JP2009090631A - Original printing plate of lithographic printing plate and method for manufacturing printing plate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an original printing plate of a lithographic printing plate capable of performing an image recording by an infrared laser, excellent in on-machine developability or gum developabilities and printing wear, and with furthermore improved printing stain, and to provide a method for manufacturing the printing plate using it. <P>SOLUTION: The original printing plate of the lithographic printing plate is characterized in that it has an intermediate layer and an image recording layer in this order on an aluminum support, and in that a compound having an amino group and a functional group performing an interaction with the aluminum support is incorporated in the intermediate layer or the image recording layer. It is preferable that the intermediate layer comprises a polymer having a substrate adsorbing group, a polymerizable group and a hydrophilic group. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

  The present invention relates to a lithographic printing plate precursor. More specifically, the present invention relates to a lithographic printing plate precursor capable of image recording with a laser and capable of on-press development or gum development.

In general, a lithographic printing plate comprises an oleophilic image area that receives ink in the printing process and a hydrophilic non-image area that receives dampening water. Lithographic printing utilizes the property that water and oil-based inks repel each other, so that the oleophilic image area of the lithographic printing plate is the ink receiving area and the hydrophilic non-image area is dampened with the water receiving area (ink non-receiving area). As described above, a difference in ink adhesion is caused on the surface of a lithographic printing plate, and after ink is applied only to an image portion, the ink is transferred to a printing medium such as paper and printed.
In order to produce this lithographic printing plate, conventionally, a lithographic printing plate precursor (PS plate) in which an oleophilic photosensitive resin layer (image recording layer) is provided on a hydrophilic support has been widely used. Usually, after exposing the lithographic printing plate precursor through an original image such as a lithographic film, the image recording layer corresponding to the image portion remains, and the unnecessary image recording layer corresponding to the non-image portion is removed with an alkaline developer. Alternatively, the lithographic printing plate is obtained by dissolving and removing with an organic solvent-containing developer and exposing the surface of the hydrophilic support to form a non-image area.

  In the conventional plate making process of a lithographic printing plate precursor, a step of dissolving and removing an unnecessary image recording layer with a developer or the like is required after exposure. However, such additional wet processing is unnecessary or Simplification is cited as one of the issues. In particular, in recent years, disposal of waste liquids discharged with wet processing has become a major concern for the entire industry due to consideration for the global environment, and therefore, the demand for solving the above-mentioned problems has become stronger.

On the other hand, as one simple plate-making method, an image recording layer that can remove an unnecessary portion of the image recording layer in a normal printing process is used. After exposure, the image recording layer is unnecessary on a printing machine. A method called on-press development has been proposed in which a portion is removed to obtain a lithographic printing plate.
As a specific method of on-press development, for example, a method of using a lithographic printing plate precursor having an image recording layer that can be dissolved or dispersed in an fountain solution, an ink solvent, or an emulsion of a fountain solution and an ink. , Method of mechanically removing the image recording layer by contact with rollers or blankets of a printing press, cohesion of the image recording layer or adhesion between the image recording layer and the support by penetration of dampening water, ink solvent, etc. There is a method in which after the force is weakened, the image recording layer is mechanically removed by contact with rollers or a blanket.
Further, as another simple plate-making method, the removal of the unnecessary portion of the image recording layer in the development processing step is replaced with a conventional highly alkaline developer, and a finishing gum conventionally applied after alkali development. A method called gum development performed with a solution has also been proposed.
In the present invention, unless otherwise specified, the “development process step” refers to using a device other than a printing press (usually an automatic developing machine) and bringing a liquid (usually an alkaline developer) into contact therewith. Refers to the process of removing the image recording layer of the unexposed portion of the lithographic printing plate precursor and exposing the surface of the hydrophilic support, and “on-press development” refers to a liquid (usually printing ink) using a printing press. And / or dampening water) to remove the image recording layer of the unexposed portion of the lithographic printing plate precursor and to expose the surface of the hydrophilic support.
Of the processes through the “development process step”, development using a gum solution as a developer is particularly referred to as “gum development”.

  On the other hand, in recent years, digitization technology for electronically processing, storing, and outputting image information by a computer has become widespread, and various new image output methods corresponding to such digitization technology will be put into practical use. It is becoming. Along with this, digitized image information is carried by high-convergence radiation such as laser light, and the lithographic printing plate precursor is scanned and exposed with that light, directly without using a lithographic film. Computer-to-plate technology for manufacturing is attracting attention. Therefore, obtaining a lithographic printing plate precursor adapted to such a technique is one of the important technical issues.

In the above-described simplification, drying, or no processing of the plate-making work, the image recording layer after exposure is not fixed by the development processing, and thus has photosensitivity and may be covered before printing. Therefore, an image recording layer and a light source that can be handled in a bright room or under a yellow light are required.
As such a laser light source, a solid-state laser such as a semiconductor laser and a YAG laser that emits infrared light having a wavelength of 760 to 1200 nm is extremely useful because a high-power and small-sized laser can be obtained at low cost. . A UV laser can also be used.

As an on-press development type lithographic printing plate precursor for image recording with an infrared laser, for example, Patent Document 1 discloses an image forming layer (image recording layer) in which hydrophobic thermoplastic polymer particles are dispersed in a hydrophilic binder. A lithographic printing plate precursor provided with a layer) on a hydrophilic support is described. In this Patent Document 1, the above lithographic printing plate precursor is exposed by an infrared laser, and the hydrophobic thermoplastic polymer particles are coalesced by heat to form an image, which is then mounted on a cylinder of a printing press and moistened. It is described that it is possible to perform on-press development with water and / or ink.
Such a method of forming an image by merging by simple thermal fusion of fine particles has a problem that the image strength is extremely weak and the printing durability is insufficient, although it exhibits good on-press developability. .

Patent Documents 2 and 3 describe lithographic printing plate precursors containing microcapsules encapsulating a polymerizable compound on a hydrophilic support.
Furthermore, Patent Document 4 describes a lithographic printing plate precursor in which a photosensitive layer containing an infrared absorber, a radical polymerization initiator, and a polymerizable compound is provided on a support.

  The method using such a polymerization reaction has a feature that the image strength is relatively good because the chemical bond density of the image portion is higher than that of the image portion formed by thermal fusion of polymer fine particles. In order to satisfy the printability, on-press development property, and resistance to stains during printing (stainability), it is necessary to provide an intermediate layer between the support and the image recording layer.

It is generally known that a water-soluble resin imparted with hydrophilicity is used for such an intermediate layer. Patent Document 5 discloses a polymer having a substrate-adsorbing group, a polymerizable group, and a hydrophilic group. An on-press development type lithographic printing plate precursor provided with an intermediate layer is described.
However, in the on-press development type and gum development type lithographic printing plate precursors, even when these intermediate layers are provided, the non-image area is still not sufficiently soiled, especially in the form of circular dots of several μm to several thousand μm. Dirt (hereinafter, referred to as “hot dirt”) may occur, and further improvement is necessary.
Japanese Patent No. 2938397 JP 2001-277740 A JP 2001-277742 A JP 2002-287334 A Japanese Patent Laid-Open No. 2005-125749

  The present invention has been made in view of the above prior art, and can record an image with an infrared laser, is excellent in on-machine developability or gum developability, and printing durability, and has stain resistance, in particular, spot dirt. An object of the present invention is to provide an improved lithographic printing plate precursor and a plate making method using the same.

1. It has an intermediate layer and an image recording layer in this order on an aluminum support, and the intermediate layer or image recording layer contains a compound having an amino group and a functional group that interacts with the aluminum support in one molecule. A lithographic printing plate precursor.
2. The above-mentioned 1 characterized in that an intermediate layer and an image recording layer are provided in this order on an aluminum support, and a compound having an amino group and a functional group that interacts with the aluminum support in one molecule is contained in the intermediate layer. The lithographic printing plate precursor described.
3. Functional group that acts aluminum support and mutual, trialkoxysilyl group, an onium group, or a phenolic hydroxyl group, a carboxyl _{group, -SO 3 H, -OSO 3 H} , -PO 3 H 2, -OPO 3 H 2, 3. The lithographic printing plate precursor as described in 1 or 2 above, which is an acid group selected from —CONHSO ₂ —, —SO ₂ NHSO ₂ — and COCH ₂ CO— or a metal salt thereof.
4). 4. The compound according to any one of 1 to 3 above, wherein the compound having an amino group and a functional group that interacts with the aluminum support in one molecule is a compound represented by the following general formula (1): A lithographic printing plate precursor.

(In the formula, R represents a hydrogen atom or a group optionally selected from an alkyl group, an alkenyl group, an alkynyl group, an aryl group, and a heterocyclic group, and X ⁻ represents an arbitrary anion. To express.)

  5). 4. The compound according to any one of 1 to 3 above, wherein the compound having an amino group and a functional group that interacts with the aluminum support in one molecule is a compound represented by the following general formula (2): Lithographic printing plate precursor.

(In the general formula (2), W is .n representing the n-valent organic linking group .X representing an integer of 2 or more ^- representing the any anion.)

  6). 4. The compound according to any one of 1 to 3 above, wherein the compound having an amino group and a functional group that interacts with the aluminum support in one molecule is a compound represented by the following general formula (3): Lithographic printing plate precursor.

(In General Formula (3), W represents a divalent organic linking group, R ₁ represents an organic residue, n represents an integer of 2 to 3, and m represents a number satisfying n × m = 2. .)

7). 7. The lithographic printing plate precursor as described in any one of 1 to 6 above, wherein the intermediate layer contains a polymer having a substrate adsorptive group, a polymerizable group, and a hydrophilic group. The lithographic printing plate precursor as described in any one of 1 to 7 above, wherein the image recording layer comprises (A) an infrared absorber, (B) a polymerization initiator, and (C) a polymerizable compound. .
9. The lithographic printing plate precursor as described in any one of 1 to 8 above, wherein the image recording layer further comprises (D) a binder polymer.
10. The lithographic printing plate precursor as described in any one of 1 to 9 above, wherein the image recording layer further contains (E) a microcapsule or a microgel.
11. The image recording layer is an image recording layer capable of forming an image by supplying printing ink and fountain solution on a printing machine after exposure to remove unexposed portions, or developing with a gum solution after exposure. The lithographic printing plate precursor as described in any one of 1 to 10 above.
12 The lithographic printing plate precursor as described in 11 above is exposed imagewise, and printing ink and fountain solution are supplied on the printing machine without any development processing being performed on the exposed lithographic printing plate precursor. And a step of removing unexposed portions of the lithographic printing plate precursor by starting printing.
13. 12. An imagewise exposure of the lithographic printing plate precursor according to claim 11 and a step of removing an unexposed portion of the lithographic printing plate precursor by developing the exposed lithographic printing plate precursor with a gum solution. A plate making method of a lithographic printing plate precursor characterized by the above.

  According to the present invention, a lithographic printing plate precursor capable of recording an image with an infrared laser, having excellent on-machine developability or gum developability, printing durability, and improved stain resistance, in particular, fouling, and use thereof We can provide a plate making method.

[Lithographic printing plate precursor]
The lithographic printing plate precursor according to the invention has an intermediate layer and an image recording layer in this order on an aluminum support, and an intermediate layer or image containing a compound having an amino group and a functional group that interacts with the aluminum support in one molecule. It is contained in the recording layer.
In the lithographic printing plate precursor according to the invention, the intermediate layer preferably contains a polymer having a substrate adsorptive group, a polymerizable group and a hydrophilic group. In the lithographic printing plate precursor according to the invention, the image recording layer preferably contains (A) an infrared absorber, (B) a polymerization initiator, and (C) a polymerizable compound. Furthermore, the lithographic printing plate precursor according to the invention preferably has a protective layer on the image recording layer.
Hereinafter, the lithographic printing plate precursor according to the invention will be described in detail.

<Compound having an amino group and a functional group that interacts with the aluminum support in one molecule>
The compound having an amino group and a functional group that interacts with the aluminum support in one molecule of the present invention (hereinafter referred to as a specific compound) is contained in the intermediate layer or the image recording layer. Particularly preferably, it is contained in the intermediate layer. The specific compound of the present invention may have a plurality of functional groups that interact with an amino group and an aluminum support in one molecule.

  Here, the aluminum support means an aluminum support that has been subjected to an anodizing treatment and / or a hydrophilization treatment, which will be described later, and the interacting functional group is a metal or metal oxidation present on the aluminum support. And functional groups that interact with each other, such as covalent bonds, ionic bonds, hydrogen bonds, polar interactions, van der Waals interactions.

The amino group of the specific compound of the present invention is preferably a secondary amino group or a tertiary amino group, more preferably a tertiary amino group. Specific examples of functional groups that interact with the aluminum support include trialkoxysilyl groups, onium groups, or phenolic hydroxyl groups, carboxyl groups, —SO ₃ H, —OSO ₃ H, —PO ₃ H ₂ , —OPO. Examples include an acid group selected from ₃ H ₂ , —CONHSO ₂ —, —SO ₂ NHSO ₂ — and COCH ₂ CO— or a metal salt thereof, among which a trialkoxysilyl group, an onium group, —PO ₃ H ₂ or a salt thereof Metal salts and OPO ₃ H ₂ or metal salts thereof are more preferred.

The trialkoxysilyl group is preferably a trialkoxysilyl group having 1 to 18 carbon atoms, particularly preferably a trimethoxysilyl group or a triethoxysilyl group. As the onium group, an ammonium group and a phosphonium group are preferable, and an ammonium group is most preferable. Preferred counter anions of the onium group include halide ions (for example, chlorine ions, bromine ions), sulfonate ions (for example, methanesulfonate ions, p-toluenesulfonate ions), carboxylate ions (for example, acetate ions, propionate ions). ), Hydroxide ions, monoalkyl sulfate ions (monomethyl sulfate ions, monoethyl sulfate ions), PF ₆ ⁻ , BF ₄ ⁻ , Etc. Among these, PF ₆ ⁻ , BF ₄ ⁻ , sulfonate ions, and carboxylate ions are particularly preferable.

  Preferred specific examples of the ammonium group and phosphonium group are shown below.

  Among these, as the specific compound of the present invention, a compound represented by the following general formula (1) is particularly preferable.

R represents a hydrogen atom or a group optionally selected from an alkyl group, an alkenyl group, an alkynyl group, an aryl group and a heterocyclic group, and X ⁻ represents an arbitrary anion.
Examples of the substituent include amino group, acyl group, carboxyl group, hydroxyl group, substituted hydroxyl group, thiol group, substituted thiol group, silyl group, nitro group, cyano group, alkyl group, alkenyl group, aryl group, heterocyclic group, A sulfo group, a substituted sulfonyl group, a sulfonato group, a substituted sulfinyl group, a phosphono group, a substituted phosphono group, a phosphonato group, a substituted phosphonato group, and the like can be mentioned. If it can be introduced, it may further have a substituent.

  Examples of the alkyl group represented by R include linear, branched or cyclic alkyl groups having 1 to 20 carbon atoms. Among these, a linear alkyl group having 1 to 12 carbon atoms, a branched alkyl group having 3 to 12 carbon atoms, and a cyclic alkyl group having 5 to 10 carbon atoms are more preferable. Specific examples thereof include methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, hexadecyl group, octadecyl group. , Eicosyl group, isopropyl group, isobutyl group, s-butyl group, t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group And 2-norbornyl group.

  When the alkyl group represented by R has a substituent (that is, when it is a substituted alkyl group), the preferred range of the number of carbon atoms in the alkyl portion of the substituted alkyl group is the same as that of the alkyl group.

  Preferable specific examples of the substituted alkyl group represented by R include chloromethyl group, bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxymethyl group, methoxycarbonylmethyl group, isopropoxymethyl group, butoxymethyl group, s-butoxybutyl group, methoxyethoxyethyl group, allyloxymethyl group, phenoxymethyl group, acetyloxymethyl group, methylthiomethyl group, tolylthiomethyl group, pyridylmethyl group, tetramethylpiperidinylmethyl group, N-acetyltetra Methylpiperidinylmethyl group, trimethylsilylmethyl group, methoxyethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-cyclohexylcarbamoyloxy Til group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, allyloxycarbonylbutyl group, Chlorophenoxycarbonylmethyl group,

Carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl-N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group Sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group, N-methyl-N- (phosphonophenyl) sulfamoyl Octyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobutyl group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxy Propyl group, phosphona Oxybutyl group, a benzyl group, phenethyl group, alpha-methylbenzyl group, 1-methyl-1-phenylethyl group, p- methylbenzyl, and the like.

  Examples of the substituent that can be introduced into the alkyl group represented by R include the monovalent substituents composed of the nonmetallic atoms exemplified below in addition to the substituents described in the description of the substituted alkyl group. It is done. Preferred examples including the above-described substituent include a halogen atom (—F, —Br, —Cl, —I), hydroxyl group, alkoxy group, aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryl. Dithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group, N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, aryl Sulfoxy group, acylthio group, acylamino group, -Alkylacylamino group, N-arylacylamino group, ureido group, N'-alkylureido group, N ', N'-dialkylureido group, N'-arylureido group, N', N'-diarylureido group, N′-alkyl-N′-arylureido group, N-alkylureido group, N-arylureido group, N′-alkyl-N-alkylureido group, N′-alkyl-N-arylureido group, N ′, N '-Dialkyl-N-alkylureido group, N', N'-dialkyl-N-arylureido group, N'-aryl-N-alkylureido group, N'-aryl-N-arylureido group, N ', N '-Diaryl-N-alkylureido group, N', N'-diaryl-N-arylureido group, N'-alkyl-N'-aryl-N- Rukiruureido group, N'- alkyl -N'- aryl -N- arylureido group,

Alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl-N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N -Aryloxycarbonylamino group, formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N- di arylcarbamoyl group, N- alkyl -N- arylcarbamoyl group, an alkylsulfinyl group, an arylsulfinyl group, an alkylsulfonyl group, an arylsulfonyl group, a sulfo group (-SO 3 _H) and its conjugated base group (scan Phonato group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N-alkylsulfinamoyl group, N, N-dialkylsulfinaimoyl group, N-arylsulfinamoyl group, N, N-diaryl Sulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N-arylsulfamoyl group, N, N- Diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group,

A phosphono group (—PO ₃ H ₂ ) and its conjugate base group (referred to as phosphonato group), a dialkylphosphono group (—PO ₃ (alkyl) ₂ ) “alkyl = alkyl group, the same shall apply hereinafter”, a diarylphosphono group ( -PO _{3 (aryl) 2)} "aryl = aryl group, hereinafter the" alkylaryl phosphono group _{(-PO 3 (alkyl) (aryl} )), monoalkyl phosphono group _(-PO 3 H _(alkyl)) and Its conjugate base group (referred to as alkylphosphonate group), monoarylphosphono group (—PO ₃ H (aryl)) and its conjugate base group (referred to as arylphosphonate group), phosphonooxy group (—OPO ₃ H) ₂₎ and its conjugated base group (referred to as phosphonatooxy group), dialkylphosphono group _(-OPO 3 H _(alkyl) 2) Diarylphosphono group _{(-OPO 3 (aryl) 2)} , alkylaryl phosphono group _{(-OPO 3 (alkyl) (aryl} )), monoalkyl phosphono group _(-OPO 3 H _(alkyl)) and its Conjugated base group (referred to as alkylphosphonatoxy group), monoarylphosphonooxy group (—OPO ₃ H (aryl)) and its conjugate base group (referred to as arylphosphonatoxy group), cyano group, nitro group Aryl group, alkenyl group, alkynyl group, heterocyclic group, silyl group, and the like.

Specific examples of the alkyl moiety in the substituent that can be introduced into the alkyl group represented by R are the same as those in the case where R described above is a substituted alkyl group, and the preferred range is also the same.
Specific examples of the aryl moiety in the substituent that can be introduced into the alkyl group represented by R include phenyl, biphenyl, naphthyl, tolyl, xylyl, mesityl, cumenyl, chlorophenyl, bromophenyl. Group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylaminophenyl group, dimethylaminophenyl Group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, cyanophenyl group, sulfophenyl group A sulfophenyl group, phosphono phenyl group, phosphonium Hona preparative phenyl group, and the like.

  Examples of the alkenyl group represented by R include alkenyl groups having 2 to 20 carbon atoms. Among these, an alkenyl group having 2 to 10 carbon atoms is preferable, and an alkenyl group having 2 to 8 carbon atoms is more preferable. The alkenyl group may further have a substituent. Examples of the substituent that can be introduced include a halogen atom, an alkyl group, a substituted alkyl group, an aryl group, and a substituted aryl group. The halogen atom is a linear or branched chain having 1 to 10 carbon atoms. A cyclic alkyl group is preferred. Specific examples of the alkenyl group include, for example, vinyl group, allyl group, 2-methylallyl group, 1-propenyl group, 1-butenyl group, 2-butenyl group, cinnamyl group, 1-pentenyl group, 1-hexenyl group, 1 -Octenyl group, 1-methyl-1-propenyl group, 2-methyl-1-propenyl group, 2-methyl-1-propenylmethyl group, 2-methyl-1-butenyl group, 2-phenyl-1-ethenyl group, A 2-chloro-1-ethenyl group, and the like.

  Examples of the alkynyl group represented by R include alkynyl groups having 2 to 20 carbon atoms. Among these, an alkynyl group having 2 to 10 carbon atoms is preferable, and an alkynyl group having 2 to 8 carbon atoms is more preferable. Specific examples thereof include ethynyl group, 1-propynyl group, 2-propynyl group, 1-butynyl group, 2-butynyl group, 3-butynyl group, phenylethynyl group, trimethylsilylethynyl group and the like.

  Examples of the aryl group represented by R include a benzene ring, a group in which 2 to 3 benzene rings form a condensed ring, and a group in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Specific examples include a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, and a fluorenyl group. Among these, a phenyl group and a naphthyl group are more preferable.

