JP2012177047A - Polycarbonate resin composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a polycarbonate resin composition having both high flame retardancy and high draw down resistance.SOLUTION: The polycarbonate resin composition contains: (A) 100 pts.mass of a polycarbonate resin; (B) 3-30 pts.mass of phosphorus-based flame retardant; and (C) 0.001-1 pts.mass of fluoropolymer having a standard specific gravity (X) of 2.16-2.21 and satisfying the following formula: -200X+472≤Y. (Y represents tensile strength [MPa] of fluoropolymer (C)).

Description

  The present invention relates to a polycarbonate resin composition. More specifically, the present invention relates to a polycarbonate resin composition having high flame retardancy and high drawdown resistance at the same time.

  Polycarbonate resins are resins with excellent heat resistance, mechanical properties, and electrical characteristics, and are widely used as, for example, automobile materials, electrical and electronic equipment materials, housing materials, and other parts manufacturing materials in industrial fields. . In particular, the flame-retardant polycarbonate resin composition is suitably used as a member of OA / information equipment such as computers, notebook computers, mobile phones, printers, and copying machines.

  As a means for imparting flame retardancy to a polycarbonate resin, conventionally, a halogen-based flame retardant has been added to the polycarbonate resin. However, a polycarbonate resin composition containing a halogen-based flame retardant containing chlorine or bromine may lead to a decrease in thermal stability or corrosion of a molding machine screw or molding die during molding processing. there were. As an alternative method, many polycarbonate resin compositions containing a phosphorus-based flame retardant have been adopted (see, for example, Patent Documents 1 and 2).

  The method of incorporating such a phosphorus-based flame retardant into the polycarbonate resin can effectively shorten the combustion time by coating the resin surface with a phosphorus compound or diluting the combustion gas in the gas phase. In addition, due to the plasticizing effect of the phosphorus-based flame retardant, it has a drawback that it spreads easily during combustion and the fire spread resistance is lowered. For this reason, the method of mix | blending a fluoropolymer is normally used as a dripping prevention agent.

  However, even a resin composition containing a polycarbonate resin as described above, a phosphorus-based flame retardant, and a conventionally used fluoropolymer can satisfactorily achieve the high flame retardant level required in recent years. Therefore, a resin composition having a higher level of flame retardancy is desired. Specifically, there is a strong demand for a resin composition that simultaneously satisfies higher flame resistance and higher drip resistance.

  In addition, as described above, polycarbonate resin blended with a phosphorus-based flame retardant has been widely used as an injection molding material because of its excellent fluidity. However, it is easy to sag from the cylinder nozzle of a molding machine. Since it was necessary to stop and remove resin, there also existed the subject that continuous productivity was scarce. Furthermore, in recent years, with the diversification of products or their shapes, flame retardant polycarbonate resin materials corresponding to various processing methods such as flame retardant films and containers have been required. The melt viscosity was low, the draw-down resistance was low at the time of film and blow molding, and it was difficult to process.

  For this reason, a polycarbonate resin composition having high flame retardancy and high drawdown resistance at the same time is strongly desired, but a resin composition having such characteristics has not yet been obtained.

JP 59-202240 A JP-A-62-2746

  The present invention was devised in view of the above problems, and provides a polycarbonate resin composition having extremely high flame retardancy even in the case of a thin molded article, and also having high draw-down resistance at the same time. For the purpose.

  In order to solve the above-mentioned problems, the present inventor has paid attention to the relationship between the specific gravity and mechanical properties of the fluoropolymer to be blended and the flame retardancy and drawdown resistance of the polycarbonate resin composition blended therewith, and has conducted intensive studies. As a result, it is surprising that the polycarbonate resin has a very high flame retardancy and also has a high draw-down resistance by containing a phosphorus-based flame retardant and a specific fluoropolymer in the polycarbonate resin. The inventors found that a composition can be obtained and completed the present invention.

That is, according to 1st invention of this invention, 3-30 mass parts of phosphorus flame retardants (B) and standard specific gravity (X) are 2.16-2.100 with respect to 100 mass parts of polycarbonate resin (A). 21. The polycarbonate resin composition characterized by containing 0.001-1 mass part of fluoropolymer (C) which satisfy | fills following formula (1) by 21 is provided.
−200X + 472 ≦ Y (1)
(Y represents the tensile strength [unit: MPa] based on JIS K6891 of fluoropolymer (C).)

  According to the second invention of the present invention, in the first invention, the elastomer (D) is further contained in an amount of 0.5 to 10 parts by mass with respect to 100 parts by mass of the polycarbonate resin (A). A polycarbonate resin composition is provided.

（式中、Ｒ^１、Ｒ^２、Ｒ^３およびＲ^４は、それぞれ炭素数１〜６のアルキル基またはアルキル基で置換されていてもよい炭素数６〜２０のアリール基を示し、ｐ、ｑ、ｒおよびｓは、それぞれ０または１であり、ｋは１から５の整数であり、Ｘ^１はアリーレン基を示す。） According to the third invention of the present invention, in the first or second invention, the phosphorus-based flame retardant (B) is a phosphate ester represented by the following general formula (1). A polycarbonate resin composition is provided.

(Wherein R ¹ , R ² , R ³ and R ⁴ each represents an alkyl group having 1 to 6 carbon atoms or an aryl group having 6 to 20 carbon atoms which may be substituted with an alkyl group, and p, q , R and s are each 0 or 1, k is an integer of 1 to 5, and X ¹ represents an arylene group.)

  Furthermore, according to the fourth invention of the present invention, in any one of the first to third inventions, the elastomer (D) is a rubbery polymer, an aromatic vinyl compound, a vinyl cyanide compound, (meth) acrylic. A polycarbonate resin composition is provided which is a graft copolymer obtained by graft polymerization of at least one selected from acid ester compounds.

  According to the polycarbonate resin composition of the present invention, the flame retardancy and the drawdown resistance have both high flame retardancy and extremely high flame retardancy as well as high drawdown resistance even in the case of a thin molded article. It is possible to provide an excellent polycarbonate resin material.

It is a graph which shows the relationship between the standard density (SSG) and tensile strength in the Example and comparative example of this invention.

  Hereinafter, although an embodiment, an example thing, etc. are shown and explained in detail about the present invention, the present invention is limited to an embodiment, an example, etc. shown below and is not interpreted.

[1. Overview]
The polycarbonate resin composition of the present invention comprises at least a polycarbonate resin, a phosphorus flame retardant, and a specific fluoropolymer. Moreover, the polycarbonate resin composition of this invention may contain the other component as needed.
Thus, by including the polycarbonate resin, the phosphorus-based flame retardant and the specific fluoropolymer, flame retardancy and drawdown resistance can be remarkably improved.

[2. Polycarbonate resin (A)]
There is no restriction | limiting in the kind of polycarbonate resin used for the polycarbonate resin composition of this invention. In addition, one type of polycarbonate resin may be used, or two or more types may be used in any combination and in any ratio.

In addition, the polycarbonate resin in this invention is a polymer of the basic structure which has a carbonic acid bond represented by following General formula (2). In formula (2), X ² is generally a hydrocarbon group, but X ² into which a hetero atom or a hetero bond is introduced may be used for imparting various properties.

  The polycarbonate resin can be classified into an aromatic polycarbonate resin in which carbon directly bonded to a carbonic acid bond is aromatic carbon and an aliphatic polycarbonate resin in which aliphatic carbon is aliphatic carbon, either of which can be used. Of these, aromatic polycarbonate resins are preferred from the viewpoints of heat resistance, mechanical properties, electrical characteristics, and the like.

  Although there is no restriction | limiting in the specific kind of polycarbonate resin, For example, the polycarbonate polymer formed by making a dihydroxy compound and a carbonate precursor react is mentioned. At this time, in addition to the dihydroxy compound and the carbonate precursor, a polyhydroxy compound or the like may be reacted. Alternatively, a method of reacting carbon dioxide with a cyclic ether using a carbonate precursor may be used. The polycarbonate polymer may be linear or branched. Further, the polycarbonate polymer may be a homopolymer composed of one type of repeating unit or a copolymer having two or more types of repeating units. At this time, the copolymer can be selected from various copolymerization forms such as a random copolymer and a block copolymer. In general, such a polycarbonate polymer is a thermoplastic resin.

Among monomers used as raw materials for aromatic polycarbonate resins, examples of aromatic dihydroxy compounds include:
Dihydroxybenzenes such as 1,2-dihydroxybenzene, 1,3-dihydroxybenzene (ie, resorcinol), 1,4-dihydroxybenzene;
Dihydroxybiphenyls such as 2,5-dihydroxybiphenyl, 2,2′-dihydroxybiphenyl, 4,4′-dihydroxybiphenyl;
2,2′-dihydroxy-1,1′-binaphthyl, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, , 7-dihydroxynaphthalene, dihydroxynaphthalene such as 2,7-dihydroxynaphthalene;

2,2′-dihydroxydiphenyl ether, 3,3′-dihydroxydiphenyl ether, 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy-3,3′-dimethyldiphenyl ether, 1,4-bis (3-hydroxyphenoxy) Dihydroxy diaryl ethers such as benzene and 1,3-bis (4-hydroxyphenoxy) benzene;

