JP2008307786A - Antifalsifying printed matter - Google Patents
Antifalsifying printed matter Download PDFInfo
- Publication number
- JP2008307786A JP2008307786A JP2007157616A JP2007157616A JP2008307786A JP 2008307786 A JP2008307786 A JP 2008307786A JP 2007157616 A JP2007157616 A JP 2007157616A JP 2007157616 A JP2007157616 A JP 2007157616A JP 2008307786 A JP2008307786 A JP 2008307786A
- Authority
- JP
- Japan
- Prior art keywords
- printed
- printed matter
- printing
- antifalsifying
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、カラー複写機の性能が大幅に向上しても、偽造防止性を維持され、また特別な印刷技術を要せずに、作製できる偽造防止印刷物に関するものである。 The present invention relates to an anti-counterfeit printed matter that can maintain anti-counterfeiting properties and can be produced without requiring a special printing technique even when the performance of a color copying machine is greatly improved.
近年、カラー複写機、プリンターの分解能、色再現性等の性能が大幅に向上したことから、複写原本と見分けの付け難い複写物を容易に作製することができるようになってきた。このようなカラー複写機の出現は、本来は社会の利益となるものである。しかし、これを悪用して、紙幣、有価証券、権利書等の精巧な複写物を作製し、使用することが社会問題となっている。 In recent years, the performance of color copiers and printers, such as the resolution and color reproducibility, has greatly improved, and it has become possible to easily produce copies that are difficult to distinguish from the original copy. The appearance of such a color copier is essentially a social benefit. However, it has become a social problem to exploit and use elaborate copies such as banknotes, securities, and rights documents.
それに対し、上記のようなカラー複写機を悪用した偽造を防止する方法が種々検討されている。例えば、特許文献１に示すように、カラー複写機のスキャナーに収集されたフィルターを通して得られるシアン、マゼンタ、イエローの各色の分色情報と、それに対応するシアン、マゼンタ、イエローの各色の再現色との間にある色情報のギャップの生じ易い色を用い、再現色の変色を生じさせることで、偽造を防止する方法が知られている。また、特許文献２に示すように、スキャナーの分解精度による再現の色限界を利用して、線数の異なる印刷柄を重ねて、目視では柄のつぶれにより連続に見られる模様が複写再現では色とびを生じて、柄が不連続となることによる再現の困難な偽造防止印刷も知られている。
On the other hand, various methods for preventing forgery using the color copying machine as described above have been studied. For example, as shown in
上記の前者の方法では、スキャナー精度やトナー等の色材の色再現性が向上することにより、複写再現は可能となる傾向があり、さらに各種調整を行うことにより再現が可能になる場合もある。また、後者の方法では、線種の異なる印刷柄で目視の連続性を確保するためには、印刷時の濃淡の管理が難しく、高度な技術を要する問題がある。
したがって、本発明は、カラー複写機の性能によらず、特にカラー複写機の性能が大幅に向上しても、偽造防止性が維持され、また特別な印刷技術を要せずに、作製することができる偽造防止印刷物を提供することを目的とするものである。 Therefore, the present invention can be manufactured without depending on the performance of the color copying machine, especially when the performance of the color copying machine is greatly improved, and the anti-counterfeiting property is maintained and no special printing technique is required. It is an object to provide a forgery-proof printed matter that can be printed.
