JP2011021410A - Blind - Google Patents
Blind Download PDFInfo
- Publication number
- JP2011021410A JP2011021410A JP2009168382A JP2009168382A JP2011021410A JP 2011021410 A JP2011021410 A JP 2011021410A JP 2009168382 A JP2009168382 A JP 2009168382A JP 2009168382 A JP2009168382 A JP 2009168382A JP 2011021410 A JP2011021410 A JP 2011021410A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- slat
- blind
- undercoat layer
- thermosetting resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、スラットの日射反射率(紫外線、可視光線及び赤外線領域の波長(300nm〜2500nm)の反射率をいう)を向上させることができるブラインドに関する。 The present invention relates to a blind capable of improving the solar reflectance of slats (referring to the reflectance of wavelengths (300 nm to 2500 nm) in the ultraviolet, visible, and infrared regions).
従来、この種のブラインドとしては、例えば特許文献1に記載されたものが知られている。 Conventionally, as this type of blind, for example, one described in Patent Document 1 is known.
特許文献1に示されるブラインドは、スラット表面に、化成皮膜を形成させ、その上に日射反射率の高い太陽熱遮蔽塗料を10μm〜30μmの塗膜で塗布して、ブラインド自体の温度上昇を抑え、その結果として室内の温度上昇も抑えられるように、ブラインドに赤外線反射機能を持たせている。太陽熱遮蔽塗料は顔料とビヒクルを主成分とし、太陽熱遮蔽顔料を単独または複数混合分散させることによって配合される。 In the blind shown in Patent Document 1, a chemical conversion film is formed on the slat surface, and a solar heat shielding paint having a high solar reflectance is applied thereon with a coating film of 10 μm to 30 μm to suppress the temperature rise of the blind itself, As a result, the blind is provided with an infrared reflecting function so that the temperature rise in the room can be suppressed. The solar heat shielding paint is mainly composed of a pigment and a vehicle, and is blended by dispersing or dispersing the solar heat shielding pigment alone or in combination.
しかしながら、太陽熱遮蔽塗料は、明度の低い色のスラットに適用する場合には太陽熱遮蔽効果が得られるが、白色のような明度の高い色のスラットに適用する場合には、日射反射率を向上させることが困難であるという問題がある。 However, the solar heat-shielding paint can provide a solar heat-shielding effect when applied to slats with low lightness, but improves solar reflectance when applied to slats with high lightness such as white. There is a problem that it is difficult.
特許文献1では、太陽熱遮蔽顔料に加えて白色顔料として酸化チタン顔料を併用して明度の調整を行うことも記載されているが、そのような塗料を塗布しても、太陽熱遮蔽塗料を使用しない明度の高い一般塗料を塗布したものと同等の日射反射率しか得ることができない。 Patent Document 1 also describes that the brightness is adjusted by using a titanium oxide pigment as a white pigment in addition to the solar heat shielding pigment. However, even if such a paint is applied, the solar heat shielding paint is not used. Only a solar reflectance equivalent to that obtained by applying a general paint with high brightness can be obtained.
本発明はかかる課題に鑑みなされたもので、黒色以外の明度の高い色の塗料が塗布されたスラットにおいても、日射反射率を向上させることができるブラインドを提供することをその目的とする。 The present invention has been made in view of such problems, and an object thereof is to provide a blind capable of improving the solar reflectance even in a slat coated with a paint having a high brightness other than black.
前述した目的を達成するために、請求項1記載の発明は、角度調整可能な複数枚のスラットを有するブラインドにおいて、
スラットのスラット基材の表面には下塗層として熱硬化性樹脂層が形成され、下塗層の表面には上塗層として硬度が下塗層より高い熱硬化性樹脂層が形成され、下塗層は白色顔料を含んだ白色を呈し、上塗層はスラットの表面色を呈するための意匠顔料を含むことを特徴とする。
In order to achieve the above object, the invention according to claim 1 is a blind having a plurality of slats adjustable in angle.