2,2-bis (4-hydroxyphenyl) propane (ie, bisphenol A),
1,1-bis (4-hydroxyphenyl) propane,
2,2-bis (3-methyl-4-hydroxyphenyl) propane,
2,2-bis (3-methoxy-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-methoxy-4-hydroxyphenyl) propane,
1,1-bis (3-tert-butyl-4-hydroxyphenyl) propane,
2,2-bis (4-hydroxy-3,5-dimethylphenyl) propane,
2,2-bis (3-cyclohexyl-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-cyclohexyl-4-hydroxyphenyl) propane,
α, α′-bis (4-hydroxyphenyl) -1,4-diisopropylbenzene,
1,3-bis [2- (4-hydroxyphenyl) -2-propyl] benzene,
Bis (4-hydroxyphenyl) methane,
Bis (4-hydroxyphenyl) cyclohexylmethane,
Bis (4-hydroxyphenyl) phenylmethane,
Bis (4-hydroxyphenyl) (4-propenylphenyl) methane,
Bis (4-hydroxyphenyl) diphenylmethane,
Bis (4-hydroxyphenyl) naphthylmethane,
1-bis (4-hydroxyphenyl) ethane,
2-bis (4-hydroxyphenyl) ethane,
1,1-bis (4-hydroxyphenyl) -1-phenylethane,
1,1-bis (4-hydroxyphenyl) -1-naphthylethane,
1-bis (4-hydroxyphenyl) butane,
2-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) pentane,
1,1-bis (4-hydroxyphenyl) hexane,
2,2-bis (4-hydroxyphenyl) hexane,
1-bis (4-hydroxyphenyl) octane,
2-bis (4-hydroxyphenyl) octane,
1-bis (4-hydroxyphenyl) hexane,
2-bis (4-hydroxyphenyl) hexane,
4,4-bis (4-hydroxyphenyl) heptane,
2,2-bis (4-hydroxyphenyl) nonane,
10-bis (4-hydroxyphenyl) decane,
1-bis (4-hydroxyphenyl) dodecane,
Bis (hydroxyaryl) alkanes such as;

1-bis (4-hydroxyphenyl) cyclopentane,
1-bis (4-hydroxyphenyl) cyclohexane,
4-bis (4-hydroxyphenyl) cyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3-dimethylcyclohexane,
1-bis (4-hydroxyphenyl) -3,4-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,5-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxy-3,5-dimethylphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-propyl-5-methylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -3-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -3-phenylcyclohexane,
1,1-bis (4-hydroxyphenyl) -4-phenylcyclohexane,
Bis (hydroxyaryl) cycloalkanes such as;

Cardostructure-containing bisphenols such as 9,9-bis (4-hydroxyphenyl) fluorene, 9,9-bis (4-hydroxy-3-methylphenyl) fluorene;

Dihydroxy diaryl sulfides such as 4,4'-dihydroxydiphenyl sulfide, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfide;

Dihydroxydiaryl sulfoxides such as 4,4'-dihydroxydiphenyl sulfoxide, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide;

Dihydroxydiaryl sulfones such as 4,4'-dihydroxydiphenyl sulfone and 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfone;

Among these, bis (hydroxyaryl) alkanes are preferable, and bis (4-hydroxyphenyl) alkanes are preferable, and 2,2-bis (4-hydroxyphenyl) propane (ie, from the viewpoint of impact resistance and heat resistance). Bisphenol A) is preferred.
In addition, 1 type may be used for an aromatic dihydroxy compound and it may use 2 or more types together by arbitrary combinations and a ratio.

  Examples of the monomer that is a raw material for the aliphatic polycarbonate resin include ethane-1,2-diol, propane-1,2-diol, propane-1,3-diol, 2,2-dimethylpropane-1, 3-diol, 2-methyl-2-propylpropane-1,3-diol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, decane-1,10-diol Alkanediols such as

  Cyclopentane-1,2-diol, cyclohexane-1,2-diol, cyclohexane-1,4-diol, 1,4-cyclohexanedimethanol, 4- (2-hydroxyethyl) cyclohexanol, 2,2,4, Cycloalkanediols such as 4-tetramethyl-cyclobutane-1,3-diol;

Glycols such as 2,2'-oxydiethanol (ie, ethylene glycol), diethylene glycol, triethylene glycol, propylene glycol, spiroglycol, etc .;

  1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 1,4-benzenediethanol, 1,3-bis (2-hydroxyethoxy) benzene, 1,4-bis ( 2-hydroxyethoxy) benzene, 2,3-bis (hydroxymethyl) naphthalene, 1,6-bis (hydroxyethoxy) naphthalene, 4,4′-biphenyldimethanol, 4,4′-biphenyldiethanol, 1,4- Aralkyl diols such as bis (2-hydroxyethoxy) biphenyl, bisphenol A bis (2-hydroxyethyl) ether, bisphenol S bis (2-hydroxyethyl) ether;

  1,2-epoxyethane (ie ethylene oxide), 1,2-epoxypropane (ie propylene oxide), 1,2-epoxycyclopentane, 1,2-epoxycyclohexane, 1,4-epoxycyclohexane, 1-methyl And cyclic ethers such as -1,2-epoxycyclohexane, 2,3-epoxynorbornane, and 1,3-epoxypropane;

  Among the monomers used as the raw material for the aromatic polycarbonate resin, carbonyl halides, carbonate esters and the like are used as examples of the carbonate precursor. In addition, 1 type may be used for a carbonate precursor and it may use 2 or more types together by arbitrary combinations and a ratio.

  Specific examples of carbonyl halides include phosgene; haloformates such as bischloroformate of dihydroxy compounds and monochloroformate of dihydroxy compounds.

  Specific examples of the carbonate ester include diaryl carbonates such as diphenyl carbonate and ditolyl carbonate; dialkyl carbonates such as dimethyl carbonate and diethyl carbonate; biscarbonate bodies of dihydroxy compounds, monocarbonate bodies of dihydroxy compounds, and cyclic carbonates. And carbonate bodies of dihydroxy compounds such as

-Manufacturing method of polycarbonate resin The manufacturing method of polycarbonate resin is not specifically limited, Arbitrary methods are employable. Examples thereof include an interfacial polymerization method, a melt transesterification method, a pyridine method, a ring-opening polymerization method of a cyclic carbonate compound, and a solid phase transesterification method of a prepolymer. Hereinafter, a particularly preferable one of these methods will be specifically described.

.. Interfacial polymerization method First, the case where a polycarbonate resin is produced by the interfacial polymerization method will be described. In the interfacial polymerization method, a dihydroxy compound and a carbonate precursor (preferably phosgene) are reacted in the presence of an organic solvent inert to the reaction and an aqueous alkaline solution, usually at a pH of 9 or higher. Polycarbonate resin is obtained by interfacial polymerization in the presence. In the reaction system, a molecular weight adjusting agent (terminal terminator) may be present as necessary, or an antioxidant may be present to prevent the oxidation of the dihydroxy compound.

  The dihydroxy compound and the carbonate precursor are as described above. Of the carbonate precursors, phosgene is preferably used, and a method using phosgene is particularly called a phosgene method.

  Examples of the organic solvent inert to the reaction include chlorinated hydrocarbons such as dichloromethane, 1,2-dichloroethane, chloroform, monochlorobenzene and dichlorobenzene; aromatic hydrocarbons such as benzene, toluene and xylene; It is done. In addition, 1 type may be used for an organic solvent and it may use 2 or more types together by arbitrary combinations and a ratio.

  Examples of the alkali compound contained in the alkaline aqueous solution include alkali metal compounds and alkaline earth metal compounds such as sodium hydroxide, potassium hydroxide, lithium hydroxide, and sodium hydrogen carbonate, among which sodium hydroxide and water Potassium oxide is preferred. In addition, an alkali compound may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.

  Although there is no restriction | limiting in the density | concentration of the alkali compound in alkaline aqueous solution, Usually, in order to control pH in the alkaline aqueous solution of reaction to 10-12, it is used at 5-10 mass%. For example, when phosgene is blown, the molar ratio of the bisphenol compound and the alkali compound is usually 1: 1.9 or more in order to control the pH of the aqueous phase to be 10 to 12, preferably 10 to 11. Among these, it is preferable that the ratio is 1: 2.0 or more, usually 1: 3.2 or less, and more preferably 1: 2.5 or less.

  Examples of the polymerization catalyst include aliphatic tertiary amines such as trimethylamine, triethylamine, tributylamine, tripropylamine, and trihexylamine; alicyclic rings such as N, N′-dimethylcyclohexylamine and N, N′-diethylcyclohexylamine. Formula tertiary amines; aromatic tertiary amines such as N, N′-dimethylaniline and N, N′-diethylaniline; quaternary ammonium salts such as trimethylbenzylammonium chloride, tetramethylammonium chloride, triethylbenzylammonium chloride, etc. Pyridine; guanine; guanidine salt; and the like. In addition, 1 type may be used for a polymerization catalyst and it may use 2 or more types together by arbitrary combinations and a ratio.

  Examples of the molecular weight regulator include aromatic phenols having a monohydric phenolic hydroxyl group; aliphatic alcohols such as methanol and butanol; mercaptans; phthalimides and the like. Of these, aromatic phenols are preferred. Specific examples of such aromatic phenols include alkyl groups such as m-methylphenol, p-methylphenol, m-propylphenol, p-propylphenol, p-tert-butylphenol, and p-long chain alkyl-substituted phenol. Examples thereof include substituted phenols; vinyl group-containing phenols such as isopropanyl phenol; epoxy group-containing phenols; carboxyl group-containing phenols such as 0-oxine benzoic acid and 2-methyl-6-hydroxyphenylacetic acid; In addition, a molecular weight regulator may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.

  The usage-amount of a molecular weight regulator is 0.5 mol or more normally with respect to 100 mol of dihydroxy compounds, Preferably it is 1 mol or more, and is 50 mol or less normally, Preferably it is 30 mol or less. By making the usage-amount of a molecular weight modifier into this range, the thermal stability and hydrolysis resistance of a polycarbonate resin composition can be improved.

In the reaction, the order of mixing the reaction substrate, reaction medium, catalyst, additive and the like is arbitrary as long as a desired polycarbonate resin is obtained, and an appropriate order may be arbitrarily set. For example, when phosgene is used as the carbonate precursor, the molecular weight regulator can be mixed at any time as long as it is between the reaction (phosgenation) of the dihydroxy compound and phosgene and the start of the polymerization reaction.
In addition, reaction temperature is 0-40 degreeC normally, and reaction time is normally several minutes (for example, 10 minutes)-several hours (for example, 6 hours).

