JP2011057658A - Cosmetic - Google Patents
Cosmetic Download PDFInfo
- Publication number
- JP2011057658A JP2011057658A JP2009230976A JP2009230976A JP2011057658A JP 2011057658 A JP2011057658 A JP 2011057658A JP 2009230976 A JP2009230976 A JP 2009230976A JP 2009230976 A JP2009230976 A JP 2009230976A JP 2011057658 A JP2011057658 A JP 2011057658A
- Authority
- JP
- Japan
- Prior art keywords
- cosmetic
- bamboo
- powder
- finely pulverized
- bamboo powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、竹の微粉砕粉末を配合した化粧料に関する。
さらに詳しくは、竹の微粉砕粉末を配合することで、適度な隠蔽力を有し、かつツヤに優れた化粧料に関する。The present invention relates to a cosmetic containing a finely pulverized bamboo powder.
More specifically, the present invention relates to a cosmetic material having an appropriate hiding power and excellent gloss by blending finely pulverized bamboo powder.
以下、本発明の技術的背景について説明する。竹粉末は、特許文献1、2に示すように、竹の持つ防臭・防菌能力に着目して、生理用ナプキンや紙おむつに配合されたり、外用脱臭除菌剤に配合されたりしている。また、特許文献3に示すように、竹を炭化させた竹炭を配合した整髪料や、特許文献4に示すように、竹の抽出物を配合した皮膚化粧料も知られている。 Hereinafter, the technical background of the present invention will be described. As shown in Patent Documents 1 and 2, bamboo powder is blended in sanitary napkins and paper diapers, or blended in an external deodorizing and disinfecting agent, focusing on the deodorizing and antibacterial ability of bamboo. Further, as shown in Patent Document 3, a hair styling compounded with bamboo charcoal obtained by carbonizing bamboo, and a skin cosmetic compounded with bamboo extract as shown in Patent Document 4, are also known.
竹の粉末は、その抗菌性に注目した開発が主に行われており、竹の粉末そのものの顔料としての特性に注目した検討は実施されてこなかった。また、従来、化粧料の隠蔽力を出すための素材は酸化チタンが主に用いられてきており、弱いながらも植物の微粉末で隠蔽力が得られるものは知られていなかった。 Bamboo powder has been developed mainly focusing on its antibacterial properties, and no study has been conducted focusing on the properties of bamboo powder itself as a pigment. Conventionally, titanium oxide has been mainly used as a material for concealing cosmetics, and it has not been known that the material can be concealed with fine plant powder.
そこで、本発明人は鋭意検討した結果、竹の微粉末を配合することで、適度な隠蔽力とツヤに優れた化粧料が得られることを見いだした。 Therefore, as a result of intensive studies, the present inventor has found that a cosmetic having an appropriate hiding power and gloss can be obtained by blending fine bamboo powder.
すなわち、本発明は、竹の微粉砕粉末を配合した化粧料にある。 That is, the present invention is a cosmetic containing a finely pulverized bamboo powder.
第2の本発明は、竹の微粉砕粉末が、竹の表皮から得られたものであることを特徴とする上記の化粧料にある。 A second aspect of the present invention is the cosmetic described above, wherein the finely pulverized bamboo powder is obtained from a bamboo skin.
第3の本発明は、竹の微粉砕粉末の平均一次粒子径が1〜15μmの範囲にあることを特徴とする上記の化粧料にある。 A third aspect of the present invention is the cosmetic described above, wherein the average primary particle diameter of the finely pulverized bamboo powder is in the range of 1 to 15 μm.
以上説明するように、本発明は、竹の微粉砕粉末を配合することで、適度な隠蔽力を有し、かつツヤに優れた化粧料が得られることは明らかである。 As described above, according to the present invention, it is clear that a cosmetic having an appropriate hiding power and excellent gloss can be obtained by blending finely pulverized bamboo powder.
以下、上記本発明を詳細に説明する。
本発明の化粧料では、竹の微粉砕粉末を配合する。本発明で用いる竹とは、イネ科タケ亜目に属する植物を指し、例えばモウソウチク、マダケ、ハチク、ホテイチク、キッコウチク、ホウライチク、ナリヒラダケ、チシマザサ、トウチク、シホウチク、カンチク、ヤダケ、メダケなどが挙げられる。竹は、幹を粉砕しても、表皮を分離後粉砕しても構わないが、表皮を用いることが好ましい。また、竹は事前に乾燥されているものを用いても構わない。本発明の化粧料で言う微粉砕粉末とは、平均一次粒子径で1〜20μm、より好ましくは1〜15μmの範囲に入るように、竹を粉砕して得られるものが挙げられる。平均一次粒子径の測定及び形状観察は電子顕微鏡観察や、粒度分布計を用いて検討することが好ましい。平均一次粒子径が1μm未満ではツヤが出にくい問題があり、また、20μmを超えると皮膚への付着性が悪化する問題がある。また、本発明の化粧料では、竹は機械的に粉砕されたものを用いることが好ましい。爆砕法は化粧料への火薬由来成分の混入の恐れがあるため好ましくない。Hereinafter, the present invention will be described in detail.
