチャンネルブラシを示す断面図である。洗車機用洗浄ブラシ１２０は、ブラシ用毛材１３３を芯線１３２、及び帯状体１３１にて挟み付けると共に、折り合わして形成された長尺形状のチャンネルブラシ１３０が、アルミニウム、鉄等の金属材料、あるいは塩化ビニル、ポリアセタール等の合成樹脂材料からなる略円筒形状の軸体１２３の外周部に螺旋状に巻き付けられると共に、チャンネルブラシ１３０の両端部に係止具１２５ａを覆い被せ、係止具１２５ａの両端部をネジ１２５ｂにて軸体１２３に固定して形成されている。 FIG. 10 is a perspective view showing a washing brush for a car wash machine using the brush bristle material according to the present invention. Moreover, FIG. 11 is sectional drawing which shows the channel brush which uses the bristle material for brushes based on this invention. The washing brush 120 for a car wash machine has a long channel brush 130 formed by sandwiching a bristle material 133 for a brush with a core wire 132 and a belt-like body 131 and a metal material such as aluminum or iron. Alternatively, it is spirally wound around the outer periphery of a substantially cylindrical shaft body 123 made of a synthetic resin material such as vinyl chloride or polyacetal, and the locking tool 125a is covered on both ends of the channel brush 130. Both ends are fixed to the shaft body 123 with screws 125b.

チャンネルブラシ１３０を構成する芯線１３２は、概丸形断面を有する略円柱形状で、アルミニウム、鉄等の金属材料からなる。また、帯状体１３１は、概コ字状断面を有する長尺形状で、アルミニウム、鉄等の金属材料からなる。ブラシ用毛材１３３は、分岐部１３６を有すると共に、端部に先割れ部１３５が形成された長尺形状であり、芯線１３２、及び帯状体１３１にて挟み付けられると共に、概Ｖ字断面を有するように折り合わされている。ブラシ用毛材１３３は、洗車機用洗浄ブラシ１２０の回転に伴い、先割れ部１３５、分岐部１３６にて分離されたモノフィラメント発泡糸、及びマルチフィラメント状に形成されたブラシ用毛材１３０の各部が被洗浄面に当接する。先割れ部１３５及びモノフィラメント発泡糸にて細かな汚れの洗浄ができると共に、マルチフィラメント状の箇所にて傷つくことなく洗浄できると共に、好適な毛腰を付与できる。また、被洗浄面の状態に応じて、先割れ部１３５及び分岐部１３６にて分離されたモノフィラメント発泡糸のみを被洗浄面に当接させることもできる。 The core wire 132 constituting the channel brush 130 has a substantially cylindrical shape with a substantially round cross section, and is made of a metal material such as aluminum or iron. The strip 131 has a long shape having a substantially U-shaped cross section and is made of a metal material such as aluminum or iron. The brush bristle material 133 has an elongated shape having a branching portion 136 and a tip crack portion 135 formed at the end, and is sandwiched between the core wire 132 and the belt-like body 131 and has a substantially V-shaped cross section. It is folded to have. The bristle material for brush 133 is a monofilament foamed yarn separated by a splitting part 135, a branching part 136, and each part of the bristle material for brush 130 formed in a multifilament shape as the washing brush 120 for a car wash machine rotates. Contacts the surface to be cleaned. It is possible to clean fine dirt with the front cracked portion 135 and the monofilament foamed yarn, and it is possible to clean without damaging the multifilament-shaped portion and to impart a suitable bristle waist. Further, depending on the state of the surface to be cleaned, only the monofilament foamed yarn separated by the tip crack portion 135 and the branch portion 136 can be brought into contact with the surface to be cleaned.

図１２は、本発明に係るブラシ用毛材を使用した洗車機を示す正面図である。図１２において、１２０は洗車機用洗浄ブラシ、１４０は洗車機、１４２は駆動源、１４３はノズル、１４４は乾燥機である。 FIG. 12 is a front view showing a car wash using the brush bristle material according to the present invention. In FIG. 12, 120 is a washing brush for a car wash machine, 140 is a car wash machine, 142 is a drive source, 143 is a nozzle, and 144 is a dryer.

