JP2010065177A - Black ink - Google Patents
Black ink Download PDFInfo
- Publication number
- JP2010065177A JP2010065177A JP2008234414A JP2008234414A JP2010065177A JP 2010065177 A JP2010065177 A JP 2010065177A JP 2008234414 A JP2008234414 A JP 2008234414A JP 2008234414 A JP2008234414 A JP 2008234414A JP 2010065177 A JP2010065177 A JP 2010065177A
- Authority
- JP
- Japan
- Prior art keywords
- disperse
- black ink
- weight
- thread
- hue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、耐光性及び色相に優れた記録画像を得ることができる、インクジェット記録用のブラックインクに関する。 The present invention relates to a black ink for inkjet recording, which can obtain a recorded image excellent in light resistance and hue.
インクジェット記録方法は、微細なノズルヘッドからインクの小滴を吐出して飛翔させ、紙等の記録媒体に付着させて印刷を行う印刷方法である。この方法は、比較的安価な装置で高解像度かつ高品位な画像を、高速で印刷可能であるという特徴を有する。 The ink jet recording method is a printing method in which printing is performed by ejecting small droplets of ink from a fine nozzle head so that the ink droplets are ejected and adhered to a recording medium such as paper. This method is characterized in that a high-resolution and high-quality image can be printed at a high speed with a relatively inexpensive apparatus.
近年、インクジェット記録方法を用いて、記録媒体である布帛を捺染する技術が提案されている。布帛のインクジェット捺染に適したインクには、インクの滲みがないことや高い印字特性などが要求される。例えば、分散染料を含むインクを用いたインクジェット捺染により、耐光性及び発色性に優れた捺染物を提供する方法が提案されている(特許文献1)。 In recent years, a technique for printing a cloth, which is a recording medium, using an inkjet recording method has been proposed. Ink suitable for inkjet textile printing is required to have no ink bleeding and high printing characteristics. For example, there has been proposed a method for providing a printed matter excellent in light resistance and color developability by inkjet printing using an ink containing a disperse dye (Patent Document 1).
本発明は、耐光性及び色相に優れた記録画像を得ることができる、インクジェット記録用のブラックインクを提供することを課題とする。 An object of the present invention is to provide a black ink for ink jet recording, which can obtain a recorded image excellent in light resistance and hue.
本発明は、(1)少なくとも水と、分散染料として、C.I.ディスパースイエロー163と、C.I.ディスパースレッド152と、C.I.ディスパースレッド191と、C.I.ディスパースブルー165と、を含む、ブラックインク;
(2)さらにC.I.ディスパースブルー60を0.1〜1重量%含む、前記(1)に記載のブラックインク;
(3)前記C.I.ディスパースレッド152と前記C.I.ディスパースレッド191との重量比が0.2:3.3〜1.9:1.5である、前記(1)又は(2)に記載のブラックインク;
(4)前記C.I.ディスパースレッド152と前記C.I.ディスパースレッド191との重量比が0.6:2.9〜1.3:2.1である、前記(1)又は(2)に記載のブラックインク;
(5)前記C.I.ディスパースブルー165を0.6〜3.5重量%含む、前記(1)〜(4)のいずれかに記載のブラックインク;
(6)前記C.I.ディスパースイエロー163を1.6〜6.4重量%含む、前記(1)〜(5)のいずれかに記載のブラックインク;
(7)前記C.I.ディスパースレッド152と前記C.I.ディスパースレッド191との重量比が0.6:2.9〜1.3:2.1であり、前記C.I.ディスパースブルー165を1.4〜2.6重量%含み、前記C.I.ディスパースイエロー163を3.6〜5.0重量%含む、前記(1)〜(6)のいずれかに記載のブラックインク;を提供する。
The present invention relates to (1) at least water and, as a disperse dye, C.I. I. Disperse Yellow 163, C.I. I. Disperse thread 152, C.I. I. Disper thread 191 and C.I. I. Disperse Blue 165, and a black ink;
(2) Further, C.I. I. The black ink according to (1), containing 0.1 to 1% by weight of disperse blue 60;
(3) C.I. I. Disper thread 152 and the C.I. I. The black ink according to (1) or (2), wherein the weight ratio to the disperse thread 191 is 0.2: 3.3 to 1.9: 1.5;
(4) The C.I. I. Disper thread 152 and the C.I. I. The black ink according to (1) or (2), wherein the weight ratio with respect to the disperse thread 191 is 0.6: 2.9 to 1.3: 2.1;
(5) C.I. I. The black ink according to any one of (1) to (4), comprising 0.6 to 3.5% by weight of disperse blue 165;
(6) The C.I. I. The black ink according to any one of (1) to (5), comprising 1.6 to 6.4% by weight of Disperse Yellow 163;
(7) The C.I. I. Disper thread 152 and the C.I. I. The weight ratio with respect to the disperse thread 191 is 0.6: 2.9 to 1.3: 2.1. I. Disperse Blue 165 is contained in an amount of 1.4 to 2.6% by weight, and the C.I. I. The black ink according to any one of (1) to (6), comprising 3.6 to 5.0% by weight of disperse yellow 163;
本発明によれば、耐光性及び色相に優れた記録画像を得ることができる、インクジェット記録用のブラックインクを提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the black ink for inkjet recording which can obtain the recorded image excellent in light resistance and hue can be provided.
