JP2010269199A - Ball for ball game - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a ball for a ball game in which the fly or rolling distance of the ball after a blow can be largely lengthened and the struck ball feeling of the ball is good. <P>SOLUTION: In the ball for the ball game for park golf or ground golf, which consists of a spherical core, which has a hollow part and an enclosure layer which coats the hollow part, and covers of one or more layers, which coat the spherical core part, and has a diameter of 60 mm, the Shore D hardness of the enclosure layer is 57-61, the Shore D hardness of the outermost layer among the covers is 37-50, and the hardness of the enclosure layer is larger than the cover hardness by 7-24 as the Shore D hardness, an ionomer resin is employed as the resin material of the enclosure layer, and a deformation quantity when loaded with 100 kg burden is 1.49-1.87 mm. In the ball for the ball game, the fly or rolling distance of the ball after the blow can be largely lengthened and the struck ball feeling of the ball is good. <P>COPYRIGHT: (C)2011,JPO&INPIT

Description

  The present invention relates to a ball for ball games, and more particularly to a ball for ball games suitable for park golf and ground golf.

  In recent years, various sports similar to golf competitions have been carried out, and in particular, park golf and grand golf are attracting attention as easy sports exceeding age, gender, experience, and the like. In this park golf and grand golf, a ball having a diameter and mass larger than that of a normal golf ball is used, and the performance of the ball is such that the hit ball goes straight on the ground or flies in the air. It is desired that the reach is large.

  As a ball for park golf or the like, for example, a ball described in JP-A-2002-78829 has been proposed. As shown in FIG. 3, this ball is a ball having a hollow core portion a and a two-layer covering portion composed of an inner layer portion b and an outer layer portion c, and is improved by improving the surface hardness of the ball. It is intended to improve the wear resistance and improve straightness.

  However, although the surface hardness of the above-mentioned balls is adjusted to a Shore D hardness of 50 to 70, the flying distance and the rolling distance after hitting are poor, and there is a drawback that the shot feeling is poor. In particular, the feel at impact is influenced not only by the surface hardness of the ball but also by the hardness distribution inside the ball, and it is desired that not only the flight distance and rolling distance be increased, but also the feel at impact is good.

JP 2002-78829 A

  The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a game ball that not only extends the movement distance of the ball after hitting but also provides a good shot feeling.

  As a result of intensive studies to achieve the above object, the present inventors have found that a spherical core having a hollow portion and an enveloping layer covering the hollow portion, and one or more layers covering the spherical core portion. In a ball game ball for park golf or ground golf having a diameter of 60 mm, the Shore D hardness of the envelope layer is adjusted within a specific range, and the Shore D hardness of the outermost layer of the cover is adjusted. While adjusting the hardness within a specific range, an ionomer resin is used as the resin material of the envelope layer, and by setting the deformation amount at the time of 100 kg load within the specific range, surprisingly a good shot feeling can be obtained. The present inventors have found that the flying distance and rolling distance of a ball after hitting can be greatly increased, and the present invention has been made.

Accordingly, the present invention provides the following ball game balls.
[1] For park golf or ground golf having a diameter of 60 mm, comprising a spherical core having a hollow portion and an enveloping layer covering the hollow portion, and one or more covers covering the spherical core portion In the ball for ball game, the envelope layer has a Shore D hardness of 57 to 61, the outermost layer of the cover has a Shore D hardness of 37 to 50, and the envelope layer has a hardness of Shore D higher than the cover hardness. A ball ball having a hardness of 7 to 24, an ionomer resin is used as a resin material of the envelope layer, and a deformation amount at a load of 100 kg is 1.49 to 1.87 mm.

  According to the ball for ball game of the present invention, the flying distance or rolling distance of the ball after hitting can be greatly increased, and the shot feeling of the ball is good.

(A) is a schematic sectional drawing of the ball game ball concerning the Example of this invention, (B) is a schematic sectional drawing of the ball game ball concerning a reference example. It is sectional drawing of the metal mold | die for shaping | molding of the said ball game balls. It is a schematic sectional drawing of the conventional ball game ball.

