JP2009060999A

JP2009060999A - Golf ball

Info

Publication number: JP2009060999A
Application number: JP2007229686A
Authority: JP
Inventors: Katsunori Sato; 克典佐藤; Atsuki Kasashima; 厚紀笠嶋
Original assignee: Bridgestone Sports Co Ltd
Current assignee: Bridgestone Sports Co Ltd
Priority date: 2007-09-05
Filing date: 2007-09-05
Publication date: 2009-03-26
Anticipated expiration: 2027-09-05
Also published as: JP5251045B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a golf ball which makes it possible to maintain a clear pattern without using conventional ink, to achieve durability of a ball surface, and to increase carry by further improving aerodynamic performance achieved by unevenness such as dimples of the ball surface. <P>SOLUTION: The golf ball G keeps the pattern M such as letters or figure displayed on the ball outer surface 1a on which a recess part and/or a projection part is formed. The pattern M is indicated by hollows 10a in which depth d<SB>p</SB>from the outer surface 1a is substantially uniform as a whole. The golf ball is characterized by (1) or (2). (1) S/N×100 is 100% or lower, where S is the total number of the hollows having the depth from the outer surface which is substantially uniform as a whole, and N is the total number of the dimples. (2) The pattern is circular, elliptical or polygonal. The aerodynamic performance of the golf ball is improved by the substantially uniform hollows arranged on the surface in good balance. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

本発明は、ボール表面に文字，図形等の模様を表示したゴルフボールに関し、特には、製造時における模様表示工程において、ボールの不良品の発生を実質上無くすことができるゴルフボールに関する。 The present invention relates to a golf ball that displays a pattern such as characters and figures on the surface of the ball, and more particularly, to a golf ball that can substantially eliminate the occurrence of defective balls in a pattern display process at the time of manufacture.

一般に、ゴルフボールの表面には、商品名や数字などのロゴマーク等の模様を表わす図形が単色又は複合色で表示されている。従来より、このような模様の形成方法としては、パッド印刷法によって直接印刷したり、所謂全ベタの転写フィルムを用いて刻印で押す転写法を用いたり、或いは、ベースフィルムの上に表示すべき模様の転写インキ層を形成した転写フィルムを用いて熱転写で印刷する熱転写法等により行なわれていた。これらの方法の共通するところは、有機系又は無機系の顔料を用いた印刷インキを用いること及び外部から圧力を加えて表示することである。 In general, on the surface of a golf ball, a figure representing a pattern such as a brand name or a logo such as a number is displayed in a single color or a composite color. Conventionally, as a method for forming such a pattern, printing should be performed directly by a pad printing method, a transfer method in which a so-called all-solid transfer film is pressed by imprinting, or displayed on a base film. It has been carried out by a thermal transfer method in which printing is performed by thermal transfer using a transfer film on which a pattern transfer ink layer is formed. The common point of these methods is to use printing ink using an organic or inorganic pigment and to display by applying pressure from the outside.

しかしながら、ゴルフボールの表面は、滑らかな球面とは異なり、表面にディンプル等の多数の凹凸が密度高く配置されているため、球面上に均一な圧力が加わり難く、特には、窪んだディンプルの底部分に印刷むらが生じたり、インクが滲んでしまい、模様の境界部分が不鮮明になるなど印刷不良が生じ、問題であった。 However, unlike a smooth spherical surface, the surface of a golf ball has a large number of irregularities such as dimples arranged at a high density on the surface, so that it is difficult to apply a uniform pressure on the spherical surface. This is a problem due to printing defects such as uneven printing on the portion, ink bleeding, and a boundary portion of the pattern becoming unclear.

また、過去において、更なる飛距離向上のため、ボール内部の各層の硬度や厚さ、材料を検討し、ボール内部構造に関して多くの技術が提案されてきたが、これらの開発にも限りがあり、最近では、上記の技術開発のほかに、ボール表面に形成されるディンプルなどの凹凸模様をユニークなものにし、表面占有率を更に増加させて空気力学的性能を向上させることも重要課題の一つになっている。 In the past, in order to further improve the flight distance, the hardness, thickness, and material of each layer inside the ball have been studied, and many technologies have been proposed regarding the internal structure of the ball, but these developments are also limited. Recently, in addition to the above-mentioned technological developments, it is also important to improve the aerodynamic performance by making the uneven pattern such as dimples formed on the ball surface unique and further increasing the surface occupancy. It is connected.

特開平１０−１４７０９７号公報JP-A-10-147097 特開２００４−２４３０３３号公報JP 2004-243033 A

本発明は、上記事情に鑑みなされたものであり、上記の種々の問題点を有する従来のインキを用いることなく、模様の鮮明性を良好に維持し、ボール表面の耐久性に優れたゴルフボールを提供することを目的とする。また、ディンプル等のボール表面の凹凸部による空気力学性能を更に向上させて飛距離増大を図ることができるゴルフボールを提供する。 The present invention has been made in view of the above circumstances, and without using the conventional inks having the above-mentioned various problems, a golf ball having excellent pattern surface clarity and excellent ball surface durability. The purpose is to provide. In addition, a golf ball is provided that can further improve the aerodynamic performance due to the irregularities on the surface of the ball such as dimples and increase the flight distance.

本発明者らは、上記目的を達成すため鋭意検討を重ねた結果、従来から採用されているような有機系又は無機系の顔料を用いた印刷インキを用いることを避けて、ボール外表面の凹部及び／又は凸部に、文字，図形等の模様を、ボール外表面からの深さが全体に実質上均一な窪みによって表示することにより、ゴルフボールの表面に表示された模様の鮮明性をボールの寿命が実質上尽きるまで良好に維持することができ、本発明を完成したものである。 As a result of intensive studies to achieve the above object, the present inventors have avoided the use of printing inks using organic or inorganic pigments as conventionally employed, By displaying the pattern of characters, figures, etc. in the recesses and / or protrusions by depressions whose depth from the outer surface of the ball is substantially uniform throughout, the sharpness of the pattern displayed on the surface of the golf ball is improved. The present invention has been completed as it can be maintained well until the life of the ball is substantially exhausted.

