JP2010125657A - Foam molding mold and method for molding different hardness pad using the same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a foam molding mold capable of pouring a raw material only in a region having a part of a lower mold partitioned when pouring a polyurethane raw material in the region in order to mold a different hardness part of the outside of a side support in a different hardness pad of a vehicular seat. <P>SOLUTION: A first notch 4 is formed at a part of a cavity surface of a second region 12b for forming the outside part of the side support part, and a recessed part 16 for pouring which communicates with the first notch 4 is formed at outside the cavity surface. Furthermore, the height of a bottom surface 17 at the first notch 4 is made to be lower than the height of a partition wall 14. Meanwhile, a first projection where a part of a parting surface closed by a lower mold 2 is projected is formed on an upper mold, and when the upper mold is closed with respect to the lower mold 2, the first notch 4 is closed by the first projection. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

  The present invention relates to a foam molding die for polyurethane foam and a method for molding a different hardness pad using the same.

  As seat cushions and seat backs for automobile seats, a polyurethane foam obtained by injecting a polyurethane raw material into a foaming mold and foam-molding is reinforced with a frame and covered with a skin material is generally used. In recent years, automobile seats have been designed so that the thighs are not subjected to loads during driving operations, the posture of the passengers is maintained against the lateral acceleration experienced during driving, and fatigue is caused by prolonged driving. In order to prevent the accumulation of heat, a different hardness pad having a partially different hardness is employed. In particular, in order to keep the occupant's posture against lateral acceleration during running, only the hardness of the outer side part of the side support part is increased, and the hardness of the inner side of the main support part and side support part is relatively lowered Is being used. One of the methods for forming the different hardness pad is a method in which polyurethane raw materials having different components are injected into different regions of the cavity of the lower mold of the foam molding die to perform integral foam molding.

  In the lower mold of the foam molding die, the wall surface of the cavity for molding the outer portion of the side support portion is in an overhanging state upward, and the upper end edge is disposed on the inner side of the lower wall surface. Yes. In general, the shape of the region partitioned for molding of the outer side portion of the side support portion is a narrow and narrow shape. Moreover, in order to efficiently mold a plurality of pads having different shapes and sizes, it is common to use a production line in which a plurality of types of foaming molds circulate. In the production line, the injection of the polyurethane raw material is performed by one injection head that can be applied to all the foaming molds. In this injection head, the discharge pressure is set within a predetermined range and the discharge amount can be adjusted within the predetermined range. For example, it is difficult to discharge an extremely small amount at a low pressure.

  Therefore, in the above production line, it is difficult to inject the polyurethane raw material only into the elongated region of the lower mold, and it is necessary to inject the raw material across the region for molding the inner part of the side support part and the main support part. You will not get. Therefore, at the boundary between the inner part of the main support part and the side support part and the outer part of the side support part, a part with high hardness is formed on the main support part side, and the problem that makes the user of the different hardness pad feel uncomfortable was there.

  In order to solve such a problem, the present applicant has already proposed a “foaming mold and a sheet pad to be molded from this” disclosed in Patent Document 1. In the lower mold of the foam molding die, a partition wall portion that divides a cavity surface for molding the side support portion into an inner side and an outer side is provided on the bottom surface. Then, an inclined wall portion in which a part of the partition wall portion is inclined inward is provided, and an opening formed by the inclined wall portion is set as an injection point wider than the injection port of the injection nozzle. By injecting the polyurethane raw material into the injection point, the raw material does not reach the inside of the partition wall.

Further, in the “foaming mold and sheet pad manufacturing method” disclosed in Patent Document 2, the foaming mold has an inlet formed on the mating surface of the lower mold and the upper mold, and the inlet is used for a sheet. An opening is formed facing the edge forming portion for forming the edge portion (side support portion) of the pad. Further, the guide surface of the injection port is inclined toward the cavity, so that the polyurethane raw material injected into the guide surface flows down to the edge molding portion.
JP 2001-38747 A (see [Summary]) JP 2008-68582 A (see [Summary])

  In the foam mold disclosed in Patent Document 1, an injection point is provided, and it is possible to inject a polyurethane raw material into a predetermined portion of the lower mold. In the pad for a sheet, a part with different hardness is formed in a part of the inside of the boundary part with different hardness on both sides. This partially different hardness portion exists at a predetermined position slightly recessed from the surface of the pad, but there is a possibility that the pad user having a sharp sense may feel uncomfortable. Further, when the molded product pad is removed from the lower mold, the inclined wall portion is undercut, so that it is necessary to carefully remove the pad so that a part of the pad is not scraped off.

