JP2009045027A - Light-shielding agricultural film - Google Patents
Light-shielding agricultural film Download PDFInfo
- Publication number
- JP2009045027A JP2009045027A JP2007215567A JP2007215567A JP2009045027A JP 2009045027 A JP2009045027 A JP 2009045027A JP 2007215567 A JP2007215567 A JP 2007215567A JP 2007215567 A JP2007215567 A JP 2007215567A JP 2009045027 A JP2009045027 A JP 2009045027A
- Authority
- JP
- Japan
- Prior art keywords
- light
- weight
- agricultural film
- shielding
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、農作物の栽培施設（農業用ハウス）に使用される遮光性農業用フィルムに関する。詳しくは、金属製のパイプなどにより構成された栽培施設内において、太陽からの採光を調整するために栽培施設内に展張される遮光性農業用フィルムに関する。 The present invention relates to a light-shielding agricultural film used in a crop cultivation facility (agricultural house). Specifically, the present invention relates to a light-shielding agricultural film that is spread in a cultivation facility in order to adjust daylighting in a cultivation facility constituted by a metal pipe or the like.
近年、植物の栽培方法として植物の習性を利用した栽培方法が提案されている。このような栽培方法の一つとして、植物の光周性を利用した栽培方法が挙げられ、これは太陽からの採光を適宜調整することにより、陽の当たる時間（明期）と陽の当たらない時間（暗期）とを調整して、花芽の生育や開花を早めたり逆に遅らせたりする方法である。 In recent years, cultivation methods using plant habits have been proposed as plant cultivation methods. As one of such cultivation methods, there is a cultivation method using the photoperiodicity of the plant, and this is adjusted by appropriately adjusting the daylighting from the sun, so that it is not exposed to the sun. This is a method of adjusting the time (dark period) to accelerate or reverse the growth and flowering of flower buds.
上記植物の光周性を利用した栽培方法は、例えば、暗期を長くすることによって花芽がつきやすくなるキクの栽培などに用いられている。ここで、暗期を長くする方法としては、昼間に遮光性の高いフィルムで農業用ハウス内を覆う方法が採られている。 The cultivation method using the photoperiodicity of the above-mentioned plant is used, for example, for cultivation of chrysanthemum that makes flower buds easily attached by extending the dark period. Here, as a method of lengthening the dark period, a method of covering the inside of an agricultural house with a film having a high light shielding property in the daytime is employed.
このような暗期を長くして行う栽培方法に使用される遮光率の高いフィルムとしては、例えば、特許文献１に、三層以上の多層フィルムにおいて、白色層（酸化チタン含有）、黒色層（カーボンブラック含有）銀色層（アルミニウム含有）がこの順に積層された農業用フィルムが、特許文献２に、透明層、白色層（酸化チタン含有）、灰色層（酸化チタン、カーボンブラック含有）、銀色層（アルミニウム含有）及び透明層がこの順に積層された農業用フィルムが開示されている。 As a film with a high light-shielding rate used for the cultivation method performed by extending such a dark period, for example, in Patent Document 1, in a multilayer film of three or more layers, a white layer (containing titanium oxide), a black layer ( Agricultural film in which silver layers (containing aluminum) are laminated in this order is disclosed in Patent Document 2, as a transparent layer, a white layer (containing titanium oxide), a gray layer (containing titanium oxide and carbon black), and a silver layer. An agricultural film in which (aluminum-containing) and a transparent layer are laminated in this order is disclosed.
しかしながら、アルミニウムを含有してなる農業用フィルムは、フィルムの腰が強くなっているため、農業用ハウス内張り資材（以下、「カーテン資材」という）として使用した場合、カーテン資材を収納する際にコンパクトに収納することができないという問題があった。 However, since agricultural films containing aluminum have a strong film, they are compact when storing curtain materials when used as agricultural lining materials (hereinafter referred to as “curtain materials”). There was a problem that it could not be stored.
又、上述のような農業用フィルムは、防曇性が不十分であるため、農業用フィルムの農業用ハウス内面側の表面に付着した結露水が作物の上に落下する、所謂、ボタ落ち現象により作物に病害が発生するという問題も生じた。 Moreover, since the above-mentioned agricultural film has insufficient anti-fogging property, so-called “bottom dropping phenomenon” in which dew condensation water adhering to the surface of the agricultural film on the inner surface of the agricultural house falls on the crop. As a result, there was a problem that crops caused diseases.
防曇性に優れた農業用フィルムとしては、特許文献３や特許文献４に、フィルム表面にコロイダルシリカやコロイダルアルミナなどの無機微粒子を主成分とする防曇層を形成してなる農業用フィルムが提案されている。 As an agricultural film excellent in antifogging properties, Patent Document 3 and Patent Document 4 disclose an agricultural film formed by forming an antifogging layer mainly composed of inorganic fine particles such as colloidal silica and colloidal alumina on the film surface. Proposed.
しかしながら、上記無機微粒子を主成分とする防曇層を形成してなる農業用フィルムは、カーテン資材として使用した場合、カーテンの開閉時に無機微粒子が防曇層に擦れて擦れ傷が発生し、その傷部分に結露水が停滞して、ボタ落ち現象が発生してしまうという問題があった。 However, the agricultural film formed with the antifogging layer mainly composed of the inorganic fine particles, when used as a curtain material, the inorganic fine particles rub against the antifogging layer when the curtain is opened and closed, and scratches are generated. There was a problem that the condensed water stagnated at the scratched part, resulting in a dripping phenomenon.
本発明は、遮光性に優れ且つカーテン資材として使用した際にコンパクトに収納することができると共に、ボタ落ち現象を生じさせにくい遮光性農業用フィルムを提供する。 The present invention provides a light-shielding agricultural film that is excellent in light-shielding properties and that can be stored compactly when used as a curtain material and that is less likely to cause a drop-off phenomenon.
本発明の遮光性農業用フィルムは、密度が０．９００〜０．９３０ｇ／ｃｍ3で且つメルトフローレイト（ＭＦＲ）が０．３〜５．０ｇ／１０分であるポリエチレン系樹脂１００重量部、白色顔料５．０〜３０重量部及び黒色顔料０．１〜５．０重量部を含有してなる樹脂組成物（ａ）からなる層（Ａ）、酢酸ビニル含有量が５．０〜２５重量％で且つメルトフローレイト（ＭＦＲ）が０．５〜４．０ｇ／１０分であるエチレン−酢酸ビニル共重合体１００重量部、白色顔料１．０〜１０重量部及び黒色顔料０．１〜５．０重量部を含有してなる樹脂組成物（ｂ）からなる層（Ｂ）、並びに、酢酸ビニル含有量が３．０〜１０重量％で且つメルトフローレイト（ＭＦＲ）が０．５〜４．０ｇ／１０分であるエチレン−酢酸ビニル共重合体１００重量部及び白色顔料５．０〜３０重量部を含有し且つ黒色顔料を含有せずになる樹脂組成物（ｃ）からなる層（Ｃ）が、この順に積層一体化されてなる遮光性農業用フィルムであって、上記樹脂組成物（ａ）、（ｂ）及び（ｃ）のうちの少なくとも一つに、上記樹脂組成物を構成している樹脂成分１００重量部に対して非イオン系界面活性剤が０．１〜１０重量部含有されていることを特徴とする。 The light-shielding agricultural film of the present invention has a density of 0.900 to 0.930 g / cm 3 and a melt flow rate (MFR) of 0.3 to 5.0 g / 10 min. A layer (A) comprising a resin composition (a) containing 5.0 to 30 parts by weight of a white pigment and 0.1 to 5.0 parts by weight of a black pigment, and a vinyl acetate content of 5.0 to 25 weights % And an ethylene-vinyl acetate copolymer having a melt flow rate (MFR) of 0.5 to 4.0 g / 10 min, 100 to 10 parts by weight of a white pigment, and 0.1 to 5 parts of a black pigment. A layer (B) comprising the resin composition (b) containing 0.0 part by weight, a vinyl acetate content of 3.0 to 10% by weight and a melt flow rate (MFR) of 0.5 to 4; 0.0 g / 10 min ethylene-vinyl acetate copolymer 10 For light-shielding agriculture, a layer (C) made of a resin composition (c) containing 5.0 parts by weight and white pigment and containing no black pigment is laminated and integrated in this order. It is a film, Comprising: At least one of the resin compositions (a), (b) and (c) has a nonionic surface active activity with respect to 100 parts by weight of the resin component constituting the resin composition. 0.1 to 10 parts by weight of the agent is contained.
