JP2011006804A - Method for producing carbon fiber bundle and apparatus for producing the same - Google Patents
Method for producing carbon fiber bundle and apparatus for producing the same Download PDFInfo
- Publication number
- JP2011006804A JP2011006804A JP2009149701A JP2009149701A JP2011006804A JP 2011006804 A JP2011006804 A JP 2011006804A JP 2009149701 A JP2009149701 A JP 2009149701A JP 2009149701 A JP2009149701 A JP 2009149701A JP 2011006804 A JP2011006804 A JP 2011006804A
- Authority
- JP
- Japan
- Prior art keywords
- fiber bundle
- precursor fiber
- roll
- folding
- regulating member
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、炭素繊維束の製造方法、および炭素繊維束の製造装置に関する。 The present invention relates to a carbon fiber bundle manufacturing method and a carbon fiber bundle manufacturing apparatus.
アクリル系前駆体繊維束(以下、「前駆体繊維束」という。)を耐炎化する方法としては、図5に示すように、炭素繊維束の製造装置20に具備された耐炎化炉22の外側に折り返しロール23を配置し、前駆体繊維束21をジグザグ状に折り返して耐炎化炉22内を走行させ、耐炎化処理する方法が一般的である。耐炎化処理された前駆体繊維束は、炭素化手段24により炭素化処理されて炭素繊維束となる。
このような方法においては、折り返しロールとしてロール表面に溝が設けられた溝付きロールを多数使用し、前駆体繊維束を溝付きロールの溝内に案内することによって、前駆体繊維束を分離、独立させて、耐炎化処理される前駆体繊維束同士の絡み、折り返しロール乗り越え、処理斑等を防止する場合が多い。
As shown in FIG. 5, the acrylic precursor fiber bundle (hereinafter referred to as “precursor fiber bundle”) is flame-proofed as shown in FIG. 5 by the outside of the
In such a method, a large number of grooved rolls provided with grooves on the roll surface are used as folding rolls, and the precursor fiber bundles are separated by guiding the precursor fiber bundles into the grooves of the grooved rolls. Independently, it often prevents entanglement of precursor fiber bundles to be subjected to flameproofing treatment, overturning rolls, processing spots, and the like.
しかし、溝付きロールを使用しても、耐炎化処理される前駆体繊維束1本当たりのフィラメント数が多くなると、その断面形状が円形の場合、糸の最大厚みが大きくなり、蓄熱による糸切れが発生しやすくなるという問題があった。
糸切れの発生を抑制するには耐炎化処理の温度を下げればよいが、処理時間が長くかかりやすかった。また、耐炎化反応に必要な酸素が前駆体繊維束の内部にまで十分に拡散されにくくなり、内部と表面とで耐炎化の進行度が異なり、耐炎化処理の後に行われる炭素化処理において毛羽立ちや糸傷み等が発生することがあった。
However, even if a grooved roll is used, if the number of filaments per precursor fiber bundle subjected to flameproofing treatment increases, the maximum thickness of the yarn increases when the cross-sectional shape is circular, and the yarn breaks due to heat accumulation. There was a problem that it is easy to occur.
In order to suppress the occurrence of yarn breakage, the temperature of the flameproofing treatment may be lowered, but the treatment time tends to be long. In addition, oxygen necessary for the flameproofing reaction is not sufficiently diffused to the inside of the precursor fiber bundle, the progress of flameproofing differs between the inside and the surface, and fluffing occurs in the carbonization process performed after the flameproofing process. In some cases, thread damage or the like occurred.
そこで、例えば特許文献1には、耐炎化炉の両側に配置された溝付きロールの溝形状を規定することによって、略矩形断面を有するポリアクリロニトリル系前駆体繊維束の平均扁平率と平均繊度を制御する方法、および装置が記載されている。これにより、均一な耐炎化進行度の耐炎化繊維束が得られ、後の炭素化処理での毛羽立ちや糸傷み等の発生を抑制し、高品質、高品位の炭素繊維束を得られるとしている。 Therefore, for example, in Patent Document 1, by defining the groove shape of the grooved roll disposed on both sides of the flameproofing furnace, the average flatness and average fineness of the polyacrylonitrile-based precursor fiber bundle having a substantially rectangular cross section are set. A method and apparatus for controlling are described. Thereby, it is said that a flame-resistant fiber bundle having a uniform progress of flame resistance can be obtained, and generation of fuzz and yarn damage in subsequent carbonization treatment can be suppressed, and a high-quality, high-quality carbon fiber bundle can be obtained. .
しかしながら、特許文献1に記載の方法では、特に糸幅/糸厚み比で規定される平均扁平率が大きく、単位幅当たりの見かけの平均繊度が小さい前駆体繊維束の場合、溝付きロールを通過時に略矩形に保たれた前駆体繊維束の端が折れたり、厚み斑となったりすることがあった。その結果、耐炎化炉内を走行することで耐炎化斑や蓄熱による糸切れを引き起こすことがあった。
また、溝付きロールの溝内において、溝を形成する凸部のうち、片方の凸部の傾斜部に前駆体繊維束の走行位置がずれた場合、溝底部の端部を境に前駆体繊維束が折れやすくなり、走行する前駆体繊維束の形態が不安定になるという問題があった。
さらに、特許文献1に記載のように、折り返しロールとして溝付きロールを用いる場合、溝付きロールの交換が容易ではなく、メンテナンスが困難であった。
However, in the method described in Patent Document 1, in the case of a precursor fiber bundle having a particularly large average flatness ratio defined by a yarn width / yarn thickness ratio and a small apparent average fineness per unit width, it passes through a grooved roll. Sometimes, the end of the precursor fiber bundle kept in a substantially rectangular shape is broken or becomes thick. As a result, running in the flameproofing furnace sometimes caused flameproof spots and yarn breakage due to heat storage.
Moreover, in the groove | channel of a grooved roll, when the run position of a precursor fiber bundle has shifted | deviated to the inclination part of one convex part among the convex parts which form a groove | channel, it is a precursor fiber from the edge part of a groove bottom part as a boundary There was a problem that the bundle was easily broken and the shape of the traveling precursor fiber bundle became unstable.
Further, as described in Patent Document 1, when a grooved roll is used as the folding roll, the grooved roll is not easily exchanged, and maintenance is difficult.
本発明は上記事情に鑑みてなされたもので、ポリアクリロニトリル系前駆体繊維束を耐炎化処理するに際し、ポリアクリロニトリル系前駆体繊維束の折れや厚み斑を防止するとともに、耐炎化炉内を走行するポリアクリロニトリル系前駆体繊維束の形態を安定に維持できる炭素繊維束の製造方法を提供することを目的とする。
また、本発明は、ポリアクリロニトリル系前駆体繊維束を耐炎化処理するに際し、ポリアクリロニトリル系前駆体繊維束の折れや厚み斑を防止し、耐炎化炉内を走行するポリアクリロニトリル系前駆体繊維束の形態を安定に維持でき、かつメンテナンスが容易な炭素繊維束の製造装置を提供することを目的とする。
The present invention has been made in view of the above circumstances, and when the polyacrylonitrile-based precursor fiber bundle is subjected to flameproofing treatment, the polyacrylonitrile-based precursor fiber bundle is prevented from being bent or thick and running in a flameproofing furnace. An object of the present invention is to provide a method for producing a carbon fiber bundle capable of stably maintaining the form of the polyacrylonitrile-based precursor fiber bundle.
