JP2009155466A - Polishing liquid composition - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a polishing liquid composition capable of restraining roll-off. <P>SOLUTION: The polishing liquid composition contains a copolymer having a constitutional unit expressed by formula (I) and a constitutional unit expressed by formula (II), and an abrasive. Methoxy polyethylene glycol methacrylates are enumerated as a monomer having the constitutional unit expressed by the formula (I), and oxypropyl dimethyl polysiloxane methacrylates are enumerated as a monomer having the constitutional unit expressed by the formula (II). <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

  The present invention relates to a polishing composition and a method for producing a substrate using the same.

  With the rapid spread of computers and the start of digital broadcasting, etc., it is desired to increase the recording capacity of hard disk drives. In order to realize this increase in recording capacity, for example, in a polishing process of a memory hard disk used in a hard disk drive, a method of suppressing the occurrence of roll-off (end face sag) and increasing the recording area is performed. As a polishing liquid composition for suppressing roll-off, a polishing liquid composition containing a polyoxyethylene monomer compound and an acid (Patent Document 1) or a polishing liquid composition containing a monomer compound such as polyoxyethylene sorbitan fatty acid ester ( Patent Document 2) has been proposed.

However, with the expansion of the information society, there is a demand for a further increase in recording capacity. Therefore, the effect of suppressing the conventional polishing liquid composition is not sufficient, and a polishing liquid composition that can further suppress roll-off is provided. It has been demanded.
JP 2002-167575 A Japanese Patent Laid-Open No. 2003-160781

  The present invention provides a polishing composition for suppressing roll-off and a method for producing a substrate using the same.

  The present invention is a polishing composition comprising a copolymer and an abrasive, wherein the copolymer is a structural unit represented by the following formula (I) and a structural unit represented by the following formula (II): It is related with the polishing liquid composition which is a copolymer which has. The present invention also relates to a method for manufacturing a substrate including a step of polishing a substrate to be polished using the polishing composition.

［前記式（Ｉ）において、Ｒ¹は水素原子又はメチル基であり、Ｒ²は炭素数１〜４のアルキル基であり、ＡＯは炭素数１〜８のアルキレンオキシド基であり、ｐは０又は１であり、ｎはＡＯの全平均付加モル数であって６〜３００の数であり、
前記式（ＩＩ）において、Ｒ³は水素原子又はメチル基であり、Ｒ⁴は炭素数１〜４の直鎖又は分岐鎖のアルキレン基であり、Ｒ⁵は炭素数１〜３０の直鎖又は分岐鎖のアルキル基であり、Ｘは酸素原子又はＮＨであり、ｍはジメチルシロキサンの全平均付加モル数であって０〜３０の数であり、ｈは０〜２の数である。］

[In the formula (I), R ¹ is a hydrogen atom or a methyl group, R ² is an alkyl group having 1 to 4 carbon atoms, AO is an alkylene oxide group having 1 to 8 carbon atoms, and p is 0. Or n, where n is the total average added mole number of AO and is a number from 6 to 300;
In the formula (II), R ³ is a hydrogen atom or a methyl group, R ⁴ is a linear or branched alkylene group having 1 to ⁴ carbon atoms, and R ⁵ is a linear or branched group having 1 to 30 carbon atoms. It is a branched alkyl group, X is an oxygen atom or NH, m is the total average added mole number of dimethylsiloxane, and is a number from 0 to 30, and h is a number from 0 to 2. ]

  ADVANTAGE OF THE INVENTION According to this invention, the polishing liquid composition which can suppress the roll-off in the grinding | polishing process of a board | substrate, and the manufacturing method of a board | substrate using the same can be provided.

(Polishing liquid composition of the present invention)
The present inventors have found that the cause of roll-off is the deformation of the polishing pad during polishing of the substrate. Specifically, first, the polishing pad is deformed by applying a polishing load when polishing the substrate. Then, a high pressure is locally applied to the end portion of the substrate due to this deformation, so that the end portion of the substrate is excessively polished. As a result, it is estimated that roll-off has occurred. As a result of repeated studies to reduce the pressure acting locally on the edge of the substrate, the inventors have reduced the pressure acting locally on the edge of the substrate by reducing the frictional force between the polishing pad and the abrasive. I came up with the knowledge that it can be reduced. That is, the polishing liquid composition of the present invention can reduce the frictional force between the polishing pad and the abrasive as compared with the conventional polishing liquid composition, and the amount of the abrasive held in the deformed portion of the polishing pad. As a result, it is presumed that roll-off is suppressed without excessive polishing of the edge of the substrate. However, these assumptions do not limit the present invention. ADVANTAGE OF THE INVENTION According to this invention, the polishing liquid composition which can suppress the roll-off in the grinding | polishing process of a board | substrate, and the manufacturing method of a board | substrate using the same can be provided.