また、本発明者らは、表面に実質的に均一な窪みとディンプルとの個数の適正化を図り、これらをバランスよく配置することにより、ディンプル及び上記窪みによる表面占有率を向上させ、ゴルフボールの空気力学的性能を向上させることができることを知見し、本発明を完成したものである。 In addition, the present inventors have optimized the number of substantially uniform depressions and dimples on the surface and arranged them in a balanced manner, thereby improving the surface occupancy by the dimples and the depressions, and thereby improving the golf ball. It has been found that the aerodynamic performance can be improved, and the present invention has been completed.

従って、本発明は、下記〔Ｉ〕〜〔Ｖ〕のゴルフボールを提供する。
〔Ｉ〕凹部及び／又は凸部が形成されたボール外表面に文字，図形等の模様を表示したゴルフボールにおいて、上記外表面からの深さが全体に実質上均一な窪みによって上記模様を表示すると共に、上記外表面からの深さが全体に実質上均一な窪みの個数をＳ、ディンプル総数をＮとするとき、Ｓ／Ｎ×１００が１００％以下であることを特徴とするゴルフボール。
〔ＩＩ〕上記模様のうち輪郭長が１０〜５５ｍｍの範囲内である模様を含む〔Ｉ〕記載のゴルフボール。
〔ＩＩＩ〕上記模様が直線及び／又は曲線によって形成される〔Ｉ〕又は〔ＩＩ〕記載のゴルフボール。
〔ＩＶ〕凹部及び／又は凸部が形成されたボール外表面に文字，図形等の模様を表示したゴルフボールにおいて、上記外表面からの深さが全体に実質上均一な窪みによって上記模様を表示し、その模様が円形または楕円形であることを特徴とするゴルフボール。
〔Ｖ〕凹部及び／又は凸部が形成されたボール外表面に文字，図形等の模様を表示したゴルフボールにおいて、上記外表面からの深さが全体に実質上均一な窪みによって上記模様を表示し、その模様が多角形であることを特徴とするゴルフボール。 Therefore, the present invention provides the following golf balls [I] to [V].
[I] In a golf ball displaying a pattern such as letters and figures on the outer surface of the ball on which a concave portion and / or a convex portion are formed, the above pattern is displayed by a depression having a substantially uniform depth from the outer surface. In addition, the golf ball is characterized in that S / N × 100 is 100% or less, where S is the number of depressions having a substantially uniform depth from the outer surface and N is the total number of dimples.
[II] The golf ball according to [I], including a pattern having a contour length within a range of 10 to 55 mm among the patterns.
[III] The golf ball according to [I] or [II], wherein the pattern is formed by a straight line and / or a curved line.
[IV] In a golf ball displaying a pattern of characters, figures, etc. on the outer surface of the ball on which concave and / or convex portions are formed, the pattern is displayed by a depression having a substantially uniform depth from the outer surface. And a golf ball characterized in that the pattern is circular or elliptical.
[V] In a golf ball displaying a pattern of characters, figures, etc. on the outer surface of the ball on which a concave portion and / or a convex portion are formed, the above pattern is displayed by a depression having a substantially uniform depth from the outer surface. And a golf ball characterized in that the pattern is polygonal.

本発明のゴルフボールによれば、各種インキを用いた印刷法を用いることなく、商標名や番号等の文字及び／又は図形からなる模様をボール表面に顕示することができ、その模様の鮮明性を長期に亘って維持することができる。 According to the golf ball of the present invention, a pattern composed of characters and / or figures such as trade names and numbers can be revealed on the surface of the ball without using a printing method using various inks. Can be maintained over a long period of time.

また、本発明のゴルフボールは、表面に実質的に均一な窪みとディンプルとの個数の適正化を図り、これらをバランスよく配置することにより、ディンプル及び上記窪みによる表面占有率を向上させ、ゴルフボールの空気力学的性能を向上させることができる。 Also, the golf ball of the present invention improves the surface occupancy by the dimples and the depressions by optimizing the number of substantially uniform depressions and dimples on the surface and arranging them in a balanced manner. The aerodynamic performance of the ball can be improved.

以下、本発明を、図面に基づき更に詳しく説明する。
図１は、本発明（第１発明）の第１実施例を示すゴルフボールの正面図であり、図２は、図１におけるボールに表示された模様部分のＡ−Ａ断面図である。 Hereinafter, the present invention will be described in more detail with reference to the drawings.
FIG. 1 is a front view of a golf ball showing a first embodiment of the present invention (first invention), and FIG. 2 is a cross-sectional view taken along line AA of the pattern portion displayed on the ball in FIG.

図１において、ゴルフボールＧは、常法により、球面上に多数のディンプルＤが配置され、各ディンプルの間の球面部分（ボール中心から放射方向に最も遠い位置）に陸部Ｌが形成されたものである。図１におけるディンプルは、本実施例においては平面視円形であるが、ゴルフボールとしての機能を有する限りにおいて、楕円形，長円形，種々多角形など種々の形状を採用することができる。 In FIG. 1, a golf ball G has a large number of dimples D arranged on a spherical surface by a conventional method, and a land portion L is formed in a spherical portion between the dimples (a position farthest in the radial direction from the ball center). Is. The dimples in FIG. 1 are circular in plan view in this embodiment, but various shapes such as an ellipse, an oval, and various polygons can be adopted as long as they have a function as a golf ball.