上記層（Ａ）を構成する樹脂組成物（ａ）には、ポリエチレン系樹脂が含有される。上記ポリエチレン系樹脂としては、特に限定されず、例えば、低密度ポリエチレン、中密度ポリエチレン、エチレン−α−オレフィン共重合体などが挙げられ、単独で用いられても、二種以上が併用されてもよい。これらのポリエチレン系樹脂の中でもエチレン−α−オレフィン共重合体が好ましく、直鎖状低密度ポリエチレンがより好ましい。 The resin composition (a) constituting the layer (A) contains a polyethylene resin. The polyethylene resin is not particularly limited, and examples thereof include low density polyethylene, medium density polyethylene, and ethylene-α-olefin copolymer. Good. Among these polyethylene resins, ethylene-α-olefin copolymers are preferable, and linear low density polyethylene is more preferable.
上記直鎖状低密度ポリエチレンは、Ziegler触媒や、メタロセン触媒などのシングルサイト系触媒を用いて、エチレンとα−オレフィンとを共重合して得られ、α−オレフィンの種類や量を調整することによって密度範囲を制御することができる。 The linear low-density polyethylene is obtained by copolymerizing ethylene and α-olefin using a single-site catalyst such as Ziegler catalyst or metallocene catalyst, and adjusting the type and amount of α-olefin. Can control the density range.
なお、上記α−オレフィンとしては、プロピレン、１−ブテン、１−ペンテン、１−ヘキセン、４−メチル−１−ペンテン、１−ヘプテン、１−オクテンなどが挙げられ、単独で用いられても、二種以上が併用されてもよい。 In addition, examples of the α-olefin include propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-heptene, 1-octene, and the like. Two or more kinds may be used in combination.
そして、上記ポリエチレン系樹脂の密度は、低いと、遮光性農業用フィルムを畳んで保管する際にブロッキングが発生する一方、高いと、遮光性農業用フィルムは腰が強くなって、カーテン資材として使用した際にコンパクトに収納することができなくなるので、０．９００〜０．９３０ｇ／ｃｍ3に限定され、０．９０５〜０．９２５ｇ／ｃｍ3が好ましく、０．９１０〜０．９２０ｇ／ｃｍ3がより好ましい。 When the density of the polyethylene resin is low, blocking occurs when the light-shielding agricultural film is folded and stored, while when the density is high, the light-shielding agricultural film is stiff and used as a curtain material. since it is impossible to compact storage upon, limited to 0.900~0.930g / cm 3, preferably 0.905~0.925g / cm 3, 0.910~0.920g / cm 3 Is more preferable.
なお、本発明における熱可塑性樹脂の密度は、ＪＩＳ Ｋ７１１２「プラスチック−非発泡プラスチックの密度及び比重の測定方法」に準拠して測定された値をいう。 The density of the thermoplastic resin in the present invention refers to a value measured in accordance with JIS K7112 “Plastic—Method for measuring density and specific gravity of non-foamed plastic”.
又、上記ポリエチレン系樹脂のメルトフローレイト（ＭＦＲ）は、小さいと、層（Ａ）ひいては遮光性農業用フィルムの製膜性が悪化する一方、大きいと、層（Ａ）ひいては遮光性農業用フィルムの機械的強度が低下するので、０．３〜５．０ｇ／１０分に限定され、０．５〜３．０ｇ／１０分が好ましく、０．８〜２．０ｇ／１０分がより好ましい。 On the other hand, if the melt flow rate (MFR) of the polyethylene resin is small, the layer (A) and thus the film-forming property of the light-shielding agricultural film is deteriorated. On the other hand, if the melt flow rate (MFR) is large, the layer (A) and thus the light-shielding agricultural film. Is reduced to 0.3 to 5.0 g / 10 minutes, preferably 0.5 to 3.0 g / 10 minutes, and more preferably 0.8 to 2.0 g / 10 minutes.
ここで、本発明におけるポリエチレン系樹脂及びエチレン−酢酸ビニル共重合体のメルトフローレイト（ＭＦＲ）は、ＪＩＳ Ｋ７２１０「プラスチック−熱可塑性プラスチックのメルトマスフローレイト及びメルトボリュームフローレイトの試験方法」に準拠して、温度１９０℃、荷重２１．１８Ｎの条件で測定された値をいう。 Here, the melt flow rate (MFR) of the polyethylene resin and the ethylene-vinyl acetate copolymer in the present invention conforms to JIS K7210 “Testing method for melt mass flow rate and melt volume flow rate of plastic-thermoplastic plastic”. The value measured under conditions of a temperature of 190 ° C. and a load of 21.18N.
なお、上記樹脂組成物（ａ）に複数種類のポリエチレン系樹脂が含有されている場合、ポリエチレン系樹脂の密度及びメルトフローレイト（ＭＦＲ）とはそれぞれ、ポリエチレン系樹脂の混合物の見かけ上の密度及びメルトフローレイト（ＭＦＲ）をいう。 When a plurality of types of polyethylene resin are contained in the resin composition (a), the density of the polyethylene resin and the melt flow rate (MFR) are the apparent density of the mixture of polyethylene resins and Melt flow rate (MFR).
そして、上記樹脂組成物（ａ）には、遮光性農業用フィルムの遮光性及び遮熱性を高める目的で白色顔料が含有される。上記白色顔料としては、白色を呈する顔料であれば特に限定されず、例えば、ルチル型酸化チタン、アナターゼ型酸化チタンなどの酸化チタン、酸化亜鉛（亜鉛華）、硫化亜鉛、鉛白、モリブデンホワイト、リトポンなどが挙げられ、これらの中でも遮光性に優れた酸化チタンが好ましく、特に遮光性に優れたルチル型酸化チタンがより好ましい。なお、上記白色顔料は、単独で用いられても、二種以上が併用されてもよい。なお、本発明において、白色とは、いわゆるマンセル表色系でいう明度が８〜１０である色を意味する。 And the said resin composition (a) contains a white pigment in order to improve the light-shielding property and heat-shielding property of a light-shielding agricultural film. The white pigment is not particularly limited as long as it is a white pigment. For example, rutile titanium oxide, titanium oxide such as anatase titanium oxide, zinc oxide (zinc white), zinc sulfide, lead white, molybdenum white, Among them, titanium oxide having excellent light shielding properties is preferable, and rutile type titanium oxide having particularly excellent light shielding properties is more preferable. In addition, the said white pigment may be used independently or 2 or more types may be used together. In the present invention, white means a color having a brightness of 8 to 10 in the so-called Munsell color system.
又、上記白色顔料の平均粒子径は、小さいと、白色顔料が凝集しやすくなって、樹脂組成物（ａ）中に白色顔料を均一に分散させることが困難になったり、遮光性農業用フィルムの取扱性が悪化することがある一方、大きいと、層（Ａ）ひいては遮光性農業用フィルムの機械的強度が低下することがあるので、１００〜３００ｎｍが好ましく、１５０〜２５０ｎｍがより好ましい。 If the average particle size of the white pigment is small, the white pigment tends to aggregate, making it difficult to uniformly disperse the white pigment in the resin composition (a). On the other hand, if it is large, the mechanical strength of the layer (A) and thus the light-shielding agricultural film may be lowered. Therefore, 100 to 300 nm is preferable, and 150 to 250 nm is more preferable.
なお、本発明における白色顔料の平均粒子径は、レーザー回折法により測定された値をいう。 In addition, the average particle diameter of the white pigment in the present invention refers to a value measured by a laser diffraction method.
上記樹脂組成物（ａ）中における白色顔料の含有量は、上記密度が０．９００〜０．９３０ｇ／ｃｍ3で且つメルトフローレイト（ＭＦＲ）が０．３〜５．０ｇ／１０分であるポリエチレン系樹脂１００重量部に対して５．０〜３０重量部に限定され、１０〜２５重量部が好ましい。これは、上記樹脂組成物（ａ）における白色顔料の含有量が、少ないと、層（Ａ）における黒色顔料の割合が高くなって層（Ａ）が黒っぽくなり、ひいては層（Ｃ）の色目が黒くなって、遮光性農業用フィルムの遮熱性が低下する一方、多いと、層（Ａ）ひいては遮光性農業用フィルムの製膜性及び機械的強度が低下するからである。 The content of the white pigment in the resin composition (a) is such that the density is 0.900 to 0.930 g / cm 3 and the melt flow rate (MFR) is 0.3 to 5.0 g / 10 minutes. The amount is limited to 5.0 to 30 parts by weight with respect to 100 parts by weight of the polyethylene resin, and preferably 10 to 25 parts by weight. This is because when the content of the white pigment in the resin composition (a) is small, the ratio of the black pigment in the layer (A) becomes high, the layer (A) becomes dark, and the color of the layer (C) This is because the film becomes black and the heat shielding properties of the light-shielding agricultural film are lowered. On the other hand, if the amount is large, the film-forming property and mechanical strength of the light-shielding agricultural film are lowered.