[Copolymer]
The polishing liquid composition of the present invention contains a copolymer having a structural unit represented by formula (I) and a structural unit represented by formula (II) as a roll-off inhibitor. In the copolymer, a structural unit represented by the following formula (I) serves as a hydrophilic group, and a structural unit represented by the following formula (II) serves as a hydrophobic group. In the copolymer, the addition of the structural unit represented by the following formula (I) and the structural unit represented by the following formula (II) may be random, block, or graft, and a combination thereof. It may be. The mechanism of roll-off reduction by the copolymer is not clear, but the copolymer is adsorbed to the polishing pad via the hydrophobic structural unit, and the hydrophilic structural unit in the copolymer adsorbed to the polishing pad is polished. By reducing the frictional force between the pad and abrasive, the amount of abrasive held in the deformed part of the polishing pad is reduced compared to other parts, and as a result, the effect of reducing roll-off is manifested. It is guessed.

In the formula (I), R ¹ is a hydrogen atom or a methyl group, and among them, a methyl group is preferable because the stability of the structural unit and the copolymer can be further improved. R ² is an alkyl group having 1 to 4 carbon atoms, preferably 1 to 3 carbon atoms, and more preferably a methyl group.

In the formula (I), AO is an alkylene oxide group having 1 to 8 carbon atoms, preferably 2 to 3 carbon atoms, and more preferably an ethylene oxide group. The proportion of ethylene oxide groups in (AO) _n is preferably 80 mol% or more, more preferably 90 mol% or more, and even more preferably 100 mol%. In the formula (I), n, which is the total average added mole number of AO, is 6 to 300 from the viewpoint of suppressing roll-off, suppressing foaming of the polishing composition, and improving the dispersibility of the copolymer. It is a number, and since roll-off can be further suppressed and foaming of the polishing composition can be further suppressed, it is preferably 9 or more, more preferably 23 or more, still more preferably 60 or more, and particularly preferably 90 or more. Further, n is preferably 250 or less, more preferably 200 or less, still more preferably 170 or less, and particularly preferably 150 or less, because the dispersibility of the copolymer in the polishing composition can be further improved. Therefore, n is preferably a number of 9 to 250, more preferably a number of 23 to 200, still more preferably a number of 60 to 170, and particularly preferably a number of 90 to 150. In the formula (I), p is 0 or 1. From the viewpoints of suppression of roll-off and suppression of foamability of the polishing composition, and improvement of the dispersibility of the copolymer, p is preferably 1.

  Specific examples of the monomer for forming the structural unit represented by the formula (I) include methoxypolyethylene glycol methacrylate (PEGMA), methoxypolyethylene glycol acrylate, and the like as the monomer when p = 1. In the case of 0, examples of the monomer include polyethylene glycol allyl ether.

In the formula (II), R ³ is a hydrogen atom or a methyl group, and among them, a methyl group is preferable because the stability of the structural unit and the copolymer can be further improved. X is an oxygen atom or an NH group, and among them, an oxygen atom is preferable because roll-off can be further suppressed. R ⁴ is a linear or branched alkylene group having 1 to 4 carbon atoms, and among them, an alkylene group having 2 to 4 carbon atoms is preferable because the stability of the structural unit and the copolymer can be further improved. R ⁵ is a linear or branched alkyl group having 1 to 30 carbon atoms, and among these, an alkyl group having 1 to 2 carbon atoms is preferable from the viewpoint of roll-off. m is the total average number of added moles of dimethylsiloxane and is a number from 0 to 30, but from the viewpoint of roll-off, a number from 1 to 20 is more preferable, and a number from 1 to 12 is even more preferable. A methyl group and a polydimethylsiloxane group can be bonded to the silicon atom bonded to R ⁴ , and h and 3-h represent the number of methyl groups and polydimethylsiloxane groups bonded to the silicon atom, respectively. , H is a number from 0 to 2, and h is preferably 2 from the viewpoint of roll-off.

  Specific examples of the monomer for forming the structural unit represented by the formula (II) include, for example, oxypropyldimethylpolysiloxane (meth) acrylate, oxypropylmethyldi (trimethylsiloxy) silane (meth) acrylate, and oxypropyl. And tris (trimethylsiloxy) silane (meth) acrylate.

  Specific examples of the copolymer include methoxypolyethylene glycol methacrylate-oxypropyldimethylpolysiloxane methacrylate copolymer, methoxypolyethylene glycol methacrylate-oxypropylmethyldi (trimethylsiloxy) silane methacrylate copolymer, methoxypolyethylene glycol methacrylate-oxy. And propyltris (trimethylsiloxy) silane methacrylate copolymer. These copolymers may be used alone or in combination of two or more.

  The total proportion of the structural units represented by the formulas (I) and (II) in all the structural units constituting the copolymer is preferably 60% by weight or more, and 70% by weight or more from the viewpoint of roll-off reduction. Is more preferable, and 80% by weight or more is even more preferable.