A thermosetting resin layer is formed as a primer layer on the surface of the slat substrate of the slat, and a thermosetting resin layer having a higher hardness than the primer layer is formed as a primer layer on the surface of the primer layer. The coating layer is white including a white pigment, and the top coating layer includes a design pigment for exhibiting the surface color of the slats.
請求項2記載の発明は、請求項1記載の前記上塗層及び前記下塗層が、それぞれ10μm〜20μmの塗膜厚で形成されることを特徴とする。 The invention according to claim 2 is characterized in that the overcoat layer and the undercoat layer according to claim 1 are each formed with a coating thickness of 10 μm to 20 μm.
請求項3記載の発明は、請求項1または2記載の前記下塗層が熱硬化性ポリエステル樹脂層であり、前記上塗層は熱硬化性アクリル樹脂層であることを特徴とする。 The invention described in claim 3 is characterized in that the undercoat layer according to claim 1 or 2 is a thermosetting polyester resin layer, and the overcoat layer is a thermosetting acrylic resin layer.
請求項4記載の発明は、請求項1ないし3のいずれか1項に記載の前記下塗層に含まれる白色顔料が、酸化チタンであることを特徴とする。 The invention according to claim 4 is characterized in that the white pigment contained in the undercoat layer according to any one of claims 1 to 3 is titanium oxide.
請求項5記載の発明は、ブラインド用スラットであって、スラット基材の表面には下塗層として熱硬化性樹脂層が形成され、下塗層の表面には上塗層として硬度が下塗層より高い熱硬化性樹脂層が形成され、下塗層は白色顔料を含んだ白色を呈し、上塗層はスラットの表面色を呈するための意匠顔料を含むことを特徴とする。 The invention according to claim 5 is a blind slat, wherein a thermosetting resin layer is formed on the surface of the slat substrate as an undercoat layer, and the surface of the undercoat layer has an undercoat hardness as an overcoat layer. A thermosetting resin layer higher than the layer is formed, the undercoat layer exhibits a white color including a white pigment, and the overcoat layer includes a design pigment for exhibiting the surface color of the slats.
本発明によれば、スラットの表面色を決定する上塗層の下に、白色顔料を含む白色の下塗層を形成することによって、白色の下塗層がスラット基材の色を隠して、スラットの表面色の明度が高くなり日射反射率を向上させることができる。 According to the present invention, a white primer layer containing a white pigment is formed under the primer layer that determines the surface color of the slat, so that the white primer layer hides the color of the slat substrate, The brightness of the surface color of the slats can be increased and the solar reflectance can be improved.
上塗層を下塗層よりも硬度の高いものとして、硬度の異なる2つの層から塗膜層を形成することにより、塗膜のスラット基材に対する付着性を良好にしてスラットの成形時における塗膜の割れなどを防ぐと共に、スラットの表面を実用性に足る十分に硬いものとすることができる。 By making the topcoat layer harder than the undercoat layer and forming the coating layer from two layers with different hardnesses, the adhesion of the coating film to the slat substrate is improved and coating during slat molding is performed. While preventing the film from cracking, the surface of the slat can be made sufficiently hard to be practical.
例えば、下塗層を熱硬化性ポリエステル樹脂層とし、上塗層を熱硬化性アクリル樹脂層とすることにより、実用性に足る塗膜の柔軟性を持たせると共に実用性に足るスラットの表面の硬さを持たせることができる。 For example, by making the undercoat layer a thermosetting polyester resin layer and the topcoat layer a thermosetting acrylic resin layer, the flexibility of the coating film sufficient for practicality is provided and the surface of the slat surface sufficient for practicality is provided. Hardness can be given.
下塗層の白色顔料を酸化チタンとすることで、値段の高価な特殊な太陽熱遮蔽顔料を含む太陽熱遮蔽塗料を使用することなく、日射反射率を向上させることができる。 By using titanium oxide as the white pigment for the undercoat layer, the solar reflectance can be improved without using a solar heat shielding paint containing a special expensive solar heat shielding pigment.