洗車機１４０は、図１２の如く、本発明のブラシ用毛材を配した洗車機用洗浄ブラシ１２０が搭載されており、前記洗車機用洗浄ブラシ１２０は駆動源１４２により回転される。ノズル１４３からは、被洗浄面にたいして、洗浄剤、及び水が散布され、洗車機用洗浄ブラシ１２０により、洗浄され、洗浄後は洗車機１４０の乾燥手段である乾燥機１４４により被洗浄面が乾燥される。尚、洗車機１４０の回転数は、高速回転では、１００ｒｐｍ〜１５０ｒｐｍの範囲に設定されており、１２０ｒｐｍ程度が好適である。 As shown in FIG. 12, the car wash machine 140 is equipped with a car wash machine cleaning brush 120 provided with the brush bristle material of the present invention, and the car wash machine brush 120 is rotated by a drive source 142. From the nozzle 143, a cleaning agent and water are sprayed on the surface to be cleaned, and the surface is cleaned by the cleaning brush 120 for the car wash machine. After the cleaning, the surface to be cleaned is dried by the dryer 144 which is a drying means of the car wash machine 140. Is done. In addition, the rotation speed of the car wash machine 140 is set in the range of 100 rpm to 150 rpm in high speed rotation, and about 120 rpm is preferable.

本発明のブラシ用毛材を配した洗車機用洗浄ブラシ１２０を搭載した洗車機１４０の動作、作用は下記の通りである。 The operation and action of the car wash machine 140 equipped with the car wash machine cleaning brush 120 provided with the brush hair material of the present invention are as follows.

洗車機１４０は、被洗浄面である車体にたいして、打痕傷や細かな傷を付ける事が無く、且つ、高い洗浄性を兼ね備えた洗車機用洗浄ブラシ１２０が使用できる。その為、洗車機１４０は、洗車機用洗浄ブラシ１２０を高速回転に設定すると共に、洗浄時間を短時間に設定した場合においても、被洗浄面に傷が付着すること無く、且つ洗浄残りの無い高い洗浄性が付与される。また、洗車機用洗浄ブラシ１２０の回転を、低速回転から高速回転等に急変させた場合においても、前記と同様の作用が洗車機１４０に付与される。その為、被洗浄面である車体に傷を付けること無く、非常に高い洗浄性が発揮できる洗車機１４０を提供することができる。 The car wash machine 140 can use the washing brush 120 for a car wash machine that does not cause dents or fine scratches on the vehicle body that is the surface to be cleaned, and also has high cleanability. For this reason, the car wash machine 140 sets the car wash machine cleaning brush 120 to a high speed rotation, and even when the cleaning time is set to a short time, the surface to be cleaned is not damaged and there is no cleaning residue. High detergency is imparted. Further, even when the rotation of the washing brush 120 for a car wash machine is suddenly changed from a low speed rotation to a high speed rotation, the same action as described above is given to the car wash machine 140. Therefore, it is possible to provide the car wash machine 140 that can exhibit very high cleanability without damaging the vehicle body that is the surface to be cleaned.

図１３は、本発明の第１０実施形態を示す断面図である。第１０実施形態に係るブラシ用毛材８１は、複数のモノフィラメント発泡糸８２、８２同士を数珠状に形成し、中央部に中空部８３を形成している。また、モノフィラメント発泡糸８２、８２同士の間には、接合部８２ｂが形成されている。したがって、中空部によって外力を吸収、分散させることができると共に、被洗浄面への当接時における断面変形が容易となる為、扁平等に変形することにより、ブラシ用毛材８１の被洗浄面への接触面積を大きくすることができ、より確実に洗浄ができる。 FIG. 13 is a sectional view showing a tenth embodiment of the present invention. The brush bristle material 81 according to the tenth embodiment forms a plurality of monofilament foamed yarns 82 and 82 in a bead shape and forms a hollow portion 83 in the center. Further, a joining portion 82b is formed between the monofilament foamed yarns 82 and 82. Therefore, the external force can be absorbed and dispersed by the hollow portion, and the cross-sectional deformation at the time of contact with the surface to be cleaned is facilitated, so that the surface to be cleaned of the brush bristle material 81 is deformed flat. The contact area can be increased, and cleaning can be performed more reliably.