  In the foaming mold disclosed in Patent Document 2, it is only necessary to inject a small amount of polyurethane raw material from the injection head at a low pressure, but in the production line as described above, an excessive discharge amount is more than necessary. It is discharged by pressure and injected into the guide surface of the inlet of the joint part of the lower mold and the upper mold. Then, the injected raw material is guided not only by the guide surface and flowing down to the edge molding portion, but also accelerated by the inclined guide surface and part of it flows out to the main molding portion. Accordingly, the molded different hardness pad is such that a portion having high hardness is formed on the main support portion side at the boundary portion between the main support portion and the side support portion. Further, if the height of the ridge is increased in order to prevent the flow to the main molded portion, the thickness of the cushion at that portion may be reduced and the support force may be reduced.

  The present invention has been made paying attention to such a problem. The object of the present invention is to form a lower mold in order to form a different hardness portion outside the side support portion of a different hardness pad of an automobile seat. An object of the present invention is to provide a foaming mold capable of injecting a raw material only into the region when the polyurethane raw material is injected into the region where the section is partitioned. Another object of the present invention is to provide a method for forming a different hardness pad using the foaming mold.

  In order to solve the above problem, the foam molding die according to claim 1 is a foam molding die for molding a pad of an automobile seat comprising a main support portion and side support portions on both sides thereof. A pair of left and right ridges that divide the main support portion and the side support portions are formed on the lower mold of the foaming mold that molds different hardness pads with different hardnesses on the inside and outside of each portion, and each ridge portion The second region is formed in a foam mold in which a partition wall partitioning an inner first region and an outer second region is erected on a bottom surface in a side cavity for forming an outer side support portion. A first cutout portion whose upper part is opened is provided in a part of the cavity surface, and an injection recess that is open to the upper portion in communication with the first cutout portion is provided outside the cavity surface. In addition, the height of the bottom surface portion of the first notch portion is lower than the height of the top portion of the partition wall portion, while the upper die has a parting surface protruding partly close to the lower die. One protrusion is formed, and when the upper mold is closed with respect to the lower mold, the first notch is closed by the first protrusion.

  In the first aspect of the present invention, an injecting recess having an open upper part is provided outside the cavity surface forming the second region, and the polyurethane raw material discharged from the injecting head is a part of the lower mold. It is possible to inject into the injecting recess without being blocked by the above. Then, the material overflowing from the indentation through the first notch formed in the cavity surface of the second region flows into the second region and foams to form a high hardness portion outside the side support portion. Will do. At this time, since the height of the bottom surface portion of the first notch portion is lower than the height of the top portion of the partition wall portion, the material flowing into the second region gets over the partition wall portion and overflows into the first region. Is prevented. In addition, when the upper mold is closed with respect to the lower mold, the first notch is closed by the first protruding part from which a part of the upper parting surface protrudes, so that the foam expands in the cavity. It is prevented that the polyurethane raw material to be leaked into the injection recess through the first notch.

  According to a second aspect of the present invention, in the foam molding die according to the first aspect, the height of the bottom surface of the injection recess is gradually increased toward the first notch. It is what.

  According to the invention described in claim 2, since the height of the bottom surface of the recess for injection gradually increases toward the first notch, the polyurethane raw material fills the bottom of the recess for injection, It overflows from the first notch and flows into the second region. Therefore, the raw material that has flowed into the second region is prevented from flowing over the partition wall to the first region.

  According to a third aspect of the present invention, in the foam molding die according to the first or second aspect, the injection recess is provided on the outer side of one end side in the longitudinal direction of the second region. Is.

  According to the third aspect of the present invention, since the recess for injection is provided outside the one end side in the longitudinal direction of the second region, the lower mold is inclined to move from one end side to the other end side. Thus, if the bottom surface of the second region is lowered, the polyurethane raw material flowing into one end side of the second region can be spread over the entire bottom surface of the second region. Further, even if the lower mold is not inclined, the polyurethane raw material that has flowed into one end side of the second region can be spread over substantially the entire bottom of the second region before the chemical reaction proceeds and the viscosity increases. it can.

  According to a fourth aspect of the present invention, in the foam mold according to any one of the first to third aspects, the inner surface of the first projecting portion forms a part of the cavity surface of the second region. It is characterized by that.

  According to the fourth aspect of the present invention, since the inner surface of the first protrusion is a part of the cavity surface of the second region, the cavity in which the inner surface of the first protrusion and the surrounding cavity surface are continuous. Form a surface. Therefore, it is possible to prevent the first notch from forming a convex portion on the surface of the pad.

  According to a fifth aspect of the present invention, in the foam mold according to any one of the first to fourth aspects, the second region is formed outside the other end side in the longitudinal direction of the second region. A second notch that is open at the top is provided in a part of the cavity surface that is open, a disposal recess that communicates with the second notch and opens the upper part is provided, and the second notch A height of the bottom surface portion is made lower than a height of the top portion of the partition wall portion. On the other hand, the upper die is formed with a second protruding portion in which a parting surface that closes the lower die protrudes, and the lower die When the upper mold is closed with respect to the mold, the second notch is closed by the second protrusion.