In addition, the present invention provides a polyacrylonitrile-based precursor fiber bundle that prevents the polyacrylonitrile-based precursor fiber bundle from being bent or thickened when the polyacrylonitrile-based precursor fiber bundle is subjected to flameproofing treatment, and travels in the flameproofing furnace. An object of the present invention is to provide a carbon fiber bundle manufacturing apparatus that can stably maintain the form of the above and can be easily maintained.
本発明の炭素繊維束の製造方法は、総繊度が14,000〜40,000dtexのポリアクリロニトリル系前駆体繊維束を耐炎化炉の外側で、折り返しロールにより折り返して、前記耐炎化炉内に走行させ耐炎化処理する工程と、耐炎化処理されたポリアクリロニトリル系前駆体繊維束を炭素化処理する工程とを有する炭素繊維束の製造方法において、前記耐炎化炉と折り返しロールとの間に、下記式(1)〜(3)を満足する溝が設けられた繊維束規制部材を配置し、前記耐炎化炉から送出したポリアクリロニトリル系前駆体繊維束を繊維束規制部材に通過させ、前記繊維束規制部材を通過後のポリアクリロニトリル系前駆体繊維束の幅1mm当たりの見かけの平均繊度を2,500〜5,000dtexに保つことを特徴とする。
0.5≦b/a≦0.8 ・・・(1)
0.4×a≦h≦0.7×a ・・・(2)
0.45×(a−b)≦R≦0.8×(a−b) ・・・(3)
(式(1)〜(3)中、aは溝開口部の平均幅(mm)であり、bは溝底部の平均幅(mm)であり、hは溝の平均深さ(mm)であり、Rは溝底部の曲率半径(mm)である。)
In the method for producing a carbon fiber bundle of the present invention, a polyacrylonitrile-based precursor fiber bundle having a total fineness of 14,000 to 40,000 dtex is folded by a folding roll outside the flameproofing furnace and travels in the flameproofing furnace. In the method for producing a carbon fiber bundle, the method comprising the steps of: flameproofing, and carbonizing the flameproofed polyacrylonitrile-based precursor fiber bundle, between the flameproofing furnace and the folding roll, A fiber bundle regulating member provided with grooves satisfying the formulas (1) to (3) is arranged, and the polyacrylonitrile-based precursor fiber bundle sent from the flameproofing furnace is passed through the fiber bundle regulating member, and the fiber bundle The apparent average fineness per 1 mm width of the polyacrylonitrile-based precursor fiber bundle after passing through the regulating member is maintained at 2,500 to 5,000 dtex.
0.5 ≦ b / a ≦ 0.8 (1)
0.4 × a ≦ h ≦ 0.7 × a (2)
0.45 × (ab) ≦ R ≦ 0.8 × (ab) (3)
(In the formulas (1) to (3), a is the average width (mm) of the groove opening, b is the average width (mm) of the groove bottom, and h is the average depth (mm) of the groove. , R is the radius of curvature (mm) of the groove bottom.)
また、前記繊維束規制部材と折り返しロールとの中心間距離が150mm以上となるように、繊維束規制部材を折り返しロールの送入側に配置することが好ましい。
さらに、前記繊維束規制部材と折り返しロールとの中心間距離が350mm以上となるように、繊維束規制部材を折り返しロールの送出側に配置することが好ましい。
Moreover, it is preferable to arrange the fiber bundle regulating member on the feeding side of the folding roll so that the distance between the centers of the fiber bundle regulating member and the folding roll is 150 mm or more.
Furthermore, it is preferable to arrange the fiber bundle regulating member on the sending side of the folding roll so that the distance between the centers of the fiber bundle regulating member and the folding roll is 350 mm or more.
また、本発明の炭素繊維束の製造装置は、総繊度が14,000〜40,000dtexのポリアクリロニトリル系前駆体繊維束を耐炎化処理する耐炎化炉と、該耐炎化炉の外側でポリアクリロニトリル系前駆体繊維束を折り返して、耐炎化炉内に走行させる折り返しロールと、耐炎化処理されたポリアクリロニトリル系前駆体繊維束を炭素化処理する炭素化手段とを具備する炭素繊維束の製造装置において、前記耐炎化炉と折り返しロールとの間に、下記式(1)〜(3)を満足する溝が設けられた繊維束規制部材が配置されたことを特徴とする。
0.5≦b/a≦0.8 ・・・(1)
0.4×a≦h≦0.7×a ・・・(2)
0.45×(a−b)≦R≦0.8×(a−b) ・・・(3)
(式(1)〜(3)中、aは開口部の平均幅(mm)であり、bは溝底部の平均幅(mm)であり、hは溝の平均深さ(mm)であり、Rは溝底部の曲率半径(mm)である。)
The carbon fiber bundle manufacturing apparatus of the present invention includes a flameproofing furnace for flameproofing a polyacrylonitrile-based precursor fiber bundle having a total fineness of 14,000 to 40,000 dtex, and a polyacrylonitrile outside the flameproofing furnace. Apparatus for producing a carbon fiber bundle, comprising: a folding roll that folds the system precursor fiber bundle and travels in the flameproofing furnace; and a carbonization means for carbonizing the flameproofed polyacrylonitrile precursor fiber bundle The fiber bundle regulating member provided with a groove satisfying the following formulas (1) to (3) is disposed between the flameproofing furnace and the folding roll.
0.5 ≦ b / a ≦ 0.8 (1)
0.4 × a ≦ h ≦ 0.7 × a (2)
0.45 × (ab) ≦ R ≦ 0.8 × (ab) (3)
(In the formulas (1) to (3), a is the average width (mm) of the opening, b is the average width (mm) of the groove bottom, and h is the average depth (mm) of the groove. R is the radius of curvature (mm) of the groove bottom.
さらに、前記繊維束規制部材が前記折り返しロールの送入側に配置され、繊維束規制部材と折り返しロールとの中心間距離が150mm以上であることが好ましい。
また、前記繊維束規制部材が前記折り返しロールの送出側に配置され、繊維束規制部材と折り返しロールとの中心間距離が350mm以上であることが好ましい。
Furthermore, it is preferable that the fiber bundle regulating member is disposed on the feeding side of the folding roll, and the distance between the centers of the fiber bundle regulating member and the folding roll is 150 mm or more.
Moreover, it is preferable that the said fiber bundle control member is arrange | positioned at the sending side of the said folding | returning roll, and the distance between centers of a fiber bundle control member and a folding | turning roll is 350 mm or more.