次に、本発明の実施の形態について説明する。以下の実施形態は、本発明を説明するための例示であり、本発明をこの実施形態にのみ限定する趣旨ではない。本発明は、その要旨を逸脱しない限り、さまざまな形態で実施することができる。 Next, an embodiment of the present invention will be described. The following embodiment is an example for explaining the present invention, and is not intended to limit the present invention only to this embodiment. The present invention can be implemented in various forms without departing from the gist thereof.
本発明のブラックインクは、少なくとも水と、分散染料として、C.I.ディスパースイエロー163と、C.I.ディスパースレッド152と、C.I.ディスパースレッド191と、C.I.ディスパースブルー165と、を含む。
上記ブラックインクを用いて捺染することにより、耐光性及び色相に優れた記録画像を得ることができる。
The black ink of the present invention contains at least water and C.I. I. Disperse Yellow 163, C.I. I. Disperse thread 152, C.I. I. Disper thread 191 and C.I. I. Disperse Blue 165.
By printing using the black ink, a recorded image having excellent light resistance and hue can be obtained.
上記ブラックインクは、さらにC.I.ディスパースブルー60を0.1〜1重量%含むことが好ましい。
このような組成とすることにより、耐光性、色相、及び演色性を両立させた記録画像を得ることができる。
演色性とはランプなどがある物体を照らしたときにその物体の色の見え方に及ぼす光源の性質のことである。
The black ink further contains C.I. I. It is preferable to contain 0.1 to 1% by weight of Disperse Blue 60.
By using such a composition, a recorded image having both light resistance, hue, and color rendering can be obtained.
Color rendering is the property of a light source that affects the color appearance of an object when a lamp or the like is illuminated.
上記ブラックインクにおいて、前記C.I.ディスパースレッド152と前記C.I.ディスパースレッド191との重量比は、0.2:3.3〜1.9:1.5であることが好ましく、0.6:2.9〜1.3:2.1であることがより好ましい。 In the black ink, the C.I. I. Disper thread 152 and the C.I. I. The weight ratio with the disperse thread 191 is preferably 0.2: 3.3 to 1.9: 1.5, more preferably 0.6: 2.9 to 1.3: 2.1. preferable.
上記ブラックインクは、前記C.I.ディスパースブルー165を0.6〜3.5重量%含むことが好ましく、1.4〜2.6重量%含むことがより好ましく、1.7〜2.3重量%であることがさらに好ましい。 The black ink includes the C.I. I. Disperse Blue 165 is preferably contained in an amount of 0.6 to 3.5% by weight, more preferably 1.4 to 2.6% by weight, and even more preferably 1.7 to 2.3% by weight.
上記ブラックインクは、前記C.I.ディスパースイエロー163を1.6〜6.4重量%含むことが好ましく、3.6〜5.0重量%含むことがより好ましく、4.0〜4.5重量%であることがさらに好ましい。 The black ink includes the C.I. I. Disperse Yellow 163 is preferably contained in an amount of 1.6 to 6.4% by weight, more preferably 3.6 to 5.0% by weight, and even more preferably 4.0 to 4.5% by weight.
