JP2012007142A - Optical film, polarizing plate and image display device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an optical film excellent in optical properties and having excellent ultraviolet absorbing performance, and to provide high performance polarizing plates and image display devices using the film.SOLUTION: There is provided an optical film composed of a polypropylene resin mixture comprising (A) a polypropylene resin containing a propylene polymer, (B) 2-(hydroxyphenyl)benzotriazole derivative 1 and (C) 2-(hydroxyphenyl)benzotriazole derivative 2, wherein the (C) 2-(hydroxyphenyl)benzotriazole derivative 2 is 2-(2-hydroxy-3-tert-butyl-5-methylphenyl)-5-chlorobenzotriazole and the content of the (C) to the total amount of the (B) and the (C) is 8-60 mass%, and optical plates and image display devices using the film are provided.

Description

  The present invention relates to an optical member used in an image display device, and more particularly to an optical film having ultraviolet absorption performance and excellent optical characteristics. The present invention also relates to a polarizing plate in which the optical film is provided on at least one surface of a polarizer, and an image display device using the polarizing plate.

  An optical film is a film for industrial materials that requires transparency. For example, a window film such as a scattering prevention film or an ultraviolet ray prevention film, a polarizer protective film, an optical compensation film, an antireflection film, or the like. Films for industrial use such as film for surface protection and surface protection film used for steel plates and design building materials to prevent scratches and dirt. Among these optical films, along with the development of image display devices such as liquid crystal display devices including liquid crystal cells, organic electroluminescence display devices, and touch panels, optical films used in these image display devices have attracted attention. Examples of the optical film include a retardation film provided for optical compensation and an optical film used for protecting a polarizer. As this retardation film, a retardation film produced by stretching propylene is known (see Patent Documents 1 and 2).

  The polarizing plate is an optical member having a function of transmitting only light having a specific vibration direction and shielding other light, and is widely used in the image display apparatus as described above. As such a polarizing plate, what has the structure by which the optical film for polarizer protection was provided in the single side | surface or both surfaces of the polarizer is generally used. Among these, the polarizer has a function of transmitting only light having a specific vibration direction, and a uniaxially stretched polyvinyl alcohol (hereinafter referred to as “PVA”) film dyed with iodine or a dichroic dye is used. Recently, a coating type film is also used, but there is a problem that it is generally thin and weak in strength.

Moreover, since the polarizer used for a polarizing plate is a member comprised with an organic material, there exists a problem that it is easy to deteriorate with an ultraviolet-ray. The deterioration of the organic material (resin) constituting the polarizer is generally caused by irradiation with ultraviolet rays having a wavelength of 280 to 400 nm, and the ultraviolet light in this region is absorbed (blocked) before reaching the polarizer. Accordingly, it is possible to prevent the deterioration of the polarizer or the deterioration of the liquid crystal.
Ultraviolet rays become more damaging to optical films as their wavelengths become shorter. However, because the ozone layer, atmospheric oxygen, etc. absorb sunlight with short wavelengths, ultraviolet rays with a wavelength of 280 nm or less reach the ground. . On the other hand, as described above, the deterioration of the polypropylene resin is mostly caused by irradiation with ultraviolet rays in the wavelength region of 280 to 400 nm. Therefore, in order to prevent the deterioration of the polypropylene resin, it is necessary to absorb the light beam in the range with an ultraviolet absorber that absorbs the light beam in the range. Therefore, the optical film for protecting a polarizer provided on the surface of the polarizer is provided with ultraviolet absorbing performance, so that the polarizer, the liquid crystal cell inside the polarizing plate, the phase difference plate, and each adhesive layer inside the display are protected from ultraviolet rays. A function to protect is required. Further, since the polarizer protective film may be deteriorated by irradiation with high temperature or ultraviolet light, it is necessary to impart ultraviolet absorbing performance to itself from the viewpoint of preventing deterioration of the polarizer protective film itself. .

  In particular, in a liquid crystal display device using a fluorescent tube as a backlight, it is essential to impart ultraviolet absorption performance to a protective film used in the device. In general, a liquid crystal display device using a fluorescent tube as a backlight includes two polarizers sandwiching a liquid crystal cell, and the polarizer has a structure in which a protective film is provided on both sides thereof. Here, since light is directly radiated from the fluorescent tube of the backlight to the polarizing plate, it is essential to provide an ultraviolet absorbing performance to the protective film used for the polarizing plate provided closer to the backlight. . Therefore, a polarizer protective film having an ultraviolet absorbing function on the backlight side is generally attached to the polarizer of the backlight side polarizing plate. As a polarizer protective film of the backlight side polarizing plate, a polyethylene terephthalate film (see Patent Document 3), a (meth) acrylic resin film (see Patent Document 4), a cyclic olefin polymer, and vinyl added with an ultraviolet absorber. A resin film containing a polymer is known (see Patent Document 5). However, these resin films are expensive and more inexpensive materials are required.

Therefore, a polarizer protecting optical film using a polypropylene resin has been proposed as a polarizer protecting optical film having moisture resistance and low cost (see Patent Documents 6 and 7). However, in general, the polypropylene resin itself tends to be deteriorated by high temperatures and direct sunlight. Therefore, when a polypropylene resin is used for the optical film for protecting a polarizer, it is necessary to impart ultraviolet absorption performance to the polypropylene resin. .
Examples of ultraviolet absorbers generally used for imparting ultraviolet absorption performance include oxybenzophenone compounds, benzotriazole compounds, salicylic acid ester compounds, benzophenone compounds, cyanoacrylate compounds, and nickel complex compounds. A wide variety can be mentioned. Moreover, the example which added the above ultraviolet absorbers to the propylene-type resin is also known (refer patent document 8). However, when an optical film for protecting a polarizer is prepared by mixing an ultraviolet absorber with a polypropylene resin, many ultraviolet absorbers deteriorate optical properties such as good transparency, haze, or in-plane retardation of the polypropylene resin. End up. Even if the decrease in the optical characteristics due to the use of the ultraviolet absorber is a decrease in the optical characteristics that is acceptable in other applications, the use of the optical film for protecting the polarizer requires high optical characteristics. It becomes a big problem. In addition, UV absorbers that cannot exhibit UV absorption performance unless added in a large amount, and the phenomenon that UV absorbers are deposited on the film surface during film forming processing (bleed out) occur only by adding a small amount. There are also many UV absorbers that impair suitability and product quality. Furthermore, when two or more types of ultraviolet absorbers are used in combination, there is a problem that bleeding out often occurs depending on the blending amount and blending ratio or the type of ultraviolet absorber to be combined. Therefore, whether or not to bleed when added to the resin, that is, from the viewpoint of bleed performance, it is necessary to select not only the type and combination of UV absorbers, but also the blending amount and blending ratio.