  In addition, the aryl group represented by R may have a substituent on the carbon atom forming the ring, and as such a substituent, a monovalent substituent composed of a nonmetallic atom is included. Can be mentioned. Preferable examples of the substituent to be introduced include those described above in the description of the alkyl group, the substituted alkyl group, and the substituent in the substituted alkyl group.

  The heterocyclic group represented by R is preferably a 3- to 8-membered heterocyclic group, more preferably a 3- to 6-membered heterocyclic group containing a nitrogen atom, an oxygen atom or a sulfur atom, and a nitrogen atom. Further, a 5- to 6-membered heterocyclic group containing an oxygen atom or a sulfur atom is more preferable. Specifically, pyrrole ring group, furan ring group, thiophene ring group, benzopyrrole ring group, benzofuran ring group, benzothiophene ring group, pyrazole ring group, isoxazole ring group, isothiazole ring group, indazole ring group, benzoiso Xazole ring group, benzoisothiazole ring group, imidazole ring group, oxazole ring group, thiazole ring group, benzimidazole ring group, benzoxazole ring group, benzothiazole ring group, pyridine ring group, quinoline ring group, isoquinoline ring group, Pyridazine ring group, pyrimidine ring group, pyrazine ring group, phthalazine ring group, quinazoline ring group, quinoxaline ring group, acylidin ring group, phenanthridine ring group, carbazole ring group, purine ring group, pyran ring group, piperidine ring group, Piperazine ring group, morpholine ring group, indole ring group, indolizine ring group, Road ring group, a cinnoline ring group, an acridine ring group, a phenothiazine ring group, a tetrazole ring group, a triazine ring group, and the like.

  In addition, the heterocyclic group represented by R may have a substituent on the carbon atom forming the ring, and as such a substituent, a monovalent substituent composed of a nonmetallic atom. Is mentioned. Preferable examples of the substituent to be introduced include those described above in the description of the alkyl group, the substituted alkyl group, and the substituent in the substituted alkyl group.

Preferred embodiments of R are listed below.
R is preferably a hydrogen atom or an alkyl group which may have a substituent having 1 to 20 carbon atoms, more preferably a hydrogen atom or an alkyl group which may have a substituent having 1 to 5 carbon atoms, a hydrogen atom or An alkyl group which may have a substituent having 1 to 3 carbon atoms is more preferable.

X < ^- > is an arbitrary anion and is preferably an acid anion. Specific examples include a halogen atom anion, BF ₄ ⁻ , BCl ₄ ⁻ , ZnCl ₄ ⁻ , SbCl ₆ ⁻ , FeCl ₄ ⁻ , GaCl ₄ ⁻ , GaBr ₄ ⁻ , AlI ₄ ⁻ , AlCl ₄ ⁻ , SbF ₆ ⁻ , CF ₃ SO ₃ ⁻ , PF ₆ ⁻ , BPh ₄ ⁻ , benzenesulfonic acid anion, p-toluenesulfonic acid anion, naphthalene-1-sulfonic acid, condensed polynuclear sulfonic acid anion such as anthracene-1-sulfonic acid, anthraquinonesulfonic acid anion , N-cyclohexylamide sulfate anion, N-phenylamidesulfate anion, sulfo group-containing dye (anion having a sulfo group and a chromophoric group), and the like, but are not limited thereto.

The compound represented by the general formula (1) includes a compound in which a plurality of cation skeleton portions are bonded via R in the general formula (1), and two or more cation skeleton portions are contained in one molecule. Such compounds are also preferably used.
As a compound having two or more cationic skeleton portions in one molecule, a compound represented by the following general formula (2) is particularly preferable.

In general formula (2), W represents an n-valent organic linking group. n represents an integer of 2 or more. X ⁻ represents an arbitrary anion.

X ^- represents the general formula (1) X ^- as synonymous. The n-valent organic linking group represented by W is a polyvalent organic group composed of non-metallic atoms, from 1 to 60 carbon atoms, from 0 to 10 nitrogen atoms, from 0 Preferred are those composed of up to 50 oxygen atoms, 1 to 100 hydrogen atoms, and 0 to 20 sulfur atoms. More specific examples include organic linking groups constituted by combining the following structures (linking group unit structures) singly or in combination.

  The organic linking group represented by W may further have a substituent. Examples of the substituent that can be introduced include a halogen atom, a hydroxyl group, a carboxyl group, a sulfonate group, a nitro group, a cyano group, and an amide group. Amino group, alkyl group, alkenyl group, alkynyl group, aryl group, substituted oxy group, substituted sulfonyl group, substituted carbonyl group, substituted sulfinyl group, sulfo group, phosphono group, phosphonato group, silyl group, heterocyclic group, etc. Can be mentioned.

  As the compound having two or more cationic skeleton portions in one molecule, a compound represented by the following general formula (3) is also preferable.

In general formula (3), W represents a divalent organic linking group, and R ₁ represents an organic residue. n represents an integer of 2 to 3, and m represents a number satisfying n × m = 2.
Examples of the organic residue represented by R ₁ include aliphatic hydrocarbon, aromatic hydrocarbon residue, and heterocyclic compound residue having 20 or less carbon atoms. Of these, aromatic hydrocarbon residues are preferable, and divalent or trivalent residues of benzene and naphthalene are particularly preferable. Particularly preferred specific examples of the anion moiety containing these residues include 1,5-naphthalenedisulfonate anion, 2,6-naphthalenedisulfonate anion, 2,7-naphthalenedisulfonate anion, 2-naphthol-6,8. -Disulfonic acid anion, 1,3,6-naphthalene trisulfonic acid anion, 1,3-benzenedisulfonic acid anion, etc. are mentioned. W is synonymous with W in the case of representing a divalent organic linking group in the general formula (2).

Furthermore, as a compound represented by General formula (1), the compound by which the cation frame | skeleton part is introduce | transduced into the polymer side chain via R is also mentioned as a preferable aspect.
As the compound in which the cationic skeleton portion is introduced into the polymer side chain, a compound represented by the following general formula (4) is particularly preferable.

In general formula (4), L represents a single bond or a divalent organic linking group. m represents an integer of 1 or more, and X ⁻ represents an anion. P represents a polymer main chain.

  Although there is no restriction | limiting in particular in the polymer principal chain represented by P, Preferably, a poly (meth) acrylate chain, a polystyrene chain, a polyvinyl chain, a polyurethane chain, a polyacetal chain etc. are mentioned. Among these, from the viewpoint of printing durability when applied to the recording layer of a lithographic printing plate precursor, a poly (meth) acrylate chain, a polystyrene chain, and the like are particularly preferable.

  The divalent organic linking group represented by L is a divalent organic group composed of nonmetallic atoms, including 1 to 60 carbon atoms, 0 to 10 nitrogen atoms, 0 To 50 oxygen atoms, 1 to 100 hydrogen atoms, and 0 to 20 sulfur atoms are preferred. As a more specific example, the organic coupling group comprised by the above-mentioned coupling group unit structure individually or in combination can be mentioned.

  The organic linking group represented by L may further have a substituent. Examples of the substituent that can be introduced include a halogen atom, a hydroxyl group, a carboxyl group, a sulfonate group, a nitro group, a cyano group, and an amide group. Amino group, alkyl group, alkenyl group, alkynyl group, aryl group, substituted oxy group, substituted sulfonyl group, substituted carbonyl group, substituted sulfinyl group, sulfo group, phosphono group, phosphonato group, silyl group, heterocyclic group, etc. Can be mentioned.

m is an integer greater than or equal to 1, 1-6 are preferable and 1-3 are more preferable.
X ⁻ in the general formula (4) has the same meaning as X ⁻ in the general formula (1), and the preferred range is also the same.

  Specific examples of the compounds represented by the general formula (1) to the general formula (4) are given below, but the present invention is not limited thereto.

  The content of the specific compound of the present invention in the intermediate layer is preferably 10 to 90% by mass, more preferably 20 to 80% by mass, and most preferably 25 to 75% by mass of the solid content of the intermediate layer. The content in the image recording layer is preferably from 0.1 to 90 mass%, more preferably from 0.2 to 80 mass%, most preferably from 0.3 to 70 mass%, based on the solid content of the image recording layer. In this range, a good dirt improving effect can be obtained.

(Middle layer)
For the intermediate layer provided between the image recording layer and the support in the lithographic printing plate precursor according to the invention, conventionally known intermediate layer compounds can be used in addition to the specific compound. Examples of such intermediate layer compounds include silane coupling agents having addition-polymerizable ethylenic double bond reactive groups described in JP-A-10-282679, and JP-A-2-304441. The phosphorus compound etc. which have the ethylenic double bond reactive group of description are mentioned suitably.
The most preferable compound includes a polymer for an intermediate layer obtained by copolymerizing a monomer having an adsorptive group, a monomer having a hydrophilic group, and a monomer having a crosslinkable group.
The coating amount (solid content) of the intermediate layer is preferably 0.1 to 100 mg / m ² and more preferably 1 to 50 mg / m ² from the viewpoint of achieving both printing durability and resistance to stains.
By such an intermediate layer, the soiling property (especially pot soiling) is improved, and the on-machine developability or gum developability, printing durability and soiling property can be satisfied. Since the intermediate layer easily causes peeling of the image recording layer in the unexposed area, the on-press developability or gum developability is improved. In addition, in the case of infrared laser exposure, since the intermediate layer functions as a heat insulating layer, the heat generated by the exposure does not diffuse to the support and can be used efficiently, so that the sensitivity can be increased. is there. Further, after printing, it remains on the substrate and is hydrophilic, so that stain resistance is maintained.
In addition, it is possible to suppress the residual film due to the dark polymerization reaction that occurs at the substrate interface with time, and to prevent pot-like dirt.

<Interlayer polymer having substrate adsorptive group, polymerizable group, and hydrophilic group>
An essential component of the polymer for the intermediate layer is an adsorbing group on the surface of the hydrophilic support. The presence or absence of adsorptivity on the surface of the hydrophilic support can be determined by the following method, for example.
A coating night is prepared by dissolving the test compound in a readily soluble solvent, and the coating night is coated and dried on the support so that the coating amount after drying is 30 mg / m ² . Next, the support on which the test compound is applied is sufficiently washed with an easily soluble solvent, and then the residual amount of the test compound that has not been removed by washing is measured to calculate the amount of adsorption of the support. Here, the measurement of the remaining amount may be performed by directly quantifying the amount of the remaining compound or by quantifying the amount of the test compound dissolved in the cleaning liquid. The compound can be quantified by, for example, fluorescent X-ray measurement, reflection spectral absorbance measurement, liquid chromatography measurement and the like. A compound having a support adsorptivity is a compound that remains at 1 mg / m ² or more even after the washing treatment as described above.

The adsorptive group on the surface of the hydrophilic support is a substance (for example, metal, metal oxide) or a functional group (for example, hydroxyl group) existing on the surface of the hydrophilic support and a chemical bond (for example, ionic bond, hydrogen). Bond, coordination bond, bond by intermolecular force). The adsorptive group is preferably an acid group or a cationic group.
The acid group preferably has an acid dissociation constant (pKa) of 7 or less. Examples of the acid group include a phenolic hydroxyl group, a carboxyl _{group, -SO 3 H, -OSO 3 H} , -PO 3 H 2, -OPO 3 H 2, -CONHSO 2 -, - SO 2 NHSO 2 - and COCH ₂ COCH ₃ is included. Of these, OPO ₃ H ₂ and PO ₃ H ₂ are particularly preferable. These acid groups may be metal salts.
The cationic group is preferably an onium group. Examples of the onium group include an ammonium group, a phosphonium group, an arsonium group, a stibonium group, an oxonium group, a sulfonium group, a selenonium group, a stannonium group, and an iodonium group. An ammonium group, a phosphonium group and a sulfonium group are preferred, an ammonium group and a phosphonium group are more preferred, and an ammonium group is most preferred.

  Particularly preferred examples of the monomer having an adsorptive group include compounds represented by the following formula (U1) or (U2).

In the above formula, R ¹ , R ² and R ³ are each independently a hydrogen atom, a halogen atom or an alkyl group having 1 to 6 carbon atoms. R ¹ , R ² and R ³ are each independently preferably a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atoms. More preferred is a hydrogen atom or a methyl group. R ² and R ³ are particularly preferably a hydrogen atom. Z is a functional group that adsorbs to the surface of the hydrophilic support.

  In the above formula, X is an oxygen atom (—O—) or imino (—NH—). X is more preferably an oxygen atom. L is a divalent linking group. L is a divalent aliphatic group (alkylene group, substituted alkylene group, alkenylene group, substituted alkenylene group, alkynylene group, substituted alkynylene group), divalent aromatic group (arylene group, substituted arylene group) or divalent A heterocyclic group, or an oxygen atom (—O—), a sulfur atom (—S—), an imino (—NH—), a substituted imino (—NR—, R is an aliphatic group, an aromatic group; Or a heterocyclic group) or a combination with carbonyl (—CO—).

The aliphatic group may have a cyclic structure or a branched structure. The number of carbon atoms in the aliphatic group is preferably 1 to 20, more preferably 1 to 15, and most preferably 1 to 10. The aliphatic group is preferably a saturated aliphatic group rather than an unsaturated aliphatic group. The aliphatic group may have a substituent. Examples of the substituent include a halogen atom, a hydroxyl group, an aromatic group, and a heterocyclic group.
The number of carbon atoms in the aromatic group is preferably 6 to 20, more preferably 6 to 15, and most preferably 6 to 10. The aromatic group may have a substituent. Examples of the substituent include a halogen atom, a hydroxyl group, an aliphatic group, an aromatic group, and a heterocyclic group.
The heterocyclic group preferably has a 5-membered or 6-membered ring as the heterocycle. The hetero ring may be condensed with another hetero ring, an aliphatic ring or an aromatic ring. The heterocyclic group may have a substituent. Examples of substituents include halogen atoms, hydroxyl groups, oxo groups (═O), thioxo groups (═S), imino groups (═NH), substituted imino groups (═N—R, R is an aliphatic group, aromatic Group or heterocyclic group), aliphatic group, aromatic group and heterocyclic group.

Among the above, L is preferably a divalent linking group containing a plurality of polyoxyalkylene structures. The polyoxyalkylene structure is more preferably a polyoxyethylene structure. In other words, L preferably contains — (OCH ₂ CH ₂ ) _n — (n is an integer of 2 or more).

  In the formula (U2), Y is a carbon atom or a nitrogen atom. When Y is a nitrogen atom and L is connected to Y to form a pyridinium group, Z itself is adsorbable, so Z is not essential, and Z may be a hydrogen atom.

  Examples of typical compounds represented by formula (U1) or (U2) are shown below.

  Examples of the hydrophilic group of the intermediate layer polymer that can be used in the present invention include a hydroxyl group, a carboxyl group, a carboxylate group, a hydroxyethyl group, a polyoxyethyl group, a hydroxypropyl group, a polyoxypropyl group, and an amino group. Aminoethyl group, aminopropyl group, ammonium group, amide group, carboxymethyl group, sulfo group, phosphoric acid group and the like are preferable. Among these, a monomer having a sulfo group exhibiting high hydrophilicity is preferable. Specific examples of the monomer having a sulfo group include methallyloxybenzenesulfonic acid, allyloxybenzenesulfonic acid, allylsulfonic acid, vinylsulfonic acid, p-styrenesulfonic acid, methallylsulfonic acid, acrylamide t-butylsulfonic acid, Examples include 2-acrylamido-2-methylpropanesulfonic acid, (3-acryloyloxypropyl) butylsulfonic acid sodium salt, and amine salt. Of these, 2-acrylamido-2-methylpropanesulfonic acid sodium salt is preferred in view of hydrophilic performance and handling of synthesis.

  The water-soluble polymer for the intermediate layer of the present invention preferably has a crosslinkable group. The crosslinkable group can improve the adhesion with the image area. In order to make the polymer for the intermediate layer crosslinkable, a crosslinkable functional group such as an ethylenically unsaturated bond is introduced into the side chain of the polymer, or a substituent having a counter charge with the polar substituent of the polymer. And a compound having an ethylenically unsaturated bond can be introduced by forming a salt structure.

  Examples of polymers having an ethylenically unsaturated bond in the side chain of the molecule are polymers of esters or amides of acrylic acid or methacrylic acid, where the ester or amide residue (R of -COOR or CONHR) is ethylene. Examples thereof include polymers having a polymerizable unsaturated bond.

Examples of the residue (the R) having an ethylenically unsaturated _{bond, - (CH 2) n CR} 1 = CR 2 R 3, - (CH 2 O) n CH 2 CR 1 = CR 2 R 3, - _{(CH 2 CH 2 O) n} CH 2 CR 1 = CR 2 R 3, - (CH 2) n NH-CO-O-CH 2 CR 1 = CR 2 R 3, - (CH 2) n -O-CO -CR ₁ = _CR 2 _{R 3,} and _(CH 2 CH ₂ O) in ₂ -X _(wherein, R 1 to R ₃ are each a hydrogen atom, a halogen atom or an alkyl group having 1 to 20 carbon atoms, an aryl group, Represents an alkoxy group or an aryloxy group, and R ₁ and R ₂ or R ₃ may combine with each other to form a ring, n represents an integer of 1 to 10. X represents dicyclopentadienyl. Represents a residue).
Specific examples of the ester residue include —CH ₂ CH═CH ₂ (described in JP-B-7-21633), —CH ₂ CH ₂ O—CH ₂ CH═CH ₂ , —CH ₂ C. _{(CH 3) = CH 2,} -CH 2 CH = CH-C 6 H 5, -CH 2 CH 2 OCOCH = CH-C 6 H 5, -CH 2 CH 2 NHCOO-CH 2 CH = CH 2, and CH ₂ CH ₂ O—X (wherein X represents a dicyclopentadienyl residue).
Specific examples of the amide residue include —CH ₂ CH═CH ₂ , —CH ₂ CH ₂ O—Y (wherein Y represents a cyclohexene residue), —CH ₂ CH ₂ OCO—CH═CH _2. Is mentioned.
As the monomer having a crosslinkable group of the polymer for the intermediate layer, an ester or amide of acrylic acid or methacrylic acid having the above crosslinkable group is suitable.

  The content of the crosslinkable group in the intermediate layer polymer (content of unsaturated double bond capable of radical polymerization by iodometric titration) is preferably 0.1 to 10.0 mmol, more preferably 1. 0 to 7.0 mmol, most preferably 2.0 to 5.5 mmol. Within this range, both good sensitivity and dirtiness and good storage stability can be obtained.

The polymer for the intermediate layer preferably has a mass average molar mass of 5000 or more, more preferably 10,000 to 300,000, and the number average molar mass is preferably 1000 or more, 2000 to 25 More preferably, it is 10,000. The polydispersity (mass average molar mass / number average molar mass) is preferably 1.1 to 10.
The polymer for the intermediate layer may be any of a random polymer, a block polymer, a graft polymer, etc., but is preferably a random polymer.

The intermediate layer polymer may be used alone or in combination of two or more, and the amine may be used alone or in combination of two or more. The intermediate layer coating solution is obtained by dissolving the above intermediate layer polymer in an organic solvent (for example, methanol, ethanol, acetone, methyl ethyl ketone, etc.) and / or water. The intermediate layer coating solution may contain an infrared absorber.
Various known methods can be used as a method of applying the intermediate layer coating solution to the support. Examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.

  The intermediate layer polymer may contain two or more kinds in the intermediate layer. The amount of the intermediate layer polymer added to the intermediate layer is preferably 10 to 90 mass%, more preferably 20 to 80 mass%, and most preferably 25 to 75 mass%, based on the solid content of the intermediate layer.

(Image recording layer)
The image forming elements and components of the image recording layer of the present invention will be described in detail.
The imaging element preferably usable is at least one of (a) an imaging element utilizing polymerization, and (b) an imaging element utilizing thermal fusion or thermal reaction of a hydrophobized precursor. (A) As an image-forming element utilizing polymerization, an element containing (A) an infrared absorber, (B) a polymerization initiator, and (C) a polymerizable compound, and capable of image recording with an infrared laser is preferable. . In addition, (b) as an image forming element utilizing thermal fusion or thermal reaction of a hydrophobized precursor, it contains (A) an infrared absorber and (D) a hydrophobized precursor, and image recording can be performed with an infrared laser. What is possible is preferred. Further, (D) a hydrophobizing precursor may be additionally contained in the image forming element (a).
Furthermore, the image recording layer of the present invention can contain other components in addition to these elements as required.
Hereinafter, formation of these image recording layer constituent components and the image recording layer will be described.

<(A) Infrared absorber>
When forming an image of the lithographic printing plate precursor according to the present invention using a laser emitting infrared rays of 760 to 1200 nm as a light source, it is usually essential to use an infrared absorber. The infrared absorber has a function of converting the absorbed infrared rays into heat and a function of being excited by infrared rays and transferring electrons / energy to a polymerization initiator (radical generator) described later. The infrared absorber used in the present invention is a dye or pigment having an absorption maximum at a wavelength of 760 to 1200 nm.

As the dye, commercially available dyes and known dyes described in documents such as “Dye Handbook” (edited by the Society for Synthetic Organic Chemistry, published in 1970) can be used. Specifically, dyes such as azo dyes, metal complex azo dyes, pyrazolone azo dyes, naphthoquinone dyes, anthraquinone dyes, phthalocyanine dyes, carbonium dyes, quinoneimine dyes, methine dyes, cyanine dyes, squarylium dyes, pyrylium salts, metal thiolate complexes, etc. Is mentioned.
Preferred dyes include, for example, cyanine dyes described in JP-A-58-125246, JP-A-59-84356, JP-A-60-78787, JP-A-58-173696, The methine dyes described in JP-A-58-181690 and JP-A-58-194595, JP-A-58-112793, JP-A-58-224793, JP-A-59-48187, Naphthoquinone dyes described in JP-A-59-73996, JP-A-60-52940, JP-A-60-63744, and the like, squarylium dyes described in JP-A-58-112792, and the like; And cyanine dyes described in British Patent No. 434,875.