上記課題を解決するために、本発明の請求項１の発明は、基紙に、アミド化合物、またはその塩を主成分とする透明化材料と、蛍光材料を含有するインキにより、印刷層が形成されたことを特徴とする偽造防止印刷物である。また、請求項２は、前記印刷層の上に、固定情報あるいは可変情報の印刷、印字がなされていることを特徴とする。
In order to solve the above-mentioned problems, the invention of
本発明の偽造防止印刷物は、基紙に、アミド化合物、またはその塩を主成分とする透明化材料と、蛍光材料を含有するインキにより、印刷層が形成されている。したがって、セルロース繊維からなる基紙の空隙に対し、前記インキが浸透して、その空隙を埋めることで、該インキによる印刷された部分（印刷層）が透明化した印刷物を得ることができる。これにより、この印刷物をカラー複写機により、複製しようとしても、透明化した印刷層は再現できず、偽造防止の十分な効果を発揮することができる。また、その偽造防止印刷物は、特別な印刷技術を必要とせずに、グラビア印刷、凸版印刷等、従来から知られた一般的な印刷方法で形成することができる。 In the forgery-preventing printed matter of the present invention, a printed layer is formed on a base paper with a transparent material mainly composed of an amide compound or a salt thereof and an ink containing a fluorescent material. Accordingly, the ink penetrates into the gaps in the base paper made of cellulose fibers and fills the gaps, whereby a printed matter in which the printed portion (printing layer) with the inks is transparent can be obtained. As a result, even if the printed material is reproduced by a color copying machine, the transparent printed layer cannot be reproduced, and a sufficient effect of preventing forgery can be exhibited. Further, the forgery-preventing printed matter can be formed by a conventionally known general printing method such as gravure printing or letterpress printing without requiring a special printing technique.
また、本発明の偽造防止印刷物は、前記印刷層の上に、固定情報あるいは可変情報の印刷、印字を行うことができる。前記の透明化材料と、蛍光材料を含有するインキにより形成された印刷層は、表面にべたつきや、目立つ凹凸が無く、オフセット印刷、グラビア印刷等で、固定情報を問題なく、設けることができ、また電子写真方式、熱転写記録方式等により、住所、氏名等の個人情報等の可変情報を印字することも、何ら問題なく行える。これにより、偽造防止性がより高められ、個人用途、特定商品向けなど、各種用途に利用することができる。 In addition, the forgery-preventing printed matter of the present invention can perform printing and printing of fixed information or variable information on the printing layer. The printing layer formed of the transparent material and the ink containing the fluorescent material has no stickiness or conspicuous unevenness on the surface, and can provide fixed information without problems by offset printing, gravure printing, Also, variable information such as personal information such as address and name can be printed without any problem by an electrophotographic system, a thermal transfer recording system, or the like. Thereby, forgery prevention property is improved more and it can utilize for various uses, such as a personal use and for specific goods.
以下、本発明の偽造防止印刷物について詳細に説明する。
（実施形態）
図１に、概略図として本発明の偽造防止印刷物の一つの実施形態を示す。基紙２に、アミド化合物、またはその塩を主成分とする透明化材料と、蛍光材料を含有するインキにより、印刷された印刷層３が形成されている。図示した偽造防止印刷物１は、基紙２の一方の面に、固定情報４が、印刷層３の上、及び印刷層３から外れた位置に、形成されている。また、基紙２の一方の面に、可変情報５が印刷層３の上、及び印刷層３から外れた位置に形成されている。図示したものに限らず、基紙の両面に固定情報、可変情報を設けたり、固定情報を基紙の片面に設け、可変情報を基材の他方の面に設けたり、適宜変更することができる。
Hereinafter, the anti-counterfeit printed matter of the present invention will be described in detail.
(Embodiment)
FIG. 1 schematically shows one embodiment of the anti-counterfeit printed matter of the present invention. A printed layer 3 is formed on the base paper 2 by using a transparent material mainly composed of an amide compound or a salt thereof and an ink containing a fluorescent material. The illustrated anti-counterfeit printed
（基紙）
本発明の偽造防止印刷物の基紙２は、セルロース繊維を主体として構成され、針葉樹晒クラフトパルプ（ＮＢＫＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒サルファイトパルプ（ＮＢＳＰ）、サーモメカニカルパルプ（ＴＭＰ）等の製紙用パルプを主体として、抄造したものである。平滑性を有し、透明化材料、蛍光材料を含有するインキにより印刷された部分が基紙に浸透して、透明化すれば、基紙として適用できるものは限定しないが、一般的に用いられる上質紙、中質紙（中性紙または酸性紙）を用いることが好ましい。
(Base paper)
The base paper 2 of the anti-counterfeit printed matter of the present invention is mainly composed of cellulose fibers, and is composed of softwood bleached kraft pulp (NBKP), hardwood bleached kraft pulp (LBKP), softwood bleached sulfite pulp (NBSP), and thermomechanical pulp (TMP). ) And other paper pulp. There are no limitations on what can be used as the base paper if it is smooth and transparent when the portion printed with the ink containing the transparent material or fluorescent material penetrates into the base paper and becomes transparent. It is preferable to use high quality paper or medium quality paper (neutral paper or acidic paper).