  According to the fifth aspect of the present invention, the disposal concave portion communicating with the second notch formed in the cavity surface of the second region is provided outside the other end side in the longitudinal direction of the second region. Therefore, the raw material that has flowed into the second region is discarded in the disposal recess without overcoming the partition wall and overflowing into the first region. Therefore, even if the amount of the polyurethane raw material injected into the second region is increased, the raw material is prevented from flowing out into the first region. In addition, when the upper mold is closed with respect to the lower mold, the second notch is closed by the second protruding portion from which a part of the upper mold parting surface protrudes, so that the foam expands in the cavity. It is prevented that the polyurethane raw material to be leaked into the disposal recess through the second notch.

  A sixth aspect of the present invention is the foam molding die according to the fifth aspect, characterized in that the inner surface of the second projecting portion forms a part of the cavity surface of the second region. Is.

  According to the sixth aspect of the present invention, since the inner surface of the second protrusion is a part of the cavity surface of the second region, the cavity in which the inner surface of the second protrusion and the surrounding cavity surface are continuous. A surface is formed, and the second notch portion prevents the convex portion from being formed on the surface of the pad.

  An invention of a different hardness pad molding method according to claim 7 is a molding method for molding a different hardness pad of an automobile seat using the foam molding die according to any one of claims 1 to 6. The first polyurethane raw material is injected into the first region on the left and right sides of the lower mold and the inside thereof, and the second polyurethane raw material having a component different from the first polyurethane raw material is injected into the injecting recess, (2) The polyurethane raw material overflows from the first notch portion of the injection recess to the second region, the upper die is closed with respect to the lower die, and the first notch portion protrudes from the first die. The first polyurethane raw material injected into the first region and the inside thereof and the second polyurethane raw material overflowing into the second region are expanded and expanded, respectively, thereby foaming in the first region and the inside thereof. expansion And it is characterized in that the hardness and the second region of the foam made different from the hardness of the foam expanded foam.

  According to the seventh aspect of the present invention, the injection head is disposed above the injection recess before or after the first polyurethane raw material is injected into the left and right first regions of the lower mold and the inside thereof. The second polyurethane raw material is discharged, and the raw material can be injected into the injection recess without being blocked by a part of the lower mold. And after a raw material fills the bottom part of the recessed part for injection | pouring, a raw material can overflow to a 2nd area | region from a 1st notch part, and can spread over the whole surface of the bottom part of a 2nd area | region. Since the raw material is prevented from flowing over the partition wall to the first region, the upper mold is closed with respect to the lower mold, and then the first polyurethane raw material and the second polyurethane raw material are integrally foamed. Thus, it is possible to form a different hardness pad in which a boundary surface having different hardness is formed above the partition wall.

  The invention according to claim 8 is the method for forming the different hardness pad according to claim 7, wherein a part of the second polyurethane raw material in the second region is discarded in the disposal recess, The amount of the second polyurethane raw material is adjusted so that the second polyurethane raw material does not flow out to the first region.

  According to the eighth aspect of the present invention, when an amount of the second polyurethane raw material exceeding the necessary amount is injected, an excessive amount of the raw material can be discarded in the disposal recess. Therefore, even if the injection amount of the second polyurethane raw material into the second region where the injection amount is extremely small is larger than the predetermined amount, the second polyurethane raw material is prevented from flowing out into the first region.

  According to a ninth aspect of the present invention, in the method for forming a different hardness pad according to the eighth aspect, the lower polyurethane die is inclined so that the second polyurethane raw material flows in the second region. The portion is discarded in the discard recess.

  According to the ninth aspect of the invention, since the lower mold is inclined, the second polyurethane raw material that has flowed in from the vicinity of one end of the second region is transferred to the other end side of the bottom surface of the second region. It can be made to flow toward.

  According to the present invention, when the polyurethane raw material is injected from the injection head into the region where a part of the lower mold is partitioned in order to form the different hardness portion outside the side support portion in the different hardness pad of the automobile seat, Since the injecting recess for injecting the raw material is provided outside the region, it is possible to provide a foaming mold capable of injecting the raw material only in the region. In addition, a method for forming a different hardness pad using the foaming mold can be provided.

(First embodiment)
Hereinafter, an embodiment of a foaming mold 1 embodying the present invention and a method of forming a different hardness pad by the foaming mold 1 will be described with reference to FIGS. The upper mold 3 is depicted as a downward perspective view in FIG. 2 and as an upward plan view in FIG. 4, but the vertical direction in the description of each part of the upper mold 3 is shown in FIG. Based on.