In the cosmetic of the present invention, bamboo finely pulverized powder is blended. Bamboo used in the present invention refers to a plant belonging to the family Gramineae, for example, Mosouchiku, Madake, Hachiku, Hoteiku, Kikkochiku, Horaichiku, Narihiratake, Chishimasa, Tochiku, Shihochiku, Kanchiku, Yadatake, Medake and the like. Bamboo may be crushed by pulverizing the trunk or crushed after separating the epidermis, but it is preferable to use the epidermis. Moreover, you may use the bamboo dried beforehand. The finely pulverized powder referred to in the cosmetic of the present invention includes those obtained by pulverizing bamboo so that the average primary particle diameter falls within the range of 1 to 20 μm, more preferably 1 to 15 μm. The measurement of the average primary particle diameter and the shape observation are preferably studied using an electron microscope observation or a particle size distribution meter. When the average primary particle size is less than 1 μm, there is a problem that gloss is difficult to occur, and when it exceeds 20 μm, there is a problem that adhesion to the skin is deteriorated. In the cosmetic of the present invention, it is preferable to use bamboo that has been mechanically pulverized. The blasting method is not preferable because there is a risk of mixing explosive-derived components into cosmetics.
本発明の化粧料で用いる竹の微粉砕粉末は、別途乾燥処理や洗浄、滅菌処理、脱臭処理、漂白処理が行われていても構わない。 The finely pulverized bamboo powder used in the cosmetic of the present invention may be separately subjected to drying treatment, washing, sterilization treatment, deodorization treatment, and bleaching treatment.
本発明の化粧料では、こうして得られた竹の微粉砕粉末を、化粧料の質量に対して0.1〜99.9質量%の範囲で配合することが可能である。また、隠蔽力やツヤなどの光学機能を期待する場合は、竹の微粉砕粉末を化粧料の質量に対して1.0〜99.9質量%の範囲で配合することが好ましい。 In the cosmetic of the present invention, the finely pulverized bamboo powder thus obtained can be blended in the range of 0.1 to 99.9% by mass relative to the mass of the cosmetic. When optical functions such as hiding power and gloss are expected, it is preferable to blend bamboo finely pulverized powder in the range of 1.0 to 99.9% by mass with respect to the mass of the cosmetic.
本発明の化粧料では、上記竹の微粉砕粉末以外の成分として、通常化粧料で使用される各種の素材、例えば顔料、紫外線吸収剤、紫外線散乱剤、油剤、界面活性剤、フッ素化合物、樹脂、粘剤、防腐剤、香料、保湿剤、塩類、溶媒、酸化防止剤、キレート剤、中和剤、pH調整剤、昆虫忌避剤、生理活性成分等の成分を使用することができる。 In the cosmetic of the present invention, as a component other than the finely pulverized bamboo powder, various materials usually used in cosmetics, for example, pigments, ultraviolet absorbers, ultraviolet scattering agents, oil agents, surfactants, fluorine compounds, resins Ingredients such as stickers, preservatives, fragrances, humectants, salts, solvents, antioxidants, chelating agents, neutralizing agents, pH adjusters, insect repellents, physiologically active ingredients, and the like can be used.
本発明の化粧料としては、ファンデーション、口紅、アイシャドウ、マスカラ、頬紅、白粉、ネイルカラー、コンシーラーなどのメイクアップ化粧料以外にも、クリーム、乳液、クレンジング料、サンスクリーン剤、パックなどの基礎化粧料、染毛料、コンディショナーなどの頭髪化粧料、ボディソープ、ボディパウダーなどの全身化粧料においても有効に利用することができる。 In addition to makeup cosmetics such as foundations, lipsticks, eye shadows, mascaras, blushers, white powder, nail colors, concealers, etc., the cosmetics of the present invention include the foundations of creams, emulsions, cleansing agents, sunscreen agents, packs, etc. It can also be used effectively in hair cosmetics such as cosmetics, hair dyes and conditioners, and in whole body cosmetics such as body soaps and body powders.
以下に実施例を挙げ、本発明を更に詳細に説明するが、本発明はこれに限定されるものではない。 The present invention will be described in more detail with reference to examples below, but the present invention is not limited thereto.