In the previous invention, the present inventors have found that a polypropylene resin using benzotriazole-based phenol as an ultraviolet absorber is suitable for an optical film for protecting a polarizer with little bleeding out of the absorber (patent) Reference 9). However, a polypropylene resin synthesized with a metallocene catalyst is excellent in that it has excellent optical properties such as low haze, excellent transparency, high visible light transmittance, and low birefringence.
By the way, with respect to the ultraviolet absorption performance of the optical film, it is generally desirable that the light transmittance is 10% or less at a wavelength of 380 nm (“KONICA TECHNIC REPORT”, vol. 16, (2003), p. 76). Development of an optical film having sufficient ultraviolet absorption performance in the wavelength region of 370 to 400 nm is desired. However, the optical film formed of the polypropylene resin added with the ultraviolet absorber disclosed in the above-mentioned Patent Document 9 satisfies a good ultraviolet absorbing performance in the wavelength region of 370 nm or less in the ultraviolet region, but is in the ultraviolet region. In the region of the wavelength of 370 to 400 nm, the ultraviolet absorption performance may not be sufficient under more severe environments or standards. More specifically, the ultraviolet absorber used in Patent Documents 4 and 5, 2- (2H-benzotriazol-2-yl) -4- (1,1,3,3-tetramethylbutyl) -phenol, In 2- (2H-benzotriazol-2-yl) -4,6-di-tert-pentylphenol, sufficient ultraviolet absorption performance cannot be obtained in the wavelength region of 370 to 400 nm. Furthermore, in this case, if the amount of the ultraviolet absorber added is increased in order to enhance the ultraviolet absorption performance in the wavelength range of 370 to 400 nm, the absorber may bleed out, and the transparency and processing suitability of the film may be impaired. there were.

International Publication No. 2007/108562 Pamphlet JP 2007-286615 A JP 2009-169393 A JP 2007-17555 A JP 2006-188555 A JP 2008-146023 A JP 2007-334295 A JP 2007-45070 A International Publication No. 2009/51188 Pamphlet

  This invention is made | formed by such a situation, and the subject of this invention is providing the optical film which is excellent in an optical characteristic and an ultraviolet-ray absorption performance, and is excellent also in an external appearance without a ultraviolet absorber bleeding out. Another object of the present invention is to provide a high-performance polarizing plate and an image display device using the same.

As a result of intensive studies to achieve the above object, the present inventors have found that the use of two kinds of ultraviolet absorbers at a specific blending ratio with respect to a polypropylene resin containing a propylene-based polymer can solve the problem. I found out that it could be solved. The present invention has been completed based on such findings.
That is, the gist of the present invention is as follows.

1. (A) a polypropylene resin containing a propylene-based polymer, (B) a 2- (hydroxyphenyl) benzotriazole derivative 1, and (C) a polypropylene resin mixture comprising a 2- (hydroxyphenyl) benzotriazole derivative 2. The (C) 2- (hydroxyphenyl) benzotriazole derivative 2 is 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole, and the (B) and (C The optical film whose content rate of this (C) with respect to the total amount of 8) is 8-60 mass%.
2. (B) 2- (hydroxyphenyl) benzotriazole derivative 1 is 2- [2-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] benzotriazole and 2- (2-hydroxy-3 The optical film as described in 1 above, which is at least one selected from (2,5-di-tert-pentylphenyl) benzotriazole.
3. 3. The optical film as described in 1 or 2 above, wherein the propylene polymer is a random copolymer of propylene and α-olefin.
4). 4. The optical film as described in any one of 1 to 3 above, wherein the propylene polymer is a propylene copolymer synthesized with a metallocene catalyst.
5). 5. The optical film as described in any one of 1 to 4 above, wherein the total content of (B) and (C) in the polypropylene resin mixture is 0.3 to 1.5% by mass.
6). 6. The optical film as described in any one of 1 to 5 above, wherein the light transmittance at a wavelength of 380 nm is 10% or less.
7). 7. The optical film as described in any one of 1 to 6 above, which is used for protecting a polarizer.
8). A polarizing plate, wherein a polarizer is used in a liquid crystal display device, and the optical film described in 7 above is provided on one side of the polarizer on the backlight side.
9. 9. The polarizing plate according to 8 above, wherein the backlight is a fluorescent tube.
10. 10. An image display device using the polarizing plate as described in 8 or 9 above.

According to the present invention, it is possible to obtain an optical film that is excellent in optical characteristics and ultraviolet absorption performance and excellent in appearance without bleeding out of the ultraviolet absorber. That is, when the above (B) and (C), which are ultraviolet absorbers with respect to the above (A) polypropylene resin, are used in a predetermined ratio, the transparency, haze, or surface of the polypropylene resin that these ultraviolet absorbers have. It was found that excellent optical properties such as internal retardation are not impaired and excellent ultraviolet absorption performance can be obtained.
The optical film of the present invention is particularly suitable for protecting a polarizer, and a high-performance polarizing plate and an image display device can be obtained by using the optical film.

It is a figure which shows the structural example of the polarizing plate of this invention. It is a figure which shows the structural example of the liquid crystal display device using the polarizing plate of this invention. 5 is a graph showing light transmittances of Example 1 and Comparative Example 1. It is a graph which shows the light transmittance of Examples 7 and 9 and Comparative Example 9.

[Optical film]
The optical film of the present invention is obtained by molding and processing a polypropylene resin mixture containing a polypropylene resin containing a propylene polymer and a mixture of predetermined benzotriazole compounds (hereinafter simply referred to as “ultraviolet absorber mixture”). Is. More specifically, (A) polypropylene resin containing a propylene-based polymer (hereinafter sometimes referred to as polypropylene resin (A)), (B) 2- (hydroxyphenyl) benzotriazole derivative 1 (hereinafter referred to as ultraviolet light). And (C) 2- (hydroxyphenyl) benzotriazole derivative 2 (hereinafter sometimes referred to as UV absorber (C)). The (C) 2- (hydroxyphenyl) benzotriazole derivative 2 is 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole, (B) And the optical film whose content rate of this (C) with respect to the total amount of (C) is 8-60 mass%.
Below, the optical film of this invention is demonstrated in detail.

<< (A) Polypropylene resin containing propylene-based polymer >>
In the present invention, the polypropylene resin means a propylene polymer, that is, a homopolymer of propylene, or a copolymer of propylene and one or more comonomers (hereinafter sometimes referred to as “propylene copolymer”). Is included. In the present invention, either a propylene homopolymer or a propylene copolymer may be used, or these may be used alone, or a mixture of a propylene homopolymer and one or more propylene copolymers. You may use, and may mix and use 2 or more types of propylene copolymers. In addition, polypropylene homopolymers or propylene copolymers having different proportions of propylene-derived structural units, molecular weight, tacticity, and the like may be mixed and used.
In the present invention, in consideration of transparency and other optical characteristics and difficulty in bleeding out the ultraviolet absorbent mixture, a propylene-based copolymer is preferable. As the propylene-based copolymer, propylene and an α-olefin are used. A random copolymer is preferred.