In addition, a near infrared absorption sensitizer described in US Pat. No. 5,156,938 is also preferably used, and a substituted arylbenzo (thio) described in US Pat. No. 3,881,924 is also suitable. ) Pyrylium salt, trimethine thiapyrylium salt described in JP-A-57-142645 (US Pat. No. 4,327,169), JP-A-58-181051, 58-220143, 59- No. 41363, No. 59-84248, No. 59-84249, No. 59-146063, No. 59-146061, and Pyrlium compounds described in JP-A-59-216146. And pentamethine thiopyrylium salts described in US Pat. No. 4,283,475, and Japanese Patent Publication Nos. 5-13514 and 5-19702. Pyrylium compounds shown also preferably used. Another preferable example of the dye includes near infrared absorbing dyes described as the formulas (I) and (II) in US Pat. No. 4,756,993.
Other preferable examples of the infrared absorbing dye of the present invention include specific indolenine cyanine dyes described in JP-A-2002-278057 as exemplified below.

  Among these dyes, cyanine dyes, squarylium dyes, pyrylium salts, nickel thiolate complexes, and indolenine cyanine dyes are preferable. Further, cyanine dyes and indolenine cyanine dyes are preferable, and one particularly preferable example is a cyanine dye represented by the following general formula (i).

In formula (i), X ¹ represents a hydrogen atom, a halogen atom, -NPh _2, X ² -L ¹ or a group represented by the following structural formulas. Here, X ² represents an oxygen atom, a nitrogen atom, or a sulfur atom, and L ¹ represents a hydrocarbon group having 1 to 12 carbon atoms, an aromatic ring having a hetero atom, or 1 to 1 carbon atom containing a hetero atom. 12 hydrocarbon groups are shown. In addition, a hetero atom here shows a nitrogen atom, a sulfur atom, an oxygen atom, a halogen atom, and a selenium atom. R ^a represents a hydrogen atom, an alkyl group, an aryl group, a substituted or unsubstituted amino group, a substituted amino group and a halogen atom, X a ^_- is Z _a to be described later ^_- is the same definition.

R ¹ and R ² each independently represent a hydrocarbon group having 1 to 12 carbon atoms. From the storage stability of the recording layer coating solution, R ¹ and R ² are preferably hydrocarbon groups having 2 or more carbon atoms, and R ¹ and R ² are bonded to each other to form a 5-membered ring or It is particularly preferable that a 6-membered ring is formed.

Ar ¹ and Ar ² may be the same or different and each represents an aromatic hydrocarbon group which may have a substituent. Preferred aromatic hydrocarbon groups include a benzene ring and a naphthalene ring. Preferred substituents include a hydrocarbon group having 12 or less carbon atoms, a halogen atom, an alkoxy group having 12 or less carbon atoms, a hydrocarbon group having 12 or less carbon atoms, and 12 carbon atoms. Most preferred are not more than alkoxy groups. Y ¹ and Y ² may be the same or different and each represents a sulfur atom or a dialkylmethylene group having 12 or less carbon atoms. R ³ and R ⁴ may be the same or different and each represents a hydrocarbon group having 20 or less carbon atoms which may have a substituent. Preferable substituents include an alkoxy group having 12 or less carbon atoms, a carboxyl group, and a sulfo group, and an alkoxy group having 12 or less carbon atoms is most preferable. R ⁵ , R ⁶ , R ⁷ and R ⁸ may be the same or different and each represents a hydrogen atom or a hydrocarbon group having 12 or less carbon atoms. From the availability of raw materials, a hydrogen atom is preferred. Z _a ⁻ represents a counter anion. However, when the cyanine dye represented by formula (i) has an anionic substituent in the structure thereof, Z _a is does not require charge neutralization ^- is not necessary. Preferred Z _a ⁻ is a halogen ion, a perchlorate ion, a tetrafluoroborate ion, a hexafluorophosphate ion, and a sulfonate ion, particularly preferably a perchlorate ion, from the storage stability of the recording layer coating solution. Tetrafluoroborate ion, hexafluorophosphate ion, and aryl sulfonate ion.

Specific examples of cyanine dyes represented by formula (i) that can be suitably used in the present invention include those described in paragraph numbers [0017] to [0019] of JP-A No. 2001-133969. Can do.
Further, other particularly preferable examples include specific indolenine cyanine dyes described in JP-A-2002-278057 described above.

  Examples of the pigment used in the present invention include commercially available pigments and color index (CI) manual, “Latest Pigment Handbook” (edited by Japan Pigment Technology Association, published in 1977), “Latest Pigment Application Technology” (CMC Publishing, 1986), “Printing Ink Technology”, CMC Publishing, 1984) can be used.

  Examples of the pigment include black pigments, yellow pigments, orange pigments, brown pigments, red pigments, purple pigments, blue pigments, green pigments, fluorescent pigments, metal powder pigments, and other polymer-bonded dyes. Specifically, insoluble azo pigments, azo lake pigments, condensed azo pigments, chelate azo pigments, phthalocyanine pigments, anthraquinone pigments, perylene and perinone pigments, thioindigo pigments, quinacridone pigments, dioxazine pigments, isoindolinone pigments In addition, quinophthalone pigments, dyed lake pigments, azine pigments, nitroso pigments, nitro pigments, natural pigments, fluorescent pigments, inorganic pigments, carbon black, and the like can be used. Among these pigments, carbon black is preferable.

  These pigments may be used without surface treatment, or may be used after surface treatment. The surface treatment method includes a method of surface coating with a resin or wax, a method of attaching a surfactant, a method of bonding a reactive substance (eg, silane coupling agent, epoxy compound, polyisocyanate, etc.) to the pigment surface, etc. Can be considered. The above-mentioned surface treatment methods are described in “Characteristics and Applications of Metal Soap” (Shobobo), “Printing Ink Technology” (CMC Publishing, 1984) and “Latest Pigment Application Technology” (CMC Publishing, 1986). Yes.

  The particle size of the pigment is preferably in the range of 0.01 μm to 10 μm, more preferably in the range of 0.05 μm to 1 μm, and particularly preferably in the range of 0.1 μm to 1 μm. Within this range, good stability of the pigment dispersion in the image recording layer coating solution and good uniformity of the image recording layer can be obtained.

  As a method for dispersing the pigment, a known dispersion technique used in ink production, toner production, or the like can be used. Examples of the disperser include an ultrasonic disperser, a sand mill, an attritor, a pearl mill, a super mill, a ball mill, an impeller, a disperser, a KD mill, a colloid mill, a dynatron, a three-roll mill, and a pressure kneader. Details are described in "Latest Pigment Applied Technology" (CMC Publishing, 1986).

These infrared absorbers may be added to the same layer as other components, or may be added to another image recording layer provided, but when preparing a negative lithographic printing plate precursor, The image recording layer is added so that the absorbance at the maximum absorption wavelength in the wavelength range of 760 nm to 1200 nm is in the range of 0.3 to 1.2 by the reflection measurement method. Preferably, it is the range of 0.4-1.1. Within this range, a uniform polymerization reaction proceeds in the depth direction of the image recording layer, and good film strength of the image area and adhesion to the support can be obtained.
The absorbance of the image recording layer can be adjusted by the amount of infrared absorber added to the image recording layer and the thickness of the image recording layer. Absorbance can be measured by a conventional method. As a measuring method, for example, on a reflective support such as aluminum, an image recording layer having a thickness appropriately determined in a range in which the coating amount after drying is necessary as a lithographic printing plate is formed, and the reflection density is set to the optical density. And a method of measuring with a spectrophotometer by a reflection method using an integrating sphere.

<(B) Polymerization initiator>
The polymerization initiator used in the present invention is a compound that generates radicals by light, heat, or both, and initiates and accelerates polymerization of a compound having a polymerizable unsaturated group. As the polymerization initiator that can be used in the present invention, a known thermal polymerization initiator, a compound having a bond with a small bond dissociation energy, a photopolymerization initiator, or the like can be used, and a radical that is suitably used in the present invention is generated. The compound to be used refers to a compound that initiates and accelerates polymerization of a compound having a polymerizable unsaturated group by generating radicals by thermal energy. As the thermal radical generator according to the present invention, a known polymerization initiator, a compound having a bond with a small bond dissociation energy, or the like can be appropriately selected and used. Moreover, the compound which generate | occur | produces a radical can be used individually or in combination of 2 or more types.

  Examples of the radical generating compound include organic halides, carbonyl compounds, organic peroxides, azo polymerization initiators, azide compounds, metallocene compounds, hexaarylbiimidazole compounds, organic borate compounds, disulfone compounds, oximes. Examples thereof include ester compounds and onium salt compounds.

  Specific examples of the organic halide include Wakabayashi et al., “Bull Chem. Soc Japan” 42, 2924 (1969), US Pat. No. 3,905,815, Japanese Examined Patent Publication No. 46-4605, JP 48-36281, JP 55-3070, JP 60-239736, JP 61-169835, JP 61-169837, JP 62-58241, JP 62 -212401, JP-A-63-70243, JP-A-63-298339, M.S. P. Examples include compounds described in Hutt “Journal of Heterocyclic Chemistry” 1 (No 3), (1970) ”, and particularly preferable examples include oxazole compounds substituted with a trihalomethyl group and s-triazine compounds.

  More preferred are s-triazine derivatives and oxadiazole derivatives to which at least one mono, di, or trihalogen-substituted methyl group is bonded. Specifically, for example, 2,4,6-tris (monochloromethyl) -s-triazine, 2,4,6-tris (dichloromethyl) -s-triazine, 2,4,6-tris (trichloromethyl) -S-triazine, 2-methyl-4,6-bis (trichloromethyl) -s-triazine, 2-n-propyl-4,6-bis (trichloromethyl) -s-triazine, 2- (α, α, β-trichloroethyl) -4,6-bis (trichloromethyl) -s-triazine, 2-phenyl-4,6-bis (trichloromethyl) -s-triazine, 2- (p-methoxyphenyl) -4,6 -Bis (trichloromethyl) -s-triazine, 2- (3,4-epoxyphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p-chlorophenyl) -4,6- (Trichloromethyl) -s-triazine, 2- (p-bromophenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p-fluorophenyl) -4,6-bis (trichloromethyl) ) -S-triazine, 2- (p-trifluoromethylphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (2,6-dichlorophenyl) -4,6-bis (trichloromethyl) -S-triazine, 2- (2,6-difluorophenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (2,6-dibromophenyl) -4,6-bis (trichloromethyl) -S-triazine, 2- (4-biphenylyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (4'-chloro-4-biphenylyl) -4,6 Bis (trichloromethyl) -s-triazine, 2- (p-cyanophenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p-acetylphenyl) -4,6-bis (trichloromethyl) ) -S-triazine, 2- (p-ethoxycarbonylphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p-phenoxycarbonylphenyl) -4,6-bis (trichloromethyl)- s-triazine, 2- (p-methylsulfonylphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (p-dimethylsulfoniumphenyl) -4,6-bis (trichloromethyl) -s- Triazine tetrafluoroborate, 2- (2,4-difluorophenyl) -4,6-bis (trichloromethyl) -s-tria Gin, 2- (p-diethoxyphosphorylphenyl) -4,6-bis (trichloromethyl) -s-triazine, 2- [4- (4-hydroxyphenylcarbonylamino) phenyl] -4,6-bis (trichloro) Methyl) -s-triazine, 2- [4- (p-methoxyphenyl) -1,3-butadienyl] -4,6-bis (trichloromethyl) -s-triazine, 2-styryl-4,6-bis ( Trichloromethyl) -s-triazine, 2- (p-methoxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2- (pi-propyloxystyryl) -4, 6-bis (trichloro) Methyl) -s-triazine, 2- (p-tolyl) -4,6-bis (trichloromethyl) -s-triazine, 2- (4-methoxynaphthyl) -4,6-bi (Trichloromethyl) -s-triazine, 2-phenylthio-4,6-bis (trichloromethyl) -s-triazine, 2-benzylthio-4,6-bis (trichloromethyl) -s-triazine, 2,4,6 -Tris (dibromomethyl) -s-triazine, 2,4,6-tris (tribromomethyl) -s-triazine, 2-methyl-4,6-bis (tribromomethyl) -s-triazine, 2-methoxy -4,6-bis (tribromomethyl) -s-triazine, 2- (o-methoxystyryl) -5-trichloromethyl-1,3,4-oxadiazole, 2- (3,4-epoxystyryl) -5-trichloromethyl-1,3,4-oxadiazole, 2- [1-phenyl-2- (4-methoxyphenyl) vinyl] -5-trichloromethyl-1,3 4-oxadiazole, 2- (p-hydroxystyryl) -5-trichloromethyl-1,3,4-oxadiazole, 2- (3,4-dihydroxystyryl) -5-trichloromethyl-1,3 4-oxadiazole, 2- (pt-butoxystyryl) -5-trichloromethyl-1,3,4-oxadiazole and the like.

  Examples of the carbonyl compound include benzophenone, Michler ketone, 2-methylbenzophenone, 3-methylbenzophenone, 4-methylbenzophenone, 2-chlorobenzophenone, 4-bromobenzophenone, 2-carboxybenzophenone and other benzophenone derivatives, 2,2-dimethoxy- 2-phenylacetophenone, 2,2-diethoxyacetophenone, 1-hydroxycyclohexyl phenyl ketone, α-hydroxy-2-methylphenylpropanone, 1-hydroxy-1-methylethyl- (p-isopropylphenyl) ketone, 1- Hydroxy-1- (p-dodecylphenyl) ketone, 2-methyl- (4 ′-(methylthio) phenyl) -2-morpholino-1-propanone, 1,1,1-trichloromethyl- (p-butylpheny ) Acetophenone derivatives such as ketones, thioxanthone derivatives such as thioxanthone, 2-ethylthioxanthone, 2-isopropylthioxanthone, 2-chlorothioxanthone, 2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2,4-diisopropylthioxanthone, p And benzoic acid ester derivatives such as ethyl dimethylaminobenzoate and ethyl p-diethylaminobenzoate.

  As the azo compound, for example, an azo compound described in JP-A-8-108621 can be used.

  Examples of the organic peroxide include trimethylcyclohexanone peroxide, acetylacetone peroxide, 1,1-bis (tert-butylperoxy) -3,3,5-trimethylcyclohexane, 1,1-bis (tert-butyl). Peroxy) cyclohexane, 2,2-bis (tert-butylperoxy) butane, tert-butyl hydroperoxide, cumene hydroperoxide, diisopropylbenzene hydroperoxide, 2,5-dimethylhexane-2,5-dihydro Peroxide, 1,1,3,3-tetramethylbutyl hydroperoxide, tert-butylcumyl peroxide, dicumyl peroxide, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane, 2, -Oxanoyl peroxide, succinic peroxide, benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, diisopropyl peroxydicarbonate, di-2-ethylhexyl peroxydicarbonate, di-2-ethoxyethyl peroxydicarbonate , Dimethoxyisopropyl peroxycarbonate, di (3-methyl-3-methoxybutyl) peroxydicarbonate, tert-butyl peroxyacetate, tert-butyl peroxypivalate, tert-butyl peroxyneodecanoate, tert- Butyl peroxyoctanoate, tert-butyl peroxylaurate, tersyl carbonate, 3,3 ′, 4,4′-tetra- (t-butylperoxycarbonyl) benzophenone, 3,3 ′, 4 '-Tetra- (t-hexylperoxycarbonyl) benzophenone, 3,3', 4,4'-tetra- (p-isopropylcumylperoxycarbonyl) benzophenone, carbonyldi (t-butylperoxydihydrogen diphthalate) , Carbonyldi (t-hexylperoxydihydrogen diphthalate) and the like.

  Examples of the metallocene compound include JP-A-59-152396, JP-A-61-151197, JP-A-63-41484, JP-A-2-249, JP-A-2-4705, Various titanocene compounds described in JP-A-5-83588, such as di-cyclopentadienyl-Ti-bis-phenyl, di-cyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, Di-cyclopentadienyl-Ti-bis-2,4-di-fluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,4,6-trifluorophen-1-yl, di- -Cyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,3,4,5,6-penta Fluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,4,6-trifluoropheny -1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,4 , 5,6-pentafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,6-difluoro-3- (pyrrol-1-yl) phen-1-yl, JP-A-1-304453 And iron-arene complexes described in JP-A-1-152109.

  Examples of the hexaarylbiimidazole compound include, for example, Japanese Patent Publication No. 6-29285, U.S. Pat. Nos. 3,479,185, 4,311,783, and 4,622,286. And, specifically, 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-bromophenyl) )) 4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o, p-dichlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2 ′ -Bis (o-chlorophenyl) -4,4 ', 5,5'-tetrakis (m-methoxyphenyl) biidazole, 2,2'-bis (o, o'-dichlorophenyl) -4,4', 5,5 '-Tetrafeni Biimidazole, 2,2′-bis (o-nitrophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-methylphenyl) -4,4 ′, 5 , 5′-tetraphenylbiimidazole, 2,2′-bis (o-trifluorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, and the like.

  Examples of the organic borate compounds include JP-A-62-143044, JP-A-62-1050242, JP-A-9-188585, JP-A-9-188686, JP-A-9-188710, and JP-A-9-188710. 2000-131837, Japanese Patent Application Laid-Open No. 2002-107916, Japanese Patent No. 2764769, Japanese Patent Application Laid-Open No. 2002-116539, and Kunz, Martin “Rad Tech'98. Proceeding April 19-22, 1998, Chicago”. The organic borate described in JP-A-6-157623, JP-A-6-175564, JP-A-6-175561, or organic boron oxosulfonium complex, JP-A-6-175554 No. 1, JP-A-6-175553 The organoboron iodonium complex described in JP-A-9-188710, the organoboron phosphonium complex described in JP-A-9-188710, JP-A-6-348011, JP-A-7-128785, JP-A-7-140589, JP-A-5-140589 Specific examples include organoboron transition metal coordination complexes such as 7-306527 and JP-A-7-292014.

  Examples of the disulfone compound include compounds described in JP-A Nos. 61-166544 and 2003-328465.

  Examples of the oxime ester compound include JCS Perkin II (1979) 1653-1660), JCSPerkin II (1979) 156-162, Journal of Photopolymer Science and Technology (1995) 202-232, and JP-A 2000-66385. And compounds described in JP 2000-80068 A. Specific examples thereof include compounds represented by the following structural formula.

  Examples of the onium salt compound include S.I. I. Schlesinger, Photogr. Sci. Eng. 18, 387 (1974), T .; S. Diazonium salts described in Bal et al, Polymer, 21, 423 (1980), ammonium salts described in US Pat. No. 4,069,055, JP-A-4-365049, etc., US Pat. No. 4,069 , 055 and 4,069,056, phosphonium salts described in European Patent Nos. 104 and 143, U.S. Pat. Nos. 339,049 and 410,201, 2-150848, JP-A-2-296514, iodonium salts, European Patent Nos. 370,693, 390,214, 233,567, 297,443, and 297,442 U.S. Pat. Nos. 4,933,377, 161,811, 410,201, 339,049, 4,760,013, 4,73 No. 4,444, 2,833,827, German Patent Nos. 2,904,626, 3,604,580, and 3,604,581, the sulfonium salts described in J . V. Crivello et al, Macromolecules, 10 (6), 1307 (1977), J. MoI. V. Crivello et al, J.A. Polymer Sci. , Polymer Chem. Ed. , 17, 1047 (1979), a selenonium salt described in C.I. S. Wen et al, Teh, Proc. Conf. Rad. Curing ASIA, p478 Tokyo, Oct (1988), and onium salts such as arsonium salts.

In particular, the oxime ester compound, diazonium salt, iodonium salt, and sulfonium salt are preferable from the viewpoint of reactivity and stability. In the present invention, these onium salts function not as acid generators but as ionic radical polymerization initiators.
Preferred onium salts for the present invention are onium salts represented by the following general formulas (RI-I) to (RI-III).

In the formula (RI-I), Ar ¹¹ represents an aryl group having 20 or less carbon atoms which may have 1 to 6 substituents, and preferred substituents include an alkyl group having 1 to 12 carbon atoms and 1 carbon atom. -12 alkenyl group, C1-C12 alkynyl group, C1-C12 aryl group, C1-C12 alkoxy group, C1-C12 aryloxy group, halogen atom, C1-C12 An alkylamino group, a C1-C12 dialkylamino group, a C1-C12 alkylamide group or arylamide group, a carbonyl group, a carboxyl group, a cyano group, a sulfonyl group, a C1-C12 thioalkyl group, A C1-C12 thioaryl group is mentioned. Z ^11- represents a monovalent anion, a halogen ion, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, thiosulfonate ion, sulfate ion, stability, Perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, and sulfinate ion are preferable from the viewpoint of the visibility of the printout image.

In formula (RI-II), Ar ²¹ and Ar ²² each independently represent an aryl group having 20 or less carbon atoms which may have 1 to 6 substituents, and preferred substituents have 1 to 12 carbon atoms. An alkyl group, an alkenyl group having 1 to 12 carbon atoms, an alkynyl group having 1 to 12 carbon atoms, an aryl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryloxy group having 1 to 12 carbon atoms, a halogen atom An alkylamino group having 1 to 12 carbon atoms, a dialkylamino group having 1 to 12 carbon atoms, an alkylamide group or arylamide group having 1 to 12 carbon atoms, a carbonyl group, a carboxyl group, a cyano group, a sulfonyl group, and 1 carbon atom -12 thioalkyl group and C1-C12 thioaryl group are mentioned. Z ^21- represents a monovalent anion, which is a halogen ion, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, thiosulfonate ion, sulfate ion, Perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, and carboxylate ion are preferable from the viewpoint of the visibility of the printout image.