ボールの外表面に表示された模様Ｍは、図１では英文字を表示しているが、一般にゴルフボールの商標名などである。図１の表示された数字「５」はゴルフボールの番号を表わす。そして、これらの商標名や番号等の模様Ｍは、ボール全体１ａに実質上均一な窪み１０ａによって表示されている。このようにして構成された模様１０は、特に色彩を施さなくても、光の反射により周囲の陸部Ｌ及びディンプルＤとの形状の違いによって模様が十分に識別されるものである。 The pattern M displayed on the outer surface of the ball is displayed with English letters in FIG. 1, but is generally a trademark name of a golf ball. The displayed number “5” in FIG. 1 represents the golf ball number. The patterns M such as trade names and numbers are displayed by a substantially uniform recess 10a on the entire ball 1a. The pattern 10 thus configured can be sufficiently identified by the difference in shape between the surrounding land portion L and the dimple D due to the reflection of light without any particular color.

本発明において、模様Ｍを形成する窪み１０ａを立体的に視ると、図２に示された形状を有する。即ち、図２において、模様Ｍを表示した窪み１０ａの深さｄ_pは全体に亘って実質上均一である。即ち、陸部Ｌに施した窪みの部分１１及びそこから延びるディンプルの部分に施した窪みの部分１２を通じて、表面からの深さｄ_pが実質上均一である。なお、上記表面からの深さｄ_pとは、陸部Ｌ，ディンプルＤ等を形成する曲面からの法線方向に沿った深さを意味する。この深さｄ_pは、０．１２ｍｍ以下であることが好ましく、更に好ましくは０．０９ｍｍ以下である。深さｄ_pが０．１２ｍｍを超えると模様の大きさ又は球面上の配置状態によってはボールの飛び性能に悪影響を及ぼす場合がある。この深さｄ_pの下限値としては０．０１５ｍｍが好ましい。一方、ディンプルの深さｄ_Dは通常０．２〜０．４ｍｍである。即ち、上記窪みの深さｄ_pはディンプルの深さｄ_Dよりも著しく小さいものである。 In the present invention, when the recess 10a forming the pattern M is viewed three-dimensionally, it has the shape shown in FIG. That is, in FIG. 2, the depth d _p of the recess 10a displaying the pattern M is substantially uniform throughout. That is, the depth d _p from the surface is substantially uniform through the recessed portion 11 formed in the land portion L and the recessed portion 12 formed in the dimple portion extending therefrom. The depth d _p from the surface means a depth along the normal direction from the curved surface forming the land portion L, the dimple D, and the like. This depth d _p is preferably 0.12 mm or less, and more preferably 0.09 mm or less. If the depth d _p exceeds 0.12 mm, the flying performance of the ball may be adversely affected depending on the size of the pattern or the arrangement state on the spherical surface. The lower limit value of the depth d _p is preferably 0.015 mm. On the other hand, the dimple depth d _D is usually 0.2 to 0.4 mm. That is, the depth d _{p of the} depression is significantly smaller than the depth d _{D of the} dimple.

図３は、本発明（第１発明）の第２実施例を示すゴルフボールの正面図であり、図４は、図３におけるボールに表示された模様部分のＢ−Ｂ断面図である。 FIG. 3 is a front view of a golf ball showing a second embodiment of the present invention (first invention), and FIG. 4 is a BB cross-sectional view of a pattern portion displayed on the ball in FIG.

この実施例の特徴とするところは、平面視多角形に延びる縁部ｓによって区画された多数のディンプルＤがボール表面１ａに多数形成されていると共に、縁部を介して一方のディンプルから他方のディンプルに亘って模様の窪み１０ａが形成された点である。更に詳述すると、この実施例のゴルフボールでは、図３に示されるように、ディンプルＤが直線状に延びる複数の縁部ｓによって多角形状に取り囲んでなる多角形ディンプルを球面全体にバランス良く配置したものである。ボールを球面１２面体に見立て、この球面１２面体を構成するユニット五角形Ｔを便宜上１個だけ１点鎖線で示しているが、このユニット五角形Ｔに五角形ディンプルＤ₅を主体として大きさが異なる複数のディンプルＤを２６個均等に配置したものである。ディンプルＤの配置については、ユニット五角形Ｔの中心の位置に、このユニット五角形Ｔと実質上相似する五角形ディンプルＤ₅が、ユニット五角形Ｔとの間で両者の各辺がそれぞれ平行となる状態で配置されている。また、この五角形ディンプルＤ₅の周囲には、該ディンプルを中心として、七角形ディンプルＤ₇が５個配置されている。そして、ユニット五角形Ｔの５個の頂点、または角の部分に夫々ユニット五角形Ｔの辺に内接して五角形ディンプルＤ₅’を配置すると共に、ユニット五角形Ｔ内の上記角の五角形ディンプルＤ₅’と七角形ディンプルＤ₇の間に各々他の五角形ディンプルＤ₅”を３個ずつバランス良く配置している。この結果、２１個の五角形ディンプルＤ₅，Ｄ₅’，Ｄ₅”と５個の七角形ディンプルＤ₇の合計２６個のディンプルがユニット五角形Ｔ内に配置され、ボール外表面の全体に亘って五角形ディンプル及び七角形ディンプルが合計３１２個配置されている。 A feature of this embodiment is that a large number of dimples D defined by edges s extending in a polygonal shape in plan view are formed on the ball surface 1a, and from one dimple to the other through the edges. This is a point where a pattern depression 10a is formed over the dimples. More specifically, in the golf ball of this embodiment, as shown in FIG. 3, the polygonal dimples in which the dimples D are surrounded by a plurality of edges s extending linearly are arranged in a well-balanced manner on the entire spherical surface. It is a thing. The ball is regarded as a spherical dodecahedron, and only one unit pentagon T constituting the spherical dodecahedron is shown by a one-dot chain line for convenience. A plurality of unit pentagons T having a pentagonal dimple D ₅ as a main component are different in size. 26 dimples D are equally arranged. The arrangement of the dimples D is the position of the center of the unit pentagon T, pentagonal dimple D ₅ that similar on this unit pentagon T substantially, disposed in a state where both sides of the parallel respectively between the unit pentagon T Has been. Around the pentagonal dimple D _5, around the dimple, heptagonal dimples D ₇ are five arrangement. The five vertices of the unit pentagon T or the portion of the corner 'with placing, pentagonal dimple D ₅ of the corner in the unit pentagon T' inscribed on the sides of each unit pentagon T pentagonal dimple D ₅ and, Three other pentagonal dimples D ₅ ″ are arranged in a balanced manner between the heptagonal dimples D _7. As a result, 21 pentagonal dimples D ₅ , D ₅ ′, D ₅ ″ and five seven dimples are arranged. A total of 26 dimples of square dimples D ₇ are arranged in the unit pentagon T, and a total of 312 pentagon dimples and heptagon dimples are arranged over the entire outer surface of the ball.