本発明の炭素繊維束の製造方法によれば、ポリアクリロニトリル系前駆体繊維束を耐炎化処理するに際し、ポリアクリロニトリル系前駆体繊維束の折れや厚み斑を防止するとともに、耐炎化炉内を走行するポリアクリロニトリル系前駆体繊維束の形態を安定に維持できる。
また、本発明の炭素繊維束の製造装置によれば、ポリアクリロニトリル系前駆体繊維束を耐炎化処理するに際し、ポリアクリロニトリル系前駆体繊維束の折れや厚み斑を防止し、耐炎化炉内を走行するポリアクリロニトリル系前駆体繊維束の形態を安定に維持でき、かつメンテナンスが容易である。
According to the method for producing a carbon fiber bundle of the present invention, when the polyacrylonitrile-based precursor fiber bundle is subjected to a flame resistance treatment, the polyacrylonitrile-based precursor fiber bundle is prevented from being bent or thick and running in a flame-resistant furnace. It is possible to stably maintain the form of the polyacrylonitrile-based precursor fiber bundle.
In addition, according to the carbon fiber bundle manufacturing apparatus of the present invention, when the polyacrylonitrile-based precursor fiber bundle is subjected to flame resistance treatment, the polyacrylonitrile-based precursor fiber bundle is prevented from being bent or thick, and the inside of the flame resistance furnace is prevented. The form of the traveling polyacrylonitrile-based precursor fiber bundle can be stably maintained, and maintenance is easy.
以下、本発明の実施形態の一例について、図面を用いて詳細に説明する。
図1は、本発明の炭素繊維束の製造装置の一例を示す概略構成図である。この例の炭素繊維束の製造装置10は、ポリアクリロニトリル系前駆体繊維束(以下、「前駆体繊維束」という。)11を耐炎化処理する耐炎化炉12と、耐炎化炉12の外側で前駆体繊維束11を合計6回折り返して、前駆体繊維束を耐炎化炉12内に走行させる折り返しロール13と、耐炎化処理された前駆体繊維束11を炭素化処理する炭素化手段14とを具備する。そして、前記耐炎化炉12と折り返しロール13との間には、繊維束規制部材15が配置されている。
Hereinafter, an example of an embodiment of the present invention will be described in detail with reference to the drawings.
FIG. 1 is a schematic configuration diagram illustrating an example of a carbon fiber bundle manufacturing apparatus according to the present invention. The carbon fiber
本発明に用いられる前駆体繊維束11としては、アクリロニトリル系重合体からなる繊維を束ねたものが挙げられる。アクリロニトリル系重合体としては、アクリロニトリルのホモポリマーおよび/またはアクリロニトリルと共重合可能なモノマーとの共重合体を用いることができる。
また、本発明に用いられる前駆体繊維束11は、総繊度が14,000〜40,000dtexである。前駆体繊維束の総繊度が14,000dtex以上であれば、断面形状を円形から略矩形にすることで前駆体繊維束の厚みの抑制量が大きくなり、蓄熱による糸切れ防止などにつながる。一方、総繊度が40,000dtex以下であれば、幅1mm当たりの見かけの平均繊度の範囲から、前駆体繊維束の幅が広くなりすぎず、形態を安定に維持することが容易となる。
本発明は、特に総繊度が20,000〜30,000dtexの前駆体繊維束を耐炎化処理するのに好適である。
Examples of the
The
The present invention is particularly suitable for flameproofing a precursor fiber bundle having a total fineness of 20,000 to 30,000 dtex.
耐炎化炉12内を走行する前駆体繊維束11の断面形状は略矩形に保たれ、その平均扁平率が10〜50の範囲に制御されるのが好ましい。平均扁平率が10未満であると、前駆体繊維束11の厚みが増大し、耐炎化処理での反応による蓄熱で糸切れ等が起こりやすくなる。また、平均扁平率が50を超えると前駆体繊維束11の幅が増大するため、耐炎化炉12幅に対して処理可能な前駆体繊維束11の本数が減少し、設備生産性が低下する。従って、前駆体繊維束11は平均扁平率が10〜50の範囲に制御されるのが好ましく、より好ましくは15〜35の範囲である。
ここで、「略矩形」とは、略平行な2組の直線で囲まれた形状を指し、角が曲線であっても構わない。
It is preferable that the cross-sectional shape of the
Here, “substantially rectangular” refers to a shape surrounded by two sets of substantially parallel straight lines, and the corners may be curved.
略矩形の前駆体繊維束の平均扁平率は以下のようにして定義した。
一般に知られるレーザー変位計をアクチュエータにより20mm/sの速度にてトウの幅方向に渡ってスライドさせながら、前駆体繊維束の厚みをサンプリング周期10ミリ秒毎にて測定する。同様の測定を1サンプルにつき5回行い、それを平均して繊維束厚みAとする。
また、走行する前駆体繊維束の駆動を止めて、ノギスを用いて前駆体繊維束の幅を長手方向に5cmの間隔で5点測定し、それを平均して繊維束幅Bとする。
繊維束幅Bを繊維束厚みAで除した値(B/A)を平均扁平率とする。
The average flatness of the substantially rectangular precursor fiber bundle was defined as follows.
While a generally known laser displacement meter is slid across the width of the tow by an actuator at a speed of 20 mm / s, the thickness of the precursor fiber bundle is measured every 10 milliseconds. The same measurement is performed five times for each sample, and the average is defined as the fiber bundle thickness A.
Further, driving of the traveling precursor fiber bundle is stopped, and the width of the precursor fiber bundle is measured at intervals of 5 cm in the longitudinal direction using a caliper, and this is averaged to obtain a fiber bundle width B.
A value (B / A) obtained by dividing the fiber bundle width B by the fiber bundle thickness A is defined as an average flatness.