In the formula (RI-III), R ³¹ , R ³² and R ³³ each independently represents an aryl group having 20 or less carbon atoms, an alkyl group, an alkenyl group or an alkynyl group which may have 1 to 6 substituents. In view of reactivity and stability, an aryl group is desirable. Preferred substituents are alkyl groups having 1 to 12 carbon atoms, alkenyl groups having 1 to 12 carbon atoms, alkynyl groups having 1 to 12 carbon atoms, aryl groups having 1 to 12 carbon atoms, alkoxy groups having 1 to 12 carbon atoms, Aryloxy group having 1 to 12 carbon atoms, halogen atom, alkylamino group having 1 to 12 carbon atoms, dialkylamino group having 1 to 12 carbon atoms, alkylamide group or arylamide group having 1 to 12 carbon atoms, carbonyl group, carboxyl Group, a cyano group, a sulfonyl group, a thioalkyl group having 1 to 12 carbon atoms, and a thioaryl group having 1 to 12 carbon atoms. Z ^31- represents a monovalent anion, which is a halogen ion, perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, thiosulfonate ion, sulfate ion, Perchlorate ion, hexafluorophosphate ion, tetrafluoroborate ion, sulfonate ion, sulfinate ion, and carboxylate ion are preferable from the viewpoint of the visibility of the printout image, and more preferable examples are described in JP-A-2001-343742. Carboxylate ions, particularly preferably the carboxylate ions described in JP-A No. 2002-148790.
Examples of onium salts that can be suitably used as a polymerization initiator in the present invention will be given below, but the present invention is not limited thereto.

Moreover, you may use the polymerization initiator of the azinium structure salt of the following general formula (RI-IV) as a polymerization initiator of this invention. In the formula, R ¹ , R ² , R ³ , R ⁴ , R ⁵ , and R ⁶ each independently represent a hydrogen atom, a halogen atom, or a monovalent substituent. X ⁻ represents an anion.

  Examples of the monovalent substituent include, for example, a halogen atom, amino group, substituted amino group, substituted carbonyl group, hydroxyl group, substituted oxy group, thiol group, thioether group, silyl group, nitro group, cyano group, alkyl group, Alkenyl group, aryl group, heterocyclic group, sulfo group, substituted sulfonyl group, sulfonate group, substituted sulfinyl group, phosphono group, substituted phosphono group, phosphonate group, substituted phosphonate group, etc. It may have a substituent.

In addition, as the compound represented by the general formula (RI-IV), a skeleton (cation part) having a specific structure in the compound represented by the general formula (RI-IV) is bonded via R ¹ to form a cation part. Are included in the molecule (multimeric form), and such compounds are also preferably used.
Furthermore, the compound represented by the general formula (RI-IV) may be a compound (polymer type) introduced into the polymer side chain via any of R ^{1 to} R ⁶ , and is listed as one of preferred embodiments. It is done.

  Specific examples of the compound represented by the general formula (RI-IV) [Exemplary Compounds AZ-1 to AZ-34] are listed below, but the scope of the present invention is not limited thereto.

The polymerization initiator is not limited to the above, but a triazine-based initiator, an organic halogen compound, an oxime ester compound, a diazonium salt, an iodonium salt, and a sulfonium salt are more preferable from the viewpoints of reactivity and stability. Among these, from the viewpoint of improving the visibility of the printout image in combination with an infrared absorber, it is an onium salt and has an inorganic anion such as PF ₆ ⁻ , BF ₄ ⁻ or the like as a counter ion. Those are preferred. Furthermore, diaryliodonium is preferred as the onium because of its excellent color development.

  These polymerization initiators are each preferably 0.1 to 50% by mass, more preferably 0.5 to 30% by mass, and particularly preferably 0.8 to 20% by mass with respect to the total solid content constituting the image recording layer. Can be added at a ratio of Within this range, good sensitivity and good stain resistance of the non-image area during printing can be obtained. These polymerization initiators may be used alone or in combination of two or more. Moreover, these polymerization initiators may be added to the same layer as other components, or another layer may be provided and added thereto.

<(C) Polymerizable compound>
The polymerizable compound that can be used in the present invention is an addition polymerizable compound having at least one ethylenically unsaturated double bond, and is a compound having at least one terminal ethylenically unsaturated bond, preferably two or more. To be elected. Such a compound group is widely known in the industrial field, and can be used without any particular limitation in the present invention. These have chemical forms such as monomers, prepolymers, i.e. dimers, trimers and oligomers, or mixtures thereof and copolymers thereof. Examples of monomers and copolymers thereof include unsaturated carboxylic acids (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.), and esters and amides thereof. In this case, an ester of an unsaturated carboxylic acid and an aliphatic polyhydric alcohol compound, or an amide of an unsaturated carboxylic acid and an aliphatic polyvalent amine compound is used. In addition, an addition reaction product of an unsaturated carboxylic acid ester or amide having a nucleophilic substituent such as a hydroxyl group, amino group or mercapto group with a monofunctional or polyfunctional isocyanate or epoxy, and monofunctional or polyfunctional A dehydration condensation reaction product with a functional carboxylic acid is also preferably used. Further, an addition reaction product of an unsaturated carboxylic acid ester or amide having an electrophilic substituent such as an epoxy group or an epoxy group with a monofunctional or polyfunctional alcohol, amine or thiol, a halogen group or Also suitable are substitution reaction products of unsaturated carboxylic acid esters or amides having a leaving substituent such as a tosyloxy group with monofunctional or polyfunctional alcohols, amines or thiols. As another example, it is also possible to use a group of compounds substituted with unsaturated phosphonic acid, styrene, vinyl ether or the like instead of the unsaturated carboxylic acid.

  Specific examples of the monomer of an ester of an aliphatic polyhydric alcohol compound and an unsaturated carboxylic acid include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol diacrylate , Tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate , Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, polyester acrylate oligomer, isocyanuric acid There are EO-modified triacrylate and the like.

  Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [p- (3-methacryloxy- 2-hydroxypro ) Phenyl] dimethyl methane, bis - [p- (methacryloxyethoxy) phenyl] dimethyl methane.

  Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,3-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate. Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate. Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate.

  Examples of other esters include, for example, aliphatic alcohol esters described in JP-B-51-47334 and JP-A-57-196231, JP-A-59-5240, and JP-A-59-5241. And those having an aromatic skeleton described in JP-A-2-226149 and those containing an amino group described in JP-A-1-165613. Furthermore, the ester monomers described above can also be used as a mixture.

  Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylene bisacrylamide, xylylene bismethacrylamide and the like. Examples of other preferable amide monomers include those having a cyclohexylene structure described in JP-B-54-21726.

  Further, urethane-based addition polymerizable compounds produced using an addition reaction of isocyanate and hydroxyl group are also suitable. Specific examples of such compounds are described in, for example, Japanese Patent Publication No. 48-41708. It contains two or more polymerizable vinyl groups in one molecule obtained by adding a vinyl monomer containing a hydroxyl group represented by the following general formula (ii) to a polyisocyanate compound having two or more isocyanate groups in the molecule. A vinyl urethane compound etc. are mentioned.

^{_{CH 2 = C (R 4)}} COOCH 2 CH (R 5) OH (ii)
(However, R ⁴ and R ⁵ represent H or CH _3. )

  Further, urethane acrylates as described in JP-A-51-37193, JP-B-2-32293, JP-B-2-16765, JP-B-58-49860, JP-B-56-17654 And urethane compounds having an ethylene oxide skeleton described in JP-B-62-39417 and JP-B-62-39418. Furthermore, addition polymerizable compounds having an amino structure or a sulfide structure in the molecule described in JP-A-63-277653, JP-A-63-260909, and JP-A-1-105238 are used. Depending on the case, it is possible to obtain a photopolymerizable composition excellent in the photosensitive speed.

  Other examples include polyester acrylates, epoxy resins and acrylic acid or methacrylic acid described in JP-A-48-64183, JP-B-49-43191, JP-B-52-30490, and JP-B-52-30490. Mention may be made of polyfunctional acrylates and methacrylates such as reacted epoxy acrylates. In addition, JP-B-46-43946, JP-B-1-40337, JP-B-1-40336, specific unsaturated compounds described in each gazette, vinylphosphonic acid compounds described in JP-A-2-25493, and the like are also included. Can be mentioned. In some cases, a structure containing a perfluoroalkyl group described in JP-A-61-22048 is preferably used. Furthermore, Journal of Japan Adhesion Association vol. 20, no. 7, pages 300 to 308 (1984), which are introduced as photocurable monomers and oligomers, can also be used.

About these addition polymerizable compounds, the details of usage, such as the structure, single use or combination, addition amount, etc. can be arbitrarily set according to the performance design of the final lithographic printing plate precursor. For example, it is selected from the following viewpoints.
From the viewpoint of sensitivity, a structure having a large unsaturated group content per molecule is preferable, and in many cases, a bifunctional or higher functionality is preferable. Further, in order to increase the strength of the image area, that is, the cured film, those having three or more functionalities are preferable, and furthermore, different functional numbers and different polymerizable groups (for example, acrylic acid ester, methacrylic acid ester, styrenic compound, vinyl ether type). A method of adjusting both sensitivity and strength by using a compound) is also effective.
Further, the selection and use method of the addition polymerization compound is also an important factor for the compatibility and dispersibility with other components (for example, binder polymer, initiator, colorant, etc.) in the image recording layer. In some cases, the compatibility can be improved by using a low-purity compound or by using two or more kinds in combination. In addition, a specific structure may be selected for the purpose of improving the adhesion of the substrate and the protective layer described later.

  The addition polymerizable compound is preferably used in the range of 5 to 80% by mass, more preferably 25 to 75% by mass, with respect to the non-volatile component in the image recording layer. These may be used alone or in combination of two or more. In addition, the use method of the addition polymerizable compound can be arbitrarily selected from the viewpoint of polymerization inhibition with respect to oxygen, resolution, fogging, refractive index change, surface adhesiveness, etc. Depending on the case, a layer configuration and coating method such as undercoating and overcoating can be performed.

<Hydrophobic precursor>
In the present invention, the hydrophobized precursor is a fine particle capable of converting the image recording layer to hydrophobic when heat is applied. The fine particles are preferably at least one particle selected from hydrophobic thermoplastic polymer fine particles and heat-reactive polymer fine particles.

  As the hydrophobic thermoplastic polymer fine particles used in the image recording layer, Research Disclosure No. 33303 of January 1992, JP-A-9-123387, JP-A-9-131850, JP-A-9-171249, Hydrophobic thermoplastic polymer fine particles described in JP-A-9-171250 and European Patent No. 931647 can be mentioned as preferable examples. Specific examples of the polymer constituting the polymer fine particle include homopolymers of monomers such as ethylene, styrene, vinyl chloride, methyl acrylate, ethyl acrylate, methyl methacrylate, ethyl methacrylate, vinylidene chloride, acrylonitrile, vinyl carbazole, or the like. Mention may be made of copolymers or mixtures thereof. Among them, more preferred are polystyrene and polymethyl methacrylate.

  The average particle diameter of the hydrophobic thermoplastic polymer fine particles used in the present invention is preferably 0.01 to 2.0 μm. As a method for synthesizing such hydrophobic thermoplastic polymer fine particles, in addition to emulsion polymerization and suspension polymerization, these compounds are dissolved in a water-insoluble organic solvent and mixed with an aqueous solution containing a dispersant. There is a method of emulsifying and further solidifying into fine particles while heating the organic solvent (dissolution dispersion method).

  Examples of the heat-reactive polymer fine particles used in the present invention include thermosetting polymer fine particles and polymer fine particles having a heat-reactive group.

  Examples of the thermosetting polymer include a resin having a phenol skeleton, a urea resin (for example, a urea derivative such as urea or methoxymethylated urea resinized with an aldehyde such as formaldehyde), a melamine resin (for example, melamine or Examples thereof include those obtained by converting the derivatives into resins with aldehydes such as formaldehyde, alkyd resins, unsaturated polyester resins, polyurethane resins, and epoxy resins. Among these, resins having a phenol skeleton, melamine resins, urea resins, and epoxy resins are particularly preferable.

  Suitable resins having a phenol skeleton include, for example, phenol resins obtained by resinizing phenol, cresol, etc. with aldehydes such as formaldehyde, hydroxystyrene resins, N- (p-hydroxyphenyl) methacrylamide, and p-hydroxyphenyl methacrylate. Examples thereof include a polymer or copolymer of methacrylamide or acrylamide or methacrylate or acrylate having a phenol skeleton.

  The average particle diameter of the thermosetting polymer fine particles used in the present invention is preferably 0.01 to 2.0 μm. Such thermosetting polymer fine particles can be easily obtained by a solution dispersion method, but may be formed into fine particles when the thermosetting polymer is synthesized. However, it is not restricted to these methods.

  The thermally reactive group of the polymer fine particle having a thermally reactive group used in the present invention may be any functional group that undergoes a reaction as long as a chemical bond is formed, but is an ethylenically unsaturated group that undergoes a radical polymerization reaction. Group (for example, acryloyl group, methacryloyl group, vinyl group, allyl group, etc.), cationically polymerizable group (for example, vinyl group, vinyloxy group, etc.), isocyanate group that performs addition reaction or its block, epoxy group, vinyloxy group And a functional group having an active hydrogen atom as a reaction partner (for example, an amino group, a hydroxyl group, a carboxyl group, etc.), a carboxyl group for performing a condensation reaction, a hydroxyl group or an amino group as a reaction partner, a ring-opening addition reaction The acid anhydride to be used and the amino group or hydroxyl group as the reaction partner may be mentioned as suitable ones. Kill.

  The introduction of these functional groups into the polymer fine particles may be performed at the time of polymerization, or may be performed using a polymer reaction after the polymerization.

  When introduced at the time of polymerization, it is preferable to carry out emulsion polymerization or suspension polymerization of the monomer having the above functional group. Specific examples of the monomer having the above functional group include allyl methacrylate, allyl acrylate, vinyl methacrylate, vinyl acrylate, 2- (vinyloxy) ethyl methacrylate, p-vinyloxystyrene, p- {2- (vinyloxy) ethyl} styrene, Block isocyanate with glycidyl methacrylate, glycidyl acrylate, 2-isocyanatoethyl methacrylate or alcohol thereof, block isocyanate with 2-isocyanate ethyl acrylate or alcohol thereof, 2-aminoethyl methacrylate, 2-aminoethyl acrylate, 2- Hydroxyethyl methacrylate, 2-hydroxyethyl acrylate, acrylic acid, methacrylic acid, maleic anhydride, bifunctional acrylate, 2 officers Methacrylate, and the like, but not limited thereto.

  In the present invention, a copolymer of these monomers and a monomer that is copolymerizable with these monomers and does not have a thermally reactive group can also be used. Examples of the copolymer monomer having no heat-reactive group include styrene, alkyl acrylate, alkyl methacrylate, acrylonitrile, vinyl acetate, and the like. It is not limited to.

  Examples of the polymer reaction used when the introduction of the thermally reactive group is carried out after the polymerization include the polymer reaction described in International Publication No. 96/34316 pamphlet.

  Among the polymer fine particles having a heat-reactive group, those in which the polymer fine particles are coalesced by heat are preferable, and those having a hydrophilic surface and being dispersed in water are particularly preferable. The contact angle (water droplets) of the film prepared by applying only polymer fine particles and drying at a temperature lower than the solidification temperature is higher than the contact angle (water droplets) of the film prepared by drying at a temperature higher than the solidification temperature. It is preferable to lower. In order to make the surface of the polymer fine particles hydrophilic in this way, a hydrophilic polymer or oligomer such as polyvinyl alcohol or polyethylene glycol or a hydrophilic low molecular weight compound may be adsorbed on the surface of the polymer fine particles. However, the surface hydrophilization method is not limited to this.

  The solidification temperature of the polymer fine particles having these thermoreactive groups is preferably 70 ° C. or higher, but more preferably 100 ° C. or higher in view of the stability over time. The average particle size of the polymer fine particles is preferably 0.01 to 2.0 μm, more preferably 0.05 to 2.0 μm, and most preferably 0.1 to 1.0 μm. Within this range, good resolution and stability over time can be obtained.

<(D) Binder polymer>
In the image recording layer of the present invention, a binder polymer can be used in order to improve the film strength of the image recording layer. As the binder polymer that can be used in the present invention, conventionally known binder polymers can be used without limitation, and polymers having film properties are preferred. Examples of such binder polymers include acrylic resins, polyvinyl acetal resins, polyurethane resins, polyurea resins, polyimide resins, polyamide resins, epoxy resins, methacrylic resins, polystyrene resins, novolac phenolic resins, polyester resins, and synthetic rubbers. And natural rubber.
The binder polymer may have crosslinkability in order to improve the film strength of the image area. In order to impart crosslinkability to the binder polymer, a crosslinkable functional group such as an ethylenically unsaturated bond may be introduced into the main chain or side chain of the polymer. The crosslinkable functional group may be introduced by copolymerization.
Examples of the polymer having an ethylenically unsaturated bond in the main chain of the molecule include poly-1,4-butadiene and poly-1,4-isoprene.
Examples of polymers having an ethylenically unsaturated bond in the side chain of the molecule are polymers of esters or amides of acrylic acid or methacrylic acid, where the ester or amide residue (R of -COOR or CONHR) is ethylene. Examples thereof include polymers having a polymerizable unsaturated bond.

Examples of the residue (the R) having an ethylenically unsaturated _{bond, - (CH 2) n CR} 1 = CR 2 R 3, - (CH 2 O) n CH 2 CR 1 = CR 2 R 3, - _{(CH 2 CH 2 O) n} CH 2 CR 1 = CR 2 R 3, - (CH 2) n NH-CO-O-CH 2 CR 1 = CR 2 R 3, - (CH 2) n -O-CO —CR ¹ ═CR ² R ³ and (CH ₂ CH ₂ O) ₂ —X (wherein R ^{1 to} R ³ are each a hydrogen atom, a halogen atom, or an alkyl group having 1 to 20 carbon atoms, an aryl group, and alkoxy. R ¹ and R ² or R ³ may be bonded to each other to form a ring, n represents an integer of 1 to 10. X represents a dicyclopentadienyl residue. Represents a group).
Specific examples of the ester _{residue, -CH 2 CH = CH 2,} ( described in JP Kokoku _{7-21633.) - CH 2 CH 2} O-CH 2 CH = CH 2, -CH 2 C _{(CH 3) = CH 2,} -CH 2 CH = CH-C 6 H 5, -CH 2 CH 2 OCOCH = CH-C 6 H 5, -CH 2 CH 2 -NHCOO-CH 2 CH = CH 2 and CH ₂ CH ₂ O—X (wherein X represents a dicyclopentadienyl residue).
Specific examples of the amide residue include —CH ₂ CH═CH ₂ , —CH ₂ CH ₂ —Y (wherein Y represents a cyclohexene residue), —CH ₂ CH ₂ —OCO—CH═CH _2. Is mentioned.

  The binder polymer having crosslinkability, for example, has a free radical (polymerization initiation radical or a growth radical in the polymerization process of the polymerizable compound) added to the crosslinkable functional group, and the polymerization chain of the polymerizable compound is formed directly between the polymers. Through addition polymerization, a cross-link is formed between the polymer molecules and cured. Alternatively, atoms in the polymer (eg, hydrogen atoms on carbon atoms adjacent to the functional bridging group) are abstracted by free radicals to form polymer radicals that are bonded together, thereby causing cross-linking between polymer molecules. Forms and cures.

  The content of the crosslinkable group in the binder polymer (content of unsaturated double bond capable of radical polymerization by iodine titration) is preferably 0.1 to 10.0 mmol, more preferably 1.0, per 1 g of the binder polymer. -7.0 mmol, most preferably 2.0-5.5 mmol. Within this range, good sensitivity and good storage stability can be obtained.

  Further, from the viewpoint of improving on-press developability or gum developability of the image recording layer unexposed portion, the binder polymer preferably has high solubility or dispersibility in ink and / or fountain solution. In order to improve solubility or dispersibility in ink, the binder polymer is preferably oleophilic, and in order to improve solubility or dispersibility in dampening water, the binder polymer is hydrophilic. Is preferred. For this reason, in the present invention, it is also effective to use a lipophilic binder polymer and a hydrophilic binder polymer in combination.

  Examples of the hydrophilic binder polymer include hydroxyl group, carboxyl group, carboxylate group, hydroxyethyl group, polyoxyethyl group, hydroxypropyl group, polyoxypropyl group, amino group, aminoethyl group, aminopropyl group, and ammonium. Preferred examples include those having a hydrophilic group such as a group, an amide group, a carboxymethyl group, a sulfo group, or a phosphoric acid group.

  Specific examples include gum arabic, casein, gelatin, starch derivatives, carboxymethylcellulose and its sodium salt, cellulose acetate, sodium alginate, vinyl acetate-maleic acid copolymers, styrene-maleic acid copolymers, polyacrylic acids and their salts, Polymethacrylic acids and their salts, hydroxyethyl methacrylate homopolymers and copolymers, hydroxyethyl acrylate homopolymers and copolymers, hydroxypropyl methacrylate homopolymers and copolymers, hydroxypropyl acrylate homopolymers and copolymers, hydroxybutyl methacrylate homopolymers Polymers and copolymers, homopolymers and copolymers of hydroxybutyl acrylate, polyethylene glycol , Hydroxypropylene polymers, polyvinyl alcohols, hydrolyzed polyvinyl acetate, polyvinyl formal, polyvinyl butyral, polyvinyl pyrrolidone, acrylamide homopolymers and copolymers having a hydrolysis degree of 60 mol% or more, preferably 80 mol% or more Methacrylamide homopolymers and polymers, N-methylolacrylamide homopolymers and copolymers, polyvinylpyrrolidone, alcohol-soluble nylon, polyether of 2,2-bis- (4-hydroxyphenyl) -propane and epichlorohydrin, etc. Is mentioned.