-Melt transesterification method Next, the case where a polycarbonate resin is manufactured by the melt transesterification method is demonstrated. In the melt transesterification method, for example, a transesterification reaction between a carbonic acid diester and a dihydroxy compound is performed.

The dihydroxy compound is as described above.
On the other hand, examples of the carbonic acid diester include dialkyl carbonate compounds such as dimethyl carbonate, diethyl carbonate, and di-tert-butyl carbonate; diphenyl carbonate; substituted diphenyl carbonate such as ditolyl carbonate, and the like. Among these, diphenyl carbonate and substituted diphenyl carbonate are preferable, and diphenyl carbonate is more preferable. In addition, 1 type may be used for carbonic acid diester, and it may use 2 or more types together by arbitrary combinations and a ratio.

  The ratio of the dihydroxy compound and the carbonic acid diester is arbitrary as long as the desired polycarbonate resin can be obtained, but it is preferable to use an equimolar amount or more of the carbonic acid diester with respect to 1 mol of the dihydroxy compound. Is more preferable. The upper limit is usually 1.30 mol or less. By setting it as such a range, the amount of terminal hydroxyl groups can be adjusted to a suitable range.

  In the polycarbonate resin, the amount of terminal hydroxyl groups tends to have a great influence on thermal stability, hydrolysis stability, color tone and the like. For this reason, you may adjust the amount of terminal hydroxyl groups as needed by a well-known arbitrary method. In the transesterification reaction, a polycarbonate resin in which the amount of terminal hydroxyl groups is adjusted can be usually obtained by adjusting the mixing ratio of the carbonic diester and the aromatic dihydroxy compound; the degree of vacuum during the transesterification reaction, and the like. In addition, the molecular weight of the polycarbonate resin usually obtained can also be adjusted by this operation.

When adjusting the amount of terminal hydroxyl groups by adjusting the mixing ratio of the carbonic acid diester and the dihydroxy compound, the mixing ratio is as described above.
Further, as a more aggressive adjustment method, there may be mentioned a method in which a terminal terminator is mixed separately during the reaction. Examples of the terminal terminator at this time include monohydric phenols, monovalent carboxylic acids, carbonic acid diesters, and the like. In addition, 1 type may be used for a terminal terminator and it may use 2 or more types together by arbitrary combinations and a ratio.

  When producing a polycarbonate resin by the melt transesterification method, a transesterification catalyst is usually used. Any transesterification catalyst can be used. Among them, it is preferable to use, for example, an alkali metal compound and / or an alkaline earth metal compound. In addition, auxiliary compounds such as basic boron compounds, basic phosphorus compounds, basic ammonium compounds, and amine compounds may be used in combination. In addition, 1 type may be used for a transesterification catalyst and it may use 2 or more types together by arbitrary combinations and a ratio.

  In the melt transesterification method, the reaction temperature is usually 100 to 320 ° C. The pressure during the reaction is usually a reduced pressure condition of 2 mmHg or less. As a specific operation, a melt polycondensation reaction may be performed under the above-mentioned conditions while removing a by-product such as an aromatic hydroxy compound.

  The melt polycondensation reaction can be performed by either a batch method or a continuous method. When performing by a batch type, the order which mixes a reaction substrate, a reaction medium, a catalyst, an additive, etc. is arbitrary as long as a desired aromatic polycarbonate resin is obtained, What is necessary is just to set an appropriate order arbitrarily. However, considering the stability of the polycarbonate resin and the polycarbonate resin composition, the melt polycondensation reaction is preferably carried out continuously.

  In the melt transesterification method, a catalyst deactivator may be used as necessary. As the catalyst deactivator, a compound that neutralizes the transesterification catalyst can be arbitrarily used. Examples thereof include sulfur-containing acidic compounds and derivatives thereof. In addition, a catalyst deactivator may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.

  The amount of the catalyst deactivator used is usually 0.5 equivalents or more, preferably 1 equivalent or more, and usually 10 equivalents or less, relative to the alkali metal or alkaline earth metal contained in the transesterification catalyst. Preferably it is 5 equivalents or less. Furthermore, it is 1 ppm or more normally with respect to aromatic polycarbonate resin, and is 100 ppm or less normally, Preferably it is 20 ppm or less.

-Other matters regarding polycarbonate resin The molecular weight of the polycarbonate resin is arbitrary and may be appropriately selected and determined. The viscosity average molecular weight [Mv] converted from the solution viscosity is usually 10,000 or more, preferably 16,000. Above, more preferably 17,000 or more, and usually 40,000 or less, preferably 30,000 or less, more preferably 24,000 or less. By setting the viscosity average molecular weight to be equal to or higher than the lower limit of the above range, the mechanical strength of the polycarbonate resin composition of the present invention can be further improved, which is more preferable when used for applications requiring high mechanical strength. On the other hand, by setting the viscosity average molecular weight to be equal to or lower than the upper limit of the above range, the polycarbonate resin composition of the present invention can be suppressed and improved in fluidity, and the molding processability can be improved and the molding process can be easily performed. Two or more types of polycarbonate resins having different viscosity average molecular weights may be mixed and used, and in this case, a polycarbonate resin having a viscosity average molecular weight outside the above-mentioned preferred range may be mixed.

The viscosity average molecular weight [Mv] is obtained by using methylene chloride as a solvent and obtaining an intrinsic viscosity [η] (unit: dl / g) at a temperature of 20 ° C. using an Ubbelohde viscometer. , Η = 1.23 × 10 ⁻⁴ Mv ^0.83 . The intrinsic viscosity [η] is a value calculated from the following equation by measuring the specific viscosity [η _sp ] at each solution concentration [C] (g / dl).

  The terminal hydroxyl group concentration of the polycarbonate resin is arbitrary and may be appropriately selected and determined, but is usually 1,000 ppm or less, preferably 800 ppm or less, more preferably 600 ppm or less. Thereby, the residence heat stability and color tone of the polycarbonate resin composition of the present invention can be further improved. In addition, the lower limit is usually 10 ppm or more, preferably 30 ppm or more, more preferably 40 ppm or more, particularly for polycarbonate resins produced by the melt transesterification method. Thereby, the fall of molecular weight can be suppressed and the mechanical characteristic of the polycarbonate resin composition of this invention can be improved more.

  In addition, the unit of a terminal hydroxyl group density | concentration represents the mass of the terminal hydroxyl group with respect to the mass of polycarbonate resin in ppm. The measurement method is colorimetric determination (method described in Macromol. Chem. 88 215 (1965)) by the titanium tetrachloride / acetic acid method.

  The polycarbonate resin is a polycarbonate resin alone (the polycarbonate resin alone is not limited to an embodiment containing only one type of polycarbonate resin, and is used in a sense including an embodiment containing a plurality of types of polycarbonate resins having different monomer compositions and molecular weights, for example. .), Or an alloy (mixture) of a polycarbonate resin and another thermoplastic resin may be used in combination. Further, for example, for the purpose of further improving flame retardancy and impact resistance, a polycarbonate resin is copolymerized with an oligomer or polymer having a siloxane structure; for the purpose of further improving thermal oxidation stability and flame retardancy A monomer, oligomer or polymer having a copolymer; a monomer, oligomer or polymer having a dihydroxyanthraquinone structure for the purpose of improving thermal oxidation stability; A copolymer with an oligomer or polymer having an olefin structure; a copolymer with a polyester resin oligomer or polymer for the purpose of improving chemical resistance; Good.

  Further, in order to improve the appearance of the molded product and improve the fluidity, the polycarbonate resin may contain a polycarbonate oligomer. The viscosity average molecular weight [Mv] of this polycarbonate oligomer is usually 1,500 or more, preferably 2,000 or more, and usually 9,500 or less, preferably 9,000 or less. Furthermore, the polycarbonate ligomer contained is preferably 30% by mass or less of the polycarbonate resin (including the polycarbonate oligomer).

Further, the polycarbonate resin may be not only a virgin raw material but also a polycarbonate resin regenerated from a used product (so-called material-recycled polycarbonate resin). Examples of the used products include: optical recording media such as optical disks; light guide plates; vehicle window glass, vehicle headlamp lenses, windshields and other vehicle transparent members; water bottles and other containers; eyeglass lenses; Examples include architectural members such as glass windows and corrugated sheets. Also, non-conforming products, pulverized products obtained from sprues, runners, etc., or pellets obtained by melting them can be used.
However, the regenerated polycarbonate resin is preferably 80% by mass or less, more preferably 50% by mass or less, among the polycarbonate resins contained in the polycarbonate resin composition of the present invention. Recycled polycarbonate resin is likely to have undergone deterioration such as heat deterioration and aging deterioration, so when such polycarbonate resin is used more than the above range, hue and mechanical properties can be reduced. It is because there is sex.

[3. Phosphorus flame retardant (B)]
The polycarbonate resin composition of the present invention contains 3 to 30 parts by mass of the phosphorus-based flame retardant (B) with respect to 100 parts by mass of the polycarbonate resin (A). Thus, the flame retardance of the polycarbonate resin composition of this invention can be improved by containing a phosphorus flame retardant.

  The phosphorus-based flame retardant in the present invention is a compound containing phosphorus in a molecule, and may be a low molecule, an oligomer, or a polymer. The phosphate ester compound represented by the formula (1) and the phosphazene compounds represented by the general formulas (3) and (4) are particularly preferable.