そして、上記樹脂組成物（ａ）には、遮光性農業用フィルムの遮光性を高める目的で黒色顔料が含有される。上記黒色顔料としては、黒色を呈する顔料であれば特に限定されず、例えば、塗料用、ペースト用、プラスチックへの充填用などの用途に使用されているカーボンブラック、アニリンブラックなどが挙げられ、安全性及び経済性からカーボンブラックが好ましい。なお、上記黒色顔料は、単独で用いられても、二種以上が併用されてもよい。なお、本発明において、黒色とは、いわゆるマンセル表色系でいう明度が０〜２である色を意味する。 The resin composition (a) contains a black pigment for the purpose of enhancing the light shielding properties of the light shielding agricultural film. The black pigment is not particularly limited as long as it is a black pigment, and examples thereof include carbon black and aniline black that are used for paints, pastes, plastics, and the like. Carbon black is preferable from the viewpoint of safety and economy. In addition, the said black pigment may be used independently, or 2 or more types may be used together. In the present invention, black means a color having a lightness of 0 to 2 in the so-called Munsell color system.
又、上記樹脂組成物（ａ）中における黒色顔料の含有量は、上記密度が０．９００〜０．９３０ｇ／ｃｍ3で且つメルトフローレイト（ＭＦＲ）が０．３〜５．０ｇ／１０分であるポリエチレン系樹脂１００重量部に対して０．１〜５．０重量部に限定され、０．５〜３．０重量部が好ましく、１．０〜２．５重量部がより好ましい。これは、上記樹脂組成物（ａ）における黒色顔料の含有量が、少ないと、遮光性農業用フィルムの遮光性が低下する一方、多いと、層（Ａ）が黒っぽくなり、ひいては層（Ｃ）の色目が黒くなって、遮光性農業用フィルムの遮熱性が低下するからである。 The black pigment content in the resin composition (a) is such that the density is 0.900 to 0.930 g / cm 3 and the melt flow rate (MFR) is 0.3 to 5.0 g / 10 minutes. The amount is limited to 0.1 to 5.0 parts by weight, preferably 0.5 to 3.0 parts by weight, and more preferably 1.0 to 2.5 parts by weight with respect to 100 parts by weight of the polyethylene resin. This is because if the content of the black pigment in the resin composition (a) is small, the light-shielding property of the light-shielding agricultural film is deteriorated, whereas if it is large, the layer (A) becomes dark, and as a result, the layer (C). This is because the color of the film becomes black and the heat-shielding property of the light-shielding agricultural film is lowered.
本発明の遮光性農業用フィルムの層（Ｂ）を構成する樹脂組成物（ｂ）には、エチレン−酢酸ビニル共重合体が含有される。上記エチレン−酢酸ビニル共重合体における酢酸ビニル成分の含有量は、少ないと、層（Ｂ）ひいては遮光性農業用フィルムは柔軟性が不十分になって、遮光性農業用フィルムをカーテン資材として使用した際にコンパクトに収納することができないという問題が生じる一方、多いと、層（Ｂ）ひいては遮光性農業用フィルムの製膜性が悪化したり、機械的強度が低下したりするので、５．０〜２５重量％に限定され、１０〜２０重量％が好ましい。 The resin composition (b) constituting the layer (B) of the light-shielding agricultural film of the present invention contains an ethylene-vinyl acetate copolymer. If the content of the vinyl acetate component in the ethylene-vinyl acetate copolymer is small, the layer (B) and thus the light-shielding agricultural film is insufficiently flexible, and the light-shielding agricultural film is used as a curtain material. On the other hand, there is a problem that it cannot be stored in a compact manner. On the other hand, if it is large, the film-forming property of the layer (B) and thus the light-shielding agricultural film is deteriorated, and the mechanical strength is lowered. It is limited to 0 to 25% by weight, and preferably 10 to 20% by weight.
又、上記エチレン−酢酸ビニル共重合体のメルトフローレイト（ＭＦＲ）は、小さいと、層（Ｂ）ひいては遮光性農業用フィルムの製膜性が低下する一方、大きいと、層（Ｂ）ひいては遮光性農業用フィルムの機械的強度が低下するので、０．５〜４．０ｇ／１０分に限定され、０．８〜２．０ｇ／１０分が好ましい。 On the other hand, if the melt flow rate (MFR) of the ethylene-vinyl acetate copolymer is small, the layer (B) and thus the film-forming property of the light-shielding agricultural film is deteriorated. Since the mechanical strength of the agricultural film is reduced, it is limited to 0.5 to 4.0 g / 10 minutes, and preferably 0.8 to 2.0 g / 10 minutes.
なお、上記樹脂組成物（ｂ）に複数種類のエチレン−酢酸ビニル共重合体が含有されている場合、エチレン−酢酸ビニル共重合体の酢酸ビニル成分の含有量及びメルトフローレイト（ＭＦＲ）とはそれぞれ、エチレン−酢酸ビニル共重合体の混合物の見かけ上の酢酸ビニル成分の含有量及びメルトフローレイト（ＭＦＲ）をいう。 In addition, when multiple types of ethylene-vinyl acetate copolymer is contained in the resin composition (b), the content of the vinyl acetate component of the ethylene-vinyl acetate copolymer and the melt flow rate (MFR) They respectively refer to the apparent vinyl acetate component content and melt flow rate (MFR) of the ethylene-vinyl acetate copolymer mixture.
そして、上記樹脂組成物（ｂ）には、遮光性農業用フィルムの遮光性及び遮熱性を向上させる目的で白色顔料が含有される。上記白色顔料としては、上記樹脂組成物（ａ）に含有される白色顔料と同様のものが挙げられ、中でも遮光性に優れた酸化チタンが好ましく、特に遮光性に優れたルチル型酸化チタンがより好ましい。なお、上記白色顔料は、単独で用いられても、二種以上が併用されてもよい。 The resin composition (b) contains a white pigment for the purpose of improving the light shielding properties and heat shielding properties of the light shielding agricultural film. Examples of the white pigment include those similar to the white pigment contained in the resin composition (a). Among these, titanium oxide having excellent light shielding properties is preferable, and rutile titanium oxide having particularly excellent light shielding properties is more preferable. preferable. In addition, the said white pigment may be used independently or 2 or more types may be used together.
又、上記白色顔料の平均粒子径は、小さいと、白色顔料が凝集しやすくなって、樹脂組成物（ｂ）中に白色顔料を均一に分散させることが困難になったり、遮光性農業用フィルムの取扱性が悪化することがある一方、大きいと、層（Ｂ）ひいては遮光性農業用フィルムの機械的強度が低下することがあるので、１００〜３００ｎｍが好ましく、１５０〜２５０ｎｍがより好ましい。 If the average particle size of the white pigment is small, the white pigment tends to aggregate, making it difficult to uniformly disperse the white pigment in the resin composition (b). On the other hand, if it is large, the mechanical strength of the layer (B) and thus the light-shielding agricultural film may be lowered. Therefore, 100 to 300 nm is preferable, and 150 to 250 nm is more preferable.
更に、上記樹脂組成物（ｂ）における白色顔料の含有量は、上記酢酸ビニル含有量が５．０〜２５重量％で且つメルトフローレイト（ＭＦＲ）が０．５〜４．０ｇ／１０分であるエチレン−酢酸ビニル共重合体１００重量部に対して１．０〜１０重量部に限定され、３．０〜８．０重量部が好ましく、４．０〜６．０重量部がより好ましい。これは、上記樹脂組成物（ｂ）における白色顔料の含有量が、少ないと、層（Ｂ）における黒色顔料の割合が高くなって層（Ｂ）が黒っぽくなり、ひいては層（Ｃ）の色目が黒くなって、遮光性農業用フィルムの遮熱性が低下する一方、多いと、層（Ｂ）ひいては遮光性農業用フィルムの製膜性及び機械的強度が低下するからである。 Furthermore, the content of the white pigment in the resin composition (b) is such that the vinyl acetate content is 5.0 to 25% by weight and the melt flow rate (MFR) is 0.5 to 4.0 g / 10 minutes. The amount is limited to 1.0 to 10 parts by weight, preferably 3.0 to 8.0 parts by weight, and more preferably 4.0 to 6.0 parts by weight with respect to 100 parts by weight of an ethylene-vinyl acetate copolymer. This is because, when the content of the white pigment in the resin composition (b) is small, the ratio of the black pigment in the layer (B) becomes high, the layer (B) becomes dark, and the color of the layer (C) This is because the heat-shielding property of the light-shielding agricultural film is lowered and the heat-shielding property of the light-shielding agricultural film is lowered.