  First, the cushion 52 of the pad 50 of the automobile seat made of the polyurethane foam molded by the foam molding die 1 of the present invention will be described with reference to FIGS. 7 and 8. The pad 50 shown in FIG. 7 shows a state where the polyurethane foam is not covered with the skin material.

  In the cushion 52, a main support portion 53 serving as a seating portion is partitioned forward and backward by a lateral groove 56a. The left and right sides of the main support portion 53 are partitioned by a pair of left and right vertical grooves 56b, and a side support portion 54 is disposed outside. The horizontal grooves 56a and the vertical grooves 56b are hog ring grooves for drawing the skin material. That is, a wire (not shown) is installed at the bottom of the hog ring groove, and the skin is bound to the wire. And the side support part 54 is divided into the inner part 54a and the outer part 54b by the slit part 55, and the hardness of the outer part 54b is formed higher than the hardness of the inner part 54a. The back 51 of the automobile seat has the same configuration as the cushion 52 except that the main support portion 57 partitioned vertically by the lateral groove 56a serves as a backrest portion, and therefore the description thereof will be omitted.

Next, the foam molding die 1 for molding the cushion 52 will be described with reference to FIGS.
As shown in FIGS. 1 and 3, the lower mold 2 of the foaming mold 1 having a square shape in plan view has a cavity surface formed at a position lower than the upper surface portion 24 on four sides. A hinge portion 2c is provided outside the rear side surface 2a of the lower mold 2, and a hinge portion 3c of an upper mold 3 described later is rotatably connected to the hinge portion 2c. The front side surface 2b opposite to the rear side surface 2a is the side facing the molding operator. Note that portions indicated by reference numerals 21, 22, and 23 are a front parting surface 21, a side parting surface 22, and a rear parting surface 23, respectively.

  At the center of the lower mold 2, a protrusion 11 for forming the hog ring horizontal groove 56a and the vertical groove 56b is substantially H-shaped by the pair of left and right vertical protrusions 11a and the horizontal protrusion 11b. Has been placed. A main cavity 10 for forming the main support portion 53 is partitioned in the front-rear direction (vertical direction in FIG. 3) by the lateral protrusion 11b. Further, side cavities 12 for forming the side support portions 54 are formed on the outer sides of the respective vertical protrusions 11a, and the side cavities 12 are separated from the inner first region 12a and the outer second cavities by the partition walls 14. It is partitioned into a region 12b. The partition wall portion 14 is erected on the bottom surface of the side cavity 12 to form the slit portion 55, and a high portion 14 b higher than other portions is formed at the front end portion thereof.

  A first cutout portion 4 in which a part of a cavity surface forming the second region 12b is cut is formed at an end portion of the second region 12b on the front side surface 2b side. The first cutout portion 4 faces the high portion 14b. An injection recess 16 that communicates with the first cutout 4 is formed outside the second region 12b.

  As shown in FIGS. 5A and 5D, the injection recess 16 forms a substantially inverted trapezoidal space opened upward, and its bottom surface 16a has a quadrangular shape. 16 a is disposed at a position lower than the bottom surface portion 17 of the first cutout portion 4. The bottom surface portion 17 is closed by a projecting end portion 33 of the first projecting portion 6 described later, and is lower than the top portion 14a of the partition wall portion 14 that partitions the first region 12a and the second region 12b. Is formed. In addition, the side part 17a which is connected to both ends of the bottom face part 17 and extends upward so as to be able to be closed with the projecting end part 33 is an inclined surface which opens as it goes upward.

  And the step part 18 is formed in three directions of the upper edge of the recessed part 16 for injection | pouring, and the upper end part 34 of the 1st protrusion part 6 of the upper mold | type 3 mentioned later contacts this step part 18. As shown in FIG. Furthermore, the left side wall part 25b, the rear wall part 25a, the right side wall part 25c, and the oblique side wall part 25d are formed so as to open upward as they extend upward from the outer edge of each step part 18. .

  As shown in FIG. 5B, the second region 12b extends upward to form an overhanging wall surface. And since the upper end edge 15 of the 2nd area | region 12b which is the boundary of the wall surface and the side parting surface 22 protrudes inside, as shown in FIG. It appears as an elongated shape having a narrower width than the width of the second region 12b.

  A second notch portion 5 in which a part of a cavity surface forming the second region 12b is notched is formed at the end of the second region 12b on the rear surface 2a side, and communicates with the second notch portion 5. A disposal recess 19 is formed outside the second region 12b.

  As shown in FIGS. 1, 3, and 5 (c), a part of the planar rectangular disposal recess 19 faces the second region 12 b. The upper end portion 20 of the discard recess 19 is formed higher than the bottom surface of the second region 12 b and lower than the top portion 14 a of the partition wall portion 14. Accordingly, the polyurethane raw material flowing through the second region 12b passes over the upper end 20 without being over the top 14a and is discarded on the bottom surface 19a. Note that the left side wall portion 26b, the rear wall portion 26a, and the rear parting surface 23 are formed so as to open upward as they extend upward from the respective outer edges of the three upper end portions 20.