耐炎化炉12は、前駆体繊維束11を耐炎化処理する手段である。耐炎処理温度は200〜300℃が好ましい。
耐炎化炉12の対面する側壁には、前駆体繊維束11が送入または送出するスリット状の送入口または送出口(図示略)が設けられている。このような耐炎化炉12としては、炭素繊維束を製造する際に用いられる公知の耐炎化炉を使用できる。
The flameproofing
A slit-like inlet or outlet (not shown) through which the
折り返しロール13は、耐炎化炉12の外側に回転可能に設けられている。折り返しロール13は、耐炎化炉12から送出された前駆体繊維束11を掛け回して折り返すことにより、前駆体繊維束11の走行方向を逆方向に転換させ、再び耐炎化炉12内に走行させる。
折り返しロール13としては、軸方向に対して直線状である平ロールが適している。また、折り返しロール13の材質としては特に限定されず、例えば炭素鋼、ステンレス鋼、セラミックス、アルミニウム、チタンなどが挙げられる。
The
As the
繊維束規制部材15は、耐炎化炉12と折り返しロール13との間に配置されている。
ここで、繊維束規制部材15について、図2、3を用いて具体的に説明する。図2は繊維束規制部材15の一例を示す正面図であり、図3は繊維束規制部材15の部分拡大図である。
繊維束規制部材15の表面には、前駆体繊維束の進行方向に沿って延びる複数の溝151が設けられている。図3に示すように、繊維束規制部材15の表面には、複数の凸部152が離間して設けられ、溝151が形成されている。凸部152は、溝151に面する壁面153a、153bと、先端部154を有する。また、溝151の溝底部155は、その端部156a、156bが曲率半径R’の曲面状である。
The fiber
Here, the fiber
On the surface of the fiber
繊維束規制部材15に設けられた溝151は、下記式(1)〜(3)を満たす。
0.5≦b/a≦0.8 ・・・(1)
0.4×a≦h≦0.7×a ・・・(2)
0.45×(a−b)≦R≦0.8×(a−b) ・・・(3)
The
0.5 ≦ b / a ≦ 0.8 (1)
0.4 × a ≦ h ≦ 0.7 × a (2)
0.45 × (ab) ≦ R ≦ 0.8 × (ab) (3)
式(1)〜(3)中、aは溝開口部158の平均幅(mm)であり、bは溝底部155の平均幅(mm)であり、hは溝151の平均深さ(mm)であり、Rは溝底部155の曲率半径(mm)である。
ここで、溝開口部158の幅とは、図3に示すように、隣接する凸部152の先端部154間の幅(凸部の先端部から、隣接する凸部の先端部までの距離a’)のことである。溝開口部158の平均幅は、距離a’を10点測定し、これらの値を平均したものである。
溝底部155の幅とは、図3に示すように、溝底部155の端部156aの形状を形成する曲率半径R’の円と、溝151に面する壁面153aとの接点157aから、端部156bの形状を形成する曲率半径R’の円と、溝151に面する壁面153bとの接点157bまでの距離b’のことである。溝底部155の平均幅は、距離b’を10点測定し、これらの値を平均したものである。
溝151の深さとは、図3に示すように、凸部152の先端部154から溝底部155までの距離h’のことである。溝151の平均深さは、距離h’を10点測定し、これらの値を平均したものである。
溝底部155の平均曲率半径は、曲率半径R’を10点測定し、これらの値を平均したものである。
In the formulas (1) to (3), a is the average width (mm) of the
Here, as shown in FIG. 3, the width of the
As shown in FIG. 3, the width of the
As shown in FIG. 3, the depth of the
The average radius of curvature of the
本発明者らは鋭意検討した結果、前駆体繊維束の断面形状を略矩形に保つには、溝底部155の曲率半径R’を規定し、溝底部155に幅をもたせることが重要であることを見出した。
すなわち、溝開口部158の平均幅(a)と、溝底部155の平均幅(b)の比(b/a)が0.5未満であると、溝151の形状がV字状に近づき、前駆体繊維束の断面形状を略矩形に保持しにくくなる。一方、b/aが0.8を越えると、凸部152の壁面153a、153bの傾きが溝底部155に対して大きくなり、走行中の前駆体繊維束の端が折れやすくなり、前駆体繊維束の形態維持性が低下する。b/aは0.55〜0.65が好ましい。
As a result of intensive studies, the present inventors have determined that it is important to define the radius of curvature R ′ of the
That is, when the ratio (b / a) of the average width (a) of the
溝151の平均深さ(h)が溝開口部158の平均幅(a)の0.4倍未満であると、走行中の前駆体繊維束の一部が溝151を乗り越える場合があり、隣接する前駆体繊維束同士が絡んで毛羽立ちを生じることがある。一方、hが溝開口部158の平均幅(a)の0.7倍を超えると、溝151の断面積に対する前駆体繊維束の断面積が小さくなり、加工コストが増大して経済的ではない。hは0.45×a〜0.55×aが好ましい。
If the average depth (h) of the
溝底部155の平均曲率半径(R)が0.45×(a−b)未満であると、前駆体繊維束の端が折れやすくなったり、溝底部155の端部156a、156bにおいて前駆体繊維束に厚み斑が生じたりしやすくなる。一方、Rが0.8×(a−b)を超えると、溝底部155の幅に対して、端部156a、156bの形状を形成する円の半径が大きくなりすぎ、前駆体繊維束が溝151を乗り越える場合があり、隣接する前駆体繊維束同士が絡んで毛羽立ちを生じることがある。また、Rが大きくなると、凸部152の壁面153a、153bと、溝底部155とが滑らかにつながりにくくなり、前駆体繊維束の端が折れる原因となる可能性がある。Rは0.45×(a−b)〜0.65×(a−b)が好ましい。
When the average curvature radius (R) of the
なお、溝底部155は図2、3に示すような平底に限定されず、円弧状であてもよい。円弧状であれば、前駆体繊維束の幅方向の走行の振れを抑制しやすくなり、走行位置制御性の向上が図れる。
The
図1に示すように、繊維束規制部材15が折り返しロール13の送入側に配置される場合、繊維束規制部材15と折り返しロール13との中心間距離W1が150mm以上であることが好ましい。前駆体繊維束11は、繊維束規制部材15の通過時に溝に沿った形状となるため、中心間距離W1が150mm未満であると、前駆体繊維束11の幅が狭まった状態で折り返しロール13に到達し、次いで耐炎化炉12へ投入される可能性がある。中心間距離W1は200mm以上がより好ましい。中心間距離W1は、繊維束規制部材15を耐炎化炉12の外に配置している限り長くても構わないが、550mm以下が好ましい。
As shown in FIG. 1, when the fiber
また、図4に示すように、繊維束規制部材15が折り返しロール13の送出側に配置される場合、繊維束規制部材15と折り返しロール13との中心間距離W2が350mm以上であることが好ましい。折り返しロール13の送出側で前駆体繊維束を制御する場合、前駆体繊維束の幅方向の拘束力が強いため、中心間距離W2が350mm未満であると、前駆体繊維束が溝を乗り越えやすくなる。中心間距離W2は450mm以上がより好ましい。中心間距離W2は、繊維束規制部材15を耐炎化炉12の外に配置している限り長くても構わないが、700mm以下が好ましい。
As shown in FIG. 4, when the fiber
繊維束規制部材15の形態としては、図2に示すようなロール状(溝付きロール)でも、プレートに同溝を加工したプレート状(溝付きプレート)でもよく、前記式(1)〜(3)を満足する溝形状を有したものであれば何ら差し支えない。
また、繊維束規制部材15の材質としては特に限定されず、例えば炭素鋼、ステンレス鋼、セラミックス、アルミニウム、チタンなどが挙げられる。
The form of the fiber
Moreover, it does not specifically limit as a material of the fiber
炭素化手段14は、耐炎化処理された前駆体繊維束11を炭素化処理する手段である。炭素化処理の温度は600℃を超える温度が好ましい。
炭素化手段14としては、炭素繊維束を製造する際に用いられる公知の炭素化炉を使用できる。
The carbonization means 14 is a means for carbonizing the
As the carbonization means 14, the well-known carbonization furnace used when manufacturing a carbon fiber bundle can be used.