又、上記樹脂組成物（ｂ）には、遮光性農業用フィルムの遮光性を高める目的で黒色顔料が含有される。上記黒色顔料としては、上記樹脂組成物（ａ）に含有される黒色顔料と同様のものが挙げられ、安全性及び経済性からカーボンブラックが好ましい。なお、上記黒色顔料は、単独で用いられても、二種以上が併用されてもよい。 The resin composition (b) contains a black pigment for the purpose of enhancing the light shielding properties of the light shielding agricultural film. As said black pigment, the same thing as the black pigment contained in the said resin composition (a) is mentioned, Carbon black is preferable from safety | security and economical efficiency. In addition, the said black pigment may be used independently, or 2 or more types may be used together.
そして、上記樹脂組成物（ｂ）における黒色顔料の含有量は、上記酢酸ビニル含有量が５．０〜２５重量％で且つメルトフローレイト（ＭＦＲ）が０．５〜４．０ｇ／１０分であるエチレン−酢酸ビニル共重合体１００重量部に対して、０．１〜５．０重量部に限定され、０．５〜３．０重量部が好ましく、１．０〜２．０重量部がより好ましい。これは、上記樹脂組成物（ｂ）における黒色顔料の含有量が、少ないと、遮光性農業用フィルムの遮光性が低下する一方、多いと、層（Ｂ）が黒っぽくなり、ひいては層（Ｃ）の色目が黒くなって、遮光性農業用フィルムの遮熱性が低下するからである。 And as for content of the black pigment in the said resin composition (b), the said vinyl acetate content is 5.0 to 25 weight%, and melt flow rate (MFR) is 0.5 to 4.0 g / 10min. It is limited to 0.1 to 5.0 parts by weight with respect to 100 parts by weight of a certain ethylene-vinyl acetate copolymer, preferably 0.5 to 3.0 parts by weight, and 1.0 to 2.0 parts by weight. More preferred. This is because when the content of the black pigment in the resin composition (b) is small, the light-shielding property of the light-shielding agricultural film is deteriorated, whereas when it is large, the layer (B) becomes dark and as a result, the layer (C). This is because the color of the film becomes black and the heat-shielding property of the light-shielding agricultural film is lowered.
本発明の遮光性農業用フィルムの層（Ｃ）を構成する樹脂組成物（ｃ）には、エチレン−酢酸ビニル共重合体が含有される。上記エチレン−酢酸ビニル共重合体における酢酸ビニル成分の含有量は、少ないと、層（Ｃ）ひいては遮光性農業用フィルムの柔軟性が不十分になって、遮光性農業用フィルムをカーテン資材として使用した際にコンパクトに収納することができないという問題が生じる一方、多いと、層（Ｃ）ひいては遮光性農業用フィルムの製膜性及び機械的強度が低下するので、３．０〜１０重量％に限定され、５．０〜８．０重量％が好ましい。 The resin composition (c) constituting the layer (C) of the light-shielding agricultural film of the present invention contains an ethylene-vinyl acetate copolymer. When the content of the vinyl acetate component in the ethylene-vinyl acetate copolymer is small, the flexibility of the layer (C) and thus the light-shielding agricultural film becomes insufficient, and the light-shielding agricultural film is used as a curtain material. On the other hand, there is a problem in that it cannot be stored in a compact manner. On the other hand, if it is large, the film-forming property and mechanical strength of the light-shielding agricultural film are reduced, so that it is 3.0 to 10% by weight. It is limited and 5.0 to 8.0 weight% is preferable.
又、上記エチレン−酢酸ビニル共重合体のメルトフローレイト（ＭＦＲ）は、小さいと、層（Ｃ）ひいては遮光性農業用フィルムの製膜性が悪化する一方、大きいと、層（Ｃ）ひいては遮光性農業用フィルムの機械的強度が低下するので、０．５〜４．０ｇ／１０分に限定され、０．８〜２．０ｇ／１０分であることが好ましい。 On the other hand, if the melt flow rate (MFR) of the ethylene-vinyl acetate copolymer is small, the layer (C) and thus the film-forming property of the light-shielding agricultural film is deteriorated. On the other hand, if the melt flow rate (MFR) is large, the layer (C) Since the mechanical strength of the agricultural film is reduced, the film is limited to 0.5 to 4.0 g / 10 minutes, and preferably 0.8 to 2.0 g / 10 minutes.
ここで、上記樹脂組成物（ｃ）に複数種類のエチレン−酢酸ビニル共重合体が含有されている場合、エチレン−酢酸ビニル共重合体の酢酸ビニル成分の含有量及びメルトフローレイト（ＭＦＲ）とはそれぞれ、エチレン−酢酸ビニル共重合体の混合物の見かけ上の酢酸ビニル成分の含有量及びメルトフローレイト（ＭＦＲ）をいう。 Here, when a plurality of types of ethylene-vinyl acetate copolymers are contained in the resin composition (c), the content of the vinyl acetate component of the ethylene-vinyl acetate copolymer and the melt flow rate (MFR) Respectively refers to the apparent vinyl acetate component content and melt flow rate (MFR) of the ethylene-vinyl acetate copolymer mixture.
なお、本発明の遮光性農業用フィルムを共押出によって製膜する場合、遮光性農業用フィルムの製膜性の面から、樹脂組成物（ａ）中のポリエチレン系樹脂、樹脂組成物（ｂ）中のエチレン−酢酸ビニル共重合体、及び、樹脂組成物（ｃ）中のエチレン−酢酸ビニル共重合体は、互いにメルトフローレイト（ＭＦＲ）の値が近いものを用いるのが好ましく、具体的には、上記樹脂組成物（ａ）中のポリエチレン系樹脂、樹脂組成物（ｂ）中のエチレン−酢酸ビニル共重合体及び樹脂組成物（ｃ）中のエチレン−酢酸ビニル共重合体のうち、メルトフローレイト（ＭＦＲ）が最も大きいものと最も小さいものとのメルトフローレイト（ＭＦＲ）の差が２．０ｇ／１０分以下であるのが好ましい。 In addition, when film-forming the light-shielding agricultural film of this invention by coextrusion, the polyethylene-type resin in the resin composition (a), the resin composition (b) from the film forming property side of a light-shielding agricultural film The ethylene-vinyl acetate copolymer in the resin and the ethylene-vinyl acetate copolymer in the resin composition (c) are preferably those having close melt flow rate (MFR) values. Among the polyethylene resin in the resin composition (a), the ethylene-vinyl acetate copolymer in the resin composition (b), and the ethylene-vinyl acetate copolymer in the resin composition (c), melt The difference in melt flow rate (MFR) between the largest flow rate (MFR) and the smallest flow rate (MFR) is preferably 2.0 g / 10 min or less.
上記樹脂組成物（ｃ）には、遮光性農業用フィルムの遮光性及び遮熱性を向上させる目的で白色顔料が含有される。上記白色顔料としては、上記樹脂組成物（ａ）に含有される白色顔料と同様のものが挙げられ、中でも遮光性に優れた酸化チタンが好ましく、特に遮光性に優れたルチル型酸化チタンがより好ましい。なお、上記白色顔料は、単独で用いられても、二種以上が併用されてもよい。 The resin composition (c) contains a white pigment for the purpose of improving the light shielding properties and heat shielding properties of the light shielding agricultural film. Examples of the white pigment include those similar to the white pigment contained in the resin composition (a). Among these, titanium oxide having excellent light shielding properties is preferable, and rutile titanium oxide having particularly excellent light shielding properties is more preferable. preferable. In addition, the said white pigment may be used independently or 2 or more types may be used together.
又、上記白色顔料の平均粒子径は、小さいと、白色顔料が凝集しやすくなって、樹脂組成物（ｃ）中に白色顔料を均一に分散させることが困難になったり、遮光性農業用フィルムの取扱性が悪化することがある一方、大きいと、層（Ｃ）ひいては遮光性農業用フィルムの機械的強度が低下することがあるので、１００〜３００ｎｍが好ましく、１５０〜２５０ｎｍがより好ましい。 If the average particle size of the white pigment is small, the white pigment tends to aggregate, making it difficult to uniformly disperse the white pigment in the resin composition (c). On the other hand, if it is large, the mechanical strength of the layer (C) and thus the light-shielding agricultural film may be lowered. Therefore, 100 to 300 nm is preferable, and 150 to 250 nm is more preferable.