〔実施例1〜3、比較例1〕
表2に示す処方と製造方法により、ファンデーションを得た。尚、配合比率の単位は質量%である。竹の微粉砕粉末としては、マダケの表皮の粉砕物を用いた。この竹の微粉砕粉末の走査型電子顕微鏡写真の例を図1に示す。また、竹の微粉砕粉末の粒子径を表1に示す。尚、平均一次粒子径(累積50%粒子径)は、日機装社製マイクロトラックMT3300EXII型を用い、イソプロピルアルコールを用いて動的光散乱法にて測定した。[Examples 1 to 3, Comparative Example 1]
A foundation was obtained by the formulation and production method shown in Table 2. In addition, the unit of a mixture ratio is the mass%. As a finely pulverized powder of bamboo, a pulverized material of mushroom skin was used. An example of a scanning electron micrograph of this finely pulverized bamboo powder is shown in FIG. Table 1 shows the particle size of the finely pulverized bamboo powder. The average primary particle size (cumulative 50% particle size) was measured by a dynamic light scattering method using MICROTRACK MT3300EXII type manufactured by Nikkiso Co., Ltd. and using isopropyl alcohol.
製造方法
粉体成分をミキサーを用いて良く混合した。ここに、均一に溶解、混合した油性成分を加え、良く撹拌混合した。ついで、金型を用いて金皿に打型して製品(ファンデーション)を得た。Production Method The powder components were mixed well using a mixer. To this was added the oily component that was uniformly dissolved and mixed, and the mixture was well stirred. Subsequently, the product (foundation) was obtained by stamping into a metal plate using a metal mold.
〔実施例4〜6、比較例2〜3〕
表3に示す処方と製造方法により、W/O型リクイドファンデーションを得た。尚、竹の微粉砕粉末としては、モウソウチクの表皮を粉砕したもの(平均一次粒子径9.1μm)を使用した。尚、表3における配合比率の単位は質量%である。[Examples 4-6, Comparative Examples 2-3]
A W / O liquid foundation was obtained by the formulation and manufacturing method shown in Table 3. In addition, as a finely pulverized powder of bamboo, a pulverized Moso bamboo skin (average primary particle size: 9.1 μm) was used. In addition, the unit of the mixture ratio in Table 3 is mass%.
製造方法
油相を70℃に加熱し、均一に混合した後、良く混合しておいた粉体成分を加え、攪拌する。次いで、70℃に加熱し、均一に混合した水相を加え、攪拌した後、室温まで冷却し、容器に充填して製品を得た。Manufacturing Method After heating the oil phase to 70 ° C. and mixing uniformly, the well-mixed powder component is added and stirred. Next, the mixture was heated to 70 ° C., a uniformly mixed aqueous phase was added, stirred, cooled to room temperature, and filled into a container to obtain a product.
〔実施例7〜9、比較例4〕
表4に示す処方と製造方法により、ほほ紅を得た。尚、竹の微粉砕粉末としては、実施例1で用いたものをそのまま用いた。また、表4における配合比率の単位は質量%である。[Examples 7 to 9, Comparative Example 4]
According to the formulation and manufacturing method shown in Table 4, cheek red was obtained. As the finely pulverized bamboo powder, the powder used in Example 1 was used as it was. Moreover, the unit of the blending ratio in Table 4 is mass%.
製造方法
粉体成分をミキサーを用いて良く混合した。ここに油性成分を加え、良く撹拌混合した。ついで、容器に充填して製品を得た。Production Method The powder components were mixed well using a mixer. The oily component was added here and mixed well with stirring. Subsequently, the product was obtained by filling the container.
実施例及び比較例の評価
パネラー10名を用い、アンケート形式にて、実施例及び比較例の評価を実施した。アンケートは各評価項目に対して、一番優れた評価を5点、一番悪い評価を1点として、パネラー全員の平均点を以て評価結果とした。従って、点数が高い方がその評価項目に対して評価が高かったことを示す。評価結果を表5に示す。Evaluation of Examples and Comparative Examples The evaluation of Examples and Comparative Examples was performed in a questionnaire format using 10 panelists. The questionnaire was evaluated with the average score of all the panelists, with 5 being the best evaluation and 1 being the worst. Therefore, the higher the score, the higher the evaluation for the evaluation item. The evaluation results are shown in Table 5.
表5の結果から、本発明の実施例は比較例と比べて、各評価項目において優れた性能を示していることが判る。表5の結果から、竹の微粉砕粉末は適度な隠蔽力があり、ツヤに優れていることが判る。 From the results of Table 5, it can be seen that the example of the present invention shows superior performance in each evaluation item as compared with the comparative example. From the results in Table 5, it can be seen that the finely pulverized bamboo powder has a suitable hiding power and is excellent in gloss.
Claims (3)