  The weight ratio (weight of hydrophilic group / weight of hydrophobic group) of the structural unit (hydrophilic group) represented by formula (I) and the structural unit represented by formula (II) in the copolymer is hydrophobic to some extent. By increasing the proportion of the group, the frictional force between the polishing pad and the polishing material can be further reduced, and roll-off can be further suppressed. Therefore, it is preferably 97.5 / 2.5 or less, more preferably 92.5 / 7. 5 or less, more preferably 85/15 or less. Further, the weight ratio is preferably 25/75 or more, more preferably 40/60 or more, and further preferably 65/35 or more, since the dispersibility of the copolymer in the polishing composition can be further improved. Therefore, the weight ratio of the hydrophilic group to the hydrophobic group in the copolymer is preferably 25/75 to 97.5 / 2.5, more preferably 40/60 to 92.5 / 7.5, still more preferably 65/35 to 85/15. The weight ratio of each structural unit in the copolymer can be calculated by measuring a deuterium-substituted dimethyl sulfoxide solution containing 1% by weight of the copolymer using a proton nuclear magnetic resonance spectrum.

  The weight average molecular weight of the copolymer is preferably 5000 or more, more preferably 20,000 or more, still more preferably 60,000 or more, and even more preferably 90,000 or more, because roll-off can be further suppressed. The weight average molecular weight of the copolymer is preferably 500,000 or less, more preferably 450,000 or less, and still more preferably 400,000 or less, because the dispersibility of the polymer in the polishing composition can be further improved. Accordingly, the weight average molecular weight of the copolymer is preferably 5,000 to 500,000, more preferably 20,000 to 500,000, still more preferably 20,000 to 450,000, still more preferably 60,000 to 450,000, and even more preferably. Is 60,000 to 400,000, and more preferably 90,000 to 400,000. In addition, the said weight average molecular weight can be measured by the average molecular weight of polystyrene conversion by the gel permeation chromatography (GPC) method of the following conditions.

<GPC conditions>
Column: α-M-α-M (manufactured by Tosoh Corporation)
Eluent: 60 mmol / L H ₃ PO ₄ , 50 mmol / L LiBr / DMF
Flow rate: 1.0 mL / min
Column temperature: 40 ° C
Detection: RI
Reference material: Polystyrene

  The copolymer may contain other monomers in addition to the monomers for forming the structural units represented by the formulas (I) and (II). By containing other monomers, the dispersibility of the copolymer in the polishing composition can be further improved. Examples of the other monomers include acrylic acid, methyl acrylate, ethyl acrylate, methacrylic acid (MAA), methyl methacrylate, ethyl methacrylate, acrylamide, dimethylacrylamide (DMAA), dimethylaminopropylacrylamide (DMAPAA), and methacrylic acid. Dimethylaminoethyl (DMAEMA), hydroxyethyl methacrylate (HEMA), trimethylammonioethyl methacrylate chloride (QDM), methacryloyloxyethyldimethylammonium ethyl sulfate (MOEDES), N, N-dimethylaminopropyl methacrylamide (DMAPMAAm), acrylamide Methylpropanesulfonic acid (AMPS), sodium styrenesulfonate (NaSS), styrene, vinyl acetate And the like. The content of other monomers in the copolymer is preferably 40% by weight or less, more preferably 30% by weight or less, and still more preferably 20% by weight or less from the viewpoint of roll-off characteristics.

  Specific examples of the copolymer containing the other monomer include methoxypolyethylene glycol methacrylate-oxypropyldimethylpolysiloxane methacrylate-methacrylic acid copolymer, methoxypolyethylene glycol methacrylate-oxypropyldimethylpolysiloxane methacrylate-dimethylaminoethyl methacrylate copolymer. A polymer etc. are mentioned. These copolymers may be used alone or in combination of two or more.

  The content of the copolymer in the polishing liquid composition of the present invention is preferably 3% by weight or less, more preferably 2% by weight or less, and still more preferably 1% by weight since foaming of the polishing liquid composition can be further suppressed. % Or less. Moreover, since roll-off can be further suppressed, the content of the copolymer is preferably 0.001% by weight or more, more preferably 0.003% by weight or more, and further preferably 0.005% by weight or more. Therefore, the content of the copolymer is preferably 0.001 to 3% by weight, more preferably 0.003 to 2% by weight, and still more preferably 0.005 to 1% by weight.

[Abrasive]
Examples of the abrasive used in the polishing composition of the present invention include abrasives generally used for polishing. Examples of the abrasive include metal or metalloid carbides, nitrides, oxides and borides, and diamond. The metal element or metalloid element belongs to 2A, 2B, 3A, 3B, 4A, 4B, 5A, 6A, 7A or 8A in the long-period periodic table. Specific examples of the abrasive include α-alumina, intermediate alumina, alumina sol, silicon carbide, magnesium oxide, zinc oxide, cerium oxide, zirconium oxide, colloidal silica, and fumed silica, which are used alone. Alternatively, two or more types may be used in combination as necessary. In the case of rough polishing a Ni-P plated aluminum alloy substrate, the combination of α-alumina and intermediate alumina (especially θ alumina) can further improve the polishing rate, further prevent surface defects and reduce surface roughness. Therefore, it is preferable. In the case of polishing a glass substrate, cerium oxide, alumina, and silica are preferable.

