JP2010130906A - Pellet made from rice straw, method for producing the same, and livestock feed - Google Patents

Pellet made from rice straw, method for producing the same, and livestock feed Download PDF

Info

Publication number
JP2010130906A
JP2010130906A JP2008307070A JP2008307070A JP2010130906A JP 2010130906 A JP2010130906 A JP 2010130906A JP 2008307070 A JP2008307070 A JP 2008307070A JP 2008307070 A JP2008307070 A JP 2008307070A JP 2010130906 A JP2010130906 A JP 2010130906A
Authority
JP
Japan
Prior art keywords
rice straw
pellet
pellets
rice straws
straw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2008307070A
Other languages
Japanese (ja)
Inventor
Hiroto Sato
博人 佐藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to JP2008307070A priority Critical patent/JP2010130906A/en
Publication of JP2010130906A publication Critical patent/JP2010130906A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a pellet made from rice straws enabling utilization of the rice straws as a bio-mass resource, to provide a method for producing the pellet, and to provide livestock feed. <P>SOLUTION: The pellet made from rice straws is produced by cutting rice straws into a prescribed length, adding water to the rice straws each with a prescribed length to make them moist, applying prescribed pressure on the moist rice straws to push them out of a dice so as to be molded. Such a molded pellet enables reduction in emission of carbon dioxide when transported, and securement of a storage place. The hardness of the pellet is adjustable owing to the moisture of the rice straws and the pressure in compression mold, so that the pellet is produced according to the utilization purpose (application) of the rice straws. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、稲わらからなるペレット及びその製造方法並びに家畜飼料に関する。   The present invention relates to a pellet made of rice straw, a method for producing the pellet, and livestock feed.

近年、二酸化炭素の排出による地球温暖化が問題となっている。そのため、大気中の二酸化炭素の増減に影響を与えない燃料、すなわちカーボンニュートラルなエネルギー源が開発されている。例えば、植物の光合成により吸収される二酸化炭素の量とその植物の焼却により排出される二酸化炭素の量が相殺される。植物をエネルギー源とすれば、大気中の二酸化炭素の増減に影響を与えない。このような概念をカーボンニュートラルと呼んでいる。   In recent years, global warming due to carbon dioxide emissions has become a problem. Therefore, a fuel that does not affect the increase or decrease of carbon dioxide in the atmosphere, that is, a carbon neutral energy source has been developed. For example, the amount of carbon dioxide absorbed by the photosynthesis of the plant and the amount of carbon dioxide emitted by the incineration of the plant are offset. If plants are used as energy sources, they will not affect the increase or decrease of carbon dioxide in the atmosphere. This concept is called carbon neutral.

しかし、植物をエネルギー源として利用する場合、植物を産出場所から燃料製造場所や利用場所まで輸送する必要がある。輸送の際は、化石燃料を使用することになり二酸化炭素の排出量が生じてしまうという問題がある。また、輸送された植物又は燃料を保管する場所の確保が問題となる場合もあった。   However, when a plant is used as an energy source, it is necessary to transport the plant from the production site to the fuel production site or use site. When transporting, fossil fuel is used, and there is a problem that carbon dioxide emissions occur. In addition, securing a place to store the transported plant or fuel may be a problem.

上記問題を解決する手段として、エネルギー源をペレット化して輸送・保管することが考えられている。これにより、輸送量を拡大でき、保管場所も縮小できる。例えば、木材や籾殻などをペレット化する技術が提供されている（例えば、特許文献１）。木材を使用するペレットは、製材により産出するおが粉などを原料とする木質ペレットであり、直径数ｍｍの穴（ダイ孔）から押し出しその圧力によってペレット状に成型し固めた固形燃料である。木質バイオマスペレットとも称されている。
特開２００５−２３０５号公報 As means for solving the above problems, it is considered to pelletize the energy source for transportation and storage. As a result, the transportation amount can be increased and the storage location can be reduced. For example, a technique for pelletizing wood or rice husk is provided (for example, Patent Document 1). Wood pellets are wood pellets made from sawdust or the like produced by lumbering, and are solid fuel that is extruded from a hole (die hole) with a diameter of several millimeters and molded into a pellet shape by the pressure. It is also called woody biomass pellet.
JP 2005-2305 A