[3-1. Phosphate ester compound]
The phosphate ester compound represented by the general formula (1) may be a mixture of compounds having different numbers of k. In the case of a mixture of condensed phosphate esters having different k, k is a mixture thereof. The average value of k is usually an integer of 0 to 5, and in the case of a mixture of compounds having different k numbers, the average k number is preferably 0.5 to 2, more preferably 0.6 to 1.5, and even more preferably. Is in the range of 0.8 to 1.2, particularly preferably 0.95 to 1.15.

X ¹ represents a divalent arylene group such as resorcinol, hydroquinone, bisphenol A, 2,2′-dihydroxybiphenyl, 2,3′-dihydroxybiphenyl, 2,4′-dihydroxybiphenyl, 3,3 ′. -Dihydroxybiphenyl, 3,4'-dihydroxybiphenyl, 4,4'-dihydroxybiphenyl, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 1,4-dihydroxynaphthalene, 1,5-dihydroxynaphthalene, 1, Divalent derivatives derived from dihydroxy compounds such as 6-dihydroxynaphthalene, 1,7-dihydroxynaphthalene, 1,8-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 2,6-dihydroxynaphthalene and 2,7-dihydroxynaphthalene It is a group. Of these, divalent groups derived from resorcinol, bisphenol A, and 3,3′-dihydroxybiphenyl are particularly preferable.

  Further, p, q, r and s in the general formula (1) each represent 0 or 1, and 1 is particularly preferable.

R ¹ , R ² , R ³ and R ⁴ each represent an alkyl group having 1 to 6 carbon atoms or an aryl group having 6 to 20 carbon atoms which may be substituted with an alkyl group. Examples of such aryl groups include phenyl group, cresyl group, xylyl group, isopropylphenyl group, butylphenyl group, tert-butylphenyl group, di-tert-butylphenyl group, and p-cumylphenyl group. Group, cresyl group and xylyl group are more preferred.

Specific examples of the phosphate ester compound represented by the general formula (1) include
Triphenyl phosphate (TPP), tricresyl phosphate (TCP), trixylenyl phosphate (TXP), cresyl diphenyl phosphate (CDP), 2-ethylhexyl diphenyl phosphate (EHDP), tert-butylphenyl diphenyl phosphate, bis- ( aromatic phosphates such as tert-butylphenyl) phenyl phosphate, tris- (tert-butylphenyl) phosphate, isopropylphenyldiphenyl phosphate, bis- (isopropylphenyl) diphenyl phosphate, tris- (isopropylphenyl) phosphate;
Condensed phosphate esters such as resorcinol bis-diphenyl phosphate (RDP), resorcinol bis-dixylenyl phosphate (RDX), bisphenol A bis-diphenyl phosphate (BDP), biphenyl bis-diphenyl phosphate;
Etc.

  The acid value of the phosphoric acid ester compound represented by the general formula (1) is preferably 0.2 mgKOH / g, more preferably 0.15 mgKOH / g or less, still more preferably 0.1 mgKOH or less, particularly preferably Is 0.05 mgKOH / g or less. The lower limit of the acid value can be substantially zero. On the other hand, the content of the half ester is more preferably 1.1 parts by mass or less, and still more preferably 0.9 parts by mass or less. When the acid value exceeds 0.2 mgKOH / g or the half ester content exceeds 1.5 mg, the thermal stability and hydrolysis resistance of the polycarbonate resin composition of the present invention are reduced.

  As the phosphate ester compound used in the present invention, in addition to the above-mentioned compounds, 10- (2,5-dihydroxyphenyl) -10H-9-oxa-10-phosphaphenanthrene-10-oxide, 10- (2,3 -Dihydroxyphenyl) -10H-9-oxa-10-phosphaphenanthrene-10-oxide, 10- (2,4-dihydroxyphenyl) -10H-9-oxa-10-phosphaphenanthrene-10-oxide, phosphoric acid Naturally, polyester resins, polycarbonate resins or epoxy resins containing an ester moiety are also included.

[3-2. Phosphazene compound]
Examples of the phosphazene compounds represented by the general formulas (3) and (4) include phenoxyphosphazene, (poly) tolyloxyphosphazene (for example, o-tolyloxyphosphazene, m-tolyloxyphosphazene, p-tolyloxyphosphazene, o, m-tolyloxyphosphazene, o, p-tolyloxyphosphazene, m, p-tolyloxyphosphazene, o, m, p-tolyloxyphosphazene, etc.), (poly) xylyloxyphosphazene, etc. and Jo _{C 1-6} alkyl _{C 6-20} aryloxy phosphazene, (poly) phenoxy tolyloxy phosphazene (e.g., phenoxy o- tolyloxy phosphazene, a phenoxy m- tolyloxyethyl phosphazene, a phenoxy p- tolyloxy phosphazene, a phenoxy o m-tolyloxyphosphazene, phenoxy o, p-tolyloxyphosphazene, phenoxy m, p-tolyloxyphosphazene, phenoxy o, m, p-tolyloxyphosphazene, etc.), (poly) phenoxysilyloxyphosphazene, (poly) phenoxy Examples thereof include cyclic and / or chain C _6-20 aryl C _1-10 alkyl C _6-20 aryloxy phosphazene such as tolyloxyxyloxyphosphazene.
Of these, cyclic and / or chain phenoxyphosphazene, cyclic and / or chain C _1-3 alkyl C _6-20 aryloxyphosphazene, C _6-20 aryloxy C _1-3 alkyl C _6-20 Aryloxyphosphazenes (eg, cyclic and / or chain tolyloxyphosphazenes, cyclic and / or chain phenoxytolylphenoxyphosphazenes, etc.).

In the cyclic phosphazene compound represented by the general formula (3), R ⁵ and R ⁶ may be the same or different and each represents an aryl group or an alkylaryl group. Examples of such an aryl group or alkylaryl group include a phenyl group, a naphthyl group, a methylphenyl group, and a benzyl group. Among them, cyclic phenoxyphosphazene in which R ⁵ and R ⁶ are phenyl groups is particularly preferable.
Examples of such a cyclic phenoxyphosphazene compound include hexachlorocyclotriphosphazene, octachlorocyclohexane, and a mixture of cyclic and linear chlorophosphazene obtained by reacting ammonium chloride and phosphorus pentachloride at a temperature of 120 to 130 ° C. Examples include compounds such as phenoxycyclotriphosphazene, octaphenoxycyclotetraphosphazene, and decaffenoxycyclopentaphosphazene obtained by removing a cyclic chlorophosphazene such as cyclotetraphosphazene and decachlorocyclopentaphosphazene and then substituting with a phenoxy group. .

  Moreover, in formula (3), t represents an integer of 3 to 25. Among them, a compound in which t is an integer of 3 to 8 is preferable, and a mixture of compounds having different t may be used. Among them, a mixture of compounds in which t = 3 is 50% by mass or more, t = 4 is 10 to 40% by mass, and t = 5 or more is 30% by mass or less is preferable.

In formula (4), R ⁷ and R ⁸ may be the same or different and each represents an aryl group or an alkylaryl group. Examples of such an aryl group or alkylaryl group include a phenyl group, a naphthyl group, a methylphenyl group, a benzyl group, and the like, and a chain phenoxyphosphazene in which R ⁷ and R ⁸ are phenyl groups is particularly preferable.
Such a chain phenoxyphosphazene compound is obtained by, for example, subjecting hexachlorocyclotriphosphazene obtained by the above-described method to reverse polymerization at a temperature of 220 to 250 ° C., and the obtained linear dichloromethane having a polymerization degree of 3 to 10,000. Examples thereof include compounds obtained by substituting phosphazene with a phenoxy group.

Also, R ⁹ is represented by -N = P (OR ⁷ ) ₃ groups, -N = P (OR ⁸ ) ₃ groups, -N = P (O) OR ⁷ groups, and -N = P (O) OR ⁸ groups. At least one selected is shown, and R ¹⁰ is -P (OR ⁷ ) ₄ group, -P (OR ⁸ ) ₄ group, -P (O) (OR ⁷ ) ₂ group, -P (O) (OR ⁸ ) At least one selected from _two groups.

  Moreover, in Formula (4), u shows the integer of 3-10,000, Preferably it is 3-1,000, More preferably, it is 3-100, More preferably, it is 3-25.

The phosphazene compound used in the present invention may be a crosslinked phosphazene compound partially crosslinked. By having such a crosslinked structure, the heat resistance tends to be improved.
Examples of such a crosslinked phosphazene compound include a compound having a crosslinked structure of 4,4′-sulfonyldiphenylene (bisphenol S residue) and a crosslinked structure of 2,2- (4,4′-diphenylene) isopropylidene group. Having a crosslinked structure of 4,4′-diphenylene group, such as a compound having a crosslinked structure of 4,4′-oxydiphenylene group, a compound having a crosslinked structure of 4,4′-thiodiphenylene group, etc. Compounds and the like.

［式（５）中、Ｘ^３は−Ｃ（ＣＨ_３）_２−、−ＳＯ_２−、−Ｓ−、又は−Ｏ−であり、ｖは０又は１である。］

[In Formula (5), X ³ is —C (CH ₃ ) ₂ —, —SO ₂ —, —S—, or —O—, and v is 0 or 1. ]

In addition, as the crosslinked phosphazene compound, a crosslinked phenoxyphosphazene compound obtained by crosslinking a cyclic phenoxyphosphazene compound in which R ⁵ and R ⁶ are phenyl groups in the general formula (3) with a crosslinking group represented by the general formula (5). Alternatively, a crosslinked phenoxyphosphazene compound obtained by crosslinking a chain phenoxyphosphazene compound in which R ⁷ and R ⁸ are phenyl groups in the general formula (4) with a crosslinking group represented by the general formula (5) is flame retardant. From the above point, a crosslinked phenoxyphosphazene compound obtained by crosslinking a cyclic phenoxyphosphazene compound with a crosslinking group represented by the general formula (5) is more preferable.