  The binder polymer preferably has a mass average molar mass of 5000 or more, more preferably 10,000 to 300,000, and a number average molar mass of 1000 or more, preferably 2000 to 250,000. Is more preferable. The polydispersity (mass average molar mass / number average molar mass) is preferably 1.1 to 10.

  The binder polymer can be obtained by purchasing a commercial product or synthesizing it by a known method.

The content of the binder polymer is 5 to 90% by mass, preferably 5 to 80% by mass, and more preferably 10 to 70% by mass with respect to the total solid content of the image recording layer. Within this range, good image area strength and image formability can be obtained.
Further, (C) the polymerizable compound and the binder polymer are preferably used in a mass ratio of 0.5 / 1 to 4/1.

<(E) Microcapsule and / or microgel>
In the present invention, several modes can be used as a method of incorporating the image recording layer constituent components (A) to (C) and other constituent components into the image recording layer. One is a molecular dispersion type image recording layer in which the constituent components are dissolved and applied in an appropriate solvent as described in, for example, JP-A-2002-287334. In another embodiment, for example, as described in JP-A-2001-277740 and JP-A-2001-277742, all or part of the constituent components are encapsulated in microcapsules and contained in the image recording layer. It is a microcapsule type image recording layer. Further, in the microcapsule type image recording layer, the constituent component can be contained outside the microcapsule. Here, it is preferable that the microcapsule-type image recording layer includes a hydrophobic constituent component in the microcapsule and a hydrophilic constituent component outside the microcapsule.
As still another embodiment, an embodiment in which the image recording layer contains crosslinked resin particles, that is, microgel, can be mentioned. The microgel may contain a part of the constituent components (A) to (C) in and / or on the surface thereof. In particular, an embodiment in which (C) a reactive microgel is formed by having a polymerizable compound on the surface thereof is particularly preferable from the viewpoint of image forming sensitivity and printing durability.
In order to obtain better on-press developability, the image recording layer is preferably a microcapsule type or microgel type image recording layer.

  As a method for microencapsulating or microgelling the components of the image recording layer, known methods can be applied.

  For example, as a method for producing microcapsules, a method using coacervation found in U.S. Pat. Nos. 2,800,547 and 2,800,498, U.S. Pat. No. 3,287,154, JP-B-38-19574, 42-446 by the interfacial polymerization method, US Pat. No. 3,418,250, US Pat. No. 3,660,304 by polymer precipitation method, US Pat. No. 3,796,669, isocyanate polyol A method using a wall material, a method using an isocyanate wall material found in US Pat. No. 3,914,511, and a urea-formaldehyde system found in US Pat. Nos. 4,001,140, 4,087,376 and 4,089,802. Or urea formaldehyde-resorcinol A method using a wall forming material, a method using a wall material such as melamine-formaldehyde resin, hydroxycellulose, etc. found in US Pat. No. 4,025,445, and Japanese Patent Publication Nos. 36-9163 and 51-9079. In situ method by monomer polymerization, spray drying method found in British Patent No. 930422, US Pat. No. 3,111,407, electrolytic dispersion cooling method seen in British Patent Nos. 952807, 967074, etc. However, it is not limited to these.

  A preferable microcapsule wall used in the present invention has a three-dimensional cross-linking and has a property of swelling with a solvent. From such a viewpoint, the wall material of the microcapsule is preferably polyurea, polyurethane, polyester, polycarbonate, polyamide, and a mixture thereof, and particularly preferably polyurea and polyurethane. Moreover, you may introduce | transduce into the microcapsule wall the compound which has crosslinkable functional groups, such as an ethylenically unsaturated bond which can be introduce | transduced into the binder polymer mentioned later.

On the other hand, as a method for preparing the microgel, granulation by interfacial polymerization described in JP-B-38-19574 and JP-A-42-446, as described in JP-A-5-61214, etc. It is possible to utilize granulation by non-aqueous dispersion polymerization. However, it is not limited to these methods.
As the method using the interfacial polymerization, the known microcapsule production method described above can be applied.

  Preferred microgels used in the present invention are those granulated by interfacial polymerization and having three-dimensional crosslinking. From such a viewpoint, the material to be used is preferably polyurea, polyurethane, polyester, polycarbonate, polyamide, and a mixture thereof, and polyurea and polyurethane are particularly preferable.

  The average particle size of the microcapsules or microgel is preferably 0.01 to 3.0 μm. 0.05-2.0 micrometers is further more preferable, and 0.10-1.0 micrometer is especially preferable. Within this range, good resolution and stability over time can be obtained.

<Other image recording layer components>
The image recording layer of the present invention can further contain various additives as required. These will be described below.

<1> Surfactant In the image recording layer of the present invention, a surfactant can be used in order to promote on-press developability or gum developability and to improve the coated surface state. Examples of the surfactant include nonionic surfactants, anionic surfactants, cationic surfactants, amphoteric surfactants, and fluorosurfactants. Surfactant may be used independently and may be used in combination of 2 or more type.

  The nonionic surfactant used for this invention is not specifically limited, A conventionally well-known thing can be used. For example, polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, glycerin fatty acid partial esters, sorbitan fatty acid partial esters, pentaerythritol Fatty acid partial esters, propylene glycol mono fatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, polyglycerin fatty acid partial esters, Polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acid diethanolamides, N N- bis-2-hydroxyalkylamines, polyoxyethylene alkylamines, triethanolamine fatty acid ester, trialkylamine oxide, polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol.

  The anionic surfactant used in the present invention is not particularly limited, and conventionally known anionic surfactants can be used. For example, fatty acid salts, abietic acid salts, hydroxyalkane sulfonates, alkane sulfonates, dialkyl sulfosuccinate esters, linear alkyl benzene sulfonates, branched alkyl benzene sulfonates, alkyl naphthalene sulfonates, alkyl phenoxy poly Oxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium salt, N-alkyl sulfosuccinic acid monoamide disodium salt, petroleum sulfonates, sulfated beef oil, fatty acid alkyl esters Sulfates, alkyl sulfates, polyoxyethylene alkyl ether sulfates, fatty acid monoglyceride sulfates, polyoxyethylene alcohol Ruphenyl ether sulfates, polyoxyethylene styryl phenyl ether sulfates, alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl phenyl ether phosphates, styrene / maleic anhydride Examples thereof include partial saponification products of polymers, partial saponification products of olefin / maleic anhydride copolymers, and naphthalene sulfonate formalin condensates.

The cationic surfactant used in the present invention is not particularly limited, and conventionally known cationic surfactants can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.
The amphoteric surfactant used in the present invention is not particularly limited, and conventionally known amphoteric surfactants can be used. Examples thereof include carboxybetaines, aminocarboxylic acids, sulfobetaines, aminosulfuric esters, and imidazolines.

  Of the above surfactants, the term “polyoxyethylene” can be read as “polyoxyalkylene” such as polyoxymethylene, polyoxypropylene, polyoxybutylene, etc. These surfactants can also be used.

  More preferable surfactants include fluorine-based surfactants containing a perfluoroalkyl group in the molecule. Examples of such fluorosurfactants include anionic types such as perfluoroalkyl carboxylates, perfluoroalkyl sulfonates, and perfluoroalkyl phosphates; amphoteric types such as perfluoroalkyl betaines; Cation type such as trimethylammonium salt; perfluoroalkylamine oxide, perfluoroalkylethylene oxide adduct, oligomer containing perfluoroalkyl group and hydrophilic group, oligomer containing perfluoroalkyl group and lipophilic group, perfluoroalkyl Nonionic types such as an oligomer containing a group, a hydrophilic group and a lipophilic group, and a urethane containing a perfluoroalkyl group and a lipophilic group. Moreover, the fluorine-type surfactant described in each gazette of Unexamined-Japanese-Patent No. 62-170950, 62-226143, and 60-168144 is also mentioned suitably.

Surfactant can be used individually or in combination of 2 or more types.
The content of the surfactant is preferably 0.001 to 10% by mass and more preferably 0.01 to 5% by mass with respect to the total solid content of the image recording layer.

<2> Colorant In the image recording layer of the present invention, a dye having a large absorption in the visible light region can be used as an image colorant. Specifically, Oil Yellow # 101, Oil Yellow # 103, Oil Pink # 312, Oil Green BG, Oil Blue BOS, Oil Blue # 603, Oil Black BY, Oil Black BS, Oil Black T-505 (orientated chemistry) Kogyo Co., Ltd.), Victoria Pure Blue, Crystal Violet (CI42555), Methyl Violet (CI42535), Ethyl Violet, Rhodamine B (CI145170B), Malachite Green (CI42000), Methylene Blue (CI522015), etc., and JP-A-62-2 And dyes described in No. 293247. Also, pigments such as phthalocyanine pigments, azo pigments, carbon black, titanium oxide, etc. can be suitably used.
When these colorants are used, it is easy to distinguish between an image area after image formation and a non-image area, so it is preferable to add them. The addition amount is 0.01 to 10% by mass with respect to the total solid content of the image recording material.

<3> Print-out agent To the image-recording layer of the present invention, a compound that changes color by an acid or a radical can be added to form a print-out image. As such a compound, for example, various dyes such as diphenylmethane, triphenylmethane, thiazine, oxazine, xanthene, anthraquinone, iminoquinone, azo, and azomethine are effectively used.

  Specific examples include brilliant green, ethyl violet, methyl green, crystal violet, basic fuchsin, methyl violet 2B, quinaldine red, rose bengal, methanyl yellow, thymol sulfophthalein, xylenol blue, methyl orange, paramethyl red, Congo Fred, Benzopurpurin 4B, α-Naphthyl Red, Nile Blue 2B, Nile Blue A, Methyl Violet, Malachite Green, Parafuchsin, Victoria Pure Blue BOH [manufactured by Hodogaya Chemical Co., Ltd.], Oil Blue # 603 [Orient Chemical Industry Co., Ltd.], Oil Pink # 312 [Made by Orient Chemical Co., Ltd.], Oil Red 5B [Made by Orient Chemical Co., Ltd.], Oil Scarlet # 308 [Orient Gaku Kogyo Co., Ltd.], Oil Red OG [Orient Chemical Co., Ltd.], Oil Red RR [Orient Chemical Co., Ltd.], Oil Green # 502 [Orient Chemical Co., Ltd.], Spiron Red BEH Special [made by Hodogaya Chemical Co., Ltd.], m-cresol purple, cresol red, rhodamine B, rhodamine 6G, sulforhodamine B, auramine, 4-p-diethylaminophenyliminonaphthoquinone, 2-carboxyanilino-4-p- Diethylaminophenyliminonaphthoquinone, 2-carboxystearylamino-4-pN, N-bis (hydroxyethyl) amino-phenyliminonaphthoquinone, 1-phenyl-3-methyl-4-p-diethylaminophenylimino-5-pyrazolone, 1-β-naphthyl-4- - dyes and p of diethylamino phenyl imino-5-pyrazolone, p ', p "- hexamethyl triamnotriphenylmethane (leuco crystal violet), and a leuco dye such as Pergascript Blue SRB (manufactured by Ciba-Geigy).

  In addition to the above, a leuco dye known as a material for thermal paper or pressure-sensitive paper is also suitable. Specific examples include crystal violet lactone, malachite green lactone, benzoylleucomethylene blue, 2- (N-phenyl-N-methylamino) -6- (Np-tolyl-N-ethyl) amino-fluorane, 2-anilino. -3-methyl-6- (N-ethyl-p-toluidino) fluorane, 3,6-dimethoxyfluorane, 3- (N, N-diethylamino) -5-methyl-7- (N, N-dibenzylamino) ) -Fluorane, 3- (N-cyclohexyl-N-methylamino) -6-methyl-7-anilinofluorane, 3- (N, N-diethylamino) -6-methyl-7-anilinofluorane, 3 -(N, N-diethylamino) -6-methyl-7-xylidinofluorane, 3- (N, N-diethylamino) -6-methyl-7-chloro Fluorane, 3- (N, N-diethylamino) -6-methoxy-7-aminofluorane, 3- (N, N-diethylamino) -7- (4-chloroanilino) fluorane, 3- (N, N-diethylamino) -7-chlorofluorane, 3- (N, N-diethylamino) -7-benzylaminofluorane, 3- (N, N-diethylamino) -7,8-benzofluorane, 3- (N, N-dibutyl) Amino) -6-methyl-7-anilinofluorane, 3- (N, N-dibutylamino) -6-methyl-7-xylidinofluorane, 3-piperidino-6-methyl-7-anilinofluorane 3-pyrrolidino-6-methyl-7-anilinofluorane, 3,3-bis (1-ethyl-2-methylindol-3-yl) phthalide, 3,3-bis (1-n-butyl- -Methylindol-3-yl) phthalide, 3,3-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide, 3- (4-diethylamino-2-ethoxyphenyl) -3- (1-ethyl- 2-methylindol-3-yl) -4-zaphthalide, 3- (4-diethylaminophenyl) -3- (1-ethyl-2-methylindol-3-yl) phthalide, and the like.

  A suitable addition amount of the dye that changes color by an acid or a radical is 0.01 to 10% by mass with respect to the solid content of the image recording layer.

<4> Polymerization inhibitor A small amount of a thermal polymerization inhibitor is added to the image recording layer of the present invention in order to prevent unnecessary thermal polymerization of the polymerizable compound (C) during the production or storage of the image recording layer. It is preferable to do this.
Examples of the thermal polymerization inhibitor include hydroquinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4'-thiobis (3-methyl-6-t- (Butylphenol), 2,2'-methylenebis (4-methyl-6-tert-butylphenol), N-nitroso-N-phenylhydroxylamine aluminum salt are preferred. The addition amount of the thermal polymerization inhibitor is preferably about 0.01 to about 5% by mass with respect to the total solid content of the image recording layer.

<5> Higher fatty acid derivative and the like In the image recording layer of the present invention, a higher fatty acid derivative such as behenic acid and behenic acid amide is added to prevent polymerization inhibition due to oxygen, and the drying process after coating is performed. May be unevenly distributed on the surface of the image recording layer. The amount of the higher fatty acid derivative added is preferably about 0.1 to about 10% by mass with respect to the total solid content of the image recording layer.

<6> Plasticizer The image recording layer of the present invention may contain a plasticizer in order to improve the on-press developability.
Examples of the plasticizer include phthalates such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, diisobutyl phthalate, dioctyl phthalate, octyl capryl phthalate, dicyclohexyl phthalate, ditridecyl phthalate, butyl benzyl phthalate, diisodecyl phthalate, diallyl phthalate; Glycol esters such as glycol phthalate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, butyl phthalyl butyl glycolate, triethylene glycol dicaprylate; Phosphate esters such as tricresyl phosphate and triphenyl phosphate Diisobutyl adipate, dioctyl adipate, dimethyl sebacate, dibutyl sebacate, dioct Ruazereto, aliphatic dibasic acid esters such as dibutyl maleate; polyglycidyl methacrylate, triethyl citrate, glycerin triacetyl ester, butyl laurate in.
The plasticizer content is preferably about 30% by mass or less based on the total solid content of the image recording layer.

<7> Inorganic fine particles The image recording layer of the present invention may contain inorganic fine particles in order to improve the cured film strength and on-press developability.
As the inorganic fine particles, for example, silica, alumina, magnesium oxide, titanium oxide, magnesium carbonate, calcium alginate, or a mixture thereof is preferably exemplified. These can be used for strengthening the film, strengthening the interfacial adhesion by surface roughening, and the like.
The inorganic fine particles preferably have an average particle size of 5 nm to 10 μm, and more preferably 0.5 μm to 3 μm. Within the above range, it is possible to form a non-image portion having excellent hydrophilicity, which is stably dispersed in the image recording layer, sufficiently retains the film strength of the image recording layer, and hardly causes stains during printing.
The inorganic fine particles as described above can be easily obtained as a commercial product such as a colloidal silica dispersion.
The content of the inorganic fine particles is preferably 40% by mass or less, and more preferably 30% by mass or less, based on the total solid content of the image recording layer.

<8> Low molecular weight hydrophilic compound The image recording layer of the present invention may contain a hydrophilic low molecular weight compound in order to improve the on-press developability or gum developability. Examples of the hydrophilic low-molecular compound include water-soluble organic compounds such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol and the like, and ether or ester derivatives thereof, glycerin, Polyhydroxys such as pentaerythritol, organic amines such as triethanolamine and diethanolamine monoethanolamine and salts thereof, organic sulfonic acids such as alkylsulfonic acid, toluenesulfonic acid and benzenesulfonic acid and salts thereof, alkylsulfamic acid and the like Organic sulfamic acids and their salts, organic sulfuric acids and their salts such as alkyl sulfuric acid and alkyl ether sulfuric acid, organic phosphonic acids and their salts such as phenylphosphonic acid, tartaric acid, sulphate , Citric acid, malic acid, lactic acid, gluconic acid, organic carboxylic acids and salts thereof and amino acids and the like.

  Among these, organic sulfonic acid, organic sulfamic acid, and sodium salt or lithium salt of organic sulfuric acid are preferably used.

  Specific examples of organic sulfonates include sodium normal butyl sulfonate, sodium isobutyl sulfonate, sodium sec-butyl sulfonate, sodium tert-butyl sulfonate, sodium normal pentyl sulfonate, and sodium 1-ethylpropyl sulfonate. Sodium hexyl sulfonate, sodium 1,2-dimethylpropyl sulfonate, sodium 2-ethylbutyl sulfonate, sodium cyclohexyl sulfonate, sodium normal heptyl sulfonate, sodium normal octyl sulfonate, sodium tert-octyl sulfonate, normal Sodium nonyl sulfonate, sodium allyl sulfonate, sodium 2-methylallyl sulfonate, sodium benzene sulfonate Sodium p-toluenesulfonate, sodium p-hydroxybenzenesulfonate, sodium p-styrenesulfonate, dimethyl-5-sulfonate sodium isophthalate, disodium 1,3-benzenedisulfonate, 1,3,5-benzenetri Trisodium sulfonate, sodium p-chlorobenzenesulfonate, sodium 3,4-dichlorobenzenesulfonate, sodium 1-naphthylsulfonate, sodium 2-naphthylsulfonate, sodium 4-hydroxynaphthylsulfonate, 1,5-naphthyldisulfone Examples thereof include disodium acid, disodium 2,6-naphthyldisulfonate, trisodium 1,3,6-naphthyltrisulfonate, and lithium salt exchangers thereof.

  Specific examples of the organic sulfamate include sodium normal butyl sulfamate, sodium isobutyl sulfamate, sodium tert-butyl sulfamate, sodium normal pentyl sulfamate, sodium 1-ethylpropyl sulfamate, sodium normal hexyl sulfamate, Examples include sodium 1,2-dimethylpropylsulfamate, sodium 2-ethylbutylsulfamate, sodium cyclohexylsulfamate, and lithium salt exchangers thereof.

  These compounds have a small hydrophobic part structure and almost no surface-active action, and are clearly distinguished from the above-mentioned surfactants in which long-chain alkyl sulfonates and long-chain alkyl benzene sulfonates are used favorably. .

  As the organic sulfate, a compound represented by the following general formula (iii) is preferably used.

  In the general formula (iii), R represents a substituted or unsubstituted alkyl group, alkenyl group, alkynyl group, aryl group or heterocyclic group, m represents an integer of 1 to 4, and X represents sodium or potassium. Or represents lithium.

  R is preferably a substituted or unsubstituted, linear, branched or cyclic alkyl group having 1 to 12 carbon atoms, alkenyl group having 1 to 12 carbon atoms, alkynyl group having 1 to 12 carbon atoms, carbon number Examples include 20 or less aryl groups. Examples of the substituent include a linear, branched or cyclic alkyl group having 1 to 12 carbon atoms, an alkenyl group having 1 to 12 carbon atoms, an alkynyl group having 1 to 12 carbon atoms, a halogen atom, and an aryl having 20 or less carbon atoms. Groups.

  Preferred examples of the compound represented by the general formula (iii) include sodium oxyethylene-2-ethylhexyl ether sulfate, sodium dioxyethylene-2-ethylhexyl ether sulfate, potassium dioxyethylene-2-ethylhexyl ether sulfate, dioxy Ethylene-2-ethylhexyl ether lithium sulfate, sodium trioxyethylene-2-ethylhexyl ether sulfate, sodium tetraoxyethylene-2-ethylhexyl ether sulfate, sodium dioxyethylene hexyl ether sulfate, sodium dioxyethylene octyl ether sulfate, dioxyethylene Examples include sodium lauryl ether sulfate. Most preferred compounds include sodium dioxyethylene-2-ethylhexyl ether sulfate, potassium dioxyethylene-2-ethylhexyl ether sulfate, and lithium dioxyethylene-2-ethylhexyl ether sulfate.

The amount of these low molecular weight hydrophilic compounds added to the image recording layer is preferably 0.5% by mass or more and 20% by mass or less of the total solid content of the image recording layer. More preferably, they are 1 mass% or more and 10 mass% or less, More preferably, they are 2 mass% or more and 8 mass% or less. In this range, good on-press developability or gum developability and printing durability can be obtained.
These compounds may be used alone or in combination of two or more.

<9> Grease-sensitizing agent In the lithographic printing plate precursor according to the invention, a phosphonium compound can be added to the image recording layer and / or the protective layer in order to improve the inking property. Examples of suitable phosphonium compounds include compounds represented by the following general formula (iv) described in JP-A-2006-297907 or the following formula (v) described in JP-A-2007-50660.

In the general formula (iv), R _{1 to} R ₄ are each independently an alkyl group, alkenyl group, alkynyl group, cycloalkyl group, alkoxy group, aryl group, aryloxy group, alkylthio group which may have a substituent. Represents a group, a heterocyclic group or a hydrogen atom. At least two of R _{1 to} R ₄ may combine to form a ring. X ⁻ represents a counter anion.