上記ブラックインクは、前記C.I.ディスパースレッド152と前記C.I.ディスパースレッド191との重量比が0.6:2.9〜1.3:2.1であり、前記C.I.ディスパースブルー165を1.4〜2.6重量%含み、前記C.I.ディスパースイエロー163を3.6〜5.0重量%含むことが好ましい。 The black ink includes the C.I. I. Disper thread 152 and the C.I. I. The weight ratio with respect to the disperse thread 191 is 0.6: 2.9 to 1.3: 2.1. I. Disperse Blue 165 is contained in an amount of 1.4 to 2.6% by weight, and the C.I. I. It is preferable to contain 3.6 to 5.0% by weight of disperse yellow 163.
上記インクジェット捺染用のブラックインクは、上記の各分散染料を分散剤により分散させることが好ましい。好適な分散剤としては、花王株式会社製デモールSS−L(芳香族スルホン酸ホルマリン縮合物のナトリウム塩)、花王株式会社製デモールRS−L(β‐ナフタレンスルホン酸ホルマリン縮合物ナトリウム塩)、日本製紙ケミカル株式会社製サンエキスP252(リグニンスルホン酸ナトリウム)、BASF社製Luvitec K30(ポリビニルピロリドン)、BASFポゾリス社製レオビルド2440(メラミンスルホン酸塩)等が挙げられる。 In the black ink for ink jet textile printing, it is preferable to disperse each disperse dye with a dispersant. As suitable dispersing agents, DEMOL SS-L (sodium salt of aromatic sulfonic acid formalin condensate) manufactured by Kao Corporation, DEMORS RS-L (sodium salt of β-naphthalenesulfonic acid formalin condensate) manufactured by Kao Corporation, Japan Examples include Sun Extract P252 (sodium lignin sulfonate) manufactured by Paper Manufacturing Chemical Co., Ltd., Luvitec K30 (polyvinylpyrrolidone) manufactured by BASF, and Leo Build 2440 (melamine sulfonate) manufactured by BASF Pozzolith.
上記インクジェット捺染用のブラックインクは、水に加えて水溶性有機溶剤を含むことが適当な粘度と保湿性を確保するために好ましい。好適な水溶性有機溶剤としては、グリセリン、エチレングリコール、ジエチレングリコール、トリエチレングリコール、2−ピロリドン、2−イミダゾリジノン、1,3−ジメチル−2−イミダゾリジノン等が挙げられる。 The black ink for ink jet textile printing preferably contains a water-soluble organic solvent in addition to water in order to ensure appropriate viscosity and moisture retention. Suitable water-soluble organic solvents include glycerin, ethylene glycol, diethylene glycol, triethylene glycol, 2-pyrrolidone, 2-imidazolidinone, 1,3-dimethyl-2-imidazolidinone and the like.
表1〜4に示す組成によりインクジェット捺染用インクを調製した。表中の数値は重量%を表す。表1〜4中における[1]〜[5]は以下のとおりである。
[1] ナフタレンスルホン酸とホルマリンの縮合物ナトリウム塩の40%水溶液
[2] ナフタレンスルホン酸とシェファー酸とクレゾール縮合物ナトリウム塩の40%水溶液
[3] 日信化学株式会社製
[4] 耐光性評価によりOD値の低下率が7日経過時までに80%低下したものを5、70%を4、60%を3、50%を2、それ以下を1とする。
[5]a*とb*が±2以下のものを5、±3以下のものを4、±4以下のものを3、±5以下のものを2、それ以上のものを1とする。
[6] 自然光とタングステンランプで色相が同じとき2、異なるとき1とする。
Ink jet textile printing inks were prepared according to the compositions shown in Tables 1 to 4. The numerical values in the table represent% by weight. [1] to [5] in Tables 1 to 4 are as follows.
[1] Naphthalenesulfonic acid / formalin condensate sodium salt 40% aqueous solution
[2] 40% aqueous solution of sodium salt of naphthalenesulfonic acid, shepheric acid and cresol condensate
[3] Nissin Chemical Co., Ltd.