この実施例において、図４に示されるように、各縁部ｓは、１点鎖線で示したボールの外周仮想線Ｎ１と、該仮想線より距離ｈだけ小さく、且つ同心円状に延びる２点鎖線で示した基準線Ｎ２の間に形成され、この縁部ｓの形状はボールの外側向けて突出した断面円弧状である。そして、ディンプルＤは、基準線Ｎ２からボールの内側に向けて凹形状に形成される。なお、図３において、縁部ｓを示した一対の平行に延びる線は、図４における基準線Ｎ２と交わる縁部の基点位置を示している。 In this embodiment, as shown in FIG. 4, each edge s is composed of an outer peripheral virtual line N1 indicated by a one-dot chain line, and a two-dot chain line that is smaller than the virtual line by a distance h and extends concentrically. The edge portion s is formed between the reference line N2 shown in FIG. 1, and the shape of the edge portion s is an arc of a cross section projecting outward from the ball. The dimple D is formed in a concave shape from the reference line N2 toward the inside of the ball. In FIG. 3, a pair of parallel extending lines indicating the edge s indicate the base position of the edge that intersects the reference line N <b> 2 in FIG. 4.

本実施例においては、図４に示すように、模様Ｍを形成する窪み１０ａは、縁部ｓを挟んだ左右のディンプルＤ，Ｄに亘って形成されたものである。なお、縁部ｓの頂点を連ねた外周仮想線Ｎ１と基準線Ｎ２との間の距離ｈ（言い換えれば、この距離は縁部の高さを示す。）は、約０．１５ｍｍであることが好適であり、この距離ｈを加算したディンプル深さｄについては０．３〜０．５ｍｍの範囲に適宜調整することが好適である。 In this embodiment, as shown in FIG. 4, the recess 10a forming the pattern M is formed across the left and right dimples D and D with the edge s interposed therebetween. Note that the distance h (in other words, this distance indicates the height of the edge) between the outer peripheral imaginary line N1 connecting the vertices of the edge s and the reference line N2 is about 0.15 mm. The dimple depth d obtained by adding this distance h is suitably adjusted within a range of 0.3 to 0.5 mm.

図５は、本発明（第１発明）の他の実施態様を示したものである。図５におけるゴルフボールの特徴は、上記実施例で用いた縁部ｓを配置してボールの球面を多角形又は非円形状の区画部１２を形成し、縁部ｓを挟んで左右の球面１ａに模様Ｍを表わした窪み１０ａを配置した点にある。この窪み１０ａの構造や形状については、図３，４において示したものと実質上相違点はなく、図４に示した実施例と共に、外周仮想線Ｍは、縁部ｓの頂点を連ねたものであり、ボールＧの中心から放射方向に最も遠い位置にあり、球面１ａと一致する外表面と同心円をなして延びたものである。 FIG. 5 shows another embodiment of the present invention (first invention). The golf ball shown in FIG. 5 is characterized in that the edge s used in the above embodiment is arranged to form a spherical or polygonal partition 12 on the spherical surface of the ball, and the left and right spherical surfaces 1a sandwiching the edge s. The dent 10a representing the pattern M is arranged at the point. The structure and shape of the depression 10a are substantially the same as those shown in FIGS. 3 and 4, and together with the embodiment shown in FIG. 4, the outer peripheral virtual line M is a series of apexes of the edge s. It is located farthest from the center of the ball G in the radial direction and extends concentrically with the outer surface coinciding with the spherical surface 1a.

図６は、本発明（第２発明）の第１実施例を示すゴルフボールの正面図であり、図７は、図６におけるボールに表示された模様部分ＭのＣ−Ｃ断面図である。 FIG. 6 is a front view of a golf ball showing a first embodiment of the present invention (second invention), and FIG. 7 is a cross-sectional view of the pattern portion M displayed on the ball in FIG.

この発明は、第１発明と同様に、凹部及び／又は凸部が形成されたボール外表面１ａに文字，図形等の模様Ｍを溝１０ｂによって表示したゴルフボールＧであるが、その特徴とするところは、上記外表面１ａからの深さが全体に実質上均一な溝１０ｂによって上記模様Ｍを表示した点にある。 Like the first invention, the present invention is a golf ball G in which a pattern M such as letters and figures is displayed on the outer surface 1a of the ball formed with recesses and / or protrusions by grooves 10b. However, the pattern M is displayed by the groove 10b having a substantially uniform depth from the outer surface 1a.