そして、上記樹脂組成物（ｃ）における白色顔料の含有量は、上記酢酸ビニル含有量が３．０〜１０重量％で且つメルトフローレイト（ＭＦＲ）が０．５〜４．０ｇ／１０分であるエチレン−酢酸ビニル共重合体１００重量部に対して、５．０〜３０重量部に限定され、１０〜２５重量部が好ましく、１５〜２０重量部がより好ましい。これは、上記樹脂組成物（ｃ）における白色顔料の含有量が、少ないと、層（Ｃ）の白色性が不十分になって、遮光性農業用フィルムの遮熱性が低下する一方、多いと、層（Ｃ）ひいては遮光性農業用フィルムの製膜性及び機械的強度が低下するからである。 The content of the white pigment in the resin composition (c) is such that the vinyl acetate content is 3.0 to 10% by weight and the melt flow rate (MFR) is 0.5 to 4.0 g / 10 minutes. It is limited to 5.0 to 30 parts by weight with respect to 100 parts by weight of a certain ethylene-vinyl acetate copolymer, preferably 10 to 25 parts by weight, and more preferably 15 to 20 parts by weight. This is because when the content of the white pigment in the resin composition (c) is small, the whiteness of the layer (C) becomes insufficient, and the heat shielding properties of the light-shielding agricultural film are reduced. This is because the film-forming property and mechanical strength of the light-shielding agricultural film are lowered.
又、上記樹脂組成物（ｃ）には、黒色顔料が含有されない。これは、遮光性農業用フィルムに黒色顔料が含有されると、層（Ｃ）の白色性が損なわれ、層（Ｃ）が赤外線、遠赤外線を十分に反射できなくなり、遮光性農業用フィルムの遮熱性が低下するからである。 Further, the resin composition (c) does not contain a black pigment. This is because when the black pigment is contained in the light-shielding agricultural film, the whiteness of the layer (C) is impaired, and the layer (C) cannot sufficiently reflect infrared rays and far-infrared rays. This is because the heat shielding property is lowered.
本発明の遮光性農業用フィルムには、その防曇性を向上させる目的で非イオン系界面活性剤が含有される。上記非イオン系界面活性剤としては、防曇性を付与できるものであれば特に限定されないが、多価アルコール脂肪酸エステルや、多価アルコール脂肪酸エステルにエチレンオキサイドやプロピレンオキサイドなどのアルキレンオキサイドを付加してなるアルキレンオキサイド付加多価アルコール脂肪酸エステルが好適に用いられる。 The light-shielding agricultural film of the present invention contains a nonionic surfactant for the purpose of improving the antifogging property. The nonionic surfactant is not particularly limited as long as it can impart antifogging properties, but a polyhydric alcohol fatty acid ester or an alkylene oxide such as ethylene oxide or propylene oxide is added to the polyhydric alcohol fatty acid ester. An alkylene oxide-added polyhydric alcohol fatty acid ester is preferably used.
そして、上記多価アルコール脂肪酸エステルとしては、特に限定されず、グリセリンステアリン酸エステル、ジグリセリンステアリン酸エステル、ポリグリセリンステアリン酸エステル、ソルビトールステアリン酸エステルなどの多価アルコール飽和脂肪酸エステル；グリセリンオレイン酸エステル、ジグリセリンオレイン酸エステルなどの多価アルコール不飽和脂肪酸エステルなどが挙げられ、多価アルコール飽和脂肪酸エステルが好ましい。 The polyhydric alcohol fatty acid ester is not particularly limited, and is a polyhydric alcohol saturated fatty acid ester such as glycerin stearate, diglycerin stearate, polyglycerin stearate, sorbitol stearate; glycerin oleate And polyhydric alcohol unsaturated fatty acid esters such as diglycerin oleate and the like, and polyhydric alcohol saturated fatty acid esters are preferred.
又、上記アルキレンオキサイド付加多価アルコール脂肪酸エステルとしては、上述の多価アルコール脂肪酸エステルに、エチレンオキサイドやプロピレンオキサイドを付加させたものが挙げられる。 Moreover, as said alkylene oxide addition polyhydric alcohol fatty acid ester, what added ethylene oxide and propylene oxide to the above-mentioned polyhydric alcohol fatty acid ester is mentioned.
そして、上記アルキレンオキサイド付加多価アルコール脂肪酸エステルにおけるアルキレンオキサイドの付加モル数は、０．１〜１０モルが好ましい。これは、アルキレンオキサイドの付加モル数が少ないと、遮光性農業用フィルムの防曇性が低下することがある一方、多いと、アルキレンオキサイド付加多価アルコール脂肪酸エステルの水に対する溶解性が高くなり、アルキレンオキサイド付加多価アルコール脂肪酸エステルが結露水に溶解して流れ出し、遮光性農業用フィルムの防曇性が低下することがあるからである。 And as for the addition mole number of the alkylene oxide in the said alkylene oxide addition polyhydric alcohol fatty acid ester, 0.1-10 mol is preferable. This is because when the added mole number of alkylene oxide is small, the antifogging property of the light-shielding agricultural film may be lowered, whereas when it is large, the solubility of the alkylene oxide-added polyhydric alcohol fatty acid ester in water is increased, This is because the alkylene oxide-added polyhydric alcohol fatty acid ester dissolves in the condensed water and flows out, and the antifogging property of the light-shielding agricultural film may be lowered.
そして、上記非イオン系界面活性剤は、上記遮光性農業用フィルムを構成する樹脂組成物（ａ）、（ｂ）又は（ｃ）のうちの少なくとも一つの樹脂組成物に、好ましくは全ての樹脂組成物に、各樹脂組成物を構成している樹脂成分１００重量部に対して０．１〜１０重量部含有され、好ましくは１．０〜５．０重量部含有される。 And the said nonionic surfactant is a resin composition (a), (b) or (c) which comprises the said light-shielding agricultural film, Preferably it is all resin. The composition contains 0.1 to 10 parts by weight, preferably 1.0 to 5.0 parts by weight, based on 100 parts by weight of the resin component constituting each resin composition.
これは、上記遮光性農業用フィルムを構成する樹脂組成物（ａ）、（ｂ）及び（ｃ）の全てにおいて、非イオン系界面活性剤の含有量が、各樹脂組成物を構成している樹脂成分１００重量部に対して０．１重量部未満である場合、遮光性農業用フィルムの防曇性が不十分となり、遮光性農業用フィルムの表面に付着した結露水が農業用ハウス内で栽培している作物の上に直接落下する、所謂、ボタ落ち現象によって作物に病害が発生しやすくなるからである。 This is because, in all of the resin compositions (a), (b) and (c) constituting the light-shielding agricultural film, the content of the nonionic surfactant constitutes each resin composition. When the amount is less than 0.1 part by weight with respect to 100 parts by weight of the resin component, the antifogging property of the light-shielding agricultural film becomes insufficient, and the dew condensation water adhering to the surface of the light-shielding agricultural film is in the agricultural house. This is because a so-called “bottom dropping phenomenon” that falls directly on the cultivated crop is likely to cause disease in the crop.
一方、上記遮光性農業用フィルムを構成する樹脂組成物（ａ）、（ｂ）又は（ｃ）の何れかの樹脂組成物において、非イオン系界面活性剤の含有量が、各樹脂組成物を構成している樹脂成分１００重量部に対して１０重量部を超える場合にあっては、遮光性農業用フィルムの表面に非イオン系界面活性剤がブリードアウトし過ぎて遮光性農業用フィルムがべたつき、遮光性農業用フィルムの取扱性が低下する。 On the other hand, in any one of the resin compositions (a), (b) or (c) constituting the light-shielding agricultural film, the content of the nonionic surfactant is such that each resin composition When the amount exceeds 10 parts by weight with respect to 100 parts by weight of the resin component, the non-ionic surfactant bleeds out on the surface of the light-shielding agricultural film and the light-shielding agricultural film is sticky. The handling property of the light-shielding agricultural film is reduced.
又、上記のようにして遮光性農業用フィルム中に含有されている非イオン系界面活性剤は、ブリードアウトして遮光性農業用フィルムの表面に滲出するため、遮光性農業用フィルムは優れた防曇性を発揮する。 Moreover, since the nonionic surfactant contained in the light-shielding agricultural film as described above bleeds out and oozes out on the surface of the light-shielding agricultural film, the light-shielding agricultural film is excellent. Demonstrates anti-fogging properties.
なお、上記遮光性農業用フィルムには、必要に応じて物性を損なわない範囲においてヒンダードアミン系光安定剤、熱安定剤、紫外線吸収剤、滑剤などが添加されてもよい。 In addition, a hindered amine light stabilizer, a heat stabilizer, an ultraviolet absorber, a lubricant, and the like may be added to the above light-shielding agricultural film as long as the physical properties are not impaired.