バイオマス（再利用可能な有機性資源）として利用する開発が求められているものの一つに、現在未利用の稲わらがある。稲わらは、バイオマスとして、燃料、堆肥（土壌改良剤）、バイオエタノール、飼料の原料としての利用が検討されている。しかしながら、現在、稲わらのペレット化が実現されていないことから上述の輸送時の二酸化炭素の排出、保管場所の確保という問題があり、稲わらのほとんどは利用されていない。そのため、稲わらは、わら焼き（焼却処分）されることが多く、付近住民の健康を害するという問題も発生している。   One of the things that need to be developed as biomass (a reusable organic resource) is currently unused rice straw. Rice straw is being studied for use as a raw material for fuel, compost (soil conditioner), bioethanol, and feed as biomass. However, since rice straw pelletization has not been realized at present, there are problems such as the above-mentioned emission of carbon dioxide during transportation and securing of a storage place, and most of the rice straw is not used. For this reason, rice straw is often baked (incinerated), resulting in the problem of harming the health of nearby residents.

稲わらのペレットを、木質ペレットの製造方法すなわち木質ペレット製造機を用いて押し出し成型でペレット化することが考えられる。木質ペレットは、原料の間伐材・廃木材等を粉砕しおが粉を製造する工程（粉砕工程）、おが粉を乾燥する工程（乾燥工程）、乾燥したおが粉を木質ペレット製造機（ペレタイザー）のダイ孔から押し出しその圧力によってペレット状に成型し固める工程（成型工程）、成型されたペレットを空気で冷却する工程（冷却工程）の工程順によって製造することができる。
しかし、上記木質ペレットの製造工程では、稲わらをペレット状に成型することができなかった。 It is considered that rice straw pellets are pelletized by extrusion molding using a wood pellet manufacturing method, that is, a wood pellet manufacturing machine. Wood pellets are made from raw thinned wood, waste wood, etc. to produce sawdust (pulverization process), sawdust drying process (drying process), dried sawdust into wood pellet making machine ( It can be manufactured in the order of the process of extruding from a die hole of a pelletizer) and molding and solidifying it into a pellet by the pressure (molding process) and cooling the molded pellet with air (cooling process).
However, rice straw could not be formed into pellets in the wood pellet manufacturing process.

また、稲わらは、従来から牛や豚などの家畜飼料として利用されていたが、当該飼料を家畜が好んで食べるよう飼料の嗜好性を高める必要があった。そこで、畜産農家では、従来稲わらにジュース用リンゴの搾り粕（本願において「リンゴ粕」という。）を混ぜて飼料として与えていた。リンゴ粕は産業廃棄物として有料で廃棄処分されているものであるため、家畜飼料としての有効利用が期待されていた。
しかし、リンゴ粕は運搬中に当該粕に大量に含まれる水分（リンゴジュース）と搾り粕（繊維質）に分離してしまうことから、リンゴジュースの含有量が少ないリンゴ粕が飼料として使用されていた。リンゴ粕は飼料の嗜好性を高める効果が高いものであったものの、リンゴ粕は家畜飼料として有効に利用されていなかった。 In addition, rice straw has been conventionally used as livestock feed for cattle, pigs and the like, but it has been necessary to increase the palatability of the feed so that the livestock prefers this feed. Therefore, livestock farmers have conventionally mixed rice straw with apple squeezed straw for juice (referred to as “apple candy” in the present application) as feed. Since apple cake is disposed of as industrial waste for a fee, it has been expected to be effectively used as livestock feed.
However, apple cocoons are separated into water (apple juice) and squeezed potatoes (fiber) contained in a large amount during transportation, so apple candy with a low content of apple juice is used as feed. It was. Although apple candy has a high effect of enhancing the palatability of feed, apple candy has not been effectively used as livestock feed.

本発明は、上記問題を解決するために、稲わらをバイオマス資源として利用可能にする稲わらからなるペレット及びその製造方法並びに家畜飼料を提供することを目的とするものである。   In order to solve the above problems, an object of the present invention is to provide a pellet made of rice straw that makes rice straw available as a biomass resource, a method for producing the pellet, and livestock feed.

本願発明者は、上記目的を実現するために種々の検討を行った結果、稲わらを湿潤させて押し出し成型することにより稲わらをペレット化でき、また、稲わらの水分及び成型時の圧力を調整することにより、バイオマス利用の目的・用途に応じたべレットを成型できることを見出し、本願発明を完成するに至った。   The inventor of the present application has made various studies in order to achieve the above object, and as a result, the rice straw can be pelletized by wetting the rice straw and extruding it. By adjusting, it discovered that the pellet according to the objective and the use of biomass utilization could be shape | molded, and came to complete this invention.