  Since the average primary particle diameter of the abrasive can further suppress roll-off, it is preferably 0.01 to 3 μm, more preferably 0.02 to 3 μm, and still more preferably 0.03 to 3 μm. In addition, when primary particles are aggregated to form secondary particles, the polishing rate can be further improved, and roll-off can be further suppressed. Therefore, the average secondary particle size is 0.02 to 3 μm. More preferably, it is 0.05-3 micrometers, More preferably, it is 0.1-3 micrometers. The average primary particle size is an enlarged photograph of an abrasive taken with a scanning electron microscope (preferably 3000 to 30000 times) or an enlarged photograph of an abrasive taken with a transmission electron microscope (preferably 10,000 to 30000 times). It can be obtained by image analysis. The average secondary particle diameter can be obtained as a volume average particle diameter using a laser beam diffraction method.

  The specific gravity of the abrasive is preferably 2 to 6, because it further improves the dispersibility of the abrasive in the polishing composition, and further facilitates the supply to the polishing apparatus and the recovery of the polishing composition. Preferably it is 2-5, More preferably, it is 2-4.

  The content of the abrasive in the polishing liquid composition of the present invention is preferably 0.05% by weight or more, more preferably 0.1% by weight because the polishing rate can be further improved and the waviness of the substrate surface can be further reduced. % Or more, more preferably 0.5% by weight or more, and particularly preferably 1% by weight or more. Further, the content of the abrasive is preferably 40% by weight or less, more preferably 35% by weight or less, and still more preferably 30% by weight because roll-off can be further suppressed and the quality of the obtained substrate surface can be further improved. Hereinafter, it is particularly preferably 25% by weight or less. Therefore, the content of the abrasive is preferably 0.05 to 40% by weight, more preferably 0.1 to 35% by weight, still more preferably 0.5 to 30% by weight, and particularly preferably 1 to 25% by weight. It is.

[acid]
The polishing liquid composition of the present invention may further contain an acid, and both inorganic and organic acids can be used as the acid. Examples of the inorganic acid include nitric acid, nitrous acid, sulfuric acid, sulfurous acid, amidosulfuric acid, phosphoric acid, polyphosphoric acid, and phosphonic acid. Examples of the organic acid include glycolic acid, oxalic acid, succinic acid, maleic acid, fumaric acid, itaconic acid, malic acid, tartaric acid, citric acid, phosphonohydroxyacetic acid, hydroxyethylidene-1,1-diphosphonic acid, phosphonobutane Examples include tricarboxylic acid and ethylenediaminetetramethylenephosphonic acid. Among these, sulfuric acid, sulfurous acid, amidosulfuric acid, phosphoric acid, polyphosphoric acid, phosphonic acid, oxalic acid, succinic acid, itaconic acid, malic acid, citric acid, hydroxy, from the viewpoint of further improving the polishing rate and further reducing waviness. Ethylidene-1,1-diphosphonic acid and ethylenediaminetetramethylenephosphonic acid are preferred, and sulfuric acid, phosphoric acid, polyphosphoric acid, itaconic acid and citric acid are more preferred. These acids may be used alone or in combination of two or more. Further, these acids may be present in the polishing composition in the form of a partially or completely neutralized salt.

  The acid content in the polishing composition of the present invention is preferably 0.05% by weight or more, more preferably 0.075% by weight or more, and still more preferably 0.1% by weight because the polishing rate can be further improved. That's it. The acid content is preferably 10% by weight or less, more preferably 7.5% by weight or less, and still more preferably 5% by weight or less because corrosion of the polishing apparatus can be further suppressed. Therefore, the content of the acid is preferably 0.05 to 10% by weight, more preferably 0.075 to 7.5% by weight, and still more preferably 0.1 to 5% by weight.