  The α-olefin is preferably ethylene or an α-olefin having 4 to 18 carbon atoms, more preferably an α-olefin having 4 to 12 carbon atoms. From the viewpoint of copolymerization, 1-butene and 1-pentene are preferable. 1-hexene, 1-octene, 1-heptene, 4-methyl-pentene-1, 4-methyl-hexene-1, 4,4-dimethylpentene-1, etc. are preferable, 1-butene, 1-pentene, 1 -Hexene and 1-octene are more preferable, and 1-butene and 1-hexene are more preferable. From the viewpoint of the balance between transparency and heat resistance, the proportion of propylene units in the copolymer is preferably 80 mol% or more and less than 100 mol%, and the comonomer is more than 0 to 20 mol% or less. As the comonomer, the α-olefin is not limited to one type, and two or more types can be used, and the copolymer can be a multi-component copolymer such as a terpolymer. In addition, the content of the structural unit derived from a comonomer in a copolymer can be calculated | required by the measurement of an infrared (IR) absorption spectrum.

  In addition, the polypropylene resin (A) used in the present invention is a propylene polymerized using a known polymerization catalyst such as a Ziegler-Natta catalyst or a metallocene catalyst, considering the difficulty of bleeding out of the ultraviolet absorber mixture. It is preferable that the polymer is composed of a propylene polymer, and it is preferable that the polymer is composed of a propylene polymer polymerized using a metallocene catalyst from the viewpoint of more excellent transparency. Propylene polymers polymerized using a metallocene catalyst generally have the characteristics of uniform molecular weight and crystallinity, and low molecular weight and low crystallinity components, so when the propylene polymer is used as an optical film Can have high transparency and low birefringence.

(Metallocene catalyst)
As the metallocene catalyst, a known catalyst can be appropriately used. Generally, a group 4-6 transition metal compound such as Zr, Ti, or Hf, particularly a group 4 transition metal compound and an organic transition metal compound having a cyclopentadienyl group or a cyclopentadienyl derivative group is used. be able to.

  As the group of the cyclopentadienyl derivative, an alkyl substituent such as pentamethylcyclopentadienyl, or a group in which two or more substituents are combined to form a saturated or unsaturated cyclic substituent may be used. Typically, an indenyl group, a fluorenyl group, an azulenyl group, or a partial hydrogenated product thereof can be given. Moreover, what combined several cyclopentadienyl group with the alkylene group, the silylene group, the germylene group etc. can be mentioned suitably.

(Cocatalyst)
In the production of the propylene polymer, a cocatalyst can be used together with the metallocene catalyst. The cocatalyst was selected from the group consisting of an aluminum oxy compound, an ionic compound capable of reacting with the metallocene compound to convert the metallocene compound component into a cation, or a Lewis acid, a solid acid, or a layered silicate. At least one compound can be used. Moreover, an organoaluminum compound can be added with these compounds as needed.

(Propylene Polymerization Method Using Metallocene Catalyst)
As a method for synthesizing a propylene polymer using the metallocene catalyst (polymerization method), in the presence of these catalysts, a slurry method using an inert solvent, a gas phase method using substantially no solvent, a solution method Or a bulk polymerization method using a polymerization monomer as a solvent.

(Physical properties of propylene polymer)
The propylene polymer used in the present invention preferably has a melting point (Tm) of 120 to 170 ° C. If the melting point (Tm) is within the above range, the heat resistance of the optical film is improved, and it can be used for applications requiring heat resistance such as a polarizing plate. Here, the melting point is evaluated at a temperature at which the peak of the highest intensity appears in the melting curve measured by a differential scanning calorimeter (DSC), and 10 mg of a propylene polymer press film is measured at 230 ° C. in a nitrogen atmosphere. After heat treatment for 5 minutes, cool down to 30 ° C. at a temperature drop rate of 10 ° C./min, keep the temperature at 30 ° C. for 5 minutes, and further determine the melting peak temperature when heating from 30 ° C. to 230 ° C. at a temperature rise rate of 10 ° C./min Value.

The propylene polymer preferably has an in-plane retardation measured by the following resin selection test of 20 nm or less in order to obtain an optical film having high optical isotropy. In particular, since the propylene random copolymer has a small birefringence, it can be preferably used for the optical film in the present invention.
(Resin Selection Test) A pellet-like sample is hot press-molded to produce a film having a size of 10 cm square and a thickness of 100 μm. In the above hot press molding, the resin is preheated at 220 ° C. for 5 minutes, then pressurized to 100 kgf / cm ² over 3 minutes, held at 100 kgf / cm ² for 2 minutes, and then at 30 ° C. and 30 kgf / cm ² pressure. Cool for 5 minutes. By determining the in-plane retardation of the film thus produced, a propylene-based copolymer having a small birefringence can be selected. The in-plane retardation is measured using a phase difference measuring machine under conditions of a wavelength of 589.3 nm and an incident angle of 0 degree.

The propylene polymer preferably has a melt flow rate (MFR) of 0.5 to 50 g / 10 minutes, more preferably 7 g / 10 minutes or more. This is because, if the MFR of the propylene polymer is within the above range, distortion hardly occurs during the formation of the unstretched film, so that an optical film having a small birefringence can be obtained. Moreover, it is because sufficient intensity | strength as an optical film is obtained and a post-process can be performed easily. Furthermore, the amount of additives such as MFR regulators can be reduced, so that physical properties are not adversely affected. The MFR of the mixture can be adjusted with a general MFR adjusting agent such as an organic peroxide.
In addition, the value of MFR is measured on condition of temperature 230 degreeC and load 21.18N based on JISK7210.

The width of the molecular weight distribution of the propylene-based polymer can be evaluated by the ratio (dispersion degree) of the weight average molecular weight Mw to the number average molecular weight Mn, and preferably Mw / Mn = 1-20.
Mn and Mw are measured by gel permeation chromatography (GPC) using o-dichlorobenzene at 140 ° C. as a solvent and polystyrene as a standard sample.

<Ultraviolet absorber mixture>
The polypropylene resin mixture used in the present invention contains (B) 2- (hydroxyphenyl) benzotriazole derivative 1 and (C) 2- (hydroxyphenyl) benzotriazole derivative 2, and the (C) 2- ( 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole (hydroxyphenyl) benzotriazole derivative 2 (ultraviolet absorber (C)) represented by the following general formula (1): CAS number: 3896-11-5).

  The polypropylene resin mixture used in the present invention contains the 2- (hydroxyphenyl) benzotriazole derivative represented by the general formula (1), so that the effect of improving the ultraviolet absorption performance in the wavelength region of 370 to 400 nm can be obtained. . In particular, in the derivative represented by the general formula (1), when the benzene ring forming the benzotriazole skeleton has a structure substituted with a halogen atom, the effect of improving the ultraviolet absorption performance is high in the wavelength region of 370 to 400 nm.