  Hereinafter, the present invention will be described in more detail. A ball game ball of the present invention includes a spherical core having a hollow portion and an envelope layer covering the hollow portion, and one or more layers of a cover covering the spherical core portion. Composed. For example, as shown in FIG. 1A, a ball game ball formed in a multi-layer structure including a hollow portion 1a, a spherical core 1 composed of an envelope layer 1b covering the hollow portion 1a, and a single-layer cover 2 is there.

  Further, the ball for ball game of the reference example is composed of a spherical core made of a foam and one or more layers covering the spherical core portion. For example, as shown in FIG. 1B, a ball game ball formed in a two-layer structure of a spherical core 10 made of a foam and a single-layer cover 2.

  In FIG. 1, the cover 2 is formed as a single layer, but the cover can be multi-layered into a two-layer or three-layer structure, if necessary.

  The diameter of the hollow portion 1a in the ball structure of FIG. 1A is adjusted to 31 mm to 45 mm, preferably 32 to 40 mm as usual. If the diameter of the hollow portion 1a is too large, the ball may be damaged when hit.

  The thickness of the envelope layer of the spherical core is recommended to be 7 mm or more, preferably 8 mm or more, and the upper limit is 14 mm or less, preferably 12 mm or less. If the thickness of the envelope layer is too small, the impact durability may be inferior. If the envelope layer is too thick, it may be difficult to adjust the product weight.

The envelope layer has a Shore D hardness of 57-61. If the lower limit is not reached, the rebound of the ball is inferior, and the reach distance at the time of a full shot may be reduced. If the upper limit is exceeded, the hit feeling at the time of putting may be impaired.
The “Shore D hardness” in the present invention is a measured value based on ASTM-D2240.

  On the other hand, in the ball structure of FIG. 1 (B), the Shore D hardness of the foam material is 61. The Shore D hardness of the foamed material in this case is the material hardness when not foamed.

The diameter of the core made of the foam is 44 mm or more, preferably 46 mm or more, and the upper limit is 58 mm or less, preferably 56 mm or less.
The specific gravity of the foam is preferably adjusted to 0.5 to 0.8.

  In the ball structure shown in FIGS. 1A and 1B, the cover is formed softer than the envelope layer or the foam core of the hollow core. Specifically, in the ball structure shown in FIG. The cover has a Shore D hardness of 37 to 50. On the other hand, in the ball structure of FIG. 1 (B), the cover has a Shore D hardness of 37. If the lower limit is not reached, scratch resistance on the ball surface may be deteriorated. In particular, if the envelope layer is too soft, the reach distance may be significantly reduced. In addition, about the Shore D hardness of the cover explained in full detail here, when a cover is formed in multiple layers, it means the Shore D of the outermost layer cover located in the outermost side.

  In the present invention, as described above, the Shore D hardness of the cover is adjusted within a range of 35 to 50. In this case, the cover (the outermost layer in the case of a plurality of layers) constitutes the spherical core. It is preferable to adjust the Shore D hardness to be 6 to 30 softer than the foam material or the envelope layer.

  The thickness of the cover, that is, the thickness of the entire cover is not particularly limited, but is usually 1 mm or more, preferably 2 mm or more, and the upper limit is 30 mm or less, preferably 29 mm or less. In addition, it is recommended that the thickness of the outermost layer of the above cover is 1 mm or more, preferably 2 mm or more, and the upper limit is 8 mm or less, preferably 6 mm or less. If the thickness is too small, the durability may deteriorate, and if the thickness is too large, the productivity may deteriorate.

  The material of the envelope layer 1b covering the hollow portion 1a and the cover 2 covering the spherical core portion is not particularly limited as long as the material satisfies the above-mentioned predetermined Shore D hardness. It is preferable to use the thermoplastic resin described in 1.

That is, as the thermoplastic resin,
(I) Olefin-unsaturated carboxylic acid random copolymer and / or olefin-unsaturated carboxylic acid-unsaturated carboxylic acid ester terpolymer,
(II) a metal ion neutralized product of an olefin-unsaturated carboxylic acid random copolymer and / or a metal ion neutralized product of an olefin-unsaturated carboxylic acid-unsaturated carboxylic acid terpolymer, and (III) It is preferably at least one selected from thermoplastic elastomers.

  Here, the olefin in the components (I) and (II) preferably has a carbon number of usually 2 or more and an upper limit of 8 or less, particularly 6 or less. Specifically, ethylene, propylene, butene, pentene. Hexene, heptene, octene and the like, and ethylene is particularly preferable.