  The content of the phenylene group in the crosslinked phenoxyphosphazene compound is such that the cyclic phosphazene compound represented by the general formula (3) and / or the all phenyl groups in the chain phenoxyphosphazene compound represented by the general formula (4) and Based on the number of phenylene groups, it is usually 50 to 99.9%, preferably 70 to 90%. The crosslinked phenoxyphosphazene compound is particularly preferably a compound having no free hydroxyl group in the molecule.

  In the present invention, the phosphazene compound is a crosslinked phenoxy obtained by crosslinking the cyclic phenoxyphosphazene compound represented by the general formula (3) and the cyclic phenoxyphosphazene compound represented by the general formula (4) with a crosslinking group. In view of flame retardancy and mechanical properties, at least one selected from the group consisting of phosphazene compounds is preferable.

  The content of the phosphorus-based flame retardant (B) is 3 parts by mass or more, preferably 5 parts by mass or more, more preferably 8 parts by mass or more, and 30 parts by mass or less, with respect to 100 parts by mass of the polycarbonate resin (A). Preferably it is 25 parts by weight or less, more preferably 20 parts by weight or less. When the blending amount of the phosphorus-based flame retardant is less than 3 parts by mass, the flame retardancy is insufficient, and when it exceeds 30 parts by mass, a remarkable decrease in heat resistance and a decrease in mechanical properties are caused.

[4. Fluoropolymer (C)]
The polycarbonate resin composition of the present invention contains 0.001 to 1 part by mass of the fluoropolymer (C) with respect to 100 parts by mass of the polycarbonate resin (A). One type of fluoropolymer (C) may be used, or two or more types may be used in any combination and in any ratio.

  Examples of the fluoropolymer (C) include a fluoroolefin resin. The fluoroolefin resin is usually a polymer or copolymer containing a fluoroethylene structure. Specific examples include difluoroethylene resin, tetrafluoroethylene resin, tetrafluoroethylene / hexafluoropropylene copolymer resin, tetrafluoroethylene / perfluoroalkyl vinyl ether copolymer resin, and the like. Of these, tetrafluoroethylene resin and the like are preferable. Examples of the fluoroethylene resin include a fluoroethylene resin having a fibril forming ability.

  The fluoropolymer (C) in the present invention needs to have a standard specific gravity value of 2.16 or more and 2.21 or less. When the standard specific gravity is less than 2.16, the combustion time is prolonged and the flame extinguishing property tends to be inferior, and the drip resistance, that is, the flame spread resistance tends to be lowered, which is not preferable. Also, when the standard specific gravity exceeds 2.21, the drip resistance is lowered and the drawdown resistance is also lowered. The standard specific gravity value is preferably 2.165 to 2.205, more preferably 2.170 to 2.200, particularly preferably 2.171 to 2.200, and 2.173. Most preferred is ˜2.199.

In addition, in this invention, it has the characteristics that the effect which a polycarbonate resin composition expresses differs by the value of the standard specific gravity of a fluoropolymer (C) being 2.19.
That is, when the standard specific gravity (X) of the fluoropolymer (C) is 2.16 to 2.19, the flame retardancy is particularly excellent, and the standard specific gravity (X) is 2.19. When it is more than or equal to 2.21 or less, the handling property of the resin composition is particularly good and the appearance is improved.

  In the present specification, the standard specific gravity (also referred to as SSG) is a value measured by a water displacement method using a sample molded according to ASTM D4895.

  The fluoropolymer is produced by emulsion polymerization, and the standard specific gravity (SSG) can be adjusted by adjusting the polymerization conditions. For example, in the emulsion polymerization process of tetrafluoroethylene monomer, the polymerization initiator injection and A fluoropolymer having a standard specific gravity of 2.16 to 2.21 can be obtained by selecting the stopping time and adjusting other polymerization conditions.

Furthermore, it is essential that the fluoropolymer (C) in the present invention is a fluoropolymer having a tensile strength Y (unit: MPa) in accordance with JIS K6891 that satisfies the following formula (1).
−200X + 472 ≦ Y (1)
Here, X is the above-mentioned standard specific gravity.
By using the fluoropolymer (C) having the standard specific gravity in the above-described range and in such a range, the flame retardancy and the drawdown resistance of the polycarbonate resin composition of the present invention are extremely good. . This is because the fluoropolymer (C) having such a relationship between the standard specific gravity and the tensile strength effectively exerts the tension improving effect of the resin composition at the time of melting, and further, it is difficult to obtain a phosphorus-based difficulty with the polycarbonate resin (A). The dispersibility of the flame retardant (B) in the mixed matrix is excellent, so that the flame retardant effect of the phosphorus-based flame retardant can be effectively extracted, and the drip resistance of the fluoropolymer (C) itself can be effectively exhibited. This is thought to be possible.

In addition, the upper limit of the tensile strength Y is preferably 50 MPa. Therefore, a preferable range of the above formula (1) is represented by the following formula (2).
−200X + 472 ≦ Y ≦ 50 (2)
A more preferable range of the tensile strength Y of the fluoropolymer (C) is 30 to 50 MPa. Those exceeding 50 MPa are difficult to produce industrially.

  The average particle size of the fluoropolymer (C) in the present invention is not particularly limited, but is preferably 300 to 1,000 μm. When the average particle size is less than 300 μm, the drip resistance of the polycarbonate resin composition of the present invention may be reduced. When the average particle size is more than 1,000 μm, the fluoropolymer is likely to aggregate, resulting in a molded product. In such a case, it is not preferable because it may cause appearance defects such as white spot foreign matter. From such a viewpoint, the average particle size of the fluoropolymer is more preferably 350 to 800 μm, further preferably 380 to 750 μm, and particularly preferably 400 to 700 μm.

  The content of the fluoropolymer (C) is usually 0.001 parts by mass or more, preferably 0.01 parts by mass or more, more preferably 0.05 parts by mass or more, particularly 100 parts by mass of the polycarbonate resin (A). Preferably it is 0.1 mass part or more, and is 1 mass part or less, Preferably it is 0.75 mass part or less, More preferably, it is 0.5 mass part or less. When the content of the fluoropolymer (C) is less than or equal to the lower limit of the above range, the flame retardancy effect due to the anti-dripping agent becomes insufficient, and when the content exceeds the upper limit of the above range, the polycarbonate resin composition There is a possibility that the appearance defect or the mechanical strength of the molded product formed from the above will be deteriorated.

[5. Elastomer (D)]
The polycarbonate resin composition of the present invention preferably contains an elastomer (D). By containing the elastomer (D), the impact resistance of the polycarbonate resin composition can be improved.

  The elastomer used in the present invention is preferably a graft copolymer obtained by graft copolymerizing a rubbery polymer with a monomer component copolymerizable therewith. The production method of the graft copolymer may be any production method such as bulk polymerization, solution polymerization, suspension polymerization, and emulsion polymerization, and the copolymerization method may be single-stage graft or multi-stage graft.

The rubber component usually has a glass transition temperature of 0 ° C. or lower, preferably −20 ° C. or lower, more preferably −30 ° C. or lower.
Specific examples of the rubber component include polybutadiene rubber, polyisoprene rubber, polybutyl acrylate and poly (2-ethylhexyl acrylate), polyalkyl acrylate rubber such as butyl acrylate-2-ethylhexyl acrylate copolymer, and polyorganosiloxane rubber. Silicone rubber, butadiene-acrylic composite rubber, composite rubber made of polyorganosiloxane rubber and polyalkylacrylate rubber, styrene-butadiene rubber, ethylene-propylene rubber, ethylene-butene rubber, ethylene-α-olefin system such as ethylene-octene rubber Examples thereof include rubber, ethylene-acrylic rubber, and fluorine rubber. These may be used alone or in combination of two or more.
Among these, polybutadiene rubber, polyalkyl acrylate rubber, polyorganosiloxane rubber, composite rubber composed of polyorganosiloxane rubber and polyalkyl acrylate rubber, and styrene-butadiene rubber are preferable from the viewpoint of mechanical properties and surface appearance.

Specific examples of monomer components that can be graft copolymerized with the rubber component include aromatic vinyl compounds, vinyl cyanide compounds, (meth) acrylic acid ester compounds, (meth) acrylic acid compounds, glycidyl (meth) acrylates, and the like. Epoxy group-containing (meth) acrylic acid ester compounds; maleimide compounds such as maleimide, N-methylmaleimide and N-phenylmaleimide; α, β-unsaturated carboxylic acid compounds such as maleic acid, phthalic acid and itaconic acid and their anhydrides (For example, maleic anhydride, etc.). These monomer components may be used alone or in combination of two or more.
Of these, aromatic vinyl compounds, vinyl cyanide compounds, (meth) acrylic acid ester compounds, and (meth) acrylic acid compounds are preferable from the viewpoint of mechanical properties and surface appearance, and more preferably aromatic vinyl compounds, A vinyl cyanide compound and a (meth) acrylic acid ester compound are preferred, and a (meth) acrylic acid ester compound is more preferred. Specific examples of the (meth) acrylate compound include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, cyclohexyl (meth) acrylate, octyl (meth) acrylate, (meta ) Phenyl acrylate and the like.

The graft copolymer obtained by copolymerizing the rubber component is preferably of the core / shell type graft copolymer type from the viewpoint of impact resistance and surface appearance. Among these, at least one rubber component selected from a polybutadiene-containing rubber, a polybutyl acrylate-containing rubber, a polyorganosiloxane rubber, a polyorganosiloxane rubber and a polyalkyl acrylate rubber (Interpenetrating Polymer Network (IPN) type) composite rubber is used. A core / shell type graft copolymer comprising a shell layer formed by copolymerizing (meth) acrylic acid ester around the core layer is particularly preferred.
The core / shell type graft copolymer preferably contains 40% by mass or more of a rubber component, and more preferably contains 60% by mass or more. Moreover, what contains 10 mass% or more of (meth) acrylic acid is preferable.