  The ultraviolet absorber (B) is a 2- (hydroxyphenyl) benzotriazole derivative different from the ultraviolet absorber (C), and has a structure in which phenol is bonded to a benzotriazole skeleton. If it is, there is no restriction | limiting in particular, (i) What has a functional group which has tertiary carbons, such as a tert- alkyl group, like the derivative | guide_body shown by the following general formula (2)-(5), (ii ) A compound having an oxyalkyl group having about 1 to 10 carbon atoms, such as a derivative represented by the following general formula (6), or (iii) a derivative represented by the following general formula (7) itself (Iv) a dimer or trimer via a linking group such as a derivative represented by the following general formula (5), (v) An ultraviolet ray having a structure such as a derivative represented by the general formula (1) in which a benzene ring forming a benzotriazole skeleton is substituted with a halogen atom or a hydrocarbon group such as an alkyl group Absorbers are preferred because they have a high effect of improving ultraviolet absorption performance in the wavelength range of 280 to 400 nm.

  More specifically, the derivative represented by the following general formula (2) is 2- [2-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] benzotriazole (CAS number: 3147-75). -9), and the derivative represented by the following general formula (3) is 2- (2-hydroxy-3,5-di-tert-pentylphenyl) benzotriazole (CAS number: 25973-55-1), The derivative represented by the following general formula (4) is 2- [2-hydroxy-3,5-bis (α, α-dimethylbenzyl) phenyl] benzotriazole (CAS number: 70321-86-7). The derivative represented by the formula (5) is 2,2′-methylenebis [3-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] bis (benzotriazole) (CA S number: 103597-45-1), and the derivative represented by the following general formula (6) is 2- (2-hydroxy-4-octyloxyphenyl) benzotriazole (CAS number: 3147-77-1). The derivative represented by the following general formula (7) is 2- [2-hydroxy-3-[(1,3,4,5,6,7-hexahydro-1,3-dioxo-2H-isoindole-2- Yl) methyl] -5-methylphenyl] benzotriazole (CAS number: 59129-18-9). Among these, 2- [2-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] benzotriazole represented by the following general formula (2) and the following general formula (3) 2- (2-hydroxy-3,5-di-tert-pentylphenyl) benzotriazole is preferred.

  Ultraviolet light, which is light energy, is an electromagnetic wave having a wavelength of 400 nm or less. In order to suppress the deterioration of the polarizer and the liquid crystal cell due to the ultraviolet light, it is necessary to block the ultraviolet light particularly in the wavelength range of 280 to 400 nm with a polarizer protective film. There is. The ultraviolet absorber (B) and the ultraviolet absorber (C) used in the present invention are both excellent benzotriazole-based ultraviolet absorbers, but the ultraviolet absorber (C) is easy to bleed out, and the transparency of the film Processing suitability may be impaired, and the ultraviolet absorber (B) may not have sufficient ultraviolet absorption performance in the wavelength region of 370 to 400 nm. In the present invention, it is seen that by using these ultraviolet absorbers at a predetermined ratio, excellent ultraviolet absorption performance in the wavelength region of 370 to 400 nm can be obtained, and at the same time, excellent bleed-out suppression effect can be obtained. It was issued.

(Content ratio of UV absorber (C))
In this invention, the content rate of a ultraviolet absorber (C) needs to be 8-60 mass% with respect to the total amount of a ultraviolet absorber (B) and (C). When the content ratio of the ultraviolet absorber (C) exceeds the above range, bleeding out occurs during the production of the optical film, and the transparency and processability of the film are impaired. On the other hand, when the content of the ultraviolet absorber (C) is less than the above range, the ultraviolet absorption performance in the wavelength range of 280 to 400 nm, particularly the wavelength range of 370 to 400 nm, is impaired. From such a viewpoint, the content of the ultraviolet absorber (C) is preferably 20 to 60% by mass, and more preferably 40 to 60% by mass.

(Total content of UV absorbers (B) and (C))
In this invention, it is preferable that the minimum of the total content of the ultraviolet absorbers (B) and (C) in a polypropylene resin mixture is 0.08 mass% or more with respect to a mixture. Further, from the viewpoint of obtaining good ultraviolet absorption performance, it is preferably 0.3% by mass or more, and more preferably 0.4% by mass or more.
On the other hand, the upper limit of the total content of the ultraviolet absorbers (B) and (C) in the polypropylene resin mixture is 5.5 masses with respect to the mixture from the viewpoint of preventing bleeding out of the ultraviolet absorber during film formation. % Or less is preferable. From the viewpoint of cost, the content is more preferably 1.5% by mass or less, and further preferably 1.2% by mass or less, based on the mixture.
From the above, in order to obtain a high-quality optical film, the total content of the ultraviolet absorbers (B) and (C) in the polypropylene resin mixture is preferably 0.08 to 5.5% by mass, 0 .3-1.5 mass% is more preferable, More preferably, it is 0.4-1.2 mass%.

《Other ingredients》
In the present invention, various additives and additive resins can be added as optional components of the polypropylene resin mixture as desired.
For example, depending on the desired physical properties of the film, various olefin resins other than polypropylene polymerized using a metallocene catalyst can be blended as an additive resin within a range that does not impair the birefringence and transparency required for the retardation film. In addition, weather resistance improver, light stabilizer, wear resistance improver, polymerization inhibitor, crosslinking agent, infrared absorber, antistatic agent, adhesion improver, leveling agent, thixotropic agent, coupling agent, Plasticizers, antifoaming agents, fillers, solvents and the like can be added.

<Optical film>
The optical film of the present invention is an optical film composed of the above-described polypropylene resin mixture. The thickness of the optical film of the present invention is preferably in the range of 35 to 160 μm, more preferably 60 to 120 μm.
When an ultraviolet absorber having the same absorbance is used for a film, it is known that the ultraviolet absorption performance of the film is proportional to the thickness of the film according to Lambert Beer's law expressed by the following equation.
−log (I / IO) = ε × c × d
Here, IO is the intensity of incident light, I is the intensity of transmitted light, -log (I / IO) is absorbance, ε is an optical coefficient, c is the concentration of the substance, and d is the thickness of the absorbing substance. As can be seen from this equation, it is preferable if the thickness of the optical film is within the above range because excellent ultraviolet absorption performance can be obtained and the transparency is not lowered. Moreover, the intensity | strength as an optical film is securable that thickness is 35 micrometers or more. When the thickness is 160 μm or less, sufficient flexibility can be obtained, and since it is lightweight, handling is easy and advantageous in terms of cost.

  The flexural modulus of the optical film of the present invention is preferably 700 MPa or more. When the flexural modulus is within the above range, sufficient rigidity is obtained when handled in a film state, post-processing can be easily performed, and there is sufficient scratch resistance to function as a protective sheet for a polarizing plate. It is because it is obtained. Furthermore, the flexural modulus of the optical film of the present invention is more preferably 900 MPa or more. This is because if the pressure is 900 MPa or more, the in-plane retardation can be stabilized when manufactured by T-die extrusion. Here, the flexural modulus is measured according to JIS K7171.