図６に示した例では、棒状，或いは見方を変えればＶ字状の模様Ｍを溝１０ｂによって描いたものであり、この模様Ｍをボールの外表面全体にバランス良くほぼ均一に配置したものである。この溝１０ｂの深さｄ_Gは、第１発明における窪み１０ａの深さと同様に、０．１２ｍｍ以下であることが好ましく、更に好ましくは０．０９ｍｍ以下であり、下限値としては０．０１５ｍｍが好ましい。この溝１０ｂの断面形状については、図７に示した円弧状のほか、略Ｖ字状，略Ｕ字状，その他多角形状等が挙げられ、特に制限はない。また、この溝の最大幅については、特に制限はないが、溝の深さと同程度に調整したり、或いは、溝の深さの２倍から３倍程度に調整することが好適である。 In the example shown in FIG. 6, a V-shaped pattern M is drawn by the groove 10b in a bar shape or a different way of viewing, and this pattern M is arranged almost uniformly in a well-balanced manner on the entire outer surface of the ball. is there. The depth d _G of the groove 10b is preferably 0.12 mm or less, more preferably 0.09 mm or less, and the lower limit is 0.015 mm, similar to the depth of the recess 10a in the first invention. preferable. The cross-sectional shape of the groove 10b is not particularly limited, and includes a substantially V shape, a substantially U shape, and other polygonal shapes in addition to the arc shape shown in FIG. Further, the maximum width of the groove is not particularly limited, but is preferably adjusted to the same level as the depth of the groove, or adjusted to about 2 to 3 times the depth of the groove.

本発明の第１発明及び第２発明において、実質上均一な深さによって形成された模様Ｍを表わす溝１０ｂの深さを０．０１２ｍｍ以下に調整した場合、打球の飛行時のバランスの面で悪影響が生じることは少ないものであるが、この場合においても、ボール外表面１ａ上に上記模様をバランスよく配置することが望まれる。例えば、２０面体、１２面体、８面体等の球面多面体等の公知の配置手法を利用することにより、ボール外表面全体に亘って模様Ｍを偏りなく表示し、ボールＧの美的外観を良くすることができる。また、上記の模様ＭをボールＧの赤道及び／又は経線に沿って模様を配置した場合、この模様を、プレイ時にパットを行うときのボール上の目標として利用することもできる。 In the first invention and the second invention of the present invention, when the depth of the groove 10b representing the pattern M formed with a substantially uniform depth is adjusted to 0.012 mm or less, in terms of the balance at the time of flight of the hit ball Even in this case, it is desirable to arrange the pattern in a balanced manner on the ball outer surface 1a. For example, by using a known arrangement technique such as a spherical polyhedron such as a icosahedron, a dodecahedron, an octahedron, etc., the pattern M is displayed evenly over the entire outer surface of the ball, and the aesthetic appearance of the ball G is improved. Can do. Further, when the pattern M is arranged along the equator and / or meridian of the ball G, this pattern can also be used as a target on the ball when putting in play.

また、本発明では、外表面からの深さが全体に実質上均一な窪みの個数をＳ、ディンプル総数をＮとするとき、Ｎに対するＳの比率が１００％以下であることが必要であり、好ましくは９０％以下、より好ましくは７０％以下、更に好ましくは５０％以下である。上記範囲を超えること、即ち、窪みをディンプルと同数以上に配置すると、窪みとディンプルとのバランスが悪くなってしまう。また、上限値としては、特に制限はないが、３％以上であることが好ましい。このように、本発明では、窪みの個数Ｓとディンプルの総数Ｎとの適正化を図り、これらをバランスよく配置することにより、ディンプル及び上記窪みによる表面占有率を向上させ、ゴルフボールの空気力学的性能を向上させることができるものである。 Further, in the present invention, when the number of depressions having a substantially uniform depth from the outer surface is S and the total number of dimples is N, the ratio of S to N needs to be 100% or less. Preferably it is 90% or less, More preferably, it is 70% or less, More preferably, it is 50% or less. When the above range is exceeded, that is, when the number of depressions is equal to or more than the number of dimples, the balance between the depressions and the dimples is deteriorated. The upper limit is not particularly limited, but is preferably 3% or more. As described above, in the present invention, by optimizing the number S of the depressions and the total number N of the dimples and arranging them in a balanced manner, the surface occupancy by the dimples and the depressions is improved, and the aerodynamics of the golf ball Performance can be improved.

ここで言う「窪み」については、１つの輪郭によって閉鎖された領域を窪みの単位（１個）と定義し、窪みの個数はその領域の個数に相当する。 Regarding the “dent” here, a region closed by one contour is defined as a unit (one) of the recess, and the number of the recesses corresponds to the number of the regions.

また、実質上均一な窪みによって表示される模様の輪郭長については、５５ｍｍ以下とすることが好ましく、より好ましくは４５ｍｍ以下、更に好ましくは３５ｍｍ以下であり、上限としては、好ましくは１０ｍｍ以上、より好ましくは１５ｍｍ以上、更に好ましくは２０ｍｍ以上である。 Further, the contour length of the pattern displayed by the substantially uniform depression is preferably 55 mm or less, more preferably 45 mm or less, still more preferably 35 mm or less, and the upper limit is preferably 10 mm or more, more Preferably it is 15 mm or more, More preferably, it is 20 mm or more.

また、上記模様の輪郭長１０ｍｍ以上５５ｍｍ以下のものを模様全体の１０％以上とすることが本発明の効果を有効に発揮させることができ、より好ましくは３０％以上、更に好ましくは５０％以上、最も８０％以上とすることであり、１００％であっても差し支えない。 Further, the effect of the present invention can be effectively exhibited by setting the pattern contour length of 10 mm or more and 55 mm or less to 10% or more of the entire pattern, more preferably 30% or more, and still more preferably 50% or more. , 80% or more, and 100% is acceptable.