  As shown in FIGS. 2 and 4, the upper mold 3 of the foaming mold 1 having a square plan view has a cavity surface or the like inside the lower surface portion 38 arranged along the three sides of the upper mold 3. It is formed at a position higher than the lower surface portion 38. A hinge portion 3c is provided outside the rear side surface 3a (downward in FIG. 4), and is rotatably connected to the hinge portion 2c of the lower mold 2. The front side surface 3b opposite to the rear side surface 3a is the side facing the molding operator. The first protrusion 6 and the second protrusion 7 protrude from the lower surface 38 of the upper mold 3 on both the left and right sides, and when the upper mold 3 is closed with respect to the lower mold 2, The 1 protrusion part 6 and the 2nd protrusion part 7 are arrange | positioned in the position corresponding to the 1st notch part 4 and the 2nd notch part 5 of the lower mold | type 2. FIG.

  The first projecting portion 6 has a substantially square trapezoidal shape in which the upper end portion 34 has a substantially quadrangular shape, and a side wall is formed by a part of the second region 12b, the wall portion 35b, the rear wall portion 35a, the inclined wall portion 35d, and the wall portion 35c. It is. A projecting end 33 of a substantially plate-like body projects from the upper end 34, and a side surface 33b inside the projecting end 33 forms a cavity surface that is continuous with the second region 12b.

  As shown in FIGS. 5A and 5D, the side surface 33 a in the width direction of the protruding end 33 is the side surface of the first notch portion 4 when the upper die 3 is closed with respect to the lower die 2. The slope is in contact with the portion 17a without a gap. Further, the upper surface of the protruding end portion 33 is in close contact with the bottom surface portion 17 of the first cutout portion 4.

  The 2nd protrusion part 7 is formed in the hollow rectangular tube shape. The upper end 36 is formed so as to close the upper end 20 of the disposal recess 19 of the lower mold 2 when the upper mold 3 is closed with respect to the lower mold 2 as shown in FIG. Has been.

Next, a method for forming a different hardness pad using the foam mold 1 will be described with reference to FIGS. 3, 5, and 6.
First, the first polyurethane raw material is injected from the injection head 40 (FIG. 6) into the main cavity 10 and the left and right first regions 12a of the lower mold 2 with the upper mold 3 opened relative to the lower mold 2. To do. In the present embodiment, the injection head 40 capable of separately discharging either the first polyurethane material or the second polyurethane material is used, but each of the first polyurethane material and the second polyurethane material is injected. Therefore, it is possible to use two injection heads.

  Next, as shown in FIG. 6, the second polyurethane raw material 41 is injected from the injection head 40 into the injection recess 16 of the lower mold 2. The injection amount of the second polyurethane raw material 41 is extremely small compared to the injection amount of the first polyurethane raw material injected into the main cavity 10 and the first region 12a. At this time, since the opening above the injection recess 16 is opened larger than the outer diameter of the fluid of the second polyurethane raw material 41 discharged from the injection head 40, the second polyurethane raw material 41 is injected into the injection recess 16. It can be injected only into. Further, since the injection amount of the second polyurethane raw material 41 is set to be larger than the amount that fills the injection recess 16 up to the height of the bottom surface portion 17, the second polyurethane raw material 41 gets over the bottom surface portion 17 and enters the second region 12b. Will be leaked.

  The second polyurethane raw material 41 that has flowed out to the second region 12b flows along the partition wall 14 and spreads over substantially the entire bottom surface of the elongated second region 12b. In this case, since the high portion 14b is formed at the end portion of the partition wall portion 14 on the front side surface 2b side, the second polyurethane raw material 41 over the bottom surface portion 17 is blocked by the high portion 14b, and the partition wall portion 14 is There is no overcoming. Then, as shown in FIG. 5 (c), an excessive amount of the second polyurethane raw material 41 gets over the upper end portion 20 formed higher than the second region 12b and is discarded into the disposal recess 19. . Therefore, after the second polyurethane raw material 41 fills the second region 12b, the second polyurethane raw material 41 is prevented from flowing over the partition wall portion 14 to the first region 12a. For this reason, the second polyurethane raw material 41 injected into the second region 12b having an extremely small required injection amount passes over the partition wall 14 and flows out to the first region 12a even if the injection amount is larger than necessary. There is no.