すなわち、本発明の稲わらからなるペレットは、切断した稲わらと、前記稲わらに予め加水し湿潤させる水とを原料とし、前記湿潤させた稲わらに圧力を加えてダイスから押し出すことにより成型するペレットであって、稲わらの用途に応じて加水する水量および加圧する圧力を調整するようにしたものである。   That is, the pellets made of the rice straw of the present invention are formed by using the cut rice straw and water that is pre-hydrated and wetted with the rice straw, and extruding the wet rice straw from a die by applying pressure. The amount of water to be added and the pressure to be pressurized are adjusted according to the purpose of rice straw.

本発明の稲わらからなるペレットの製造方法は、稲わらを所定の長さに切断し、前記所定の長さの稲わらに水を加水し湿潤させ、前記湿潤させた稲わらに所定の圧力を加えてダイスから押し出すことによりペレットを成型するようにしたものである。   The method for producing a pellet made of rice straw according to the present invention includes cutting rice straw into a predetermined length, adding water to the rice straw of the predetermined length to wet it, and applying a predetermined pressure to the wet rice straw. And pellets are formed by extruding from a die.

また、本発明の家畜飼料は、上記の稲わらからなるペレットとリンゴ粕とを混合したものである。   Moreover, the livestock feed of this invention mixes the pellet which consists of said rice straw, and apple straw.

本発明は、稲わらとその稲わらを湿潤させる水を原料とする稲わらからなるペレットである。稲わらの水分、押し出し時の圧力を調整することにより、利用目的に合う稲わら１００％のバイオマスペレットを創出することができる。   The present invention is a pellet made of rice straw and rice straw made from water that wets the rice straw. By adjusting the moisture of rice straw and the pressure at the time of extrusion, biomass pellets of 100% rice straw suitable for the purpose of use can be created.

本発明は、水を加水し湿潤させた稲わらを圧縮成型するものである。これにより、既知のペレット製造機を用いて稲わらをペレットに成型することができる。   The present invention compresses and molds rice straw that has been wetted with water. Thereby, a rice straw can be shape | molded into a pellet using a known pellet manufacturing machine.

さらには、ペレット化した稲わらとリンゴ粕とを混合した家畜飼料は、リンゴジュースの成分を多量に含むものであり、嗜好性が高い飼料となる。   Furthermore, livestock feed in which pelletized rice straw and apple straw are mixed contains a large amount of the components of apple juice, and is highly feedable.

以上のように、本発明によると、稲わらをバイオマスとして利用することが可能となることから、わら焼きを防止でき、付近住民の健康を害するという問題を解消することができる。また、稲わらをペレット化することにより輸送時の二酸化炭素の排出・保管場所の確保という問題も解消できる。さらには、産業廃棄物として廃棄処分されていたリンゴ粕を家畜飼料として有効に利用することが可能となる。   As described above, according to the present invention, since rice straw can be used as biomass, straw burning can be prevented and the problems of harming the health of nearby residents can be solved. In addition, the problem of carbon dioxide emission and storage space during transportation can be solved by pelletizing rice straw. Furthermore, apple straw that has been disposed of as industrial waste can be effectively used as livestock feed.

本発明は、稲わらをバイオマスとして利用することを実現するものである。   This invention implement | achieves utilizing rice straw as biomass.

本発明の稲わらからなるペレットの製造方法は、切断した稲わらと、前記稲わらに予め加水し湿潤させる水とを原料とし、前記湿潤させた稲わらに圧力を加えてダイ孔から押し出すことにより成型するペレットである。ペレットは、既知の木質ペレット製造機（ペレタイザー）を用いた押し出し成型により形成する。   The method for producing a pellet made of rice straw according to the present invention uses a cut rice straw and water that is pre-hydrated and wetted with the rice straw as raw materials, and applies pressure to the wet rice straw and pushes it out from a die hole. It is a pellet to be molded. The pellets are formed by extrusion using a known wood pellet making machine (pelletizer).