（印刷層）
透明化材料と、蛍光材料を含有するインキを用いて、上記基紙に文字、パターンなどを印刷して、印刷層３が形成される。透明化材料は、アミド化合物、またはその塩を主成分とするが、アミド化合物としては、以下のものが使用できる。モノカルボン酸や、多価カルボン酸等のカルボン酸と、ポリアルキレンポリアミン、アルカノールアミン等のアミン化合物とを縮合させて得られるアミド化合物が、本発明で好ましく使用される。また前記アミド化合物を、カルボン酸等で中和して得られるアミド化合物の酸塩であってもよい。また、紙への浸透性を向上させるために、エタノール、プロピルアルコール等のアルコール溶剤や、アニオン界面活性剤等を少量添加することができる。
(Print layer)
A printing layer 3 is formed by printing characters, patterns, and the like on the base paper using a transparent material and an ink containing a fluorescent material. The transparent material is mainly composed of an amide compound or a salt thereof. As the amide compound, the following can be used. Amide compounds obtained by condensing monocarboxylic acids, carboxylic acids such as polycarboxylic acids, and amine compounds such as polyalkylene polyamines and alkanolamines are preferably used in the present invention. Further, it may be an acid salt of an amide compound obtained by neutralizing the amide compound with carboxylic acid or the like. Moreover, in order to improve the permeability to paper, a small amount of an alcohol solvent such as ethanol or propyl alcohol, an anionic surfactant or the like can be added.
また印刷層における蛍光材料は、紫外線または赤外線の照射により蛍光発光する材料であり、本発明では紫外線励起可視光蛍光発光タイプ、あるいは赤外線励起可視光蛍光発光タイプの蛍光材料を使用することができる。紫外線励起可視光蛍光発光タイプは、紫外線により励起され、これよりも低いエネルギー準位に戻るときに発するスペクトルのピークが青、緑、赤等の波長域にあるものであり、硫化亜鉛やアルカリ土類金属の硫化物などの高純度蛍光体に発光をより強くするために微量の金属（銅、銀、マンガン、ビスマス、鉛）を付活剤として加え高温焼成して得られる。 The fluorescent material in the printed layer is a material that emits fluorescence when irradiated with ultraviolet rays or infrared rays. In the present invention, an ultraviolet-excited visible light fluorescent emission type or an infrared-excited visible light fluorescent emission type fluorescent material can be used. The UV-excited visible light fluorescent emission type has a spectrum peak emitted in the wavelength range of blue, green, red, etc. when excited by UV and returns to a lower energy level. It is obtained by adding a trace amount of metal (copper, silver, manganese, bismuth, lead) as an activator and firing at high temperature in order to enhance the emission of light to a high-purity phosphor such as a sulfide of a similar metal.