以下、図面を参照して、本発明の実施形態を説明する。 Hereinafter, embodiments of the present invention will be described with reference to the drawings.
図3は、本発明のブラインドの一例を表しており、ブラインド30は、角度調整可能な複数枚の長尺状のスラット10を有している。
FIG. 3 shows an example of the blind according to the present invention, and the blind 30 has a plurality of
図1に示すように、スラット10は、スラット基材12と、下塗層14と、上塗層16と、を有し、その横断面が矢形湾曲形状に成形されている。
As shown in FIG. 1, the
スラット基材12としては、アルミニウムまたはアルミニウム合金等の金属材料から構成することができる。スラット基材12の表面は、化成処理による20〜30nmの化成皮膜13となっており、化成皮膜13の表面は、非晶質(アモルファス)となっている。
The
スラット基材12の表面には、下塗層14としての熱硬化性樹脂層が形成される。下塗層14は硬度の比較的低い熱硬化性樹脂を含み、熱硬化性樹脂として、例えば、熱硬化性ポリエステル樹脂、エポキシ樹脂が選択される。下塗層14の膜厚としては、10μm〜20μm、好ましくは10μm〜15μm、より好ましくは13μm〜15μmとするとよい。また、下塗層14は、白色顔料を含み、白色を呈している。白色顔料としては、酸化チタンとすることができる。
A thermosetting resin layer as the
また、下塗層14の表面には、上塗層16としての熱硬化性樹脂層が形成される。上塗層16は下塗層14よりも硬度の高い熱硬化性樹脂を含み、熱硬化性樹脂として、例えば、熱硬化性アクリル樹脂が選択される。また、上塗層16は、意匠顔料を含み、そのスラットの表面色となる色を呈している。上塗層16の膜厚としては、10μm〜20μm、好ましくは10μm〜15μm、より好ましくは11μm〜13μmとするとよい。
Further, a thermosetting resin layer as the
以上のスラットを作製するには、平坦形状をなしたスラット基材を用意し、その表面に化成処理を行って化成皮膜13を形成し、次いでその上に熱硬化性樹脂及び白色顔料を含む下塗塗料を塗布して下塗層14を形成し、さらにその上に熱硬化性樹脂及び意匠顔料を含む上塗塗料を塗布して上塗層16を形成した後、フォーミング加工を行って、最終のスラット形状に成形する。
In order to produce the above slats, a slat substrate having a flat shape is prepared, a chemical conversion treatment is performed on the surface thereof to form a
下塗層14と上塗層16からなる塗膜の硬度は、引っかき硬度試験(鉛筆法)(JIS-K5600.5.4)により、2H以上となっているとよく、好ましくは4H以上となっているとよい。
The hardness of the coating film comprising the
また、塗膜の付着性は、碁盤目テープ法(JIS−K5400-1990 8.5.2)に準拠し、NTカッターで碁盤目にカットしセロハン粘着テープ(JIS−Z1522)剥離テストを行った場合の塗膜剥離個数が0個となっているとよい。 In addition, the adhesion of the coating film was based on a cross-cut tape method (JIS-K5400-1990 8.5.2), cut with a NT cutter into a cross-cut, and a cellophane adhesive tape (JIS-Z1522) peel test was performed. In this case, it is preferable that the number of peeled coating films is zero.