  There is no restriction | limiting in particular as an adjustment method of the bending elastic modulus of an optical film, It can adjust with the following methods. For example, a method of selecting by the original properties (crystallinity, average molecular weight, etc.) of polypropylene, a method of adding a filler selected from inorganic or organic fillers to a resin, a method of adding a crosslinking agent, etc. Examples thereof include a method of mixing two or more different types of resins, a method of selecting a plasticizer composition of a curable resin, or a method of appropriately combining a plurality of these methods.

  The tensile strength of the optical film is preferably 20 MPa or more. When the pressure is 20 MPa or more, when the polarizer photon protective film is molded, when the optical film is bonded to the polarizer via the adhesive layer by a roll-to-roll method, the orientation is not applied, and the phase difference This is because the performance of the polarizing plate can be improved. Here, in this invention, tensile strength shall be measured based on ASTMD638 (Type4 conditions).

  The surface of the optical film of the present invention that is in contact with the polarizer can be subjected to easy adhesion treatment in order to improve adhesion. Examples of the easy adhesion treatment include surface treatment such as corona treatment, plasma treatment, low-pressure UV treatment, and saponification treatment, and a method of forming an anchor layer, and these can be used in combination. Among these, a corona treatment, a method of forming an anchor layer, and a method of using these in combination are preferable.

  In addition, a functional layer is laminated on the surface of the optical film, and various functions such as a so-called hard coat function, anti-fogging coat function, anti-fouling coating function, and anti-glare coating function having high hardness and scratch resistance. Further, an antireflection coating function, an ultraviolet shielding coating function, an infrared shielding coating function, and the like can be provided.

<< Optical film manufacturing method >>
The optical film of the present invention is prepared by mixing the above-described polypropylene resin (A), ultraviolet absorbers (B) and (C) with various additives and additive resins as desired, and heat-melting them, followed by extrusion. It can be manufactured by being molded into a film shape by various molding methods such as a coating molding method, a casting method, a T-die extrusion molding method, a water cooling method inflation method, an air cooling method inflation method, and an injection molding method. In the present invention, since it is preferable that the optical film provided on the polarizer is not oriented, an unstretched T-die extrusion method that does not require stretching, or an inflation method is preferable.
The heating temperature during processing is usually in the range of 160 to 250 ° C, preferably 190 to 250 ° C. If heating temperature is in the said range, the optical film which is more excellent in performance stability can be obtained.
The optical film of the present invention thus obtained is excellent in optical properties and ultraviolet absorption performance, and the UV absorber does not bleed out and is excellent in appearance, so it is particularly suitably used as an optical film for protecting a polarizer. .

[Polarizer]
The optical film of the present invention can be used as a polarizer protective film provided on at least one surface of a polarizer. As a method of providing an optical film on a polarizer, a method of directly forming an optical film for protecting a polarizer on a polarizer or an optical film for protecting a polarizer are prepared in advance, and then an adhesive layer A method of bonding to a polarizer through a film is mentioned, and any method may be used.
In FIG. 1, the structural example of the polarizing plate of this invention is shown. In FIG. 1, reference numeral 2 denotes a polarizer, and the optical film 1 of the present invention is provided on one side of the polarizer via an adhesive layer (not shown) to constitute a polarizing plate 3 as a whole. And the polarizing plate of this invention is used for a liquid crystal display device, and has the structure that the optical film of this invention is provided in the single side | surface of the backlight side mentioned later.

《Polarizer》
As the polarizer used in the polarizing plate, any polarizer may be used as long as it has a function of transmitting only light having a specific vibration direction. In general, a PVA polarizer is preferably used.
Examples of PVA polarizers include hydrophilic polymers such as PVA films, partially formalized polyvinyl alcohol films, and ethylene / vinyl acetate copolymer partially saponified films, and two colors such as iodine and dichroic dyes. And uniaxially stretched by adsorbing the active substance. Among these, a polarizer composed of a PVA film and a dichroic substance such as iodine is preferably used. The thickness of these polarizers is not particularly limited, and is generally about 1 to 100 μm.

<< Polarizing plate manufacturing method >>
The polarizing plate is, for example, a process of uniaxially stretching a PVA film as described above, a process of dyeing a PVA resin film with a dichroic dye, and adsorbing the dichroic dye, and a dichroic dye being adsorbed. A process for treating a PVA-based film with an aqueous boric acid solution, a step for washing with water after the boric acid aqueous solution treatment, and a uniaxially stretched PVA-based film on which dichroic dyes are adsorbed and oriented by applying these steps It is manufactured through a process of attaching an optical film.

The polarizer protective optical film can be attached by an adhesive layer provided by applying an adhesive on either or both sides of the polarizer protective film or the polarizer. It is preferable to use a known PVA adhesive for forming the adhesive layer.
The adhesive layer is formed by applying an adhesive on either or both sides of the polarizer protective film or the polarizer. The thickness of the adhesive layer is preferably 0.01 to 10 μm, more preferably 0.03 to 5 μm, since it is not preferable in terms of the adhesive property of the polarizer protective film if the thickness after drying becomes too thick. .

  Also, when bonding the polarizer protective film to the polarizer, surface treatment such as corona treatment, plasma treatment, low-pressure UV treatment, saponification treatment, etc. to improve the adhesion to the surface of the polarizer protective film in contact with the polarizer. And an easy adhesion treatment such as a method of forming an anchor layer. Of these, a corona treatment, a method of forming an anchor layer, and a method of using these in combination are preferable.

Next, an adhesive layer is formed on the surface subjected to the easy adhesion treatment as described above, and the polarizer and the polarizer protective film are bonded to each other through the adhesive layer.
Bonding of the polarizer and the polarizer protective film can be performed with a roll laminator or the like. The heating drying temperature and drying time are appropriately determined according to the type of adhesive.

(Other)
In the polarizing plate in which the optical film of the present invention is formed on one surface of the polarizer, the optical film of the present invention can be formed on the other surface of the polarizer as necessary, or from other resins. A film can be formed. Examples of the film made of other resins include cellulose film, polyethylene terephthalate film, polycarbonate film, cyclic polyolefin film, maleimide resin film, and fluorine resin film. Among these, cellulose films such as triacetylcellulose are known to have good water drainage due to their high water vapor permeability, and the water vapor permeability of optical films using the polypropylene resin of the present invention is low and difficult to pass water. For this reason, it is desirable to attach a cellulose-based film to the other surface because it facilitates the removal of water in the drying step when manufacturing the polarizing plate. The film made of the other resin may be a retardation film having a specific retardation.