[4] According to the light resistance evaluation, when the decrease rate of the OD value has decreased by 80% by the end of 7 days, 5, 70% is 4, 4, 60% is 3, 50% is 2, and less is 1.
[5] 5 for a * and b * of ± 2 or less, 4 for ± 3 or less, 3 for ± 4 or less, 2 for ± 5 or less, and 1 for more.
[6] Set to 2 when natural light and tungsten lamp have the same hue, and 1 when different.
以下の印捺条件により印捺させたサンプルを、以下の条件にて定着及び洗浄をした後、耐光性及び色相を評価した。
評価結果を表1〜4に示す。表1はC.I.ディスパースレッド152及びC.I.ディスパースレッド191の添加比率検討、表2はC.I.ディスパースブルー165の添加比率検討、表3はC.I.ディスパースイエロー163の添加比率検討、表4は演色性の検討、を示す。
A sample printed under the following printing conditions was fixed and washed under the following conditions, and then light resistance and hue were evaluated.
The evaluation results are shown in Tables 1 to 4. Table 1 shows C.I. I. Disperse thread 152 and C.I. I. Disperse thread 191 addition ratio study, Table 2 shows C.I. I. Dispersion Blue 165 addition ratio study, Table 3 shows C.I. I. Examination of addition ratio of Disperse Yellow 163, Table 4 shows examination of color rendering properties.
(印捺条件)
プリンタ:PM−A750
解像度:720dpi×720dpi
布:ポンジクロス(ポリエステル) セーレン製
(Printing conditions)
Printer: PM-A750
Resolution: 720 dpi x 720 dpi
Cloth: Ponji cloth (polyester) Made of Seiren
(定着条件)
温度:170℃
湿度:100%×10分
(Fixing conditions)
Temperature: 170 ° C
Humidity: 100% x 10 minutes
(洗浄条件)
80℃条件下でハイドロサルファイト、水酸化ナトリウム、各0.2%の濃度にて10分間浸漬洗いを実施し、その後40℃、20℃のお湯により順次洗浄して仕上げた。その後はアイロンにより乾燥させた。
(Cleaning conditions)
Immersion washing was performed for 10 minutes at a concentration of 0.2% of hydrosulfite and sodium hydroxide under the conditions of 80 ° C., and then washed with hot water of 40 ° C. and 20 ° C. to finish. Thereafter, it was dried with an iron.
(耐光性試験)
耐光性試験は、キセノンレーザーメーターXL−75(スガ試験機株式会社製)を用いて、24℃、相対湿度60%RHの条件下で、照度70000luxを照射を行った。
セイコーエプソン株式会社製PM−A750を用いて、各インクを用いて印刷してODの低下率(%)を測定することによって行った。
(Light resistance test)
In the light resistance test, irradiation with an illuminance of 70000 lux was performed using a Xenon laser meter XL-75 (manufactured by Suga Test Instruments Co., Ltd.) at 24 ° C. and a relative humidity of 60% RH.
Using PM-A750 manufactured by Seiko Epson Corporation, printing was performed using each ink, and the reduction rate (%) of OD was measured.
(色相評価)
記録媒体は、綿布としてポンジクロス(セーレン製)を用いた。印刷した記録物をグレタグ濃度計(グレタグマクベス社製)を用いてCIEで規定される色差表示法のa*b*を測定した。
(Hue evaluation)
As the recording medium, Ponji cloth (manufactured by Seiren) was used as a cotton cloth. A * b * of the color difference display method defined by CIE was measured for the printed matter using a Gretag densitometer (manufactured by Gretag Macbeth).
表1〜4に示すように、実施例のインクを用いた場合では、比較例に比べて、耐光性、及び色相に優れていることが判った。特に、実施例3〜7、14〜17、25〜27は耐光性と色相の双方が4以上であり極めて良好であった。 As shown in Tables 1 to 4, it was found that when the inks of the examples were used, the light resistance and hue were superior to those of the comparative examples. In particular, Examples 3 to 7, 14 to 17, and 25 to 27 were extremely good because both the light resistance and the hue were 4 or more.
Claims (7)