Preferable specific examples of these core / shell type graft copolymers include methyl methacrylate-butadiene-styrene copolymer (MBS), methyl methacrylate-acrylonitrile-butadiene-styrene copolymer (MABS), and methyl methacrylate-butadiene copolymer. Copolymer (MB), methyl methacrylate-acrylic rubber copolymer (MA), methyl methacrylate-acrylic rubber-styrene copolymer (MAS), methyl methacrylate-acrylic-butadiene rubber copolymer, methyl methacrylate-acrylic-butadiene rubber- Examples thereof include styrene copolymers, methyl methacrylate- (acryl silicone silicone IPN (interpenetrating polymer network) rubber) copolymers, and the like. Such rubbery polymers may be used alone or in combination of two or more.

  Examples of such core / shell type graft copolymers include “Paraloid EXL2602”, “Paraloid EXL2603”, “Paraloid EXL2655”, “Paraloid EXL2311”, “Paraloid EXL2313”, manufactured by Rohm and Haas Japan. “Paraloid EXL2315”, “Paraloid KM330”, “Paraloid KM336P”, “Paraloid KCZ201”, manufactured by Mitsubishi Rayon Co., Ltd., “Metabrene C-223A”, “Metabrene E-901”, “Metabrene S-2001”, “Metabrene SRK-” 200, manufactured by Kaneka Corporation, “Kane Ace M-511”, “Kane Ace M-600”, “Kane Ace M-400”, “Kane Ace M-580”, “Kane Ace MR-01”, and the like.

  The content of the elastomer (D) is preferably 0.5 parts by mass or more, more preferably 0.75 parts by mass or more, further preferably 1 part by mass or more, with respect to 100 parts by mass of the polycarbonate resin. Is 10 parts by mass or less, more preferably 7.5 parts by mass or less, and still more preferably 6 parts by mass or less. When the elastomer (D) is not more than the lower limit of the above range, the impact resistance improvement effect by the elastomer may be insufficient, and when the content of the elastomer (D) exceeds the upper limit of the above range, There is a possibility that the appearance defect, heat resistance, and flame retardancy of a molded product obtained by molding the polycarbonate resin composition may be reduced.

[6. Phosphorus stabilizer]
The polycarbonate resin composition of the present invention preferably contains a phosphorus-based stabilizer as necessary. Any known phosphorous stabilizer can be used. Specific examples include phosphorus oxo acids such as phosphoric acid, phosphonic acid, phosphorous acid, phosphinic acid, and polyphosphoric acid; acidic pyrophosphate metal salts such as acidic sodium pyrophosphate, acidic potassium pyrophosphate, and acidic calcium pyrophosphate; phosphoric acid Group 1 or Group 2B metal phosphates such as potassium, sodium phosphate, cesium phosphate and zinc phosphate; organic phosphate compounds, organic phosphite compounds, organic phosphonite compounds, etc. Particularly preferred.

Organic phosphite compounds include triphenyl phosphite, tris (monononylphenyl) phosphite, tris (monononyl / dinonyl phenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphite, monooctyl Diphenyl phosphite, dioctyl monophenyl phosphite, monodecyl diphenyl phosphite, didecyl monophenyl phosphite, tridecyl phosphite, trilauryl phosphite, tristearyl phosphite, 2,2-methylenebis (4,6-di- tert-butylphenyl) octyl phosphite and the like. Specific examples of such organic phosphite compounds include, for example, “Adeka Stub 1178”, “Adeka Stub 2112”, “Adeka Stub HP-10” manufactured by Adeka Corporation, “JP-351” manufactured by Johoku Chemical Industry Co., Ltd., “ JP-360 "," JP-3CP "," Irgaphos 168 "manufactured by Ciba Specialty Chemicals, and the like.
In addition, 1 type may contain phosphorus stabilizer and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the phosphorus stabilizer is usually 0.001 parts by mass or more, preferably 0.01 parts by mass or more, more preferably 0.03 parts by mass or more, with respect to 100 parts by mass of the polycarbonate resin (A). Moreover, it is 1 mass part or less normally, Preferably it is 0.7 mass part or less, More preferably, it is 0.5 mass part or less. If the content of the phosphorus stabilizer is less than or equal to the lower limit of the range, the thermal stability effect may be insufficient, and if the content of the phosphorus stabilizer exceeds the upper limit of the range, the effect May stop and become economical.

[7. Phenolic stabilizer]
The polycarbonate resin composition of the present invention preferably contains a phenol-based stabilizer. As a phenol type stabilizer, a hindered phenol type antioxidant is mentioned, for example. Specific examples thereof include pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl). ) Propionate, thiodiethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], N, N′-hexane-1,6-diylbis [3- (3,5-di-) tert-butyl-4-hydroxyphenylpropionamide), 2,4-dimethyl-6- (1-methylpentadecyl) phenol, diethyl [[3,5-bis (1,1-dimethylethyl) -4-hydroxyphenyl ] Methyl] phosphoate, 3,3 ′, 3 ″, 5,5 ′, 5 ″ -hexa-tert-butyl-a, a ′, a ″-(mesi Tylene-2,4,6-triyl) tri-p-cresol, 4,6-bis (octylthiomethyl) -o-cresol, ethylenebis (oxyethylene) bis [3- (5-tert-butyl-4- Hydroxy-m-tolyl) propionate], hexamethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], 1,3,5-tris (3,5-di-tert- Butyl-4-hydroxybenzyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) -trione, 2,6-di-tert-butyl-4- (4,6-bis ( Octylthio) -1,3,5-triazin-2-ylamino) phenol, 2- [1- (2-hydroxy-3,5-di-tert-pentylphenyl) ethyl] -4,6-di-te t- pentylphenyl acrylate.

Among them, pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate preferable. Specific examples of such phenolic antioxidants include, for example, “Irganox 1010” and “Irganox 1076” manufactured by Ciba Specialty Chemicals, “Adekastab AO-50” and “Adekastab” manufactured by Adeka. AO-60 "etc. are mentioned.
In addition, 1 type may contain the phenol type stabilizer, and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the phenol-based stabilizer is usually 0.001 part by mass or more, preferably 0.01 part by mass or more, and usually 1 part by mass or less, preferably 100 parts by mass of the polycarbonate resin (A). 0.5 parts by mass or less. When the content of the phenolic stabilizer is not more than the lower limit of the above range, the effect as the phenolic stabilizer may be insufficient, and the content of the phenolic stabilizer exceeds the upper limit of the above range. If this is the case, the effect may reach its peak and not economical.

[8. Lubricant]
Moreover, it is also preferable to contain a lubricant if necessary. Examples of the lubricant include aliphatic carboxylic acids, esters of aliphatic carboxylic acids and alcohols, aliphatic hydrocarbon compounds having a number average molecular weight of 200 to 15,000, and polysiloxane silicone oils.

  Examples of the aliphatic carboxylic acid include saturated or unsaturated aliphatic monovalent, divalent or trivalent carboxylic acid. Here, the aliphatic carboxylic acid includes alicyclic carboxylic acid. Among these, preferable aliphatic carboxylic acids are monovalent or divalent carboxylic acids having 6 to 36 carbon atoms, and aliphatic saturated monovalent carboxylic acids having 6 to 36 carbon atoms are more preferable. Specific examples of such aliphatic carboxylic acids include palmitic acid, stearic acid, caproic acid, capric acid, lauric acid, arachidic acid, behenic acid, lignoceric acid, serotic acid, mellicic acid, tetrariacontanoic acid, montanic acid, adipine Examples include acids and azelaic acid.

  As aliphatic carboxylic acid in ester of aliphatic carboxylic acid and alcohol, the same thing as the said aliphatic carboxylic acid can be used, for example. On the other hand, examples of the alcohol include saturated or unsaturated monohydric or polyhydric alcohols. These alcohols may have a substituent such as a fluorine atom or an aryl group. Among these, monovalent or polyvalent saturated alcohols having 30 or less carbon atoms are preferable, and aliphatic saturated monohydric alcohols or aliphatic saturated polyhydric alcohols having 30 or less carbon atoms are more preferable. Here, the term “aliphatic” is used as a term including alicyclic compounds.

  Specific examples of such alcohols include octanol, decanol, dodecanol, stearyl alcohol, behenyl alcohol, ethylene glycol, diethylene glycol, glycerin, pentaerythritol, 2,2-dihydroxyperfluoropropanol, neopentylene glycol, ditrimethylolpropane, dipentaerythritol, and the like. Is mentioned.

  In addition, said ester may contain aliphatic carboxylic acid and / or alcohol as an impurity. Moreover, although said ester may be a pure substance, it may be a mixture of a plurality of compounds. Furthermore, the aliphatic carboxylic acid and alcohol which combine to form one ester may be used alone or in combination of two or more in any combination and ratio.

  Specific examples of esters of aliphatic carboxylic acids and alcohols include beeswax (a mixture based on myricyl palmitate), stearyl stearate, behenyl behenate, stearyl behenate, glycerin monopalmitate, glycerin monostearate Examples thereof include rate, glycerol distearate, glycerol tristearate, pentaerythritol monopalmitate, pentaerythritol monostearate, pentaerythritol distearate, pentaerythritol tristearate, pentaerythritol tetrastearate and the like.

  Examples of the aliphatic hydrocarbon having a number average molecular weight of 200 to 15,000 include liquid paraffin, paraffin wax, microwax, polyethylene wax, Fischer-Tropsch wax, and α-olefin oligomer having 3 to 12 carbon atoms. Here, the aliphatic hydrocarbon includes alicyclic hydrocarbons. Further, these hydrocarbons may be partially oxidized.