In order to improve the surface property and scratch resistance, or to provide a known antiglare function such as antireflection or low reflection treatment as necessary, the polarizing plate is at least one layer more than the polarizer protective film. A laminate having a hard coat layer or an antireflection layer is preferred. In this case, the order of lamination of the hard coat layer and the antireflection layer with respect to the polarizer protective film does not matter.
The laminate can be produced by providing a polarizer protective film with a hard coat layer or an antireflection layer. Examples of the hard coat layer and the antireflection layer include ultraviolet curable resins such as ultraviolet curable acrylic urethane, ultraviolet curable epoxy acrylate, ultraviolet curable (poly) ester acrylate, and ultraviolet curable oxetane, silicone resins, and acrylic resins. Examples thereof include a hard coat layer made of a resin, a urethane hard coat agent, and the like. From the viewpoint of transparency, scratch resistance, and chemical resistance, the hard coat layer is preferably made of an ultraviolet curable resin. These hard coat layers and antireflection layers can be used in one or more kinds.
The thickness of the hard coat layer and the antireflection layer is preferably from 0.1 to 100 μm, particularly preferably from 1 to 50 μm, and further preferably from 2 to 20 μm. In addition, a primer treatment may be performed between the hard coat layer or the antireflection layer.
Moreover, the said laminated body can also be produced by laminating | stacking a hard coat film and an antireflection film on a polarizer protective film. The hard coat film and the antireflection film can be produced by, for example, providing a polyethylene terephthalate (PET) film containing no ultraviolet absorber and providing the hard coat layer or the antireflection layer.

[Image display device]
The polarizing plate using the optical film of the present invention can be preferably used in various display devices. The image display device is not particularly limited as long as it uses a polarizing plate, and examples thereof include a liquid crystal display device including a liquid crystal cell, an organic EL display device, and a touch panel. Among them, the optical film of the present invention is used. From the viewpoint of taking advantage of the features, the polarizing plate using the optical film is preferably used for a liquid crystal display device. In the case of a liquid crystal display, an image display device is generally formed by appropriately assembling components such as a liquid crystal cell, an optical film, and an illumination system as necessary, and incorporating a drive circuit. In the invention, the configuration of the image display device is not particularly limited except that the polarizing plate described above is used. For example, an appropriate image display device such as an image display device in which a polarizing plate is disposed on one side or both sides of a liquid crystal cell, or a backlight or a reflection plate as an illumination system is exemplified. As the liquid crystal cell, any type such as a TN type, an STN type, or a π type can be used. When configuring an image display device, for example, appropriate components such as a diffusion plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusion plate, and a backlight are placed at appropriate positions. A layer or two or more layers can be arranged.
Below, the example of the liquid crystal display device containing a liquid crystal cell is demonstrated.

<< Liquid Crystal Display Device Including Liquid Crystal Cell >>
As an example of the image display device of the present invention, FIG. 2 shows a configuration example of a liquid crystal display device including the polarizing plate of the present invention. In FIG. 2, 8 indicates a liquid crystal cell. Examples of the liquid crystal cell 8 include an active matrix driving type typified by a thin film transistor type, a simple matrix driving type typified by a twisted nematic type, and a super twisted nematic type. An upper polarizing plate 7 (a polarizing plate on the upper surface side of the panel with respect to the liquid crystal cell) is laminated on one surface of the liquid crystal cell 8 via an adhesive layer (not shown) and a retardation plate 15. A lower polarizing plate 12 (a polarizing plate on the backlight side with respect to the liquid crystal cell) is laminated on the other surface. The upper polarizing plate 7 has a polarizer 5 at the center, polarizer protective films 4 and 6 are laminated on both sides of the polarizer 5, and the lower polarizing plate 12 has a polarizer 10 at the center. Polarizer protective films 9 and 11 are laminated on both sides of the polarizer 10. In the configuration example shown in FIG. 2, an antireflection layer (or antireflection film) 14 is further provided on the polarizer protective film 4 provided on the panel upper surface side of the upper polarizing plate.

  The optical film of the present invention can be used for any of the polarizer protective films 4, 6, 9 and 11, but is preferably used as the polarizer protective films 4 and 11. When used as the polarizer protective film 4, the ultraviolet rays of sunlight and external light (light from the outside of the liquid crystal display device) can be blocked, and when used as the polarizer protective film 11, the ultraviolet rays from the backlight are blocked. Because it can. In addition, the optical film of the present invention is preferably used in a liquid crystal display device in which a fluorescent tube is used as a backlight from the viewpoint of sufficiently utilizing the performance. Since the fluorescent tube emits a lot of ultraviolet rays, the excellent ultraviolet absorption performance of the optical film of the present invention is effective.

When laminating the upper polarizing plate 7 or the lower polarizing plate 12 and the liquid crystal cell 8, an adhesive layer may be provided in advance on the upper polarizing plate 7, the lower polarizing plate 12 or the liquid crystal cell 6. The pressure-sensitive adhesive used here is not particularly limited. For example, an acrylic pressure-sensitive adhesive is excellent in optical transparency, exhibits appropriate wettability, cohesiveness, and adhesive pressure-sensitive adhesive properties, weather resistance, heat resistance, etc. Preferably, it is preferable.
The pressure-sensitive adhesive is required to be excellent in optical transparency, moderate wettability, cohesiveness, adhesive properties such as adhesion, weather resistance, heat resistance and the like. Furthermore, the moisture absorption rate is low in terms of prevention of foaming and peeling phenomena due to moisture absorption, deterioration of optical characteristics due to thermal expansion differences, prevention of warping of liquid crystal cells, and the formation of high-quality and durable image display devices. Therefore, a pressure-sensitive adhesive layer having excellent heat resistance is required.

  Application of the above-mentioned pressure-sensitive adhesive to the polarizing plate is, for example, 10 to 40% by mass in which a base polymer or a composition thereof is dissolved or dispersed in a solvent composed of a single solvent or a mixture of appropriate solvents such as toluene and ethyl acetate. Prepare a pressure-sensitive adhesive solution to the extent, and apply it directly on the polarizing plate by an appropriate development method such as a coating method such as gravure coating, bar coating, roll coating, or casting method, or according to this method. Examples thereof include a method of forming an adhesive layer on a releasable base film and transferring it to a polarizing plate.

The pressure-sensitive adhesive layer can be provided on one side or both sides of the polarizing plate as a superimposed layer of different compositions or types. Moreover, when providing in both surfaces, the adhesive does not need to be the same composition in the front and back of a polarizing plate, and it is not necessary to be the same thickness. It can also be set as the adhesive layer of a different composition and different thickness.
The thickness of the pressure-sensitive adhesive layer can be appropriately determined according to the purpose of use and adhesive force, and is generally 1 μm to 500 μm, preferably 5 μm to 200 μm, particularly preferably 10 μm to 100 μm.

  The exposed surface of the pressure-sensitive adhesive layer is coated with an appropriate thin film such as a plastic film, if necessary, with an appropriate release agent such as a silicone film for the purpose of preventing contamination until it is put to practical use. It is preferable that the released release film is temporarily attached and covered. Thereby, it can prevent contacting an adhesive layer in the usual handling state.

EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited at all by this example.
(Evaluation methods)
(1) Evaluation of UV absorption performance Using a UV-visible absorption spectrometer (“UV-2400 (model number)” manufactured by Shimadzu Corporation), wavelengths of 280 nm, 330 nm, 370 nm, 375 nm, 380 nm, 385 nm, 390 nm, 395 nm, 400 nm The light transmittance of the optical film was measured under the conditions of Examples 1 to 6 and Comparative Examples 2 to 5, and the light transmittance of Comparative Example 1 was set to 100, and the index was expressed by the following formula (i). . Moreover, about Examples 7-12 and Comparative Examples 7-9, the light transmittance of the comparative example 6 was set to 100, and the index display was carried out by the following (ii) formulas. The smaller the index, the better the ultraviolet absorption performance. Specifically, when the index was 90 or less, it was judged good.
(I) UV absorption performance index = (UV light transmittance of Examples 1 to 6 and Comparative Examples 2 to 5 / UV light transmittance of Comparative Example 1) × 100
(Ii) UV absorption performance index = (UV light transmittance of Examples 7 to 12 and Comparative Examples 7 to 9 / UV light transmittance of Comparative Example 6) × 100
(2) Evaluation of ultraviolet absorption performance at wavelength 380 nm The ultraviolet absorption performance at wavelength 380 nm measured in the above (1) was evaluated according to the following criteria.
A: The ultraviolet ray transmittance is less than 10%. O: The ultraviolet ray transmittance is 10% or more and less than 40%. X: The ultraviolet ray transmittance is 40% or more. (3) Haze evaluation According to JIS K7105. The hazes of the optical films obtained in Examples and Comparative Examples were measured and evaluated according to the following criteria.
◎: Haze is less than 5% ○: Haze is 5% or more and less than 10% ×: Haze is 10% or more (4) Evaluation of visible light transmittance UV-Visible Absorption Spectrometer (Shimadzu Corporation “UV-2400” ) "), The light transmittance of the optical film was measured under the conditions of wavelengths of 550 nm and 750 nm, and evaluated according to the following criteria.
A: Light transmittance is 90% to 100%
○: Light transmittance is 80% or more and less than 90% ×: Light transmittance is less than 80% (5) Appearance evaluation (bleed out)
The produced optical film was left for 1000 hours in an environment of condition 1: temperature of 80 ° C. and relative humidity of 10 to 40% (dry condition), condition 2: temperature of 60 ° C. and relative humidity of 90%. The appearance of the optical film after being left under the conditions 1 and 2 (presence / absence of bleeding out of the ultraviolet absorber) was visually evaluated according to the following criteria.
○: Appearance defects such as whitening due to bleed were not confirmed.

Example 1
Propylene copolymer (Propylene copolymer polymerized using metallocene catalyst ("Wintech (registered trademark)" manufactured by Nippon Polypro Co., Ltd., flexural modulus: 900 MPa, melting point: 142 ° C, MFR: 30 g) / 10 minutes), hereinafter referred to as “PP-A”) in 99.5 parts by mass of 2- [2-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] Benzotriazole ("TINUVIN329 (trade name)" manufactured by BASF Corporation. Hereafter referred to as "UV-B1") 0.25 parts by mass and 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) ) -5-Chlorobenzotriazole ("TINUVIN 326 (trade name)" manufactured by BASF Corporation. Hereinafter referred to as "UV-C") 0.25 part by mass is added and mixed. The polypropylene resin mixture was heated and melted. An optical film was obtained by extrusion-molding the resin mixture with a film thickness of 80 μm under conditions of a processing temperature of 200 ° C. and a take-up roll temperature of 50 ° C.

(Example 2)
In Example 1, PP-A was mixed with a propylene copolymer (a propylene copolymer with a Ziegler-Natta catalyst ("J-3021GR (trade name)", manufactured by Prime Polymer Co., Ltd., flexural modulus: 1000 MPa, melting point). : 150 ° C., MFR: 33 g / 10 min), and hereinafter referred to as “PP-B”), an optical film was obtained in the same manner as in Example 1.

(Example 3)
An optical film was obtained in the same manner as in Example 1 except that 99 parts by mass of PP-A and 0.5 parts by mass of UV-B1 and UV-C were used in Example 1.

Example 4
An optical film was obtained in the same manner as in Example 1 except that 99 parts by mass of PP-A, 0.9 parts by mass of UV-B1, and 0.1 parts by mass of UV-C were obtained in Example 1.

(Example 5)
In Example 1, except that PP-A was 99 parts by mass, UV-B1 and UV-C were each 0.5 parts by mass, and the thickness of the optical film was 40 μm, the optical film was the same as Example 1. Obtained.

(Example 6)
In Example 1, except that PP-A was 99.5 parts by mass, UV-B1 and UV-C were each 0.25 parts by mass, and the thickness of the optical film was 150 μm. A film was obtained.

(Comparative Example 1)
In Example 1, an optical film was obtained in the same manner as in Example 1 except that PP-A was 99.5 parts by mass, UV-B1 was 0.5 parts by mass, and UV-C was not used.

(Comparative Example 2)
In Example 1, an optical film was obtained in the same manner as in Example 1 except that 99 parts by mass of PP-A and 1 part by mass of UV-B1 were used, and UV-C was not used.

(Comparative Example 3)
An optical film was obtained in the same manner as in Example 1, except that PP-A was 99 parts by mass, UV-C was 1 part by mass, and UV-B1 was not used.

(Comparative Example 4)
In Example 1, an optical film was obtained in the same manner as in Example 1 except that 99 parts by mass of PP-A, 0.95 parts by mass of UV-B1, and 0.05 parts by mass of UV-C were used. .

(Comparative Example 5)
In Example 1, an optical film was obtained in the same manner as in Example 1 except that PP-A was 99 parts by mass, UV-B1 was 0.2 parts by mass, and UV-C was 0.8 parts by mass. .

(Example 7)
In Example 1, UV-B1 was replaced with 2- (2-hydroxy-3,5-di-tert-pentylphenyl) benzotriazole (“TINUVIN328 (trade name)” manufactured by BASF Corp .; hereinafter referred to as “UV-B2”). Except for the above, an optical film was obtained in the same manner as in Example 1.

(Example 8)
An optical film was obtained in the same manner as in Example 7 except that PP-A was changed to PP-B in Example 7.

Example 9
In Example 7, an optical film was obtained in the same manner as in Example 7 except that 99 parts by mass of PP-A and 0.5 parts by mass of UV-B2 and UV-C were each used.

(Example 10)
In Example 7, an optical film was obtained in the same manner as in Example 7 except that PP-A was 99 parts by mass, UV-B2 was 0.9 parts by mass, and UV-C was 0.1 parts by mass. .