[Oxidant]
The polishing composition of the present invention may further contain an oxidizing agent, and examples of the oxidizing agent include peroxides, metal peroxo acids or salts thereof, and oxygen acids or salts thereof. In addition, the oxidizing agent is roughly classified into an inorganic oxidizing agent and an organic oxidizing agent according to the structure, but the polishing rate can be further improved and handling such as availability and solubility in water becomes easier. Therefore, an inorganic oxidizing agent is preferable. Examples of the inorganic oxidant include hydrogen peroxide, alkali metal or alkaline earth metal peroxide, peroxocarbonate, peroxosulfuric acid or salt thereof, peroxophosphoric acid or salt thereof, peroxoborate, peroxochromate Permanganate, halogen-containing oxyacid salt, inorganic acid metal salt, and the like. Examples of the alkali metal or alkaline earth metal peroxide include sodium peroxide, potassium peroxide, calcium peroxide, barium peroxide, magnesium peroxide and the like. Examples of the peroxo carbonate include sodium peroxo carbonate and Examples of the peroxosulfuric acid or salt thereof include ammonium peroxodisulfate, sodium peroxodisulfate, potassium peroxodisulfate, and peroxomonosulfuric acid. Examples thereof include sodium phosphate, potassium peroxophosphate and ammonium peroxophosphate. Examples of the peroxoborate include sodium peroxoborate and potassium peroxoborate, and the peroxochromate. To the sodium potassium peroxo chromic acid and peroxo chromic acid and the like. Examples of the permanganate include sodium permanganate and potassium permanganate. Examples of the oxyacid salt containing halogen include sodium perchlorate, potassium perchlorate, sodium hypochlorite, and periodate. Examples include sodium acid, potassium periodate, sodium iodate, and potassium iodate, and examples of the inorganic acid metal salt include iron (III) chloride and iron (III) sulfate. On the other hand, examples of the organic oxidizing agent include percarboxylic acids, peroxides, and organic acid iron (III) salts. Examples of the percarboxylic acids include peracetic acid, performic acid, perbenzoic acid, and the like. Examples of the peroxide include t-butyl peroxide and cumene peroxide. The organic acid iron (III ) Examples of the salt include iron (III) citrate. Among these, hydrogen peroxide, sodium peroxoborate, sodium iodate, and potassium iodate are preferable. These oxidizing agents may be used alone or in combination of two or more.

  The content of the oxidizing agent in the polishing composition of the present invention is preferably 0.002% by weight or more, more preferably 0, because the polishing rate can be further improved, and waviness and substrate contamination can be further reduced. 0.005% by weight or more, more preferably 0.007% by weight or more, and particularly preferably 0.01% by weight or more. In addition, the content of the oxidizing agent is preferably 20% by weight or less, more preferably 15% by weight or less, and even more preferably 10% by weight because roll-off can be further suppressed and the quality of the obtained substrate surface can be further improved. Hereinafter, it is particularly preferably 5% by weight or less. Therefore, the content of the oxidizing agent is preferably 0.002 to 20% by weight, more preferably 0.005 to 15% by weight, still more preferably 0.007 to 10% by weight, and particularly preferably 0.01 to 5%. % By weight.

[Medium]
As a medium used in the polishing composition of the present invention, water can be used, and examples of the water include distilled water, ion exchange water, pure water, and ultrapure water. The content of the medium in the polishing liquid composition of the present invention is preferably 55% by weight or more, more preferably 75% by weight or more, and still more preferably 85% by weight or more because the handling of the polishing liquid composition becomes easier. Particularly preferably, it is 90% by weight or more. Further, the content of the medium is preferably 99.8% by weight or less, more preferably 99.3% by weight or less, and still more preferably 98.% or less because the polishing rate can be further improved and roll-off can be further suppressed. 8% by weight or less. Therefore, the content of the medium is preferably 55 to 99.8% by weight, more preferably 75 to 99.3% by weight, still more preferably 85 to 98.8% by weight, and particularly preferably 90 to 98.8% by weight. %.

  The pH of the polishing liquid composition of the present invention can be appropriately determined according to the material of the substrate to be polished, etc., but it becomes easier to clean the substrate to be polished, and further prevents corrosion of the processing machine. Since it is possible to work more safely, 1 or more is preferable, 1.2 or more is more preferable, and 1.4 or more is more preferable. In general, the oxidizing agent is more stable in the case of being acidic, so that it is preferably 12 or less, more preferably 11 or less, still more preferably 10 or less. Therefore, the pH of the polishing composition is preferably 1 to 12, more preferably 1.2 to 11, and still more preferably 1.4 to 10. When the substrate to be polished is a metal material, the pH is preferably less than 7, more preferably 6 or less, further preferably 5 or less, and particularly preferably 4 or less from the viewpoint of improving the polishing rate.

  The polishing composition of the present invention may further contain a bactericidal agent, an antibacterial agent, a thickener, a dispersant, a rust inhibitor, a basic substance, a pH adjuster, and the like. The content of these components in the polishing composition is preferably 10% by weight or less, more preferably 8% by weight or less, and still more preferably 6% by weight or less from the viewpoint of polishing characteristics.

  The polishing liquid composition of the present invention can be used in any polishing step in a substrate manufacturing method, and is particularly suitable for use in a rough polishing step in a substrate manufacturing method.

(Method for preparing polishing liquid composition)
The method for preparing the polishing composition of the present invention is not limited at all, and can be prepared, for example, by mixing the copolymer and the abrasive in an appropriate aqueous medium. The dispersion of the abrasive is not particularly limited, and can be performed using a homomixer, a homogenizer, an ultrasonic disperser, a stirrer such as a wet ball mill, or the like.