上記模様は、円形、楕円形または多角形のいずれの形状であってもよい。また、円弧状であってもよく、特に好ましくは円の一部となるような形状を用いることである。楕円形状は、正円から所定度ずれた形のものを楕円として定義される。記載する。また、曲線の間に、直線状部材を持つものであっても構わない。また、多角形としては、幾何学的に言われる多角形を意味し、具体的には、３角形、４角形、５角形、６角形、７角形、８角形、１６角形の中から選ばれた多角形を用いることが好適である。この場合、上記の多角形について、その角部にカーブ（Ｒ）を持たせることが好ましく、これによりボールに働く抗力をできる限り抑えることができ、その結果、飛距離を向上させることができる。 The pattern may be any shape of a circle, an ellipse, or a polygon. Further, it may be arcuate, and it is particularly preferable to use a shape that becomes a part of a circle. An elliptical shape is defined as an ellipse having a shape deviated from a perfect circle by a predetermined degree. Describe. Moreover, you may have a linear member between curves. In addition, the polygon means a polygon that is geometrically referred to, and specifically selected from among a triangle, a tetragon, a pentagon, a hexagon, a heptagon, an octagon, and a hexagon. It is preferable to use a polygon. In this case, it is preferable that the polygon has the curve (R) at the corners, whereby the drag acting on the ball can be suppressed as much as possible, and as a result, the flight distance can be improved.

上記の模様が多角形である例として図９に示されたゴルフボールが挙げられる。このゴルフボールの表面に形成された模様Ｍは３角形、５角形及び６角形であり、それぞれの模様Ｍ０，Ｍ１，Ｍ２が複数のディンプルと交差してボール表面にバランスよく配置されている。上記模様を拡大した図が図１０（Ａ）（Ｂ）に示されているが、これらの模様の角部はカーブ（またはＲ）に施されている。 An example in which the above pattern is a polygon is the golf ball shown in FIG. The pattern M formed on the surface of the golf ball is a triangle, a pentagon, and a hexagon. The patterns M0, M1, and M2 intersect with a plurality of dimples and are arranged on the ball surface in a balanced manner. FIGS. 10A and 10B show enlarged views of the above patterns, but the corners of these patterns are given to the curve (or R).

上記の模様は、外表面からの深さが全体に実質上均一な窪みであり、この窪みは、具体的には、図１１に示されるように、複数のディンプルに跨って刻まれているような比較的浅い溝に相当する。この場合、上記溝は陸部及びディンプル内面において実質上均一であることを要する。 The pattern described above is a recess whose depth from the outer surface is substantially uniform as a whole. Specifically, as shown in FIG. 11, the recess seems to be engraved across a plurality of dimples. This corresponds to a relatively shallow groove. In this case, the groove needs to be substantially uniform in the land portion and the dimple inner surface.

また、他の模様として図１２に示された模様があり、比較的大きな６角形模様Ｍ３と比較的小さな５角形模様Ｍ４とがボール表面に均一に配置されている。これらの模様Ｍ３，Ｍ４は、図１３に示されるように１個の円形ディンプルＤを取り囲むように５角形または６角形の模様を現している。 As another pattern, there is a pattern shown in FIG. 12, and a relatively large hexagonal pattern M3 and a relatively small pentagonal pattern M4 are uniformly arranged on the ball surface. These patterns M3 and M4 represent pentagonal or hexagonal patterns so as to surround one circular dimple D as shown in FIG.

更に、別の模様として、図１４に示された模様があり、この模様は、５個または６個のディンプルに交差して大小の真円形Ｍ５，Ｍ６を呈するものである。これらの真円模様Ｍ５，Ｍ６は、図１５に示されるように、１個の円形ディンプルＤを取り囲むように配置されている。 Furthermore, as another pattern, there is a pattern shown in FIG. 14, and this pattern crosses five or six dimples to present large and small true circles M5 and M6. These perfect circle patterns M5 and M6 are arranged so as to surround one circular dimple D as shown in FIG.

なお、本発明では、図９〜図１５に示された多角形模様または円形模様の形状に限定されるものではなく、また、その模様の配置態様も図面の態様に限定されるものではなく、本発明の要旨を逸脱しない限り、その模様の構成等は適宜設計変更することができる。なお、ボール表面に窪みとディンプルとをバランスよく配置させる方法としては、回転対称や正多面体等の公知のディンプルの配置方法を利用することが望ましい。 In addition, in this invention, it is not limited to the shape of the polygonal pattern or circular pattern shown by FIGS. 9-15, Moreover, the arrangement | positioning aspect of the pattern is not limited to the aspect of drawing, As long as the gist of the present invention is not deviated, the structure of the pattern and the like can be appropriately changed in design. In addition, as a method of arranging the depressions and the dimples in a balanced manner on the ball surface, it is desirable to use a known dimple arrangement method such as rotational symmetry or regular polyhedron.

上記の模様Ｍの形成方法としては、例えば、ボール成形金型のキャビティ壁部に、模様用の窪み１０ａや溝１０ｂに相当する突条部をディンプル等の凹凸部とともに形成し、この金型を用いて射出成形することにより、ボール表面１ａに模様Ｍを形成する方法が挙げられる。このような金型を作成する場合は、通常の手法と同様、３ＤＣＡＤ・ＣＡＭを使用し、反転用マスター型に、全表面形状を直接３次元で削りだす手法、或いは、成型用金型のキャビティ壁部を直接３次元で削りだす手法を用いることができる。 As a method for forming the pattern M, for example, a protrusion corresponding to the pattern depression 10a and the groove 10b is formed on the cavity wall portion of the ball molding die together with uneven portions such as dimples. A method of forming the pattern M on the ball surface 1a by injection molding using the method can be mentioned. When creating such a mold, the 3D CAD / CAM is used as in the normal method, and the entire surface shape is directly cut in three dimensions on the reversal master mold, or the cavity of the molding mold It is possible to use a method of directly cutting the wall portion in three dimensions.

なお、本発明のゴルフボールにおいては、従来の印刷手法によって形成された模様をボール表面に表示することを妨げるものではない。 In the golf ball of the present invention, it does not prevent the display of the pattern formed by the conventional printing technique on the ball surface.