図1に示す炭素繊維の製造装置1を用いた炭素繊維の製造方法では、前駆体繊維束11を耐炎化炉12にて、例えば200〜300℃の温度で耐炎化処理し、次いで炭素化手段14にて、例えば600℃を超える温度で炭素化処理することで、炭素繊維束を製造できる。
In the carbon fiber manufacturing method using the carbon fiber manufacturing apparatus 1 shown in FIG. 1, the
具体的には、前駆体繊維束11は、耐炎化炉12の側壁内に設けられたスリット状の送入口(図示略)から送入され、耐炎化炉12を直線的に走行した後、対面の側壁に設けられたスリット状の送出口(図示略)から耐炎化炉12の外側に一旦送出される。次いで、繊維束規制部材15を通過する際に束毎に繊維束規制部材15の溝151に押し込まれて、前駆体繊維束の幅が任意の幅になるように規制されながら移送される。そして、折り返しロール13によって折り返され走行方向を転換し、再び耐炎化炉12内に送入される。このように、前駆体繊維束11は、繊維束規制部材15を通過することによって走行位置や断面形状を規制されつつ、折り返しロール13によって走行方向を複数回折り返すことで、耐炎化炉12内への送入送出を複数回繰り返しながら、耐炎化炉12内を全体として図1の上から下に向けて移動し、耐炎化処理される。耐炎化処理された前駆体繊維束(耐炎化繊維束)は、炭素化手段14によって炭素化処理され、炭素繊維束が得られる。
なお、炭素繊維束を製造する際は、前駆体繊維束を複数本平行に並べ、同時に耐炎化炉および炭素化手段内を走行させて、耐炎化処理および炭素化処理してもよい。
Specifically, the
In addition, when producing a carbon fiber bundle, a plurality of precursor fiber bundles may be arranged in parallel and simultaneously run in a flameproofing furnace and a carbonizing means to perform a flameproofing treatment and a carbonization treatment.
繊維束規制部材15を通過した前駆体繊維束は、該前駆体繊維束の幅1mm当たりの見かけの平均繊度が2,500〜5,000dtexに保たれる。見かけの平均繊度が2,500dtex未満であると、処理可能な前駆体繊維束の本数が少なくなり、設備生産性が低下する。一方、見かけの平均繊度が5,000dtexを超えると、厚みが増大して耐炎化反応による蓄熱で毛羽立ちや糸切れが発生しやすくなる。前駆体繊維束の幅1mm当たりの見かけの平均繊度は、2,900〜4,200dtexに保たれるのが好ましい。
The precursor fiber bundle that has passed through the fiber
本発明によれば、前駆体繊維束の幅1mm当たりの見かけの平均繊度を上記範囲内に保つことができるので、耐炎化処理温度を下げることなく、耐炎化反応の蓄熱による毛羽立ちや糸切れの発生を抑制でき、生産性を良好に維持できる。さらに、耐炎化反応に必要な酸素が前駆体繊維束の内部にまで十分に拡散されるので、内部と表面とで均一に耐炎化が進行しやすくなる。よって、炭素化処理において毛羽立ちや糸傷み等の発生を抑制できる。 According to the present invention, since the apparent average fineness per 1 mm width of the precursor fiber bundle can be maintained within the above range, fluffing and yarn breakage due to heat accumulation of the flameproofing reaction can be achieved without lowering the flameproofing temperature. Generation can be suppressed and productivity can be maintained well. Furthermore, since the oxygen necessary for the flameproofing reaction is sufficiently diffused into the precursor fiber bundle, the flameproofing easily progresses uniformly between the inside and the surface. Therefore, generation | occurrence | production of a fuzz, a thread | yarn damage, etc. can be suppressed in carbonization processing.
また、耐炎化炉12内を走行する前駆体繊維束は、耐炎化炉12前後に設置される駆動ローラーやニップローラー等の駆動装置(図示略)によって2×10−2〜2.1×10−1g/dtexの張力を付与されるのが好ましい。張力が5.2×10−2g/dtex未満であると、前駆体繊維束が懸垂し耐炎化炉の底にこすれて毛羽が発生し、後の炭素化処理で得られる炭素繊維束の品位、および引張り強度低下を招くおそれがある。一方、張力が2.1×10−1g/dtexを超えると、耐炎化処理での単糸切れによる毛羽立ちが増長し、ロール上で巻付きを発生するおそれがある。耐炎化炉内にて安定して耐炎化処理するには、前駆体繊維束にかかる張力を1×10−1〜1.7×10−1g/dtexとするのがより好ましい。
The precursor fiber bundle traveling in the flameproofing
以上説明したように、本発明によれば、前駆体繊維束を耐炎化処理するに際し、溝の形状を規定した繊維束規制部材を用いることで、前駆体繊維束の走行位置を規制するとともに、前駆体繊維束の断面形状を略矩形に維持しつつ、平均繊度を所望の値に保つことができる。従って、耐炎化処理するに際し、特に繊維束規制部材通過時の前駆体繊維束の折れや厚み斑を防止でき、かつ耐炎化炉内を走行する前駆体繊維束の形態を安定に維持できる。
従って、本発明によれば、耐炎化処理中の糸切れや毛羽立ちを抑制でき、安定して高品位の炭素繊維束を製造できる。また、耐炎化炉と折り返しロールの間に繊維束規制部材を配置することで、繊維束規制部材の交換が簡便となり、メンテナンスが容易であるため、作業性の向上を図れる。
As described above, according to the present invention, when the precursor fiber bundle is flameproofed, by using the fiber bundle regulating member that defines the shape of the groove, the travel position of the precursor fiber bundle is regulated, The average fineness can be maintained at a desired value while maintaining the cross-sectional shape of the precursor fiber bundle in a substantially rectangular shape. Therefore, when performing the flameproofing treatment, it is possible to prevent the precursor fiber bundles from being bent and thickness unevenness particularly when passing through the fiber bundle regulating member, and it is possible to stably maintain the form of the precursor fiber bundle running in the flameproofing furnace.
Therefore, according to the present invention, yarn breakage and fluff during the flameproofing treatment can be suppressed, and a high-quality carbon fiber bundle can be produced stably. Further, by disposing the fiber bundle regulating member between the flameproofing furnace and the folding roll, replacement of the fiber bundle regulating member becomes simple and maintenance is easy, so that workability can be improved.
以下、本発明について実施例を挙げて具体的に説明する。ただし、本発明はこれらに限定されるものではない。
各種測定方法は、以下の通りである。
Hereinafter, the present invention will be specifically described with reference to examples. However, the present invention is not limited to these.
Various measurement methods are as follows.
(平均扁平率)
レーザー変位計(株式会社キーエンス製、「LK−G10」)をアクチュエータ(THK株式会社製、「KT45」)により20mm/sの速度にてトウの幅方向に渡ってスライドさせながら、前駆体繊維束の厚みをサンプリング周期10ミリ秒毎にて測定した。同様の測定を1サンプルにつき5回行い、それを平均して繊維束厚みAとした。
また、走行する前駆体繊維束の駆動を止めて、ノギスを用いて前駆体繊維束の幅を長手方向に5cmの間隔で5点測定し、それを平均して繊維束幅Bとした。
繊維束幅Bを繊維束厚みAで除した値(B/A)を平均扁平率とした。
(Average flatness)
While displacing a laser displacement meter (manufactured by Keyence Corporation, “LK-G10”) across the width of the tow at a speed of 20 mm / s by an actuator (manufactured by THK, “KT45”), the precursor fiber bundle Was measured at a sampling period of 10 milliseconds. The same measurement was performed 5 times per sample, and the average value was defined as the fiber bundle thickness A.