また、下塗層14と上塗層16からなる塗膜の膜厚は、20μm〜30μm、好ましくは、24μm〜27μmであるとよい。
Moreover, the film thickness of the coating film which consists of the
以上のようにスラット10の表面色を決定する意匠顔料を含む上塗層16の下に、白色顔料を含み白色を呈した下塗層14を設けることで、下塗層14がスラット基材12の色を隠してスラット10の表面色の明度が高くなり、日射反射率を向上させることができる。このスラット10を備えたブラインド30を窓に設定することによって室内への熱の流入を抑制する効果が得られ、夏季には冷房負荷を軽減することができて、省エネルギー化を図ることができる。
As described above, the
好ましくは、スラット基材12に下塗層14を形成した状態における日射反射率を60%以上とし、その上に上塗層16を形成した状態における日射反射率を70%以上とするように、膜厚及び顔料配分量が決定されるとよい。
Preferably, the solar reflectance in a state where the
通常の白色顔料を有して白色を呈した下塗層14が日射反射効果を持つために、特殊な太陽熱遮蔽顔料を含む太陽熱遮蔽塗料を使用することなく、日射反射効果を得ることができる。こうして、明度が高く淡い色を表面色とするスラットにも高い日射反射率を持たせることができる。
Since the
単純に塗膜厚を厚くした1層の塗膜からなるスラットと比較して、異なる硬度を持つ2層から構成したスラットとすることで、実用的なスラットとすることができる。即ち、下塗層14を柔軟性を有する硬度の低い熱硬化性樹脂から構成することで、塗膜のスラット基材に対する付着性を良好にすることができると共に、フォーミング加工時における塗膜の割れなどを防ぐことができる。また、上塗層16を硬度の高い熱硬化性樹脂から構成することで、スラット10表面をブラインド用スラットとして使用に耐え得る硬度とすることができる。
A slat composed of two layers having different hardnesses can be used as a practical slat as compared to a slat composed of a single-layer coating having a simple coating thickness. That is, by forming the
(実施例)
アルミニウムからなるスラット基材に対して以下の配合例による下塗塗料と上塗塗料をそれぞれ順番に塗布して下塗層と上塗層とを形成した。下塗層の塗膜厚は14μm、上塗層の塗膜厚は12μm、合計の塗膜厚が26μmとなるようにし、その後、フォーミング加工を行って、図2で説明する曲率半径40mmの矢形形状の断面形状で、スラット幅が24.6mm、矢高が2.2mmのスラットを作製した。
(Example)
An undercoat layer and an overcoat layer according to the following formulation examples were sequentially applied to a slat substrate made of aluminum to form an undercoat layer and an overcoat layer. The coating thickness of the undercoat layer is 14 μm, the coating thickness of the topcoat layer is 12 μm, and the total coating thickness is 26 μm. After that, forming is performed, and an arrow shape having a radius of curvature of 40 mm described in FIG. A slat having a cross-sectional shape with a slat width of 24.6 mm and an arrow height of 2.2 mm was produced.
下塗塗料
白色顔料(酸化チタン) 22%(質量%、以下同じ)
ポリエステル樹脂 17%
メラミン樹脂 3%
消泡剤 0.5%
レベリング剤 0.5%
溶剤 57%
Undercoat paint White pigment (titanium oxide) 22% (mass%, the same shall apply hereinafter)
17% polyester resin
Melamine resin 3%
Antifoam 0.5%
Leveling agent 0.5%
Solvent 57%
上塗塗料
白色顔料(酸化チタン) 35%(質量%、以下同じ)
アクリル樹脂 18%
メラミン樹脂 4%
エポキシ樹脂 3%
消泡剤 1%
レベリング剤 1%
溶剤 38%
Top coating white pigment (titanium oxide) 35% (mass%, the same shall apply hereinafter)
Acrylic resin 18%
Melamine resin 4%
Epoxy resin 3%
Antifoam 1%
Leveling agent 1%
Solvent 38%
(比較例1)
アルミニウムからなるスラット基材に対して、実施例の上塗塗料と同じ配合による塗料を塗布して、塗膜厚が15μmとなるようにした後、フォーミング加工を行って実施例と同一寸法のスラットを作製した。
(Comparative Example 1)
A slat substrate made of aluminum is coated with a coating having the same composition as the top coating of the example so that the coating thickness is 15 μm, and then subjected to forming to form a slat having the same dimensions as the example. Produced.