上記ヒンダードアミン系光安定剤としては、従来公知の任意のものが使用され、単独あるいは二種以上を混合して使用することができる。具体的には、コハク酸ジメチル−１−（２−ヒドロキシエチル）−４−ヒドロキシ−２，２，６，６−テトラメチルピペリジン重縮合物、テトラキス（２，２，６，６−テトラメチル−４−ピペリジル）−１，２，３，４−ブタンテトラカルボキシレート、ポリ｛［６−［（１，１，３，３−テトラメチルブチル）アミノ］−１，３，５−トリアジン−２，４−ジイル］［（２，２，６，６−テトラメチル−４−ピペリジル）イミノ］ヘキサメチレン［（２，２，６，６−テトラメチル−４−ピペリジル）イミノ］｝などが挙げられる。 As the hindered amine light stabilizer, any conventionally known one can be used, and these can be used alone or in admixture of two or more. Specifically, dimethyl succinate-1- (2-hydroxyethyl) -4-hydroxy-2,2,6,6-tetramethylpiperidine polycondensate, tetrakis (2,2,6,6-tetramethyl- 4-piperidyl) -1,2,3,4-butanetetracarboxylate, poly {[6-[(1,1,3,3-tetramethylbutyl) amino] -1,3,5-triazine-2, 4-diyl] [(2,2,6,6-tetramethyl-4-piperidyl) imino] hexamethylene [(2,2,6,6-tetramethyl-4-piperidyl) imino]} and the like.
そして、上記熱安定剤としては、従来公知の任意のものが使用され、具体的には、カルボン酸の金属塩、フェノール系抗酸化剤、有機亜燐酸エステルなどのキレーターなどが挙げられ、単独で用いられても、二種以上が併用されてもよい。 And as said heat stabilizer, conventionally well-known arbitrary things are used, Specifically, chelators, such as a metal salt of carboxylic acid, a phenolic antioxidant, organic phosphorous acid ester, etc. are mentioned independently Even if it uses, 2 or more types may be used together.
そして、上記紫外線吸収剤としては、従来公知の任意のものが使用され、例えば、ベンゾフェノン系、ベンゾトリアゾール系、サリチル酸エステル系、シアノアクリレート系などを単独あるいは二種以上を混合して使用することができる。具体的には、２，４−ジヒドロキシベンゾフェノン、２−ヒドロキシ−４−オクトキシベンゾフェノン、２−ヒドロキシ−４−ドデシルオキシベンゾフェノン、２，２’−ジヒドロキシ−４−メトキシベンゾフェノン、２，２’−ヒドロキシ−４，４’−ジメトキシベンゾフェノン、２−ヒドロキシ−４−メトキシ−５−スルホベンゾフェノンなどのベンゾフェノン系紫外線吸収剤、２−（２’−ヒドロキシ−５’−ｔｅｒｔ−ブチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−５’−メチルフェニル）ベンゾトリアゾール、２−（２’−ヒドロキシ−３’−ｔｅｒｔ−ブチル−５−メチルフェニル）−５−クロロベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−ブチルフェニル）−５−クロロベンゾトリアゾール、２−（２’−ヒドロキシ−３’，５’−ジ−ｔｅｒｔ−アミルフェニル）−５−クロロベンゾトリアゾールなどのベンゾトリアゾール系紫外線吸収剤が挙げられる。 As the ultraviolet absorber, any conventionally known one can be used. For example, a benzophenone series, a benzotriazole series, a salicylic acid ester series, a cyanoacrylate series or the like can be used alone or in combination of two or more. it can. Specifically, 2,4-dihydroxybenzophenone, 2-hydroxy-4-octoxybenzophenone, 2-hydroxy-4-dodecyloxybenzophenone, 2,2′-dihydroxy-4-methoxybenzophenone, 2,2′-hydroxy Benzophenone ultraviolet absorbers such as -4,4'-dimethoxybenzophenone and 2-hydroxy-4-methoxy-5-sulfobenzophenone, 2- (2'-hydroxy-5'-tert-butylphenyl) benzotriazole, 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2- (2′-hydroxy-3′-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole, 2- (2′-hydroxy- 3 ', 5'-di-tert-butylphenyl) -5-chlorobe Zotoriazoru, 2- (2'-hydroxy-3 ', 5'-di -tert- amylphenyl) -5-benzotriazole ultraviolet absorbents such as chloro benzotriazole.
又、上記滑剤としては、従来公知の任意のものが使用され、ステアリン酸アマイドなどの飽和脂肪酸アマイド、エルカ酸アマイド、オレイン酸アマイドなどの不飽和脂肪酸アマイド、エチレンビスステアリン酸アマイドなどのビスアマイドなどが挙げられ、単独で用いられても、二種以上が併用されてもよい。 As the lubricant, any conventionally known lubricant is used, and saturated fatty acid amide such as stearic acid amide, unsaturated fatty acid amide such as erucic acid amide and oleic acid amide, bisamide such as ethylene bis stearic acid amide and the like. May be used alone or in combination of two or more.
上記遮光性農業用フィルムの厚みは、薄いと、遮光性農業用フィルムの機械的強度が低下することがある一方、厚いと、遮光性農業用フィルムの裁断、接合、展張作業などが困難になり、取扱性が低下するので、５０〜１５０μｍが好ましく、７０〜１２０μｍがより好ましい。 If the light-shielding agricultural film is thin, the mechanical strength of the light-shielding agricultural film may be reduced. On the other hand, if it is thick, it becomes difficult to cut, bond, and stretch the light-shielding agricultural film. Since handling property falls, 50-150 micrometers is preferable and 70-120 micrometers is more preferable.
次に、上記遮光性農業用フィルムの製膜方法について説明する。上記遮光性農業用フィルムの製造方法としては、特に限定されず、例えば、多層インフレーション法、多層Ｔダイ法、多層ラミネート法、カレンダー法などの従来公知の方法が挙げられる。 Next, a method for forming the light-shielding agricultural film will be described. The method for producing the light-shielding agricultural film is not particularly limited, and examples thereof include conventionally known methods such as a multilayer inflation method, a multilayer T-die method, a multilayer lamination method, and a calendar method.
上記製膜方法の中でも、各層を構成する樹脂組成物をそれぞれ別々の押出機内で溶融混練させた後、それぞれの押出機から溶融状態の樹脂組成物を円形の多層ダイスに供給し、円形の多層ダイスから溶融状態の樹脂組成物を共押出して円筒状のフィルムを製膜すると共に、この円形の多層ダイスの中心部から圧縮空気を供給し、共押出製膜された円筒状のフィルムを周方向に延伸することによって遮光性農業用フィルムを製膜する多層インフレーション法が好ましい。 Among the film forming methods described above, the resin composition constituting each layer is melted and kneaded in separate extruders, and then the molten resin composition is supplied from each extruder to a circular multilayer die. A cylindrical resin film is formed by co-extrusion of a molten resin composition from a die, and compressed air is supplied from the center of the circular multi-layer die, so that the co-extruded cylindrical film is circumferentially formed. A multilayer inflation method is preferred in which a light-shielding agricultural film is formed by stretching the film.
そして、本発明の遮光性農業用フィルムは、農業用ハウス内において植物の光周性を利用した栽培方法に使用される。具体的には、遮光性農業用フィルムは、農業用ハウス内において栽培されている植物に日光が照射されないようにするために用いられ、層（Ａ）を内側にして農業用ハウスに張設された農業用フィルムの内面に沿って配設されて用いられる。 And the light-shielding agricultural film of this invention is used for the cultivation method using the photoperiodicity of the plant in the agricultural house. Specifically, the light-shielding agricultural film is used to prevent the plants cultivated in the agricultural house from being exposed to sunlight, and is stretched on the agricultural house with the layer (A) inside. Used along the inner surface of the agricultural film.
このようにして農業用ハウス内に照射される日光を遮光性農業用フィルムによって遮蔽し或いは調整し、植物の光周性を利用すると共に農業用ハウス内の温度を調整することによって、例えば、花芽の形成や開花時期を調整することができる。 In this way, the sunlight irradiated in the agricultural house is shielded or adjusted by the light-shielding agricultural film, the photoperiodicity of the plant is used, and the temperature in the agricultural house is adjusted, for example, flower buds. The formation and flowering time can be adjusted.
一方、農業用ハウス内において栽培されている植物に日光を照射させる場合には、遮光性農業用フィルムを除去すればよく、植物に対する日光の照射及び遮蔽を遮光性農業用フィルムの配設、除去によって容易に調整することができる。 On the other hand, when irradiating the plants cultivated in the agricultural house with sunlight, the light-shielding agricultural film may be removed, and the irradiation and shielding of the sunlight with respect to the plants are arranged and removed. Can be adjusted easily.