  Moreover, as unsaturated carboxylic acid, acrylic acid, methacrylic acid, maleic acid, fumaric acid etc. can be mentioned, for example, It is especially preferable that they are acrylic acid and methacrylic acid.

  Further, the unsaturated carboxylic acid ester is preferably a lower alkyl ester of the above-mentioned unsaturated carboxylic acid, specifically, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, acrylic acid. Examples thereof include methyl, ethyl acrylate, propyl acrylate, butyl acrylate and the like, and butyl acrylate (n-butyl acrylate, i-butyl acrylate) is particularly preferable.

  The olefin-unsaturated carboxylic acid random copolymer and the olefin-unsaturated carboxylic acid-unsaturated carboxylic acid terpolymer of component (I) can both be obtained according to known methods. However, the content (acid content) of the unsaturated carboxylic acid in the component is usually 2% by mass (synonymous with weight percent, the same shall apply hereinafter) or more, preferably 6% by mass or more. It is recommended that the content be 8% by mass or more, and the upper limit is 25% by mass or less, preferably 20% by mass or less, and more preferably 15% by mass or less. If the acid content is low, the resilience may be reduced, and if it is high, the processability may be reduced.

  Moreover, the metal ion neutralized product of the olefin-unsaturated carboxylic acid-random copolymer of the above component (II) and the metal ion neutralized product of the olefin-unsaturated carboxylic acid-unsaturated carboxylic acid terpolymer Can be obtained by partially neutralizing the acid group in the random copolymer or terpolymer of the component (I) with a metal ion.

Here, examples of metal ions that neutralize acid groups include Na ⁺ , K ⁺ , Li ⁺ , Zn ⁺⁺ , Cu ⁺⁺ , Mg ⁺⁺ , Ca ⁺⁺ , Co ⁺⁺ , Ni ⁺⁺ , and Pb. ^{++, and the} like, preferably Na ⁺ , Li ⁺ , Zn ⁺⁺ , Mg ^{++ and the} like are preferably used. The degree of neutralization of the random copolymer or ternary copolymer of these metal ions is It is not particularly limited.

  Further, the neutralization method is not particularly limited, and compounds such as the above-mentioned metal ion formate, acetate, nitrate, carbonate, bicarbonate, oxide, hydroxide and alkoxide are used as component (I). A method of introducing an olefin-unsaturated carboxylic acid random copolymer and an olefin-unsaturated carboxylic acid-unsaturated carboxylic acid ester terpolymer and neutralizing acid groups with the metal ions can be employed.

  Commercially available products can be suitably used as the components (I) and (II), and olefin-unsaturated carboxylic acid random copolymer, olefin-unsaturated carboxylic acid-unsaturated carboxylic acid ester ternary copolymer. Examples of the coalescence include Nucleel AN4311, AN4318, and 1560 (all manufactured by Mitsui-DuPont Polychemical Co., Ltd.), metal ion neutralized olefin-unsaturated carboxylic acid random copolymer, and olefin-unsaturated carboxylic acid. Examples of the metal ion neutralized product of the acid-unsaturated carboxylic acid ester terpolymer are commercially available as ionomer resins, such as Himilan 1554, 1557, 1601, 1605, 1706, 1855, 1856, AM7316, AD8512, 1652, 1653 (all are Mitsui Dupo Polychemical Co., Ltd.), Surlyn 6320, 7930, 8120, 8945, 9945 (all manufactured by DuPont of the United States), etc., especially Nuclerel AN4318, 1560, High Milan 1706, 1605 are preferably used. be able to.

  The above (III) thermoplastic elastomer is recommended to be a neutral to basic thermoplastic elastomer having no acid group. For example, polyolefin, olefin elastomer, urethane elastomer, polyester elastomer, styrene elastomer And polyamide-based elastomers.

  Other than the above (I) to (III), polyethylene resins such as polypropylene, polyethylene, and ethylene-vinyl acetate copolymer may be used, and one of these may be used alone or in combination of two or more. Can be used. These resins can be used by mixing with the components (I) to (III) described above.

  In addition, an inorganic filler such as titanium dioxide or barium sulfate can be added to the material of the envelope layer and the cover. In addition, various layers such as dyes and pigments can be added to finish each layer in color, or a transparent cover layer can be formed.