木質ペレットは、一般に以下の（１）〜（４）工程によって製造されている。
（１）粉砕工程
原料の間伐材・廃木材等の木材を粉砕機に投入し粉砕しておが粉（微粒子の粉末）を製造する。なお、製造されたおが粉は、多くの水分を含み燃え難い状態にある。
（２）乾燥工程
おが粉をロータリードラム乾燥機（高温の温風を吹き出すチェンバー）で乾燥させ、含水率およそ６％〜１０％程度まで乾燥させる。
（３）成型工程
乾燥されたおが粉は、木質ペレット製造機（ペレタイザー）で圧縮成型されペレットに成型される。圧縮成型の際、通常接着材等の添加物を使用しない。ペレット化時に木材のリグニンが軟化し（又は溶け出し）、接着剤の役割を果たす。
成型されるペレットは、木質ペレット製造機の仕様によってその大きさは異なるが、直径６ｍｍ程度、長さ１０〜２０ｍｍの円柱状（粒状）の固形燃料である。
（４）冷却工程
リグニンを硬化させるため、成型されたペレットを空気で冷却する。
（５）その他の工程（選別、袋詰め、貯蔵）
成型されたペレットは、袋詰めされ貯蔵される。一方、ペレット化しないおが粉は、上記（２）の乾燥工程に戻る。
上記（１）〜（４）工程により稲作で育成された稲わらのペレット化を試みた。しかし、ペレットを成型することはできなかった。稲わらを微粒子に粉砕するとペレット形状に成型されず、また、稲わらが長すぎるとダイ孔に詰まってしまい押し出し成型できないという問題が起こった。 Wood pellets are generally manufactured by the following steps (1) to (4).
(1) Grinding process Raw materials such as thinned wood and waste wood are put into a grinder and pulverized to produce sawdust (fine particle powder). In addition, the manufactured sawdust contains a lot of moisture and is in a state where it is difficult to burn.
(2) Drying process Sawdust is dried by a rotary drum dryer (chamber that blows out hot air at high temperature) and dried to a moisture content of about 6% to about 10%.
(3) Molding process The dried sawdust is compression molded by a wood pellet making machine (pelletizer) and molded into pellets. During compression molding, additives such as adhesives are usually not used. The wood lignin softens (or dissolves) during pelletization, and acts as an adhesive.
Although the size of the pellets to be molded varies depending on the specifications of the wood pellet manufacturing machine, it is a cylindrical (granular) solid fuel having a diameter of about 6 mm and a length of 10 to 20 mm.
(4) Cooling step In order to cure the lignin, the molded pellets are cooled with air.
(5) Other processes (sorting, bagging, storage)
The molded pellets are packaged and stored. On the other hand, the sawdust that is not pelletized returns to the drying step (2).
Attempts were made to pelletize rice straw grown in rice cultivation through the above steps (1) to (4). However, pellets could not be molded. When rice straw was pulverized into fine particles, it was not molded into a pellet shape, and when the rice straw was too long, the die holes were clogged and extrusion molding was not possible.

上記問題を解決するため、本願発明者は、種々の試験を行った結果、以下の（ａ）〜（ｃ）工程により稲わらをペレット化することができた。
（ａ）切断工程
稲わらを所定の長さに切断する。例えば、ダイ孔の直径が６ｍｍの場合は、２５ｍｍ以下とするのが好ましい。
（ｂ）湿潤工程
切断した稲わらに水を散布して加水し所定の水分を含ませ湿潤する。このときの水分は１２％〜２０％が好ましい。
（ｃ）成型・冷却工程、
木質ペレットと同様、湿潤された稲わらは、木質ペレット製造機（ペレタイザー）を用いて所定の圧力により圧縮成型することにより、ペレットを成型することができる。また、リグニンを硬化させるため、成型されたペレットを空気で冷却する。 In order to solve the above problem, the present inventor has been able to pellet rice straw by the following steps (a) to (c) as a result of various tests.
(A) Cutting process Rice straw is cut into a predetermined length. For example, when the diameter of the die hole is 6 mm, the diameter is preferably 25 mm or less.
(B) Wetting process Water is sprayed on the cut rice straw to add water and moisten it. The moisture at this time is preferably 12% to 20%.
(C) molding / cooling process,
Like wood pellets, wet rice straw can be molded by compression molding at a predetermined pressure using a wood pellet making machine (pelletizer). Moreover, in order to harden lignin, the shape | molded pellet is cooled with air.

上記（ａ）〜（ｃ）工程では、湿潤させた稲わらの水分と圧縮成型時の圧力によってペレットの硬度が異なるが、貯蔵が可能なペレットを製造することができた。これにより、稲わらの保管・貯蔵が容易となる。また、稲わらの加工プラントへの輸送・貯蔵コストを軽減することができる。例えば、１ｍ３当たりの稲わらの収納量６０ｋｇをペレット化することにより８１０ｋｇとすることができ、１ｍ３当たり約１３倍〜１４倍の稲わらを収納することが可能となる。これにより、輸送・保管コストを大幅に軽減することができる。 In the steps (a) to (c), pellets that can be stored could be produced, although the hardness of the pellets differed depending on the moisture of the wet rice straw and the pressure during compression molding. This facilitates storage and storage of rice straw. In addition, transportation and storage costs for rice straw processing plants can be reduced. For example, by pelletizing 60 kg of rice straw per 1 m 3 , it can be made 810 kg, and 13 to 14 times of rice straw per 1 m 3 can be stored. Thereby, transportation and storage costs can be greatly reduced.