本発明のゴルフボールは、上記実施例に限定されるものではなく、ボール表面に形成されるディンプル等の凹凸部の形状や配置態様、更には模様の種類、形成位置などは、適宜変更することができ、その他の構成も本発明の要旨を逸脱しない限り、適宜変更して差し支えない。本発明のゴルフボールにおける他の構成要素については特に制限されず、ワンピースゴルフボール，ツーピースゴルフボール及び３層構造以上のマルチピースゴルフボール等のソリッドゴルフボールとしてもよく、コアやカバー等である各部材の材料については、公知のゴム材料やアイオノマー樹脂，ポリエステルエラストマー及びウレタン樹脂等の公知の熱可塑性樹脂又は熱可塑性エラストマーなどを任意に採用し、所望の厚さや硬度に調整することができる。なお、ボール全体の重量、直径についてはゴルフ規則に従って適宜設定することができ、通常は直径４２．６７ｍｍ以上、重量４５．９３ｇ以下である。 The golf ball of the present invention is not limited to the above-described embodiments, and the shape and arrangement of irregularities such as dimples formed on the surface of the ball, as well as the type and position of the pattern, can be changed as appropriate. However, other configurations may be appropriately changed without departing from the gist of the present invention. Other components in the golf ball of the present invention are not particularly limited, and may be a solid golf ball such as a one-piece golf ball, a two-piece golf ball, and a multi-piece golf ball having a three-layer structure or more, each of which is a core, a cover, or the like. About the material of a member, well-known thermoplastic resins or thermoplastic elastomers, such as a well-known rubber material, an ionomer resin, a polyester elastomer, and a urethane resin, are arbitrarily employ | adopted, It can adjust to desired thickness and hardness. Note that the weight and diameter of the entire ball can be set as appropriate according to the golf rules, and usually the diameter is 42.67 mm or more and the weight is 45.93 g or less.

以下、実施例と比較例を示し、本発明を具体的に説明するが、本発明は下記の実施例に制限されるものではない。 EXAMPLES Hereinafter, although an Example and a comparative example are shown and this invention is demonstrated concretely, this invention is not restrict | limited to the following Example.

〔実施例１〜３、比較例１〕
表１に示す共通の配合によりコア組成物を調整した後、１５５℃，１５分間の加硫条件により加硫成形することによりゴム製コアを作成した。このコアに対して、下記表２に示す樹脂材料Ｎｏ．１〜Ｎｏ．３を用いて包囲層、中間層、及びカバー（最外層）を順に射出成形法により成形して図８に示したフォーピースソリッドゴルフボールを作成した。図中の符号について、Ｇはゴルフボール、１はコア、２は包囲層、３は中間層及び４はカバーであり、カバー４の表面には所定のディンプルＤが形成される。そして、各実施例及び比較例のゴルフボールの構造の詳細は表３に示し、ディンプル態様については表４及び図９，１２，１４及び１６に示した。ゴルフボールの飛び性能を評価し、その結果を表４に併記した。 [Examples 1 to 3, Comparative Example 1]
After adjusting the core composition according to the common formulation shown in Table 1, a rubber core was prepared by vulcanization molding at 155 ° C. for 15 minutes. The resin material No. shown in Table 2 below is applied to this core. 1-No. The four-piece solid golf ball shown in FIG. 8 was formed by sequentially molding the envelope layer, the intermediate layer, and the cover (outermost layer) using No. 3 by the injection molding method. In the figure, G is a golf ball, 1 is a core, 2 is a surrounding layer, 3 is an intermediate layer, and 4 is a cover. A predetermined dimple D is formed on the surface of the cover 4. The details of the structures of the golf balls of the examples and comparative examples are shown in Table 3, and the dimple modes are shown in Table 4 and FIGS. The flying performance of the golf ball was evaluated, and the results are also shown in Table 4.

なお、表１中に記載した主な材料の商品名は以下の通りである。
・ポリブタジエン：商品名「ＢＲ７３０」ＪＳＲ社製
・老化防止剤：商品名「ノクラックＮＳ−６」大内新興化学工業社製
２，２−メチレンビス（４−メチル−６−ブチルフェノール）
・過酸化物：商品名「パーヘキサＣ４０」日本油脂社製
１，１−ジ（ｔ−ブチルパーオキシ）シクロヘキサンとシリカとの混
合物 The trade names of main materials described in Table 1 are as follows.
・ Polybutadiene: Trade name “BR730” manufactured by JSR ・ Anti-aging agent: Trade name “NOCRACK NS-6” manufactured by Ouchi Shinsei Chemical Industry Co., Ltd.
2,2-methylenebis (4-methyl-6-butylphenol)
・ Peroxide: Product name “Perhexa C40” manufactured by NOF Corporation
Mixture of 1,1-di (t-butylperoxy) cyclohexane and silica
Compound

なお、表２中に記載した主な材料の商品名は以下の通りである。上記の数字は全て重量部である。
・ハイミラン：三井デュポンポリケミカル社製のアイオノマー
・ダイナロン６１００Ｐ：ＪＳＲ社製の水添ポリマー
・ハイトレル：東レデュポン社製のポリエステルエラストマー
・ベヘニン酸：日本油脂社製ＮＡＡ２２２−Ｓビーズ指定
・水酸化カルシウム：白石工業社製ＣＬＳ−Ｂ指定
・Ｔ８２６０、Ｔ−８２９０、Ｔ８２９５：
DIC Bayer Polymer社製の商標パンデックス、ＭＤＩ−ＰＴＭ
Ｇタイプ熱可塑性ポリウレタン
・ポリエチレンワックス：「サンワックス１６１Ｐ」（三洋化成社製）
・イソシアネート化合物：４，４’−ジフェニルメタンジイソシアネート In addition, the trade names of main materials described in Table 2 are as follows. All the above numbers are parts by weight.
・ High Milan: Ionomer made by Mitsui DuPont Polychemical ・ Dynalon 6100P: Hydrogenated polymer made by JSR ・ Hytrel: Polyester elastomer made by Toray DuPont ・ Behenic acid: NAA222-S bead designated by NOF Corporation ・ Calcium hydroxide: CLS-B designation, T8260, T-8290, T8295 made by Shiroishi
DIC Bayer Polymer's trademark Pandex, MDI-PTM
G-type thermoplastic polyurethane / polyethylene wax: “Sun Wax 161P” (manufactured by Sanyo Chemical Industries)
・ Isocyanate compound: 4,4'-diphenylmethane diisocyanate