  The pH of the polishing composition may be adjusted to a predetermined pH after mixing the components, or may be adjusted before mixing. The pH can be adjusted with a pH adjusting agent.

(Manufacturing method of the substrate of the present invention)
The substrate manufacturing method of the present invention is a method for manufacturing a substrate including a step of polishing a substrate to be polished using the polishing composition of the present invention. Since the polishing process using the polishing composition of the present invention is included, according to the method for manufacturing a substrate of the present invention, a substrate in which roll-off is suppressed can be manufactured. In addition, it is characterized by including the process of grind | polishing a to-be-polished board | substrate using the polishing liquid composition of this invention, Other conditions, processes, etc. are not restrict | limited at all. As one embodiment of the substrate manufacturing method of the present invention, a hard disk substrate manufacturing method can be mentioned.

  In the polishing step, the polishing liquid composition of the present invention is supplied to the polishing surface of the substrate to be polished, the polishing pad is brought into contact with the polishing surface, and the polishing pad and the substrate to be polished are moved while applying a predetermined pressure (load). Etc. In addition, the said grinding | polishing can be performed with a conventionally well-known grinding | polishing apparatus.

  The polishing composition may be used as it is, or diluted if it is a concentrated solution. In the case of diluting the concentrated liquid, the dilution ratio is not particularly limited, and can be appropriately determined according to the concentration of each component in the concentrated liquid (abrasive content, etc.), polishing conditions, and the like.

  The polishing pad is not particularly limited, and a conventionally known polishing pad can be used. Examples of the material for the polishing pad include organic polymers, and examples of the organic polymer include polyurethane. The shape of the polishing pad is preferably a nonwoven fabric.

  The polishing load means the pressure of the surface plate applied to the polishing surface of the substrate to be polished during polishing. The polishing load in the production method of the present invention is preferably 50 kPa or less, more preferably 40 kPa or less, and even more preferably 30 kPa or less because roll-off can be further suppressed. The polishing load is preferably 3 kPa or more, more preferably 5 kPa or more, and even more preferably 7 kPa or more because productivity can be further improved. Therefore, the polishing load is preferably 3 to 50 kPa, more preferably 5 to 40 kPa, and even more preferably 7 to 30 kPa. The polishing load can be adjusted by applying air pressure or weight to the surface plate or the substrate.

The supply rate of the polishing composition is preferably 0.25 mL / min or less per 1 cm ^{2 of the} substrate to be polished, more preferably 0.2 mL / min or less, and further preferably 0.15 mL / min from the viewpoint of low cost. It is as follows. The supply rate is preferably 0.01 mL / min or more per 1 cm ^{2 of the} substrate to be polished, more preferably 0.025 mL / min or more, and even more preferably 0.05 mL / min or more because the polishing rate can be further improved. is there. Accordingly, the supply rate is preferably 0.01 to 0.25 mL / min per 1 cm ^{2 of the} substrate to be polished, more preferably 0.025 to 0.2 mL / min, and still more preferably 0.05 to 0.15 mL / min. It is.

  The substrate to be polished is not particularly limited, but a substrate for recording disk used as a recording medium, for example, a substrate to be polished for manufacturing a substrate for hard disk is preferable. Specific examples of substrates to be polished for hard disk substrates and the like include substrates obtained by applying Ni-P plating to aluminum alloys, glass, glassy carbon, and the like. The substrate etc. which coat | covered the metal compound by plating, vapor deposition, etc. may be sufficient.

(Semiconductor substrate polishing method, semiconductor device manufacturing method)
The polishing composition of the present invention can reduce roll-off even when used for polishing a semiconductor substrate. Therefore, the present invention, as one aspect thereof, relates to a method for polishing a semiconductor substrate. Examples of the semiconductor substrate include silicon wafers, and other materials such as elemental semiconductors such as Si or Ge, compound semiconductors such as GaAs, InP, or CdS, mixed crystal semiconductors such as InGaAs, HgCdTe, and the like. A substrate is mentioned.

  The polishing liquid composition of the present invention can also be applied to a polishing process performed in the process of manufacturing a semiconductor device. The polishing step includes chemical mechanical polishing (CMP). Accordingly, the present invention relates to a method of manufacturing a semiconductor device as another aspect. The manufacturing method of the semiconductor device includes a thin film forming step in which one main surface on a semiconductor substrate forms a crocodile thin film, and a concavo-convex surface forming step in which the thin film semiconductor substrate forms a concavo-convex pattern on the opposite surface of the crocodile surface. And a polishing step of polishing the concavo-convex surface using the polishing liquid composition of the present embodiment. You may perform a thin film formation process in multiple times as needed.

  As a thin film formed in a thin film formation process, conductor layers, such as an insulating layer, a metal layer, a semiconductor layer, etc. are mentioned, for example. Examples of the material included in the insulating layer include silicon oxide, silicon nitride, and polysilicon. Examples of the method for forming the uneven surface include a conventionally known lithography method. In the lithography method, photoresist application, exposure, development, etching, photoresist removal, and the like are performed in this order.