(比較例2)
アルミニウムからなるスラット基材に対して、比較例1と同じ塗料を塗布して、塗膜厚が26μmとなるようにした後、フォーミング加工を行って実施例と同一寸法のスラットを作製した。
(Comparative Example 2)
The same paint as in Comparative Example 1 was applied to a slat substrate made of aluminum so that the coating thickness was 26 μm, and then a forming process was performed to produce a slat having the same dimensions as in the example.
(結果)
比較例2は、フォーミング加工により塗膜が割れやすいという不具合があり、この構成による製品化は困難と判断された。
(result)
The comparative example 2 had the fault that a coating film was easy to be cracked by forming, and it was judged that commercialization by this structure was difficult.
実施例と比較例1では、塗膜の割れの発生はなく、硬度も4H(Uni,MITSU−BISHI製)であり、十分な硬度が得られた。 In Example and Comparative Example 1, there was no cracking of the coating film, and the hardness was 4H (Uni, manufactured by MITSU-BISHI), and sufficient hardness was obtained.
実施例と比較例1との外観を比較すると、実施例の方が、明度が高くなっており、反射率が高くなっていることが期待できた。 When the external appearances of the example and the comparative example 1 were compared, it was expected that the example had higher brightness and higher reflectance.
そこで、実施例及び比較例1についての反射率をJIS−R−3106に準拠して測定して比較を行ったところ、図4に示す結果が得られた。図4において太線が実施例、細線が比較例1の反射率である。この結果から日射反射率(300nm〜2500nm)、近赤外領反射率(800nm〜2100nm)及び可視光反射率(380nm〜780nm)を求めると、実施例は比較例1に対して日射反射率において1.08倍、可視光反射率が1.05倍、近赤外領域反射率において1.09倍の向上がみられた。また、明度指数も実施例は比較例1に対して高くなっていた。 Then, when the reflectance about an Example and the comparative example 1 was measured based on JIS-R-3106 and compared, the result shown in FIG. 4 was obtained. In FIG. 4, the bold line is the reflectance of the example, and the thin line is the reflectance of Comparative Example 1. When the solar reflectance (300 nm to 2500 nm), the near infrared region reflectance (800 nm to 2100 nm), and the visible light reflectance (380 nm to 780 nm) are obtained from this result, the example is compared with the comparative example 1 in the solar reflectance. Improvements of 1.08 times, visible light reflectance of 1.05 times, and near infrared region reflectance of 1.09 times were observed. In addition, the brightness index of the example was higher than that of Comparative Example 1.
尚、以上の実施例では、表面色として白色について行ったが、淡い黄色、ベージュ、淡い灰色、淡い緑色、淡い青色、淡い紺色、淡いピンク色、といった従来の太陽熱遮蔽顔料では効果が期待できない明度の高い淡色の表面色を持つスラットにおいても白色顔料を含む下塗層によって、同様の日射反射率及び近赤外領域反射率の向上が得られた。 In the above examples, white was used as the surface color, but lightness that cannot be expected with conventional solar heat shielding pigments such as pale yellow, beige, pale gray, pale green, pale blue, pale amber, and pale pink. Even in a slat having a light surface color with a high color, the same solar radiation reflectance and near-infrared reflectance were obtained by the undercoat layer containing a white pigment.
10 スラット
12 スラット基材
14 下塗層
16 上塗層
10
Claims (5)
スラット(10)のスラット基材(12)の表面には下塗層(14)として熱硬化性樹脂層が形成され、下塗層の表面には上塗層(16)として硬度が下塗層より高い熱硬化性樹脂層が形成され、下塗層は白色顔料を含んだ白色を呈し、上塗層はスラットの表面色を呈するための意匠顔料を含むことを特徴とするブラインド。 In a blind having a plurality of adjustable slats,
A thermosetting resin layer is formed as an undercoat layer (14) on the surface of the slat substrate (12) of the slat (10), and the surface of the undercoat layer has a hardness as an undercoat layer (16). A blind, wherein a higher thermosetting resin layer is formed, the undercoat layer has a white color including a white pigment, and the overcoat layer contains a design pigment for exhibiting a surface color of slats.