飛び性能
ドライバー（Ｗ＃１）を打撃ロボットにセットし、ヘッドスピード４５ｍ／ｓにて打出し角１０°で打撃した時の飛距離を測定した。 A flying performance driver (W # 1) was set on the hitting robot, and the flying distance when hitting at a launch angle of 10 ° at a head speed of 45 m / s was measured.

表４に示されるように、外表面からの深さが全体に実質上均一な窪みによって模様を形成した実施例１〜３のゴルフボールは、そのような窪みを形成しない比較例１のゴルフボールに比べて、飛距離が伸びることが分かった。即ち、本実施例のゴルフボールでは、表面に実質的に均一な窪みをバランスよく配置することでボールの空気力学的性能を向上させたものである。 As shown in Table 4, the golf balls of Examples 1 to 3 in which a pattern is formed by a depression having a substantially uniform depth from the outer surface as a whole. The golf ball of Comparative Example 1 in which such a depression is not formed. It was found that the flight distance was increased compared to. That is, in the golf ball of this example, the aerodynamic performance of the ball is improved by arranging substantially uniform depressions on the surface in a balanced manner.

本発明のゴルフボールを示す正面図である。1 is a front view showing a golf ball of the present invention. 図１のゴルフボールの外表面付近を示す一部断面図（Ａ−Ａ断面図）である。FIG. 2 is a partial cross-sectional view (AA cross-sectional view) showing the vicinity of the outer surface of the golf ball in FIG. 1. 本発明の他のゴルフボールを示した正面図である。It is the front view which showed the other golf ball of this invention. 図３のゴルフボールの外表面付近を示す一部断面図（Ｂ−Ｂ断面図）である。FIG. 4 is a partial cross-sectional view (BB cross-sectional view) showing the vicinity of the outer surface of the golf ball in FIG. 3. ボール外表面に形成される模様の他の例を示した一部断面図である。It is the partial cross section figure which showed the other example of the pattern formed in a ball | bowl outer surface. 本発明の別のゴルフボールを示す正面図である。It is a front view which shows another golf ball of this invention. 図６のゴルフボールの外表面付近を示す一部断面図（Ｃ−Ｃ断面図）である。FIG. 7 is a partial cross-sectional view (CC cross-sectional view) showing the vicinity of the outer surface of the golf ball in FIG. 6. ゴルフボールの内部構造の一例を示す断面図である。It is sectional drawing which shows an example of the internal structure of a golf ball. 実施例１のゴルフボールを示す正面図である。1 is a front view showing a golf ball of Example 1. FIG. 図９の模様を表したボール表面の一部拡大図である。FIG. 10 is a partially enlarged view of the ball surface representing the pattern of FIG. 9. 模様として現れるボール表面上の溝の様子を示す部分斜視図である。It is a fragmentary perspective view which shows the mode of the groove | channel on the ball | bowl surface which appears as a pattern. 実施例２のゴルフボールを示す正面図である。6 is a front view showing a golf ball of Example 2. FIG. 図１２の模様を表したボール表面の一部拡大図である。FIG. 13 is a partially enlarged view of the ball surface showing the pattern of FIG. 12. 実施例３のゴルフボールを示す正面図である。6 is a front view showing a golf ball of Example 3. FIG. 図１４の模様を表したボール表面の一部拡大図である。FIG. 15 is a partially enlarged view of the ball surface showing the pattern of FIG. 14. 比較例のゴルフボール示す正面図である。It is a front view which shows the golf ball of a comparative example.

Explanation of symbols

Ｇゴルフボール
Ｄディンプル
Ｌ陸部
Ｍ模様
１ａボール表面
１０ａ窪み
１０ｂ溝
ｄ_p 窪みの深さ
ｄ_D ディンプルの深さ G Golf ball D Dimple L Land M Pattern 1a Ball surface 10a Depression 10b Groove d _p Depth depth d _D Dimple depth

Claims

In a golf ball displaying a pattern of characters, figures, etc. on the outer surface of the ball on which the concave and / or convex portions are formed, the pattern is displayed by a depression having a substantially uniform depth from the outer surface as a whole, A golf ball characterized in that S / N × 100 is 100% or less, where S is the number of depressions with substantially uniform depth from the outer surface and N is the total number of dimples.

The golf ball according to claim 1, wherein among the patterns, a pattern having a contour length within a range of 10 to 55 mm includes 10% or more of the entire pattern.

The golf ball according to claim 1, wherein the pattern is formed by a straight line and / or a curved line.

In a golf ball displaying a pattern of characters, figures, etc. on the outer surface of the ball on which a concave portion and / or a convex portion are formed, the above pattern is displayed by a depression having a substantially uniform depth from the outer surface. A golf ball characterized in that the pattern is circular or elliptical.

In a golf ball displaying a pattern of characters, figures, etc. on the outer surface of the ball on which a concave portion and / or a convex portion are formed, the above pattern is displayed by a depression having a substantially uniform depth from the outer surface. A golf ball characterized by a polygonal pattern.