  As an example, copolymer 1 was synthesized as described below, and a polishing composition was prepared as described below using the synthesized copolymer 1. And the to-be-polished substrate was grind | polished using the prepared said polishing liquid composition, and the roll-off of the said board | substrate after grinding | polishing was evaluated.

1. Synthesis of Copolymer 1 The synthesis of copolymer 1 will be specifically described below.

  In order to form a structural unit represented by the formula (II) using methoxypolyethylene glycol (9 mol) methacrylate (PEGMA (EO9)) as a monomer for forming the structural unit represented by the formula (I). Copolymer 1 was synthesized using oxypropyldimethylsiloxane methacrylate (m = 9, h = 2, trade name FM-0711, manufactured by Chisso Corporation) as a monomer, and methacrylic acid as another monomer. Specifically, 55 g of (PEGMA (EO9)), 40 g of (FM-0711), 5 g of methacrylic acid, 100 g of methyl ethyl ketone as a polymerization solvent, and a polymerization initiator (trade name V-65, manufactured by Wako Pure Chemical Industries, Ltd.) 1.0 g was put into a reactor equipped with a stirrer, a reflux condenser, a thermometer, and a nitrogen introduction tube, subjected to a polymerization reaction at 65 ° C. for 6 hours, and then dried to obtain a copolymer 1. . The weight average molecular weight of the obtained copolymer 1 was 72,000. Further, the proportion of (PEGMA (EO9)) in the copolymer 1 was 55% by weight, the proportion of (FM-0711) was 40% by weight, and the proportion of methacrylic acid was 5% by weight.

2. Preparation of polishing liquid composition Copolymer 1, prepared α-alumina particles (average secondary particle size 0.30 μm), θ-alumina particles (average secondary particle size 0.22 μm), sulfuric acid (98% product), citric acid Then, ammonium sulfate and hydrogen peroxide (30% by weight, manufactured by Asahi Denka Co., Ltd.) were mixed with water to prepare polishing liquid compositions of Examples. The content of the copolymer 1 in the polishing composition is 0.02% by weight, and the content of the alumina particles (total amount of α-alumina particles and θ-alumina particles) is 3.84% by weight, The pH was 1.6. The content of other components was 0.62% by weight sulfuric acid, 0.97% by weight citric acid, 0.52% by weight ammonium sulfate and 0.58% by weight hydrogen peroxide.

3. Measuring method (Method for measuring weight average molecular weight)
The copolymer is dissolved in chloroform, GPC (gel permeation chromatography (α-M-α-M (manufactured by Tosoh Corporation)), developing solvent: 60 mmol / L H ₃ PO ₄ , 50 mmol / L LiBr / DMF) Was used to measure the weight average molecular weight in terms of standard polystyrene.
(Method for measuring the proportion of each structural unit in the copolymer)
The copolymer was dissolved in deuterium-substituted dimethyl sulfoxide (copolymer concentration: 1% by weight) and measured using a proton nuclear magnetic resonance spectrum.
(Measurement method of average secondary particle diameter of alumina particles)
The average secondary particle diameter of the α and θ alumina particles was calculated from the volume average particle diameter using a laser diffraction method.

4). Polishing Method Using the prepared polishing liquid composition, the substrate was polished for 4 minutes under the following polishing conditions (single-side polishing amount 2.2 μm).
(Substrate to be polished)
The substrate to be polished was an aluminum alloy substrate plated with Ni-P. The substrate to be polished had a thickness of 1.27 mm and a diameter of 95 mm.
(Polishing conditions)
Polishing tester: Double-side polishing machine (9B type double-side polishing machine, manufactured by Speed Farm Co., Ltd.)
Polishing pad: 1.04 mm thick, average pore diameter 43 μm (FILWEL)
Surface plate rotation speed: 45 rpm
Polishing load: 7.7 kPa (set value)
Polishing liquid supply amount: 100 mL / min (0.076 mL) / (cm ² · min)
Polishing time: Number of substrates loaded for 4 minutes: 10