In (v), Ar _{1 to} Ar ₆ each independently represents an aryl group or a heterocyclic group, L represents a divalent linking group, X ⁿ⁻ represents an n-valent counter anion, and n represents 1 Represents an integer of ˜3, and m represents a number satisfying nx m = 2. Here, as the aryl group, phenyl group, naphthyl group, tolyl group, xylyl group, fluorophenyl group, chlorophenyl group, bromophenyl group, methoxyphenyl group, ethoxyphenyl group, dimethoxyphenyl group, methoxycarbonylphenyl group, dimethylaminophenyl A group and the like are preferable. Examples of the heterocyclic group include a pyridyl group, a quinolyl group, a pyrimidinyl group, a thienyl group, and a furyl group. L represents a divalent linking group. 6-15 are preferable and, as for carbon number in a coupling group, More preferably, it is a C6-C12 coupling group. X ⁿ⁻ represents an n-valent counter anion, and preferred examples include halogen anions such as Cl ⁻ , Br ⁻ and I ⁻ , sulfonate anions, carboxylate anions, sulfate ester anions, PF ₆ ⁻ , BF ₄ ⁻ , And perchlorate anion. Among these, halogen anions such as Cl ⁻ , Br ⁻ and I ⁻ , sulfonate anions, and carboxylate anions are particularly preferable.

  Specific examples of the phosphonium compound represented by the general formula (iv) or (v) are shown below.

  The amount of the phosphonium compound added to the image recording layer or protective layer is preferably 0.01 to 20% by mass, more preferably 0.05 to 10% by mass, and more preferably 0.1 to 5% by mass in the solid content of each layer. Most preferred. Within these ranges, good ink fillability can be obtained.

<Formation of image recording layer>
The image recording layer of the present invention is coated by preparing a coating solution by dispersing or dissolving each of the necessary components in a solvent. Solvents used here include ethylene dichloride, cyclohexanone, methyl ethyl ketone, methanol, ethanol, propanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, 2-methoxyethyl acetate, 1-methoxy-2-propyl acetate, dimethoxy Examples include ethane, methyl lactate, ethyl lactate, N, N-dimethylacetamide, N, N-dimethylformamide, tetramethylurea, N-methylpyrrolidone, dimethyl sulfoxide, sulfolane, γ-butyllactone, toluene, water, and the like. However, the present invention is not limited to this. These solvents are used alone or in combination. The solid content concentration of the coating solution is preferably 1 to 50% by mass.
The image recording layer of the present invention can be formed by preparing a plurality of coating solutions in which the same or different components are dispersed or dissolved in the same or different solvents, and repeating a plurality of coating and drying operations.

Further, the coating amount (solid content) of the image recording layer on the support obtained after coating and drying varies depending on the use, but generally 0.3 to 3.0 g / m ² is preferable. Within this range, good sensitivity and good film properties of the image recording layer can be obtained.
Various methods can be used as a coating method. Examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.

(Protective layer)
In the lithographic printing plate precursor according to the invention, a protective layer (overcoat layer) is preferably provided on the image recording layer. In addition to the function of suppressing the image formation inhibition reaction by blocking oxygen, the protective layer also has functions such as preventing scratches in the image recording layer and preventing ablation during high-illuminance laser exposure. Below, a protective layer component etc. are demonstrated.

  Usually, the exposure processing of a lithographic printing plate is carried out in the atmosphere. The image forming reaction in the image recording layer caused by the exposure process can be inhibited by low molecular compounds such as oxygen and basic substances present in the atmosphere. The protective layer prevents low molecular compounds such as oxygen and basic substances from entering the image recording layer, and as a result, suppresses image formation inhibition reaction in the air. Therefore, the property desired for the protective layer is to reduce the permeability of low-molecular compounds such as oxygen, and furthermore, the transparency of light used for exposure is good, and the adhesiveness with the image recording layer is excellent. And it can be easily removed in an on-press development process after exposure. The protective layer having such characteristics is described in, for example, US Pat. No. 3,458,311 and Japanese Patent Publication No. 55-49729.

  As a material used for the protective layer, either a water-soluble polymer or a water-insoluble polymer can be appropriately selected and used. Specifically, for example, polyvinyl alcohol, modified polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl imidazole, polyacrylic acid, polyacrylamide, partially saponified product of polyvinyl acetate, ethylene-vinyl alcohol copolymer, water-soluble cellulose derivative, gelatin, starch Examples thereof include water-soluble polymers such as derivatives and gum arabic, and polymers such as polyvinylidene chloride, poly (meth) acrylonitrile, polysulfone, polyvinyl chloride, polyethylene, polycarbonate, polystyrene, polyamide, and cellophane. These may be used in combination of two or more as required.

  A relatively useful material among the above materials includes water-soluble polymer compounds having excellent crystallinity. Specifically, water-soluble acrylic resins such as polyvinyl alcohol, polyvinyl pyrrolidone, polyvinyl imidazole, and polyacrylic acid, gelatin, gum arabic, and the like are suitable. Among these, water can be applied as a solvent, and at the time of printing Polyvinyl alcohol, polyvinyl pyrrolidone, and polyvinyl imidazole are preferable from the viewpoint that they are easily removed by the fountain solution. Among them, polyvinyl alcohol (PVA) gives the best results for basic properties such as oxygen barrier properties and development removability.

  The polyvinyl alcohol that can be used in the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains a substantial amount of an unsubstituted vinyl alcohol unit having the required water solubility. Similarly, a part may contain other copolymerization components. For example, various hydrophilic modification sites such as anion modification sites modified with anions such as carboxyl groups and sulfo groups, cation modification sites modified with cations such as amino groups and ammonium groups, silanol modification sites, and thiol modification sites are randomly selected. Polyvinyl alcohol having various degrees of polymerization, the anion-modified site, the cation-modified site, the silanol-modified site, the thiol-modified site, the alkoxyl-modified site, the sulfide-modified site, and the ester modification of vinyl alcohol and various organic acids. Polyvinyl alcohol having various degrees of polymerization having various modified sites such as a site, an ester-modified site of the anion-modified site and alcohols, an epoxy-modified site, etc. at the polymer chain end is also preferably used.

  Suitable examples of the modified polyvinyl alcohol include compounds having a hydrolysis degree of 71 to 100 mol% and a polymerization degree in the range of 300 to 2400. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405, PVA- 420, PVA-613, L-8 and the like. Examples of the modified polyvinyl alcohol include KL-318, KL-118, KM-618, KM-118, SK-5102 having an anion-modified site, C-318, C-118, and CM-318 having a cation-modified site. M-205 and M-115 having terminal thiol modification sites, MP-103, MP-203, MP-102 and MP-202 having terminal sulfide modification sites, and ester modification sites with higher fatty acids HL-12E, HL-1203, and other reactive silane-modified R-1130, R-2105, R-2130, and the like.

The protective layer preferably contains an inorganic stratiform compound. The layered compound is a particle having a thin plate-like shape. For example, the following general formula A (B, C) _2-5 D ₄ O ₁₀ (OH, F, O) ₂
[However, A is any of Li, K, Na, Ca, Mg, organic cation, B and C are any of Fe (II), Fe (III), Mn, Al, Mg, V, and D is Si or Al. And mica groups such as natural mica and synthetic mica, talc, teniolite, montmorillonite, saponite, hectorite, zirconium phosphate and the like represented by the formula 3MgO.4SiO.H ₂ O.
Examples of the natural mica include muscovite, soda mica, phlogopite, biotite and sericite. Further, as the synthetic mica, non-swelling mica such as fluorine phlogopite mica ₃ (AlSi ₃ O ₁₀ ) F ₂ , potassium tetrasilicon mica KMg _2.5 Si ₄ O ₁₀ ) F ₂ , and Na tetrasilicic mica NaMg _2.5 (Si ₄ O ₁₀ ) F ₂ , Na or Li Tenniolite (Na, Li) Mg ₂ Li (Si ₄ O ₁₀ ) F ₂ , Montmorillonite Na or Li Hectorite (Na, Li) _1/8 Mg Swellable mica such as _2/5 Li _1/8 (Si ₄ O ₁₀ ) F ₂ can be used. Synthetic smectite is also useful.

Among the above layered compounds, fluorine-based swellable mica which is a synthetic layered compound is particularly useful. That is, swellable clay minerals such as mica, montmorillonite, saponite, hectorite, bentonite, etc. have a laminated structure composed of unit crystal lattice layers with a thickness of about 10 to 15 mm, and metal atom substitution in the lattice is other than Significantly greater than viscous minerals. As a result, the lattice layer has a shortage of positive charges, and in order to compensate for this, organic cations such as Li ⁺ , Na ⁺ , Ca ²⁺ , Mg ²⁺ , amine salts, quaternary ammonium salts, phosphonium salts and sulfonium salts are provided between the layers. Adsorbs cations. These layered compounds swell with water. If shear is applied in this state, it will be easily cleaved to form a stable sol in water. Bentonite and swelling synthetic mica have this tendency.

As the shape of the layered compound, from the viewpoint of diffusion control, the thinner the better, the better the plane size as long as the smoothness of the coated surface and the transmittance of actinic rays are not impaired. Accordingly, the aspect ratio is 20 or more, preferably 100 or more, particularly preferably 200 or more. The aspect ratio is the ratio of the thickness to the major axis of the particle, and can be measured, for example, from a projected view of the particle by a micrograph. The larger the aspect ratio, the greater the effect that can be obtained.
As for the particle diameter of the layered compound, the average major axis is 0.3 to 20 μm, preferably 0.5 to 10 μm, particularly preferably 1 to 5 μm. When the particle diameter is smaller than 0.3 μm, the suppression of permeation of oxygen and moisture is insufficient, and the effect cannot be sufficiently exhibited. On the other hand, if it is larger than 20 μm, the dispersion stability in the coating solution is insufficient, resulting in a problem that stable coating cannot be performed. The average thickness of the particles is 0.1 μm or less, preferably 0.05 μm or less, and particularly preferably 0.01 μm or less. For example, among the inorganic layered compounds, the size of the swellable synthetic mica that is a representative compound is about 1 to 50 nm in thickness and about 1 to 20 μm in surface size.

  When the inorganic layered compound particles having such a large aspect ratio are contained in the protective layer, the coating film strength is improved, and the permeation of oxygen and moisture can be effectively prevented. Deterioration is prevented, and even when stored for a long time under high-humidity conditions, the storage stability of the planographic printing plate precursor does not deteriorate due to changes in humidity, and the storage stability is excellent.

  Next, an example of a general dispersion method when a layered compound is used for the protective layer will be described. First, 5 to 10 parts by mass of the swellable laminar compound mentioned above as a preferred laminar compound is added to 100 parts by mass of water, and the mixture is thoroughly swelled and swollen. Examples of the disperser used here include various mills that disperse mechanically by applying a direct force, a high-speed stirring disperser having a large shearing force, and a disperser that provides high-intensity ultrasonic energy. Specifically, ball mill, sand grinder mill, visco mill, colloid mill, homogenizer, tisol bar, polytron, homomixer, homo blender, ketdy mill, jet agitator, capillary emulsifier, liquid siren, electrostrictive ultrasonic generator, An emulsifying device having a Paulman whistle can be used. A dispersion of 5 to 10% by mass of the inorganic stratiform compound dispersed by the above method is highly viscous or gelled and has very good storage stability. When preparing the protective layer coating solution using this dispersion, it is preferably prepared by diluting with water and stirring sufficiently, and then blending with the binder solution.

  It is preferable that content of the inorganic stratiform compound in a protective layer is 5/1-1/100 by mass ratio with respect to the quantity of the binder used for a protective layer. Even when a plurality of types of inorganic layered compounds are used in combination, the total amount of these inorganic layered compounds is preferably the above-described mass ratio.

The inorganic layered compound can be added not only to the protective layer but also to the image recording layer. Addition of an inorganic layered compound to the image recording layer is useful for improving printing durability, polymerization efficiency (sensitivity), and stability over time.
The amount of the inorganic stratiform compound added to the image recording layer is preferably from 0.1 to 50 mass%, more preferably from 0.3 to 30 mass%, most preferably from 1 to 10 mass%, based on the solid content of the image recording layer. preferable.

  As other additives for the protective layer, glycerin, dipropylene glycol, and the like can be added in an amount corresponding to several mass% with respect to the water-soluble or water-insoluble polymer to give flexibility. Anionic surfactants such as sodium alkyl sulfonate; amphoteric surfactants such as alkylaminocarboxylate and alkylaminodicarboxylate; nonionic surfactants such as polyoxyethylene alkylphenyl ether can be added. These active agents can be added in an amount of 0.1 to 100% by mass with respect to the water-soluble or water-insoluble polymer.

  In order to improve the adhesion to the image area, for example, JP-A-49-70702 and British Patent Application No. 1303578 disclose an acrylic polymer in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesion can be obtained by mixing 20 to 60% by mass of a water-based emulsion, a water-insoluble vinylpyrrolidone-vinyl acetate copolymer and the like, and laminating the mixture on an image recording layer. Any of these known techniques can be used in the present invention.

  Furthermore, other functions can be imparted to the protective layer. For example, by adding a colorant (for example, a water-soluble dye) that is excellent in the transparency of infrared rays used for exposure and that can efficiently absorb light of other wavelengths, safe light is not caused. Suitability can be improved.

The protective layer is formed by applying and drying a protective layer coating solution prepared by dispersing or dissolving the protective layer component in a solvent on the image recording layer. The coating solvent can be appropriately selected in relation to the binder, but when a water-soluble polymer is used, it is preferable to use distilled water or purified water.
This protective layer coating solution includes known anionic surfactants, nonionic surfactants, cationic surfactants, fluorosurfactants and water-soluble plasticizers for improving the physical properties of the coating. Additives can be added. Examples of the water-soluble plasticizer include propionamide, cyclohexanediol, glycerin, sorbitol and the like. A water-soluble (meth) acrylic polymer can also be added. Furthermore, a known additive for improving the adhesion with the image recording layer and the temporal stability of the coating solution may be added to the coating solution.
The method for applying the protective layer is not particularly limited, and a known method such as the method described in US Pat. No. 3,458,311 or Japanese Patent Publication No. 55-49729 can be applied. . Specific examples of the protective layer include blade coating, air knife coating, gravure coating, roll coating coating, spray coating, dip coating, and bar coating.

The coating amount of the protective layer of the coating amount after drying is preferably in the range of 0.01 to 10 g / ^{m 2,} more preferably in the range of 0.02 to 3 g / ^{m 2,} and most preferably 0. in the range of 02~1g / ^{m 2.}

(Support)
The support used for the lithographic printing plate precursor according to the invention uses an aluminum plate.
The aluminum plate is a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of foreign elements, or a plastic laminated on a thin film of aluminum or an aluminum alloy. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is preferably 10% by mass or less. In the present invention, a pure aluminum plate is preferable, but completely pure aluminum is difficult to manufacture in terms of refining technology, and therefore may contain a slightly different element. The composition of the aluminum plate is not specified, and a publicly known material can be used as appropriate.

  The thickness of the support is preferably from 0.1 to 0.6 mm, more preferably from 0.15 to 0.4 mm.

  Prior to using the aluminum plate, it is preferable to perform a surface treatment such as roughening treatment or anodizing treatment. By the surface treatment, it is easy to improve hydrophilicity and secure adhesion between the image recording layer and the support. Prior to the roughening treatment of the aluminum plate, a degreasing treatment with a surfactant, an organic solvent, an alkaline aqueous solution or the like for removing rolling oil on the surface is performed as desired.

The surface roughening treatment of the aluminum plate is performed by various methods. For example, mechanical surface roughening treatment, electrochemical surface roughening treatment (surface roughening treatment for dissolving the surface electrochemically), chemical treatment, etc. Surface roughening treatment (roughening treatment that chemically selectively dissolves the surface).
As a method for the mechanical surface roughening treatment, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used. Moreover, the transcription | transfer method which transfers an uneven | corrugated shape with the roll which provided the unevenness | corrugation in the rolling stage of aluminum can also be used.
Examples of the electrochemical surface roughening treatment include a method in which an alternating current or a direct current is used in an electrolytic solution containing an acid such as hydrochloric acid or nitric acid. Another example is a method using a mixed acid as described in JP-A-54-63902.

  The surface-roughened aluminum plate is subjected to an alkali etching treatment using an aqueous solution of potassium hydroxide, sodium hydroxide or the like, if necessary, further neutralized, and if desired, wear resistant. In order to increase the anodic oxidation treatment.

As the electrolyte used for the anodizing treatment of the aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, hydrochloric acid, oxalic acid, chromic acid or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.
The conditions of anodizing treatment vary depending on the electrolyte used, and thus cannot be specified in general. dm ² , voltage 1 to 100 V, and electrolysis time 10 seconds to 5 minutes are preferable. The amount of the anodized film formed is preferably from 1.0 to 5.0 g / ^{m 2,} and more preferably 1.5 to 4.0 g / ^{m 2.} Within this range, good printing durability and good scratch resistance of the non-image area of the lithographic printing plate can be obtained.

  As the support used in the present invention, the substrate having the above-mentioned surface treatment and having an anodized film may be used as it is, but in order to further improve the adhesion to the upper layer, hydrophilicity, resistance to dirt, heat insulation, and the like. If necessary, it is immersed in an aqueous solution containing a hydrophilic compound and a micropore enlargement treatment or sealing treatment of an anodized film described in JP-A-2001-253181 or JP-A-2001-322365. The surface hydrophilization treatment to be performed can be appropriately selected and performed. Of course, the enlargement process and the sealing process are not limited to those described above, and any conventionally known methods can be performed. For example, as the sealing treatment, in addition to the vapor sealing, a single treatment with fluorinated zirconic acid, a treatment with sodium fluoride, and a vapor sealing with addition of lithium chloride are possible.

  The sealing treatment used in the present invention is not particularly limited, and a conventionally known method can be used. Among them, sealing treatment with an aqueous solution containing an inorganic fluorine compound, sealing treatment with water vapor, and hot water. Sealing treatment is preferred. Each will be described below.

<1> Sealing treatment with an aqueous solution containing an inorganic fluorine compound As the inorganic fluorine compound used for the sealing treatment with an aqueous solution containing an inorganic fluorine compound, a metal fluoride is preferably exemplified.
Specifically, for example, sodium fluoride, potassium fluoride, calcium fluoride, magnesium fluoride, sodium fluoride zirconate, potassium fluoride zirconate, sodium fluoride titanate, potassium fluoride titanate, zircon fluoride Ammonium acid, ammonium fluoride titanate, potassium fluoride titanate, zirconate fluoride, titanate fluoride, hexafluorosilicic acid, nickel fluoride, iron fluoride, phosphor fluoride, ammonium fluoride phosphate It is done. Of these, sodium fluorinated zirconate, sodium fluorinated titanate, fluorinated zirconic acid, and fluorinated titanic acid are preferable.

  The concentration of the inorganic fluorine compound in the aqueous solution is preferably 0.01% by mass or more, more preferably 0.05% by mass or more, from the viewpoint of sufficiently sealing the micropores of the anodized film. Further, in terms of dirtiness, it is preferably 1% by mass or less, and more preferably 0.5% by mass or less.

  It is preferable that the aqueous solution containing the inorganic fluorine compound further contains a phosphate compound. When the phosphate compound is contained, the hydrophilicity of the surface of the anodized film is improved, so that the on-press developability and stain resistance can be improved.

Suitable examples of the phosphate compound include phosphates of metals such as alkali metals and alkaline earth metals.
Specifically, for example, zinc phosphate, aluminum phosphate, ammonium phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, monoammonium phosphate, monopotassium phosphate, monosodium phosphate, dihydrogen phosphate Potassium, dipotassium hydrogen phosphate, calcium phosphate, sodium ammonium hydrogen phosphate, magnesium hydrogen phosphate, magnesium phosphate, ferrous phosphate, ferric phosphate, sodium dihydrogen phosphate, sodium phosphate, hydrogen phosphate Disodium, lead phosphate, diammonium phosphate, calcium dihydrogen phosphate, lithium phosphate, phosphotungstic acid, phosphotungstic acid, sodium phosphotungstate, ammonium phosphomolybdate, sodium phosphomolybdate, sodium phosphite , Tripolyphosphate Potassium, and sodium pyrophosphate. Of these, sodium dihydrogen phosphate, disodium hydrogen phosphate, potassium dihydrogen phosphate, and dipotassium hydrogen phosphate are preferable.
The combination of the inorganic fluorine compound and the phosphate compound is not particularly limited, but the aqueous solution contains at least sodium zirconate fluoride as the inorganic fluorine compound and contains at least sodium dihydrogen phosphate as the phosphate compound. Is preferred.

  The concentration of the phosphate compound in the aqueous solution is preferably 0.01% by mass or more, more preferably 0.1% by mass or more, from the viewpoint of improving the on-press developability and stain resistance. From the viewpoint of solubility, the content is preferably 20% by mass or less, and more preferably 5% by mass or less.

The ratio of each compound in the aqueous solution is not particularly limited, but the mass ratio of the inorganic fluorine compound and the phosphate compound is preferably 1/200 to 10/1, and preferably 1/30 to 2/1. Is more preferable.
The temperature of the aqueous solution is preferably 20 ° C. or higher, more preferably 40 ° C. or higher, preferably 100 ° C. or lower, more preferably 80 ° C. or lower.
The aqueous solution preferably has a pH of 1 or more, more preferably has a pH of 2 or more, preferably has a pH of 11 or less, and more preferably has a pH of 5 or less.
The method for sealing with an aqueous solution containing an inorganic fluorine compound is not particularly limited, and examples thereof include an immersion method and a spray method. These may be used alone or in combination, or may be used in combination of two or more.
Of these, the dipping method is preferred. When the treatment is performed using the dipping method, the treatment time is preferably 1 second or longer, more preferably 3 seconds or longer, and preferably 100 seconds or shorter, and 20 seconds or shorter. More preferred.