具体例としては、Ｃａ2Ｂ5Ｏ9Ｃｌ：Ｅｕ2+、ＣａＷＯ4、ＺｎＯ：Ｚｎ、Ｚｎ2ＳｉＯ4：Ｍｎ、Ｙ2Ｏ2Ｓ：Ｅｕ、ＺｎＳ：Ａｇ、ＹＶＯ4：Ｅｕ、Ｙ2Ｏ3：Ｅｕ、Ｇｄ2Ｏ2Ｓ：Ｔｂ、Ｌａ2Ｏ2Ｓ：Ｔｂ、Ｙ3Ａｌ5Ｏ12：Ｃｅ、Ｓｒ5（ＰＯ4）3Ｃｌ：Ｅｕ、３（Ｂａ，Ｍｇ）Ｏ・８Ａｌ2Ｏ3：Ｅｕ、Ｚｎ2ＧｅＯ4：Ｍｎ、Ｙ（Ｐ，Ｖ）Ｏ4：Ｅｕ、０．５ＭｇＦ2・３．５ＭｇＯ・ＧｅＯ2：Ｍｎ、ＺｎＳ：Ｃｕ、ＺｎＳ：Ｍｎなどがあり、これらを単体、又はこれらから数種類を任意に選択して混合して使用する。これらの蛍光スペクトルはピークを青、緑、赤等の波長域以外に持つものであり、所望の蛍光スペクトルに応じて適宜選択することができる。 Specific examples include Ca 2 B 5 O 9 Cl: Eu 2+ , CaWO 4 , ZnO: Zn, Zn 2 SiO 4 : Mn, Y 2 O 2 S: Eu, ZnS: Ag, YVO 4 : Eu, Y 2. O 3 : Eu, Gd 2 O 2 S: Tb, La 2 O 2 S: Tb, Y 3 Al 5 O 12 : Ce, Sr 5 (PO 4 ) 3 Cl: Eu, 3 (Ba, Mg) O · 8Al 2 O 3 : Eu, Zn 2 GeO 4 : Mn, Y (P, V) O 4 : Eu, 0.5MgF 2 · 3.5MgO · GeO 2 : Mn, ZnS: Cu, ZnS: Mn, etc. Are used alone, or several kinds of them are arbitrarily selected and mixed for use. These fluorescence spectra have peaks outside the wavelength range such as blue, green, and red, and can be appropriately selected according to a desired fluorescence spectrum.
なお、紫外線発光蛍光剤は、紫外線の短波長域（約２００〜３００ｎｍ、とくに好ましくは２５４ｎｍ）により発光する短波長紫外線発光蛍光剤と、長波長域（約３００〜４００ｎｍ、とくに好ましくは３６５ｎｍ）により発光する長波長紫外線発光蛍光剤があり、いずれのものでも使用できる。 The ultraviolet light emitting fluorescent agent is a short wavelength ultraviolet light emitting fluorescent agent that emits light in the short wavelength range of ultraviolet rays (about 200 to 300 nm, particularly preferably 254 nm) and the long wavelength range (about 300 to 400 nm, particularly preferably 365 nm). There are long-wavelength ultraviolet-emitting fluorescent agents that emit light, and any of them can be used.
赤外線励起可視光蛍光発光タイプは、赤外光（約８００〜約１２００ｎｍ）で励起し可視光（約４００〜約８００ｎｍ）を発光する蛍光材料である。このタイプの具体例としてはＹＦ3：Ｙｂ＋Ｅｒ、ＹＦ3：Ｙｂ＋Ｔｍ、ＢａＦＣｌ：Ｙｂ＋Ｅｒなどがある。尚、上記の紫外線発光蛍光剤、赤外線発光蛍光剤は通常その組成を、主成分である母体結晶とその中に分散した付活剤または発光中心に分け、（：）で繋いで表記する。 The infrared excitation visible light fluorescence emission type is a fluorescent material that is excited by infrared light (about 800 to about 1200 nm) and emits visible light (about 400 to about 800 nm). Specific examples of this type include YF 3 : Yb + Er, YF 3 : Yb + Tm, BaFCl: Yb + Er, and the like. The composition of the ultraviolet light emitting fluorescent agent and the infrared light emitting fluorescent agent is usually divided into a parent crystal, which is a main component, and an activator or a light emission center dispersed therein, and connected by (:).