5. Evaluation of Roll-Off Regarding the substrate after polishing, 0.5 mm roll-off and 1.0-3.0 Valley roll-off were measured under the following conditions. The obtained results are shown in Tables 1 and 2 together with the copolymer composition. The measurement was performed by selecting one of the 10 substrates loaded, performing 3 points (arbitrary) on the substrate, and taking the average value of the 3 points as the measurement result. The value of 0.5 mm roll-off indicates that the larger the value is, the higher the end of the substrate is, and it can be said that roll-off is suppressed. Further, the value of 1.0-3.0 Valley roll-off indicates that the smaller the value is (the larger the absolute value is), the higher the edge of the substrate is, and the roll-off is suppressed. It can be said that it was done.
(Roll-off measurement)
The roll-off measurement was performed under the following measurement conditions for the following 0.5 mm roll-off and 1.0-3.0 Valley roll-off.
0.5 mm roll-off As shown in FIG. 1, the substrate surfaces of 3.0 mm and 4.0 mm from the end of the substrate are point A and point B, respectively, and extension lines connecting point A and point B are shown. Let it be the first reference line. The distance between this first reference line and the point C of the substrate surface 0.5 mm from the endmost part of the substrate was measured, and the shortest one was defined as 0.5 mm roll-off (nm) (hereinafter referred to as “0.5 mm”). Say).
1.0-3.0Valley roll-off As shown in FIG. 2, the substrate surface of 1.0 mm and 3.0 mm from the substrate end is defined as D point and E point, respectively. A straight line connecting the two is defined as a second reference line. The distance from the second reference line to the substrate surface at right angles was measured, and the longest one was defined as 1.0-3.0 Valley roll-off (nm) (hereinafter also referred to as “1.0-3.0 Valley”). .
(Measurement condition)
Measuring instrument: Brand name New View 5032 (manufactured by Zygo)
Lens: 2.5x zoom: 0.5x Analysis software: Product name Zygo Metro Pro (manufactured by Zygo)

<Comparative Examples 1-4>
In Comparative Example 1, a polishing composition was prepared in the same manner as in the above example except that the copolymer 1 was not used. Moreover, in Comparative Examples 2-4, the polishing liquid composition was prepared like the said Example except having used the component shown in following Table 1 as an alternative component of the copolymer 1 of the said Example. And the to-be-polished substrate was grind | polished like the said Example except having used the said polishing liquid composition of Comparative Examples 1-4, and the roll-off of the said board | substrate after grinding | polishing was evaluated. The obtained results are shown in Table 1 below. In addition, the copolymer 2 of the comparative example 2 was obtained like the said Example except having used 90 g of methoxy polyethyleneglycol (90 mol) methacrylate (PEGMA (EO90)) and 10 g of methacrylic acid as a monomer. The weight average molecular weight of the obtained copolymer 2 was 187,000. Moreover, the ratio of (PEGMA (EO90)) in the copolymer 2 was 90 weight%, and the ratio of methacrylic acid was 10 weight%.

  As shown in Table 1 above, the substrate polished using the polishing liquid composition of the example has a 0.5 mm roll-off value compared to the substrate polished using the polishing liquid composition of Comparative Examples 1 to 4. And the value of 1.0-3.0 Valley roll-off was small (absolute value was large). In other words, it can be said that roll-off could be suppressed by using the polishing composition of the example.

  From the above results, according to the polishing composition of the present invention comprising a copolymer having the structural unit represented by the formula (I) and the structural unit represented by the formula (II), roll-off is performed. It was shown that it can be suppressed.

  According to the polishing composition of the present invention, roll-off can be suppressed in the substrate polishing step. Therefore, the polishing composition of the present invention is useful in the production of various substrates, and is particularly useful in the production of hard disk substrates.

FIG. 1 is a cross-sectional view showing a location where (0.5 mm roll-off) measurement was performed in an example of the present invention. FIG. 2 is a cross-sectional view showing a place where (1.0-3.0 Valley roll-off) measurement was performed in the example of the present invention.

Claims (8)

A polishing liquid composition comprising a copolymer having a structural unit represented by the following formula (I) and a structural unit represented by the following formula (II) and an abrasive.

[In the formula (I), R ¹ is a hydrogen atom or a methyl group, R ² is an alkyl group having 1 to 4 carbon atoms, AO is an alkylene oxide group having 1 to 8 carbon atoms, and p is 0. Or n, where n is the total average added mole number of AO and is a number from 6 to 300;
In the formula (II), R ³ is a hydrogen atom or a methyl group, R ⁴ is a linear or branched alkylene group having 1 to ⁴ carbon atoms, and R ⁵ is a linear or branched group having 1 to 30 carbon atoms. It is a branched alkyl group, X is an oxygen atom or NH, m is the total average added mole number of dimethylsiloxane, and is a number from 0 to 30, and h is a number from 0 to 2. ] The polishing composition according to claim 1, wherein in the formula (II), X is an oxygen atom. The polishing composition according to claim 1 or 2, wherein h is 2 in the formula (II). The weight ratio of the structural unit represented by the formula (I) to the structural unit represented by the formula (II) in the copolymer (weight of the structural unit represented by the formula (I) / expressed by the formula (II) The polishing composition according to any one of claims 1 to 3, wherein the weight of the structural unit is 25/75 to 97.5 / 2.5. The polishing composition according to any one of claims 1 to 4, wherein the copolymer has a weight average molecular weight of 5,000 to 500,000. The polishing composition according to any one of claims 1 to 5, wherein the abrasive is alumina. The manufacturing method of a board | substrate including the process of grind | polishing a to-be-polished board | substrate using the polishing liquid composition as described in any one of Claim 1 to 6. The method for manufacturing a substrate according to claim 7, wherein the substrate is a substrate for a hard disk.