Further, the driving of the traveling precursor fiber bundle was stopped, and the width of the precursor fiber bundle was measured at intervals of 5 cm in the longitudinal direction using a caliper, and this was averaged to obtain a fiber bundle width B.
A value (B / A) obtained by dividing the fiber bundle width B by the fiber bundle thickness A was defined as the average flatness.
(平均繊度)
前駆体繊維束の幅1mmに対する見かけの平均繊度は、前駆体繊維束の総繊度を前記ノギスを用いて測定した繊維束幅Bで除することにより求めた。
(Average fineness)
The apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle was determined by dividing the total fineness of the precursor fiber bundle by the fiber bundle width B measured using the caliper.
(張力)
前駆体繊維束にかかる張力は、走行する前駆体繊維束をテンションメータ(日本電産シンポ株式会社製、「DTMB」)により測定した。
(tension)
The tension applied to the precursor fiber bundle was measured by using a tension meter (“DTMB” manufactured by Nidec Shinpo Co., Ltd.).
[実施例1]
炭素繊維束の製造装置として、図1に示す装置を用いた。耐炎化炉12と折り返しロール13の間には、繊維束規制部材15としてa=10mm、b=6.5mm、h=5mm、R=2.5mm[すなわち、b/a=0.65、h=0.50×a、R=0.71×(a−b)]の溝が表面に設けられた溝付きロールAを配置した。溝付きロールAは、折り返しロール13との中心間距離が450mmとなるように、折り返しロール13の送入側に配置した。
そして、総繊度が28,800dtexのポリアクリロニトリル系前駆体繊維束を用い、炭素繊維束を製造した。
前駆体繊維束が溝付きロールAを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表1に示す。
[Example 1]
The apparatus shown in FIG. 1 was used as a carbon fiber bundle manufacturing apparatus. Between the flameproofing
A carbon fiber bundle was manufactured using a polyacrylonitrile-based precursor fiber bundle having a total fineness of 28,800 dtex.
The form when the precursor fiber bundle passed through the grooved roll A was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 1.
[実施例2]
繊維束規制部材として、a=8mm、b=4.8mm、h=4mm、R=1.5mm[すなわち、b/a=0.60、h=0.50×a、R=0.47×(a−b)]の溝が表面に設けられた溝付きロールBを用いた以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールAを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表1に示す。
[Example 2]
As a fiber bundle regulating member, a = 8 mm, b = 4.8 mm, h = 4 mm, R = 1.5 mm [that is, b / a = 0.60, h = 0.50 × a, R = 0.47 × A carbon fiber bundle was produced in the same manner as in Example 1 except that the grooved roll B having the groove (a-b)] provided on the surface thereof was used.
The form when the precursor fiber bundle passed through the grooved roll A was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 1.
[実施例3]
繊維束規制部材として、a=8mm、b=4.8mm、h=4mm、R=1.5mm[すなわち、b/a=0.60、h=0.50×a、R=0.47×(a−b)]の溝が表面に設けられた溝付きプレートAを用いた以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きプレートAを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表1に示す。
[Example 3]
As a fiber bundle regulating member, a = 8 mm, b = 4.8 mm, h = 4 mm, R = 1.5 mm [that is, b / a = 0.60, h = 0.50 × a, R = 0.47 × A carbon fiber bundle was produced in the same manner as in Example 1 except that the grooved plate A provided with the grooves (a−b)] on the surface thereof was used.
The form when the precursor fiber bundle passed through the grooved plate A was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 1.
実施例1および2のように、上記式(1)〜(3)を満たす形状を有する溝が設けられた溝付きロールで前駆体繊維束の走行位置や形態を制御した場合、前駆体繊維束の端の折れや厚み斑、溝とび(溝乗り越え)等のトラブルは発生しなかった。また、表1の結果は、同じ形状の溝が設けられた溝付きロールと溝付きプレートの糸条形態制御性は同等であり、溝を加工する部材によって大きな差異がないことを示している。 When the running position and form of the precursor fiber bundle are controlled by the grooved roll provided with the grooves having the shapes satisfying the above formulas (1) to (3) as in Examples 1 and 2, the precursor fiber bundle is controlled. Troubles such as edge breakage, thickness unevenness, and groove jumping (over the groove) did not occur. Moreover, the result of Table 1 shows that the thread form controllability of the grooved roll provided with the groove having the same shape and the grooved plate is equivalent, and there is no great difference depending on the member that processes the groove.
[実施例4]
溝付きロールAと折り返しロール13との中心間距離が250mmとなるように、溝付きロールAを折り返しロール13の送入側に配置した以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールAを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表2に示す。
[Example 4]
A carbon fiber bundle is produced in the same manner as in Example 1 except that the grooved roll A is arranged on the feeding side of the
The form when the precursor fiber bundle passed through the grooved roll A was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 2.
[実施例5]
繊維束規制部材として溝付きロールBを用い、溝付きロールBと折り返しロール13との中心間距離が250mmとなるように、溝付きロールBを折り返しロール13の送入側に配置した以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールBを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表2に示す。
[Example 5]
Except for using the grooved roll B as the fiber bundle regulating member and arranging the grooved roll B on the feeding side of the
The form when the precursor fiber bundle passed the grooved roll B was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 2.
[比較例1]
繊維束規制部材としてa=10mm、b=6.8mm、h=5mm、R=3mm[すなわち、b/a=0.68、h=0.50×a、R=0.94×(a−b)]の溝が表面に設けられた溝付きロールCを用い、溝付きロールCと折り返しロール13との中心間距離が250mmとなるように、溝付きロールCを折り返しロール13の送入側に配置した以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールCを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表2に示す。
[Comparative Example 1]
As a fiber bundle regulating member, a = 10 mm, b = 6.8 mm, h = 5 mm, R = 3 mm [that is, b / a = 0.68, h = 0.50 × a, R = 0.94 × (a− b)] using the grooved roll C provided on the surface, the grooved roll C is fed to the
The form when the precursor fiber bundle passed through the grooved roll C was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 2.
[比較例2]
繊維束規制部材としてa=8mm、b=4.5mm、h=4mm、R=1mm[すなわち、b/a=0.56、h=0.50×a、R=0.29×(a−b)]の溝が表面に設けられた溝付きロールDを用い、溝付きロールDと折り返しロール13との中心間距離が250mmとなるように、溝付きロールDを折り返しロール13の送入側に配置した以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールDを通過したときの形態を観察し、平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表2に示す。
[Comparative Example 2]
As a fiber bundle regulating member, a = 8 mm, b = 4.5 mm, h = 4 mm, R = 1 mm [that is, b / a = 0.56, h = 0.50 × a, R = 0.29 × (a− b)] using the grooved roll D provided on the surface, the grooved roll D is fed to the
The form when the precursor fiber bundle passed through the grooved roll D was observed, and the average flatness, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, and the tension applied to the precursor fiber bundle were determined. The results are shown in Table 2.