図１４は、本発明の第１１実施形態を示す断面図である。第１１実施形態に係るブラシ用毛材９１は、複数のモノフィラメント発泡糸９２、９２同士を略Ｃ字形状に形成し、開口部９３が形成されている。また、モノフィラメント発泡糸９２、９２同士の間には、接合部９２ｂが形成されている。したがって、開口部９３によって、外力を吸収、分散させることができると共に、水分を保持することができる。また、開口部９３が閉じて、接触状態になった場合においても、外力の吸収、分散、水分保持等の効果は著しく低下するものではない。 FIG. 14 is a sectional view showing an eleventh embodiment of the present invention. In the brush bristle material 91 according to the eleventh embodiment, a plurality of monofilament foamed yarns 92, 92 are formed in a substantially C shape, and an opening 93 is formed. Further, a joining portion 92b is formed between the monofilament foamed yarns 92, 92. Therefore, the opening 93 can absorb and disperse external force and can retain moisture. Even when the opening 93 is closed and brought into contact, the effects of absorption, dispersion, moisture retention, etc. of external force are not significantly reduced.

図１５は、本発明の第１２実施形態を示す断面図である。第１２実施形態に係るブラシ用毛材１０１は、断面略円形の中央のモノフィラメント発泡糸１０３の周囲に、断面略円形の周囲のモノフィラメント発泡糸１０２が配置されている。また、モノフィラメント発泡糸１０２、１０３は、概柱形状を有している。そして、中央のモノフィラメント発泡糸１０３は、周囲のモノフィラメント発泡糸１０２との間に接合部１０２ａを有している。一方、周囲のモノフィラメント発泡糸１０２、１０２同士の間は、接合されておらず、開口部１０２ｃが形成されている。したがって、開口部１０２ｃによって、外力を吸収、分散させることができると共に、水分を保持することができる。 FIG. 15 is a sectional view showing a twelfth embodiment of the present invention. In the brush bristle material 101 according to the twelfth embodiment, a monofilament foam yarn 102 having a substantially circular cross section is disposed around a central monofilament foam yarn 103 having a substantially circular cross section. The monofilament foamed yarns 102 and 103 have a substantially columnar shape. The central monofilament foam yarn 103 has a joint 102 a between the monofilament foam yarn 102 and the surrounding monofilament foam yarn 102. On the other hand, the surrounding monofilament foam yarns 102 are not joined to each other, and an opening 102c is formed. Therefore, the opening 102c can absorb and disperse external force and can retain moisture.

図１６は、本発明の第１３実施形態を示す断面図である。第１３実施形態に係るブラシ用毛材１１１は、断面略円形で大径の中央のモノフィラメント発泡糸１１３の周囲に、断面略円形で、中央のモノフィラメント発泡糸１１３の約３分の１の小径の周囲のモノフィラメント発泡糸１１２が配置されている。また、モノフィラメント発泡糸１１２、１１３は、概柱形状を有している。そして、中央のモノフィラメント発泡糸１１３は、周囲のモノフィラメント発泡糸１１２との間に接合部１１２ａを有している。一方、周囲のモノフィラメント発泡糸１１２、１１２同士の間は、接合されておらず、開口部１１２ｃが形成されている。したがって、開口部１１２ｃによって、外力を吸収、分散させることができると共に、水分を保持することができる。また、中央のモノフィラメント発泡糸１１３は、周囲のモノフィラメント発泡糸１１２よりも機械的強度が大である為、設定に応じて強い毛腰を付与できる。 FIG. 16 is a sectional view showing a thirteenth embodiment of the present invention. The brush bristle material 111 according to the thirteenth embodiment has a substantially circular cross-section and a large-diameter central monofilament foam yarn 113 around the central monofilament foam yarn 113 and a small diameter of about one third of the central monofilament foam yarn 113. A surrounding monofilament foam yarn 112 is arranged. The monofilament foamed yarns 112 and 113 have a substantially columnar shape. The central monofilament foam yarn 113 has a joint portion 112 a between the surrounding monofilament foam yarn 112. On the other hand, the surrounding monofilament foam yarns 112 are not joined to each other, and an opening 112c is formed. Therefore, the opening 112c can absorb and disperse external force and can retain moisture. Further, since the central monofilament foam yarn 113 has higher mechanical strength than the surrounding monofilament foam yarn 112, it can impart a strong bristle according to the setting.

本発明のブラシ用毛材は、自動車や車両等を洗浄する自動洗車機、各種ガラス洗浄機等に搭載される回転ブラシ、食器洗浄ブラシ、食品洗浄ブラシ等の各種洗浄用ブラシ、各種清掃用ブラシに、ブラシ用毛材として使用する。 The brush bristle material of the present invention is an automatic car washer for washing automobiles, vehicles, etc., various cleaning brushes such as rotating brushes, dish washing brushes, food washing brushes, etc. mounted on various glass washing machines, etc., and various cleaning brushes Used as a brush hair material.