Among these, paraffin wax, polyethylene wax, or a partial oxide of polyethylene wax is preferable, and paraffin wax and polyethylene wax are more preferable.
The number average molecular weight of the aliphatic hydrocarbon is preferably 5,000 or less.
The aliphatic hydrocarbon may be a single substance, but even a mixture of various constituent components and molecular weights can be used as long as the main component is within the above range.

  Examples of the polysiloxane silicone oil include dimethyl silicone oil, methylphenyl silicone oil, diphenyl silicone oil, and fluorinated alkyl silicone.

  In addition, 1 type may contain the lubricant mentioned above, and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the lubricant is usually 0.001 part by mass or more, preferably 0.01 part by mass or more, and usually 2 parts by mass or less, preferably 1 part by mass with respect to 100 parts by mass of the polycarbonate resin (A). It is as follows. When the content of the lubricant is less than or equal to the lower limit of the above range, the effect of releasability may not be sufficient, and when the content of the lubricant exceeds the upper limit of the above range, the hydrolysis resistance is reduced, injection There is a possibility of mold contamination during molding.

[9. Other ingredients]
The polycarbonate resin composition of the present invention may contain other components in addition to those described above as necessary, as long as the desired physical properties are not significantly impaired. Examples of other components include resins other than polycarbonate resins and various resin additives. In addition, 1 type may contain other components and 2 or more types may contain them by arbitrary combinations and ratios.

Other resins Examples of the other resins include thermoplastic polyester resins such as polyethylene terephthalate resin, polytrimethylene terephthalate, and polybutylene terephthalate resin;
Polystyrene resin, high impact polystyrene resin (HIPS), acrylonitrile-styrene copolymer (AS resin), acrylonitrile-styrene-acrylic rubber copolymer (ASA resin), acrylonitrile-ethylenepropylene rubber-styrene copolymer (AES resin) And the like; polyolefin resins such as polyethylene resins and polypropylene resins; polyamide resins; polyimide resins; polyetherimide resins; polyurethane resins; polyphenylene ether resins; polyphenylene sulfide resins;
In addition, 1 type may contain other resin and 2 or more types may contain it by arbitrary combinations and ratios.

-Resin additive Examples of the resin additive include ultraviolet absorbers, dyes and pigments, antistatic agents, antifogging agents, antiblocking agents, fluidity improvers, plasticizers, dispersants, antibacterial agents, and the like. In addition, 1 type may contain resin additive and 2 or more types may contain it by arbitrary combinations and a ratio.
Hereinafter, the example of an additive suitable for the polycarbonate resin composition of this invention is demonstrated concretely.

... Ultraviolet absorbers Examples of ultraviolet absorbers include inorganic ultraviolet absorbers such as cerium oxide and zinc oxide; benzotriazole compounds, benzophenone compounds, salicylate compounds, cyanoacrylate compounds, triazine compounds, oxanilide compounds, malonic acid ester compounds And organic ultraviolet absorbers such as hindered amine compounds. In these, an organic ultraviolet absorber is preferable and a benzotriazole compound is more preferable. By selecting the organic ultraviolet absorber, the polycarbonate resin composition of the present invention has good transparency and mechanical properties.

Specific examples of the benzotriazole compound include, for example, 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2- [2′-hydroxy-3 ′, 5′-bis (α, α-dimethylbenzyl). ) Phenyl] -benzotriazole, 2- (2′-hydroxy-3 ′, 5′-di-tert-butyl-phenyl) -benzotriazole, 2- (2′-hydroxy-3′-tert-butyl-5 ′) -Methylphenyl) -5-chlorobenzotriazole, 2- (2'-hydroxy-3 ', 5'-di-tert-butyl-phenyl) -5-chlorobenzotriazole), 2- (2'-hydroxy-3 ', 5'-di-tert-amyl) -benzotriazole, 2- (2'-hydroxy-5'-tert-octylphenyl) benzotriazole, 2,2'-methylenebis [4 (1,1,3,3-tetramethylbutyl) -6- (2N-benzotriazol-2-yl) phenol], among others, 2- (2′-hydroxy-5′-tert-octylphenyl) ) Benzotriazole, 2,2′-methylenebis [4- (1,1,3,3-tetramethylbutyl) -6- (2N-benzotriazol-2-yl) phenol], particularly 2- (2 ′ -Hydroxy-5'-tert-octylphenyl) benzotriazole is preferred.
Specific examples of such a benzotriazole compound include “Seesorb 701”, “Seesorb 705”, “Seesorb 703”, “Seesorb 702”, “Seesorb 704”, and “Seesorb 709” manufactured by Sipro Kasei Co., Ltd. “Biosorb 520”, “Biosorb 582”, “Biosorb 580”, “Biosorb 583” manufactured by Yakuhin Kagaku Co., Ltd. “Chemisorb 71”, “Chemisorb 72” manufactured by Chemipro Kasei Co., Ltd. “Siasorb UV5411” manufactured by Cytec Industries, Inc. “ “LA-32”, “LA-38”, “LA-36”, “LA-34”, “LA-31”, “Tinubin P”, “Tinubin 234”, “Tinubin 326” manufactured by Ciba Specialty Chemicals , “Tinuvin 327”, “tinuvin 328”, etc.

  Specific examples of the benzophenone compound include, for example, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-methoxybenzophenone-5-sulfonic acid, 2-hydroxy-4-n-octoxy Benzophenone, 2-hydroxy-n-dodecyloxybenzophenone, bis (5-benzoyl-4-hydroxy-2-methoxyphenyl) methane, 2,2'-dihydroxy-4-methoxybenzophenone, 2,2'-dihydroxy-4 4,4′-dimethoxybenzophenone and the like. Specific examples of such a benzophenone compound include “Seesorb 100”, “Seesorb 101”, “Seesorb 101S”, “Seesorb 102”, and “Seesorb 102” manufactured by Cypro Kasei Co., Ltd. Seesorb 103 ", joint medicine “Biosorb 100”, “Biosorb 110”, “Biosorb 130”, manufactured by Kemipro Kasei Co., Ltd. “Chemisorb 10”, “Chemisorb 11”, “Chemisorb 11S”, “Chemisorb 12”, “Chemsorb 13”, “Chemisorb 111” BASF “Ubinur 400”, BASF “Ubinur M-40”, BASF “Ubinur MS-40”, Cytec Industries “Thiasorb UV9”, “Thiasorb UV284”, “Thiasorb UV531”, “Thiasorb” UV24 "," ADEKA STAB 1413 "," ADEKA STAB LA-51 "manufactured by Adeka Corporation and the like.

  Specific examples of the salicylate compound include phenyl salicylate and 4-tert-butylphenyl salicylate. Specific examples of such a salicylate compound include, for example, “Seesorb 201” and “Seesorb” manufactured by Sipro Kasei Co., Ltd. 202 ”,“ Kemisorb 21 ”,“ Kemisorb 22 ”manufactured by Chemipro Kasei Co., Ltd., and the like.

  Specific examples of the cyanoacrylate compound include, for example, ethyl-2-cyano-3,3-diphenyl acrylate, 2-ethylhexyl-2-cyano-3,3-diphenyl acrylate, and the like. Specifically, for example, “Seasorb 501” manufactured by Sipro Kasei Co., Ltd., “Biosorb 910” manufactured by Kyodo Yakuhin Co., Ltd., “Ubisolator 300” manufactured by Daiichi Kasei Co., Ltd., “Ubinur N-35” manufactured by BASF, 539 "and the like.

  Examples of the triazine compound include a compound having a 1,3,5-triazine skeleton. Specific examples of such a triazine compound include, for example, “LA-46” manufactured by ADEKA Corporation, Ciba Specialty Chemicals. “Tinuvin 1577ED”, “Tinuvin 400”, “Tinuvin 405”, “Tinuvin 460”, “Tinuvin 477-DW”, “Tinuvin 479”, and the like are available.

  Specific examples of the oxanilide compound include, for example, 2-ethoxy-2′-ethyl oxalinic acid bis-arinide and the like. Specific examples of such an oxalinide compound include “Sanduboa” manufactured by Clariant Corporation. VSU "etc. are mentioned.

  As the malonic acid ester compound, 2- (alkylidene) malonic acid esters are preferable, and 2- (1-arylalkylidene) malonic acid esters are more preferable. Specific examples of such a malonic acid ester compound include “PR-25” manufactured by Clariant Japan, “B-CAP” manufactured by Ciba Specialty Chemicals, and the like.

  The content of the ultraviolet absorber is usually 0.01 parts by mass or more, preferably 0.1 parts by mass or more, and usually 3 parts by mass or less, preferably 1 with respect to 100 parts by mass of the polycarbonate resin (A). It is below mass parts. If the content of the UV absorber is below the lower limit of the above range, the effect of improving the weather resistance may be insufficient, and if the content of the UV absorber exceeds the upper limit of the above range, the mold Debogit etc. may occur and cause mold contamination. In addition, 1 type may contain the ultraviolet absorber and 2 or more types may contain it by arbitrary combinations and a ratio.

... Dye / pigment Examples of the dye / pigment include inorganic pigments, organic pigments, and organic dyes.
Examples of inorganic pigments include sulfide pigments such as cadmium red and cadmium yellow; silicate pigments such as ultramarine blue; titanium oxide, zinc white, petal, chromium oxide, iron black, titanium yellow, zinc-iron brown , Titanium Cobalt Green, Cobalt Green, Cobalt Blue, Oxide Pigment such as Copper-Chromium Black, Copper-Iron Black, Chromic Acid Pigment such as Yellow Lead and Molybdate Orange; Ferrocyan Pigment such as Bitumen Etc.

  Examples of organic pigments and organic dyes include phthalocyanine dyes such as copper phthalocyanine blue and copper phthalocyanine green; azo dyes such as nickel azo yellow; thioindigo, perinone, perylene, quinacridone, dioxazine, iso Examples thereof include condensed polycyclic dyes such as indolinone and quinophthalone; anthraquinone, heterocyclic and methyl dyes.