  Further, if the lower mold 2 is tilted and fixed to a carriage that circulates in the production line, and the lower mold 2 is inclined downward from the front side surface 2b side to the rear side surface 2a side, the second region 12b The second polyurethane raw material 41 that has flowed in from the vicinity of the end portion on the front side surface 2b side can flow toward the rear side surface 2a side through the bottom surface of the second region 12b. At this time, instead of inclining and fixing the lower mold 2 to the cart that circulates in the production line, the lower mold 2 that is pivotally fixed to the cart is used before or after the second polyurethane raw material 41 is injected. It is possible to incline it after it has been done and return it to its original posture after a predetermined time has elapsed.

  Then, the upper mold 3 is closed with respect to the lower mold 2, the first protruding part 6 is closed with respect to the first notch part 4 of the lower mold 2, and the second notch part 5 of the lower mold 2 is closed. On the other hand, the 2nd protrusion part 7 is closed. Then, the cavity formed by the lower mold 2 and the upper mold 3 becomes a continuous cavity surface in the first notch portion 4 and the second notch portion 5 without forming a gap or a recess.

  In addition, the first polyurethane material and the second polyurethane material are expanded and expanded from the bottom surface of the cavity defined by the partition wall 14, and are integrated above the partition wall 14. Therefore, a boundary surface where the first polyurethane raw material and the second polyurethane raw material do not bite into each other can be formed.

  It should be noted that the foam expanded and solidified while remaining in the injection recess 16 or the foam expanded and solidified after being discarded in the disposal recess 19 is removed simultaneously with demolding of the foam molded product.

Therefore, according to the above embodiment, the following effects can be obtained.
(1) In the above embodiment, the first notch 4 in which a part of the cavity surface of the second region 12b is notched is formed at the end of the second region 12b on the front side surface 2b side. An injecting recess 16 communicating with the notch 4 was formed outside the second region 12b. And the height of the bottom face part 17 of the 1st notch part 4 was made lower than the height of the top part 14a of the partition part 14. FIG. Therefore, the second polyurethane raw material 41 injected into the injection recess 16 flows into the second region 12b beyond the bottom surface portion 17, but is prevented from overflowing the partition wall portion 14 and overflowing into the first region 12a. The Therefore, it is possible to provide the foaming mold 1 in which the polyurethane raw materials having different components are partitioned by the partition wall portion 14 and foamed and expanded without being mixed before foaming.

  (2) In the above embodiment, when the upper die 3 is closed with respect to the lower die 2, the first notch portion 4 is the first protruding portion from which a part of the parting surface of the upper die 3 protrudes. 6 to be closed. Therefore, it is possible to prevent the second polyurethane raw material 41 that expands and expands in the cavity from leaking into the injecting recess 16 through the first notch 4.

  (3) In the above embodiment, the injection recess 16 is provided outside the second region 12b on the front side 2b side. Therefore, by inclining the lower mold 2 so as to descend downward from the front side surface 2b side to the rear side surface 2a side, the second polyurethane raw material 41 flowing into the second region 12b is spread over the entire bottom surface of the second region 12b. Can be spread.

  (4) In the above-described embodiment, the second cutout portion 5 in which a part of the cavity surface of the second region 12b is cut out is formed at the end of the second region 12b on the rear surface 2a side. A disposal recess 19 communicating with the notch 5 was formed outside the second region 12b. Therefore, even if the amount of the second polyurethane raw material 41 that has flowed into the second region 12b is large, the second polyurethane raw material 41 does not overflow the partition region 14 and overflow into the first region 12a, but is discarded in the disposal recess 19. Will be. Therefore, even if the injection amount of the second polyurethane raw material 41 is set to a large value, the raw material is prevented from flowing out into the first region 12a. Therefore, even when the injection amount into the second region 12b is extremely small, it is possible to provide the foam molding die 1 capable of setting stable molding conditions.

  (5) In the above embodiment, when the upper die 3 is closed with respect to the lower die 2, the second notch portion 5 is the second protruding portion 7 in which a part of the parting surface of the upper die 3 protrudes. Closed. Therefore, the second polyurethane raw material 41 that expands and expands in the cavity can be prevented from leaking to the disposal recess 19 through the second notch 5.

  (6) In the above embodiment, after injecting the first polyurethane raw material from the injection head 40 into the main cavity 10 and the first region 12 a inside the partition wall 14 in the lower mold 2, the injection recesses from the injection head 40 16, the second polyurethane raw material 41 was injected. And the 2nd polyurethane raw material 41 was made to flow out from the recessed part 16 for injection | pouring to the 2nd area | region 12b, and it was made to spread over the whole surface of the bottom part of the 2nd area | region 12b. At this time, the second polyurethane raw material 41 is prevented from flowing over the partition wall 14 to the first region 12a. Accordingly, the first polyurethane raw material and the second polyurethane raw material 41 partitioned by the partition wall portion 14 are expanded and expanded, and the cushions 52 having different hardnesses between the inner portion 54a and the outer portion 54b with the upper portion of the partition wall portion 14 as the boundary. Can be molded.