１、１１、２１、３１、４１、５１、６１、７１、８１、９１、１０１、１１１、１３３ブラシ用毛材
２、１２、２２、３２、４２、５２、６２、７２、８２、９２、１０２、１１２周囲のモノフィラメント発泡糸
２ａ、２ｂ、１２ａ、１２ｂ、２２ａ、２２ｂ、３２ａ、４２ａ、４２ｂ、６２ａ、７２ａ、７２ｂ、８２ｂ、９２ｂ、１０２ａ、１１２ａ接合部
２ｃ、２２ｃ、３２ｃ空隙部
３、１３、２３、３３、４３、５３、６３、７３、１０３、１１３中央のモノフィラメント発泡糸
４気泡
４ａ長尺な気泡
２４表皮層
３２ｂ接触部
４４螺旋状部
５４、１３６分岐部
５５、１３５先割れ部
７４波形状部
８３中空部
９３、１０２ｃ、１１２ｃ開口部
１２０洗車機用洗浄ブラシ
１２３軸体
１２５ａ係止具
１２５ｂネジ
１３０チャンネルブラシ
１３１帯状体
１３２芯線
１４０洗車機
１４２駆動源
１４３ノズル
１４４乾燥機 1, 11, 21, 31, 41, 51, 61, 71, 81, 91, 101, 111, 133 Brush hair material 2, 12, 22, 32, 42, 52, 62, 72, 82, 92, 102 , 112 Surrounding monofilament foam yarns 2a, 2b, 12a, 12b, 22a, 22b, 32a, 42a, 42b, 62a, 72a, 72b, 82b, 92b, 102a, 112a Joint portions 2c, 22c, 32c 23, 33, 43, 53, 63, 73, 103, 113 Monofilament foamed yarn 4 in the center 4 Bubble 4a Long bubble 24 Skin layer 32b Contact portion 44 Spiral portion 54, 136 Branch portion 55, 135 Tip crack portion 74 Wave-shaped part 83 Hollow part 93, 102c, 112c Opening part 120 Car wash washing brush 123 Shaft body 125a Locking tool 125b Screw 130 Neruburashi 131 strip 132 core 140 car wash 142 drive source 143 nozzles 144 Dryer

Claims

The monofilament foamed yarn composed of a plurality of substantially columnar shapes made of thermoplastic resin is converged and formed into a multifilament shape with a melt-joined joint, and the monofilament foam is joined by an external force. A bristle material for a brush, wherein yarns are separable from the joint or the vicinity of the joint.

The bristle material for brushes which consists of a structure of Claim 1 WHEREIN: The cross section of the said bristle material for brushes has the space | gap part formed between several monofilament foaming yarns, The bristle material for brushes characterized by the above-mentioned.

The bristle material for brushes having the configuration according to claim 1 or 2, wherein a cross-section of the bristle material for brushes has a skin layer formed on the outer edge of the monofilament foam yarn, and the skin layers of the adjacent monofilament foam yarns. A bristle material for a brush characterized by having joints joined together.

The bristle material for brushes having the configuration according to any one of claims 1 to 3, wherein a cross-section of the bristle material for brushes has a monofilament foam yarn at a central portion, and around the monofilament foam yarn at the central portion. A bristle material for a brush, wherein a plurality of monofilament foamed yarns are formed with joints.

5. The bristle material for a brush having the configuration according to claim 1, wherein the cross-section of the bristle material for the brush has a monofilament foam yarn at a central portion, and around the monofilament foam yarn at the central portion. A bristle material for a brush characterized in that a plurality of monofilament foamed yarns are formed with joints, and a plurality of adjacent monofilament foamed yarns have contact portions with each other.

In the bristle material for brushes which has the composition according to any one of claims 1 to 3, the cross-section of the bristle material for brushes formed a plurality of monofilament foamed yarns in a bead shape, and provided a hollow part in the center part. Brush hair material characterized by the above.

The bristle material for brushes having the configuration according to any one of claims 1 to 3, wherein a cross section of the bristle material for brushes is formed by forming a plurality of monofilament foam yarns in a substantially C shape and providing openings. Brush material characterized by.

The bristle material for brushes having the structure according to any one of claims 1 to 7, wherein the bristle material for brushes has a branched portion in which a plurality of monofilament foamed yarns joined to each other are separated from each other. Brush hair material.

The bristle material for brushes having the configuration according to any one of claims 1 to 8, wherein the bristle material for brushes has monofilament foamed yarns having long bubbles in the longitudinal direction. .