本発明の稲わらからなるペレットは、切断した稲わらと、前記稲わらに予め加水し湿潤させる水とを原料とし、前記湿潤させた稲わらに圧力を加えてダイスから押し出すことにより成型するペレットであって、稲わらの用途に応じて加水する水量および加圧する圧力を調整したものである。
稲わらからなるペレット（以下、単に「稲わらペレット」という。）は、稲わら以外の添加物は含有されていないこと、稲わらの水分と圧縮成型時の圧力によってペレットの硬度を調整できることから、稲わらの利用目的（用途）に応じたペレットを提供することができる。例えば、以下の１）〜５）の用途に利用することが可能となる。
１）固形燃料
稲わらの水分量を少なくし、押し出し成型時の圧力を高くすると、固形燃料に適した硬度を有する稲わらペレットを得ることができる。この稲わらペレットは化石燃料の代替品として利用でき、ボイラーの燃料として利用できる。また、二酸化炭素排出量の軽減を図ることができる。
同じ大きさの粒（ペレット）のパークペレット、稲わらペレットを用いてボイラーでの燃焼テストを行った結果、パークペレットの着火までの所要時間は６〜８秒であったのに対し、稲わらペレットは８〜１０秒を要した。しかし、稲わらペレットはパークペレットに比べ火持ちが良かった。火持ちがよい稲わらペレットは、ハウス栽培の安価な燃料として最適であった。
なお、パークペレットと稲わらペレットとの所要時間の相違は、ペレットに含まれる水分量の相違に起因するものと考えられる。
２）家畜飼料
稲わらペレットの比重（嵩比重）が他の飼料と同等にできることから、粗飼料と混ぜて家畜に与えることができる。また、現在使用されている粗飼料（とうもろこし、小麦、ふすま等）に替えて、稲わらペレットを使用することにより、配合飼料の価格を下げることができる。よって、本発明の稲わらペレットは、今後の畜産農家、飼料製造業界の発展に寄与するものと考えられる。
さらに、稲わらペレットとリンゴ粕とを混合させることにより、リンゴ粕に含まれるリンゴジュース又はリンゴ粕から分離したリンゴジュースを稲わらペレットに吸収させることができる。また、リンゴジュースを吸収した稲わらペレットからなる家畜飼料は、稲わらの発酵により家畜飼料の嗜好性が高められ、家畜の食欲を増進させることができる家畜に適した飼料となる。なお、稲わらペレットとリンゴ粕との混合比（質量比）は、稲わらペレットが１０質量％で、リンゴ粕が９０質量％であることが好ましいが、この質量比に限定されるものではない。
３）動物（ペット、家畜を含む）用床材・敷材
動物の敷材として利用できる。これにより、飼育環境を衛生に保つことができ、農場畜舎における労力の軽減が図れる。
４）バイオエタノールの採取
稲わらからバイオエタノールを採取する場合、エタノール搾取工程における作業時間を短縮することが可能となる。
５）農業用土壌改良剤
畜糞を含む稲わら（敷材）やバイオエタノール採取後の残渣を堆肥（土壌改良剤）に加工し、農業用土壌改良剤として利用することができる。
また、ハウス栽培の燃料として利用された稲わらペレットの灰を農業用土壌改良剤や融雪剤として利用することができる。 The pellet made of the rice straw of the present invention is a pellet formed by using a cut rice straw and water that is pre-hydrated and wetted with the rice straw, and applying pressure to the wet rice straw and extruding it from a die. However, the amount of water to be added and the pressure to be pressurized are adjusted according to the use of rice straw.
Pellets made of rice straw (hereinafter simply referred to as “rice straw pellets”) contain no additives other than rice straw, and the hardness of the pellets can be adjusted by the moisture of rice straw and the pressure during compression molding. It is possible to provide pellets according to the purpose (use) of rice straw. For example, it can be used for the following uses 1) to 5).
1) Solid fuel Rice straw pellets having hardness suitable for solid fuel can be obtained by reducing the moisture content of rice straw and increasing the pressure during extrusion molding. The rice straw pellets can be used as a substitute for fossil fuels and as boiler fuel. In addition, it is possible to reduce carbon dioxide emissions.
As a result of a combustion test in a boiler using park pellets and rice straw pellets of the same size (pellet), the time required to ignite the park pellets was 6-8 seconds, whereas rice straw The pellet took 8-10 seconds. However, rice straw pellets lasted longer than park pellets. Rice straw pellets with good fire resistance were optimal as inexpensive fuels for house cultivation.
In addition, it is thought that the difference in the required time of a park pellet and a rice straw pellet originates in the difference in the moisture content contained in a pellet.
2) Livestock feed Since the specific gravity (bulk specific gravity) of rice straw pellets can be equal to other feeds, it can be mixed with roughage and given to livestock. In addition, the price of the mixed feed can be reduced by using rice straw pellets instead of the currently used roughage (corn, wheat, bran, etc.). Therefore, the rice straw pellet of the present invention is considered to contribute to the future development of livestock farmers and the feed manufacturing industry.
Furthermore, by mixing rice straw pellets and apple straw, apple juice contained in apple straw or apple juice separated from apple straw can be absorbed into the rice straw pellets. Moreover, the livestock feed which consists of the rice straw pellet which absorbed apple juice becomes the feed suitable for the livestock which can raise the appetite of a livestock feed and can raise the appetite of livestock by fermentation of rice straw. The mixing ratio (mass ratio) of rice straw pellets and apple straw is preferably 10% by weight for rice straw pellets and 90% by weight for apple straw, but is not limited to this weight ratio. .
3) Floor materials and covering materials for animals (including pets and livestock) Can be used as animal covering materials. Thereby, the breeding environment can be kept hygienic, and the labor in the farm barn can be reduced.
4) Collection of bioethanol When collecting bioethanol from rice straw, it is possible to shorten the working time in the ethanol extraction process.
5) Agricultural soil conditioner The rice straw (laying material) containing livestock dung and the residue after collecting bioethanol can be processed into compost (soil conditioner) and used as an agricultural soil conditioner.
Moreover, the ash of rice straw pellets used as fuel for house cultivation can be used as an agricultural soil conditioner or snow melting agent.