印刷層を形成するためのインキは、上記の透明化材料に対して、蛍光材料を０．５〜５％（質量基準）の割合で混合したものを、有機溶剤、アルコール、水等の溶媒に、分散あるいは溶解させて調整し、作製することができる。そして、そのインキにより、グラビア印刷、凸版印刷等の方法により、各種の文字、パターンの図柄を形成する。その印刷層を形成する際、塗工量で、印刷対象の基紙の坪量に対して、２０〜１００質量％（乾燥時）が好ましい。その塗工量が少なすぎると、透明化が十分でなく、また一方で塗工量が多すぎると、印刷部の表面がべたつき好ましくない。 The ink for forming the printing layer is a mixture of the above-mentioned transparent material mixed with a fluorescent material in a proportion of 0.5 to 5% (mass basis) in a solvent such as an organic solvent, alcohol or water. It can be prepared by dispersing or dissolving. Then, various characters and patterns are formed with the ink by a method such as gravure printing or letterpress printing. When the printing layer is formed, the coating amount is preferably 20 to 100% by mass (when dry) with respect to the basis weight of the base paper to be printed. If the coating amount is too small, the transparency is not sufficient. On the other hand, if the coating amount is too large, the surface of the printing part is not preferable because it is sticky.
（固定情報、可変情報）
本発明の偽造防止印刷物は、上記のアミド化合物、またはその塩を主成分とする透明化材料と、蛍光材料を含有するインキにより、形成された印刷層と、さらに固定情報あるいは可変情報を、印刷や印字により設けることができる。特に、印刷層の上に、固定情報あるいは可変情報の印刷、印字がなされていることが好ましく、これにより偽造防止性がより高められる。
(Fixed information, variable information)
The forgery-preventing printed matter of the present invention is a printing layer formed of a transparent material mainly composed of the amide compound or salt thereof and an ink containing a fluorescent material, and further printing fixed information or variable information. Or by printing. In particular, it is preferable that fixed information or variable information is printed or printed on the print layer, thereby further improving the anti-counterfeiting property.
可変情報とは、一単位の偽造防止印刷物毎に異なる情報、または一単位の偽造防止印刷物の或る複数単位を一群として、該一群単位で異なる情報である。例えば、偽造防止印刷物が身分証明書であれば、個人名、生年月日等である。また、固定情報とは、一単位の偽造防止印刷物間で共通する情報、一単位の偽造防止印刷物の或る複数単位を一群として、該一群単位で共通する情報である。例えば、偽造防止印刷物が身分証明書であれば、会社名、有効期限の月日等である。 The variable information is information that is different for each unit of anti-counterfeit printed matter, or information that is different for each group by taking a plurality of units of one unit of anti-counterfeit printed matter as a group. For example, if the anti-counterfeit printed matter is an identification card, the personal name, date of birth, etc. The fixed information is information common to one unit of anti-counterfeit printed matter, and information common to one group of a plurality of units of one unit of anti-counterfeit printed matter. For example, if the forgery-preventing printed material is an identification card, the company name, the expiration date, etc.
固定情報は、一定の情報を多数の単位で印刷されるもので、オフセット印刷、グラビア印刷等で、印刷装置で形成することができる。可変情報は、電子写真方式、熱転写記録方式等のノーインパクトプリンターにより、印字して形成することができる。上記の印刷層が、透明化材料と、蛍光材料を含有するインキとして、水性タイプのインキを用いて形成された場合、固定情報、可変情報を印刷層の上に形成する際、特に親水性の色材を用いたインクジェット記録方式や、水性インキを用いたフレキソ印刷等は避ける。 The fixed information is a piece of information that is printed in a number of units, and can be formed by a printing apparatus by offset printing, gravure printing, or the like. The variable information can be printed and formed by a no-impact printer such as an electrophotographic system or a thermal transfer recording system. When the printing layer is formed using a water-based ink as an ink containing a transparent material and a fluorescent material, it is particularly hydrophilic when forming fixed information and variable information on the printing layer. Avoid ink-jet recording methods using color materials and flexographic printing using water-based ink.