(Example 11)
In Example 7, the optical film was prepared in the same manner as in Example 7 except that 99 parts by mass of PP-A, 0.5 parts by mass of UV-B2 and UV-C were each used, and the thickness of the optical film was 40 μm. Obtained.

(Example 12)
In Example 7, except that PP-A was 99.5 parts by mass, UV-B2 and UV-C were each 0.25 parts by mass, and the thickness of the optical film was 150 μm, the same as in Example 7 was used. A film was obtained.

(Comparative Example 6)
In Example 7, an optical film was obtained in the same manner as in Example 7 except that 99.5 parts by mass of PP-A and 0.5 parts by mass of UV-B2 were used, and UV-C was not used.

(Comparative Example 7)
In Example 7, an optical film was obtained in the same manner as in Example 7 except that PP-A was 99 parts by mass, UV-B2 was 1 part by mass, and UV-C was not used.

(Comparative Example 8)
An optical film was obtained in the same manner as in Example 7 except that PP-A was 99 parts by mass, UV-B2 was 0.95 parts by mass, and UV-C was 0.05 parts by mass. .

(Comparative Example 9)
In Example 7, an optical film was obtained in the same manner as in Example 7 except that PP-A was 99 parts by mass, UV-B2 was 0.2 parts by mass, and UV-C was 0.8 parts by mass. .

The evaluation results of the optical films obtained in Examples 1 to 6 and Comparative Examples 1 to 5 are shown in Table 1-1 and Table 2-1. Moreover, the evaluation result of the optical film obtained in Examples 7-12 and Comparative Examples 6-9 was shown to Table 1-2 and Table 2-2.
The optical films for protecting the polarizers of Examples 1 to 12 have excellent ultraviolet absorption performance by using a polypropylene resin mixture in which the ultraviolet absorbers (B) and (C) are mixed with the polypropylene resin (A) at a predetermined ratio. In addition, excellent performance was shown in haze evaluation, transparency evaluation, and appearance evaluation. In addition, in the area | region of wavelength 280nm of Examples 1, 2, and 5, although light transmittance may exceed the comparative example 1, all have light transmittance of 20% or less, and it has the outstanding performance as an optical film. It can be said that it has. Moreover, the optical film for polarizer protection of Examples 7-12 using UV-B2 (2- (2-hydroxy-3,5-di-tert-pentylphenyl) benzotriazole) as an ultraviolet absorber (B). In general, the optics of Examples 1 to 6 using UV-B1 (2- [2-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] benzotriazole) as the ultraviolet absorber (B). It was confirmed that the film was superior in terms of appearance evaluation as compared with the film, that is, the ultraviolet absorber was difficult to bleed out from the optical film.
On the other hand, in Comparative Examples 1, 2, 6, and 7 in which UV-C (ultraviolet absorber (C)) was not used, ultraviolet absorption in the wavelength regions of 375 to 400 nm, 385 to 400 nm, 385 to 400 nm, and 390 to 400 nm, respectively. In Comparative Examples 4 and 8 in which the performance was not sufficient and the content of UV-C (ultraviolet absorber (C)) was small, the ultraviolet absorption performance in the wavelength region of 385 to 400 nm and 390 to 400 nm, respectively, was not sufficient. Moreover, content of the comparative example 3 and UV-B1 (ultraviolet absorber (B)) which used UV-C (ultraviolet absorber (C)) independently without using UV-B1 (ultraviolet absorber (B)). In Comparative Example 5 with a small content and Comparative Example 9 with a small content of UV-B2 (ultraviolet absorber (B)), appearance defects such as whitening due to bleed out were remarkable.
Graph 1 shows the light transmittance of the optical film of Example 1 and the optical film of Comparative Example 1, and Graph 2 shows the light transmittance of the optical films of Examples 7, 9 and Comparative Example 6. It is. From the results of graphs 1 and 2, by combining the ultraviolet absorbers (B) and (C), the effect of improving the ultraviolet absorption performance particularly in the wavelength region of 370 to 400 was confirmed.

＊１，実測値／評価
＊２，実測値／評価

* 1, Actual value / Evaluation * 2, Actual value / Evaluation

＊１，実測値／評価
＊２，実測値／評価

* 1, Actual value / Evaluation * 2, Actual value / Evaluation

  The optical film of the present invention is particularly suitable as an optical sheet for protecting a polarizer because it is excellent in optical properties and ultraviolet absorption performance, and the ultraviolet absorber does not bleed out and is excellent in appearance. The polarizing plate obtained by combining the optical film of the present invention and a polarizer can be effectively used for image display devices such as a liquid crystal display device including a liquid crystal cell, an organic electroluminescence display device, and a touch panel.

1: Optical film for protecting a polarizer 2: Polarizer 3: Polarizing plate 4: Polarizer protective film of upper polarizing plate (panel upper surface side)
5: Polarizer of upper polarizing plate 6: Polarizer protective film of upper polarizing plate (backlight side)
7: Upper polarizing plate 8: Liquid crystal cell 9: Polarizer protective film for lower polarizing plate (panel upper surface side)
10: Polarizer of lower polarizing plate 11: Polarizer protective film of lower polarizing plate (backlight side)
12: Lower polarizing plate 13: Backlight part 14: Antireflection layer (or antireflection film)
15: Retardation plate

Claims (10)

  (A) a polypropylene resin containing a propylene-based polymer, (B) a 2- (hydroxyphenyl) benzotriazole derivative 1, and (C) a polypropylene resin mixture comprising a 2- (hydroxyphenyl) benzotriazole derivative 2. The (C) 2- (hydroxyphenyl) benzotriazole derivative 2 is 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole, and the (B) and (C The optical film whose content rate of this (C) with respect to the total amount of 8) is 8-60 mass%.   (B) 2- (hydroxyphenyl) benzotriazole derivative 1 is 2- [2-hydroxy-5- (1,1,3,3-tetramethylbutyl) phenyl] benzotriazole and 2- (2-hydroxy-3 The optical film according to claim 1, wherein the optical film is at least one selected from (2,5-di-tert-pentylphenyl) benzotriazole.   The optical film according to claim 1 or 2, wherein the propylene-based polymer is a random copolymer of propylene and an α-olefin.   The optical film according to claim 1, wherein the propylene polymer is a propylene copolymer synthesized with a metallocene catalyst.   5. The optical film according to claim 1, wherein the total content of (B) and (C) in the polypropylene resin mixture is 0.3 to 1.5 mass%.   The optical film according to any one of claims 1 to 5, wherein the light transmittance at a wavelength of 380 nm is 10% or less.   The optical film according to claim 1, which is used for a polarizer protective film.   A polarizing plate comprising the optical film according to claim 7 on at least one surface of a polarizer.   An image display device using the polarizing plate according to claim 8.   A liquid crystal display device, wherein a polarizer is used in a liquid crystal display device, the optical film according to claim 7 is provided on one side of the backlight side of the polarizer, and the backlight is a fluorescent tube.