本発明の遮光性農業用フィルムは、各層に白色顔料が含有されると共に、層（Ａ）及び層（Ｂ）に黒色顔料が含有されているため、層（Ｃ）が白色に、層（Ａ）及び（Ｂ）が灰色になるように構成されている。従って、上記遮光性農業用フィルムの層（Ｃ）にて日光の一部が反射されると共に、層（Ｂ）を透過した日光は、層（Ａ）及び（Ｂ）にて吸収されるので、優れた遮光性を有している。 The light-shielding agricultural film of the present invention contains a white pigment in each layer and a black pigment in layers (A) and (B), so that the layer (C) is white and the layer (A ) And (B) are configured to be gray. Therefore, part of the sunlight is reflected by the layer (C) of the light-shielding agricultural film, and the sunlight transmitted through the layer (B) is absorbed by the layers (A) and (B). Has excellent light shielding properties.
又、上記遮光性農業用フィルムは、各層に白色顔料を含有し且つ層（Ｃ）が白色であり、熱線である赤外線や遠赤外線を反射するので、遮熱性に優れている。 Further, the light-shielding agricultural film contains a white pigment in each layer and the layer (C) is white and reflects infrared rays or far-infrared rays, which are heat rays, and thus has excellent heat shielding properties.
そして、本発明の遮光性農業用フィルムは、アルミニウムを含有せず、柔軟性に優れているため、コンパクトに収納することができ、カーテン資材として好適に使用することができる。 And since the light-shielding agricultural film of this invention does not contain aluminum and is excellent in a softness | flexibility, it can accommodate compactly and can be used suitably as a curtain material.
更に、本発明の遮光性農業用フィルムは、その表面に無機微粒子を有する防曇剤を塗布していないので、カーテン資材として使用した場合、カーテン資材の開閉によりフィルム表面が擦れても、フィルム表面に擦れ傷が生じにくい。そのため、上記遮光性農業用フィルムの表面に付着した結露水が、擦れ傷部分で停滞して植物の上に落下することなく、フィルム表面を伝って円滑に地面へと流れるため、作物に病害が発生するようなことはほとんどない。 Furthermore, since the light-shielding agricultural film of the present invention is not coated with an antifogging agent having inorganic fine particles on its surface, when used as a curtain material, even if the film surface is rubbed by opening and closing the curtain material, the film surface Scratches are less likely to occur. For this reason, the condensed water adhering to the surface of the light-shielding agricultural film does not stagnate at the scratched part and falls on the plant, but flows smoothly through the film surface to the ground. There is almost no occurrence.
以下に実施例を挙げて本発明の態様を更に詳しく説明するが、本発明はこれら実施例にのみ限定されるものではない。 Hereinafter, embodiments of the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these examples.
（実施例１〜７、比較例１〜９）
〔樹脂組成物（ａ）の調製〕
表１、２に示した所定量の、直鎖状低密度ポリエチレン（密度：０．９２０ｇ／ｃｍ3、メルトフローレイト：１．２ｇ／１０分）、低密度ポリエチレンＡ（密度：０．９２０ｇ／ｃｍ3、メルトフローレイト：１．２ｇ／１０分）、非イオン系界面活性剤マスターバッチ（理研ビタミン社製 商品名「Ｓ７１−Ｄ」、非イオン系界面活性剤含有量：２０重量％、低密度ポリエチレン含有量：８０重量％、非イオン系界面活性剤の主成分：ジグリセリンステアリン酸エステル、低密度ポリエチレンの密度：０．９２０ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：４．０ｇ／１０分）、白色顔料マスターバッチ（東京インキ社製 商品名「ＰＥＸ６８００」、ルチル型酸化チタン含有量：６０重量％、低密度ポリエチレン含有量：４０重量％、ルチル型酸化チタンの平均粒子径：２３０ｎｍ、低密度ポリエチレンの密度：０．９１９ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：２．０ｇ／１０分）及び黒色顔料マスターバッチ（東京インキ社製 商品名「ＰＥＸ９９８０２０」、カーボンブラック含有量：４０重量％、低密度ポリエチレン含有量：６０重量％、低密度ポリエチレンの密度：０．９１９ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：２．０ｇ／１０分）からなる樹脂組成物（ａ）を調製した。なお、表１、２中における「低密度ポリエチレンＭ」の含有量とは、白色顔料マスターバッチ、黒色顔料マスターバッチ及び非イオン系界面活性剤マスターバッチに含有されている低密度ポリエチレンの合計量を示す。
(Examples 1-7, Comparative Examples 1-9)
[Preparation of resin composition (a)]
A predetermined amount of linear low density polyethylene (density: 0.920 g / cm 3 , melt flow rate: 1.2 g / 10 min), low density polyethylene A (density: 0.920 g / min) shown in Tables 1 and 2. cm 3 , melt flow rate: 1.2 g / 10 min), nonionic surfactant master batch (trade name “S71-D” manufactured by Riken Vitamin Co., Ltd.), nonionic surfactant content: 20% by weight, low Density polyethylene content: 80% by weight, main component of nonionic surfactant: diglycerin stearate, density of low density polyethylene: 0.920 g / cm 3 , melt flow rate of low density polyethylene: 4.0 g / 10 minutes), white pigment master batch (trade name “PEX6800” manufactured by Tokyo Ink Co., Ltd.), rutile titanium oxide content: 60% by weight, low density polyethylene content: 4 Wt%, average particle diameter of the rutile type titanium oxide: 230 nm, density of the low density polyethylene: 0.919 g / cm 3, a low density polyethylene melt flow rate: 2.0 g / 10 min) and a black pigment master batch (Tokyo Ink Product name “PEX998020”, carbon black content: 40% by weight, low density polyethylene content: 60% by weight, density of low density polyethylene: 0.919 g / cm 3 , melt flow rate of low density polyethylene: 2. A resin composition (a) consisting of 0 g / 10 min was prepared. In Tables 1 and 2, the content of “low density polyethylene M” is the total amount of low density polyethylene contained in the white pigment masterbatch, black pigment masterbatch and nonionic surfactant masterbatch. Show.
〔樹脂組成物（ｂ）の調製〕
エチレン−酢酸ビニル共重合体Ｂ（酢酸ビニル成分含有量：１０重量％、密度：０．９３０ｇ／ｃｍ3、メルトフローレイト：１．０ｇ／１０分）１００重量部、非イオン系界面活性剤マスターバッチ（理研ビタミン社製 商品名「Ｓ７１−Ｄ」、非イオン系界面活性剤含有量：２０重量％、低密度ポリエチレン含有量：８０重量％、非イオン系界面活性剤の主成分：ジグリセリンステアリン酸エステル、低密度ポリエチレンの密度：０．９２０ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：４．０ｇ／１０分）１０重量部、並びに、表１、２に示した所定量の、白色顔料マスターバッチ（東京インキ社製 商品名「ＰＥＸ６８００」、ルチル型酸化チタン含有量：６０重量％、低密度ポリエチレン含有量：４０重量％、ルチル型酸化チタンの平均粒子径：２３０ｎｍ、低密度ポリエチレンの密度：０．９１９ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：２．０ｇ／１０分）及び黒色顔料マスターバッチ（東京インキ社製 商品名「ＰＥＸ９９８０２０」、カーボンブラック含有量：４０重量％、低密度ポリエチレン含有量：６０重量％、低密度ポリエチレンの密度：０．９１９ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：２．０ｇ／１０分）からなる樹脂組成物（ｂ）を調製した。
[Preparation of resin composition (b)]
100 parts by weight of ethylene-vinyl acetate copolymer B (vinyl acetate component content: 10% by weight, density: 0.930 g / cm 3 , melt flow rate: 1.0 g / 10 min), nonionic surfactant master Batch (Riken Vitamin Co., Ltd., trade name “S71-D”, nonionic surfactant content: 20% by weight, low density polyethylene content: 80% by weight, main component of nonionic surfactant: diglycerin stearin Acid ester, density of low-density polyethylene: 0.920 g / cm 3 , low-density polyethylene melt flow rate: 4.0 g / 10 min) 10 parts by weight, and a predetermined amount of white pigment shown in Tables 1 and 2 Master batch (trade name “PEX6800” manufactured by Tokyo Ink Co., Ltd., rutile titanium oxide content: 60% by weight, low density polyethylene content: 40% by weight, rutile acid The average particle size of the titanium: 230 nm, a low density polyethylene Density: 0.919g / cm 3, a low density polyethylene melt flow rate: 2.0 g / 10 min) and a black pigment master batch (Tokyo Ink Co., Ltd. trade name "PEX998020 ”, Carbon black content: 40 wt%, low density polyethylene content: 60 wt%, low density polyethylene density: 0.919 g / cm 3 , low density polyethylene melt flow rate: 2.0 g / 10 min) A resin composition (b) was prepared.