Of these, titanium oxide, cyanine-based, quinoline-based, anthraquinone-based, and phthalocyanine-based compounds are preferable from the viewpoint of thermal stability.
In addition, 1 type may contain the dye / pigment, and 2 or more types may contain it by arbitrary combinations and a ratio.

  The content of the dye / pigment is usually 5 parts by mass or less, preferably 3 parts by mass or less, more preferably 2 parts by mass or less with respect to 100 parts by mass of the polycarbonate resin (A). If the content of the dye / pigment is too large, the impact resistance may not be sufficient.

[10. Production method of polycarbonate resin composition]
There is no restriction | limiting in the manufacturing method of the polycarbonate resin composition of this invention, The manufacturing method of a well-known polycarbonate resin composition can be employ | adopted widely.
Specific examples include polycarbonate resin (A), phosphorus-based flame retardant (B), fluoropolymer (C), and other components blended as necessary, such as various mixers such as tumblers and Henschel mixers. And a method of melt-kneading using a mixer such as a Banbury mixer, roll, Brabender, single-screw kneading extruder, twin-screw kneading extruder, and kneader.

In addition, for example, without mixing each component in advance, or only a part of the components is mixed in advance, and fed to an extruder using a feeder and melt-kneaded to produce the polycarbonate resin composition of the present invention. You can also
Also, for example, by mixing a part of the components in advance and supplying the resulting mixture to an extruder and melt-kneading it as a master batch, this master batch is again mixed with the remaining components and melt-kneaded. The polycarbonate resin composition of the present invention can also be produced.
In addition, for example, when mixing a component that is difficult to disperse, the component that is difficult to disperse is dissolved or dispersed in a solvent such as water or an organic solvent in advance, and kneaded with the solution or the dispersion. It can also improve sex.

[11. Molded body]
The polycarbonate resin composition of the present invention is usually molded into an arbitrary shape and used as a molded body (resin composition molded body). There is no restriction | limiting in the shape, pattern, color, dimension, etc. of this molded object, What is necessary is just to set arbitrarily according to the use of the molded object.

  Examples of the molded body include parts such as electrical and electronic equipment, OA equipment, information terminal equipment, machine parts, home appliances, vehicle parts, building members, various containers, leisure goods / miscellaneous goods, and lighting equipment. Among these, it is particularly suitable for use in parts such as electrical and electronic equipment, OA equipment, information terminal equipment, home appliances, and lighting equipment, and particularly suitable for use in electrical and electronic equipment, parts of lighting equipment, sheet members, and film members. It is.

  Examples of the electric and electronic devices include display devices such as personal computers, game machines, televisions, and electronic paper, printers, copiers, scanners, fax machines, electronic notebooks and PDAs, electronic desk calculators, electronic dictionaries, cameras, and video cameras. Mobile phones, battery packs, recording medium drives and reading devices, mice, numeric keys, CD players, MD players, portable radio / audio players, and the like. Especially, it can use suitably for the battery pack of the portable equipment represented by a notebook personal computer, a mobile telephone, a camera, and a video camera.

The manufacturing method of a molded object is not specifically limited, The molding method generally employ | adopted about the polycarbonate resin composition can be employ | adopted arbitrarily. For example, injection molding method, ultra-high speed injection molding method, injection compression molding method, two-color molding method, hollow molding method such as gas assist, molding method using heat insulating mold, rapid heating mold were used. Molding method, foam molding (including supercritical fluid), insert molding, IMC (in-mold coating molding) molding method, extrusion molding method, sheet molding method, thermoforming method, rotational molding method, laminate molding method, press molding method, Examples thereof include a blow molding method. A molding method using a hot runner method can also be used.
The obtained molded article of the present invention can be used as a practical molded article having high flame retardancy and mechanical properties without impairing the excellent properties of the polycarbonate resin as described above.

Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not construed as being limited to the following examples.
In the following description, “parts” means “parts by mass” based on mass standards unless otherwise specified.

[Production of resin pellets]
Each component described in Tables 2 to 3 to be described later was blended in proportions (mass ratios) described in Tables 4 to 5, mixed for 20 minutes with a tumbler, and manufactured by Nippon Steel Works, Ltd. equipped with 1 vent. (TEX30HSST), kneaded under the conditions of a screw speed of 200 rpm, a discharge rate of 15 kg / hour, a barrel temperature of 270 ° C., the molten resin extruded in a strand shape is rapidly cooled in a water tank, and pelletized using a pelletizer, A pellet of a polycarbonate resin composition was obtained.

[Preparation of test piece]
After drying the pellets obtained by the above manufacturing method at 120 ° C. for 5 hours, the pellets were injection-molded under the conditions of a cylinder temperature of 270 ° C. and a mold temperature of 80 ° C. using an SE100DU injection molding machine manufactured by Sumitomo Machine Co., Ltd. A test piece for UL test having a length of 125 mm, a width of 13 mm, and a thickness of 0.8 mm was molded.

[Flame retardance evaluation]
The flame resistance of each polycarbonate resin composition was evaluated by conditioning the test specimen for UL test obtained by the above method for 48 hours in a temperature-controlled room at 23 ° C. and 50% humidity. The test was conducted in accordance with UL94 test (combustion test of plastic materials for equipment parts) defined by Laboratories (UL). UL94V is a method for evaluating flame retardancy from the after-flame time and drip properties after indirect flame of a burner for 10 seconds on a test piece of a predetermined size held vertically, V-0, V- In order to have flame retardancy of 1 and V-2, it is necessary to satisfy the criteria shown in Table 1 below.

ここで残炎時間とは、着火源を遠ざけた後の、試験片の有炎燃焼を続ける時間の長さである。また、ドリップによる綿着火とは、試験片の下端から約３００ｍｍ下にある標識用の綿が、試験片からの滴下（ドリップ）物によって着火されるかどうかによって決定される。なお、表４〜５中、「ＵＬ難燃性」と表記する。

Here, the after-flame time is the length of time for which the flammable combustion of the test piece is continued after the ignition source is moved away. The cotton ignition by the drip is determined by whether or not the labeling cotton, which is about 300 mm below the lower end of the test piece, is ignited by a drip from the test piece. In Tables 4 to 5, “UL flame retardancy” is used.

[Anti-flammability]
Evaluation (unit: second) was performed based on the average burning time (average of 10 tubes) when flame retardancy was evaluated by the above-described method. In Tables 4 to 5, “average combustion time” is used.

[Drip resistance]
Evaluation was made by drip establishment (average of 10 units, unit:%) when flame retardancy was evaluated by the method described above. In Tables 4 to 5, it is expressed as “drip probability”.

[Drawdown resistance]
After the pellets obtained by the above-mentioned method were dried at 120 ° C. for 5 hours, in a Capillograph 1C manufactured by Toyo Seiki Co., Ltd., orifice: φ1 mm × 10 mm, cylinder temperature: 280 ° C., preheating time: 3 minutes, shear rate: 91 The time until the strand length reached 150 mm when extruded under the condition of 2 sec ⁻¹ was measured. It means that it is excellent in drawdown-proof property, so that this value is large, and is preferable. In Tables 4 to 5, “draw-down resistance” is used.

From Examples 1 to 7 shown in Table 4, the polycarbonate resin composition containing a predetermined amount of the phosphoric flame retardant (B) and the fluoropolymers (C1 to C6) defined in the present invention in the polycarbonate resin (A) is UL. It can be seen that the flame retardancy is V-0, the average burning time is short, the flame extinguishing property is high, the flame retardancy is excellent, and the drawdown resistance is also excellent.
On the other hand, the polycarbonate resin composition of the comparative example containing the fluoropolymer (C7 to C12) that does not satisfy the requirements defined in the present invention has a poor flame retardancy of V-2, and the average combustion time is longer than that of the examples. It can be seen that the flame retardancy is poor and the drawdown resistance is slightly lowered.
Therefore, from the above Examples and Comparative Examples, it was confirmed that the effect of simultaneously satisfying a high degree of flame retardancy and high draw-down resistance was obtained for the first time by the configuration of the present invention.

  According to the polycarbonate resin composition of the present invention, a polycarbonate resin molding material having high flame retardancy and high draw-down resistance can be obtained at the same time. It can be suitably used for parts such as equipment, and its industrial utility is very high.

Claims (4)

Fluoropolymer satisfying the following formula (1) with 3 to 30 parts by mass of the phosphorus-based flame retardant (B) and a standard specific gravity (X) of 2.16 to 2.21 with respect to 100 parts by mass of the polycarbonate resin (A) ( A polycarbonate resin composition comprising 0.001 to 1 part by mass of C).
−200X + 472 ≦ Y (1)
(Y represents the tensile strength [unit: MPa] based on JIS K6891 of fluoropolymer (C).)   Furthermore, 0.5-10 mass parts of elastomers (D) are contained with respect to 100 mass parts of polycarbonate resin (A), The polycarbonate resin composition of Claim 1 characterized by the above-mentioned. The polycarbonate resin composition according to claim 1 or 2, wherein the phosphorus-based flame retardant (B) is a phosphate ester represented by the following general formula (1).

(Wherein R ¹ , R ² , R ³ and R ⁴ each represents an alkyl group having 1 to 6 carbon atoms or an aryl group having 6 to 20 carbon atoms which may be substituted with an alkyl group, and p, q , R and s are each 0 or 1, k is an integer of 1 to 5, and X ¹ represents an arylene group.)   The elastomer (D) is a graft copolymer obtained by graft polymerizing at least one selected from an aromatic vinyl compound, a vinyl cyanide compound, and a (meth) acrylic acid ester compound to a rubbery polymer. The polycarbonate resin composition according to any one of claims 1 to 3.