なお、本発明は、上記実施形態に限定されるものではない。上記実施形態は例示であり、本発明の特許請求の範囲に記載された技術的思想と、実質的に同一の構成を有し、同様な作用効果を奏するものは、いかなる場合であっても本発明の技術的範囲に包含される。 The present invention is not limited to the above embodiment. The above-described embodiment is an exemplification, and the technical idea described in the claims of the present invention has substantially the same configuration and exhibits the same function and effect regardless of the case. It is included in the technical scope of the invention.
次に、実施例を挙げて、本発明についてさらに具体的に説明する。
なお、以下、「部」又は「％」とあるのは、特に断りのない限り質量基準である。
（実施例１）
坪量６４ｇ／ｍ2の上質紙に、下記の印刷層用インキを用いて、グラビア印刷にて、１０ｍｍ幅のストライプ状で、印刷した。塗工量は、基紙の坪量に対して、５０質量％（乾燥時）に相当する、３２ｇ／ｍ2（乾燥時）で、印刷した。
＜印刷層用インキ＞
日華化学（株）製透明化インキの商品名クリネア溶液（アミド化合物、またはその塩を主成分とする透明化材料の溶液）に対し、（株）ユニオンコーポレーション製の商品名エアロインク＃６３３０インビジブル（蛍光材料の含有インキ）を、透明化材料に対して、蛍光材料を１％（質量基準）の割合で混合したもの。
Next, the present invention will be described more specifically with reference to examples.
Hereinafter, “part” or “%” is based on mass unless otherwise specified.
Example 1
It printed on the fine paper of the basic weight of 64 g / m < 2 > by the gravure printing using the following printing layer ink in the stripe form of 10 mm width. The coating amount was 32 g / m 2 (during drying) corresponding to 50% by mass (during drying) with respect to the basis weight of the base paper.
<Ink for printing layer>
Nihonka Chemical Co., Ltd. clearing ink trade name Clinair solution (amide solution or a solution of a clearing material containing a salt thereof as a main component), trade name Aero Ink # 6330 manufactured by Union Corporation (Fluorescent material-containing ink) mixed with a transparent material in a proportion of 1% (based on mass) of the fluorescent material.
上記の印刷層が形成された印刷物に対し、基紙の片面の全面に、大日本印刷（株）のロゴマークを青色インキで固定情報として、オフセット印刷により形成した。さらに、電子写真方式のプリンターを用いて、上記の印刷層の上に、及び印刷層から外れた位置にも、黒色で可変情報を印字した。 For the printed matter on which the above printed layer was formed, the Dainippon Printing Co., Ltd. logo mark was formed as offset information with blue ink on the entire surface of one side of the base paper by offset printing. Furthermore, using an electrophotographic printer, variable information was printed in black on the print layer and at a position off the print layer.
上記の実施例１で作製した偽造防止印刷物は、特別な印刷技術を必要とせずに、従来から知られた一般的な印刷方法で形成したものであり、この偽造防止印刷物をカラー複写機により、複製しようと試みたが、透明化した印刷層は再現できなく、複製に失敗した。また、実施例１で作製した偽造防止印刷物に対し、紫外線ランプ（ブラックライト）を照射すると、印刷層の部分のみが可視光で発光して、偽造防止性の高いものであった。 The anti-counterfeit printed matter produced in the above Example 1 is formed by a conventionally known general printing method without requiring a special printing technique, and the anti-counterfeit printed matter is obtained by a color copying machine. An attempt was made to duplicate, but the transparent printed layer could not be reproduced and the duplication failed. When the anti-counterfeit printed matter produced in Example 1 was irradiated with an ultraviolet lamp (black light), only the printed layer portion emitted light with visible light and had high anti-counterfeiting properties.
１ 偽造防止印刷物
２ 基紙
３ 印刷層
４ 固定情報
５ 可変情報
1 Print forgery prevention 2 Base paper 3 Print layer 4 Fixed information 5 Variable information
Claims (2)
The forgery-preventing printed matter according to claim 1, wherein fixed information or variable information is printed or printed on the printed layer.