  (7) In the above embodiment, after the second polyurethane raw material 41 that has flowed out to the second region 12b is spread over substantially the entire bottom surface of the second region 12b, an excess amount is discarded into the disposal recess 19 It was made to be. Accordingly, the second polyurethane raw material 41 can be prevented from flowing over the partition wall 14 and flowing into the first region 12a, so that the injection amount of the second polyurethane raw material 41 can be made larger than a predetermined amount. . For this reason, even when the injection amount into the second region 12b is extremely small, the second polyurethane raw material 41 is prevented from flowing over the partition wall portion 14 to the first region 12a. Stable molding conditions can be obtained.

  (8) In the above-described embodiment, the lower mold 2 is tilted and fixed to a cart that circulates in the production line, and the lower mold 2 is inclined downward from the front side surface 2b side to the rear side surface 2a side. . By doing so, the second polyurethane raw material 41 that has flowed in from the vicinity of the end portion on the front side surface 2b side of the second region 12b can flow toward the rear side surface 2a side on the bottom surface of the second region 12b. .

(Second Embodiment)
Next, a second embodiment of the foam mold 1 embodying the present invention will be described with reference to FIG. 9 with a focus on differences from the first embodiment.

  As shown in FIG. 9, in the injecting recess 16 of the present embodiment, the bottom surface of the first notch portion 4 has a slant bottom surface portion 17b inclined downward toward the direction opposite to the second region 12b, The bottom surface 16a is connected to the inclined bottom surface portion 17b. Therefore, the second polyurethane raw material 41 injected into the injecting recess 16 first flows to the bottom surface 16a, and thereafter, as the injection amount increases, it flows up to the inclined bottom surface portion 17b and flows out to the second region 12b. become. Therefore, the second polyurethane raw material 41 is prevented from flowing out to the second region 12b and exceeding the top portion 14a of the partition wall portion 14 while maintaining the flow.

Further, the upper surface of the protruding end portion 33 of the upper mold 3 is a slope corresponding to the inclined bottom surface portion 17b so that it can contact the inclined bottom surface portion 17b of the first cutout portion 4 without any gap.
(9) In the above embodiment, the injection recess 16 and the first notch 4 are connected to each other at the bottom surface by the inclined bottom surface portion 17b. Therefore, the second polyurethane raw material 41 injected into the injection recess 16 can first flow into the bottom surface 16a, and then flow up the oblique bottom surface portion 17b to the second region 12b. Therefore, it is possible to provide the foam molding die 1 in which the second polyurethane raw material 41 flowing out to the second region 12b is prevented from overflowing to the first region 12a beyond the top portion 14a of the partition wall 14.

(Example of change)
In addition, the said embodiment can also be changed and actualized as follows.
In the first embodiment and the second embodiment, the first notch 4 in which a part of the cavity surface forming the second region 12b is notched is formed at the end of the second region 12b on the front side surface 2b side. An injecting recess 16 that was formed and communicated with the first notch 4 was formed outside the second region 12b. On the other hand, a first notch portion 4 in which a part of the cavity surface forming the second region 12b is notched is formed near the center in the front-rear direction of the second region 12b, and the first notch portion 4 is formed in the first notch portion 4. An injecting recess 16 that communicates is provided outside the second region 12b. In this way, when the bottom surface of the second region 12b is a flat surface or a curved surface close to a flat surface and the height difference is small, the second polyurethane raw material 41 that flows into the vicinity of the center of the second region 12b It can flow and spread over substantially the whole area of the 2nd field 12b.

At this time, the disposal recess 19 may be provided at either one of the outer side of the end on the rear side 2a side of the second region 12b or the outer side of the end of the second region 12b on the front side 2b side. , Both may be provided. Further, the discard recess 19 may not be provided.
The injection recess 16 is provided on the front side 2b side of the lower mold 2 and the disposal recess 19 is provided on the rear side 2a side of the lower mold 2, but the injection recess 16 is provided on the rear side 2a side of the lower mold 2 The recess 19 for disposal is provided on the front side 2b side of the lower mold 2.
The lower mold 2 is provided with the injection recess 16 and the disposal recess 19, but only the injection recess 16 is provided and the disposal recess 19 is not provided regardless of the position of the injection recess 16. . At this time, if the injection amount of the second polyurethane raw material 41 is managed, the second polyurethane raw material 41 is prevented from overflowing the partition wall portion 14 and overflowing into the first region 12a.
The first polyurethane raw material is injected into the main cavity 10 of the lower mold 2 and the left and right first regions 12a, and then the second polyurethane raw material 41 is injected into the injecting recess 16, but the injecting recess 16 After injecting the second polyurethane raw material 41, the first polyurethane raw material is injected into the main cavity 10 and the left and right first regions 12a.