<2> Sealing treatment with water vapor Sealing treatment with water vapor includes, for example, a method in which pressurized or normal pressure water vapor is contacted with the anodized film continuously or discontinuously.
The temperature of the water vapor is preferably 80 ° C. or higher, more preferably 95 ° C. or higher, and preferably 105 ° C. or lower.
The water vapor pressure is preferably in the range (1.008 × 10 ^{5 to} 1.043 × 10 ⁵ Pa) from (atmospheric pressure−50 mmAq) to (atmospheric pressure + 300 mmAq).
Further, the time for which the water vapor is contacted is preferably 1 second or longer, more preferably 3 seconds or longer, 100 seconds or shorter, more preferably 20 seconds or shorter.

<3> Sealing treatment with hot water Examples of the sealing treatment with hot water include a method of immersing an aluminum plate on which an anodized film is formed in hot water.
The hot water may contain an inorganic salt (for example, phosphate) or an organic salt.
The temperature of the hot water is preferably 80 ° C. or higher, more preferably 95 ° C. or higher, and preferably 100 ° C. or lower.
Further, the time of immersion in hot water is preferably 1 second or longer, more preferably 3 seconds or longer, more preferably 100 seconds or shorter, and even more preferably 20 seconds or shorter.

  In the present invention, preferred hydrophilization treatments include US Pat. Nos. 2,714,066, 3,181,461, 3,280,734 and 3,902,734. There is an alkali metal silicate method as described in the book. In this method, the support is subjected to immersion treatment or electrolytic treatment with an aqueous solution such as sodium silicate. In addition, the treatment with potassium zirconate fluoride described in JP-B 36-22063, U.S. Pat. Nos. 3,276,868, 4,153,461 and 4,689, And a method of treating with polyvinylphosphonic acid as described in each specification of No.272.

  The support preferably has a center line average roughness of 0.10 to 1.2 μm. Within this range, good adhesion to the image recording layer, good printing durability and good stain resistance can be obtained.

(Back coat layer)
After surface treatment is performed on the support or after the above-described intermediate layer is formed, a backcoat layer can be provided on the back surface of the support, if necessary.
Examples of the back coat layer include hydrolysis and polycondensation of organic polymer compounds described in JP-A-5-45885, organic metal compounds or inorganic metal compounds described in JP-A-6-35174, and the like. Preferable examples include a coating layer made of a metal oxide. Of these, the use of silicon alkoxy compounds such as Si (OCH ₃ ) ₄ , Si (OC ₂ H ₅ ) ₄ , Si (OC ₃ H ₇ ) ₄ , Si (OC ₄ H ₉ ) ₄ is inexpensive. It is preferable in that it is easily available.

[Plate making method]
There are two modes for the plate making method of the lithographic printing plate precursor according to the invention. The first is on-press development and the second is gum development.

(On-press development method)
A step of performing image exposure of the lithographic printing plate precursor, and a printing step of printing by supplying printing ink and dampening water without performing any development treatment on the exposed lithographic printing plate precursor, An unexposed portion of the lithographic printing plate precursor is removed during the printing process. The imagewise exposure may be performed by first mounting the lithographic printing plate precursor on a printing machine, or the exposed lithographic printing plate precursor may be mounted on a printing machine, and then printing using the printing machine. By supplying ink and fountain solution and printing as it is, on-machine development processing at the initial stage of printing, that is, the image recording layer in the unexposed area is removed, and accordingly the hydrophilic support surface is formed. Exposed to become dampening water receiving area and can be printed.
This will be described in more detail below.

In the present invention, the light source used for image exposure is preferably a laser. Although the laser used for this invention is not specifically limited, The solid laser and semiconductor laser etc. which irradiate infrared rays with a wavelength of 760-1200 nm are mentioned suitably.
Regarding the infrared laser, the output is preferably 100 mW or more, the exposure time per pixel is preferably within 20 microseconds, and the irradiation energy amount is preferably 10 to 300 mJ / cm ² . In the laser, it is preferable to use a multi-beam laser device in order to shorten the exposure time.

  The exposed lithographic printing plate precursor is mounted on a plate cylinder of a printing press. In the case of a printing press equipped with a laser exposure device, image exposure is performed after a lithographic printing plate precursor is mounted on a plate cylinder of the printing press.

  After exposing the lithographic printing plate precursor imagewise with an infrared laser and supplying it with dampening water and printing ink without going through a development process such as a wet development process, the exposed part of the image recording layer The image recording layer cured by exposure forms a printing ink receiving portion having an oleophilic surface. On the other hand, in the unexposed area, the uncured image recording layer is removed by dissolution or dispersion by the supplied dampening water and / or printing ink, and a hydrophilic surface is exposed in that area. As a result, the fountain solution adheres to the exposed hydrophilic surface, and the printing ink is deposited on the image recording layer in the exposed area and printing is started.

Here, dampening water or printing ink may be supplied to the printing plate first, but printing is first performed in order to prevent the dampening water from being contaminated by the removed image recording layer components. It is preferable to supply ink. As the fountain solution and printing ink, normal lithographic fountain solution and printing ink are used.
In this way, the lithographic printing plate precursor is subjected to on-press development on an offset printing machine and used as it is for printing a large number of sheets.

(Gum development method)
After imagewise exposure, the unexposed area image recording layer may be removed (developed) using a gum solution. It is then used for printing. In the present invention, the gum solution means an aqueous solution containing a hydrophilic resin. By including a hydrophilic resin, it is possible to protect the exposed hydrophilic support from which the unexposed image recording layer has been removed, or to protect the image area.
Generally gum arabic having a strong desensitizing action is often used for the gum solution, and an aqueous solution of about 15 to 20% of gum arabic is often used as the gum solution. In addition to gum arabic, various water-soluble resins are used as a desensitizing agent. For example, water-soluble polysaccharides extracted from dextrin, steravic, structan, alginates, polyacrylates, hydroxyethylcellulose, polyvinylpyrrolidone, polyacrylamide, methylcellulose, hydroxypropylcellulose, hydroxymethylcellulose, carboxyalkylcellulose salts, soybean okara In addition, pullulan or pullulan derivatives and polyvinyl alcohol are also preferable.

  Furthermore, as modified starch derivatives, roasted starch such as British gum, enzyme-modified dextrins such as enzyme dextrin and shardinger dextrin, oxidized starch shown in solubilized starch, alpha-modified starch such as modified pregelatinized starch and non-modified pregelatinized starch , Phosphate starch, fat starch, sulfate starch, nitrate starch, xanthate starch, carbamic acid starch and other esterified starch, carboxyalkyl starch, hydroxyalkyl starch, sulfoalkyl starch, cyanoethyl starch, allyl starch, benzyl starch, carbamyl Etherified starch such as ethyl starch and dialkylamino starch, methylol crosslinked starch, hydroxyalkyl crosslinked starch, phosphoric acid crosslinked starch, crosslinked starch such as dicarboxylic acid crosslinked starch, starch polyacrylamide copolymer, starch polyacrylic acid copolymer, starch Vinyl acetate copolymer, starch polyacrylonitrile copolymer, chaotic starch polyacrylic acid ester copolymer, chaotic starch vinyl polymer copolymer, starch polystyrene maleic acid copolymer, starch polyethylene oxide copolymer, starch Starch graft polymers such as polypropylene copolymers are preferred.

  Natural polymer compounds include starches such as candy starch, potato starch, tapioca starch, wheat starch and corn starch, carrageenan, laminaran, seaweed mannan, funari, Irish moss, agar and algae such as sodium alginate. , Plant mucilage such as troroaoy, mannan, quince seed, pectin, tragacanth gum, karaya gum, xanthine gum, guar bin gum, locust bin gum, carob gum, benzoin gum, homopolysaccharides such as dextran, glucan, levan and saxino glucan and santang gum Proteins such as microbial mucilage such as hetropolysaccharide, glue, gelatin, casein and collagen are preferred.

  These water-soluble resins can be used in combination of two or more, and can be contained in the gum solution in an amount of preferably 1 to 50% by mass, more preferably 3 to 30% by mass.

  The gum solution used in the present invention contains a pH adjuster, surfactant, preservative, antifungal agent, lipophilic substance, wetting agent, chelating agent, antifoaming agent, etc. in addition to the above desensitizing agent. It can be contained.

  The gum solution is advantageously used in a pH range of 3 to 12, and therefore a pH adjuster is generally added. In order to make the pH neutral to weakly acidic, a mineral acid, organic acid, inorganic salt or the like is generally added to the gum solution and adjusted. The addition amount is 0.01-2 mass%. For example, the mineral acid includes nitric acid, sulfuric acid, phosphoric acid, metaphosphoric acid and the like. Examples of the organic acid include acetic acid, succinic acid, malonic acid, p-toluenesulfonic acid, levulinic acid, phytic acid, organic phosphonic acid, and amino acids such as glycine, α-alanine, and β-alanine. Inorganic salts include magnesium nitrate, primary sodium phosphate, secondary sodium phosphate, nickel sulfate, sodium hexametaphosphate, sodium tripolyphosphate, and the like. You may use together at least 1 sort (s) or 2 or more types, such as a mineral acid, an organic acid, or an inorganic salt.

  Examples of the surfactant contained in the gum solution of the present invention include anionic surfactants, cationic surfactants, amphoteric surfactants, and nonionic surfactants. Anionic surfactants include fatty acid salts, abietic acid salts, hydroxyalkane sulfonates, alkane sulfonates, α-olefin sulfonates, dialkyl sulfosuccinates, alkyl diphenyl ether disulfonates, linear alkyl benzene sulfonates, branched Chain alkylbenzene sulfonates, alkylnaphthalene sulfonates, alkylphenoxy polyoxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, sodium N-methyl-N-oleyl taurate, disodium N-alkylsulfosuccinate monoamide Salts, petroleum sulfonates, sulfated castor oil, sulfated beef tallow oil, fatty acid alkyl ester sulfate esters, alkyl sulfate esters, polyoxy Ethylene alkyl ether sulfates, fatty acid monoglyceride sulfates, polyoxyethylene alkylphenyl ether sulfates, polyoxyethylene styryl phenyl ether sulfates, alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene Examples thereof include alkyl phenyl ether phosphate esters, partially saponified products of styrene-maleic anhydride copolymers, partially saponified products of olefin-maleic anhydride copolymers, naphthalene sulfonate formalin condensates, and the like. Among these, dialkyl sulfosuccinates, alkyl sulfate esters, alkyl naphthalene sulfonates, α-olefin sulfonates, and alkyl diphenyl ether disulfonates are particularly preferably used.

  As the cationic surfactant, alkylamine salts, quaternary ammonium salts and the like are used.

  As the amphoteric surfactant, alkyl carboxybetaines, alkyl imidazolines, alkylaminocarboxylic acids and the like are used.

  Nonionic surfactants include polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ether, polyoxyethylene polyoxypropylene alkyl ether, glycerin fatty acid partial esters, sorbitan fatty acid partial esters , Pentaerythritol fatty acid partial esters, propylene glycol monofatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, polyglycerin fatty acid partial esters , Polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acid diethanol Mido, N, N-bis-2-hydroxyalkylamines, polyoxyethylene alkylamine, triethanolamine fatty acid ester, trialkylamine oxide, polypropylene glycol molecular weight 200-5000, trimethylolpropane, glycerin or sorbitol poly Examples include adducts of oxyethylene or polyoxypropylene, and acetylene glycols. Fluorine-based and silicon-based nonionic surfactants can also be used in the same manner.

  Two or more surfactants can be used in combination. The amount used is not particularly limited, but a preferable range is 0.01 to 20% by mass, preferably 0.05 to 10% by mass based on the total mass of the gum solution.

  As the preservative, known materials used in the fields of fiber, wood processing, food, medicine, cosmetics, agricultural chemicals and the like can be used. For example, quaternary ammonium salts, monohydric phenol derivatives, dihydric phenol derivatives, polyhydric phenol derivatives, imidazole derivatives, pyrazolopyrimidine derivatives, monovalent naphthols, carbonates, sulfone derivatives, organotin compounds, cyclopentane derivatives, phenyl derivatives , Phenol ether derivatives, phenol ester derivatives, hydroxylamine derivatives, nitrile derivatives, naphthalenes, pyrrole derivatives, quinoline derivatives, benzothiazole derivatives, secondary amines, 1,3,5 triazine derivatives, thiadiazole derivatives, anilide derivatives, pyrrole derivatives , Halogen derivatives, dihydric alcohol derivatives, dithiols, cyanic acid derivatives, thiocarbamic acid derivatives, diamine derivatives, isothiazole derivatives, monohydric alcohols, saturated aldehydes, Japanese monocarboxylic acid, saturated ether, unsaturated ether, lactone, amino acid derivative, hydantoin, cyanuric acid derivative, guanidine derivative, pyridine derivative, saturated monocarboxylic acid, benzenecarboxylic acid derivative, hydroxycarboxylic acid derivative, biphenyl, hydroxamic acid derivative , Aromatic alcohols, halogenophenol derivatives, benzenecarboxylic acid derivatives, mercaptocarboxylic acid derivatives, quaternary ammonium salt derivatives, triphenylmethane derivatives, hinokitiol, furan derivatives, benzofuran derivatives, acridine derivatives, isoquinoline derivatives, arsine derivatives, thiocarbamine Acid derivatives, phosphate esters, halogenobenzene derivatives, quinone derivatives, benzenesulfonic acid derivatives, monoamine derivatives, organophosphate esters, piperazine derivatives , Phenazine derivatives, pyrimidine derivatives, thiophanate derivatives, imidazoline derivatives, isoxazole derivatives, known preservatives such as ammonium salt derivatives can be used. Particularly preferred preservatives include pyridinethiol-1-oxide salts, salicylic acid and its salts, 1,3,5-trishydroxyethylhexahydro-S-triazine, 1,3,5-trishydroxymethylhexahydro-S- Examples include triazine, 1,2-benzisothiazolin-3-one, 5-chloro-2-methyl-4-isothiazolin-3-one, and 2-bromo-2-nitro-1,3-propanediol. The preferred addition amount is an amount that exerts stability against bacteria, molds, yeasts, etc., and varies depending on the types of bacteria, molds, yeasts, but 0.01 to The range of 4% by mass is preferable, and it is preferable to use two or more preservatives in combination so as to be effective against various molds and bacteria.

  The gum solution can also contain a lipophilic substance. Preferred lipophilic substances include organic carboxylic acids having 5 to 25 carbon atoms such as oleic acid, lanolinic acid, valeric acid, nonylic acid, capric acid, myristic acid, palmitic acid, castor oil and the like. These lipophilic substances can be used alone or in combination of two or more. The lipophilic substance contained in the gum solution is in the range of 0.005 to 10% by mass, more preferably 0.05 to 5% by mass, based on the total mass.

  In addition, glycerin, ethylene glycol, propylene glycol, triethylene glycol, butylene glycol, hexylene glycol, diethylene glycol, dipropylene glycol, glycerin, trimethylolpropane, diglycerin, etc. may be added as a wetting agent to the gum solution as necessary. it can. These wetting agents may be used alone or in combination of two or more. The preferred use amount of these wetting agents is 0.1 to 5% by mass.

  A chelate compound may be added to the gum solution. Usually, the gum solution is usually marketed as a concentrated solution, and is used after being diluted by adding tap water, well water or the like at the time of use. Calcium ions contained in the diluted tap water and well water may adversely affect printing and may cause the printed matter to become dirty. Therefore, the above disadvantages can be eliminated by adding a chelate compound. . Preferred chelate compounds include, for example, ethylenediaminetetraacetic acid, its potassium salt, its sodium salt; diethylenetriaminepentaacetic acid, its potassium salt, its sodium salt; triethylenetetraminehexaacetic acid, its potassium salt, its sodium salt, hydroxyethylethylenediaminetrimethyl Acetic acid, potassium salt, sodium salt; nitrilotriacetic acid, sodium salt; 1-hydroxyethane-1,1-diphosphonic acid, potassium salt, sodium salt; aminotri (methylenephosphonic acid), potassium salt, sodium Examples thereof include organic phosphonic acids such as salts and phosphonoalkanetricarboxylic acids. Organic amine salts are also effective in place of the sodium and potassium salts of the chelating agents. These chelating agents are selected so that they are stably present in the gum solution composition and do not impair the printability. The addition amount is suitably 0.001 to 1.0 mass% with respect to the gum solution at the time of use.

  An antifoaming agent can be added to the gum solution, and a silicon antifoaming agent is particularly preferable. Among them, an emulsified dispersion type and a solubilized type can be used. Preferably, the range of 0.001 to 1.0 mass% is optimal with respect to the gum solution at the time of use.

  The remaining component of the gum solution is water. It is advantageous in terms of transportation that the gum solution is a concentrated solution in which the water content is less than at the time of use, and is diluted with water at the time of use. In this case, the degree of concentration is appropriate such that each component does not cause separation or precipitation. The gum solution may be prepared as an emulsified dispersion type, an organic solvent is used as its oil phase, and it may be made into a solubilized type (emulsified type) with the aid of a surfactant as described above. .

  The organic solvent is preferably an organic solvent having a solubility in water at 20 ° C. of 5% by mass or less and a boiling point of 160 ° C. or more. For example, phthalic acid diester agents such as dibutyl phthalate, diheptyl phthalate, di-n-octyl phthalate, di (2-ethylhexyl) phthalate, dinonyl phthalate, didecyl phthalate, dilauryl phthalate, butyl benzyl phthalate, etc. , Aliphatic dibasic esters such as butyl glycol adipate, dioctyl azelate, dibutyl sebacate, di (2-ethylhexyl) sebacate, dioctyl sebacate, for example, epoxidized triglycerides such as epoxidized soybean oil, The freezing point of phosphoric acid esters such as cresyl phosphate, trioctyl phosphate, trischlor ethyl phosphate, for example, benzoic acid esters such as benzyl benzoate is 15 ° C. or less, Boiling point at atmospheric pressure include 300 ° C. or more plasticizers.

  Examples of other alcohols include 2-octanol, 2-ethylhexanol, nonanol, n-decanol, undecanol, n-dodecanol, trimethylnonyl alcohol, tetradecanol, and benzyl alcohol. Examples of glycols include ethylene glycol isoamyl ether, ethylene glycol monophenyl ether, ethylene glycol benzyl ether, ethylene glycol hexyl ether, and octylene glycol.

  Odor is particularly mentioned as a condition when selecting the compound. A preferable range of the amount of these solvents used is 0.1 to 5% by mass of the plate surface protecting agent, and a more preferable range is 0.5 to 3% by mass. These solvents can be used alone or in combination of two or more.

  The gum solution used in the present invention is prepared by preparing a water phase at a temperature of 40 ° C. ± 5 ° C., stirring at a high speed, slowly dropping the prepared oil phase into the water phase, stirring sufficiently, and then emulsifying and dispersing through a pressure type homogenizer. It is produced by doing.

  As the plate making method of the present invention, following the removal process of the unexposed area image recording layer using the above-described gum solution, a water washing process and further a desensitization process of the non-image area with the gum liquid are appropriately performed. I can do it.

  The gum development processing of the present invention can be suitably carried out by an automatic processor equipped with a supply means such as a gum solution and a rubbing member. Examples of the automatic processor include an automatic processor described in Japanese Patent Application Laid-Open No. 2006-235227 that performs rubbing while conveying a lithographic printing plate precursor after image recording. Among these, an automatic processor using a rotating brush roll as the rubbing member is particularly preferable.

The rotating brush roll that can be preferably used in the present invention can be appropriately selected in consideration of the difficulty of scratching the image area and the stiffness of the lithographic printing plate precursor support.
As the rotating brush roll, a known one formed by planting a brush material on a plastic or metal roll can be used. For example, a metal or plastic in which brush materials are implanted in rows, as described in Japanese Patent Application Laid-Open No. 58-159533, Japanese Patent Application Laid-Open No. 3-100534, or Japanese Utility Model Publication No. 62-167253. A brush roll in which the groove mold material is radially wound around a plastic or metal roll as a core without any gap can be used.
The brush material includes plastic fibers (for example, polyesters such as polyethylene terephthalate and polybutylene terephthalate, polyamides such as nylon 6.6 and nylon 6.10, polyacrylonitrile, poly (meth) acrylate, etc. Acrylic and polyolefin synthetic fibers such as polypropylene and polystyrene can be used. For example, the fiber has a hair diameter of 20 to 400 μm, and a hair length of 5 to 30 mm is preferable. Can be used.
Furthermore, the outer diameter of the rotating brush roll is preferably 30 to 200 mm, and the peripheral speed at the tip of the brush rubbing the plate surface is preferably 0.1 to 5 m / sec.

  The rotating direction of the rotating brush roll used in the present invention may be the same or opposite to the conveying direction of the planographic printing plate precursor of the present invention. Thus, when two or more rotating brush rolls are used, it is preferable that at least one rotating brush roll rotates in the same direction and at least one rotating brush roll rotates in the opposite direction. This further ensures the removal of the image recording layer in the unexposed area. Furthermore, it is also effective to swing the rotating brush roll in the direction of the rotation axis of the brush roll.

  The gum solution used in the gum development of the present invention and the temperature of the washing water in the post-process can be used separately at any temperature, but are preferably 10 ° C to 50 ° C.

  In the gum development method of the present invention, it is possible to provide a drying step at any location after gum development. The drying step is generally performed by blowing a drying air having an arbitrary temperature after most of the processing liquid is removed by a roller nip.

  EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these.