  As for the material of the foamed core in the ball structure of FIG. 1B, it is preferable to use a thermoplastic resin having a Shore D hardness of 55 to 70, specifically, the above-described thermoplastic resin is exemplified. can do. Then, an appropriate amount of a chemical foaming agent is blended with the above thermoplastic resin to produce a foam core having a specific gravity of 0.5 to 0.9. As the chemical foaming agent, for example, azodicarbonamide, dinitrosopentamethylenetetramine, p, p′-oxybisbenzenesulfonyl hydrazide and the like can be used. As a commercial product, “Unihome AZ series” manufactured by Otsuka Chemical Co., Ltd. And “Unifine P series” (both are mainly composed of azodicarbonamide).

  The deformation amount of the game ball of the present invention when loaded with 100 kg is 1.45 mm or more, and the upper limit is 1.87 mm or less. If the amount of deformation is too small, the feel at the time of putting may be impaired. If the amount of deformation is too large, the reach during full shot may be reduced.

  For the production of the ball game ball of the present invention, an injection molding method can be adopted. For example, the spherical core 1 in which the hollow portion 1a is covered with the envelope layer 1b is prepared in advance, and as shown in FIG. A method in which a sphere is arranged in the mold 5 and the cover material 2 is introduced into the cavity 5a while the sphere 1 is supported by the support pins 6 and the cover is injection-molded is preferably employed.

  The ball game ball of the present invention is a ground golf ball or a park golf ball having a diameter of 50 to 70 mm and a ball game ball similar to these games. The diameter and mass of the ball match the rules of various games. The design can be changed as appropriate. For example, in the case of a golf ball for a park golf, the official ball game can have a diameter of 6 cm and a weight of 80 to 95 g in accordance with the rules of the International Park Golf Association.

  EXAMPLES Hereinafter, although an Example and a comparative example are shown and this invention is demonstrated concretely, this invention is not restrict | limited to the following Example.

[Examples 1 to 3, Reference Example I and Comparative Examples 1 to 4]
In Examples 1 to 3 and Comparative Examples 1 to 3, a pair of hemispheres (half cups) are produced by injection molding, and the hemispheres are fitted together to form a hollow core portion having a predetermined diameter with an envelope layer. An enclosed spherical core was obtained. Moreover, in Reference Example I and Comparative Example 4, 2 parts by mass of a foaming agent (“AZH-115E” manufactured by Otsuka Chemical Co., Ltd.) is blended with 100 parts by mass of the core material shown in the following table, and has a spherical cavity with a diameter of 52 mm. A foam core having a specific gravity of 0.76 was obtained by injection molding into a mold.

  Next, this spherical core was introduced into the upper and lower divided molds shown in FIG. 2, and various cover materials were injection-molded to produce park golf balls of examples and comparative examples.

About each obtained park golf ball, the flying performance and the hit feeling were evaluated by the following method. The results are also shown in Table 1 below.

The final arrival point of the ball was measured when hitting at a head speed (HS) of 28 m / s with a flying robot (manufactured by Miyamae). The club used was “Grand Persimmon SS-350P” manufactured by Bridgestone Sports.

10 hitting feeling testers evaluated the hitting feeling when the ball of each example was put-shot with a park golf club.
4 to 5 out of 10 people who feel that 6-7 out of 10 judges that the hit feeling is good when 8 or more out of 10 judges that the hit feeling is good. △ if it is determined to be good △ 3 or less out of 10 people who feel that the hit feeling is good is ×

DESCRIPTION OF SYMBOLS 1 Spherical core 1a Hollow part 1b Enveloping layer 10 Foam core 2 Cover

Claims (1)

  A ball game ball for park golf or ground golf having a diameter of 60 mm, comprising a spherical core having a hollow portion and an envelope layer covering the hollow portion, and one or more covers covering the spherical core portion. The outer layer has a Shore D hardness of 57 to 61, and the outermost layer has a Shore D hardness of 37 to 50, and the envelope layer has a Shore D hardness of 7 with a Shore D hardness higher than the cover hardness. A ball game ball characterized in that it is hard and has an ionomer resin as a resin material of the envelope layer, and has a deformation amount of 1.49 to 1.87 mm when loaded with 100 kg.