The perspective view which shows typically the lower mold | type of the foaming mold of embodiment of this invention. The perspective view which shows typically the upper mold | type of the foaming mold of embodiment of this invention. The top view which shows typically the lower mold | type of the foaming mold of embodiment of this invention. The top view which shows typically the upper mold | type of the foaming mold of embodiment of this invention. (A) is a partial cross-sectional view taken along arrow AA in FIG. 3, (b) is a partial cross-sectional view taken along arrow BB in FIG. 3, (c) is a partial cross-sectional view taken along CC arrow in FIG. ) Is a partial cross-sectional view taken along DD in FIG. The schematic diagram which shows a part of behavior of a polyurethane raw material using the partial cross section of DD arrow of FIG. The perspective view which shows the pad shape | molded using the foaming mold of embodiment of this invention. The EE arrow partial cross section figure of FIG. The partial cross section figure which shows the recessed part for injection | pouring of 2nd Embodiment of this invention using the partial cross section figure of AA of FIG.

Explanation of symbols

  DESCRIPTION OF SYMBOLS 1 ... Foam mold, 2 ... Lower mold, 3 ... Upper mold, 4 ... 1st notch part, 5 ... 2nd notch part, 6 ... 1st protrusion part, 7 ... 2nd protrusion part, 11 ... Projection Part, 12 ... side cavity, 12a ... first region, 12b ... second region, 14 ... partition wall part, 14a ... top part, 16 ... injection recess, 16a, 19a ... bottom, 17 ... bottom part, 19 ... disposal recess 41 ... second polyurethane raw material, 50 ... pad, 53, 57 ... main support part, 54 ... side support part.

Claims (9)

  A foam molding die for molding a car seat pad comprising a main support portion and side support portions on both sides of the main support portion. The foam molding die molds different hardness pads with different hardnesses on the inside and outside of the side support portion. The lower mold is formed with a pair of left and right ridges that divide the main support portion and the side support portion, and a side cavity for forming a side support portion outside each ridge portion has an inner first region and In the foaming mold in which the partition wall partitioning the outer second region is erected on the bottom surface, a first notch portion having an open top is provided on a part of the cavity surface forming the second region, An injecting recess having an open top communicating with the first notch is provided outside the cavity surface, and the height of the bottom surface of the first notch is the height of the partition wall. On the other hand, the upper mold is formed with a first protruding portion in which a part of a parting surface that is closed with the lower mold protrudes, and the upper mold is closed with respect to the lower mold. The foaming mold is characterized in that the first notch is closed by the first protrusion.   The foaming mold according to claim 1, wherein a height of the bottom surface of the injecting recess gradually increases toward the first notch.   The foaming mold according to claim 1 or 2, wherein the injection recess is provided on an outer side of one end side in the longitudinal direction of the second region.   4. The foaming mold according to claim 1, wherein an inner surface of the first projecting portion forms a part of a cavity surface of the second region. 5.   Outside the second region in the longitudinal direction on the other end side, a second notch is provided in a part of the cavity surface that forms the second region and the upper part is opened, and the second notch A disposal recess that communicates and opens the upper part is provided, and the height of the bottom surface of the second notch is lower than the height of the top of the partition wall, while the upper mold includes the lower mold A second projecting portion is formed in which a part of the parting surface that closes is projected. When the upper mold is closed with respect to the lower mold, the second notched portion is closed by the second projecting section. The foaming mold according to any one of claims 1 to 4, wherein the foaming mold is used.   The foaming mold according to claim 5, wherein an inner surface of the second projecting portion forms a part of a cavity surface of the second region.   A molding method for molding a different hardness pad of an automobile seat using the foam molding die according to any one of claims 1 to 6, wherein the first region on the left and right of the lower mold and the inside thereof are formed. While injecting the first polyurethane raw material, a second polyurethane raw material having a different component from the first polyurethane raw material is injected into the injecting recess, and the second polyurethane raw material is injected from the first notch of the injecting recess. Overflowing into the second region, the upper die is closed with respect to the lower die, and the first notch is closed with the first protruding portion of the upper die, and injected into the first region and the inside thereof. When the first polyurethane raw material and the second polyurethane raw material overflowing into the second region expand and expand, respectively, the hardness of the foam expanded and expanded in the first region and the inside thereof and the foam expanded and expanded in the second region. Method of molding different hardness pad, characterized in that was different from the body of hardness.   A part of the second polyurethane raw material in the second region is discarded in the disposal recess, the amount of the second polyurethane raw material in the second region is adjusted, and the second polyurethane raw material does not flow out to the first region. The method for forming a different hardness pad according to claim 7, wherein:   9. The different hardness pad according to claim 8, wherein the lower mold is inclined so that the second polyurethane raw material flows in the second region and a part thereof is discarded in the disposal recess. Molding method.

Images