〔樹脂組成物（ｃ）の調製〕
エチレン−酢酸ビニル共重合体Ｃ（酢酸ビニル成分含有量：５重量％、密度：０．９３０ｇ／ｃｍ3、メルトフローレイト：１．０ｇ／１０分）１００重量部、非イオン系界面活性剤マスターバッチ（理研ビタミン社製 商品名「Ｓ７１−Ｄ」、非イオン系界面活性剤含有量：２０重量％、低密度ポリエチレン含有量：８０重量％、非イオン系界面活性剤の主成分：ジグリセリンステアリン酸エステル、低密度ポリエチレンの密度：０．９２０ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：４．０ｇ／１０分）１０重量部、及び、表１、２に示した所定量の白色顔料マスターバッチ（東京インキ社製 商品名「ＰＥＸ６８００」、ルチル型酸化チタン含有量：６０重量％、低密度ポリエチレン含有量：４０重量％、ルチル型酸化チタンの平均粒子径：２３０ｎｍ、低密度ポリエチレンの密度：０．９１９ｇ／ｃｍ3、低密度ポリエチレンのメルトフローレイト：２．０ｇ／１０分）からなる樹脂組成物（ｃ）を調製した。
[Preparation of resin composition (c)]
100 parts by weight of ethylene-vinyl acetate copolymer C (vinyl acetate component content: 5% by weight, density: 0.930 g / cm 3 , melt flow rate: 1.0 g / 10 min), nonionic surfactant master Batch (Riken Vitamin Co., Ltd., trade name “S71-D”, nonionic surfactant content: 20% by weight, low density polyethylene content: 80% by weight, main component of nonionic surfactant: diglycerin stearin Acid ester, density of low density polyethylene: 0.920 g / cm 3 , melt flow rate of low density polyethylene: 4.0 g / 10 min) 10 parts by weight, and a predetermined amount of white pigment master shown in Tables 1 and 2 Batch (trade name “PEX6800” manufactured by Tokyo Ink Co., Ltd., rutile type titanium oxide content: 60% by weight, low density polyethylene content: 40% by weight, rutile type titanium oxide The average particle diameter of: 230 nm, a low density polyethylene Density: 0.919 g / cm 3, low density polyethylene melt flow rate: was prepared 2.0 g / 10 min) resin composition comprising (c).
（遮光性農業用フィルムの製膜）
層（Ａ）用、層（Ｂ）用、層（Ｃ）用の三機の押出機の先端を同一の円形の多層ダイスに接続させてなる多層製膜装置を用意し、この多層製膜装置の層（Ａ）用の押出機に樹脂組成物（ａ）を、層（Ｂ）用の押出機に樹脂組成物（ｂ）を、層（Ｃ）用の押出機に樹脂組成物（ｃ）を供給して、上記三機の押出機内でそれぞれ溶融混練させた後、各押出機から溶融状態の樹脂組成物を円形の多層ダイスに供給し、円形の多層ダイスから溶融状態の樹脂組成物を、層（Ａ）、層（Ｂ）、層（Ｃ）がこの順に積層一体化された状態となるように共押出製膜すると共に、円形の多層ダイスの中心部から圧縮空気を供給して、共押出製膜された円筒状のフィルムを周方向に延伸した後、冷却空気により円筒状のフィルムを冷却し、円筒状のフィルムを切り開いて巻き取ることにより、全体厚みが１００μｍ、各層の厚み比（層（Ａ）／層（Ｂ）／層（Ｃ））が１／３／１である遮光性農業用フィルムを製膜した。
(Shading of light-shielding agricultural film)
A multilayer film forming apparatus in which the tips of three extruders for layer (A), layer (B), and layer (C) are connected to the same circular multilayer die is prepared. The resin composition (a) for the layer (A) extruder, the resin composition (b) for the layer (B) extruder, and the resin composition (c) for the layer (C) extruder. The melted resin composition is supplied from each extruder to a circular multilayer die, and the molten resin composition is supplied from the circular multilayer die. The layer (A), the layer (B), and the layer (C) are co-extruded to form a laminated and integrated state in this order, and compressed air is supplied from the center of the circular multilayer die, After the coextruded cylindrical film is stretched in the circumferential direction, the cylindrical film is cooled by cooling air, and the cylindrical film is cut. By open wound, the whole thickness of 100 [mu] m, each layer thickness ratio of (the layer (A) / layer (B) / layer (C)) is was formed a light-shielding agricultural film is 1/3/1.
次に、上記のようにして得られた遮光性農業用フィルムの遮光性、層（Ｃ）の白色性、機械的強度を下記の要領で評価し、その結果を表１及び表２に示した。なお、表１及び表２中の樹脂組成物（ａ）、（ｂ）及び（ｃ）の「非イオン系界面活性剤含有量」の欄における括弧内の数値は、各樹脂組成物中に含有されている樹脂成分の総量を１００重量部に換算したときの非イオン系界面活性剤の含有量（重量部）を示す。又、表１及び表２中の樹脂組成物（ａ）の「白色顔料含有量」及び「黒色顔料含有量」の欄における括弧内の数値は、樹脂組成物（ａ）中に含有されている、密度が０．９００〜０．９３０ｇ／ｃｍ3で且つメルトフローレイト（ＭＦＲ）が０．３〜５．０ｇ／１０分であるポリエチレン系樹脂の総量を１００重量部に換算したときの白色顔料含有量（重量部）又は黒色顔料含有量（重量部）を示す。 Next, the light shielding property of the light shielding agricultural film obtained as described above, the whiteness of the layer (C), and the mechanical strength were evaluated in the following manner, and the results are shown in Tables 1 and 2. . In addition, the numerical value in the parenthesis in the column of “nonionic surfactant content” of the resin compositions (a), (b) and (c) in Table 1 and Table 2 is included in each resin composition. It shows the content (parts by weight) of the nonionic surfactant when the total amount of the resin components used is converted to 100 parts by weight. The numerical values in parentheses in the columns of “white pigment content” and “black pigment content” of the resin composition (a) in Tables 1 and 2 are contained in the resin composition (a). White pigment when the total amount of polyethylene resin having a density of 0.900 to 0.930 g / cm 3 and a melt flow rate (MFR) of 0.3 to 5.0 g / 10 min is converted to 100 parts by weight The content (parts by weight) or the black pigment content (parts by weight) is shown.
（遮光性）
得られた遮光性農業用フィルムを用いて照度計（カスタム社製 商品名「ＬＸ−１３３２」）の受光部を隙間なく覆い、この照度計を用いて、外部照度１０万ルクスの条件下における照度を測定して、下記基準に基づき、遮光性農業用フィルムの遮光性を評価した。
○：照度が２ルクス未満であった。
△：照度が２ルクス以上で且つ５ルクス未満であった。
×：照度が５ルクス以上であった。
(Light shielding)
The light-shielding agricultural film thus obtained is used to cover the light receiving part of the illuminance meter (trade name “LX-1332” manufactured by Custom Co., Ltd.) without any gap, and the illuminance under the condition of an external illuminance of 100,000 lux is obtained using this illuminance meter. Was measured, and the light-shielding property of the light-shielding agricultural film was evaluated based on the following criteria.
○: Illuminance was less than 2 lux.
Δ: Illuminance was 2 lux or more and less than 5 lux.
X: Illuminance was 5 lux or more.
（層（Ｃ）の白色性）
得られた遮光性農業用フィルムの層（Ｃ）を目視観察し、下記基準に基づき、層（Ｃ）の白色性を評価した。
○：層（Ｃ）は、きれいな白色を呈している。
△：層（Ｃ）は、やや灰色っぽく見えるものの概ね白色である。
×：層（Ｃ）は、灰色っぽくなり、白色性が失われている。
(Whiteness of layer (C))
The layer (C) of the obtained light-shielding agricultural film was visually observed, and the whiteness of the layer (C) was evaluated based on the following criteria.
○: The layer (C) has a beautiful white color.
(Triangle | delta): Although a layer (C) looks a little grayish, it is substantially white.
X: The layer (C) becomes grayish and whiteness is lost.
（機械的強度）
得られた遮光性農業用フィルムの引張破断点荷重を、ストログラフ（東洋精機製作所社製）を用いて、ＪＩＳ Ｋ６７８１に準拠して測定し、下記基準に基づき、遮光性農業用フィルムの機械的強度を評価した。
○：破断点荷重は３０００ｇ以上であった。
△：破断点荷重は１０００ｇ以上で且つ３０００ｇ未満であった。
×：破断点荷重は１０００ｇ未満であった。
(Mechanical strength)
The tensile breaking point load of the obtained light-shielding agricultural film was measured according to JIS K6781 using a strograph (manufactured by Toyo Seiki Seisakusho Co., Ltd.). The strength was evaluated.
(Circle): The breaking point load was 3000 g or more.
(Triangle | delta): The breaking point load was 1000 g or more and less than 3000 g.
X: The load at break was less than 1000 g.
Claims (4)