<Synthesis Method of Specific Compound (A-1)>
Methyl p-toluenesulfonate (manufactured by Tokyo Chemical Industry Co., Ltd.) 83 in a solution of 1,4-diazabicyclo [2,2,2] octane 50 g (manufactured by Tokyo Chemical Industry Co., Ltd.) in 150 ml of acetonitrile at 0 ° C. A solution of 1 g of acetonitrile in 30 ml was added dropwise. After dripping, after stirring at room temperature for 1 hour, the precipitated crystals were filtered, washed with 200 ml of acetonitrile and dried to obtain 130 g (yield 98%) of the specific compound (A-1) of the present invention. The structure was identified by 1H-NMR (DMSO).
¹ H-NMR (400 MHz, DMSO-d6): δ 7.52 (d, J = 7.0 Hz, 2H), 7.13 (d, J = 7.0 Hz, 2H), 3.24 (t, J = 7.0 Hz, 6H), 2.99 (t, J = 7.0Hz, 6H), 2.94 (s, 3H), 2.29 (s, 3H)

<Synthesis Method of Specific Compound (A-2)>
Ethyl p-toluenesulfonate (manufactured by Tokyo Chemical Industry Co., Ltd.) 89 in a solution of 1,4-diazabicyclo [2,2,2] octane 50 g (manufactured by Tokyo Chemical Industry Co., Ltd.) in 160 ml of acetonitrile at 0 ° C. A solution of 3 g of acetonitrile in 30 ml was added dropwise. After the dropwise addition, the mixture was stirred at 0 ° C. for 7 hours and further stirred at room temperature for 1 hour to obtain 135 g (yield 97%) of the specific compound (A-2) of the present invention. The structure was identified by 1H-NMR (DMSO).
¹ H-NMR (400 MHz, DMSO-d6): δ 7.52 (d, J = 7.0 Hz, 2H), 7.13 (d, J = 7.0 Hz, 2H), 3.24 (t, J = 7.0 Hz, 6H), 3.19 (q, J = 7.0Hz, 2H), 2.99 (t, J = 7.0Hz, 6H), 2.29 (s, 3H), 1.18 (t, J = 7.0Hz, 3H)

1. Production of lithographic printing plate precursors (1) to (19) (1) Production of support (part 1)
In order to remove rolling oil on the surface of an aluminum plate (material JIS A 1050) having a thickness of 0.3 mm, a degreasing treatment was performed at 50 ° C. for 30 seconds using a 10 mass% sodium aluminate aqueous solution, and then the hair diameter was adjusted to 0. The aluminum surface was grained using ^three 3 mm bundle-planted nylon brushes and a pumice-water suspension (specific gravity 1.1 g / cm ³ ) having a median diameter of 25 μm and washed well with water. This plate was etched by being immersed in a 25 mass% sodium hydroxide aqueous solution at 45 ° C for 9 seconds, washed with water, further immersed in 20 mass% nitric acid at 60 ° C for 20 seconds, and washed with water. The etching amount of the grained surface at this time was about 3 g / m ² .

Next, an electrochemical roughening treatment was performed continuously using an alternating voltage of 60 Hz. The electrolytic solution at this time was a 1% by mass nitric acid aqueous solution (containing 0.5% by mass of aluminum ions) and a liquid temperature of 50 ° C. The AC power source waveform is electrochemical roughening treatment using a trapezoidal rectangular wave alternating current with a time ratio TP of 0.8 msec until the current value reaches a peak from zero, a duty ratio of 1: 1, and a trapezoidal rectangular wave alternating current. Went. Ferrite was used for the auxiliary anode. The current density was 30 A / dm ² at the peak current value, and 5% of the current flowing from the power source was shunted to the auxiliary anode.
The amount of electricity in the nitric acid electrolysis was 175 C / dm ² when the aluminum plate was the anode. Then, water washing by spraying was performed.

Next, a 0.5% by mass hydrochloric acid aqueous solution (containing 0.5% by mass of aluminum ions) and an electrolytic solution having a liquid temperature of 50 ° C. and nitric acid electrolysis under the condition of an electric quantity of 50 C / dm ² when the aluminum plate is an anode. In the same manner as above, an electrochemical surface roughening treatment was performed, followed by washing with water by spraying.
Next, the plate was provided with a DC anodized film of 2.5 g / m ² at a current density of 15 A / dm ² using 15% by mass sulfuric acid (containing 0.5% by mass of aluminum ions) as an electrolyte, and then washed with water. It dried and produced the support body (1).

In order to ensure the hydrophilicity of the non-image area, the support (1) was subjected to a silicate treatment at 70 ° C. for 12 seconds using a 1.5 mass% No. 3 sodium silicate aqueous solution. When the amount of Si was quantified by fluorescent X-ray, the amount of Si deposited was 6 mg / m ² . Then, it washed with water and the support body (2) was obtained. The centerline average roughness (Ra) of this substrate was measured using a needle having a diameter of 2 μm and found to be 0.51 μm.

(2) Formation of Intermediate Layer On the support (2), the following intermediate layer coating solution (1) was applied so that the dry coating amount was 8 mg / m ² to form an intermediate layer.

Intermediate layer coating solution (1)
-The following intermediate layer polymer (1) 0.017 g
・ Methanol 9.00 g
・ Distilled water 1.00g
・ Specific compounds (described in Table 1) 0.017 g

(3) Formation of image recording layer After applying bar coating of the image recording layer coating liquid (1) having the following composition on the support shown in Table 1 having an intermediate layer, it was oven-dried at 100 ° C for 60 seconds, and the dry coating amount 1 An image recording layer of 0.0 g / m ² was formed.
The image recording layer coating solution (1) was obtained by mixing and stirring the following photosensitive solution (1) and microgel solution (1) immediately before coating.

Photosensitive solution (1)
・ The following binder polymer (1) 0.162 g
・ The following infrared absorber (1) 0.030 g
・ The following polymerization initiator (1) 0.162 g
・ Polymerizable compound (Aronix M215, manufactured by Toagosei Co., Ltd.) 0.385 g
・ Pionine A-20 (Takemoto Yushi Co., Ltd.) 0.055g
・ The following oil sensitizer (1) 0.044 g
・ The following fluorosurfactant (1) 0.008 g
・ Methyl ethyl ketone 1.091g
・ 1-methoxy-2-propanol 8.609g

Microgel solution (1)
-Microgel (1) synthesized as follows: 2.640 g
・ Distilled water 2.425g

(Synthesis of microgel (1))
As oil phase components, trimethylolpropane and xylene diisocyanate adduct (Mitsui Takeda Chemical Co., Ltd., Takenate D-110N) 10 g, pentaerythritol triacrylate (Nippon Kayaku Co., Ltd., SR444) 3.15 g, And 0.1 g of Pionein A-41C (manufactured by Takemoto Yushi Co., Ltd.) was dissolved in 17 g of ethyl acetate. As an aqueous phase component, 40 g of a 4% by mass aqueous solution of PVA-205 was prepared. The oil phase component and the water phase component were mixed and emulsified for 10 minutes at 12,000 rpm using a homogenizer. The obtained emulsion was added to 25 g of distilled water, stirred at room temperature for 30 minutes, and then stirred at 50 ° C. for 3 hours. The solid content concentration of the microgel solution thus obtained was diluted with distilled water so as to be 15% by mass. The average particle size was 0.2 μm.

(4) Formation of protective layer A protective layer coating solution (1) having the following composition was further bar-coated on the image recording layer, followed by oven drying at 120 ° C. for 60 seconds, and a dry coating amount of 0.15 g / m ^2. A lithographic printing plate precursor (1) to (19) was obtained.

Protective layer coating solution (1)
-1.5 g of inorganic layered compound dispersion (1) prepared as follows
・ Polyvinyl alcohol (Nippon Synthetic Chemical Industry Co., Ltd. CKS50, sulfonic acid modified,
Saponification degree 99 mol% or more, polymerization degree 300) 6% by mass aqueous solution 0.55 g
・ Polyvinyl alcohol (PVA-405 manufactured by Kuraray Co., Ltd., saponification degree: 81.5 mol%,
Polymerization degree 500) 6% by mass aqueous solution 0.03 g
・ Nippon Emulsion Co., Ltd. surfactant (Emalex 710),
1 mass% aqueous solution 8.60g
・ Ion-exchanged water 6.0g

(Preparation of inorganic layered compound dispersion (1))
6.4 g of synthetic mica Somasif ME-100 (manufactured by Coop Chemical Co., Ltd.) was added to 193.6 g of ion-exchanged water, and dispersed using an homogenizer until the average particle size (laser scattering method) became 3 μm. The aspect ratio of the obtained dispersed particles was 100 or more.

2. Preparation of lithographic printing plate precursor (23) The intermediate layer coating solution (1) was changed to the following intermediate layer coating solution (23) not containing a specific compound in the same manner as the preparation of the lithographic printing plate precursor (1). Thus, a lithographic printing plate precursor (23) for a comparative example was obtained.

Intermediate layer coating solution (23)
・ Intermediate layer polymer (1) 0.017 g
・ Methanol 9.00 g
・ Distilled water 1.00g

3. Preparation of lithographic printing plate precursor (24) A lithographic printing plate for a comparative example in the same manner as the preparation of lithographic printing plate precursor (1) except that the intermediate layer described in the preparation of lithographic printing plate precursor (1) is not provided. The original version (24) was obtained.

4). Preparation of planographic printing plate precursor (20) The intermediate layer coating solution (23) used for preparing the planographic printing plate precursor (23) is used on the support (2), and instead of the image recording layer coating solution (1). The lithographic printing plate precursor (20) was prepared in the same manner as in the production of the lithographic printing plate precursor (1) except that a coating solution in which 0.017 g of the specific compound (A-1) was further added to the image recording layer coating liquid (1) was used. )

5). Preparation of lithographic printing plate precursor (21) (1) Formation of image recording layer A lithographic printing plate precursor (1) except that the following image recording layer coating solution (21) was used instead of the image recording layer coating solution (1) ) To form an image recording layer.

Image recording layer coating solution (21)
-Polymer fine particles (hydrophobized precursor) aqueous dispersion prepared as follows: 33.0 g
・ The following infrared absorber (3) 1.0 g
・ Pentaerythritol tetraacrylate 0.5g
・ 1,5-Naphthalenedisulfonic acid disodium 0.1g
・ Methanol 16.0g

(Production of polymer fine particle (hydrophobized precursor) aqueous dispersion)
A stirrer, thermometer, dropping funnel, nitrogen inlet tube, reflux condenser is applied to a 1000 ml four-necked flask, and 350 mL of distilled water is added while deoxygenating by introducing nitrogen gas, and the internal temperature becomes 80 ° C. Until heated. 1.5 g of sodium dodecyl sulfate was added as a dispersant, 0.45 g of ammonium persulfide was added as an initiator, and then a mixture of 45.0 g of glycidyl methacrylate and 45.0 g of styrene was dropped from the dropping funnel over about 1 hour. did. After the completion of the dropping, the reaction was continued as it was for 5 hours, and then the unreacted monomer was removed by steam distillation. Thereafter, the mixture was cooled and adjusted to pH 6 with ammonia water, and finally pure water was added so that the nonvolatile content was 15% by mass to obtain an aqueous dispersion of polymer fine particles (hydrophobized precursor). The particle size distribution of the polymer fine particles had a maximum value at a particle size of 60 nm.

  Here, the particle size distribution is obtained by taking an electron micrograph of polymer fine particles, measuring a total of 5000 fine particle sizes on the photograph, and a logarithmic scale between 0 and the maximum value of the obtained particle size measurement values. The frequency of appearance of each particle size was plotted and divided into 50. For non-spherical particles, the particle size of spherical particles having the same particle area as that on the photograph was used as the particle size.

(2) Formation of protective layer The following protective layer coating solution (2) was bar-coated on the image recording layer formed as described above, and then oven-dried at 60 ° C for 120 seconds to obtain a dry coating amount of 0.3 g / A protective layer of m ² was formed to obtain a planographic printing plate precursor (21).

Protective layer coating solution (2)
・ Carboxymethylcellulose (mass average molar mass 20,000) 5.0 g
・ Water 50.0g

6). Production of planographic printing plate precursor (22) (1) Production of support (part 2)
In order to ensure the hydrophilicity of the non-image area, the support (1) was immersed for 10 seconds in a treatment tank containing a 1% by mass aqueous solution of polyvinylphosphonic acid having a liquid temperature of 50 ° C. to obtain a support (3). . The centerline average roughness (Ra) of this substrate was measured using a needle having a diameter of 2 μm and found to be 0.51 μm.

On the support (3), an intermediate layer coating solution (1) using the specific compound (A-1) was applied so that the dry coating amount was 8 mg / m ² to prepare a support B.
A lithographic printing plate precursor (22) was prepared in the same manner as the lithographic printing plate precursor (1) except that the support B was used in place of the support A.

7). Evaluation of planographic printing plate precursor (1)-On-press development
[Examples 1-22 and Comparative Examples 1-2]
The obtained lithographic printing plate precursors (1) to (24) were subjected to the conditions of an external drum rotation speed of 1000 rpm, a laser output of 70%, and a resolution of 2400 dpi on a Fujixel-made Luxel PLANETTER T-6000III equipped with an infrared semiconductor laser. Exposed. The exposure image included a solid image and a 50% halftone dot chart of a 20 μm dot FM screen.
The obtained exposed original plate was attached to a plate cylinder of a printing machine LITHRONE 26 manufactured by Komori Corporation without developing. Equality-2 (manufactured by FUJIFILM Corporation) / tap water = 2/98 (volume ratio) dampening water and Values-G (N) black ink (manufactured by Dainippon Ink & Chemicals, Inc.) After dampening water and ink were supplied by the standard automatic printing start method of LITHRONE 26 and developed on the machine, 100 sheets were printed on Tokuhishi Art (76.5 kg) paper at a printing speed of 10,000 sheets per hour.

(A) On-machine developability On-machine development is performed on the number of print sheets required until the on-press development on the printing machine of the unexposed area of the image recording layer is completed and ink is not transferred to the non-image area. Measured as sex. These results are shown in Table 1.

(B) Printing durability After the on-press developability was evaluated, printing was further continued. As the number of printed sheets was increased, the image recording layer was gradually worn out, so that the ink density on the printed material decreased. Printing durability was evaluated using the number of printed copies when the value measured by the Gretag densitometer for the 50% halftone dot area ratio of the FM screen in the printed material was 5% lower than the measured value for the 100th printed sheet. . The results are shown in Table 1.

(C) Stains The obtained lithographic printing plate precursor is left in a constant temperature and humidity chamber set at 60 ° C. and a relative humidity of 75% for 2 days, then exposed and printed in the same manner as described above, and appears in the non-image area. The pot-shaped dirt was visually counted using a magnifying glass having a magnification of 5 times. The results are shown in Table 1.

  As can be seen from Table 1, according to the present invention, it is possible to provide a lithographic printing plate precursor having excellent on-press developability and printing durability and improved stain resistance.

8). Evaluation of planographic printing plate precursor (2)-gum development (1)
[Examples 23 to 44 and Comparative Examples 3 to 4]
The resulting lithographic printing plate precursors (1) to (24) were subjected to gum development after exposure and subjected to the following printing evaluation.

(A) Fine line reproducibility (developability)
The resulting lithographic printing plate precursor was image-exposed with a Trend setter 3244VX manufactured by Creo equipped with an infrared semiconductor laser under the conditions of an output of 6.4 W, an outer drum rotation speed of 150 rpm, and a resolution of 2400 dpi. The exposure image includes a solid image and a fine line image.

The obtained exposed original plate was subjected to development and desensitization treatment in the same process using the automatic developing apparatus shown in FIG. A gum solution 1 having the following formulation was used.
<Gum solution 1> The following composition Arabic gum 1.6%
Enzyme modified potato starch 8.8%
Phosphorylated waxy onion starch 0.80%
Dioctylsulfosuccinate sodium salt 0.10%
Citric acid 0.14%
α-Alanine 0.11%
EDTA-tetrasodium salt 0.10%
Dodecyl diphenyl ether disulfonic acid 2Na salt 0.18%
Ethylene glycol 0.72%
Benzyl alcohol 0.87%
Sodium dehydroacetate 0.04%
Emulsion type silicon antifoaming agent 0.01%
Add water to make 100%
pH 5.0

  The lithographic printing plate obtained by making the plate as described above is attached to the cylinder of the Speedmaster 52 printing machine manufactured by Heidelberg, and dampening water [IF102 (Etchi solution manufactured by FUJIFILM Corporation) / water = 3/97 (volume ratio)]. And TRANS-G (N) black ink (manufactured by Dainippon Ink & Chemicals, Inc.), and after supplying dampening water and ink, 100 sheets were printed at a printing speed of 6000 sheets per hour.

  As a technique for evaluating whether or not the unexposed portion of the image recording layer has been removed as desired by the above development processing, an exposed fine line image (white fine line (in the image part from 10 μm to 50 μm) is taken every 2 μm. Evaluate the thickness of the white thin line that is reproduced by visually observing the printing paper to determine how thick the white thin line can be reproduced on the printing paper. did. That is, a smaller value indicates that a finer fine line is well developed, and a preferable result is shown. These results are shown in Table 2.

(B) Printing durability After the above-described evaluation of fine line reproducibility, printing was further continued, and printing durability was evaluated in the same manner as in the case of the above-described on-press developed printing plate. The results are shown in Table 2.

(C) Dirtiness As in the case of Example 1, the lithographic printing plate precursor was left in a constant temperature and humidity chamber set at 60 ° C. and a relative humidity of 75% for 2 days, and then the evaluation of fine line reproducibility was performed in the same manner. Then, the plate was made by exposure, gum development and printing, and the spot-like stains appearing in the non-image area were visually counted using a magnifying glass having a magnification of 5 times. The results are shown in Table 2.

9. Evaluation of planographic printing plate precursor (3)-gum development (2)
[Examples 45 to 66 and Comparative Examples 5 and 6]
The processing solution used in the developing section was used as weak alkaline gum solution 1, and gum solution 2 having a pH of 9.7 by adding sodium hydroxide was used. Lithographic printing plate precursors (1) to (24) were prepared in the same manner as in Examples 23 to 44, and fine line reproducibility (developability), printing durability, and stain resistance were evaluated. The evaluation results are shown in Table 3.

  As can be seen from Table 3, according to the present invention, it is possible to provide a lithographic printing plate precursor exhibiting good gum developability (thin line reproducibility) and printing durability and improved stain resistance.

It is a figure which shows the structure of the automatic image development apparatus of the lithographic printing plate which concerns on this invention.

Explanation of symbols

1: rotating brush roll 2: receiving roll 3: transport roll 4: transport guide plate 5: spray pipe 6: pipeline 7: filter 8: plate supply table 9: plate discharge table 100: developer tank 101: circulation pump 102: plate

Claims (13)

  It has an intermediate layer and an image recording layer in this order on an aluminum support, and the intermediate layer or image recording layer contains a compound having an amino group and a functional group that interacts with the aluminum support in one molecule. A lithographic printing plate precursor.   An intermediate layer and an image recording layer are arranged in this order on an aluminum support, and the intermediate layer contains a compound having an amino group and a functional group that interacts with the aluminum support in one molecule. 1. The lithographic printing plate precursor as described in 1. Functional group that acts aluminum support and mutual, trialkoxysilyl group, an onium group, or a phenolic hydroxyl group, a carboxyl _{group, -SO 3 H, -OSO 3 H} , -PO 3 H 2, -OPO 3 H 2, _{-CONHSO 2 -, - SO 2 NHSO} 2 - and acid group or a lithographic printing plate precursor as claimed in claim 1 or 2, characterized in that it is a metal salt selected from COCH ₂ CO-. The compound which has an amino group and the functional group which interacts with an aluminum support body in one molecule is a compound represented by following General formula (1), It is any one of Claims 1-3 characterized by the above-mentioned. Lithographic printing plate precursor.

(In the formula, R represents a hydrogen atom or a group optionally selected from an alkyl group, an alkenyl group, an alkynyl group, an aryl group, and a heterocyclic group, and X ⁻ represents an arbitrary anion. To express.) The compound having an amino group and a functional group that interacts with the aluminum support in one molecule is a compound represented by the following general formula (2). The lithographic printing plate precursor described.

(In the general formula (2), W is .n representing the n-valent organic linking group .X representing an integer of 2 or more ^- representing the any anion.) The compound having an amino group and a functional group that interacts with the aluminum support in one molecule is a compound represented by the following general formula (3). The lithographic printing plate precursor described.

(In General Formula (3), W represents a divalent organic linking group, R ₁ represents an organic residue, n represents an integer of 2 to 3, and m represents a number satisfying n × m = 2. .)   The lithographic printing plate precursor as claimed in any one of claims 1 to 6, wherein the intermediate layer contains a polymer having a substrate adsorptive group, a polymerizable group, and a hydrophilic group.   The lithographic printing plate according to any one of claims 1 to 7, wherein the image recording layer contains (A) an infrared absorber, (B) a polymerization initiator, and (C) a polymerizable compound. Original edition.   The lithographic printing plate precursor as claimed in claim 1, wherein the image recording layer further comprises (D) a binder polymer.   The lithographic printing plate precursor as claimed in any one of claims 1 to 9, wherein the image recording layer further comprises (E) a microcapsule or a microgel.   The image recording layer is an image recording layer capable of forming an image by supplying printing ink and fountain solution on a printing machine after exposure to remove unexposed portions, or developing with a gum solution after exposure. The lithographic printing plate precursor as claimed in any one of claims 1 to 10, wherein:   The lithographic printing plate precursor according to claim 11 is imagewise exposed, and printing ink and fountain solution are supplied on the printing machine without any development processing being performed on the exposed lithographic printing plate precursor. And a process for removing an unexposed portion of the lithographic printing plate precursor by starting printing.   12. An imagewise exposure of the lithographic printing plate precursor according to claim 11 and a step of removing an unexposed portion of the lithographic printing plate precursor by developing the exposed lithographic printing plate precursor with a gum solution. A plate making method of a lithographic printing plate precursor characterized by the above.

Images