以上のように、本発明によると、稲わらをバイオマスとして、燃料、堆肥（土壌改良剤）、バイオエタノール、飼料としての利用できるため、従来のわら焼き（焼却処分）による付近住民の健康を害するという問題も解消される。
また、ペレット化を可能とすることにより、輸送時の二酸化炭素の排出の軽減、保管場所の確保が可能となる。
さらには、産業廃棄物として廃棄処分されていたリンゴ粕を家畜飼料として有効に利用することが可能となる。 As described above, according to the present invention, rice straw can be used as biomass, fuel, compost (soil conditioner), bioethanol, and feed, and thus harms the health of nearby residents by conventional straw burning (incineration disposal). The problem is solved.
In addition, by making pelletization possible, it is possible to reduce carbon dioxide emission during transportation and secure a storage location.
Furthermore, apple straw that has been disposed of as industrial waste can be effectively used as livestock feed.

Claims (3)

切断した稲わらと、前記稲わらに予め加水し湿潤させる水とを原料とし、前記湿潤させた稲わらに圧力を加えてダイスから押し出すことにより成型するペレットであって、稲わらの用途に応じて加水する水量および加圧する圧力を調整することを特徴とする稲わらからなるペレット。 Pellets formed by cutting rice straw and water that is pre-hydrated and wetted with the rice straw and pressing the wet rice straw by pressing it from a die, depending on the use of the rice straw A pellet made of rice straw characterized by adjusting the amount of water to be added and the pressure to be pressurized. 稲わらを所定の長さに切断し、前記所定の長さの稲わらに水を加水し湿潤させ、前記湿潤させた稲わらに所定の圧力を加えてダイ孔から押し出すことによりペレットを成型することを特徴とする稲わらからなるペレットの製造方法。 The rice straw is cut into a predetermined length, water is added to the rice straw of the predetermined length to wet it, and a predetermined pressure is applied to the wet rice straw to extrude it from the die hole to form a pellet A method for producing pellets made of rice straw. 請求項１又は請求項２記載の稲わらからなるペレットとリンゴ粕とを混合したことを特徴とする家畜飼料。
A livestock feed comprising a mixture of the rice straw pellets according to claim 1 and apple straw.
JP2008307070A 2008-12-02 2008-12-02 Pellet made from rice straw, method for producing the same, and livestock feed Pending JP2010130906A (en)