溝付きロールA、またはBの通過後と折り返しロール上での前駆体繊維束の形態を観察したところ、前駆体繊維束の形態は制御されていた。また、実施例4、5では、前駆体繊維束の幅方向に溝付きロールA、またはBの設置位置をずらし、繊維束規制部材の凸部の壁面に片あたりさせて走行させたが、前駆体繊維束の形態は制御可能であった。
一方、比較例1の場合、溝付きロールCの通過後と折り返しロール上での前駆体繊維束の形態を観察したところ、前駆体繊維束の形態は制御されていたが、前駆体繊維束の幅方向に溝付きロールCの設置位置をずらし、繊維束規制部材の凸部の壁面に片あたりさせて走行させた場合、前駆体繊維束の端が厚くなり厚み斑が生じた。
比較例2の場合、溝付きロールDの通過後と折り返しロール上での前駆体繊維束の形態を観察したところ、前駆体繊維束の形態は制御されていたが、前駆体繊維束の幅方向に溝付きロールDの設置位置をずらし、繊維束規制部材の凸部の壁面に片あたりさせて走行させた場合、前駆体繊維束の端が折れた状態で折り返しロールを通過する結果となった。
以上の結果より、上記式(1)、(2)を満足する溝であっても、繊維束規制部材の凸部の壁面と溝底部を滑らかに接続する曲率半径Rでなければ、特に前駆体繊維束が片あたりして走行した場合に前駆体繊維束の端が折れたり、厚み斑が生じたりするなどのトラブルが発生することになる。従って、上記式(3)を満足する範囲内に平均曲率半径Rを設定する必要がある。
When the form of the precursor fiber bundle after passing the grooved roll A or B and on the folding roll was observed, the form of the precursor fiber bundle was controlled. In Examples 4 and 5, the grooved roll A or B was shifted in the width direction of the precursor fiber bundle, and the fiber bundle restricting member was allowed to run on the wall surface of the protruding portion. The morphology of the body fiber bundle was controllable.
On the other hand, in the case of Comparative Example 1, when the form of the precursor fiber bundle was observed after passing through the grooved roll C and on the folding roll, the form of the precursor fiber bundle was controlled. When the installation position of the grooved roll C was shifted in the width direction and allowed to run on the wall surface of the convex portion of the fiber bundle regulating member, the end of the precursor fiber bundle was thickened, resulting in thickness spots.
In the case of Comparative Example 2, when the form of the precursor fiber bundle was observed after passing through the grooved roll D and on the folding roll, the form of the precursor fiber bundle was controlled, but the width direction of the precursor fiber bundle was When the installation position of the grooved roll D is shifted to run on the wall surface of the convex portion of the fiber bundle regulating member, the result is that the end of the precursor fiber bundle is folded and passes through the folding roll. .
From the above results, even if the groove satisfies the above formulas (1) and (2), unless the curvature radius R smoothly connects the wall surface of the convex part of the fiber bundle regulating member and the groove bottom part, it is particularly a precursor. When the fiber bundle travels in contact with each other, troubles such as the end of the precursor fiber bundle being broken or a thickness unevenness occur. Therefore, it is necessary to set the average radius of curvature R within a range that satisfies the above formula (3).
[実施例6〜9]
繊維束規制部材として溝付きロールBを用い、溝付きロールBと折り返しロール13との中心間距離が表3に示す値になるように、溝付きロールBを折り返しロール13の送入側に配置した以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールBを通過したときの形態を観察し、溝付きロールBを通過する前の平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表3に示す。
[Examples 6 to 9]
The grooved roll B is used as the fiber bundle regulating member, and the grooved roll B is arranged on the feeding side of the
Observe the form when the precursor fiber bundle passed through the grooved roll B, the average flatness before passing through the grooved roll B, the apparent average fineness for the width of 1 mm of the precursor fiber bundle, the precursor fiber bundle Such tension was determined. The results are shown in Table 3.
折り返しロールの送入側に繊維束規制部材を配置する場合、前駆体繊維束は繊維束規制部材通過時に溝に沿った形状になり、走行位置規制と前駆体繊維束の形態制御がなされる。そして繊維束規制部材通過後に略矩形の形状に戻り、折り返しロールを通過する。特に、折り返しロールと繊維束規制部材の中心間距離が150mm以上となるように、溝付きロールBを配置した実施例6〜8では、トラブルもなく前駆体繊維束の走行位置および断面形状を容易に制御できた。
なお、実施例9では、折り返しロール上での前駆体繊維束の幅が、繊維束規制部材を設置しない時に比較して0.8〜0.9倍程度に収縮した状態で通過する結果となった。実施例9の場合、前駆体繊維束の断面形状が実施例6〜8に比べると若干略矩形に戻りにくくなり、前駆体繊維束の端が厚みをもち、幅の狭まった状態で折り返しロールに到達し、次いで耐炎化炉内に送入された。
従って、前駆体繊維束の断面形状を略矩形により制御しやすくするには、折り返しロールと繊維束規制部材の中心間距離を150mm以上に設定するのが好ましい。
When the fiber bundle regulating member is arranged on the feeding side of the folding roll, the precursor fiber bundle has a shape along the groove when passing through the fiber bundle regulating member, and travel position regulation and shape control of the precursor fiber bundle are performed. Then, after passing through the fiber bundle regulating member, the shape returns to a substantially rectangular shape and passes through the folding roll. In particular, in Examples 6 to 8 in which the grooved roll B is arranged so that the distance between the centers of the folding roll and the fiber bundle regulating member is 150 mm or more, the traveling position and the cross-sectional shape of the precursor fiber bundle are easy without any trouble. I was able to control.
In Example 9, the width of the precursor fiber bundle on the folding roll passes through in a state of being contracted by about 0.8 to 0.9 times compared to when the fiber bundle regulating member is not installed. It was. In the case of Example 9, the cross-sectional shape of the precursor fiber bundle is slightly less likely to return to a substantially rectangular shape as compared with Examples 6 to 8, and the end of the precursor fiber bundle has a thickness and becomes a folded roll in a narrowed state. Then it was fed into a flameproofing furnace.
Therefore, in order to make it easy to control the cross-sectional shape of the precursor fiber bundle with a substantially rectangular shape, it is preferable to set the distance between the centers of the folding roll and the fiber bundle regulating member to 150 mm or more.
[実施例10〜13]
繊維束規制部材として溝付きロールBを用い、溝付きロールBと折り返しロール13との中心間距離が表4に示す値になるように、溝付きロールBを折り返しロール13の送出側に配置した以外は、実施例1と同様にして炭素繊維束を製造した。
前駆体繊維束が溝付きロールBを通過したときの形態を観察し、溝付きロールBを通過する前の平均扁平率、前駆体繊維束の幅1mmに対する見かけの平均繊度、前駆体繊維束にかかる張力を求めた。結果を表4に示す。
[Examples 10 to 13]
A grooved roll B is used as the fiber bundle regulating member, and the grooved roll B is arranged on the delivery side of the
Observe the form when the precursor fiber bundle passed through the grooved roll B, the average flatness before passing through the grooved roll B, the apparent average fineness with respect to the width of 1 mm of the precursor fiber bundle, the precursor fiber bundle Such tension was determined. The results are shown in Table 4.
折り返しロールの送出側に繊維束規制部材を配置する場合、前駆体繊維束が折り返しロールによって拘束されるため、折り返しロールの送入側に繊維束規制部材を配する場合と比較して、中心間距離が長くなるように設定するのが好ましい。特に、折り返しロールと繊維束規制部材の中心間距離が350mm以上となるように、溝付きロールBを配置した実施例10〜12では、トラブルもなく前駆体繊維束の走行位置および断面形状を容易に制御できた。
なお、実施例13では、実施例10〜12に比べると走行位置制御性が若干低下し溝とび(溝乗り越え)が発生した。
従って、前駆体繊維束の走行位置および断面形状をより制御しやすくするには、折り返しロールと繊維束規制部材の中心間距離を350mm以上に設定するのが好ましい。
When the fiber bundle regulating member is arranged on the sending side of the folding roll, the precursor fiber bundle is restrained by the folding roll, so compared with the case where the fiber bundle regulating member is arranged on the feeding side of the folding roll, It is preferable to set the distance to be long. In particular, in Examples 10 to 12 in which the grooved roll B is arranged so that the distance between the centers of the folding roll and the fiber bundle regulating member is 350 mm or more, the travel position and the cross-sectional shape of the precursor fiber bundle are easy without any trouble. I was able to control.
In Example 13, as compared with Examples 10 to 12, the traveling position controllability was slightly lowered, and a groove jump (over the groove) occurred.
Therefore, in order to make it easier to control the traveling position and cross-sectional shape of the precursor fiber bundle, it is preferable to set the distance between the centers of the folding roll and the fiber bundle regulating member to 350 mm or more.
10:炭素繊維束の製造装置、
11:前駆体繊維束、
12:耐炎化炉、
13:折り返しロール、
14:炭素化手段、
15:繊維束規制部材、
151:溝、
155:溝底部、
158:溝開口部。
10: Carbon fiber bundle manufacturing device,
11: precursor fiber bundle,
12: Flame-resistant furnace,
13: Folding roll,
14: Carbonization means,
15: Fiber bundle regulating member,
151: groove,
155: groove bottom,
158: groove opening.
Claims (6)
耐炎化処理されたポリアクリロニトリル系前駆体繊維束を炭素化処理する工程とを有する炭素繊維束の製造方法において、
前記耐炎化炉と折り返しロールとの間に、下記式(1)〜(3)を満足する溝が設けられた繊維束規制部材を配置し、前記耐炎化炉から送出したポリアクリロニトリル系前駆体繊維束を繊維束規制部材に通過させ、
前記繊維束規制部材を通過後のポリアクリロニトリル系前駆体繊維束の幅1mm当たりの見かけの平均繊度を2,500〜5,000dtexに保つ、炭素繊維束の製造方法。
0.5≦b/a≦0.8 ・・・(1)
0.4×a≦h≦0.7×a ・・・(2)
0.45×(a−b)≦R≦0.8×(a−b) ・・・(3)
(式(1)〜(3)中、aは溝開口部の平均幅(mm)であり、bは溝底部の平均幅(mm)であり、hは溝の平均深さ(mm)であり、Rは溝底部の曲率半径(mm)である。) A step of folding the polyacrylonitrile-based precursor fiber bundle having a total fineness of 14,000 to 40,000 dtex on the outside of the flameproofing furnace with a folding roll and running the flameproofing furnace in the flameproofing furnace;
In the method for producing a carbon fiber bundle having a step of carbonizing the flame-resistant polyacrylonitrile-based precursor fiber bundle,
A fiber bundle regulating member provided with a groove satisfying the following formulas (1) to (3) is arranged between the flameproofing furnace and the folding roll, and the polyacrylonitrile-based precursor fiber fed from the flameproofing furnace Let the bundle pass through the fiber bundle regulating member,
A method for producing a carbon fiber bundle, wherein an apparent average fineness per 1 mm width of the polyacrylonitrile-based precursor fiber bundle after passing through the fiber bundle regulating member is maintained at 2,500 to 5,000 dtex.
0.5 ≦ b / a ≦ 0.8 (1)
0.4 × a ≦ h ≦ 0.7 × a (2)
0.45 × (ab) ≦ R ≦ 0.8 × (ab) (3)
(In the formulas (1) to (3), a is the average width (mm) of the groove opening, b is the average width (mm) of the groove bottom, and h is the average depth (mm) of the groove. , R is the radius of curvature (mm) of the groove bottom.)
該耐炎化炉の外側でポリアクリロニトリル系前駆体繊維束を折り返して、耐炎化炉内に走行させる折り返しロールと、
耐炎化処理されたポリアクリロニトリル系前駆体繊維束を炭素化処理する炭素化手段とを具備する炭素繊維束の製造装置において、
前記耐炎化炉と折り返しロールとの間に、下記式(1)〜(3)を満足する溝が設けられた繊維束規制部材が配置された、炭素繊維束の製造装置。
0.5≦b/a≦0.8 ・・・(1)
0.4×a≦h≦0.7×a ・・・(2)
0.45×(a−b)≦R≦0.8×(a−b) ・・・(3)
(式(1)〜(3)中、aは溝開口部の平均幅(mm)であり、bは溝底部の平均幅(mm)であり、hは溝の平均深さ(mm)であり、Rは溝底部の曲率半径(mm)である。) A flameproofing furnace for flameproofing a polyacrylonitrile-based precursor fiber bundle having a total fineness of 14,000 to 40,000 dtex;
A folding roll that folds the polyacrylonitrile-based precursor fiber bundle outside the flameproofing furnace and travels in the flameproofing furnace;
In a carbon fiber bundle production apparatus comprising a carbonization means for carbonizing a polyacrylonitrile-based precursor fiber bundle subjected to flame resistance treatment,
A carbon fiber bundle manufacturing apparatus in which a fiber bundle regulating member provided with a groove satisfying the following formulas (1) to (3) is disposed between the flameproofing furnace and the folding roll.
0.5 ≦ b / a ≦ 0.8 (1)
0.4 × a ≦ h ≦ 0.7 × a (2)
0.45 × (ab) ≦ R ≦ 0.8 × (ab) (3)
(In the formulas (1) to (3), a is the average width (mm) of the groove opening, b is the average width (mm) of the groove bottom, and h is the average depth (mm) of the groove. , R is the radius of curvature (mm) of the groove bottom.)